Search Documents

By M. A. Dayananda, R. E. Grace, P. F. Kirsch

Ternary diffusion experiments were carried out at 750°C with vapor-solid diffusion couples in single-phase copper-rich Cu-Zn-Sn alloys. The Philibert-Guy method was used to calculate intrinsic diffusion coefficients at compositions corresponding to the plane of inert markers imbedded in the diffusion couples. Inter diffusion coefficients were determined at common composition points of intersecting diffusion paths. Intevdiffusion coefficients were also obtained at compositions corresponding to maxima in the tin concentration pvofiles Relations between the interdiffusion coefficients and the expansion of vapor-solid diffusion couples are described in detail. Such relations permit the calculation of constant interdiffusion coefficients in binary couples from expansion data directly. In ternary couples expansion data provide an additional constraint on the interdiffusion coefficzents. ThE phenomenological analysis of diffusion in ternary solid solutions has been developed extensively, and various approaches taken in the determination of diffusion coefficients have been reviewed recently by Guy et al.' Finite,' semi-infinite,3 and infinite4 diffusion couples have been used in studies of ternary diffusion, but most of the work has been done with infinite diffusion couples. Semi-infinite diffusion couples3 (vapor-solid couples) have been used to determine both intrinsic and interdiffusion coefficients in the Cu-Zn-Mn system, in which two diffusing species, zinc and manganese, were supplied from the vapor phase. If only one component has a sufficiently high vapor pressure to be supplied from a vapor source, vapor-solid diffusion couples may still be used. In this case the boundary conditions at the gas/solid interface may be governed by partial equilibria rather than by virtually complete equilibrium between the phases. In the present work diffusion measurements were carried out at 750°C with vapor-solid couples of Cu-Zn-Sn alloys. Only zinc was transported between the vapor source and the diffusion disks, because the vapor pressures of both copper and tin are at least 108 lower than that of zinc. Both intrinsic and interdiffusion measurements were made at several compositions. A secondary objective was to relate expansion of the diffusion couples with the interdiffusion process. Such measurements for binary couples yield average values of the interdiffusion coefficients over composition increments. In ternary diffusion couples ex- pansion data provide an additional constraint on the interdiffusion coefficients. COMPOSITION-DEPENDENT INTRINSIC AND INTERDIFFUSION COEFFICIENTS As shown by Philibert and GUy5 the determination of intrinsic diffusion coefficients in a ternary system requires two independent diffusion couples containing marker planes with identical composition. In the case of vapor-solid couples such a requirement torresponds to two couples set up with the same vapor source exposed to two diffusion disks of different composition. Inert markers placed initially on the disk surfaces become imbedded during diffusion. If the pair of couples exhibits appreciable marker burial with marker planes of virtually the same composition, the intrinsic diffusion coefficient may be evaluated at the composition of the marker planes. Fig. 1 is a schematic diagram of the concentration of of a Cu-Zn-Sn ternary vapor-solid couple after diffusion of zinc from a vapor source into a binary Cu-Sn alloy. The areas, Ai correspond to the cumulative intrinsic fluxes of the three diffusing species across the marker plane:5 where Ji is the intrinsic flux of component i, t is the diffusion time, and D3i are the intrinsic diffusion coefficients. For the determination of interdiffusion coefficients a pair of diffusion couples with intersecting diffusion paths is needed. At the composition point of intersection (C1, C2) the coefficients are evaluated from the equation:3

Jan 1, 1969

By Charles E. Lundin

Pressure-temperature-composition data were obtainedfor the Er-H system. Measurements werecar-ried out in the temperature range of 473° to 1223°K, the composition range of erbium to ErH,, and the pressure range of 10-5 to 760 Torr. Solubility relationships were established from these data throughout the system. Three solid-solution phases were delineated: metal solid solution, dihydride phase, and trihydride phase. The trihydride Phase decomposes at about 656°K and 1 atm pressure. The dihydride phase is stable to about 1023°K, but becomes more deficient in hydrogen above this temperature. The equilibrium decomposition pressure-temperature relationships in the two-phase regions, erbium solid solution plus dihydride and dihydride plus trihydride, were deter- The differential heats of reaction in these two regions are AH = - 52.6 * 0.3 and - 19.8 i 0.2 kcal per mole of Hz, respectively. The differential entropies of reaction are AS = - 35.2 * 0.3 and - 30.1 * 0.4 cal per mole HZ.deg, respectively. Relative partial molal and integral thermodynamic quuntities were calculated in the system to the dihydride phase. RARE earth metal-hydrogen systems have been the subject of general survey,1"4 and all have been found to form hydride phases. The heavy rare earths, of which erbium is a member, form dihydride and trihydride phases with different crystal structures, whereas the light rare earths form only a single-phase dihydride which expands without structure change, as hydrogen is added, to the trihydride composition. These materials are of interest primarily because of their theoretical properties, such as bonding, defect structure, and thermodynamic and electronic characteristics. Erbium has been studied in several previous investigations.5, 6 It was deemed desirable to more thoroughly and accurately define the system, both for the phase equilibria and the thermodynamic properties. I) EXPERIMENTAL PROCEDURE A Sieverts&apos; apparatus was employed to conduct the experimental measurements. Briefly, it consisted of a source of pure hydrogen, a precision gas-measuring buret, a heated reaction chamber, a mercury manometer, and two McLeod gages (a CVC, GM 100A and CVC, GM 110). Pure hydrogen was obtained by passing hydrogen through a heated Pd-Ag thimble. The hydrogen was analyzed and found to have only a trace of oxygen and nitrogen. A 100-ml precision gas buret graduated to 0.1-ml divisions was used to measure and admit hydrogen to the reaction chamber. The reaction unit consisted of a quartz tube surrounded by a nichrome-wound furnace. The furnace temperature was controlled by a recorder-controller to ±1°K. An independent measurement of the sample temperature in the quartz tube was made by means of a chromel-alumel thermocouple situated outside, but adjacent to, the quartz tube near the specimen. Pressure in the manometer range was measured to ±0.5 Torr and in the McLeod range (10-4 to 10 Torr) to ±3 pct. The hydrogen compositions in erbium were calculated in terms of hydrogen-to-erbium atomic ratio. These compositions were estimated to be ±0.01 H/Er. The erbium metal was obtained from the Lunex Co. in the form of sponge. The metal was nuclear grade with a purity of 99.9 pct +. The oxygen content was reported to be 340 ppm and the nitrogen not detectable. Metallographically the structure was almost free of second phase (<1 vol pct). A quantity of sponge was arc-melted for use as charge material. The solid material was compared with the sponge in the pressure-temperature-composition relationships. They were found to be identical. Therefore, sponge material was used henceforth, so that equilibrium could be attained more rapidly. The specimen size was about 0.2 grain for each loading of the reaction chamber. The procedure employed to obtain the pressure-temperature-composition data was to develop experimentally a family of isothermal curves of composition vs pressure. First, a specimen of erbium was wrapped in a tungsten foil capsule to prevent contact with the quartz tube. After loading the specimen, the system was evacuated to less than l0-6 Torr, flushed several times with high-purity hydrogen, and evacuated again ready for the start of the experiment. The furnace was then brought to the desired temperature. A measured amount of hydrogen was admitted into the chamber. Equilibrium was allowed to be attained, the pressure read, and the process then repeated many times until 1 atm of gas pressure was finally reached. Other isotherms were then developed in the same manner. The partial pressure plateaus were determined by another manner. In the solid solution-dihydride region a composition of approximately 1.0 H/Er was selected on the plateau. The temperature was varied throughout the range of interest. At each temperature level, equilibrium was achieved, the pressure read, and the next temperature attained. The temperature was cycled both up and down. In the dihydride-trihy-dride region, the plateaus were determined in the 473" to 651°K range only by heating to the desired temperature and not by both heating and cooling. The data were much more reproducible in this manner. Equilibrium required long periods of time. Specimens were initially hydrided to 2.8 H/Er, so that at the higher

Jan 1, 1969

By J. W. Martin, L. K. Singhal

Grain boundary M23CB precipitates have been shown to form by a process involving the migration of an austenite grain boundary, and each plate of precipitate is in parallel orientation with one of the austenite grains constituting the boundary. The carbide distribution and morphology appear to be sensitive to grain boundary mis orientation. Some areas of austenite grain bowzdary permit the development of an array of M,C, particles, some of which are in parallel orientation with one grain and some with the other grain constituting the boundary. Massive carbide at grain boundary triple points is also shown to be in parallel orientation with one constituent grain. PREFERENTIAL precipitation during aging of carbides of the type (Fe,Cr)23C6, usually written MZ3C6, in grain boundaries of quenched austenitic stainless steels has been widely recognized. M23C6 has a complex cubic crystal structure&apos; which contains ninety-two metal atoms and twenty-four carbon atoms per unit cell. Less energy is involved in forming grain boundary precipitates than in the formation of intragranular precipitates, and the process is further enhanced by the accelerated diffusion rates in the boundaries and by the probability of segregation of chromium atoms and carbon atoms to the region of the grain boundaries during prior solution heat treatment in order to reduce lattice strain. Early electron micrographic studies2, 3 involving either extraction replica or normal replica techniques established the geometric or dendritic form of the carbide particles, although this approach led to dis- pute as to whether the particles grew within the plane of the boundary or grew into the matrix.4-6 More recent thin-foil studies&apos; have claimed to identify a discontinuous precipitation process involving M23C6 at grain boundaries, and the object of the present work was to attempt to clarify the situation using modern electron micrographic and diffraction techniques. 1) EXPERIMENTAL 1.1) Material. The steel selected for this work had a base composition of 24 pct Ni-25 pct Cr-3 pct Ti and contained about 0.04 pct C. The full analysis if given in Table I. This alloy was in the form of strip which had been hot- and cold-rolled to a thickness of 0.6 mm. 1.2) Heat Treatment. Specimens 4 cm long by 1 cm wide were solution-heat-treated for 3 hr in argon at 1150°C, followed by water-quenching. Specimens were subsequently aged in vacuo at 750°C for periods up to 500 hr. 1.3) Preparation of Electron Microscope Specimens. The heat-treated strips were cut bv spark machining into discs of 3 mm diam and 0.6 mm thickness. he-discs were dished on both sides using an electrolytic jet of 15 pct HCl electrolyte at 80 v. Final electro-polishing of the discs was carried out using 10 pct perchloric acid, 20 pct glycerol, and 70 pct ethanol at 10 v. The current density was kept below 300 ma. cm"2 by cooling the electrolyte to 0" to 5°C. As soon as a small hole appeared, the electropolishing was stopped and the specimen was quickly washed with ethanol.

Jan 1, 1969

By N. A. D. Parlee, I. D. Shah

The solubilities of oxygen in liquid Ag-Au, Ag-Pt, and Ag-Pd alloys have been determined in the range of 940° to 1200°C at 1 atm pressure of oxygen using an improved Sieverts technique. The additions of gold (0 to 57 pct), platinum (0 to 27 pct), and palladium (0 to 22 pct) to liquid silver continuously decrease the solubility of oxygen in liquid silver. Activity coefficients and interaction coefficients of oxygen in these alloys and have been calculated. The interaction coefficientscan be described by the following equations: Approximate second-order interaction coefficients (pM have been calculated. The contribution of the product, pMxNM, to In yo only becomes significant at high alloy concentrations. RECENTLY several investigators1"3 have redeter-mined the solubility of oxygen in liquid silver. In general the recent findings1" for Po, = 1 atm are in good agreement with the equation:4 log %O = 695.4/T + 1.086 [1] It is established1, 2 that the solubility of oxygen follows Sieverts&apos; law reasonably well, at least up to 1 atm partial pressure of oxygen. It should be noted that a very slight deviation from Sieverts&apos; law has been reported by Lupis and Elliott.3 Only recently has the solubility of oxygen in Ag-X binary liquid systems received much attention, and only the Ag-Cu, Ag-Au, Ag-Pt, and Ag-Pd systems have been studied. Par lee, Sacris, and zoellners reported that the solubility of oxygen in liquid silver increases progressively with the small additions of copper (0 to 0.5 pct) up to the point where the copper oxide phase appears. Lupis and ~lliott~ have reported that the solubilities of oxygen in liquid silver decrease progressively with the additions of gold, platinum, and palladium. However, their investigation was limited to 0 to 5 pct of these alloying elements, a range too limited to satisfy the requirements of the research program of this laboratory, where the solubilities of oxygen in the range of 0 to 30 pct were required for the calculation of chemical diffusion coefficients of oxygen in these alloys. The present paper deals only with the solubilities of oxygen in these alloys while another paper will deal with the diffusion of oxygen in these alloys. EXPERIMENTAL METHOD A Sieverts technique was employed which involved an improved design of the reaction tube, Fig. 1, as described briefly in a previous communication.4 Liquid melts (70 to 100 g) were held in Norton Alun-dum crucibles. The induction furnace used had a maximum output of 2.5 kw with very fine control. This induction system had excellent stability and the final equilibrium temperatures measured by calibrated Pt-Pt, 10 pct Rh thermocouples are believed to be within ±2C. These thermocouples were checked against the melting point of pure gold wire, and the results agreed with standard tables (±l°C). Each run involved a careful sequence of operations. The sample was heated to and held at about 900°C in vacuum for 3 to 4 hr with the thermocouple in a retracted position. After melting, the melts were usually exposed to a small amount of oxygen (0.5 to 2.0 cu cm) and then degassed slowly for 1 to 2 min to remove any oxidizable volatile impurities such as carbon and sulfur as CO, CO2, SO2, and SO forth. Argon gas was then allowed to enter the system. The protection tube containing the thermocouple was then

Jan 1, 1969

By T. W. Watson, D. R. Flynn

Measurements have been made of the thermal conductivity and electrical resistivity of two specimens of 0.005-cm (2-mil) Be-Cufoil over the temperature range -140° to +200°C. The thermal cmductivity of Be-Cu Alloy 125 was found to be significantly higher than that of Alloy 25, which had a higher impurity content. The thermal conductivity and electrical resistivity values obtained were in concordance with the Smith and Palmer relation for copper alloys which states that ? = 0.0239 (T/p) + 0.075 where A is thermal conductivity (W cm-&apos; deg-&apos;), p is electrical resistivity (microhm-cm), and T is absolute temperature (OK) , indicating that the Smith and Palmer relation can be used to predict the thermal conductivity of this type of Be-Cu alloy over the temperature range -140" to + 200°C to within an accuracy suitable for most engineering applications. THE National Aeronautics and Space Administration, Goddard Space Flight Center, Greenbelt, Md., requested the National Bureau of Standards to measure the thermal conductivity of 0.005-cm Be-Cu foil which was to be used to fabricate antennae for use in Radio Astronomy Explorer space craft. It was felt that measurements had to be made on the actual antenna material, rather than on a thick bar of similar material, since the cold-working and age-hardening properties of the alloy would make it very difficult, if not impossible, to place a thick bar in the same metallurgical state as the 0.005-cm material. As discussed in Section 111 of this paper, the thermal conductivity of many copper alloys can be computed rather accurately from electrical resistivity data using an empirical relation developed by Smith and palmer&apos; and further confirmed by owell.&apos; However, there has been very little work done on correlating thermal and electrical conductivities on Be-Cu alloys. We were reluctant to assume the validity of the Smith-Palmer relation on Be-Cu alloys because of the very large mass difference between beryllium and copper. As will be seen, however, our experimental results indicate that the Smith-Palmer relation is valid for the two alloys on which we made measurements. I) DESCRIPTION OF SAMPLES Samples of Be-Cu Alloy 25 and Be-Cu Alloy 125 were furnished to NBS in the form of rolled strip material, 0.005 cm thick by 5.08 cm wide. The Be-Cu Alloy 25 was purchased by NBS in the form of a continuous length of flat strip. The Be-Cu Alloy 125 was furnished to NBS by Goddard Space Flight Center in the form of two lengths of strip that had been formed into "tubing" of about 1.2 cm diam, with one side of the strip overlapping (but not connected to) the other side by about 90 deg. This "tubing" had been opened up to be flat and then rolled onto spools of about 3 cm diam. When unrolled, the strip would spring back into tubular form. Samples of both of the Be-Cu alloys were chemically analyzed by the NBS Analytical Chemistry Division. The beryllium content was determined quantitatively by the phosphate-gravimetric method to be 1.83 wt pct for Alloy 25 and 1.80 wt pct for Alloy 125. The two alloys were also examined by a general qualitative spectrochemical method for metallic elements. The Alloy 25 specimen contained between 0.1 and 1.0 wt pct Al, Co, Fe, and Si and between 0.01 and 0.1 pct Ni. The Alloy 125 specimen contained between 0.1 and 1.0 pct Co and between 0.01 and 0.1 pct Al, Fe, and Si. Other metallic elements present were in amounts less than 0.01 pct. The NBS Engineering Metallurgy Section measured the tensile strength, elongation, and Knoop hardness of both the Be-Cu Alloy 25 and the Be-Cu Alloy 125. These are given in Table I. The NBS Engineering Metallurgy Section also prepared photomicrographs of the two alloys; these are shown in Figs. 1 and 2.

Jan 1, 1969

By T. W. Watson, D. R. Flynn

,Measurements are reported for the thermal conductivity of four heat-resistant alloys which were measured at the National Bureau of Standards. Data are given for two samples of AISI Type 316 stainless steel covering a combined temperature range from -150° to + 800°C. The thermal conductivities of three samples of AISI Type 347 were measured over the temperature range from -150° to +150C. Thermal conductivity values are given for Carpenter 20 stainless steel from 100" to 800" C. Data are given for Inconel 702, in both the solution-annealed and the age-hardened condition, over the temperature range from -150" to +800C. SINCE 1958 the National Bureau of Standards, at the request of other government agencies or private laboratories, has carried out measurements of the thermal conductivity of a number of metals and alloys. This paper presents available thermal conductivity data obtained in this way on samples of four heat-resistant alloys. The data presented for Carpenter 20* stainless steel are, to the best of our knowledge, the only thermal conductivity values which have been reported for this alloy to date. Although thermal conductivity values for AISI stainless steels 316 and 347 have been reported by previous investigators, the present data are believed to be of particular interest because, for each alloy, the effect on thermal conductivity of small changes in chemical composition can be observed. The data on Inconel 702&apos; are of interest, not only for

Jan 1, 1969

By Y. Kondo, S. Yamazaki, Z. Asaki

Thermal deco7nposition of Pyrite particles in a fluidized bed with inert gas stream was studied. Assuming that heat transfer from the surroundings to the fluidized particles controls the overall decomposition rate, rate equations for the batch process and for the continuous process were derived. In the batch experiment, a linear rate equation satisfies the experimental results and the overall heat transfer coefficient calculated from the rate constant agrees fairly well with that obtained by Leva.l1 For the continuous process, two rate equations were derived, one on the assumption of complete mixing of particles and another on the upward piston flow of particles in a fluidized bed. The former holds for a bed containing a higher fraction of decomposed pyrite realized at lower feeding rates. The latter can be applied for a bed at higher feeding rates. Thus, segregation of particles in the fluidized bed was indicated at higher feeding rates. Bed temperatures also correspond to these conditions. ThERMAL decomposition of pyrite may be represented by Eq. [I]. The pressure of diatomic sulfur gas reaches 1 atm at about 690°C. The thermodynamics,&apos; kinetics,2&apos;3 composition, and properties3-5 of decomposed products of such a reaction have been studied. Pyrite is a very common sul-fide mineral and is often accompanied with other sul-fides. It is of basic interest in nonferrous metallurgy to clarify the behavior of pyrite in the pyrometallur-gical processes of sulfide minerals of metals such as copper, lead, zinc, nickel, and so forth. Interest in this reaction increased recently because of possible elimination of arsenic from pyrite in processing highly purified iron oxide pellets. Producing elemental sulfur from pyrite, instead of sulfuric acid, also aroused interest in this reaction. It is indicated that the thermal decomposition of solid particles, such as calcium carbonate, proceeds through three major sequential steps: heat transfer, interfacial chemical reaction, and mass transfer.637 It is known that the decomposed product of pyrite is very porous2, 3 and the diatomic sulfur gas evolved can easily escape through this layer of decomposed product. It depends upon the circumstances, therefore, whether the heat transfer to the interface within particles or the chemical reaction at the interface determines the overall decomposition rate. The enthalpy change in the decomposition of pyrite is about 33 kcal per mole FeS2 which is comparable to that of calcium carbonate. The decomposition of calcium car- bonate becomes more and more dependent on the rate of transport of heat when reaction temperature increases, such as occurs in a fluidized bed.6&apos;7 It is reasonable to presume, therefore, that the thermal decomposition of pyrite, an endothermic process, carried out in a fluidized bed may be analyzed according to the heat transfer controlling model. This work intends, first, to propose a mathematical model that determines the overall rate in a fluidized bed for the decomposition process and, second, to investigate a few characteristics of the fluidized bed based upon the experimental results obtained. KINETICS OF THERMAL DECOMPOSITION IN A FLUIDIZED BED It is intended in this section to obtain rate equations for thermal decomposition of pyrite in a fluidized bed by assuming that the overall rate is determined by heat transfer from the surroundings to the particles. Both batch and continuous processes are considered. 1) Batch Process. To obtain the rate equation in the batch process, the following two additional assumptions are made. First, the temperature of preheated inert gas, tg, blown into the fluidized bed is assumed to be the same as the temperature of the fluidized bed, tf. Thus, no heat exchange occurs between the gas and particles in the bed and only the heat transfer from the reactor wall kept at tw to the particles is to be considered. Second, the decomposition is assumed to start at the outer surface of the particles and to proceed toward the center. At any given time during decomposition, undecomposed pyrite remains in the tori at a temperature: td. The decomposed shell is composed of FeS1+x whose outer surface is at tp Diatomic sulfur gas evolving at the interface is heated to tf during its escape through the decomposed shell. This is illustrated in Fig. 1. With the above-mentioned assumptions of heat transfer, we have:

Jan 1, 1969

By Niels Hansen

Dispersion-strengthened aluminum products consist of an aluminum matrix containing finely distributed ceramic or intermetallic particles. Examples of the two types of product are SAP, in which the dispersed phase is aluminum oxide, and materials made from atomized aluminum alloy powder, in which the dispersed phase can be FeA1, particles.&apos; A fundamental difference between the two types of product is that the elongation of aluminum/aluminum oxide products decreases with increasing temperature, whereas the elongation of aluminum- FeA13 products, like that of aluminum alloys, increases with increasing temperature. As regards the structural stability, aluminum/aluminum oxide products are stable to temperatures above 600° C as aluminum oxide does not react with aluminum, whereas prolonged heating at above 400°C of aluminum-FeA1, products leads to coarsening of the intermetallic phase and loss of strength.&apos; On the basis of these results it is supposed that a dispersion-strengthened product combining strength, ductility, and stability at elevated temperatures may be obtained if the dispersed phase reacts with the matrix in such a way that the reaction does not proceed at any significant rate at the application temperature. Different ceramic or intermetallic compounds may be selected as the dispersed phase, and, as alloying of the matrix phase may also influence the reaction, many possibilities exist for each metal. In the present study, aluminum products containing different oxides have been examined. For a reaction to take place between the dispersed oxide and the aluminum the free energy of formation of the oxide (MeO) must be greater than that of aluminum oxide; the difference should, however, not be too great in order to limit the reaction rate. Furthermore the aluminum alloy formed when aluminum reacts with the dispersed oxide should have a melting point near

Jan 1, 1969

By E. Rudy, St. Windisch

The only complete phase diagram investigation of the Ti-W system is by Maykuth and coworkers,&apos; Fig. 1. Although previous work by Gonser2 indicated complete miscibility, later investigations3°5 essentially confirmed the diagram depicted in Fig. 1. The present study was undertaken because preliminary results on metal-rich ternary Ti-W-C alloys indicated complete solid solubility between 0 titanium and tungsten at temperatures above 1300°C—in contradiction to the presently accepted diagram. The powdered elements, as well as crystal bar titanium and tungsten sheet, were used in the preparation of the experimental alloys. The iodide titanium, obtained from Foote Mineral Co., Exton, Pa., had a total impurity content of less than 410 ppm, of which 150 ppm were interstitials (H, O, N, C). The overall purity of the titanium powder (Var-Lac-Oid Chemical Co., New York) was better than 99.7 pct. Major contaminants, in ppm, included: 0, 800; N, 10; H, 1500; Fe + Co + Ni + Cu + Zn, 50; C1, 200. The measured lattice parameters of the titanium were a = 2.94A and c = 4.68,A. The tungsten sheet and the tungsten powder (Wah Chang Corp., Albany, Ore.) contained the following impurities (in ppm, values in parentheses refer to the sheet tungsten): Mo, 50 (70); 0, 140 (110); Fe, 20 (60); Ni, 20 (not determined); N, 110 (not determined); sum of other impurities, <60 (<100). Samples from the iodide titanium bar stock and from tungsten sheet were prepared by repeated melting of the chipped materials in a nonconsumable electrode arc furnace under high-purity helium. The melted alloys were heavily cored, and homogeneity of the alloys could only be achieved after prolonged heat treatments at subsolidus temperatures. The majority of the alloys were therefore prepared by cold compacting the well-mixed powders in steel dies and pre-homogenizing the compacts for 6 hr at 1300°C in a tungsten-element furnace. The vacuum was better than 10"6 Torr, but for additional protection the sample container was wrapped in zirconium foil. Both preparation methods led to identical results. The measurements of the solidus temperatures were carried oat in the Pirani-type furnace described in a previous paper.6 Incipient melting in alloys containing between 20 and 90 at. pct W was rather difficult to detect visually, and therefore a photoelectric transducer system7 was employed to indicate the phase change. For the investigation of the solid-state equilibria, the specimens were first homogenized for 2 hr at slightly subsolidus temperatures in the Pirani fur- nace and then reequilibrated at, and rapidly cooled (-100°C per sec) from, the selected equilibrium temperatures. After the runs, the alloys were analyzed microscopically and by X-ray diffraction. With the exception of spot checks for oxygen and nitrogen in processed alloys, no other chemical analyses were performed. However, as the weight changes of the alloys during processing were within 0.05 pct and the lattice parameters of indeqendently prepared alloy series agreed within 0.0015A, it is reasonable to assume that no significant concentration shifts with respect to the nominal compositions had occurred. The measured solidus temperatures, shown together with literature data in Fig. 2, ascend smoothly from

Jan 1, 1969

By E. S. Tankins

The main purpose of this work was to study the effect of gold on the activity coefficient of oxygen in the liquid Fe-Au alloy and to determine how copper and silver change the activity coefficient of oxygen. A preliminary investigation has been made of equilibrium in the reaction of hydrogen with oxygen in some of the liquid gold alloys. The experimental method, which has been described in detail elsewhere,&apos; consisted of bubbling accurately known H-A-water vapor mixtures through the Fe-Au alloys contained in alumina crucibles within a vertical closed furnace. When equilibrium was reached, the samples were quenched by rapidly lowering the crucible under an atmosphere of argon to a water cooled brass fixture at the bottom of the furnace tube. The melts were found to freeze from the top in less than 4 sec. The heats were carefully prepared for oxygen analysis. The oxygen content was determined by vacuum fusion analysis.&apos; Only high purity electrolytic materials were used in this investigation. The activity and free energy of oxygen in the liquid iron alloys were studied by means of the reaction; The data for the 80 Fe-Au alloys, obtained as a function of temperature, are summarized in Table I and presented in Fig. 1, where log is plotted against . The results can be expressed by: The data were obtained using water vapor-hydrogen ratios between 0.04 and 0.30, and a 25 pct H2-75 pct A mixture. An oxygen content between 0.030 and 0.060

Jan 1, 1970

By David L. Holt, Walter A. Backofen, Anwar-ul Karirn

ANNEALING the binary alloy, Mg-0.5 wt pct Zr in a hydrogen atmosphere results in extensive precipitation of zirconium hydride. The morphology of these precipitates has already been investigated.lm3 Squires, Weiner, and phillips4 found, following creep testing of the hydrided alloy at 450" and 500°C, that hydride denuded zones formed along grain boundaries that were aligned approximately normal to the tensile axis. Zone formation was attributed to diffusional creep by magnesium transport down the prevailing stress gradients.4&apos;5 Recently, electron microprobe analysis by Karim, Holt, and Backofen6 showed the zones indeed to be zirconium-free and furthermore it was shown that in compression, zones formed along boundaries approximately parallel to the stress axis. Thus it was confirmed that the zones are formed by diffusional creep. Typical zone-formation is shown in Fig. 1. Karim, Holt, and Backofen also measured the con- tribution to the total strain, from diffusional flow, slip creep, and grain boundary shear: results showed that diffusional strain tends to saturate with increasing imposed strain, while grain boundary shear eventually becomes the dominant deformation mode. It was suggested in explanation that the precipitate-denuded zones are soft and easily sheared, such deformation contributing to the grain boundary shear measurement. A point to be emphasized is that the Mg-0.5 Zr alloy was not superplastic for the index of strain rate sensitivity of flow stress, m = a log log 6 was only 0.25. It was recognized that diffusional creep in a poly crystalline aggregate must be accompanied by boundary shearing.&apos; The suggestion was that the non Newtonian-viscous character of diffusional creep in the Mg-0.5 wt pct Zr alloy is due to resistance to sliding of boundaries lying approximately parallel to the tensile axis.= The work described in the present note should be seen against the above background for it represents initial efforts to observe in a similar way diffusional creep in a superplastic alloy. Previous work with the ternary-alloy Mg-6 Zn-0.5 Zr, pellet extruded, showed it to be superplastic however it does not contain resolvable precipitates to act as internal markers for diffusional creep. Also the fine grain size of the alloy (0.5 p) made conventional metallography rather difficult. Solubility relationships in the Mg-Zn-Zr system are not well known, however making reasonable guesses about the probable phase diagram of the ternary, Mg-Zn-Zr, various heat treatments were attempted to produce hydride precipitation. Finally a 16-hr anneal at 495&apos; in hydrogen was found to pro-

Jan 1, 1970

By W. F. Laverty

Two recent papers in this journal1,2 contain experimental evidence for an anomaly in the concentration gradient for tracer diffusion. In both papers, the authors suggest that this anomaly is due to a Gibbs&apos; absorption effect. Their hypothesis is that surface active tracer elements tend to remain in or near the surface adsorption layer, thereby altering the diffusion flux and concentration gradient. It is not clear how the anomaly can be explained in terms of an adsorption effect. Surface tension forces act parallel rather than perpendicular to a surface and therefore should affect only the rate of spreading of surface active agents tangentially across a surface. Frenkel3 has given a short treatment of surface tension as a driving force for surface diffusion. While the equilibrium concentration of a surface active agent at the surface of a solution is known to be higher than in the bulk, its chemical potential is necessarily the same. It is difficult to see how adsorption can result in an anomaly in the chemical potential gradient, which is the driving force for diffusion. A more detailed explanation by the authors of the adsorption mechanism is in order. A similar anomaly does not seem to arise where

Jan 1, 1970

By Anwar-ul Karim

In one of our recent papers, Cheng, Karim, Langdon, and Dom1 analyzed the creep mechanisms in a Fe-4 pct Si alloy. The experimental results of apparent ac-

Jan 1, 1970

By J. H. Swisher

Two recent papers in this journal1,2 contain experimental evidence for an anomaly in the concentration gradient for tracer diffusion. In both papers, the authors suggest that this anomaly is due to a Gibbs&apos; absorption effect. Their hypothesis is that surface active tracer elements tend to remain in or near the surface adsorption layer, thereby altering the diffusion flux and concentration gradient. It is not clear how the anomaly can be explained in terms of an adsorption effect. Surface tension forces act parallel rather than perpendicular to a surface and therefore should affect only the rate of spreading of surface active agents tangentially across a surface. Frenkel3 has given a short treatment of surface tension as a driving force for surface diffusion. While the equilibrium concentration of a surface active agent at the surface of a solution is known to be higher than in the bulk, its chemical potential is necessarily the same. It is difficult to see how adsorption can result in an anomaly in the chemical potential gradient, which is the driving force for diffusion. A more detailed explanation by the authors of the adsorption mechanism is in order. A similar anomaly does not seem to arise where

Jan 1, 1970

By C. Feng, W. E. Krul

A study was made of the development of texture and the anisotropy in plastic flow of Ti-8Al-1Mo-1V alloy. Based on Pole figure determinations, the shifting of texture induced by rolling at approximately 400°C was found to be due primarily to slip rotation for the major Portion of the material. Grain boundary shear is believed to be an important factor. The anisotropy of the textured alloy was examined in terms of the variations of yield stress under tension and the ratio of bi -axial strain increments µp, in the temperature range 25" to 290°C. The results were related to Hill&apos;s theory on plastic anisotropy. The Schmid factors of (1100)[1120], (1101)[1120/, and (1101)[1120] slip systems were analyzed and found to be compatible with the observed anisotropy. Cross-slip between these planes was proposed as a possible deformation mode. In a number of published articles, considerable interest has been directed to the possible achievement of texture hardening in hcp metals. Following Backofen, Hosford, and Burke,&apos; this phenomenon was related to the yield criteria of the material and was expressed in terms of the biaxial strain ratio, r = d?w/d?l. The higher the value of r, the greater is the expected potential for texture hardening under certain loading conditions. For a given material, r varies with direction. Such variation can be traced to the anisotropy in plastic flow and can be explained within the framework of the various modes of deformation. Hatch2 found that a high r value coincides with a texture whereby the (0001) pole is closely aligned with the surface normal for sheet materials, Based on the analysis of the slip on the {1010}, {1011}, and (0001) planes, Lee and Backofen3 and Avery, Hosford, and Backofen4 concluded that the resistance to thinning is reduced by the operation of the (0001) <1120> slip system; with this reasoning they were able to explain the low r values (i.e., r « 1) observed in magnesium alloy sheets in the rolling direction and in commercially pure titanium in the transverse direction. The general equation, dealing with plastic flow in a polycrystalline aggregate has been used to correlate the plastic anisotropy and texture. In this expression, T and s are shear and normal stresses, and dri and d? are shear and normal strain increments, respectively. Assuming that five slip systems are operative within each grain and applying the principle of maximum work,5,6 one can determine the m value among the available systems. On this basis, Hosford7 and Chin, Nesbitt, and Williams&apos; were able to correlate m with yield stress under plane-strain compression, and Svensson9 was able to predict the variation of yield stress in textured aluminum. These workers made their analyses from materials in which slip operation is known to be associated with plastic flow. Questions remain regarding the derivation of Hill&apos;s theory on plastic anisotropy,10,11 since it was formulated on von Mises&apos; yield criterion.&apos;&apos; Its ability to deal with other forms of deformation has been in doubt.13 Others have discussed the validity of Hill&apos;s quadratic equation relating strain and yield stress.14&apos;15 For hcp titanium, deformation by various modes of slip and twinning operations has been reported.16-20 If all possible modes of deformation operate and contribute substantially to the plastic flow, it is difficult to imagine how the quadratic expression can suitably describe the anisotropic plastic flow of titanium alloys. Backofen and Hosford15 considered that Hill&apos;s is a macroscopic theory and implied that the major mode of deformation by slip mechanism will adequately describe anisotropy of the material. In the present investigation, slip operation will be shown to play the major role in the development of sheet texture induced by rolling of a commercial titanium alloy. Although twinning and other modes of deformation may also operate, their operation is believed to be secondary. The anisotropic properties of the sheet, which can be expressed in terms of directional variation of r, µp = -d?w/d?l and the yield stress will be shown to be governed primarily by slip operation. MATERIALS AND EXPERIMENTAL TECHNIQUES The titanium alloy chosen for the present investigation had a nominal composition of 8 wt pct Al, 1 wt pct Mo, 1 wt pct V, and 0.1 wt pct interstitial impurities. Sheets varying between 0.1 and 0.15 in. thickness were used. The alloy was received in a condition which was prepared by rolling at 900°C and annealing at 700°C. Subsequently, the sheets were subjected to further reduction in thickness by rolling at 400°C. A total reduction in thickness of 65 to 70 pct was obtained by a series of quick passes in a rolling mill with intermediate reheating. Further reduction in thickness was not possible due to cracking developed at the edges of the sheets. X-ray measurements were conducted in a Siemens and a Norelco unit to determine the texture of the sheets. Reflection techniques were used exclusively with CuK, radiation and a nickel filter. The loss of X-ray intensity due to geometric defocusing was calibrated with a technique described previously." The (0001), (1010), and (1071) pole figures were plotted from 0 to 80 deg, and to present the texture elements quantitatively, inverse pole figures were constructed following the technique described by Jetter, McHargue, and Williams.22 Tensile experiments were carried out at 25", 175",

Jan 1, 1970

By J. P. Hirth, A. H. Clauer

A simple graphical method is presented for the determination of climb forces on dislocations exerted by uniaxial stresses. In conjunction with standard stereographic projections, the technique is applicable for any crystal system. Climb forces on glide dislocations in bcc crystals are determined as an application. In connection with a study1 of elevated temperature creep of molybdenum single crystals, a detailed analysis of the climb force on a dislocation was necessary. In general, such forces can be calculated for an arbitrary dislocation segment from the Peach-Koehler equation2 (or one of its variants3"6) where Fk are the components of the force per unit length of dislocation line, ?i of the unit sense vector tangent to the line, ojl of the stress tensor, bl of the dislocation Burgers vector, and is the Einstein permutation operator with components ?123 = ?231 = ?321 = —?132 = — ?321 = —?—213 = unity, and all other components zero. It is understood in the suffix notation of Eq. [I.] that repeated indices are to be summed over 1, 2, and 3. For the most general coordinate system, the matrix manipulations required to solve Eq. [I] are fairly complex. However, a simplification can be achieved by specifying a coordinate system based on the dislocation in question. The pertinent system involves cartesian coordinates xi, x;, xi, with attendant unit vectors e&apos;i; ei being parallel to the Burgers vector b, and e&apos;3; being parallel to the climb directions (b x ?), i.e., normal to the slip plane. In this coordnate system b = (bi, 0, 0) and ? = (?&apos;1,?&apos;2, 0). Hence, Eq. [I] yields for the climb force per unit length F3 = ?&apos;2s&apos;11b&apos;1—?&apos;1s&apos;12b&apos;1 [2] The first term on the right side of Eq. [2] is the climb force on the edge component of the dislocation, while the second is the (cross-slip) force normal to the glide plane acting on the screw component. Thus, the problem of determining the climb force reduces to that of resolving the stress components —il and s&apos;12 in the xi coordinate system. Several authors7- l0 have shown, for the glide case, that such stress resolution can be performed most readily by graphical methods. Therefore, we present a similar method for the climb case. Of the suggested methods, we follow that of Hartley and Hirth,9 which can be performed directly with a standard stereographic projection for the crystal system in question. We treat the case of simple tension, or compression, this being the most common creep test in which climb is important. A set of cartesian coordinates (x1, x2, x3) is fixed with x3 parallel to the specimen axis. This set is connected to the x&apos;i set by the factors defined in Table I. A perspective view of the coordinate systems relating them to the glide ellipse, is given in Fig. 1, while a stereographic projection of the coordinate systems is presented in Fig. 2. The transformation matrix connecting the xi and xi coordinates is x&apos;i =aijXj [3] where an a11 a13 aij = a21 a22 a23 a31 a23 [4] s The corresponding transformation for the stresses is i [5] The only nonzero component of okl for the simple tension case is s33,. Hence, using Eqs. [4] and 151, we find that Eq. [2] becomes F3 = b&apos;1s33 sin2 cos ?[cos ? sin a - sin ? cos a] [6] = m1b&apos;1s033 sin a- rn2b&apos;s33 cos a where sin a = 5: and cos a = ?i, with a the angle measured from b to ?, i.e., a polar angle in the x1, x2 plane. The same equation with a sign change applies for compression. A graphical plot of the "Schmid" factor m1, relating to the climb force on the edge component, is presented in the stereographic projection of Fig. 3. In this projection the glide plane normal points toward the top of the page and the glide direction points normal to the plane of the page. To use the graph, one

Jan 1, 1970

By Ashok K. Sinha

The quasi-binary systems "VFe3"—VCo,—VNi,— "VCu3"and "TiFe3"—TiCo3,—TiNi3-"TiCu3"have been studied by a combination of microscopic and X-ray methods. Of the Phases encountered, eleven had close-packed ordered layer structures. Within each system, there is an approximately linear variation of the degree of hexagonality of the stacking arrangement with electron concentration, e/a. A study of eighty -four known examples of AB3 structures in transition metal alloys indicates that at e/a = 8.65 the ordered structure of the close -packed layers changes from "triangular" (AuCu3 type) to "rectangular" (SbCu3 type). At e/a < 8.65, the slope of hexagonality us e/a line increases with the group number of the A component. An interesting series of close-packed ordered structures is known to exist at the composition AB3; however, their alloy chemistry has not yet been fully understood. Dwight and Beck1 observed a correlation between position of the components in the periodic table and the type of crystal structure of the binary AB2 structures formed by transition metals. No consistent effect due to atomic size was noted and they proposed that electron concentration* predominates in In the present paper, the AB3 structures are characterized by a symbol describing the stacking and a symbol specifying the ordered layer. The stacking symbol used was introduced by Zhdanov,7 and later used in the International Tables,8 and by Beck9 in his survey of possible layer stacking structures. Alternating positive and negative integers are used to represent the number of positive (e.g., in abcabc...) and negative (e.g., in cbacba...) stacking sequences. T denotes the triangular ordering found in close-packed planes of the AuCu3 structure and R the rectangular ordering found in close-packed planes of the SbCu3 structure, Figs. 3(a) and (b). The present structure symbols are listed in Table I alongside the prototypes, where known, and other structural characteristics of AB3 phases found in the present investigation. EXPERIMENTAL The starting materials were metals of 99.9+ purity. The alloys were prepared by arc melting under argon atmosphere using a nonconsumable tungsten electrode and water-cooled copper hearth. The total weight loss upon melting and subsequent annealing was always less than 0.5 pct and hence the alloys will be referred to by their intended (unanalyzed) compositions. The alloys were homogenized and annealed at suitable temperatures in the range 750" to 1200°C, the annealing periods varying from 3 days at 1200°C to 10 days at 750°C. The heat treatments were carried out in sealed silica capsules under argon atmosphere and with a molybdenum foil cover between the alloy and the walls of the capsule. The quenched alloys were microscopically examined and reduced to powder by crushing or filing. The powders were, whenever necessary, given a stress-relieving anneal at the original annealing temperature. X-ray powder patterns were obtained with an asymmetrical focusing camera, a Guinier-deWolff focusing camera, or a Debye-Scherrer camera. Cr, Co, or Cu radiations were used. In some cases, to ensure the minimum degree of contamination, the deeply etched specimens were mounted in the asymmetrical focusing camera to obtain an X-ray pattern. Internal silicon standards were employed for lattice parameter determinations. The intensity calculations were made by using a Fortran IV program

Jan 1, 1970

By Kun Li, Alex Simkovich

The rate of dissolution of alumina in carbon-saturated liquid iron has been studied experimentally in a system where alumina was in the form of a cylindrical rod immersed in an iron bath contained in a graphite crucible. Data obtained consisted of the concentrations of aluminum in the melt as a function of time. In the case of static experiments, the data are shown to agree with theoretical prdictions based on the diffusion of aluminum.. The rate of dissolution was greatly increased by the rotation of the alumina rod. It is concluded that the diffusion of aluminum from the alumina/metal interface is the rate-controlling step. In the past, thermodynamic investigations of systems encountered in ferrous process metallurgy have received widespread attention. More recently, considerable work has been devoted to the study of kinetics associated with these systems in an effort to determine their rate controlling mechanisms. The alumina-iron system is of great importance in ferrous metallurgy. Yet information concerning kinetics of reaction in this system is seriously limited. The present study was made in order to establish the rate-controlling step for dissolution of solid alumina in liquid iron. LITERATURE REVIEW A number of papers concerning dissolution of solid metals in liquid metals have been reported in the literat~re. Generally, for these simple systems, dissolution is controlled by mass transfer of the dissolving species. Complex systems involving dissolution of solid metal carbides and oxides in liquid metals and slags have been studied to a much lesser extent. Skolnick5,6 reported on the reaction between liquid cobalt and poly-crystalline cylinders of tungsten carbide, in which the cylinders were dissolved while being rotated about their longitudinal axes at various speeds and temperatures. As a result of unexpected preferential grain boundary attack by the liquid cobalt, large errors in the measured dissolution rates occurred because of loss of tungsten carbide grains to the liquid cobalt. Nevertheless, it was possible to establish that the liquid Co-W carbide reaction was not controlled by mass transfer. In a similar approach, cooper7 was able to show that artificial sapphire rods, (alumina single crystals) dissolving in lime-alumina-silica slags obeyed a mechanism of mass transfer control. Here, again, the rods were rotated at various speeds and temperatures, and the process was followed as a function of these variables. Forster and Knacke8 took a practical approach to reaction between slags and refractories. By blowing argon through refractory cylinders of silica, silli-manite, or dolomite and directing the gas to rise along the slag-refractory interface, it was possible to increase the rate of mass transfer. Although the method was admittedly crude, it nevertheless permitted an evaluation of the relative stabilities of refractories with respect to slag attack. Data were interpreted on the basis of mass transfer control. EXPERIMENTAL TECHNIQUE Apparatus. An illustration of the apparatus used in this study is shown in Fig. 1. The furnace consisted of a Morganite recrystallized alumina tube wound with a molybdenum coil. A secondary molybdenum heater was mounted around the upper half of the primary coil to aid in controlling the thermal gradient within the furnace. The primary heater tube was 3 in. in ID and 30 in. long. A reducing mixture of 95 pct N and 5 pct H was maintained around the heating elements. Thermal insulation was provided by alumina powder. The chamber within the primary combustion tube contained a boron nitride block near the top to assist in controlling the thermal gradient to the furnace and also to provide a bearing surface for the rotating graphite shaft. The outside diameter of the graphite shaft was $ in. A separate threaded graphite specimen holder was screwed into the end of the shaft. The holder contained a tapered hole drilled into the end to guide the oxide specimens as they were pressed into it for mounting. Additional guidance for the rotating graphite shaft was furnished by a water-cooled bronze bushing attached to the top of the furnace. A steel clamp was fastened to the upper end of the graphite shaft and rested on a thrust bearing; the shaft and clamp were driven by a dc motor through a set of gears. Two O-rings located immediately above the bronze bushing maintained a gas-tight seal about the graphite shaft. The lower half of the alumina tube housed the crucible and charge, which were placed on a 3/4-in. diam movable alumina support tube. With this arrangement, charges could be inserted into or removed from the furnace while the hot zone was maintained at or above 1000°C. To control the temperature of the furnace, the thermocouple was mounted inside the support tube and in contact with the crucible bottom. Stray electric fields in the furnace were of sufficient intensity to cause erratic indications by the thermocouple. By enclosing the thermocouple protection tube in a molybdenum sheath and grounding this shield, the problem was eliminated. Output of the thermocouple went to an automatic continuous balance controller. Procedure. A typical run was as follows. First, electrolytic iron was premelted in graphite crucibles and cast into graphite molds with the same configura-

Jan 1, 1970

By K. Tangri, M. Chaturvedi

The addition of 0.5 wt pct Cu to Zr-2.5 Cb alloy increases the as -quenched hardness of the hexagonal martensitic a&apos; phase, produced by water-quenching bccß-Zr phase, by about 35 pct. This strengthening has been attributed to the solid -solution hardening of the matrix. On aging ternary martensite, a&apos; phase reverts to equilibrium a and Zr2Cu and ß-Cb precipitate out, mainly at the twin and grain boundaries, causing a secondary hardening of the matrix. COLD-worked Zircaloy-2 pressure tubes have been in use in power reactors for a considerable period of time. The search for a better material led to the development of Zr-2.5 wt pct Cb alloy which in the quench-aged condition develops 50 pct more strength than that of cold-worked Zircaloy-2, however, its corrosion resistance in water and steam in the temperature range of 316" to 400°C, in absence of neutron flux, is inferior to that of zircaloy-2.&apos; Work carried out by Ells et al.1 and Dalgaard2 has shown that the corrosion properties of Zr-2.5 wt pct Cb alloy can be considerably improved by the ternary addition of 0.5 wt pct Cu. This paper is concerned with the effect of 0.5 wt pct Cu on the formation of martensitic a and its aging characteristics in a Zr-2.5 wt pct Cb alloy. MATERIALS AND EXPERIMENTAL TECHNIQUES Zr-2.5 Cb-0.5 Cu (referred to as the ternary alloy) and Zr-2.5 Cb (referred to as the binary alloy) alloys, supplied by the Chalk River Nuclear Laboratories of the AECL were used. The detailed chemical analysis is given in Table I. Cold rolling and swagging with frequent intermediate anneal of 1000°C were used for the initial fabrication of the alloys. All the heat treatments were carried out after the specimens were wrapped in zirconium foils and encapsulated in silica tubes under a vacuum of 5 x 10-6 mm of Hg. For optical metallography and hardness measurements specimens were mechanically and then chemically polished in a 45 pct HNOj, 45 pct HzO, and 10 pct HF solution. Hardness was measured on a Vickers hardness tester using a 10-kg load. For each specimen at least fifteen indentations were made in order to obtain a representative value. The phase identification and structural analysis were carried out using X-rays and electron diffraction techniques. Wires of 1.5 mm diam reduced to 0.12 mm diam by chemical etching were used for making Debye-Scherrer powder patterns using Cu Ka radiation in a 114.6 mm diam camera. Carbon extraction replicas were prepared by etching the specimens, after depositing a layer of carbon on the metallographic specimen, in one part HF and thirty parts ethyl alcohol. Thin films were prepared by electropolishing heat-treated 3/4 by 1/2 by 0.005 in. thick strips using a modified Bollman-Window technique. The 10 pct perchloric acid-90 pct methyl alcohol bath was kept at -50°C and polishing was done at 5 to 10 V. The thinned specimens were washed in ethyl alcohol at -30º to -40°C and dried between filter papers. Replicas and thin films were examined in a Phillips 300 G electron microscope. For resistivity measurements thin strip specimens 0.02 by 0.3 by 10.0 cm long were used. The potential leads were spot welded to the specimens in order to maintain a fixed length for the initial and the final resistivity measurements. The resistivity was measured by a Kelvin bridge in a temperature controlled room. The temperature was maintained at 72º ±1°F and the accuracy of the resistivity measurements was 0.03 µa-cm. RESULTS As-Quenched Structures. In order to produce a homogeneous matrix to study the precipitation reaction the solution-treatments of both the alloys were carried out in the -field region. From the Zr-Cb phase diagram due to Lundin and cox3 ß/a + ß phase boundary for Zr-2.5 wt pct Cb alloy is 820°C. Ells et al.1 have reported this boundary for Zr-2.5 Cb alloy containing 1100 ppm 0 to be at 920°C. Also, the addition of 0.5 wt pct Cu reduces this temperature by 50°C. Therefore, the solution-treatments were carried out at 1000°C to ensure that the alloys were in ß-phase region. The soaking time was 1 hr and the specimens were water-quenched. The as-quenched hardness of the binary alloy was 245 Vpn whereas, that of the ternary alloy was 330 Vpn. The X-ray diffraction studies indicated that the as-quenched structure of both the alloys consists of martensitic hexagonal phase a&apos;, with a c/a ratio of 1.591, and some retained ß-Zr. The presence of a&apos; phase was further confirmed by thin film electron microscopy. Electron micrographs of typical ß-quenched structures of the ternary and the binary alloys are shown in Figs. 1 and 2, respectively. Fig. 3 shows the diffraction pattern from an area similar to that shown in Fig. 1. Although, the as-quenched hardness of the ternary alloy is about 35 pct greater than that of the binary alloy, the structure of both the alloys seems to be the same. The matrix of both alloys is heavily twinned and shows very few dislocations. Furthermore, there is no evidence of any precipitation taking place in either of the two specimens during quenching from the solution-treatment temperature. Aging Behavior of Martensitic a&apos;. The aging kinetics of the ternary alloy were followed by resistivity and hardness measurements. The as-quenched values

Jan 1, 1970

By A. U. Seybolt, J. L. Walter

The effects of the addition of 0.5 pct ThO2 (by volume) on the grain structure and texture of heavily rolled tungsten sheet were studied. Powder metallurgy ingots were rolled to sheet, 0.001 in. thick, and samples were annealed at temperatures from 1200" to 2500°C. The heating rate to the anneal temperature was varied from 3°C per min to 6500°C per min. The orientations of the largest grains were determined by X-ray diffraction. The disposition and loss of the ThO2 particles were determined by electron transmission microscopy and the activation energy for remozlal of the thorium was measured by mass spec-troscopy. Heating rates below about 800 C per min produced large, highly elongated grains. Higher heating rates produced much smaller, less elongated grains. The grain structure and texture of the slowly heated samples were identical to the structures and textures of heavily rolled tungsten foil conventionally doped with aluminum, silicon, and potassium but the recrystallization temperature was about 200°C lower. There was stringer-like dispersion of larger ThO2, particles superimposed on a uniform dispersion of fine particles. The particles increased in size and decreased in number with time at temperature. The loss of particles was accompanied by formation of grain boundary voids and surface pits. The activation energy for removal of the ThO2 was about 40 kcal per mole. THE addition of small amounts of aluminum, silicon, and potassium to tungsten has a profound effect on the grain structure of heavily rolled sheet1 or drawn wire."4 Thus, "doped" tungsten sheet, rolled to 0.001 in. and recrystallized, develops a structure consisting of large, highly elongated grains of a specific preferred orientation.&apos; It has been shown that the elongated grain structure was caused by a dispersion of particles, identified as mullite (Al6si2O13),1,4 in strings parallel to the rolling direction in sheet or to the wire axis. Identical results were obtained for iron which was doped with glass and rolled to 99 pct reduction of thickness and recrystallized.5 Again, the glass particles were disposed in strings parallel to the rolling direction. The strings retarded boundary migration in the lateral direction but grain growth was able to proceed relatively unhindered along the direction parallel to the strings.1,5 In both the doped tungsten and the glass-doped iron, the particles were highly plastic during the high-temperature deformation. Since mullite melts at about 1800°C and the glass employed melts at about 810ºC, the particles were probably molten during the recrystallization anneals (above 1800°C for the doped tungsten and 850°C for the glass-doped iron). There are indications in the literature that particles not plastic at hot-working temperatures (up to about 1550°C for tungsten) may also impart elongated grain structures by primary recrystallization of worked alloys. Examples are dispersions of tantalum carbide in chromium,6 and ThO2 in nickel where elongation ratios of recrystallization grains of up to 20:l were obtained.7 Strings of ThO2 particles in W-ThO2 wire have been seen by Rieck.8 In view of the available evidence, it was of interest to extend the previous studies of doped tungsten and glass-doped iron to include W-ThO2 sheet materials. Of specific interest was the grain structure, preferred orientation, recrystallization temperature, and disposition of the thoria particles. EXPERIMENTAL PROCEDURE A) Material Preparation. About 380 g of blue tungsten oxide (approximate composition WO3) was wet with a sufficient amount of aqueous solution of Th(N03)4 to provide 0.5 vol pct ThO2. The wet mixture was stirred to distribute the doping material uniformly throughout the powder. Stirring was continued while the mixture was heated until it was completely dry. The dried, doped mixture was then reduced to tungsten powder by heating at 850°C for 2 hr in a stream of dry hydrogen. The doped tungsten powder was hydropressed in a rubber sack at pressures of 50,000 psi to produce an ingot approximately 2 cm diam by about 5 cm long. Next, the pressed cylinder was heated in hydrogen for 2 hr at 1350°C to render it strong enough for machining. The cylinder was machined to a square cross section of 1.6 by 1.6 cm with rounded corners. Finally, the bar was heated for 2 hr at 2150°C in hydrogen to provide a sufficiently dense mate rial to withstand the hot-rolling operation. Prior to rolling, the ingot was reduced in thickness by about 20 pct by forging at 1550°C. This served to increase the density of the material and to widen it slightly for better rolling characteristics. The forged ingot was then rolled at 1550°C to a reduction of 45 pct of thickness, following which the rolling temperature was reduced to 1300°C and the slab rolled, with several reheats, to 0.050 in. Further reduction was accomplished at 800°C in tungsten sheet packs to a total reduction of about 99.85 pct. B) Annealing Treatment and Observation of Structure. Small samples of the rolled foil were annealed in one of two ways. Some of the samples were suspended in a covered tungsten can and annealed at temperatures from 1200" to 2200°C for various times in vacuum of l0-7 to 10-6 mm Hg. The can was heated by induction and temperatures were determined by optical pyrometry

Jan 1, 1970