By G. C. Rauch, T. H. Courtney, J. Wulff

The superconducting behavior of Nb-Ti alloys containing 40 and higher wt pct of Nb and variable oxygen content was studied as a function of thermomechanical processing. Critical current density (Jc) us applied transverse magnetic field (H) data were obtained for 0.010 in. diam wires at 4.2° Kin steady fields up to 120 kOe. The precipitate responsible for increase in Jc in each of the alloys studied was related to niobium and oxygen content. In alloys containing 40 to 60 wt pct Nb with less than about 1600 ppm of oxygen, w precipitation in the range 350° to 450°C appears to be responsible for the maximum value of Jc observed. In alloys of higher oxygen content (-2500 ppm), the oxygen-enriched a phase which precipitates in the temperature range 450° to 550°C is a more effective fluxoid pinner. Maximum Jc in low oxygen (350 ppm) 80 wt pct Nb alloys was achieved by 600°C aging heat treatments. Measurements of resistive critical field also reflect the changes in composition accompanying precipitation in these alloys. It is well known that the superconducting critical current density, Jc, of solid solution superconducting alloys can be increased by precipitation heat treatments.1-4 The precipitate, to serve as an effective superconzlucting fluxoid pinner and increase Jc, must be of proper size and spacing.' Its electronic properties must also be different from those of the matrix.6 As in age-hardenable systems, optimum temperature and time of aging are dictated by the composition and history of the particular solid-solution alloy under consideration. The alloy diagram of Ti-Nb7-9 shown in Fig. 1 is typical of ß-stabilized Ti alloys. Precipitation to achieve high Jc in Ti-Nb and Ti-Ta alloys is usually carried out in what is believed to be a two-phase a + ß region.1,2,4,10 Previous work on Ti-Nb4,11 and on other ß-stabilized systems such as Ti-V, Ti-Mo,12-14 has shown, however, that the first precipitate to appear is not necessarily (Y. Under specific conditions the meta-stable w phase is precipitated instead. A further complication arises in such alloys from the strong influence of contained oxygen on the phase stability and on the kinetics of precipitation.15,16 The superconducting critical current density of Nb-Ti alloy containing less than 36 wt pct Nb has been studied by Vetrano and Boom1 and Kramer and Rhodes.4 The most effective aging temperature was found to be about 425°C; fluxoid pinning was attributed to the precipita- tion of a by Vetrano and Boom and of w by Kramer and Rhodes. Although the latter workers used recrystal-lized material and the former cold-worked, studies carried out in our laboratory lead us to believe that the type of precipitate responsible for increased Jc is unaffected by prior cold-work.17 That other types of precipitates may also be effective, especially in higher oxygen-containing alloys, has been demonstrated by Reuter, et al.2 in this laboratory with the aid of electron microscopy. Reuter et al. found that at an aging temperature of 600°C, fee-TiO is precipitated, resulting in high values of Jc. Even higher values of Jc were observed after heat treatment at 500°C, but the precipitate could not be indexed as fee-TiO. Whether the precipitate was oxygen-rich w or a could not be clearly distinguished. The work nevertheless indicates that appreciable amounts of oxygen alter the nature of the phases precipitated at different temperatures, at least in alloys containing more than 36 wt pct Nb. Since such compositions are more readily worked into suitable wire than lesser niobium content alloys, it was decided to study the response to aging of the alloy compositions reported in the present paper with the hope of clarifying the effect of composition on the precipitation processes responsible for high values of Jc. I. EXPERIMENTAL Nb-Ti alloys containing 40, 50, 60, and 80 wt pct Nb were prepared by are-melting 35 g ingots of iodide crystal bar titanium and electron-beam melted niobium.

Jan 1, 1969

By Winston A. Wong, John J. Jonas

Commercial purity aluminum was deformed by extrusion over the temperature range 320° to 616°C and the strain rate range 0.1 to 10 per sec. Flow stresses and strain rates were calculated from the experimenLa1 ram pressures and speeds. The stress-strain rate-lemperature relationship in extrusion was found to be similar to that in creep. Extrusion, torsion, compression, and creep data extending over ten orders of magnitude of strain rate and over two orders of magnitude of stress were correlated by a single creep equation. It was concluded that hot-working is a thermally activated process, in which the rate-controlling mechanism is either the climb of edge dislocations or [he motion of jogged screw dislocations. The microstructural changes observed during extrusion were consistent with the proposed deformation mechanisms. ALTHOUGH great progress has been made in understanding the technology of extrusion, very little is known about the actual deformation mechanisms operating during flow. Previous accounts describing extrusion have indicated that the relationship between ram speed (V), pressure (P), and temperature (T) can be given as follows:1 V = apb and P = A' exp(-AT). In these equations, a and b are constants which depend on temperature, A' is a constant which depends on ram speed, and A is a "coefficient" with a different value for each metal. Although these equations have fairly wide application, they do not contribute much to a fundamental understanding of the deformation. Furthermore, extrusion has not hitherto been considered as a thermally activated rate process. This lacuna is surprising because hot-working is similar to high-temperature creep in several respects. There is, in fact, a fair body of experimental evidence suggesting that the material response under hot-working conditions is similar to that occurring under creep conditions, in spite of the many orders of magnitude difference in strain rate.2"4 Since creep has been extensively analyzed in terms of dislocation mechanisms, the comparison of hot-working to creep is useful, for it can suggest the possible deformation mechanisms operating during hot-working. In this paper, the hot extrusion of aluminum will be examined from the point of view of thermally activated deformation mechanisms, such as operate during creep. EXPERIMENTAL PROCEDURE The experimental procedure consisted of extruding commercial purity aluminum* over a range of ram velocities and temperatures at constant die reduction by the direct method. Details of the experimental equipment have been published elsewhere.5 Extrusion was carried out at each of the following billet temperatures: 320°, 376°, 445°, 490°, 555°, and 616°C at the following constant ram speeds: 0.002, 0.008, 0.02, 0.1, and 0.2 in. per sec.* All results were obtained using a square-shouldered die with an extrusion ratio of 40:1, giving a reduction in area of 97.5 pct. The ram force was the dependent variable, and was measured by means of strain gages on the ram and was plotted as a function of ram travel. The sequence of events before making an extrusion was duplicated before each run so as to minimize as much as possible variations in experimental conditions. For example, after the equipment had been assembled, the billet was allowed to heat up to temperature inside the insulated container. Once the container attained the desired temperature, a period of 1/2 hr was allowed to elapse before the extrusion was made. This time was found to be required to allow the billet to reach a steady-state temperature, as determined from previous tests. When all was ready, extrusion was carried out without interruption; that is, the billet was upset and extruded in one operation. EXPERIMENTAL RESULTS AND DISCUSSION The two usual experimental approaches for investigating high-temperature deformation exhibit an important common feature. In the first approach, which corresponds to creep, a constant stress (or load) is applied to the material at constant temperature and the resultant strain is recorded against time. After an initial transient stage, a state of constant strain rate exists (secondary creep), in which a steady-state condition is established which is sensitive to variation in either applied stress or temperature. In the second approach, a constant strain rate is applied and the resultant flow stress is recorded. This corresponds to the situation in hot torsion or hot compression, where it is observed that, for a constant test temperature, there is an initial rise in stress to a steady value which is maintained up to very high strains. In tests of this type, a steady-state region is also established in which the stress is sensitive to variation in either the strain rate or the temperature.3,4,6-16 In both types of tests, therefore, a steady-state region is established after an initial transient. In the case of hot-working this region may be called steady-state hot-working, and it is analogous to steady-state creep with which it has many common features. Stress Dependence of the strain Rate in Extrusion. In order to assess the stress dependence of the strain rate under extrusion conditions, and to compare it to that of creep, as well as of hot torsion and hot compression, the extrusion data were analyzed according to power, exponential and hyperbolic sine creep equations.

Jan 1, 1969

By Michael Epstein, Daniel E. Rosner

Fume nucleation sufficiently close to vaporizing suvfaces can augment net vaporization rates into cooler environments. Environmental conditions favoring large vaporization rate enhancements are briefly discussed and a previous theoretical treatment of this nucleation phenomenon is generalized to account for the self-regulating effect of condensalion-heat release within the boundary layer. Despite kinetic limitations on homogeneous nucleation, and latent heat release, non-diffusive condensate removal processes appear to make possible large enhancements in steady-state vaporization rates, provided surface temperatures are well below the boiling point. When condensed phases vaporize (or dissolve) into cooler media, the diffusion-limited mass loss rate can be strongly influenced by the process of nucleation/con-densation (or precipitation) within the thermal boundary layer. This condensation process (which typically leads to mists or fumes in the case of evaporation into cooler gases) has the effect of steepening the vapor pressure profiles near the evaporating surface, since the condensation zone acts as a vapor sink. However. the resulting enhancement in the diffusion-limited evaporation rate can be estimated (as first done by Turkdogan1 for the case of molten iron/nickel alloys evaporating into helium) only if one has independent knowledge of the critical supersaturation, sCrit(T), required to homogeneously nucleate the vapor.* In a recent reformulation and generalization of the theoretical model of Ref. 1 it has been shown that, when log sCrit is approximately linear in reciprocal temperature, rather simple expressions can be derived4 for the ratio of the actual rate of vaporization j" to either the minimum (no condensation) rate j"min, or the maximum (equilibrium condensation) rate j"max In the present communication we wish to briefly report on further developments and implications of the formulation of Ref. 4, with emphasis on i) environmental conditions favoring large enhancements in vaporization rate, and ii) the self-regulatory influence of condensation heat release (neglected in Refs. 1 to 4) on predicted vaporization rates. Additionally, we take this opportunity to correct several misprints appear- ing in Ref. 4, and comment on Elenbaas's recent criticism5 of Ref. 1. MAXIMUM POSSIBLE VAPORIZATION RATE IN PRESENCE OF CONDENSATION A nonequilibrium theory is of interest because of the very large difference between the minimum (no condensation) and maximum (equilibrium condensation) vaporization rate. The magnitude of this maximum possible enhancement can be shown quite clearly by combining a result of Refs. 3 and 4 with the fact that for most liquids there is a simple relationship between the molar heat of evaporation, A, and its boiling point, i.e., A/(RTBp) = C, where the constant C, often called the Trouton ratio, takes on values not very different from 11.* More generally, for any substance (including The Trouton ratio (which for water is 13, for methane, 10, and so forth) will be recognized as the ratio of the molar entropy change upon vaporization (at TBP or Ttransf) to the unlversal gas constant R. Its near constancy reflects the fact that the change in atomic order upon vaporization depends only weakly on the kinds of molecules involved. those that sublime under ordinary conditions) we can define a characteristic transformation temperature. Ttransf, by a relation of the form Ttransf =A/(CR), and then examine the maximum possible evaporation rates as a function of how far removed from Ttransf are the surface temperature, Tw, and ambient temperature, T. Subject to the assumptions: 1) equilibrium vapor pressure, pv,eq, everywhere small compared to prevailing total pressure, p, and 2) negligible effect of condensation heat on temperature profile, the maximum enhancement ratio was found (Eq. [17], Ref. 4) to be: where, for most vapors, Nu/NuD (the ratio of heat transfer coefficient to mass transfer coefficient for the same configuration) is a number near unity.* Ex- *An alternative derivation of the Nu = NuD special case of this equation. revealing its validity for arbitrary velocity/temperature profiles in a laminar boundary layer, is given in Ref. 3. amining this result for a "Trouton substance", one obtains the results shown in Fig. 1, constructed for C = 11. Since we are concerned with vaporization enhancements (j'max/J"min > 1) at surface temperatures below Ttransf, this area of interest is shown unshaded. One notes that at a fixed ambient temperature (hence, T/TtranSf) there is a unique surface temperature, 2T , at which j"max/j"min attains its peak value; moreover, the peak enhancement ratio, see dashed locus. Fig. 1, is: (NuA/NuD)(C/4)(Ttransf/T,). Hence, if Nu = NuD, when the ambient temperature is less than 1/4 of TtranSf the peak enhancement exceeds the Trouton

Jan 1, 1969

By E. Breinan, M. Salkind

Al3Ni whiskers were chemically extracted from unidirectionally solidified Al-A13Ni eutectic ingots, bent into loops, and heated for 0.1 to 10 hr at 320°, 415", and 510°C. The initial strains ranged from 0.003 to 0.055. In all cases, permanent plastic deformation was noted after heat treatment. The deformation consisted of relatively uniform bending at low stresses and temperatures and short times and kinking followed by fracture at high stresses and temperatures and long times. After kinking, the whisker segments adjacent to the kinks were found to have straightened, which is evidence of a dislocation condensation mechanism. The range of temperatures and strains at which time dependent plastic deformation was found indicates that creep of whiskers probably plays a role in the creep of A13Ni whisker-reinforced aluminum. WHISKERS may be defined as nearly perfect single crystals which exhibit high strength. Because they can support high stresses at relatively low strains, they have been successfully employed in reinforcing metals at both ambient and elevated temperatures. In studying the creep behavior of A13Ni whisker-reinforced aluminum at elevated temperatures,1,2 it was noted that the composites exhibited measurable creep deformation. This investigation of the creep relaxation of individual A13Ni whiskel, extracted chemically from the composite was initiated to determine if creep of whiskers could con. "bute to the overall creep of the composite material. Many observations of plastic deformation of metal and halide whiskers have been made. Brenner3-8 noted that copper, silver, and iron whiskers exhibited heterogeneous plastic deformation at room temperature when strained beyond their yield points. Gyulai9 and Gordon10 observed plastic deformation of relatively large (>3 µ) NaCl and KC1 whiskers, although the smallest, most perfect whiskers were completely elastic. Eisner" noted plastic deformation and microcreep of iron and silicon whiskers at room temperature after straining beyond the yield point. Whiskers reported to exhibit creep at stresses below the yield point were zinc1'-" and Silicon.15 Cabrera and price" observed some zinc whiskers which crept at room temperature after a short incubation period but then stopped creeping after a short time. Because some of their specimens exhibited no creep, they concluded that those whiskers that crept were relatively imperfect. Pearson, Reed, and Feldman15 observed similar creep behavior of silicon whiskers at 800°C. They also concluded that creep of the whiskers was a result of imperfections in their crystals. Brenner16 observed delayed failure of A12O3 whiskers at elevated temperatures but found no evidence of plastic deformation up to 2030°C (99 pct of E.EREINAN and M.SALKIND,JuniorMembers AIME,are Research Scientist and Chief, respectively, Advanced Metallurgy Section, United Aircraft Research Laboratories, East Hartford, Conn. Maunscript submitted April 5, 1968. IMD the melting temperature). Brenner also noted7 that some copper and iron whiskers exhibited delayed kinking above 350°C while others did not. One can conclude from these observations that small relatively perfect whiskers could exhibit completely elastic behavior during sustained elevated-temperature loading of composites. Since A13Ni whiskers tested in both bending and tension were found to exhibit no evidence of plastic deformation at room temperature'7'18 this study was initiated to determine whether or not creep of A13Ni whiskers occurred at the elevated temperatures at which creep in the composites was observed. Whiskers were chemically extracted from ingots of unidirectionally solidified A1-A13Ni eutectic, constrained in bending to various elastic strains and heat-treated. The bending constraints were removed after heat treatment and the amount of permanent set was taken as a measure of the time-dependent plastic deformation. EXPERIMENTAL PROCEDURES Ingots of eutectic Al-A13Ni containing nominally 6.2 wt pet Ni were unidirectionally solidified at approximately 11 cm per hr using a process described elsewhere.19,20 The starting materials were 99.99 pct pure. Cylindrical sections cut from the center of each ingot were placed in a 3 pct aqueous solution of hydrochloric acid and the whiskers were extracted as described previously.17 The whiskers nearest the surface were blackened somewhat due to overexposure to the acid while the center of the ingot was being dissolved These partially attacked whiskers were discarded. An intermediate zone of silver-gray-colored whiskers was collected and stored in methanol for use in relaxation experiments. Individual long pieces of A13Ni whiskers were placed on Fisher Precleaned Microscope Slides. These normally straight whiskers were bent elastically into arcs or loops of varying radii by manipulating their ends with a slender probe. The mass attraction between the whisker and the probe was sufficient to cause the whisker to follow the probe. The whiskers were retained in the elastic bend by the surface tension of a fine residual film on the slides. By using long whiskers, the action of the surface tension on the unlooped ends of the whisker allowed high elastic strains to be maintained in the loops. After each whisker was bent, a photomicrograph was taken for use in measuring the bending strain. The range of strains studied was 0.003 to 0.055. The bent whiskers were then encapsulated in Pyrex tubes at pressures between 10"6 and 5 x 10"6 mm of mercury and heat-treated at 320°, 415°, and 510°C (respectively 53, 61, and 70 pct of the peritectic decomposition temperature). After each heat treatment, the liquid film on the slides was found to have dried, but the whiskers were held in their original shapes by a residue on the slide. The minimum radius of curvature of each bent whisker was measured before and

Jan 1, 1969

By M. Metzger, L. E. Hendrickson

Grain boundary attack in 16 pct HCl was found to be substantially the same at low penetrations in zone-refined aluminum (individual impurities 0.1 at. ppm), superior electrolytically refined aluminum (51 at. ppm), and aluminum with various impurities at much higher levels. It was concluded that impurity atom segregation affecting corrosion would have been detected and that the corrosion susceptibility did not originate in this segregation but in the structure of the boundary. It was pointed out that the significance of most previous studies in this system had been obscured by an unrecognized autocatalytic copper reaction. Although general corrosion rate was also impurity-insensitive , there was shallow pitting attributed to iron seg-regation and a hillocked surface texture associated with copper; these were interpreted as due to cathodic damage affecting- cathode distribution. THE grain boundary corrosion suffered by high-purity aluminum in hydrochloric acid has been the object of some interest (the earlier work is summarized in Ref. 1). The central metallurgical question here is whether the corrosion susceptibility of a boundary originates in its structure or in impurity atom segregation. An attempt to study this question revealed large catalytic effects associated with small quantities of the copper impurity in the aluminum, 220 ppm, or in the corrodent, and these magnified the preferential boundary attack and obscured the intrinsic susceptibility question.' After the catalytic effects had been examined,"' test conditions could be designed to avoid them and methods developed for studying the shallow boundary penetrations prevailing when they were absent.= It then became possible to determine whether intrinsic boundary corrosion in aluminum involves impurity segregation. The older work provided no firm information on grain boundary segregation of specific solutes influencing corrosion although several studies suggested iron segregates.4,5 perryman4 found in 10 pct HC1 that the slowly developing (microns per month) grain boundary grooves were deeper in material of higher iron content (range 10 to 550 ppm, with 5 to 80 pprn Cu) but he did not measure the depths of general corrosion, which were probably several times greater, and his reference surfaces may have varied more than did the groove depths. Metzger and Intrater's results for 20 pct HC~,' which yielded higher time-average rates (mm per month) and deeper penetrations, suggested that boundary segregation of iron (range 4 to 230 ppm, with 22 pprn Cu) decreased the penetration rate. However. in the stronger acid the autocatalytic l.E. HENDRICKSON, Student Member AIME ,and M. METZGER, Member AIME, are Research Assistant and Professor of Physical Metallurgy, respectively, Department of Mining, Metallurgy and Petroleum Engineering, University of Illinois, Urbana, Ill. Manuscript submitted March 11, 1968. IMD effect of the copper impurity is greater1,2 and it is now evident that their corrosion rates had been much magnified by this effect and did not provide a proper basis for the analysis of segregation. In exploratory studies of other solutes (made under the same conditions), 1000 ppm additions of Mg, Mn, or Si or 100 ppm Ca were without effect.1 Montariol6 noted that boundary attack in 22 pct HC1 persisted after zone refining although with fewer deep fissures (ranges 0.06 to 4 ppm Cu, 4 to 23 ppm Fe). Autocatalytic effects may have influenced these results also and those of Perryman.4 The present objective was, as a first step, to see whether quantitative tests designed to exclude autocatalytic influences would indicate the existence of low-level impurity effects on intrinsic boundary corrosion. Comparison of electrolytically refined with zone-refined aluminum of lower copper and iron contents revealed no differences in boundary corrosion, but certain impurity-sensitive differences in general corrosion morphology were noted and investigated further at higher impurity levels. I) EXPERIMENTAL PROCEDURE A) Material. A selection from commercially available material was made with the cooperation of several producers. An electrolytically refined lot (III-A, 1 ppm Cu, 2.4 ppm Fe) studied previously3 provided a starting point. Since material of substantially higher copper content could not be used if the autocatalytic corrosion reaction were to be avoided,2,3 a lot (III-B) of about the same purity was added as a check, two zone-refined lots (I-A and I-B) with copper and iron an order of magnitude lower were selected for comparison, and an intermediate lot (11) was included. Analytical data are given in Table I. For copper in I-B and iron in I-A and I-B, the actual concentration is thought to be near the limit given, i.e., about 0.1 ppm. For titanium, vanadium, and chromium in III-B, the actual amounts are thought to be, like those in III-A, substantially lower than in the zone-refined lots (these elements concentrate in the solid on freezing). Data are given later for some additional lots surveved. B) Specimen Preparation and Procedure. one by 3 cm blanks with a notched stem were cut from 1-mm cold-rolled sheet, annealed 24 hr in air at 650°C, and quenched in an air stream (42°C per sec initial cooling rate, 100 sec to cool to 100°C). The high annealing temperature maximized diffusivities and approach to equilibrium impurity distributions. A water quench, in principle more efficient in preserving the distribution established, was undesirable because the boundaries were almost plane and they tended to shear and migrate during the quench and thus to be separated from any existing impurity atmosphere. Test procedures, previously described,3 involved electropolish-ing, etching 2 min in 10 pct HF at 24.0°C, and expos-

Jan 1, 1969

By R. W. Heckel, R. A. Tanzilli

Treatment of the finite, diffusion-controlled, two-phase, moving-interface homogenization problem has been carried out by numerical methods for a wide range of input parameters. Solutions have been obtained for planar, cylindrical, and spherical diffusion geometries. The effects of parameters such as the interdiffusion coefficients (concentration-independent) of- both phases, the concentrations (time-independent) of each phase at the interlace, mean composition, initial size of the dissolving- phase, and initial composition of- the two phases are considered. The results are displayed to show both the position of the interjace and the degree of homogenization (expressed in terms of concentration at the matrix phase symmetry boundary) as a function of diffusion time. Typical exaw~ples to which the results may be applied are discussed. A limited number of exact, closed-form solutions to the multiphase, diffusion-controlled, moving-interface problem exists in the literature, e.g., Refs. 1 to 7. The exact, closed-form solutions generally consider the outermost phases to be infinite in extent and also assume an interfacial velocity function. It is through use of such boundary conditions that closed-form solutions are readily obtained. An extensive literature also exists on numerical solutions to the mathematically analogous solidification problem, e.g., Refs. 8 to 12. In addition, a numerical solution involving mass transfer with spherical interfaces and infinite boundaries has recently been carried out.13 A practically important class of diffusion problems exists, however, in which the boundaries of each phase away from the interface are finite. For example the finite boundary condition arises when one sets up a model for analyzing the homogenization behavior of two-component powder compacts in two-phase systems or for studying the solution behavior of precipitates. Although exact, closed-form solutions have as yet not been found to this class of problems, solutions are possible using numerical methods. The purpose of this paper is twofold: 1) to describe a numerical method for treating the two-phase, diffusion-controlled, moving-interface problem involving finite boundaries with planar, cylindrical, and spherical interfaces; 2) to present the results of a parametric study which identifies the role played by each variable appearing in the analytical model. R. A. TANZlLLI,Student MemberAIME,onleaveofabsence from the General Electric Co., Re-entry Systems Department and A. W. HECKEL, Member AIME, are Graduate Student in Materials Engineering, and Professor, Department of Metallurgical Engineering, respectively, Drexel Institute of Technology, Philadelphia, Pa. Manuscript submitted May 6. 1968. IMD MATHEMATICAL MODEL The three geometries analyzed are shown in Fig. 1. For each configuration a symmetry element is shown, across whose boundaries the mass transfer is zero. Mean composition, C, and the characteristic solute-rich phase half-thickness (or radius), 1/2, are the independent variables while the characteristic symmetry element half-thickness, L/2 (measured from solute-rich phase center to the matrix phase plane of zero mass transfer), is a dependent variable. The symmetry element for a planar interface accurately represents a real diffusion situation involving the stacking of symmetry elements of constant size. Because cylindrical and spherical symmetry elements of constant size cannot be stacked to fill space, the meaning of the dimension, L/2, for these situations may be considered in terms of the following approximations: and where NA is the number of parallel cylindrical elements per unit area on a surface normal to the cylinder axes and Nv is the number of spherical elements per unit volume. The model consists of a solute-rich phase matrix phase composite of limited mutual solubility. The concentrations at the interface are assumed constant with time; no assumption of local equilibrium at the interface is necessary except for the case where the

Jan 1, 1969

By A. R. Krause, C. Laird

In order to establish whether or not there is a real temperature effect in fatigue (independent of environment) , poly crystalline copper and Cu- 7.9 A1 alloy have been cycled at 298° and 7° K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen. The lives of both copper and the alloy were found to be highly temperature-dependent in the absence of environment. This result casts serious doubt on the validity of the cell structure hypothesis for stage I crack propagation as presently formulated, because it predicts that there should be no such tempevnture dependence. On the other hand, the plastic blunling process is consistent with the result. Effects of environment aside, the homogenization of slip which accompanies testing at low temperature, and at low strains, seems to be the main cause for increased fatigue life. At high strain amplitudes, the fatigue lives of wavy slip materials, typically copper, are independent of temperature.' It is well-known, however, that low-strain lives greatly as as the temperature of testing is decreased. By contrast, the lives of planar slip materials, such as Cu-7.9 pct A1 alloy, increase to an even greater extent with decreasing temperature throughout both the high and low strain ranges.1'2'5 The mechanism of this temperature effect is associated with the earliest stages of fatigue failure,'" crack nucleation, and stage I growth,"' which is slow propagation along slip bands to the depth of a few grain diameters. Such life behavior has been interpreted on at least two different bases. On the one hand, those interested in the temperature effect at high strain amplitudes1 believe that stage I growth occurs by the plastic blunting process of crack propagation.7'9 They explain the effect in planar slip materials by the homogenization of slip* which accompanies fatigue testing at low temper- atures and serves both to delay crack nucleation and to decrease the rate of stage I propagation. On the other hand, Holt and Backofen,2 who have studied the effect in low strain fatigue, believe that stage I growth can be interpreted by a cell structure hypothesis.10-12 They have challenged2 the conclusion that there is a real temperature effect in this regime of fatigue testing and have interpreted the increased fatigue lives almost entirely in terms of the "environmental-protective'' effect of the liquid nitrogen and helium baths used to obtain low temperatures. This interpretation by Holt and Backofen2 may offer a means of discriminating between these two mechanisms as currently formulated and used to explain stage I growth. On the basis of the plastic blunting process applied to stage I crack propagation,7* the low strain fatigue lives of both wavy and planar slip materials should be increased with decreasing temperature. This follows because both materials show increased slip homogenization in this strain regime."13 Consequently, crack nucleation in intensified bands will be delayed and the linking of such small cracks into larger stage I cracks will be difficult. In addition, the blunting process required to lengthen a stage I crack from the order of 2 to 10 (where the strain concentration of the crack begins to overcome the slip homogenization property of the material) will also be retarded. These delays will give rise to longer lives in both kinds of material. In contrast to the blunting hypothesis, no temperature dependence has been predicted on the basis of the cell structure hypothesis, because it is well-known that materials cycled at low temperature show no differences in type of dislocation structure for a given strain amplitude.18"20 If the lives of wavy and planar slip materials do show a temperature dependence when the environment is eliminated as a variable, then it is questionable whether cell structures per se have a fundamental role in fatigue fracture. Accordingly, specimens of copper and Cu-7.9 wt pct A1 have been cycled at 298° and 77°K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen, in order to establish whether or not there is a real temperature effect in low strain fatigue. Since it is difficult to measure the strains in specimens when cycled in vacuo, S-N curves have been used as the basis of comparison. In studying the influence of temperature on fatigue life in ordinary environment, Holt and Backofen2 used the superior basis of E-N curves. However, they also published S-N curves and thus established the relationship between E-N and S-N curves. This relationship is used to support the S-N comparison reported in the present investigation. EXPERIMENTAL Materials. The copper employed in this investigation was of 99.99 pct purity and the cu-7.9 pct A1 was prepared from metals of the same purity. The stock, of 3 in. initial diam, was reduced in size by rolling

Jan 1, 1969

By E. Mille, R. Geffken

The Mg-Si and Mg-Ge phase diagrams were rede-levtnined by thermal analysis, and the existence of a single congruent melting compound in each system was confirmed. The melting points of the two compounds Mg2Ge and ,Wg2Si were found to be 1117.4° and 1085.0°C respectively. The euteclics for the Mg-Ge system occur at 635.6°C (1.15 at. pcl Ge) and 696. 7°C (64.3 at. pct Ge); for the Mg-Si system the eutectics are at 6376°C (1.16 at. pct Si) and 945.6°C (53.0 al. pcl Si). The phase diagrams and known thermodynamic data were used to calculate activity values for both systems. The activities calculated for the Mg-Ge system agreed very well with those previously published. Partial molar enthalpy values for the Mg-Si systetn were calculated from the phase diagram for the composition region where no experimental values have been reported. THE phase diagram for any system is an important source of thermodynamic data. Steiner, Miller, and Komarek1 have derived equations which permit calculation of the activity in binary systems with an inter-metallic compound! if the liquidus and enthalpy data are known. The thermodynamic properties of the Mg-Ge and Mg-Si systems have recently been determined in this by by an isopiestic method, and it was considered that it would be interesting to compare these directly determined values with those computed from the phase diagram. The basic features of the Mg-Ge and Mg-Si systems are essentially similar. The one intermediate compound present in each system. Mg2X, crystallizes in the antifluorite structure and melts congruently. Raynor4 has accurately determined the temperature and composition of the magnesium-rich eutectic in both the Mg-Ge and Mg-Si systems. Klemm and West-linning5 investigated the entire Mg-Ge liquidus, employing sintered alumina crucibles; the purity of the magnesium and germanium starting materials was not reported. The melt was not stirred, and the temperature was automatically recorded to an accuracy of ±3°C. The authors reported large weight changes due to magnesium evaporation between 50 and 67 at. pct Mg. The Mg-Si system has been studied by a number of investigators, and the results have been compiled by Hansen and Anderko.6 Significant discrepancies exist between the two principle investigations of voge17 and Wohler and Schliephake.8 Two different grades of silicon were used by Vogel, one of 99.2 pct purity and the other quite impure, containing 6 pct Fe and 1.7 pct Al. The magnesium purity was not specified. The melts were contained in graphite crucibles with porcelain thermocouple protection tubes under an atmosphere of hydrogen. Samples weighing 10 g were rapidly heated to 50° to 100°C above the liquidus: held, and then rapidly cooled without stirring. Accuracy was ±1 at. pct which is equivalent to a maximum error in temperature of ±18°C. Wohler and Schliephake used 97.9 pct Mg and 99.48 pct Si. The graphite crucibles contained a stirrer and the 15-g samples were melted under an atmosphere of streaming hydrogen. The samples were chemically analyzed after each run. Because of the scarcity of the data, the impurity of the starting materials, and the resultant uncertainty and inconsistency in the published liquidus values, it was decided to undertake a reevaluation of the Mg-Ge and Mg-Si phase diagrams by thermal analysis. EXPERIMENTAL PROCEDURE Alloys were prepared from 99.99+ pct Mg (Dominion Magnesium Ltd.) with impurities in ppm: 20 Al, 30 Zn, 10 Si, <1 Ni, <1 Cu. <10 Fe; 99.999 pct Ge (United Mineral and Chemical Corp.), and 99.999 pct Si (Wacker Chemie Corp.). All graphite parts were machined from high-density (1.89 g per cu cm) G-grade graphite obtained from Basic Carbon Corp. with a total ash content of 0.04 pct. Boron nitride parts were machined from rods of National-grade H.B.N. boron nitride. All graphite and boron nitride pieces were baked out under running vacuum at 1100°C for 24 hr before us Cylindrical graphite crucibles (1; in. OD, 23/4 in. long, l3/8 in. ID) were tightly closed with threaded graphite covers which had 21/4-in.-long thermocouple wells and 1/4-in.-diam off-center holes for stirrers. The cover and thermocouple well were machined from a single piece of graphite. A stirrer was made from a flat cylindrical graphite plate perforated with five 3/16-in.-diam holes and a 1/2-in.-diam central hole, and was held parallel to the crucible bottom by a 1/4-in.-diam. 4-in.-long graphite rod which screwed into the plate and extended up through a tightly fitting hole in the crucible cover. An iron core enclosed in a glass capsule was attached to the stirrer with an 18-in.-long molybdenum wire, so that the stirrer could be magnetically raised and lowered from outside the system. One crucible and stirrer with essentially the same dimensions given above was made entirely of boron nitride. Chunks of magnesium were premelted, cast into 11/2-in.-diam. rods, and then cut into lengths varying from a to 1 in. A 5/16-in. hole was drilled through the center of each piece to accommodate the thermocouple well and the individual pieces were then cleaned and rinsed with acetone. The total weight of an alloy was 50 to 70 g in the Mg-Ge system and 40 to 60 g in the Mg-Si system. The pure components were weighed to an accuracy

Jan 1, 1969

By A. F. Crawley

The density and viscosity of 1iquid thallium have been measured by absolute methods to temperatures of about 200° and 150°C, respectively, above the melting point. These new data reported, especially density data, do not closely confirm previous work. Density p, in g per cu Cm, is shown to vary linearly with temperaluve t, in °C, according to the equation p = 11.658 - 1.439 X l0-3t. The viscosity data obey the well-known Andrade equation nv1/3 = A exp C/vT , the constants A and C for thallium having values of 2.19 x A and 79.648, respectively. This paper reports some new data for the density and viscosity .of liquid thallium. Measurements of these fundamental physical properties were undertaken as part of a continuing research program at the Mines Branch, Department of Energy, Mines and Resources, Ottawa. Canada. A literature search has revealed that data are so scarce that there could not be a consensus on the true values of the density and viscosity of liquid thallium. To be more specific, there exists only one set of viscosity data&apos; and only two acceptable sets of density data,273 one of which is limited in scope.3 In Liquid Metals Handbook,3 another density study is reported but indications of impurities in the thallium render the results suspect. In this situation, further careful experimentation was required to realize the true density and viscosity of thallium. EXPERIMENTAL METHODS Density. Densities were determined using a graphite pycnometer. The technique and its accuracy have been discussed in earlier papers.4&apos;5 It is considered that experimental data can be obtained which are accurate within +0.05 pct, all sources of random and systematic errors having been evaluated. Density results for thallium were identical whether measured under an atmosphere of argon or a vacuum of 5 x 10-6 torr and, for the most part, the argon atmosphere was used. Viscosity. Viscosity measurements were made in an oscillational viscosimeter by an absolute method—the liquid metal being held in a closed graphite cylinder. Design and operation of the apparatus, constructed in this laboratory, have previously been discussed.6 For thallium, runs were made under a vacuum of about 2 x 10-6 torr. To evaluate viscosity coefficients from the various experimental parameters, the mathematical analysis of Roscoe7 was used. Measurements of the necessary parameters and the accuracy of these measurements have also been discussed.6 The cylinder dimensions were corrected for the anisotropic expansion of graphite, as discussed for density measurements.4,5 It is well-known that thallium oxidizes rapidly and hence a newly machined surface quickly tarnishes in air. The oxide film, however. is nonadherent and is easily removed by rubbing or by solution in water. Hence, immediately before use, both density and viscosity charges were immersed in water, wiped dry, and quickly transferred to the apparatus which was then rapidly evacuated. Specimens removed after determinations were only slightly tarnished and there was no other evidence that tarnishing affected the results. For example, the sharpness of the specimen edges from the containing vessels indicated complete filling by the liquid metal. Thallium of 99.999 pct purity was used in this investigation. Because of its high toxicity care was exercised in handling this material. For example, the melting procedure to prepare machinable ingots was carried out in an open, well-ventilated area, while protective gloves were always worn when handling the solid metal. RESULTS AND DISCUSSION Density. Measurements were made over a tempera-ture range of about 200°C above the melting point. The results are listed in Table I and plotted in Fig. 1. From the graph it is evident that the relation between density and temperature is linear. Such a relation has been observed before in this program for other metals and alloys475 and elsewhere by other workers. A least-squares analysis of experimental data gives the equation: pT1 = 11.658 - 1.439 x 10-3t where p = density in g per cu cm and t = temperature in "C. In Fig. 1, together with the present results, the data of Schneider and Heymer2 in the corresponding temperature range have also been plotted. Evidently, the two sets of data do not agree well, the results of Schneider and Heymer being about 0.6 pct higher. Viscosity. Viscosity data were obtained from the melting point, 303.5°C, up to 457.5"C. The data are listed in Table I and in Fig. 2 the plot of these results demonstrates a smooth curvilinear relation between

Jan 1, 1969

By J. R. Bell, W. J. Childs, J. H. Bucher, G. A. Wilber

A technique for determining recrystallization times as short as 0.10 sec was developed utilizing the "Gleeble", a commercially available testing system designed for the study of short-time, high-temperaLure themal and mechanical processes. The procedure consisted of heating a small tensile specimen to a given temperature of hot deformation, loading to a given reduction in area, unloading, delaying various intervals at temperature, and then reloading- to failure. The magnitude of the ultimate load obtained upon reloading decreased with delay lime as recrys-lallization proceeded. The technique was applied to austenite recrystallization in AISI 1010 and AISI 1010 uith 0.02 pct Cb steels. For each steel the reduction in area given the specimen on the first pull was mainlairred at 30 ± 5 pct and recrystallization times deterntined at various temperatures. The results indicaled a significantly slower rate of recrystallization for the columbium-modified composition, suggested the presence of- a recovery stage in the softening process , and indicated a greatly increased softening rate at a temperatuve where significant allotropic transformation to a partially ferritic Structure could occur. In recent years increasing attention has been paid to the fact that the process of recrystallization of austenite deformed at elevated temperatures is far from instantaneous at many practical hot-working temperatures.1-3 This realization has given rise to such terms as hot cold-working1 or warm-working,2 These terms generally describe processes where the recrystallization rate at the temperature of deformation is slow enough to have an appreciable effect on mechanical properties despite a relatively high deformation ternperature. The mechanical properties of interest can be either the properties at the deformation temperature as in hot-workability studies4 or the room-temperature properties after cooling as in the many recent studies of various thermomechanical processes172 where heat treatment and deformation are intentionally combined to give a unique set of room-temperature properties. Because of this interest in processes where the austenite recrystallization kinetics can be an important variable, the development of quantitative methods of following the course of short-time, high-temperature recrystallization has received increasing attention.l,3,5 The experimental methods to date have, in general, relied upon rapidly deforming the austenite, holding at temperature for various brief intervals, quenching as G.A.WILBER and W. J. CHILDS, Members AIME,are Research-Fellow and Professor, respectively, Rensselaer Polytechnic Institute, Troy, N. Y. J. R. BELL and J. H. BUCHER, Member AIME, are Research Engineer and Research Supervisor, respectively, Graham Research Laboratory, Jones & Laughlin Steel Co., Pittsburgh, Pa. Manuscript submitted March 13, 1968. IMD. rapidly as possible, and then using room-temperature measurements to follow the recrystallization process. Although such methods can be successfully applied to certain alloy steels, the existence of the allotropic transformation during cooling of plain-carbon or low-alloy steels tends to obscure the results. Thus, such room-temperature measurements as hardness and X-ray line widths do not correlate well with the extent of austenite recrystallization before quenching,5 and results based on room-temperature microstruc-tural observations are dependent upon the success in correlating the observed structure with the prior aus-tenitic grain structure.1,3,5 The purpose of the present work was to develop a quantitative method for the determination of short-time, high-temperature recrystallization rates, based on measurements made at the temperature of deformation. EXPERIMENTAL TECHNIQUE The basic technique consisted of heating a small tensile specimen to a given temperature of hot deformation, loading to a given reduction in area, unloading, delaying various intervals at temperature, and then reloading to failure. The data were obtained in the form of traces of load and elongation as a function of time. Due to the high deformation temperature, the strain hardening introduced during initial loading was progressively annealed out with holding time after unloading and the loads obtained upon reloading decreased as this softening proceeded. Although the value of the second load at any Consistent point On the load-elongation curve could have been used as a measure of the degree of softening, the most convenient to use was the ultimate load. The softening indicated by the decrease in the second ultimate load with time is essentially a process of annealing of cold-worked material at a high deformation temperature. Although some recovery grain growth may contribute to such a softening process, it is generally considered that the major softening which must take place to achieve complete removal of substantial Strain hardening will occur by the formation of new, stress-free grains. As the results of this work indicate that essentially complete removal of strain hardening did in fact occur. the primary softening process will be attributed to recrystallization, and specific reference made where it appears that other mechanisms may be contributing to the total observed softening. It would, of course, be of interest to attempt to correlate the results of this work with the actual austenite fraction recrystallized as determined by other techniques. This was not attempted in the present work because it would have required running a large number of additional specimens and, as discussed previously, there is limited assurance that the results would accurately reflect the prior austenite fraction recrys-

Jan 1, 1969

By d&apos, K. Mukherjee, C. R. Antonio, R. J. Maciag, G. J. Fischer

Tensile data indicate that over the range of strain rates 10-5 to 10-1 sec-1 and in the temperature range 298° to 743°K the flow stress at a given temperature may be expressed as: C0 = Cem where m changes abruptly at a critical strain rate of 10-2 sec-1. The Zener-Hollomon parameter was tested and found to be invalid except at temperatures exceeding 700° K. Values of AH calculated for temperatures above 700°K ranged from 30 to 47.5 kcal per g-mole. ThE flow characteristics of aluminum and aluminum alloys as a function of temperature and strain rate have been of interest to various experimenters for many years. Trozera et al.1 determined tensile flow curves for pure aluminum and concluded that the combined effect of temperature and strain rate on the flow stress could be related using the Zener-Hollomon parameter. More recently, Hockett2 proposed a relationship between compressive flow stress, temperature, and true strain rate which could be represented by a surface. Holt et al.3 studied strain rate effects on flow stress in a number of aluminum alloys at room temperature. It was determined that there is a critical strain rate above which a strain rate effect is observed. It was also reported that the strain rate sensitivity was significant in aluminum alloys in the "0" condition only. In a recent review paper McQueen4 has considered a number of mathematical expressions which have been used to describe the relationship between stress, strain rate, and temperature. These expressions have been applied to the flow characteristics of a number of different metals and alloys including aluminum. In the present work the strain rate sensitivity of 7075-0 aluminum was determined in the temperature range of 298° to 743°K. The tensile flow stress at 0.2 pct offset was obtained over a nominal strain rate range of 10-5 to 10-1 sec-1. EXPERIMENTAL Threaded tensile specimens were cut from a single heat of 7075-T6 aluminum. The composition of this heat is given in Table I. The test bars had a gage section 1.5 in. long by 0.250 in. diam and conformed to ASTM specification E-8-57T. After machining, the bars were annealed at 413° ± 10°C for 2 hr. They were then cooled to 260°C in 3 hr, and finally air cooled to room temperature. This treatment is commonly used to produce the "0" condition. Load-time curves at constant crosshead speeds were obtained at various temperatures using an Instron testing machine. Crosshead speeds ranged from 0.002 to 40 in. per min. A three-zone resistance tube furnace was used for the elevated-temperature tests. Temperatures were measured at three points along the gage length by means of suitably placed thermocouples. Each tensile bar was held at temperature for 30 min prior to testing and the maximum temperature variation along the gage length was kept below 1°C. In all, 275 samples were tested and each data point plotted is an average of at least two tests. In many cases the point represents up to six tests. RESULTS AND DISCUSSION Values of the flow stress at 0.2 pct offset at six different temperatures are plotted vs strain rate on log-log coordinates in Fig. 1. Over discrete ranges of strain rate, the data for each temperature fit the expression:

Jan 1, 1969

By A. Rosenzweig, M. M. Karnowsky

The generalized binary diagram of the Au-Sn-Pb system is presented. The chief characteristic is the pseudobinary between lead and AuSn. On the high-gold side of the pseudobinary, four reaction isotherms were found at 363°, 274°, 225°, and 204°C. On the low-gold side of the pseudobinary, three reaction isotherms at 277°, 205°, and 176°C were found. A vertical section from the eutectic solder composition to gold was developed from the isothermal sections generated. METALLURGICAL problems arising from the intentional or accidental formation of Au-Sn-Pb alloys in soldering applications have indicated a need for information on the phase equilibria in this ternary system. The literature indicates that a complete diagram presenting this information has not been prepared. Even the recent excellent work by prince&apos; entitled "The Au-Pb-Sn Ternary System" actually extends only to the AuSn or 50 at. pct Au range. There are more events in the 50 to 100 at. pct Au than in the less than 50 at. pct range. This article by Prince furnished much guidance in preparing this report. Initial efforts with the isopleth from the eutectic solder composition 61.9 wt pct Sn-38.1 wt pct Pb and 0 to 90 wt pct Au indicated that extensions of the work to the whole of the diagram (even if in less detail) were necessary to understand this system. In undertaking the construction of such a diagram, this study used differential thermal analyses (DTA) and metallography with verification and identification of phases by electron microprobe analyses. EXPERIMENTAL PROCEDURE The procedure began with the development of a cell which would be unreactive with lead, tin, and gold, retain its strength to 1100°C, exclude oxygen, and also furnish a suitable well for insertion and protection of a thermocouple to monitor temperature changes in the material. Such a cell would make it possible to reuse the sample should a repetition of determination be desired. Fig. 1 is a photograph of two such quartz cells as finally developed. The specimens have been run many times. The cell is made up of an inner sample bucket and an outer capsule with a thermocouple well which the sample surrounds. The DTA unit was an assembly devised from available instrumentation. The sample holder was a 3-in.-long cylinder of nickel, 2 1/2 in. in diam, fitted securely in a vertical tube furnace. Two holes 7/8 in. in diam were symmetrically located to receive the quartz cells. A dummy cell with nickel powder was used as the reference. The absolute temperature was recorded with a Pt/Pt 10-pct Rh thermocouple with an automatic Kaye ice bath compensator. (Calibration indicated the compensator to be accurate to better than ±0.5° over the 100° to 1000°C range.) The absolute temperature was measured in the sample and recorded on an L&N mul-tirange recorder with a full-scale display of 1 mv and automatic ranging of 99 mv. The differential signal between the sample temperature and the reference temperature was amplified with an L&N microvolt amplifier and recorded on an L&N Speedomax G recorder. Since two charts were obtained, the chart speeds were equalized and each event was noted on the differential chart, and the temperature at that time was obtained from the temperature record.

Jan 1, 1969

By R. Maddin, R. Pond

THERE have been many recent studies of nonequi-librium alloy structures using specimens which have been formed by rapid solidification.&apos; The general methods for achieving nonequilibrium structure utilize high velocity impingement of a liquid metallic droplet(s) and one or more substrates of relatively high heat conductivity. Specimens formed by current popular techniques are small and have various forms of irregular geometry which severely limit their use for many measurements of physical or mechanical properties. As a result of geometric limitations most research has been restricted to X-ray diffraction, electron microscopy, and to a small degree, electrical resistivity. Recently several attempts in mechanical property evaluation have been reported.2,3 A technique for casting large quantities of regular, rectilinear, continuous metallic fibers has existed for a number of years.4 We have utilized this technique with some slight modifications to produce nonequi- librium alloy structures. The apparatus is composed of a small open tube furnace, a pneumatic cage which raises and lowers a graphite ejection mold, and a

Jan 1, 1970

By D. P. Pope, T. Vreeland

Observations of dislocations in zinc using Berg-Barrett X-ray micrography confirm the validity of a dislocation etch for (1010) surfaces. A technique for measurement of the depth in which dislocations can be imaged in X-ray micrographs is given. This depth on (0001) surfaces of zinc was found to be 2.5 µ using a (1013) reflection and CoKa radiation. BUCHANAN and Reed-Hill (B & RH) have recently questioned the ability of a dislocation etch to reveal all of the basal dislocations which intersect (1010) surfaces in annealed zinc crystals.&apos; This etch was developed by Brandt, Adams, and Vreeland who conducted a number of different experiments to check its ability to reveal dislocations.2,3 B & RH prepared (0001) foil specimens for transmission electron microscopy from annealed crystals and observed dislocation densities of about l08 cm per cu cm in the foils, while the etch indicated densities of the order of l04 cm per cu cm in their annealed crystals. As this etch has been used in a number of studies of dislocations in zinc, it is of considerable importance to reassess its validity in the light of the B & RH results. The X-ray work reported here was undertaken to check the ability of the etch to reveal dislocation intersections on (1070) surfaces of zinc. The X-ray technique was chosen for this check because it could be applied to the as-grown crystals with a relatively small amount of specimen preparation. We believe that the possibility of accidental deformation in preparation of the bulk specimens is considerably less than that for thin foil specimens suitable for transmission electron microscopy. Unfortunately, basal dislocations are not visible on Berg-Barrett topo-graphs of (1010) surfaces, which are the surfaces on which the etch is most effective. Therefore, a one-to-one correspondence between the etch and X-ray observations could not be made. Basal dislocations near (0001) surfaces have been observed by Schultz and Armstrong4 using the Berg-Barrett technique, but they did not report the as-grown dislocation density observed in their crystals. We have applied the X-ray technique in this study to surfaces oriented from 1 to 2 deg of the (0001) to determine the basal dislocation density, and have compared this density with that observed using the etch on a (1070) plane of the same crystal. The X-ray observations permit determination of the depth in which basal dislocations can be observed under the diffracting conditions used. SPECIMEN PREPARATION High purity zinc crystals are very soft, so a good deal of care must be exercised in the preparation of observation surfaces. As-grown crystals approximately 2.5 cm in diam and 20 cm long were acid cut into 1.25 cm cubes. A thin slab was cleaved from an (0001) surface to produce an accurately oriented reference surface on the specimen. Some of the cubes were examined in the as-machined condition while some were annealed in argon at 410°C for 2 hr. Heating and cooling rates were less than 2°C per min. Some of the specimens were scratched on a (0001) surface with a razor blade to produce fresh dislocations. Approximately 2 mm of material was acid lapped from one face of a cube to produce a surface oriented between 1 and 2 deg from the basal plane and parallel to the [1210] direction. A (1070) surface was also acid lapped. The lap used a 1 to 3 pct solution of HN03 in water to saturate a soft cloth which was backed by a stainless steel plate. The cloth was moved over the crystal surface at a rate of 20 cm per sec while a normal force of about 4 g was maintained between the cloth and the specimen. As-lapped surfaces were examined as were surfaces which were chemically and electrolytically polished after lapping. The small angle between a lapped surface and the (0001) plane was measured to 0.1 deg using a Unitron microgoniometer microscope (the cleaved surface was used as a reference in this measurement). The microscope was modified so that the intensity of reflected light could be continuously monitored on a meter. This modification produced nearly a ten-fold increase in the reproduceability of orientation readings. OBSERVATIONS The Unitron Microgoniometer observations indicated that the lapped surfaces had a terraced structure with the terraces quite rounded and spaced about 0.1 mm in the [1010] direction. The maximum change in slope between terraces was 0.25 deg, indicating a terrace height of about 0.1 µ. A Unitron measurement of the average angle between (0001) and a lapped surface was checked by micrometer measurement of the specimen and found to agree within 0.1 deg. The Berg-Barrett micrographs using (1013) reflections and CoKa radiation5 revealed subboundaries, short dislocation segments, spirals, and loops near the surfaces which were oriented from 1 to 2 deg of the (0001). Micrographs of surfaces prepared by lapping appeared very similar to those of the chemically and electrolytically polished surfaces. The loops and spirals were not extinct in (1013) or (0002) reflections, indicating that they have a nonbasal Burgers vector. Extinctions of the short, straight dislocations indicated that they belonged to an (0001)(1210) system. Fig. 1 is an example of a micrograph which shows a subboundary, and dislocation segments which are pre-

Jan 1, 1970

By J. Szekely, P. Tarassoff, N. J. Themelis

In a copper converter air enters the bath in the form of turbulent jets. The interaction of these jets with the molten matte is fundamental to the converting process. In the present study, an equation is derived to describe the trajectory of a gas jet in a liquid. Calculated and experimental results for air jets injected into water are in good agreement. The trajectories of air jets in copper matte are predicted. THE air injected through the tuyeres of a Peirce-Smith copper converter emerges into the bath of molten matte in the form of a highly turbulent jet. The air jets affect a number of chemical and physical processes occurring in the converter: i) Converting Rate. It is generally recognized that the production capacity of a converter is limited by the flow of air which can be injected through the tuyeres and by the oxygen efficiency. In turn, the air flow is limited by pressure drop considerations or by the amount of splashing within the converter. ii) Oxygen Efficiency. This depends on the dispersion of the air jet in the liquid bath, and its trajectory through the bath. iii) Mixing. The jets act as mixing devices by transferring momentum energy to the bath; in this way the heat generated by the converting reactions occurring in the jets is distributed through the bath. iv) Refractory Wear. The proximity of the jets, which are centers of heat generation, to the refractories in the tuyere zone may have an important effect on refractory life. Mixing conditions in the bath will also influence refractory erosion. v) Splashing, and Accretion Build-Up. The energy of the jets is not dissipated entirely in mixing the bath. particles of liquid are carried out kith the gas above the surface of the bath in the form of liquid spouts and droplets. These result in the undesirable build-up of accretions on the converter mouth, and dust losses in the flue gas. Despite the importance of the interaction of the air jets and the matte in a converter, very few studies of the fluid dynamics of converting have been reported in the literature. Metallurgists in the USSR appear to have been more concerned with the subject than their Western counterparts. Deev et al.1 studied the interaction of an air jet with aqueous solutions in a converter model and qualitatively determined the tuyere air velocity and tuyere inclination which produced the most favorable results with respect to good mixing in the bath, and minimum splashing. Shalygin and Meyer-ovich2 also examined the air-matte physical interaction both in models and in industrial converters; they concluded that in conventional converting practice, there was no significant penetration of the air jets into the matte layer, and consequently the converting reactions occurred mainly in a zone adjacent to the tuyeres. The behavior of air jets in a converter bath, and the aerodynamic characteristics of tuyeres are discussed at length in a monograph on converting by Shalygin.3 However, the description of the phenomena occurring in the converter bath is largely qualitative. The side-blown Bessemer converter for steelmak-ing is very similar to the Peirce-Smith copper converter. Among the few investigations of the behavior of air jets in the bath of a Bessemer converter are those of Kootz and Gille4 who studied splashing in the course of an investigation on the effect of blowing conditions and converter shape on nitrogen pick-up in Bessemer steel. They found that during blowing standing waves were formed on the surface of the bath; the amplitude of the waves increased with the depth and angle of tuyere immersion until the whole bath moved backwards and forwards causing heavy splashing. Kazanstev5 used a model of a Bessemer converter to obtain correlations between the axial velocity of a gas jet and distance from the tuyere orifice and the Froude number of the jet. shalygin3 used these results to calculate the horizontal penetration of an air jet in a copper converter; the penetration was defined as the distance in which the axial jet velocity decreased to 10 pct of its initial value. However, the rising trajectory of the jet was not taken into account. In the absence of quantitative information on the fluid dynamics of converting, the design of copper converters has been based mainly on operating experience. Such experience tends to vary widely from smelter to smelter., This is reflected in Table I which is based on data compiled by Lathe and Hodnett.6 Aside from a rough, and perhaps obvious correlation between the total air flow and converter volume, Fig. 1, no pattern emerges from the data. For example, tuyere throat air velocities vary from 215 to 465 ft per sec in converters of the same size, for little apparent reason. The air jet energy input per cubic foot of converter volume, which may be taken as a measure of the amount of mixing in the converter bath, also varies greatly. A recent analysis of converter data by Milliken and Hofinger7 has also revealed unexplained variations in operating parameters. It is believed that by gaining a better understanding of the fluid dynamics of converting a more rational basis may be provided for the design of converters. In particular, it is proposed that if one takes into account the desirable criteria of a high converting rate, high oxygen efficiency and long refractory life, there should be an optimum configuration of tuyere air flow for a converter of a given diameter. The present investigation is concerned with the form and trajectory of an air jet in a converter bath. The general theory of turbulent jets has been expounded by Schlichting8 and Abramovich.9 However, most experi-

Jan 1, 1970

By J. J. Frawley, W. J. Childs

Experiments were carried out to induce grain refinement during solidification by applying vibrational energy (freq 20 kc) to small specimens of bismuth, tin, and bismuth-tin alloys. The results show that if the intensity of the applied sound -field is not great enough to fragment the growing dendrites of a pure metal, no grain refinement is observed and the pain size of the dynamically nucleated specimens is the same as the grain size of a specimen statically supercooled the same amount. Bismuth specimens did not show any grain refinement; whereas, the tin specimens did show grain refinement. This phenomenon is the result of the difference in growth habit between the bismuth and tin dendrites. The bismuth-tin alloys showed grain refinement and, in addition, the segregation pattern was changed. THE solidification process is a change in phase requiring the nucleation of the solid phase from the liquid and the growth of this solid phase at the expense of the liquid phase. Since many physical properties and also the integrity of a casting are dependent on the solidification process, understanding and controlling this process are very important.&apos; A good example in the controlling of a cast structure using heterogeneous nucleation theory is the reduction of grain size in aluminum castings by nucleation catalysis.2 This mechanism of nucleation catalysis has been explained by Turnbull.3 Another technique for grain refinement, which has received much attention but the mechanism has not been fully understood, is to vibrate the solidifying melt. Vibrations can be applied to the melt either by vibrating the mold directly or by introducing a vibrating rod into the melt.4-13 Three mechanisms have been proposed to explain this phenomenon: 1) The mechanical fragmentation of the original dendrites that grew into the melt. These crystals or fragmented dendrites act as new growth sites. 2) The nucleation of new grains in the liquid by the generation of very high pressure pulses caused by cavitation in the liquid. 3) The remelting of the dendrite arms during the solidification process. This mechanism is operative only in alloy systems and would be enhanced by stirring or mechanical vibration. The purpose of this investigation was to determine the mechanism that will increase the number of grains when mechanical energy is introduced into a solidifying melt. APPARATUS The unit used to generate the ultrasonic vibrations was manufactured by the Redford Co., and is similar to the one used in ultrasonic soldering. Fig. 1 is a sketch of the major components used for generating ultrasonic vibrations. The crystal transducer assembly consisted of four lead zirconate ti-tanate piezoelectric crystals in an aluminum holder. An acoustical horn, which was fabricated from stainless steel, was attached to the holder by a set screw. The resonant frequency of this unit was 20,000 cycles per sec. A Pyrex crucible, 4 in. in diam and 4 in. high, was contained in a hole in the top of the horn. The piezoelectric crystals changed volume when excited by an electric signal, thereby generating a sound signal which passed through the horn. The crucible was coupled to the horn by a liquid silicone oil. The purpose of the couplant was to transmit the soundwaves from the horn to the crucible. Without the couplant, much of the sound energy would be lost. The energy transmitted was sufficient at the resonant frequency used, so that acoustical cavitation always occurred in the molten metal. The presence of acoustical cavitation was detected by the characteristic hissing sound emitted from the liquid. EXPERIMENTAL PROCEDURE The influence of ultrasonic vibration on the grain refinement of bismuth, tin, and bismuth-tin alloys was studied. These metals were chosen because of their low melting temperature and the relative ease with which they can be thermally supercooled. The following procedure was used for obtaining large amounts of supercooling. Pure bismuth (99.999+), which was received in bar form, was mechanically broken into pieces small enough to be accommodated in a 50 ml beaker. About 200 to 300 g of bismuth and a few grams of SnCl2 as a flux were placed in the 50 ml beaker and melted by induction heating. The melt was held for 20 min at

Jan 1, 1970

By G. L. Fisher, R. H. Geils

The effect of small amounts of columbium (<0.01 to 0.10 pct) on the ?-a transformation occurring during the continuous cooling of a low carbon Ni-Cu steel was investigated. Dilatometer specimens were aus-tenitized at 950" and 1068?C and cooled at 17? and 375 C° per min. Columbium caused a marked depression in the ?-a transformation temperature except when cooling at the slower rate from 950°C. The effec of columbium on the transformation temperature was greater the higher the austenitizing temperature and rate of cooling. A maximum depression of 92 C" was observed. Metallographic examination of specimens of <0.01 and 0.07pct Cb steels heated at 1200°C for 1 hr and cooled at various rates showed that columbium had a major effect on the ferrite morphology. The fer rite in the columbium -free steel remained equiaxed at cooling rates as high as 440 C? per min while the columbium-bearing steel exhibited mixed structures o equiaxed and bainitic ferrite at cooling rates as low as 130 C° per min. The ? grain boundaries in the columbium -free steel provided the ferrite nucleation sites in rapidly cooled specimens. There was a complete absence of nucleation at these sites in the colum bium-bearing steel. It is concluded that columbium depresses the transformation temperature by suppressing ferrite nucleation at the austenite grain bound-aries. In this respect the effects of columbium are analogous to those of boron in low C-Mo steels. It is well known that small columbium additions can substantially strengthen plain carbon steels. As little as 0.02 pct Cb can increase the yield strength of mild steels by 10,000 psi.1 A fine precipitate of CbC has been observed in columbium-bearing steels2 and is generally thought to be responsible for the strengthening. Little attention has been devoted to the effect of columbium on the ?-a transformation. Webster and woodhead3 have studied the effect of columbium on the isothermal proeutectoid ferrite reaction in mild steels. They found similar transformation behavior in steels both with and without columbium additions. However, as the austenitizing temperature increased, the incubation time for the start of the ferrite transformation became longer in the columbium-containing steel. Morrison1 found that the addition of 0.03 pct Cb to a C-Mn steel lowered the transformation temperature by 50 C° during cooling from 1200°C at a rate of 80 C" per min. The strengthening effect of columbium has recently been utilized in an age-hardenable, low-alloy steel containing copper and nickel.4 A small amount of columbium has a substantial effect on the as-rolled strength of this steel. By increasing the columbium level from <0.01 to 0.13 pct the as-rolled yield strength is increased by 15,000 psi. Columbium also significantly lowers the ?-to-a transformation temperature of this steel during continuous cooling from the austenitizing temperature. Because of the low carbon level in this steel (0.05 pct max), it is almost entirely ferritic. Thus, it offers the opportunity of studying the effect of small columbium additions on the proeutectoid ferrite reaction. Of particular interest in this study was the reason for the marked lowering of the transformation temperature by columbium during continuous cooling. EXPERIMENTAL PROCEDURE Materials. The compositions of the steels used in this investigation are shown in Table I. The steels were 30-lb air induction melts. They were forged to 4 by 8 by 1 in. plate at 1230°C, air cooled, and then reheated to 1230°C and cross-rolled in two passes to in. plates. Dilatometry. A Leitz Bollenrath dilatometer was used to record the transformation during continuous cooling from two different austenitizing temperatures. The dilatometer specimens were + in. in diam and 2 in. long. Oxidation and decarburization of the specimens was prevented by maintaining a small positive pressure of dry argon in the dilatometer furnace and by plating the specimens with 1 mil of Cu. For the lowest cooling rate, 17 C" per min, the temperature of the specimen was measured with a Pt-Pt 10 pct Rh thermocouple placed in a & in. diam well in the center of the specimen. During air cooling, 375 C° per min, this method of measuring the temperature interfered with the operation of the dilatometer. However, it was found that the temperature of the specimen could be measured accurately by placing a thermocouple in an identical specimen in a holder adjacent to the one being used to operate the dilatometer mechanism. The dilation-temperature curves were recorded on photographic film and then converted to volume percent ferrite-vs-temper-ature curves. The cooling rates obtained with the dilatometer are shown in Table 11. Cooling rates of

Jan 1, 1970

By R. A. Graham, R. W. Rohde

The effect of hydrostatic pressure upon the austenite start temperature of a commercial Fe-28.4 at. pct Ni-0.5 at. pct C alloy has been determined. For pressures to 20 kbar, the austenite start temperature decreased from its atmospheric pressure value of 380°C at the rate of about 4°C per kbar. These data are analyzed by two different thermodynamic approaches; first, considering the transformation as an isothermal process, and second, considering the transformation as an isentropic process. It was found that both these approaches fit the experimental data equally well. The effect of hydrostatic pressure upon the austenite start temperature is best described by considering the mechanical work done during the transformation as that work obtained by multiplying the applied pressure with the gross volume change of the transformation. It is widely recognized1 that strain has an important effect on the initiation of martensitic transformations.* For example, the martensite start tempera- *In this paper, use of the term martensitic transformation implies the reversal of martensite to austenite as wen as the formation of martensite from austenite. ture, M,, may be increased by plastic deformation. Similarly, plastic deformation is observed to lower the austenite start temperature, A,. The effect of uniaxial stress on the M, of iron-nickel alloys has been studied by Kulin, Cohen, and Averbach.2 They found that the martensite start temperature was significantly changed by stresses well within the elastic region. Moreover, the effect of tensile and compres-sive stresses differed. These effects were explained in terms of the interaction of the applied stress with both the dilational and shear components of the transformation strain. The magnitudes of the influence of uniaxial tension, compression and hydrostatic pressure on Ms were measured in 30 pct Ni 70 pct Fe by Pate1 and Cohen.3 Their thermodynamic calculations and similar calculations by Fisher and Turnbull4 predicted the experimental results when the transformation was assumed to occur isothermally at some fixed driving force. This driving force was assumed to be supplied by a combination of the chemical free energy difference between the austenitic and martensitic phases and the work performed during transformation by the applied stress. More recently, Russell and winchel15 reported the effect of rapidly applied shear stress on the reversal of martensite to austenite in iron-nickel-carbon alloys. They performed a thermodynamic analysis of this transformation based upon the assumption that the re- versal occurred adiabatically. They concluded that the applied shear stress did not significantly interact with the transformation strain and thus did not assist in inducing the reversal. Rather they concluded that the reversal was effected by localized strain heating which resulted from the gross local shear deformation of the experiment. In either the adiabatic or isothermal analysis it is necessary to compute the work performed by the interaction of the applied stress and the transformation strains. In the case of hydrostatic pressure this interaction has been treated by two different methods. In either case the applied pressure is assumed to remain constant during the transformation. In one treatment the applied pressure is assumed to interact directly with the dilatational strain associated with the formation of an individual martensite plate.3&apos;4 This local strain has been measured at atmospheric pressure in iron-nickel alloys by Machlin and Cohen.6 In the above treatment this local strain is assumed invariant with temperature and pressure changes. In the other treatment the applied pressure is assumed to interact with the gross volume change of the transformation.7,8 The usefulness of this latter treatment has been demonstrated by Kaufman, Leyenaar, and Harvey7 who calculated the effects of pressure upon the martensite and austenite start temperatures of Fe-10 at. pct Ni and Fe-25 at. pct Ni alloys. Excellent agreement was obtained between their calculations and their experimental data on an Fe-9.5 at. pct Ni alloy. However, this treatment suffers from the fact that the data required to calculate the volume change of the transformation (i.e., the initial specific volumes, the thermal expansion and compressibility data for both the austenitic and martensitic phases) is, in general, not available for any material except pure iron. Thus the calculations of Kaufman et al.7 were necessarily performed by assuming that the volume change of the martensitic transformation in the iron-nickel alloys was that same volume change occurring during the a-? transformation in pure iron. While this approximation may suffice for very dilute alloys it is likely to be inaccurate in high nickel alloys. We have performed measurements of the effect of hydrostatic pressure to 20 kbar on the A, temperature of an Fe-28.4 at. pct Ni-0.5 at. pct C alloy. The composition is similar to the alloy used by Pate1 and Cohen3 to determine the effect of pressure upon the M, temperature. The present measurements permit calculation of the interaction between the applied pressure and the transformation strain. Additionally, measurements have been made which allow precise determination of the gross volume change of the transformation. The data allow direct comparison between the alternate hypotheses of the interaction between the applied pressure and a dilatational transformation strain characterized by either the formation

Jan 1, 1970

By A. E. Jenkins, O. C. Roberts, D. G. C. Robertson

Using an inverted-cone coil at 450 kHz, it has been possible to levitate iron (FeS), cobalt (CoS), and nickel (NiS) sulfides. Important nontransition metal sulfides such as ZnS, PbS, and Cu2S have proven impossible to levitate although Cu-Fe-S ternary alloys containing 30 wt pct S and up to 10 wt pct Cu, and Cu-Co-S and Cu-Ni-S ternary alloys containing 30 wt pct Cu have been levitated. The levitation technique has been used in preliminary experiments on the vaporization from liquid sulfides and the reaction of liquid metal-sulfur alloys with oxidizing atmospheres. The course of the reactions with pure oxygen were followed using highspeed photography and two-color pyrometry. ELECTROMAGNETIC levitation is now established as a basic laboratory technique in high-temperature research but its application has been restricted mainly to metals and alloys. Applications have included alloy preparation,&apos; metal purification,2&apos;3 determination of liquid metal densities and emissivities,4,5 and studies of metal supercooling,4 alloy thermodynamics,6 and vaporization phenomena.7-9 The application of the technique to compounds has not been considered previously. The successful investigation of the reactions between dilute iron alloys and oxidizing atmospheres10&apos;1 has prompted the current physico-chemical studies involving levitated metal sulfide drops and flowing inert or oxidizing atmospheres. This paper presents the results of such a study and provides a basis for future studies involving a wide range of other compounds of metallurgical interest. The successful levitation of many metal sulfides and mattes provides a method of studying the oxidation reactions fundamental to flash-smelting and similar pyrometallurgi-cal operations under closely controlled laboratory conditions. In addition the system allows the use of a controlled atmosphere (e.g., a gas stream of a certain H2/H2S ratio) with a particular chemical potential to study the relevant thermodynamic equilibria or the mass transfer processes between the atmosphere and the levitated drop under conditions where the hydrodynamics of the system can be closely defined. The optimum frequency for the levitation melting of metals in an inverted-cone coil type inductor is within the radio frequency range 400 to 500 kHz. At frequencies lower than 10 kHz the rate of heat generation is usually insufficient to melt the levitated charge&apos; or where melting is achieved, "dripping" from the charge is encountered.&apos;&apos; At frequencies above 2 mHz the levitation force decreases. Metals, alloys and preheated elemental semiconductors such as germanium and silicon, have been levitated but the levitation of only a few metal compounds has been reported. Jostsons13 and the authors have levitated liquid titanium-oxygen alloys containing 50 at. pct 0 while clark14 has reported the levitation of mixtures of FeS and MnS for short periods. With a "cold crucible" inductor sterling15 has melted ferrites by preheating them by induction in a 4 mHz field and melting at a lower frequency. However this second type of inductor has been designed purely for the melting of materials without contamination; there is only a small gas film between the charge and the inductor and the electromagnetic levitation effect is of secondary importance. For this reason further discussion will be restricted to the use of the coil type inductor. The assessment of the suitability of a particular metal compound for levitation is based upon the following two criteria: i) thermal stability, and ii) physical "levitability". In this paper these two criteria will be considered separately. The thermal stability of a solid or liquid metal compound with respect to a gaseous environment depends upon its chemical reactivity with that environment or, in the case of an inert atmosphere considered here, its volatility. The physical criterion as to whether or not a particular compound can be levitated is based upon a comparison between those physical properties of the compound determining "levitability" which are defined by the fundamental equations of levitation theory as developed by Okress et a1.,16 and the properties of the metals. Since it is not practical to cover the vast field of metal compounds, further discussion will concentrate on the metal sulfides but the treatment would be applicable to any metal compound. THE THERMAL STABILITY OF METAL SULFIDES The temperatures usually encountered during levitation in inert atmospheres cover the range 1400" to 2000°C. The stabilities of the condensed states of the sulfides under these conditions are considered in relation to the periodic classification by reference to Table I. Two general classes of sulfides emerge. The solid sulfides of elements of group IIB and of groups further to the right are volatile while those sulfides of group IB and of groups further to the left are nonvolatile solids. The sulfides described as volatile may be dismissed as unsuitable for levitation. The stabilities of the more favorable nonvolatile sulfides under the anticipated conditions must be studied more closely From Table I it is seen that the alkali metal sulfides exist as liquids in the temperature range of in-

Jan 1, 1970

By D. T. Camp, J. A. Clum

WITH experience, the indexing of back-reflection Laue patterns for cubic crystals is usually a straightforward matter. However, for noncubic systems where in general tables of interplanar angles are not available or when inexperienced personnel are involved, properly indexing a crystal is normally a tedious, time-consuming affair. The authors have written a digital-computer program which calculates and prints out a table of interplanar angles for an arbitrary crystal structure and then systematically searches through this table attempting to obtain a consistent fit to back-reflection Laue data supplied by the user. Of course it is possible simply to calculate a desired set of interplanar angles should this be the only requirement. The program was originally written in ALGOL for use on a Control Data G-21 computer and a preliminary version is described elsewhere.&apos; A version in FORTRAN TV which has been run on an IBM 7040 and one in FORTRAN II run on an IBM 1620 are also available. While it is not the purpose of this communication to describe the program in detail, an indication of how the program operates may help one to decide whether the program would be useful under particular circumstances. The hypothetical example chosen involves the indexing of the zinc crystal which has a hexagonal structure and a c/a ratio of 1.856. Input data for this example consists of only nine cards: The first card controls the list of families of planes to be considered. If the Miller indices of a prospective family are (h k 1), the first digit places a limit, in this case 3, on the absolute values of any individual index. The second digit limits the sum (h +k + l + 1), in this case to 5. Therefore the families (013) and (112) are considered but the family (122) is not. All systems, including the hexagonal, are treated using three-digit Miller indices. The second card contains the crystallographic parameters required to define the system. The first digit is 0 if the system is rectangular, that is all angles are 90 deg. If the system is nonrectangular, as in this example, the digit 1 so indicates. The next three values are the lengths of the sides of the reference cell, a, b, c. The final three entries on the card are the angles, a, 8, y between the sides. The digit 0 on the third card indicates that more data follows, the digit 6 shows that a set of six planes is to be indexed, and the value 2.0 indicates that agreement between a tabulated angle and an input angle is considered adequate if their absolute difference is less than 2 deg. The fourth card lists the measured input angles. a12 = 38 deg, a13 = 24 deg, and so forth. More input angles are listed on cards five to eight with the latter giving the input angle 058 = 40 deg. The final card in this series indicates by the digit 1 that no more data is to be processed. The program operates in the following manner: 1) The input data from cards 1 and 2 is read, thereby indicating the crystal system to be examined and the crystallographic parameters of the particular crystal to be indexed. 2) A table of interplanar angles is generated. 3) The input angles contained on cards 4 to 8 are read. 4) The measured input data is systematically compared with the generated table of standard angles. All combinations of poles whose interplanar angles compare with the requisite, specified accuracy are printed out. If no adequate fit is found an indication of this is printed. A typical line from the generated table of interplanar angles is: (001) - (111) 74.92 64.99 It can be shown that in the Miller-Bravais system the first value corresponds to the angles between (0001)-(1121) and the second to that between (0001)-(1011). This particular set of data gave the following result for the planes 1 to 6: (011) (110) (121) (111) (112) (010) The ALGOL version also has the option of simply providing the Greninger-chart coordinates ? and 6

Jan 1, 1967