By A. K. Schellinger, R. D. Lalkaka

IF the ball mill is considered only from an energy standpoint, it can be thought of as a converter of kinetic energy into heat energy and surface energy. The law of the conservation of energy must apply to the ball mill as it does to any machine or process in nature. The heat energy output of the ball mill is apparent to any casual observer of the operating mill since the outflow pulp will be appreciably warmer than the inflow water and rock. The rock in the ball mill is crushed by shearing of its ionic bonding caused by some impact-induced stresses beyond the elastic limit. As the bonds holding the mineral crystal lattices together are ruptured, new surface area is created on each unit of which a definite number of unsaturated bonds exist. Such unsaturated energy of bonding may be termed the "surface energy," and is a potential energy figure. This created energy was withdrawn from the ball mill system and represents an absorption, or disappearance of heat. To reduce the size of the rock, surface area must be created and with it the at- tendant characteristic surface energies of the minerals concerned. Thus the creation of surface energy, from an energy viewpoint, is the creation of useful work by the ball mill. Because of the controversial nature of the energy efficiency figures for modern operating ball mills, it seemed worthwhile to approximate the ordinary magnitude of such efficiencies from the above viewpoint. This was done by an energy balance of the three aforementioned forms of energy, kinetic, heat, and surface energy, for two 9Y2x10-ft grate-type ball mills grinding cement raw materials. Kinetic energy input to the balls was approximated as closely as possible while the heat energy output was measured by means of a thermometer and water and rock flow rates. The assumption was made

Jan 1, 1952

By Robert L. Slobod

In much of the work reported in the literature on long cores. true connate water value, probably have not been obtained because of insufficient flow of 011 to attain equilibrium. A -.satisfactory method for establishing connate water in long cores has been developed in which oil flow is maintained until no additiona1 water is displaced. INTRODUCTION Long cores have been used by sev-erals investigators in an effort to evaluate the efficiency of oil recovery for various producing schemes. The effects of many variables such as rate of displacement. pressure drop, volume of displacing medium, gas-oil ratio, inter-facial tension, and others have been investigated, and the merits of gas drive have been compared with water drive. In the older experiments no connate water was used. but in the more recent stndies the philosophy of the experiment calls for a core containing oil and connate water (irreducible water) as the starting point of the experiment. The method generally used to establish this condition in long cores involves dynamic' displacement wherein one or more phases are forced through the core. flow being maintained at a constant rate or at a constant pressure until a steady state is reached wherein there is no change of saturation with time. It is one purpose of this paper to point out that in much of the work reported in the literature true connate water values probably have not been obtained. The reason for this failure is pointed out. and a method for obtaining more reliable connate water values on long cores is presented. It is impossible at this time to completely evaluate the effect on the conclusions in the earlier papers resulting from the failure to obtain true connate water in the long cores, but some data are presented which indicate that serious errors may he present in many cases. MATERIALS AND APPARATUS Cores cut front outcrop sandstones (Strawn. Torpedo, and Elgin sandstones) with permeabilities of the order of 300 md were used. The major experiments were made with a core 18-in. long and 2-in. in diameter. Cores of the same diameter but only 12-in. long were used in a few tests? and in some work a core I-in. in diameter and 11-in. long was used. These materials were all somewhat bentonitic. 'To reduce the effect of such constituents, one of the cores (Torpedo No. 10) on which the most work was performed was acid extracted at the start of the experiment. Brine containing 50,000 ppm chloride and naphtha (Stoddard's Solvent) were used as the water and oil phases, respectively. The core was mounted in a rubber sleeve which forms the inner lining of a brass cylinder. In this arrangement2 the rubber sleeve is forced against the core by applying pressure to water in the annular space between the rubber sleeve and the brass cylinder wall. The core is therefore sealed in rubber so that all fluids introduced at the input end of the core flow through the core. With this equipment the core may be easily removed for inspection and analysis. Also, other cores may be introduced for study with no extra time for preparation such as is required when plastic mounting is used. When pressure or conductivity measurements are desired at intermediate points along tile length of the core, the brass cylinder comprising the outer jacket of the core holder is cut into section, of the desired length. Each section is then made up as an individual unit with its own rubber sleeve (see Fig. 1). The individual units are then butted up against a ring of plastic or other insulating material which carries an electrical contact for resistivity measurements and an opening which can be used for the measurements of fluid pressures. The individual units are forced tightly against the plastic ring separators and held in place with several tie rods. Inlet and outlet end butts of the same diameter as the core and several inches in length are provided to control the introduction and withdrawal of fluids and to complete the arrangement for sealing the core within the rubber sleeve. Fluid flow is maintained either by applying pressure to the liquid confined in a reservoir or by the use of a gear pump. The latter is preferable where continuous flow at a moderate rate over a long time interval is desired since a small volume of liquid can be readily recirculated using filters to prevent plugging of the core. EXPERIMENTAL The oven-dried core is weighed and is then completely saturated with brine

Jan 1, 1950

By H. Krueger, H. N. Hersh

USE of autoradiography in diffusion studies offers the advantage that no repeated sectioning is necessary and that the analyses are performed in a simple manner over the continuous range of penetration depths. As part of a program of solid-state physics, it was desired to develop the autoradio-graphic method' quantitatively for use in diffusion studies. Results are reported here for the self-diffusion of silver. Silver was chosen because the existing data are good enough to evaluate the technique." The silver used in this investigation was obtained in the form of ¼ in. diam rods of polycrystalline material, 99.99 pct purity. The radioactive silver, Ag110 (ß, y), was obtained as the nitrate and converted to the chloride for use in a standard cyanide plating bath. The diffusion specimens were 1/2 in. lengths of the rod. They were mounted in bake-lite and the exposed circular face carefully ground and polished. Prior to electrodepositing radioactive

Jan 1, 1956

By R. Greenwood

The advent of the space age and its promise of interplanetary flight has prompted new ideas for propulsion systems that will allow maximum energy with minimum fuel weight. The use of cesium as the source of energy for such rocket flights has been found desirable. Theoretical efficiency of a rocket fuel is measured in terms of specific impulse, defined as the number of pounds of thrust per pound of propellant consumed per second. Specific impulse is usually expressed in seconds (the number of seconds for which one pound of fuel would produce one pound of thrust) although it is really a measure of total energy, not of power. The most sophisticated chemical fuels have a specific impulse of 300 to 400 sec; liquid hydrogen heated by nuclear reactor has a specific impulse of 1000 to 1200 sec. Specific impulses as high as 20,000 sec, however, are theoretically attainable with the ion rocket, in which free cesium ions are accelerated across a voltage drop and ejected at high velocity.' Characteristics of the system have been sketched by Boden.2 The desirable properties of an ion propellant are: 1) low ionization potential, 2) low boiling point, and 3) high atomic weight. Alkali metals best fulfill these requirements, and Table I indicates the superiority of cesium. The use of heavy complex ions such as UCl3 is ruled out by their instability and other disadvantages.' Despite its enormous superiority in specific impulse, the ion rocket is inherently low-powered, capable of very small acceleration. Application of ion propulsion will be limited to large rockets and spaceships on missions requiring powered flight for weeks or months and employing a separate chemical propulsion system for escape from the earth's atmosphere where power requirements are large but of brief duration. For example, Kraemer and Larson3 considered the case of an unmanned 25,000-lb pay-load placed in a 300-mile orbit by chemical rockets, proceeding thence by ion propulsion to the vicinity of Mars, where it would go into orbit once again. Calculations provide for 8500 lb of cesium for such a voyage. The question of whether such quantities of cesium will be readily available to the space program does not appear to have been considered by geologists and mining engineers. Present Production and Uses Literature on industrial applications of cesium is scanty. The metal is used in scintillation counters, photocells, infra-red detection devices, and as a "getter" in low-voltage vacuum tubes. Production is sporadic and total figures are not published, but the annual consumption is measured in pounds rather than in tons. The few pollucite deposits known, small as they are, can easily supply the present limited demand for gram or pound lots of cesium. Until recently the price of cesium was $2 to $4 per gram, but according to Chemical Engineering, cesium salts are now available at $13 to $27.50 per lb. Geochemical Distribution As a large alkali ion, the cesium ion accompanies potassium in geological processes and tends to be concentrated in the latest crystallizing fractions of potassium minerals in much the same manner as rubidium. Most of the cesium in igneous rocks, therefore, is in the micas and potash feldspars of granites, and especially in granitic pegmatites. The cesium content rises markedly in the micas of the late by-drothermal replacement stage in complex pegmatite~.' Typically, cesium is only 0.5 to 0.01 times as abundant as rubidium in potassium minerals. Rb', with a radius of 1.47 A, is close enough in size to K' (1.33 A) so that rubidium forms no minerals of its own. Cs+ is so large (1.67 A) that only small concentrations can be taken up in potassium minerals; when cesium is present in solution in larger concentration it forms the mineral pollucite, Cs3-Na2A17Si17O48.3H2O, which is known only in pegmatites. In the weathering of igneous rocks, cesium is dissolved, carried to the ocean, and apparently in-

Jan 1, 1961

By H. I. Aaronson, C. Wells

THIS is a preliminary report on a detailed metal- lographic investigation of the bainite reaction in a plain carbon hypoeutectoid steel. In view of the current interest in the bainite reaction and of the controversies which still exist about even the basic phenomenology of this mode of transformation, it was considered desirable to present a summary of the more important results obtained to date prior to the completion of this investigation. The steel used contained 0.29 pct C, 0.76 pct Mn, 0.25 pct Si, 0.005 pct P, and 0.007 pct S. The alloy was homogenized for 48 hr at 1250°C. Individual specimens were then austenitized for 30 min at 1300°C and isothermally transformed for various times at temperatures above and within the bainite region, ranging from 775" through 500°C at intervals of 25°C. These specimens were carefully examined on a research metallograph; a few specimens of especial interest were also studied electron microscopically.' Bainite may be defined as the aggregate structure resulting from the precipitation of carbides from supersaturated ferrite which formed by nucleation and diffusion-limited growth. Two groups of experimental observations made during the present study provide support for this mechanism of the bainite reaction: 1—at 625°C, partial conversion of pro-eutectoid ferrite to bainite began after more than 99 pct of the austenite had decomposed and 2—the precipitation of bainitic carbides occurred only within the ferrite phase. The proeutectoid ferrite and the bainite reactions in the steel studied were found to be morphologically continuous. Following the classification scheme of Mehl and Dube,2 three principal morphologies of proeutectoid ferrite were identified in the temperature region (625" to 550°C) in which the two reactions blend—grain boundary allotriomorphs," * Grain boundary allotriomorphs are crystals which nucleate at and grow preferentially along matrix grain boundaries. Widmanstaetten side plates, and intragranular plates. Carbide precipitation converted these morphologies into their bainitic equivalents with increasing isothermal reaction time. Conversion took place more rapidly as the reaction temperature was reduced. The replacement of supersaturated ferrite by bainite, however, did not occur uniformly even within individual austenite grains and was noticeably incomplete at higher transformation temperatures, e.g., 625° to 575°C. The ferritic and bainitic forms of a given morphology thus were frequently found to coexist, often inextricably intermixed, in a given specimen. At 625" and 600°C, the conversion of ferrite to bainite was clearly seen to have occurred entirely by the nucleation of carbides at ferrite/ferrite boundaries, as shown in Fig. 1. The nature of the loci at which carbides formed at lower temperatures was often difficult to ascertain with a light microscope, although the alignment in rows of many of the carbides, illustrated in Fig. 2, suggested that nucleation had again occurred at grain boundaries or subboundaries within the ferrite. Application of the electron microscope confirmed this deduction for bainitic structures formed at these temperatures, as shown in Fig. 3. The dense black appearance of bainite formed at very low reaction temperatures in higher carbon steels3 indicates, however, that isolated lattice defects within ferrite crystals prob-

Jan 1, 1956

By William Loblowitz

A simplified system of flotation testing has been developed recently at the Bureau of Mineral Research of Rutgers University. The technique involves the known principle of skin flotation and can be used with minute quantities of sample and reagents in a beaker. A vessel containing the conditioned sample with added water and flotation reagents is held inclined and rotated slowly. Water-repellent particles come in contact with air and float on the surface of the liquid, while wettable particles are submerged. The float is poured off and filtered whereas the nonfloat remains in the beaker. The filtrate may be returned to repeat the process. This procedure can be made quantitative. Separations are obtained and are remarkably complete and repeatable. The effect of different reagents, optimum quantities, pH and other variables can be determined in a fraction of the time required for conventional testing. However, the method gives no information on the effect of frothers and the quality of froth to be expected in a cell, and it is not practical for particles finer than 200-mesh. Unlike other preliminary tests, separate float and nonfloat products are obtained, and their contents can be determined quantitatively by chemical analysis or grain counts. After the optimum reagent combination has been determined, the effect of fines and frothing may be verified in the conventional flotation cell. On the other hand, agglomeration-tabling can be directly duplicated from beaker tests. Procedure: Five to ten grams of sample are weighed into a 100-ml beaker. Flotation reagents and a small initial quantity of water are stirred together; additional water is then added to produce the proper water-solids ratio. The beaker is then tilted to 45" and rotated slowly. After three to five rotations, liquid and float are poured off and filtered; the filtrate may be recycled until the separation is completed. One test generally requires less than 10 min. Reagent concentration and pH remain quite constant because of the recycling of the filtrate. Two to four tests may be made simultaneously, and the effect of varied conditions may be observed by comparison. Considerable time is saved in preparation and handling since small quantities of sample suffice for a series of systematic tests. Repeatability One test was repeated four times under constant conditions. The sample used was a quartz sand containing approximately 24 pct feldspar and some clay aggregates. The +28-mesh grains had been screened out, and most of those finer than 100-mesh had been removed by hydraulic classification. The results are presented in Table I. For comparison, 500 g of the sample were separated by agglomeration-tabling using the same reagent combination and quantities as given in Table I. The weight percent float was 18.3 pct, composed almost entirely of feldspar and with only traces of quartz. Most of the remaining feldspar was recovered in a middling product with 2.2 pct by weight.

Jan 1, 1952

By J. A. Jaekel, W. C. Aitkenhead

Uranium deposits in the Spokane Indian Reservation, as well as those around Mt. Spokane, are essentially low grade, much of the ore containing less than 0.2 pct U3O8. The Mining Experiment Station of the Division of Industrial Research, State College of Washington, has been engaged in intensive research on the amenability of these low grade ores to froth flotation. The results: successful flotation of autinite, chief mineral constituent. At the outset of this work the goal was a concentrate of 1 pct U3O8 with a 90 pct recovery from ores containing less than 0.2 pct U3O8. Most of the work has been done on argillite ore from the Midnight mine on the Spokane Indian Reservation. The goal has not been attained using this ore, but samples of the granite ore from Mt. Spokane yielded successful results. For example, a concentrate containing 11.2 pcl U3O8 was produced from a Mt. Spokane high grade ore containing 1.27 pct U3O8 with a recovery of 97.8 pct. Another Mt. Spokane ore yielded a concentrate of 5.0 pct U3O8 from an ore containing 0.13 pct U3O8. with a recovery of 85 pct. This same ore gave a recovery of 93.5 pct when the grade of concentrate was reduced to 2.0 pct. It has been concluded that a successful method for floating autunite has been developed and that the mediocre results from the Midnight argillite ore are probably caused by the presence of some other uranium mineral or minerals less amenable to these reagents. The experimenters tested a third type of Washington ore, found on the Northwest Uranium Mines Inc. property on the Spokane Indian Reservation. This is a conglomerate of pebbles and small boulders of partially decomposed granite and is shot through with autunite. Its characteristics lie between those of the Midnight ore and the granite ore from the Spokane district. It responds better than the ore from Midnight but not as well as that from Mt. Spokane. As the fatty acids are the only type of collectors showing promise, investigation has been concerned with these acids and the optimum conditions for their use. The first method for treating the argillite ore from the Spokane Indian Reservation made use of Cyanamid's R-708 as a collector, a tall oil product described as a substitute for oleic acid. Although the investigators proved that R-708 is a collector for autunite when mixtures of autunite and silica sand are used, results on the ore were mediocre. Tests of other fatty acids revealed that the solid fatty acids of the saturated series are collectors for autunite and that their collecting power increases with the length of the carbon chain. The even carbon members of the whole series were tested from the 10 carbon acid (capric) to the 22 carbon acid (be-henic). The least expensive collector, stearic acid (18 carbon), proved to be a good one, so this was used in most of the tests. In first attempts with stearic acid, the collector was dissolved in various hydrocarbons and the solutions were added to the flotation cell. Cyclohexane, gasoline, fuel oil, kerosene, and other solvents were tried. Small amounts of high grade concentrates could be brought up, but recoveries were low. Finally emulsions of stearic acid were tried. It was discovered that stearic acid alone has little collecting power except when conditioning is carried out at high temperature. When hydrocarbon solvents were also present, it proved to be an excellent collector. An example of one emulsion that proved satisfactory for some ores is given as follows: 1 part stearic acid by weight, 1 part sodium oleate by weight, 1.2 parts kerosene by weight, 100 parts water. In some successful tests part of the stearic acid was replaced by oleic acid. The emulsions were made by agitating the stearic acid and sodium oleate together with hot water, then adding the kerosene and agitating while cooling. In the five tests reported in Table 1, 650 g of ore were ground with 650 cc water in a laboratory rod mill. The pulp was filtered to eliminate excess water and the ground ore transferred to a stainless steel beaker for conditioning at high pulp density. In most of the tests sodium hydroxide was added to the conditioner during agitation, then the collector emulsion, and finally the sodium silicate. The amount of alkali was adjusted to give a pH of 8.5 to 9.0 in the flotation cell. After conditioning the pulp was transferred to a laboratory flotation cell and the test completed in a normal manner. It is interesting to note that a deposit of high grade concentrate forms on the conditioning agitator and in the conditioning vessel, and at times on the agitator of the flotation cell itself. A few grams of concentrate running as high as 4 pct U3O8 were recovered from the conditioner when Midnight ore containing less than 0.2 pct U3O8 was treated. In the examples given in Table I this conditioner concentrate is calculated as part of the total concentrate. The authors have not yet fully explored the possi-

Jan 1, 1960

By Robert R. French

Beneficiation of low-grade nonmetalliferous mineral deposits by electronic color sorting is currently undergoing a period of rapid development. For those deposits in which the specific gravity, strength, soundness, and electric and magnetic properties of the ore and gangue are similar, the possibility of separation by color, reflectivity, or fluorescence offers hope for the utilization of much poorer quality ore than previously thought possible. For those ores in which consistency of color is required or for which a dry process is preferred, the electronic color sorter is particularly adaptable. Tests performed late in 1966 and reported herein are the result of continued interest in the dry beneficiation of gypsum and the development of higher capacity color-sorting machines. These tests should be considered only as an indication of the efficiency of the process and only with respect to the low-grade, untreated ore tested. Although most of the ore mined in Martin County, Ind., is of acceptable quality, a few thin carbonate strata and irregular nodules of dolomite and limestone are present within the main evaporite bed (Fig. 1).

Jan 1, 1969

By Nicholas J. Grant, Ernest P. Abrahamson

IN recent work, Bloom and Grant' and Stein and IGrant' have indicated that a high temperature chromium phase exists. In the 68 pct Cr-Ni binary they found a eutectoid reaction, P chromium transforming to a chromium plus y nickel at 1215°C. Un-

Jan 1, 1957

By J. B. Seabrook

The accompanying Fig 1 is a graphical scheme of intermediate accuracy for expediting interconversions of mol, weight, and volume percents. This chart consists of a family of curves of mol or atomic or volume percent plotted against weight percent, each curve in the family providing for a certain ratio of molecular or atomic weights or densities. Thus, the whole range of variations is presented in a very familiar format, and the conversion is effected simply by choosing the proper curve and reading off the required values. An entire series of conversions for a given binary system can be found by following the appropriate curve. It is interesting to examine the analytical geometry of the plots. The curves, which must fit into a square and all join at the 0 and 100 pet points, may be shown to be hyperbolas with their centers on the extension of the diagonal of the square which they intersect. Multiplying out the expression x A atomic fraction of A = y = ------ where x is the weight fraction of A, and A and B are atomic weights, we get xy+A/By- A/Bxy=x Upon rotating and translating axes and avoiding imaginaries, it is found that the angle of rotation is —45°, the origin moves upv2/2 units andv2/2(A/B+1/A/B-1) units to the right, and the standard form is Thus the curves are equilateral hyperbolas, their centers are units away from their intersection with

Jan 1, 1950

By C. W. Spencer, R. A. Rummel, F. N. Rhines

SPECIMENS of five cast Cu-Bi alloys, containing 4.68, 0.53, 0.043, 0.0064, and 0.0025 wt pct Bi and cast pure copper were subjected to a bend test to determine their relative ductility. Using metallo-graphlc methods the structures of the fractured surfaces were compared with those of the polished cross sections. Embrittlement was found to be associated with the presence of a second phase in the grain boundaries although, in the lower bismuth

Jan 1, 1958

By Robert J. White

Strong's equation for calculating bottom-hole pressure reduction due to gas cutting of drilling mud is corrected, resulting in a simpler equation which is easier to use. Use of the equation is illustrated by examples. It is shown that reduction of weight of a 10 lb/gal mud by 50 per cent at the surface due to gas cutting produces only n 3 per cent decrease in hydrostatic head at the bottom of a 5,000-ft well. It is also shown that at the surface 5 volumes of air per volume of mud are required to reduce the apparent mud weight from 8.5 to 6.5 lh/gal in a 3,000-ft well. Illustrative graphs are included to show the effect of various degrees of gas cutting on apparent mud weight at depths of 2,000, .5,000 and 10,000 ft and to show variation of apparent mud weight, with depth for a 100 lb/cu ft (13.37 lb/gal) mud gas cut to 90 lb/cu ft (12.03 lb/gal) at the surface. INTRODUCTION In 1938, Strong' published the following equation for calculating reduction in bottom-hole pressure due to gas cutting of drilling mud h = 1/D [p + pn/100 In p + p(1-n/100)/p(1- n-100)] where: h = depth in feet P = pressure in atmospheres at depth h due to mud column only D = hydrostatic pressure in atmospheres of a col-umn of uncut mud 1 ft high p = back pressure at well-head (in atmospheres) n/100 = fraction by volume of gas in mud at well-head at back pres-sure p This equation was recently found to contain an error due to an incor-rect expression for variation of vol-ume fraction of gas with pressure. Values calculated by the original equation are close to the correct values for small percentages of gas for which it was derived but become increasingly erroneous as the gas content increases and are completely unusable at the very high gas con-tents employed in aerated mud. DERIVATION The nomenclature used is the same as in Strong's paper. The pres-sure dP exerted by a lamina of thickness dh at a depth h ft is ex-pressed by Eq. 1 where x = volume fraction of gas at depth h dP = D (l - x)dh . . . (1) When we express x in terms of the wellhead per cent gas n, the well-head pressure p and the pressure P at depth h, the result is Eq. 2. x = (np/p+p)/(100-n) + (np/P + p) When this is substituted in Eq. 1 and rearranged to separate the var-iables the result is dh = 1/D [dp + np/100-n dp/(P + p]. Integration between appropriate lim-its results in or if the wellhead is open so that p = 1 atm and we rearrange Eq. 4, the result is loss in head = hD — P = n/100-n In (P + 1) ...(5) Eq. 5 can be solved easily by successive approximation using hD as a first approximation for P on the right-hand side and calculating a first value for loss in head. This can then be used to get a new value of P using the left-hand side of the equation. Values converge very rap-idly even for quite large values of per cent by volume gas n. EXAMPLES The effect on bottom-hole pressure of 50 per cent gas cutting of the mud in a 5,000-ft well using 10 Ib/ gal mud will be calculated, we have: h = 5,000 ft 10 X 7.48 144 X 14.7 = 0.0353 atm/ft hD = 176.5 atm n = 50 Substituting these values in Eq. 5 and using hD as a first approxima-tion of P on the right, we have, approximate loss in head = 50/50 In (176.5 + 1) = 2.30 log 177.5 = 5.17 atm. We calculate a new value of P as follows:

Jan 1, 1958

By A. Zomosa

In the operation of continuous countercurrent decantation it is well known that an increase in the number of thickeners results in an increase of the fixed costs. But inversely it happens that the variable costs are reduced, i.e. the valuable material has a better recovery. The aim of this paper is to solve the problem by means of an economic balance of both parameters, in order to determine the optimum number of stages.

Jan 1, 1991

By David Cornell

Back pressure test data on natural gas wells are short time test data of unsteady state nature. Performance curves from which unsteady state effects have been eliminated, called stabilized performance curves, are necessary for understanding the behavior of gas wells and for scheduling gas fields for periods up to 20 years. A calculation procedure has been developed whereby three day, seven day, 30 day, or other duration stabilized performance curves may be calculated from back pressure test data. Such curves are essential for correct gas deliverability calculations and gas field scheduling. I NTRODUCTION The manner in which a back pressure test is made will affect the slope of the back pressure curve because the radius of drainage changes with the length of time that the well is allowed to flow. The reciprocal of the slope of the back pressure curve is defined as n in Equation 1 and varies from 0.5 to 1.0. If the flow is viscous and the radius of drainage constant, n will have a value of 1.0. Because of turbulence in the formation near the wellbore, the pressure drop is usually greater than the viscous flow pressure drop and the exponent n is frequently less than 1.0. In addition, since the radius of drainage moves away from the well-bore during the test, the gas flows a greater and greater distance as the test proceeds, with a resulting increased pressure drop at the high flow rates, and, again, n for the test tends to be less than 1.O. The effect of the changes in the radius of drainage may be calculated and the results used in preparing stabilized performance curves for fixed values of the radius of drainage. Such curves can be made for a defi- nite time period, such as three day, seven day, or 30 day stabilized performance curves. These cukes will show the effect of turbulence near the wellbore and can be used to predict the performance of the gas well at any flow rate or for any production period. In order to discuss the importance of the radius of drainage quantitatively, it should be defined. Muskat" defines the radius of drainage as follows: "... the radius of drainage gives the distance from the well to which the approximately steady state condition has been established ... it being assumed that no gas is removed from any point until the radius of drainage has passed that uoint." An eauivalent definition of the radius of drainage is that radius at which the extrapolated portion of the steady state portion of the pressure gradient gives a pressure equal to the shut-in reservoir pressure. This definition is also implied in the back pressure equation. The radius of drainage is, then, the distance into the reservoir from which the gas appears to originate at any time. It is, however, only a useful concept and does not actually exist. Fig. 1 illustrates the definition of the radius of drainage. At the end of each flow period the radius of drainage may depend on three factors: (1) the duration of each flow period; (2) the rate of gas production; and (3) the rate and duration of the previous flow periods. In general, back pressure tests are conducted with various lengths of production time and at various flow rates. Each individual back pressure test, therefore, requires an individual analysis. The calculations of the change in the radius of drainage have been made, however, for the case of equal flow periods for all four production rates and several sets of increasing flow rates. Fig. 2 illustrates the results of such calculations made by the method of Cornell and Katz2 for the case of 8, = 50,000 and the flow rate increasing in the ratio 1.0:2.0:3.0:4.0 for each flow period. The increase in the radius of drainage during the test is apparent.

Jan 1, 1956

By R. E. Collins, Paul B. Crawford

Mathematical equations have been derived to show the effect of the slippage phenomomenon (Klinkenberg effect) on unsteady-state gas flow through porous media. The assumption is made that the slippage may be represented by an equation of the type It is pointed out that most of the existing data on unsteady gas flow may be corrected for slippage by a simple change in definition of the dimen-sionless groups. INTRODUCTION Several solutions to the various problems associated with the unsteady-state flow of gas through porous media have been recently presented in the literature.','" The cited publications have resented solutions for flow under ideal conditjons. The principal assumptions involved include: (a) the density of the gas obeys the perfect gas law; (b) the viscosity of the gas is constant; and (c) the gas permeability is constant. Few, if any, actual gases under reservoir conditions are believed to conform with the above, but the ideal solutions do provide the basis for making improved estimates on the performance of gas reservoirs. The purpose of this paper is to show the performance characteristics when assumption (c) is corrected for the slippage phenomenon or the Klinkenberg effect. This is believed to be a step nearer to reality. MATHEMATICAL DEVELOPMENT Case 1. Gas Flow — Ideal Conditions The equations describing the flow of gas under ideal conditions have been clearly presented in the cited literature; however, for completeness of this work they are repeated here. The basic differential equation describing the flow of gas is Equation (6). It may be derived as follows: The continuity equation, the perfect gas law and Darcy's law are combined to give: Manuscript received in the Petroleum Branch office Aug. 3, 1963 or If — is constant, Equation (5) is rewritten to form the basic Equation (6). or for the linear case A dimensionless equation is obtained by dividing through by (pl)z and making the substitutions shown below: The resulting equation is A similar procedure for the radial case leads to the following equations: where and Equations (11), (12), and (13) are those used by Bruce, et al., and Jenkins and Aronofsky for their computational work.

Jan 1, 1953

By W. F. Baldwin

The timing circuit generally employed in Carter Reservoir Behavior Analyzers consists of a synchronous motor driven cam which actuates a microswitch. A mechanically actuated timer of this type has several inherent disadvantages, among which are the following: 1. The first time interval may not be of uniform length, depending on the exact position of the cam at the conclusion of a previous run. 2. The positioning adjustments on the microswitch lever arms are critical and require periodic readjustment. 3. The mechanical system is subject to wear which will ultimately impair its accuracy. It was therefore considered desirable to devise an alternate method which would eliminate these difficulties without introducing others that would be equally troublesome. This note describes the design of an electronic timing device which has been incorporated in the analyzer constructed by the Field Research Laboratories of Magnolia Petroleum Co. The electronic timer circuit is built around a simple neon glow tube relaxation oscillator, the complete circuit diagram of which is shown in Fig. l. The operation of the circuit is as follows: Condenser C, is charged to the critical firing voltage of the neon glow tube VR-75 by battery B1 through resistors R1 and R2. When the neon glow tube fires, the condenser C, is discharged, The charging cycle then repeats itself,

Jan 1, 1950

By R. P. Steijn

IT has been observed by a number of investigators that under certain conditions metals freeze into an aggregate of small hexagonal strands, parallel to one another and with their axes approximately in the direction of growth.'" This structure has been termed "cellular structure" and is explained in various ways by different workers, notably by Rutter and Chalmers." These investigators attribute the phenomenon to the presence of minute quantities of solute atoms which induce constitutional supercooling. However, if this is true, observations of the cellular structure in extremely pure substances, like frozen distilled water' and germanium of less than 0.0001 atomic pct metallic solute,' are difficult to comprehend. The purpose of this communication is to describe several observations made of the prismatic structure in zinc of 99.99 pct purity. Zinc single and bicrystals grown in a constant gradient electrical resistance furnace exhibit the cellular structure after etching in 15 pct HC1. (See Figs. 1 and 2.) It is noticed that the hexagonal substructure sometimes continues unbroken across the bicrystalline grain boundary.

Jan 1, 1956

By W. G. Pfann

WHEN a molten zone traverses a long, solid ingot in a level, open boat the ingot becomes tapered. While the taper may be slight after one zone pass, it can be appreciable after repeated zone passes, even to the extent of causing an overflow of matter at the end of the boat. It will be shown here that such matter transport by a molten zone arises from the volume change on melting and that it corresponds in magnitude and direction to the magnitude and sign of the volume change. It will be shown also that the mechanism of matter transport is basically similar to that of solute transport by a molten zone, which has been discussed elsewhere,1,2 and that the two processes can be described by similar equations. Finally it will be shown that matter transport can be prevented by inclining the ingot at a critical angle. Contraction on melting results in forward transport, that is, transport in the direction of zone travel; expansion on melting results in reverse transport. The way in which forward transport arises from the contraction on melting may be seen as follows: At the starting end of a solid horizontal ingot of uniform rectangular cross section of height h., form a molten zone of length 1, as shown in Fig. 1. The height h of the liquid will be h. where a is the ratio of density of solid to that of liquid. Advance the molten zone, at constant length, a distance dx. The volume of solid melted will be hdx; the volume of solid frozen will be Izdx, because the height of the freezing solid will tend to be equal to that of the liquid. The resultant change, dv, in liquid volume will be the difference in these quantities multiplied by the density ratio. Hence the following equation may be used for a zone at any distance x from the origin: which is valid in all but the last zone length in the

Jan 1, 1954

By C. A. Wert

THE change in mechanical properties accompanying quench aging of carbon in a iron has been known for a number of years. Since the amount of carbon involved is rather small, however, no measurements could be made to correlate the property change with the state of precipitation of the carbide. Indeed, until a few years ago it was not plain which property might be used to indicate the state of the progress of precipitation. Some years ago the internal friction of solid solutions of carbon in a iron was demonstrated, and the use of this phenomenon to ascertain the amount of carbon in solid solution at any given time was developed. Shortly afterward the author made a number of measurements in which changes in electrical resistance, thermoelectric emf, and hardness were determined simultaneously with the internal friction (and hence with the precipitation) ? A little later Dijkstra and Wert measured the change in magnetic coercive force accompanying aging.' The present work was undertaken to inquire into the changes in yield strength accompanying aging. The work was done on specimens made of Puron. These specimens were 0.05 in. in diam and about 6 in. long. Though specimens of this small size are not ideal for yield strength measurements, such specimens are desirable for internal friction meas-

Jan 1, 1952

By V. J. Decarlo, J. J. Gilman

POLISHING pure zinc differs somewhat from polishing less reactive metals. The problem is not that of finding a suitable reagent, but rather of producing the polish in such a way that the surface remains polished after it is removed from the polishing bath. In other words., the anodic film that is vital to the polishing mechanism' must be tightly adherent and nonporous. It is usually desirable that it be thin. Polishing solutions consist of proper proportions of an acid and a strong oxidizing agent. In electro-polishing, the external circuit acts as the oxidizing agent. The proportions are critical because the essential surface film must be maintained at approximately constant thickness during the polishing process. In the case of zinc, chiefly two oxidizing agents, chromic and nitric acids, have been used. The simplest polishing reagent is concentrated nitric acid. However, it has certain disadvantages. It tends to pit: an excessive amount of heat is evolved during polishing; and the oxide film that it produces is not very stable, so that the polished sur-

Jan 1, 1957