By A. E. Jenkins, A. Jostsons

Isothermal sections of the Ti-0-H phase diagvam at 600°, 700°, and 800°C have been constructed from equilibrium hydrogen pressure measurements over a range of Ti-0-H alloys containing up to 34 at. pct 0. Oxygen reduces the hydrogen solubility at fixed hydrogen pressure but increases the terminal solubility in the a solid solutions at the a/(a + P) phase boundary. Metal-lographic studies of alloys annealed below the eutectoid temperature show that oxygen also increases the ter-ninal solubility of hydrogen in the a solid solution in equilibrium with the hydride phase. The effect of oxygen on hydrogen solubility is discussed in terms of the electronic and geometric structure of interstitial solid solutions. THE isothermal solubility of hydrogen in a Ti-0 alloys at 800°C has been measured by Hepworth and ~chuhmann' who subsequently used ternary Gibbs-Duhem integrations to calculate oxygen activities in binary Ti-0 alloys. The present study aims to extend Hepworth and Schuhmann's measurements to alloys richer in oxygen and to a range of temperatures. This paper presents the results of hydrogen equilibrium pressure/concentration measurements in Ti-0 alloys as well as observations on the effect of oxygen on the terminal solubility of hydrogen in a titanium. The thermodynamic properties of binary Ti-0 alloys, derived from these measurements, will be published separately.' EXPERIMENTAL METHODS Specimen Preparation. Ti-0 alloys were prepared from iodide-refined titanium and titanium dioxide obtained by hydrolysis of redistilled titanium tetrachlo- ride. Specimens containing up to 16 at. pct 0 were prepared by electromagnetic levitation3 whereas a conventional tungsten arc furnace with a water-cooled copper hearth was used to melt oxygen-rich alloys. The specimen homogeneity was indicated by the constancy of lattice parameters of samples from various parts of the ingot as well as by the sharpness of the reflections on X-ray powder patterns. Oxygen-rich specimens in the composition range (20 to 34 at. pct), where ordering has been ~bserved,~ were annealed for 300 hr at 600°C prior to use in hydrogen solubility measurements. Apparatus. The hydrogen pressure/concentration measurements were made with a modified Sieverts apparatus shown diagrammatically in Fig. 1. Specimens were placed in a clear silica tube and impurity pickup by direct reaction with silica was prevented by lining the heated end of the silica tube with thin molybdenum sheet. A double silica tube was required to eliminate loss of hydrogen by diffusion through silica at high temperatures and high hydrogen pressures, the space between the tubes being maintained at a hydrogen pressure equal to that above the specimen. Hydrogen was purified by diffusion through a Ag-Pd tube.= Hydrogen pressures were measured with a mercury McLeod gage in the range 0.001 to 4 Torr

Jan 1, 1968

By M. C. Flemings, G. E. Nereo

General expressions are given to describe macro-segregation in castings and ingots which results from mass flow of solute-rich liquid to feed solidification and thermal contractions. Analytical solutions are given for solidification with planar isotherms (unidirectional and bidirectional heat flow). These solutions describe inverse segregation and centerline segregation. Numerical examples are given for A1-4.5 pct Cu alloy. In 1540, Vannoccio Biringuccio published one of the first references to macrosegregation, describing the problem of exudation and inverse segregation in the manufacture of bronze gun barrels.' Since then, a great many studies of macrosegregation have been reported. Recent work of particular engineering interest includes that of Marburg 2 and others:" on centerline segregation and other types of segregation in large steel ingots, and work of Adams,5 Scheil, 6 and Kirkaldy and youdelis7 on inverse segregation in nonferrous ingots. In most studies on this subject, the various types of macrosegregation have been treated as separate phenomena. For example, quite different mechanisms have been proposed for formation of centerline segregation, negative cone of segregation, inverse segregation, banding, and so forth. In this, and in several papers to follow, it is proposed that these as well as other types of macrosegregation result from the same basic mechanism and can be quantitatively described by the same basic equation. It has often been suggested that some types of segregation (such as centerline segregation and banding) occur as a result of buildup of solute at the tips of growing dendrites.2-4 ,8-10 As example, banding can be induced in centrifugal castings by mechanical vibration, and Northcott 10 suggests this might be due to the influence of the vibration on the boundary layer at the dendrite tips of the growing dendrites. However, in view of the extremely small boundary layer known to exist at the tips of the dendrites,11,12 any interpretation of macrosegregation based on this boundary layer is clearly incorrect. Note that experiment has shown that significant buildup of solute does not occur at dendrite tips in ingot solidification, but even if such buildup occurred the thickness of the enriched zone would only be the order of D/U where D is liquid diffusion coefficient and U is dendrite tip velocity. For usual casting or ingot solidification this solute-enriched layer is 10"3 cm, far too small to account, for example, for centerline segregation.11'12 It has also been suggested that convection in the bulk liquid (ahead of the advancing dendrites) might cause segregation by sweeping away the solute-rich boundary layer in front of the dendrites.3 However, since there is no significant boundary layer, this explanation must be incorrect. The convection might directly cause segregation by penetrating between the dendrite arms, and presumably in a rimming steel ingot it is sufficiently vigorous to cause some segregation in this way. Centerline segregation, however, cannot be interpreted as resulting from this convection since a sharply segregated zone is usually found near the centerline, with the bulk of the ingot being nearly of nominal composition. If convection in the bulk liquid were the direct cause, a gradual change in ingot composition over the entire cross section would be expected. It is known that sudden changes in convection of the bulk liquid during solidification can result in banding,14 but it is not clear that the banding results directly from the effect of convection on solute distribution. Changes in convection also affect thermal conditions in the liquid-solid region of a solidifying ingot. It will be seen later in this paper, and in a paper to follow, that macrosegregation is strongly influenced by these thermal changes. Recognizing that in some cases of ingot solidification (as in solidification of rimming steels) convection in the bulk liquid may have a direct effect on solute distribution, we neglect it in this paper and in the several to follow. We then derive general expressions describing macrosegregation which results from the mechanism of interdendritic flow of solute-rich liquid

Jan 1, 1968

By Klaus Schwerdtfeger

In order to test the performance of ZrO, (CaO) and Tho,(Yz03) electrolytes in the electrochemical determination of oxygen activities in liquid metals at steel-rrzakitng temperatures , electromotive force measurements have been made with the following cells: The oxygen-- activities are calculated from the electmrnotive forces for the investigated systems. The standard free energy of- formation of MnO and the activity of manganese in Fe-Mn melts are derived. Indications are that the Zr 0z(Ca0) electrolyte exhibits little electronic conductivity at oxygen pressures as low as 10'a atnz at 1600°C; however, the partial electronic conductivity may become noticeable at lower oxygen activities. The Tho,(Yz03) electrolyte is found to be an ionic conductor at the oxygen pressure as low as that for the Mn + MnO equilibrium, but exhibits partial electronic conductivity at oxygen pressures higher than 10"1 atm (1500°C). fi. better control of oxidation and deoxidation reactions in steelmaking may be facilitated if the oxygen activity in the steel is known during various stages of the process. In the present work oxygen activities have been measured in liquid iron, manganese, and iron alloys with galvanic cells using ZrOz(CaO) and s solid electrolytes with the object of establishing the range of oxygen pressure in which these materials can be used as electrolytes at steelmaking temperatures. Calcia-stabilized zirconia and Tho2-Y203 solid solutions are oxygen ion conductors. Such electrolytes were first used by Kiukkola and Wagner1 and Peters and ~ann' in galvanic cells for the determination of thermodynamicquantities of oxide systems in the temperature range 700" to 1200°C. At these moderate temperatures calcia-stabilized zirconia has been found to exhibit predominantly ionic conductivity at oxygen pressures as low as those for the Cr + Crz03 equilibrium,394 but at lower oxygen pressures elec- tronic contribution to conductivity becomes significants4 The Th02-Y203 solid solutions are ionic conductors at oxygen pressures lower than those applicable to zirconia base electrolytes.5'6 At high oxygen pressures Thoz base electrolytes exhibit significant p-type semiconduction. At the time the present experiments were carried out several papers1'-* were published on the electrochemical determination of oxygen activities in liquid iron using the ZrOz(CaO) electrolyte. The results of different authors do not agree well. For instance, according to Fischer and ~ckermann" stabilized zirconia can be used to measure oxygen contents in liquid iron larger than 0.02 wt pct, but according to Baker and west1' ZrOz(CaO) cannot be used for the determination of oxygen content in liquid iron because of high electronic contribution to the conductivity. Fig. 1 is a schematic diagram of the apparatus used. About 500 g of liquid metal is contained in a crucible into which a stabilized zirconia or Th02(Y203) tube is immersed. A platinum contact wire is pressed (with a spring mechanism) against the inside bottom wall of the electrolyte tube. The tube is flushed continuously with a stream of air, CO-CO, (or Hz-C02) (at 0.96 atm and at a rate of about 300 cu cm per min), via an alumina tube inserted inside the electrolyte tube. This alumina tube also contains the Pt-Pt/10 pct Rh thermocouple. A capillary alumina tube shielding the other contact wire is immersed in the melt. The molybdenum contact wires were used mostly; in some cases platinum wire was employed. Molybdenum has the advantage that it dissolves more slowly in the melt than platinum. The whole cell was contained in the alumina reaction tube of a resistance furnace with molybdenum winding. The reaction tube was closed gas tight at both ends and flushed continuously with argon. Because of the poor thermal shock resistance of the electrolyte tubes the cell had to be assembled in the cold furnace. The electrolyte tube and alumina sheath

Jan 1, 1968

By Fred H. Perfect

The thermite process, now approximately 80 years old, has heretofore been practiced in ceramic vessels. This paper outlines the successful production of several million pounds of alloy produced in zuater-cooled copper vessels. THE high temperatures necessary to produce fluid high-alumina slags have probably discouraged earlier workers from attempting to utilize water-cooled vessels. The following is a report of the successful application of this method, together with a report of the physical and chemical problems which had to be solved to make the process practical. About 1955, when Reading Alloys was more concerned with the production of ferrotungsten than with most other types of alloys, it was found to be exceedingly difficult to predict the reaction rate that one would experience from one tungsten ore to another . This difficulty was increased for two reasons: the physical state of the ore as received was seldom uniform, and the size of the mass to be reduced is a very important factor in developing the proper mix for the final reaction rate and temperature. For example, the reduction of ferric oxide with aluminum would theoretically produce temperatures of about 2600°C, and, in spite of the losses due to radiation, the energy is quite sufficient to produce a very fluid slag and iron effecting a very clean separation. On the other hand, the reduction of ferrous oxide with aluminum, while it is not as energetic as the first reaction, nevertheless should give temperatures above 2000"C, which should cause separation of alumina and iron, but, in practice, this is not the case and good fluid slag is not obtained. The heat of reaction, calculated from the thermo-dynamic heats of formation of the constituents of the reaction, offers a convenient guide to the feasibility of a thermite reaction. Thus, the values listed in Table I can be used as an approximate guide for estimating the results which may be expected in the reduction of various oxides and combinations of oxides using aluminum as the reducing agent. As a generalization, those reactions releasing approximately 600 cal per g of total mass represent the lower limit at which to expect separation of slag and metal. On the other hand, those reactions which release 1100 to 1200 cal per g are too violent to be used successfully without the addition of considerable inert material, such as lime, fluorspar, and so forth. Reaction rate is also a very important factor. This, of course, is governed very largely by the sizing and intermingling of the oxidant and reductant and by the starting temperature of the reactants. This is why those figures shown in Table I can only be a general guide. Further, it must be understood, that by adding powerful oxidizing agents, such as nitrates, chlorates or metallic oxides, such as molybdenum trioxide or chromium trioxide, certain problems respecting low temperatures are not necessarily solved. This is true in the addition of oxidants, such as sodium chlorate. By adding too high a concentration of sodium chlorate as a booster for a particular reduction, explosions are generated. Generally, they are of an intermittent type so as to give a Roman Candle effect to the reduction itself; with each surge resulting from a minor explosion more and more material is thrown

Jan 1, 1968

By F. S. Pettit

The oxidation of Ni-3 to 25 wt pd Al alloys has been studied in 0. 1 atm of oxygen at temperatures between 900° and 1300°C. These alloys have been found to oxidize by three different mechanisms which depend on the temperature of- oxidation and the alloy composition. Two of the three mechanisms do not permit a continuous layer of Al,0, to be formed on the alloy surface and the oxidation rates are greater than that for pure nickel. The third mechanism results in the formation of an external A1203 scale and lke oxidation rates are about three orders of magnitude smaller than those for pure nickel. The minimum amount of aluminum required for the formation of external scales of A L,0, has been determined. NICKEL-base alloys are currently the main source of materials for use at elevated temperatures in gas turbine engines. These alloys are usually coated to obtain oxidation resistance. Coatings on nickel-base alloys are frequently formed by reaction of the alloy with aluminum whereby alloyed nickel aluminides are formed. The alloyed nickel aluminides provide protection to the nickel base alloy because external scales of A1203 (alumina) are formed during oxidation and mass transport through A120, is slow in comparison to mass transport through most other oxides. In view of the protective properties of A1203, it is important to know how much aluminum is required in these alloys in order to form external scales of AlzO,. The present paper is concerned with the oxidation kinetics and the oxidation mechanisms of Ni-A1 alloys and the minimum amount of aluminum required in these alloys for the formation of external scales of Alz03. THEORETICAL CONSIDERATIONS When a Ni-A1 alloy is heated in oxygen at elevated temperatures, the following reactions can take place on the surface of the alloy where the oxide phases are assumed to be virtually pure: These oxide phases are in the form of nuclei scattered over the surface of the alloy and, in view of their rapid formation, they need not be in equilibrium with the alloy. As the oxidation process continues, equilibrium between the alloy surface and the oxide phases is approached and the stability of the oxide nuclei is determined by the composition of the alloy at the alloy/oxide interface because of the following reactions: 3NiA1204 + 2A1 (alloy) = 4AlzO3 + 3Ni (alloy) [41 4Ni0 + 2Al (alloy) = NiA120, + 3Ni (alloy) [ 5 1 Application of the mass-action law to Eqs. [4J and [5J yields the following equilibrium conditions for these reactions: where aA1 and aNi are the activities of aluminum and nickel, are the standard free energies of formation of NiO, A1203, and NA1204, respectively, R is the gas constant, and T is the absolute temperature. If the composition of the alloy at the alloy/oxide interface is such that (akl/ahi) is greater than the equilibrium values defined by Eqs. [6] and [7], then Reactions (41 and [5] will go to the right as written. Conversely, if the alloy composition is such that the activity ratio (aLl,/aki) at the alloy/oxide interface is less than the equilibrium values, then Reactions [4] and [5] will proceed to the left. The equilibrium activity ratios in Eqs. [6] and 171 can be calculated since values for the standard free energies of formation of the oxide phases are available. Standard free energies of formation for NiO and A1203 have been tabulated by Elliott and ~leiser.' The standard free energy of formation for NiA1204 can be obtained from the data of Tretjakow and Schmalzried.' The results of these calculations are tabulated in Table I. Table I shows that the following inequality is valid over the temperature interval 900" to 1300°C: (Reaction [5]) (Reaction [4]) « 1and therefore the aluminum activity for these compositions can be taken as equal to the square root of the activity ratios (i.e., aNi = 1). If equilibrium is estab-

Jan 1, 1968

By J. E. Hanlon, S. R. Butler, R. J. Wasilewski

The temperature, orientation, and strain-rate dependence of tensile flow in single-crystal NiA1 of equiatomic composition have been investigated up to 800°C. Compression tests at room temperature have also been carried out. Optical and replica electron microscopy and X-ray diffraction methods were used to investigate the slip mechanisms. NiAl exhibits {110)(001) slip and cube slip {l00)(010) was also observed. This results in very high strength of single crystals in cube orientation. The implications of this slip mode, with the resultant small number of possible slip systems and three mutually perpendicular slip vectors, are discussed. ThE CsCl structure compounds represent a class related to the bcc elements, but their behavior is affected by three additional variables: composition (within the stability range of the compound), extent of long-range order perfection, and bonding energy. Very little data are available on the effects of these variables on mechanical properties. Rachinger and ~ottrell' suggested slip to occur along (111) in compounds of low ordering energy; in compounds of higher bond strength (>0.06 ev), they observed (110) (001) slip. As pointed out by copley,' only three in- dependent slip systems are available in the latter case; hence general deformation is impossible. Brown3 carried out a theoretical calculation of the yield-point variation with the degree of long-range order in the CsCl structure, based on the assumption of superdislocations. More general approaches, based on considerations of superlattice dislocations and antiphase domain boundaries in ordered structures, were carried out by Flinn~ and by Vidoz and Brown.' These, however, give no information on changes in the slip structure—if any—between the ordered and the disordered compounds. This aspect was investigated experimentally and theoretically by Stoloff and Davies' and by Marcinkowski and chessin7 in FeCo. The latter workers proposed the deformation behavior of the ordered FeCo to be essentially the same as that in many other bcc metals. Investigations of polycrystalline A~M~'-'O indicate considerable variation in mechanical properties with composition and test temperature. The existence of {123)(111) slip was reported in AgMg.'9'9'0 (The formation energy of this compound, presumed to be ordered at all temperatures below melting, is 4.38 cal per g-atom," i.e., 0.024 ev per bond.) The yield strength has been reported as relatively independent of temperature below 0.45 T, (where T, is the absolute melting temperature). Tensile deformation of single-crystal AgMg was also investigated by Kurf-man," who observed marked tendency to single glide on{112}(111) and {110)(111). From observations of slip lines in deformed poly-crystalline NiA1, Westbrook et a1.I3 suggested the

Jan 1, 1968

By W. A. Backofen, B. C. Wonsiewicz

The Plasticity transition in magnesium was studied by plane-strain compression of single crystals and polycrystalline material at temperatures from about 20" to 307°C. Reduction of single crystals along the c axis was accommodated by twinning on {1011) and retwinning on (10 12}, followed by basal shear in the doubly twinned volume. Deformation in that mode can result in sufficient independent shears for arbitrary shape change. Fracture in c axis compression, below about 100°C, has been related to excessive shear caused by unloading from the stress for {1011} twinning (-50 ksi at 20°C) to that for slip within the twin (-3 ksi); ductility follows from heating because the stress difference is lowered and the twin volume, in which elastic strain energy is dissipated on unloading, is increased. The stress for (1011) twinning is strongly temperature-dependent but not given by a critical resolved shear stress law. The latter is attributed to the influence of stress concentration from prior intersecting shear on nonbasal planes, the former to the temperature dependence of the preliminary slip. THE basic symmetry of hcp crystals has the effect of limiting the number of independent slip systems and making twinning an important deformation mechanism. The general result in wrought polycrystalline aggregates is a more or less sharply developed texture (or preferred orientation) which underlies a strong anisotropy in mechanical behavior. Knowing how the one influences the other is essential background for the use of such materials. Magnesium was of interest in this work because of the unexplained plasticity transition that it undergoes somewhere in the neighborhood of 200°c.''~ At lower temperatures plastic deformation before fracture in polycrystalline material is limited, while at higher temperatures extensive deformation is possible. The transition temperature commonly determines the lower limit of the range in which magnesium is worked. The limited ductility can be traced to a lack of independent crystallographic shears. A minimum of five are required for arbitrary shape change.' Around room temperature, however, slip on all known systems provides only four.' In each case, the slip direction is in the (0001) basal plane so that slip does not allow strain along the c axis. With increasing temperature, more slip occurs on the ( 1011) pyramidal plane and the ( 1010) prism plane but without change in direction.'?' Thus, that development alone cannot explain the transition temperature.

Jan 1, 1968

By L. J. Kashar

By means of a continuum-mechanics approach, the following equation for calculuting the pressure for axisymmetric cold forging has been derived: where P is the extrusion pressure; K and n are the strength coefficient and the strain-hardening exponent of the steel, respectively; a and b are strain factors, primarily dependent on the die design; and R is the extrusion ratio. Data from compression and backward-extrusion tests performed at a crosshead speed of 0.5 in. per min on a nonwork-hardening material pure lead) and on a work-hardening material (1018 steel) indicate that the predicted extrusion pressures obtained from the derived equation agree very closely with the actual extrusion pressures. Therefore, the equation can be used to predict backward-extrusion pressures from standard mechanical-test data. The decision to cold-forge a part is based on several considerations, most of them related to economics. However, the production feasibility is usually determined by the pressure needed to extrude the part and the availability of tooling that can repeatedly sustain this pressure for over several hundred thousand cycles. A major contribution to the cold forging of steel would result from the development of steels that could be forged at reduced pressures and from the development of techniques that permit the accurate prediction of the pressure necessary to cold-forge the part. The ability to predict extrusion pressures is necessary to properly design the tooling required for the cold-forging process. Attempts to theoretically predict the cold-forging pressure, especially for work-hardening materials, have been unsuccessful in previous investigations of the cold-forging process.1-3 Many empirical relations have, therefore, been proposed relating the extrusion pressure to the chemical composition,' the extrusion ratio,2 the tensile strength,273 and hard- ness, 2 and the yield strength3 of the material being extruded. However, these empirical relations are valid only for the specific conditions used in their development, and, in some cases, the empirical relations had a scatter band greater than * 10 pct. A study of the extrusion process was undertaken with the objective of developing predictor equations for extrusion pressure by using a continuum-mechanics approach to the problem of metal flow. The derivation of such an equation is summarized in this paper, and data are presented that confirm the validity of the derived equation. DERIVATION OF THE EXTRUSION EQUATION If the extrusion of a material through a die is considered in terms of a work balance, it has been shown that it is possible to derive an equation relating the work necessary to move the material through the die to the deformation work undergone by the material. The work done, W, in moving the material is given by where F is the extrusion force, I, is the distance the material was moved, A, is the original cross-sectional area of the material, P is the extrusion pressure acting on A,, Ap is the cross-sectional area of the extrusion punch, and Pp is the punch pressure acting on Ap. The deformation work, WD, is given by where V is the volume of metal deformed, ay is the flow stress of the metal, and E is the total strain undergone in the extrusion. If there are no frictional losses, the work done, W, is equal to the deformation work, WD; therefore, Since the volume of a metal does not change during deformation,

Jan 1, 1968

By G. D. Rieck, M. M. P. Janssen

Chemical diffusion coefficients and heats of activation for diffusion in the NizAh fy), NiAl (6), and Ni3A1 (E) intermetallic phases and the solid solution of aluminum in nickel (( phase) were calculated from layer growth experiments. No finite diffusion coefficient for the NiAl3 ((3) inter metallic phase could be calculated. The values of the diffusion coefficients are dependent both on the method of calculation and the type of diffusion couple. The heat of activation for diffusion in the y phase was found to be 47 kcal per mole in the temperature range oj 428" to 610°C. Heats of activation of 41, 12, and 48 kcal per mole were found for diffusion in the 6, E, and ( phases, respectively , in the temperature range of 655" to 1000°C. Experiments with markers in the diffusion zone demonstrate a very pronounced Kirkendall effect. It appears that only aluminum atoms take an active part in the diffusion process during the formation of the 0 and y phases at temperatures of about 600°C. During the formation of the 6, E, and < phases at higher temperatures only nickel atoms are moving. It is suggested that the great stability of the intermetallic compounds in the Ni-A1 system governs the Kirkendall effect. SOME factors controlling layer growth during inter-diffusion in the Ni-A1 system (phase diagram, see Fig. 1) were studied by Castleman and Seig1e.l&apos;~ They found the NiA1, ((3) and NiAl3 (y) intermetallic compounds to appear in the diffusion zone of Ni-A1 couples at annealing temperatures of 400" to 625°C; the NiAl (6) and Ni3A1 (E) intermetallic compounds appeared in y-Ni couples at annealing temperatures of 800" to 1050°C. These authors carefully examined metallographically Ni-A1 couples after 340 hr annealing at 600°C. Besides the (3 and y phases they found very thin layers of the 6 and E phases. ~n~erman~ and Castleman and Froot4 observed a much more rapid growth of the 5 and E phases at 600°C in Ni-A1 couples in case a crack was present at the /3-A1 interface. Numerous layer thickness measurements carried out by Castleman and Seigle on the y phase prove that the layer growth of this phase obeys the parabolic law after a certain transient period. From this they concluded that the layer growth of the y phase is controlled by volume diffusion. The growth of the 13, 6, and E phases appeared to be volume-diffusion-controlled also. The authors estimated that at 600°C and at atmospheric pressure Dp was 1.8 x lo-"ll sq cm per sec, D, 9.1 x 10" ™ sq cm per sec, Qp 27 kcal per mole, and Qy 31 kcal per mole. The present work was carried out to obtain more quantitative data about the kinetics of growth of the phases of the Ni-A1 system and the reactions that occur during the formation of these phases. Because in this system the diffusion process results in the formation of several distinct intermetallic compounds, the current term reaction diffusion is used in the title of this paper. In order to obtain layers of the fl phase compound of uniform thickness, a new technique for preparing diffusion couples was developed. The kinetics of growth of the y phase in 6-Al, E-Al, and Ni-A1 diffusion couples was studied at different temperatures. The kinetics of growth of the 6, c, and ( phases in Ni-y, Ni-6, and Ni-c diffusion couples was also studied at different temperatures. The calculation of the diffusion coefficients Dp and Dy by Castleman and Seigle are critically considered in this paper; by means of a revised method of calculation more reliable val-ues of , and Dg were found. These values are in good agreement with the values of the diffusion coefficients obtained by the method of Boltzmann-Matano. From the temperature dependence of the diffusion coefficients the heats of activation for diffusion were calculated by means of an Arrhenius-type equation. The investigation of the Kirkendall effect has been used to obtain information about the ratio of the intrinsic diffusion coefficients of the separate atoms5 and the mechanism of diffusion. Moreover porosity as a result of a distinct Kirkendall effect would be of practical importance in connection with the bonding of diffusion coatings. The analyses of the diffusion couples were carried out by metallographic methods. The values of the concentrations at the phase boundaries and the concentration profile in each of the phases, which are needed for the calculation of diffusion coefficients, were obtained by electron-pro be X-ray microanalysis. EXPERIMENTAL PROCEDURE A) Materials for Diffusion Couples. The intermetallic compounds 6 (50 at. pct Ni) and E (74 at. pct Ni) were prepared from the pure metals by high-frequency induction melting in argon atmosphere. Use was made of aluminum wire (99.99 wt pct Al) and nickel sheet (99.95 wt pct Ni). The 6 and E phase melts and the nickel shiet (thickness 0.1 and 0.5 mm) used for preparing diffusion couples were annealed for 64 hr at 1200°~ for homogenization and grain coarsening (final crystal size 1 to 3 mm). composition and homogeneity of the intermetallic compounds were checked by mi-crohardness measurements and X-ray diffraction. From the 6 and E phase melts discs of 0.5 mm thickness were prepared by means of a water-cooled rotat-

Jan 1, 1968

By E. P. Sadowski, L. P. Trudeau, C. R. Cupp

The apparent high radiation resistance of two varieties of maraging steel is described and an indication is given of some phenomena that require further study. Two aspects were included in this work: a) effects of neutron irradiation on the room-ternperature tensile properties of 18 Ni (250) maraging steel; b) effects of neutron irradiation on the room-temperature tensile properties and on the impact resistance of 12 pct Ni-5pct Cr-3 pct Mo maraging steel. Subsize tensile and impact test specimens were used. The 18 pct Ni steel was irradiated to a neutron fluence of 3.3 x 10 n per sq cm (>1 mev). The 12-5-3 variety was irradiated to two neutron fluence levels: 1) 1.5 x 10 per sq CTTL (>I mev) 2) 3.1 x 10&apos;9nper sq cm (>1 mev) In all respects both varieties showed unusually high resistance to change in strength and ductility after neutron irradiation. There was no noteuorthy over-aging in fully aged specimens. The aged 18 pct Ni variety showed a 4 pct drop in yield strength upon irradiation with little or no decrease in ductility. The aged 12-5-3 variety showed a 5 pct increase in yield strength on irradiation with a very slight decrease in ductility. The impact transition of the 12-5-3 variety only increased 35 to 45 Co upon irradiation, and the shear energy fracture value for the subsized specimens decreased only half as much as expected frorn experience with conventional steels. THE development of new reactor concepts and nuclear technology now depends to a large extent on the availability of new alloys capable of operating in stringent reactor environments. One of the most important new types of metallurgical material that has been developed in recent years is the maraging steels. This type of alloy is notable for its remarkable retention of toughness at high strength levels. In the course of a research program which incorporated ambient temperature radiation effects studies to determine the mechanisms of strengthening of 18 pct nickel maraging steel,&apos; it became evident that the resistance of the alloy to neutron-induced changes in mechanical properties should be studied. This paper is to present evidence for the apparent high radiation resistance of maraging steel. The experimental program was in two parts: a) Effect of neutron irradiation on the room-temperature tensile properties of 18 Ni (250) maraging steel. b) Effect of neutron irradiation on the room-temperature tensile properties and on the impact resistance of 12 pct Ni-5 pct Cr-3 pct Mo maraging steel, a cobalt-free alloy. EXPERIMENTAL PROCEDURE 18 Ni (250) Maraging Steel. Tensile test specimens were machined to the dimensions shown in Fig. 1 from $-in.-diam hot-rolled bar of the composition shown in Table I. All specimens were austenitized for 1 hr at 1500°F (815°C) in argon and water-quenched. Half of the specimens were then mar aged for 3 hr at 900° F (482°C) in argon. The specimens were irradiated in a fast neutron transformer rod at approximately 120°F (50°C) to a neutron fluence of 3.3 x 10 10 n per sq cm (>1 mev). The irradiation was performed in the NRX reactor of Atomic Energy of Canada, Ltd., at Chalk River, Ontario, Canada. In all cases, the thermal neutron flux was three times as high as the reported (> 1 mev) fluxes. The room-temperature tensile tests were performed with an Instron tensile testing machine operating at a crosshead speed of 0.05 in. per min. The loading frame of the machine, mounted in a hot cell, was remotely controlled. The specimens were tested either

Jan 1, 1968

By G. S. Cole

The temperature has been measured ahead of stationary solid-liquid interfaces under conditions approximating luzidirectional heat flow and therefore unidirectional solidification. Natural convection flow patterns may be deduced from the temperature distributions , temperature fluctuations, and shape of the interface. Fluid flow increases with the height and the rate of heat transfev through the interface and this is further manifested by a deviation of the interface from aflat vertical plane. The influence of fluid flow on solute inhomogeneity during alloy crystal growth can be inferred from the observed temperature distributions. A buoyancy force exists in the liquid ahead of a vertical solid-liquid interface, caused by a difference in density between cold fluid near the interface and warmer fluid in the bulk liquid. When the viscous and inertia forces in the melt exceed this buoyancy force, a flow of fluid takes place, termed natural or free thermal convection. Natural convection in purely liquid systems has been extensively studied for many years. 1"u On the other hand, fluid flow during horizontal crystal growth has oniy recently been the subject of experimental investigation."-25 The requirements for horizontal crystal growth differ from other heat flow systems. The small aspect ratio (ratio of height of cold wall to length of fluid) has never been considered. The uniform furnace gradient which supplies heat radially (and not necessarily symmetrically) differs from previous boundary conditions of uniform heat flux at the cold and hot ends. And most important of all an isothermal s/l interface is present which can adjust its shape and position to conform to heat and fluid flow. All of these boundary conditions involve complexities which cannot be readily solved analytically. Preliminary observation has demonstrated the penera1 shape of the natural convective flow pattern in transparent media.20&apos;24&apos;25 The flow is circulatory, directed toward the interface at the surface of the liquid, down and away from the interface at the bottom, and then up at the hot end of the melt. During crystal growth such a flow may interact with the solute boundary layer at the s/l interface to affect solute incorporation.M&apos;1B|28&apos;i!T Evidence has also been presented recently to show that thermal convective flow will affect the structure of ca~tin~s.~~-~~ The rate of heat transfer (conduction plus convection) in a given fluid system is a function of the temperature difference between the hot end of the liquid and the s/l interface and the height of the interface. At the lowest values of these variables* all heat is *It has been shown&apos; that adverse temperature gradients as low as O.OOS°C oer cm are sufficient to cause convection. transferred by conduction. When the temperature difference or interface height are increased, laminar fluid flow commences and heat transport takes place by laminar convection as well as by conduction; turbulent heat transfer takes place at higher values of these variables. In the transition region between laminar and turbulent flow, boundary layer separation takes place; fluctuations in temperature are also noted and increase in amplitude and frequency as turbulence becomes dominant. In this paper, fluid flow patterns in the melt ahead of a stationary interface are deduced from observations of temperature distribution and fluctuations, heat flow rate, and interface shape. The fluid flow ahead of advancing interfaces and the effect of such flow on solute incorporation may be inferred from these measurements on stationary interfaces. Observations during enforced fluid motion will also be considered. EXPERIMENTAL PROCEDURE The metal was contained in a lava boat 10 cm in length, 1+ cm in width, and 2 cm in height, as shown in Fig. 1. A water-cooled, molybdenum block heat-sink is at one end of the boat; surrounding this assembly is a slotted stainless-steel tube noninductively wound with a nichrome heating element. Temperature was measured by 38-gage Chrome1 vs Alumel thermocouples sheathed in 0.05-cm-diam graphite-coated stainless-steel tubing, which were moved longitudinally and vertically through the melt by means of a two-dimensional motorized micrometer stage. In some experiments the thermocouple junction was exposed, but in the majority of experiments the junction was welded to the sheath tip; no significant difference

Jan 1, 1968

By S. Shapiro, G. Krauss

The strutural and cr~stallo~aphic features of the plates of austenite produced by the martensite to aus-tenite or reverse martensitic tramformation have been determined in an Fe-33 wt pct Ni alloy. Micro-focus X-ray techniques and single-surface trace analysis 072 bulk samples yielded two distinct habit planes, (0.174, 0.309, 0.~35)~ and (0.375, 0.545, 0.749jM. The former plane uas the one predorninantly observed and its existence was verified by transn~ission electron microscopy. The orientation relation-ship between the reversed austenite and the parent martensite was approximately the same as the Nishiyamna and other relationships reported for the direct tramformation. Replica and thin-joil obser-vations show that both high densities of tangled dis-locations and occasional twins constitute the fine structure of the reversed austenite. Application of the phenomenological theory to a variant of the predominant habit plane defines an irrational plane and direction for the second shear in accordance with the comnplexity of the fine structure. The shear accompanying the reverse martensitic transformation is at least 0.51, the maximnum value of- the tangent oJ the tilt angle measured on surface replicas. A mechanism relating the fine transformation twins in martensite to the nucleation of reversed austenite of the predominant habit is proposed. The reversal of Fe-Ni martensite takes place both at the edges of martensite plates and in a piecewise fashion within them.&apos; The shear-type nature of the reverse transformation is verified by the surface relief which accompanies both edge-type reversal2 and the fragmentation of plates of martensite&apos; as a result of rapid heating above the A, (austenite start temperature). The orientation relationship between the edge-type reversal product and the parent martensite, as determined by transmission electron microscopy, is reported to be within 4 deg of either the Kurdyumov-Sachs or Nishiyama relationships,&apos; but there is no work at present in the literature relating to the crystallography of the platelike reversed austenite. The fine structure of reversed austenite after heating to 50°C above the Af is reported4 to be composed primarily of tangled and jogged dislocations in concentrations up to 10" per sq cm. A replica investigation of partially reversed Fe-Ni martensites5 corroborates the increase in dislocation density following reversal and presents indications of other possible modes of fine structure. This paper reports on an investigation performed to examine in detail the morphology and crystallography of the plates of reversed austenite and the shear which accompanies their formation in a matrix of Fe-Ni martensite. EXPERIMENTAL PROCEDURE Discs of a high-purity Fe-32.9 wt pct Ni single crystal served as the starting material. The single crystal had been produced in the course of an earlier investigation6 and the carbon content was determined at the time to be 0.006 wt pct. The M,, and the A,, were respectively -120" and 300°C. Partial transformation to martensite was performed at -125°C and reversal of some of the martensite was accomplished by heating in the temperature range 340" to 355°C. Most samples were heated to the reversal temperature by immersion&apos; in a salt bath for 2 min. For surface-relief studies some polished and etched Samples were heated in a tube furnace for ten min in a hydrogen atmosphere maintained over the samples throughout the heating and cooling cycles. Samples were prepared for metallographic examination by electropolishing and etching with an HC1-HNOs-H20 et~hant.~ On one of the surface-relief samples two sets of fiducial scratches were placed on the etched sample by drawing it over a slurry of 0.06 p alumina on a "microclothJ&apos;. The orientations of individual plates of martensite were determined by X-ray analysis. A Rigaku-Denki microbeam X-ray generator in conjunction with a Micro-Laue camera with facility for precision location of the sample in front of the beam was employed for this purpose. The collimator size was 30 p and the specimen to film distance was 5 mm. The Laue photograms were enlarged to an equivalent 3-cm specimen to film distance for analysis. The orientation of each of the plates of martensite was compared to that of the parent austenite and the relationship be -tween the two phases was, in all cases, within a few degrees of those predicted for the direct transformation. The orientation relationship between one of the larger plates of reversed austenite and its parent martensite was determined in a similar manner. The habit plane of the islands of reversed austenite in the X-rayed plates of martensite was determined by a single-surface trace analysis. Each reversal island had with the parent phase one comparatively straight boundary which was presumed to represent the habit plane trace. The pole locus technique7 was applied to traces from six different plates of martensite to determine the indices of the habit plane. A 40-cm stereographic net was employed for this analysis The morphology and fine structure of the reversed austenite were studied by electron microscopy of pre-shadowed direct carbon replicas,5 and the macroscopic shear was evaluated by a two-stage replica technique similar to that employed in electron fractog-

Jan 1, 1968

By N. A. D. Parlee

The diffusion rate of hydrogen in liquid iron has been measured by a gas-liquid metal diffusion cell technique. The diffusion cell was formed by immersing an alumina tube containing hydrogen gas at 1 atm in a bath of stagnant liquid iron. The change in the composition of the melt in the cell was determined by measuring the rate of absorption of the gas in the cell. The appropriate solution to Fick&apos;s second law was used to examine the data and calculate diffusivi-ties. The absorption of hydrogen in stagnant pure liquid iron has been found to be diffusion-controlled. The results show that the chemical diffusion coefficient, D, of hydrogen in pure iron in the range of 1547" to 1726°C can be represented by the following Arrhenius relation: D(sq cnz per sec) = 3.2 x X exp(- 3300 i 1800/RT) where the uncertainty in the activation energy corresponds to the YO pct confidence level. Oxygen in the melt (above 0.015 pct 2) increased the apparent rate of absorption of hydrogen. The importance of diffusion data on liquid metals for predicting the rates of certain metallurgical processes has been recognized for a long time. Moreover, these data are much needed to test and develop theory for diffusion in liquid metals. Despite this practical and theoretical interest, however, relatively little reliable information about diffusion in liquid metals is available in the literature. This is particularly true for gas components such as hydrogen, oxygen, and nitrogen in liquid metals, where almost no data on chemical diffusion coefficients are to be found. This is probably due to a multitude of experimental difficulties particularly associated with high-temperature melts. In an effort to fill this gap in information, a research program was undertaken to study the diffusivities and rates of solution of gases in liquid metals. This paper presents the results of a study of the diffusion of hydrogen in liquid iron. EXPERIMENTAL METHOD Two methods for the study of the kinetics of dissolution of gases in liquid metals are being employed in this laboratory. Both involve the measurement of the volume of gas absorbed by the melt as a function of time and as such both avoid the uncertainties involved in chemical analyses of quenched samples for relatively small amounts of gas. In the first method, the gas dissolves in an inductively stirred melt and, in the absence of a slow surface reaction, the results are often interpreted in terms of mass transport across a liquid "boundary layer" between the homogeneous gas phase and well-stirred part of the melt. Other interpretations of the results of such experiments have also been described in the literature.1&apos;5 In the second method a gas-liquid metal diffusion cell is used.&apos; The gas dissolves in a cylindrical column of stagnant liquid metal and, in the absence of a slow surface reaction, the results are interpreted in terms of a non-steady-state diffusion solution to Fick&apos;s second law. The weakness of the first method is that while it gives information on the mechanism of absorption by stirred melts it yields an overall rate constant which even in the simplest cases depends on the nature and the thickness of the "mass transport layer" or "boundary layer". It yields no values of diffusion coefficients. The second method was used in this research because in many cases it is possible to determine the diffusion coefficient of the gas component in the liquid metal. In this research it has been utilized to measure diffusion coefficients of hydrogen in liquid iron. The apparatus used was essentially the same as that described by Mizikar, Grace, and par lee but certain modifications have been introduced to meet the elevated temperatures and special conditions of this research. Fig. 1 is a schematic drawing of the apparatus and Table I gives the identification of various parts in this figure. The diffusion cell, shown in detail in Fig. 2, was formed by immersing an impervious alumina tube (hereafter called absorption tube) in a bath of pure liquid iron contained in an alumina crucible. Two types of tubes were used, Morganite triangle RR and McDanel AP35. The crucible was contained in a vertical impervious alumina combustion tube (32 mm ID by 914 mm long) which was closed at both ends by water-cooled brass heads employing O-ring compression seals, Fig. 1. A protection tube enclosing a Pt, 5 pct Rh-Pt, 20 pct Rh thermocouple was introduced through the lower end of the combustion tube

Jan 1, 1968

By S. Floreen, H. W. Hayden

The effects of additions of iridium, rhodium, ruthenium, and platinum on the mechanical properties of Fe-C alloys were determined. Each alloying element significantly improved the toughness. The results support the general correlation that substitutional alloying elements that stabilize austenite are beneficial to toughness, but the reason for this improvement is not obvious at this time. The effects of substitutional alloying elements on the toughness of steel has long been a subject of both practical and theoretical interest. Despite the obvious importance of this subject, there has been little progress toward understanding the mechanisms by which alloying elements influence the fracture behavior. In some cases the deleterious effects of alloying elements have been shown to be due to mechanisms such as embrit-tlement of prior austenite grain boundaries or inhibition of cross slip in the ferrite lattice. In other cases, however, the reasons for the change in properties are not clear. This is particularly true for elements, such as nickel, that improve the resistance to brittle fracture. Several investigators&apos;-3 have pointed out that there is a correlation between an alloying element&apos;s phase diagram with iron and its effect on toughness. Those substitutional alloying elements that stabilize austenite generally are beneficial to toughness, while ferrite-stabilizing elements generally are detrimental to toughness. The word "generally" should be emphasized, because exceptions to this rule can be found. Nevertheless, this correlation does offer a starting point at which to try to understand the effects of alloying elements on toughness. Thus far only two austenite-stabilizing elements, manganese and nickel, have been considered. In order to test the validity of this correlation several other austenite-stabilizing elements were evaluated. The noble metals, iridium, rhodium, ruthenium, and platinum, have binary phase diagrams with iron similar to the Fe-Ni and Fe-Mn diagrams. That is, each element expands the austenite field, and also higher concentrations of each element produce martensitic transformations at low temperatures. Presumably then, each of these elements should improve the toughness of steel. The present study was conducted to determine if this were so. EXPERIMENTAL PROCEDURE The alloys were made as l-lb air-induction melts using electrolytic iron and commercially pure noble metals. Each heat was initially deoxidized by a carbon boil, and further carbon was added to attempt to produce a 0.05 wt pct C content in each alloy. Before pouring, a final refining addition of 0.2 wt pct A1 and 0.1 wt pct Ti was made to each heat. The alloys were cast in a copper mold to produce ingots approximately 1 in. in diam and 5 in. long. The chemical compositions of the alloys tested are given in Table I. The residual nitrogen, aluminum, and titanium contents were all relatively constant at 0.003, 0.03, and 0.02 pct, respectively. The carbon

Jan 1, 1968

By J. A. Roberson, Robert A. Rapp

From the observation of platinum wire marker movement in the oxidation of columbium at high lemperatures and low oxygen pressures, predonzinant cation diffusion in CbO, has been demonstrated. The Cu,0 molecule was used as an oxidizing species to study the nature of the porous scale and the location of the reduction site in the oxidation of colum-bium. The Cb205 scale contains microporosity and forms by alternate ionic diffusional growth and fracture. The oxidation of columbium at high temperatures and very low po, results in a relatively compact and protective Cb205 layer. THE observation of marker movements during oxidation is one means for the identification of the mobile ionic species in an oxide lattice. Previous marker experiments in the oxidation of columbium have all resulted in the markers being found on the outside surface of the Cbz05 scale. The Cr203 powder markers of Klopp et a1.,&apos; the gold film marker of Kofstad and ~jijllesdal,&apos; and the platinum wire marker of Cathcart et a1 .3 were found at the oxide/gas interface for oxidation temperatures ranging from 450" to 120O0C. However, in all experiments relatively high oxygen pressures were used. As discussed by Mrowec, even the interpretation of marker experiments in simple scales containing only one compound is not without ambiguities. In brief, it can be said that a marker may be found almost anywhere in the scale layer if the metal oxidizes by cation diffusion through the scale; the position of the marker depends upon morphological happenings in the scale. When considering marker movement in a polyphase scale one must proceed with extreme caution. For example, in the past (and present) work markers have never been found at the columbium-scale interface, and one might infer that the oxygen ion is mobile in CbO and CbO,. However, only trace quantities of CbO and CbOz have been present on any of the specimens, so no firm statement is justified on this basis. Despite previous experimental work, considerable doubt still exists concerning the role of the oxides CbO and CbOz in the oxidation of columbium. The identification of the mobile ionic species in CbO and CbOz from the observation of platinum wire markers was one goal of the present investigation . The linear kinetics of columbium oxidation at high temperatures (T - 1000°C) suggests that the Cbz05 scales which form on columbium are porous. From mercury absorption measurements on a Cbz05 scale formed at 500"C, Aylmore et al.&apos; reported a minimum volume fraction of connected voids equal to 0.15. While these scales often appear to be quite porous when viewed in metallographic cross section, they are so brittle that metallographic preparation is likely to exaggerate any porosity originally present. In this investigation, porosity developed during the oxidation of pure columbium and present at the high temperature was detected by oxidizing specimens in sealed evacuated capsules containing large compacts of mixed copper and CuzO powders. wooda has demonstrated that the CuzO, or (CuzO),, molecule is volatile and that oxygen is transferred by the CuzO molecule from a Cu/CuzO mixture to materials having a greater affinity for oxygen. For each molecule of CuzO that is reduced at a sink for oxygen, two atoms of copper are deposited. Quantitatively, essentially all of the oxidation carried out by a Cu-Cu20 compact results from a displacement reaction involving the CuzO molecule. When a metal which oxidizes to form a porous scale is exposed to the CuzO vapor, the CUZO molecules are reduced in the pores leaving a deposit of metallic copper to mark the site of the reduction. This technique has the rather unique advantage that any copper-coated pores found in the scale are unambiguously related to the reduction site in the growth of the scale under consideration. Pores or cracks which form in a msition*- external to the reduction site or which occur as a result of cooling or handling of the specimen will not exhibit the copper deposit. EXPERIMENTAL PROCEDURE Marker experiments were made on columbium metal, and on pellets of CbO which had been pressed and sintered. Platinum wire markers (0.001 and

Jan 1, 1968

By Emerson F. Heald

A systematic study was made of new and old data on chemical activities in Fe-Pt alloys at elevated ternperatuves. Experimental results may be expressed in terms of the excess free energy using Least-squares analysis of the data gave the following values for the constants: for the temperature range 1130° to 1350°C, and tentatively to 155O°C, B = -3.326564 and C = 0.221051; for the temperature range 650" to 850°C, B = -2.555690, C = 1.762735, and D =0.097196. In the study of iron-containing silicate systems, it is sometimes desirable to have a direct experimental measure of the activity of iron in the system. The well-known solubility of iron in platinum, often a headache in experimental work on iron compounds under reducing conditions, can be used to advantage in this respect. If the activity of iron in an Fe-Pt alloy in equilibrium with the silicate is known as a function of the composition of the alloy, chemical analysis of the alloy will give a knowledge of the activity of iron in all of the phases in the system. The present study was undertaken in order to elucidate the characteristics of Fe-Pt alloys as iron activity indicators. This work is intended to tie together some previous work, which may be summarized as follows. Larson and Chipman1 determined the activity of iron in Fe-Pt alloys at 1550°C by equilibrating platinum metal with calcium oxide-iron oxide-silica melts of known iron activity. Compositions of the resulting alloys were determined by chemical analysis. A similar study was carried out by Taylor and ~uan,&apos; who worked at 1300°C. They brought the Fe-Pt alloys into equilibrium with iron oxide under conditions of known partial pressure of oxygen, and thus, from the work of Darken and ~urr~,~ conditions of known iron activity. Compositions were determined indirectly, by following the change in weight of the sample. Sundaresen et el* used the electromotive force of cells in which the alloy formed one electrode in order to measure the activity of iron in the alloy at 650" and 850°C. These temperatures were chosen to be above and below the first-order phase transition which takes place upon the ordering of Fe3Pt and the second-order transition which occurs upon the ordering of FePt3. EXPERIMENTAL 1) High Temperatures. The starting materials used were thin platinum foil, about 0.002 mm thick, and Fisher Certified reagent ferric oxide, Fez03, which had been heated for 24 hr at 1000°C. An intimate mixture of 80-mesh Fez03 and platinum platelets was placed in a thin platinum foil envelope. The latter was suspended from thin platinum wires in the hot zone of a vertical-tube, platinum-wound furnace of the type described by Muan and ~sborn.~ A capillary gas mixer similar to that used by Darken and Gurry3 was used to prepare a precisely known mixture of carbon dioxide and hydrogen, which was allowed to flow upward through the furnace tube. The partial pressure of oxygen in contact with the sample was thereby fixed at a value which was calculated from the charts prepared by porter? Temperatures were measured with a Pt-10 pct Rh-in-platinum thermocouple, which was calibrated using the melting points of gold (1062 .@C) and diopside, CaMgSizOB (1391.5"C). Temperature control was maintained to within i3"C with a Geophysical Laboratory proportional controller, using the furnace resistance as the sensing element. Samples were quenched by passing a small current through the platinum suspension wires, allowing the sample to drop into a bath of dibutyl phthalate at the bottom of the furnace tube. Prior to chemical analysis the samples were washed with acetone and dried. 2) Chemical Analysis. It proved possible, in almost all cases, to separate the Pt-Fe platelets physically from particles of iron oxide. The platelets were dissolved in a small volume of aqua regia, evaporated to dryness, and redissolved to 0.1 M HC1. In order to determine iron in the platinum alloy potentiometrically, it is necessary first to remove the platinum. A 10-cm column of Amberlite IR-120 cation exchange resin in the hydrogen form provided separation quickly and quantitatively: The mixture of iron and platinum in 0.1 M HC1 was added to the top of the column, and washed with about 100 ml of 0.1 M HC1. Under these conditions, the iron, principally in the form of cations such as FeC1" and FeCl;, is held quantitatively in the uppermost centimeter of the column. The platinum, in the form of anions such as PtC&- , is washed through without being adsorbed. After a qualitative test with stannous chloride indicated all of the platinum was removed, the iron was

Jan 1, 1968

By K. Mukherjee

A quasi-thermodynamic calculation is presented for estirt~ating vacancy Parameters in fcc metals. For fcc metals the equilibrium vacancy concentration at the melting point can be approximated by a constant mole fraction. The Gibbs free energy of formation of the vacancies can then be expressed as a simple function of the absolute melting temperature alone. From this description the formation energy Ef, the vibrational entropy Sv, and the formation volume of a vacancy can be calculated in terms of known thermodynamic parameters. The calculated values are in good agree-rnent with available experimental results. IT appears that many of the physical parameters associated with lattice defects can be empirically related to thermodynamic melting parameters.&apos;-7 Besides the implicit correlations between melting phenomenon and point defects, the melting temperature itself at atmospheric pressure can be used as a reference temperature for the purpose of comparison of vacancy concentrations in a given crystal class. The concentration at the melting point then corresponds to the maximum vacancy super saturation in the crystalline state at a fixed pressure. For pure fcc metals such as Au, Cu, Al, Ag, Pb, and Pt the mole fraction of vacancies at the melting point8 is of the order of 10*"3 to 10"1. The equation expressing the equilibrium vacancy concentration at the melting point contains three parameters: the formation energy, the vibrational entropy, and the absolute melting temperature, see Eq. [2]. Since these three parameters cover a wide range of values8 in the above-mentioned metals, it can be assumed that in other fcc metals, for which no reliable data are available, the mole fraction of vacancies at the melting point most likely lies in the range 10~3 to lO"4. This is then the basis of the calculations described in this article. Within this range the mixing entropy can be linearized and the vibrational entropy, the formation energy, and the vacancy formation volume can be calculated in terms of known thermodynamic constants. 1} LINEARIZATION OF MIXING ENTROPY The Helmholtz free energy of a crystal containing n vacancies at the melting point can be writteng as where Ef, T,, k, and S, are the formation energy of a vacancy, the absolute melting temperature, Boltz-mann&apos;s constant, and the vacancy formation entropy, respectively. After applying Stirling&apos;s approximation in Eq. [l] and minimizing with respect to n where (n/N), is the equilibrium vacancy concentration in mole fraction at the melting temperature at 1 atm pressure. If instead of setting (6~/6n) = 0 immediately after Stirling&apos;s approximation in Eq. [I], the configurational partition function is simplified, then some useful and significant results can be obtained by utilizing the experimental inforrnation After applying Stirling&apos;s approximation and rearranging is plotted as a function of (n/N) in Fig. 1. The points, not all of which are shown, are fitted by a straight line substituting from Eq. [5] into Eq. [I] and minimizing with respect to n combining Eqs. [6] and [2] It must be emphasized that Eq. [7] is only a crude approximation based on an oversimplified model of

Jan 1, 1967

By C. A. Stickels

A heat of electrolytic iron, to whzch alunzinutn and nitrogen had been added, was hot-rolled, cold-rolled 90 pct, and recrystallized at temperatures from 500" to 700°C. Primary recrystallization textures appear to arise from competitive growth of two types of nuclei: 1) those having orientations belonging to the "usual" primary recrystallization texture found in riming steel, and 2) those with the {111} (110) ovientation. Development of a (111}(1 10) component in the primary recrystallization texture occurs only over a certain interval of isothermal recrystallizatzon temperatures when the material is supersaturated with respect to the precipitation of AlN. Lowering the degree of supersaturation depresses the temperature interval in which a (111)(110) component occurs. An elongated, &apos;pancake-shaped" recrystallized pain structure and a marked delay in the start of recrystallization were found in all specimens which were supersaturated with respect to A1N precipitation after cold work, regardless of their recrystallization texture. ONE of the consequences of killing low-carbon steel with aluminum is a significant change in recrystallization behavior. About 15 years ago, Solter and eatttiel showed that this behavior was largely controlled by aluminum and nitrogen in the steel. If complete precipitation of A1N was prevented before cold rolling, an increased "recrystallization temperature" was observed in subsequent. annealing, and the recrystal-lized grains were not equiaxed. Leslie et a1.2 studied this phenomenon in some detail and clearly demonstrated the relationship between A1N precipitation, recrystallization kinetics, and the development of "pancake-shaped" grains. It has also been known for some time that aluminum-killed steels, processed to produce elongated "pancake" grains, develop a (11 I}( 110) primary recrystallization texture. This texture has not been found in iron or low-carbon rimming steel as a primary texture4j5 but has been observed following grain growth in electrolytic iron.5 The present work was undertaken to study in more detail the effect of A1N supersaturation on recrystallization textures in iron. LITERATURE REVIEW The deformation texture in heavily rolled iron has been studied in detail by Bennewitz.~ The texture consists primarily of a partial fiber texture about a (110) axis in the rolling direction, designated here as fiber texture A. It includes the range of orienta- tions (111)[110] - (001)[ 110] - (11l)[110]. A weak secondary texture also is present.6 This is a duplex partial fiber texture about two (110) fiber axes located 60 deg from the rolling direction and 30 deg from the sheet normal. The range of this texture, designated here as fiber texture B, about the [101} fiber axis is (112)[110] - near (545)[252] - (211:1[011] *The range given here follows Bennewit~.~ A few pole figures from re-crystallized material indicate a broader range than this.&apos; However, the components which are strongest in the recrystallization texture are in this range.&apos;________________________________________________________ Primary recrystallization textures in unkilled steels can be accounted for by growth of members of fiber texture B present in the deformed metal.5 However, while members of fiber texture B dominate the primary texture, other orientations survive primary recrystallization as well. In particular, some {111}(110) members of fiber texture A must also grow during primary recrystallization, because a well-defined {1ll)( 110) texture develops during subsequent grain growth at 700°C.5 The unusual recrystallization behavior of deformed supersaturated solid solutions has been attributed to: 1) retention of the solute in solution,&apos; 2) formation of coherent, preprecipitation solute clusters prior to and during re~r~stallization,~ and 3) formation of a precipitate prior to and concurrent with recrystallization.&apos;~-&apos;~ When aluminum is supersaturated with iron, the difference in grain boundary mobility between general high-angle boundaries and certain special coincidence site boundaries is apparently eliminated.&apos; In aluminum-killed steels, precipitation of A1N can take place at ordinary subcritical recrystallization temperatures. The rate of precipitation increases with increasing aluminum or nitrogen contents.2&apos;13 There is some doubt, however, as to whether true precipitates form during the time at temperature needed to complete recrystallization. Leslie ef a1.2 found that precipitation in one steel was complete after about 100 min at 700GC, or after about 1000 min at 650GC, as measured by chemical analysis for AlN. Aoki et a1.,13 using internal friction for dissolved nitrogen, showed that a large fraction of the dissolved nitrogen was removed from solution within a few minutes annealing time at temperatures from 400" to 800°C. However , the rate of formation of AlN, as detected bv chemical analvsis. was much slower than the apparent rate of nitrogen removal. Hasebe,&apos;~~ using carbon extraction replicas, has identified A1N precipitates by electron diffraction in a 0.2 C steel, solution-treated at 1300°C and annealed 2 hr at 700°C. Borchers and kim,I6 also using a replication technique, observed precipitates after annealing treatments as short as 2 min at 640°C. However, Leslie et a1.&apos; state that no A1N precipitate can be seen while recrystallization is being inhibited in aluminum-killed steel.

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968