By J. E. Hilliard

A procedure is described for determining, from measurements on a section, the moments of any degree n (i.e., the mean value of Dn, where D is a linear dimension) of the size distribution of particles (or grains) in an opaque sarnple. The analysis is applicable to particles of alnzost any shape and to any mixture of shapes. However, if absolute values of the wloments are required, it is necessary to know what shapes are present and the relative frequency of their occurrence. In addition, certain shape-dependent parameters have to be evaluated before the formulas can be used. The measurement required is the distribution of intercept lengths. This can be determined either visually or with an automatic scanning instrument. Corrections me derived for the bias due to instrumental end effects. The proposed analysis has the following advantages over existing ones: 1) Confidence limits are easily estimated for the measured properties or, conversely, the number of counts required to achieve a given accuracy can be determined. 2) The analysis is not restricted to particles of a special shape. 3) The error resulting from any known degree of departure of the actual from the assumed particle shape can be estimated. 4) The computations are simple and, apart from a change in constants, are independent of particle shape. 5) The number of particles per unit volume can be determined by a simple counting procedure. MANY procedures have been described for determining the size distribution of particles from measurements on a section (or plane of polish). They differ from one another in the property measured on the section (radius, intercept length, profile area) and in the method used for the numerical solution of the integral equation relating the property to the particle size distribution. However, all existing analyses share at least two of the following disadvantages. 1) They are limited to a particular shape of particle (usually spherical). 2) It is very difficult to determine how the statistical sampling error is propagated into the computed size distribution. The investigator thus has no means of knowing the reliability of his result and, what is of equal concern, he is unable to estimate how many measurements are required to obtain a result of the required accuracy. 3) It is also difficult to assess the error resulting from any deviation between the actual and assumed particle shape. The foregoing limitations stem from the complex relationship between the particle size distribution and the distribution of the property measured on the section. As will be shown, they can be avoided by defining the size distribution in terms of discrete parameters

Jan 1, 1969

By K. R. Carson, J. Weertman

An attempt is made to ascertain the mechanism of tangle and cell formation and its dependence upon dislocation-interstitial carbon interactions. The strain-hardening behavior of single crystals of 3.25 pct Si-Fe was determined at 300° and 425°K and under conditions of both continuous and interrupted tensile strain. Significantly enhanced hardening was observed in crystals deformed at the elevated temperature, and it was further accentuated by interrupted straining. Transmission electron microscopy was used to study the resultant dislocation structures. Strain aging was found to aid tangle and cell formation at 425°K, but at both temperatures embryo tangles formed solely from primary glide dislocations, presumably by a process involving cross slip and "mushrooming". IN the course of plastic deformation all bcc metals and alloys develop a dislocation structure characterized by loose-knit groups of tangled dislocations. With increasing strain the tangles become more tightly knit and grow larger; finally a three-dimensional cellular substructure is formed:1 This process has been observed with the transmission electron microscope.'-l7 However, most investigations were confined to the study of nearly pure polycrystalline metals at relatively low temperatures. At intermediate temperatures, 0.17 to 0.14 Tm where T, is the melting temperature in degrees absolute, the mobility of interstitial impurities such as carbon is high enough to permit migration to nearby glide dislocations but is still low enough so that a significant drag force is exerted.18,19 it is also in this temperature range that a hump occurs in the curve of work-hardening rate vs temperature for iron. Analogous plots for tantalum" and columbiumzo show a definite upward trend in the work-hardening rate. Keh and Weissman1 have pointed out that this behavior may be explained solely on the basis of changes in the dislocation configuration: at low temperatures the dislocations tend to be relatively straight and uniformly distributed, but at intermediate temperatures tightly knit tangles and cellular substructure appear. The interference of these tangles with glide dislocations causes the observed increase in the work-hardening rate. This explanation appears reasonable, yet one might ask what factors cause tangle formation to be so favorable at intermediate temperatures. It seens likely that the strong dislocation-interstitial interactions which are known to occur in this temperature range are at least partly responsible," with the magnitude of the effect being proportional to the interstitial concentration. The purpose of the present work is to study the relationship between tangle formation and strain hardening in a bcc metal in the temperature range 0.17 to 0.4 Tm. Particular emphasis was placed upon a study of the effects of interstitial-dislocation interactions. Single crystals of 3.25 pct Si-Fe containing about 200 ppm of C in solid solution were used in the investigation for the following reasons: 1) The mobility of interstitial carbon in 3.25 pct Si-Fe is negligible at 300°K but increases rapidly at slightly elevated temperature22. Hence, differences between the flow curves and dislocation structures of crystals deformed at 300°K, 0.17 T,, and crystals deformed, say, at 425°K, 0.24 Tm, should be appreciable because of the enhanced dislocation-carbon interactions at the elevated temperature. This effect was accentuated in some samples by interrupted straining, thereby introducing a certain amount of aging. 2) Near room temperature, slip in suitably oriented 3.25 pct Si-Fe single crystals is largely confined to the (110) planes.23'24 Dislocation structures formed under conditions of single glide are the least complicated and their method of formation is the most easily discernable. 3) Dislocations in Si-Fe can be tightly locked with carbon atmospheres by a low-temperature aging treatment. The subsequent thinning of samples to foil thicbess causes little or no rearrangement in the dislocation structure.25 EXPERIMENTAL PROCEDURE Large single-crystal sheets of 3.25 pct Si-Fe were donated by Dr. C. G. Dunn of the General Electric Research Laboratory, Schenectady, N. Y. The orientations of the sheets were determined and slabs 1.0 by 0.25 by 0.05 in. were cut such that the desired tensile axis corresponded to the long dimension. The slabs were mechanically polished and subsequently decar-burized by heating at 1000°C for 3 days in a flowing wet-hydrogen atmosphere. A carbon content of about 200 ppm was introduced by heating at 805°C for 25 min in a flowing atmosphere of dry hydrogen containing heptane vapor. Shaped copper tools were then used to spark-machine at 0.125 by 0.50 in. gage length onto each slab. Vacuum annealing at 1225°C for 2 days followed by a quench into the cold end of the furnace to retain carbon in solid solution concluded the soecimen preparation. Continuous tensile flow curves for crystals of severa1 orientations Were obtained both at 300' and 425°K. A strain rate of 6.67 x 10-4 Per set was used in these and all other tests. Crystals oriented for single glide, B and D in Fig. 1, were subjected to a 3.5 pct plastic elongation to insure uniform slip along the gage length; they were then immediately subjected to interrupted strain cycling as indicated in Fig. 2(a). Each cycle consisted of unloading to 1.5 kg per sq mm, holding

Jan 1, 1969

By W. T. Roberts, N. G. Turner

A study of the fatigue properties of several grades of commercially pure titanium has established that the strain-aging process is of minor importance in the development of a fatigue limit and a relatively high fatigue strength ratio. Metallographic observations and damping measurements at room temperature indicate that striations are able to spread from grain to grain only at stress levels above the fatigue limit. This suggests that the fatigue limit represents the stress above which large-scale dislocation unlocking takes place. Fatigue tests on annealed material at - 60" and - 196" c showed that under conditions when a thermally activated diffusion process would be suppressed the fatigue limit is not eliminated. Prestraining at room temperature did not have a detrimental effect on fatigue strength at room temperature but a decrease was recorded at — 60°C. This is further evidence that initial dislocation locking is a important strengthening mechanism. TITANIUM and titanium alloys have S-N curves with a definite fatigue limit, and a high ratio of fatigue limit to UTS can be attained. Other materials which show similar fatigue characteristics are mild steel and some Al-Mg alloys. The fatigue limit of these materials has been associated with their strain-aging capacity. It is well-known that commercial-purity titanium contains interstitial impurities which can give rise to a sharp yield point, and a small strain-aging effect following static strain has been demonstrated.7 This type of aging reaction is differentiated from the dynamic aging process when aging occurs during plastic deformation, and which is generally observed at elevated temperatures. In a titanium at room temperature, dislocation locking is associated with the interaction of interstitial oxygen, nitrogen, and carbon atoms with dislocations. Ehr-lich has shown that the distortion produced by introduction of these atoms into the hcp lattice has no shear stress component and hence there is no interaction between the stress field and the screw component of a dislocation. Thus the dislocations as a whole are only weakly locked. It is clear that strain-aging effects in hcp a titanium will be much less pronounced than those observed in bcc iron and steel. In recent years, the attribution of the fatigue limit solely to strain aging has been questioned. It has been pointed out that a definite fatigue limit is observed at temperatures as low as -196°C in some titanium alloys,' and strain aging is not expected to be effective at this temperature. The role of initial locking of dislocations in determining fatigue behavior has been examined in low-carbon steel by Oates and Wilson. They showed that under conditions in which the aging potential is low the factors which control the buildup of local stresses and hence affect dislocation unlocking, e.g., grain size, are important. There are indications that other metals can have a definite fatigue limit with no established strain-aging capacity, an example being magnesium12 which has the same crystal structure as a titanium. The spread of plasticity from grain to grain in hexagonal metals may be more difficult than in cubic metals because of the limited number of slip systems in the former, and this may account in part for their fatigue behavior. The present work was undertaken to elucidate the relative importance of crystal structure, strain aging, and initial dislocation locking in determining the properties of commercially pure titanium when subjected to cyclic stressing. 1) EXPERIMENTAL METHODS Three grades of commercial-purity titanium were used and a material of lower interstitial content was prepared by melting high-purity Japanese sponge titanium (referred to as H.P. Ti). The compositions and typical mechanical properties of the materials are shown in Table I. Fatigue tests were made in push-pull (zero mean stress) using an Amsler Vibraphore machine at a frequency of about 160 cps. Two types of fatigue specimen were used—one with a waisted gage length for determination of S-N curves and the other with a parallel gage length for metallographic studies and damping measurements. After careful machining and mechanical polishing, all specimens were electropolished prior to fatigue testing. The electrolyte consisted of 10 parts methyl alcohol, 6 parts 2-butoxyethanol, and 1 part perchloric acid (SG 1.54) and it was maintained at a temperature of -10" to -20°C during polishing. Tests at room temperature were normally carried out with the specimen immersed in a silicone oil bath which could be heated for elevated-temperature tests.

Jan 1, 1969

By Che-Yu Li, J. L. Gregg, W. F. Brehm

Oriented, oxygen-doped niobium bicrystals were tested in liquid lithium. The grain boundaries were attacked preferentially. The depth of the penetrated zone varies as (time)2. The penetration was aniso-tropic, had a high activation energy, and increased with the increased oxygen doping level. A possible model was proposed to account for the experimental observations. 1 HE grain boundary penetration of a metallic system by liquid metal has been studied by several investigators. Their results are summarized by Bishop.' Most of these works show that the penetration by liquid metal corresponds to the phenomenon of liquid metal wetting. In the case of a grain boundary, wetting will occur when twice the solid-liquid interfacial tension is smaller than the grain boundary tension resulting in the replacement of the grain boundary by two new solid-liquid interfaces. Other possibilities exist; for example, the atoms of the liquid metal may diffuse into the grain boundary region due to chemical potential gradient. The gradient can be produced by impurity segregation or simply be due to the increase in solubility in the grain boundary region. The penetrated grain boundary in these cases may remain solid at the test temperature. The Nb-Li system has been of considerable interest because of its possible technological applications. For fundamental interest it provides a possibility of studying the grain boundary penetration process which is not controlled by the wetting mechanism. The pure niobium is not attacked by the liquid lithium, but if niobium containing more than 300 to 500 ppm oxygen by weight is exposed to liquid lithium, corrosion occurs at the solid-liquid interface and preferentially at grain boundaries. Previous investigators2-' have proposed that this preferential corrosion at grain boundaries is caused by oxygen segregation there, with subsequent inward diffusion of lithium to form a Li-Nb-0 compound. These investigators also found that the corrosion could be retarded by adding 1 pct Zr to the niobium to precipitate the oxygen as ZrO2 upon proper heat treatment. However, there are no quantitative data on the kinetics of the grain boundary penetration process to test the validity of the proposed corrosion mechanism. In this work an investigation of this penetration process in oriented bicrystals was made as a function of the oxygen doping level in the bulk niobium and the grain boundary orientation. A possible model for the penetration process based on the experimental results was proposed. EXPERIMENTS Oriented niobium bicrystals were grown by arc-zone melting oriented single-crystal seeds.7 These bicrystals contained simple tilt boundary. The [001] directions in the two grains were tilted about a common [110]. The bicrystals were 31/2 in. long and 5 by 4 in. in cross section with the straight, symmetric, planar grain boundary longitudinally bisecting the crystal rod. The bicrystals were doped with oxygen by anodically depositing a layer of Nb2O on the surface in a 70 pct HNO solution at 100 v, using a stainless-steel cathode. The specimens were homogenized by annealing in evacuated quartz tubes at 127 5°C. Oxygen content of the niobium was measured from microhardness values, after DiStefano and Litmman.' Supplementary checks were made with vacuum-fusion analysis.7 Individual test specimens cut from the doped bi-crystal rods, about by by % in. in size, were tested inside double jacket sealed capsules. The inner jacket was niobium, the outer was stainless steel. The niobium inner jacket eliminated the problem of dissimilar-metal mass transfer.' The lithium (99.8 pct pure, obtained from Lithium Corp. of America) was handled only in a purified argon atmosphere in a Blickman stainless-steel glove box. After introduction of lithium, the capsules were sealed by welding. Further detailed experimental procedures are given in Ref. 7. The capsules were heat-treated in vertical Marshall resistance furnaces. Temperatures were controlled to When heating above 1100°C, it was necessary to seal the furnace work tube and flow argon through to prevent failure of the stainless-steel outer jacket of the capsule. Tests were made on 6" 2", 16" 2, and 33" i2" bicrystals at oxygen levels up to 2600 ppm by weight in the 6' and 16" crystals and with 1300 ppm oxygen in the 33' crystals. The oxygen levels were controlled to 100 ppm. Most of the quantitative data were obtained from 16" bicrystals between 800" and 1050°C. The capsules were quenched into water after the test and cut open with a water-cooled abrasive wheel. The capsules were then submerged in water, which dissolved the lithium and freed the specimen. Measurement of the depth of the penetrated zone in the grain boundary was done either on metallographically prepared surfaces or directly on the grain boundary plane after the specimen was fractured in tension in the grain boundary plane. The depth of penetration measured by both methods agreed well. Further details describing these techniques have been reported elsewhere.'p7

Jan 1, 1969

By M. J. Marcinkowski, K. S. Sree Harsha

A detailed numerical analysis has been made of the equilibrium configuration of partial dislocations in a blocked deformation twin under an externally applied stress. Twins made up of both pure screw and pure edge partials have been considered. The components of stress in the vicinity of the twin tip associated with each of these configurations have been plotted. It has been found that at some critical degree of oblateness the shear stress fields of the blocked screw or edge twin can both sPontaneously nucleate slip, whereas only the component of stress oxx about the edge twin can nucleate and propagate cracks. TWINNING becomes a predominant mode of plastic deformation at low temperatures and/or high strain rates. Fig. l(a) shows what must be the first step in the formation of a deformation twin, namely the formation of a loop of imperfect dislocation bounding a stacking fault. In an fcc crystal the partial dislocations have Burgers vectors of the type 1/6 a,(112) and the fault is of the intrinsic type while in the bcc crystal the partials have Burgers vectors of the type ao(lll). The stacking sequence of (111) planes in a perfect fcc crystal is given by ABC ABC, and so forth, and in one which contains a twin by ABCABACBA, and so forth. It is apparent that the stacking fault and twin give rise to no mistakes associated with adjacent close-packed planes; however, with respect to second-neighbor close-packed planes the faulted crystal has twice as many mistakes as the twin. The energy of the twin boundary may thus be taken to be one-half that of the intrinsic fault boundary. In the case of the bcc crystal the stacking sequence of (112) planes is given by ABCDEFABCD, and so forth, in a perfect crystal, by ABCDCDEFA, and so forth, in a crystal which contains a fault, and by ABCDCBAF, and so forth, in one which contains a twin. An analysis similar to that applied in the fcc crystal shows that both the fault as well as the twin involve no neighbor violations across adjacent planes. However, there are twice as many violations across second-neighbor (112) planes associated with the fault as compared to that of the twin. Thus once again the energy of the twin boundary may be taken as one-half that of the fault. It is important to note that, unlike the fcc, the faults in the bcc crystal involve first nearest-neighbor violations and are thus expected to be of much higher energy than those in fcc crystals. A more detailed analysis of the material discussed above can be found in Ref. 1. To a good approximation then, the lenticular twin shown in Fig. l(b) can be generated by adding partial dislocation loops on successive (111) planes for fcc crystals or (112) planes for bcc crystals in the manner shown, with no additional expenditure of chemical energy other than that required for the fault shown in Fig. l(a). In practice, deformation twins are much more extended than that shown in Fig. l(b) and more closely resemble one shown schematically in Fig. l(c). It is readily apparent that the free energy of the twin and matrix are identical. In those cases where the partials lead to a structural change, the free energy of the material contained within the dislocation array is lower than that of the matrix and we have the so-called martensite transformation. The present investigation is the first in a series of five major theoretical-experimental efforts which will deal with the static and dynamic behavior of twin nucleation and growth. There has been a recent surge in activity pertaining to the equilibrium shapes of twin lamellae2'3 and

Jan 1, 1969

By C. J. Rosa, W. C. Hagel

An attempt is made to determine the diffusion coefficients of oxygen ions in hypostoichiometric zirconium oxide. A phenomenological theory is developed for three-phase, unidirectional volume diffusion of a gaseous species from a planar source. Knowledge about oxygen diffusion in a and ß zirconium and experimentally measured rates of movements of interfaces permit the evaluation of oxygen ion diffusivi-ties in ZrO2-x. The results conform to the relationship: sq cm per sec, for the temperature range of 875" to 1050° C. DIFFUSION coefficients of oxygen ions in stoichio-metric oxides have been studied by many investigators. The obtained results not only supplement the knowledge about the lattice-defect structures of oxides and conduction mechanisms but also provide information of technological importance. Rate processes such as oxide sintering, high-temperature creep deformation, and oxidation of metals and their alloys are directly dependent on diffusion phenomena. Unfortunately, diffusion coefficients obtained from studies on stoichio-metric oxides cannot be treated without restraints when applied to oxidation kinetics, if precise evaluations of oxidation rates are desired. Oxides formed on metals are usually nonstoichiometric and exhibit nonuniform distribution of either cation or anion vacancies across their thicknesses. Debuigne and Lehr1 extended Danckwerts'2 mathematical analyses and furnished a semitheoretical treatment for evaluating oxygen diffusion coefficients in zirconium oxide in terms of weight gain measurements during oxidation of zirconium in the temperature range 400° to 850°C. Their calculations are based on theoretical partitioning3 of the total amount of oxygen between a zirconium and its oxide phase. An inherent discrepancy appears to continue throughout their calculations. The amount of oxygen confined to the oxide phase should be corrected by multiplying the calculated oxide thickness by the inverse of Pilling-Bedworth ratio, if expansion of zirconium dioxide is taken into account. The purpose of the present investigation is to provide a new semitheoretical treatment for evaluating diffusion coefficients of moving species in hypostoichiometric oxide. The analyses are relevant to unidirectional volume diffusion. Although the presented method is quite general, its applicability will be discussed in terms of kinetic measurements from oxidation of zirconium at temperatures above the a/ß transition, for reasons stated in the later part of this paper. EXPERIMENTAL Pure, 99.93 wt pct, zirconium samples of approximately 2 by 1 by 0.35 cm were exposed to oxygen for various times at four temperature levels: 875°, 950°, 1000°, and 1050°C. High-purity, better than 99.9 vol pct oxygen was passed through a cold trap and columns containing anhydrous CaSO4 to remove residual water vapor. Before exposing to oxygen at a pressure of 500 Torr, specimens were subjected to wet abrasion on 200- through 600-grit Sic papers and polished with 1—p diamond dust. Prior to oxidizing, all zirconium samples were vacuum-annealed at 10-6 mm Hg for about 15 min at the test temperature. The temperature variation across the uniform heat zone was ±2°C from the preset value. Final polishing, for phase thicknesses measurements, was performed by using 8- and 1-p diamond dust and followed by vibrator polishing with 0.05-µ ? Al2O3 solution. Measurements of phase thicknesses were made by projection on a metallographic viewing screen. Conventional powder X-ray analyses for the oxide were employed. RESULTS Fig. 1 is an example of the cross section of oxidized zirconium. Designations of phases given below this figure are the same as those used in the three-phase diffusion system represented by Fig. 5 in the following section. Zirconium oxidized for longer exposure times showed two types of oxides: white oxide at the surface and an underlaying layer of gray oxide. X-ray powder patterns of these oxides at room tern-

Jan 1, 1969

By H. I. Aaronson, C. Laird

The kinetics of thickening and of lengthening of ?' plates in an Al-3.93 pct Cu alloy in the temperature range 203" to 300" C were determined by means of transmission electron microscopy. The rate of thickening was found to be less than that allowed by volume diffusion control at all temperatures, by amounts which increased with decreasing temperature, in agreement with the predictions of a general theory of precipitate morphology.1 Thickening was treated on the basis of the ledge mechanism. Ledges were deduced to spread across the broad faces of ?' plates at volume dzjrfusion-controlled rates, as anticipated from the disordered structure of their edges. Lengthening of 8' plates, on the other hand, took Place more rapidly than allowed by volume dzjrfusion. This occurred despite clear morPhological evidence of a bmrier to growth at the edges of these plates. It was concluded that the misfit dislocation structure comprising the barrier requires that lengthening take place by a jog mechanism. The tnisfit dislocations, however, also serve as diffusion short circuits, and allow high overall lengthening rates to be achieved. In Part I' it was shown that, within the range of aging temperatures and times studied, the broad faces of 8' plates formed in Al-4 pct Cu are fully coherent with the a, matrix. Virtually .all of the dislocations present in these faces were found to have developed as a result of plastic deformation in the a phase. Such dislocations are thus "intruders", rather than the more usual misfit-compensating variety. The edges of 8' plates were confirmed, by extension of the earlier studies of Mat-suura and Koda,3 to be made up of edge-type misfit dislocations, in sessile orientation with respect to lengthening of the plates. These interfacial structures should cause 8' plates to thicken and to lengthen at rates less than those allowed under the condition of volume diffusion control, such as would be expected if the interphase boundaries had disordered structures.' The narrow width of 8' plates, the reproducible crystallography of their broad faces, and the appearance of these plates in cross section as octagons rather than as circular discs2 provide qualitative support for these deductions. The present study of the rate of thickening and the rate of lengthening of 8' plates was undertaken in order to examine them on a quantitative basis. I) THICKENING KINETICS OF THE BROAD FACES OF?' PLATES A) Literature Review. The measurements now available on the thickening kinetics of single-phase precipitate plates consist of one plot of the thickening of a proeutectoid ferrite plate in an Fe-C alloy,' showing (as predicted) thickening rates less than those allowed by volume diffusion control. B) Experimental Procedure. Details of the preparation of the 4-3.93 pct Cu alloy used in this study have been previously reported.4 As in Part 1,' transmission electron microscopy was the observational tool employed. A general description of the apparatus and procedures of the electron microscopy studies is given in Section I of Part I. In thin foils, 0' plates tend to form at and parallel to the foil surface.' A direct investigation of the thickening process by means of hot-stage transmission electron microscopy was therefore not feasible. It was thus necessary to use the conventional method of aging individual bulk specimens for a wide range of different times at the various temperatures studied. In each specimen, the thicknesses of a number of plates were measured. Since thin foils prepared from "bulk-aged" material contain a large proportion of grains with orientations near (001) , it was relatively easy to find, near the edges of the foils, the characteristic multifold patterns of intersecting extinction contours which indicate regions where the foil is exactly at an (001) orientation. The thicknesses of large numbers of plates were measured along the (200) branches of the "stars" so that the 8' plates were precisely parallel to the optical axis of the microscope. Wherever possible, intersecting extinction contours were adjusted with the parameter s > 0 to improve the visibility of the plates in bright-field illumination. These precautions, in combination with taking the measurements at the thinnest parts of the foils, minimized the errors in the measurement of the thickness of the plates resulting from inexact parallelism to the electron beam. Since the plates were very thin, it was not easy to measure their thickness on the photographs. The techniques of enlargement and of microdensitometry were employed to minimize errors from this part of the measurement. A further source of possible error, that the plates can appear thicker because of contrast associated with mismatch normal to the plane of the plate, was also considered. The images of the plates were usually thinner than those of dislocations, however, and no anomalous changes in apparent plate thickness were observed when regions of foil containing plates were tilted through various diffracting conditions. Any error from this cause must therefore be small. Other sources contributing errors were: a) the microdensitometer traces per se and the subjective estimates of their peak limits, and b) slight fluctuations in magnification associated with small changes in the current of the objective lens of the electron microscope. The overall error probably amounted to no more than 5 to 10 pct. In order to obtain readily interpretable data on thickening kinetics, it is essential that the diffusion fields of adjacent ?' plates not be allowed to overlap. Calculations'-' showed that this condition is definitely not ful-

Jan 1, 1969

By H. I. Aaronson, C. Laird

Although the past results of X-ray experiments indicate that the broad faces of 0' plates are coherent with their matrix, dislocations lying in arrays have frequently been observed at these boundaries by transmission electron microscopy. Critical experiments employing the latter technique have been carried out in order to determine the origin of these dislocations. It is concluded that 8' plates are essentially coherent with the matrix at their broad faces throughout the aging temperature/time envelope studied. Virtually all of the dislocation arrays observed are deduced to have been formed by plastic deformation accompanying transformation. The proportion of dislocations arising from convexity of the plates is shown to be negligible by comparison with that from plastic deformation. At the higher aging temperatures, a[001] dislocations appeared in moderate numbers. These dislocations were traced directly, however, to the ledgewise dissolution of 0' occasioned by the formation nearby of 0 crystals. On the other hand, since there is a parametric difference normal to the broad faces of the ?' plates, mismatch dislocations do form at their edges. A previous conclusion that these dislocations have Burgers vectors of type a[001] was confirmed directly. The edges of 0' plates were observed to develop octagonal shapes when growing, but circular shapes during dissolution. 1 HIS paper presents the results of an investigation of the interfacial structures of plates of the transitional phase, 8', formed in an A1-4 pct Cu alloy. In a companion paper, Part 11, the effects of these structures upon the migration kinetics of a:?f boundaries are reported. This work is pa.rt of a general program designed to establish the basis of precipitate morphology. The present authors in Al-Ag,1 and whitton2 previously in U-C alloys, have used transmission electron microscopy to examine directly the vander Merwe3-6 networks of dislocations anticipated7 to compensate the small amount of lattice misfit normally founda at the broad faces of Widmanstatten plates. Since the broad faces of 0' plates are considered to be perfectly coherent with the corresponding habit planes in the a matrix,' no dislocations should be present at these faces. Many reports have been published, however, giving evidence to the contrary.10-18 The primary objective of this investigation was therefore to ascertain the nature of these dislocation structures. An attempt to do this is described in the first three sections of this paper. Inspection of the matching of the a and 8 ' lattices at the orientations of the 0:0' boundary corresponding to the edges of 0' plates raises the possibility that these edges may be made up of rather closely spaced edge- type misfit dislocations oriented so as to be sessile with respect to the lengthening or shortening of the plates. Since this structure should severely inhibit migration of the plate edges (Ref. 7, Part II), a situation not originally anticipated,' an experimental determination of the interfacial structure of the edges of 8' plates was clearly in order, and is reported in Section III. Those aspects of the experimental procedure applicable to both Parts I and I1 are presented in the next section. Specific procedures applicable to individual aspects of each investigation, and also the relevant surveys of the literature, are then individually reported in the appropriate sections. I) GENERAL EXPERIMENTAL PROCEDURE The material used in both parts of these studies was the same as that of a previous investigation:" strips of A1-3.93 pct Cu, 0.009 in. thick, prepared as before, solution-annealed at 548°C for 6 hr, and quenched. Details of subsequent aging, and in some cases deformation treatments, are given in the Experimental Procedure sections of the individual parts of both papers. Specimens of the heat-treated strips were electro-thinned as beforeLg and examined in a Philips EM 200 microscope equipped with a goniometer stage. A commercial hot stage, of the grid-heater type and capable of * 30-deg tilt about one axis in the plane of the specimen, was also used for kinetic studies. The usual precaution of calibrating for the additional heat supplied by the electron beam was taken.19 A 16-mm cine cam-I era mounted outside the viewing window was frequently used to record the transformations. Conventional selected-area diffraction and dark-field viewing techniques were used to identify the precipitates in the foils. Normal bright-field images corresponding to two-beam diffracting conditions or dark-field images were employed to characterize the dislocations observed at the interfaces of the precipitates. The application of these techniques to the study of an interphase boundary, and the interpretation of the images,20'21 has been fully described in a previous paper.'

Jan 1, 1969

By F. D. George, M. J. Salkind

Al3Ni whisker-reinforced aluminum was found to exhibit good Charpy impact toughness and little notch sensitivity even though its room-temperature tensile elongation parallel to the whiskers is only 2 pct. This impact behavior was maintained d liquid nitrogen temperature (-196"C). It is postulated that this behavior is due primarily to the presence of the continuous aluminum matrix which provides sufficient 10calized ductility in the vicinity of the crack tip to absorb considerable energy from the advancing crack. The impact behavior of Al-Alni was found to be quite anisotropic. Of six orientations studied, the transverse orientation having the notch normal to the whisker axis was found to exhibit the lowest impact energy, whereas the transverse orientation having the notch parallel to the whisker axis was found to exhibit the highest impact energy. A significant differnce was noted between the impact behavior of material containing needlelike whiskers and that containing bladelike whiskers. Only two of the six orientations studied exhibited complete fracture for the material containing needlelike whiskers. On the other had, most of the specimens containing bladelike whiskers exhibited complete fracture. It was postulated that the bladelike whiskers block transverse flow, thus reducing the amount of plastic deformation ahead of the crack tip. One of the more significant advantages of composite materials is the prospect of combining high strength with toughness. In general, toughness is associated with materials which exhibit considerable ductility and can deform plastically in the presence of a stress concentration. Very strong materials which resist plastic deformation generally exhibit low toughness. At first glance, then, it would appear as though strength and toughness are mutually incompatible so that useful engineering materials would have to be a compromise between the two. One approach to the problem of combining the high intrinsic strength of ceramics with the toughness of metals was to mix them together to form a cermet. Unfortunately, the toughness of cermets was found to be rather disappointing. Whisker reinforcement of metals, however, appears to be a more promising approach. It has been demonstrated that whisker-reinforced metals produced by unidirectional solidification exhibit enhanced strength due to the presence of high strength nonmetallic whiskers. The total strain capacity of these composites in the direction of fiber alignment is limited to that of the fibers, the matrix being unable to carry the load once the fibers have failed. A characteristic, then, of whisker composites is low ductility in the direction of whisker alignment, on the order of a few percent elongation. This low elongation, which is usually associated with brittle behavior, should not be taken as an indication of low toughness. Such a material can exhibit significant ductility in directions other than parallel to the fibers7 and can therefore possess significant intrinsic toughness. Toughness in a fiber-reinforced metal is derived from several mechanisms. The first is due to the toughness of the matrix itself. A continuous ductile metal matrix can act as an effective crack arrest medium by undergoing localized plastic deformation. Cracks initiated from the surface of the composite or from a brittle fiber failure must travel through the matrix before reaching another brittle phase particle. A second crack arrest mechanism peculiar to fiber composites is due to the fact that, as a crack travels through the matrix and approaches a fiber, the plastic deformation ahead of the crack tip will result in loading of the fiber. This causes the matrix shear strength in the plastic zone to be apparently higher, thus extracting more energy from the crack and diverting the crack at an angle to the original direction of propagation. A third crack arrest mechanism occurs in fiber composites which exhibit a weak bond between fiber and matrix. The idea was proposed by Cook and Gordons that if a crack propagating transversely in a fiber composite were made to turn and run along the fibers by decohesion of the fiber-matrix bond, then toughness would be imparted by the blunting of the crack tip and the creation of new surfaces. The last mechanism, interfacial decohesion, is commonly noted in naturally occurring fiber composites such as wood, bone, and bamboo, and has been observed in man-made composites such as glass fiber-reinforced resins,g silica fiber-reinforced aluminum," laminated steel," and tungsten and silica fiber-reinforced electroplated copper.'' The first mechanism, crack arrest by plastic deformation in the matrix, has been noted in tungsten wire reinforced cast copper." The purpose of this investigation was to quantitatively assess the toughness of a whisker-reinforced metal as a function of orientation. Previous investigation considered only cracks propagating nominally perpendicular to the reinforcement. In this investigation, crack propagation in three mutually perpendicular directions as well as three intermediate orientations was investigated. The system chosen for study was the unidirectionally solidified A1-A13Ni eu-tectic alloy which has a microstructure consisting of 10 pct by volume of A13Ni whiskers in a matrix of aluminum This material exhibits two different kinds of whisker morphology, depending upon the rate at which it is solidified.' At low rates of solidification (less than 2 cm per hr) the whiskers are bladelike, whereas at higher rates of solidification they are

Jan 1, 1969

By R. A. Vandermeer, J. C. Ogle

The preferred crystallographic orientations (texture) developed in randomly oriented, poly crystalline niobium during rolling were studied by means of X-ray diflraction techniques. The evolution of texture at both the surface and center regions of the rolled strip was carefully examined as a function of increasing defamation throughout the range 43 to 99.5 pct reduction in thickness. Certain aspects of the center texture development in niobium are in agreement with the predictions of a theory by Dillamore and Roberts, but others cannot be explained by the theory in its present form. Above 87 pct reduction by rolling, a distinctly different texture appeared in the surface layers which was unlike the center texture. The present results are compared with previous results obtained from other bcc metals and alloys. RANDOMLY oriented, poly crystalline metal aggregates when plastically deformed to a sufficiently large extent develop preferred orientations or textures. In a recent review article, Dillamore and Roberts1 pointed out that the nature of the developed texture may be influenced by a large number of variables. These include both material variables such as crystal structure and composition and treatment variables such as stress system, amount of deformation, deformation temperature, strain rate, prior thermal-mechanical history, and so forth. From a practical point of view, the control of preferred orientation may often be important for the successful fabrication of metals into usable components. During the past few decades many experiments have been devoted to the study of deformation textures. This work, however, has been confined in large part to metals and alloys that have an fcc crystal lattice. By comparison, bcc metals and alloys have received much less attention, and consequently our understanding of preferred orientations in these materials is only shallow. This state of affairs worsens when it is realized that almost all of our present howledge about this class of materials derives from studies on irons and steels.' The bcc refractory metals, which are relative newcomers to the industrial world, have, on the other hand, been given at best only passing glances in the area of texture development. Our understanding of the evolution of preferred orientations in bcc metals can only remain fairly limited until systematic studies of metals and alloys other than the irons and steels have been carried out and the influence of the many variables has been determined. To that end a program was initiated to investigate in detail texture development in niobium. The present paper reports some of the results of this study. Textures were determined at both the center and surface of strips rolled variously to as much as 99.5 pct reduction in thickness at subzero temperatures. Emphasis in this paper is on texture description and on texture evolution during rolling to progressively heavier deformation. EXPERIMENTAL PROCEDURE The niobium was purchased from the Wah Chang Corp. as a 3-in.-diam electron-beam-melted billet. Chemical analysis indicated the impurities to be less than 300 ppm Ta, 40 ppm C, 10 ppm H, 170 ppm 0, and 110 ppm N. All other impurities were below the limits of detection by spectrochemical analysis. This large-grained billet was fabricated into specimen stock so that a fine-grained randomly oriented grain structure resulted. This was accomplished in three deformation steps alternated with recrystalli-zation anneals of 1 hr at 1200°C in a vacuum of low 10"6 Torr range after each deformation step. The first step was to alternately compress the billet 10 to 20 pct in each of three orthogonal directions. The second step was to compress in only two directions 90 deg apart to produce a 2-in.-sq bar. The final step was to roll this bar 50 pct to give a 1-in. by 2-in. cross section. After the final anneal, metallo-graphic examination showed the material to have an average grain size equivalent to ASTM No. 5 at 100 times (i.e., 0.065 in. diam). Specimens cut from the center and edges of this bar gave no indication of detectable preferred orientation when examined by X-ray diffraction. Samples 1.5 in. long, either 0.625 or 0.750 in. wide, and approximately 0.400 in. thick were machined from this fabricated ingot. The surfaces corresponding to the rolling planes were ground so as to be parallel. The samples were chemically polished in a solution of 60 pct nitric acid and 40 pct hydrofluoric acid (48 pct solution) prior to rolling to remove any cold work introduced in the machining operations. Rolling was accomplished with a 2-high hand-operated laboratory rolling mill that had 2.72-in.-diam rolls. Prior to operation, the rolls were polished with 600 grit paper, cleaned with acetone, and then soaked in a container of liquid nitrogen for several hours. The samples were also soaked in liquid nitrogen prior to rolling and were recooled between each pass. While some slight heating of the samples occurred during rolling, this procedure maintained the sample temperature well below 0°C at all times. The samples were rolled unidirectionally, and the rolling plane surfaces were not inverted during any phase of the operation. The draft per pass averaged between 0.010 to 0.012 in. After 96 or 97 pct reduction the draft was reduced to 0.001 to 0.002 in. per pass. Samples were rolled to various reductions in thickness between 43 and 99.5 pct.

Jan 1, 1969

By R. D. Daniels, T. G. Oakwood

A study was made of the effects of small quantities of hydrogen on the mechanical properties of colum-bium. Tensile specimens, hydrogenated to concentrations of 20 to 200 ppm, were tested at temperatures of 300°, 191°, and 77°K. Although hydrogen was found to have little effect on the strength of columbium, the ductility of Cb-H alloys was found to be quite sensitive to both hydrogen concentration and temperature. At 300°K, an abrupt loss in ductility occurred at a critical hydrogen concentration, although some ductility was observed beyond the tolerance limit. A similar result was found at a lower hydrogen concentration at 191°K. At 77°K, however, a more gradual loss in ductility with increasing hydrogen concentration was observed. Hydrogenated columbium was thus observed to undergo a ductile-brittle-ductile transition. Metallographic examination of fractured specimens revealed extensive porosity at both 77° and300°K which was a distinct function of hydrogen content. At 191°K, although some secondary cracking was noted, the amount of observed porosity was minimal. These observations are interpreted in terms of hydrogen solubility and mobility as a function of temperature and in the role of hydrogen in promoting growth of microcracks. lHE effect of hydrogen on the mechanical properties of the refractory metals is not, at present, completely understood. A number of studies have shown these materials to be susceptible to hydrogen embrittlement. Roberts and Rogers1 have found that vanadium can be embrittled by hydrogen. It was further demonstrated that fracture undergoes a ductile-brittle-ductile transition as the temperature is lowered from 150° to -196°C; i.e., there is a ductility minimum observed at a certain temperature. The ductility is increased by either raising or lowering the temperature from this point. A more complete study by Eustice and Carlson2 on vanadium containing 10 to 800 ppm placed the ductility minimum at about -100°C with variations reportedly due to hydrogen content and strain rate. Ductility minima have also been found at certain temperatures for tantalum containing 7 ppm H3 and 140 ppm H.4 At hydrogen concentrations above 270 ppm, however, the ductility return at low temperatures was considerably reduced.4 In the case of columbium, some disagreement exists in the literature. Eustice and Carlson,5 Wilcox et al.,6 and Imgram et al.4 failed to find a ductility minimum although a composition-dependent ductile-brittle transition was observed. Hydrogen concentrations in these investigations were 20 ppm,5 1 to 30 ppm,6 and 200 to 390 ppm.4 However, Wood and Daniels7 observed a rather pronounced ductility minimum at hydrogen contents ranging from 19 to 252 ppm. Those theories of hydrogen embrittlement involving the precipitation of diatomic hydrogen which have been applies to ferrous metals8-12 do not seem to be applicable to the case of columbium and other exothermic occluders. Such theories propose that extensive crack formation and propagation occurs by the precipitation and expansion of diatomic hydrogen at internal voids and microcracks. However, photomicrographs of hydrogenated columbium do not show any evidence of damage introduced by the sorption and precipitation of diatomic hydrogen; rather, at high hydrogen concentrations, a hydrogen-rich second phase is precipitated.13'14 In addition, a number of these theories require the development of high hydrogen pressures at voids in the structure.8'10'12 This does not appear to be feasible in the concentration ranges discussed in the aforementioned paragraphs. The possible interaction of atomic hydrogen with microcracks resulting from dislocation pile-ups15,16 remains in doubt since pile-ups have not been observed in bcc metals17 including columbium.18 Wood and Daniels7 have put forth the possibility that a hydride precipitation could be responsible for crack nucleation in columbium. Work by Longson19 has shown that hydrogen embrittlement of columbium parallels the bulk solubility limit; i.e., as the solubility increases, for instance with temperature, the amount of hydrogen necessary to cause embrittlement also increases. Although a hydride precipitation appears attractive as a means of nucleating microcracks in columbium, what require more intensive study are the low-temperature anomalies which have been observed, i.e., the ductile-brittle-d'ictile transition characteristics. Also, the hydrogen concentrations where embrittlement occurs are often below the bulk solubility limits determined by Albrecht et al.13,14 and Walter and Chandler.20 This work is an attempt to determine more definitively the effects of concentration and temperature on the mechanical properties of dilute Cb-H alloys. EXPERIMENTAL PROCEDURE Ultrahigh-purity columbium rods, obtained from the Wah Chang Corp., were cold-reduced by rotary swaging. A chemical analysis is given in Table I. The material was cut into cylindrical blanks 1.50 ±0.005 in. long. Individual specimens were either given a stress relief anneal at 750°C or recrystal-lized at 1200°C. Resulting microstructures were either a "bamboo" structure characteristic of a wrought material or a recrystallized structure with a grain diameter of approximately 100 n. All heat treatments were carried out in a vacuum of 10-5 Torr or less.

Jan 1, 1969

By J. L. Jorstad

The hypereutectic Al-Si alloys 390 and A390 have wear characteristics superior to any of the more common aluminum casting alloys. This excellent wear resistance, coupled with good mechanical properties, high hardness, and low coefficient of thermal expansion, has made these alloys candidates for the all-aluminum internal combustion engine, the application for which they were primarily developed. A390 alloy is intended for sand and permanent mold casting, and requires a lower iron ccxltent (0.5 pct maximum) than its die casting companion 390 alloy (0.6 to 1.1 pct Fe). The 17 pct nominal silicon in these alloys provides sufficient quantities of the hard primary silicon phase to assure a high degree of wear resistance, yet little enough of this phase, to minimize the casting and m achining problems associated in the past with the hypereutectic alloys. The mechanical and physical properties of 390 and A390 alloys are competitive with the best of the common aluminum casting alloys with the exception of low ductility. This low ductility is not considered a detriment, since in many applications these alloys replace cast iron. Corrosion resistance is similar to the standard alloys 380 and 333. Numerous parts, of varying degrees of complexity, have been cast of alloys 390 and A390, including engine blocks and heads. The deviations from normal good handling and casting practices that are required for the alloys are those associated with the presence of the primary silicon. To obtain optimum strength and machinability, the molten alloys should be treated with phosphorus to refine the primary silicon phase. Care must be exercised to properly control the pouring temperature and rate in order to minimize primary silicon growth and segregation. AUTOMOTIVE engineers have for years recognized the advantages of lighter weight and better heat transfer that aluminum could offer as material of construction for engine blocks. These advantages alone, however, are insufficient justification for acceptance of aluminum engines by the automotive industry. To be acceptable, an aluminum engine first must pass all tests to which cast-iron engines are subjected, and, in addition, must represent no cost penalty in manufacturing. None of the conventional aluminum casting alloys have sufficient wear resistance to withstand the tests to which cast iron is subjected as a cylinder bore material, and recent attempts to manufacture aluminum engines with cast-in-place iron sleeves could not compete costwise with the equivalent cast-iron engine. The prerequisite to an acceptable aluminum engine seemed to be a casting alloy with a high degree of wear resistance that would eliminate the necessity of cast-in iron sleeves or liners. The hypereutectic A1-Si alloys 390 and A390 have met this challenge.' Combined with modified pistons and a patented cylinder bore surface finish,2 the performance of these alloys in more than 1300 cold start and cold scuff tests, over 3500 hr of dynamometer wear and endurance tests, and more than 350,000 miles of road tests leaves no doubt as to the feasibility of running on bare aluminum cylinder bores. ALLOY DEVELOPMENT The desirable characteristics of the hypereutectic A1-Si alloys have been recognized for some time. Their excellent wear resistance and low coefficient of thermal expansions have been used to advantage in the production of diesel-type pistons in Europe and to a limited extent in this country. The major contributor to the good wear resistance of these alloys is the extremely hard primary silicon phase in the microstructure. Although the percent silicon used experimentally has been much higher, most commercial alloys have ranged from about 14 to 25 pct. Generally, as the silicon content is increased, wear resistance increases, and the coefficient of thermal expansion decreases. With increases in silicon, however, machinability and cast-ability tend to suffer. The development of a satisfactory aluminum engine block material at Reynolds involved the testing and evaluation of many alloys, covering a wide range of silicon contents and numerous variations of iron, copper, magnesium, manganese, and other alloying additions. Castability, mechanical and physical prop-

Jan 1, 1969

By M. I. Jacobson, M. L. Hammond

The solid solubilities of high-purity silver, aluminum, chromium, copper, and iron in zone-refined beryllium have been determined. Diffusion couple sandwiches of beryllium with aluminum, copper, and silver foil and diffusion couples of beryllium with two-phase alloys in the Be-Cr. Be-Fe, and Be-Ag systems were analyzed by electron beam micro-probe techniques. This paper describes the material used, the experimental methods for preparing the diffusion couples and the alloys, the analytical techniques, and the results obtained. The results are compared with those of previous investigators who used materials of lower purity. ~NVESTIGATORS of beryllium phase diagrams have often been hampered in their interpretations of certain phase boundaries because of the relatively low purity of the beryllium used. This has sometimes resulted in the appearance of three phases in the regions where only two should exist. Advances in purification methods, specifically zone refining, have made available beryllium that is considerably purer than the material previously used for phase diagram studies. The primary object of this investigation was to reex-amine portions of the beryllium-rich end of the binary systems of beryllium with silver, aluminum, chromium, copper, and iron to determine more accurately the limits of terminal solid solubility. The five elements—silver, aluminum, chromium, copper, and iron—include some which are commonly found as the major impurities in beryllium, some of which are being used as solid-solution alloying elements, and some of which are used in ductile matrix alloys. They are thus of considerable importance to physical metallurgists who must work with beryllium but who must rely on the present inaccurate or incomplete diagrams. The determination of more reliable diagrams would aid researchers concerned with the problems of alloying, heat treatment, and ductility. MATERIAL The beryllium was acquired from the Franklin Institute in the form of a single-crystal, 6 in. long by 1 in. in diam, zone-refined in three passes from Pechiney SR-grade beryllium bar. The principal impurities, as determined by mass spectrography at Battelle Memorial Institute, are shown in Table I. Vacuum-melted copper, silver, and aluminum, and electron-beam zone-refined iron were obtained from the Materials Research Corp. in the form of 1/2-in.- diam bars. Iodide chromium was obtained as flakes from the Chromalloy Corp. Analyses supplied with these metals are shown in Table 11. EXPERIMENTAL PROCEDURE Preparation of Diffusion Couples. Two types of dif-fusion couples were used in this study. For the copper, silver, and aluminum systems, the couples were sand-

Jan 1, 1969

By H. W. Schadler

The superplastic behavior of low carbon and manganese bearing steels has been evaluated. The results of elevated-temperature stress-strain rate and elongation tests are reported which indicate that high strain rate sensitivity (>0.5) and adequate elongations are achievable in ultrafine-grained steels 1 to 2 p, but at strain rates which are not commercially attractive. It has been demonstrated that the fine grain size is retained after long times and high strains if the temperature is kept within the range of the two-phase (a + ?) field. INTEREST in superplasticity has been stimulated by the desire to: 1) understand the origin of, and mechanisms responsible for, the large uniform elongations observed, and 2) exploit this property for commercial advantage in metal forming operations. Although the Zn-22 wt pct Al alloy presently being studied as a model material1-5 may find application in sheet forming and extrusion, the potential of super-plasticity should best be realized in large tonnage materials, such as steel and aluminum alloys. The degree of superplasticity in low-carbon and manganese-bearing steels has been evaluated. The results of elevated-temperature stress-strain rate and elongation tests on ultrafine grain size material are reported. Avery and Backofen6 and Hart7 have shown that geometrically stable flow leading to extensive uniform elongation in the tension test is associated with high values of the strain rate sensitivity, m, defined: Lozinsky had reported that titanium and zirconium experience permanent deformation if subjected to a constant load and cyclic heating through the temperature range of the phase transformation. Although strain rate sensitivities in excess of about 0.2 had not been reported previously for steel, permanent deformation had been observed11-13 in a wide variety of steels subjected to a constant load and cyclic heating through the temperature range of the a-? phase transformation. Thus by analogy, steel could be expected to exhibit high strain rate sensitivity but only in the a + ? condition. High strain rate sensitivity has been observed at 650°C (a + Fe3C), but not reported as such, by Bailey, Dickenson, and pearson14 in 1931 at a strain rate of about 10-9 per min. It then remained to determine whether high tensile elongations would be observed in a rate-controlled test at constant temperature and at what strain rate strain rate sensitivity values greater than 0.5 would be observed. Since previous experience8 had indicated the importance of fine grain size to realizing high m at reasonable strain rates, it was first necessary to produce an ultrafine grain size and then keep the grains from growing during the test. The results of this investigation show that fine grain size can be readily produced16 and maintained by restricting the temperature of testing to below the ? transus. Further, superplasticity (high m and large uniform elongation) is observed. However, the strain rate range is only marginally useful for commercial forming operations with the finest grain size produced. MATERIAL The material investigated initially was a 1.9 wt pct Mn, 0.42 wt pct C, hot-rolled bar previously used by Low and Turka1015 and available in the laboratory. The 0.500-in. round was cold-rolled to a 0.090-in. flat, annealed for 4 hr at 850°C in argon, air-cooled, and cold-finished to 0.050 in. Subsequently, four additional steels of the compositions given in Table I were investigated to explore the effects of manganese, carbon, and test temperature on the observed stress-strain rate behavior. These steels were melted under argon, cast to 0.75 by 2 by 5 in. slabs, hot-rolled at 850°C, surface-finished to 0.13 in., and cold-finished to 0.050 in. Sheet tensile specimens 0.200 in. x thickness with 1- or 2-in. gage length were cut parallel to the rolling direction. Table I also includes the nominal transformation temperatures for the AISI 1340 and the four experimental steels. EXPERIMENTAL PROCEDURE Production of Fine Grain Size. Ultrafine grain size (1 to 5 p) was considered essential for this studv. Grange16 has described two techniques for producing

Jan 1, 1969

By T. R. Ingraham

When aluminum sulfate was decomposed in an evacuated apparatus and the sample cooled, Q alumina was found. The thermodynamics of the decomposition reaction were resolved by measurements of the total pressure of SO3, SO2, and O2 generated over the sample at various temperatures. The results were correlated with other published data to calculate the rmges of thermodynamic stability of the various compounds involved. The thermal decomposition of aluminum sulfate was studied by Wijhler, Pluddeman, and Wöhler1 and by Warner and Ingraham.2 The results of both studies were critically reviewed by Kellogg,3 who observed that "each set of data shows considerable scatter and strong curvature on a plot of log pso3 vs 1/T".3 He agreed with Warner and Ingraham2 that both the discrepancy in the two sets of results and their curvature may arise from the indefinite properties of the particular form of A12O3 which is formed during the decomposition. While studying the thermal stability of other sulfate systems, we had noted the presence of nonequilibrium oxide properties in both the cobalt4 and manganese5 systems, but neither had shown any appreciable curvature on a logPSO, vs 1/T relationship, and the data from both systems agreed reasonably well with prior work. It therefore seemed reasonable to reexamine the technique which had been used in our earlier work on aluminum sulfate.2 The principal difference was that a tightly compacted pellet had been used for the earlier aluminum sulfate work, whereas a loose powder, contained in a platinum boat, was used for our work on other sulfate systems. In addition, a better technique had been developed for dehydrating the samples. From work done on the nickel system,6 we had become aware of the highly protective nature of some sulfate layers on their oxjdes, and hence of the necessity of providing a large surface area of P3e sample when equilibrium was to be attained in a reasonable time. That observation suggested that perhaps a steady state, rather than equilibrium, had been reached in the earlier work on aluminum sulfate. This paper reports a repetition of the experimental work with large, finely divided samples of anhydrous aluminum sulfate. APPARATUS AND PROCEDURE The apparatus used in the experimental work was described in earlier papers.2,7 The source material was Anachemia reagent-grade Al2(sO4)3 - 18H2O which was first partly dehydrated by heating at 400°C for 48 hr and then completely dehydrated by repeated baking of an aluminum sulfate-oleum slush to dryness at 450°C. ? Alas was prepared by decomposing some of the sulfate in a muffle furnace at 800° C overnight. Approximately equal amounts of the 7) alumina and aluminum sulfate were used in the experiments. The finely divided samples were handled under dry box conditions, and in addition some of the aluminum sulfate was decomposed in the apparatus while it was under vacuum, to ensure its complete dehydration prior to sealing the apparatus. The samples were heated to a series of constant temperatures on both increasing- and decreasing-tem-perature programs. Two to three days were required to obtain steady readings of the total decomposition pressure on an increasing-temperature program, and 5 to 6 days on a decreasing-temperature program. Three samples were examined on both programs. Within experimental error, the results for each sample and each program could not be distinguished.

Jan 1, 1969

By Carl F. Cline, Richard R. Vandervoort, Willis L. Barmore

THE objective of this investigation was to determine the high-temperature plastic deformation behavior of stoichiometric uranium mononitride as a function of stress and temperature. Interest in the properties of this material stems from its potential use in high-temperature nuclear reactor systems. The creep of other refractory compounds containing uranium (e.g., U02, UC) has been studied by various investigators.1"4 Fassler et al.4 have studied the creep of UN in vacuum from 1100° to 1350°C at stresses of 6000 and 8000 psi. In the present work, the creep of stoichiometric UN was investigated from 1500° to 1800°C at stresses from 2000 to 5000 psi in a partial pressure of 200 mm of nitrogen. The specimens were prepared by hot isostatic pressing of UN powder into cylinders of $ in. diam by about 1 in. high. After pressing, the specimens were heat-treated in nitrogen at 1900°C for 50 hr. The densities of individual specimens were determined by the water displacement method. All specimens were theoretically dense, based on a value of 14.32 g per cu cm.5 Principal metallic impurities in ppm by weight were: Ca, 50; Cu, 5; Fe, 30; Mg, 5; Ni, 10; and Si, 20. Oxygen content was 400 ± 50 pprn and carbon content was 100 i25 ppm. The nitrogen content was 5.56 ±0.05 wt pct. The average grain size for five specimens, as determined by the intercept method, was 0.14 i 0.01 mm. One specimen had a grain size of 2.0 mm. This large grain size is an anomaly, since all specimens had the same chemical and thermal histories. Specimens of 1/4 in. diam by 1/2 in. high were creep-tested in compression in a clam shell furnace heated by W-25 pct Re sheet elements. Temperature was measured to ilODC by an optical pyrometer which had been calibrated by a standard source. The distance between fiducial marks on the specimen was measured before placement into the furnace. The furnace chamber was evacuated to 10-5 Torr and back-filled to 200 mm N2. After heating rapidly to temperature, the load was applied and controlled to ±2 pct by an Instron testing machine. Upon initial loading, the specimen was deformed until a constant crosshead rate was obtained, then quenched to room temperature, remeasured, and replaced in the furnace. Upon subsequent reloading at temperature, the crosshead rate was constant for the selected condition indicating steady-state creep.

Jan 1, 1969

By O. A. Cheadle, F. E. Lane

ThE computer program for arbitrary crystal systems reported by Camp and Clum' has been modified to make it more convenient for hexagonal crystals. The program' uses the Miller indexes (hkl) which can be confusing for hexagonal crystals while the modified program uses the Miller-Bravais indexes with four axes; e.g., the angles between the (110) planes, Fig. 1, are 0 and 90 deg but in the (hkil) system the angles between the (1150) planes are 0 and 60 deg. If a Laue photograph is taken of a crystal oriented with the prismatic planes nearly parallel to the film then the spots on the stereo graphic projection will be from high-index planes. The probable positions of the low-index planes, e.g., (0001) plane, can only be obtained from the intersection of zones and this is not accurate to 1 or 2 deg. The number of planes considered by the program (card 1)' has to be limited to the ones of low index or the program time is excessive but a solution will not be obtained if one of the spots has an index that is not being considered. To overcome this problem the program1 was modified so that if no fit was obtained at *1 deg (card 3) of the tabulated angles then ±2 or ±3 deg was tried. If still no solution was obtained either due to one of the angles not being measured correctly to ±3 deg or because one of the spots was from a high-index plane, then the last spot was discounted and a fit tried for the remaining spots at i1 deg, and so forth. The minimum number of spots that the program will try to fit is five. If the limit on any individual index is 4 (card 1) and (h + k + l + 1) is six then twenty-three planes are considered and there are over 1000 interplanar angles. Many pairs of planes have very similar interplanar angles and with the errors previously mentioned the program will often produce several alternative solutions to a group of spots particularly at ±2 or ±3 deg. However without the program the alternative solutions would probably not have been found. If a large number of spots are used the number of possible fits is reduced. In the example shown in Fig. 2, if only spots which are on the film are used (case 1) the program gives six possible solutions, Table I. However if points 7 and 8 are also used (case 2) the program gives only one fit which also agrees with a standard projection of the crystal. In addition to time-saving the program ensures that a correct solution is obtained since it is unlikely that all the alternatives would have been gound manually; the first would probably be assumed to be the correct solution. The program has been used for zirconium crystals but is equally suitable for other hexagonal materials.

Jan 1, 1969

By D. Kunstelj, M. Stubicar, A. Tonejc, A. Bonefacic

A. Bonefafcic, D. Kunsfeli, M. Stubicar, and A. Tonejc The present communication is concerned with the variation of the texture in aluminum wires with die angle and temperature, at constant speed of extrusion. Experiments were carried out concurrently on refined samples, with a stated purity of 99.997 pct pure A1 and commercial samples of 99.5 pct Al. Ingots of refined aluminum samples were machined to 30-mm-diam by 150-mm-long billets. These billets were transformed to 5-mm-diam wires by drawing. The final form, suitable for examination, was obtained by extrusion through conical-face dies with a 1-mm hole diam and extrusion ratio 5:l in diam. The initial form of the commercial aluminum samples was drawn wire 5 mm in diam. These samples showed a poorly defined texture with (111) as a major and (001) as a minor component. A similar defined texture appeared in the refined aluminum samples after drawing to 5 mm diam. Conical-face dies with different angles (defined by the axis and the generating line of the cone) were used in our experiments. The values of the angles were 27, 35, 45, 57, 63, and 90 deg. The extrusion container was fitted with a heating element and controller permitting temperatures up to 600°C to be maintained within i5"C. Extrusion was performed at 250°, 300°, 350°, 400°, and 500°C at constant speed (approximately 1 mm per sec) and constant die reduction. The extrusion product was a wire 1 mm in diam and approximately 20 cm long. In order to remove the surface layer with the "conical" texture and to reduce the absorption by the X-ray examination of the samples, the extruded wire was etched to 0.22 mm in diam. Experiments were performed in the middle sections of the 20-cm-long wires. In addition to the die of l-mm hole diam, dies with a 1.5-, 0.7-, 0.6-, 0.5-, and 0.4-mm hole diam and 63-deg die angle were constructed. In our experiments we did not find in these ranges any important difference concerning the texture of the extruded wires and we continued our work solely on the 1.0-mm die. The diffracted X-rays (Cu K radiation) were recorded photographically. Diffracted intensities were measured on the (111) reflection with a microphotometer. The relative amounts of texture components were determined from the areas under the diffracted maxima. We found the texture of extruded aluminum wires to be strongly influenced not only by the temperature of extrusion and the purity of the sample but also by the form of the die. It is generally admitted that cold-drawn aluminum wires have mainly a (111) texture with a small amount of (001) component, Table I of Ref. 1. In our experiments with wires extruded in conditions represented by Fig. 1, in some cases a single (001) texture was obtained. If these wires were drawn repeatedly at room temperature, X-ray measurements revealed a duplex (001)-(111) fiber texture. Further drawings increased the (111) and decreased the (001) texture component. In Fig. 1 the percentage of material oriented with (001) parallel to the extrusion direction is represented as a function of the temperature and the die angle (a), for commercial and refined aluminum samples, respectively. From these diagrams we may draw the following conclusions. The slope of the die (a) influenced more strongly the texture at the lower rather than the higher temperatures. Again, a stronger influence was found in the case of the commercial in comparison with refined aluminum samples. In the case of the commercial aluminum samples the amount of material with (001) texture increases with increasing wire temperature in an approximately linear manner. This effect is less pronounced in the pure aluminum samples, with the exception of the die with a = 45 deg. In this case the (001) texture decreases with increasing temperature, as shown in Fig. 1. Component (001) is more pronounced in higher-purity aluminum samples. Our experiments led to the conclusion that both (001) and (111) components are essentially stable in extruded aluminum wires. As we obtained a single (001) texture starting with a sample of drawn wire in which the (001) component was very weak, our experiments revealed that the (001) component is not a remnant of the initial texture; this is in disagreement with the findings of Vandermeer and McHargue.1 We gratefully acknowledge discussions with Professor M. Paic. 1 R. A. Vandermeer and C. J. McHargue: Trans. 7MS-AME, 1964, vol. 230, p. 667.

Jan 1, 1969

By T. O. Massalski, J. D. Ayers

A massive transformation, 0 —am, takes place in a number of copper-based systems where the ß phase field at high temperatures extends to compositions that are slightly less solute-rich than the limits of the a phase field that exists at lower temperatures. Consequently a solid-state transformation becomes possible that does not involve a change of composition. Within this narrow range of composition the massive am phase can be usually produced in two ways: by a fast quench from the ß phase through the a phase field, or by pulse heating into the a phase field of an undecomposed ß phase retained at room temperature by a prior quench. In the Cu-Ga system the occurrence of a massive am phase has been also observed in alloys whose composition falls outside the equilibrium a phase field1 but not in the Cu-Zn system.2 We have recently observed the occurrence of the ß — am transformation also in two silver-based systems, Ag-Zn and Ag-Cd. The a and 0 phase fields in these systems again slightly "overlap" in a narrow composition range. In the Ag-Zn system this range falls between 36.7 and 40.2 at. pct Zn, and in the Ag-Cd system between approximately 41 and 42.5 at. pct Cd. Alloys were prepared from high-purity materials and cast in quartz tubes under inert atmosphere. No significant change of composition occurred during casting. After homogenizing in the 0 phase field, small pieces of each alloy were reheated at the homogenizing temperatures for a few minutes and quenched into various media. There were examined metallographic-ally after removal of surface layers that may have suffered from contamination or from the loss of the solute element. In the Ag-Zn system extensive areas of the am phase (identified by selective etching, observation of the slip trace variants, and occurrence of twinning) were observed in a comparatively low-zinc alloy (37.8 at. pct Zn) for all quenching media employed: iced

Jan 1, 1969

By M. J. Pool, P. J. Spencer, J. R. Guadagno

THE present work was carried out as part of a general program to study the magnitude and concentration dependence of exothermic heats of solution of various metals in liquid tin. Thermodynamic data for the Te-Sn system are very limited, particularly for dilute alloys. Indeed, apart from the prior heat of solution determinations of Pool,1 the only other published values are those of McAteer and seltz2 who carried out electromotive force measurements on solid alloys of compositions from 75 to 95 at. pct Te at temperatures between 543° and 668° K, of Colin and Dro-wart3 who made mass-spectrometric studies of the vapor in equilibrium with solid SnTe, and of Robinson and Bever4 who determined the heat of formation of SnTe by solution calorimetry. The present work thus provides further thermodynamic information for this system, specifically in a temperature range where the solubility of tellurium is very limited. The liquid metal solution calorimeter used in this investigation has been described previously.' No further discussion of its design or operation will therefore be given here. For each series of measurements a tin bath consisting of approximately 70 g of 99.99 pct pure Sn was carefully weighed out and inserted in the calorimeter which was maintained at the desired temperature to within ± 1/4°c. Tellurium, of 99.999 pct purity, was supplied by Atomergic Chemetals Co., a division of Gallard-Schlesinger Chemical Manufacturing Corp. Approximately 0.0006 to 0.001 g-atom specimens of tellurium were used for each experimental run and these were added to the calorimeter from a temperature of 273" K. Heat of solution values were calculated by analysis of a strip-chart recorder plot of the heat effect accompanying the solution of each sample in the tin bath. The heat capacity of the latter was determined at regular intervals during a series of tellurium drops by using pure tin or tungsten calibration samples, the heat contents of which were obtained from the standard compilation of Hultgren et al5 The composition of the bath was calculated after each drop from a knowledge of the weights of tin and tellurium added. Values of the heat of solution of tellurium at 725" and 775° K are listed in Table I together with the corresponding tellurium contents of the alloys. The data are also plotted as a function of tellurium concentration in Fig. 1, which includes the equivalent data obtained by pool' at 750° K. It can be seen that the heat of solution remains

Jan 1, 1969