By W. R. Hibbard

Although extensive pole figure studies have been reported by Brick1 and others2,3 showing preferred orientations in rolled and annealed 70-30 alpha brass, and by Hermann and Sachs4 in 70-30 alpha brass cups, comparatively little information has been published on textures in drawn 70-30 alpha brass tubes. Crampton5 reported a (110) , [111] texture in drawn brass tubes based on selected individual X ray photograms following the method of Norton and Hiller,6 but the extent and ease of developing this texture and the annealing texture have not been reported and pole figures of these structures were not found in the literature. The present investigation was further stimulated by the possible influence of textures on the mercury stress-corrosion cracking of brass tubes. According to Snoek,7 iron-nickel alloy sheet with a strong cubic texture was more resistant to corrosion than a randomly oriented sheet. Crampton5 reported that single crystals of 70-30 alpha brass drawn into tubes did not crack after 24 hr in a standard mer-curous nitrate test. Edmunds12 found that single crystals of 70-30 alpha brass did not crack in a standard mercurous nitrate test but did crack when subjected to ammoniacal vapor. Wasserman11 reported a similar failure of a single crystal of brass in ammonia. A tube with a strong texture might approach single crystal behavior and tend to resist mercury cracking if the differences in orientation between adjacent grains were sufficiently slight. Preparation OF Specimens Crampton's5 tubes drawn 28 pct reduction in area developed a slight degree of preferred orientation while in tubes drawn 48 pct it was more marked. Based on this information, in order to obtain specimens with markedly different degrees of preferred orientation but with the same final draw, two sets of 70-30 alpha brass tubes were made following the mill schedules shown in Table I. The final draw involved a large reduction in outside diameter, and a ratio of reduction in area to reduction in outside diameter similar to that reported by Crampton,5, 10 to cause mercury cracking of brass tubes. The brass contained 71.31 pct copper, 0.01 pct lead, 0.01 pct iron and zinc by difference. Determination of Pole Figures A 6-in. length from each tube was rotated rapidly by an electric stirrer in 25 pct nitric acid until the gauge was reduced to 0.003-0.005 in. The tubes were carefully cut longitudinally and the walls gently flattened. They were further etched in 25 pet nitric acid to 0.0015 in. thickness and (111) pole figures were determined using copper K-alpha radiation in the manner described by Brick.' The three general types of pole figures

Jan 1, 1949

By W. R. Hibbard

The term lineage was first introduced by Buergerl to denote dendritic branches, grown from a crystal nucleus during solidification from the liquid, with imper- fections in alignment of the order of 10 : to 10-4 cm. These imperfections are associated with distortions of the dendrites caused by the subsequent solidification of the inter-dendritic filling and are illustrated in Fig I. Buerger etched zinc single crystals made by the Bridgman3 method to develop this dendritic pattern and show lineage microscopically. Since maximum crystal growth in face-centered cubic metals occurs along the [IT] directions,2 lineage would appear in copper as small deviations of dendritic branches from these directions. Elam4 and others5"8 reported etching effects resulting from coring along the cube face traces of various copper alloy crystals. These traces were used by Samans8 to orient single crystals. Williamson9 noted a "lined structure (in alpha brass single crystals) consisting of an ordered arrangement of etch pits" which were probably traces of {IOO} planes but somewhat uncertain because they were never straight (that is, apparently lineage). Greningerl1 described the distortion and multiplicity of Laue spots in back reflection X ray photograms of copper single crystals showing lineage. The present investigation -includes metal-lographic, X ray, and property studies of lineage in large grain and single crystal specimens of copper. Preparation of Specimens specilnens 10 in. long 35 1/2 in. diam of oxygen-free copper (o.F.H.c.) (99.985 pet) were' melted vertically in graphite crucibles under an atmosphere of commercial nitrogen purified through a gas train including sulfuric acid, potassium chloride, magnesium chiorate, hot copper chips and phosphorus pentoxide. After a temperature of 1200°C had been maintained for 1/2 hr, the furnace was turned off and the specimens cooled at a rate of about 150°c an hour' This method of direct solidification was used by Greningerlo to produce single crystals with marked lineage and in this investigation produced a fair yield of single crystal specimens in

Jan 1, 1949

By W. R. Hibbard

The term lineage was first introduced by Buergerl to denote dendritic branches, grown from a crystal nucleus during solidification from the liquid, with imper- fections in alignment of the order of 10 : to 10-4 cm. These imperfections are associated with distortions of the dendrites caused by the subsequent solidification of the inter-dendritic filling and are illustrated in Fig I. Buerger etched zinc single crystals made by the Bridgman3 method to develop this dendritic pattern and show lineage microscopically. Since maximum crystal growth in face-centered cubic metals occurs along the [IT] directions,2 lineage would appear in copper as small deviations of dendritic branches from these directions. Elam4 and others5"8 reported etching effects resulting from coring along the cube face traces of various copper alloy crystals. These traces were used by Samans8 to orient single crystals. Williamson9 noted a "lined structure (in alpha brass single crystals) consisting of an ordered arrangement of etch pits" which were probably traces of {IOO} planes but somewhat uncertain because they were never straight (that is, apparently lineage). Greningerl1 described the distortion and multiplicity of Laue spots in back reflection X ray photograms of copper single crystals showing lineage. The present investigation -includes metal-lographic, X ray, and property studies of lineage in large grain and single crystal specimens of copper. Preparation of Specimens specilnens 10 in. long 35 1/2 in. diam of oxygen-free copper (o.F.H.c.) (99.985 pet) were' melted vertically in graphite crucibles under an atmosphere of commercial nitrogen purified through a gas train including sulfuric acid, potassium chloride, magnesium chiorate, hot copper chips and phosphorus pentoxide. After a temperature of 1200°C had been maintained for 1/2 hr, the furnace was turned off and the specimens cooled at a rate of about 150°c an hour' This method of direct solidification was used by Greningerlo to produce single crystals with marked lineage and in this investigation produced a fair yield of single crystal specimens in

Jan 1, 1949

By Y. G. Shiau, J. E. Burke

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949

By J. E. Burke, Y. G. Shiau

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949

By J. E. Burke, C. S. Barrett

The fine lines shown in Fig I are typical of markings that ma): be detected after polishing and etching deformed specimens of alpha brass and other alloys. Although they have long been the subject of discussion by metallurgists their nature is still uncertain and the names that have been applied: to them, such as deformation line4 or strain markinas, indicate this uncertainky. In this paper which repotts the results of a furthcr investigatinn of their nature, they will be called strain mxrkings. Introduction Mathewson and Phillips1 described strain markinps in 1 916 and concluded that they appear only after 20 pet deformation. They objected to the markings being called slip tines believing this term should be sewrved for surface markings protluced by plastic deformntion. In 1921. vogel² described similar striations which appeared after polishing and etching the roughly ground surface of numerous alloys. He reported that the markings were crystallo-graphic in nature, and since they resemble Seumann hands in iron, at least superficially, he assumed them to be mechanical twins. In 1928, Matherwson reported work by Phillips which indicated that the lines were more readily produced by impact than by slow deformation and that in many cases the twins inside recrystallized grains were parallel to strain markings in the original deformed grains. This was taken as cvirlence that the markings coalesce into anncaling twins. and hence that they themselves are mechanical twins. Many attempts have been made to demonstrate directly that the markings are mechanical twins. In 1934, Samans described the results of X ray studies of two defomed crystals of alpha brass. Evidence was obtained which could be interpreted to indicate that the strain markings arc mechanical twins, and this remains the only direct evidence to this effect. Several other attempts to obtain similar evidence by X ray diffraction have failed5.8.7 although in no Ease was the original method of Samans employed. An

Jan 1, 1949

By C. S. Barrett, J. E. Burke

The fine lines shown in Fig I are typical of markings that ma): be detected after polishing and etching deformed specimens of alpha brass and other alloys. Although they have long been the subject of discussion by metallurgists their nature is still uncertain and the names that have been applied: to them, such as deformation line4 or strain markinas, indicate this uncertainky. In this paper which repotts the results of a furthcr investigatinn of their nature, they will be called strain mxrkings. Introduction Mathewson and Phillips1 described strain markinps in 1 916 and concluded that they appear only after 20 pet deformation. They objected to the markings being called slip tines believing this term should be sewrved for surface markings protluced by plastic deformntion. In 1921. vogel² described similar striations which appeared after polishing and etching the roughly ground surface of numerous alloys. He reported that the markings were crystallo-graphic in nature, and since they resemble Seumann hands in iron, at least superficially, he assumed them to be mechanical twins. In 1928, Matherwson reported work by Phillips which indicated that the lines were more readily produced by impact than by slow deformation and that in many cases the twins inside recrystallized grains were parallel to strain markings in the original deformed grains. This was taken as cvirlence that the markings coalesce into anncaling twins. and hence that they themselves are mechanical twins. Many attempts have been made to demonstrate directly that the markings are mechanical twins. In 1934, Samans described the results of X ray studies of two defomed crystals of alpha brass. Evidence was obtained which could be interpreted to indicate that the strain markings arc mechanical twins, and this remains the only direct evidence to this effect. Several other attempts to obtain similar evidence by X ray diffraction have failed5.8.7 although in no Ease was the original method of Samans employed. An

Jan 1, 1949

By C. H. Mathewson, W. R. Hibbard, Robert Maddin

A satisfactory mathematical relationship between shear, elongation and change of orientation in the axial straining of a single crystalline rod or wire may be based on a simple model in which blocks, representing glide lamellae, glide over one another and rotate so as to maintain the original fixed position of the axis as the wire elongates.' Obviously such a model gives no information concerning strain-hardening or the atomic adjustments at the sliding surfaces and their influence on the internal structure of the blocks. Moreover such an operation could be conducted with rigid blocks only by using self-aligning grips or a flexible attachment which would permit the adjacent blocks to freely assume their changing orientations. There are many unsolved problems (see Andrade2) concerning the manner in which nature departs from the simple model in permitting the essentials of slip, rotation and elongation to occur along with strain-hardening and the appearance of glide lamellae of various dimensions and special characteristics, not fully appreciated at the present time. This paper describes part of an extensive investigation on the development and characteristics of glide ellipses in single crystalline alpha brass rods and is especially concerned with the observation of cross-slip in crystals oriented wholly within the range of slip on a single system according to the generalizations first presented by Taylor and Elam in 1923.³ Experimental Procedure Half-inch rods of alpha brass (nominally 70 pet Cu, 30 pet Zn)* were converted into single crystals by melting and gradual solidification in a graphite mold according to the Bridgman method.4 In order to remove any coring, the crystals were homogenized at 800°C for 16 hr and tested by etching with a 50 pet nitric acid solution. The back-reflection Laue technique as described by Greninger6 was used for determining the orientations of the crystals. Standard stereographic operations were employed to locate the specimen axis in a triangle of the Taylor and Elam3 projection so that the slip plane and direction could be predicted. The lineage structure reported by Buer-ger6 was present in the crystals used in this investigation. However, only crystals were used in which the internal differences in orientation did not exceed two degrees. Very little is known concerning the effect of the presence of a lineage structure on the detailed mechanism of plastic deformation.

Jan 1, 1949

By C. H. Mathewson, Robert Maddin, W. R. Hibbard

A satisfactory mathematical relationship between shear, elongation and change of orientation in the axial straining of a single crystalline rod or wire may be based on a simple model in which blocks, representing glide lamellae, glide over one another and rotate so as to maintain the original fixed position of the axis as the wire elongates.' Obviously such a model gives no information concerning strain-hardening or the atomic adjustments at the sliding surfaces and their influence on the internal structure of the blocks. Moreover such an operation could be conducted with rigid blocks only by using self-aligning grips or a flexible attachment which would permit the adjacent blocks to freely assume their changing orientations. There are many unsolved problems (see Andrade2) concerning the manner in which nature departs from the simple model in permitting the essentials of slip, rotation and elongation to occur along with strain-hardening and the appearance of glide lamellae of various dimensions and special characteristics, not fully appreciated at the present time. This paper describes part of an extensive investigation on the development and characteristics of glide ellipses in single crystalline alpha brass rods and is especially concerned with the observation of cross-slip in crystals oriented wholly within the range of slip on a single system according to the generalizations first presented by Taylor and Elam in 1923.³ Experimental Procedure Half-inch rods of alpha brass (nominally 70 pet Cu, 30 pet Zn)* were converted into single crystals by melting and gradual solidification in a graphite mold according to the Bridgman method.4 In order to remove any coring, the crystals were homogenized at 800°C for 16 hr and tested by etching with a 50 pet nitric acid solution. The back-reflection Laue technique as described by Greninger6 was used for determining the orientations of the crystals. Standard stereographic operations were employed to locate the specimen axis in a triangle of the Taylor and Elam3 projection so that the slip plane and direction could be predicted. The lineage structure reported by Buer-ger6 was present in the crystals used in this investigation. However, only crystals were used in which the internal differences in orientation did not exceed two degrees. Very little is known concerning the effect of the presence of a lineage structure on the detailed mechanism of plastic deformation.

Jan 1, 1949

By W. R. Hibbard, Ming-Kao Yen

Various rationalizations of preferred orientations in cold worked polycrystalline metals have been based on the operation of at least two three2 five, an indefinite number, and all,6 slip systems of the type occurring in single crystals. Pickus and Mathewson3 suggested that the cold rolling texture in face-centered cubic metals could be rationalized on the basis of two or more operating slip directions symmetrically disposed about the direction of flow in such a manner that the resolved shear stress factor is equal for all operating slip systems and lattice rotations cancel each other. The importance of the direction of flow, the necessity for the operation of slip systems capable of producing the required changes in external dimensions, the maintenance of a common surface between adjacent grains and a symmetrical arrangement of the operating slip systems in order to produce an end orientation which is stable under additional deformation lead to the following rationalization of textures based on the type of slip systems operative in single crystals. The rationalization is intended to explain why certain orientations are suitable for deformational flow without a change in orientation and thus are stable end orientations or ideal texture orientations. It does not attempt to explain how the grains of a randomly oriented polycrystalline aggregate will reach this orientation. The rationalization is based on the following four postulates: 1. The ideal textures for polycrystalline aggregates are the result of reorientations of individual crystals toward the same stable end orientation at which no further reorientation will occur even during additional deformation. Since, in simple slip, the relative orientations of the stress axis and the active slip system determine the change in orientation during slip, it is considered that the orientation of the stress axis with respect to the ideal texture determines what slip systems must be active to retain the stable end orientation. Therefore the stable end orientation should be a symmetrical one around the stress axis with respect to the active slip systems such that lattice rotations resulting from slip will cancel each other and prevent a resultant change in orientation. (Rotational symmetry only—not translation, inversion, nor others—is considered here.) Thus a metal under a pure stress should develop a texture consisting of one or more of the crystallographically symmetrical directions, <100>, <110> or <111> for cubic metals or <0001>, <1010> or <1120> for hexagonal close-packed metals, parallel to the stress axis. 2. Since the active slip direction is the direction of glide during simple slip and thus the direction of maximum shear movement, in the ideal texture the active slip

Jan 1, 1949

By Ming-Kao Yen, W. R. Hibbard

Various rationalizations of preferred orientations in cold worked polycrystalline metals have been based on the operation of at least two three2 five, an indefinite number, and all,6 slip systems of the type occurring in single crystals. Pickus and Mathewson3 suggested that the cold rolling texture in face-centered cubic metals could be rationalized on the basis of two or more operating slip directions symmetrically disposed about the direction of flow in such a manner that the resolved shear stress factor is equal for all operating slip systems and lattice rotations cancel each other. The importance of the direction of flow, the necessity for the operation of slip systems capable of producing the required changes in external dimensions, the maintenance of a common surface between adjacent grains and a symmetrical arrangement of the operating slip systems in order to produce an end orientation which is stable under additional deformation lead to the following rationalization of textures based on the type of slip systems operative in single crystals. The rationalization is intended to explain why certain orientations are suitable for deformational flow without a change in orientation and thus are stable end orientations or ideal texture orientations. It does not attempt to explain how the grains of a randomly oriented polycrystalline aggregate will reach this orientation. The rationalization is based on the following four postulates: 1. The ideal textures for polycrystalline aggregates are the result of reorientations of individual crystals toward the same stable end orientation at which no further reorientation will occur even during additional deformation. Since, in simple slip, the relative orientations of the stress axis and the active slip system determine the change in orientation during slip, it is considered that the orientation of the stress axis with respect to the ideal texture determines what slip systems must be active to retain the stable end orientation. Therefore the stable end orientation should be a symmetrical one around the stress axis with respect to the active slip systems such that lattice rotations resulting from slip will cancel each other and prevent a resultant change in orientation. (Rotational symmetry only—not translation, inversion, nor others—is considered here.) Thus a metal under a pure stress should develop a texture consisting of one or more of the crystallographically symmetrical directions, <100>, <110> or <111> for cubic metals or <0001>, <1010> or <1120> for hexagonal close-packed metals, parallel to the stress axis. 2. Since the active slip direction is the direction of glide during simple slip and thus the direction of maximum shear movement, in the ideal texture the active slip

Jan 1, 1949

By B. J. Nelson, F. N. Rhinos

Studies upon the rates of oxidation of copper alloys containing small quantities of the alloying elementsl,2 have shown that steady growth of the scales at predictable rates is limited to a small concentration range and to oxidation at temperatures above 600°C., whereas unpredictable and erratic oxidation behavior is found with alloys containing larger additions and at low temperatures. The latter effect appears to be associated with modifications in the geometric disposition of the oxides. At low concentrations of the baser elements in copper, simple oxidation behavior is typified by the formation of two distinguishable zones of oxidation: (I) a subscale composed of discrete particles of the oxide of the alloying element embedded in substantially pure copper and (2) an external scale composed of cuprous oxide (with a very thin layer of cupric oxide on the outside) containing particles of the alloying element distributed throughout, but most profusely near the metal surface (see Fig. 2, top). Where this type of structure obtains, the process of oxidation is believed to be implemented, and its rate controlled, by the diffusion of the reacting elements through a&apos; continuous matrix phase; i.e., through the alpha (metallic) phase of the subscale and alloy and through the cuprous oxide of the external scale. Copper is presumed to diffuse outward through the cuprous oxide layer to the external surface, where it reacts to form more cuprous oxide.3 Oxygen is delivered at the oxide-metal interface in the form of cuprous oxide, which may either react with the alloying element to deposit its oxide at the inner limit of the external scale or dissolve in the pure copper that remains at the surface of the metal after it has become depleted in its oxidiza-ble alloying elements. Both oxygen and the alloying element are pictured as diffusing through the metal, the oxygen inward and the alloying element outward. Where the two diffusion streams meet in sufficient concentration the oxide of the subscale is precipitated. If the oxygen pressure in the surrounding atmosphere is just below the pressure necessary to maintain cuprous oxide undecomposed, no cuprous oxide can be formed; some of the oxide of the alloying element may form upon the external surface, if its decomposition pressure is below that of cuprous oxide, and a normal sub-scale appears. This condition is achieved experimentally by enclosing the alloy with cuprous oxide together with an excess of copper. At temperatures from 600°C. downward, the precipitated oxides tend to accumulate at the grain boundaries of the alpha phase where a relatively small volume establishes a partial barrier to the diffusion of the reactants- Similarly, large volumes of Precipitated oxides tend to deposit in various patterns that may be expected to

Jan 1, 1944

By F. N. Rhinos, B. J. Nelson

Studies upon the rates of oxidation of copper alloys containing small quantities of the alloying elementsl,2 have shown that steady growth of the scales at predictable rates is limited to a small concentration range and to oxidation at temperatures above 600°C., whereas unpredictable and erratic oxidation behavior is found with alloys containing larger additions and at low temperatures. The latter effect appears to be associated with modifications in the geometric disposition of the oxides. At low concentrations of the baser elements in copper, simple oxidation behavior is typified by the formation of two distinguishable zones of oxidation: (I) a subscale composed of discrete particles of the oxide of the alloying element embedded in substantially pure copper and (2) an external scale composed of cuprous oxide (with a very thin layer of cupric oxide on the outside) containing particles of the alloying element distributed throughout, but most profusely near the metal surface (see Fig. 2, top). Where this type of structure obtains, the process of oxidation is believed to be implemented, and its rate controlled, by the diffusion of the reacting elements through a&apos; continuous matrix phase; i.e., through the alpha (metallic) phase of the subscale and alloy and through the cuprous oxide of the external scale. Copper is presumed to diffuse outward through the cuprous oxide layer to the external surface, where it reacts to form more cuprous oxide.3 Oxygen is delivered at the oxide-metal interface in the form of cuprous oxide, which may either react with the alloying element to deposit its oxide at the inner limit of the external scale or dissolve in the pure copper that remains at the surface of the metal after it has become depleted in its oxidiza-ble alloying elements. Both oxygen and the alloying element are pictured as diffusing through the metal, the oxygen inward and the alloying element outward. Where the two diffusion streams meet in sufficient concentration the oxide of the subscale is precipitated. If the oxygen pressure in the surrounding atmosphere is just below the pressure necessary to maintain cuprous oxide undecomposed, no cuprous oxide can be formed; some of the oxide of the alloying element may form upon the external surface, if its decomposition pressure is below that of cuprous oxide, and a normal sub-scale appears. This condition is achieved experimentally by enclosing the alloy with cuprous oxide together with an excess of copper. At temperatures from 600°C. downward, the precipitated oxides tend to accumulate at the grain boundaries of the alpha phase where a relatively small volume establishes a partial barrier to the diffusion of the reactants- Similarly, large volumes of Precipitated oxides tend to deposit in various patterns that may be expected to

Jan 1, 1944

By R. S. Dean. J. R. Long T. R. Graham, Roberson A. H., Armantrout C. E.

The general program of the Federal Bureau of Mines on the study of alloys made with electrolytic manganese has been extended to copper-manganese-aluminum alloys. The initial results of the work are presented in this report and concern a determination of the mutual solubilities of these three metals to form the alpha solid solution. The principal studies of this system, reported in the literature, have been focused on the Heusler alloys containing ro to 30 per cent Mn with 9 to 15 per cent Al. These investigations concern the ferromagnetic properties and the determination of the crystallization contours, with little emphasis on the phases present in the solid state outside of this area. Heuslerl recognized a breakdown of the beta solid solution of the magnetic alloy, which he says decomposes into the alpha, beta, and gamma phases of the copper-aluminum system, somewhat modified by the presence of manganese. Rosenhain and Lantsberry2 examined alloys ranging up to 10 per cent Mn and 10 per cent A1 but were unable to reach definite conclusions concerning the phase boundaries in that area. Krings and Ostmann3 made magnetic studies and examined the system by thermal analysis. They present contours of the liquidus surface but do not place any of the phase boundaries. Corson4 has drawn a hypothetical boundary for the alpha field with few, data to support such construction. The binary systems involved have rcceived considerable attention by numerous investigators, and their general features are well established. The copper-ahminum system (Fig. I) has been thoroughly examined by Stockdale,5 who places the limit of solubility of aluminum in copper at 7.4 per cent at the liquidus and 9.5 per cent at room temperature. Smith6 established the eutectoid temperature at 570°C. by a study of isothermal decomposition of the beta phase. The copper-manganese system (Fig&apos; &apos;) has been recently reviewed by Dean and CO-WorkersS.7 Using high-purity alloys,

Jan 1, 1947

By Armantrout C. E., R. S. Dean. J. R. Long T. R. Graham, Roberson A. H.

The general program of the Federal Bureau of Mines on the study of alloys made with electrolytic manganese has been extended to copper-manganese-aluminum alloys. The initial results of the work are presented in this report and concern a determination of the mutual solubilities of these three metals to form the alpha solid solution. The principal studies of this system, reported in the literature, have been focused on the Heusler alloys containing ro to 30 per cent Mn with 9 to 15 per cent Al. These investigations concern the ferromagnetic properties and the determination of the crystallization contours, with little emphasis on the phases present in the solid state outside of this area. Heuslerl recognized a breakdown of the beta solid solution of the magnetic alloy, which he says decomposes into the alpha, beta, and gamma phases of the copper-aluminum system, somewhat modified by the presence of manganese. Rosenhain and Lantsberry2 examined alloys ranging up to 10 per cent Mn and 10 per cent A1 but were unable to reach definite conclusions concerning the phase boundaries in that area. Krings and Ostmann3 made magnetic studies and examined the system by thermal analysis. They present contours of the liquidus surface but do not place any of the phase boundaries. Corson4 has drawn a hypothetical boundary for the alpha field with few, data to support such construction. The binary systems involved have rcceived considerable attention by numerous investigators, and their general features are well established. The copper-ahminum system (Fig. I) has been thoroughly examined by Stockdale,5 who places the limit of solubility of aluminum in copper at 7.4 per cent at the liquidus and 9.5 per cent at room temperature. Smith6 established the eutectoid temperature at 570°C. by a study of isothermal decomposition of the beta phase. The copper-manganese system (Fig&apos; &apos;) has been recently reviewed by Dean and CO-WorkersS.7 Using high-purity alloys,

Jan 1, 1947

By Blake M. Loring, Robert A. Colton

MeltiXg procedures for most metals and alloys usually include some provision for the control of oxygen, since this element frequently has some undesirable effect on the properties of the metal or alloy concerned. In the melting of the various bronzes, this is especially true, since oxygen can be introduced into the melt in a number of ways, most of which are difficult to control. In making bronzes from virgin materials, oxygen is usually present in the commercial grades of copper used; electrolytic fire-refined copper ingots usually contain from 0.02 to 0.05 per cent oxygen. When ingot metal or scrap bronze is used in the charge, oxides are almost always present to some degree. Under certain melting conditions and in certain types of melting equipment the atmosphere over the metal may be highly oxidizing. This, of course, may be desirable in the melting practice used, but is certain to introduce appreciable amounts of oxygen into the melt, and that may not be entirely desirable. From the foundry viewpoint oxygen may have several harmful effects on bronzes. The formation of excessive amounts of oxides may produce drossy metal, which, in turn, means dirty castings and a potentially high rejection rate. It is claimed, too, that oxides in the metal may combine with hydrogen to form steam and thereby produce porosity in certain of the bronzes. The presence of certain refractory oxides, such as SnOz, may be undesirable from the viewpoint of making machining difficult, or as possible stress-raisers in the metal matrix. It is often said that excessive oxide present in the liquid metal makes the metal run sluggishly. Since it appears impractical to try to control the amount of oxygen introduced into the metal beyond taking the economical limit of precaution about charging dirty scrap, it would seem&apos; that control of the oxygen content of the liquid metal offers the most promising approach to this problem. This might be done by using slags, or covers, or by the use of some element or compound added to the melt to remove oxygen preferentially. Most aspects of this problem have been considered and considerable work has been done along these lines. A reconsideration of the problem is indicated, however, by the controversial nature of the evidence at hand, especially on the possibility of using a chemical deoxidizer to control the oxygen content of bronzes. Choice of Deoxidizer The choice of the chemical agent selected as a deoxidizer would naturally depend first on the alloy in which it is to ~he used: in this particular case the alloy is Navy gun metal. In Table. I are listed a group of elements that might be considered as deoxidizers for bronze, with some of their properties that should be considered in

Jan 1, 1946

By Blake M. Loring, Robert A. Colton

MeltiXg procedures for most metals and alloys usually include some provision for the control of oxygen, since this element frequently has some undesirable effect on the properties of the metal or alloy concerned. In the melting of the various bronzes, this is especially true, since oxygen can be introduced into the melt in a number of ways, most of which are difficult to control. In making bronzes from virgin materials, oxygen is usually present in the commercial grades of copper used; electrolytic fire-refined copper ingots usually contain from 0.02 to 0.05 per cent oxygen. When ingot metal or scrap bronze is used in the charge, oxides are almost always present to some degree. Under certain melting conditions and in certain types of melting equipment the atmosphere over the metal may be highly oxidizing. This, of course, may be desirable in the melting practice used, but is certain to introduce appreciable amounts of oxygen into the melt, and that may not be entirely desirable. From the foundry viewpoint oxygen may have several harmful effects on bronzes. The formation of excessive amounts of oxides may produce drossy metal, which, in turn, means dirty castings and a potentially high rejection rate. It is claimed, too, that oxides in the metal may combine with hydrogen to form steam and thereby produce porosity in certain of the bronzes. The presence of certain refractory oxides, such as SnOz, may be undesirable from the viewpoint of making machining difficult, or as possible stress-raisers in the metal matrix. It is often said that excessive oxide present in the liquid metal makes the metal run sluggishly. Since it appears impractical to try to control the amount of oxygen introduced into the metal beyond taking the economical limit of precaution about charging dirty scrap, it would seem&apos; that control of the oxygen content of the liquid metal offers the most promising approach to this problem. This might be done by using slags, or covers, or by the use of some element or compound added to the melt to remove oxygen preferentially. Most aspects of this problem have been considered and considerable work has been done along these lines. A reconsideration of the problem is indicated, however, by the controversial nature of the evidence at hand, especially on the possibility of using a chemical deoxidizer to control the oxygen content of bronzes. Choice of Deoxidizer The choice of the chemical agent selected as a deoxidizer would naturally depend first on the alloy in which it is to ~he used: in this particular case the alloy is Navy gun metal. In Table. I are listed a group of elements that might be considered as deoxidizers for bronze, with some of their properties that should be considered in

Jan 1, 1946

By C. Ernest Birchenall, Robert F. Mehl

Application of diffusion laws in the customary form to experimental studies in binary metallic solid solutions has shown the diffusion cocfficient to vary with concentration for all systems investigated. The factors determining this variation have not been ascertained. However, the question of whether the diffusion coefficient would become a constant, independent of concentration throughout a single phase if the concentration gradient in the diffusion equation were replaced by an activity gradient has been an attractive subject for speculation. Wagner¹ derived an expression for the force acting on a diffusing particle in terms of the chemical potential. This was also the approach chosen by Jost2 in his monograph. From a somewhat different point of view, Eyring3 and his co-workers have used activity gradients when dealing with diffusion in concentrated nonideal solutions. The only actual test with experimental data is that given by Darken,4 though this is more qualitative than quantitative. Many others opposed the application in any way of thermodynamic concepts to kinetic phenomena, including diffusion processes. A rigorous examination of this principle requires good data expressing the relationship between activity and concentration for solid solutions for which reliable diffusion work has been done. The literature provides such information only for the interstitial solution of carbon in gamma iron (austenite) and for the substitutional copper-zinc solutions (alpha brass). Activity data for carbon in austenite at 800°C and 1000°C are available from the recent work of Smith5 on the equilibrium of hydrogen-methane and carbon monoxide-carbon dioxide mixtures with gamma iron. Combining these with the diffusion studies of Wells and Mehl6 makes possible a quantitative test for this interstitial solid solution. The vapor-pressure determinations for zinc over brass by Hargreaves7 allowed the calculation of activities in this system over a wide range of temperatures and concentrations. Extensive investigation of diffusion in this substitutional solid solution has been carried out by Rhines and Mehl.8 Activities in Brass9 If the vapor phase of zinc is assumed to behave as an ideal gas, any solid or liquid solutions that are in equilibrium with the same partial pressure of zinc at the same temperature have the same thermodynamic activity of zinc. In order to assign a numerical value to the activity azn, it is necessary to choose some standard reference state to which an activity value of unity is arbitrarily assigned. It is customary to choose the liquid or solid state of the pure material. Then azn is defined numerically by

Jan 1, 1947

By C. Ernest Birchenall, Robert F. Mehl

Application of diffusion laws in the customary form to experimental studies in binary metallic solid solutions has shown the diffusion cocfficient to vary with concentration for all systems investigated. The factors determining this variation have not been ascertained. However, the question of whether the diffusion coefficient would become a constant, independent of concentration throughout a single phase if the concentration gradient in the diffusion equation were replaced by an activity gradient has been an attractive subject for speculation. Wagner¹ derived an expression for the force acting on a diffusing particle in terms of the chemical potential. This was also the approach chosen by Jost2 in his monograph. From a somewhat different point of view, Eyring3 and his co-workers have used activity gradients when dealing with diffusion in concentrated nonideal solutions. The only actual test with experimental data is that given by Darken,4 though this is more qualitative than quantitative. Many others opposed the application in any way of thermodynamic concepts to kinetic phenomena, including diffusion processes. A rigorous examination of this principle requires good data expressing the relationship between activity and concentration for solid solutions for which reliable diffusion work has been done. The literature provides such information only for the interstitial solution of carbon in gamma iron (austenite) and for the substitutional copper-zinc solutions (alpha brass). Activity data for carbon in austenite at 800°C and 1000°C are available from the recent work of Smith5 on the equilibrium of hydrogen-methane and carbon monoxide-carbon dioxide mixtures with gamma iron. Combining these with the diffusion studies of Wells and Mehl6 makes possible a quantitative test for this interstitial solid solution. The vapor-pressure determinations for zinc over brass by Hargreaves7 allowed the calculation of activities in this system over a wide range of temperatures and concentrations. Extensive investigation of diffusion in this substitutional solid solution has been carried out by Rhines and Mehl.8 Activities in Brass9 If the vapor phase of zinc is assumed to behave as an ideal gas, any solid or liquid solutions that are in equilibrium with the same partial pressure of zinc at the same temperature have the same thermodynamic activity of zinc. In order to assign a numerical value to the activity azn, it is necessary to choose some standard reference state to which an activity value of unity is arbitrarily assigned. It is customary to choose the liquid or solid state of the pure material. Then azn is defined numerically by

Jan 1, 1947

By C. S. Barrett, P. Coheur

AXnealing twins are common in the microstructure of copper that has been rolled and recrystallized. In such samples it follows that a twin relationship should exist between components of the re-crystallization texture,&apos; and several examples of this have been reported. For example, twin relationships have been found in recrystallized electrolytic copper sheet, as indicated in Fig. I, from a paper by Coheur and Lejeune.2 In this pole figure the cube texture (100) [001] is indicated by the hollow squares in the lower half of the figure (the pole figure for 200 reflections) and in the upper, (III), part of the figure. The texture contains, in addition to this orientation, the first-order twins of it, shown in the figure by the filled triangles. This orientation relation has been suggested by others also, under certain annealing conditions,3&apos;4 although pole figures have not been published to confirm it. Some orientations in recrystallized sheets are identical with their twins, because of the symmetry elements of the texture— this is true, for example, with the (113) [ZII] texture so commonly reported for brass—hence it appears impossible in such samples to decide whether the twin relationships result from twinning or merely from the symmetry of the deformation process. The present investigation of a commercial copper strip seems to yield an example in which annealing twins account unambiguously for the principal orientations present. It proves to be a case, also, for which the recrystallization texture cannot be viewed as derived from the deformation texture by a first or second-order twinning mechanism. Materials and Methods The samples investigated were of secondary copper (melted in belgium) to which 0.19 per cent iron had been added to raise the recrystallization temperature. How much the orientation characteristics of this metal can be ascribed to the iron content and how much to other impurities or to melting and pouring practice have not been investigated.* The rolling was done in one direction only, on a mill with rolls of about 20-cm diameter. A strip I. cm wide was reduced from 5 mm thickness to 0.05 mm by several cold passes at commercial speeds. The samples cut from this 99 per cent reduced strip were X-rayed throughout their entire thickness. A pole figure made soon after rolling and annealing was identical, within experimental error, with one that was made when a two-year interval occurred between rolling and annealing. X-ray patterns were made on a camera2 that traversed

Jan 1, 1947