Search Documents

By D. Cox, M. J. Duggin, L. Zwell

The carbides of approximate composition and Mn have been studied using X-ray diffraction techniques. Those carbides of the type (Fe,Aln)zC ave isostructural with cementite. The cell pararmeters a and c have minimum values at approximately 10 at. pd substitution of manganese for iron; no satisfactory explanation has yet been found for this phenomenon. The carbide fFeMn4)C has a monoclinic unit cell whose dimensions are close to those of ,11,15Cz A neu-troip-dij~ractiot~ study of (F'eAlrz4)C~ reveals that, like MnsCZ, it is isostructural with Pd5Bz. The iron and manganese atoms occupy the palladium atom sites, while the carbon atoms were found to have the same atomic coordinates as the hovon atoms. A neutrorr-diffraction study of indicates that the carbon-atom positions are very close to those occupied in (Fez.,ll/lr~,.3)C. In both carbides studied, tlre iron and manganese atomzs were found to be essentially randomly distributed, although, in the case of (Fe,.811fn1.2)C, it is possible that there may be a slight preference of manganese atoms for- the general (d) positions and a corresponding slight preference of iron atoms for the special (c) positions. It has been found that a complete range of solid solution exists between Fe3C and Mn3C at 1050°C,I although Mn3C becomes unstable when the temperature is reduced to 95O0C,' and can only be retained by rapid quenching. It is also known that a complete range of solid solution exists from Fe5Cz to M~SC~,~ although the stability range of carbides of the type (Fe,Mn)sCz as a function of the relative proportions of iron and manganese is not known. X-ray examinations of Oh-man's carbide3 and Spiegeleisenkristall,~ which have the approximate compositions (Fe3.67Mnl.33)C2 and (Fe3-,Mn,)C, where x lies between 0.4 and 1, respectively, have been made. The following carbides have also been studied: ] The lattice parameters determined during these investigations are listed in Table I. It is seen that carbides of the type (Fe,Mn)sCz have a monoclinic unit cell while carbides of the type (Fe,Mn)3C have an orthorhombic unit cell. It is evident that the variation of lattice parameters with manganese content is not linear for carbides of the type (Fe,Mn)3C. The coordinates of the atoms in (Fe2.7Mno.3)C have recently been determined by single-crystal analysis., The fractional atomic coordinates have been shown by Fasiska and jeffrey to be in good agreement withj those deduced from an earlier analysis of Fe3C by Lipson and etch.' However, it was impossible to determine whether iron and manganese atoms occupied ordered positions because of the small difference between the atomic scattering factors of iron and manganese. The atomic positions in Mn5Cz (Refs. 8 and 9) and Fe5C2 (Refs. 7 and 8) have been obtained only by comparisons made with the isostructural compounds P~SB~.' Since X-ray diffraction techniques were used in these investigations, accurate positioning of the carbon atoms, which have a low atomic scattering factor, was difficult. No attempt has been made to determine the atomic positions in the other carbides previously studied. It was felt that an investigation of the lattice parameters of a number of intermediate carbides of the types (Fe,Mn)sCZ and (Fe,Mn)& would be of interest. It seemed likely that a neutron-diffract ion study of such carbides would indicate whether ordering occurred between the iron and manganese atoms because of the large difference between the neutron-scattering cross sections of iron and manganese. It also seemed probable that such an investigation would provide a determination of the atomic coordinates of the carbon atoms. I) EXPERIMENTAL DETAILS Specimens, each weighing approximately 20 g, were carefully prepared according to the following proportions: The components were 500-mesh powders of 99.995 pct purity iron and spectroscopically pure carbon and a 200-mesh powder of 99.995 pct purity manganese. The component powders were intimately mixed by prolonged shaking, then each specimen was inserted into a spot-welded cylindrical container of tantalum foil, whose end was closed but not sealed. Each specimen in its envelope was then sintered at 1050° C for 24 hr in a thin-walled evacuated quartz capsule, such a time having been previously found sufficient for equilibrium to be attained.' Each specimen was then quenched in order to attempt to retain the high-temperature phase, as the literature indicates that transformations may occur on cooling. Debye-Scherrer X-ray photographs were taken of each specimen using a 114.6-mm-diam camera, Fig. 1, patterns 2 to 6. The exposure time was 6 hr using filtered iron radiation at a tube voltage of 40 kv and a tube current of 12 ma.

Jan 1, 1967

By J. D. Embury, R. M. Fisher, A. S. Keh

An investigation of the defect structure and properties following large strain deformation has been carried out using transmission electron microscopy and mechanical testing for a range of ferrous materials and for copper. It is shown that, for a variety of ferrous materials, a cellular substructure is developed during the initial stages of working and on further deformation the dimensions of this substructure are reduced. Quantitative measurements of the flow stress and the scale of the substructure indicate that the strength of heavily worked materials is largely determined by the spacing of cell walls. These cell walls act as dislocation barriers in a manner analogous to grain boundaries. FCC materials do not harden as extensively as bcc after cold working and the present observations on copper indicate that the dimensions of the substructure in fcc materials are not markedly reduced on deformation. The differences between the fcc and bcc structures produced by large plastic strains are ascribed to differences in the extent of dynamic recovery. It is tentatively proposed that the greater stability of substructural barriers in bcc structures results from strong interstitial Pinning effects. It is proposed that for large plastic strains the work-hardening process may be considered in terms of the reduction of substructural-barrier spacing during the working process. This pvovides a simplified hut useful analysis of the strain hardening occurring during mechanical processes. THE mechanisms of strain-hardening processes have occupied the attention of numerous investigators over the past three decades and a multitude of theories have emerged in this field. The majority of previous work has been concerned with the development of a description of the plastic behavior of single crystals in terms of dislocation theory.'" In contrast, scant attention has been given to the strengthening mechanisms operative during mechanical working processes such as rolling and drawing. The large plastic strains involved in these processes make it difficult to correlate the observations with any elementary dislocation theory. Further, as Bullen and coworkers3 have opined, for large plastic strains both hardening and recovery occur simultaneously and thus it is extremely difficult to estimate the effect of plastic strain on the ambient internal stress field. It is probable that for large plas- tic strains any theoretical estimate of the internal stress field must be made in terms of complex dislocation groups. Although some valuable theoretical work has been done toward calculating the elastic properties of dislocation groups4 any detailed self-consistent model for large plastic strain is as yet impossible. With these limitations in view it is still of value to examine the mechanical properties of highly strained materials as a function of their substructure. This relationship is explored in the present communication for a variety of materials subjected to rolling, drawing, or swaging. The primary object of this investigation has been to establish the validity and the limitations of the substructural strengthening mechanism proposed by Embury and eisher' for drawn pearlitic wire and by Meieran and Thomas for drawn tungsten wire. No attempt has been made to delineate the basic interaction mechanism which occurs between a slip dislocation and the substructure and the authors believe that a great deal more experimental evidence must be compiled before these fundamental aspects can be explored. Also, no specific attention has been given to the detailed formation of substructure during working. Experimental Details. A variety of materials were used in this investigation, the compositions and heat treatment of which are tabulated in Table I. The commercially pure iron is referred to throughout this report as Ferrovac E. The mechanical working processes were all performed at room temperature. The wire drawing was performed on a manual drawing bench. Reductions of between 10 and 20 pct in area per pass were used in both swaging and drawing. The experimental parameter used to evaluate the mechanical properties of the materials was the 0.2 pct proof stress. This was determined for wire samples using an Instron tensile machine at a crosshead speed of 0.02 in. per min. The techniques for preparation of samples for transmission electron microscopy have been described previo~sl~.~ Specimens from wire samples were prepared from longitudinal sections and in some cases from transverse sections. To evaluate the substructural characteristics of rolled materials, thin foil samples were prepared of both the face and edge sections. Results. One of the more familiar ways of expressing work hardening in mechanical working is by the flow stress as a function of reduction in cross-sectional area. Fig. 1 shows such a plot for Ferrovac E eutectoid carbon steel and for copper. The curve for Ferrovac E is characterized by an initial stage of rapid work hardening and a final stage of rapid work hardening separated by an intermediate stage with a low rate of work hardening. This behavior is typical of many ferrous materials and the drawn pearlite wire previously investigated by Embury and Fisher is a more pronounced example. Copper shows an initial

Jan 1, 1967

By Harry C. Gatos, Frank J. Bachner

It was shown through high-pressure experiments that tin loss by volatilizatim is necessary for the degrada-tion of the superconducting transition temperature of Nb,Sn associated with high-temperature annealing. Crystallochemical analysis of the degraded Nb3Sn showed that it constitutes a new phase with ordered niobium-site vacancies, created by the migration of niobium atoms to vaccnt tin sites. This new phase was found to form when 4 pct Nb-site vacancies were present. It has a transition temperature of 6'K and a lattice parameter of 5.283A. A similar degradation effect was observed in Nb,Al. Its superconducting transition temperature dropped from 16.5" to 8" K following a high-temperature annealing. The superconducting temperature degradation in these 0-tungsten structure compounds is attributed to the disruption of the interchain d bonding by the periodic interruption of the niobium atom chains. By annealing the degraded Nb, Sn at 1000 C in nitrogen its normal superconducting behavior is restored most likely due to the incorporation of nitrogen atoms causing the elimination of the ordered vacancies. HANAK et al.' have observed low superconducting transition-temperature values (T, - 9"K) in some NbsSn samples deposited from the vapor phase. They attributed such low T, values to disorder in the 0-tung-sten structure. Much lower T values (down to 5.6"K) were reported by Reed et al.zC for NbsSn samples annealed at high temperatures. These authors also attributed this degradation effect to disorder (random occupation of the A and B sites by niobium and tin) but pointed out that such disorder could be brought about (by high-temperature treatment) only in samples containing niobium in excess of the stoichiometric composition NbsSn. Both groups reported that the normal superconductivity behavior could be rever-sibly restored by appropriate heat treatment. Courtney et al., also found that degradation in NbsSn requires excess niobium brought about by the loss of tin during the treatment. However, these investigators proposed that the degradation is due to niobium-site vacancies resulting from the migration of the niobium atoms to the vacated tin atom sites. They did not consider the reversibility of the effect. The present study attempts to establish the nature of the above degradation phenomenon. EXPERIMENTAL PROCEDURES All compounds prepared for this investigation were made from the powders or filings of the elements which were intimately mixed, cold-pressed into a cylindrical pellet at approximately 50,000 lb per sq in., and then submitted to the desired heat treatment. The samples annealed under high pressure were placed in a MgO sample container which was mounted in a pyrophyllite tetrahedron designed for a tetra-hedral-anvil press. Details of the experimental arrangement are given elsewhere. This setup allowed heating at 1800°C or above under pressures in excess of 30kbars for 3 hr. The samples annealed in a vacuum were prepared in a high-temperature vacuum furnace which could reach temperatures up to 2400°C under a pressure of 2 x lo-' Torr. For annealing in a reactive atmosphere, a quartz tube was placed in a clamshell furnace and the desired gas ambient passed through the tube. Lattice parameters were determined using a Debye-Scherer 114.6-mm camera. Cohen's method, programmed for the IBM 7094 computer, was used to calculate the lattice parameter from the measured d spacings. X-ray integrated intensity measurements were made on several samples. These samples were ground to -400 mesh and the powder mixed with a solution of collodion in amyl acetate. The mixture was poured into a depression milled in a bakelite disc. When the mixture dried, the surface of the disc was ground flat leaving a diffraction surface defined by the face of the disc. The disc was mounted in a Philips rotating specimen holder which allowed the rotation of the sample in the plane of the diffraction surface and the integrated intensity measured using a scintillation counter and a pulse-height analysis sys-tem. The superconducting transition temperatures were determined by means of self-inductance techniques.' EXPERIMENTAL RESULTS AND DISCUSSION The Role of Tin Loss in the Degradation of Super-conductivity. The loss of tin during high-temperature annealing can be effectively suppressed by annealing under high hydrostatic pressures. Accordingly, a series of experiments were performed under pressures of approximately 30kbars. This pressure was the minimum under which high-temperature experiments could be safely performed in the particular pressure apparatus employed. Experiments were also designed to test high-pressure effects on the superconductivity behavior of NbJSn. The results of the high-pressure annealing experi-ments are summarized in Table I. All samples were prepared as described earlier. They were reacted and homogenized at 1000°C for 24 hr under argon at-

Jan 1, 1967

By N. A. Gjostein

The formal descnption of the decay of an isolated scratch can be written in terms of an appropriate Fourier integral. With the application of certain approximations, this description leads to the second-moment analysis developed by King and Mullins. It is shown that the second-moment analysis does not adequately describe the behavior of a decaying, isolated scratch, and that it is difficult to obtain internally consistent values of the surface self-diffusion coefficient, D,,from this analysis. This inconsistency arises from contributions of higher-order moments to the decay process. Two new analytical methods, based on the Fourier integval representation of a scratch profile, have been developed for determining values of D, from the decay kinetics of isolated scratches. In the profile-matching method, a given initial profile is resolved into its Fourier components, the components are allowed to decay exponentially over an annealing time interval, At, and finally they are synthesized to form a decayed profile. The predicted profile is adjusted to fit the experimental profile by varying only the parameter, D,At; the contribution from volume diffusion is directly taken into account and the integrals involved in the Fourier analysis are evaluated by numerical integration on an electronic computer. In the kinetic method, the widths, W, of a series of predicted profiles are determined for various volume-diffusion contributions, and the results are plotted in the form W vs DSAt. For a fixed ratio of surface to volume diffusivities, R, these plots are linear; the slope of the lines increases as R decreases. A simi-lar analysis can be performed on the depths of the predicted profiles. In this case, plots of (l/df3 vs D,At are found to be nonlinear. The proper value of Ds is found by superimposing the data for the experimental widths and depths on Plots of this kind and adjusting Ds until a fit is obtained with the line having the appropriate value oj R. An analysis of the slopes of these plots for R —= (surface diffusion only) reveals that they do not give the correct value, 2276, for width tf second-moment standard profile. This finding allows one to modify the second-moment analysis in such a way as to obtain internally consistent values of Ds. ThERE are several processes, involving a flow of matter along a surface, due to gradients in curvature of the surface, that may be used to determine the surface self-diffusion coefficient, Ds. These processes are commonly known as 1) thermal grooving, 2) single and 3) multiple scratch decay, 4) blunting of field-emitter tips, and 5) sintering. In this series of papers, the first three of these processes are examined in detail in an attempt to subject the phenomenological theories governing these processes to a critical test and, furthermore, to make a critical comparison of the values of D, obtained from these techniques. Although the thermal grooving technique has been established'' as a reliable method for determining D, , this has not been the case for the process of scratch flattening. Mullins and coworkers374 have proposed phenomenological laws governing the growth of the width and the decay of the amplitude of an isolated scratch, but only in one study5 has the width-growth law been supported by experimental evidence. In paper I of this series detailed experimental evidence is presented that points up the deficiencies of the second-moment analysis; the origins of these deficiencies are also discussed. Following this development, some new analytical procedures, based on representing the scratch profile by Fourier integrals, are presented as a means of obtaining reliable values of D, from the kinetics of the scratch-flattening process. Further applications of the Fourier integral approach are reported in papers 11' and 111,~ where the method has been useful in interpreting the anisotropy of flattening rates of isolated scratches (paper 11) and in describing the multiple scratch decay process (paper 111). THEORY OF SCRATCH DECAY Following ~ullins" approach we consider an arbitrarily shaped scratch profile, Fig. 6, at some time, t. The profile is designated by a function z(x,t) which can be expressed in terms of a Fourier integral as follows:

Jan 1, 1967

By P. G. Shewmon, H. E. Collins

A study has been made to determine the sites at which sulfur adsorption occurs on copper surfaces. measurements were made of the relative torques, Ys, at the intersection of twin boundaries with surfaces near the three low-index orientations, i.e., (100), @lo), and 011), over a range of H2S/H2 ratios. HZS concerztvations j'ro~n 3 to 1500pp)n between 830" and 1050°C were used. It is concluded that sulfur adsorption occurved preferentially though not exclusively at edge sites near the (100) and (110) surfaces in the HzS range — 700 Ppm giving rise to negative torques near these orientations. Beyond this HzS range, adsorption occurred at all sites. Near the (111) surface, 7/y little with HzS concentration up to approxiwzately 75pptn. Above this range, the results indicate adsorption is occurring OH both terrace and edge sites. SCIENTIFIC interest in surfaces and their interactions with a gaseous environment dates back to the beginning of the 19th century. The scientific luminaries of that period—Faraday, Maxwell, Rayleigh, Dewar, and Gibbs—were already concerned about such processes. However, it has only been within the past several decades that adsorption on metal surfaces has been actively studied. This increased interest in adsorption has been brought about by the advent of new and improved experimental techniques and apparatus, e.g., ultrahigh vacuum, and field-emission and ion microscopes. However, most of the work done using these techniques has been carried out at low temperatures. When adsorption studies have been made at either low or high temperatures, they usually gave no indication of the particular surface orientations or type of sites on which adsorption was occurring. In the last few years, there have been a series of studies in which the surface tension, y,, and/or its derivative with respect to orientation, 7, have been studied as a function of orientation and atmosphere.'-7 Nearly all of the work on the relative torque,* ~/y, silver annealed in hydrogen and air.6 Recently Winterbottom and Gjostein" have used a modified and more accurate Mykurian method to determine the y plot of gold in hydrogen The only work in which T/~, has been measured over a range of chemical potentials for a given solute, p2, is that of Robertson and shewmon7 on the Cu-0 system. They measured T/Y, vs Po, (10"" to 10- l3 atm) at 1000°C in various mixtures of Hz0 and HZ. From this work they estimated the value of p2 at which one half of the surface sites are occupied with oxygen, pg, as being in the range 10- l6 to 10- l5 atm of oxygen. They also found that increasing Pa increased the magnitude of ~/y, near the (111) and (100) orientations. This indicates that oxygen is not adsorbed preferentially at step edges, but uniformly over all surface sites. In addition, they did one experiment on sulfur adsorption on copper surfaces, which indicated that sulfur adsorption decreases ~/y, near the (100) orientation, while not affecting ~/y, near the (111). This could be interpreted as indicating that sulfur adsorbs preferentially at step edges near the (100). In this paper the primary objective of the work has been to carry out a study of sulfur adsorption on copper surfaces over a range of temperatures and p,. In conjunction with this work, thermal grooving at grain boundaries has been examined as a method of determining the effect of sulfur adsorption on y,. METHODS Ideally, one would like to have information on the quantity of solute adsorbed on a surface and the types of sites at which it is absorbed as a function of p2. The total quantity adsorbed or the surface excess is given by the thermodynamic equation Thus data on the variation of y, with pz indicates the value of p2 at which adsorption becomes appreciable and the quantity adsorbed. The type of adsorption site is more difficult to deduce but information on this can be obtained from the variation of rz with 8, the angular deviation of the surface orientation. This is obtained from the thermodynamic equationlg Data on t and ys as functions of p2 have been obtained by the following methods. 1) Twin Boundary Grooving—By determining the effect of adsorption on the torque, 7, where T is the variation of surface energy, y,, with orientation, it is possible to obtain some indication as to the preferred sites of adsorption. Experimentally, the torque value measured is the relative torque, 7/ys The twin boundary grooving technique suggested by Mykura'' was used in this study to determine near the three low-index orientations— (loo), (110), and (111). Mykura's equation relates 7 /yS to measurements of the di-

Jan 1, 1967

By Robert Maes, Robert de Strycker

The Cu-Sn-As systeM was studied in the region near the Cu-42 and (214-As binary diagrams, where reactions in the solid state appear, resulting from the decomposition of the y(Cu-Sn) phase and from the formation of the 7 phase (Cu,As). The techniques used were microscopic observation, thermal analysis by dilatometry, and X-vay diffraction. The formation of the 7 phase gives rise to a ternavy pevitectoid veaction; the decomposition of the y phase gives rise to five transitional reactions. The temperatures of almost all these reactions could be determined; in the most favorable cases , the accuracy of this determination was of 11.5-C. The 7 phase is stabilized by tin additions, the arsenic atoms being replaced by tin atoms up to 35 pct; this has allowed the preparation of pure j) phase and the confirmation, by extrapolation, of the conrposition of this compound in the Cu-As diagram. In the first part of this work, the solidification reactions in the Cu-Sn-As phase diagram were studied. In the copper corner, the structure of the alloys presented the evidence of reactions in the solid state: on the one hand, all the alloys containing the y phase of the Cu-Sn diagram showed, under the microscope, that this phase had formed different decomposition products after complete solidification; on the other hand, the appearance of the 7 phase of the Cu-As diagram necessitated the introduction of a peritectoid formation reaction. The study of the decomposition of the y phase has been done by preparing about forty alloys that were homogeneous y at high temperature. The formation of the 7 phase has been studied by means of a few alloys with a composition near the homogeneity field of this phase at room temperature. The part of the Cu-Sn phase diagram of interest for this study is represented by Fig. 1, with the phase designation which will be used in the remainder of this paper; it is drawn after Hansen and Anderko.' The Cu-As diagram has already been presented in Part I of this work; the significant features of this study are the existence of the arsenides CusAs and Cu5Asz, and the formation of a compound CUEAS, designated as the 7 phase, by a peritectoid reaction at about 325°C. EXPERIMENTAL METHODS The fundamental technique for the investigation of this part of the Cu-Sn-As constitution diagram was microscopic observation; the greatest part of the observed alloys has also been subjected to thermal analysis by dilatometry; a few selected alloys have then undergone an X-ray analysis by powder diffraction. Alloy Preparation. The alloys were prepared from the same products as in Part I of this study: cathode copper, arsenic with a purity better than 99.5, and tin with a purity of 99.98. The fusion of the ternary alloys was realized from

Jan 1, 1967

By P. G. Shewmon, H. E. Collins

We have studied the effect of adsorbed sulfur on the surface self-diffusion of copper using eight diflerent surface orientations and the grain boundary grooving method. The eight orientations studied were the four lying near the low-index surfaces—(loo), (Ill), and two directions in the (110)-plus four higher-index surfaces. Surface-diffusion measurements were made over a range of HZS concentrations (in Hz) from 3 to 1500 ppm between 830°and 1050°C. The results can be divided into two groups—Group 1 contains the two (110) surfaces while Group 2 contains the remaining six surfaces. In Group 1, increasing the temperature increases the effect of Hz S on DS for the Hz S range 5700 ppvn. Qs and Do increase with increasing H2S concentration in this Hz S range. Beyond this range, increasing the temperature decreases this effect on D,; also Q, and Do decrease. In Group 2, increasing the telnperature decreases the effect of H2 S on D, for the H2S range studied, and Qs and Do decrease with increasing Hz S concentration. In any study of surface phenomena, there invariably arises the question of the possible presence of and effect of adsorbed impurities. Such questions are well-founded since the presence of adsorbed atoms can sometimes produce marked changes in the kinetics of surface-energy-driven processes. In the last few years, values of the surface self-diffusion coefficient, D,, have been determined on a variety of metals by studying the decay of scratches or the growth of grain boundary grooves.L~3-L0~L3 Yet there has been relatively little work done in which the concentration of an adsorbed impurity was systematically varied and the effects observed. Work of this sort would provide some basis in fact for the assertions often made about the ro1.e of adsorbed impurities in the differences between the results of different workers in different atmospheres and on different metals. It also is relevant to those cases in which surface monolayers produce profound effects in commercially important processes. The most marked example of such effects is the ability of nickel or palladium to increase the sintering rate of tungsten by many orders of magnitude.' The aim of this work was to study the effect of sulfur partial pressures on the surface self-diffusion of copper. It was felt that this in conjunction with a study of the degree of adsorption and type of active sites involvedL8 would provide a wide range of data for one system and hopefully lead to some insight into the mechanism by which sulfur adsorption influences copper diffusion. The main reasons for choosing the Cu-S system were, first, faceting was reported not to accompany the adsorption of sulfur. This is required if our experimental technique is to work. Second, Oudar has determined a high temperature adsorption isotherm for this system, an event which puts the Cu-S system almost in a class by itself.I4 EXPERIMENTAL PROCEDURE Initially, we considered studying the effect of an adsorbed impurity on surface self-diffusion of copper using isolated (or single) scratch smoothing as the technique and oxygen as the impurity. Copper was chosen as the material because the effects of orientation and anisotropy of the surface self-diffusion coefficient, D,, of copper in a dry hydrogen atmosphere had been studied extensively by Gjostein' and by Shewmon and ~hoi.~,~ The isolated scratch technique was chosen because both the effects of surface orientation and anisotropy of D, in a given surface could be easily studied with this method.~ Oxygen was tried as the impurity because Robertson and Shewmon""~ had studied its adsorption on copper at 1000°C over the range of oxygen partial pressures of 10"22 to 10-l3 atm. After several preliminary runs, it became evident that neither the scratch technique nor the impurity oxygen would be satisfactory for this work. Scratching deforms an annealed surface so that the region near the scratches recrystallizes, thereby disrupting the scratch profiles. One can avoid this by deforming the specimen sufficiently before scratching to give complete recrystallization on subsequent heating.4 However, as a result of Gjostein's success in scratching and annealing undeformed gold single crystals without local recrystallization,13 we attempted something similar with copper single crystals using a 0.7-mil diamond phonograph needle mounted in a Tukon hardness tester. All specimens recrystallized upon being annealed. Also, some copper specimens were sent to Gjostein to be scratched using his technique. The results were the same. As a result, the scratch technique was dropped in favor of the grooving of symmetric grain boundaries. Preliminary work using oxygen showed that faceting began to occur before oxygen adsorption had any measurable effect on D, at 938°C (at Pbo/P, = 0.12). Since heavy faceting would interfere with the measurement, we decided to use a sulfur-containing atmosphere (H2S/H2). Work by Oudar and Benard' and Robertson" showed that sulfur absorbed on copper and that faceting was not observed.

Jan 1, 1967

By Richard R. Zupp, David A. Stevenson

An experimental method to determine the carbon activity in various solid solutions was developed. Samples of the solid solutions and an Fe-C reference sample were equilibrated with respect to carbon content by annealing them in a Hz-CHI gas mixture in a closed cell. The carbon content of each sample was determined, and the carbon activity was obtained from the carbon content of' the reference sample and well-established data for the dependence of the carbon activity on the carbon content in Fe-C alloys. The influence of vanadium on the activity of carbon in austenitic Fe-C-V alloys at 1000°C was determined by this technique. A general semiempirical correlation was developed to describe the dependence of the activity coefficient of- carbon on the composition of ternary austenitic iron-base alloys containing interstitial carbon and a substitutional solute. The correlation is particularly useful in predicting the partitioning of- carbon between various alloys. THE influence of substitutional solutes on the activity of interstitial solutes in metallic solid solutions is important in the theory of alloy phases. Solid solutions of particular interest are the fcc austenite phases of ternary Fe-C-Z systems, in which carbon is the interstitial solute and Z represents any substitutional solute. Carbon-activity data are also needed in these solid solutions to solve practical problems; the quantitative treatment of diffusion-controlled transformations' is an examvle. Experimental information is available for ternary austenitic solid solutions containing Mn,2 Si,2 and A16 as the substitutional solute. Because qualitative preliminary studies indicated that vanadium appreciably decreases the carbon activity,14 the present investigation was undertaken to determine the influence of vanadium on the activity of carbon in austenite. Although Flender and ever" measured carbon activity over a range of compositions in the Fe-C-V system, they were primarily interested in determining phase boundaries in the ternary system, so most of their measurements were outside the composition range for stability of single-phase austenite. Petrova and Shvartsman' also made limited measurements of the carbon activity in Fe-C-V alloys. The dependence of the carbon activity on the carbon content of an alloy may be determined by passing COCOz or H2-CH4 gas mixtures of carefully measured composition over the alloys, determining their equilibrium carbon content, and utilizing the relevant equilibrium relationships. smith16 used this technique with both CO-COZ and HZ-CH4 gas mixtures to determine the dependence of carbon activity on carbon content in pure Fe-C alloys. His data, which are in good agreement with those of some previous and subsequent investigators,6'17 but not with those of others,lfl'ao are usually considered to be the most reliable. Although the same method can be applied to Fe-C-Z alloys, it is difficult experimentally, because the appropriate gas mixtures are almost pure CO or Hz. A simpler technique is to simultaneously equilibrate the Fe-C-Z alloys and pure Fe-C alloys with the gas mixtures, and then use Smith's data to determine the carbon activity in the pure Fe-C alloy. A number of investigators have employed this technique. others Have used the partitioning of carbon at the interface of a diffusion couple prepared from an Fe-C alloy and a Fe-C-Z alloy. In the present study, a closed-cell method was developed by which carbon was selectively transferred via a gas medium between pure Fe-C alloys and Fe-C-V alloys which were not in physical contact. A similar method was developed independently by Heckler and winchel14 and used to study the Fe-C-Ni system. EXPERIMENTAL METHOD A schematic diagram of the experimental arrangement is shown in Fig. 1. In a typical experiment, a 5-g Fe-C sample was placed in one compartment of a quartz cell, and a 5-g Fe-V sample was placed in each of the other compartments. The cell was evacuated, outgassed, backfilled with approximately 125 Torr of hydrogen, and sealed. After being placed in a fur-

Jan 1, 1967

By Robert K. Steunenberg, Irving Johnson, James B. Knighton

The activity coefficient of plutonium in liquid magnesium, over the temperature range 650° to 800°C, was obtained from measurements of the distribution of plutoninm between a 50 mole pct MgC12-30 mole pct NaCl-20 mole pct KC1 molten-salt mixture and liquid Zn-Mg alloys. For dilute solutions (0.08 at. pct Pu) the activity coefficient of plutonium was found to vary from 10.1 at 650°C to 12.2 at 800°C. The activity coefficients of plutonium in dilute liquid solutions of plutonium in uranium, silver, lanthanum. cerium, and calcium were estimated to be. The distribution data indicate a value of about 0.1 at 800°C for the activity coefficient of PuCl3 dissolved in the above ternary salt mixture. LIQUID magnesium and several liquid alloys of magnesium with metals such as zinc and cadmium have been shown to be useful solvents in pyrochemical processes for the recovery of uranium and plutonium from discharged nuclear fuels,' and for the separation of transuranium elements.' The present study was undertaken to determine the activity coefficient of plutonium in liquid Pu-Mg alloys in support of process-development work. The activity coefficient of plutonium in liquid magnesium was determined from experimental data on the distribution of plutonium between a liquid ternary MgC12-NaC1-KC1 salt mixture and various liquid Zn-Mg alloys. The distribution data were used to calculate the ratio of the activity coefficients of plutonium in liquid zinc and in liquid magnesium. The activity coefficient of plutonium in liquid magnesium was then computed from the known activity coefficient of plutonium in liquid zinc. It was not necessary to know the thermodynamic properties of the molten-salt system explicitly. The major features of the Pu-Mg system have been reported by Schonfeld.3 At the temperatures of interest in the present study, i.e., above about 600°C, the phase diagram indicates the existence of a wide liquid-miscibility gap, with the plutonium-rich liquid containing about 8 at. pct Mg and the magnesium-rich liquid containing about 10 at. pct Pu at the intersection with the solidus regions. Additional data on the compositions of the two equilibrium liquid phases obtained in this laboratory4 have defined the miscibility gap up to the consolute temperature (at about 1040°C). EXPERIMENTAL PROCEDURE AND RESULTS Materials. The 50 mole pct MgC12-30 mole pct NaC1-20 mole pct KC1 salt mixture was prepared by melting the required proportions of reagent-grade NaCl and KC1 with anhydrous MgC12. The molten salt was then purified by contacting it with liquid Cd-30 wt pct Mg alloy (at 450°C) to reduce oxidizing impurities, followed by filtration through a stainless-steel frit (pore size, 65 µ) to remove solid MgO formed during the reduction. The purity specifications of the zinc, magnesium, and plutonium were 99.999, 99.8, and 99.85 pct, respectively. Apparatus. The liquid salt and metal were contained in a tantalum crucible inside a graphite secondary vessel. The crucible assembly was located inside a resistance-heated stainless-steel furnace tube. The furnace tube was closed by means of a stainless-steel cover, which was attached by bolts, with a neoprene O-ring serving as a gas-tight seal. The top of the furnace tube was water-cooled to protect the O-ring. The furnace-tube cover was provided with a tantalum thermowell, a tantalum stirrer, and a port through which sampling tubes could be inserted and materials could be added to the melt without admitting air to the furnace tube. Vacuum and an argon atmosphere were available through a side-arm on the furnace tube. The furnace temperature was regulated by a proportional controller that was actuated by a chromel-alumel thermocouple between the furnace tube and the heating elements of the furnace. The melt temperature was measured by means of a chromel-alumel thermocouple in the tantalum thermowell. The accuracy of temperature measurement was ±3°C. The salt and metal phases were intermixed by a motor-driven tantalum paddle positioned at the liquid interface. The tantalum crucible was provided with four baffles to increase the turbulence. The sampling tubes consisted of 1/4-in.-OD tantalum tubing that terminated in a tantalum frit (Kawecki Chemical Co.; average pore size, 30 µ). Procedure. The zinc, magnesium, plutonium, and salt were charged to the tantalum crucible; then the system was evacuated and filled with argon. The melt was brought to the desired temperature, and agitated for 1 to 2 hr. After allowing the salt and metal to separate, both phases were sampled. Filtered samples were obtained by immersing the end of the sampling tube in the liquid and increasing the argon pressure sufficiently to force the liquid salt or metal through the frit into the tantalum tube. The sample was then partially withdrawn into the cooler portion of the furnace tube and permitted to solidify before being removed. The temperature sequence for sampling at each magnesium concentration was 800°, 700°, 600°, 650°, and 750°C. The composition of the liquid-metal phase was varied by incremental additions of magnesium in a series of experiments at low magnesium

Jan 1, 1967

By J. J. Fischer

COMPOSITES containing cold-drawn, high-strength steel wires have shown promise for normal and slightly elevated temperature applications, particularly where strength-to-weight ratios or corrosion resistance are important.'-3 Although tensile strengths up to 500,000 psi may be obtained by cold drawing these wires, processing the composite at elevated temperatures will result in a rapid decrease of the wires' strength. In wrought maraging steels, high-strength levels can be obtained by aging at 900' . Because these alloys do not rely on heavy cold working to achieve their strength, and because they do not overage readily, they are of potential interest for use in composites. In view of this, the tensile strengths of composites containing The total heat effect thus represents the heat of formation, AHf of the compound at 273' . Since the heat of solution of tin in the tin solvent bath is zero, AHz = 3( - H273)Sn and Hf is given by: For LaSn3, AH3 had a measured value of 11,285 i 380 cal per g-atom while for La2Sn, the corresponding value was 33,658 870 cal per g-atom. Using the measured data for the compounds and pure lanthanum, a value of -15,150 200 cal per g-atom was calculated for the heat of formation of LaSn, at 273°K, while Hf for La2Sn3 was found to be -28,090 400 cal per g-i&om. The authors would like to acknowledge the financial support of the Army Research Office, Durham, North Carolina. under contract No. DA-31-124-ARO-D-384.

Jan 1, 1969

By Robert E. Reed-Hill, Edward R. Buchanan

A recent paper by Adams and vreeland30 describes dislocation density changes in zinc as a function of shear strain. The dislocation density was determined with the aid of an etching technique previously described by Brandt, Adams, and Vreeland.31 However, comparison of dislocation densities obtained by electron microscopy and this etching technique are not in good agreement, as will be shown below. Several zinc crystals of 99.999 pct purity were grown in air using a modified Bridgman technique.' These were annealed in air a 400°C for 1 hr and

Jan 1, 1969

By S. Shapiro, G. Krauss

We will reply to Dr. Pitsch's discussion by 1) presenting in greater detail the single surface trace analysis which we performed on the reversed austenite plates in a single parent plate of martensite of known orientation, 2) relating the results of our analysis to the conclusions which Dr. Pitsch makes on the basis of our data, and 3) examining the validity of our selection of twenty-nine individual traces from the over 200 austenite plates which were observed in a surface of this single martensite plate. Fig. 7 shows a standard (001) projection of the martensite plate from which the austenite-martensite interface traces were taken. The traces are plotted on the projection as the small solid circles, and the great circles corresponding to the loci of plane normals which could contain each trace or could intersect the surface plane along the measured directions are also plotted. It can be seen that these great circles intersect at a point which corresponds to the normal of the surface plane on which the traces were observed. Also rate which occurred only at particularly low heating rates, see Figs. 1 and 3 in the paper.2 Since in this case the interpretation of Jana and Wayman is plausible and since we have no alternative to this interpretation, we would like to state only that the existence of a diffusion-controlled reversal at low temperatures seems to be not yet proved beyond any doubt. The author wishes to thank Professor G. Krauss for making available his manuscript prior to publication. It is also a pleasure to acknowledge the lively written discussions, which the author has had with Professors G. Krauss and C. M. Wayman prior to this communication. The financial support of the Deutsche For-schungsgemeinschaft for the work on which this communication is based is also gratefully acknowledged. plotted within small dotted circles which represent a i3 deg scatter in each of the twenty-four unit stereo-graphic triangles are our A and B poles7 and the pole P determined by Kessler and itsch.' The data presented in Fig. 7 permit a direct association of the measured traces and the various proposed habit plane poles for the reversed austenite plates in the martensite crystal. If the sample measurements do in fact

Jan 1, 1969

By S. S. Shen, M. J. Pool, P. J. Spencer, J. R. Guadagno

VERY few thermodynamic data are available for rare-earth alloys, partly because of the difficulties of obtaining the metals in sufficiently pure form and also because of their comparative scarcity up to the present time. The rare earths form a very interesting series in the periodic table in view of the progressive filling of their 4f subvalence electron shell and would be expected to provide useful information with regard to alloying characteristics of transition elements. It has been found in recent calorimetric investigations that the heats of solution of a number of the rare-earth metals in liquid tin are highly exothermic.1-4 Exceptionally strong bonding between rare-earth and tin atoms is clearly indicated in the liquid solutions. Continued thermodynamic studies of the behavior of rare earths in solution could thus contribute a great deal to present theoretical knowledge of alloying behavior and would yield an insight into bonding of a strength hitherto unencountered in liquid alloys. The determination of the heats of solution of the pure components in liquid tin is an essential preliminary to calorimetric work of this nature. Heats of solution of praseodymium, neodymium, and samarium in liquid tin at 750" ' and the heats of mixing of Pr-Nd solid solutions' have already been determined in this laboratory. The present investigations with lanthanum continue the study of rare-earth elements. Details of the construction and operation of the liquid metal solution calorimeter used in this work have been published previously by Pool and Peluso and no further description will be given here. The lanthanum used in heat of solution determinations was supplied by Lunex who quoted the purity as 99.9 pct. Their detailed analysis of the material is given in Table I. Samples of 0.0003 to 0.0005 g-atom were used for each run and great care was taken to remove all surface oxide prior to weighing. The samples were stored at all other times in a beaker of oil to prevent their otherwise rapid oxidation. The compounds LaSn (Cudu, L1P type structure) and La&, (structure not classified) were prepared from the appropriate quantities of the two pure components by arc melting under a purified argon atmosphere and once again great precautions were taken to avoid any subsequent oxidation of the specimens. Although no structural examination of the compounds was made, the consistency of thermodynarnic measurements carried out on twenty or so individual samples of each indicates that the compounds were in fact homogeneous, single phase alloys. Samples of the compounds consisting of 0.0003 to 0.002 moles were used in the calorimetric measurements. A solvent bath consisting of approximately 80 g of 99.9 pct pure Sn was used for each series of runs and its heat capacity was determined at regular intervals throughout the experiments using pure tin or tungsten calibration samples. Measurements were made of the heat of solution of lanthanum in liquid tin at 725", 750C, and 775°K and at compositions up to 2.21, 4.76, and 5.25 at. pct La at the three temperatures respectively. In every case, the heat of solution of lanthanum remained constant at its limiting value, within experimental limits, up to the highest lanthanum concentration investigated. Since no change in was observed, it was concluded that the liquid/liquid + LaSn, phase boundary had not been

Jan 1, 1969

By R. E. Robbins, H. R. Brager

THIS note describes an unusual result obtained in an electron microscope investigation of cavities produced in commercial type 304 stainless steel irradiated in a thermal reactor (ETR) at 290°C to a high neutron flu-ence, 6 x loz1 n per sq cm. The analysis of the steel used is given in Table I. The unusual result is that the calculated quantity of helium gas produced by transmutation during the irradiation, 12 ppm, is less than one-tenth the amount of gas necessary to balance the surface tension of the observed cavities produced in the steel during ETR irradiation. Therefore, the cavities would be expected to behave like voids; however, they behave like "gas filled" bubbles. The maximum quantity of helium produced in the steel by B" transmutation was 8 ppm. In addition, the amount of helium formed by (n, (1) fast neutron reactions with the major alloy constituents and nitrogen was calculated to be 4 ppm based on the tabulated differential or effective fission-averaged cross sections of elements in type 304 stainless steel irradiated in typical thermal reactors.', In previous investigations concerning commercial austenitic stainless steel irradiated in a thermal reactor, the amount of helium gas calculated to be produced by transmutation has always been significantly greater than the amount calculated on the basis that the bubbles were gas filled, PPs= 2y/R. The balance of the gas was assumed to be in bubbles smaller than could be detected on the electron micrographs. Accordingly, the bubbles were attributed to helium produced from transmutation of impurity boron by thermal neutrons. These bubbles were not uniformly dispersed in the matrix but were located principally at grain boundaries, or were radially positioned around a few precipitates located in the matrix and at the grain bundaries., 4 Voids have also been observed in austenitic stainless steel irradiated at high temperature to high neutron fluences in the EBR-I1 and Dounreay Fast Reactors. The voids were uniformly distributed throughout the matrix. The amounts of helium gas produced by transmutation during these irradiations were less than one-tenth the amounts needed to balance the surface tension of the voids formed by the fast reactor irradiation. The fast reactor results are quite analogous to those reported here for the ETR irradiated steel. Electron microscope examination of the fast reactor irradiated material after a 1 hr postirradiation annealing at 900°C disclosed that essentially all the voids had been eliminated. The authors stated that the voids had developed due to the high concentration of vacancies produced during irradiatin., 6, ' The microstructure of the ETR irradiated material as-tested at 75O°C, Fig. 1, contained about 2 X lot5 cavities per cm3 with an average diameter of 110A. With the Van der Waals b correction and y = 1500 ergs per cm2, 300 ppm He would balance the surface tension of the observed cavities. Stereoscopic examination of the electron micrographs showed that the cavities were neither preferentially located near the grain boundaries nor highly concentrated at specific regions or precipitates. The cavities were nearly uniformly distributed throughout the matrix, on dislocations and at grain boundaries. These observations imply that the cavities were not the sole results of B'O

Jan 1, 1969

By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO'AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor' and Kay and alor' determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.' , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969

By P. K. Strangway, H. U. Ross

Briquets consisting of pure artificial magnetite, pure artificial hematite, and mixtures of the two were reduced by hydrogen in a loss-in-weight furnace at temperatures in the range 500° to 1000° . The rate of reduction of the pure hematite briquets increased continuously with increased temperature. In contrast, the pure nmgnetite briquets exhibited a pronounced rate ninimutn at about 700°C. Metallographic studies of partially reduced briquets rerlealed that, at this temperature, the he.matite samples reduced in a topo-chemical manner while the magnetite ones reduced uniformly throughout, and after partial reduction their cross sections contained a mixture of iron and unreacted wustite grains. No iron shells could be detected on the surfices of any of these uwstite grains. X-ray diffraction investigations indicated that these grains had a rzinimum lattice parameter when they had been formed at the rate rninimum temperature. Also, it was found that an activation energy of 41,000 cal per mole zoas required for reduction when only these wustite grains were present. Thus, it is suggested that the overall reduction rate of the rnagnetile su?nples at temperatures in the range influenced by the rate nzinirnum phenomenon was limited by the rate qf iron ion diffusion in the unreacted wustite grains. THE rate minimum phenomenon, which has often been observed when reducing iron oxides at a temperature of about 700°C, is one of the most interesting, yet unresolved, problems in the field of reduction kinetics. Basic principles of chemical kinetics and 'In some instance, a second rate minimum has been observed at about 900°C. Since most investigators are in agreement that this minimum is directly related to the transformation from a to y iron (which takes place at 911°C) and since it was not encountered during the present reduction tests, it will not be referred to in this vaver. fundamental laws of diffusion all agree that, as the temperature is increased, the rate of reduction should also increase. However, with certain ores, it has been found that their reduction rate actually decreases with an increase in temperature up to some value X where a minimum reduction rate is reached. With further temperature increases beyond X the rate becomes more rapid again. Temperature X is usually referred to as the "rate minimum temperature", while the overall type of behavior constitutes the "rate minimum phenomenon". This phenomenon has been reported by numerous investigators. They have found rate minima during the reduction of both artifiial' and natural374 magnetites and artificia15j6 and natural5" hematites. Rate minima have been observed when reducing high-purity material2 or low-grade ores,3'4 when studying particles in the micronsize range5 or relatively large agglomerates,g10 and during reduction with either hydrogen7 or carbon monoxide.11"2 Previously, this phenomenon has been attributed to many factors; these include sintering and recrystallization of the iron formed during reduction374 changes in microporosity of the ore upon redction,"" formation of dense iron shells around retained wustite grains,11716 and chem-isorption,17 to name only a few. However, most investigators who have reported a rate minimum merely speculated as to what seemed to influence it and they did not examine the fundamental causes. Consequently, the present experimental study was initiated in order to evaluate the basic factors which could be associated with this phenomenon. MATERIALS AND METHODS The experimental techniques, followed during this investigation, are similar to those which have been described previously.18 The chemically pure magnetic powder was prepared by partially reducing Fisher reagent-grade hematite with a gaseous mixture of carbon monoxide and carbon dioxide in a rotating-drum furnace. Three-quarter-inch diam cylindrical briquets which weighed about 12 g were formed from this magnetite powder and pure hematite powder. All of the briquets were sintered while they were slowly raised through the 1200°C hot zone of a vertical tube furnace. An argon stream was continually flushed through this furnace in order to prevent oxidation of the magnetite briquets, while in the case of the pure hematite briquets sintering was carried out in air. The sintered hematite briquets had a density of 5.06 g per cu cm while the density of the sintered magnetite briquets was 4.27 g per cu cm. The sintered briquets were reduced by purified hydrogen in a loss-in-weight furnace at temperatures in the range 500" to 1000°C. In all instances, the critical reducing gas velocity was exceeded and, in order to ensure that the results were reproducible, duplicate briquets of each type were reduced under each set of experimental conditions. A continuous record of the weight loss during reduction was obtained with the aid of a Statham transducer. The present experimental setup was capable of detecting a change in weight as small as 10 mg. Since a weight loss of over 2 g usually occurred during each reduction test, an accuracy of better than 0.5 pct of the total weight loss could be achieved. RESULTS AND DISCUSSION Reducibility Tests. In the first set of experiments, pure hematite and pure magnetite briquets were used.

Jan 1, 1969

By David V. Ragone, James A. Craig, Richard E. Balzhiser

The Gibbs free energies of formation of UC2 and UC were measured by equilibrating two-phase mixtures of UC2 + C and UC, + UC with liquid bismuth. The measured equilibrium concentrations of uranium in the bismuth combined with available activity coefficient information yielded uranium activities in these two-phase regions. Measurements on UC2 were performed over the range 1015 to 1160 K and on UC over the range 1115° to 1165°K. The values obtained for UC2 are in excellent agveement with values determined using combustton calorimetry and low-temperature heat capacity measurements. The UC values are in fair agreement with the calorimetric values, differing by about 10 pct from the calorimetric determination. MUCH interest has been shown in the uranium carbides in recent years because of their potential as nuclear fuels. As nuclear reactor operating temperatures have been raised to increase thermal efficiency, new fuels have been required. The uranium carbides are of interest because of their high melting points, >2000°C, high thermal conductivity, and resistance to irradiation damage. The manufacture and use of uranium carbides are aided by a knowledge of their stability and reactivity under various conditions. In this regard the thermo-chemical properties of the carbides, i.e., heat capacity, heat of formation, free energy of formation, and so forth, are particularly important. A great amount of work has recently been done on the thermodynamics of the U-C system. Unfortunately, however, there has not been good agreement among the various investigations. This study of the free energies of formation of uranium monocarbide and uranium di-carbide in the temperature region 1100°-1200° K was undertaken to help clarify the situation. It should be noted that in the temperature range of this investigation, 1100°- 1200° K, the thermodynam-ically stable phase in equilibrium with graphite is U2C3, not UC2, Fig. 1. However, U2C3 is reported to be stable only under extremely low oxygen and nitrogen pressure. Although UC2 is metastable below 150O°C, it exists under most experimental conditions. It should also be noted that "UC," never exists as UC2 but with compositions near UC1.9. However, "UC2" will be used to designate the dicarbide phase except when the stoi-chiometry is necessary for clarity. METHOD The approach taken in this study of the free energies of formation of UC and UC2 was to determine the thermo- dynamic activities of uranium in the two-phase regions UC, + C and UC + UC, by equilibrating the two-phase mixtures with the liquid bismuth. When a mixture of solid UC2 + C is brought to equilibrium with liquid bismuth, the reaction that occurs is: Neither carbon nor UC, could be detected as dissolved material in the bismuth. The standard free energy for this reaction may be written: In the two-phase region UC, + C, Fig. 1, the thermo-dynamic activities of UC2 and carbon are unity. The activity of uranium in this region was determined by measuring the concentration of uranium in a liquid bismuth melt in equilibrium with the two-phase mixture. This concentration was then used in conjunction with the activity coefficient data of uranium in bismuth reported by Tien et al.' to determine the activity of uranium in the two-phase region, UC, + C. All of the quantities in Eq. [2] were then known, and the AG; (uc,) was evaluated. UC + UC2. For the studies involving UC + UC,, the reaction taking place when the two-phase mixture is brought to equilibrium with liquid bismuth is: The standard free-energy change for this reaction is given by:

Jan 1, 1969

By A. U. Seybolt

Experiments on both suljidation and hot corrosion have been carried out using ternary Ni-Cr-X alloys and commercial nickel-base superalloys. It has been shown that lhere are certain micro structural similarities between sulfidation using H,S/H2 mixtures and hot corvosion using Na,S04 in "crucible" experiments or hot corrosion tests using a flame tunnel apparatus. It is proposed that two key processes in the hot cowosion process are: 1) formation of chromium sulfides which deplete the alloy matrix, and 2) oxidation which can be accelerated because of chromium depletion. Other processes play an important role in the hot corrosion process, such as accelerated oxidation attack due to the presence of a N& S04 or N&SO,- NaC2 film which inhibits the formation of a protective external oxide scale. However, this latter phenomenon was not studied in this work. THE term hot corrosion has come to mean a combination of sulfur and oxygen attack on nickel-base or cobalt-base superalloys used as gas turbine blades or partitions. This attack can be initiated by any combustion process in air involving fuel containing sulfur if the sulfur level is sufficiently high. Levels of 5 pet SO2l for example, in the combusting gas have been observed to produce hot corrosion attack on nickel-base alloys. The important immediate corroding medium in aircraft gas turbines, however, has been established to be Na2S04, formed from reaction between NaCl from sea air and sulfur in the fuel.' The Na2S04 concentrates the sulfur sufficiently so that superalloy parts heated in the range 1400" to 1900°F can become sulfided by reducing the Na2S04 film which forms on the parts, and this reaction allows sulfur to gain access to the alloy. The sulfur thus released diffuses into the superalloy and forms primarily chromium sulfides of various compositions, but frequently Cr2S, has been identified. Figs. 1 and 2 show the morphology typical of hot corrosion of a cobalt-base superalloy X-45 (25 Cr, 10 Ni, 7.5 W, 0.25 C) and a nickel-base alloy, Udimet 500 (19 Cr, 19 Co, 4 Mo, 3 Ti, 2.9 Al, 0.07 C). Both alloy samples were subjected to the same hot corrosion conditions: 616 hr at 1600°F in a combusted 2.9 pct S distillate oil containing 125 ppm Na as NaC1. It will be noted at once that the nickel-base alloy is much more severely attacked. The depth of corrosion is much greater and the number and size of the sulfides present are much greater. Both alloys show a duplex oxide scale, which is more noticeable in the X-45 alloy. The external scale is probably a spinel in both cases, with CrQ3 lying next to the alloy. Many investigators1 -"ve been concerned with hot corrosion phenomena, but there has been a lack of unanimity of opinion as to the details of the hot corrosion mechanism. More than one definition of hot corrosion is possible. Some investigators con- sider as a measure of hot corrosion only the weight gain due to an accelerated oxidation. However another point of view is that the total depth of affected alloy may be used as a measure. While it is recognized that surface oxidation attack is greatly accelerated by the presence of salts like Na2S04 or Na2S04-NaC1 mixtures, sulfur penetration into the alloy also undoubtedly produces very important effects. The region of sul-fide penetration which is so prominent in Fig. 2 is one of the outstanding characteristics of hot corrosion. For highly stressed parts, such as first-stage buckets, this sulfur-penetrated region can be more significant in mechanical property loss than the reduction of cross section produced by the formation of the massive external scale. In addition, evidence will be presented that this sulfided region can be less resistant to subsequent oxidation attack. Since it appears that the sulfided region below the surface oxide scale plays an important role in the overall corrosion process,

Jan 1, 1969

By J. R. Hauber, N. R. Borch

A study uras made on the creep behavior of cast and extruded SR grade beryllium. It is shown that, for stresses below about 1000 psi in the temperature range 760" to 85o° c, the creep behatior is nearly exactly described by the Nabarro-Herring mechanism. The activation energy is apparently that for self-diffusion, 42 2 kcal per mole, below 1000 psi, but it rises to 88.6' kcal per mole at higher stresses. The slress exponent is 4.5 at the higher stresses. Tertiary creep in this material is clearly related to void formation apparently caused by grain boundary sliding. BERYLLIUM is becoming an increasingly important technological material. A search of the literature has revealed a lack of fundamental studies on the creep of beryllium. This investigation was therefore undertaken to gain insight into the creep behavior of this material. EXPERIMENTAL PROCEDURE Tensile creep samples were prepared from cast and extruded SR grade beryllium. The vendor's chemical analysis of the beryllium tested is shown in Table I. The test specimens were machined as shown in Fig. 1 from i -in.-diam rods. The machined creep specimens were annealed to remove surface damage and to establish a variation in grain size. The heat treatments and their resulting grain diameters are shown in Table 11. The average grain diameters were determined by the intercept method. True average grain diameters were estimated by multiplying the measured average grain diameters by 1.5.' The creep tests were performed at temperatures from 700" to 850°C in a vacuum of 105 Torr or better in a tantalum-element resistance furnace. Loads were applied by an Instron testing machine such that the stress was held constant to within 20 psi. The test temperature was measured by thermocouples on the sample. With one exception the deviation from the desired test temperature was 2"C, and in that case the deviation was 4"C. Elongations were measured by an extensometer within the vacuum chamber which was fastened to the creep specimens at the grooves in the grip ends, as shown in Fig. 1. The precision of measurement of elongation was 1 X loe4 in. The creep tests were begun only after thermal equilibrium had been established in the sample and the extensometer to insure that there was no strain rate component due to transient thermal effects. Two kinds of creep experiments were performed. First, at constant grain size, the effects of varying stress and temperature were studied. In the second set of experiments, the temperature was held constant and the grain size was varied. The activation energy for creep was determined by varying the temperature at constant stress, as described by orn, during the first set of experiments. The variable grain size experiments revealed that creep at low stress apparently occurred by the abarro-errin' mechanism. In all of the creep tests, the stress was held constant only until sufficient strain had occurred to accurately determine the creep rate. The stress was then raised to a new value and the new creep rate determined. This process was reported until tertiary creep occurred. In this manner several data points were obtained from each specimen. The assumption was made that the structure was not changing appreciably between the incremental stress levels. This was verified by reducing stresses to previously tested levels and comparing the creep rates with the creep rates obtained at the lower strains. The re-producibility was within experimental error over strains on the order of 1 pct. EXPERIMENTAL RESULTS A typical series of creep tests is shown in Fig. 2. Primary creep was not observed in any test. Transient creep, which we define as creep rates that are nonlinear with time, was not observed for any change in stress except where tertiary creep occurred. The absence of both primary and transient creep has been previously reported for hot-pressed powder beryllium.= The data for the creep behavior at constant grain size are summarized in Fig. 3. The data show two distinctly different stress dependencies. At stresses below about 1000 psi, in the equation:

Jan 1, 1969

By M. Kitada, U. Kawabe, F. Ishida, T. Doi

The relations between micros tructures and critical current density in transverse magnetic field were experimentally investigated due to each transformation of the 0 to 0' + P" phases at 700' C for superconductmainly examined using replication electron microscopy. The ß' or a precipitates were found to pin down magnetic flux lines in these alloys. The effects of precipitation upon the critical current density were discussed in relation with the size, spacing, and characler of these precipitates. HIGH magnetic field superconductors, such as Nb-Zr, Nb-Ti, and Nb-Zr-Ti alloys, have been recently put to extensive practical use as winding materials for superconducting magnets.13 The critical current density of these hard superconductors under an applied magnetic field is an important characteristic for magnet materials and is very sensitive to metallurgical structure. It is generally known that the critical current density is increased by introducing dislocations and precipitates into a superconductor; that is, dislocations and precipitates are presumed to be barriers that hinder quantized flux lines from moving.4'5 Theoretical6'7 and experimental analyses of the motion of flux lines and the interaction between flux lines and various defects have already been reported by many authors. Metallographic analysis of high magnetic field superconductors such as Nb-Zr and Nb-Ti is difficult, so that no quantitative relationship between microstruc-ture and critical current density has been established yet. In this paper, the effect of precipitation on the critical current density in magnetic field was investigated for two superconducting alloys, Nb-40Zr-10Ti and Nb-5Zr-60Ti. In these alloys the resistive critical field H, at 4.2oK was about 100 kG and the critical current density Jc at 80 kG was of the order of 104 amp per sq cm.13-l5 The superconducting properties were examined in relation to the microstructural changes due to transformation of i) the ß to ß' + ß" phases at 700°C for Nb-40Zr-10Ti alloy and ii) the ß to a + ß phases at 500°C for Nb-5Zr-6OTi alloy. The effect of size, spacing, and character of precipitates on flux line pinning was in particular examined. The microstructures were studied by means of residual resistivity, microhardness, and tensile strength measurements as well as by X-ray diffraction, optical, and replication electron microscopies. I) EXPERIMENTAL PROCEDURE Pure niobium, zirconium, and titanium, in the form of rods 0.8 cm in diam, served as raw materials. Results of chemical analyses of these rods are given in Table I. Ingots of the alloys, 0.4 cm in diam and 3 cm in length, were prepared by means of levitation melting, utilizing a copper mold in an argon-gas atmosphere. Samples from the ingot then were cold-worked by grooved mill to 0.2 cm in diam, heat-treated homogeneously (in the ß phase region) for 5 hr at 1100° in a vacuum of 1 x 106 Torr, and finally cold-drawn to 0.025 cm in diam. For heat treatments, samples were wrapped in niobium foil and sealed in an argon-gas atmosphere in fused quartz capsules. Water quenching was done after each heat treatment. Subsequently H-J, were performed at 4.2° by slowly transporting the current through the samples 4 cm long, under transverse magnetic field, until the least detectable resistive terminal voltage was observed. The resistive critical field H, was taken as the field at which 100 pv appeared at 4.2°K across a sample 3 cm in length, with a current of 5 ma. The critical temperature T, was measured by means of a conventional four-probe resistivity technique and taken as the temperature at which the sample resistance reached one-half of full restoration of the normal-state resistance with a current l ma flowing through a sample 2 cm in length. Precipitates were observed by means of optical microscopy and carbon replication electron microscopy. The etching solution consisted of 5 ml HF, 10 ml H2SO4 10 ml H2O2, and 50 ml H2O, and shadowed carbon replicas were examined in a itachi HU-11 electron microscope operated at 50 kv. X-ray diffraction photographs were taken by a 11.46-cm-diam Debye-Scher-rer camera using copper Ka radiation. The micro-hardness was measured under a load of 200 g using

Jan 1, 1969