By R. C. Hall

In the present work, experiments determined the effect of the order-disorder reaction near the Fe,Al composition on the magnetic anisotropy and magnetostriction of single crystals: A material which is more difficult to magnetize in one direction than in another is anisotropic, that is, the ease with which ferromagnetic materials may be magnetized in different crystallographic directions determines the anisotropy. Two investigators have estimated the anisotropy of the aluminum iron alloys from poly-crystalline data;1,2 however, these estimates should not be considered to be reliable. Siege1 made two accurate measurements of the first anisotropy constant* from single crystals of 4.0 wt pct aluminum sotropy throughout the ferromagnetic aluminum iron system have been described. These results were obtained from single crystals which were slowly cooled and, hence, ordered near the Fe3Al composition.4 Magnetostriction is the change in length per unit length resulting from applying a magnetic field to a ferromagnetic material. For the purpose of this report, the saturation magnetostriction was measured. This is the maximum change in length per unit length resulting from an applied magnetic field large enough to saturate the material in a given direction. This magnetostriction has been determined for single crystals of the ferromagnetic aluminum-iron system.' The crystals near Fe3Al were also ordered. PREPARATION AND TREATMENT OF SINGLE CRYSTALS Single crystal bars were grown from the melt.' The raw materials for these crystals were iron and aluminum of 99.9 and 99.99 pct purity, respectively. From the bars, crystals in the shape of circular

Jan 1, 1959

By M. L. Bleiberg, L. J. Jones

THE changes induced in metals by subjecting them to heavy particle bombardment have received widespread attention in recent years and results of such investigations have been reviewed by Slater, Dienes, Seitz, Siegel, and Seitz and Koehler.1-5 Of particular significance are the property changes that occur in uranium-base alloys due to neutron bombardment. These changes are generally very severe since fission occurs within the sample, resulting in the formation of heavy, highly energetic fission fragments, as well as additional neutrons born in fission, which serve to intensify the damage generally associated with fast neutron bombardment of nonfissionable metals. The property changes in uranium and uranium alloys due to neutron bombardment have been summarized by Paine and Kitte16 and Billington.7 It has also been shown that neutron bombardment of

Jan 1, 1959

By C. Feng, C. Elbaum

AN investigation of the fracture plane of titanium, containing 0.5 wt pct to 1 wt pct 0, was recently carried out by fracturing large-grain specimens in a tensile jig at room and liquid air temperature. The experiments were carried out on strip specimens 3 to 5 mm wide, 2 mm thick and about 100 mm long. The specimens consisted of several grains, each occupying the entire cross section of the strip and extending over a length varying from 5 to 20 mm. These specimens were prepared by a method described elsewhere.' The identification of the fracture plane was possible in twelve of approximately thirty crystals investigated. In some cases severe local distortion took place near the fracture and prevented identification of the fracture plane. On, at least, three occasions the fracture propagated in a helicoidal

Jan 1, 1959

By E. Buehler

THE floating zone refining technique'-4 has provided a new experimental approach to the purification of many reactive materials especially those with high melting points. The method avoids the use of a crucible and at the same time it provides a favorable environment at the freezing interface for the growth of single crystals. The physical properties of refractory metals such as molybdenum and tungsten have long been of interest from a fundamental point of view and because of their widespread use in vacuum electronics. Single crystals are often desirable for study. Prior to the introduction of zone melting, single crystals of these metals were usually grown in the solid state at temperatures slightly below the melting point by strain annealing3 or by the application of a moving temperature gradient. Such techniques were mostly successful on wires, ribbons, or rods having small cross-sectional areas. Recently, larger samples of tungsten, molydbenum, tantalum, columbium, and rhenium were melted by a floating zone process which employed electron bombardment heating.10 Single crystals were obtained in many instances

Jan 1, 1959

By J. Gurland

A method of measuring the degree of contact between grains of 1 phase in multiphase alloys is derived. It is shown that the number and the areas of contacts between grains can be determined by metallographic analysis. Relations between the area of contact, the dihedral angle, and the mean free path of spherical grains are developed. It is often desirable to interpret the mechanical behavior of alloys in terms of structural features observed under the microscope. A quantitative description of microstructures of multi-phase alloys requires consideration of geometrical and topological factors such as the amount, size, and shape of grains and the continuity of the constituent phases. The number and dimensions of grains may be metallographically determined by applying the methods described by Smith and Guttman1 and by Fullman2 in their papers on the measurement of particle size and internal boundaries in opaque bodies. The present work intends to show that the same methods can be used to evaluate some of the parameters of phase continuity; namely, contiguity, number of contacts, and areas of contact of grains of 1 phase. Application of these concepts may be found in such problems as the calculation of electrical conductivity of 2-phase alloys, or the evaluation of the length of fracture path through grains of a brittle phase more or less dispersed in a matrix. I. DEFINITION The following definitions and derivations are based on 2-phase alloys, of which the units of the microstructure are grains. Contiguity is defined as the average fraction of surface area shared by 1 grain of a phase with all neighboring grains of the same phase. In a 2-phase alloy of constituents A and B, the contiguity of phase B is given by: where Cb is the contiguity of phase B aBß is the average area of contact between a grain of phase B and adjacent grains of phase B, aAB is the average area of contact between a grain of phase B and adjacent grains of phase A. The contiguity is a measure of the average degree of contact between grains of phase B in the 2-phase mixture. The ratio varies from 0 to 1 as the distribution of phase B changes from a completely dispersed to a fully agglomerated structure. Smith and Guttman1 have shown that the relative areas of 2 kinds of interfaces in a volume are directly proportional to the number of interfaces of each type intersected by a random line. The lines can be drawn on metallographically prepared surfaces as long as these are random sections through the sample. The contiguity ratio of phase B then becomes: Cb = 2NBB/NAB + 2N BB [2] where: NBB is the number of interfaces between grains of phase B intersected per unit length of random line. Nab is the number of interfaces between grains of phase B and grains of phase A intersected per unit length of random line. The factor 2 arises in Eq. [2] because each interface B-B is associated with 2 grains of B-phase, whereas the interface A-B involves only 1 grain of B-phase. The calculations of contiguity do not require any assumption as to volume fraction, particle size, or particle shape. Fullman2 gives an expression for the determination of the mean free path between particles. The mean free path PB between grains of phase A, i.e., through grains or agglomerates of phase B, may be found from the relationship: PB =2fB/NAB [3] where fB is the volume fraction of phase B. The calculation of the mean free path is independent of grain shape and grain size distribution. The calculation of the number of contacts and of contact area requires assumptions of grain shape, grain size, and contact shape. In the case of uni-

Jan 1, 1959

By T. F. Archbold, R. E. Grace

The use of interference colors is the simplest experimental way to determine the approximate film thicknesses of oxides formed on liquid metals. A large amount of data under various conditions can be obtained easily and quickly. The oxidation of liquid lead has been studied by several investigators,1-5 but all of these studies have been on thick oxide scales. The purpose of- this work was to investigate the range 0 to 2000A film thickness. By using electron diffraction, Jenkins concluded that the surface of the film on molten lead is yellow orthorhombic PbO with the (110) planes parallel to the surface. This was confirmed by Shimaoka and Yamai7 who also used electron diffraction from the melting point of lead to 730°C. The rate of oxidation of pure liquid lead in air was measured in the temperature range 453" to 643°C by observing the rate of formation of interference colors on static lead baths. Approximately 170 g of lead (99.999 pct) was placed in a refractory dish having a working surface of 13.8 sq cm. This crucible was placed in a deep-well resistance furnace open to the atmosphere. The times at which the various interference colors appeared, after wiping the molten metal surface clean, were determined at 453", 533°, 600°, and 643°C. Elapsed times were determined with a stopwatch and all colors were estimated by eye. Bath temperatures

Jan 1, 1959

By E. S. Bartlett, D. N. Williams

QUANTITATIVE values for the oxidation rate of unalloyed molybdenum in air at temperatures above the melting point (1460°F) of the characteristic oxide are contained in the literature as a result of previous investigations. Lustman' reported values corresponding to 0.36 in. penetration per day (IPD) at 1500 and 1600°F in still air, noting essentially no variation in rate with temperature. Jones, Spretnak, and Speiser' reported values corresponding to 0.14 and 0.13 IPD at 1500 and 1800°F, respectively, in still air, attributing the decreased oxidation rate at higher temperatures to a lesser accumulation of the corrosive molten oxide on the surface at the higher temperature as a result of increased volatilization rate. Harwood3 ecently summarized work in the field, presenting generalized data corresponding to 0.48 to 0.96 IPD at 1800°F and 0.55 to 0.83 IPD at 1700°F in slowly flowing air. In a recent program at Battelle, it became desirable to know more about the characteristic oxidation behavior of molybdenum under varying conditions of temperature and atmosphere. Using oxidation-test apparatus designed for dynamic, continuous recording of weight change during testing,' values for the oxidation rate of molybdenum were obtained at temperatures from 1400 to 2150°F. In addition the effect of air flow on the oxidation rate was studied briefly at temperatures of 1600, 1800, and 2000°F. Exhaust of the contaminated atmosphere from the oxidation chamber was effected by an impeller pump attached to a 3/16-in.-diam opening in the oxidation chamber. The volumetric exhaust rate (cubic feet per hour) was normally maintained slightly in excess of the input rate to avoid condensation of MOO,,' on the sample suspension rod. The entering atmosphere was preheated prior to admission to the oxidation chamber by a 1 1/2-in.-diam cup packed with shredded asbestos. The experimental data are presented in Table I. Comparing conditions 2 and 3 (taking into account the temperature difference) and conditions 8 and 9. shows that in the absence of forced exhaust an atmosphere of moving air results in greater oxidation rate than a stagnant atmosphere. The use of forced exhaust, as shown by comparing conditions 3 and 4 and conditions 14 and 15: resulted in an even greater increase in oxidation rate. By virtue of the size of the atmosphere input and exhaust openings, it was calculated that the exhaust velocity was about 60 times that of the input velocity for essentially equal volumetric flow rates. Because of the proximity (about 3/4 in.) of the exhaust port to the specimen, it is logical to assume that cleansing of the atmosphere immediately surrounding the specimen was accomplished much more efficiently by the exhaust flow than by the input flow at a constant-volumetric flow rate. Also, it can be seen by comparing conditions 4 through 7 and conditions 11 through 13 that increasing the rate of atmosphere flow (by increasing input velocity with a proportional increase in exhaust velocity) above some optimum value has little, if any, further effect on the oxidation rate. These results suggest that there is a maximum oxidation rate for molydenum at a given temperature which is obtained when conditions are maintained such that the partial pressure of MOO3 in the atmosphere surrounding the specimen is at a low value. By controlling the partial pressure of MOO, surrounding the sample, it is possible to control the rate of volatilization of MOO:, from the surface. This, in turn, affects the rate of oxidation, since the thickness of the MOO3 layer determines the amount of oxygen which will be able to reach the reaction surface.' When the liquid oxide layer is less than some critical thickness, i.e., when the volatilization rate is high, enough oxygen is transported to the active surface to permit oxidation to proceed at the maximum rate allowed by the kinetics of the oxidation reaction. However, if the volatilization of MOO,, is suppressed, the thickness of the layer of MOO3 on the surface increases, and the diffusion of oxygen through the oxide layer becomes the rate-controlling step in the oxidation process. The lack of agreement between the present results and those of previous investigators is presumed to be due to differences in removal of the oxidation product (Moo,) from the immediate vicinity of the sample. By comparing conditions 1, 5, 10, 12 and 14, it is seen that when forced exhaust was used the oxidation rate of molybdenum increased with increasing temperature. A rapid increase was observed between 1400 and 1600°F, attributable to the effects

Jan 1, 1959

By A. H. Daane, J. J. Hanak, F. H. Spedding

IN the study of the rare earths at the authors' laboratory, methods have been devised for preparing pure rare earths and many of their properties'- have been determined. Very little information is found in the literature on the properties of europium metal, which is the scarcest of the naturally occurring rare earths. Since we have recently prepared europium in appreciable quantities, we are in a position to describe the method of preparation and some of the properties of this metal. Metallic europium was first prepared by Klemm and Bommera who heated a mixture of potassium and EuC1, in vacuo, and obtained a mixture of europium metal and KC1. Trombe4 electrolyzed a molten salt bath containing NaC1, KC1 and EuC1, and collected the europium in a molten cadmium electrode as a cadmium alloy. The cadmium was subsequently removed by distillation but the properties of the residue indicate that pure europium was not obtained. McCoy attempted to prepare europium by distilling mercury from europium amalgam, but the stability of the Eu-Hg intermetallic compounds prevented a complete separation of the two elements. The preparation of very pure europium was suggested by previous work in this laboratory1,4 in which ytterbium and samarium were prepared by heating the respective sesquioxides with lanthanum metal turnings to 1450°C in vacuo and distilling ytterbium and samarium from the mixtures. Subsequently, small test experiments showed that europium also could be prepared by this method. A more detailed version of this method was used in the work described in this paper. Klemm and Bommer3 found by X-ray analysis that the metal had a body-centered cubic (bcc) structure with a lattice constant a, = 4.582 ± 0.00A (converted from kX units), with a bulk density of 5.30 g per cu cm. They found europium to be weakly ferromagnetic. Spedding, et al,7 found a,, to be 4.606 ± 0.001A. Barrett' showed that the bcc structure persists throughout the temperature range 5 to 3000K with a, at 5, 78, and 300°K being 4.551 ± 0.003, 4.551 ± 0.004 and 4.577 ± 0.001A, respectively. Trombe1 described europium as being iron gray, malleable, about as hard as neodymium and not attacked by cold water. He estimated the melting point to be between 1100 and 1200°C. Previous work in this laboratory indicated that the pure metal corrodes rapidly in air and reacts with cold

Jan 1, 1959

By C. F. Lucks, W. D. Wood, H. W. Deem

Electrical ad thermal-conductivity measurements have been made on titanium and 6 titanium alloys. The following expression was derived for calculating thermal conductivity from electrical conductivity: K = 0.626 s T x 10-8 + 0.00497 where K = thermal conductivity, cal sec-1 cm-2 cm0C-1 s = electrical conductivity, ohm-]cm-1 T = temperature, deg Kelvin This expression gives calculated thermal conductivities that are not in error by more than 10 pct from the experimental values for A-55 titanium and the 6 alloys measured; namely, A-110AT, C-110M, C-130AM, Ti-6A1-4V, Ti-140A, and Ti-155A, which are representative of the presently available commercial a and a-ß titanium alloys. THERMAL conduction in a gas, liquid, or amorphous solid is accomplished by energy diffusion from molecule to molecule, a relatively slow process. For this reason, such materials have a low thermal conductivity. When a material is crystalline, there is in addition a heat transfer by a vibratory motion of the crystal lattice. It is the contribution of this lattice conduction that makes a crystal a much better conductor than a gas, liquid, or amorphous solid. Lattice conduction, however, does not account for the relatively enormous thermal conductivity of a metal. This is explained by the freedom of movement of valence electrons. These valence electrons drift in a metal in a direction toward a drop in electrical potential and, to a lesser degree, in the direction of a temperature drop in the metal. Since both the electrical and thermal conductivities of a metal depend upon the presence of free electrons, there should be some relatively simple relation between the two. Wiedemann and Franz in 1653 first discovered an approximate empirical relation between the electrical and thermal conductivities of metals at the same temperature. This ratio varies appreciably with temperature, and Lorenz later showed that by adding a temperature factor to the Wiedemann-Franz ratio the value of K/(s T) is constant, where K is the thermal conductivity, a the electrical conductivity, and T the absolute temperature. This Lorenz constant shows a greater variation for alloys than it does for pure metals, the ratio increasing slightly as the proportion of alloying elements increases. It has been found that a closer correlation between electrical conductivity and thermal conductivity can be obtained by means of an equation of the form K - A s T + B [1] where A and B are constants. In this equation the term AsT is the contribution of electronic conduction and B is the contribution of lattice conduction to the total thermal conductivity. EXPERIMENTAL MEASUREMENTS Electrical-resistivity and thermal-conductivity measurements on titanium and 6 titanium alloys serve as the basis for determining an equation of the K = AsT + B type for titanium alloys. Specimens—Table I shows nominal compositions of the 7 metals on which electrical and thermal conductivities were measured. The electrical and thermal-conductivity specimens for each alloy were taken from stock of the same heat and usually from adjacent sections of the same bar. All of the metals measured were in a mill-annealed condition. Methods—Electrical-resistivity measurements

Jan 1, 1959

By J. R. Mihalisin

THE application of electron-microscopic techniques to the study of high-temperature alloys has met with considerable success.' This is due, in part, to the submicroscopic nature of the phases present in this type of alloy making high resolution methods necessary. Among the newer electron-microscopic techniques, the extraction replica technique' has proven to be of great value. This method allows phases to be examined in situ in the microstructure and permits their identification by means of electron diffracticn. This technique eliminates the main disadvantage in using electrolytic extraction of residues as a means of phase identification; that is, the uncertainty of relating constituents identified in the residue to what is observed microscopically. In the course of work relating microstructure to physical properties in high-temperature alloys, it was found that the formation of grain-boundary carbide phases and intragranular precipitation of an age-hardening phase greatly influence strength and ductility at high temperature. In particular, it was found that the formation of a unique type of precipitate in Nimonic "80" (a nickel-chromium-aluminum-titanium type superalloy), termed cellular or discontinuous precipitate, at grain boundaries generally results in poor ductility at high temperature. However, this mode of precipitation can be avoided by proper heat-treatment. It was assumed that this precipitate was either a carbide or age-hardening type of phase. Using various etching procedures with the extraction-replica technique, it was found to be possible to extract the carbide and age-hardening phases preferentially in this type of alloy. Previous work has shown that the age-hardening phase can be extracted from superalloys merely by

Jan 1, 1959

By E. A. Peretti

BEFORE embarking on a detailed investigation of the system indium-antimony-bismuth, experiments were carried out to determine the existence of quasi-binary sections. The bordering binary systems are known1 and show the occurrence of three intermetallic binary species corresponding closely to InSb, InBi and In2Bi. Attention was focused on the low-indium end of the ternary diagram where the possible quasi-binary sections, excluding ternary compound formation, would involve the pairs: InSb-Bi, InBi-Sb and InSb-InBi. The latter pair revealed itself as a true quasi-binary, so it was investigated fully by thermal analysis, x-ray and microscopic examinations. All compositions were made by proper combination of three elements involved. The indium had a guaranteed purity of 99.97 pet; the antimony contained 99.99 pet Sb, and the bismuth had a purity of 99.99 pet. Alloys were made by melting together antimony, bismuth and indium in evacuated, sealed pyrex-glass tubes at a temperature of 600°C with vigorous agitation. The melts, weighing about 80 grams, were allowed to freeze in the sealed tubes and finally were transferred to glass tubes for the taking of cooling and heating curves. A protective atmosphere of helium was used, and the melts were stirred mechanically while cooling at rates of from 0.5 to 3°C per min. Temperatures were measured with a calibrated chromel-alumel thermocouple and were recorded graphically on a Minneapolis-Honeywell extended-range recorder working in conjunction with a Leeds and Northrup type K-2 potentiometer. Conventional polishing techniques gave satisfactory results in preparing specimens for microscopic examination. Etching was carried out with Vilella's reagent or aqueous mixtures of chromic oxide with either nitric acid or sulfuric acid plus dichromate. Conclusions deduced from the thermal analysis and microscopic examinations were confirmed by X-ray photograms using Co-K alpha radiation. The phase diagram is shown in Fig. 1. The liqui-dus consists of an uninterrupted line running from the freezing point of InSb (525°C) to a eutectic point experimentally indistinguishable from the freezing point of InBi (110°C). X-ray patterns of the InSb show a slight expansion of the lattice with the addition of InBi, and microscopic work indicated the solid solubility of InBi in InSb to be less than 0.5 pet at room temperature. Acknowledgment We wish to thank the Indium Corporation of America for the loan of the indium used in this investigation. References 1 E. A. Peretti and S. C. Carapella, Jr.: Trans. ASM., 1949, vol. 41, P. 947. T. S. Liu and E. A. Peretti: Trans. ASM, 1952, vol. 44, p. 539. Metals Reference Book, vol. 1, 2nd ed., AIME, p. 345.

Jan 1, 1959

By W. Rostoker, R. F. Domagala, R. P. Elliott

The phase equilibria of the Hg-Th system over the composition range 0-100 pct Th and temperatures up to 1000°C have been studied for a small-volume, closed system. The solubility of Th in liquid Hg is about 5 pct at 300°C and decreases sharply with decreasing temperature. Two intermediate phases occur, Hg3 Th and HgTh. The structures of these are hexagonal (nonideally close-packed) and face-centered cubic, respectively. The HgTh phase decomposes eutectoidally at 400°-500°C. The solubility of Hg in solid thorium seems to be negligible. AFULL-phase diagram for this system would have to be defined on temperature-composition-pressure co-ordinates. This paper describes the pseudo phase diagram of a closed system, that is, where the alloy enclosed in a small volume equilibrates with a vapor pressure of mercury dictated by composition and temperature. Because of the experimental difficulties in studying a system of this nature, many of the phase relations can only be sketched. Alloy Preparation Alloys over the full range of composition were made from triple distilled mercury and one of two grades of thorium. For the bulk of the work, a calcium-reduced metal in sintered pellet form of reported 99+ pct total thorium content was used. Arc-melted specimens of this thorium gave a hardness of 135 VPN. The microstructure showed small primary dendrites of ThO2. A number of alloy compositions were made with a high-purity, iodide-decomposition thorium metal. The are-melted hardness of a button of this material was 35 VPN. Although the microstructure of the arc-melted specimens showed no dendrites of ThO2, there was definite evidence of an unidentified phase enveloping the grain bound-aries. There were no distinguishable differences between the constitution of alloys made with the two grades of thorium metal. Under normal conditions thorium is not wetted by liquid mercury. The film of ThO2 on all thorium metal cannot be penetrated by either liquid or vaporous mercury. It was therefore necessary to comminute thorium in the presence of mercury under such conditions that oxide films could not reform on the newly exposed metal surfaces. This was accomplished by the use of a high-speed, carbide-tipped rotary cutter incorporated in a chamber purged with argon and connected at the bottom to a demountable Vycor bulb containing a weighed amount of mercury. This experimental device is fully described in a separate paper.1 Alloy compositions were calculated by weighing the empty bulb, the bulb containing the mercury, and the bulb containing the mercury and the thorium chips. Many alloys were analyzed chemically for thorium and/or mercury after subsequent homogenization; the agreement between analyzed and calculated compositions was invariably very close. Bulbs containing the requisite amounts of mercury and fine thorium chips were clamped off, removed to a sealing unit, evacuated and sealed. Amalgamation under these conditions proceeded rapidly even at room temperature. To insure homogeneity, the specimens were annealed to 300-400°C. Alloys containing less than 30 pct Th remained pasty after all treatments, indicating an equilibrium condition of liquid plus solid. Alloys with more than 30 pct Th were transformed into a dark powdery product. These latter specimens were annealed for times of up to 1 week to complete interdiffusion. Many of the alloy compositions are pyrophoric. On exposure to air they oxidize with considerable evolution of heat to a mixture of ThO2 and free mercury. It was mandatory that alloy specimens be handled in a "dry box" purged thoroughly with argon. All X-ray diffraction specimens were powdered, screened, and sealed in capillary tubes within the dry box. Experimental Procedures Thermal analysis experiments, useful only in the mercury-rich region of the system, were conducted with the alloys in their original containers. A reentrant thermocouple well formed an integral part of the bulb. These bulbs were heated in a silicone oil bath and cooled in a dry ice-acetone mixture. The rates of heating and cooling were slowed by immersing the specimen bulb in a larger tube containing silicone oil. This provided a suitable thermal lag. In all tests, pure mercury was run as a basic standard. While the invariant reaction at about the melting point of mercury was detected by thermal analysis, the heat effect at the liquidus was not sufficient to produce an inflection in the cooling curve. It was necessary to determine the liquidus temperatures at the mercury-rich end of the system by "breaks" in electrical reslstivity versus temperature curves for individual alloys. The apparatus for this purpose consisted of a pyrex tube about 2 in. diam and 12 in

Jan 1, 1959

By L. C. Weiner

For zinc single crystals, xo = 3o, a surface coating raises both the cleavage and yield strengths over a large temperature range. The "brittle temperature," associated with slip after completion of twinning, does not coincide with the point of intersection of the flow and cleavage curves, which is associated with twinning. A surface film has no effect on the brittle temperature, while it lowers the intersection temperature some 20°. For crystals, yn = 83o, a coating decreases the cleavage strength, making it temperature independent, as well as increases the brittle temperature or its equivalent, the intersection temperature, 20°. These observations are described on the basis of a dislocation-pile-up-at-a-barrier model for brittle fracture; in crystals x,, = 3o the number and distribution of twins play a vital role. IN a recent investigation on the effects of solid environments on the brittle fracture of zinc single crystals,' it was demonstrated that the presence of a surface film changes the cleavage strength of these crystals, either increasing or decreasing it, depending on the crystal orientation. An increase in cleavage strength of some 43 per cent was found for coated crystals oriented x, — 3o K = 28",* while a decrease of 48 per cent was observed with crystals X" = y» — 83". Moreover, these effects were found

Jan 1, 1959

By A. H. Daane, J. F. Haefling

BECAUSE of the wide use of platinum in industry and research, the physical properties of this metal, including its vapor pressure, have been studied in some detail.' The other members of the palladium-platinum group of metals have not been studied as extensively, and only qualitative information is available on the vapor pressure of palladium. Data given in literature by Vines1 and Brewer2 on the vapor pressure of palladium are based on the qualitative observations by Holborn and Austin3 and Crookes4 on the rate of volatilization of palladium filaments in various atmospheres. The general observation that palladium is the most volatile metal of the palladium-platinum metal group was corroborated by Bell, Love and Normand who studied the separation of isotopes of the platinum-group metals by a mass spectrometric method. We have measured the vapor pressure of palladium using the Knudsen effusion technique. In this work, the effusion vessel was suspended from a quartz-fiber microbalance into an induction furnace, and the amount of vapor effusing from the vessel was determined by direct weighing of the vessel during the measured heating times. This technique has been described in a report from this laboratory." The vapor pressure of palladium was calculated from these measurements using the equation P...... = 17.14 -W- (77m)'u [1] a t where ? is the weight loss in grams of vapor of molecular weight m from a vessel having an orifice of a sq cm, during t sec. The derivation of this equation from kinetic theory has been described in a previous report from this laboratory: as well as in texts discussing the kinetic theory of gases.%" Test Vessel—In the search for a suitable material for the effusion vessel, it was found that tantalum reacted with palladium metal to form intermetallic compounds, and graphite was readily dissolved in palladium metal to form what appeared to be a liquid phase at a temperature several hundred degrees below the melting point of palladium. On cooling, the graphite gathered into spherical balls in the palladium, with crystals extending radially from the center of these balls, some of which were a millimeter or more in diameter. However, palladium metal vapor did not attack the graphite vessel, so graphite could be used where it did not contact condensed palladium. Tungsten did not appear to react with palladium vapor or molten palladium at its melting point, but it was not convenient to use a tungsten-vapor pressure vessel because of the difficulty of fabricating this metal. Since the vapor-pressure range to be studied (10 2 to 10 ' mm) did not appear to extend above the melting point of palladium, a combination of tungsten and graphite served to provide a very satisfactory effusion vessel. The lower half of the graphite vessel was lined with some strips of tungsten foil and the sample of palladium consisting of a coil of sheet was placed in the tungsten liner; in this way, no contamination of the palladium by carbon occurred. Procedure After outgassing at 1500C, the tungsten-lined graphite effusion vessel was loaded with 300 mg of

Jan 1, 1959

By F. D. Rosenthal, F. J. Dunkerley, G. J. Mills

Activities, free energies, and heats and entropies of mixing of liquid Pb-Zn alloys have been obtained by the electrode-potential method between 400° and 650°C. The large positive deviations observed from Raoult's law are in agreement with the phase diagram, which indicates a wide immiscibility field. A vapor-pressure method was used to extend the activity measurements to 900°C, allowing the maximum of the immiscibility gap to be estimated by thermodynamic calculation. Data on the mono-tectic and eutectic points compare favorably with previously existing work. SEVERAL long-standing methods have been in use for the study of phase diagrams from measurement of the activities of the component metals.' The use of thermodynamic analysis for interpreting equilibria data is comparatively recent, however. Such analysis is usually undertaken by first evaluating the principal thermodynamic functions as, for example, the enthalpy, entropy, and free energy of the alloy constituents. These, in turn, quite often can be correlated with the interatomic potential energies and atomistics of the system, from which a clearer understanding of the causes leading to deviations from ideal behavior is gained. The present study of liquid Pb-Zn alloys is concerned with a determination of these quantities by electrode-potential and vapor-pressure measurements, using these values in calculations involving phase equilibria and to obtain a theoretical insight into an alloy system exhibiting strong positive deviations from ideal metallic solution. A considerable portion of the previously reported work is based on thermal analysis. Supplemented by optical studies of solid alloys, these techniques have revealed the essential nature of the immiscible mixtures that are formed. It is difficult, however, using the phase-

Jan 1, 1959

By J. C. M. Li

This exploratory survey was undertaken to repeat some experiments- in which anomalous results were reported1 for bismuth and to measure the thermoelectric power of some bismuth alloys and inter-metallic compounds. sato1 reported that the thermoelectric power of bismuth depends on the temperature gradient. This seems rather unreasonable especially when the Benedicks effect' has not been detected. Even if the material is not homogeneous, the observed thermoelectric power can be represented by

Jan 1, 1959

By D. H. Turner, F. A. Crossley

The titanium-rich corner of the system Ti-Al-Si has been studied to determine the phase relationships in the temperature interval 600° to 1200°C. Metallographic examination of long time isothermally annealed specimens was the means of investigation. PART of a program on phase relations and transformation processes of titanium alloy systems included the study of the titanium-rich corner of the Ti-Al-Si system. The investigation covered ternary compositions in the range 2 to 8 pet A1 and 0.1 to 2 pet Si and binary compositions in the range 0.2 to 2 pet Si. Temperatures were in the range of 600" to 1200°C. Alloys containing 6 pet A1-0.1 to 0.5 pet Si were investigated down to 400°C. Partial vertical sections are presented for 2, 4, 6, and 8 pet Al. The Ti-Si system has been reported by Hansen et al.' It is characterized by a eutectoid decomposition, ß = ± a + Ti3Si3, at 860°C. The maximum solubility of silicon in a is reported to be about 0.5 pet at the eutectoid temperature. The solubility of silicon in 0 increases from 0.9 pet at the eutectoid temperature to approximately 3 pet at the eutectic temperature, 1330°C. Several investigations in the composition range of interest have been reported for the Ti-A1 system."' These investigations are in agreement on the phase fields, but differ to small extents on boundary positions. However, very recent, and as yet unpublished, findings" " indicate that there are perhaps two phases which occur at lower aluminum contents than the ? (TiA1) phase, and that the solubility of aluminum in a titanium is less than 6 pet. In the present investigation phase relations found are in agreement with the published literature exemplified by the work of Bumps et al.3 Therefore, it is probable that the partial system reported herein is metastable and does not represent true equilibrium. Experimental Procedure High purity Bureau of Mines titanium sponge of 103 Bhn hardness, granulated aluminum shot of 99.7 pet purity, and silicon powder of 99.8 pet purity were used in making the alloys. For the work in the range from 600" to 1200°C, 100 g ingots were prepared by arc melting. Melting losses were negligible and spot checks by chemical analysis showed good agreement between nominal and analyzed results. Nominal compositions are used throughout this paper. Ingots were forged to 3/8 in. rounds and cut into specimens for heat treatment. Isothermal anneals in the range from 600" to 900°C were preceded by solution treatment at 1000°C for 1 hr, followed by furnace cooling to the annealing temperature. Samples were sealed in evacuated Vycor bulbs for heat treatments up to 1000°C. Higher temperature anneals were done with the samples sealed in quartz bulbs under a partial pressure of argon.

Jan 1, 1959

By W. Rostoker, S. A. Spachner

FOLLOWING the discovery of the w transition phase in certain titanium-chromium alloys by Frost, Parris, Doig, and Schwartz, much interest has centered on the alloys in which this phase is found and its mode of precipitation. The w phase has been found in alloys of Ti-Cr, Ti-Fe, Ti-Mn, Ti-MO,2 and Ti-v.3 The temperature-time-transformation characteristics have, as yet, not been determined for most of these. In this study, such transformation characteristics have been investigated for two heat-treatable titanium alloys known to exhibit transition phase phenomena. The alloys chosen, Ti-8Cr and Ti-13M0, are representative of two classes of binary equilibrium systems. In the

Jan 1, 1959

By R. Bakish, C. S. Barnett

IN experiments on tantalum strained in tension, Bechtold did not observe deformation-twinning even at a temperature as low as that of liquid air.' This is an unexpected behavior for a metal of body-centered-cubic structure. Therefore, it is desirable to determine whether the lack of twinning is an inherent characteristic of this particular metal, or whether the reluctance to twin can be overcome under suitable conditions. The following experiments were performed under conditions favorable to twinning and cleavage in their competition with slip, namely, with impact loading on large-grained sheet at low temperatures. The crystallography of cleavage in tantalum sheet was also investigated carefully because of the remarkable ductility of tantalum at low temperatures and because recent tests on oxygen-embrittled tantalum had disclosed unusual cleavage behavior for a metal of this structure: cleavage primarily on (110) planes and only occasionally on {100}.2 The tantalum, supplied by Fansteel, was of 99.9 pet purity, with the chief impurities being iron (0.03 pet) and carbon (0.03 pet). Coarse grains were produced by the strain-anneal method, the anneal being 4 hr at 2000°C in a vacuum of 10-3 mm Hg, followed by furnace cooling. Impact deformation was applied in various ways: a) by hammer blows on an anvil, the specimen and anvil being immersed in liquid nitrogen ( —196°C), b) by driving a precooled center-punch into the sheet, and c) by bending around a crystallographically determined axis with a hammer blow. The impact-deformation produced bands and slip lines on the surface, Fig. 1. The bands have every appearance of being deformation twins, a) They are tilted with respect to the untwinned surface. b) They have the appearance of Neumann bands in iron, thin lens shape, some having serrated edges. c) The orientation in each is different from that of the surrounding matrix and uniform within a given band, see slip lines within them in Fig. 1. d) Upon repolishing and etching, the difference in orientation and the resemblance to Neumann bands is again evident, Fig. 2. (In this micrograph the slight bend in the bands as they cross grain boundaries was noted frequently and results from the high degree of preferred orientation in the sheet.) e) The bands persist after annealing treatments that would have removed them had they been a low-temperature martensitic phase, e.g., after an anneal of 1/2 hr at 900°C. When back-reflection Laue data were plotted for single-surface analysis of several grains, every trace of the bands in each grain could be explained by (112) planes. In addition, two of the bands were located in space by traces on two surfaces, and these also were found to lie on (112) planes within the error of the stereographic plot. Since (1 12) is the anticipated composition plane for deformation twins in body-centered-cubic metals it is felt that the observations listed above are conclusive evidence for the identification of the bands as twins. Similar tests with impact at —77° and at 25°C produced no twinning. It is concluded that the critical shear stress for slip at the rates of straining used was always low enough to prevent the applied stress from reaching the value required for twinning at these temperatures. It was noted that the serrations along the edges of the twin bands exhibited parallel crystal facets. Several similarly oriented notches are visible in Fig. 1, and a remarkable set is shown in Fig. 3. It appears from Fig. 1 and similar areas that notches are frequently associated with the intersection of a slip line with a twin, although not all such intersections are at notches. In some instances a slip line appears to enter the twin, cross it, reflect from the opposite side and recross it, producing a pattern resembling a notch but without producing the notch itself, see Fig. 1. It is suggested that the stress concentration at the end of a slip line is responsible for these details. The strain energy associated with the pile-up of dislocations at a twin boundary may be lessened by untwin-ning or failing to twin a portion of the twin band, or

Jan 1, 1959

By W. D. Robertson, W. L. Phillips Jr.

Stress-strain curves were obtained for single crystals of alpha brass in tension and in direct shear. Specimens were strained various amounts in a given slip direction, unloaded, and immediately strained in a second slip direction 60°, 120°, or 180&apos; from the original slip direction. Crystals strained in tension and direct shear had comparable critical resolved shear stresses and stress-strain curves. The density of slip lines in direct shear and in tension was essentially the same. The stress-strain curves obtained in shear were independent of initial orientation, choice of {111 } slip plane, choice of <110> slip direction, prior annealing temperature, and rate of cooling after annealing. There was no recovery after annealing for 4 hr at room temperature or 200°C; recovery was observed after 4 hr at 400°C. The crystals showed no asterism and mechanical properties were completely recoverable up to 20 pct strain. It was found that there is a barrier to slip in all latent close-packed directions, and that the magnitude of these barriers, evaluated at 3 pct strain, is proportional to prior strain and independent of the choice of latent direction in the {111} plane. The formation of Cottrell-Lomer barriers is discussed as a possible explanation for the hardening of the latent systems. AN idealized concept of plastic deformation indicates that a single crystal should yield at some stress that is dependent on crystal perfection and it should then continue to deform plastically by the process of "easy glide," which is characterized by a linear stress-strain curve and a low coefficient, ds/dE, of work-hardening. Hexagonal metal crystals generally conform to this ideal concept of laminar flow. In face-centered cubic metals the range of easy glide is always restricted in magnitude and it is strongly dependent on orientation, composition, crystal size, shape, surface preparation, and temperature. Since one of the principal differences between the two crystal systems, both of which deform by slip on close-packed planes, is the existence of secondary (latent) slip planes in the face-centered cubic crystals, it has been proposed that the transition from easy glide to turbulent flow, characterized by rapid linear hardening, is due to slip on secondary planes intersecting the primary plane.&apos;-.; However, the characteristic differences between individual face-centered cubic metals remain to be explained; in particular, it is not clear why the range of easy glide should vary so greatly in different metals and alloys similarly oriented for single slip. An investigation and comparison of different metals with respect to latent hardening on the primary slip plane should provide some of the information required to specify the necessary and sufficient conditions governing the transition from easy glide to turbulent flow. But, in order to accomplish this purpose, plastic strain must be produced by simple shear in a chosen plane and in a predetermined direction by some form of directed shear apparatus, the results of which must be correlated with the corresponding tension experiments. Two such experiments have been performed previously with zinc and with aluminum. Edwards, Washburn, and Parker" and Edwards and Washburn7 found that the strain-hardening coefficients in two latent directions in the basal plane of zinc were the same as in the primary direction. However, to initiate and propagate slip in either the [2110] or the [1210] direction, following primary slip in the [1l20] direction, it was necessary to increase the stress above that required to continue slip in the primary direction; when the direction of shear was reversed 180 deg plastic strain began at a much lower stress than that required to initiate slip in the original direction and the stress to propagate slip in the reverse direction was lower than the stress to continue slip in the forward direction, indicating a permanent loss of strain-hardening. Rohm and Kochendorfer observed softening in aluminum for all latent close-packed planes and directions. They also found that the critical resolved shear stress obtained from their direct shear apparatus was 50 pct lower than the value obtained from conventional tension tests, that the stress-strain curve was linear at 50 pct plastic strain, and that slip lines were not visible at strains less than 30 pct. At present it is uncertain whether these diverse results correspond to real differences in work-hardening characteristics of the close-packed planes of aluminum and zinc or to differences in experimental technique. In view of Read&apos;s analysis &apos;" of the stress distribution in the experimental arrangement of Rohm and Kochendorfer, there is some reason to question the significance of the latter results. In order to resolve this problem it is necessary to re-valuate the direct-shear technique and either repeat the previous measurements or investigate a third system. The latter choice seemed most likely to produce significant results with respect to work-hardening, and accordingly, it was decided to examine the hardening characteristics of the latent slip directions in alpha-brass. The choice of alpha-brass was dictated by the fact that easy glide is more extensive in this alloy than in any other face-centered cubic metal or alloy and, presumably, more nearly like the idealized hexagonal system. Experimental Procedure Crystals were made in graphite by the Bridge-man method in the form of cylinders, 11/2 in. diam and 8 to 9 in. long. Material for the crystals was 70/30 brass containing the following impurities:

Jan 1, 1959