By M. T. Hepworth, T. P. Papazoglou

Hydrogen diffusion in hcp and bcc titanium in the temperature range 610° to 900°C was measured by reacting cylindrical specimens of high-purity titanium at constant temperature with small constant pressures of hydrogen of the order of a few Torr. In the range 0 to 6.7 at. pct H in hcp titanium, the diffusion coefficient D in sq cm per sec is given by: where T is in °K and R in cal per g-atom OK. Only three measurements of diffusivity in bcc titanium were made: at 900' : the diffusivity in ß titanium was found to be 1.8 x 10-4 sq crn per sec. McQUILLAN1 has studied the constitution of the Ti-H system and reported the concentration of hydrogen as a function of pressure of hydrogen and temperature. He found hydrogen absorption was reversible and rapid at temperatures above 500°C in both crystallographic modifications, the a (hcp) phase and the ß (bcc) phase, with the latter phase stabilized by hydrogen additions. Wasilewski and Kehl 2 measured the diffusivity of hydrogen in hcp and bcc Ti-H alloys. For bcc alloys, they reacted cylindrical specimens of titanium with hydrogen gas at 1 atm pressure. They measured the rate of absorption of hydrogen isothermally on specimens ranging from zero hydrogen content when above the transformation temperature to hydrogen contents sufficient to stabilize the bcc phase when below the transformation temperature. By integrating Fick's second law for a cylindrical geometry, assuming a diffusion coefficient independent of composition, they calculated diffusivities as a function of temperature. In the range 650" to 1000°C their results in bcc titanium yielded the expression: where D is in sq cm per sec, T in OK, and R the gas constant in cal per g-atom-OK. Their studies on the hcp a phase were conducted by exposing long cylindrical titanium specimens to hydrogen at a sufficiently high pressure to establish a surface layer of fl phase 80 to 120 u thick for the duration of an isothermal experiment. Concentration profiles were then determined by hydrogen analysis from chips obtained upon machining quenched specimens. The diffusivity of hydrogen was then calculated yielding the expression: The present investigation was undertaken principally to redetermine the diffusivity data on a titanium by a direct absorption from the gas phase at sufficiently low hydrogen pressures to avoid the presence of a surface bcc phase and also to check the diffusivity data at low hydrogen concentrations in the bcc stmcture. EXPERIMENTAL PROCEDURE High-purity electrolytic sponge titanium (99.9 pct) of BHN 91 was arc-melted, forged, rolled, and machined into cylinders of final hardness, upon annealing, of BHN 92. Cylindrical specimens of two sets of dimensions were used: 1.524 by 2.931 cm and 1.905 by 3.663 cm diam and length, respectively. The experimental apparatus used for annealing specimens and for admitting known amounts of hydrogen at constant pressure is shown in Fig. 1. In a typical experiment, a specimen was lightly abraded with fine-grain silicon carbide, washed with water and detergent, and then thoroughly degreased with reagent-grade tri-chlorethylene and acetone. The specimen was suspended by a Chrome1 wire in the center of a quartz furnace tube, without contact with the tube, and heated to 925°C (as measured by a thermocouple adjacent to the specimen, outside the tube) for a period of at least 4 hr under a vacuum of from 10-6 to -7 Torr as measured by an ionization gage. The furnace temperature was then adjusted to the temperature chosen for the particular diffusion study and the specimen allowed to equilibrate thermally. Hydrogen was then ad-

Jan 1, 1969

By J. P. Neumann, Y. A. Chang

Lattice parameter measurements of the hcp phase in the system Ag-A1 near the stoichiometric composition Ag2Al were carried out for specimens quenched from 825°K, annealed for 10 days at 453°K, and annealed for 100 days at 413°K. The three heat treatments resulted in the same lattice parameters at room temperature. None of the specimens showed any superlattice lines. The lattice parameters of this alloy were also measured at temperature from 77° to 750°K. An anomaly in the temperature variation of the lattice paramete.rs occurs in the region near 400°k, which may be associated with local ordering. FROM measurements of the diffuse scattering of X-rays, it is known that the [ phase in the system Ag-A1 near the stoichiometric composition Ag2A1 ex- hibits a considerable degree of short-range order at room temperature.' Moreover, based on the position of the short-range order peaks a superlattice model had been proposed in the same study and it was suggested that lowering the annealing temperature to 420°K might result in long-range order. In the present study, the diffraction patterns and the lattice parameters of three differently heat-treated specimens, i.e., quenched from 825°K, annealed for 10 days at 453°K, and annealed for 100 days at 413°K, were determined from 77" to 750°K. The purpose of these measurements was to investigate 1) whether long-range order could be established by prolonged annealing and 2) whether the lattice parameters at room temperature depended on the heat treatment, since it had been proposed earlier2 that the lattice parameters in this phase are related to the atomic arrangement. 1) EXPERIMENTAL TECHNIQUES Silver and aluminum, both 99.99 pct purity, were melted in a zirconium oxide crucible under helium in

Jan 1, 1969

By J. Szekely, Robert J. Fisher

A formulation is Presented and solutions are given for the problem of transient heat conduction in a sphere that undergoes a spatially uniform radiative heat exchange with its environment. The solutions were obtained by the numerical integration of the appropriate Partial differential equation and are Presented in a graphical form by Plotting a dimensionless average temperature against the Fourier number with the radiation number as a paranreter, for various initial sphere and environment temperatures. In addition to these numerical results asymptotic analytical solutions are also given. PROBLEMS involving the transient heating or cooling of droplets and particles frequently arise and are of importance in metallurgical operations. Spray refining, vacuum degassing, high-temperature gas-solid reaction systems, and pebble heaters are but few of the numerous examples that may be quoted. The practical interest in these problems from a design or operational point of view is to evaluate the change in the particle temperature with the time given its physical properties, initial temperature, and that of the environment. At the high temperatures encountered the principal mode of heat transfer between the particles and their environment is by thermal radiation; in case of vacuum degassing due to the very low thermal conductivity of the gas space the convec-tive components are negligible and radiation is the only heat transfer mechanism. Although much work has been done on transient heat conduction problems, the special class mentioned here, in which thermal radiation is specified at the bounding surface, received little attention to date. One contributory factor to this situation may be the nonlinearity of the radiation term in temperature, which in general precludes the use of analytical techniques and requires numerical or analog solution of the appropriate differential equations. In fact the only solutions of general nature that are available at present pertain to semi-infinite media and slabs.'-3 The work on which the paper reports forms part of a program aimed at the theoretical and experimental study of transient radiative heat exchange between particles and their environment. The purpose of the present paper is to develop a formulation and solutions to the problem of transient heat conduction in a sphere that undergoes a spatially uniform radiative heat exchange with its surroundings. The solutions, obtained by the numerical integration of the appropriate differential equations, will be presented graphically, by plotting dimensionless parame- ters covering the range of variables relevant to metallurgical interests, thus affording a ready reference for design calculations. In addition to these results, approximate analytical solutions are also given which represent asymptotes, corresponding to extreme values of the variables mentioned. FORMULATION Consider a spherical particle of radius, a, initially at uniform temperature, Ti (T measured on the absolute scale), having a thermal conductivity, k, density, , specific heat, C, and thermal diffusivity, a. At time = 0 let this particle be exposed to an environment which is at a temperature T, and subsequently let there be a purely radiative heat exchange between the particle and the environment resulting in a spatially uniform heat flux at the surface. If in addition to the above we make the assumptions that the sphere is a gray body radiator, homogeneous, isotropic, and opaque, and that the physical properties are independent of temperature, conservation of heat in the sphere may be written as follows: The boundary condition contained in Eq. [3] states that the initial temperature of the sphere is considered uniform, equalling Ti, whereas Eq. [4] is readily obtained from symmetry considerations. Eq. [5] expresses the continuity of the heat flux at the surface of the sphere, or in other words the condition that the rate of heat exchange between the sur-

Jan 1, 1969

By I. S. Servi, N. W. Marr

TIN markedly increases the softening temperature of pure copper with only a moderate effect on conductivity. Smart and smith' indicated a substantial increase in softening temperature upon addition of different levels of tin up to 0.05 pct in oxygen-free copper. However, after finding no effect of tin in copper containing about 0.025 pct O, they concluded that "the presence of oxygen completely nullifies these changes in properties by precipitation of SnO2.'' Since preliminary tests on Cu-Sn-0 alloys indicated that this conclusion is not valid outside the extremely limited tin range investigated by Smart and Smith, research was primarily directed toward the partition of tin between the copper-base matrix and the oxide phases. Experimental. Material was prepared by sealing an 80 to 100-g charge consisting of oxygen-free copper, tin, and copper oxide into a y-in.-ID quartz capsule which was evacuated and back-filled with tank-grade argon to 3 atm. The sealed vials were heated to 1125ºC, kept at temperature for 30 min, occasionally agitated, and then allowed to air-cool outside the furnace ("as-cast"). The castings were cold-swaged to 0.370 in., annealed 1 hr at 600°C ("as-annealed"), and cold-swaged 16.5 pct ("as-swaged"). Cross sectional wafers were annealed for 1 hr at various temperatures and Rockwell F hardness measured. The "softening temperature" was defined as the interpolated temperature at which the hardness was 50 Rockwell F. Electrical resistance was measured by an ac poten-tiometric method on 0.040-in.-diam wires after a 1 hr anneal at 600°C. Relative accuracy was of the order of 1 pct. Chemical analyses for tin were performed by two methods, identified as "Acid flux" and "HN03 dissolution". The first consisted of fusing the sample with potassium pyrosulfate and leaching the resulting melt with 10 pct sulfuric acid. The spectrophotometric procedure which followed is described in Ref. 2. Oxygen analyses were performed by the vacuum-fusion method with a bath temperature of 1650°C. Tin content of oxides and copper phases was measured with the X-ray microprobe, using a calibration curve based on a series of oxygen-free Cu-Sn alloys. Results. In Fig. 1, the nominal tin composition for alloys containing nominally 400 ppm O was plotted vs the analyzed or the computed tin content—the latter derived from one of the following: 1) "acid flux" chemical analysis; 2) "HN03 dissolution" chemical analysis; 3) X-ray microprobe analysis of the copper matrix; 4) equivalent tin content, based on the measured increase in electrical resistivity (an increase in resistivity of 1.6 microhm-cm is approximately equivalent to 1 wt pct of sn1,3). It is evident from Fig. 1 that the results of the acid flux analysis are consistent with the nominal composition while the HNO3 dissolution method generally yields lower values, consistent with those obtained from electrical resistivity measurements and somewhat higher than those obtained by microprobe analysis. Microprobe and resistivity values are affected only by the tin in solid solution; hence the HN03 method

Jan 1, 1970

By P. T. Gallagher, W. A. Oates, J. A. Lambert

FAIRLY extensive equilibrium data exists for carbon dissolved in r iron.1-8 However the temperature coefficients of the carbon activity, ac , are insufficierltly preciseto reveal whether the heat of solution of carbon, ?HC , varies with composition. It is doubtful

Jan 1, 1970

By A. P. Coldren, V. Biss

SINCE the r ? a transformation rates of many carbon-free ferrous alloys and low-carbon alloy steels are relatively fast, conventional equipment is not suitable for the dilatometric determination of continuous cooling transformation diagrams. On the other hand, a method based on metallographic analysis of quenched specimens would not be practicable because the various products of shear-dominated transformation are essentially indistinguishable in low-carbon iron-base alloys. Both problems may be avoided by a thermal analysis method employing gas quenching of small specimens austenitized in vacuo. The laboratory equipment employed in the present study consisted of a Tektronix Type 564 Storage Screen Oscilloscope and a Kinney high-vacuum evaporator, modified as shown in Fig. 1, to permit heating a small specimen and cooling it slowly by programmed cooling or rapidly (up to about 8000°F per sec) by a controlled quench with helium gas. The oscilloscope records the electromotive force of a 40-gage (0.003-in.-diam) Chromel-Alumel thermocouple in the specimen during cooling. The temperature at which the cooling curve begins to show the influence of the heat produced by the phase change in the specimen was arbitrarily taken as the transformation-start temperature.*

Jan 1, 1970

By B. C. Wonsiewicz, G. Y. Chin

THE presence of deformation bands in cold-worked metals is known to influence the development of deformation textures1 but has not been considered in any theoretical treatments. At the present time the most rigorous theory of deformation textures appears to be based on Taylor's concept of homogeneous deformation of a crystal within a polycrystalline aggregate.' For each crystal the Taylor theory allows the operation of several equivalent combinations of five or more slip systems. Hence deformation bands can arise from the operation of a separate combination of slips in each of several portions within a crystal. On the other hand, a second type of band may occur as a consequence of slip on systems other than those selected on the basis on homogeneous deformation. This type appears to be associated with crystals of symmetrical orientations, such as the [loo] and [lll.] axial orientations in drawn wires of fcc single crystals studied by Ahlborn.3 In this note we propose a simple mechanism of deformation banding of the second type, and compare the theoretical results for wire drawing of [loo] and [Ill] with Ahlborn's observations. In outlini the model requires that the work to accomplish a given overall shape change by banding be less than or equal to the work to accomplish the same change by homogeneous deformation. While the work by homogeneous deformation, WH = ?T ;dri, can be calculated exactly by the equivalent methods of Taylor2 or of Bishop and Hill,4 the work by banding, WB, is less certain. The latter consists of 1) Wi, work by slip within a band, 2) Wb, work associated with formation of a boundary between bands, and 3) Wc, work to correct the difference in shape change arising from banding and homogeneous deformation. The Wi term can be evaluated explicitly for a band with an assumed set of slip systems, but a satisfactory analysis of Wb and Wc has not been obtained. Since WB = Wi + Wb + Wc WH, for banding to occur, however, a necessary condition is Wi = WH . Hence it seems reasonable to choose a band with the lowest value of Wi among competing bands consistent with Wi = WH, and then minimize Wb and Wc by arranging the physical configuration of the selected band. Wc is minimized by combining neighboring bands such that their net strain matches the macroscopic strain as closely as possible, and Wb is minimized by enforcing strain compatibility across the boundary between two neighboring bands, similar to the case of a grain boundary.5 It is realized that this procedure is not completely satisfactory, but it does seem to explain Ahlborn's observations reasonably well. The procedure is now outlined for the two corner orientations. a) [l00]. Fig. 1 shows a (100) stereographic projection. The results of the Taylor analysis for axi-symmetric flow by homogeneous deformation6 show that, while [loo] itself is unstable, the rotation of the tensile axis will nevertheless be confined to within about 15 deg from [loo]. Alternatively, less work may be expended by banding with slip on a pair of systems with primary-conjugate relationship, e.g., (ll1)[10l.I + (li1.)[110]. The latter represents minimum Wi for all possible bands.* Since there are four symmetrically

Jan 1, 1970

By P. Ramachandraraa, T. R. Anantharaman

THE technique developed by Duwez, Willens and Kle-ment' for rapid solidification of molten alloys in small quantities by ejecting them on to a highly conducting substrate with the aid of a shock wave has come to be known as "liquid quenching" or "splat cooling" in literature and has already been applied to alloys of many binary systems.' The very high cooling rates of the order of l060 to 1080 per sec obtained in this technique and the consequent drastic undercooling of the melt have led to such striking results as formation of new amorphous and crystalline metastable phases and extension of solid-solubility limits in many alloy systems. The cooling rates in these experiments can, however, be neither accurately measured nor effectively controlled and hence the occurrence of either more than one metastable phase or appreciable differences in constitution in splat-cooled alloys of the same composition cannot be ruled out.3 In fact, workers in two laboratories have reported formation of two different cubic metastable phases in liquid-quenched Au-Si alloys containing 17 to 20 at. pct si.4,5 The present note deals with some new and interesting results obtained in a Ag-21 at. pct Ge alloy and a Au-27 at. pct Ge alloy subjected to the liquid-quenching treatment at different cooling rates. Two alloys of nearly the same composition had earlier been rapidly solidified by the standard "gun technique" in the same laboratory and shown to solidify in nonequilibrium structures, viz., an hcp phase (a = 2.987Å;c =4.718Å) in the Ag-Ge system6,7 and both hcp (a = 2.885Å; c = 4.754Å) and tetragonal (a = 11.627A; c = 22.491Å) phases in the Au-Ge system.3 Apart from different substrates (copper and stainless steel), different melt temperatures (50º to 500°C above the liquidus), and different capillary sizes (0.4 to 1.5 mm diam) in the "gun technique", slower cooling rates of the order of l050C per sec were also obtained in the present work by replacing the substrate by water at room temperature in a modification of the technique due to Olsen and Hultgren.8 No attempt was made to measure the cooling rate in any experiment. The products varied from fine powder (>40 pct by wt—200 mesh) obtained by quenching in water to thin flakes and foils (11.0 sq mm to 4.0 sq cm) produced by splat cooling. They were subjected to the Debye-Scherrer method of X-ray examination in each case. In case of the Ag-Ge alloy, in addition to the expected metastable hcp phase,6 a coexistent tetragonal phase (a = 5.093,Å; c = 7.009Å) was detected in some experiments. Eight weak X-ray reflections from this phase could be identified, two of them being the same as reported earlier.7 With increase in the cooling rate, the dominant hcp phase seems to be first accompanied by traces of silver or germanium and then either homogeneous or mixed with traces of this new tetragonal phase. The splat-cooled Au-Ge alloy showed generally the expected hcp and tetragonal phases,3 but sometimes traces of germanium were also present. Further, two new tetragonal phases with the following lattice param ters could be clearly identified in samples quenched

Jan 1, 1970

By P. Ramachandrarao, T. R. Anantharaman

CONSIDERABLE interest has lately been evinced as regards the nature of chill zones in solidified metals and alloys. Biloni and Chalmersl were the first to show through their study of segregation substructures in some nonferrous alloys that the formation of the dendritic region may be preceded by a diffusionless solidification process, viz., predendritic solidification. Subsequently Bower and Flemings2 tried a special solidification technique wherein the liquid was drawn into a narrow copper mold with polished surfaces and concluded that convection might trigger some multiplication mechanism leading to grain refinement. Using uncoated and partially coated surfaces for molds in the Bower-Flemings technique as well as in conventional molds, Biloni and Morando3 have very recently brought out the importance of the rate of heat extraction on the mechanism of solidification. We report here on the surface structures and substructures observed in a Sn-1 wt pct Pb alloy solidified at even higher cooling rates (riz., l05 to l07 ºc per sec) than those employed by earlier workers. The alloy was made by melting tin (99.99+ pct) and lead (99.9+ pct) in a silica tube under vacuum. Small quantities of the homogenized alloy (0.5 to 1.0 g) were then quenched (or splat-cooled) from the melt by the "gun technique" developed by Duwez et al.4 The thickness of the resultant foils varied from specimen to

Jan 1, 1970

By S. A. Levy, J. D. Wood, J. F. Libsch

A study of the preparation and characteristics of a sevies of Fe-C-N alloys has been conducted. X-ray, microhardness, and metallographic data from a series of single-phase alloys produced by controlled nitriding of carburized foils are reported. The existence of a, y', and E carbonitride has been confirmed and it has been found that y' is the hardest of these three phases. These results have been used to interpret the structures observed in nitrided steels. ThIS paper represents the second phase of a three-part study concerning combined nitriding and induction hardening. The first part' reports the engineering properties (depth hardness, fatigue, corrosion, and tempering resistance) obtained when seven different steels were subjected to the combined surface hardening treatment. The present paper concerns the nature of a series of single-phase alloys prepared by controlled nitriding of carburized foils. The objective was to simulate the various layers present in the as-nitrided steels. A third paper will report data concerning induction hardening of the foils and will attempt to set forth a mechanism for the high hardness obtained with the combined treatment. Studies of nitriding generally fall into three categories. The first were performed with bars using conventional nitriding procedures, thus yielding a nitrogen gradient and a series of phase layers near the surface.2-6 Such studies were complicated by the presence of the nitrogen gradient, for it was difficult to correlate microhardness and X-ray data with chemical composition. There were always complications due to penetration of the X-ray beam which yielded data influenced by underlying layers. Similar difficulty was experienced in taking hardness readings on a tapered specimen or in isolating various layers by machining. A second group of investigations was primarily concerned with establishment of regions in the Fe-N7,9,10 or the Fe-C-N phase diagram.8 These were performed with powder specimens which were nitrided in am-monia-hydrogen mixtures to produce a series of single-phase specimens. Unfortunately, the powder specimens were not amenable to either microstruc-ture or microhardness study. The third was essentially a compromise of the first two. Bose and Hawkes," using 0.005-in.-thick iron foils, were able to obtain microhardness, microstruc-ture, composition, and X-ray data on Fe-N alloys of eutectoid composition by equilibration in ammonia-hydrogen mixtures at 1290°F. To obtain a better understanding of the nitriding process and the characteristics of the phases in ni-trided plain carbon steels, the present investigation was undertaken. The investigation was patterned after that of Bose and Hawkes with the exception that nitriding was performed at 930°F (below the eutectoid temperature), as in the case of conventional nitriding. In addition to gaining some understanding of the source of high hardness of nitrided and induction-hardened steels, found in a previous study,' this investigation was concerned with the possibility of controlling the phases present in a nitrided case through the use of ammonia-hydrogen mixtures. Knowledge of the properties of each phase and the conditions necessary for its production could make it possible to avoid undesirable surface layers in nitriding. EXPERIMENTAL PROCEDURE Specimen Preparation. A specimen thickness of 0.005 in. was selected to insure that a uniform nitrogen concentration could be obtained in a reasonable length of time by equilibration in an ammonia-hydro-gen atmosphere. The starting material was a vacuum-cast ingot of pure iron, the major impurities of which were: C, 0.003 pct; 0, 0.014 pct; S, 0.004 pct; N, 0.003 pct.* 'Compositions are quoted as weight percent except as noted. The ingot was heated to 1500°F in a nitrogen atmosphere and forged to a slab 0.25 in. thick. The material was then reduced to 0.005 in. by alternately cold rolling and annealing in a nitrogen atmosphere at 1600°F. This material was divided into five groups of specimens which, after carburizing, yielded the following carbon contents: 0.003, 0.28, 0.36, 0.46, and 0.74 pct C. The carburizing was performed by the Leeds and Northrup Research Laboratories, using a controlled "carburizing potential" which yielded a uniform carbon concentration throughout the cross section.

Jan 1, 1970

By M. Murakami, Y. Murakami, O. Kawano

The formation and growth of Guinier-Preston zones in Al-Zn alloys containing 4.4, 6.8, 9.7, and 12.4 at. pct zn have been studied by the X-ray small-angle scattering method. Particular attention was paid to the effects of small amounts of third elements silver, silicon, and magnesium on the formation and growth of G.P. zones. It was noticed that an appreciable number of G.P. zones were formed during the course of rapid cooling and that the size, volume fraction, and number of these G.P. zones were influenced by the existence of the third elements. During subsequent aging it was also found that the addition of both silver and silicon lowered the temperature for the growth of G.P. zones, whereas the addition of magnesium raised it. These results were explained in terms of the mutual interactions among zinc atoms, vacancies, and the third elements. A number of studies on the formation and growth of Guinier-Preston zones in Al-Zn alloys have been reported.1-4 Panseri and Federighii have found that the initial stages of zone growth take place at temperatures as low as around -100°C. For investigation of the mechanism of the initial stages of zone growth, growth studies must be carried out at low temperatures. In order to investigate the possibility of the formation of G.P. zones by the nucleation mechanism or the spinodal decomposition during quenching which was reported by Rundman and Hilliard,5 the examination of the as-quenched structure must be performed. In this paper the investigation of the early stages of the formation and growth were determined by means of the X-ray small-angle scattering method. With this technique, change of X-ray scattering intensities was measured while quenched specimens were heated slowly from liquid-nitrogen temperature to room temperature. At as-quenched state and after heated to room temperature, investigation of zone size, volume fraction, and zone number per unit volume was carried out. Measurements on these specimens yielded information on the early stages of zone formation and growth. Measurements were made also on specimens quenched to and aged at room temperature. From these measurements the previously reported model6 for the later stages of growth is confirmed; namely, the larger zones grow at the expense of smaller ones. Three elements, silver, silicon, and magnesium, were chosen as the third elements for the following reasons: Silver. In the binary A1-Ag alloy the spherical disordered 77' zones were observed immediately after quenching.7 Therefore, in the Al-Zn-Ag alloys, it is suggested that silver atoms might induce cluster formation during quenching. Also, since the migration energy of the zinc atoms was found to be raised by the addition of silver atoms,' silver atoms may have a great effect of the zinc diffusion, especially during low-temperature agings. Silicon. The effects of the addition of silicon atoms were found to be marked, especially at low-tempera-ture aging. In the binary Zn-Si system, no mutual solid solubilities between silicon and zinc9 and no in-termetallic compounds10 are reported to exist. Shashkov and Buynov11 investigated the behavior of silicon atoms in Al-Zn alloys and showed that silicon was not in the G.P. zones. The interaction between silicon atoms and vacancies is strong enough to increase the quenched-in vacancy concentration.* Magnesium. Magnesium atoms are reported to trap quenched-in vacancies and after much longer aging times these trapped vacancies will become free and act as diffusion carriers.13 Therefore at intermediate aging times, the diffusion of zinc atoms in Al-Zn-Mg alloys will be slower than in the binary Al-Zn alloys, whereas at longer times zinc diffusion will become faster. EXPERIMENTAL PROCEDURE The alloys used in this investigation had compositions of 4.4, 6.8, 9.7, and 12.4 at. pct Zn with or without 0.1 and 0.5 at. pct Ag, Si, or Mg. The alloys were prepared from high-purity aluminum, zinc, silver, silicon, and magnesium, with each metal having a purity better than 99.99 pct. The analyzed composition of the specimens is given in Table I. The measurements of the X-ray small-angle scattering were carried out with foils of 0.20 mm thick. The change of the scattering intensity was always measured at the fixed scattering angle of 20 = 2/3 deg. This angle exists nearly on the position of the intensity maximum. The value of the interparticle interference function14 which has large effect in this range of angles may not change abruptly in the case of the spherical shape of small zones. Therefore, from the above considerations, it is concluded that an increase of the intensity measured at this constant angle corresponds to an increase of the average radius and volume fraction of G.P. zones. The specimens were homogenized at 500°, 450°, and 300°C for 1 hr in an air furnace. For the study of the formation and growth at low temperatures, the foil

Jan 1, 1970

By D. E. Mikkola, G. E. Poquette

X-ray diffraction was used to study the growth of antiphase domains in quenched (or "disordered&apos;? Cu3Au annealed in the range 300" to 385°C. Measurements of the long-range order parameter indicate that a high degree of order is established rapidly at these annealing temperatures. Average domain sizes obtained by Fourier analysis of the superlattice peak profiles show that antiphase domain growth is analogous to classical metallurgical grain growth (i.e.,fol-lows a D2 US kt relation). The activation energy for the growth process, 44 kcal per mole, indicates diffusion control. The anisotropy in the observed effective domain sizes from seven different superlattice peaks can be best accounted for by a configuration involving antiphase domain boundaries on {100 } and (111 ) planes, where the (100) boundary is the low-energy type, {lOO} Type I. The disappearance of the (111) antiphase domain boundary during domain growth is dif-fusion-controlled with an activation energy of 48.5 kcal per mole. On the other hand, the behavior of the parameter representing the amount of (100) Type I boundary indicates that there may be a conversion of the higher-energy boundary types to (100) Type I boundary during the growth process. THE order-disorder transformation in the alloy Cu3Au has been the subject of numerous experimental investigations over the past 40 years, most of which have involved measurements of convenient physical properties such as resistivity and hardness as a function of heat treatment. The interpretation of these data is difficult because measurements of this type have the disadvantage that they yield total changes resulting from several different atomic processes which may be occurring simultaneously. The present study was undertaken to establish by means of X-ray diffraction the kinetic behavior of one of these atomic processes, namely antiphase domain growth. In the completely ordered state Cu3Au has an L12 structure which can be described as an fcc type arrangement of atoms in which the gold atoms occupy the corner sites and copper atoms the face-centered sites. Three other equivalent unit cells can be formed by allowing two gold atoms to occupy opposite face-centered sites and copper atoms to occupy the remaining corner and face-centered sites. These four different unit cells are crystallographically related by a shift of 1/2<110>. Quenching from above the critical temperature (392°C) to room temperature retains the "disordered" structure-a "random" arrangement of copper and gold atoms having the fcc structure. Annealing the disordered alloy below the critical temperature causes ordering to occur through the nucleation and growth of ordered regions at different points throughout the crystal. These small ordered regions, each based on one of the four types of unit cell, grow by consuming the disordered material until they impinge to form a domain structure in which the domains are antiphase by a shift of 4(110). The boundaries between domains are called antiphase domain boundaries (APDB) and they have been found to lie primarily on &apos; {100} planes in highly ordered Cu3Au. Two types of APDB can occur on ( 100) planes. An example of an (001)1/2[110] shear type APDB is shown in Fig. I. Because of the layer of copper atoms separating the domains in this case, there are no near-neighbor violations across the boundary and it has a low surface ener This type of APDB will be referred to as {lOO} Type I. Fig. 2 shows an (001): [011] climb type APDB, (100) Type 11. This type of APDB can be described as resulting from removal of a (200) plane followed by a shift of 1/2<110> to bring the separated regions together. Near-neighbor violations across (100) Type I1 APDB make it a high-energy boundary. There are numerous other possible APDB configurations; however, it is only worth noting that shear type APDB can be produced on the (111) plane by motion of a normal fcc dislocation with Burgers vector 1/2<110> through the ordered structure. A (111); [110] shear type APDB is shown in Fig. 3. Again, because of the near-neighbor violations this type of APDB has a higher energy than the (100) Type I APDB.

Jan 1, 1970

By Å. Sterten, R. Tunold, J. Brun, K. Dalatun

The subjects of this study are two corrosion phenomena familiar to operators of aluminum plants employing Soderberg anodes of the vertical type, namely the sul-fide scale formation observed at the steel contact spikes and the corrosion wear observed at the lower edge of the gas collecting skirts. The causes of these corrosion phenomena are discussed on the basis of observations from practice and measurements on commercial cells as well as on laboratory experiments. It is concluded that the anode spike corrosion is mainly due to the attack by sulfur compounds contained in the anodically evolved gases and that this attack is greatly promoted by cracks and pores in the anode carbon embedding the lower spike ends. The corrosion of the gas collecting skirt is mainly attributed to anodic dissolution of the iron during occasional contacts with the melt. ANODE SPIKE CORROSION The visible result of this corrosion is the formation of a brittle loosely adherent scale on the lower ends of the mild steel spikes maintaining the electric contact to the carbon anode, Fig. 1. The thickness of the scale usually varies from 0.5 to 3 mm, but in some cases scale of about 10 mm thickness has been observed by the writers. During the spike pulling, usually repeated every 3 weeks, part of the scale often loosens and remains in the anode carbon, resulting in contamination of the aluminum with iron. This corrosion has been attributed to reaction of the iron with gaseous sulfur compounds originating from the anode paste materials.&apos;-4 This paste usually consists of 70 pct precalcined petroleum coke with 1.2 to 1.4 pct S and 30 pct coal tar pitch containing 0.5 to 0.7 pct S. During operation the gasification of the anode materials takes place in two ways: First, gases are evolved by the gradual baking of the anode paste added on top of the anode. Due to the sealing effected by the upper semifluid zone of the paste, these gases, containing sulfur compounds from the pitch, are forced downward through pores and cracks in the rigid anode carbon. At the temperatures of the zone of the lower ends of the spikes, 700" to 900°C, the original components of the baking gas must undergo decomposition, similar to that taking place with the production of coal gas, resulting in a gas mixture consisting mainly of H2 and CH4 with small percentages of H2S as the main sulfur compound.5 Second, the anodic reaction results in a mixture of C02 and CO, the total quantity of which is about 15 times that of the baking gas. These anode gases must carry the entire sulfur content of the carbon gasified by the anodic reaction. Henry and Holliday6 have shown that COS is the main sulfurous component of the anode gases from Soderberg cells. Soderberg anodes usually exhibit a network of vertical cracks, frequently traversing from one spike to the next one and to the outside of the block and widening downward to the working face of the anode. In addition the anode carbon, particularly that below the spike ends, is rather porous, as indicated in Fig. 1. It therefore seems probable that the anode gases also may partly penetrate to the spike ends. As the anode is partly immersed in the melt, the static pressure of this must forward this penetration. I) SPIKE SCALE COMPOSITION A great number of freshly extracted spikes from industrial plants were inspected and samples of the scale collected for examination. Before analyzing the samples a thin iron oxide layer, formed by air oxidation of the outside of the red hot scale immediately after spike pulling, was removed. On the average the Fe/S ratio found by these analyses corresponded to I the composition FeSl. oo7. X-ray powder patterns showed no oxide and otherwise agreed with those found by Haraldsen7 for iron sulfide with 50.00 at. Pct

Jan 1, 1970

By W. G. Davenport, M. Paneni

Experiments in sheets of mercury and water have confirmed that the dynamics of bubble rise are simi-lur in Liquid metal and aqueous systems. RECOGNITION that bubble/metal interactions are important in pyrometallurgical refining processes (e.g., steelmaking, vacuum degassing, deoxidation of copper) has led to a number of investigations into the dynamic behavior of bubbles rising in liquid metals. Terminal velocities of bubbles rising in mercury (20°C)&apos; and silver (1000" to 1050"c)1,2 have been measured. Good agreement between aqueous and liquid metal systems has been obtained. Shapes of air bubbles rising in mercury have been determined experimentally by Davenport, Bradshaw, and Richardsonl who used a system of electric probes to measure maximum horizontal and vertical dimensions, Fig. 5. In the present work the motion and shape of nitrogen bubbles rising in a thin sheet of mercury (i.e., a "two-dimensional" environment) have been studied with the view of confirming dynamic similarity between aqueous and metallic systems. The use of thin sheets of liquid permitted direct visual and photographic comparisons of bubble behavior in clear liquids and in mercury. EXPERIMENTAL METHOD The thin sheets of mercury or water were held in a clear acrylic plastic container, Fig. 1. The sheets of liquid were 80 cm high by 30 cm wide and 0.47 cm thick. Single bubbles were formed by injecting the desired volume of nitrogen into an inverted semicircular cup (stainless steel). The cup was then rotated into the upright position using an external handle thus releasing a single bubble of measured volume. Nitrogen was injected into the cup from a nitrogen cylinder through the external handle and a hollow rotating axle. The volume of a bubble (volume range 0.01 to 10 cu cm) at any instant was obtained by connecting a soap film meter to a small gas space above the liquid. By this technique any change in the volume of a gas bubble in the liquid (i.e., during cup filling or during rise) produces an equivalent displacement from gas space A into the buret B. This displacement is determined by measuring the movement of a horizontal soap film in the buret. Bubble shapes were determined using single-frame photography. Rising velocities were determined by cinephotography with a 1/100-sec stopwatch in the field of view. In both cases dimensions were referenced to a rule attached to the container surface, also in the field of view. Linear dimensions were measured on projections of the single-frame negatives. Rising velocities were calculated from measured heights of rise (10 to 20 cm) and times of rise. The effects of disturbances caused by cup rotation and by bubble release were minimized by photographing bubbles at a point not less than 25 cm above the cup. MATERIALS Mercury: Technical-grade purified: minimum 99 pct Hg; Johnson Matthey and Mallory Limited, Toronto. Nitrogen: Technical-grade purified nitrogen: 99.99 pct Nz, 0.01 pct 02, trace argon; Air Liquide Canada Limitee, Montreal.

Jan 1, 1970

By R. K. Iyengar, G. C. Duderstadt

An investigation was carried out to determine the effect of Ca-Si additions on the dissolved oxygen content of liquid steel. An apparent equilibrium was reached after holding the melt for some time when the total oxygen content of the melt was identical with the dissolved oxygen. Results of the investigation show that for deoxidation with silicon and manganese the apparent equilibrium is reached after 8 to 12 min and the oxygen content of the melt is in good agreement with values reported in the literature for similar steel compositions. Ca-Si additions decrease the dissolved oxygen content appreciably below that obtained with Si-Mn deoxidation. It is postulated that some calcium dissolved in liquid steel at the time of its vaporization combines with dissolved oxygen to form CaO which then fluxes the manganese silicate, thereby lowering the activity of the deoxidation products. Slow flotation of calcium silicate inclusions is attributed to their slower growth rate. An addition of aluminum (to yield <0.005 pct Alsol) prior to introduction of Ca-Si improves the kinetics of removal of resulting deoxidation products. WITH the introduction of continuous casting of billets and blooms, application of calcium-containing alloys for deoxidation purposes has gained new interest. More so than in conventional ingot casting, the degree of control of the dissolved and total oxygen contents in steel for continuous casting can determine the success or failure of the operation because these affect both surface (pinholes) and internal quality of the billets. Of the available deoxidizers, only silicon has so far found wide application. However, in the typical range of application (0.20/0.30 pct Si), it is too weak a deoxidizer to suppress pinhole frequency to the level desirable for all but the least demanding appli-cations (approximately 10/50 pinholes per sq ft, de-pending on degree of subsequent reduction). On the other hand, Vincent&apos; has shown that it requires ap-proximately 0.007/0.008 pct A1 soluble in the steel to suppress pinhole formation to <10 pinholes per sq ft. In view of the difficulty of consistently maintaining this aluminum level and the associated problem of tundish nozzle constriction2 when aluminum is added to the ladle, steelmakers have searched for other de-oxidation alloys to circumvent the problem. Calcium-containing alloys offer such a possibility. When employed as a partial substitute for silicon, CaSi (30 pct Ca/60 pct Si) additions are reported to yield adequate pinhole contro1.3 Its use simultaneously preserves the "fluidity" of the steel and ensures good castability.4 Oxygen contents as low as 0.007 to 0.014 pct have been obtained with CaSi additions varying between 3 to 8 lb per ton.5-7 Due to the high degree of vaporization of calcium at the temperature of molten steel and the different methods used to introduce it into the liquid, the reported results show considerable scatter and lack of consistency. According to several investiga- deoxidation tors, the flotation characteristics of CaSi products are not as favorable as those found for alumi-num but are similar to those established for silicates with low alumina content.678 Thus, cleanliness ratings were improved when CaSi was replaced by a com-bination of Si + A1 followed by CaMnSi additions.5,9 In view of the lack of a comprehensive description of the deoxidation potential of CaSi alloys, a study was undertaken of the effect of CaSi additions on oxygen content in comparison to Si + Mn and Si + Mn + Al. The alloy chosen for this study contained 63 pct Si, 32 pct Ca, <3 pct Al, and 2.5 pct Fe. EXPERIMENTAL PROCEDURE The experiments were divided in three groups as shown in Table I. In each group, the CaSi addition was increased successively while maintaining the melt composition constant. The experiments in the third group were designed to determine the effect of prede-oxidation with small amounts of aluminum. Ingot iron, containing 0.02 to 0.03 pct C and 0.03 to 0.05 pct Mn, was melted in a 100-lb magnesia crucible. Pig iron was added to the melt under air in an induction furnace to attain the desired carbon content of 0.05 to 0.15 pct and thereby control the initial oxygen content of the melt between 0.04 and 0.015 pct. After removal of the slag, the furnace was sealed and argon was introduced through an opening in the graphite cover, Fig. 1. When the desired temperature was reached, electrolytic manganese was added to the melt and pin samples were taken (7 mm silica tubing) to establish initial oxygen content. To obtain maximum efficiency, CaSi and metallic silicon were introduced in a sealed steel pipe into the bath. This procedure assured minimum loss of calcium through vaporization as the deoxidants were always released at the bottom of the melt. Samples were taken at regular intervals and quenched in water. Temperature of the bath was measured with a Pt/Pt-10 pct Rh thermocouple. Portions of the pin sample were used for oxygen analysis; five determinations per sample were made to obtain average oxygen content. Oxygen analyses were made by the inert carrier gas fusion method with frequent cross checks with the vacuum fusion method.

Jan 1, 1970

By Pervez Patel, Martin G. Frohberg, Demetrios Papamantellos

Model experiments were carried out on the mass transfer of iodine between n-hexane and a 4 2 X 10-3 M aqueous sodium hydroxide solution. The influence of mechanical stirring by means of small gas bubbles (ca. 0.01 ml in volume) on mass transfer was examined in independent experiments. The results were described with the help of the penetration theory and in the case of bubble stirring with the help of a mathematical model based on this theory. S LAG-METAL reactions, especially those in steel-making processes, often occur under conditions where gas is evolved in the form of bubbles that break through the slag-metal interface. It is known that stirring by means of bubbles increases the mass transfer coefficient, but there has been very little quantitative work done in this field. Because of the difficulties that attach to experimental work at high temperatures this study was confined to model experiments at room temperature. EXPERIMENTAL APPARATUS The transport of iodine from an n-hexane layer into a weak sodium hydroxide solution was studied a) with stirring by means of bubbles and b) with mechanical stirring. The apparatus for the experiments with bubbles consisted of the cell, two Dreschel bottles filled with hexane in order to saturate the nitrogen flow, one flow meter, and a nitrogen gas cylinder fitted with a fine-regulating valve. Fig. 1 shows the cell consisting of a glass cylinder 33 cm in height with an overall diameter of 7.5 cm embedded in a copper flange. The flange is connected to a Plexiglas plate and to the gas inlet. The Plexiglas plate has holes of 0.2 mm diam bored into it which are spaced 1 cm from each other. For the experiments with mechanical stirring the bottom of the cell was sealed off by a Plexiglas plate. The upper layer was stirred by means of a glass stir-rer and the bottom layer with the help of a magnetic stirrer in a counter rotatory direction. Both stirrer speeds could be varied continuously. EXPERIMENTAL PROCEDURE Iodine dissolves in n-hexane producing a stable violet color thus enabling the iodine concentration in

Jan 1, 1970

By R. R. Vandervoort, W. L. Barmore

Tensile creep experiments were conducted on high-purity, poly cvystalline rhenium from 1500" to 2300°C at stresses from 1500 to I0,OOO psi in a vacuum of 10-a torr. The apparent activation energy for creep was 60 kcal per mole, and the steady-state creep rate varied directly with stress to the 3.4 power. Dislocation substructure that developed during creep was studied by transmission electron microscopy. Possible rate-controlling deformation mechanisms are discussed. The creep behavior of most metals at elevated temperature can be represented by the following equation:&apos;&apos;&apos; t = Cf(s)(^)(s/E)nD [1] where i = steady-state creep rate, C = constant, f(s) = a function involving microstructure, s = applied stress, E = the average elastic modulus at test temperature, n = constant, D = diffusion coefficient According to this well-established relationship, metals with higher elastic moduli and lower diffusion coefficients should have greater creep resistance at the same stress and temperature and equivalent mi-crostructures. While no diffusion data are available, the diffusivity of rhenium should be less than that for most other refractory metals because of its high melting point and hcp crystal structure. The Sherby-Simnad relation for calculating atomic mobility in metallic systems3 predicts that the diffusion coefficient for rhenium is less than that experimentally determined for tungsten4 in the temperature region 1500. to 2200°C. At these temperatures the elastic modulus for tungsten5 is only slightly larger than the extrapolated modulus for rhenium.6 Thus, rhenium is a good possibility for a a high-temperature structural material, but few data on the creep of rhenium have been reported. This investigation was undertaken to study the high-tempera-ture deformation behavior of rhenium in detail. EXPERIMENTAL TECHNIQUES The material used in this study was consolidated from high-purity powder. After cold pressing the powder to a plate a in. thick, the billet was sintered in hydrogen at 2250°C for 24 hr. The plate was reduced to 0.100 in. by cold cross rolling with intermediate anneals at 1650°C for 20 min between passes. The plate was further reduced to 0.060 in. by unidirectional cold rolling with similar heat treatments between passes, and then finally stress-relieved in hydrogen at 1650°C for 30 min. Specimens tested at 1900°C and below were pretest-annealed at 1900°C for 2 50 hr. Specimens tested above 1900°C were pretest-annealed at 2400°C for 5 hr. The impurity content in the "as-received" plate was quite low, table I. Essentially no change in impurity levels was detected in specimens after creep testing. All creep tests and annealing treatments were conducted in a vacuum of 10-8 torr in a test furnace heated by a tungsten mesh element. The load was applied to the specimens through a bellows, and stresses were maintained to ±1 pct of the selected value by periodic corrections for changes in specimen cross-sectional area during creep and for changes in the bellows spring force due to load column extension. One-inch-diameter tungsten force rods were used in the hot zone of the furnace. Deformation at temperature was measured by optically tracking gage marks on the specimen. Temperature was measured by a calibrated optical pyrometer and was determined to ±5"C. Grain sizes were determined by the linear intercept method and specimens were examined in the "as-polished" condition, using polarized light. Specimens annealed at 1900°C had a grain size of 52 ± 5µ , and those annealed at 2400°C had a grain size of 148 * 11 µ. Pieces were cut from the gage section of creep-tested specimens and planed to a thickness of about 0.010 in. by spark discharge machining. Thin foils for viewing by transmission electron microscopy were obtained by electropolishing in a solution of 6:3:1 ethyl alcohol, perchloric acid, and butoxy ethanol, respectively, using the window technique. Bath temperature was —4OoC, and the cell potential was 35 v. The foils were examined in Siemens Elmiskop I, operating at 100 kv. RESULTS AND DISCUSSION In order to analyze the results from creep experiments, Eq. [I] is rewritten in the following form: <=Kf(s)ne-/RT [2] where K = constant, ?// = apparent activation energy for creep,

Jan 1, 1970

By R. D. Pehlke, J. V. Gluck

The limiting activity coefficient of zinc in a "binary " solvent has been described for several dilute ternary solutions by combining literature data from recent interaction studies in the terminal regions with thermodynamic data for the central regions. Results are discussed in terms of the Alcock and Richardson random solution model. The observed behavior agrees semiquantitatively with predictions using the model. RECENT efforts in the thermodynamics of dilute ternary liquid metallic solutions have been mainly concerned with the interactions between two dilute solutes, that is, the terminal region at an apex of the composition diagram.&apos;-&apos; A more general case is that of the behavior of a dilute solute over the full range of a ternary system, or, more specifically, the limiting activity of solute i as projected to the k-j binary side of the i-j-k composition triangle. An implication of this is that the interaction between i and j at the k apex should connect in some way to the interaction between i and k at the j apex. A model to characterize various types of expected behavior has been discussed by Alcock and Richardson.9,10 Such behavior can range from a simple linear relation for In yi over the 1-k binary to more complex curved relations which depend on various assumptions regarding the heat of solution in the j-k binary system and the presence or absence of clustering with solute i. Quantitative data to assess these concepts have been limited primarily to the cases of nonmetallic interstitial solutes in ferrous solutions. Alcock, Richardson, and various coworkers9-13 have discussed the behavior of oxygen, sulfur, silicon, or hydrogen in dilute solution over the range of iron + metal systems; however, the only data considered by them for substitutional nonferrous metallic solutions were the results of Elliott and Chipman concerning the activity of cadmium in the Pb + Sn, Pb + Bi, and Pb + Sb systems.9 These data were limited and did not cover the terminal regions in detail. An opportunity to extend the Alcock and Richardson considerations to the dilute solution of zinc in various "binary" solvents has been afforded by combining results of several of the recent investigations of ter-minal-region interactions with previous data from the literature for the same more concentrated solutions. RESULTS AND DISCUSSION The results of the analysis are shown in Figs. 1 to 5 where the log activity coefficient, (In yZn)xzn--o, is plotted vs the composition of the "binary" solvent. In these plots the end points are the values for In yzn in the appropriate binary solution with Bi, Pb, Sn, Cd, or In at the indicated temperature—usually 550°C (823°K). For the terminal regions the slopes were drawn using the first-order interaction parameters taken from various studies reported in the literature. The data points shown in the central regions were obtained by the short extrapolation to infinite dilution of the logarithm of the activity coefficient calculated from thermodynamic studies reported in the literature for the same systems. The sources of the data are indicated on each figure. Second-order effects were not considered. Reasonably smooth curves can be drawn to connect the central region with the terminal regions for the Zn-Pb + Bi system, Fig. 1, the Zn-Pb + Zn system, Fig. 1, and the Zn-Bi + Cd and Zn-Bi + Sn systems, Fig. 2. As shown in Fig. 2, where central region data are available from two independent investigations, the agreement is quite good. The Zn-Pb + Cd system does not appear to be as well behaved as the previous four, Fig. 3; however, this type of behavior has also been

Jan 1, 1970

By C. R. Whitney, G. N. Maniar, D. R. Muzyka

Previous results have shown that Pyromet 860, an Fe-Ni-base heat-resistant alloy, is stable at temperatures as high as 1500°F for aging times as long as 100 hr. This Paper describes the results of long-time creep-rupture testing at 1050" to 1400°F at various stress levels. Times as long as 37,660 hr were employed. The effects of time, temperature, and stress on the precipitates and their morphologies were studied by optical and electron microscopy, X-ray and electron diffraction, and microprobe techniques. phase, containing cobalt, nickel, and molybdenum, was detected after extended exposures from 1200" to 1400°F and careful study was performed to describe the kinetics of its formation in this alloy. µ phase formation apparently has little effect on the elevated-tem-perature properties of Pyromet 860. For times as long as 500 hr at 1300°F and below, with µ phase present, m significant effects on ambient temperature properties were noted. For longer times at 1300°F and after 1400°F exposure, the effects of u phase on ambient temperature tensile strength properties are not clear due to y&apos; effects and grain boundary reactions. Electron-vacancy, N,, numbers were calculated using different methods described in literature and correlated with the present findings. In the selection of alloys for use in gas turbine applications, structural stability ranks as a primary criterion. High-temperature strength and cost are also of major concern. With these factors in mind, Pyromet 860 alloy, an Fe-Ni-base superalloy was designed. This alloy combines the cost advantages of Fe-Ni-base alloys such as A-286, 901, and V-57 with improved strength and structural stability&apos;1,2 and no tendency to form the embrittling cellular 77 phase. A previous study3 reported on the stability of Pyro-met 860 at temperatures from 1375" to 157 5°F and times up to 100 hr. That study showed that the y&apos; precipitates increased in size and separation and decreased in number with an increase in time or aging temperature. No deleterious phases were found to occur. In the present work, samples from four production heats were subjected to long-time creep-rupture testing at 1050" to 1400°F at various stress levels. Various heat treatments were used on the starting samples and tests were run up to 37,660 hr. The effects of time, temperature, and stress on the precipitates and their morphologies were studied by optical and electron microscopy, X-ray and electron diffrac- tion, and microprobe techniques. Electron vacancy numbers, Nv , calculations were made by TRW.4 Experimental results are correlated with the Nv data used to predict occurrence of intermetallic phases such as a phase. EXPERIMENTAL PROCEDURE Mechanical Tests. Material for the present study came from four production size heats of Pyromet 860 alloy, weighing from about 3000 to about 10,000 lb. All of these heats were made by vacuum induction melting plus consumable electrode vacuum remelting. The nominal analysis for this alloy is compared with the actual analysis of the four heats in Table I. Sections of these heats were forged to 9/16-in. round bar,3/4-in. square bar, 3-in. round bar, 4-in. square bar, and a gas turbine blade forging about 16 in, long, about 6 in. wide, and weighing about 20 lb. In general, all forging of this alloy is done from a 2050°F furnace temperature. Longitudinal test blanks were cut from the centers of the smaller bars, from mid-radius positions for the 3- and 4-in. bars, and from the air foil of the gas turbine blade and heat-treated according to the procedures outlined in Table 11. Heat treatment A is the "standard treatment" recommended for this alloy for best all-around strength and ductility. Heat treatment B is a modification of treatment A for improved tensile strength at moderate temperatures. The treatment coded C was designed for treating large sections according to a procedure previously described.&apos; Heat treatment D was developed to yield optimum stress relaxation characteristics at 1050°F for a steam turbine bolting application. After heat treatment, the test blanks were machined either to plain bar creep specimens with a gage diameter of 0.252 in., to combination smooth-notched stress-rupture bars with a plain bar diameter of 0.178 in. and a concentration factor of Kt 3.8&apos; at the notched section, or to notch-only specimens. All specimens conformed to ASTM requirements. Metallography. Most of the creep-rupture tests were continued to failure. A few bars were fractured as smooth or notch tensiles after creep-rupture exposures. After fracturing, ordinary metallographic sections were made primarily in gage areas adjacent to fractures to represent a "high-stress" region and through specimen threads to represent a "low-stress" region. All metallographic sections were made in a longitudinal direction with respect to the test specimen axes. For optical microscopy, the samples were etched in glyceregia (15 ml HC1, 5 ml HNO,, 10 ml glycerol). For XRD analysis, the phases were extracted electrolytically in two media: 20 pct &Po4 in H20 for selective extraction of y&apos; and 10 pct HC1 in methanol for carbides and other phases.

Jan 1, 1970

By P. N. Richards, M. K. Ormay

Commercially hot-rolled low-carbon steel strip may have one of two basic types of orientation texture, depending upon the amount of a iron which was present during the finishing passes. The changes in these textures with varying amounts of cold reduction up to 95 pct have been determined for the sheet surface plane and for parallel planes down to the mid-plane. The development of cold reduction textures has been reassessed on the basis of (200), (222). and (110) stereographic pole figures and pole density or inverse pole figure values. In agreement with the literature, it is shown that the textures can be described in terms of partial fiber textures but alternative descriptions are given for one of the fiber textures, in order to more closely correlate with experimental data. One partial fiber texture consists of orientations of the type (hkk)[011] extending from (100)[011] to {322}(011) in agreement with the literature. At moderate amounts of cold reduction, a second partial fiber texture forms with a <331> fiber axis inclined 20 deg to the sheet normal and a range of orientations centered on one close to (1 11)[112] and reaching to (232)[101] or (322)[011]. An alternative description involves a (111) fiber axis parallel to the sheet normal but capable of rotation about the rolling direction with rotation about the fiber axis. ORIENTATIONS developed in low-carbon steel strip after cold reduction are of commercial importance because they control, in part, the final preferred orientations after subsequent annealing. The method of control however is not understood completely. Some preliminary work indicated that the cold-reduced orientations and the subsequent annealing textures of commercial low-carbon steel were dependent on the orientations present in the material before cold reduction, that is, those present in the hot-rolled strip but, to date, the effects of initial orientations have not been extensively investigated. For this reason, much of the information given in the literature on development of preferred orientation is difficult to assess as details of initial texture and processing conditions are often inadequate or are altered by a subsequent heat treatment such as normalizing.&apos; It is known2 that anomalous results for near surface orientations may be obtained if lubrication during cold rolling is not adequate but whether lubricant was used during the experiments has not always been given, nor has the exact depth below the surface at which determinations have been made. A comprehensive review of cold rolling textures has been made recently by Dillamore and Roberts&apos; and more restricted recent reviews are due to stickels4 and Abe.5 Based largely on the experimental work of Bennewitz,1 reviewers have accepted that the preferred orientations produced on cold reducing low-carbon steel can be described in terms of two partial fiber textures as follows: Partial Fiber Texture A which has a (011) direction in the rolling direction and includes orientations within the spread from (211)[011] through (100)[Oll] to (211)[011.]; there is some controversy as to whether it extends as far as the orientation (111)[011]. As Dillamore6 has observed, the extent of this partial fiber texture depends on the intensity levels selected. Partial Fiber -texture B which has a (011) direction located 60 den from the rolling direction in the plane containing the rolling direction and the sheet normal. There are two directions which satisfy these conditions and orientations in this partial fiber texture extend from (21l)[0ll] through (554)[225] to (121)[101]. The orientations {211}(011) are members of both partial fiber textures A and B and it can be noted that a variant of {554)<225> is within 6 deg of a variant of {111}(112). Barrett7 had postulated earlier that, in addition to orientations which would fall into partial fiber texture A, a true fiber texture with a (111) direction in the sheet normal was present after heavy cold reduction. This fiber texture would include orientations such as {111}(011) and {111}(112). Later investigators, notably Bennewitz,&apos; have discounted this, mostly on the ground that the partial fiber textures A and B, as described above, contain all the strong orientations that have been observed. However in other work it has been reported2 that (222) pole density or inverse pole figure values show a continuing increase with increasing reduction by cold rolling and give values considerably greater than for any other low indices plane. Thus it could be inferred that a (111) fiber texture as described by Barrett would be one which becomes more dominant with increasing cold reduction, whereas Bennewitz&apos; concluded that components such as {554)(225) in partial fiber texture B began to decrease in intensity at high reductions. Following Bennewitz, one would expect a decreasing (222) pole density value (parallel to the sheet normal) with increasing cold reduction. Because fiber textures consist of grains with a range of orientations that have one axis in common, it has been inferred that during deformation the crystal orientations rotate about the fiber axis&apos;74 and that the orientations of crystals that at one stage belong to one fiber texture can rotate on further cold reduction into the other fiber texture through an orientation in which the two fiber textures intersect.&apos; For example,

Jan 1, 1970