By G. Sachs, L. J. Ebert, W. F. Brown

Isothermal transformation, or "aus-tempering," of a carbon-containing aus-tenite at elevated temperatures yields so-called "intermediate products." Their structure and properties are, for a given hardness, rather different from those of "tempered martensite" obtained on conventional quenching and tempering.' Several investigators2,3 have found that for high carbon and slightly alloyed steels the intermediate products formed at temperatures close to that of the martensite reaction possess strength properties superior to those of tempered martensite. The structure of these low temperature, intermediate products is generally acicular (bainite) but clearly different from that of martensite. However, at higher austempering temperatures, between 1000 and 1300°F (540 and 700°C) carbon steels were found to exhibit a rather low ductility.4,5 Thus notch bar tensile tests showed the ratio between notch strength and regular tensile strength to decrease with increasing austempering temperature. For ductilities below a few percent this notch strength ratio is a measure of ductility, according to investigations on low alloy steels.637 Furthermore the presence of intermediate products formed unintentionally on quenching was considered as responsible for the low ductility and impact energy of some heat treated steels,8 These intermediate products could result from partial transformation at the so-called "nose-temperature" where the rate of the transformation is a maximum. Tempering improved such mixtures of martensite and intermediate products, their properties approaching those of tempered martensite of equal hardness. The following investigation constitutes an attempt to determine certain strength properties of a partially austempered and subsequently quenched low alloy steel, namely, a chromium steel (SAE 5140) The structures formed by such a treatment should consist of a mixture of intermediate products formed on austempering and a martensite formed on oil quenching from the austempering temperature. It was intended, by varying the austempering time, to vary the quantity of the intermediate products between zero and 100 pct. The austempering temperature of 860°F was selected after extensive preliminary tests close to the nose-temperature. Austempering at this temperature yielded an acicular intermediate product. .Additional tests under less exacting conditions were made for an austempering temperature of 950°F where the intermediate product appeared to be very fine pearlite. To determine the effects of tempering on structures containing various amounts of

Jan 1, 1949

By R. Ingerson

Bore surfaces of used guns commonly show a pattern of cracks in various degrees of development. It has been suggested that these cracks may aid erosion by providing channelways for the gases, eventually leading to the tearing out of blocks of metal. Under the general studies of gun erosion conducted at the Geophysical Laboratory it appeared desirable to consider this factor, and to determine the resistance to surface cracking offered by gun steel and by various other materials that might be used in the bores of guns. Method and Apparatus In order to make such a determination it is necessary to have (I) an arrangement in which the surface to be studied can be subjected to conditions similar to those in a gun with respect to temperature, pressure (developed by explosion gases), composition of the gases and length of time the surface is exposed to the gases; and (2) a specimen that can be examined readily after any number of shots, and then fired again, if necessary. The first of these conditions can be met by using an explosion vessel designed by H. S. Roberts of the Geophysical Laboratory. Fig I shows a cross-section of the apparatus. The "gun" G from which the charge is fired is made from the receiver of a caliber 0.30 army rifle, M1903, and the charges are prepared in caliber 0.30 cartridge cases. The test specimen S is held in place by a cone-shaped plug P and by a steel bridge B which is bolted to the outside of the explosion vessel on either side of the section shown. The plug, in turn, is held in place by a screw collar C. Maximum pressure is controlled by a brass rupture disk R. Part of the explosion gases flow past the two flat areas on S. Temperature and composition of gases, and the time before the rupture disk breaks, can be controlled by amount and kind of powder used, and pressure can be controlled by using rupture disks of different thickness. While the explosion vessel used was not designed so that temperature and pressure could be measured, in other vessels of closely similar size and shape containing proportionate charges of the same kind of powder as that used for standard testing procedure, values of 2700°K and 50,000 psi were obtained. Since the orifices past the flat areas on the plug are small compared to the rupture disk hole (I:I6), most of the gas goes out through the rupture disk when it breaks. The amount that goes by the plug depends on (I) the pressure attained before the rupture disk breaks and (2) the time it takes for this pressure to be built UP. The second condition (examination at will after any firing) is met by using for specimens short rods that have flat areas ground on opposite sides. These flat

Jan 1, 1949

By R. Ingerson

Bore surfaces of used guns commonly show a pattern of cracks in various degrees of development. It has been suggested that these cracks may aid erosion by providing channelways for the gases, eventually leading to the tearing out of blocks of metal. Under the general studies of gun erosion conducted at the Geophysical Laboratory it appeared desirable to consider this factor, and to determine the resistance to surface cracking offered by gun steel and by various other materials that might be used in the bores of guns. Method and Apparatus In order to make such a determination it is necessary to have (I) an arrangement in which the surface to be studied can be subjected to conditions similar to those in a gun with respect to temperature, pressure (developed by explosion gases), composition of the gases and length of time the surface is exposed to the gases; and (2) a specimen that can be examined readily after any number of shots, and then fired again, if necessary. The first of these conditions can be met by using an explosion vessel designed by H. S. Roberts of the Geophysical Laboratory. Fig I shows a cross-section of the apparatus. The "gun" G from which the charge is fired is made from the receiver of a caliber 0.30 army rifle, M1903, and the charges are prepared in caliber 0.30 cartridge cases. The test specimen S is held in place by a cone-shaped plug P and by a steel bridge B which is bolted to the outside of the explosion vessel on either side of the section shown. The plug, in turn, is held in place by a screw collar C. Maximum pressure is controlled by a brass rupture disk R. Part of the explosion gases flow past the two flat areas on S. Temperature and composition of gases, and the time before the rupture disk breaks, can be controlled by amount and kind of powder used, and pressure can be controlled by using rupture disks of different thickness. While the explosion vessel used was not designed so that temperature and pressure could be measured, in other vessels of closely similar size and shape containing proportionate charges of the same kind of powder as that used for standard testing procedure, values of 2700°K and 50,000 psi were obtained. Since the orifices past the flat areas on the plug are small compared to the rupture disk hole (I:I6), most of the gas goes out through the rupture disk when it breaks. The amount that goes by the plug depends on (I) the pressure attained before the rupture disk breaks and (2) the time it takes for this pressure to be built UP. The second condition (examination at will after any firing) is met by using for specimens short rods that have flat areas ground on opposite sides. These flat

Jan 1, 1949

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world's annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months' to several years' duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1'2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis' method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world's annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months' to several years' duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1'2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis' method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By Gorr W. W., Wyche E. H, R. Smith

The combination of high strength and corrosion resistance of cold-worked 18 Cr, 8 Ni steel has been advantageously utilized for some time, particularly in aircraft and rail car structures. There are, however, certain limitations on the use of such materials because the high strengths can be obtained only by cold-working, limiting the available products to sheets, strip, wire and tubes. The authors sought to overcome these limitations by resorting to precipitation-hardening, which has been used so successfully in nonferrous metallurgy but only to a limited extent in iron-base alloys. Accomplishment of this objective not only overcame the limitations, but also effected certain improvements in mechanical and other properties. This paper is an account of the development by Carnegie-Illinois Steel Corporation of a precipitation-hardening 18-8 stainless steel (called Stainless W‡ and tentatively identified as type 322). A description is given of its composition and metallurgical characteristics, heat-treatment, physical and mechanical properties and corrosion resistance. Development of the New Steel For a considerable length of time the authors were unable to determine the mechanism of the precipitation-hardening process that had been noted by Ffield18,19 in 18-8 Ti or 18-8 Cb after cold-working and reheating to moderately elevated temperatures. All known variables were exhaustively studied, but with little success. However, results began to indicate that chemical composition was the most important variable, particularly the ratio of austenite-forming to ferrite-forming elements. The investigators then focused their attention upon the composition, and, in particular, upon the element titanium and its mode of alloying in the presence of other elements. A heat was obtained that could not be brought to the softness level of annealed 18-8. The response to cold-straining and aging* was very marked by previous standards, and, more important, cold-straining was found to be entirely unnecessary to produce the precipitation-hardening effect. The chemical composition of this heat was: C, 0.06 per cent; Mn, 0.54; P, 0.016; S, 0.016; Si, 0.58; Ni, 7.28; Cr, 17.60; Ti, 0.90; Al, 0.17. For some time the development work, particularly on composition, was carried

Jan 1, 1947

By Gorr W. W., R. Smith, Wyche E. H

The combination of high strength and corrosion resistance of cold-worked 18 Cr, 8 Ni steel has been advantageously utilized for some time, particularly in aircraft and rail car structures. There are, however, certain limitations on the use of such materials because the high strengths can be obtained only by cold-working, limiting the available products to sheets, strip, wire and tubes. The authors sought to overcome these limitations by resorting to precipitation-hardening, which has been used so successfully in nonferrous metallurgy but only to a limited extent in iron-base alloys. Accomplishment of this objective not only overcame the limitations, but also effected certain improvements in mechanical and other properties. This paper is an account of the development by Carnegie-Illinois Steel Corporation of a precipitation-hardening 18-8 stainless steel (called Stainless W‡ and tentatively identified as type 322). A description is given of its composition and metallurgical characteristics, heat-treatment, physical and mechanical properties and corrosion resistance. Development of the New Steel For a considerable length of time the authors were unable to determine the mechanism of the precipitation-hardening process that had been noted by Ffield18,19 in 18-8 Ti or 18-8 Cb after cold-working and reheating to moderately elevated temperatures. All known variables were exhaustively studied, but with little success. However, results began to indicate that chemical composition was the most important variable, particularly the ratio of austenite-forming to ferrite-forming elements. The investigators then focused their attention upon the composition, and, in particular, upon the element titanium and its mode of alloying in the presence of other elements. A heat was obtained that could not be brought to the softness level of annealed 18-8. The response to cold-straining and aging* was very marked by previous standards, and, more important, cold-straining was found to be entirely unnecessary to produce the precipitation-hardening effect. The chemical composition of this heat was: C, 0.06 per cent; Mn, 0.54; P, 0.016; S, 0.016; Si, 0.58; Ni, 7.28; Cr, 17.60; Ti, 0.90; Al, 0.17. For some time the development work, particularly on composition, was carried

Jan 1, 1947

By Carl A. Zapffe, M. Eleanor Haslem

The present investigation has three principal purposes: 1. To develop a method for measuring hydrogen embrittlement that avoids cer, tain errors complicating previously used methods. 2. To explore in a preliminary way some of the fundamental factors controlling embrittlement. 3. To apply the measurements specifically to stainless grades of steel, whose sensitivity or insensitivity to hydrogen embrittlement has never been clearly defined. Selecting a Test Method Hydrogen embrittlement is a condition of low ductility resulting from excessive absorption of hydrogen by the steel at some period in its history, and may be revealed by almost any test involving cold deformation. Tensile tests, impact tests, and bend tests are commonly used for detecting hydrogen embrittlement; although numerous other tests, such as cold-upsetting or extrusion, could be used. The simplicity of using a wire specimen for cathodic and acid pickling tests, and the especial adaptability of the bend test to wire specimens, led to selection of the bend test for the present research. Bend tests usually have been of three general types: (I) fatigue, (2) reversed bend, and (3) single bend. The first two types, though widely used, are inaccurate because their measurements are counteracted by an aging effect; and the third type has not been developed to its fullest utility. The effect of cold-working in removing hydrogen is well known. During a bend test hydrogen can be observed escaping from the convex side simply by coating the specimen with oil; and any technique employing flexing or reverse bending may therefore have its measurements masked because the mechanical action reduces the embrittlement during the test. This factor is so important that even elastic flexing of a hydrogen-charged wire specimen should be avoided before testing if accurate measurements are desired. Developing a Machine for Measuring Hydrogen Embrittlement As for the single-bend test, its theory is good, and recovery caused by mechanical work is kept to a minimum. With a given degree of hydrogen embrittlement, a specimen will break at a given angle if the bending is applied unidirectionally and uniformly. The radius of the bend must be kept constant; and the rate of bending should be a constant, slow enough to allow reading of the breaking angle, and yet rapid enough to prevent significant recovery from the escape of hydrogen during bending. A simple apparatus (Fig. I) was constructed using a type H Foxboro drive unit A, which is a synchronous motor with a gear-reduction ratio of 600 to I. A cord, fixed at one end to a wooden pulley B on the drive shaft of the motor, follows the pe-

Jan 1, 1947

By Carl A. Zapffe, M. Eleanor Haslem

The present investigation has three principal purposes: 1. To develop a method for measuring hydrogen embrittlement that avoids cer, tain errors complicating previously used methods. 2. To explore in a preliminary way some of the fundamental factors controlling embrittlement. 3. To apply the measurements specifically to stainless grades of steel, whose sensitivity or insensitivity to hydrogen embrittlement has never been clearly defined. Selecting a Test Method Hydrogen embrittlement is a condition of low ductility resulting from excessive absorption of hydrogen by the steel at some period in its history, and may be revealed by almost any test involving cold deformation. Tensile tests, impact tests, and bend tests are commonly used for detecting hydrogen embrittlement; although numerous other tests, such as cold-upsetting or extrusion, could be used. The simplicity of using a wire specimen for cathodic and acid pickling tests, and the especial adaptability of the bend test to wire specimens, led to selection of the bend test for the present research. Bend tests usually have been of three general types: (I) fatigue, (2) reversed bend, and (3) single bend. The first two types, though widely used, are inaccurate because their measurements are counteracted by an aging effect; and the third type has not been developed to its fullest utility. The effect of cold-working in removing hydrogen is well known. During a bend test hydrogen can be observed escaping from the convex side simply by coating the specimen with oil; and any technique employing flexing or reverse bending may therefore have its measurements masked because the mechanical action reduces the embrittlement during the test. This factor is so important that even elastic flexing of a hydrogen-charged wire specimen should be avoided before testing if accurate measurements are desired. Developing a Machine for Measuring Hydrogen Embrittlement As for the single-bend test, its theory is good, and recovery caused by mechanical work is kept to a minimum. With a given degree of hydrogen embrittlement, a specimen will break at a given angle if the bending is applied unidirectionally and uniformly. The radius of the bend must be kept constant; and the rate of bending should be a constant, slow enough to allow reading of the breaking angle, and yet rapid enough to prevent significant recovery from the escape of hydrogen during bending. A simple apparatus (Fig. I) was constructed using a type H Foxboro drive unit A, which is a synchronous motor with a gear-reduction ratio of 600 to I. A cord, fixed at one end to a wooden pulley B on the drive shaft of the motor, follows the pe-

Jan 1, 1947

By R. L. Rickett, N. C. Fick

Despite the large volume of literature on alloys of iron and silicon,' there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carl~on and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in sheet and strip form, the constitution nas determined of a series of commercial silicon steels containing 0.05 to 0.08 per cent carbon and 0.20 to 4.1 per cent silicon, over the temperature range 1300° to 1500°F. These alloys were all from regular production heats and of commercial quality. The results of the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented Material and Procedure All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness—the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1947

By N. C. Fick, R. L. Rickett

Despite the large volume of literature on alloys of iron and silicon,' there is little published information dealing specifically with the constitution, at various temperatures, of the alloys containing less than 0.10 per cent carl~on and from 0.5 to 4.5 per cent silicon that are used extensively in the electrical industry. Because such information was needed by those engaged in the production of these alloys in sheet and strip form, the constitution nas determined of a series of commercial silicon steels containing 0.05 to 0.08 per cent carbon and 0.20 to 4.1 per cent silicon, over the temperature range 1300° to 1500°F. These alloys were all from regular production heats and of commercial quality. The results of the tests are given in Fig. I and for comparison the constitution diagram of iron-silicon alloys with 0.01 to 0.02 per cent carbon, taken from the literature, is also presented Material and Procedure All steels were hot-rolled to a thickness of 0.060 to 0.080 in. and used in this condition. Their chemical compositions, including over-all check analysis, and "center" analysis for carbon and silicon, are given in Table I. The so-called center analysis was determined on samples pickled to remove the outer surface and leave only the center third of the gauge thickness—the portion of the sample on which metallographic ratings were based. In most, but not all, of the alloys, slightly higher carbon was found at the center than when the whole strip was sampled; the two methods of sampling show relatively little difference in silicon. Two of the steels, A and E, contain relatively high phosphorus, while I and K are somewhat higher in manganese than the others. The procedure consisted essentially of heating specimens (about 1/16 by 3/8 by 3/4 in.), protected from oxidation or change in carbon content, at a temperature in the desired range and for a selected period, after which they were quenched in iced brine; the degree of transformation that had then occurred was determined by metallographic examination. The soaking periods were selected after preliminary investigation had shown that a con-

Jan 1, 1947

By C. G. Dunn

Nuclei that are formed during the recrystallization of a grain following plastic deformation generally have orientations that differ from the original. This aspect of recrystallization may be described in terms of orientation changes. It was shown previously, in an investigation on recrystallization in silicon ferrite,&apos; that the observed orientation changes were highly improbable on a chance basis, and that some mechanism must be involved. Analysis showed that the data could be satisfactorily classified into the smaller of two subclasses† of the 36 third-order twin transformations. No attempt was made at that time to classify the data within the special class of 12 third-order twin transformations, although results did indicate a greater probability for some of them to occur. A classification of this type would be more valuable, of course, with more data on orientation changes per old deformed grain. The present work fulfills this condition to some degree and also extends the scope of the investigation to include the effects of original orientation and the amount of plastic deformation. The effect of original orientation is of considerable interest because of the known effects of orientation on plastic deformation, particularly with regard to degree of fragmentation and the formation of deformation bands, and because the orientations produced by deformation should influence the orientations obtained through recrystallization. Barrett and Levenson2 reported that single crystals of iron deformed in the range 82 to 97 per cent could be put into three general classes; namely, crystals in class I maintained a reasonably sharp single orientation, those in class 2 transformed into two distinct orientations, and those in class 3 changed into a large number of major and minor orientations. Something similar would be expected for silicon ferrite crystals, and verification of this for a few cases of types class I and class 2 deformation has been reported elsewhere3 for single crystals of silicon ferrite cold-rolled in the range 10 to 20 per cent. As an example of class 2 deformation, it was shown that a crystal of silicon ferrite cold-rolled in a (110) plane in a <100> direction developed two layers, or deformation bands differing in orientation. When this happens it is possible to etch away one band and leave a single structure for use in studying the orientation changes that occur during recrystallization. when preferred crystal orientations are obtained in recrystallization, it is not particularly necessary to evaluate groups of common orientation, as was done previously (ref. I, Table 6); but an

Jan 1, 1947

By C. G. Dunn

Nuclei that are formed during the recrystallization of a grain following plastic deformation generally have orientations that differ from the original. This aspect of recrystallization may be described in terms of orientation changes. It was shown previously, in an investigation on recrystallization in silicon ferrite,&apos; that the observed orientation changes were highly improbable on a chance basis, and that some mechanism must be involved. Analysis showed that the data could be satisfactorily classified into the smaller of two subclasses† of the 36 third-order twin transformations. No attempt was made at that time to classify the data within the special class of 12 third-order twin transformations, although results did indicate a greater probability for some of them to occur. A classification of this type would be more valuable, of course, with more data on orientation changes per old deformed grain. The present work fulfills this condition to some degree and also extends the scope of the investigation to include the effects of original orientation and the amount of plastic deformation. The effect of original orientation is of considerable interest because of the known effects of orientation on plastic deformation, particularly with regard to degree of fragmentation and the formation of deformation bands, and because the orientations produced by deformation should influence the orientations obtained through recrystallization. Barrett and Levenson2 reported that single crystals of iron deformed in the range 82 to 97 per cent could be put into three general classes; namely, crystals in class I maintained a reasonably sharp single orientation, those in class 2 transformed into two distinct orientations, and those in class 3 changed into a large number of major and minor orientations. Something similar would be expected for silicon ferrite crystals, and verification of this for a few cases of types class I and class 2 deformation has been reported elsewhere3 for single crystals of silicon ferrite cold-rolled in the range 10 to 20 per cent. As an example of class 2 deformation, it was shown that a crystal of silicon ferrite cold-rolled in a (110) plane in a <100> direction developed two layers, or deformation bands differing in orientation. When this happens it is possible to etch away one band and leave a single structure for use in studying the orientation changes that occur during recrystallization. when preferred crystal orientations are obtained in recrystallization, it is not particularly necessary to evaluate groups of common orientation, as was done previously (ref. I, Table 6); but an

Jan 1, 1947

By C. G. Dunn

It is well known that plastic deformation alters many of the properties of a metal and subsequent heat-treatment partially or completely restores these properties.l In the deformed or strained state, the metal is unstable and tends to change toward a condition called a "strain-free state." The transformation occurs through recovery, recrystallization, and grain growth—processes that may take place singly or in combination. The distortion of the lattice of an individual grain of a metal in a state of strain may be rather complex in nature, because plastic deformation produces: (I) dislocations within mosaic blocks; (2) elastic variations of the lattice spacings; and (3) gross alterations throughout the lattice, especially along slip planes, along composition planes between a grain and its mechanical twins, and along boundaries of deformation bands. These gross alterations are of the nature of bent planes or rotated regions of the crystal lattice and are revealed by a spread in the orientation of the grain. Although we cannot describe these strains and their formation accurately because of insuffcient knowledge, we can, nevertheless, use the information as well as possible to obtain a better understanding of recovery processes. In recovery, the lattice of a grain is not made anew as it is in recrystallization, but is improved or mended in such a way that the basic structure remains unaltered: Until recatly observations were .that recovery produced no marked changes in the shapes of spots in Laue diffraction patterns, whereas recrystallization did, but now it is known for silicon ferrite2 that Laue spots may become quite sharp entirely through recovery. Consequently, the shape of Laue spots alone would not be a suitable test to distinguish between recovery and recrystallization. There is considerable evidence that the micro-structure usually does not change visibly during recovery. Absence of a visible change in the microstructure, therefore, provides a sufficient test of recovery in many cases. However, including this observation in a definition of recovery as a necessary condition (this is usually done) is unfortunate, because recovery may, as will become evident later, produce new grain boundaries that are visible not only in the microstructure but also in the macrostructure. For the present, therefore, let us say that a necessary condition for a process to be one of recovery is that the principal orientation or orientations of a deformed grain be essentially unchanged throughout the transformation toward the strain-free state. Several transformations may occur that fulfill this condition, and the nature of the distortion in a grain indicates what these must be if the lattice is to be mended in part or fully. Consequently, it will be convenient as well as

Jan 1, 1947

By C. G. Dunn

It is well known that plastic deformation alters many of the properties of a metal and subsequent heat-treatment partially or completely restores these properties.l In the deformed or strained state, the metal is unstable and tends to change toward a condition called a "strain-free state." The transformation occurs through recovery, recrystallization, and grain growth—processes that may take place singly or in combination. The distortion of the lattice of an individual grain of a metal in a state of strain may be rather complex in nature, because plastic deformation produces: (I) dislocations within mosaic blocks; (2) elastic variations of the lattice spacings; and (3) gross alterations throughout the lattice, especially along slip planes, along composition planes between a grain and its mechanical twins, and along boundaries of deformation bands. These gross alterations are of the nature of bent planes or rotated regions of the crystal lattice and are revealed by a spread in the orientation of the grain. Although we cannot describe these strains and their formation accurately because of insuffcient knowledge, we can, nevertheless, use the information as well as possible to obtain a better understanding of recovery processes. In recovery, the lattice of a grain is not made anew as it is in recrystallization, but is improved or mended in such a way that the basic structure remains unaltered: Until recatly observations were .that recovery produced no marked changes in the shapes of spots in Laue diffraction patterns, whereas recrystallization did, but now it is known for silicon ferrite2 that Laue spots may become quite sharp entirely through recovery. Consequently, the shape of Laue spots alone would not be a suitable test to distinguish between recovery and recrystallization. There is considerable evidence that the micro-structure usually does not change visibly during recovery. Absence of a visible change in the microstructure, therefore, provides a sufficient test of recovery in many cases. However, including this observation in a definition of recovery as a necessary condition (this is usually done) is unfortunate, because recovery may, as will become evident later, produce new grain boundaries that are visible not only in the microstructure but also in the macrostructure. For the present, therefore, let us say that a necessary condition for a process to be one of recovery is that the principal orientation or orientations of a deformed grain be essentially unchanged throughout the transformation toward the strain-free state. Several transformations may occur that fulfill this condition, and the nature of the distortion in a grain indicates what these must be if the lattice is to be mended in part or fully. Consequently, it will be convenient as well as

Jan 1, 1947

By Bever M. B., Floe Carl F., Hung Liang

Data on the solubility of hydrogen in iron-silicon alloys are of practical interest, as hydrogen causes gas unsoundness and embrittlement in iron and steel and is also a factor in the metallurgy of cast iron. Zapffe and Simsl have recently demonstrated that in deoxidized iron and steel castings gassiness and bleeding are primarily functions of the hydrogen content of the liquid metal. These authors also suggested convincingly that ordinary melting and casting practice provides several sources of hydrogen for absorption by the metal. Norbury and Morgan2 and Boyles3 have shown that dissolved hydrogen affects the graphitization of cast iron. Schneble and Chipman4 included in a study of the effects of superheating on the properties of cast iron an investigation of the part played by hydrogen. Schwartz, Guiler and Barnett5 investigated the significance of hydrogen in the metallurgy of malleable cast iron. A complete interpretation of investigations of this kind calls for equilibrium values of the solubility of hydrogen in the liquid and solid phases. From the theoretical standpoint, the solubility of gases, especially hydrogen, may reveal some aspects of the nature of liquid metallic solutions. This was implied in the early work of Sieverts6 on the effect of alloying additions on the solubility of hydrogen in copper. Recent work by Bever and Floe7 has shown that in liquid copper-tin alloys the solubility of hydrogen changes abruptly at the composition of the intermetallic compound Cu3Sn. It is of considerable interest to determine whether liquid alloys of iron also have compositions at which the solubility of hydrogen exhibits a discontinuous or otherwise unique behavior. Among the various alloys of iron the iron-silicon system is important because of the presence of silicon in various structural alloy steels, transformer sheets, cast irons and special acid-resisting castings. The various grades of ferrosilicon, finally, cover almost the entire remainder of the composition range. Published information on the solubility of hydrogen in iron-silicon alloys is meager. The first values for pure liquid iron were reported in 1910-191 1 sieverts and Krumbhaar8 and by sieverts.9 They found that 100 grams of iron absorbs 28 c.c. of hydrogen at 1550°C and One atmosphere pressure, and 31 C.C. at 1650°C. In 1938 Sieverts, Zapf and Moritz10 published a value of 26.3 C.C. at 1550°C. Data on the solubility of hydrogen in liquid iron-silicon alloys and in liquid silicon are not available. Martin1&apos; investigated

Jan 1, 1947

By Bever M. B., Floe Carl F., Hung Liang

Data on the solubility of hydrogen in iron-silicon alloys are of practical interest, as hydrogen causes gas unsoundness and embrittlement in iron and steel and is also a factor in the metallurgy of cast iron. Zapffe and Simsl have recently demonstrated that in deoxidized iron and steel castings gassiness and bleeding are primarily functions of the hydrogen content of the liquid metal. These authors also suggested convincingly that ordinary melting and casting practice provides several sources of hydrogen for absorption by the metal. Norbury and Morgan2 and Boyles3 have shown that dissolved hydrogen affects the graphitization of cast iron. Schneble and Chipman4 included in a study of the effects of superheating on the properties of cast iron an investigation of the part played by hydrogen. Schwartz, Guiler and Barnett5 investigated the significance of hydrogen in the metallurgy of malleable cast iron. A complete interpretation of investigations of this kind calls for equilibrium values of the solubility of hydrogen in the liquid and solid phases. From the theoretical standpoint, the solubility of gases, especially hydrogen, may reveal some aspects of the nature of liquid metallic solutions. This was implied in the early work of Sieverts6 on the effect of alloying additions on the solubility of hydrogen in copper. Recent work by Bever and Floe7 has shown that in liquid copper-tin alloys the solubility of hydrogen changes abruptly at the composition of the intermetallic compound Cu3Sn. It is of considerable interest to determine whether liquid alloys of iron also have compositions at which the solubility of hydrogen exhibits a discontinuous or otherwise unique behavior. Among the various alloys of iron the iron-silicon system is important because of the presence of silicon in various structural alloy steels, transformer sheets, cast irons and special acid-resisting castings. The various grades of ferrosilicon, finally, cover almost the entire remainder of the composition range. Published information on the solubility of hydrogen in iron-silicon alloys is meager. The first values for pure liquid iron were reported in 1910-191 1 sieverts and Krumbhaar8 and by sieverts.9 They found that 100 grams of iron absorbs 28 c.c. of hydrogen at 1550°C and One atmosphere pressure, and 31 C.C. at 1650°C. In 1938 Sieverts, Zapf and Moritz10 published a value of 26.3 C.C. at 1550°C. Data on the solubility of hydrogen in liquid iron-silicon alloys and in liquid silicon are not available. Martin1&apos; investigated

Jan 1, 1947

By V. L. Elliott, C. L. Meyette

The conditioning of semifinished steel products such as billets, blooms, and slabs to remove surface defects before further processing to finished products is a necessary accompaniment to steel mill rolling operations. A knowledge of the kinds of defects which occur and of the conditions in melting, teeming, and rolling that may lead to their occurrence is favorable to the production of quality products. Surface defects may be classed as either of mechanical origin such as those that occur in the heating and rolling operations and include breaks, tears, guide marks, mechanical laps and the like, or they may have been in the ingot before heating and rolling. Examples of the latter are ingot cracks, blow-holes, scabs, and inclusions which lead to the numerous known types of seams and surface flaws. Most of the common types of surface defects and methods for their identification by visual examination or by the aid of macro-etch tests are well known. The conditions which caused their formation are also appreciably understood and this knowledge has been instrumental in the establishment of methods for metallurgical control. There are, however, defects of doubtful origin. In any endeavor to trace the causes for their occurrence, the question of first concern is: I. Whether they were formed in the rolling procedure. 2. Whether they existed in the ingot prior to rolling. In the case of semifinished products which are rerolled to finished products there is also the question of whether they were formed in the primary or in the secondary rolling. In metallurgical laboratories where numerous or routine examinations of the quality of rolled products are made over the course of time, there will doubtless be many puzzling cases of defect origin. Microscopic examination of the defects may, however, reveal a characterizing condition that can be used to classify them broadly with respect to their origin. Such a condition has been observed and, after detailed investigation, is described here with the thought that it may offer a usable and relatively simple solution to a bothersome problem. Basis For Classifying In this discussion the term "mechanical type defects" will be used to designate those that have occurred as a result of the rolling operations such as in rolling from the ingot to billets, blooms, or slabs or in rerolling to finished products. The term "steel type defects" will be used to designate those that were present in the ingot prior to primary rolling or that were in the semifinished product prior to secondary rolling to finished product. The basis for distinguishing between the two types of defects lies in the relative degree of subscale formation surrounding them. Subscale is defined1 as a zone of

Jan 1, 1949

By V. L. Elliott, C. L. Meyette

The conditioning of semifinished steel products such as billets, blooms, and slabs to remove surface defects before further processing to finished products is a necessary accompaniment to steel mill rolling operations. A knowledge of the kinds of defects which occur and of the conditions in melting, teeming, and rolling that may lead to their occurrence is favorable to the production of quality products. Surface defects may be classed as either of mechanical origin such as those that occur in the heating and rolling operations and include breaks, tears, guide marks, mechanical laps and the like, or they may have been in the ingot before heating and rolling. Examples of the latter are ingot cracks, blow-holes, scabs, and inclusions which lead to the numerous known types of seams and surface flaws. Most of the common types of surface defects and methods for their identification by visual examination or by the aid of macro-etch tests are well known. The conditions which caused their formation are also appreciably understood and this knowledge has been instrumental in the establishment of methods for metallurgical control. There are, however, defects of doubtful origin. In any endeavor to trace the causes for their occurrence, the question of first concern is: I. Whether they were formed in the rolling procedure. 2. Whether they existed in the ingot prior to rolling. In the case of semifinished products which are rerolled to finished products there is also the question of whether they were formed in the primary or in the secondary rolling. In metallurgical laboratories where numerous or routine examinations of the quality of rolled products are made over the course of time, there will doubtless be many puzzling cases of defect origin. Microscopic examination of the defects may, however, reveal a characterizing condition that can be used to classify them broadly with respect to their origin. Such a condition has been observed and, after detailed investigation, is described here with the thought that it may offer a usable and relatively simple solution to a bothersome problem. Basis For Classifying In this discussion the term "mechanical type defects" will be used to designate those that have occurred as a result of the rolling operations such as in rolling from the ingot to billets, blooms, or slabs or in rerolling to finished products. The term "steel type defects" will be used to designate those that were present in the ingot prior to primary rolling or that were in the semifinished product prior to secondary rolling to finished product. The basis for distinguishing between the two types of defects lies in the relative degree of subscale formation surrounding them. Subscale is defined1 as a zone of

Jan 1, 1949

By H. T. Clark, S. Feigenbaum

The importance of measuring the temperature of molten steel in the open-hearth furnace has been recognized for many years. Poor temperature control may be costly to steelmaking operations and lead to a lowered quality of the steel. Low or excessive temperatures may shorten the life of the furnace, ladles and molds. Rates of reactions in the furnace and efficiencies of deoxidizers are known to change materially with a change in the temperature of the metal and slag. Ladle skulls and mold and stool stickers cause steel to be scrapped instead of being converted into useful products. Finally, the structure, segregation and surface condition of ingots are affected by the teeming temperature. Mill investigations of the effect of bath temperature upon steelmaking operations have been largely qualitative in character, based upon observations by practical melting men. The physical chemist has used the empirical information available and has reached reasonable and useful conclusions with respect to the various melting processes. The introduction of a reliable direct-reading pyrometer will permit accurate quantitative evaluation of the effects of temperature and should furnish a more rational basis for study of the thermochemistry of steelmaking. The problem is not merely one of making a small numbcr of temperature measurements in the open-hearth furnace. This has been done by several methods to a * Assistant Manager, Research and Development, Jones and Laughlin Steel Corporation, Pittsburgh, Pennsylvania. Issued as T.P. 2031 in MEtals Technology, June 1946; also in Open Hearth Proc., 1946. † Open-hearth Metallurgist, Jones and 1aughlin Steel Corporation, Aliquippa. Pennsylvania. degree of precision that was apparently satisfactory. Considerable effort by a number of investigators has been directed rather to the development of an open-hearth bath pyrometer that would be both accurate and practical for routine measurements. To be practical, the pyrometer should be inexpensive to operate; that is, the installation, operating and maintenance costs should be exceeded by the tangible benefits to the open-hearth operator. Temperatures from 2800&apos; to 3100°F. are. encountered in the open-hearth furnace. The surface of the molten metal is covered by several inches of slag, which prevents direct observation of the metal surface for optical or radiation measurements. Both slag and metal are highly reactive at these temperatures and will attack to a greater or lesser extent any material immersed in them. Adequate protectioil of thermocouples, which of necessity must be brought to the temperature of the bath, has generally resulted in a large, heavy assembly made up of brittle materials, unsuited for handling on the open-hearth floor. The life of the equipment was short and maintenance was an important consideration. Earlier Work Any of a number of Physical Properties of liquid steel could conceivably be used a a basis for temperature measurement. Efforts to the present time, however, have been confined largely to measuring either the thermal electromotive force generated between two dissimilar materials immersed in the steel or the intensity of radiation from the surface of the steel. These

Jan 1, 1947