By P. K. Koh

With identical annealing heal treatment the development of major annealed texture component seems to depend primarily upon the degree of cold reduction. Cube texture was evident on annealing- 1/2-, 1,/4- , and 1/8-mil tapes at 760°C, but it dissap-)eared on 927°C annealing of 1/8-mil tape cold reduced 96.9 pct. Some cube texturee remained as tile strongest 927 °C annealed texture component in 1/4- and 1/2-mil tapes cold reduced 93.8 and 87.5 pet, respectively. The switching coefficient increases and the squareness ratio of the hysteresis loop decreases proportionally with increasing cube pole concentration. PREVIOUS studies 1,2 on the 1/8-mil ultra-thin molybdenum permalloy tape established cold rolled and annealed textures and their magnetic performance for switch-core and coincident-current memory applications, The major cold-rolled texture was found to be of {110}<335> which is quite similar to the cold-rolled texture of silver and 70-30 cartridge brass. The major annealed texture components were found to be of {120)-- <001> and {113)<785>. Although the direction for easy magnetization for this type of alloy by the single-crystal technique is not avaliable, knowledge from related studies indicated [Ill] as the easy magnetization direction, similar to that of nickel.&apos; Therefore, a cube orientation, if present in the tape core, would be most detrimental to its magnetic performance.3 In its cold-rolled state the tape had < 111 > directions in the rolling plane 14.5 deg from the rolling direction.&apos; But the coercive force of the tape in such condition will be excessive due to large amounts of internal stresses, and therefore makes its use impossible for memory applications due to long switching time. In lower nickel alloys, suchas 50-50 nickel-iron and 65 pct Ni-Fe sheets, previous investigators4"7 found the presence of cube texture on annealing at 900° to 1000°C. Although no cube texture was found in annealed 1/8-mil tape,"&apos; its presence in some annealed 1,/4-mil tape cores was firmly established a year ago as verified by significant differences in magnetic properties. The present investigation is devoted to the orientation study and related magnetic measurements on three thicknesses of the ultra-thin tape, namely, 1/8 mil, 1/4 mil, and 1/2 mil, cold rolled directly from annealed 4-mil stock in the cold-rolled state as well as after they were annealed at 760°C (1400° F) and 927°C (1700°F). The results obtained might serve to elucidate the development of annealed texture as well as to establish clearly the importance of preferred orientation on the magnetic performance of such memory tape core despite its well-known low magnetic anisotropy exchange energy. EXPERIMENTAL PROCEDURE Samples were taken from one production heat (0.010 wt pct C, 0.004 P. 0.016 S, 0.80 Mn. 0.29 Si. 79.69 Ni. 4.42 Mo. 0.054 Co, 0.002 Ti, 0.12 Al, 0.04 Mg, 14.56 Fe). Annealed 4-mil sheets were cold re-

Jan 1, 1962

By P. A. Beck, M. V. Nevitt

All binary and a number of ternary u alloys formed by first long period transition elements were examined and found to be ferromagnetic at low temperatures. The Curie temperatures for these alloys were measured. It was found that the correlation of the Curie temperature with composition may be described qualitatively in terms of the contributions of the various component atomic moments to the saturation moment of the alloy. Ternary Fe-Cr-Mo u phase alloys were also found to be ferromagnetic, with a Curie temperature dependent on the iron content and largely independent of the unit cell dimensions. Similar relations were found for the Co-Fe-Cr and the Co-Cr-Mo a alloys, where the Co + Fe content appears to determine the Curie temperature. RECENTLY, it has become increasingly evident that the u phase is some kind of an "electron compound." Several papers1-&apos; discussed the empirical correlation between the composition of the various u phases in alloys of the transition elements and the distribution of electrons in the partially filled d-levels of the component atoms. However, a picture of the latter can be formed only in a more or less intuitive manner, as in the Pauling theory," and the rigorous treatment of these problems is at present prevented by lack of adequate knowledge of the electronic structure of the transition elements in the metallic state. It appeared reasonable to expect that investigation of the magnetic properties, which are related to d-shell electrons, may help in clarifying the physical nature of the foregoing empirical correlation. Qualitative tests of samples of various compositions have shown that certain u alloys become ferromagnetic at liquid nitrogen temperature." The present investigation was undertaken to determine whether or not low temperature ferromagnetism is characteristic of a large variety of u alloys and to establish how the Curie temperatures of ferromagnetic u alloys are influenced by changes in composition and in lattice parameter. In the first portion of the in- vestigation, Curie temperatures were measured for a series of u alloys containing either vanadium or chromium with one or two of the elements manganese, iron, cobalt, or nickel. In the second phase of the work, data were obtained on the Curie temperature of ternary (Fe, Co, Cr)a, (Fe, Cr, Mo)a, and (Co, Cr, MO)U alloys, as a function of composition and of interatomic spacing. Experimental Procedures High frequency vacuum melting in high purity re-crystallized alumina crucibles was employed in the preparation of the u alloys, using metals whose lot analyses are given in Table I. Approximately two-thirds of the alloys were analyzed chemically, the analytical results being in acceptable agreement with the intended compositions, as seen in Tables I1 and 111. The specimens were annealed for homogen-ization in an atmosphere of purified 92 pct He and 8 pct H, mixture or in evacuated and sealed Vycor tubes at temperatures from 780" to 1300°C, depending on the temperature range of the u phase field for the particular composition. The annealing temwerature and time for kach alloy are given in Tables 11 and 111. Curie points were determined by an induction method; the change with temperature of mutual inductance between two coils was observed when the i-u specimen was inserted into the flux path between the coils. The transformer consisted of three coils each containing 1200 turns of 0.0050 in. diam enameled copper wire. The center coil, P in Fig. 1, served as the primary coil, and was linked magnetically with each of the two secondary coils, S, and S? which were connected in series opposition. The primary coil, P, was energized by an audio-oscillator, set at a frequency of 500 cycles per sec, while the signal from the transformer secondary circuit,

Jan 1, 1956

By F. R. Brotzen, A. R. Troiano, E. L. Harmon

Precipitation processes leading to drastic property changes are a frequent occurrence in titanium alloys containing large amounts of the retained high temperature P phase. In order to establish the kinetics and nature of these precipitation processes, a series of Ti-V alloys was studied. Time-temperature-transformation diqgrams were obtained for 12.5 and 15 pct V-Ti alloys. These diagrams consisted of two intersecting C-shaped curves: one in the high temperature region for the euilibrium transformation P +u+P, and another at lower temperatures depicting the formation of the meta-stable transition phase, o. Presence of the transition phase retarded the precipitation of the equilibrium a phase. Deformation of retained P resulted in the formation of the o phase. Reversion and retrogression phenomena of the transition phase were observed. A negative temperature coefficient of resistance was found in quenched alloys containing from 15 to 20 pct V. CERTAIN titanium-base alloys can be heat treated to produce appreciable changes in properties. For example, remarkably high hardness values may be obtained by aging or isothermal quenching treatments. Most of the information available to date on the hardening of titanium-base alloys has been systematized recently in an article by L. D. Jaffe.&apos; It was pointed out by that author that the hardening was the result of the decomposition of the retained j3 phase to the equilibrium constituents, a and p, and that this decomposition had many of the characteristics of an age-hardening reaction. Recent work by Frost et al.&apos; 3 has contributed much to the fundamental understanding of the hardening mechanism in titanium-base systems. These authors established the presence of a transition phase in the transformation from j3 to a + j3, which they designated o. The transition phase, in their opinion, was at least partially responsible for the hardening and embrittling effects which accompanied low temperature aging. The present investigation of the mechanism and kinetics of the hardening reaction was carried out for the Ti-V system. Ti-V alloys were ideally suited for a study of the decomposition of j3, since age hardening was known to occur readily in this system." Moreover, no intermetallic compounds occur in this system, Fig. 1, thus simplifying the interpretation of the results. Material and Procedure Alloys containing 12.5 and 15 pct V were prepared by Battelle Memorial Institute from iodide titanium furnished by Watertown Arsenal and vanadium of 99.8 pct purity. Ingots of 8 Ib each were prepared by arc melting in an inert atmosphere with a tungsten electrode and water-cooled copper crucible. Each of the ingots was melted once, forged at 1600°, and rolled at 1400°F. Following this, the ingots were remelted, forged, and then rolled to % in. sq bars, which were subsequently grit blasted, pickled, and wire brushed. Another set of alloys containing nominally 17.5 and 20 pct V was produced by the Research Div., New York University. These alloys were arc melted in an inert atmosphere in lots of 20 g each. Heat-Treating Procedure: Whenever feasible, specimens were heat treated in high vacuum resistance furnaces at pressures below 5x10." mm of Hg. Aging and isothermal quenching treatments were generally carried out in salt baths. Specimens were not attacked by the salt, provided the tempera-

Jan 1, 1956

By N. S. Stoloff, M. Gensamer

The effects of temperature, grain size, and magnesium content on the strength and ductility of cadmium were studied in the range -269° to 23 °C. A sharp drop in ductility between -140° and -190°C marked a transition in fracture mode from ductile shear to inter gvanular fracture. The addition of up to 15.35 wt pct Mg in solid solution raised the transition temperature, and for two compositions produced basal cleavages. The relatively high ductility of unalloyed cadmium at cryogenic temperatures is attributed to temperature independence of the yield stress and the absence of dislocation locking. ALTHOUGH numerous studies have been made of the mechanical properties of cadmium single crystals,1-5 no comprehensive investigation of deformation and fracture in polycrystalline cadmium has been carried out. This investigation was initiated to determine the mechanisms of deformation and fracture in polycrystalline cadmium, and to attempt to correlate these mechanisms with the behavior of other metals of hexagonal close-packed structure. A second objective of this work was to determine whether the slip systems and mode of fracture of polycrystalline cadmium could be altered by reduction of the axial ratio, which is 1.886, through alloying. Dorn and co-workers&apos; have been able to induce prismatic slip in magnesium through alloying to reduce the axial ratio. Single crystals of cadmium are so highly ductile that glide strains of 400 pct are observed at room temperature, and 80 pct at -269°c.l Failure in every reported case is by necking down and shearing off of the crystal. Cleavage in cadmium single crystals has never been observed. Magnusson and aldwin reported a ductile to brittle transition for polycrystalline cadmium at about —160 C for specimens tested at a strain rate of 0.05 in. per in. per min in tension. However, even at -196° substantial ductility was retained. The transition temperature was strain rate dependent, impact loading at 19,000 in. per in. per min raising the transition temperature to about -85°C while leaving the low temperature ductility unchanged. No information was given on microstructures or fracture mode, nor were stress-strain characteristics reported. In the present investigation, tensile tests were carried out on polycrystalline cadmium and solid solution Cd-Mg alloys to determine flow stresses, work-hardening behavior, fracture strength, and fracture ductility. Variables employed included temperature, alloy content (and c/a ratio), and grain size.Some compression data also have been obtained for comparison purposes. I) EXPERIMENTAL PROCEDURES A) Polycrystalline Cadmium. Two purities of cadmium were employed in this investigation. Cadmium of 99.95 pct purity was supplied by Belmont Smelting and Refining Co. Cadmium of 99.99+ pct purity was supplied by American Smelting and Refining Co. Threaded cylindrical tensile specimens were machined to give approximately a 1/2 in. long straight gage section with a reduced diameter of about 0.110 in. Specimens were heat treated in evacuated pyrex capsules in the range 140" to 290°C to produce desired grain sizes. All specimens were polished in a solution containing 320 g Cr03 and 20 g NaS04 in 1000 cc of H20. Occasionally this solution caused staining of the specimen, in which case a further polish with a solution of one part HN03 and two parts H202 in two parts ethyl alcohol was employed.&apos; Tensile testing was carried out on a screw-driven Instron machine, at a constant rate of crosshead movement, which for most tests was 0.01 in. per in. per min. Load vs time, and therefore load vs total strain, were recorded. Temperatures from -196" to -40°C were obtained by passing nitrogen gas through a copper coil immersed in liquid nitrogen, and then feeding the gas into a jacket around the specimen. Tests at -269°C were carried out in a helium cryostat, at a crosshead rate of 0.1 in. per in. per min, with specimens of 1 in. gage length. Compression specimens were tested in a jig similar to one designed by ilman. The jig was mounted on the under side of the Instron crosshead. Load was transmitted by means of a rod connected to a movable part of the jig at one end, and the load cell at the other end. A downward movement of the crosshead applied a compressive load to the specimen.

Jan 1, 1963

By H. W. Schadler

Single crystals of tungsten, which were grown by electron bombardment floating zone refining, were strained 2 pet in tension and bending at 298°, 77°, and 20°K to determine the modes and crystallography of the plastic deformation of these temperatures. At 77° and 20°K plastic deformation occurs by slip on systems of the type (011) [111] and by twinning on (112)-type planes. For crystals strained at 298°K, deformation occurs by slip in [111] directions on either (Oil)- or (112)-type planes. CURRENT models for the initiation of brittle fracture in crystalline materials are based on a knowledge of the details of their plastic deformation.1 Body-centered cubic tungsten exhibits brittle failure at temperatures below about 500 °K yet the modes and crystallography of its plastic deformation have not been studied below 1000°K. In 1924, Goucher2 reported that tungsten single crystals with a total impurity content of less than 0.01 wt pet deformed by slip on the (112) [111] system in the temperature range 1000° to 3000°K. He also observed (001) [010] slip in one crystal which was constrained by the presence of a large fissure. According to Barrett3 tungsten also deforms by twinning on the (112) plane in the [111] direction, but he gives no details on the tendency for twin formation or the temperature range in which twinning occurs. Therefore, as a necessary part of a study of the factors influencing the brittle fracture of tungsten, the modes and crystallography of the plastic deformation were determined at 298°, 77°, and 20°K. Tungsten single crystals, grown using the electron-bombardment zone-refining technique first described by Calverly,4 were deformed to between 1 and 2 pet plastic strain in tension and bending. The surface offset resulting from slip or twinning was observed with an optical microscope to determine the crystallography of the deformation. The existence of twins was proven by the standard polishing and etching technique; and the crystallography of dislocation motion was followed using the dislocation etchant described by Wolff.5 Some observations on the fracture characteristics of tungsten single crystals are included. EXPERIMENTAL TECHNIQUES Growth, Purity, and Perfection of the Crystals-Several years ago Calverly, Davis, and Lever4 dem-onstrated the feasibility of growing tungsten single crystals by the electron-bombardment floating zone-refining technique, and Carlson6 showed that crystals produced in this way had a high degree of purity and were ductile at room temperature. Tungsten single crystals produced by this technique in equipment similar to that described by Carlson were used in this study. The starting material, a powder metallurgy product, was obtained in the form of a swaged 1/8-in. rod from the General Electric Wire Plant in Cleveland, Ohio. The crystals were grown from this material in a vacuum of 10"4 mm of Hg by passing a molten zone 1/8 in. long down the rod twice at a speed of 3 mm per min. At this zone speed

Jan 1, 1961

By S. Floreen

Measurements have been mode of the effects of tempering and austenitizing heat treatments, the work-hardening characteristics, and the effects of test temperature and strain rate on the properties of a low-carbon Fe-18 pet Ni martensitic alloy. In many respects the alloy behaved quite similarly to cold-worked iron. One notable quality was the excellent ductility at temperatures as low as 20°K. Many of the qualities of the maraging steels could he related to the properties of the Fe-Ni matrix. THE 18 pet Ni maraging steels have demonstrated that unusual combinations of strength and toughness may be obtained by age hardening a low-carbon Fe-Ni martensite matrix.&apos; These properties must, to some extent, reflect the properties of this Fe-Ni matrix, and therefore an understanding of the properties of this matrix is a prerequisite to a complete understanding of the steels. There have been several recent studies of Fe-Ni-C martensites, but not much attention has been paid to alloys with very low carbon contents. At low carbon levels the crystal structure of these alloys is essentially bee.2 Electron transmission microscopic examination of a 20 pet Ni binary alloy showed martensite platelets separated by low angle boundaries.3 Plastic deformation of the low-carbon alloys has been shown to proceed by wavy glide.4 The hardness of these martensites is typically RC 28, and their yield strengths are 70 to 80 kg per sq mm.2, 5 Their ductility is excellent. Room-temperature tensile elongations of 18 pet and reductions of area of 70 pet have been observed in an Fe-18 pet Ni binary alloy.5 These observations have provided a qualitative understanding of the flow characteristics of these alloys. To date, however, no thorough study of their properties has been made. In particular, it is not known to what extent the deformation characteristics of low-carbon martensites are similar or dissimilar to those of pure iron or other bee metals. The present work was undertaken to provide more detailed information on the flow characteristics of a low-carbon Fe-18 pet Ni martensite. PROCEDURES, RESULTS, AND DISCUSSION Materials. A 40-lb heat of the Fe-18 pet Ni alloy used in this study was made by vacuum-induction melting. The charge materials were electrolytic iron and electrolytic nickel. A carbon boil was used to achieve deoxidation. After the boil the heat was refined by additions of 0.1 wt pet Ti and Al. These additions are commonly used in the maraging steels to keep the carbon and nitrogen contents in solid solution at a minimum. After casting, the heat was

Jan 1, 1964

By S. Feuerstein, J. M. Galligan

SURFACE effects in the deformation of metal single crystals have been noted by a variety of workers.&apos; A large majority of these experiments have used surface roughening or a second chemical constituent at the surface. We performed the following experiment to see how the presence of a fine polycrystalline layer influenced the stress-strain behavior of single crystals of zinc. Spherical single crystals oriented for single slip were acid-machined into cylindrical dumbbell-shape shear specimens having a gage length of 3.2 mm and a cross section of 20 sq mm. The crystals were then deformed varying amounts at the surface of the gage section with emery paper. Following this treatment, the crystals were heated for approximately 8 hr at 200°C. This resulted in a polycrystalline surface layer, with an observed grain size of approximately 1/10 mm in diameter. Deformation of these crystals was undertaken at 78°K in pure shear, the shear direction <1120> lying in the basal plane. The deformation apparatus has been described elsewhere.2 The presence of a polycrystalline layer markedly raises the first observed plastic deformation, as can be seen from Fig. 1. This yield stress is then followed by a region of low work hardening comparable to that observed in shear tests on similar untreated zinc single crystals. However, the extent of easy glide is quite seriously curtailed, and is followed by a more rapid increase in work hardening, reminiscent of Stage II observed in the deformation of fcc crystals. The higher yield can probably be attributed to the difficulty of penetrating the grain boundaries by dis locations from sources interior to the boundaries. If we associate this yield stress with this breakthrough, then we might expect that more dislocations would be trapped in the crystal than is normally the case. If there is an increased density of trapped dislocations, this could lead to an increase in the amount of trapping with increasing strain, giving a larger strain hardening in the crystal. Although other explanations can be given, it is quite tempting to characterize the region of increased work hardening as a manifestation of Stage II-type deformation. This seems reasonable if the polycrystalline layer is quite efficient in holding up a large number of dislocations. In zinc crystals, since it is well-known that the slip distance can be as large as the specimen dimensions, one would only expect to entrap a large number of dislocation with very large crystals or by applying surface layers. If this interpretation of increased strain hardening is correct, it might present a method of studying Stage II in single crystals of zinc. This research was supported, in part, by the Office of Naval Research (1959). The encouragement and stimulation given by Professor E. R. Parker is gratefully acknowledged.

Jan 1, 1965

By A. T. Churchman

The deformation modes of rhenium have been identified as those typical of the hexagonal metals, titanium, zirconium, and beryllium whose c/a ratios, in common with rhenium, are less than ideal for close packing. Slip is observed on (1010), (1011), and (0001) planes and twinning on (1121), (1122), and (1012) planes. The very high rate of work hardening is believed to be associated with intersecting partial dislocations on two (1010) systems which can combine to form sessile barriers. If the stacking fault energy is low, as postulated by Seeger, these barriers should be strong and not easily bypassed by cross slipping. Such an explanation could also account for the very small temperature dependence of the yield stress which was observed. RHENIUM is interesting scientifically as a member of the group of high melting point hexagonal metals: titanium, beryllium, and zirconium with a c/a ratio less than that for ideal close packing. Unlike them, however, it work hardens at a very high rate. This rate is greater and continues to a much higher degree of deformation than for nickel, normally considered to have a high rate of work hardening. This paper presents experimental observations on the modes of deformation of rhenium and, by comparison with other hexagonal metals, some speculation on the cause of the high work hardening. MATERIALS Johnson, Matthey rhenium powder of both 99.9 pct and 99.5 pct purity, see Table I, was compacted at 10 tons per sq in., part sintered at 1350°C in vacuo, and finally arc melted in a "gettered" argon atmosphere arc furnace to produce small buttons. Little difference was observed in the as-cast hardness or working down behavior of the two purities suggesting that either silicon and potassium do not have a significant effect on the working properties of rhenium or they were lost during arc melting. SPECIMEN PREPARATION The cast structure was broken up by cold-rolling with inter-stage annealing at 1600o or 1800°C in a vacuum high-frequency furnace using a tungsten susceptor. Strip for tensile testing was taken from two thicknesses of material 0.011 and 0.064 in. The former with intermediate anneals at 1800°C had a grain size of 900 grains per sq mm, while the latter with inter-stage annealing at 1600°C had a grain size of 3600 grains per sq mm. A coarse grain size was obtained by secondary recrystallization in a half button cold-worked by 30 pct reduction. Annealing times of from half an hour to several hours at 2200° to 2600°C in a "gettered" argon atmosphere arc furnace1 resulted in grains of up to 2 mm diam.

Jan 1, 1961

By S. R. Dunbas, D. C. Jillson, E. A. Anderson

THE present work was undertaken to furnish information, lacking in the literature, on the deformation mechanisms active in pure titanium at room temperature. Since it was started, Rosi, Dube, and Alexander&apos; have indicated that slip can occur in coarse-grained (2 to 6 mm diameter) titanium on the {1010} and {1011} planes and twinning can take place on the {1072}, (1122) and (1151) planes. Liu and Steinberg,&apos; working with titanium flakes produced by fused salt electrolysis, found evidence of twinning on the {1032$, {1121), {1122}, (1123}, and (1154) planes. The crystals used in the present work were substantially longer (up to nearly 2 in. in length) and possibly purer. Production of Large Crystals It was the purpose of this part of the work to provide single crystal or large grain specimens for use in the deformation studies rather than to study the mechanism of crystal growth. Accordingly, all further exploratory studies on methods were abandoned when it was found that cold-rolled bars sealed in vacuo in individual Vycor tubes and given three or more cycles of 4 hr at 1200°C and three to five days at 850°C, gave large grains. Eighteen specimens about 0.2 in. square x 2 in. long yielded 33 useful grains, ranging from Va in. to nearly 2 in. in length, with an agreeably wide range of orientations, Fig. l. The 0.25 in. thick strip from which the starting specimens were cut had been reduced 67 pct on 18 in. diameter rolls from a scalped, hot-forged (959" to 1000°C), arc-melted, iodide titanium ingot. Thc bar was at room temperature, but the rolls were at 200°C. Reductions of about 0.03 in. per pass were used. The bar was cut into four segments, each of which was rolled in a somewhat different manner. No effect on the growth of large grains was noted. The composition of the titanium, determined on turnings from the ingot scalping operations, is given in Table I. The Rockwell A hardness of the ingot was 26. The standard starting specimens, about 1/4x1/4x2 in., were milled on all four sides, hand polished on 280 and 400 mesh emery papers, etched for 3 min in a 50 HF-50 glycerine solution, rinsed, and dried in alcohol and ether just before sealing them in Vycor tubes. The average specimen weight was 7.5 g, and the tube volume was 6.5 cc. A vacuum of less than 1 micron pressure was applied. The specimen tubes were placed in an evacuated Inconel muffle to minimize the danger of collapse of the glass tubes at temperature. In practice the specimens were first heated to 1200 °C for 4 hr and then transferred fairly quickly to an 850°C furnace where they were held for three to five days. This cycle was repeated at least three times before the specimens were cooled, removed from the tubes, lightly polished and etched on one surface for examinstion. Those in which large grains had not developed were resealed in Vycor and returned to the cycling. Satisfactory specimens (about one out of every four cycled) were polished with emery paper on all four side;, then metallographically polished using ctchinz between wheels to remove distorted metal and, finally, given a very light etch to reveal the grain boundaries. This was necessary because the surface was roughened by the sublimation of titanium under high temperature vacuum conditions. Specimens were identified by TiXl numbers using supplementary letters to designate specific grains.

Jan 1, 1954

By K. E. J. Rapperport, C. S. Hartley

The only slip system observed in zirconium crystals deformed at 77", 575", and 1075OK was (1010) [1210] with a critical resolved shear stress in tension of 1.0 kg per sq mm at 77°K; 0.2 kg per sq mm at 575 °K; and 0.02 kg per sq mm at 1075 OK. The active twin planes were {1012}, (1121}, (11221, and (11233) with varying temperature dependence. A detailed analysis for the slip direction using Laue spot asterism is appended. NeARLY all metals of the hexagonal close-packed structure exhibit basal slip, i. e.,(0002)<1120>- type slip. This is true of magnesium,&apos; zinc,&apos; cadmium,3 beryllium,4 titanium,= yttrium,6 and rhenium.Many of these such as titanium 5&apos;8-&apos;0beryllium,4&apos;" magnesium, and zinc13&apos;14 display other slip modes even at room temperature, and nearly all have been reported to slip on other systems under particular loading or temperature conditions of testing. As is shown in this paper, basal slip was not found at any of four test temperatures from 77" to 1075°K in hexagonal close-packed zirconium under the simple loading conditions of tension and compression, even though in one case the resolved shear stress on the inactive (0002) <llgO> system was twenty-five times higher than the critical resolved shear stress on the active (1010) [1210] system. This result is consistent with prior studies on the active deformation processes in zirconium deformed at room temperature. &apos;&apos;-I7 SPECIMEN PREPARATION A) Material—The zirconium used in this work was of two types: 1) as-deposited reactor grade crystal-bar, and 2) arc-melted and forged reactor grade crystal-bar. Typical chemical and spectrographic analyses of these materials as received, and after hydrogen removal and crystal growth are given in Ref. 17. Crystals of type 1) above have the letter prefix (A) and those of type 2) have the prefix (B) throughout this paper. B) Crystal Growth— he zirconium was machined into rectangular parallelepipeds about 0.2-in. scl in cross section and 2 in. iong. These were hand polished through 4/0 abrasive paper, electropolished, given a hydrogen removal anneal, and subjected to long-time anneals at 840 °C in vacuo to produce usable crystals.&apos;7 A second technique used to obtain large crystals was to cycle the samples two or three times between 1200" and 840°C, allowing them to remain at the higher temperature for about 4 hr and at the lower temperature for 5 days.17 These techniques yielded some grains which occupied the entire cross section of the bar and were as long as 3/4 in. C) Orientation Determination—After the growth of large crystals by thermal cycling, the samples were repolished with extreme care through 4/0 abrasive paper and electropolished. Metallographic examination after polishing showed the surfaces to be free of visible deformation traces. Standard Laue back-reflection X-ray techniques were used to find the crystallographic orientations of selected large grains with respect to a specimen face and edge. Fig. 1 shows the stereographic projections of the stress axes for the crystals used. The sharpness of the spots on the Laue photographs indicated that the crystals were of good quality. EXPERIMENTAL METHODS Nine crystals were deformed in tension at 77"K, nine in tension and five in compression at 300°K in previous tests,17 fifteen in tension at 575"K, and eleven in tension at 1075°K. All specimens were stressed by load increments. After a predetermined load was applied, the specimen was removed from the loading appratus and metallographically examined for deformation traces. An attempt was made to initially stress each bar so that some crystals slipped a small amount and others not at all. This was done to bracket the critical resolved shear stress. One bar of special orientation (B-11) was repolished and annealed at 1075°K for 1 hr after lower temperature deformation, before final deformation at 1075°K. In the other bars the loading by increments, followed by metallographic examination, was continued until the surface distortion would interfere with analysis, or until fracture. One example of a crystal pulled to fracture is shown in Fig. 2. This photograph shows a crystal (B-14C) which was pulled at 1075°K and failed by slip on two (10i0) planes. The approximate orientation of this crystal is illustrated in the figure. Specimens were deformed at 77°K in liquid nitrogen on a tensile machine using an insulated bucket with an internal hook to accept a clamped specimen.

Jan 1, 1961

By R. M. Rose, D. P. Ferriss, J. Wulff

Single crystals of tantalum were grown by multipass zone melting in an electron beam apparatus. Tension tests of these crystals at 4.2 x 10&apos;* per sec-gave a resolved louler yield stress of 7300 psi at with a chisel edge; total uniform deformation increased from 1 to 2 pct at 77°K to over 20 pct at 300°K. This, and slip traces, indicated that deformation is more inhomogeneous at lower temperatures. Deformation occurred exclusively by slip in <III> directions, on planes in the <111> zones. Cross slip was frequent, particularly for those orientations where the resolved shear stress on the cross system was comparable with that on the primary plane. The existence and magnitude of the upper yield point were found to be sensitive to orientation. This effect was related to the circumvention of dislocations which were "locked" by interstitial atoms, by double cross slip, or composite slip, of screw dislocations. Prestrainirg at 300°K did not remove the upper yield point in subsequent tension at 77°K. Also, this treatment was found to cause yield points, where none existed for the unprestrained material. This behavior was also rationalized in terms of the circumvention mechanism. The mechanical properties of polycrystalline tantalum have been investigated by several workers,1"4 and may be summarized by pointing out the following features: a) Sharp rise of yield stress with decreasing temperature below room temperature. b) Response to strain aging at 300" to 400"C. c) Yielding with upper and lower yield-point phenomenon at and below room temperature. d) Low strain hardening below room temperature. e) Reluctance to twin except at very high strain rate. Furthermore, tantalum is ductile at ordinary strain rates as low as 4.2"K.&apos; This feature, in particular, makes tantalum unique among the high melting point, bee transition metals of Groups V and VI in the periodic system. Therefore, a more fundamental and detailed knowledge of the low-tempera- ture deformation of tantalum is required. Since high purity and the absence of grain boundary effects make such a study most productive and unambiguous, the method of electron beam zone melting was selected for the preparation of test specimens. This technique has the further advantage that crystals may be seeded in order to obtain any desired orientation. EXPERIMENTAL The electron beam zone-melting equipment was constructed as a modification of that described by Calverley, Davis, and Lever? All crystals were made by three passes of the molten zone at 4 mm per min to achieve an optimum purity commensurate with economy of time and material. Table I reports the chemical analyses of the starting and refined metal. It will be noted that there remain some 50 to 70 wt ppm of interstitial elements, while all substi-tutional elements have been removed by evaporation. Tungsten is picked up by evaporation of the cathode filament wire. Crystal seeding was normally successful within 3 deg, and the orientation of all crystals are given in the standard stereographic triangle in Fig. 1. Tensile bars were prepared from the crystals by centerless grinding to the shape in Fig. 2. Specimens were then electropolished to remove 10 pct of the diameter in order to remove worked material and to prepare a metallographic surface for subsequent deformation trace observations. All specimens were held in the split bushing grips as indicated in the cross section view of Fig. 2. All tests were made at a strain rate of 2 112 pct per min in an Instron testing machine.

Jan 1, 1962

By J. E. Burke, A. M. Turkalo

IN 1923 Desch¹ pointed out that the grains in a metal which is anisotropic with respect to its thermal coefficient of expansion would contract differently upon cooling, and that the stresses developed might approximate the plastic strength of the metal. More recently Boas and Honeycombe2-5 studied the behavior of several metals upon thermal cycling and observed that the stresses developed in arlisotropic metals are great enough to produce slip lines in individual grains and a roughening of the specimen surface. This phenomenon they have named "thermal fatigue." The mechanism they propose involves essentially a kneading of the grains, the deformation being alternately in compression and tension in a given grain as the temperature is changed in one direction and then the other. The present work was undertaken to investigate the possibility that an additional mechanism might operate to produce plastic deformation during thermal cycling—a "thermal ratchet" that depends upon a combination of grain boundary flow to relax the stress that develops between differently oriented grains upon raising the temperature and transcrys-talline slip to relax the oppositely directed stress which develops on lowering the temperature. Thus, thermal cycling should produce a nonreversible distortion such that certain grains will change shape differently from their neighbors with a simultaneous displacement being produced at the grain boundary. Temperature Dependence of Grain Boundary and Grain Strength The critical resolved stress for the initiation of slip in metal grains is only mildly affected by temperature." For example, in cadmium it decreases from 0.15 to about 0.05 kg per sq mm when the temperature is increased from 20° to 458°K and further temperature increase causes little further decrease. On the other hand, the work of KG1 indicates that the grain boundaries behave in a viscous fashion that can be described8 by the expression: t = BVexp(Q/RT) [1] t is the shearing stress on the boundary; B, a constant; V, the flow rate at the boundary; Q, the activation energy for grain boundary flow; R, the gas law&apos;s constant; and T, the absolute temperature. Eq 1 indicates that the stress necessary to cause a given grain boundary flow rate, V, decreases rapidly with increasing temperature. The value of the constant B is such that at sufficiently low temperature and ordinary strain rates deformation will occur preferentially by slip rather than by grain boundary flow. There is considerable evidence to indicate Consider the bicrystal shown in Fig. 1. In grain 1 the slip plane lies 45 " to the boundary while in grain 2 the slip plane is 90" to the boundary. The coefficients of expansion of the grains in a direction parallel to the length of the crystal are a1 and a, with a, > a2 for the orientations shown. The sequence of events that can occur upon heating and cooling this specimen is illustrated schematically in Fig. 2. Initially there is assumed to be no stress in the specimen (A). Upon heating, grain 1 attempts to become longer than grain 2, but is constrained by grain 2. Thus grain 1 is loaded in compression and grain 2 is loaded in tension, and a shearing stress is present across the boundary (B). As the temperature is increased, the stress will build up, and finally grain 1 will be plastically deformed by slip, since the greater stress is resolved on its slip planes. Any further heating will result in more slip and the stress will remain constant until some temperature T* is reached where the stress can be relaxed by grain boundary flow.† At this relaxation temperature (C) a step will appear between grain 1 and grain 2. Further heating above T* will cause grain 1 to become relatively longer, but no stress will appear because the grain boundary is too weak to support the stress (D). Upon cooling again, at T* (E), the grain boundary will again be able to support a shearing stress, and upon cooling further, grain 1 will be loaded in tension and grain 2 in compression (F). When the decrease in temperature below T* is sufficient to impose the critical shear stress upon the slip plane of grain 1, it will be stretched by slip.

Jan 1, 1953

By W. N. Roberts

Hadfielcl steel has been studied by transmission electron microscopy to determine the microsl.rtic-ture of the cold-worked material, which has been a subject of controversy for many years. The presence of fcc deformation twins in specimens deformed in tension, by hamnzering, and by explosive -shock loading at room temperature lzas been established by electron diffraction. No evidence of a mar tensite was detected in any of the speciwens. Small amounts of E martensite were idenLified in the hamnleved specimens. DESPITE numerous researches on Hadfield steel since its discovery in 1882, there is still disagreement on the nature of transformations in the cold-worked material. Collette el al.,&apos; using X-ray and electron diffraction, have found evidence for stacking faults, E martensite, and a martensite in Hadfield steel deformed in tension at room temperature. Nishiyama and Simizu,&apos; using electron microscopy, have found stacking faults and E martensite in hammered Hadfield steel. White and Honeycombe have concluded from X-ray diffraction that Hadfield steel remains fully austenitic even after severe cold work at -196 Previous work by the author, indicating the presence of a, martensite in deformed Hadfield steel, was in error due to a faulty interpretation of the electron-diffraction patterns. Various workers,5&apos;7 over the years, have speculated on the presence of deformation twins in Hadfield steel, largely from such circumstantial evidence as the persistence of slip bands with repeated polishing and etching, the presence of serrations in the stress-strain curve, and the absence of evidence of a martensite by X-ray measurements. The advent of electron-transmission microscopy and se- lected-area diffraction has made possible the positive identification of fine deformation twinning. PROCEDURE For tensile tests, standard ASTM specimens of 2-in. gage length, ground from 0.12-in. Hadfield steel sheet, were solution-treated at 1050°C for 30 min in a salt bath, to avoid decarburization, and water-quenched. The grain size was about 0.01 sq mm. Chemical analysis of the steel after heat

Jan 1, 1964

By I. R. Kramer

The delay time for single crystals of iron, zinc, and pre-strained aluminum was measured under conditions of high-speed deformation. The delay time of aluminum was found to be affected by the orientation of the crystal. Under the dynamic conditions employed, tile calculated "activated volume" term appears to be very small for the three metals studied. IN a previous paper,1 it was shown that under dynamic testing conditions at 78° K, there was a delayed yield in single crystals of aluminum and copper which had been cold-worked prior to testing. The experimental results also indicated that the delay-time effect was not due to the interaction of dislocations with impurity atoms or vacancies, but rather to a dislocation-dislocation interaction since aluminum which has not been prestrained shows no delay-time phenomenon. In this paper, some data are reported on the effects of orientation on the delay time of aluminum single crystals; the delay time of zinc single crystals saturated with nitrogen and the delay time of iron single crystals also were measured. EXPERIMENTAL PROCEDURE Aluminum (99.997 pct) and zinc (99.999 pct) crystals, 1/2 in. in diam and 8 in. long were grown by the Bridgman technique. The iron single crystal was supplied by Dr. R. Maddin. The zinc crystals containing nitrogen were prepared by melting high-purity zinc in a graphite crucible and the nitrogen was introduced by additions of ammonium chloride. The liquid zinc was then drawn up into glass tubes of 1/2 in. diam and allowed to solidify. The rods were cooled to room temperature before the transfer to the mold for conversion into single crystals. The orientation of all specimens was determined by the Laue&apos; back-reflection technique, Fig. 2 and Table I. To prepare for the delay-time measurements, the crystals were cut with a fine jewelers saw and the ends carefully machined. The specimens then were electrolytic ally polished to remove the cold-worked metal, mounted in a special fixture and hand-lapped. As a final step, the crystals were annealed in evacuated tubes. Specimens of aluminum crystals, Nos. 24 and 26, were compressed 0.5 and 2 pct, respectively, in the direction of the later impact. The zinc specimens were aged at 50°C for 15 min, In the case of iron, only two specimens could be obtained. To obtain sufficient data, it was necessary to resort to a reaging treatment. After each delay-time test, the specimens were aged at 65° C for 100 min. This treatment, according to Clark,2 is sufficient to restore the original delay time. It is believed that although the specimens were plastically deformed approximately 10-4 pct, after each test the delay-time values are reliable. The delay-time measurements were made in an apparatus similar to that described previously.&apos; Single crystals approximately 1 in. long and having a diameter of 1/2 in. were placed in a pendulum which consisted of a bar 1/2 in. in diam and 8 ft long, designed with a crystal holder to accommodate the specimen at low temperatures. The crystal was held at a position 2 ft from the front part of the pendulum. This portion of the apparatus was supported on a fine molybdenum wire. A projectile bar of the same diameter and length comprised the other portion of the apparatus. This bar was supported on

Jan 1, 1962

By Roman Šejnoha, Karel Mazanec

A pronounced tendency for delayed fracture zoas observed in the martensite structure of low-alloy steels in the as-quenched condition. Cracks of predominantly intercrystalline nature nucleated and propagated at stresses substantially lower than the short-titne tensile strength of- the steels, and were observed even in hydrogen-free speciunens. The occurrence of delayed fractures in the as-quenched condition is interpreted as a supevposition of the effect of free dislocations generated during the martensite transforlnation, and of a weakening of the prior austenite grain boundaries caused by dynamic shocks exerted on the boundaries by growing martensite plates. AN important metallurgical problem, connected with the production and use of high-strength steels, is delayed fracture in martensitic structures. Such fractures occur in quenched steels as a result of prolonged loading with external stresses far lower than the short-time tensile strength of the steel. The same effect can be produced by sufficiently high internal stresses: it is well-known that quenched structures will in some cases crack intergranularly at room temperature if not tempered quickly enough even in the absence of any externally applied stress. In Troiano&apos;s papers1,2 on delayed fractures in high-strength steels, the fundamental role of hydrogen migrating under the influence of multiaxial stress towards the nuclei of cracks was found. Fig. 1 shows the typical relationship between stress and the time to fracture found by Troiano in hydrogen-charged high-strength steels. On the other hand, Shurakov 3,4 explains the realization of delayed fractures in martensite as due to a "quasi-viscous" behavior of the austenite grain boundaries immediately after the martensitic transformation. 1) MATERIALS AND EXPERIMENTAL METHODS Two low-alloy steels of commercial purity were used for the experiments reported in this paper. Their chemical composition is shown in Table I. The heats were melted in a laboratory furnace, cast to ingots, forged to bars of 3/4 in. diameter, and annealed. Machined test pieces were heat-treated as follows: Ni-Cr-Mo steel held at 900°C for 30 min and quenched in oil; Mn-Si-Cr steel held at 900°C for 30 min and quenched in water. For the delayed-fracture tests, notched cylindrical test pieces, Fig. 2, stressed in torsion, and unnotched cylindrical tensile-test pieces, 1/4 in. diameter, were used. The specimens were normally loaded with a constant static load 45 min after quenching for the torsional tests and 10 min

Jan 1, 1965

By Merlon C. Flemings, Theodoulos Z. Kattamis

Examination was made of the distribution of tnanganese and nickel in colutrrnar dendrites of a cast low-alloy steel; more limited work was corzducted on chromium. Corresponding "segregrction ratios" were calculnted and shown to be relntivelv insensitive to cooling rate (&apos;&apos;segregation ratio" is defined (Is the ratio of maximum to minimum concentrations within a volume whose dimensions are the order of the dendrite-arm spacing). Isoconcentratiorl curves were determined by the electron micropvobe and by rt7etallografihic studies on specimens subjected to isothermal-transformation treatments. From construction of isoconcentration curves, morphology of columnar dendrites is descvibed as intermediate between Perfect rodlike and sheetlike morphologies. The study is extended to equiaxed dendrites and it is shown that the strcture of these dendrites is sittlilar in many respects to that of columnar dendrites. On the basis of tlze sheetlike morphology of dendrites, a simple model is pvoposed for calculation of honzogenization kinetics. Results of trzatllevlatical analysis brcsed on this utzodel are given. This analysis relates residual segregation to time at homogenization temperature; it is in agreement with experiment. Calculations are given which show that even for relatively rapidly cooled material (of 1-ine dendrite-artn spacing) treatmets at 1200°C or above are necessary to achieve slgxificant Izomogenization of elenlents other than carbon itz reasonable time (e.g., rnangclnese, nickel). Conlplete homogenization of carbon is obtnined at much lowev tenlperatures (below 870°C). IN dendritic solidification of castings and ingots, solute redistribution during freezing results in mi-crosegregation of most alloy elements. The micro-segregation is such that minimum solute concentrations occur at the center of dendrite arms and maximum concentrations occur between dendrite arms. Residual segregation after subsequent therma1 processing (homogenization) depends on maximum and minimum initial concentration, on the detailed geometry of the isoconcentration surfaces within interdendritic regions, on the diffusion coefficient of the solute, and on time of thermal processing. The objective of this work was to determine, for a low-alloy steel, maximum and minimum concentrations, and the geometry of isoconcentration surfaces, primarily in order to permit calculation of homogenization kinetics. Most of the work reported was conducted on Samples from a unidirectionally solidified, fully columnar ingot. This type of ingot is made by extracting heat during solidification from one face; techniques for accomplishing this have been discussed.&apos; Samples were taken at several locations, up to 5.75 in. from the mold chill face; the bulk of the work was performed on samples at 5.75 in. Alloy cast was, nominally, 0.4 pct C, 1.8 pct Ni, 0.8 pct Cr, 0.7 pct Mn, 0.25 pct Mo, 0.3 pct Si, and the balance iron. Brief study was also made on samples from an ingot which solidified with equiaxed grain structure. SAMPLE PREPARATION AND ANALYSIS Samples for electron-microprobe analysis were incorporated in mounts that included pieces of electrolytic nickel, chromium, and manganese, in order to normalize the intensities of these solutes in the specimens; also, a piece of electrolytic iron was included to measure the background. All specimens were polished in the usual metallographic manner. After the microprobe traces were made, the path was revealed by etching the specimens with picral. All microprobe analyses were made by point counting, integrating for 30 sec. The distance between points was fixed from 2 to 10 p, according to the precision desired in each case, the fineness of the structure, and the concentration gradient existing in a given area. (The distance was chosen 2 to 5 p near the maximum-concentration regions and 5 to 10 p near the minimum concentration.) The "take-off" angle for the A.R.L.-Model No. 21000 microprobe employed was 52.5 deg. Samples for metallographic analysis of isoconcentration curves were prepared by austenitizing at 1540°F for 20 min, quenching to the nose of the TTT curves (1200°F), heat treating isothermally at this temperature for a given time 0, and then quenching to room temperature. Due to concentration gradients existing in a dendritic structure, no transformation will take place for a given time 0 of isothermal heat treatment in the regions where the a.lloy concentration is higher than a given limit. Thus, the dendrite appears limited by an isoconcentration curve and can be made to appear to grow by varying the time of isothermal heat treatment.

Jan 1, 1965

By W. G. Lidman, H. J. Hamjian

&apos; I HE fabrication of many materials from powders involves a sintering process. A mass of powder will sinter because of the excess free energy over the same mass in the densified state caused by the higher total surface area of the powder. An understanding of the kinetics and mechanism of sintering should assist in improving the properties of such materials. The present investigation conducted at the NACA Lewis laboratory deals with the sintering of chromium carbide. Dry sintering (sintering at a temperature below the melting point) was divided into two stages by Shaler:&apos; the first stage, during which the particles preserve much of their original shape and the voids are interconnected, and the second stage, during which densification occurs and the pores are isolated. The mechanism of forming interfaces between particles, or welding together of particles, has been investigated by Kuczynski2 and may be described by any one or a combination of the following mechanisms: viscous flow, evaporation and condensation, volume diffusion, or surface diffusion. The mechanism by which pores are closed or eliminated (densification) during sintering, is of interest. Grain growth observed during sintering may be attributed to the variation in the surface energies of individual grains, causing some grains to grow at the expense of others. Grain boundary migration occurs presumably by a diffusion process, therefore the rate of grain growth would be expected to increase exponentially with increasing time and temperature. Thus, for practical sintering times of less than 1 hr, a certain minimum temperature may exist at which major structural and property changes will occur. Densification and kinetics of grain growth during sintering under pressure of chromium carbide were investigated to provide additional information which will aid in describing more accurately the sintering process and the mechanisms involved. This material was selected for this study because of the current interest in high strength, oxidation resistant refractory materials, such as carbides, which are sintered to produce solid, dense materials from powders. Sintering under pressure is a process where the heat and pressure are applied to the compact simultaneously, specimens for this work were prepared by sintering under pressure at different temperatures and for various time periods. Experimental Procedure Preparation of Specimens: Chemical analysis of the commercial chromium carbide used in this investigation was as follows: Cr 86.19 pct, C 12.14 pct, and Fe 0.2 pct. X-ray diffraction powder patterns gave characteristic diffraction lines of Cr3C2 crystal structure. Powder particle size was determined microscopically and the average initial particle size was 6 microns with 85 pct between 2 and 10 microns. Specimens sintered under pressure were formed in graphite dies3 heated by induction. Sintering temperatures were measured with an optical pyrometer by sighting into a 3/8-in. hole drilled 1 in. deep at the midsection of the graphite die. A load of approximately 1 ton per sq in. was applied to the powder. The die assembly was heated in 20 min to the highest temperature (2500°F&apos;) at which no increase in grain size could be observed, and less than 2.5 min were required to heat from this temperature to the maximum temperature (3000°F). Sintering temperatures and times for the specimens of this investigation are indicated in Table I. Analysis of Specimens: Specimens polished with diamond abrasives were etched to reveal the grain boundaries with a 1:1 mixture of 20 pct potassium hydroxide and 20 pct potassium ferricyanide heated to 160°F. Representative areas of each sample were photographed at 1000 diameters. The largest diameters of all well-defined grains were measured, but only the measurements of 15 of the largest grains were averaged in order to determine an index of grain size on the assumption that they were among the first to begin growth. Densities were determined from differential weighing of the samples in air and water. The reported density values are considered correct within ±0.01 g per milliliter. Results and Discussion Metal compacts have exhibited grain growth when sintered at temperatures about two-thirds of the absolute temperature of their melting point.&apos; Grain growth also occurs during the sintering of chromium carbide and is illustrated by the micrographs shown in Fig. 1. These micrographs were prepared from specimens sintered for 90 min at temperatures ranging from 1371°C (2500°F) to 1648°C (3000°F). Average grain size and density measurements of specimens investigated are presented in Table I. The relationship between grain size and sintering tem-

Jan 1, 1954

By T. P. Papazoglou, N. A. D. Parlee, W. C. Phelps

PRACTICAL designs for good "home made" molybdenum furnaces are hard to find in the literature. The one described briefly below left something to be desired but was good enough to operate as a rather long (30 in.) two-zone furnace for periods of over 2 months at temperature (1400° to 1600°C) without shutdown. The principal problem in our application was to establish a temperature profile with two distinct constant-temperature zones and no dip between the zones. This and other problems mentioned below would not arise, however, if both zones were operated at the same temperature and if a shorter furnace were acceptable. Since molybdenum windings oxidize very rapidly when heated in air, impervious refractory tubes were used for both the furnace core and the outer jacket tube shown in the accompanying figures. A protective atmosphere of forming gas (10 pct H2, 90 pct N2) was continuously passed through the gas-tight annular volume between the core and outer jacket. The water-cooled copper ends shown in Figs. 1 to 3 sealed the ends of the tubes. Annealed molybdenum wire (40 mil) was wound on the recrys-tallized alumina core (35.5 mm OD by 28.5 mm ID by 30 in.) at a spacing of 0.36 in. The spacing was reduced to 0.29 in. close to the ends to partially compensate for end heat losses. Fig. 2 shows two molybdenum-ground lead taps off the center of the winding to produce the two independect temperature zones. The ground lead was insulated with 1/4-in. alumina tubing and connected to the grounded copper end by passing the wires through the gas port tube and crimping each wire into notches cut at the mouth. To prevent sagging of the core at high temperatures, refractory "troughs" were cut from alumina and mullite tubing to cradle the core. The support "troughs" which were 6 in. long and located about 5 in. from each end of the annular volume also served as radiation shields. In view of the different expansion coefficients and operating temperatures of the core and outer jacket (3.5 in. OD by 3 in. ID by 30 in.), the ends of the tubes were smoothed and squared to produce good sealing surfaces, and the core was ground 1/32 in. shorter than the outer tube. The power terminals were passed through their respective conductor ports which were internally lined with alumina tubing and sealed with Armstrong adhesive A-6 leaving about 1 in. of protruding lead wire for external connections. (Adhesive A-6 is a two-component system consisting of an epoxy-type resin with a mineral fibrous filler and an amine catalyst.) Figs. 1 and 3 show the entire assembly of concentric refractory tubes, copper ends, and sealing o rings, held together with two brass flanges and 3/8-in. bolts with heavy springs for dimensional flexibility. The furnace shell (19 by 19 by 30 in.) consisted of a steel frame with sheets of transite forming a box. The copper ends protruded through two 3.75-in. circular holes cut at the center of each transite square end. Thermal insulation next to the transite exterior was effected by K-23 B&W bricks alld in a central volume of approximately 9 by 9 by 30 in. a row of K-30 bricks was lined up to support the hot assembly. The rest of the volume around the outer

Jan 1, 1965

By M. E. Shank, J. Wulff

At the present time, the designer of dies for metal powder pressing is handicapped by relative ignorance of stress distribution and frictional effects at the interior surface of the die. Unckell was the first to develop a method for the study of wall friction. He used three Brinell balls on which the die rested during pressing. The total frictional wall force was determined by the size of impression these balls left on a soft metal plate. Since the method does not give radial pressures, or distribution of such pressures, coefficients of friction could not be determined. Although Unckel measured density distribution, he was not able to determine radial or shear stresses. Shaler2 has proposed theoretical expressions for the stress and density distribution within cylindrical compacts during pressing, in accordance with the experimental results of Kamm, Steinberg, and Wulff.3 By application of Siebel&apos;s method,4 Kamm et a13 plotted stress trajectories for two compacts. From the stress trajectories they calculated coefficients of friction from point to point along the die wall. As pointed out by Shaler in the discussion of Ref. 3, these values are based on progressive point-to-point calculations on finite size grid squares across the compact. In the region of the die wall such calculated values may therefore have considerable cumulative error. The purpose of the present paper is to develop an experimental method by which the nonhydrostatic pressures and shears acting on the interior wall of a cylindrical die can be measured. Such measurements can then he correlated with existing data to aid in the explanation of the pressing process. The method used is based on the elastic: properties of the thick-walled tube used as the die. The principle of super-position of force systems on an elastic body is assumed to hold. Electric strain gauges were mounted in adjacent positions on the exterior die wall in order to get an exact measurement of the variation of tangential strain over the length of the die during pressing. While in this paper, measurements in terms of only tangential strains are considered, it is well to note that similar calculations may be set up for axial strains. The latter are not preferred, since they tend to be smaller than the tangential strains and therefore permit less sensitive measurements. Discussion in this work is restricted to compacts pressed from both ends, since the elastic deformation of the die is then more amenable to analysis. Before choosing the electric strain gauge method, a more direct line of attack was considered and discarded. The discarded idea was the insertion of a pressure gauge through a hole in the die wall.* The gauge would have been in the form of a small piston. If pressure were exerted against such a gauge, it would move outward along a radius of the die. One disadvantage of the scheme is its inability to measure shears along the die wall. Another more serious disadvantage is the disturbance caused by the device itself. It would serve to change the forces it was designed to measure. No matter how small the movement of the gauge, when pressure is applied a discontinuity would exist in the wall surface at that point. Due to the stress concentration caused by the hole, abnormal deflections of the die wall would occur around the gauge. During pressing, powder would be forced into the resulting depression. The depression would then become larger with increasing compacting pressure. Powder, not being a fluid, is capable of supporting shear. The ease with which it would flow into the die wall depression to further move the piston is an indication, not of the radial pressure at that point, but of the state of shear retarding the movement. Thus the "pressure" gauge is really a criterion of flowability, and of the capability of the powder to support shear. For these reasons, it was decided that the electric strain method, herein employed, was more reliable, if more indirect. The gauges and lead wires, mounted on the external die wall do not in any way affect the behavior of the metal powder or the die during pressing. Theory of the Method THE EFFECT OF RADIAL PRESSURE ON THE DIE WALL Effect of a Single Small Band of Hydrostatic Pressure Consider a die which is a thick-walled cylinder of outer radius R. and inner radius Ri. If over a small finite length L there is a normal pressure P, a tangential strain distribution at the outer wall results. This is shown schematically in Fig 1. The exact shape of the curve may he predicted by an extension of the theory of a semi-infinite beam on an elastic foundation.6 This

Jan 1, 1950

By M. E. Shank, J. Wulff

In view of the current interest in magnetic materials having rectangular hysteresis loops, as for example those obtained with the grain oriented 50 nickel 50 iron alloys,t we wish to call attention again to the results obtainable with the perminvar (Co-Ni-Fe) alloys heat treated in a magnetic field. Data taken from direct current measurements made prior to and during World War II give the typical values shown below for two of the perrninvar alloys. Fig 1 and 2 show- the hysteresis loops for these samples. The first sample above consisted of small rings punched from 0.014 in. sheet stock. These rings were heat treated at 1000°C for one hour in a hydrogen atmosphere and then cooled with the furnace to 750°C at which point they were subjected to a magnetic field of 15 oersteds maintained during cooling to room telmperature. The molybdenum perminvar sample consisted of a spirally wound core of 0.001 in. tape. The heat treatment was the same except that box annealing methods were used and no hydrogen atmosphere was employed. Even better properties might be expected using hydrogen. The heat treating temperatures and cooling rates are not critical. Rectangular hysteresis loops produced in other perminvar alloys by heat treatment in a magnetic field were described earlier.&apos;,? Properties similar to those described above are realized in perminvars manufactured by conventional methods. Drastic cold working which in practice limits the final thickness and is gen- erally expensive may thus be avoided. This information may be of interest to those concerned with magnetic alloys and the development of contact rectifiers, magnetic amplifiers and so on.

Jan 1, 1950