By N. A. D. Parlee, I. D. Shah

ThIS reports on some work done on the solubility and diffusivity of oxygen in liquid silver. Solubility. Improvements in the measurement of the solubility of oxygen in silver and silver alloys were made because precise data were needed for calculating diffusion coefficients of oxygen in these alloys. The apparatus and the procedure used were similar to those of Parlee and Sacris.' The main improvement was in the temperature-measuring technique. A MV30 mullite protection tube containing a calibrated Pt-Pt, 10 pct Rh thermocouple was inserted in the reaction tube from the top through a vacuum-tight swage-lok fitting. The protection tube was well-immersed in the liquid silver, which was heated by induction. A Leeds and Northrup potentiometer was used in connection with the thermocouple. All runs reported were made at 1 atm. The temperature range investigated varied from 940" to 1200°C. The ternary point in Ag-0 phase diagram2 is at 939°C and 0.32 wt pct O. This point was reinvestigated using the above-described apparatus and was found to be at 939°C and 0.315 wt pct 0. It was determined by observing the sudden evolution of oxygen at this point while the solubility measurements were made. The point was easily reproducible if precautions were taken to keep the liquid silver essentially in equilibrium with oxygen and to lower the temperature very slowly. All of the results of this new solubility investigation are plotted in Fig. 1. They are represented by the "least-squares" line shown in the figure and the following equation for solubility at po2 = 1 atm: log% O =695.4/T - 1.086 This equation differs only slightly from that proposed by Parlee and sacrisl and that of Diaz, Masson, and Richardson.3 The points of Parlee and Sacris, using an optical pyrometer, are shown for comparison.

Jan 1, 1968

By Charles L. Mantell, George Ferment

This investigation determined the jeasibility of current-potential curves as an analytical tool for monitoving manganese electroicinning solutions for metallic impurities. Nine metallic impurities were studied: trickel, cobalt, silver, copper, zinc, molybdenum, catlmiun magnesium, and sodium. The individual effect of each metallic irzplrl,iLy on the standard point-izatiorr was determined for a range of 'concentration. Not all of Ihe impurities affected the polarization curve; correlation between transition current and cotrcetztration of impurity. Molybdenum had an uncorrelated effect on the polarization curie. The effects of binary mixtures of impurities were studied to see if the transition current of the mixture could be predicted. Interactions occurred between impurities which prei'etzted the pvecliction the transition current of tile rrlisLitr.e by additive laws. The polarization curve was shown to be sensitive to metallic impurities which affect the current efficiency of a manganese cell. THE application of current-potential curves in manganese electrowinning is not new but played an important part in the conversion of an inoperative large-scale pilot plant into a continuous comnercial operation.1"" The effects of trace metallic impurities in manganese electrowinning solutions on cathode current-potential curves,5-19 specifically nine impurities (nickel, cobalt, silver, copper, zinc, molybdenum, cadmium, magnesium, and sodium) were studied for a range of concentrations. Cadmium, magnesium, and sodium had no effect. Nickel, cobalt, silver, copper, and zinc yielded a correlation between transition current and concentration of impurity: molybdenum had an uncorrelated effect. Binary mixtures of impurities were studied to de-termine if the transition current could be predicted from the values for the individual constituents. Interactions between impurities prevented the prediction of the transition current of the mixtures by an additive law. The polarization curve was shown to be sensitive to metallic impurities which affected the rurrent efficiency of a manganese cell. The electrowinning of manganese relies upon maintaining a high-purity electrolyte. Purification schemes were developed to remove all of the heavy metals, the magnesium and calcium. Concentration limits have been established for single impurities. With high-purity electrolytes, favorable cell efficiencies are consistently obtained; but with impure solutions there is a reduction in efficiency. With the rapid rise to commercial prominence of electrochemical processes, there has been a lag in developing rapid methods for determining whether an electrolyte is sufficiently pure for efficient electrolysis. The most sensitive test for impurities is the behavior of the electrochemical cell. Impure electrolytes will cause a serious reduction in cell efficiency, and in many cases metal deposition will be prevented or reversed. The effects of impurities are not usually evident until after long periods of electrolysis, resulting in a disruption of the process. A method which could predict the behavior of an electrolyte in terms of cell efficiency prior to reaching the commercial cell is needed. Van Arsdale and Maier," Allmand and Campbell,a1'22 and others attempted to develop an electrochemical process for manganese,"3"29 but all met with some degree of difficulty. Jacobs et a studied the effects of metallic impurities in manganese electrowinning. Plant methods were based on a 2-hr plating in a small electrolytic cell. The final method was based on a 24-hr plating run, performed in a relatively large test cell. Here, current efficiencies were calculated with and without impurities in the electrolyte, and the critical concentration was established as the maximum amount of impurity that the electrolyte could tolerate before there was a serious loss in efficiency. The amount of impurity that could be tolerated decreased as the plating time increased, indicating deposition of the impurity. This test duplicated the conditions of commercial practire, and was sensitive to impurities. Small amounts of impurities significantly affect the hydrogen overvoltage at a metal surface, increasing or decreasing it depending upon the nature of the impurity. ockris established the limit for the onset of poisoning at 10-l moles per liter. The effects of impurities were studied by potential-time curves at a constant current density. The technique did not lend itself to rapid analysis in that several hours were needed to establish stable potential-time curves. Serfass and coworkers3' developed calorimetric and spectrophotometric techniques for analyzing for trace impurities. Our method4'" is based on current-cathode potential curves produced by continuously changing the cell voltage at a programmed rate. Starting with a clean stainless-steel cathode, the cell voltage was initially adjusted to yield zero current: the program was then started and the current was plotted as a function of the cathode potential. Fig. 1 is a typical current-potential curve. In initial region A the hydrogen-evolution reaction predominates and the polarization curve

Jan 1, 1967

By G. S. Baker, S. H. Carpenter

Langenecker has reported significant reduction in strength of high-strength metals during ultrasonic t'ibration. Decreases in static yield stress an order of magnitude greater than the calculated stress amplitude of vibrations were reported by him for a stainless steel and for tungsten. in the present work, attempts were nzadc to verify such large reductions in yield and flats stresses using resonant librations of measured amplitudes. The results show that both the soft metals (copper and aluminum) and the high-strength metals (sleels) hare reductions in yield and .flow stresses no larger than the stress amplitude of libration. BLAHA and Langenecker,' investigating the effect of vibratory stresses on the deformation of zinc and aluminum, found a decrease in the static yield and flow stresses approximately equal to the vibratory stress imposed. Langenecker later extending this work to high-strength metals such as stainless steels and tungsten2 found a much larger effect. In these metals the static yield and flow stresses decreased by an amount more than an order of magnitude greater than the calculated vibratory stresses. It was suggested that this phenomenon could be a serious hazard to high-strength structures in an acoustic environment, such as a large rocket at launch, or could be used advantageously in the working of hard-to-work materials such as the refractory metals. Langenecker and others3 have investigated the effect of high-amplitude vibrations on many metal-forming operations. The results have been quite favorable with usually a large decrease in the energy necessary for the forming operation. The processes, however, involve large frictional forces and it is not clear whether the decreases in forming forces are to be ascribed to decreased friction or to decreased flow stresses. The present paper reports an attempt to determine the effect of accurately known vibratory stresses on the static yield and flow stresses. I) EXPERIMENTAL TECHNIQUE The standard multicomponent resonator technique for measuring internal friction has been adapted to allow simultaneous high-amplitude vibration, internal-friction measurement, and tensile deformation. This has been described in detail elsewhere.4 Longitudinal oscillations of approximately 50 kc frequency are excited in a multicomponent resonator by a quartz transducer. A second transducer measures the amplitude of vibrations. Fig. 1 shows a schematic drawing of the resonator and grip arrangement and the displacement pattern produced. Since the centers of the dummy bars are at displacement nodes, they represent points where attachments will not materially affect the vibrations. The force is applied by a standard Instron tester. The sample may be deformed while simultaneously vibrating at up to 104 strain amplitude. 11) EXPERIMENTAL RESULTS The effect of high-amplitude vibrations on the yield and flow stresses of copper. aluminum, tantalum. a soft iron, and a stainless steel has been measured. In addition samples of tungsten vibrating at stress levels up to 10' dynes per sq cm have been subjected to static stresses near the static yield stress with no indication of macroscopic deformation. Fig. 2 gives typical results for 99.999 pct polycrys-talline copper. A vibratory stress of 7 x 107 dynes per sq cm is applied at points "a" and removed at points "h". The behavior of aluminum is identical. In agree-

Jan 1, 1967

By H. R. Ogden, E. S. Bartlett, A. G. Imgram

Unmodified disilicide coatirigs were applied to sheet-tensile specimens ofCb-Dg3 and Mo-TZM veJractovy- metal alloys. Coating thickness, degree of coating-substrate interdiffusion, and specimen geonzetry (notched and plain were included in the variables studied. Tensile tests were made to determine the ductile-lo-brittle transition temperature. The disilicide coating modestly increased the transition temperatlre of TZM, but had no effect on 043. Neither material condition (recrystallized or stress-velieved) nor specimen geometry (notched or unnotched) significantly altered the effects of coatings on the transilion temperatures of. the alloys. Cracks in the brittle coatings did not propagate into the substrate, and fracture modes appeared to be the same for both un-coated and coated specimens. MOST potential structural applications for refractory metals and alloys involve exposures to oxidizing environments at elevated temperatures. The general lack of oxidation resistance of these metals will require protective coatings to allow fulfillment of their potential. Currently preferred coatings for the oxidation protection of refractory metals are brittle intermetallic aluminides or silicides. These are typically formed on the surface of the refractory-metal substrate by a diffusion reaction between the substrate and a gaseous or liquid medium that is rich in aluminum or silicon. Because of the brittleness of these coatings, they will sustain no plastic deformation at low temperatures. They are frequently cracked by cooling from the coating temperature because of the thermal-expansion mismatch with the substrate alloy. Even if they survive cooling intact, they crack rather than sustain deformation under load at low temperatures. Thus, when a coated refractory metal is strained beyond the elastic limit of the coating at low temperatures, the mechanical environment of the substrate would include both static and dynamic cracks. These might be expected to influence the flow and fracture behavior of the substrate. This could be manifested in an altered fracture mode and/or an increase in the normal ductile-to-brittle transition temperature of the refractory-metal substrate. This paper presents the results of a research program that was conducted to determine the influence of the presence of a brittle surface coating on the low-strain-rate tensile behavior of typical refractory metals at low temperatures. EXPERIMENTAL PROCEDURES Material Preparation. Thirty-mil-thick sheets of molybdenum TZM alloy (Mo-0.5Ti-O.1Zr) and colum-bium D43 alloy (Cb-IOW-1Zr-O.1C) were obtained commercially. These alloys were selected as substrate materials representing two classes of materials important in current refractory-metal technology. The TZM was in the stress-relieved condition, and exhibited a heavily fibered grain structure. The D43 had been processed by the duPont "optimum" fabrication schedule,' and exhibited slightly elongated grains typical of this process. Tensile specimens of two geometries were prepared from these materials: 1) plain specimens with 0.2-in.-wide 1.0-in.-long gage sections; 2) specimens similar to above, but with a 0.06-in.-diam hole drilled in the center of the gage section, providing a stress concentration factor, Kt, of 2.5. The "notch" geometry was selected to represent a typical condition of a rivet hole or other geometric discontinuities as might be encountered in various applications. Machined specimens were degreased, with a final rinse in acetone, prior to the application of coatings. Specimens of each substrate and configuration were pack-siliconizedin a particulate mixture of 80 pct A1203, 17 pct Si, and 3 pct NaF. Specimens were embedded in this mix (contained in graphite retorts) and coated in an electrically heated argon-atmosphere furnace under time-temperature conditions to effect nominal 1- and 3-mil-thick silicide coatings: Coating Thickness, mils Thermal Treatment 0.6 to 1.4 24 hr at 982°C 2.4 to 3.2 48 hr at 1093°C Coating kinetics were similar for both the TZM and D43 substrates. These treatments had little or no visible effect on the substrate microstructure as determined by optical metallography. The coatings on TZM were essentially single-phase unmodified disilicides, while those on D43 showed substantial evidence of modification by proportionate reaction with the respective substrate elements or phases, as shown in Fig. 1. It was recognized that these coatings might not be particularly desirable regarding protective capability. However, it was desired to circumvent possible inter -ferring chemical interaction with the substrate by pack additives such as chromium, titanium, boron, aluminum, and other elements that typify the better protective coatings for these materials.' Thus, the results presented apply specifically to the simple silicide coatings investigated. They may not be rep-

Jan 1, 1967

By T. F. Bower, M. C. Flemings, H. D. Brody

A series of experiments are reported which show thai reasonable assumptions for analysis of solute redistribution in solidification of castings and ingols illclr(de: negligible undercooling before nuclcation of solid phases, negligible increase of solute in advance of the tips of growing dendrites, complete diffusion within the Liquid oer distances the order, of dentrite arm spacings, platelike dentrite t/o?$holog?.. Qzmli/ali,e and periment is obtained JOY Al-Cu alloys front measurements of amount of nonequilibrium second phase, minimum solute content at the centers dentrites arms (after solidification), and 3) change in minimum solute content in dentrite arms during solidification. In a previous paper' analyses were given describing solute redistribution in dendritic solidification. The analyses were undertaken primarily to permit prediction of "severity of microsegregation" in a casting or ingot after solidification and cooling to room temperature, but can also be used to predict "local fraction solid' as a function of temperature in the solidifying alloy. Numerical results were given for Al-Cu alloys. The aims of this paper are to examine the validity of some of the assumptions of that analysis, and to compare predictions of the theory with experiments. All experiments reported are on Al-Cu alloys, the bulk on Al-4.5 pct Cu alloy. EXPERIMENTS Experiments conducted were on small ingots, 41/2 in. in diam by about 10 in. high. solidified in a controlled thermal environment (i.e., in a resistance-heated, re-circulating air furnace, whose temperature could be controlled to 1°C). In one series of experiments, the ingots were solidified very slowly (solidification time was varied from 8 to 1000 hr) and at constant rate of heat extraction. In a second series of experiments the ingots were solidified ( 'unidirectionally". Fig. 1 is a sketch of the method of making the two different types of ingots. The unidirectionally solidified ingots were fully columnar, and the slowly solidified ingots had equiaxed structures, Fig. 2. In making the slowly solidified ingots, the mold employed was carbon steel, coated with inert refractory. Typically the mold and its environment were heated to 700°C. The molten alloy was then poured into the mold and the temperature of the system equilibrated above the liquidus. The environment of the mold was next cooled with a controller responding to a differential thermocouple that measured the difference between the temperature of the melt and the temperature of the mold environment. The differential thermocouple consisted of one chromel-alumel junction in the melt connected in opposition with a second junction in the furnace. The potential across the differential thermocouple was input to the controller which acted to keep this potential at a set. constant value; hence the temperature difference between the two junctions was maintained nearly constant. Major resistance to heat flow in the above apparatus was between the metal surface and the furnace atmosphere, not in the metal itself. By maintaining a constant temperature difference between the metal and the furnace atmosphere, the controller maintained an essentially constant rate of heat extraction during solidification, regardless of amount of heat released by the metal per unit temperature change. When the metal temperature dropped just below the eutectic temperature. the ingot was removed from the furnace and water-quenched. The unidirectionally solidified ingots were cast in a similar mold to the foregoing except that provision was made to extract heat through the bottom face of the mold by passing air or water through the mold base, Fig. 1. For these experiments, metal and mold temperature were again equilibrated above the liquidus. Temperature of the mold environment was then held

Jan 1, 1967

By Richard L. Ashbrook, John F. Wallace

Several high-temperature eutectics of cobalt and nickel alloys were modified by small additions of selected elements. Thes-e alloys were compared to unmodified melts for microstructural variations. A few modified compositions were selected on the basis of structure and their tensile and stress-rupture behavior determined. The results of stress-rupture tests in air at 1800 F and room-temperature tensile tests of four high-temperature eutectics showed modification capable of producing substantial improvements in properties. The microstructures were altered and mechanical properties improved by: a.) dispersing a subordinate phase more uniformly throughout the matrix; b) replacing large continuous -network or platelike constituents with small equiaxed discontinuous phases; and c) by forming new, finely divided phases. tHE term "modification" is most commonly used to describe the refinement in microstructure of the Al-Si eutectic that occurs as a result of rapid cooling from the melt or on slow cooling after treatment with small amounts of sodium.1 "Modification" has also been used to describe the change from flake to spheroidal graphite in the austenite-graphite eutectic of cast iron.2 This change of graphite shape is accomplished by small additions of cerium or magnesium.3 Other systems have also been shown to be capable of modification, for example: Pb-Sn by copper;4 Al-Cu by sodium;5 Al-Mn by sodium;5 and Pb-Sb by aluminum.5 Although modification of Al-Si alloys and cast irons is usually accompanied by improved mechanical properties, a general definition of modification has been suggested to include the effect of small quantities of impurity elements on the microstructures of all eutectic alloys, regardless of the effect on the mechanical properties.6 In this paper, the term "modification" is employed in a broad sense to include the formation of third phases or even the supplanting of one of the binary eutectic phases by a third phase. The mechanism of modification, as for any solidification phenomenon, must be considered primarily in terms of nucleation and growth. Although both nuclea-tion and growth mechanisms are required to explain all the phenomena observed in connection with the solidification of modified eutectics, various investigators have usually favored one or the other.7"16 It has been shown that modification of a binary eutectic can be effected by addition of a solute element that has greatly different distribution coefficients or k values in the two phases of the eutectic. Under these conditions, differences in the temperatures at the solid-liquid interfaces of the two phases retard the growth of one phase with respect to the other.4 It has also been shown that increased undercooling favors a transition from a rodlike eutectic to a globular eutectic.17 A mechanism proposed for the transition from lamellar to rodlike eutectics depends on the concept of constitutional super cooling.18 The modification of eutectic alloys may be of interest for high-temperature service as well as at room temperature. Although "high-temperature eutectic alloys" may appear to be a contradiction in terms, many eutectic systems, including those studied in this work, have melting points in excess of 2400°F. One of the mechanisms by which high-temperature alloys are strengthened is dispersion of a relatively brittle phase such as an oxide, carbide, or an inter-metallic compound throughout a ductile matrix. For a given volume fraction of dispersed phase, strength is increased by decreasing the size and spacing of the dispersed particles.19'20 Furthermore, room-temperature ductility may also be increased by changing the shape of a brittle dispersed phase from platelike to equiaxed or spheroidal.8 Overaging and redissolving of the secondary phase limit the maximum temperature to which precipitation-hardened alloys can be used. However, in a binary eutectic system, both phases coexist up to the melting point. Although all eutectic structures are not completely stable,21 a dispersion-hardened cast high-temperature alloy might result if a fine distribution of one of the eutectic phases could be obtained during solidification. An additional reason for interest in eutectic alloys is their excellent castability.22 Since eutectic alloys, like pure metals, freeze at a single temperature rather than over a range of temperatures, their castability is superior to solid-solution alloys with long liquidus to solidus ranges. The purpose of this research was to study the effects of small solute additions on the microstructure and mechanical properties of a number of high-melting-point eutectic compositions.

Jan 1, 1967

By M. M. Rao, P. G. Winchell, R. J. Russell

A detailed analysis has been used to correlate the avalable thermodynami c da In on iron-ric11 Fe-Ni (41loys in the body-centered a, and the face-centered y phases. The inp ut injovrt~ation required by the a am lysis consists of tile heat of the a, to y transformation at 1123°K, the heat of mixing of y at 1123°K, tile specific heats of both a, and y (decomposed into Debye, electronic, and magnelic contributions), and the positional and magnetic entropies of both a, and y. PYLrrzary oirt.bul of the analysis is the free energy of each phase as a Junction of temperature and composition. FOr Fe-Ni alloys the adjustment of twenty-one parunletevs allows the accurate reproduction of enthalpy data for both phases, the heat of mixing- for y, the a/y equilibrinm compositions in the Fe-Ni phase diagram, and the usually accepted enthalpy and entropy of a and y iron. Also obtaitzed are fuirly accurate reproductions of electronic specific heat coefficients predicted from electron- to-atom ratio interpolations and To temperatuves eslimanted from transformation studies. Also considered in the calculation are the elastic constants, Curie temperatures, saturation magnlelizalion values, and indications of short- range order. The measnred activity coefficient of iron in anstetnite could not be accurately matched. The major source of uncertainty in the model is thought to be the magnetic contribution to the entropy of austenite. Calcrclations were extended to Fe-ni-C alloys using available carbon-acliuity data. The free energy of transformation from martensile to r at fixed composition was obtained as a function of nickel and carbon contetzt, and binary thetal-carbon phase diagrams Were estimaled as a function of nickel contenl. We needed thermodynamic information for Fe-Ni and Fe-Ni-C alloys at temperatures between 400" and 800°K in order to interpret the results of several phase-transformation studies. The most recent theoretical analysis of the thermodynamics of Fe-Nialloysl was based on a lumped-parameter, regular-solution model and used the Fe-Ni phase diagram available at that time.' Because significant difficulties were encountered in attempting to extend this analysis to Fe-Ni-C alloys, and because more experimental data has become available recently, we decided to attempt a new correlation. The analysis used here allows the extrapolation of measured and calculated thermodynamic values to lower temperatures and the extension of the thermodynamic analysis to Fe-Ni-C alloys. The structure of this correlation consists of expressions containing a total of twenty-one adjustable parameters. The forms of these expressions are discussed in the next section; however, a less formal summary is presented now to provide a physical overview of the model and to indicate its connections to prior work. Primary input information for this correlation is described below. The measured values of the specific heat of iron3 and its analysis475 and theoretical estimates of the specific heat of y* iron at low tempera- loys at 1123°K has been measured by solution calori-metry.7 The enthalpies of both a, and y have been measured most recently by Scheil and Saftig,B who used a dry-ice calorimeter. These data are used to formulate expressions for the heat of mixing of y and the heat of transformation of a, to y both at 1123°K. The a and y solubility limits in the Fe-Ni phase diagram have been redetermined recently9 by methods which assure a close approach to equilibrium. The a to y transformation can occur without change in nickel content or free energy at a temperature called TO; TO temperatures for various nickel contents have been estimated from transformation studies. The computed free-energy functions are adjusted by means of the parameters to fit both the phase diagram and the TO temperatures. Primary emphasis is placed on the phase diagram fit. Iron activities have been measured in Fe-Ni austenite10 between 973" and 1173°K. These activity data, which cannot be fitted accurately with our model, indicate that iron is substantially ideal in iron-rich austenite. Secondary, but helpful, information for the present correlation is provided by neutron diffraction and saturation magnetization measurements on both body-centered and face-centered Fe-Ni alloys."-'3 These results were interpreted11 in terms of composition-insensitive, localized magnetic moments on both iron

Jan 1, 1968

By M. S. Seltzer

High temperature steady-state creep rates have been determined jor lead sulfide single crystals whose defect concentrations were fixed by equilibration under controlled sulfur pressure. The activation energy of creep, Qc , for undoped lead sulfide, is a function 01 composilion, decreasing from 2.9 to 2.2 ev as the carrier concentration increases from 9 x 1016 to 8 1018 electrons cm-3 for lead excess crystals, and increasing from 1.7 to 2.3 ev as the concentration of holes increases from 4 x 1017 to 1 x 1018 cm-3 in sulfur excess material. For five different composilions, Qc for undoped and bismuth-doped crystals has been found to be equal to Qpb + Qs, the self-diffusion activation energies for lead and sulfur in PbS. It is well-established1 that high-temperature steady-state creep of pure metals is a diffusion-controlled process, where the activation energy of creep is equal, within experimental error, to the activation energy of self-diffusion. The relationship between the activation energy for steady-state creep and those for self-diffusion in binary compounds is more complicated, however, because two different diffusing species must be considered, and becayse the activation energies may be influenced by compositional variations and by foreign atom additions.2-4 In some cases experimentally determined creep activation energies are correlated with those for self-diffusion of the slower-moving species, but such agreement is by no means universal. Interpretation of experimental results is difficult because few investigations include measurements of creep rates and self-diffusion coefficients of both diffusing species on single crystals of similar composition and foreign atom concentration. The objective of this investigation, therefore, is to determine the influence of stoichiometric defects and foreign atoms on steady-state creep and self-diffusion for a well-characterized binary compound. Lead sulfide, a compound semiconductor which crystallizes in the NaC1-type structure, and whose homogeneity range includes compositions on either side of the 1:l atom ratio, was chosen for study in this investigation. The pressure-temperature-composition relations for PbS are available,5,3 and deviations from stoichiometry may be monitored by electrical measurements.7 Single-crystal specimens are available to allow observation of effects due to bulk phenomena without interference from grain-boundary effects. These crystals have been employed to determine steady-state creep rates under compressive stress for "pure" and bismuth-doped PbS as a function of sulfur pressure and temperature as well as crystal orientation and applied stress in order to establish the relationships between defect concentrations and creep rates. EXPERIMENTAL PROCEDURES Crystal Growth. Lead sulfide crystals, prepared by the Bridgman method, are grown in evacuated quartz crucibles, filled with almost equal atomic proportions of high-purity (99.999 pct) lead and sulfur, and heated to a temperature above the melting point of PbS (about 1127°C) so that the lead and sulfur react to form molten PbS. The crucible and melt are dropped through the hot zone of the crystal-growing furnace at the rate of 1 cm per hr. The maximum melting point of PbS is slightly on the lead-rich side of the 50:50 composition; hence crystals grown from a near stoichiometric melt are usually n-type semiconductors containing excess lead atoms. Typically the lead excess concentration in solid solution with the PbS is 3 x 1018 atoms cm-3. Crystals containing either 1/20 or 1/2 mole pct Bi2S3 were prepared by addition of the foreign atoms prior to crystal synthesis. Preparation of Specimens of Controlled Stoichiom-etry. Since it is difficult to grow crystals of desired composition, the process of crystal growth and control of stoichiometry are separated into two distinct operations. Equilibration of as-grown PbS to a desired composition is most easily accomplished by first annealing the n-type crystals under high sulfur pressure (about 1 atm) at temperatures above 700°C. This process serves to put excess lead precipitates into solution, yielding 0 -type crystals upon quenching to room temperature. Inter diffusion occurs readily in crystals so treated, and the methods described by Bloem may then be employed to obtain crystals of controlled stoi-chiometry. For the creep measurements made in this study, this involves heating crystals in mixtures of H2 and H2S The equilibrium constant for H2S is given by: Thus the sulfur partial pressure is obtained from knowledge of the H2/H2S ratio and Kh2S for the temperature in question. Fig. 1 shows the p-T-x diagram for PbS. It can be seen that, within the stability limits for single-phase lead sulfide, desired compositions may be obtained by equilibrating under a specified sulfur pressure and temperature. Characterization of Crystals. The principal methods for evaluating PbS crystals include measurement of electrical properties and mass-spectrographic analysis. The measured electrical parameters include Hall coefficient, conductivity type, and electrical resistivity Bloem7 has shown that there is a 1:l relation between the defect concentration and carrier concentration obtained. Hence, if the contribution to the carrier con-

Jan 1, 1968

By A. W. H. Morris, E. A. Steigerwald

The jatzgue beizazriov oj Mietal matrix co))zpos~tes in tension -lensiom loading has been imestigated as a junction of Dolume fraclion veinfovcelnent using the model systems of a silver matrix reinforced with contlnuous or dzscontztinuous aligned tungsten jilamenls and continuous aligned steel filamenls. Appreciable impvocetnents in fatigue strength were obseved in all syslems inzvesLigated, the degree of sl renglhenng-increasing with increasing volume fraclion of reinforcement. The mode of fatigue failure was found to be a function of colutrre jp-actiotz and was also noted to be controlled by the relative fatigue and strength characlerislics of the matrix and reinforcemenl. THE advantages to be gained by suitably incorporating high-strength filaments or whiskers into metallic matrices are well-recognized.' To date emphasis has been placed on the experimental determination of tensile strengths and elastic moduli of metal matrix composites measured parallel to unidirectionally aligned filaments. Several attempts have been made to relate experimentally measured tensile properties to theoretical values calculated from the properties of the components on the basis of the relatively simple "rule of mixtures" analysis. However, relatively few data have been reported in the literature on the fatigue behavior and mechanism of fatigue failure of metal matrix composites. In a study of fatigue crack propagation in aluminum plus steel wires and aluminum plus tungsten wires, Forsyth et a1.2 found that the incorporation of small numbers of filaments suitably dispersed were capable of substantially reducing the rate of fatigue crack propagation. For this purpose, the strength of the filaments appeared to be more important than the aspect ratio and the authors reported that parallel filaments were not the most favorable orientation for increased strength. In a basic study of the fiber reinforcement of metals, Williams and 0'brien3 report preliminary results which indicate a considerable improvement in fatigue strength in reversed bending fatigue of a steel wire-reinforced aluminum alloy composite. In a study of the influence of interfacial bonding on fatigue behavior, Baker4 has also reported improved fatigue properties in stainless steel-reinforced aluminum composites. In contrast, Ham and place5 report that, although tensile properties are improved greatly by filament reinforcement, the reinforcement of copper with continuous, brittle tungsten wires up to 23 vol pct was comparatively ineffective against fatigue. The authors attribute the poor fatigue properties of the composite to fatigue hardening of the matrix at the tips of cracks which can build up stress concentrations sufficiently large to fracture proximate filaments. Baker and cratchley6 failed to find marked improvements in the reversed-bending fatigue properties of silica-reinforced aluminum. The study was complicated by the complex behavior in a composite during the compres-sive half-cycles imposed in this type of loading. This was manifested in the failure of the composites by de-lamination, a contributing factor being the presence of aluminum oxide at the matrix-filament interface. Prior to the general acceptance of filament-rein-

Jan 1, 1968

By D. G. Swarthout, J. W. Savage, R. W. Guard

The Nb-N constitution diagvam has been examined from 1100° to 1450°C at 1 atm N2 pressure. On the basis of- our work plus that of Brauer and coworkers the stable nitvide Phases are: a) a solid solutlion, basic niobium (bcc) with nitrogen contained interstitially; NbN,, x = <0.40; b) ß NhNx,x = 0.39 to 0.45; hexagonal (W2C type) (NbzN); a =3.058A,c = 4.961 + 0.001A c) y NbNx x = 0.75 to 0.80; tetragonal (distorted NaCl type) (Nb4N3); a = 4.386A,c = 4.332 + 0.001A; d) 6 NbN,, x = 0.88 to 0.91; cubic (NaCl type); a = 4.3885 + 0.0007A; e) E NbNx x = 0.92 to 1.00; hexagonal (Tip type); a = 2.958A, c = 11.272 * 0.0015A. In addition, a metastuble transition phase 6&apos; has been observed and occurs only during the transition 6 — E. 6&apos; NbN has these distinguishing parameters: NbNx,x = 0.96; hexagonal (anti-NiAs type); a = 2.94A, c = 5 .46A. The high-temperature phase fields in the system are governed by two reactions: a) 6 + Y + E, a entectoid reaction occurring at 1270" ± 20° C; b) o + N2 = E, a 2 012 1 reaction occurring at 1370" ± 20° C. As part of a study of the electronic low-temperature. properties of transition metal nitrides, a number of specimens of niobium nitride were prepared. Preliminary observations on these specimens showed several points of disagreement with data already in the literature. It was, therefore, decided to determine the constitution diagram for the Nb-N system between 1100" and 1450°C. The objective of this research was to define the temperature and composition regions of stability of the various phases and to explain the differences among previously proposed diagrams. Review of Previous Literature. The research on the Nb-N system to 1964 has been summarized by storms.&apos; Although he does not present a phase diagram, his review covers the research on the system thoroughly. One of the earliest works on NbN is that of Ascher-mann and coworkers2 who studied the superconductivity of the cubic 6 NbN. Subsequent work by Horn and ziegler,3 Cook, Zemansky, and Boorse,1 Rögener:5 Schroder6 and sellmaier7 has qualitatively confirmed the first results on superconductivity, although their methods of preparation differed considerably. The constitution diagrams proposed for the system by Brauer and Esselborn8 and Elliott9 are shown in Fig. l(a)and (b). The diagram in l(a) has been modified by more recent results in Brauer&apos;s laboratory (private communication). Although 6&apos; is shown on this diagram, Brauer has indicated that he now believes 6&apos; to be a metastable phase in the temperature range shown. The diagram of Elliott, Fig. l(b), is based primarily on the results of Elliott and Komjathy10 on ni-trided niobium strip or rod specimens examined by X-ray diffraction and metallography. It will be noted that these proposed diagrams are in conflict with respect to the temperature and composition ranges of

Jan 1, 1968

By S. G. Epstein

Using the capillary-reservoir technique, electromi-gvation rates of cadmium and indium in liquid bismuth were measured at several temperatures. The electric mobility of cadmium Jrom 305° to 535°C and indium from 310° to 595°C can be expressed as a function of temperature by the equations UIn = 1.52 x 10-3 exp sq caz per v-sec Migraion of both solutes was cathode-divected at a rate rnore than four tiMes tHAt previously found for siluer in liquid bisnmth. The electric mobilities of cadmium and indiulrz in liquid bismuth at 500° C are nearly identical with their respective mobilities in mercury at room temperature. AS part of a systematic study of the variables which are considered to control electromigration in liquid metals, the electromigration rates of cadmium and indium in liquid bismuth have been measured. Mass transport properties of silver in liquid bismuth have been reported previously,&apos; and measurements of tin and antimony in liquid bismuth are forthcoming. Comparisons will be made with literature values for these same solutes in mercury.2&apos;3 This series of solutes was selected to determine the effect of the solute valence on its electromigration. Silver, cadmium, indium, tin, and antimony have nearly equal atomic masses but have chemical valences ranging from +1 to +5. They are all fairly soluble in bismuth above 300°C and all have radioactive isotopes, which are an aid in making analyses. EXPERIMENTAL TECHNIQUE Electromigration of cadmium and indium in liquid bismuth was measured by the modified capillary-reservoir technique previously described.&apos; In this method irradiated cadmium or indium is added to bismuth to form alloys containing about 1 wt pct solute (<2 at. pct solute). Several quartz or Pyrex capillaries: 1 mm ID and 5 cm long, vertically oriented, are simultaneously filled in the reservoir of the liquid alloy. A direct current is passed through two of the capillaries, which contain tungsten electrodes sealed in the upper end. The other capillaries sample the reservoir during the experiment. After a measured time interval the capillaries are removed from the reservoir and rapidly cooled. The glass is then broken away from the solidi- fied alloy, which is then weighed, dissolved in acid, and analyzed for solute content by chemical and radiochem-ical techniques. An electric mobility (velocity per unit field) can be calculated from the amount of solute entering or leaving each capillary by the simplified expression1 in which Ui is the electric mobility of the solute, ?mi the solute weight change, Ci the solute concentration of the reservoir, I the current, p the alloy resistivity, and l the duration of the experiment. This expression is valid as long as the experiment is terminated before a concentration gradient develops across the capillary orifice. Earlier experiments showed that the concentration gradient formed initially at the electrode changes with time and eventually reaches the orifice, due to back-diffusion. This condition produces a solute exchange between capillary and reservoir by diffusion or convection, opposing the electromigration, which results in a lower measured value for the electric mobility. To determine if the concentration gradient had reached the orifice, the capillaries used in some of the experiments were sectioned at 1-cm intervals and the solute content of the alloy from each section was radiochemically determined. A typical concentration profile for an experiment with indium in bismuth is shown in Fig. 1; cadmium in bismuth showed similar behavior. As illustrated in the graph, very little back-diffusion has occurred in the capillary containing the cathode, since the concentration gradient is confined to the upper 1 cm of the capillary. In the capillary containing the anode, however, the concentration gradient is much broader, extending nearly to the orifice, even though the net change in solute concentration is nearlv the same in both capillaries. Since cadmium and indium probably lower the density of bismuth when alloyed, depletion of the solute from the alloy adjacent to the anode would increase the density of the liquid in the uppermost region of the capillary. This would give rise to convective mixing within the capillary, causing the broadened concentration gradient. Conversely, the alloy adjacent to the cathode should have a reduced density as the solute concentration is increased by migration, explaining the "normal" concentration profiles found in these capillaries. This disparity was not found for electromigration of silver in bismuth. Both metals have similar densities at the operating temperatures, and nearly symmetrical concentration profiles were found in the two capillaries of each exueriment. This density effect was also apparently encountered when an attempt was made to measure diffusion coefficients for indium in liquid bismuth by the same technique which was successfully used to measure diffusion of silver in bismuth.&apos; Capillaries 1 mm ID and 2 cm

Jan 1, 1968

By R. Taggart, D. H. Polonis, J. C. McMillan

Thin foil electron microscopy techniques have been used to study the micros tructure of a Ti- 7.5 wt pct vanadium alloy in the quenched and aged cond_itions. Selected area diffraction has identified a (1011) twinning mode accompanying the martens ite t9.an.sfo?rn~ation. Precipitation of the 0 phase during the aging of quenched alloys has been obsevced to occuv in the form of plates and needles with preferential growth along the (1120) direction in the a&apos; matrix. In the present work, the micro structures of quenched and aged alloys of the 0 isomorphous Ti-V system have been investigated by means of thin-foil electron-microscopy techniques. Most of the previous studies of martensitic phases in titanium-base alloys have utilized optical microscopy and X-ray diffraction techniques. The application of transmission electron microscopy is more recent, and only a few such studies have been reported.1-5 This paper is concerned particularly with the crystallographic nature of substructures formed in the martensitic a&apos; plates. The early stages of aging or tempering have also been examined to determine the modes of precipitation from the martensitic solid solutions. Such information is essential in studying strengthening mechanisms and in determining the feasibility of high-strength rnartensitic alloys based on titanium. Liu and Margolin6 reported several types of substructures within the martensitic plates of quenched Ti-Mn alloys. It was later suggested by Liu7 that the structure of martensitic plates might be very complex and not single crystals as normally assumed. The sub-markings could not be identified with the two possible habit-plane orientations {334}ß and {344}ß, and it was not positively determined whether they are associated with mechanical twinning. The recent studies by Armitage5 on titanium martensites in a variety of commercial alloys have indicated that twinning does not generally accompany the transformation. This observation is in accordance with the Mackenzie and Bowles model for the transformation in pure titanium8 which suggests that twinning is not to be expected. However, a number of other recent investigators have reported twinlike substructures in the martensitic plates of several titanium systems including commercia1 titanium,2,3 Ti-Cu,5,9 Ti-Ta,1 and the commercial alloy Ti-8A1-1Mo-1V. Blackburn* has reported that the structure of quenched Ti-8A1-1Mo-1V depends on the prior solution temperature. He identified two types of martensitic structures, one of which is described as a heavily faulted hcp or twinned fcc structure and the other an hcp structure with a high internal dislocation density. The latter type exhibited some twinning with a (1011) twin plane. EXPERIMENTAL PROCEDURES AND RESULTS The alloy used in the present work was a 7.5 wt pct V alloy that was prepared by conventional arc-melting techniques. This alloy composition was selected

Jan 1, 1968

By R. L. Stegman, M. R. Achter

Nickel, fatigued in vacuum, shows intragranular crack initiation and growth at low temperatures. An increase in temperature initially prolongs fatigue life due to a more homogeneous distribution of slip. With a further temperature increase, the mode of failure undergoes a transitiotz to intergranular crack initiation with concurrent recrystallization which results in a shorter life. The transition temperature varies with bending strain and specimen purity. UNTIL recently, very little work has been done on the effect of temperature on the mechanism of fatigue and the resultant variation in fatigue life. Except for mild steel, where strain aging raises the strength at moderate temperature, fatigue lives had been shown to decrease with an increase in temperature. In their review article, Allen and Forrest&apos; summarized the work of McCammon and Rosenberg and of Forrest and Mann on the fatigue of copper from -269" to 325°C. The fatigue life vs stress curves remained roughly parallel over this temperature range, the fatigue strength decreasing progressively with increasing temperature. When testing was done in vacuum, the present authors&apos; found the results for nickel were different from those quoted above. Initially, the fatigue lives increased with temperature and then decreased as a grain boundary mode of failure was observed. The initial increase was attributed to a more homogeneous distribution of slip, a condition which was not as conducive to crack initiation as the bunching of slip lines observed at 20°C. Ronay, Reimann, and wood3 observed a similar change of slip line distribution in brass, tested in air, with rising temperature. Our previous observations were based on preliminary work with relatively few specimens, fatigued at comparatively low strains. To learn more about the mechanisms, the present investigation was undertaken for the purpose of studying systematically this effect over a wider range of strains and as a function of purity of the nickel. EXPERIMENTAL PROCEDURES The testing equipment, procedures, and specimen geometry have been described elsewhere.&apos; An optical technique to measure bending strains was used as de-

Jan 1, 1968

By William C. Sleppy

The nmgnetic susceptibility of heat-treatable aluminuin alloys is sensitive to chanyes such as solution or dissolution of solute and the precipitation of mew phases. By measuring the change in the magnetic susceptibility of aluminum alloys caused by various heat treatments, an empirical relation was found from which atomic arrangements in dilute binary alloys of copper, zinc, and magnesiutn in aluminum have been delineated. The relation predicts the ultimate formation of C1LA12 when copper is precipitated from solid solution in aluminum. Euidexce joy silovt- range order is found for copper in solid solution in aluminum in the sense that copper atoms avoid being nearest neighbors to an extent greater than would result from a purely random arrangertzeizt. Hume-Rothery has predicted such short-range order joy solid solution of copper in aluminum The Al-Zn system agrees with evidence obtained from X-ray scattering at small angles and predicts a tendency for zinc atoms to cluster in solid solution in aluminum. In the Al-mg system, the empirical relation indicates an approach to randor distribution of magnesium in solid solution in aluminum with a tendency for magnesium segvegation which increases with incveasing temperature. ThE magnetic properties of metals are complicated by the fact that contributions are made to them both by electrons of a "metallic" type which belong to the crystal as a whole, and by electrons in states localized on particular atoms. An expression1&apos;2 for the bulk magnetic susceptibility of aluminum may be written as the sum of three contributions: where XA1 is the bulk susceptibility of aluminum per gram of material (in the cgs system, the units are those of reciprocal density); Xa1+3 is the diamagnetic contribution of the electrons localized in ion cores; Xa1 is. the paramagnetic spin contribution of conduction electrons often called Pauli paramag-netism: Xa1 is the diamagnetic contribution of the conduction electrons often called Landau diamag-netism. Ion core diamagnetism arises from the precession of the electron orbits which occurs when a magnetic field is applied to a system of electrons moving about a nucleus. Its contribution to the magnetic suscepti- bility is small, temperature-independent, and unaffected by alloying. The conduction electron diamagnetism is also temperature-independent and arises from the translatory motion of the electrons. For perfectly free electrons this contribution should be exactly one-third of the Pauli spin paramagnetism, but this relation is seldom even approximately true. Blythe2 determined the conduction electron diamagnetism in pure aluminum and found it to be extremely small. Any change in the conduction electron diamagnetism caused by alloying is neglected in this work. The Pauli paramagnetic contribution3 to the magnetic susceptibility of aluminum depends upon the number of electrons that occupy excited states and whose spins can be turned parallel to an applied magnetic field. The number of electrons free to turn in the field is proportional to the temperature and each spin contribution to the susceptibility is inversely proportional to the temperature. A slight temperature dependence of Pauli paramagnetism occurs when the number of electrons occupying excited states cannot increase sufficiently to balance the inverse dependence on temperature of each spin contribution. The decrease of the magnetic susceptibility of aluminum with increasing temperature is attributed to a temperature dependence of the Pauli paramagnetism. Estimates of the Pauli paramagnetism of aluminum have been made by several workers.2,4,5 All of the values are in reasonably good agreement with each other. In this work Xal at 17°C is taken as 0.761 X 10-8 cu cm per g. An expression similar to [I] can be written for the magnetic susceptibility of an aluminum base alloy containing a fractional weight percent x of solute:&apos; Xa = (1 -x)XAl+3 +xXsoluteion * XaPauli +Xadia) [2] where X, is the magnetic susceptibility per gram of alloy, Xal&apos;3and Xsolute ion are the ion core diamag-netic contributions, and xpauli and xdia are the Pauli and diamagnetic contributions of conduction electrons in the alloy. If the components of a mixture are not alloyed but simply mixed together in their pure states without producing a new phase, then the magnetic susceptibility of the mixture is given by the Wiedemann additivity law: Xm =x1X1 +x2x2 + ..xnxp [3] where X, is the susceptibility per gram of mixture and xnXp are the weight fractions and susceptibilities, respectively,-. for the pure components. The additivity law is not applicable to alloys because the outer electronic structures of the components are changed by alloying.&apos; Both the Pauli paramagnetism and Landau diamagnetism are affected; hence the magnetic susceptibilitv of an alloy is usually different from that calculated using the additivity law. In this work the difference, X, -X,, is taken as a measure of the change caused by alloying.

Jan 1, 1968

By M. D. Banus, M. B. Bever, A. K. Jena

Measurements of the heat effects on addition of various solid phases of InSb to a solution calorimeter have confirmed the existence of a new high-pressure plzase InSbQII), which was jormed at 37 kbar and 623°K. The heats of formation of InSbQ), InSbfl), and InSb(111) have been measured and the heats of transjormation of InSb(1) to InSb(1l) and InSb(Iii) and of &apos;InSb(ll) to InSb(iiI) at atmospheric pressure and 78°K have been determined independently. Other thermodynamic properties of these phases, the phase boundary InSb(i)/InSb(ll), and the relative positions of the triple points are calculated. The pressure-Dolume term is shown to be more critical than the internal energy difference in making the phase InSbQ) less stable than InSb(II) at high pressures. Observations on partially transformed specimens suggest that the transformation of&apos; metastable InSb (III) takes place in the two steps InSb(lll) — InSbQI) and InSbQI) — InSb(l). The compound InSb can exist as several phases depending on the temperature and pressure. The phase InSb(I), which is a semiconductor having the zinc-blende structure, transforms into the phase InSb(11) at a pressure of about 23 kbar and room temperature.&apos;-3 The phase InSb(II) has the 6 tin structure,4-6 is metallic, and becomes a superconductor below 2.lok7 An orthorhombic phase of InSb has been reported to occur above a pressure of approximately 30 kbar at room temperature.&apos; This phase is also a superconductor below about 3.4k9 The phase InSb(I1) is retained at atmospheric pressure if it is quenched to 78°K under pressure,6,7 but tends to transform at higher temperatures and does so explosively above approximately 210ok,7 A value of the heat of transformation of InSb(1) to InSb(II) at 210°K and atmospheric pressure has been reported.&apos; A concurrent publication&apos;0 reports evidence for a new solid phase InSb(III), which was formed by annealing InSb above 58 1°K at 37 kbar, above 560°K at 52 kbar, and above 473°K at 65 kbar. Specimens of InSb(II1) had a superconducting transition temperature of 4.lo ± 0.1oK. X-ray diffraction patterns also indicated the presence of a new phase. In this communication, thermodynamic properties of the phases InSb(I), InSb(II), and InSb(II1) are reported and discussed. The phase boundary InSb(I)/InSb(II) and the relative positions of the triple points are calculated. 1) EXPERIMENTAL 1.1) Preparation of Specimens. Specimens of the high-pressure phases of InSb were prepared in a belt-type high-pressure chamber by a tichnique described in detail elsewhere.&apos;&apos; Charges of 0.6 to 0.8 g of Cominco semiconductor grade InSb were used. The temperatures were measured with a chromel-alumel thermocouple, the hot junction of which was within 0.5 mm of the specimen. The specimens were heated under a pressure of 37 kbar for 1 hr at 723°K (which is well above the liquidus) and quenched to room temperature. One set was annealed at 523°K and another set at 623°K for 20 to 24 hr. These annealing temperatures were chosen because 523°K was below and 623°K was above the temperature of the transformation of InSb(II) to InSb(1Tl) at 37 kbar.10 The specimens were then cooled to 125°K by passing liquid nitrogen through the jacket of the belt die before the

Jan 1, 1968

By M. J. Blackburn

The ordering reaction and its effect on dislocation awangements in alloys based on Mg3Cd has been studied by transmission electron microscopy. Ordering occurs by the growth of ordered domains until they impinge, thus producing an antiphase domain boundary (APB) network. In the disordered alloy, slip is confined to the basal plane while in the ordered condition slip occurs on the basal, prism, and pyramidal planes. Superdislocations have been identuied on these planes and their origin and expected spacings are discussed and compared with the observations. The APBs between the dislocation pairs have been resolved and have proved useful in the identification of superdislocations. Observed slip structures are related to the changes in mechanical properties produced by ordering. At high temperatures magnesium and cadmium form a continuous series of disordered hexagonal solid solutions. At lower temperatures three ordering reactions occur; two based on the compositions Mg3Cd and MgCd3 are transformations to DO19-type superlattices while alloys based on the composition MgCd transform to a B19 lattice. The ordering process in alloys near the composition Mg3Cd has been studied by several workers&apos;-4 and it has been shown to be a first-order type transformation. The variation of mechanical properties with the degree of order and temperature have been reported in some detail by Stoloff and Davies.5 It was shown that the disordered alloy was stronger and less ductile than the ordered alloy, the differences being attributed to changes in the number of active slip planes and to the presence of short-range order in the disordered alloy. In this investigation the ordering reaction has been qualitatively followed by transmission electron microscopy. The effect of this ordering transformation on the dislocation arrangements in deformed specimens has been studied in some detail. EXPERIMENTAL Alloys were melted in a stainless-steel crucible under a flux and chill cast; both melting and casting were performed in an argon atmosphere. The ingots were hot-rolled and tensile specimens cut from the resultant strips. Some large-grained specimens were grown by the strain-anneal method. Heat treatment was carried out in inert atmosphere furnaces and in oil baths at the lower temperatures. Thin foils for transmission electron microscopy were produced by electropolishing in a cooled solution (temp = -40°C) containing 50 cu cm of nitric acid and 180 cu cm of methanol at a potential of 10 v. The ordering reaction was followed by transmission electron microscopy, X-ray, and electrical resistivity measurements but this paper will be concerned chiefly with the electron-microscopy results. Much of the work described in this paper was performed on an alloy containing 26.10 at. pct Cd although two of the micrographs are taken from work on a 25.55 at. pct Cd alloy. RESULTS i) The Quenched Solid Solution. Specimens which were quenched from above the critical temperature showed diffuse superlattice reflections. sark-field analysis on these reflections failed to reveal the presence of ordered domains and thus the superlattice reflections were assumed to arise from regions of short-range order. Quenching from temperatures of 400" to 450°C results in the formation of dislocation loops and helical dislocations. Such defects have been observed and analyzed in detail in several hexagonal metals6-&apos; and as the crystallography and interactions of such loops appear similar in this alloy they will not be reported in detail. Fig. 1 shows a high density of loops

Jan 1, 1968

By R. H. Richman, F. Borik

A 0.3 pct C-12 pct Cr-6 pct Ni steel was rolled to 93 pct reduclion in area as austenite at 510°C, and then partially transformed as desired to ~rlartensite by qnenching to - 196°C. Pole figures for the austenitic matrix and for the martensitic product were separately determined by an X-ray transmission method. The deforitration texture of&apos; the warm-worked austenite is characlerized by (110)(225) components, and is thus closely similar to those produced in a brasses. The pole jigure of the martensite in partially transformed material agrees well with that which can be constructed by transfortnation of the {110)(225) orientations according to either the Kuvdjuniov- Sacks or the Nishi-yatuu relatiotship. Howeuer, an important result of this construction is that me-third of the predicted orientations are missing. A graphical analysis can then be used to show that in deformed austenite certain crystallographic variants of martensite (related to the most probable austenite slip systems) are suppressed, resulting in this preferred transformation. The evidence for preferred transformation is corroborated by the measured elastic anisotropy of warm-rolled and fully transformed H-11 steel. EXTENSIVE plastic deformation of a polycrystal-line aggregate in a manner that causes flow predominantly in one direction results in a preferred orientation of the constituent crystallites. The particular orientations that are produced depend upon the crystal structure and composition of the material, as well as upon the temperature, mode, and degree of deformation; in any case, the preferred crystallo-graphic orientations, or textures, are reflected in directionality of mechanical properties. Although such anisotropy may be exploited in certain specialized applications, it is more commonly diminished or eliminated by heat treatment lest it interfere undesirably in subsequent forming operations or in structural design. In the recently developed thermomechanical treatments that significantly enhance the strength of some steels,1,2 considerable deformation of the metastable austenite prior to the martensite transformation is essential to the strengthening process. If the austenite is textured by the deformation, and if the transformation to martensite proceeds according to one of the relationships established for transformation in annealed austenite, then it must be expected that the martensite will also possess a preferred orientation even though the multiplicity of martensite orientations possible in a given austen- ite crystal will tend to restore some degree of randomness. The existence of a residual anisotropy, both mechanical 3-6 and crystallographic,&apos; has been substantiated. In the latter crystallographic investigation, preferred orientations were determined for the martensitic structure of an SAE 4340 steel rolled 72 pct as austenite at 833°C and then quenched. However, the choice of a composition that transformed almost completely to martensite during the quench to room temperature did not permit direct measurement of the prior austenitic texture. In fact, when the "ideal orientations&apos;&apos; associated with well-known fcc rolling textures were converted, alone or in combination, to martensite according to the Kur-djumov-Sachs (K-s)&apos; or Nishiyama8 relations, the agreement obtained with the observed martensite texture was only fair at best. Recently a pertinent aspect of the austenite to martensite transformation was reported by Bokros and parker,10 who found that certain habit-plane variants of martensite were suppressed by tensile deformation of Fe-31.7 Ni single crystals prior to the necessary subzero cooling. It might be anticipated that the consequences of such preferred transformation are sustained during the formation of martensite in warm-worked austenite that has a well-developed deformation texture. The present investigation was undertaken first to establish more firmly the relation between preferred orientations in plastically deformed austenite and in the resulting martensite, and second to examine the textures for evidence of deformation-induced preferred transformation. EXPERIMENTAL PROCEDURES An alloy containing 0.3 pct C, 12 pct Cr, 6 pct Ni, and the balance iron, was selected because the mar-tensite-start temperature (M,) of about -100°C allowed convenient experimental manipulation of either austenite or martensite at room temperature. Furthermore, this composition can be readily deformed as metastable austenite at moderately elevated temperatures without intervention of appreciable isothermal or athermal decomposition products. The alloy was austenitized at 1150°C, aircooled to 510°C, rolled unidirectionally at this temperature to 93 pct reduction of cross-sectional area, and finally oil-quenched to room temperature. Partial transformation to martensite was accomplished by quenching to -196°C as needed. The rolled stock was reduced in thickness from 0.067 to 0.010 in. by etching in a solution of 5 pct HC1, 45 pct HNO3, and 50 pct water, and further thinned by careful mechanical polishing to maintain the two sides of the sheet parallel within 0.0003 in. After mechanical polishing to 0.005 in., electropolishing in 1:9 perchloric-acetic acid solution produced a final thickness of 0.002 in. The preferred orientations were determined from

Jan 1, 1968

By R. B. Adamson

The fatigue behauior of irradiated copper single crystals is compared to that of unirradiated crystals. Proton or electron irradiation did not substantially change the fatigue-lzj.e, fatigue-hardening-, or slip-line characteristics, while neutron irradiation did appear to alter these parameters. Postfatigue transrrzission electron microscopy did not reveal any marked structural differazces between irradiated and unirradiated specimens. Possible dislocatio~a mechanisnzs to explain the observed behavior are discussed. A LTHOUGH considerable work has been done to ascertain the effects of radiation on the tensile properties of metals (e.g., Refs. 1 and 2), little work of a basic nature has been reported on the effect of radiation on fatigue properties. Since it is known that fatigue properties are sensitive to conditions at the surface of the metal, it was felt that charged particle irradiation, whose penetration into metals is very small, might influence the fatigue behavior. To investigate this surface effect, irradiations with 10 mev protons and 1.5 mev electrons were conducted. The range of 10 mev protons in copper is about 0.236 mm; which is very small compared with the thickness of the specimens used (1.53 mm). The range of 1.5 mev electrons is somewhat larger, on the order of 0.665 mm.4 On the other hand, irradiation with reactor neutrons produces damage throughout the entire specimen, so neutron irradiation can be used to study the effects of bulk damage. The damage introduced by proton and neutron irradiation is expected to con!ist of large interstitial dislocation loops,5 tiny (<25A) vacancy loops," and/or various vacancy-rich regions called depleted zones.&apos; In the case of electron irradiation at about -173°C the damage is expected to consist of isolated Frenkel pairs.&apos; The effect of radiation damage on the fatigue properties of some engineering materials has been reported,g,10 but the results are not clear-cut or consistent. SPECIMEN PREPARATION Zone-refined copper was used to grow single crystals by a modified Bridgeman technique in an inert helium atmosphere. Using a seeding method, single crystals were obtained as bars about 6 in. long with a cross section of 3 by $ in. Immediately upon removal from the split-mold graphite boat in which they were grown, the very soft bars were embedded in a room-temperature setting plastic. They could then be cut into specimen lengths without introducing any long-range damage. Generally, four or five specimens plus one seed were obtained from each bar. The plastic material was dissolved away in acetone and the orientation of each sample was checked by the standard Laue X-ray

Jan 1, 1968

By J. D. Verhoeven

The effectiue distriblltion coefficient has been Measured in a series of vertical, normal freezing experirtzents with large current densities passing through the solid-liquid interface. The results indicate that the effect of the current on solute redistribution is due to electvotransport in the liquid. The high currents produced extensive mixing in the liquid which was considerably reduced by solidifying in small lubing. Analysis of the convection indicates that it probably vesulls from a horizontal temperature gradient produced by the Joule heating- of the electvic crirver~t. Due to the strong dependence of this convection upon the specimen radius, it is conclnded that only for specit~ens with radii of less than somewhere between 1 and 2 mm wilt electric field freezing be getlerally effec-tire at enhancing the purification of zone-melting experittierats in loe-melting alloys. Experiments on 0.8-mm lubes illustrate some interesting potential applications of this techniqne as a means of solute control on smcrll specimens. In a number of papers published within the last few years&apos;-4 it has been found that passage of large dc currents through the solid-liquid interface of a freezing alloy produces a change in the solute redistribution accompanying the solidification. It had been predicted theoretically by Hucke et al.s and by Pfann and Wagner that such an effect would occur as the result of electrotransport within the liquid boundary layer at the solid-liquid interface. These authors independently derived the following relation between the effective distribution coefficient and the variables of the process: Where k0 is the equilibrium distribution coefficient, V is the mobility of the solute relative to the solvent, E is the electric field intensity, D is the solute diffusion coefficient, R is the rate of interface motion, and 6 is the boundary layer thickness. Both groups of authors show that this equation predicts the possibility of extending the purification ability of zone-melting experiments by the addition of an electric current. However, there are other effects in addition to electro-transport which could be produced by the high dc current and might, perhaps, invalidate the applicability of Eq. [I]. For example, high electric current might affect the interface reaction or perhaps the equilibrium distribution which was assumed to exist at the interface. It was the purpose of this work to determine the applicability of Eq. [I] by systematically investigating a simple system for which all of the necessary parameters were known. It was of particular interest for speculating on the potential usefulness of this technique to determine the maximum practical field intensities obtainable, and the effect of these high fields upon convective mixing in the liquid. The initial work in this study was published in a previous paper3 which will be referred to as I. In that work, a current density of 2000 amps per sq cm was used with specimen diameters of 5 mm. The results gave a qualitative confirmation of Eq. [I.], and also showed that a large amount of convective mixing was produced in the liquid by the current. The present study is an extension of that work to smaller specimen diameters and higher current densities. Two points were overlooked in I and will be emphasized here: a) the value of ko has not been well-established in the Sn-Bi system and b) the observed convection could be due to thermal convection produced from the Joule heating. EVALUATION OF k0 To evaluate Eq. [ I.] it is necessary to know the value of the equilibrium distribution coefficient, k,. Tn I the value of k, was taken as 0.3 from a published phase diagram.7 According to ansen&apos; the best data on the phase boundaries of the Sn-Bi system are those of Davidson.5 The data of Davidson give a k, value ranging from 0.21 to 0.25 for the compositions studied in this work, or an average value of around 0.23. In a recent publication, Rigaud and Tougas&apos;10 determined ko by means of a solidification technique. For an alloy of approximately the same composition as that used in this work they obtained a ko value of 0.39. Hence, there is considerable uncertainty in the value of ko and, consequently, a series of experiments were made to determine k, more accurately.

Jan 1, 1968

By R. Grierson, L. J. Bonis

The high-temperature Strength oF TD nickel has been observed to be dependent upon the previons thermal and mechanical history of the material. Variations in both the level and the anisotropy of strength have been observed. 01 this paper- these variations are correlated with the storing of annealing resistant elastic strain energy in the matrix of the TD nickel. An x-vay line -broadening tecknique is used to measure the maLrTis elastie strain. THE inclusion of a finely dispersed second phase into a ductile matrix has long been recognized as an extremely effective method of strengthening the matrix both at high and at low homologous temperatures. It has been found, however, that the factors which determine the high-temperature strength are not the same as those which are important at low temperatures. Below 0.5 Tm the size and distribution of the second phase particles are of prime importance in determining the strength,&apos;)&apos; while above this temperature the strength is mainly dependent upon the previous thermal and mechanical history of the alloy,3-7 This paper is primarily concerned with explaining the response of the high-temperature mechanical strength of one of these alloys (DuPont&apos;s TD nickel) to various thermo-mechanical treatments. It will be shown that this response is not associated with the occurrence of any form of dislocation substructure within the matrix of the alloy. It has been found, however, that a correlation does exist between the elastic strain level in the matrix and the previous thermomechanical history of the alloy and that the observed changes in elastic strain level parallel the measured changes in high-temperature strength. It therefore must be concluded that variations in high-temperature strength are a direct result of the variations in elastic strain level. MATERIAL TD nickel contains approximately 2 vol pct of Tho2 in an unalloyed nickel matrix. It is formed, as a powder, by a chemical technique and this powder is compacted to form ingots which are then extruded to give 21/2-in.-diam rod. Rod of smaller diameter is prepared from the as-extruded rod by swaging. In the studies reported in this paper, 1/2-in.-diam rod was used. This rod received an anneal of 1 hr at 1100°C prior to being used in any of these studies. EXPERIMENTAL TECHNIQUES Two methods were used to examine the structure of the nickel matrix of the TD nickel. These were: 1) transmission electron microscopy; 2) the analysis of the position and profile of X-ray diffraction lines obtained using the nickel matrix as the diffracting media. To prepare thin foils for electron-microscopical examination, slices of TD nickel approximately 0.050 in. thick were cut from the as-received 1/2-in.-diam rod. These were then chemically polished down to 0.045 in., rolled to 0.009 in., given a predetermined heat treatment, and thinned, using a modified Bollman technique, to provide the foils for observation. All observations were carried out at 100 kv, using a Hitachi HU-11 electron microscope. Specimens of the undeformed rod were prepared by grinding down the 0.050-in.-thick slices to approximately 0.015 in. and then thinning chemically and electrolytically to give the thin foils. The X-ray specimens were prepared by rolling 0.375-in.-thick rectangular blocks down to 0.075 in. The surfaces of the rolled material were ground flat, chemically polished to remove the layer disturbed by the grinding, and given a predetermined anneal in an inert atmosphere. They were then ground lightly to check their flatness and given a final chemical polish prior to being examined. The X-ray diffraction line profiles were measured using an automated Picker biplane diffractometer. A special specimen holder was built to allow a more accurate and reproducible positioning of the specimen. The line profiles were determined by carrying out intensity measurements at intervals of either 1/30 deg or 1/60 deg over a range of 3 deg on either side of the nickel peaks of interest. A piece of pure nickel which had been recrystallized to give a large grain size was used as a standard to give the X-ray line profile generated by a strain-free matrix. The analysis of the X-ray diffraction line profiles is a modification of that due initially to Warren and Aver-bach8and has been described elsewhere.3 This analysis gives a measurement of two parameters associated with the structure of the nickel matrix. These parameters are: 1) the size of the coherently diffracting domains within the nickel matrix; 2) the magnitude of the elastic strains in these domains. Both of these parameters are first determined in terms of a Fourier series. These series are obtained from other Fourier series which describe the measured profile of the X-ray diffraction lines. Thus, for both the coherently diffracting domain size and the elastic strain level, it is possible to plot Ft (the Fourier coefficient) against t (the term in the Fourier series), where t can be expressed in terms of a distance L and the Fourier coefficient Ft(S) (associated with elastic strain level) can be expressed in terms of the root mean square strain (e2)1/2. Thus a plot of (F 2)1/2 vs L can be obtained. Plots of this type are shown graphically in Figs. 6 and 8. Interpretation

Jan 1, 1968