Search Documents

By R. K. Ham, M. L. Wayman

TD-Nickel has been broken in tension and in fatigue at voom temperature. Rod specimens failed in tension by necking, with axial cracks attributed to voids elongated in the extrusion direction. Fatigue specimens failed in shear. Thin-film electron microscopy showed that the subgrain structure of TD-Nickel was very stable, and that particle-matrix detachment was very difficult, in tension and fatigue. TD-Nickel softened slightly during fatigue but had a high fatigue ratio (0.5at 10' cycles). Fractography suggested that Stage I fatigue crack propagation is greatly extended in TD-Nickel. Td-NICKEL* is a dispersion of 2 pct by volume of thoria (ThO2) in nickel, produced by powder-metallurgical methods including compaction, sintering, and extrusion. The spherical thoria particles, which may have a mean diameter of a few hundred angstroms, are dispersed with a mean planar spacing of a few thousand angstroms. By a combination of cold working and annealing, a subgrain or cell structure of dislocations intimately associated with the dispersion can be produced.' This gives the material useful tensile properties which are extremely resistant to exposure to high temperatures.'-= At the same time, the material shows considerable ductility.3'4 At the beginning of the present work, it was considered of great interest to investigate the mechanical stability of TD-Nickel under conditions of fatigue. On the one hand, materials which derive strength from a cold-worked structure are unstable in that they are susceptible to fatigue softening: in addition, the presence of discontinuities such as the particle-matrix interfaces might be expected to assist in the initiation and propagation of fatigue cracks, in that they may provide local concentrations of internal stress and sites for the initiation of voids." On the other hand, the substantial ductility of TD-Nickel suggests that if it obeys Coffin's relation8 (or the more refined form proposed by Manson9) it should have good fatigue resistance. The initial purpose of this investigation was to assess the importance of these factors. Also, relatively little fundamental work has been done on the mechanism of fatigue in dispersion-strengthened materials. Work on overaged A1-4 pct CU10-12 revealed a very large Bauschinger effect indicative of internal stresses at the particles, and very great fatigue hardening1' presumably due to the multiple slip stimulated by these internal stresses, followed by softening which was initially due to softening in the matrix, but later might have arisen from cracking at the particle-matrix interfaces. The study of overaged Al-4 pct Cu could not settle this latter point by the electron microscopy of thin films, since the dispersion is too coarse. A previous study of the fatigue of internally oxidized copper13 was complicated by inter granular failure, attributed to oxide particles at grain bouhdaries; internal oxidation of single crystals, however, improved their fatigue properties.'3 Investigations of SAP (sintered aluminum powder) are complicated by the complex particle shapes, and the possibility of continuous internal oxide films.14 It was hoped to avoid these difficulties with TD-Nickel, which had the further advantages that it was commercially available and suitable for study by the thin-film technique. 1) MATERIALS AND EXPERIMENTAL PROCEDURE TD-Nickel was purchased from the Driver-Harris Co. as 3/9-in.-diam rod which had been extruded, swaged, and "stress-relieved" (normally at 1010°C for 1 hr). Continuous-radius fatigue specimens with a minimum diameter of -0.1 in. were ground to shape and electropolished in 40 pct phosphoric, 35 pct sul-furic, 25 pct water at 25oC, with a stainless-steel cathode, at -6 v. Fatigue tests were carried out at room temperature with a Sonntag SF-1-U machine operating in push-pull at 1800 cycles per min, and in an Instron TT-C-L modified for reversed stressing at 26 cycles per min as described elsewhere.10 Round tensile specimens were ground with 0.85-in. gage lengths of 0.135 in, diam, electropolished, and tested in a Tinius Olsen hydraulic machine. The surfaces of fatigue specimens were examined with a Reichert metallograph. Discs for electron microscopy with a Siemens Elmiskop I were spark-cut 0.01 in. thick with a modified Servomet 11 employing a tool of moving molybdenum wire, cleaned in 50 pct acetic, 30 pct nitric, 10 pct phosphoric, and 10pctsul-furic at 85oC, and thinned by the window method in the electropolishing solution at -20°C and -6 v. Two-stage replicas (parlodion, then Pt-50 pct C self-shadowed at 40 deg) were taken from fatigue fracture surfaces for electron microscopy. Plane sections parallel to the specimen axis and containing the direction of fatigue crack propagation were polished, etched with Carapella's reagent, and examined optically. Transmission Laue X-ray photographs of as-received material electropolished to a point were used to determine preferred orientation. 2) RESULTS 2.1) The Structure of As-Received Material. Grains -1 µ diam and elongated 20 to 30 u in the direction of the rod axis were observed, With' elongated "intergran-ular" voids (-4 p diam and -90 µ long and identified as such using longitudinal and transverse sections and

Jan 1, 1968

By R. T. DeHoff

In any structural transfortnation which is driven by surface tension, the geometric variable of fimdamental importance is the local value of the mean surface curvatuve. Acting through the suvface free energy, this quantity determines the magtnitude of both the pressure and the chemical potential that develops in the neighborhood of an arbitrarily curved surface. A metallographic method which would permit the quaniitatiue estinzation of this propevty is of fundarnerztal irztevest to studies of such processes. In the present paper, it is shoun that the average value of the mean surface curvature in a structuve can be estimated from two simple counting measuretnents made upon a vepresentative metallograpIzic section. No simplifyirlg geonzetric assurmptions are necessary to this deviuation. It is further shoum that the result may be applied to parts of interfaces, e.g., interparticle welds in sintering, or the edge of growing platelets in a phase transformation, without loss of validity. In virtually every metallurgical process in which an interface is important, the local value of the mean surface curvature is the key structural property. This is true because the mean curvature determines the chemical potential of material adjacent to the surface, as well as the state of stress of that material. The theoretical description of such broadly different processes as sintering,1,2 grain growth,3 particle redistrib~tion4,5 and growth of Widmanstatten platelets8 all have as a central geometric variable the "local value of the mean surface curvature". The tools of quantitative metallography currently available permit the statistically precise estimation of the total or extensive geometric properties of a structure: the volume fraction of any distinguishable part:-' the total extent of any observable interface,10,11 and the total length of some three-dimensional lineal feature:' and, if some simplifying assumptions about particle shape are allowed, the total number of particles.'2"3 The size of particles in a structure, specified by a distribution or a mean value, can only be estimated if the particles are all the same shape, and if this shape is relatively simple.14-16 The relationships involved in converting measurements made upon a metallographic section to properties of the three dimensional structure of which the section is a sample are now well-established, and their utility amply demonstrated. In the present paper, another fundamental relationship is added to the tools of quantitative metallography. This relationship is fundamental in the sense that its validity depends only upon the observation of an appropriately representative sample of the structure, and not upon the geometric nature of the structure itself. It involves a new sampling procedure, devised by Rhines, called the "area tangent count". It will first be shown that the "area tangent count" is simply related to the average value of the curvature of particle outline in the two-dimensional section upon which the count is performed. The average curvature of such a section will then be shown to be proportional to the average value of the Mean surface curVature of the structure of which the section is a sample. The final result of the development is thus a relationship which permits the evaluation of the average value of the mean surface curvature from relatively simple counting measurements made upon a representative metallographic section. The result is quite independent of the geometric or even topological nature of the interface being studied. QUANTITATNE EVALUATION OF AVERAGE CURVATURE IN TWO DIMENSIONS The Area Tangent Count. Consider a two-dimen-sional structure composed of two different kinds of distinguishable areas (phases), Fig. l(a). If the system is composed of more than two "phases", it is possible to focus attention upon one phase, and consider the remaining structure as the other phase. The reference phase is separated from the rest of the structure by a set of linear boundaries, of arbitrary shapes and sizes. These boundaries may be totally smooth and continuous, or piecewise smooth and continuous. An element of such a boundary, dA, is shown in Fig. l(b). One may define the "angle subtended" by this arbitrarily curved element of arc, dO, as the angle between the normals erected at its ends, Fig. l(c). Now consider the following experiment. Let a line be swept across this two-dimensional structure, and let the number of tangents that this line forms with elements of arc in the structure be counted. This procedure constitutes the Rhines Area Tangent Count. Suppose that this experiment were repeated a large number of times, with the direction of traverse of the sweeping lines distributed uniformly over the semicircle of orientation.' Those test lines which ap- proach from orientations which lie in the range O to O + dO form a tangent with dA; those outside this range do not, see Fig. l(c). Since the lines are presumed to be uniformly distributed in direction of traverse, the fraction of test lines which form a tangent with dA is the fraction of the circumference of a semicircle which is contained in the orientation range, dO; i.e., vdO/nr or dB/n. If the number of test lines is N, the number forming tangents with dA is N(d0/n). Since each test line sweeps the entire area of the sample, the total area traversed by all N test lines is NL2. The number of tangents formed with dA, per unit area of structure sampled, is therefore

Jan 1, 1968

By John Chipman, Raymond L. Orr

Recently reported high -temperatlnre thermal data have been incorporated in a reuieu' of the therinody-r~ar,zic propesties of iron. The recent data permit mot corlsisterlt and reliuble choices to be made for many of the pvoperties, resnlling in bettev eslablished tabrtlations of the thermodynamic functions. Values of Cp, h°t- - H°298. s°t - S2sa, and (G°T -H298/T are tabulated for -the solid and liquid phases of iron in both stable and melastable regions. Consistency of the tabulations has been maintained to the precision necessr~vg to yield the Gibbs energy change belween the bcc (a, 8) and fcc (y) phases of iron at temperatures pertinenl to alloy studies. THE importance of the metal iron has stimulated many investigations of its thermodynamic properties at elevated temperatures. Reviews and summaries of the data have appeared from time to time. Among these the 1951 paper of Darken and smith' deserves highest recognition for the quality of its criticism and for the precision and thermodynamic consistency of its tabulations. These and the more recent table of Kaufman, Clougherty, and weiss2 reproduce the Gibbs energy of the (a, 6)--Y transformation with sufficient sensitivity for alloy studies. Other recent compilations of equal validity3-' make no attempt to do this. Since this Gibbs energy change is not greater than 22 cal per g-atom over the temperature range 1100° to 1800°K, it is obviously desirable to tabulate values of (G°t - H298)/T to four places of decimals even though the absolute accuracy would not warrant such precision. The necessity for reconsideration of the problem is emphasized by the recent publication of several important researches on the enthalpy and heat capacity of iron. The older work is well-covered in the reviews cited and will be mentioned here only when actually employed in the tabulations. GAMMA IRON Transition temperatures are taken from the selec -tions of Elliott and Gleiser,5 based on the work of Boulanger7 and earlier workers. For the a-y (A3) transition at 1184°K we retain the value 215 cal per g-atom adopted by Darken and smith.' It has received confirmation in the recent work of Dench and Kubaschewski,' and of Braun8 using adiabatic calori-metry, and of Wallace, Sidles, and Danielson10 using a pulse heating technique. The enthalpy data of Olette and ferrier" and of Anderson and Hultgren12 at higher and lower temperatures may be extended to 1184°K to give the following values which are adjusted to the required value of ? 1184 Ha,1184 Ha 298 = 8030 cal per g-atom [11 hr,1184-ha298 = 8245 cal per g-atom [2]

Jan 1, 1968

By Marius S. Darrow, William B. White, Rustum Roy

The PbS-PbTe systen has been studied by quench-ing and D.T.A. techniques f?om 400' to 1150°C. Runs were made in evacuated silica tubes so that all equilibria are at the vapor pressure of the system. Lattice parameters of the quenched salnples , measured by X-ray diffraction, show a complete crystalline-solution series existing over a narrow temperature range between approximately 805" and 871°C. An exsolution dome extends from a maximum of about 805"C (approximately 30 mole pct PbTe) to 1 and 96.5 pet PbTe at 400°C. A narrow melting region, deternined by D.T.A., extends form 918c (mp PbTe), The shapes of the liquides and solidus curves imply the existence of a minimum at 871°C at approximately 65 pct PbTe. THe exact composition of the minimum could not be established due to the very narrow two-phase region. At compositions containing less than 50 pet PbTe, liquidus temperatures begin to increase, while the solidus remains almost flat to about 15 mole pet PbTe before beginning to vise toward the mp of PbS (1075 C). LEAD sulfide and lead telluride are isostructural (NaC1 type) semiconductors whose electrical and optical properties have been extensively studied and used in recent years. If appreciable crystalline solution exists between these compounds, the variation of physical properties with composition could be of interest. The purpose of this investigation was to determine the extent, if any. of crystalline solution, and to obtain the phase diagram for the system. To the knowledge of the authors, only three studies of the system PbS-PbTe have been reported, and, in chronological order, each investigation found an increasing amount of crystalline solution. In 1956, Yamamoto reported finding no evidence of crystalline solution between the compounds. Sindeyeva and Godov-ikov,' in 1959, found very limited crystalline solution. but only under conditions of excess tellurium concentration. Finally Melevski s3 investigation in 1963 indicated that one solid phase exists in the region from PbS to 7 pct PbTe and from 82 pct PbTe to PbTe at 886'C, with an eutectic at 55 pct PbTe at that temperature. Detailed data on the solvus boundary were not given. EXPERIMENTAL EQUIPMENT AND MATERIALS Commercially produced PbTe and PbS powders were used as starting materials. Batches of specific mole percent composition were accurately weighed and mixed in a plastic bottle, in a shaker mill. An analy- sis of impurity content is given in Table I for pure PbS and PbTe and for two randomly selected batches after the powders were mixed. Individual samples, ranging in weight from 0.2 to 0.5 g, were sealed in evacuated silica tubes which had been thoroughly washed and rinsed with acetone and distilled water. Thus all data taken were at the pressure of the system. Subsolidus relations were studied down to 400°C by heating the samples in a vertical tube furnace for 24 hr. The sealed tubes were quenched in water with quench time from the hot zone not exceeding 1 sec. Temperatures were measured by a chromel-alumel thermocouple and controlled to 53°C for most runs. The number and composition of phases present were determined from powder X-ray diffraction patterns taken at room temperature on a Norelco diffractome-ter, using silicon as an external standard. Above 850°C quenching techniques were, in general, found to be unsatisfactory, and differential thermal analysis (D.T.A.) was used to determine melting relations. The evacuated tubes were recessed about 1 cm at one end to accommodate the differential thermocouple. Al203 was used as the reference material in a similar tube containing the other side of the differential couple. For temperature measurements, a separate thermocouple was placed in the recess of the tube containing the sample to be measured, thus providing an opportunity to obtain thermal, as well as differential, analysis. All thermocouples for these measurements were Pt-Pt 10 pct Rh. Temperature and differential curves were recorded separately on synchronized strip-chart recorders. Thermocouples and recording equipment were calibrated using NaCl and gold standards, using the melting points 801" and 1063 C, respectively, which span most of the temperature range of interest. Heating and cooling rates generally were from 4 to 7°C per min. It was found, in fact. that rates ranging from 1.5 to 25°C per min did not significantly change the data obtained.

Jan 1, 1967

By Merton C. Flemings, Harold D. Brody

Analyses that include diffusion of solute in the solid phase are formulated to describe solute redistribution in dendritic solidification of metallic alloys. The analyses are based on conditions that include negligible undercooling before nucleation of solid phases, negligible increase of solute in advance of the tips of growing dendrites, complete diffusion within the liquid over distances the order of dendrite spacings, and a plate-like dendrite morphology. The classical nonequilibrium freezing equation, Cs = kCo(I - fS)k-l accurately describes solute redistribution between dendrite arms for the solidification processes considered, provided diffusion in the solid is negligible. To account for the effect of diffusion in the solid, an analytic expression is given which is similar inform to the classical expression. 172 addition, a numerical-analysis procedure is etnployed to examine in more detail the effect of diffusion both during and after solidification. The analyses are intended for application to solidification of castings and ingots to describe a) final solute distribution after solidification and cooling to room temperature (microsegregation) and b) local fraction solid as a function of ternperatcre within the solidifying casting or ingol. SOLUTE redistribution in cellular and dendritic solidification has been discussed quantitatively in recent papers'-3 and in a series of earlier work.4-6 However, none of the analyses developed have permitted close correlation of theory with final solute distribution (microsegregation) observed in castings and ingots. In this paper, discussion is given of approximations which may reasonably be made in mathematical treatment of microsegregation, and analyses are presented based on these approximations. Numerical results are given for Al-Cu alloys. In a second paper the analyses will be compared with exeriment.7 CLASSICAL ANALYSIS The classical quantitative treatment of solute redistribution within a closed "volume element" has been derived repeatedly, for example by Gulliver,4 Scheil,' and Pfann.' This "classical nonequilibrium solidification equation" is written for constant partition ratio: where Cs = interface composition of the solid when the weight-fraction solid within the "volume element" is fs (weight fraction, wt pct); k = equilibrium partition ratio; Co = initial alloy composition within the volume element (weight fraction, wt pct). Assumptions of Eq. [11 are: 1) There is negligible undercooling before nuclea-tion, or from curvature or kinetic effects. 2) There is no mass flow in or out of the volume

Jan 1, 1967

Jan 1, 1967

By C. E. Coleman, D. Hardie, A. E. Wraith

A photoguaplric method of measuring crack velocities has been applied to an examilzation of- the effect of hydrogen on the impact properties of zirconium. Results indicate that the crack in hydrided zirconit travels at about 26 m per sec whereas that in the uacuum -annealed is dependent on the speed of the hammer. RECENT work on the effect of hydrogen on zirconium reveals that when hydrided zirconium is tested in slow bending the crack producing failure can be unstable. The mode of fracture seems to involve the crack linking up broken hydrides by a ductile mechanism in the zirconium matrix.2" In order to compare the fracture of zirconium with that of other metals which show unstable crack propagation, notably steel, the rate of the crack spread must be known. As the methods previously used for measuring crack growth are either unsuitable for the present work5-'' or very costly," a simple technique has been devised in which the maximum crack velocity is derived from a series of crack position-time measurements. EXPERIMENTAL PROCEDURE The experimental arrangement is shown schematically in Fig. 1. The flash unit12 was triggered when the Charpy hammer touched the specimen and the 6-psec flash of the lamp delayed by a preselected time interval in the range 100psec to 10 msec. The camera was left on open shutter during the test. From direct measurement on a calibrated photographic print, Fig. 2, the position of the crack and the specimen was found at a known time after impact and, from a series of such tests using an appropriate range of flash-delay times, the crack velocity was estimated. Preliminary experiments were carried out on mild steel above and below its transition temperature. Vacuum-annealed zirconium, and zirconium hydrided to 100 ppm H were then tested at 20" and 150°C. For comparison, Zr-2.6 pct Nb alloy (in the 0 + transformed /3 condition), vacuum-annealed or hydrided to 100 ppm H, was tested at 20 C. The chemical analyses of these materials are given in Table I. For the high-temperature tests a fine chromel-alumel thermocouple was spot-welded onto each specimen close to the notch. The test piece was heated up to 200°C to allow enough time for preparing the apparatus while the specimen cooled to the testing tem- perature. It was assumed that the specimen cooled uniformly. The accuracy of the flash-delay time was better than i2 pct i 5 psec. The crack length was taken as its maximum distance traveled normal to the length axis of the specimen. Errors in these measurements arise as a result of the uncertainty in the location of the crack tip and the difficulty in defining the exact position of the crack starting point. The latter was due to the bonding and large amounts of deformation at the hammer contact point, especially in the vacuum-annealed specimens tested at 150°C. The maximum error in the measurements was however estimated to be about 5 pct. DISCUSSION OF RESULTS From the trial experiments using mild steel above its transition temperature it can be seen from the plot of crack length against time after impact, Fig. 3. that a reasonable estimate of the maximum crack velocity at the surface of the specimen may be made. Other features of note are the initiation time before the crack is first seen and the slowing down period

Jan 1, 1967

By C. B. Alcock, M. G. Hocking

The kinetics of the growth of sulfate layers on blocks of Cu20 has been studied between 688" and 800°C. At 788c the over-all weight increases followed the parabolic rate law, with k = 216 30 sq mg per cm4 min, using a 1:1 entering gas mixture of SO2:02. At 757 after an initial linear period the parabolic rate law was followed, with k = 57.8 10 sq mg per cm4 min. The gas mixture required a platinum catalyst to produce the maximum SOs pressure. The sulfation rate at 757' and 788c was high until all the CUZO had changed into a core of CuO, when it became very much lower. At 757°C marker experiments showed that the sulfates (CuO. CuS04 and CuSO4) grow outwards from the oxide surface, but CuO. CuS04 mixed with CuO was found beneath the markers. At 688 markers were found at the CuO. CuS04/CuS04 interface. Visual observations at 757 showed a liquid eutectic moving beneath the sulfate surface. causing very rapid sulfation and extruding to solidify as thick 'needles" up to 8 mm long. Marker experiments have shown conclusi.cely that CuO grows on Cu20 in air by the outward migration of copper. ThermODYNAMIC measurements on the sulfate and basic sulfate of copper, reported recently,' are followed here by measurements of the rates of formation of these sulfates on cuprous oxide, in order to provide a background for the understanding of roasting processes. peretti2 and McCabe and Morgan3 have shown that the phase Cu20 lies next to Cu2S when the sulfide is roasted under conditions where sulfates will be formed. Since this would present too complex a system for kinetic study, the present work4 has been based on the kinetics of sulfation of the oxide phase. The results of a study of the kinetics and mechanism of the sulfation of cobaltous oxide have recently been reported.4,5 Results on the sulfation of cuprous oxide have also appeared,6 but are at variance with those to be reported here. This seems to be because the previous workers6 did not obtain constant SO3 pressures from the SO2/O2 sulfating gas mixtures used, as will be discussed later. Wadsworth, Leiter, Porter, and Lewis found that the sulfates produced when SO2/O2 mixtures are passed over Cu20 at red heats are CuS04 and the basic sulfate CuO.CuSO4. When the decomposition of CuS04 was followed' by differential thermal analysis, a stage corresponding to CuO .CuS04 was reached before decomposition into the oxide occurred. APPARATUS The vertical furnace used for quantitative studies was a conventional resistance-heated and propor- tionately controlled furnace with an even zone (1 deg) which was 4 cm long. The gas mixtures of SO2 and 02 were made by mixing measured flows from capillary flowmeters and drying over phosphorous pentoxide before passing them into the Pyrex top-piece of the furnace assembly. A mullite tube of bore 2% cm was used as reaction vessel and at the bottom of this tube was a trap for SO3, which condensed as a colorless liquid. The residual gas was led into a fume cupboard for ventilation to the atmosphere. The furnace used for visual observations of needle growth and other phenomena consisted of a transparent silica reaction tube of bore 3 cm, having an optically flat silica window sealed into its wall. The reaction tube was clamped vertically, inside a mullite tube of bore 4 cm and length 42 cm which was heated by Kanthal windings. The window in the silica reaction tube was arranged opposite a hole 3 cm wide and 2 cm tall which had been cut in the wall of the mullite winding tube 19 cm from its top end. A binocular microscope was used to look through the window, illumination being provided by a focusing microscope-lamp offset sideways and downwards. The oxide block to be sulfated was suspended from the removable Pyrex top-piece to the reaction tube, by means of which it was inserted at the start of the experiment, and through which entered the S02/02 gas mixture. The variation of the temperature inside the reaction tube with horizontal and vertical displacement from the window was investigated, and, while it can be said that the temperature was constant 1 deg, its value at a given position was known only to 12 deg. In both furnaces, the oxide block to be sulfated was suspended from a small silica hook immediately downstream from a platinum thimble used as catalyst, which was held on a long silica rod from a Pyrex spring attached to the removable Pyrex top-piece of the furnace. The spring was only included in the quantitative sulfating furnace; its sensitivity was 1.4 cm per g and it was found to be free from creep in a 16-hr test when carrying the working load. The extensions were followed by a cathetometer which could be read to 0.001 cm, corresponding to i0.7 mg. Extensions of the spring were measured on adding weights between 5 and 500 mg to the working load (thimble + oxide block), and Hooke's law was closely obeyed. SAMPLES Cuprous oxide blocks were prepared by oxidizing Johnson Matthey "Specpure" copper sheet of 1 mm thickness (impurities: iron at 3 ppm, silver at 2 ppm, lead, nickel, sodium, and silicon each at 1 ppm, calcium, chromium, magnesium, and manganese each at less than 1 ppm) for 6 days in air at 1000°C in a re-crystallized alumina boat. It has been reported7 that when Cu20 is prepared by heating copper sheet for 1 day the central plane of the blocks produced consists

Jan 1, 1967

By D. W. G. White

The surface tension of zinc has been determined by the sessile-drop method in a progvam emphaszzing detailed experimental care. The surface tension oj. the pure metal was measured over a range of ternperature from the melting point (419.6"C) to 540°C. At the melting point, the suvface tension of zinc was found to be: 1) 99.99+ pct Zn - 757.0 5 dynes per cm 2) 99.999+ pct Zn - 761.0 5 dynes per CI 3) 99.9999 pct Zn - 76'7.5 5 dynes pev cna From experiments carried out in a closed, isothermal cell, the temperatuve coejyicient of the surface tension (6y/6T)p, , of zinc xas found not to be negative but to be postiue. A positive tenzperatre coefficient indicates a greater depee of order in the surface than in the body of the lquid. Houlezer, by delibevately inducing continuous zaporization, a temperature coefficient of su)face tension with a negative slope can be produced. The work reported herein was undertaken as part of a larger program of fundamental research on the properties of molten zinc and zinc alloys. This program grew out of a continuing interest at the Mines Branch in the behavior of liquid metals in the foundry and of a desire on the part of the zinc industry for reliable basic data. The work was originally begun in cooperation with the Consolidated Mining and Smelting Co. Ltd., Trail, B.C., and was subsequently continued from 1960 to date in association with the Canadian Zinc and Lead Research Committee and the International Lead and Zinc Research Organization. Although the surface tension of liquid zinc has of course, been measured before, as Table I and Fig. 1 demonstrate, there is not good agreement among the existing values. Such disparities arise because sources of experimental error are insufficiently controlled. This situation places the reader in doubt. One result may be correct within narrow limits—even fortuitously—yet, because there is not agreement between several values, none can be accepted with conviction and all become suspect. It seemed, therefore, in the circumstances, that there was room for further work embodying considerable emphasis on experimental care in order that, within a small margin of error, an accurate value might be obtained. It was in this spirit that the work was undertaken. METHOD The sessile-drop method -as adopted for this work. In this method, when applied to liquid metals at elevated temperatures, the outline of the meridional section through a drop resting freely on a horizontal surface is recorded photographically. Certain parameters

Jan 1, 1967

By T. F. Archbold, P. G. McCormick

Silica fiber 11arkevs and hardness irzdentatiozs have been used to study the thermal diffusion of racancies in zinc placed in temperature gradients of 460o and 706oK per Cm All markers mored toward the higher temperatures, and the data show that the heat of trarlsport Q is greater than the eizthalpy of z,acancj3 forrjalion E by an amount equal to 3.5 kcal per mole. These results ore not in agreement with those obtained in either of the two previous studies with zinc. The problem is discussed in terms of experimental differences and racancy source and sink efficiencies. THE general interest in thermal-diffusion phenomena over the past several years has prompted a number of marker movement studies using pure metals. In order to understand better the relationships between thermal and mass flow, a general goal of the experiments has been to obtain values for the net enthalpies carried by the diffusing atoms. For self-diffusion by means of the vacancy mechanism, the determination of relative marker positions before and after an anneal in a temperature gradient permits a calculation of a value for (Q - Ef). Q is the transferred enthalpy, and Ef is the enthalpy of vacancy formation in the metal being investigated. The initial experimental study of thermal diffusion in pure metals was accomplished by Shewmon who found essentially no movement of surface-hardness indentation markers in single and bicrystals of zinc held for 20 days in a temperature gradient of 310°C per

Jan 1, 1967

By A. C. Losekamp, J. B. Conway

Thermal-expansion data for, tungsten, rhenium, tantalum, .molybdenum, niobium, W-25 pct Re, Ta-10 pct W, ant1 Mo-50 pct Re are presented covering the range from room tempature to 2500°C. In these measureMents, made in a resistively heated tungsten tube furnace operating in a helium atmosphere, data for rod and sheet specimens were found to be identical; in addition, arc-cast and sintered tungsten were found to yield essentially identical results. Optical rneasurenlents of thermal expansion .made in any atmosphere other- than vacuum are subject to a refraction error which can be quite substantial. Specimens tested in helium appear shorter than when tested in racuum and hence a special correction factor must be applied to the helium data in order to obtain accurate results. WHILE it is true that linear thermal-expansion data for many of the refractory metals have been measured to very high temperatures, it is also true that except in a few instances the data from various investigators are not in good agreement. This is particularly evident in the case of tantalum and niobium although some tungsten data have been reported which differ by as much as 40 pct from the data of other investigators. Due to the sensitivity of both tantalum and niobium with respect to impurity absorption during exposure to high temperatures, it is probable that this single factor accounts for the majority of the discrepancies in the thermal-expansion data for these metals. However, this same factor can probably not be employed to explain the existing differences in the tungsten data. In all probability, these are due to errors in the measurement technique, to material composition variations, or to changes which take place in the material during the heating process (e.g., additional densifica-tion resulting from heating a sintered specimen above the original sintering temperature). In view of the discrepancies which exist in the linear expansion data reported for many of the refractory metals, the current study was initiated in an attempt to resolve such differences. Also, no high-temperature linear thermal-expansion data were found to be available for several refractory metals. Providing such data was another objective of the current investigation. MATERIALS In this study test specimens were employed in either rod or sheet form and in several instances both arc-cast and sintered material were employed. Material compositions are presented in Table I. Helium gas was fed to the furnace at a rate of about 0.5 SCFH and no special purification procedures were employed. However, the helium contained less than 50

Jan 1, 1967

By H. I. Aaronson, H. A. Domian, G. M. Pound

The thernodyna,nics of I the Proeutectoid ferrite re-action ha1.e been investigated on the bases of three diifevent descviptions of the statistical thernzodynamics of interstitzal solid solutions. Especially at low ternperatures, substantial dijeretzces are found in the valltes of the extrapolated y/y + a and cr/a + y equilibriurn curls, and in the To- co7nposilion metastable eqliilibriunz curl-es thus co,npited. Although neither actiztity nor phase-diagram date are able to distingrish udeqiutely among the various descviptions, the statustics of Lacher, Fouller, and Guggenheinz provide the ?nost conplete epresentation az3ailable of the single carbon-ctrbon interaction energy (w) nzodel of an intevstitiril solid solution, and the relationships deduced frojrl then2 are accordingly pre.ferred. The findings tlzut w in austenite 'aries significu?ztly uith tenpevntrue and that phase-diagawr data arc not accurately con?palible usith eqcrctions deduced on the basis of actility infoation indicate, hou'e13er, that a wzore cornplex nlodel of the uustenite , und pvobably of the .feyrite, solirl solutions will have to forn the basis of f4tuve statistical t1.eat1nents. Some suggestions for such a ruodel arc advanced. Althoug11 w represents a vepltlsio energy in austozite, it was found to corvcsporzd in ferrite to a binding energy, in qualitatit.e accord zc,itlz the internal-friclion results of Keefer and wert. ThE transformation of austenite to proeutectoid fer-rite is becoming recognized as an exceptionally useful vehicle for quantitative studies of the kinetics of phase transformations.'" Reasons for this popularity include well-characterized microstructures which develop on a convenient scale with acceptable kinetics within a considerable temperature-composition region, the absence of great sensitivity to common impurities, and, especially. the availability of a unique wealth of the ancillary information indispensable for the quantitative interpretation of kinetic measurements, including phase diagram,3 crystallographies diffusivity,5 inter-facial energy,=17 elastiit," specific vlume, ''' and ativity'-' data. Development of considerable amounts of additional thermodynamic information from activity data is of particular importance with respect to kinetic studies, since much of this information is needed in temperature-composition regions not directly accessible to presently available techniques for the measurement of equilibrium properties. A generally useful approach to the thermodynamics of solid solutions, which is of especial value in this situation, is based upon the formulation of the free energy of such solutions as a function of temperature and composition. The free energy of solid solutions has been resolved into many components. Particularly in the case of interstitial solutions, with which we shall be concerned in the present study, however, only the positional entropy component has been intensively studied. The other components are conventionally taken into account by fitting equations for the activity of the interstitial species or the temperature-composition path of phase boundaries, derived principally from positional entropy considerations, to experimental information on these quantities through adjustment of one or more constants in the equations. A number of studies of the thermodynamics of interstitial solid solutions have been made primarily on this basis,'"25 but only Kaufman, Radcliffe, and cohenZ2 (hereafter KRC) and ener''% ave applied the results of such studies to develop relationships for the thermodynamic quantities of interest in the austenite —- proeutectoid ferrite transformation. KRC made use of a model developed by cheil'' (on the basis of a previous study by ohansson'), and subsequently rede-rived correctly by Speiser and retnak,' in which a carbon atom is considered to inhibit occupancy of a certain number of its nearest-neighboring interstitial sites. schei120 determined the number of sites in austenite thus excluded by matching calculated and experimentally measured curves for the variation of carbon activity with the mole fraction of carbon. zener17 used a different approach. He assumed that the positional entropy of carbon is ideal both in austenite and in ferrite (i.e., no excluded interstitial sites), and included all other contributions of carbon in a temperature-independent "free-energy change" accompanying the transfer of 1 mole of carbon between the two phases. This quantity was determined by "pinning" an equation derived for the boundaries of the a + y region to experimental data on the compositions of these boundaries at a single temperature. In the present investigation, three different approaches to the thermodynamics of the proeutectoid ferrite reaction are examined comparatively: I) the method of Zener; 2) the model employed by KRC and predecessors; and 3) the more detailed statistical thermodynamic treatment of the same model developed by acher and Fowler and uenheim, ' in which the problem of overlapping regions of influence of individual interstitial atoms is resolved. In order to make these comparisons, it is necessary to undertake an extension of one aspect of Zener's method; since the Lacher- Fowler -Guggenheim (LFG) treatment has not been previously used in the present context, the necessary thermodynamic "superstructure" for this treatment will be developed in parallel

Jan 1, 1967

By R. G. Garlick, M. Garfinkle

It was observed for several bcc metal crystals that the Knoop hardness anisotropy was dependent essentially on the direction of the lung axis of the indentor alone and not on the plane of indentation. The generality of this observation was tested for an fcc md an hcp metal and an ionic crystal. For cubic crystals, this observation was valid; for the hcp structure, however, the planes of indentation did have an effect on the hardness anisotropy, although this was not nearly as significant as the direction of indentation. Because the direction of indentation is the only significant crystal-lographic parameter necessary to describe the hardness anisotropy, it is possible to represent the anisotropy of single crystals on the standard stereographic triangle. THE commonly observed1, 2 periodic variation of indentation hardness with crystallographic direction on the high-symmetry planes of various single crystals has been inadequately related to the physical or mechanical properties of the crystals examined. In fact, the hardness anisotropy curves for the various planes of a particular metal crystal, as is illustrated in Fig. 1, are uncorrelated and appear in the literature3, 4 as unrelated observations. Attempts to correlate hardness anisotropy curves with specific physical properties can be generally divided into either mechanistic or nonmechanistic approaches. A nonmechanistic approach would be to devise a mathematical expression that could describe the various hardness anisotropy curves. Such a relation could then be compared with the known anisotropy of various physical properties to determine which contribute to the observed hardness anisotropy. No such mathematical expression has been found in the literature.

Jan 1, 1969

By Matti J. Saarivirta

The relative machinabilities of the precipitation-hardenable Cu-0.9 pct Cr, Cu-0.25 pct Zr, and Cu-0.9 pct Cr-0.25 pct Zr alloys are improved from 18 to 80 pct by 0.75 to 1.25 pct Pb. The Lead also improves the tensile strength, hardness, ad resistance to softening of the Cu-Cr and Cu-Cr-Zr alloys. When the alloy containing 0.7 to 2.2 pct Cr, 0.10 to 0.25 pct Zr, 0.75 to 1.25 pct Pb, and balance copper is solution-annealed at 1000°C (1830°F) and then aged at 525°C (Y75°F), tensile strength of 65,000 psi, 16 pct elongation, 62Rb hardness, and 84 to 87pct IACS electrical conductivity are obtained. The copper base Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys have high electrical and thermal conductivities, high strength and resistance to softening at elevated temperatures, but their machinability is poor, i.e., close to that of the pure copper. In the manufacture of various components such as welding electrodes or electrical and thermal conductors it is ofter desirable that the alloy have good machinability for high production rates and long tool life. Thus, alloys that combine these properties may be used not only for existing applications, but for new ones where good machinability is a requirement. This investigation was undertaken to improve machinability without impairing other desirable characteristics of the Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys. These commercial alloys contain about 0.4 to 1.2 pct Cr, 0.10 to 0.25 pct Zr, and balance copper. Lead was selected as an element that should improve the machinability and possibly other characteristics of the alloy. WORK PROCEDURE This investigation began with a study of the effect of lead on the hardness, tensile strength, electrical conductivity, and machinability of the binary alloy containing 0.10 to 1.30 pct Cr and balance copper. This was followed by an investigation of the effect of lead on the Cu-0.1 to 0.4 pct Zr and Cu-Cr-Zr alloys. The alloys were made from initially oxygen-free copper and for comparison some castings were made from phosphorus-deoxidized Lake Copper. Commercially pure chromium, zirconium, and lead were used for alloying. In melting the chromium was added to molten copper at 1400°C (2550°F), the heat held for 15 min at temperature, and the temperature then lowered to 1350°C (2460°F) when the other elements were added. The alloys were held for 15 min at this temperature and cast into a cast-iron mold. One-kilogram, 3-in.-diam castings were made. An argon cover was maintained during melting and casting to prevent oxidation. The chemical compositions of the alloys are shown in Table I. The micro structure and properties of the alloys were studied in the cast and wrought conditions prior to and after various solution-annealing and heat-treating cycles. The relative machinability was determined as a function of the lead content and compared with the free-machining Cu-lpct Pb alloy. To determine the machinability, 13/16-in.-diam cast specimens were cut by a machine hack saw using a constant cutting speed of 50 fpm, a fixed feed force, and a new blade for each alloy specimen. Molybdenum highspeed steel saw blades, 0.032 in. thick with 14 teeth per in., were used in all tests. No cutting fluid was used. Five tests were made on each specimen and the average elapsed time per test was taken as a measure of the relative machinability for that alloy. The variation of cutting time for each alloy was less than 110 pct.

Jan 1, 1969

By K. A. Gschneidner, O. D. McMasters, T. J. O’Keefe

X-ray diffraction, differential thermal, ad rnetallo-graphic methods were used to establish the Dy-Pb Phase diagram. Lead additions lower the 1377°C transformation temperature of dysprosium to 1360°C leading to an inverted peritectic reaction. The 327°C melting point of lead is lowered by dysprosium additions to about 326°C yielding a eutectic reaction. A second eutectic reaction occurs at 13.3 at. pct Pb and 1200°C. The dysprosium-richest intermetallic compound DysPb3 melts congruently at 1695°C and crystallizes in the hexagonal Mn5Si3 (D8,) type structure. The peritectic decomposition temperatures for the remaining compounds are Dy5Pb, at 1555C, DyPb2 at 955C, and DyPb3 at 880°C. A fifth compound near the DyPb stoichiometry exists over a 310°C temperature range decomposing at 1130°C by means of an inverted peritectic reaction and melting incongruently at 1440°C. The crystal structures of the compounds are discussed. A systematic study of the rare earth-lead alloy systems is underway in an effort to supply information concerning the alloying behavior of the rare earth metals. The Dy-Pb phase diagram is the fourth system to be investigated in this study. The Yb-Pb,1 Y-Pb,2 and Eu-Pb 3 diagrams have been published recently. Utilization of the rare earth series of metals as a research tool in this manner should yield a better understanding of alloy formation. EXPERIMENTAL PROCEDURE Materials. The lead used in this investigation was obtained from Cominco Products, Inc., and was specified to be 99.99 pct pure. The dysprosium was prepared in this Laboratory by the calcium reduction of the fluoride followed by distillation of the dysprosium. The major impurities in the dysprosium in ppm are: A1 (<40), Ca (400), Er (<50), Gd (<200), Ho (<200), Mg (<50), Si (30), Ta (400), Tb (<100), Y (<50), 0 (651, H (15), N (not detected), F (430), C (35). Alloy Preparation. Most of the alloys were prepared by melting weighed amounts of dysprosium and lead in sealed tantalum crucibles. The tantalum crucibles were sealed by are-welding in a He-Ar atmosphere welding chamber. Thus the alloys are in contact with He-Ar at about 1 atm pressure. Homogenization was achieved by holding them in the liquid state for about 1 hr, cooling, inverting the crucibles, remelting, and repeating the process at least twice. Since these alloys were prepared in sealed tantalum crucibles, chemical analysis for final composition was thought to be unnecessary. No detectable reaction of these alloys with the tantalum crucible was observed by metallographic examination. Metallographic evidence was also used to confirm the homogeneity of some of the alloys prepared in this manner. The compositions of a few alloys, which were prepared by nonconsum-able are-melting, were corrected for the small weight losses involved by assuming that the weight loss is due to vaporization of lead. The specimens obtained from the alloy samples were prepared under a dry-argon atmosphere because they were rapidly attacked by air and moisture. Thermal Analysis. Differential thermal analysis methods were used to determine the liquidus curves and reaction horizontals of the system. Both Pt vs Pt + 13 pct Rh and W + 5 pct Re vs W + 26 pct Re thermocouples were used to measure the temperature. An X- Y recorder was used to record the specimen temperature and differential electromotive force between the specimen and molybdenum standard. The arrest temperatures were measured potentiometri-cally. The accuracy limits (* values) associated with the reaction temperatures obtained by this method were estimated on the basis of both the reproducibility of the particular temperature value and the accuracy of the thermocouple at a given temperature. Liquidus temperatures were obtained from cooling arrest data while both heating and cooling arrest data were used to establish the horizontals of the diagram. Heat treatments during the thermal analyses of the alloys between 40 and 70 at. pct Pb were necessary in order to approach equilibrium conditions. The samples were held at temperatures between the various peritectic horizontals for l to 2 hr before the thermal analyses were continued. The entire range of compositions was investigated at the expense of a minimum amount of materials by adding appropriate amounts of lead to master alloys. More than sixty alloys were analyzed by this differential thermal method and for each alloy the results given herein are taken from two or three heating and cooling cycles. X-Ray and Metallographic Methods. Slice specimens for metallography and powder specimens for X-ray diffraction were prepared from rod-shaped samples which had been melted in sealed 0.62 5-cm-diam tantalum crucibles. The specimens were heat-treated in sealed tantalum crucibles which were protected by sealing them in argon-filled quartz ampules. Quenching was accomplished by breaking the ampules in ice water after heat treatment. X-ray powder specimens were sealed in 0.3-mm-diam glass capillaries under a dry-argon atmosphere. Copper, iron, and chromium radiation were used to obtain the powder patterns for these alloys. More than 150 powder patterns were obtained for specimens of various compositions and heat treatments. Included in these were several patterns for specimens which had purposely been oxidized. Patterns from specimens which had been accidentally exposed

Jan 1, 1969

By R. K. Buhr, H. Thresh, M. Bergeron, F. Weinberg

The microsegregation of nickel and chromium in directionally solidified AISI 4340 steel castings has been measured using electron probe microanalysis. Minimum concentrations were observed to occur at the center of the dendrite stalks, as reported previously. However, the position of the maximum concentrations could not be determined from the dendrite configuration. An etching technique has been developed which shows the position of maximum concentration. Measurements were made of the distribution of nickel and chromium in the dendritic structure. The ratio of maximum to minimum concentration was determined as a function of primary dendrite arm spacing for both as-cast and partially homogenized materials. The results are compared with observations reported in the literatuve. A S part of an investigation of solute segregation in directionally solidified AISI 4340 steel casting, electron probe microanalysis was used to measure the distribution of nickel and chromium in the dendritically segregated material. This complemented the observations on the segregation of radioactive phosphorus obtained by autoradiographic techniques in the same castings.&apos; Kattamis and I?lemings2 have reported similar measurements, using electron probe microanalysis, on dendritically segregated AISI 4340 steels. They found minimum solute concentrations occurred at the center of dendrites, maximum concentrations occurred in the center of interdendritic regions, for symmetrically oriented dendrites, and a regular variation of concentration within dendrite arms. The ratio of maximum to minimum concentration was found to be essentially independent of position in the castings, except near the chill surface where it was somewhat higher. Assuming complete diffusion in the liquid and no diffusion in the solid during freezing, they considered that isoconcentration curves in the steel were homothetic. As a result, isoconcentration curves of the various elements, contour surfaces of dendrites produced by isothermal-transformation studies, and the contour of the solid-liquid interface would all be similar, and could be superimposed by a uniform expansion or contraction of the contours. Preliminary results of the present investigation suggested that isoconcentration curves were not homothetic. It was also evident that points of maximum concentration could not be predicted from the dendrite configuration. Since the ratio of maximum to minimum concentration appeared to be an important parameter in defining the overall segregation in a casting, other techniques for determining the point of maximum concentration were investigated. In addition the overall solute distribution associated with the dendritic structure was examined for both nickel and chromium, and the consistency of the distribution for neighboring dendrites was determined. METHOD Fifty-pound heats of AISI 4340 steel were cast in a manner similar to that used by Flemings et al3 with a water-cooled copper base plate and exothermic sides and top. The nominal composition of the material was C, 0.41 pct; Mn, 0.66; Si, 0.35; S, 0.012; P, 0.010; Ni, 1.88; Cr, 0.95; Mo, 0.28. The steel solidified directionally from the chill surface, with a dendritic structure which increased in dendrite arm spacing with increased distance from the chill. Results of the general investigation of the cast structure and segregation of radioactive phosphorus in these castings have been reported elsewhere.&apos; For the present measurements, sections were cut from the casting at several distances from the chill surface. The sections were subsequently heat-treated, mounted, and then polished on a plane perpendicular to the general freezing direction of the casting. Electron probe microanalysis was carried out with the JEOL-JXA3 microprobe using a voltage of 25 kev and beam current of 0.15 µa. The take-off angle is 22 deg. Quartz crystals were used in the spectrometers and measurements made for Ka radiation from both nickel and chromium simultaneously. A thin layer of carbon was deposited on all specimen surfaces prior to examination in the microprobe. Early measurements were made on polished surfaces, with indentation marks produced by a hardness tester to indicate the area of interest. It was found desirable to use etched surfaces, as opposed to polished surfaces, to reduce sample preparation time and more readily relate the microprobe scan to the structure. To determine if this could be done, without introducing significant errors, a series of measurements were made on polished and etched surfaces of the same specimen. Both polished and etched surfaces produced similar results within normal scatter as shown in the observations. Subsequent measurements were then made on etched surfaces. Measurements with the microprobe analyzer were made by point counting, for periods of 100 sec, at 10-µ intervals. Ten-second counts were made on pure nickel and chromium standards, incorporated in the specimen mount before and after each set of measurements. The results were adjusted for background, then corrected for dead time using the expression:

Jan 1, 1969

By Claude H. P. Lupis, John F. Elliott

The classic Siez~erts&apos; technique has been employed to determine the solubility of oxygen in liquid pure silver and the effect on the oxygen solubility of solute metal additions to liquid silver. The results indicate that oxygen deviates slightly from Sieverts&apos; law in pure silver as = 3.9. Gold, platinum, md palladium decrease the solubility of oxygen in silver. First-order free energy, enthalpy, md entropy interaction coefficients are determined from the data. An important aspect in the establishment of the formalisms to be applied to represent the thermody-namic behavior of components of solutions is the accuracy of the experimentally determined thermody-namic properties. Wagner developed the first-order free energy interaction coefficient.&apos; Recent papers2&apos;3 extend the treatment formally to other thermodynamic properties and define the second- and higher-order interaction coefficients. A current communication4 considers in some depth the requirements and limitations imposed because of experimental error on the use of several formalisms now under active consideration in the field. This communication reports the results of an experimental study of the behavior of oxygen in liquid silver alloys that was carried out concurrently with the development of Refs. 2 and 3 with the hope of providing sufficiently precise information so that enthalpy and entropy interaction coefficients could be determined. THE EXPERIMENTS The Sieverts technique was employed using an improved design of the reaction bulb over that developed originally by Humbert5 and subsequently improved by pehlke6 and Weinstein.7 The Vycor reaction bulb as shown in Fig. 1 was air-cooled and contained a port for the thermocouple angling off to one side and a vertical port for connections to the gas supply and

Jan 1, 1969

By V. Koump, T. F. Perzak, R. G. Olsson

The rate of dissolution of recrystallized alumina in molten iron oxide in equilibrium with iron at 1450°C was studied by rotating alumina disks in the melt. The samples were rotated from 1 to 12 min at speeds from 54 to 3270 rpm. It is concluded from the experimental results that the process is limited by diffusion in the liquid boundary layer. The interdiffusion coefficient for the dissolution of alumina disks in pure molten iron oxide was estimated to be about 3 xl0-5= sq cm per sec. THE erosion of refractory materials is of considerable importance in iron- and steelmaking processes. Since many refractories contain alumina, this investigation was undertaken to develop a further understanding of the erosion mechanism. Shurygin et al.1-3 have investigated the rate of dissolution of alumina in molten silicates and molten fluorides by rotating alumina disks in various melts. The rates were reported to be limited by diffusion in the liquid boundary layer. In the present investigation the rate of dissolution of alumina in molten iron oxide in equilibrium with iron was studied in a similar manner; alumina disks were rotated at different speeds in molten iron oxide at 1450°C. The relationship between the rate of dissolution of the flat surface of the disk and the speed of rotation was used to determine whether the process is limited by diffusion in the liquid boundary layer or by some chemical reaction mechanism. APPARATUS AND EXPERIMENTAL PROCEDURE A schematic diagram of the experimental apparatus is shown in Fig. 1. The iron oxide melts were contained in 2-in.-diam high-purity iron crucibles that were centered in a cylindrical graphite susceptor. Prior to each sequence of experiments, sufficient reagent-grade ferric oxide was added to a crucible to form approximately 350 g of molten iron oxide; the depth of the melt was about 11/2 in. To prevent excessive erosion of the crucible, about 70 pct of the required iron was added to the crucible in the form of iron powder. The mixture was melted in an atmosphere of purified argon by induction heating with a 250-kc generator. After the oxide was molten, a Pt/Pt-10 pct Rh thermocouple at the exterior of the crucible was calibrated against an iron-sheathed thermocouple immersed in the melt and was thereafter used to regulate the melt temperature. All experiments were conducted at 1450°C with a probable error of 10°C. The alumina disks were constructed from pure re-crystallized alumina having a density of 3.7 g per cu cm (porosity approximately 6 pct). For each disk sample a 1-cm-diam alumina cylinder of known length (0.9 to 1.0 cm) was cemented into a ground seat at the end of a 1.27-cm-OD centerless ground alumina tube. The ends of the tube and cylinder were flush and served as the disk surface. When mounted in the apparatus the alumina tube was guided by tungsten carbide bearings and rotated by a variable-speed motor. The bearing and drive assembly could be raised and lowered in order to allow the sample to be quickly moved in and out of the melt. At the start of an experiment, a sample was preheated for several minutes directly above the melt, and then immersed in the middle of the melt to a depth of a in. and rotated for 1 to 12 min at speeds of 64 to 3270 rpm. The speed of rotation was measured by a hand tachometer. At the start and completion of each experiment, a melt sample was withdrawn with a cold copper rod and the alumina content was determined by chemical analysis. During individual experiments the alumina concentration of the melt changed by the order of 0.25 wt pct. Average melt compositions for individual experiments were used in the subsequent computations and were in the range between 0.12 and 4.3 wt pct alumina. The extent of dissolution was determined by sectioning the end of the sample and measuring the final length of the alumina cylinder with a microscope. Since the exposed end of the cylinder, i.e., the disk surface, was etched in a manner characteristic of this geometry, a number of measurements were made on

Jan 1, 1969

By Richard R. Zupp, David A. Stevenson

A theoretical treatment of austenitic Fe-C-Z solutions (where Z represents a substitutional solute) was developed by extending a solution model which was previously applied to austenitic Fe-C alloys. The model assumes that each carbon atom in the solution excludes H interstitial sites from occupancy by other carbon atoms rmd thai otherwise the assembly of carbon atoms is equivalent to a modified Langmuir lattice gas. The results of the treatment provide theoretical justification for a phenomenological expression previously developed to represent the influence of substitutional solutes on the thernlodynamics of carbon in austenitic Fe-C-Z alloys. The expression is: where Kz is a parameter which characterizes the Fe-C-Z system at a given temperature and Xz and xj are the concentrations of substitutional solute and interstitial carbon expressed as atom ratios. The parameter, Kz, was associated with the differ- A number of investigators have measured the influence of various substitutional solutes on the carbon activity in austenitic Fe-C-Z alloys, where Z represents any substitutional solute. Experimental information is available for alloys containing the following substitutional solutes: Mn,&apos; Si,&apos; Ni,2-5 CO,&apos;-&apos;, Cr,5, 9-11 CU,4 Al,= v,11, 12 and Ti.13 This information is essential for studying many phenomena in Fe-C-Z alloys, particularly diffusion and diffusion-controlled phase transformations For example the pffprts nf various ence between the interaction energies between carbon atorns and host-lattice atoms in the Fe-C-Z solution and the corresponding energies for the Fe-C solution. The carbon activity in a ternary Fe-C-Z alloy, ac, was obtained in terms of the composition of the alloy and the single parameter, Kz: where y° is the Henry&apos;s law constant for the binary Fe-C solution. Both y° and H crm be determined from the data for Fe-C solutions, without recourse to any experimental data for Fe-C-Z solutions. The theoretical treatment was extended to alloys containing several substitutional solutes. By neglecting interactions between the substitutional solutes, an expression for the carbon activity in multicomponent alloys was obtained in terms of the Kz values characterizing ternary Fe-C-Z systems. substitutional solutes on the rate of pearlite growth is explained14 on the basis of their effects on carbon diffusion, which result from their influences on the carbon activity in the solid phases. In addition, recent studies have emphasized the dependence of the pro-eutectoid ferrite transformation15 and other diffusional processes in austenite16 on the influence of substitutional solutes on the carbon activity in austenite. They have indicated the need for suitable analytical expressions to represent such influences. The present authors previously developed general phenomenological expressions to represent the equilibrium partitioning of carbon between Fe-C alloys and Fe-C-Z alloys.&apos;2 The expressions are applicable to all the austenitic Fe-C-Z alloys for which experimental data are available, and are sufficiently simple to recommend their general application. For alloys in

Jan 1, 1969

By Shiro Ban-ya, John Chipman

Equilibrium in the reaction was investigated at temperatures of 1500°, 1550°, and 1600°C for sulfur concentrations up to 7.2 wt pct. Multisample crucibles contained the liquid alloys in a resistance-heated furnace using a technique especially designed for the study of more complex alloys to be reported separately. Modern free-energy data are used to correct the H2S:H2 ratio for dissociation of H2S and calculalion of the partial pressure of S2. Published data on the equilibrium are similarly corrected. Thermodynanzic treatment of the data employs the composition variable zs = nS/(nFe — nS) and the activity coefficient Gs = as/zs The data at 1500" and 1550°C are fitted by the equation log s = —2.30zs. Within the limits of experimental error the same coefficient is applicable to the data at higher temperatures. Equations are given for the free-energy change in Reaction [I] as well as for the solution of S, gas in the metal. The heat of solution of 1/2 s2 is -32.28 i2.5 kcal. Uncertainty in the free energy is very much smaller. For dilute solutions of interest in steelmaking, the activity coefficient of sulfur is unchanged from that listed in Basic Open Hearth Steel-making. DETERMINATIONS of the thermodynamic properties of sulfur in liquid iron by Morris and williams1 and by Sherman, Elvander, and chipman&apos; provided a basis for control of sulfur in steelmaking processes. From the standpoint of understanding the chemistry of metal plus nonmetal in liquid solution they left several questions unanswered. The activity of sulfur in dilute solution at about 1600°C was well-established but temperature coefficients were uncertain, due at least in part to the use of the optical pyrometer and uncertainty regarding the effect of sulfur on emissivity. It appeared that deviation from Henry&apos;s law increased with increasing temperature, a most unusual behavior requiring either confirmation or disproof. These studies were based on experimental determination of equilibrium in the reaction: At high temperatures H2S is partially dissociated so that the gas mixture contains HS, S2, and S in addition to HS. At the time of the earlier studies the free energies of these constituents were unknown and it was therefore impossible to make adequate correction for dissociation. Observations on the effects of alloying elements by Morris and coworkers1, 3 and by Sherman and Chip-man4 enable us to assess the effects of alloying elements on the activity and to make corrections for incidental impurities in the binary liquid. These studies as well as a number of more recent investigations will be reviewed in detail after out own experimental results have been presented. It was our purpose in planning this study to avoid uncertainties regarding the emissivity of alloys and the errors of thermal diffusion which plagued some of the early attempts,5 by using a resistance furnace and thermocouple in preference to induction heating and optical pyrometer. Modern data on free energies of the gaseous species are to be applied to our data and to those of other investigators to obtain corrected values of K1 and of the activity coefficient and ultimately to relate the sulfur content of the bath to the equilibrium partial pressure of S,. Extension of the study to include ternary and complex solutions will be described in a later section. EXPERIMENTAL METHOD a) Preparation and Calibration of H2-H2s Gas Mixture. The source of hydrogen sulfide was a preparer mixture of 43 pct H2S, balance hydrogen, contained in a large aluminum cylinder. This was passed through anhydrone and through a microflowmeter. Hydrogen was passed through platinized asbestos, ascar-ite, and anhydrone, and through a capillary flowmeter. Argon was passed through copper wool at 500°C, then through ascarite, anhydrone, and a flowmeter. The flow rate of hydrogen was kept constant at 200 ml per min, to which an arbitrary amount of the hydrogen-hydrogen sulfide mixture was constantly added and then the prepared gas mixture was introduced into the reaction tube through a gas mixer. In certain experiments 200 ml per min of argon was added to the hydrogen-hydrogen sulfide gas mixture to increase the total flow rate of gas. The ratio of hydrogen-hydrogen sulfide in the inlet gas was checked for each run by chemical analysis. A sample of the gas taken from a bypass was bubbled through zinc and cadmium acetate solution (4 pct zinc acetate, 1 pct cadmium acetate, and 1 pct acetic acid) to remove hydrogen sulfide from the gas mixture, and the flow rate of the remaining hydrogen was measured by a soap bubble method to determine the volume of hydrogen. The amount of hydrogen sulfide absorbed in solution was determined by titration with iodine against sodium thiosulfate, with starch used as the indicator. The ratio of hydrogen sulfide to hydrogen in the inlet gas could be kept within ±2 pct in the range from 10-2 to 5 x 10"4 which corresponds to from 0.2 to 7.0 wt pct sulfur in liquid iron. b) Furnace Arrangement. Fig. 1 shows the furnace arrangement and the shape of the alumina crucible used in this experiment. A vertical-tube silicon carbide electric resistance furnace contained the reaction tube which consisted of two parts, the gas-tight

Jan 1, 1969