By A. F. Crawley

THIS paper describes part of a series of density measurements on low melting point metals being undertaken at the Mines Branch, Department of Energy, Mines and Resources, Ottawa, Canada. This program has received support from the Canadian Zinc and Lead Research Committee and the International Lead and Zinc Research Organization. Examples of the type of work being done have already been given in earlier papers' , which deal with the densities of lead, tin, and some of their alloys. Densities were measured using a graphite pyc-nometer by a technique which has already been described." The cadmium and indium, supplied by the Consolidated Mining and Smelting Co. of Canada were of 99.999 pct purity. Density determinations on indium, as for lead and tin,1,2 were made under a vacuum of about 5 x 10-6 torr because the oxidation and vaporization characteristics of the metal do not create experimental difficulties. This contrasts markedly with cadmium which, even at the relatively low temperatures of our experiments, has a high vapor pressure and a strong oxidation potential. To suppress the harmful effects of these properties, determinations on cadmium were made with success under an atmosphere of argon, the technique having been previously established in this laboratory for measurements on zinc.3 The densities of cadmium and indium are listed in Table I and plotted in Figs. 1 and 2. From the graphs, it is readily observed that the densities of both metals vary linearly with temperature. This relationship expressed mathematically is of the form:

Jan 1, 1969

By S. Nenno, T. Saburi, Y. Mizutani, M. Yomarnoto, K. Komatsu

In the equilibrium phase diagram of the Ni-Mo sys-tem1,2 available at present, intermetallic compounds (or ordered phases)ß(Ni4Mo) and ?(Ni3Mo) are known to exist to the nickel rich side. In our recent investigations on Ni-Mo alloys, however, it has been found that the quenched alloys from the high temperature region containing more molybdenum than the Ni4Mo do not decompose directly into 0 and when annealed isothermally below the peritectoid temperature, i.e., 865°C. This note is to report the existence of Pt2Mo type superlattice (possibly ordered Ni2Mo) as a metastable phase in the early stage of decomposition. Alloys containing 20.1, 22.7, and 24.4 at. pct Mo were prepared by vacuum-melting electrolytic nickel of 99.9 pct purity and molybdenum powder of 99.9 pct purity in an alumina crucible. From the resulting ingots, sheets 0.3 mm thick were obtained by forging, hot-, and cold-rolling. The sheet specimens were water-quenched from ! region and subsequently annealed for various periods of time at temperatures below the peritectoid temperature. On these specimens were made optical-microscopic and transmis-sion-electron-microscopic observations. Fig. 1- Optical micrograph of the 22.7 at. pct Mo specimen annealed for 100 hr at 700°C after quenching. (ß + ?) region, B, nucleated along a grain boundaries are invading the preexisting (ß + Ni2Mo) region, A. Details of A are observable only by electron microscopy. Etchant: 60 pct HNO3-40 pct CH3COOH.

Jan 1, 1970

By S. P. Ray, B. D. Sharma

THE activation energy values for self-diffusion in pure metals have been correlated with a number of physical properties such as melting points,1 valences,' Debye temperatures,3 and cohesive energy densities.4 Extending the melting point correlation, the self-diffusion activation energy values for the alloys can be similarly correlated with the solidus temperatures. For metals and alloys which exhibit phase transformations, such a correlation is not feasible because of the uncertainty of various physical properties of the corresponding phases. Using thermodynamical approach, Ardell5 calculated the hypothetical melting points of the low melting phases of the polymorphic metals. However, these calculated melting points do not show reasonable correspondence with the activation energy of self-diffusion. Recently, a new approach treating metals and alloys as electron concentration phases has been developed by Engel6 and Brewer.7 These workers have attempted to correlate the crystal structures with the electron configurations of the atoms existing either in ground state or in an excited state of low promotion energy. The basic postulate of this theory is that whereas the contribution to the bonding of the metal comes from the interaction of both d and (s-p) electrons existing either independently or in hybridized states, the existing crystal structure is controlled by the (s-p) electrons alone. Specifically, a metal is supposed to crystallize in bcc, hcp, or fcc phase provided the metal has one, two, or three valence electrons per atom in the (s-p) configurations. The diamond, or ZnO and ZnS structures, occur with four (s-p) electrons per atom. Secondly, the contribution of d electrons to bonding is supposed to increase with atomic number

Jan 1, 1970

By H. C. Gatos, J. T. A. Pollock, V. Sadagopan

PREVIOUS investigations on the effect of neutron irradiation on the superconducting properties of bulk transition metals indicated that little or no change occurred in poly crystalline disordered materials, particularly if cold-worked prior to irradiation. Only the superconducting properties of ordered intermetal-lic A15 compounds were found to be sensitive to irradiation, and the observed reduction in Tc and increased magnetic hysteresis or critical current densities were attributed to the introduction of flux pinning vacancy clusters and disorder in the lattice. Since the former would also be expected to be present after irradiation in disordered alloys, the general conclusion was that the disordering effect of the irradiation was the primary reason for the changes observed. The present note reports some unusual effects of neutron irradiation on cold worked Nb(Cb)-Ti-V alloys. Specimens with nominal composition as given in Table I were prepared by repeated arc melting, taking the usual precautions, and homogenized at 1000°C for 24 hr prior to a reduction of 15:l by cold rolling. Samples of size 1 by 1 by 25 mm were sliced from the rolled strips. The sarmples chosen for irradiating were sealed in a cadmium tube (wall thickness 1 mm) prior to exposure in a fast neutron flux of 3.7 x 1019 neutrons per sq cm in the swimming pool reactor of Union Carbide Corporation&apos;s Sterling Forest Reactor. During irradiation the temperature of the samples was maintained below 70°C. The irradiated samples were stored at room temperature for approximately 1 year allowing the radiation levels to reach a safe handling value. Tc measurements were made employing a self-inductance coil technique. Jc data at 4.2"Kwere obtained using a four lead resistivity method. The latter measurements were made at the Francis Bitter National Magnet Laboratory by setting the perpendicularly applied field and increasing the direct current through the sample until a potential of about 10-6 v was detected. Tc values for the nonirradiated samples are listed in Table I together with the change in Tc after irradiation. A decrease in Tc of 0.25 or 0.3"K was measured for three of the four samples, the exception being the Nb-30 at. pct V-20 at. pct Ti alloy which showed a decrease of 0.5K. Jc vs applied field data are plotted in Fig. 1 for the Nb-20 at. pct V-30 at. pct Ti alloy. These curves are typical of the four alloys and surprisingly indicate that a degradation occurred in all the samples after irradiation. Hc2 values, obtained by extrapolation to zero current, are 8 to 15 pct lower than those measured for the nonirradiated specimens. The reasons for the degradation of Tc and jc ob-served in the alloys on exposure to neutron irradiation are not immediately apparent. The temperature at which the samples were maintained during bombardment (<70°C) and stored (20°C) make it highly unlikely that any significant change in the dislocation density of the materials through thermally activated migration and annihilation would occur. The explanation must lie in the type of damage produced by the bombardment. McEvoy et a1. reported no change in superconduct-

Jan 1, 1970

By M. C. Flemings, R. Mehrabian

In a recent series of papers,1-3 it was shown that a variety of apparently different types of macrosegrega-tion result from the same basic mechanism, the inter-dendritic flow of solute rich liquid to feed solidification and thermal contractions. The important parameter governing sign and extent of segregation was shown to be (v.?T)/ where v is interdendritic flow velocity, ?T is temperature gradient, and E is rate of temperature change. It was proposed in one of the previous papers that the "negative cone of segregation" often found at the base of large ingots results from the large value of (v. VT)/E expected to pertain there. The reason why this parameter is expected to be large in that location is the high flow velocity to be expected there, as discussed earlier,&apos; and as shown schematically in Fig. 1. In this note, two experiments are summarized which are intended as laboratory simulations of the inter-dendritic flow behavior sketched in Fig. 1 and, therefore, of the "negative cone of segregation". Experimental procedures employed are as described in the the earlier work.3 Alloy cast was nominally Al-4.5 pct Cu. Fig. 2 shows one of these ingots, a "prism" ingot, 6 cm high by 12 cm wide by 10 cm long, unidirectionally solidified from a water cooled base. In this ingot, in-terdendritic flow velocity increases near the upper portion of the ingot because of the gradually decreasing ingot cross-section. Calculations were presented earlier of the negative segregation to be expected in this type of ingot,&apos; and results presented in Figs. 2 and 3 agree closely with those of earlier calculations. A more direct (although less easily calculable) simulation of the "negative cone of segregation" is the

Jan 1, 1970

By David N. French

In a recent paper, Miyoshi, Hara, and sugimotoL have shown that hardness increases and crack resistance decreases with polishing time in tungsten car-bide-cobalt alloys. They attribute the changes in hardness and crack resistance to cold working in these alloys. More recently Exner2 explains the decrease in crack resistance with the amount of material removed (polishing time) by suggesting that polishing removes a high compressive residual surface stress due to the initial grinding operation. He cites previous work on steel to show grinding can induce surface compressive stresses but offers no direct experimental measurements to support this in cemented tungsten carbides. In recent work we have observed changes in residual stress in the W C phase as measured by X-ray diffraction techniques with changes in polishing conditions.3 As a result of the work of Miyoshi et al.,L a brief study was undertaken to investigate the effects of polishing and grinding on the residual stress in the WC phase and have been reported.4 A single composition of tungsten carbide —10 wt pct Co was used. Two initial conditions were studied: an annealed condition with about -30,000 psi residual stress from the differences in thermal coefficients of expansion of WC and cobalt and, on the same specimen, a surface ground with a 150 grit diamond wheel. Stress was measured in the WC phase using X-ray diffractometry as a function of the amount of material removed by metallographic polishing with 6 diamond paste. The results are shown in Fig. 1. Two things are noted, 1) polishing with 6 p diamond paste has little effect on the annealed sample and 2) the magnitude of the grinding stress is markedly reduced as material is removed. By the time 0.1 mil is removed the surface has a metallographic polish satisfactory for light microscopy examination. Thus the surface, even though polished, can still retain most of the stress due to grinding. Since WC is itself slightly ductile, it seems reasonable that high compressive stresses can be generated in the surface by the plastic deformation accompanying grinding. Exner2 suggests, by analogy with steel, that as a result of grinding both WC and cobalt in the

Jan 1, 1970

By J. C. Williams, M. J. Blackburn

MANY aspects of the formation of the metastable w phase in titanium-transition metal alloys have been described in several recent papers.1-4 These papers have reviewed earlier work on the w phase and have further defined most of the important features related to the formation of this phase, e.g-., its crystal structure, composition, and morphology. There are, however, several important points regarding formation of the w phase in titanium alloys which have been described in less detail. Two of these are the relationship between lattice misfit and w phase morphology and the influence of lattice misfit on the mode of formation of the equilibrium a phase. In this communi- cation we will present transmission electron microscopy results relevant to these two points. The alloys used in this study were prepared by non-consumable electrode arc melting, each 30-g button being remelted a minimum of twelve times. The alloy compositions we have studied are listed in Table I. Thin foils were prepared using standard techniques described elsewhere. Two distinct c&apos; phase morphologies have been reported in earlier papers. The phase is ellipsoidal in the Ti-Mo3 and Ti-Nbl system and cubical in the Ti-V3 system. Results of the present study show that the w phase is also cubical in Ti-Mn, Ti-Fe, and Ti-Cr alloys as illustrated in Fig. l(b) to (d). Fig. l(a) shows the ellipsoidal morphology in Ti-MO3 for comparison purposes. It was suggested in an earlier paper3 that the w phase morphology may be controlled by the lat-

Jan 1, 1970

By W. V. Youdelis, W. H. Bear, G. Cochrane

HERETOFORE, there has been very little study of the effects of various metallurgical factors on the behavior of thermoelectric materials, the need for which is evident if optimum processing and design of thermoelectric devices is to be realized. Accordingly, we have undertaken such an investigation on the thermoelectric materials bismuth and Bi-Sb alloy and in this paper present some preliminary results which merit consideration, in particular the relatively high thermoelectric power and figure of merit values obtained for the Bi-12Sb (at. pct) alloy powder compacts. The thermoelectric parameters for ingot and powder compact specimens are determined and the results are compared with published data for single crystals. Preparation of Materials. The bismuth and antimony used in this investigation are six nines pure. Melting and casting of the ingots was carried out in air for expediency, since most oxidation unavoidably occurs during the preparation of the powder by filing of the ingots. Chill cast ingots of pure bismuth were prepared by pouring the melt into split copper chill molds, and unidirectionally solidified ingots of bismuth and Bi-Sb alloy were obtained by slow directional cooling in pyrex tubes. All melts remained bright during melting and casting, indicating minimum oxidation. Powder for the powder compact samples was obtained by filing the ingots with a fine and coarse file to give a variation in the particle size of the compacts. The particles in the fine powder compacts varied in size from approximately 28 pct less than

Jan 1, 1970

By G. R. Belton, Y. K. Rao

A galvanic cell, using liquid MgCl2 or MgC12-CaC12 mixtures as the electrolyte, has been used to determine activities in Mg-A1 liquid alloys between 700&apos; and 880°C. The incovporation of a chlorine electrode in the cell also allowed measurements to be made of the standard free energy of formation of MgCl2(l). The results are shown to be in good agreement with thermo-chetrlical values from the literature, and this is taken as evidence that the small, known solubility of magnesium in iMgCl2 introduces no significant error in galcanic cell measurements. Within experimental error, the activity coefficients and relative partial molar enthalpies at 800°C are shown to be represented by the following "subregular" solution equations: logy~~ =-0.68(1 -xMgj3 log yAL =-1.02(1 - XMf + 0.68(1 - XMf H.M = -4400(1 - %)3 / cal Mg 7Ag&apos; HZ =-6600(1 - xA1)&apos; + 4400(1 - XMf cal SCHNEIDER and toll&apos; have used a transpiration technique to measure the vapor pressures of magnesium over Mg-A1 alloys between 544" and 594°C. amsstad,&apos; however, has since suggested that the extrapolation to zero flow rate, used by these authors in interpreting their apparent pressure vs flow rate data, gives unreliable results. Rogers, Tomlinson, and Richardson,3 in interpreting the results of solution equilibria between Mg-A1 alloys and liquid MgC12, also considered the measurements of Schneider and Stoll to be unreliable and preferred to derive activities for the alloys from the earlier boiling point determinations of ~eit~ebel~ and the partial molar heats recommended by Kubaschewski and ~atterall.~ These latter heats were based substantially on the early calorimetric work of Kawa-kami but, unfortunately, his work on other systems has sometimes been found to be inaccurate.7 Rogers et al., in the above-mentioned paper,3 tentatively concluded that the most likely species responsible for the limited solubility (0.3 mole pct at 800°C) of magnesium in MgC12 were Mg° (neutral) and Mg2++. Two more recent studies8,9 have supported Mg2++ as the soluble species. In the present study, activities in Mg-A1 alloys have been determined by means of a galvanic cell involving liquid MgCl2 or MgC12CaCl, mixtures as the electrolyte. Since the reactive nature of magnesium precluded simple Faraday yield experiments, a chlorine electrode was incorporated in the cell in order that the performance of the cell could be checked by measurements of the heat and free energy of formation of MgC12. This procedure was considered necessary since it has been suggested1&apos; that the solubility of a metal in a molten salt might introduce electronic conductivity; also, previous determinations of the standard electrode potential for MgC12 differed by as much as 70 mv11-13 EXPERIMENTAL Materials. Analyses of the materials used in preparing the alloys and the electrolyte mixtures are presented in Table I. The alloys were prepared by induction melting weighed amounts of the metals in a graphite crucible held under an argon atmosphere. Pure anhydrous magnesium chloride was prepared by heating the mixture MgCl, . 6H20 +NH4C1(1:1) to 650°C, followed by melting under dry argon. The melting point of the dry MgC12 was found by differential thermal analysis to be 714.8oC, which compares well with the accepted value of 714C.14 This agreement was taken to be an indication of the high purity of the dried salt. Table I. Compositions of Materials, wt pn Impurity Mg Al MgCI2 CaCI, Ba - - 0.005 Ca - - 0.010 Cu 0.02 0.02 Fe - 0.10 0.001 0.010 Pb 0.01 - 0.001 0.005 Mn 0.15 0.001 Si - 0.10 Sr - - 0.005 MBSO* - 0.040 ARGON TUNGSTEN CHLORINE LEAD—411 11 II ALUMINA &apos;A I / ave GRAPHITE on irA~_ ( ^"l ROD MAGNESIUM S>ILICA~^ /, OR ALLOY-. I /A] ___________ -«^- _ ELECTROLYTE I y FRITTED DISCS Fig. l—Arrangement of chlorine and metal electrodes in electrolytic cell.

Jan 1, 1970

By A. G. Guy

In a special type of electrodiffusion experiment the entire specimen is at constant temperature. The vacancies are then created at one end of the specimen and flow to the other end where they are destroyed. The energy required to operate the corresponding sources and sinks results in a super saturation of vacancies at one end of the specimen and an under -saturation at the other end. This gradient in vacancy concentration produces a chemical-diffusion flux, J(D), of vacancies in addition to the flux, J(E), caused by the electric current. Using the experimental data of Ch. Herzig,5 it is shown that a super saturation of 1 pct can cause J(D) to be about 25 pct of J(E), and thus account for the anomalous behavior of short specimens. THERE are advantages in a phenomenological treatment as contrasted to an atomistic one. For example, there are many reactions involving the element copper that are quantitatively and usefully understood from a phenomenological viewpoint, even though electron theory is not yet able to predict whether copper should be fcc or cph.&apos; Similarly, the lack of a complete atomic theory of vacancies need not prevent the development of a treatment based on thermodynamics and chemical kinetics. In the following discussion, models will be used for the vacancies and for the mechanisms by which they move or are created or destroyed, but the phenomenological treatments are not dependent on the details of these models. The important product of a phenomenological analysis is an equation that describes the relation among the measurable quantities determining the behavior of the system. Based on such an equation, experiments can be performed to study these quantities in detail. Eventually atomic theory will supply an adequate theoretical base for the phenomena in question. A chemical species whose chemical potential was invariant during reactions in binary and ternary systems of varying composition would indeed be an anomaly. Yet this is the role that has frequently been assigned to the vacancies in pure metals, in dilute solutions, and even in ordinary alloys. The weight of available evidence supports the view that supersatu-rations of vacancies are on the order of 1 pct in usual diffusion processes.&apos; Although it may seem strange that such a small deviation from equilibrium could significantly affect the thermodynamic properties of the vacancies, it is well known that the driving force for an ordinary chemical reaction is the departure of the components from their equilibrium state. Similarly, the reaction of vacancies that results in the formation of pores in various types of diffusion3 can reasonably be attributed to the supersaturation of vacancies. In the present paper, it will be shown that small degrees of supersaturation can significantly affect the kinetics of the diffusion process itself. ISOTHERMAL ELECTRODIFFUSION Two different experimental techniques are convenient for studying the behavior of vacancies in a pure metal in the presence of an electric field. Gilder and Lazarus4 studied self-electrodiffusion in a gold specimen in which only the central portion was at high temperatures. In this case the significant vacancy sources operate inside the specimen in the presence of a temperature gradient. In the laboratory of Th. Heumann a method has been devised for studying self-electrodiffusion at constant temperature.5 In principle, there is then no effect of thermodiffusion. It will now be shown why in this case the significant ATungsten disks \^^ ^^ ^Gold disks^^ ^^"T>.... "TTZA ? Up Iy&apos;7 markers ///// ////// initial plane p I y/y/y of joining \I 7//// V7//A_________I_________V//// -I 0 +I Distance from center of specimen (a) -— Direction of flow of electrons —Direction of flw of vacancies %yy} Matano I z~irkendall /%W, vy/A inlerfacej "interface ///// -} HfiK- +/ 0 Distance from center of specimen (6) Fig. 1—-Schematic illustration of the essential features of isothermal self-electrodiffusion. (a) Initial condition of specimen. (b) Condition of specimen after electrodiffusion.

Jan 1, 1970

By W. C. Clarke

An empirical study of the nature of the embrittle-ment which occurs in martensitic and semiaustenitic precipitation hardening stainless steels upon exposure at temperatures of from about 550" to 875°F has been undertaken. This work was aimed at determining cazusation and means of controlling this phenomenon. A commercial copper bearing precipitation hardening alloy was used as a basic material for study. The effect of heat treatment variables was studied as was the effect of variations in analysis. It is concluded from the evidence that martensitic and semiaustenitic precipitation hardening stainless steels are subject to 885°F ernbrittlement similar to that observed in the straight chromium stainless steels. A characteristic of precipitation hardening stainless steels which has limited their use in certain applications is that they embrittle when held at temperatures in the range of from about 550" to 900°F. This is true to a more or less degree in all currently available alloys, either the basically martensitic type or the semiaustenitic type. The rate of embrittlement varies markedly with exposure temperature, being low at 550" to 600°F and in-creasing as the temperature increases. In spite of this embrittlement, these alloys with their unique combination of high mechanical strength, reasonable toughness, and good corrosion resistance are used in many hundreds of applications. Nevertheless, there are potential applications where the embrittle-ment described is a limiting factor. The purpose of this investigation was to study the embrittlement of these alloys and to find a way to control or eliminate it. GUIDELINES USED IN PRESENT WORK The work reported in this paper is based on a study of 17-4 PH*, a very widely used alloy. It has been used *Trademark of Armco Steel Corp., licensor. in pressurized water and boiling water atomic reactors operating at about 550°F for a number of years. As the life of such equipment is extended or operating temperatures are raised, the possibility of embrit-tlement becomes of increasing concern to materials engineers. Much investigation work was done with respect to the use of 17-4 PH at 550°F. K. C. Antony&apos; states "Such estimation" (of an activation energy for the diffusion of chromium in iron) "would indicate W. C. CLARKE, Jr. is Senior Research Engineer, Advanced Materials Division, Armco Steel Corp., Baltimore. Md. This manuscript is based on a talk presented at the symposium on New Developments in Stainless Steel, sponsored by the IMD Corrosion Resistant Metals Committee, Detroit, Mich., October 14-15, 1968. significant secondary aging is improbable at temperatures less than 700°F within normal component service life". This statement is modified however by the recognition of the accelerating tendencies of applied stress and internal stress as well as the possible effect of irradiation. In this investigation of 17-4 PH, the H 1100 (1900°F-1 hr oil quench or air cool + 1100°F-4 hr-air cool) condition was used, partly because this condition is normally used in atomic reactors. As shown later, the precipitation hardening temperature has no real bearing on the rate of embrittlement. An exposure temperature of 800°F was selected since embrittlement at 800°F is rapid, permitting development of relative data in time periods of 400 to 500 hr. For those not familiar, a nominal present day analysis of 17-4 PH is: C Mn P S SiCrNiCuCbN 0.04 0.30 0.015 0.015 0.60 16.00 4.30 3.25 0.23 0.030 TYPICAL BEHAVIOR OF 17-4 PH Figs. 1 and 2 show the behavior of a commercial heat of 17-4 PH under the conditions defined. Characteristically, 800°F exposure causes a rapid drop in Charpy V-notch impact strength. Tensile and yield strengths gradually increase and a gradual loss of elongation and reduction of area occur, accompanied by an increase in hardness. Notched tensile strength increases to 125 hr exposure and then sharply decreases after exposure for 500 hr. The notched vs un-notched tensile ratio remains virtually constant to exposure for 125 hr (1.67 to 1.56) but drops to 1.15 after 500 hr. Tensile ductility is not alarmingly affected even after much longer exposure times than these. For example, samples aged at 1100°F for 1 hr exposed at 800°F for 4000 hr showed a drop in elonga-tion of from 13 to 11 pct and in reduction of area of from 58 to 37 pct. Notched impact is the property SmIgth KSI 3JJ[/__________^UTS-Nrteh 260 ;/- 240 —^ 200 UTS-Smooth________._, o ioo mo Sob" m Too Hours Exposure Fig. 1—Effect of exposure at 800°F for various times on notched tensile strength and smooth tensile and 0.2 pct yield strength of 17-4 PH in the H 1100 condition.

Jan 1, 1970

By Hiroshi Oikawa, A. G. Guy

Recent experimental evidence has shown that it is often incorrect to neglect the reactions occurring at an interface with respect to the diffusion reactions. By introducing reaction-rate constants and k for the transfer of components 1 and 2 between the a and b phases, a phenomenological description has been devised for the coupled processes of diffusion and in-terfacial reaction. An illustrative example has been analyzed with the aid of a suitable computer program. The results indicate that for kab values on the order of 10&apos;1 cm per sec and Ð values of about 10¯10 sq cm per sec, the interfacial reactions are significant during the first 10 2 to l0 6 sec of a diffusion experiment. Among the observable effects of the interfacial reactions in this case appear to be the burying Kirkendall markers and an anomaly in the initial shifting of these markers. THE study of diffusion between two phases is especially important because of its direct connection to phase transformations. For example, the transformation of austenite to ferrite involves diffusion in the a and ý phases and also an interfacial reaction (trans formation) at the a/? interface. If ferrite and aus-tenite are the two members in a diffusion couple, the same two reactions occur during the diffusion process. The numerical values obtained for the diffusion coefficients and interfacial-reaction constants from diffusion experiments can then be employed to predict phase-transformation behavior. Refinement of the calculations of phase transformation is also suggested by the present method for treating two-phase diffusion. In the recent paper by Nolfi et al.&apos; only the solute com ponent is considered in the interfacial reaction accompanying a phase transformation. The present analysis demonstrates that both components must be considered. It is generally recognized that reactions of some kind must occur at the interface in a two-phase diffusion couple, but usually it is assumed that the interface reaction occurs so rapidly that its effect on the overall process is unobservable because the slower diffusion process determines the kinetics of the process. However, Seith and Heumann 2 pointed out that effects of the interfacial reaction should always occur in the early stages of diffusion, and recently Eifert et al. 3 have shown that interfacial reactions influence the composition and motion of the interface in a/ß Al-Cu diffusion couples during the entire course of prolonged, high-temperature treatments. A general procedure for handling the combined processes of interfacial reaction and diffusion in a binary, two-phase system is to introduce kinetic coefficients for the interface reactions and to develop the system of equations governing the interlinked processes of diffusion and interface reaction. The resulting equations, although not amenable to solution in closed form, can be usefully manipulated by a digital computer. INTERFACIAL REACTIONS IN TWO-PHASE DIFFUSION Consider the general case of diffusion between two solid solutions, a and ß, which are adjacent phases in a binary system, Fig. 1. Two semiinfinite bars having compositions c1 and c0ß are jointed at x = 0. If concentrations are expressed in volume fraction,4

Jan 1, 1970

By S. F. Frederick, G. F. Pittinato

The deformation mechanisms operating in Ti-5Al-2.5Sn at 20°K under uniaxial and biaxial stress fields were determined by using both optical and electron microscopy. In the uniaxially stressed specimens, de-fu~rnation twins were found only in the immediate vicinity of the fracture. Twinning was, however, established as a deformation mechanism under biaxial stress conditions. The same slip systems were opera-tiz,e under both uniaxial and biaxial stress. Prismatic slip was identified as the major slip syslem; however, basal and first-order pyramidal slip also occurred, but to a lesser degree. The interaction of moving dis-locations on intersecting slip planes resulted in the formation of jogs and dipoles. Hexagonal dislocation networks were formed only under biaxial stress conditions. A discussion is given on the formation of hexagonal dislocation networks. IT has been shown that titanium alloys can exhibit unusually high strengths when tested in a biaxial stress field.&apos;-" The high biaxial strengths are a consequence of a strong basal plane sheet texture which results in distinctly anisotropic flow properties. This texture strengthening appears to decrease with decreasing temperature2 and would seem to indicate a change in deformation modes. For example, in a uniaxial tensile test, Ti-5A1-2.5Sn yields isotropically at 20°K but is strongly anisotropic at room temperature. The increase in biaxial ultimate over uniaxial strength at 20°K is also much less than at room temperature. It is known that titanium car] form deformation twins more readily at cryogenic temperatures than at room temperature.4 Since the formation of deformation twins will reduce the degree of basal texture in sheet material,&apos; an accompanying decrease in texture strengthening would be expected. To investigate more fully the nature of texture strengthening at cryogenic temperatures, the deformation modes of Ti-5A1-2.5Sn tested in uniaxial and 1:1 biaxial tension at 20°K were studied by optical and electron transmission microscopy. EXPERIMENTAL PROCEDURE The uniaxial and biaxial stress test specimens were prepared from 0.020-in. thick sheets of Ti-5A1-2.5Sn ELI having the composition shown in Table I. Uniaxial stress conditions were obtained by using flat tensile specimens machined from the sheet material. The longitudinal axis of the tensile specimens was aligned perpendicular to the rolling direction of the sheet. Tile biaxial test specimens were prepared by rolling precut, 19-in.-lengths of sheet into 4-in.-diam cyl- inders. Following longitudinal butt welding, the cylinders were stress relieved at 1000°F for 4 hr. A 9-in. sq "window" was then chemically milled into each cylinder&apos;s surface reducing the wall thickness in the milled area to approximately 0.006 in. The testing procedure consisted of pressurizing the cylinders while simultaneously applying a tensile load. Using this technique, a 1:l axial to hoop stress was obtained. Complete details of the specimen and testing procedures are given in Refs. 1 and 2. The biaxial and uniaxial stress specimens were all tested in liquid hydrogen. Specimens for electron transmission microscopy were prepared by first chemically milling to a thickness of about 0.001 in. followed by electrolytic polishing to electron transmission thickness. The chemical milling solution, consisting of 800 ml of water,

Jan 1, 1970

By J. D. Defilippi, E. M. Gilbert, K. G. Brickner

FCC chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Transformation to martensite is considered to be responsible for this behavior in some metastable Cr-Mn-N steels. However, very stable Cr-Mn-N steels also exhibit a ductile-to-brittle transition. The results of this study indicate that deformation faulting is the probable cause of the brittle behavior of stable Cr-Mn-N steels. Deformation faulting accounts for the ductile behavior of these steels in a tension test at -320°F and brittle behavior in an impact test at -320°F. Deformation faulting also accounts for the toPological features observed on the fracture surfaces of impact specimens of these steels. FACE- centered- cubic chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Many Cr-Mn-N steels transform to martensite during deformation,l-5 and several investigatorsl-3 have suggested that the brittle behavior of these steels is caused by martensite formation. However, very stable Cr-Mn-N steels also exhibit brittle behavior. Schaller and Zackeyl reported that a very stable Cr-Mn-N steel (less than 3 pct martensite formed at -320°F) exhibited a transition temperature higher than that for steels in which large volume fractions of martensite formed during testing. The explanation given by Schaller and Zackey for this observation was that in the very stable steel the martensite, because of its higher interstitial content, was more brittle than that formed in their other steels. This explanation was questioned by Tisinai and samans4 and Baldwin.6 Moreover, because the toughness of stainless martensite at cryogenic temperatures is generally very low, this explanation does not account for Thompson&apos;s7 observation that small additions of nickel (1 to 3 pct) greatly improve the toughness of high nitrogen (0.35 pct) Cr-Mn-N steels. The present paper summarizes the results of an investigation of the low-temperature brittleness in very stable Cr-Mn-N steels. The importance of the mode of deformation on the toughness of these steels is discussed. Table I. Compositions of the Steels Invertigated, Pet Steel C Mn P S Si Ni Cr N - A 0.09 14.70 0.018 0.011 0.47 0.22 18.40 0.54 B 0.12 14.90 0.001 0.008 0.48 0.14 17.80 0.38 C 0.12 14.95 0.004 0.005 0.62 3.95 18.43 0.38 MATERIALS AND EXPERIMENTAL WORK The compositions of the steels investigated are shown in Table I. Steels A and B had compositions within the limits of a proprietary Cr-Mn-N stainless steel,* whereas Steel C was similar in composition to the proprietary steel except for its 3.95 pct Ni content. All steels were hot-rolled to 1/2-in. thick plate. The plates were subsequently annealed for 1 hr at 2000°F and water-quenched. Standard longitudinal and transverse Charpy V-notch impact specimens were machined from the annealed plates. Duplicate longitudinal and transverse impact specimens were tested at 212", 80°, 32", 0°, -100°,-160°,-200°,-256", and -320°F. Longitudinal tension-test specimens were also machined from the plates and tested at a crosshead speed of 0.05 in. per min at the aforementioned temperatures. The fractured impact and tension-test specimens of all three steels were examined to determine whether martensite had formed during testing. Magnetic, X-ray, electron-diffraction, and electron-microscopy techniques were used to detect the presence of martensite in the highly deformed areas of these specimens. Metallographic examination of highly deformed areas of impact and tension-test specimens revealed the presence of dark-etching bands, such as those shown in Fig. 1. These bands were observed only in deformed samples and were thought to be associated with the low-temperature brittleness of the Cr-Mn-N steels. Accordingly, a sample 1 in. wide by 3 in. long was cut from the 1/2-in.-thick plate of Steel C. This sample was surface-ground to a in. and then cold-rolled 60 pct at -320°F. Thin foils were prepared from the cold-rolled sample and examined in a JEM electron microscope. Brightfield, dark-field, and selected-area diffraction techniques were used to determine the cause of the dark-etching bands. Fractographic experiments were also performed. Impact specimens Of Steels A, B, and C were broken at -320oF, and the fracture surfaces of these specimens were immediately shadowed with carbon. The carbon replicas were examined in a Siemens electron microscope, and attempts were made to correlate the topological features of the fracture surfaces with the deformation mechanisms that could be occurring during an impact test of these steels.

Jan 1, 1970

By Byoung Whie Lee

In order to investigate the change in surface energy as a function of cold work ad environment, the contact angles between a liquid and the surface of elec-tropolislzed aluminum with various degrees of cold work were measured. Specinlens cut from aluminum rod (99.99 pct Al) were annealed at 600°C for 24 hr and then cold compressed parallel to the drawing di-rectzon of the rod in increments of approximately 10 pcl from 0 to 70 pct. The sections, taken transversely to the drawing direction, were mechanically and electro chemically polished. Contact angles between the sessile drop of distilled water, glycerin, and glycol and the specimen surface were measured optically. The differences in interfacial energy were calculated from the contact angle data. The effects of chemical washing and surface roughness of the specimen on the contact angle were also studied. The liquid contact angle was a linear function of the degree of cold working (D) ad changed markedly with differed liquids. THE plastic deformation of polycrystalline metals induces a preferred orientation in crystal structure. A preferred orientation changes the atomic density of a metal surface. This change in surface atomic density brings about the changes in surface interactions of the metals."&apos; Also, the plastic deformation of metals raises the internal energy by increasing the stored energy.&apos; Consequently, the total Helmholtz free energy of the metal increases and, in turn, the surface free energy of the metal. In order to study the effect of plastic deformation on solid surface phenomena, the liquid contact angle of a sessile drop made on cold compressed and elec-trochemically polished aluminum was measured. The preferred orientation in aluminum, due to uniaxial compression, is known to be [110] direction parallel to the compression axis. However, this description is only a first approximation of a rather complex orientation. In actuality, half the crystallites are more than 10 deg from this orientation, regardless of the amount of compression." For randomly oriented fcc crystals, the average surface atomic density can be calculated as follows: The number of atoms in a unit volume is 4/a3, where a is a lattice constant. Hence, the number of atoms per unit surface area is about (4/a3)2/3 = 2.52/a2 However, when the preferred orientation took place along [110] direction, the surface atomic density is as follows: The area of (110) plane of a unit cell, considering ridges and valleys, is BYOUNG WHlE LEE, Member AIME, is Research Metallurgist, Atomic Energy Research Institute of the Republic of Korea, Seoul, Korea. Manuscript submitted May 29, 1968. IMD 2 x J2- a x Ga = 6a2 Since this plane contains 4 atoms, the surface atomic density is 4i6a2 = 2.3/a2 Upon changing from random to preferred orientations, the surface atomic density decreases about 10 pct. The increase in the stored energy and the change in surface atomic density due to plastic deformation would certainly alter the surface tension of a metal. EXPERIMENT High purity aluminum rod of 6-mm diam (99.99 pct Al, obtained from Johnson, Matthey & Co., Ltd, London, England) was cut into sections approximately 1 cm long. The transverse cross section was mechanically polished. Then, the specimens were annealed in air at 600°C for 24 hr. Thus, eight annealed specimens were uniaxially compressed at room temperature from 0 to 70 pct of cold working with an increment of 10 pct. The extent of cold working was determined by the percentage of reduction in axial length to the original length. The specimens were further polished mechanically and, then, electrochemically with the Modern Battelle Type 1 electropolishing solution with a current density of 0.3 to 0.4 amp per sq cm and an electrode potential of 8 to 12 v at the solution temperature of 78" to 82°C for approxirr~ately 5 min. The Modern Whlte Diffusing Screen \t/ --------------- re Goniometer for Mercury Lamp ^-^ Sessile Drop ¦=• Condenser c=> Microscope l_*~_i bJ Mlcromster Filer with Protmcter Fig. 1—Schematic diagram of apparatus set-up for liquid contact angle measurement.

Jan 1, 1970

By C. W. Kovach, A. Moskowitz

Studies were undertaken to investigate the effects of manganese content on the machinability and other Properties of a free machining martensitic stainless steel (AISI Type 416). Machinability was found to be significantly improved in steels of high manganese content, and a direct relationship was obtained between machinability and steel Mn:S ratio. As the manganese content of the steel increases, the sulfide Phase present changes from CrS to (FeMn)Cr2S4 to (MnFeCr)S, and finally to MnS. The average sulfide inclusion hardness decreases through the same range of increasing manganese content. The mechanism for machinability improvement is discussed in terms of a soft ductile sulfide affecting deformation in the secondary shear zone. Type 416 containing relatively high manganese for improved machinability shows good general properties. The effects of increasing manganese content on mechanical properties, cold formability, and corrosion resistance are described. THE addition of sulfur is commonly used to improve the machinability of stainless steels. However, little attention has been paid in the past to the composition and characteristics of the sulfur-containing phase or phases present in these resulfurized steels. Recent information on the properties of sulfide phases, and their role in metal cutting, suggests that variations in these phases could have critical effects on machin-ability, as well as important effects on formability and other properties such as corrosion resistance. Manganese, chromium, and iron are strong sulfide forming elements present in stainless steels! of these, manganese has the greatest sulfide forming tendency and iron the least.1"1 The manganese content of resul-furized 13 pct Cr steels, often about 0.5 pct, can be insufficient or only barely sufficient to combine with the sulfur that is present; thus, the precise level of manganese can strongly influence the nature of the sulfide phase. Sulfide phases which may be present in stainless steels have been reported to include CrS, a spinel-type sulfide, chromium-rich manganese sul-fide, and manganese Sulfide.5,6 Detailed phase relationships for the Fel3Cr-Mn-S system have been reported by the present investigators,7 and a portion of this work will be referred to subsequently in this paper. Recent work by Kiessling6 and Chao et a1.8 has shown that sulfide phases can display wide variations in hardness, and may undergo considerable plastic deformation under isostatic loading.9-12 Early theories of metal cutting attributed the influence of sulfur to a lubricating effect. It is now apparent that the influence of the nonmetallic inclusions and their properties on crack initiation, deformation in the shear zones, and boundary films must also be considered in relation to the machining process. This paper presents the results of studies conducted to relate machinability to the various sulfide phases which occur in stainless steels. This work has led to the development of alloys with improved machinability, and has generated information on the effects of inclusions on metal cutting processes. Effects of sulfide inclusions and steel composition on other important metallurgical properties are also discussed. MATERIALS For drill machinability and inclusion studies, 10 lb laboratory heats were melted in an air induction furnace. These heats were made with sulfur contents be tween 0.10 and 0.50 pct and manganese contents be tween 0.05 and 3.0 pct. Residual elements were added to the heats in amounts typical for commercial steels. The typical compositional range covered by the heats is shown below: C Mn P S Si Ni Cr Mo Cu N 0.10 0.05 0.007 (M0 0.40 0.40 13.0 0.20 0.10 0.03 3.0 0750 The laboratory ingots were forged in the temperature range of 1800" to 2100°F to 3/4-in. sq bars, and all bars tempered to a hardness aim of 200 Bhn prior to testing. Because of differences in composition and tempering response, the tempered bars showed some variation in hardness (175 to 275 Bhn) as well as variations in delta ferrite content (0 to 50 pct). Composition, hardness, and delta ferrite content were considered in the analysis of the machinability data. Additional tests involving tool-life evaluation and determination of other properties were conducted on materials from commercially melted and processed 15-ton electric furnace heats. TESTS AND PROCEDURES Machinability of the laboratory heats was evaluated in a drill test. In this test, 1/4-in. diam holes, 0.4 in. deep, were drilled alternately in a test bar and in a standard bar for a total of four holes in each. This sequence was repeated three times using a freshly sharpened drill each time. The average time required to drill a hole in the test bar was compared to that for the standard bar. A drill machinability rating was assigned to the test bar relative to a rating of 100

Jan 1, 1970

By Martin F. Littmann

Inclusions of MnS and Fe3C have been introduced into single crystals of 3 pct Si-Fe to study their effects on recrystallization behavior and textures after cold rolling and annealing. The presence of MnS in (110) [001] and (111)[112] crystals inhibited primary grain growth and promoted secondary recrystallization but did not alter the texture significantly after annealing at 1200°C. The presence of Fe3C in (llO)[OOl] and (100)[001] crystals caused a refinement of the primary re crystallized grain size but did not promote secondary recrystallization. THE texture behavior of single crystals of 3 pct Si-Fe during deformation and recrystallization has been studied by numerous investigators. The early work of Dunn&apos; followed by Decker and Harker2 involved relatively small cold reductions. More detailed studies of Dunn3&apos;4 and of Dunn and Koh5&apos;6 involved a reduction of 70 pct and recrystallization at 980°C for several crystals. Walter and Hibbard7 studied a greater variety of initial orientations and sought to relate the textures to those of polycrystalline material. Attention was focused on the nucleation process during early stages of annealing and on surface energy effects in studies by Walter and Dunn8 and by HU.9&apos;10 One of the most extensive investigations has been reported by T. Taoka, E. Furubayashi, and S. Takeuchi.11 Most of this work has been conducted using relatively pure crystals with minimal amounts of precipi-tate-forming elements such as carbon, oxygen, sulfur, and nitrogen. Recently, however, S. Taguchi and A. Sakakura have observed that AIN precipitates can alter the recrystallization textures of rolled (100)[001] crystals.12 The present studies were initiated to determine effects of MnS and Fe3C precipitates on recrystalli-zation and grain growth behavior of rolled single-crystals of 3 pct Si-Fe. Both of these types of inclusions play significant roles in the recrystallization behavior leading to the formation of the (110)[001] or cube-on-edge texture in commercial grain-oriented silicon iron. It is well known that (110)[001] primary grains are formed by recrystallization of (110)[001] or (11 l)[ 112] crystals after cold reduction of about 60 pct or more. Crystals of these orientations, therefore, were selected for study of the effect of MnS in-clusions on grain growth. On the other hand, a major component of the texture of cold-rolled, polycrystal-line 3 pct Si-Fe is the (100)[011] orientation. The function of Fe3,C inclusions is of interest for this orientation. EXPERIMENTAL PROCEDURE The single crystals used are listed in Table I and were obtained from commercial Si-Fe alloy processed to produce (110)[001] and (100)[001] texture by secondary growth. The cube-on-edge material was 0.59 mm thick. Suitably large (110)[001] crystals 25 mm wide were selected and their orientations were determined using an optical goniometer. Etch pits for texture determination were formed by a ferric sulfate solution. The other crystals used in the study with (100)[001], (100)[011], and (111)[112] orientations were obtained from sheet which contained large grains developed from secondary recrystallization by a surface-energy driving force.13 Most crystals had a (100) plane very nearly parallel to the sheet surface and the rolling direction could be selected readily. The same sheet also contained a few crystals with (111) planes parallel to the sheet surface, these also being a result of growth by surface energy. The crystals selected from the sheet were about 25 mm wide and 0.25 to 0.28 mm thick. As shown in Table 11, the crystals already contained about 0.070 to 0.10 pct Mn. Inclusions of MnS were incorporated into crystal 36 in the following manner. The crystals were first sulfurized by holding them Table I. Initial Orientations of Crystals Crystal No. Initial Orientation Thickness, mm Special Treatment 34 (I10) [00l]* 0.59 None 36s (110) [001] 0.59 Sulfide precipitates added 30,40 (111)[Ti21 0.28 None 43s (III) [Ti21 0.28 Sulfide precipitates added 37 (100) [Oll] 0.30 None 37C (100) [01I] 0.27 Carbon added 41 (100) (01I] 0.25 None 41C (100) [OI11 025 Carbide precipitates added 42 (100) [OOl] 0.25 None 42C (100) [001] 0.25 Carbide precipitates added *Tilted 4 deg to r~ght about R.D. Table II. Compositions of Crystals Special Treatments Base Analysis ~ ______________________£________________Crys- Crystals Pct Si Pct C Pct Mn Pct S Pct N Pct Al tal Pct C Pct S 34.36 2.93 • 0.099 <0.005 - 0.0014 36S 0.011 30.37 to 42 2.78 0.0057 0.070 0.001 0.0008 0.0011 43S 0.022 37C 0.029 -41C 0.028 -42C 0.026 *Estimate 0.004 pct. Oxygen estimated <0.003 pct on all samples

Jan 1, 1970

By A. Moskowitz, L. S. Redmerski

The corrosion resistance of stainless steels can be strongly affected by surface treatments. Changes in corrosion resistance can relate to surface composition, integrity and stability of the passive film, and to surface profile (roughness). Operations producing oxidation at the surface, such as annealing, heat treating, and welding, can result in a chromium-rich scale and a chromium-depleted metal surface. In order to restore full corrosion resistance, chemical or mechanical clean-up techniques must remove not only the oxide, but also a very thin layer of metal. Laboratory and field test studies show that these factors are particularly significant in less highly alloyed steels. Annealing stainless in a reducing atmosphere (bright annealing) avoids chromium depletion, but as-bright-annealed material does not display optimum corrosion resistance in certain environments. Electro passiva-tion can be applied to improve pitting resistance without significantly changing bright surface appearance. Potentiometric studies show that electropassivated material also displays significantly greater resistance to breakdown of passivity in acid solutions. The application of special surface finishes for appearance purposes can affect corrosion resistance. Roughness is a key factor. Samples of related appearance but with different surface profiles can show significant differences in corrosion resistance. Thus nonreflec-tive stainless with a relatively smooth surface produced by a special rolling process is much superior to material chemically etched to a similar low reflectivity. THE corrosion resistance of a stainless steel is affected by other factors in addition to its bulk composition and metallurgical structure. These other factors include those relating to the specific chemical and physical condition of the steel&apos;s surface. This paper will consider certain aspects of surface condition in relation to corrosion resistance. In particular, studies will be described on the effects of oxidation encountered in heat treating or welding operations, of passivation after bright annealing, and of different surface finishes. EFFECTS DUE TO OXIDATION When stainless steels are exposed to high temperature in an oxidizing environment, as in annealing or welding, the oxides formed are relatively rich in chromium. As a consequence of oxidation, the metallic layer directly beneath the scale may be low in chromium to some very thin but finite depth.1"8 Such a change in chromium content could lower the corrosion resistance at the surface, whether or not the oxide layer is removed. Studies were performed relating to the effect of oxidation and chromium depletion produced during annealing and welding on the corrosion resistance of stainless steels. The nominal compositions of steels used in this study and others are given in Table I. A) Annealing Studies on 17 pet Cr Steels. 1) Effects of Pickling Treatments. Studies were performed to investigate the corrosion resistance of air annealed type 430 stainless as a function of the amount of electrolytic pickling after annealing. The material used in this study had been air annealed and electrolytically pickled in the mill. All scale had been removed, and yet the material showed unusually poor corrosion resistance. Laboratory electrolytic pickling studies were performed to determine whether additional metal removal from the surface would improve corrosion resistance. Electrolytic pickling was performed in a sulfuric acid bath using various conditions of bath acidity, temperature, time, and current density. The samples were then rated for corrosion resistance in a ferric chloride spot test. For this spot test, a solution was prepared by dissolving 10 g of FeCl3 . 6H2O, 5 g of NaCl, and 2.5 ml of concentrated HC1 in 200 ml of water. An area on a specimen was cleaned and a drop of test solution was placed on the prepared area. After 5 min, the drop was rinsed off and the area wiped dry. The spot was then rated between 1 and 5 by visual comparison with standard spots. The numerical rating of the standard spots can be described as follows: 1—No clouding of surface; 2—very slight clouding of surface; 3—slight clouding of surface; 4—moderate clouding of surface; 5—strong clouding of surface. A rating of 1 or 2 was considered to have passed the test, a rating of 4 or 5 represented failure, and a rating of 3 was considered borderline. The severity of etching in this test has been related to the actual chromium content at the surface.4 Etching (clouding) occurs on type 430 stainless (rating of 4 to 5) when the surface chromium content is 14 pct or less. The effects of current density and retention time when electrolytically repickling this material in 6 pct sulfuric acid are shown in Fig. 1. Increasing the cur-rent density or retention time improved corrosion resistance as measured by the spot test. Similarly, increasing acid concentration of the bath or bath tem-perature was found to improve corrosion resistance. The conditions making for improved spot ratings resulted in increased metal removal, regardless of specific pickling conditions used, Fig. 2.

Jan 1, 1970

By M. M. Wong, D. E. Couch, G. M. Martinez

The Bureau of Mines electrowon hafnium metal with an average oxygen content of&apos; 150 ppm at 700°C from an electrolyte containing 27 wt pct LiCl, 62 wt pct RbCl, and 11 wt pct HfC14. The average anode and cathode current efficiencies were 90 pct at anode and initial cathode current densities of 86 amp per sq ft. Haf-nium metal with an average oxygen content of 440 ppm was electrowon at 800oC from an electrolyte containing 90 wt pct KC1 and 10 wt pct HfCl4. The average anode and cathode current efficiencies were similar to those obtained in the LiCL-RbCl-HfCl, electrolyte. The chlorine gas given off at the graphite anode was vented through either a silica or a graphite tube to prevent cell corrosion. THE current method for the commercial production of high-purity hafnium is the thermal decomposition of Hfl4.1 The iodide method is not adaptable to continuous process techniques. Nettle, Hiegel, and Baker2 studied the electrorefining of hafnium from hafnium sponge containing 800 ppm oxygen. They failed to obtain hafnium with 600 ppm oxygen in their initial deposits and obtained AEC specification for oxygen only after 75 pct of the soluble hafnium had been removed from the electrolyte. Calculations using their data indicated this was approximately 4 lb of hafnium. The electrolyte was then used to produce approximately 3 lb of hafnium with a low oxygen content. However, no data are shown concerning the amount of anode material initially used or what percent of it was dissolved, therefore, results are not suitable for evaluation of a continuous operation. In general, it was not possible to consistently obtain low oxygen content metal with the electrolytes described by Nettle, Hiegel, and Baker. Wong, Hiegel, and Martinez3 investigated the electrorefining process for hafnium and showed that even by strict control of electrolyte composition only relatively low oxygen reduction could be obtained. The oxygen contained in the hafnium anode material tended to transfer to the cathode deposit and only a limited purification was possible. Both the "iodide" and the "electrorefining" processes depend upon hafnium sponge as a starting material. The sponge is normally produced by magnesium reduction of HfC14 &apos; and does not meet AEC specifications for hafnium metal. Since only 30 pct of the anode feed could be utilized3 in the electrorefining cells, the Bureau of Mines developed an electrowinning process. HfC14 was used as the feed material for the electro-winning process described in this report. Many of the electrolytes used in the electrorefining studies3 ap- peared to be suitable carrier-electrolytes for HfC14. However, in the initial studies on electrowinning, it was desirable to use electrolytes that had low solidus temperatures and could be operated over a wide temperature range to investigate parameters of the process. Therefore, electrolytes containing LiC1, NaC1, KC1, RbC1, CsC1, and HfC14, in various combinations were explored. EQUIPMENT Chlorinator. Hafnium carbide was chlorinated to produce HfC14 in the batch-type chlorination shown in Fig. 1. Chlorination temperatures were measured with a thermocouple placed in the center of the HfC charge. A flow meter was used to monitor the helium and chlorine. The exhaust side of the silica chlorina-tor tube was equipped with a flask for collecting organic material released during the initial heating of the HfC. The temperature of an internal heater, which extended from the HfC14 condensing flask to the hot end of the chlorinator, was adjusted to prevent the HfC14 from condensing before entering the collection flask. Helium and excess chlorine were exhausted through the lid of the collection flask to an aqueous NaOH solution. Sublimer. Initial studies were conducted using a sublimer, Fig. 2, made by placing a 13/8-in. OD nickel thimble 11 in. long, inside a 11/2-in. ID nickel bell 12 in. long, and locking it in place. This unit was loaded with HfC14 and partially immersed in the molten electrolyte for sublimation directly into the electrolyte. In another sublimer shown in Fig. 3, the HfC14 was contained in a "resin reaction flask". Quartz wool, previously heated to 600aC, secured between two nickel wire screens, was placed just above the HfC14 powder. The lid contained a vacuum outlet, a gage, an argon inlet, and an air-cooled pipe for condensing the HfC14. This sublimer was evacuated and heated. The sublimation temperature was not critical and the sublimer operated satisfactorily at all temperatures between 250" and 350°C. Electrolytic Cell. The electrolyte chamber, Fig. 4, was made of mild steel 8-in. schedule 20 pipe, 30 in. long. The exterior was metallized with a Ni-Cr alloy. The electrolytes were contained in a 16 gage nickel or iron liner with a nickel heat shield on top. The cell was heated by a resistance furnace. A 21/2-in. ID by 25 in. long air lock was connected to one port of a two-port cell cover assembly through a slide valve. The cover assembly of the air lock was electrically insulated from the cell and was equipped with a rubber sleeve that provided for the passage of the cathode lead. This allowed the cathode deposits to be removed and a new nickel cathode to be introduced without allowing air to enter the cell. A tube-rod assembly was bolted to the other port on the cell cover assembly and was sealed by a packing seal. The tube-rod assembly consists of a graphite

Jan 1, 1970

By Richard A. Walker, John P. Hager

The thermodynamic properties of the Pb-Au system have been determined between 750" and 1075°C by means of the cell Mo, Pb(1) |(PbO-SiO2){l) , SiO2(s) |Pb-Au(1), Mo The activities of lead and gold exhibit negative deviations from ideal behavior; the values of ? pb and ? the raoultain activity coefficients at infinite dilution, being 0.24 and 0.25, respectively, at 1200°K. The liquidus curve for the gold-rich region of the Pb-Au phase diagram has been determined from measure-ments on seven alloy compositions in the two phase region (liquid + Au(s)). The standard free energies of formation of Au2O(l) and Ag2O (1) have been estimated from cell measurements obtained by replacing the alloy electrode with pure liquid gold and silver. A new integral molar heat of mixing curve for the liquid Pb-Au system is presented and the results of previous studies discussed. The contribution of HM to FE was found to be small relative to TSE. THE use of galvanic cells of the type A(l) |A+Za|A - B(l) [I] provides an accurate means for the thermodynamic study of liquid alloy systems. In Part 1&apos; it was shown that cells of type [I] may be extended to higher temperatures and to a wider range of alloy systems if the ion A+Za is incorporated in an appropriate molten oxide phase, rather than in the classical fused salt electrolyte. In the following investigation the experimental method is extended to an investigation of the thermo-dynamic properties of the Pb-Au system by use of the cell: Mo, Pb(l) | (PbO-SiO2)(l), SiO2(S) |Pb-Au(l), Mo [] Previous measurements on liquid Pb-Au alloys were obtained by Kleppa2 by electromotive force measurements on a galvanic cell involving a molten chloride electrolyte. These measurements were confined to temperatures less than 830°C and compositions with X Pb > 0.2 because of the instability of the cell at higher temperatures. Later measurements by Kleppa3 on the heats of formation in the composition range 0.67 < Xpb < 0.98 were not consistent with the results by electromotive force measurement. The purpose of the present study is to extend the temperature and composition range of the thermodynamic properties and to obtain an independent measure of the integral molar heat of mixing over the entire composition range.

Jan 1, 1970