By A. Raman, P. P. Singh

The constitution of the La-Rh system was studied by powder X-ray diffraction, metallopaphic, and differential thermal analysis techniques and an equilibrium diagram is presented. Eleven intermediate phases occur in the system and the crystal structural data for nine of them were determined. La3Rh crystallizes in an orthorhombic structure of undetermined type, whose unit cell is obtained by doubling the 'a; and 'c,,' edges of an FesC type unit cell. The other intermediate phases of the system are LarRh-3( undetermined structures also occur in the system. LaRh, undergoes a polymorphic phase transformation at 1240°C. LaRh3 and La2Rh7 also exhibit polymorphisnz. The phases Laah and LazRh7 melt congruently. The latter undergoes a eutectoid transformation into LaRh, and Rh at 1205°C. Laah3 is formed by a peritectoid reaction between Laah and La,Rh,,. The other Phases result from peritectic reactions between the liquid and the adjacent rhodium-rich phases. The intermediate Phases of the La-Rh system are compared with those of the La-Co and La-Ni systems. DURING the course of a detailed investigation to study the occurrence of CrB, FeB, A1B2, and related structures in the rare earth alloys it was found that much information is lacking for the rare earth noble metal systems. Although the structures of several rare earth alloys containing the noble metals at the AB and AB2 stoichiometries have been reported, the occurrence of related structures at other stoichiometries has not been studied. We have initiated a project to study the crystal structural features of selected rare earth-rhodium alloys and to map the equilibrium diagrams of representative systems with conventional methods. The results of our investigation in the La-Rh system are presented in this paper. Two phases were known in the La-Rh system. LaRh has the CrB-type structure.' LaRhz is a MgCu2-type Laves phase.z EXPERIMENTAL PROCEDURE Alloys weighing less than 1 g were prepared from commercially pure lanthanum (99.9 pct +), supplied by Lunex Company, Pleasant Valley, Iowa, and rhodium (99.92 pct +), supplied by Engelhardt Industries, Newark, N.J., in a conventional arc melting furnace under argon atmosphere. The buttons were turned upside down and remelted three times to insure homogeneity in the samples. Since negligible loss of material was encountered during melting, a chemical analysis of the alloy buttons was not undertaken. Powder specimens for X-ray diffraction studies in the as cast state were then prepared. The buttons were wrapped in thin molybdenum foils and homogenized by heating in vacuum at suitable high temperatures for more than 1 week. They were then broken into three or four pieces for annealing experiments. The pieces were wrapped in molybdenum foils and annealed at various temperatures in evacuated quartz capsules. The annealing was carried out for 2 hr at or above 1200°C, 1 day at temperatures close to llOO°C, 2 days at 1000°C, and for 1 week at temperatures below 1000°C. After annealing the alloy pieces were again broken and powder specimens for X-ray diffraction were prepared. The powders of the lanthanum rich alloys with more than 80 at. pct La were prepared by filing. The filings were sealed in molybdenum tubings and stress-relieved at 600°C in vacuum. It was not deemed necessary to stress-relieve the powders of the other alloys, since the alloys were very brittle and were ground easily. POWDER X-RAY DIFFRACTION X-ray diffraction photographs of powders (-325 mesh size) of the alloys in the as cast and annealed states were prepared in a Guinier-de Wolff focussing camera with copper K, X radiations. These patterns were studied to identify the stoichiometries and the crystal structures of the intermediate phases. The lattice parameters of the phases were calculated after minimizing the differences between the observed sin2 6 values, calculated from the diffraction angles 8, and the sin2 8 values, calculated using approximate lattice constants obtained from a few lines. These differences were minimized manually to less than 0.0005. The latLice constants are judged to be accurate to *0.005A for values less thp about 10A and to k0.01~ for values greater than 10A. The relative intensities of the lines were calculated using a computer program written by Jeitschko and Parthk.~ No attempt was made to refine the atomic positional parameters in the phases. METALLOGRAPHY The phase equilibria in the investigated alloys in the as cast and annealed states were also studied by metallographic examination. The polished specimen surfaces were etched with 10 pct picric acid in alcohol (alloys up to 25 pct Rh), concentrated picric acid (from 25 to 37.5 pct Rh), 2 pct nital (40 to 50 pct Rh), 10 pct nital (from 50 to 66.7 pct Rh) and with concentrated 48 pct HF for the other rhodium-rich alloys. Selected microstruture~ were then photographed using a Po-laroid Land camera. THERMAL ANALYSIS Differential thermal analysis of the alloys was carried out in DTA-668 Stone differential thermal ana-

Jan 1, 1970

By J. R. Cahoon, H. W. Paxton

The mechanical properties of unidirectionally solidified A1(rich)-Mg and A1(rich)-Cu castings containing up to 15 wt pct solute have been determined with re -spect to the volume fraction of interdendritic eutectic. Pioperties were determined in the directions pumllel and Perpendicular to that of solidification; the volume fraction of eutectic was varied between the "as-cast" and equilibrizcm amounts by approperiate heat treatment following solidification. The principles of fiber strengthened composites and dispersion strengthened materials are adapted to explain the mechanical properties of these castings. It is generally accepted that castings often have inferior mechanical properties when con~pared to wrought products. However, there is little quantitative data available concerning the factors which make apparently sound castings weak and/or brittle. The relative ease and inexpensiveness of the casting process have always been attractive and, therefore, an understanding of the factors which contribute to the mechanical properties of castings would seem desirable. Such an understanding may lead to an improvement in the mechanical properties to an extent where castings would become competitive in applications where presently only wrought products are considered to have the requisite properties. Such an understanding could also improve the reliability of present cast products. Much of the recent research on castings has centered about determining the extent of segregation in cast alloys. Macrosegregation, particularly inverse segregation, has been studied in some detail 1-8 and a considerable understanding of microsegregation has been obtained.9'10 The effect of solidification rate on dendrite spacing and on the amount of interdendritic eutectic in binary alloys has been established, particularly for Al(rich)-Cu alloys.""0 However, the extension of these ideas to relate the amount of interdendritic eutectic, concentration gradients, micro-segregation, dendrite spacings, and so forth, to the rnechanical properties has been limited. Dean and spear" have related the mechanical properties of an Al-Si-Mg alloy, A356-T62, to the dendrite spacing and have shown that the mechanical properties improve with decreasing dendrite spacing. Passmore et al.12 have shown that annealing at high temperature improves the mechanical properties of Al(rich)-Cu al- loys and Archer and Kempf 13 have shown that an Al-1 pct Mg-1.75 pct Si alloy behaves in a similar manner. Ahearn and Quigley 14 have shown that high temperature homogenization also enhances the mechanical properties of an SAE 4330 steel. However, in the above investigations, no underlying reasons were suggested for the improvement in mechanical properties. The purpose of the present investigation is to relate the mechanical properties of castings to some of the solichfication variables and to derive some equations by which calculations of the mechanical properties may be attempted. In particular, the effect of the amount of interdendritic eutectic and the effect of stress direction with respect to that of solidification on the mechanical properties will be considered. The Al(rich)-Mg and Al(rich)-Cu binary alloy systems were chosen for study. The A1-Mg system was chosen because its constitutional relationships are such that large volunles of eutectic (up to 24 vol pct) may be obtained in the as-cast condition and then be completely dissolved by subsequent heat treatment at about 440°C. This allows a comprehensive study relating the mechanical properties of castings to the amount of interdendritic eutectic. Also the Al(rich)-Mg eutectic is almost a single phase 15 which should make the experimental results more amenable to theoretical interpretation and calculation. The A1-Cu system was chosen for study because of the large amount of related information available concerning segregation, dendrite spacing, and so forth. Unidirectionally solidified castings were used throughout the investigation so that the effect of solidification direction with respect to the direction of applied stress could be determined. THEORETICAL It is well known that upon solidification of binary alloy castings, the nonequilibrium amount of eutectic which forms is given by 10 where fe o is the weight fraction of eutectic, Cs is the solid solubility of solute at the eutectic temperature, k is the equilibrium partition coefficient, and C, is the average composition of the alloy. In the development of Eq. [I], it is assumed that the effects of inverse segregation and diffusion in the solid are negligible, and that no porosity is present. If the casting is homogenized at a high temperature for a long period of time, some (or all) of the eutectic is dissolved and the amount of eutectic for this "equilibrium" condition may be calculated directly from the constitutional diagram. By appropriate intermediate annealing, the

Jan 1, 1970

By A. W. D. Hills, M. R. Moore

An apparatus has been developed in which metals can bc solidified under closely controlled unidirectional heat flow conditions. The metals are cooled by a multiple-air jet system, designed so that the heat transfer coefficient is uniformly distributed over the cooled surface. They are contained in a special furnace system of low thermal mass which enables unidirectional heat flow conditions to be rigorously maintained for certain specific cooling rates. This apparatus has been used to study the solidijication of pure lead and pure tin at zero superheat, solid metal thicknesses being determined by thermal analysis, and by dipstick readings. Detailed thermal balances have been drawn up on the experiments in order to determzne the cooling conditions that most rigorously correspond to unidirectional heat flow. Solid metal thicknesses, measured experimentally for these conditions, have beetz shown to agree closely with the theoretical wedictzons of different integml-profile methods. lt is concluded that any errors inherent in the integval-profile method are no greater than the errors inherent in experimental investigations of solidification. A knowledge of the influence of heat transfer rates on the solidification of metals is essential to the understanding and control of industrial casting processes. Since very few formal methods are available for solving the heat conduction equation under solidification conditions several authors have developed approximate techniques for doing so. One of the most promising is the integral-profile technique that has been used by Goodman,1 Hills,2,3 Tien4 and Hills and ~oore' to predict solidification rates under certain specific heat transfer coniditions. In the first of this present series of papers6 Hills has further generalized the method and developed a universal integral-profile technique that can be used to predict solidification rates under a wide variety of unidirectional heat flow conditions. Since the method is approximate it is necessary to investigate the accuracy with which it predicts actual solidification rates. A review of the literature7 shows that solidification rates have seldom been measured under accurately known heat transfer conditions and it was therefore decided to develop experimental techniques that would enable this to be done. Results obtained would then be available as a check on the approximate solutions already developed, and in the development of further solutions that would be applicable under more complicated conditions. The initial work in this experimental program which is described here, is concerned with the solidification of pure metals at zero superheat under unidirectional heat flow conditions. Subsequent experiments have been concerned with the solidification of pure metals at appreciable superheats, under varying unidirectional heat flow conditions and under two dimensional heat flow conditions. In a series of experiments recently initiated, the solidification of binary alloys is also being investigated. The results of these subsequent experiments, together with relevant theory, will be described in later papers. The solidifying metal has been cooled in all the experiments, by a multiple air jet system designed so that the heat transfer coefficient to the cooled surface is constant and is uniformly distributed over the surface. This type of system has been chosen since only one parameter is needed to specify the heat transfer conditions and since these conditions are analogous to those met in certain continuous casting processes.' Air cooling was chosen in preference to water cooling, however, since it offers a wider range of heat transfer conditions, and since it can be investigated by analogous mass transfer techniques. The first part of this paper discusses the existing integral-profile solutions that correspond to the heat transfer conditions used in the experiments, and describes the development and use of the experimental apparatus. In subsequent sections the heat transfer and solidification results are presented, and the various theoretical predictions are compared with them, and with one another.

Jan 1, 1970

By E. J. Rapperport, J. P. Pemsler

The thermodynamic activities of zinc in six solid solution Cu-Zn alloys ranging from 5 to 35 at. pct Zn were determined experimentally in the temperature range 400° to 600°C. This low temperature investigation was canducted in order to evaluate techniques developed to utilize the inherently high sensitivity of atomic absorption flocesses in the measurement of thermodynamic activities. Analytical expressions ,for the activity and actizlity coeflcient are given for the six alloys in the temperature ranges investigated. RELATIVELY few experimental methods are available for investigation of thermodynamic activities of alloys, especially in the solid state. The techniques most frequently used have been the electrochemical potential and the effusion methods, both of which have severe limitations in many instances. It is therefore desirable to expand the ability to perform such measurements in order to obtain new information as well as to provide an additional independent verification capability. In this work, we present a significant improvement in the spectrophotometric method for sensing small vapor pressures in static absorption cells. Similar techniques have been used previously;1"5 however, applications had been limited to relatively high pressures, often greater than 1 torr. Prior investigators have, for the most part, used broad spectral sources such as xenon or mercury lamps, and high intensity arcs. Hollow cathode sources were first suggested in 1956 6 and were used soon afterwards.4'5 These sources offer significant improvements in sensitivity and freedom from interfering spectral lines.'-' EXPERIMENTAL High purity zinc was obtained from Cominco Products, Inc., and copper from American Smelting and Refining Co. Both elements were of 99.999 pct purity. Copper-zinc alloys were vacuum melted in a high fired carbon crucible with each alloy pulled from the melt as a 4 -in. diam bar. The bars were swaged to -1/4 in. rods and vacuum annealed for 160 hr at 800° + 1°C. Samples for gross chemical analysis were taken at intervals along the length of the rods to ascertain the axial zinc gradient. Electron microprobe analysis of homogenized specimens indicated that the alloys had uniform compositions over their cross sections on a macro (200 p) and micro (1 u) scale to better than *1 pct (20) of the gross composition. This tolerance was determined by counting statistics, rather than assured composition fluctuations. All SiO 2 windows were high-ultraviolet-transmission grade to minimize intensity losses. Silica absorption cells were scrupulously cleaned consecutively in organic solvents, dilute HF, and distilled water before use. The empty cells were then flamed while under a dynamic vacuum, cooled, and removed to an argon-filled glove bag. Alloy pieces were cut and filed in the glove bag to produce fresh surfaces, and then loaded into the cells. The loaded cells were temporarily sealed, removed from the glove bag, reevacuated to 10-5 torr or better, and permanently sealed. The instrument used is schematically shown in Fig. 1. The spectral emission from a commercially made hollow cathode lamp (A) of a selected element is focused through an absorption cell (B) inside a well-controlled furnace (C). The intensity of the transmitted beam is measured using the spectrometer* (D) 'Techtron model AA4 atomic absorption spectrometer. which contains a grating (E) that disperses the light prior to impingement on the photomultiplier (F). The monochromator grating is adjusted so that only the wavelength of interest is measured. The power supply delivered an interrupted voltage to the lamp, causing a chopped radiation output to be transmitted. The detector read only the intermittent component of radiation incident upon it, so that all continuous noise signals (furnace radiation, and so forth) were eliminated. Three recording thermocouples contained in the muffle furnace were positioned along the length of the absorption cell: one at each end and one at the center. An effort was made to keep the ends of the cell several degrees hotter than the center to avoid window condensate. Appropriate thermal corrections were then necessary to relate cell pressure to radiation attenuation. Water-cooled heat shields, as shown in Fig. 1, were found to aid signal stability by protecting the hollow cathode and the photomultiplier from furnace radiation. The furnace had a 2-in. diam muffle, Kan-thal wound, with SiO 2 windows at its ends to minimize convective effects. The hollow cathode radiation was masked and focused to form a conic beam that was a maximum of { in. diam within the furnace. Thus, the 1.5 in. diam absorption cell easily contained the entire beam. The furnace was mounted on ball-bearing slides with positive positioning detents. This arrangement allowed the removal of the entire furnace assembly from the radiation path, position [I], Fig. 1, so that frequent sampling of the unattenuated beam intensity could be obtained. In all cases the beam intensity was kept constant to 0.1 pct as judged by readings taken immediately before and immediately after data collection. Only data for absorptions of less than 80 pct were utilized, as systematic deviations from linearity were found for greater absorptions.

Jan 1, 1970

By T. T. Field, M. Gell

MUCH has been learned about plastic deformation behavior in crystals through the use of dislocation and slip band etchants. Slip in nickel and nickel-base alloys has previously been revealed by various etching techniques.l-5 The techniques for nickel-base super-alloys4,5 were successful only in the Udimet 700 composition in specific heat-treated conditions. The objective of this work was to develop a more generally applicable slip-band etching procedure. The nominal compositions of the alloys used in this study are listed in Table I. The low carbon Mar-M2OO alloy referred to in the text is the same as listed in Table I with the exception that the carbon content is less than 100 ppm. Mar-M200 and Udimet 700 were solutionized at 2250" and 2150°F, respectively. The aging treatment for both cast alloys was 32 hr at 1600°F and for wrought Udimet 700 was 4 hr at 1975"F, 24 hr at 1550°F, and 16 hr at 1400°F. The new slip-band etching technique consists of a chemical etch followed by a short electropolish, Table 11. Fig. l(a) shows the best result obtained on an internal section of a plastically deformed single crystal of Mar-M2OO when using a conventional slip-band etching procedure which consists of electropolishing followed by etching. Ghostlike traces corresponding to planar slip bands are observed, but the contrast between the bands and the background is weak. Fig. l(b) shows the same field using the new slip-band etching technique. After the etching step of this technique, the same ghostlike traces of Fig. l(a) are observed, but the subsequent electropolishing accentuates the slip bands and the subgrain boundaries while the rest of the matrix is being polished. Longer electropolishing obliterates the slip bands. The new slip-band etching technique makes use of the etchants and electrolytes that are normally used for a given material. Because of this, it should be possible to slip-band etch other nickel-base superal-loys by using existing etchants and electrolytes for a material and following the procedures outlined in the "Comments" section of Table 11. All the illustrative examples given below show internal plastic deformation in single crystals of regular and low carbon Mar-M200 in the solutionized and

Jan 1, 1970

By Takeyasu Ito, Mayumi Someno, Kazuhiro Goto

SINCE the pioneering work by Kiukkola and Wagner,1 many experiments have been reported on solid electrochemistry at elevated temperatures. However, the studies have been confined to experiments under isothermal conditions. One may conceive many situations under nonisothermal conditions. With two different temperatures T1, and T2 at the two electrodes, the electromotive force, E of a Galvanic cell will be expressed by the following equation under a steady state heat transfer in solid electrolytes of zirconia-lime and thoria-lime. E = ^ $ l&-dGO2+a(T2-Ti) [1] where tO2- is the transference number of oxygen ions in the electrolyte, Go, is the chemical potential of oxygen, and a is the coefficient of the thermoelec-tromotive force due to the temperature difference. The objective of the present study was to evaluate the coefficient of the thermoelectromotive force for zirconia-lime and thoria-lime under isobaric condition. The physical meaning of this coefficient is out of the scope of the present communication. The experimental cell assembly is schematically shown in Fig. 1. The zirconia-lime electrolyte tube and thoria-lime electrolyte tube were 8.0 mm OD and 5.0 ID, from commercial sources with chemical analyses of 94.8 wt pct ZrO2, 3.85 pct CaO, 0.83 pct SiO2, 0.25 pct TiO2, and 0.05 pct Fe2O3; and 95.0 pct ThO2, 4.0 pct CaO and rare earth metal oxides, respectively. The specific gravity was 5.5 g per cu cm for zirconia-lime and 9.8 g per cu cm for thoria-lime. Original powder size before shaping and sintering the tube was several microns for both electrolytes. The distance separating the two electrodes was 4.0 or 5.0 cm. Platinum wire of 0.5 mm diam was used for the electrodes. The temperature gradient was controlled by heating one electrode with a small heating coil of nichrome wire. The temperatures at the two electrodes were measured with two calibrated Pt-13 pct Rh:Pt thermocouples, directly contacting the two platinum electrodes. The atmosphere was either air or pure oxygen. The partial pressure of oxygen in air was considered equal at the vicinities of the two electrodes, with negligibly small thermal segregation in the gas phase. The difference of the chemical potential of oxygen was controlled only by the temperature difference at the two electrodes and not by the oxygen pressure difference. The temperature ranges were 600" to 1200°C for zirconia-lime and 850" to 1200°C for thoria-lime electrolytes. Fig. 2 shows the relation of the measured electromotive force and the difference of the oxygen chemical potential at the two electrodes for zirconia-lime and thoria-lime electrolytes. The electromotive forces in the figure were measured by a *0.05 mv potentiometer. The chemical potential difference was calculated by the following equations.'

Jan 1, 1970

By R. R. Hart, B. C. Wonsiewicz, G. Y. Chin

In recent years there has been increased miniaturization of electromechanical devices to keep pace with current trends toward smaller electronic components. A major problem facing the designer, however, is the higher stresses encountered by the material as a result of shorter springs. Hence an improvement in the elastic limit, as approximated by the 0.01 pct offset yield strength, would be highly desirable. An increase of 25 pct in the yield strength, for example, will permit a 20 pct reduction in both the length and thickness of a cantilever-type spring while maintaining the same compliance. One technique of improving the yield strength that has received little commercial attention is crystal-lographic texture strengthening.1,2 Texture strengthening is expected to be most beneficial in materials of hcp structure, but considerable gain can also be expected in cubic materials. A wire with a (111) fiber texture, for example, is expected to be 20 pct stronger than randomly oriented material, and 50 pct stronger than wire with a (100) fiber texture.293 For sheet specimens with a {110}(112) texture, characteristic of many heavily rolled fcc alloys, the (111) transverse direction is expected to be the maximum yield strength direction, about 20 pct higher than that in the (112) rolling direction.' In addition, the (111) direction is the direction of maximum modulus of elasticity for most cubic alloys. A large value of the elastic modulus could be desirable in designs where stiffer springs are required. To test the above idea, a 0.090 in. (-2.3 mm) thick commercial grade A (5 pct Sn) phosphor bronze sheet, a widely-used material for relay springs, was rolled from the spring-tempered condition (60.5 pct reduction) to various additional reductions up to a total reduction of 95 pct. Subsequently, additional material was obtained with a total thickness reduction of 97.3 pct Standard tensile specimens were prepared from the sheet material with the tensile axis parallel to and at 90 deg to the rolling direction. Tests were run on an Instron testing machine at a strain rate of about 0.050 min-l. Textures were determined by the use of the reflection pole-figure technique. Data were obtained using nickel-filtered CuKa radiation and with the aid of a Siemens pole figure goniometer. The X-ray pole figure studies show an incrzasing development of the texture toward the {110}(112) ideal

Jan 1, 1970

By A. F. Crawley

THIS communication reports measurements of the densities of dilute liquid alloys of 0.1 and 0.5 pct Ag in Sn over temperature ranges of 170" and 210°C, respectively, above the melting point of pure tin (232°C). The work was earried out to provide accurate density data for some liquid diffusion studies performed by Davis.1 Densities were measured using a pycnometric technique established in this laboratory. Earlier papers2, 4 attest to the accuracy of ±0.05 pct and the reliability of the method. Tin, 99.999 pct pure, and silver 99.99 pct pure, were melted in a graphite crucible in a vacuum furnace and held at temperature for 10 hr to ensure homogenization. Ingots suitable for machining

Jan 1, 1970

By Pradeep K. Rohatgi, Clyde M. Adams

Structures produced upon solidification of the eu-tectic composition (33 wt pct Cu) aluminum copper alloy have been examined as a function of freezing rate dfs /d? , the rate of change of fraction solid (fs) with time (8). Slow (dfs/d? = 0.0016 sec-1), intermediate (dfs/d? = 0.02 sec-1) and rapid (dfs/d? = 0.4 to 7.30 sec-1) freezing rates were used. The lamellar Al-Cual2 eutectic is arranged in the form of rod-shaped colonies at rapid freezing rates. The colonies are aligned parallel to the direction of heat flow, whereas the lamellae within the colonies are aligned at various angles, as high as 90 deg, to the direction of heat flow. The colony spacing (C) is proportional to the square root of inverse freezihg rate. The relationship is C = 15.5(dfs/d?)-1/2 where C is in µ and 8 is in sec. The ratio of colony spacing to lamellar spacing is greater than 20.0 and increases with a decrease in the freezing rate. A duplex dendritic structure is produced at intermediate freezing rates. A fine lamellar eutectic is arranged within the dendrites (exhibiting side branches at an angle close to 60 deg from the main stem) and a coarse irregular eutectic appears in the interdendritic regions. The duplex eutectic structure is also produced at slow freezing rates. However, at slow freezing rates there is a Platelat of CuAl2, along the center of the main stem of each dendrite and the other lamellae are arranged perpendicular to the central platelet. THE eutectic between CuA12 and a! aluminum has been reported to freeze in a lamellar form by several workers.'-3 chadwick4 has measured the interlamel-lar spacing as a function of growth rate. Kraft and Albright2 have reported on irregularities in the lamellar structures, and have proposed growth models which account for the formation of faults during solidification. In certain instances the lamellar eutectic has been found to exist in colonies. The colony formation315 has been attributed to the breakdown of a planar liquid-solid interface due to rejection of impurities. The aim of the present work is to study the structures produced from the eutectic aluminum-copper alloy under relatively fast solidification rates, such as encountered in casting and welding operations. The solid-liquid interface presumably remains planar under conditions of slow unidirectional freezing which produce lamellae aligned parallel to the direction of heat flow. The local growth velocities are the same over the entire interface and are equal to the rate of growth of the all-solid region. The spacing between the eutectic lamellae is inversely proportional to the square root of the growth rate of the all-solid region. Under the freezing conditions used in the present study, the solid-liquid interface is cellular or dendritic and the local growth velocities are different in the different regions of the interface. The relationship between the growth rate of the all solid region and the local growth velocities varies with the location and the shape of the interface. The growth rate of the all-solid region is, therefore, an inadequate parameter to describe the eutectic micro-structures which depend upon the local growth velocities. For this reason the structures have been examined as a function of freezing rate, dfs/d?, where fs is the fraction solidified at time 0. The freezing rate was varied by a factor of 4000. The relationship between the freezing rate, dfs/d?, and the growth velocit of the all solid region depends upon the specimen geometry and the shape of the interface. EXPERIMENTAL PROCEDURES The A1-33 pct Cu alloy used throughout this study was made in an induction furnace, using electrolytic copper and aluminum of commercial purity (99.7 pct), the primary impurities being silicon (0.12 pct), iron (0.14 pct), and zinc (0.02 pct). Three ranges of freezing rates were investigated: 1) A spectrum of rapid freezing rates (ranging from 0.40 to 7.30 sec-1) was obtained in arc deposits made on 2-in. thick cast plates of the eutectic alloy. The arc was operated at constant power and was made to travel at constant velocity on the surface of the plate that was in contact with the chill surface during solidification. The pool of liquid metal formed under the moving tungsten arc solidified rapidly by heat extraction through the unmelted plate. Conditions of unidirectional heat flow were achieved near the fusion zone interface, especially in the center of the arc deposits. The great advantage of the arc technique is that rapid cooling and freezing rates can be varied in a qualitative way. The correlation between the arc parameters and the solidification rate is given by the following relationship:6-8

Jan 1, 1970

By Ben-Zion Weiss, Melvin R. Meyerson

Chromium diffusion coatings on commercial Armco iron lead to carbide precipitation at the grain boundaries in and below the coatings. High compressive stresses are introduced into the coating and, as a result, tensile stresses are introduced into the base material below the coating. In coated samples, fatigue cracks form at the grain boundaries below the coating after only a limited portion of the total lifetime (5 to 10 pct). Residual tensile stresses and a stress concentration caused by precipitated carbides seems to be responsible for early crack nucleation. Stage I of Propagation may be divided into two substages: I-a in which the crack Propagates along grain boundaries, and I-b in which the crack propagates along slip boundaries according to a shear mode. In uncoated samples, the cracks form at slip bands after 40 to 50 pct of the total lifetime. In coated samples the Propagation process takes longer than in uncoated samples because of the moderate rate of crack extension until the crack breaks through the coating. The chromium-diffusion coating causes little if any increase in fatigue life. CHROMIUM diffusion is one of the most popular processes used to apply coatings to iron alloys. This popularity stems from the fact that the diffusion treatment is comparatively easy to carry out, and it improves certain surface properties such as corrosion and wear resistance as well as some other properties. Very little effort has been devoted to the investigation of the effect of chromium-diffusion coatings on mechanical properties and particularly on fatigue properties. Since the chromium coating usually represents a small fraction of the total volume of the base material it is generally assumed that the macro properties are dependent principally on the base material rather than the coating. Insofar as fatigue is concerned, there are indications that the fatigue life of the chromium coating is not less than that of the basic material and the fatigue properties are generally not reduced by it.' But chromium diffusion causes drastic structural and chemical changes in the region of the material surface2-4 which introduce additional residual stresses. Such changes must affect fatigue crack nucleation and may sometimes affect the initial stages of propagation. Furthermore, it is conceivable that the secondary stages of the crack propagation could be influenced by some irreversible structural changes in the core of the material, which stem from the long-time heat treatment at high temperatures required to apply the coating. This paper analyses the structural and compositional changes produced in commercial Armco iron by a chromium-diffusion coating and the effect of the coating on fatigue crack initiation and propagation. EXPERIMENTAL PROCEDURES The investigations were carried out with commercial Armco iron. The chemical composition of the iron, the number of specimens tested, the grain size produced during chromizing and heat treating, and the thickness and microhardness of the chromized layers are shown in Table I. Samples were chromized by a gas diffusion process. The temperature and time of the diffusion coating process were chosen according to a previous grain growth study. It had been found that at a temperature of 970°C and a holding time of between 3 and 9 hr there are practically no changes in grain size. To describe the grain size more accurately the ASTM method5 was supplemented by a statistical analysis of the mean volume diameter as outlined by Fullman6 and The The mean volume diameter was deter- mined from D = p/2m where D is the mean volume diameter, and m is the mean reciprocal value of grain diameters as seen on the micrograph. The shape and the size of the asymmetrical sample, see Fig. 1, were chosen so as to facilitate the study of fatigue crack initiation. Before coating, the samples were machined and the surface of the groove was polished. After chromizing, the two side surfaces were machined and polished so as to retain the coating only on the top surface of the groove. Residual stress in the chromized layer was measured on the top of the grooved section of the specimen after the diffusion process. The inclined incident X-ray beam procedure was used.9'10 The computations were performed with the initial assumption of a zero surface normal stress component. An electron microprobe analyzer was used to obtain the relative amounts of chromium and iron con-

Jan 1, 1970

By B. C. Allen

Grain boundary grooving has been studied in chromium, molybdenum, and tungsten under a variety of conditions using high vacuum techniques and tantalum -gettered argon. The average surface free energy of solid chromium, and the chromium-liquid silver interface free energy were respectively found to be 2200 ± 250 and 500 i 130 ergs per sq cm from groove formation kinetics and estimates of pertinent volume difffusion coefficients. The results for chromium were unffected by variations in interstitial content ranging from 0.003 to 0.09 pct C, or 0.003 to 0.03 pct O. Surface diffusion is the primary mechanism of groove formation in chromium under 1 atm argon at 1200" to 140O°C, and is essentially unaffected by 0.003 to 0.09 pct C, 0.003 to 0.03 pct O , metastable nitrogen contents up to -0.01 pct, and up to 2 torr Ag vapor. At higher temperatures, the major mechanism is volume diffusion in argon or evaporation-condensation in stutic vacuum. Surface diffusion occurs in molybdenum at 0.5 to 0.96 and in tungsten at 0.5 to 0.9 of the absolute melting tempera -ture by a single mechanism, possibly by the migration of single adatoms or vacancies. Results were slightly affected by up to 23 tory Sn vapor, and in molybdenum were essentially unaffected by 0.5 Ti or carbon in the range 0.002 to 0.02 pct. Volume difffusion through the liquid is the mechanism of groove formation in chromium-liquid silver at 1200" to 1400°C and in molybdenum-, Mo-0.5Ti-, and tungsten-liquid tin at 1200" to 2000°C. The solid-liquid interface free energies involved were estimated from grooving kanetics. WHEN a grain boundary intersects a solid surface, a groove tends to form along the line of intersection at temperatures above about half the absolute melting point (0.5 TM). The groove progressively grows by preferential atomic migration either by diffusion or evaporation. Establishment of a groove angle occurs in accordance with the grain boundary and surface free energies involved. The motivation for groove formation is a reduction in the total surface free energy of the system. This study is a continuation of previous work on thermal grooving of chromium, molybdenum, and tungsten.&apos; The temperature ranges were extended, and the effect of metallic and interstitial impurities was evaluated. The results were such that certain interface free energies and surface self-diffusion coefficients were deduced from the grooving kinetics. EXPERIMENTAL WORK Materials and Preparation. As indicated in Table I, the 0.05-0.08-cm-thick chromium, molybdenum, and tungsten sheet used was nominally 99.99 pct after recrystallization. Two lots of molybdenum with about the same analysis, Mo-0.5Ti,* and tungsten were ob- *Alloy compsitions are expressed in weight percent . tained commercially. Extruded chromium rod,&apos; prepared from iodide process crystals, was warm rolled to sheet at 700°C. Sheet of three Cr-0 impurity alloys containing up to 0.03 pct 0 was prepared by warm rolling arc melted, extruded, and swaged rod. Two Cr-C impurity alloys containing up to 0.09 pct C were made by equilibrating unalloyed chromium with a known amount of CH4 for 24 hr at 1150°C in previously evacuated quartz capsules. Chromium containing nominally 0.015 and 0.06 pct N was similarly prepared by equilibration with NH3. The sheet was recrystallized to give a stable grain size about equal to the sheet thickness. Molybdenum and Mo-O.5Ti were recrystallized in a tantalum resistance furnace 1 hr at 1 x lo-5 torr at 2300" and 220O°C, respectively. Tungsten was similarly annealed for 1 hr at 2500°C. Chromium and its impurity alloys were outgassed at 1100°C and recrystallized 1 hr at 1700°C under 1 atm Ar. Except for nitrogen, the impurity content stayed roughly constant. Nitrogen in both alloys was reduced to <0.001 pct. In fact, over 80 pct of the added nitrogen was lost after outgassing at llOO°C and annealing sheet 1 hr at 1300°C in argon in the presence of tantalum. Such a rapid loss can be rationalized since -2 torr N are required for equilibrium with 0.04 pct N in solution,3 while the equilibrium pressure is ~10-5 torr over tantalum at 1300°C.4 The recrystallized sheet was cut into small coupons which were metallographically ground and polished on one side with a minimum of grain boundary relief. The surface roughness was on the order of 0.01 µ. The tin and silver used were nominally 99.999 spec-trographically pure. After being outgassed at 1100°C and equilibrated in a molybdenum crucible for 0.5 hr at 1800°C in argon, the tin contained 3 ppm 0, <0.3 ppm N, and 0.1 ppm H. Following outgassing at 900°C and equilibration in a chromium crucible 1 hr at 1400°C in argon, the gas content of the silver was 1 ppm O, <0.5 ppm N, and 0.3 ppm H. Grooving Under Argon or Vacuum. All specimens were placed in unsealed containers made from rod or sheet of the same alloy, thereby enabling the polished surface to achieve gas-solid equilibrium. The annealing fixtures are shown in Fig. 1. The specimen was placed in a resistance furnace with a tantalum or Ta-10W heating element plus tantalum fixtures or radiation shields. Chromium was outgassed at 1100°C, and molybdenum and tungsten were outgassed at 1900°C to 1 x l0-5 torr or at the grooving temperature, whichever was lower. In vacuum anneals, the specimen was then heated directly to the intended grooving temperature. In argon anneals, 99.996 Ar was admitted

Jan 1, 1970

By H. H. Podgurski, J. C. M. Li, Y. T. Chou, F. N. Davis, R. A. Oriani

When an Fe-2 pct A1 alloy is nitrogemted at 500ºC with a gus tnixture (NH3-H2) in which the nitrogen activity has been kept Lou] enough to avoid the formation of iron nitride, a two-phase alloy is generuled which consists of AlN particles and a ferrite phase cotaining a heavy network of dislocations. The amount of nitrogen contained in such an alloy, when equilibrated with the nitrogenating atmosphere, far exceeds both that needed to satisfy the normal solution requirements of a Fe and that needed to convert all of the aluninuwi to AlN. This excess nitrogen is accounted for as being trapped on dislocations, adsorbed at the ferrite -AlN interface, and as an en-Iuznced lattice solubility in strained ferrite. This excessive uptake of nitrogen had previously been attribuled by other investigators to the formation of a nonstoichiornetric aluminum nitride. Isotope exchange experiments revealed various amomts of exchargeable N14 present in the originally nitrided samples that could not be removed by reduction with HS at 500ºC. This exchangeable nitrogen has been identified us that bound to the AlN -ferrite interface. Estimates of inter facial areas in alloys containing -3 pct by weight of A1N are as high as 10 sq m per g of alloy. ThE first1 of this series of papers described the experiments forming the basis for the elucidation of the mechanism of the formation of aluminum nitride particles within an Fe-A1 alloy. It was found that not only are dislocations necessary for the nucleation of the AlN particles but also the nitriding reaction in turn produces a dense network of dislocations in the ferrite matrix. It was also observed that nitrogen in excess of that needed for the formation of stoichiometric AIN is taken up by the alloy without the formation of an iron nitride. The present paper is an analysis of the excess nitrogen sorbed by the nitrided Fe-A1 alloy which considers the structure generated by the formation of the aluminum nitride particles. Because of the high density of dislocations, this system has proved to be quite useful in studying nitrogen-dislocation interactions. Wriedt and Darken2 have already reported such studies in a cold-worked ferritic steel. EXPERIMENTAL Nitrogen Sorption. The specimens of this alloy were cold worked (50 pct reduction) to 0.011 in. thickness and chemically cleaned in a 2:1 concentrated phosphoric acid-50 pct hydrogen peroxide solution before nitrogenation. The flowing nitrogenating atmosphere (11 pct NH3-89 pct H2) was established before the ni- trogenating temperature was reached. The same gravimetric and gas-flow equipment described in an earlier paper1 was also used in this investigation. Changes in nitrogen concentration were followed gravimetrically when establishing the isotherms. In the isotope exchange experiments, concentration changes were followed volumetrically. In some instances chemical analyses (Kjeldahl method) were used to check for material balances in both the gravimetric and volumetric procedures. Our objective was to obtain reversible nitrogen sorption isotherms for alloys equilibrated with NH3-H2 gas mixtures over a large range of nitrogen activity* and temperature. The *Defined as equal to PN H /P3/2 ,where P corresponds to partial pressure in atmospheres. Actually the nitrogen activity, aN, in the alloy equals K PNH3 /p3/2H2, where K is the equilibrium constant for the reaction NH3 = N + 3/2H2. upper limit for nitrogen activity was below that which would produce iron nitride; for reasons which will become apparent later, most of the sorption studies were made in the temperature range between 400" and 500&apos;C. The alloy sample studied most extensively in this investigation was given a series of successive reductions (100 pct H2) and nitrogenating treatments at 500°C to attain a stabilized structure. Presumably some dislocations were lost during these treatments. Throughout most of the sorption studies, temperature was held at ± 1°C and the gas-phase composition was held to k0.2 pet NH3. Based upon the results of numerous diffusion experiments with this alloy* the &apos;Results to be published in a third paper of this series. times chosen for equilibration were considered more than adequate, Nitrogen Isotope Exchange. The first exchange experiments were carried out by circulating a measured quantity of H2 and NH3* (with a predetermined isotopic *The NH3 was synthesized over a synthetic ammonia iron catalyst using H2, and N2, enriched with N15. AS the NH3 was formed it was removed continuously from the gas phase by circulating the mixture through a refrigerated (78ºK) trap. When most of the nitrogen had been converted to NH3, it was distilled from the trap into a glass storage vessel. composition, N15/N14) over a nitrided specimen at 450°C in a closed glass system. Attempts to reach the exchange limit isothermally, i.e., an isotopic ratio (N15/N14) in the gas phase identical with the extractable nitrogen in the nitrided alloy, were futile. The exchange rate between the gas phase and the alloy was too slow, involving many days. To circumvent the slow exchange with the gas phase, measured amounts of N15 and N14 were introduced into the alloy by nitrogenating with an NH3-H2, mixture at 500°C containing an N15/N14 ratio of 7.76; the charged specimens were then sealed by allowing an oxide film to form over them in air, and in this final condition the specimens were subjected to 500°C in vacuum for various times during which isotope exchange was allowed to proceed within the specimen. It was estab-

Jan 1, 1970

By F. Claisse, R. Angers

Self-diffusion in iron has been measured during rapid a-r transformations using a variant of the Kryukou and Zhukhovitskii diffusion method. The study was performed by thermally cycling iron foils (1 to 6 cpm) through the transformation (=910°C). Some foils have been subjected to over 1000 cycles and some have spent more than 15 pct of their total diffusion time in the process of transformation. The experimental results show that the a-r transformation has no measurable effect on self-diffusion in iron. The study is completed by a quantitative analysis of mechanisms which can affect the diffusion rate during the transformation. The analysis confirms the experimental results. SINCE diffusion is an important factor in many solid-state transformations, it is of interest to study how it is affected by the stresses generated during these transformations. Clinard and Sherby1&apos;2 were the first to make a study along these lines. They measured diffusion coefficients in Fe-FeCoV couples subjected to slow thermal cycling (1.5 cph) through the a-r transformation range. They found an enhancement of diffusion by a factor of about two. The purpose of the present paper is to report measurements of the self-diffusion coefficient of iron during much more rapid thermal cyclings (1 to 6 cpm) through the a-r transformation (-910°C). These more rapid cyclings produce higher strain rates during the transformation and should emphasize any possible influence of transformation upon diffusion. EXPERIMENTAL Iron foils, 25 to 35 µ thick, were cold-rolled from 99.92 pct pure iron and annealed in pure helium for 2 hr at 870°C; the resulting grain diameter was about 150 µ. Specimens 0.5 by 8 cm were cut from the foils and I7e55 was vapor deposited on one of their surfaces. A 38 gage alumel-chrome1 thermocouple was spot welded in the middle of one of the specimen long edges, Fig. 1. Two 38 gage chrome1 wires were also spot welded along the same edge on each side of the thermocouple; they were placed 2.5 cm apart and used for electrical resistance measurements. In order to prevent twisting and crumpling, the specimens were pinched between two quartz plates 0.1 by 1 by 7 cm and the assembly was close fitted into a 1 cm ID quartz tube. Four holes were drilled through the tube to let the 38 gage wires out: these were connected to the recording equipment by means of extension wires. 20-gage nickel wires fixed at both ends of the specimens were used to thermally cycle the foils by Joule heating. The above described device was placed in a 2.7 cm ID quartz tube which in turn was placed in a tubular furnace. Either a pure helium atmosphere or circulating hydrogen was used during the experiments. Specimens were subjected to thermal cycles between a minimum temperature To and a maximum temperature Tm at rates ranging from 1 to 6 cpm. This was obtained by maintaining the furnace at a constant temperature near the minimum temperature To and periodically passing an electric current through the specimen. Cooling was achieved by heat losses to the surroundings. The forms and periods of cycles were varied from one specimen to another; however, each specimen was subjected to one type of cycle only. The temperature and electrical resistance variations of the specimens were recorded as a function of time. The temperature curves were used for diffusion calculations while the electrical resistance curves were used to monitor the transformation and to determine its starting point and its approximate duration. Diffusion was measured by the method developed by Kryukov and zhukhovitskii3 and modified by Angers and Claisse.4,5 In this method a metallic foil is coated on one side with a radioactive isotope and the activity is measured periodically on both sides during the diffusion anneal. The following equation then holds: where: I1 Activity on the surface on which the deposit is made. I, Activity on the opposite surface. t Diffusion time. B Constant. D Diffusion coefficient. d Foil thickness including the deposit. G(t) A function of time; it is a second order correction term which is given graphically in Refs. 4 and 5. The diffusion coefficient D is found by plotting ln[(Il - I2)/(I1 + I,)] -G(t) against t; the resulting slope m leads to an accurate calculation of D through Eq. [2]. The effect of the a-r transformation on diffusion is expressed by the ratio DT/DU where:

Jan 1, 1970

By G. Beghi, G. Piatti

THE authors examined the problem of the gradual transformation of Al2O3 from the transition phases normally encountered in SAP (r -x-n)1-3 to the stable a phase. This phenomenon is well-known at temperatures above the melting point of aluminum,3"6 whereas in this paper the transformation was studied at temperatures lower than the melting point of the aluminum matrix.

Jan 1, 1967

By V. Patarini, M. Salkind

BECAUSE of its high strength and stiffness coupled with low density, continuous boron filament is showing great promise as a potential reinforcement for both metals and nonmetals. Of primary consideration for structural applications is the fatigue behavior of boron fiber composites. Composite fatigue behavior is dependent upon three factors: 1) fiber fatigue behavior, 2) matrix fatigue behavior, and 3) the effect of the interface and fiber ends. The purpose of this note is to describe the behavior of boron filament in rotating beam fatigue. The filament, described by Talley&apos; and Galasso, Salkind, Kuehl, and Patarini,&apos; was made by the hydrogen reduction of boron trichloride on a hot tungsten filament. Testing was performed using a commercial rotating beam wire fatigue tester* described by Votta.~ One end of the test sample is held in a chuck in a synchronous motor. The sample is bent around in a "U" shape, and the other end inserted into a carbide bushing. The maximum strain occurs at the bottom of the "U" where the radius of curvature is a minimum. The strain is adjusted by adjusting the length of the specimen and the location of the bushing. Samples were rotated at 3600 rpm and an automatic shutoff device used to determine the number of cycles to failure. The measurements were accurate to the nearest 360 cycles. The fatigue behavior is summarized in Fig. 1 for fifty-one samples of 4.8 x 10"3 in. diam fibers and ten samples of 3.2 X 10"3 in. diam fiber. The two sample groups represent two different filament production runs and two different nominal size groups. Both groups exhibited nominal tensile strengths of 400,000 psi. No significant difference in the fatigue behavior of the two sample groups is apparent. The scatter in the data is not unexpected for a brittle filament which exhibits a tensile strength distribution with a standard deviation of 10 to 15 pct. Because the test procedure provides a known outer fiber strain in the sample, the maximum stress was calculated assuming a Young&apos;s modulus of 58 x 10&apos; psi. This value was selected as being representative of several nominal fiber sizes.2 All of the samples which failed exhibited sudden, catastrophic fracture, and no permanent deformation. One sample was stopped after 1.66 x lo8 cycles at *200,000 psi. The fiber exhibited no apparent damage or deformation. It is apparent that the fatigue resistance of boron filament is quite good. It can therefore be speculated that the fatigue behavior of boron fiber composites would be controlled by the "weaker links", namely matrix fatigue resistance and interface behavior. In fact, preliminary investigations have revealed that this is true for boron-reinforced aluminum? It should be noted that the data presented herein may not necessarily reflect the tensile fatigue behavior of boron filament. It is well-known that boron filament has a radial residual stress pattern with the outer surface in ~om~ression.~ Because of this fact, tensile failure is normally nucleated in the interior of the filament.5 Since the data presented herein is for a rotating beam test in which only the outer surface of the fiber is stressed to the maximum value, it would be incorrect to assume that the failure mechanism and fatigue behavior would be the same if the fiber were tested in tensile fatigue. The fact that many of the data are well above the nominal 400,000 psi tensile strength would tend to support this argument. The authors would like to express their appreciation to the United Aircraft Research Laboratories for supporting this investigation and for permission to publish the results. A portion of this effort was supported by the Air Force Materials Laboratory under contract AF33(615)-2125.

Jan 1, 1968

By R. W. Bartlett

DISILICIDE coatings, MeSi2, on refractory metals are usually grown by a solid-state diffusion reaction similar to the parabolic oxidation of metals. Two or more silicide compounds occur in each of the binary silicon-refractory metal systems. When an adequate source of silicon is available during the coating process, the lower silicide compounds are usually not formed.1 However, during service application of the coated refractory metal, continued heating causes further diffusion and growth of the lower silicides. A study of the growth kinetics of the lower silicides in the molybdenum and tungsten binary systems with silicon was previously reported.2 The present study is concerned with the growth kinetics of Ta5Si3 and Cb5Si3, formed as conjugate layers between TaSi2/Ta and CbSi2/Cb diffusion couples, respectively. Diffusion couples consisting of disilicide-coated tantalum and columbium sheet coupons were subjected to diffusion heat treatments, cross-sectioned, and scanned by an electron-microprobe analyzer to determine the relative X-ray intensity profiles. These profiles correspond closely to concentration profiles for the constituents, and were used to identify phases and locate phase boundaries. The analysis of a single specimen after a diffusion-anneal provides only one value for the Me5Si3 phase thickness, corresponding to the time and temperature of the diffusion treatment. Consequently, each isothermal curve showing the rate of accumulation or depletion of silicide phases required several samples with identical diffusion temperatures but different diffusion times. The disilicide coatings were prepared by pyrolizing commercially pure silane in a hydrogen carrier gas. The hydrogen was purified by passage through a palladium membrane. Commercially pure tantalum and columbium sheet metal coupons, 0.005 by $ by 2 in., were used. All of the coated specimens for each system were prepared together in a single group in order to minimize coating variations among individual specimens. During pyrolysis, the brightness temperature was maintained at 1200°C. With suitable flow rates at this temperature, only the disilicides of tantalum and columbium were formed in detectable amounts. Coated specimens were subjected to diffusion an-neals in a tube furnace with automatic proportional control within ±10°C. A H2-Ar mixture, deoxidized and dried over anhydrous magnesium perchlorate, was used to prevent oxidation during the diffusion anneal. Diffusion couples were cross-sectioned, polished and examined with an A.R.L. electron-microprobe X-ray analyzer. Both metal constituents in each specimen were simultaneously scanned using a 1-p beam spot size and either 1- or 2-µ steps. Analyses were performed using the Ka radiation of columbium and silicon, and the La, radiation of tantalum. For all specimens, an acceleration voltage of 30 kv was used, and integration was made against the specimen current. LiF and A DP monochrometers were used to isolate characteristic radiations. Three or more traverses were made on each specimen. The intensity scales were adjusted using the constituent metals and standard samples of the silicide compounds which had been verified by X-ray diffraction. The relative intensity profiles were used directly, in conjunction with the standard samples, to identify compounds and phase boundaries. The stoichiometries differ considerably between the silicide compounds in both systems, and the homogeneity range for these silicide compounds is narrow. These characteristics result in marked differences in relative intensities of the fluorescing elements—differences which permit ready identification of phases and phase boundaries. Projections of both electron back-scattered images and characteristic

Jan 1, 1967

By R. D. Pehlke, J. V. Gluck

AS a portion of a general study of liquid-metal thermodynamics, high-temperature galvanic cells were used to study the effect of added dilute solutes on the activity of zinc in dilute solution with molten bismuth in the range 450° to 650°C. 1,2 The cells were of the type The experimental procedures have been described previously.1 In the course of studies conducted in the bismuth-rich corner of the systems Bi-Zn-Au and Bi-Zn-Cu, marked discontinuities were observed in the electromotive force-temperature relations for a number of the experimental compositions. Above the discontinuity temperatures, the relations, which were linear, exhibited slopes similar to the binary alloy of the same mole fraction zinc, as shown in Figs. I and 2. Below the discontinuity temperatures, the slopes were markedly different, but the relations remained linear. In general, as the amount of the third eletnent was increased, the slope of the lower portion of the relations tended to become less positive. The slopes of electromotive force-temperature relations reflect the entropy of mixing of zinc and, therefore, the occurrence of a discontinuity marks the transition between two different equilibrium situations involving the solution of zinc. A number of other investigators3-5 have used such observations to determine liquidus boundaries in binary alloys. Since the upper portions of the ternary electromotive force-temperature relations of this study had the same slopes as the binary alloys, the discontinuities are interpreted as marking the transition between the single-phase liquid region and the underlying two- and three-phase regions. Reference to the Zn-Bi equilibrium diagram6 confirms that the binary alloys were single-phase liquids at the experimental temperatures. Fig. I shows the electromotive force-temperature relations for the alloys containing Bi-Zn-Au and Fig. 2 shows similar relations for the Bi-Zn-Cu alloys. In the lower portion of each figure, the temperature of the discontinuity is plotted vs the mole fraction of the added solute at the various levels of zinc concentra- tion. Cross-plots from these curves at constant temperature permitted the construction of the partial liquidus surface isotherms shown in Figs. 3 and 4.

Jan 1, 1967

By R. M. Waterstrat, E. C. van Reuth

BINARY- alloy phases having the A15-type crystal structure have been described as occurring at a simple and more or less invariant stoichiometric composition (A3B) which corresponds to the relative number of atoms occupying each of the two crystallographi lattice sites in this structure.1,2 It is frequently assumed, therefore, that each crystallographic site is occupied exclusively by one kind of atom. In most cases, however, there have been insufficient experimental data to establish whether atomic ordering is, in fact, complete. Recent studies have shown that binary A15-type phases are sometimes stable over an appreciable composition range3&apos;&apos;* and, occasionally, the composition range of stability does not even include the "ideal" A3B stoichiometric composition.5-7 We have observed the existence of nonstoichiometric A15-type phases in the binary systems Cr-Pt and Cr-Os. This has not been reported in previous work on these alloy systems.1,8-11 A series of alloys, each weighing approximately 30 g, was prepared by are-melting in an Ar-He atmosphere using 99.999 pct Cr, 99.999 pct Os, and 99.99 pct Pt as starting materials. Each alloy was melted four times with a total weight loss of less than 1 pct. The stoichiometric (A3B) alloys were sealed in evacuated quartz tubes and annealed at 1200°C for periods of time ranging from 3 days to 2 months. Examination of the alloy microstructures revealed that little change had occurred over this time interval and it was therefore assumed that the microstructures were fairly representative of equilibrium conditions. No evidence of contamination was observed although there was apparently some loss of chromium which was confined to a thin layer at the surface of the specimens. The quartz tubes were quenched from the annealing temperature into cold water. X-ray diffraction and metallographic examination of the stoichiometric alloys revealed an estimated 10 to 30 pct of second phases which were tentatively identified as phases previously reported in these binary-alloy systems.8-11 A second series of alloys was prepared by mixing -325 mesh metal powders having a nominal purity of 99.9 pct and compressing these mixed powders in a cylindrical die at a pressure of 43,000 psi. These alloys, each weighing 15 g, and some of the arc-melted alloys were annealed in a high-temperature vacuum furnace heated by tantalum strips at a pressure of 10-8 Torr and were rapidly cooled by turning off the furnace power. X-ray and metallographic examination of both series of alloys served to establish the composition ranges of the A15-type phases. Although some chromium losses occurred during the vacuum annealing, they were largely confined to a thin layer on the outer surfaces of the samples. It was established that the A15 phases occur in the Cr-Pt system at 21 ± 1 at. pct Pt after 1 week at 1200°C and in the Cr-Os system at 28 ± 1 at. pctOs after 1 day at 1400°C (see Table I). We also observed that an arc-melted stoichiometric (A3B) alloy in the Cr-Ir system was single-phase (A15-type) in the "as-cast" condition in agreement with previous work.8,13 In addition we obtained a sample of the Cr-Os A15-type phase from Argonne National Laboratory. This alloy contained less than 1 pct second phase12 and was submitted to a density measurement. The density measurement yielded a value of 11.14 g per cu cm in comparison to a theoretical value of 11.25 g per cu cm calculated using the observed lattice constant (4.6806Å) of this alloy. The uncertainty in measurement was 0.1 pct but the sample may have contained some cracks or minor imperfections which could account for the low experimental value. We have also studied the atomic ordering in these phases by means of integrated line intensity measurements using thick, flat, rotating powder samples and CuK a radiation in an X-ray diffractometer. We have obtained order parameters of 0.90 for the Cr-Pt phase, 0.89 for the Cr-Ir phase, and 0.64 for the Cr-Os phase using the formula: where s is the usual Bragg and Williams order parameter, ra is the fraction of chromium atoms in A sites, and FA is the fraction of chromium atoms in the alloy. The values obtained are estimated to be accurate within ±4 pct. If the unusually small value for the order parameter of the Cr-Os A15 phase were due to the existence of lattice vacancies on the "B-atom" sites, then a density of 10.04 g per cu cm would be expected in contrast to the observed value of 11.14 g per cu cm. We, therefore. conclude that the fraction of lattice vacan-

Jan 1, 1967

By D. G. Westlake

NUMEROUS hydride habit planes in zirconium, Zircaloy-2, and Zircaloy-4 have been observed by various researchers and have been compiled by Louthan and Angerman.1 While only partial agreement exists on the identification of these habit planes, there is a growing consensus that a tensile stress applied on a polycrystalline rod during slow cooling will cause the hydride platelets to lie perpendicular to the tensile axis. walters2 agrees with Louthan and Angerman who reason that "The particular plane on which precipitation will occur is the plane that will result in the maximum relief of stress by precipitation of the low-density hydride." The experiment described below was initiated to test this hypothesis on a single crystal of zirconium. A single-crystalline tensile specimen of zone-refined zirconium, designated number 13 in a previous study,3 had a square cross section with one pair of parallel faces only 4 deg from the basal plane of the hcp structure. The tensile axis was about 86 deg from the (0001) pole, 14 deg from the (1010) pole, and 16 deg from the (1150) pole. The specimen was charged to 50 ppm H by allowing reaction with the correct amount of hydrogen at 1073°K, homogenizing at this temperature for 2 hr, and cooling in the furnace. Two- surface analysis revealed that hydride platelets had precipitated parallel to the three {1010} prism planes. The specimen was heated to 673°K, in air, for 16 hr to bring the hydrogen back into solid solution, and furnace-cooled to 573°K.* It was then stressed in ten- sion at 1.2 kg per sq mm. (This produced a resolved shear stress of 0.6 kg per sq mm for glide on the prism plane with the highest Schmid factor. A higher stress would have produced significant strain at this temperature because the critical resolved shear stress for prism-plane glide in this crystal was only 1.0 kg per sq mm at ambient temperature.) The poles of the three prism planes were at angles of 14, 46, and 74 deg to the tensile axis so that an applied stress would exert normal stresses on the three planes in the approximate ratios 10:5:1, respectively. As soon as the stress was applied, the sample was furnace-cooled to room temperature. It was ground on wet Sic paper and chemically polished in 50 parts HNO3, 50 parts water, and 7 parts HF before examination. The result of the experiment was negative; i.e., the three (1010) planes were of equal importance as hydride habit planes.* It must be admitted that the ex- periment is not entirely comparable to those performed by walters,2 Louthan,5 and Louthan and Marshall6 on polycrystalline materials. They have found that some critical stress (below the macroscopic yield stress) is required for stress-orienting the hydrides. The applied stress in the present experiment was, by necessity, smaller by an order of magnitude than the critical stresses they report for the various materials. If the critical stress was related to the microstructure, one might postulate that it should be decreased by increasing the degree of perfection of the metal lattice and by increasing the grain size. But the experiment above suggests that, for the extreme case of a zone-refined single crystal of zirconium, the critical stress lies above that which one can apply without introducing gross plastic strain as another variable.

Jan 1, 1967

By L. Grånäs, B. Aronsson

In a recent study of Fe-Si alloys Walter and Koch&apos; observed pairs of dislocations in Fe-6.25 pct Si crystals rolled to reductions of 10 pct and subsequently annealed for 1 hr at 650°C. They interpreted these pairs as being due to stacking faults. From the spacing of the dislocations a stacking-fault energy of 15 to 19 ergs per sq cm was calculated. These authors did not pay any attention to the order -disorder phenomena in Fe-Si alloys. It is the purpose of this communication to report some preliminary results from a study of ordering and its influence on the plastic deformation of Fe-6.0 pct Si alloys. Our results suggest that the dislocation pairs observed by Walter and Koch may have been due to long-range order rather than to stacking faults. The alloys used in this investigation were prepared from pure electrolytic iron and silicon and were melted in argon. After hot working, strip tensile specimens were machined to a gage length of 70 mm and a thickness of 1 mm. The specimens were heat- treated for 2 hr at 1000°C, furnace-cooled, and subsequently deformed 2 pct in tension at 400°C. The strain rate was 5.6 X lo-&apos; sec-&apos;. Thin foils of the deformed specimens were prepared by means of the Bollman technique and examined in a Siemens Elmis-kop I at an accelerating voltage of 100 kv. In the Fe-Si system long-range ordering occurs at a silicon content of about 6 pct Si. In our alloys evidence for ordering is given by selected-area diffraction patterns which show extra reflections consistent with a super lattice of the D0 9 type. In addition, the dislocation arrangement in deformed specimens indicates that long-range order is present. A typical mi-crophotograph of a thin foil is shown in Fig. l. The dislocations are usually straight and parallel and laying in distinct directions. In the commonly observed (111) zone the projections of the dislocations are close to (113) and (oil). Observation of the image position indicates that the two dislocations in a pair have the same Burgers vector and hence constitute a superlattice dislocation.~ According to theory3 a superlattice dislocation in the DO3 structure consists of four ordinary dislocations connected by two types of antiphase boundaries as shown in Fig. 2. In our specimens only two dislocations in each pair have been observed, Fig. 1. The problem is to decide whether the area between these is a NN or a NNN antiphase boundary. Dark-field images using the (200) reflexion (the indices are defined with respect to the DO3-type superlattice) can

Jan 1, 1968