By L. J. Howell, A. S. Roy, H. H. Kellogg

KNOWLEDGE of the phase diagram of salt systems is important for selection of the optimum con- ditions for electro winning of the refractory metals from fused salts. This note summarizes the studies of the NaC1-rich portion (0 to 22 mol pct HfC14) of the NaC1-HfC14 phase diagram. Melts in this composition range have vapor pressures well below one atmosphere and melting points between 548° and

Jan 1, 1959

By P. R. Swann, J. G. Parr

Quenched structures were studied in alloys containing up to 12.5 pct cobalt. The subsequent decomposition of a 10 pct cobalt retained-ß phase alloy was investigated using metallographic and X-ray diffraction methods. Hardness measurements also were made during the decomposition process. Precipitation of Ti2Co is by nucleation and growth; and an activation energy of 50,000 cal per mole was determined. The values of the coefficient ß suggest that the precipitate is pearlitic at temperatures between 450 and 475°C, and spheroidal between 500 and 525°C. THIS paper describes part of a series of invesligations into phase transformations in binary alloys of titanium with transition elements. The general approach is similar to that taken in work on titanium-iron and titanium-nickel alloys.' Previous investigators'' have established the titanium-rich end of the titanium-cobalt phase diagram, reproduced in Fig. 1. Orrell and Fontana' showed that alloys containing more than about 6 pct" cobalt quenched from the ß range, produced 100 pcl retained-p phase. The isothermal decomposition of alloys containing between 0.8 pct Co and 15.5 pct CO was investigated by the same workers in the temperature range 650 to 1000°C. They reported that these alloys transformed into a or Ti,Co depending on the cobalt content, but no quantitative data were given. In the work to be described a series of alloys containing 0.8 pct Co to 12.5 pct Co was examined in the quenched condition. The 10 pct Co alloy (the lowest cobalt content to retain 100 pct ß on quenching) was selected for further work on the tempering kinetics of the ß decomposition. Experimental Procedure Since our own melting equipment was not installed at the outset of this work, the Physical Metallurgy Division of the Department of Mines and Technical Surveys (Ottawa, Canada) prepared the alloys. These were made of Japanese sponge, (which when melted had a value of 103 DPH, using a 1-kg load), and electrolytically prepared cobalt. The al- loys, made up to contain 0.8, 1.6, 3.3, 5.8, 8.3, 10.0 and 12.5 pct Co, were homogenized by swaging into rods at 900°C. Filings were taken from the rods, and any iron chips from the file were separated magnetically. Size fractions of both plus and minus 200 mesh (about 75p) were shown by their constitution, after annealing just below the eutectoid temperature, to contain the same cobalt content. Consequently, it was permissible to use the —200-mesh fraction, knowing it to be representative of the rod composition. Quenching in argon was carried out in a newly designed furnace, whose features include (1) an Inconel furnace tube, (2) a positive pressure of argon maintained at all times in the furnace—even when a sample is removed or inserted. The furnace is shown in Fig. 2 and is described in the Appendix. The tempering processes were carried out on powder samples sealed in evacuated quartz capsules. Since the highest tempering temperature was 525OC, no protection against reaction with the quartz was necessary. (Tests were made on filings of iodide titanium and showed no hardness increase after equivalent heat-treatments.) A thermocouple was attached to the capsule, which was heated to the

Jan 1, 1959

By J. J. Becker

Changes in magnetic properties with particle size are used to study the precipitation process in a Cu-Co alloy. In particular, the effect of a field during aging in producing anisotropy is shown to occur entirely during the growth of the particles, after precipitation is complete. HEAT-treatment in a magnetic field is done commercially to improve the magnetic properties of a number of materials. These can be divided into solid-solution alloys and precipitation alloys. The Permalloys are representative of the first type, and magnetic annealing greatly increases their maximum permeability. On the other hand, in precipitation alloys such Alnico 5 the important result is an increase in maximum energy product. The effect of the field in all cases is to bring about an additional magnetic anisotropy, uniaxial in nature, which makes the hysteresis loop more upright when measured in the direction in which the field was applied. The structural origin of the anisotropy brought about by magnetic annealing is not well understood. In the solid solution alloys, one possible explanation is based on ordering.' Another possibility is the orientation of like-atom pairs.' The precipitation systems known to respond to magnetic heat treatment are Alnico 2, in which the effect was first discovered," Alnico 5, cobalt ferrite (oxide),' and Cu-Co alloys.3 n these materials, the field affects the precipitation process itself in some way. Although there has been much work on Alnico 5. its nature is still incompletely understood. According to Geisler,' the precipitation reaction is of the

Jan 1, 1959

By H. W. Knott, M. H. Mueller, P. A. Beck, W. P. Chernock

PREFERRED orientation studies by Harris of rolled uranium rods indicated that hot rolling to a small reduction of area caused the (010) planes to become strongly oriented and the (110) planes weakly oriented perpendicular to the rolling direc- tion. The relative intensities of these two fiber texture components were reversed upon rolling to higher reductions of area. Cold rolling caused the (010) planes to become strongly aligned and the (130) planes weakly aligned perpendicularly to the rolling direction. The present investigation was undertaken to explore in more detail the effect on the rolling texture of variables, such as the penultimate condition, the final rolling temperature and reduction of area. In addition, the recrystallization texture of rolled uranium rods was also investigated.

Jan 1, 1959

By D. L. Martin

The study of cobalt-platinum alloys has been of interest since they represent a class of permanent-magnet material in which the disorder-to-order transformation plays a controlling role. The magnetic properties of alloys in the range 40 to 60 at. pct have been found to be greatly influenced by composition and heat-treatment. The peak properties of 4700 coercive force and 9,000,000 gauss-oersteds energy product were obtained by controlled cooling and aging. These high values combined with ductility and machin-ability give the alloys useful characteristics although their high cost limits their application. THE cobalt-platinum alloys have been of interest in the study of permanent-magnet materials ever since the discovery by Jellinghaus that they had unusually high coerceive-force values.' The high coercive force was associated by Jellinghaus with the disorder-order reaction which occurred in these alloys. This was later verified by Gebhardt and Koster in a detailed study.2 An investigation of the structure, mechanism, and kinetics of the disorder-order transformation and resulting property changes in cobalt-platinum alloys has been in progress for some years. Certain phases of this study related to equilibrium rela- tions, and to the mechanism and kinetics of the ordering reaction have been published previously.3-5 In this paper, the results of the processing and heat-treatment studies on 40 to 60 at. pct CO alloys are presented. The magnetic properties have been found to be influenced greatly by the composition, by the cooling rate from the disordering treatment, and the final ordering time and temperature. Coercive force values, Hc, of 4700 oersteds and energy values, (BH)m, approaching 9,000,000 gauss-oersteds have been obtained by controlled cooling and ordering. PROCESSING OF THE ALLOYS The composition range of interest for permanent-magnet properties centers around the equiatomic composition Copt. In this region the alloys are dis-

Jan 1, 1959

By R. G. Charles, E. A. Gulbransen, S. Barnartt

KINETICS of the reaction of zirconium with pure oxygen at elevated temperatures have been studied by several workers for periods of time up to 6 hr.1-1 In two cases,3-4 . the experimental values of oxygen uptake, w, as a function of time, t, were best fitted to the parabolic rate law w2 = kPt + constant. In others,3,4 the cubic rate law w3 = kot + constant, showed better agreement. The most recent data of Gulbransen and Andrew4 indicate that the choice between the parabolic and cubic laws for empirical representation of the data will often be arbitrary. This is particularly true if the first few minutes of the reaction with a clean zirconium surface is attributed to a different oxidation mechanism, for deviations from either rate law were found primarily during the initial period. Thus, the kinetics of this reaction have been too uncertain to permit safe extrapolation to oxidation periods of practical interest (many hundreds of hours). The data to be described are of interest, for they indicate that the cubic rate law applies over long oxidation times. The reaction of zirconium with oxygen at 1 atm pressure was followed at 350" and 450°C for 500 and 200 hr, respectively. Abraded test specimens of pure zirconium sheet' 3.0 X 2.0 X 0.012 cm in size were oxidized by the procedure previously described,3 which included periodic cooling to room temperature for weighing. The surfaces were polished to a 4/0 finish using polishing paper wet with kerosene, then wiped with petroleum ether and washed in redistilled acetone. Fig. 1 shows plots of log ? vs log t. Each curve represents the average of duplicate measurements, and deviations from the average were generally less than 3 pet. The cubic rate law (slope = 1/3) is closely followed. The rate constants, 5.2, x 10 -6 and 2.4, X 10- (mg cm-2)3 per hr at 350" and 450 oC, respectively, are plotted as log k, vs 1/T in Fig. 2, together with cubic constants calculated from the data of Gulbransen and Andrew4 for abraded specimens from the same lot of zirconium. Their data refer to runs of 6-hr duration at a pressure of 0.1 atm 0 and under conditions of uninterrupted heating. In spite of these differences, the latter data yield a straight line which appears to apply equally well to the new extended time data. The energy of activation for the oxidation process, calculated from the slope of this line, i.s 38 keal per mole. This may be compared with the value of 47 keal per mole found by Belle and Mallett3 at higher temperatures. It may be concluded tentatively that extrapolation of short-term oxidation data for zirconium to obtain the long-term behavior is best done through the cubic equation ?3 = kpt + constant. References ' E. A. Gulbransen and K. F. Andrew: AIME Trans., 1949, vol. 185, p. A.515; JouRNal OF Metals, August 1949. 'D.p. Cubicciotti Journal Amer Chemical August1949.Soc., 1950, Vol. 72, P. 3 V. Belle and M. W. Mallett: Joulnal Electro chemical Soc., 1954, ' E. A. Gulbransen 339.and K. F. Andrew: Oxidation of Zirconium Between 400" Gulbransenand 800'C.and AIME Trarzs.. 1957, vol. 209, p. 394; JOUR-Nal of Metals, April 1957. IS Barnartt, B G. Charles, and E. A. Gulbransen: Oxidation of 50 weight pet uranium-zirconium alloy, Journul Electrochemical SOC., 1957, vol. 104, p. 218.

Jan 1, 1959

By W. D. Robertson, R. E. Reed-Hill

Slip on (11221 planes, which do not contain a close-packed direction, has been identified on crystals strained at —190°C. Evidence is also presented to show that (1071) pyramidal slip is a mode of deformation at 25ºC in a limited orientation range. PYRAMIDAL slip (l011) <1120> in magnesium at elevated temperatures has been established for some time.1-2 More recently, Burke and Hibbard reported this mode of deformation at 25ºC, but their results were questioned by Craig.&apos; Also, as far as the present authors know, slip in magnesium on pyramidal planes of the second order, Type II (1122)) has not previously been reported, although Gilman"," identified (1122) slip in another hexagonal metal

Jan 1, 1959

By K. U. Snowden, J. N. Greenwood

CRACKS which form in lead exposed to fluctuating stress frequently follow a rectangular pattern. It is well known that under ordinary atmospheric conditions these cracks are intercrystalline. On the other hand after fabrication the crystal grains in lead are in general irregular polygons. The observed facts appear to be mutually contradictory. Re-examination of some lead failures has confirmed that the rectangular cracks are intercrystal- line. It follows therefore that under fluctuating stress some of the grains lose their irregular outlines and become approximately regular polygons of cubic type. G. R. Gohn and W. C. Ellis* suggest that this is due to recrystallization during the life of the part, in such a way that the new grain boundaries are aligned at 45 deg to the longitudinal strain prior to the formation of the fatigue crack. Experiments at Baillieu Laboratory—Some recent experiments carried out in the Baillieu Laboratory in conjunction with the Broken Hill Associated Smelters have thrown some light on this transition. A test piece of pure lead was polished chemically

Jan 1, 1959

By H. Bernstein

WHILE the beryllium -copper (2 pct Be) alloy is nominally nonmagnetic, the presence of iron impurity causes variations in the magnetic proper- ties which, at times, attain excessive proportions. This investigation was carried out to establish the effect of small amounts of iron on the susceptibility of the material and to determine if the effect could be minimized. Beryllium-copper is an age-hardening alloy which

Jan 1, 1959

By J. W. Freeman, J. P. Rowe, R. F. Decker

HEAT-to-heat variations in properties of an alloy of constant nominal chemical composition have been a perplexing problem to the metallurgist. These heat-to-heat differences have been especially baffling in high-temperature metallurgy. In order to establish fundamental reasons for these heat-to-heat variations, the National Advisory Committee for Aeronautics has sponsored and financially assisted an extended research program on heat-resistant alloys at the University of Michigan. As part of the program to find the contribution of processing variables, Frey, Freeman, and white&apos; studied effects of heat treating on nickel-base alloys and Ewing and reeman&apos; investigated effects of hot-working practice on N155 alloy. To extend the program to the study of effects of melting practice on high-temperature properties, a 55 Ni-20 Cr-15 Co-4 Mo-3 Ti-3 pct A1 composition was selected for experimentation. The objective of this program was to establish the melting-practice variables which influenced the hot-working characteristics and creep-rupture properties and, at the same time, establish the metallurgical mechanisms for the effects. During the course of the investigation of practices using vacuum melting, it became increasingly evident through chemical analyses supplied by industrial concerns that a major variable was melt reaction with the crucible. This paper is devoted to the results of this phase of the melting-practice study. EXPERIMENTAL PROCEDURES Experimental 10-lb heats were induction melted in the University of Michigan vacuum-melting unit with the melting practices outlined in Table I. Aim analysis for the basic alloy, in wt pct, for all heats was as follows: Cr Co Mo Ti Al 20.0 15.0 4.0 3.1 3.1 Mn Si C Ni 0.12 0.12 0.08-0.15 Bal. Small amounts of boron and zirconium were added to certain heats as listed in Table I. These additions

Jan 1, 1959

By J. H. Keeler

QUESTIONS raised during earlier investigations of the preferred orientation in titanium1 and zirco-nium sheet led to the examination of the rolling and annealing textures of beryllium and hafnium sheet. Since the c/a ratios are 1.568 and 1.584, less than that of ideal close packing, 1.633, it would be expected that the preferred orientations would be similar to those exhibited by zirconium and titanium. This was found to be true. However, in several regards the orientations observed for beryllium differed from those reported by Smigels-kas and Barrett4 and so are given here. The okientations for hafnium are presented since only the cold-rolling texture has been reported in the unclassified literature. The pole figures were determined by transmission using an X-ray spectrogoniometer with copper Ka radiation and the automatic pole-figure recorder designed by Geisler described previously.6 The intensity units in the pole figures in this case are only arbitrary since calibration against a random sample of the same material was not considered necessary for the original purpose of the examination. The beryllium sheet, cold-rolled from 0.036 in. to 0.006 in., a reduction of about 84 pct, exhibited a split texture with the [1010] direction in the rolling direction as shown in Fig. 1. The same specimen annealed in vacuo for 1 hr at 1000°C showed no change in orientation. These textures

Jan 1, 1959

By D. Turnbull, J. E. May

THE (110) [001] texture in silicon iron is of considerable interest both from the technological and scientific points of view. Its occurrence was reported more than 20 years ago.1-4 The texture develops by means of secondary re crystallizatjon5 and can be very strong, that is, greater than 90 pct alignment even thouh the primary re crystallization texture is weak or complex. This behavior is in contradistinction to the face-centered metals which develop their strong secondary recrystalliza-tion texture from a strong primary recrystalliza-tion texture.&apos;, The microstructural changes accompanying the (110) [001] texture formation in silicon iron are as follows: When properly prepared cold-rolled sheet (i.e., 0.015 in. thick) is annealed at about 800°C, primary recrystallization occurs and a fairly stable fine-grained primary recrystallized matrix of about 0.02-mm-diam grain size is produced. The material at this stage does not have the strong (110) [110] texture. As the temperature is raised to about 900°C, relatively large grains appear in the finegrained matrix and they grow at the expense of the smaller grains to many times the sheet thickness. In time the complete sample is consumed by these large grains. This process of the growth of relatively few grains (about one in 105 primary grains) at the expense of many grains is called secondary recrystallization. Since all the secondary grains are of essentially (110) [001.] orientation, the strong texture is developed by this secondary recrystallization process. Theories of the (110) [001] texture in polycrystal-line silicon iron have been proposed by Decker and Harker and by Dunn.Decker and Harker have shown that grains initially in the (110) [001] orientation will upon annealing after cold-rolling, re-crystallize back to the initial orientation. To account for the sharp texture in silicon iron they propose that (110) [001] grains become more highly strained than grains in other orientations and therefore recrystallize first. They are then the lowest energy grains and can consume their higher energy neighbors. Grains in orientations other than (110)

Jan 1, 1959

By S. Kado, G. Derge, L. Yang

Self-diffusion coefficients of silver in molten silver have been measured by means of the capillary-reservoir method in the temperature range 1002" to 1105°C. The results can be .represented by the equation D = (7.10 i 0.06) X 10-4 exp [(—8150 ± 1130)/RT]. The heat of activation agrees within the limit of experimental uncertainty with that for the viscous flow. The validity of the Eyring and the Stokes-Einstein equations are examined on the basis of the self-diffusion coefficients obtained and the known viscosity data of molten silver. MEASUREMENT of the self-diffusion coefficient of silver in molten silver was made in the temperature range 1275° to 1378°K, using the capillary-reservoir method and &"&apos; as the radioactive tracer. The experimental arrangement is shown in Fig. 1. Silver of 99.99 pct purity (fine silver), was melted and degassed in vacuum in a graphite crucible situated inside a McDanel vacuum jacket. The crucible (4 in. tall and 1 in. ID) was protected both at the top and at the bottom with graphite shields and contained about 220 g of silver. The sample holder was a piece of graphite rod (1 in. long and 1/2 in. diam) with 4 capillaries drilled longitudinally into it. The holder was screwed onto a long graphite rod (12 in. long and 74 in. diam) which was connected to a steel disk hanging on a nylon string through a glass pulley. The steel disk kept the sample holder at the center of the McDanel tube and was heavy enough to overcome the buoyancy when the holder was lowered into the molten silver. By turning a handle connected to the pulley through a tapered glass joint, it was possible to raise or lower the sample holder without breaking the vacuum. Two such arrangements were constructed, sitting side by side in 2 Kanthal furnaces. One with non-radioactive silver in its crucible was used for the diffusion run and the other with radioactive silver in its crucible was used for filling the capillaries. To fill the capillaries with radioactive silver, the sample holder was degassed first and then lowered into the radioactive molten silver in vacuum. Purified argon gas was then admitted into the system to push the liquid silver into the capillaries. After cooling in argon, the filled capillaries were polished on emery paper to expose the top of the rod and used immediately as samples for the diffusion run which was carried out at the same temperature as that used for filling the capillaries. During the diffusion run, the samples were degassed in vacuum and lowered slowly into the nonradioactive molten silver before purified argon was admitted into the system. After a predetermined period of time, the samples were raised out of the melt and cooled in argon. The temperature of the melt was measured before and after the run with a chromel-alumel thermocouple inside a McDanel protection tube. Another chromel-alumel thermocouple attached to the outside wall of the McDanel vacuum jacket was used to indicate any fluctuation in the temperature of the furnace during the run, which was found to be less than ± 2°C for the longest run made (93 min). The temperature gradient inside the molten silver was found to be negligible. No significant difference was observed in the results obtained whether the melt was stagnant during the run or was stirred by raising and lowering the sample holder slowly a few times a minute for a distance of about 1/4 in. inside the melt.

Jan 1, 1959

By D. Turnbull, R. E. Cech

Small particles, 10-20 microns diameter, of a 28.6 atom pct nickel, balance iron alloy, have been supercooled 186 C with respect to bulk alloy M, temperature. Particles exhibit a marked mechanical shock sensitivity while being held in a supercooled state. The tendency for shock to induce martensitic transformation appears to be a maximum at —140 to —160°. Slow cooling of particles in mechanical contact with one another results in extensive martensite formation. This is prob-ably the same effect as the catalytic effect observed in polycrystals where martensite formation in one grain induces transformation in other grains. AS a result of extensive research over the past decade on the martensitic transformation, a much better though not complete understanding of the transformation has resulted. Recent reviews by Bilby and Christian&apos; and Kaufman and Cohen2 have

Jan 1, 1959

By R. L. Fleischer, B. Chalmers

In order to observe size effects associated with a grain boundary, aluminum single crystals and bicrystals of various cross-sectional dimensions were deformed in tension. Typical stress-strain curves are presented in conjunction with measurements of the effects of changes in crystal dimensions. Some effects of the growth rate used in preparation of crystals are also described. It is indicated that the macroscopic constraints at a grain boundary are responsible for the most prominent grain-boundary effect, the production of multiple slip. Two measurements of the width of the region of double slip are in agreement. It is concluded that the yield stress of aluminum is affected markedly by the inherent oxide coating. THE general problem to be examined is that of dimensional effects in the plastic deformation of metal crystals. These effects will be termed "size effects" and are here defined as follows: A size effect occurs in a series of crystals if their plastic-deformation properties are a function of crystal dimensions. Clearly then size effects depend on the nature of the boundary conditions imposed on the crystal. Crystal boundaries can be of three types: interphase, inter-crystalline, and free surface. Such deformation effects as are caused by distribution of phases, grain size, lineage structure, and single crystal external geometry are specific types of size effects. This discussion will be confined primarily to grain-boundary and single-crystal size effects, though in practice most "single crystals" not only have a number of small angle boundaries but also have one or more surface phases, so that the boundary conditions appropriate to a free surface do not necessarily apply. Hence, to this extent interphase size effects will be considered. The question of size effects associated with grain boundaries (called here intercrystalline size effects)

Jan 1, 1959

By C. M. Schwartz, A. E. Austin, W. B. Wilson

High-temperature X-ray diffraction studies were conducted with Th-U alloys with up to 10 wt pet U. The solid solubility of uranium in thorium as a function of temperature was determined by the method of lattice parameters. Thorium will dissolve up to 2.5 wt pet U at 950°, 4.5 wt pet U at 1150°, and 7.5 wt pet U at 1250°C. Determinations were made of the temperature of the transition of thorium and of the effect of uranium upon the transition. The a to ß transition for thorium was observed to occur at 1330&apos; ±20°C. Mean coefficients of expansion were calculated for thorium and two alloys, and for ThO2 in contact with the thorium, using X-ray lattice-parameter data. Values obtained at 950° C for thorium and Tho2 were 12.1 and 9.40 X 10-6 per OC, respectively. Impurities obtained during the X-ray exposure were identified by diffraction and were essentially Tho2 and ThC, with two additional unknown phases being detected. The effect of the impurities upon the results is discussed. DIRECT investigation (i.e., high-temperature X-ray diffraction studies) of the phase diagram of thorium-rich uranium alloys has been shown to be necessary since recent work1 - has disclosed the presence of an allotropic transformation near 1400°C in pure thorium with the room temperature face-centered-cubic phase transforming to a body-cen-tered-cubic structure at the elevated temperature. The effect upon the transition of the addition of uranium to thorium and of the solubility of uranium in thorium at high temperatures remained unknown, yet was of interest in understanding fabrication procedures and elevated temperature use. The present work was undertaken to provide information in this area by determining the transition temperature, the effect of uranium on the transition temperature, and the solubility of uranium in thorium as a function of temperature. Experimental Work The high-temperature diffraction data were obtained using a camera especially designed for the purpose3 and capable of reaching temperatures in excess of 2000°C at pressures as low as 1 x 10." mm Hg. Temperature regulation was provided by regulating the power input to ±0.1 pet variation, and by regulating the water flow through the camera jacket to provide a constant thermal load. The X-ray sample was a rod nominally 80 mil diam, which was further turned down to 20 mil and then etched to 18 mil over 1/2 in. of one end. This was placed in the sample holder and mounted on the camera so that the smaller part was surrounded by a cylindrical tantalum-sheet radiation-type heating element. Diffraction from the sample was recorded on film after passing through a slot in the heating element and radiation-baffle shield and through beryllium vacuum windows. The X-ray film mounting was of the Straumanis type4 with a camera diameter of 114.59 mm. Since previous work of Chiotti&apos; indicated that impurities considerably alter the transition temperature, chemical analysis of the arc melted iodide crystal-bar thorium samples was obtained prior to testing. The analysis disclosed the material to contain as low as 0.001 ±0,0002 wt pet H and 0.007 ±0.001 wt pet 0. Carbon was 0.003 wt pet and nitrogen less than 0.002 wt pet. This material was sealed in mild steel in an inert atmosphere and subsequently hot rolled to 3/8-in. diam rods at a temperature of 732°C. Following removal of the jacket, the material was pickled and cold swaged to 1/8-in. rods, from which the diffraction samples were prepared. The alloys were similarly prepared, with the uranium being added during arc melting. The uranium analyses of the alloys prepared appear in Table I. The experimental procedure for diffraction examination of the three samples of high-purity thorium differed from those of the Th-U alloys. The original practice, later modified, consisted of pumping down the camera with the diffusion pump on and then admitting liquid nitrogen to the cold trap of the system. This was modified for the Th-U alloys by maintaining liquid nitrogen in the cold trap at all times before and while the diffusion pump was heated. This minor change produced a reduction in the amount of carbon pickup by the sample during exposure to the diffusion-pump vapors. The sample was brought to the desired test temperature and exposed for 21/2 hr at pressures which were usually 2 x 10-6 mm Hg, or lower. Exposures were made at

Jan 1, 1959

By W. R. Hibbard

Evidence is presented which confirms previous findings that models of solution strengthening depending solely on lattice parameter changes are incomplete. Direct evidence for the Suzuki interaction of chemical effects was obtained from alloys with constant lattice parameter, for which solution strengthening was nearly independent of temperature from 300° to 20°K. SOLUTION hardening principles have been reviewed recently by Parker and Hazlett.&apos; In addition, the interactions of dislocations and solute atoms were reviewed by Cottrell.&apos; It is not proposed to review this information again here, but to refer only to those details which are pertinent to the developments which have occurred since these papers were published. Literature Survey To set the stage, it has been known for some time that solid solutions are stronger than the pure parent metals, and that the strength increases with increasing amounts of alloying element. One of the most extensive earlier investigations was that of Lacy and Gensamer,3 who reported that the solid solution strengthening of iron is a power function of the composition, that the relative strengthening is a function of the solubility limit, and that the rate of strain hardening is a function of the amount of solution hardening. Thus, the slope of the plastic portion of the stress-strain curve increases with increasing yield strength. An approach to the development of principles resulted from work by Gulyeav,4 who reported that the strengthening effect of solid solution alloys is periodic in character when plotted as a function of the atomic number of the solute. A more quantitative approach was to relate the amount of solution hardening to the lattice parameter of a solid solution. This was done quite early by Norbury,5 and later by Brick, Martin, and Angier,6 Frye and Hume-Rothery,7 and French and Hibbard. This relationship is only approximate in character. The next development was to relate the amount of solution hardening to lattice stress, as proposed by Frye and co-workers.9 They calculated what they called ionic overlap from the lattice parameter changes represented as a change in volume, using Bridgman&apos;s hydrostatic compression equation. The resulting correlation was somewhat improved as compared to the simple correlation with lattice parameter. The next step was carried out by Dorn, Pietrow-sky, and Tietz,10 who suggested an effect of valence differences in addition to the effect of lattice parameter. Their proposed parameter shows flow stress as a single valued function of the concentration and a relationship involving these two atomic variables. In addition, they contributed new data on the temperature dependence of solution hardening which indicated that it was a strong function of temperature for aluminum alloys. Allen, Schofield, and Tate11 carried the valency effect even further by reporting data indicating that with a given solvent element the stress-strain curve is a function of electron density, entirely neglecting the size factor, which varied by a factor of two. This evidence led to a quantum mechanical calculation by Cottrell, Hunter, and Nabarro,12 based on the formation of a dipole around an edge disloca-

Jan 1, 1959

By D. A. Stevenson, T. Alden, J. Wulff

A portion of the liquidus curve has been determined for the binary alloy systems Ni-Pb and Cr-Pb. The solubility of nickel is 0.53 atomic pet at 372° and 18.63 atomic pet at 1200°C. Chromium shows low solubility, 0.634 atomic pet at 1210°C. Molybdenum and tungsten were also studied and found insoluble in lead, less than 0.005 atomic pet at 1200°C. INCREASED use of liquid metals of low melting X point for heat transfer, coating, joining, and other purposes has renewed interest in the solubility of structural metals in these liquids. A study of Hansen1 and current literature indicates that few liquidus curves at the low melting end of the binary diagrams have been accurately delineated. This statement applies particularly to the binaries of lead. The present paper is limited to nickel, chromium, tungsten, and molybdenum in lead. In early studies2, 3 of the lead end of the Pb-Ni system, a monotectic at 1340°C was established. Tammann and Oelsen&apos; determined the solid solubility of nickel in lead at 20°C to be 0.023 wt pet. Recently Pelzel5 determined the liquidus curve from the eutectic temperature of 327° up to 727°C using a segregation method. In the present paper this part of the curve has been checked and extended to 1244°C. The Pb-Cr system was first studied by Hindrichs.6 He pointed out the existence of a monotectic at 1470°C and indicated a tentative liquidus. Recent corrosion studies of Fe-Cr alloys in lead suggest that chromium is more soluble than iron in lead.7-8 The solubility of tungsten in lead according to Inouye8 is about 30 wt pet at 1200°C. Appreciable solubility of molybdenum in lead might therefore be expected. Experimental Various experimental techniques have been employed in the determination of solubility in liquid metals. For low solubility, thermal analysis is unsatisfactory. A segregation method was used by Pelzel3 in his study of the Pb-Ni system. In this procedure separation of liquid and solid is possible due to difference in density. In the technique of Kleppa10 a single piece of material is maintained in contact with the liquid metal in evacuated Vycor vials. After equilibration, solid and liquid are separated by tilting. Keck and Broder" measured the weight of a piece of the solid solute before and after immersion in a pure solvent bath; the weight loss was a measure of the solubility. All of the above procedures are time-consuming since they permit only one determination per run. Numerous samples for analysis may be taken from the melt in the method described by Gurinsky and CO-workers.10 The rate of extraction of samples is limited only by the time required for equilibration. In the present work, a modification of this method was employed. A 150-g charge of analytical reagent grade lead and the added metal* were contained in an Alun- dum crucible. It rested on firiely divided silica at the closed end of a 45 mm Vycor tube, 500 mm long. The top of the tube was provided with an inlet and

Jan 1, 1959

By E. Gregory, C. G. Goetzel

The outstanding elevated temperature properties of materials made from sintered aluminum powder have been well established in recent years.1,2 and considerable investigation has been carried out on the structures which appear to be responsible for this type of strengthening.2,3 The maximum operating temperature of such materials is severely limited, however, by the low melting point of the aluminum matrix; and, therefore, considerable interest was aroused in methods of introducing the

Jan 1, 1959

By J. C. Danko, R. D. Stout, A. H. Holtzman

The deformation characteristics of pearlite have been studied by light and electron microscopy.1,2 In the electron-microscopic work, deformation was found to take place by 1) ferrite slip which is parallel to the lamellae, 2) slip transverse to the lamellae with both cementite and ferrite deforming, and 3) ferrite-cementite interfacial slip. The transverse slip gives a step-like appearance to the lamellae in light microscopic work. It was thought that spheroidization of deformed pearlite would commence at the regions of maximum cementite deformation, the "stepped" areas. Although there is no possibility for seeing slip in the microstructure if the specimen is polished after deformation, the step-like appearance of the lamellae clearly indicates the transverse deformation. Thus, the areas of cementite deformation are apparent after polishing and the effect of deformed areas on spheroidization may be studied by the usual metallographic techniques. This note reports the result of a metallographic investigation which substantiates that spheroidization begins in the "stepped" areas. An AISI 1080 steel was normalized, re-austeni-tized at 1040°C, and isothermally transformed at 700 ± 4°C for 4 hr. Cubes, 5 mm to a side, were compressed between parallel plates to strains of 20, 40, and 50 pct. After deformation, specimens were heated to 600, 650, and 700°C; withdrawn at increasing time intervals and examined metallo-graphically for the percentage and distribution of spheroidite. The percentage of spheroidite was determined by lineal analysis. A micro structural region considered as spheroidized was one in which a lamellar skeleton was not distinguishable. Table I gives the times necessary for 95 pct spheroidization for each condition of strain and annealing temperature. Fig. 1 shows the microstructure of coarse pearlite compressed 20 pct, then polished and etched. Here the lamellae form a step by bending at two

Jan 1, 1959