By J. A. Hren, C. M. Wayman

RECENT investigators have noted anomalous behavior in the electrical resistivity of vanadium below room temperature. Rostoker and Yamamoto1 in studying the vanadium-oxygen system hypothesized that the body-centered-tetragonal phase existing from 15 to 34 at. pet O at approximately 800°K was really a low-temperature allotrope of vanadium that was stabilized by oxygen. In measuring the electrical resistance of cold-swaged vanadium rod over a range of temperatures, a small discontinuity was observed at approximately 240°K, supporting their notion of allotropy. However, the magnitude of the observed discontinuity was extremely small. Loomis and Carlson2 in studying the ductile-brittle transition in vanadium also made resistance measurements and reported a discontinuity near 200°K. More recently, White and Woods3 showed that the electrical resistivity from room temperature to approximately 100 °K was not linear and at variance with the Bloch-Griineisen law. Instead of finding a discontinuity, they observed a deviation from linearity below 200°K. In discussing their results they pointed

Jan 1, 1961

By S. Storchheim

MORE and more attention is being paid to the bonding of metals in their solid states. For a better understanding of this technique for joining metals and how it is affected by changes in temperature, pressure, and time at temperature and pressure, a detailed report concerning nickel to aluminum bonding has been published.' In order to broaden the knowledge accrued, some additional work concerning solid state joining of aluminum to copper and aluminum to zirconium was performed. The investigation of the Al-Cu system was considerably more extensive than the investigation of the Al-Zr system. For the A1-Cu system, not only were tensile sudies made but intermetallic penetration rate investigations also were carried out. The effect of temperature on intermetallic penetration rate for the A1-Cu system was determined at 11 tsi pressure, held 2 min. Procedure Apparatus: The hot pressing technique was the means of solid state reaction used and required the equipment depicted in Fig. 1. The following procedure was involved: The two metals to be reacted were placed in an aquadag-lubricated 18-4-1 tool steel die, 16 in. high by 1.440 in. ID, between punches of 1.366 in. diam made of the same material. A thermocouple well was located in the die body 3½ in. down from the top of the die, while another well was located centrally in the bottom punch 8½ in. from the bottom of the die. This die assembly was located in three cylindrical ceramic heating furnaces placed in tandem. Each furnace was controlled individually by a Variac power transformer. In turn, the die and furnaces were placed in a water-cooled stainless steel pot which could be evacuated. A cover, which contained a centrally located Wilson seal with an 18-4-1 1 in. diam ram running through it, was bolted on the pot. After sealing, the pot was evacuated by a roughing pump to 200 microns pressure, after which a diffusion pump was used to bring the pressure down to 5 to 15 u. At this pressure, the furnaces were turned on. As soon as they started to heat, out-gassing of the entire unit raised the pressure to 30 to 400 p. By the time the specimens were at temperature ready to be pressed, approximately 4/2 hr, the vacuum pumps had re-established the 5 to 15 u pressure. Once the desired temperature was reached, the required pressure was applied for a predetermined length of time to the 1 in. ram, through to the top punch, and to the specimen. When the time for keeping the specimen under pressure had elapsed, the pressure was released, the energizing coil current turned off, and the assembly allowed to cool. After cooling, the die was removed from the pot and the specimen was ejected. Specimen Preparation: Two different types of specimens were made for this investigation. One was for subsequent tensile testing, while the other was for determination of intermetallic alloy zone penetration into the parent metals. Tensile Bars—Commercially rolled copper pieces in. thick or zirconium sheet pieces 1/32 in. thick and 1.366 in. diam were placed between commercial 2-S aluminum rod 1 in. thick and 1.366 in. diam. This sandwich in turn was slipped into a 2-S aluminum sleeve 1.438 in. OD and 1.370 in. ID. This sleeve lined the couple up and prevented the aquadag lubricant from getting in between either the A1-Cu or Al-Zr interfaces. Immediately prior to the specimen assembly, the copper or zirconium was abraded on the flat surfaces with 320 grit silicon carbide paper, producing clean smooth surfaces. The aluminum was chemically cleaned just before assembly by: l—degrease in acetone, 2—distilled water rinse, 3—immersion for 3 min in 5 pct NaOH at 70" to 80°C, 4—distilled water rinse, 5—immersion for 2 min in 50 pct HNO3 solution at room temperature, 6—distilled water rinse, and 7—drying in a blast of gas. After the A1-Cu sandwiches were hot pressed and ejected, the specimens were machined such that the aluminum sleeve was removed, and the remaining aluminum was then threaded; the bar so produced was tested later for tensile strength. In all the instances where Al-Cu couples were tested, the specimens broke during the test at the Cu-A1 interface and never within the aluminum or copper. The ultimate tensile strength values at times showed considerable scatter for a set of given reaction conditions. Because of this, as many as three to five specimens were made for a particular set of conditions. The trend of the average tensile strengths obtained was not as conclusive as was the trend of the maximum tensile strengths, the latter values being obtained under optimum reaction conditions. Therefore, the values of ultimate tensile strength given herein are maximums.

Jan 1, 1956

By E. F. Ketterer, D. B. Collyer, A. B. Wilder

AISI constructional alloy steels are a series of steels in which a numbering system signifies the chemical composition limits. SAE (Society of Automotive Engineers) and AISI (American Iron and Steel Institute) use basically the same numbering system. The steels contain, in part, alloy additions of chromium, molybdenum, nickel, and vanadium. They are used widely in the automotive industry but have not been adopted for high temperature service. The purpose of this investigation was to study changes in microstructure observed in typical AISI constructional alloy steels in the welded and un-welded conditions after exposure for 34,000 hr at 900" and 1050" and, in several instances, 1200°F. The tensile and creep rupture properties after exposure for 10,000 hr were also evaluated. The investigation is a continuation of the work previously discussed. Little was known concerning the existence of graphite in medium or low carbon steels before 1943. It is important to note that continued exposure at elevated temperature is required in order to develop graphite in steels. Interest in the presence of graphite in steel, and also in changes in the properties of steels after long service at elevated temperatures, developed after 1943 when a failure of a welded joint of high temperature piping was associated with the graphitization of a relatively low carbon content steel with 0.50 pct Mo,8,0 Numerous investigations have beeen made in recent years studying the relationship of this type of failure to changes in properties. Attempts have been made to evaluate the performance of a number of steels, particularly in the heat-affected zone of welds. It was the unfortunate failure of a weld-heated zone in high temperature piping in the steam-power industry which focused attention upon possible failures, and upon the need for improved steels for high temperature piping service. Investigation by the National Tube Div., U. S. Steel Corp., Lorain Works, has included a wide variety of steels in an attempt to learn the effects of numerous factors and elements upon the long time performance of steels, although many of the compositions studied will never be used at elevated temperatures.1,4-7 Included were the well established AISI steel series, which offered opportunity to test moderately high carbon content steels as well as observe the effect of nickel, chromium, molybdenum, etc., upon the properties of these well known steels. The properties of the AISI steels were also studied for comparison with the previously reported properties of the Cr-Mo steels, now used by the steam-power industry.5,7 Materials and Testing Procedure The AISI alloy steels in Table I were exposed for 10,000 and 34,000 hr at 900°, 1050°, and 1200°F.

Jan 1, 1958

By P. G. Winchell, M. Cohen, J. Woodilla

The kinetics of stabilization have been studied with respect to the isothermal component of the martensitic reaction in ivon-nickel alloys. Although the carbun (or nit-vogen) content may be very low in these alloys, it plays an important vole in the stabilization phenomenon. In fact, if these interstitial elements are removed by moist-hydrogen treatment, no evidence of stabilization is found. In the pvesence of 0.007 wt pct C, the activation energy for the stabilization process is comparable to that -for the diffusion of carbon (or nitrogen) in ferrite) rather than in austenitc. This suggests that the interstitial diffiision controlling the stabilization occurs within the martensitic embryos rather than in the matrix of the parent phase. The kinetics furthev indicate that the interstitial atoms tend to diffuse -from the embryos toward the suvroundings, thereby immobilizing the interface. This appears to be the origin of the stabilizing effect -found in these alloys. PHILIBERT' has shown recently that interstitial elements play an important role in the stabilization of martensitic transformations in iron-base alloys. However, determination of the temperature dependence for this stabilization process has produced values (- 11,000 cal per mol) that cannot be readily identified with the activation energy for diffusion of carbon (or nitrogen) in either ferrite or austenite. In the present work, the isothermal mode of the martensitic reaction was employed to derive the activation energy for stabilization, and this was found to agree fairly well with that for diffusion of carbon (or nitrogen) in ferrite. An iron-nickel alloy with 30.8 wt pct Ni and 0.007 wt pct C was used in these experiments, the specimens being in the form of rods 0.074 in. in diam and 2 1/2 in. long. The specimens were sealed in evacuated vycor tubes and austenitized at 1100°C for 1/2 hr prior to quenching in water. A second series of specimens was decarburized (and denitrogenized) prior to the above austenitizing treatment by annealing in moist hydrogen for 182 hr at 1215°C. In order to achieve a "standard" condition in the austenitic state, all the specimens were transformed to martensite by cooling to - 195°C before the final austenitizing. Both the 0.007 pct C and the decarburized series then had an Mi temperature of about - 30°C. The isothermal martensitic transformation was carried out at a reference temperature of -88"C, and was traced by means of electrical resistance measurements. Each resistance value was normalized by dividing by the resistance of the austenitic specimen at O°C, thus giving a resist- ance ratio R. The rate of decrease of the resistance ratio (-dR/dt) provided a measure of the transformation rate. It was found that a plot of R vs log t at the reference temperature resulted in a slightly curved line which could be closely approximated by two straight lines intersecting at a time of 10 min, as shown in Fig. 1. If G = dR/dlogt is the linear slope of either straight segment, the rate of transformation at any given time is: The ratio of G for 1 less than 10 min to that for t greater than 10 min was 1.19 for the 0.007 pct C series and 1.24 for the decarburized series. These ratios made it possible to compute the transformation rate at any time greater than 10 min, knowing the transformation kinetics prior to 10 min. The stabilization treatment was introduced by up-quenching from the reference temperature, usually after 10 min of isothermal transformation: to one of four stabilizing temperatures between 0" and 22"C. After holding for various times, the specimens were down-quenched to the reference temperature for additional isothermal transformation. In this way, it was possible to compare the transformation rate (- dR/dt), immediately after stabilization with the transformation rate (- dR/dt)U in the unstabilized condition. The degree of stabilization was defined as: Ordinarily, Gs and Gu would be measured after the same time of prim isothermal transformation.

Jan 1, 1960

By H. K. Birnbaum

The effect of 1ow-temperature stabilization anneals on the structure of the 0 phase Au-Cd alloys and on the diffusionless transformations observed in these alloys was examined by X-yay diffraction techniques. A phase separation in the ß-phase region was proposed to account for the experimenta1 results. The effects of quenching from elevated temperatures on the transformation behavior of these alloys were shown to be consistent with the proposed mechanism. IT has been shown that the high-temperature ß phase (CsCl structure) of the Au-Cd alloy system transforms to a phase having an orthorhombic (D2) ß&apos; structurel1-3 for compositions near 47.5 at. pct Cd and a tetragonal (4/m, m, m) ß" structure* in the vicinity of 50.0 at. pct Cd. Both transformations are diffusionless, crystallographically reversible, and occur on cooling at about 60° and 30°C respectively. The temperature interval from the beginning to the end of the transformation is of the order of 5°C in each case. Although the transformations are normally athermal, some of them have been reported to occur isothermally.= wechsler6,7 has shown that the effects of quenching a 49.0 at. pct Cd alloy from elevated temperatures are consistent with the retention of a nonequilibrium number of lattice vacancies. Annealing of these quench effects results in a broadening of the X-ray reflections.8 After a suitable quench, the 47.5 at. pct Cd alloy transforms to a phase having not the p&apos; orthorhombic structure but another structure which has properties similar to that of the ß" tetragonal structure.5.9 This change in the type of transformation has also been obtained after long anneals in the ß-phase region at about 70oC10 The present investigation was primarily concerned with the structural changes accompanying the above transformation phenomena. The change in transformation product and accompanying physical changes during an anneal in the ß phase have been termed stabilization effects. Experimental Procedure —The results reported in this investigation were obtained with the use of a Norelco diffractometer fitted with a temperature-controlled cryostat. The specimen temperature was controlled to better than ± 0.l°C during the measurements. CrKa radiation monochromated electronically with the use of a scintillation counter and pulse height analyzer was utilized. Specimens containing 47.5 and 50.0 at. pct Cd were prepared by sintering filings obtained from homogenized ingots of the proper alloy composition. (Gold of 99.999 pct purity and cadmium of 99.98 pct purity were used). All heat treatments were carried out with the specimens capsulated in vacuum ( < 10 % mm Hg) or in a He-H gas mixture. The quenching technique used in these experiments was to drop the pyrex capsule which contained the specimen from the annealing furnace into water, the temperature of which was controlled. The pyrex capsule shattered on contacting the water resulting in a relatively rapid quench. After the heat treatment, the specimens were mounted in the diffractometer and were left undisturbed in the diffractometer specimen holder during each sequence of measurements. EXPERIMENTAL RESULTS A) Low-Temperature Annealing—The transformations which were considered "normal" for these alloys were those obtained athermally during furnace cooling at approximately 50°C per hr after an elevated temperature anneal. Under these experimental conditions, the specimens were observed to transform to phases having structures whose diffraction patterns could be indexed as the ß&apos; orthorhombic structure for the 47.5 at. pct Cd and as the 0" tetragonal structure for the 50.0 at. pct Cd alloys. The transformation temperatures on cooling were approximately 60" and 30°C, respectively. Under the "normal" conditions both transformations were observed to go to completion, i.e., the entire volume of the ß phase was transformed to the product phase. In some specimens an extremely weak ß 110 reflection was observed at 20°C indicating that a small amount of retained ß was present. The effect of low-temperature annealing on the nature of the diffusionless transformations was examined for the 47.5 and 50.0 at, pct Cd alloy. The specimens were annealed in evacuated capsules at temperatures in the vicinity of 600°C (as specified in Table I) for 24 hr and were then cooled to 100°C at a rate of 50°C per hr. The specimens were then removed from the capsules and mounted in the diffractometer without allowing the specimen temperature to drop below 80°C. Annealing at the low temperatures was accomplished in the diffractometer by means of the cryostat which was mounted around the specimen. During the low-temperature anneals the lattice parameter, integral breadth of the reflections, and ratios of the integrated intensities of the fundamental and super lattice reflections for the 0 cubic phase were periodically determined. After annealing for the required time, the specimens were slowly cooled in the diffractometer and the diffraction patterns were recorded as a function of temperature. The specimens were cooled until the phase transformations were completed, following which the specimens were heated and diffraction

Jan 1, 1960

By Carlos G. Valenzuela

The value generally accepted for stacking-fault energy, of copper has been approximately 40 ergs per sq cm based on Fullman&apos;s2 value for the coherent twin-boundary energy and the assumption that is twice the twin boundary energy However, Thornton and coworkers8 determined that the lower limit of for copper is approximately 60 ergs per sq cm, based on measurements of dislocation-node radii. They suggested that the assumption of = 2t is invalid. It is the purpose of this note to present results which indicate that the values of obtained by measurement of twin-grain boundary intersections and the values obtained by measurement of dislocation-node radii are actually compatible. The most reliable values for of the a brasses, based on electron-microscope observation of dislocation nodes, are probably those values reported by Smallman and Green6 who applied the Siems correction (1961) to data obtained by Howie and Swann.3 These values shown in Fig. 1 give an extrapolated value of approximately 70 ergs per sq cm for pure copper. In the present work, Fullman&apos;s method for determining the stacking-fault energy of copper was extended to the a brasses. High-purity copper (99.999 pet) and high-purity zinc (99.999 pet) were mixed in proportioned amounts and melted in sealed and evacuated quartz tubes. The alloys were homogenized for a week at 750°C and chemically analyzed by means of X-ray fluorescence. These alloys, along with a specimen of pure copper, were rolled to 98 pet reduction and a thickness of 0.009 in., resealed, and annealed for 40 hr at 715°C. Values for the ratio of twin-boundary energy to the grain-boundary energy, it gb, were obtained from measurements of dihedral angles formed at the intersections of twin boundaries and grain boundaries by using Fullman&apos;s2 mechanical analogy of surface tensions acting at the intersection of an annealing twin and a grain boundary. The angles between the twin traces and the grain boundaries were measured for a large number of twin-grain boundary intersections at a magnification of X500 using a rotating mechanical stage on a Reichert metallograph. The rotary stage has a calibrated angle scale with vernier so that measurements can be made to 0.1 deg. The mean twin-grain boundary energy and standard deviation were calculated for copper and each of the brasses by the use of an IBM 7072 computer. It was found that the mean value of gb stabilized after approximately 100 twin-angle measurements. This was determined by plotting the mean against the number of angles measured. Since the measured angles deviate from true dihedral angles, a correction factor for grain orientation, discussed below, was applied. The stacking-fault energy was then calculated from these values and the values of grain-boundary energy derived by Taylor.7 The data obtained are tabulated in Table I. Values for stacking-fault energy are plotted in Fig. 1. The value of gb for the specimen of 1.03 pet Zn is close to the value obtained by Fullman2 for OFHC (99.98 pet) copper, 0.045. It is believed that the purity of the copper affects gb significantly. The 99.999 pet purity Cu used in this investigation yielded a value of yt/ygb, 0.76, which is much higher than that obtained by Fullman. Additional evidence suggesting that the purity of

Jan 1, 1965

By D. H. Woodard

One of the principal uses of polarized light in metallurgy is to show the granular structure of metals by contrasting reflections. This use is confined largely to anisotropic metals, such as beryllium, tin, magnesium, and the like.1 Recently, Hone and Pearson2 have extended the use of polarized light to include the isotropic metal aluminum. This was made possible by the formation of an anodic film that was optically anisotropic and that had a fixed and reproducible structural relationship to the grains in the substrata. With their method, it was possible to indicate localized textures in annealed aluminum sheet. In the course of an investigation of plastic deformation at the National Bureau of Standards, it was found that the isotropic single phase alloy Monel could be made optically anisotropic by treatment with the usual Monel contrast etchant. Experiments soon showed that dif- , ferences in orientation could be detected easily. Previous investigations involving the use of polarized light have been restricted to annealed metals. In this paper it will be shown that inhomo-geneous plastic deformation which results in lattice bending and development of deformation bands, experienced by individual grains in polycrystalline Monel, is revealed in the microstruc-ture. This interpretation of the micro-structure was confirmed by a study of slip lines formed after prior plastic strain. Materials and Procedure The material used was Monel, the chemical composition of which was C—0.17 pet, Mn—1.28 pet, Fe—1.61 pet, S—0.009 pet, Si—0.17 pet, Cu— 30.70 pet, Ni—66.04 pet. The material was divided into 2 lots which were treated as follows: Lot A was heated at 1700°F for 3 hr to produce a fully annealed, coarse grained structure. Lot B was heated at 1400°F for 1 hr to produce a close approximation of a fully annealed structure without appreciable increase in the grain size of the original material. After each of these heat treatments the material was cooled in air. Samples for metallographic examination were cut from tensile and compression test specimens and were prepared by grinding on lead-tin laps, followed by electrolytic polishing, † Etching and the development of ridges were avoided by keeping the voltage above 3.8 and by preventing contamination of the polishing solution with water. Monel, when polished and treated with most etchants, is optically isotropic. However, when given a light etch for about 4 sec with the Monel contrast solution the surface of the metal becomes optically active. The microstructure when observed under crossed nicols* appears different from that viewed by ordinary light. This is shown by a comparison of micrographs made of the same area of a plastically deformed specimen using polarized light (Fig la) and white light (Fig 16). If Monel, which has been lightly treated with the contrast etchant, is slightly deformed by compression, rectangular figures are apparent over the specimen. However, within too short a period to be photographed, these rectangles become circular, probably because of surface tension effects within the etched film. The two observations,

Jan 1, 1950

By C. G. Wilson

DURING the course of some experiments on the plastic deformation of gallium a standard stereo-graphic projection was prepared with (001) at the center and it was felt that this might be useful to others working with single crystals of gallium. The stereogram, given in Fig. 1, was made using the following crystallographic data (Bradley, 1935):

Jan 1, 1962

By M. Hoch

Equations are derived from statistical considerations to represent the activities of each component of an interstitial solution, and of a compound with a wide homogeneity range as a function of composition and temperature, based on the interaction energies between the various components, Eij. The equations are checked on the binary systems Fe-C, Ta-H, and Y-H, the ternary systems Ti-O-H, liquid Fe-C-0, and the compounds TiO, MnO, COO, and YH,. In all cases the present model represents the experimental data well. THE aim of this paper is to derive from statistical considerations the thermodynamic behavior of non-substitutional solid solutions. "Nonsubstitutional solid solution" means either an interstitial solid solution (carbon in iron, oxygen and hydrogen in hexagonal and bcc titanium, and so forth) or deviation from stoichiornetry in compounds (introduction of vacancies—removal of atoms in one or both lattice sites of compounds FeO, MnO, TiO, NbO, YH2). wagnerl and Fowler and Guggenheim considered the theory of compounds with small deviation from stoichiometry; Anderson includes larger deviations from stoichiometry, the defect being present in one component only, as vacancy and interstitial. Rees considers only vacancies in one of the components and introduces various kinds of sites for the component where the defect occurs; the various sites interact with different energies, thus giving isotherms with two or more plateaus. Both Rees and Anderson are mainly occupied in determining the limits of two-phase regions, and the defect interaction energy is determined from the critical point. Darken and Gurry5 gave a brief treatment of carbon solution in iron; Speiser and spretnak calculated the configurational entropy for binary interstitial solid solutions by assuming that each interstitial atom in the solution excludes a certain number of neighboring interstitial sites from occupancy. Use will be made of this concept later. Hoch et al treated transition metal oxides of the NaCl-type structure, and also oxygen solution in titanium.&apos; The main aim was to determine the behavior of the activity of one of the components as a function of the composition in the single-phase region. In the present paper, the various interaction energies are discussed in detail and the similarity between interstitial solid solutions and deviation from stoichiometry in ionic compounds is shown. Both types of systems have in common that at least on one kind of lattice site only one kind of atom occurs; this gives a fixed frame to the system, permitting a much easier statistical treatment than for the substitu-tional solid solutions. (The theory is also applied to ternary systems.) The difference between an interstitial solution and deviation from stoichiometry can be explained as follows. In an interstitial solution in the pure or standard state the host atom or host structure is present alone and all the interstitial sites which are going to be filled when the interstitial atom is introduced are empty. The interstitial solution is now created by introducing atoms into this empty lattice. In the deviation from stoichiometry, both kinds of lattice sites are already occupied in a special fashion (all lattice sites occupied, or the same fraction of lattice sites empty, or one kind completely filled, the other only two-thirds). Deviation from stoichiometry removes atoms from lattice sites, adds them, or removes atoms from one kind of lattice site and introduces them on the other lattice site. Though both cases (interstitial solution and deviation from stoichiometry) lead almost to the same equations, they are treated separately. The treatment given below corresponds to the "regular solution"10 treatment of substitutional solid solutions. Speiser and spretnak&apos;s6 treatment is similar to the athermal solution in the substitutional use. a) INTERSTITIAL SOLID SOLUTIONS Theory. It will be assumed that there are N lat-tice sites occupied by the host atom (denoted by 1). Corresponding to those N lattice sites there are N octahedral and EN tetrahedral interstitial sites. If only one kind of interstitial atom is added, this in-

Jan 1, 1964

By R. G. Davies

The activation energy for steady state creep above -500°C is observed to be independent of the applied stress although it varies from -67 kcal per mole at 2 at. pct Si to -100 kcal per mole at 11 at. pct Si due to changes in crystallographic order. The magnitude of the activation energy, by comparison with Fe-A1 alloys, indicates FeSi type of order in certain alloys. X-ray results confirmed the presence of FeSi type of order. It is proposed that dislocation climb is the rate controlling mechanism for all the alloys. It has been demonstrated that when a diffusion mechanism is the rate controlling process, the formation of a superlattice in brass,1 Fe3A1,2 Ni3Fe,3-5 and Feco6 1) increases the creep resistance, and 2) increases the activation energy for steady state creep. Furthermore, a study of creep in Fe-15 to 20 at. pct A1 alloys7 has revealed that as the alloy composition approaches the long-range order field, there is an increase in the activation energy for steady state creep which is thought to be due to an increase in short range order. Fe-A1 and Fe-Si alloys are similar in that they both form the DO3 superlattice in which aluminum or silicon atoms have only iron atoms as first and second nearest neighbors. There are, however, two important differences between the alloy systems: 1) The superlattice formation at -350°C commences at -10 at. pct si8 as compared to -20 at. pct Al,9 and 2) Fe-A1 alloys form a FeAl (B2 type) super-lattice where aluminum atoms have all iron first nearest neighbors even at 22 at. pct Al, but so far no similar FeSi superlattice has been observed. With the similarity between Fe-A1 and Fe-Si alloys in mind, alloys of iron with 2 to 11 at. pct Si were examined for variations with composition of the activation energy for steady state creep and of creep strength. The temperature range of greatest interest was above 1/2 TM (TM is the absolute melting temperature) where it is usually observed that diffusion is the rate controlling process. A subsidiary X-ray investigation of the Fe-Si system was undertaken in an attempt to define the position of the order-disorder boundary as a function of cooling rate. EXPERIMENTAL DETAILS a) Creep. Specimens whose gage length was 1.5 in. and with a cross-section 0.04 by 0.08 in. were strained in tension by a lever-arm arrangement, and the load was adjusted between each creep test to maintain constant stress. The apparatus and mode of operation have been fully described in a previous publication.7 As each test produced a creep strain of 0.25 pct, the variation in stress during the test was negligible. Creep strain was measured at the end of one of the alloy steel grips by a displacement transducer with the out-of-balance potential being recorded on a variable speed recorder. The full-scale deflection of the recorder could be varied in steps to give limits of sensitivity of between 0.1 and 0.001 pct creep strain. The alloys, Table I, were made available by the Metallurgical Department, National Physical Laboratory (N.P.L.), england,10 and by the Research Department, General Electric Co. (G.E.), Schenectady, N.Y. They were hot worked at -850°C, warm worked at 550° to 650°C, and recrystallized in vacuum at -750°C to give a grain diameter of -0.1 mm. All the alloys had a very low impurity content; those from the N.P.L., for which a complete analysis is available,&apos;&apos; show carbon less than 0.026 pct, manganese less than 0.006 pct, and oxygen plus nitrogen less than 0.0024 pct. b) X-ray Procedure. A General Electric XRD-5 X-ray set with a focussing lithium fluoride mono-chromator in the diffracted beam, and a pulse height analyzer to eliminate harmonic wavelengths of the cobalt radiation, was used to investigate the structure of several very fine grained (grain diameter <.01 mm) Fe-Si alloys after the following heat treatments: 1) Quenched from 700°C, 2) slow cooled from 650°C (-40°C per hr), and 3) very slowly cooled from 400° to 100°C (10°C per hr with a 24 hr anneal every 100°C). The method of obtaining the diffraction pattern over the range of 20 from 15 to 45 deg was to count for at least 100 sec every l/3 deg with a slit subtending 1 deg in 20 at the focus; the probable counting error was less than 2 pct.

Jan 1, 1963

By Robin O. Williams

The increase in internal energy as the result of deformation has been measured for lead, aluminum, silver, nickel, iron, and zirconium by using rapid, adiabatic compression. The stored energy increase is roughly Proportional to the strain; the propor-tionality constant increases rapidly with increasing melting point. The fraction of the mechanical energy which is stored increases more slowly, since the strength of the metals also increases with melting point. The values of the stored energy are considered accurate to about 10 pet. The present values appear about 50 pet larger than the more reliable published results where comparisons are possible. It is possible that this difference is due to the high strain rate used in this investigation. Immediately after deformation all these metals release energy at a rate roughly proportional to (time)-&apos;. This release is considered to be associated with dislocation motion but in aluminum (and copper) some additional process seems to be present. This release can represent 20 pet or more of the stored energy. WHEN pure metals are plastically deformed, most of the mechanical energy is converted into heat. The energy remaining within the metal is significant in that it is the energy of the disorder produced and thus detailed knowledge of this energy is a powerful tool in understanding the nature of deformational disorder. While much effort has been expended on this problem, the amount of information available is limited. The situation as of 1958 has been carefully reviewed by Titchener and ever.&apos; The present results have been obtained by a new experimental approach to this problem. The method necessitates high-strain rates which make comparisons with published results less certain, but a high-strain rate is an advantage in that the energy release immediately after deformation can be followed. EXPERIMENTAL PROCEDURE In the experimental method used, the internal (stored) energy is given as the difference between the mechanical work used in deforming the sample and the heat which is released (the first law of thermodynamics). The work is supplied by two identical hammers swinging freely from a fixed height, the available energy being the product of the mass, the gravitational constant, and the distance through which the center of gravity moves. The initial temperature rise of the sample represents the heat produced by the deformation. The sample temperature is determined by a small thermocouple embedded in and supporting the sample. This process can be repeated over and over to produce increased strains. Most samples are run through about five cycles to a total strain of around 0.7. Further details are covered elsewhere. The determination of the heat is dependent upon the sample weight, its specific heat, the rise in temperature, and any gains or losses to the surroundings. One is dependent on published results for specific heals (the values were taken from a collection).3 The values must be accurate to about 0.1 pet in order that they not affect the results. The best values thus do not contribute to the uncertainty, but this is probably not always the case. The accuracy of the temperature rise is limited primarily by knowledge of the thermocouple characteristics over short temperature intervals, but careful calibration eliminates this as an important factor. One can calculate readily the heat flow between the sample and hammers if the time of contact and the sample temperature are known and if there were no oil at the interface. Assuming the maximum temperature difference, upper values for this interchange have been calculated (the time of contact is determined from the decrease in sample length) and it may or may not be significant. However, no correction is colnsidered necessary because of the presence of a thin oil film which has a thermal conductivity much less than the metals. Except for the possible uncertainty in specific heat, the heat is considered to be adequately known. The mechitnical losses which are recognized as important are: 1) friction between the sample and the hammer:;, 2) the kinetic energy in the hammer suspension system which may not be entirely usable, 3) the rebound energy of the hammers, and 4) the vibration of the hammer heads. All these have been covered in detail elsewhere2 and only the more significant points are made here. The friction turns out to be small except for soft materials (lead)

Jan 1, 1962

By M. J. Hordon

Measurements of the 103 yield stress of ordered and disordered poly crystalline Cu ,Au were related to the ordered antiphase domain size determined by resistivity measurements. For undeformed material, a yield stress maximum wa obtained at a critical domain diameter of about 40A. Plastic deformation resulted in a marked increase in the yield stress and electrical resistivity of the ordered alloy compared to the disordered, the strain hardening rate increasing regularly with initial antiphase domain size. Order hardening was accompanied by a sharp reduction in size of the initially large domains. It has been observed that the yield stress of ordered and partially ordered Cu3Au alloy varies sensitively with antiphase domain size aid degree of order.ly2 In addition, ordering of the lattice leads to a marked increase in the strain hardening rate (order hardening) as compared to the rate for the disordered alloy. In the present investigation, changes in the electrical resistivity and yield stress of ordered polycrystalline Cudu with varying initial domain diameters were measured after tensile plastic deformation in order to examine the effect of cold work on the antiphase domain size. EXPERIMENTAL PROCEDURE Au-Cu alloy of 99.99 pct purity analyzing 50.85 wt pct Au-balance copper was obtained from the Handy-Harmon Co., N. Y., in the form of 0.061 in. diam drawn wire. Wire specimens 3 in. in length were given the following annealing treatment in nitrogen: 500" for 72 hr, 820" for 15 hr, and 450" for 5 hr, followed by a water quench. The annealing sequence resulted in a completely disordered structure with a grain size of about 0.2 mm. The disordered specimens were then reannealed at 360&apos; in nitrogen for periods varying from 10 min to 150 hr followed by quenching to produce ordered structures with varying domain sizes. The degree of ordering and variation of domain size was followed by electrical resistivity measurements made at room temperature using a low resistance precision Kelvin double bridge apparatus. The specimen resistance was determined over a length of 4.0 cm between two brass knife-edge contacts while the specimen was immersed in an oil bath to minimize temperature variations. In addition, the current flow in the circuit was minimized by a current pulse technique in balancing the bridge in order to avoid heating the specimen. Using a sensitive galvanometer to detect the bridge null, the accuracy of the resistance measurement Wire specimens were plastically strained in tension with an Instron tensile unit at strain rates in the range 5 x 10"5 sec-&apos; to 2 x 10"4 sec-&apos;. Stress and extension data were fed into the Instron chart drive amplifier to obtain the actual stress-elongation curve from which the yield stress at 10"3 strain was determined. The maximum resolution of the apparatus was approximately 50 psi stress and 3 x 104 strain. At various plastic strain levels, deformation was interrupted and the electrical resistivity determined after removing the stress. RESULTS AND DISCUSSION 1) Yield Strength of Ordered Cudu. In order to determine the effect of the ordered antiphase domains on the initial yield stress, specimens were prepared with varying domain sizes ranging from zero for 5 completely disordered structure to about lo5A for a completely ordered structure by suitable annealing treatment. Domain sizes were estimated by comparing room temperature electrical resistivity data with the original data of Jones and sykes3 as modified by rdle.&apos; In agreement with previous work, the resistivity varied sensitively with domain diameter and degree of order, decreasing from approximately 11.6 x l0- ohm-cm for the disordered structure to about 5.9 x l0- ohm-cm for ordered domains above 10"3 cm in diameter. Fig. 1 shows the change of the 103 yield stress with ordered domain size. It is evident that the maximum

Jan 1, 1963

By A. K. Mukherjee, J. E. Dorn, J. D. Mole

Investigations were carried out on the effect of polyslip on the strain hardening of aluminum single crystals. The orientations investigated were those lor which the tensile axis was in the [001], [111], [112], and [012] directions plus another for which the Schmid angles for {111}(110) slip were 1 deg. The experimental data were analyzed on a model based on the intersection of dislocations with particular emphasis on the effect of polyslip on the activation volume for inter-section. It is shown that the rate of strain hardening inreases for those orientations wherein attractive dislocation intersections occur and that those orientations which produce the greater number of such intersections exhibit the greater strain hardening. Good correlation of the data is obtained with the concept that attractive junctions, as proposed by Saada, Play an important role in accounting for the rate of strain hardening. EXISTING concepts on the nature and cause of strain hardening in fcc metals have been deduced principally from experiments on the deformation of single crystals under single slip. The effect of crystal orientation on the shapes of the stress-strain curves for single slip have been summarized by seegerl and more recently by Clarebrough and Hargreaves.2 Tensile specimens whose axes fall near the center of the [001]-[011] line of the standard triangle of the stereographic projection exhibit the longest range of easy glide (Stage I) and the lowest rates of linear hardening (Stage 11) whereas specimens whose axes lie near fie [001]-[111] line of the standard triangle have limited or no easy-glide range and exhibit somewhat higher linear strain-hardening rates. Specimens whose axes lie near the [001] or the [ill] poles do not exhibit easy glide and have the highest rates of linear hardening. Kocks3 has shown that the highest rates of linear hardening Occur under Polyslip when the tensile axis coincides with the [111] or the [ 001] pole. Since the rate of strain hardening is sensitive to specimen orientation and the incidence of polyslip, these relationships might help to discriminate between various dislocation models for strain hardening in fcc metals. Previous attempts to analyze the effect of orientation on strain hardening,1"3 however, did not provide a unique answer to this problem. Consequently the present investigation was undertaken wherein additional data, particularly that for the effect of polyslip on the activation volume for intersection, was also determined in order to provide more complete information on the details of strain hardening. Whereas analyses of these data reveal that several recommended models for strain hardening are at variance with the facts, good correlation of the data is obtained with the concept that attractive junctions4 play an important role in accounting for the rate of strain hardening. I) EXPERIMENTAL APPROACH seegerl demonstrated that slip in fcc crystals at low temperatures is dependent on thermally activated intersection of glide dislocations with forest dislocations. This has been confirmed by tests on single crystals of aluminum by Mitra, Osborne and Dorn5 and on polycrystalline aluminum by Mitra and Darn.&apos; Thus in accord with Seeger&apos;s theory, the shear strain rate, ?, below a critical temperature, T, is where .V is the number of points of contact per unit volume between forest dislocations and glide dislocations, A is the area swept out per successful intersection, b is the Burgers vector, v is the frequency of vibration of the segment of the glide dislocation undertaking intersection, U is the activation energy for intersection, k is Boltzmann&apos;s constant, and T is the absolute temperature. For aluminum, which has an extremely high staeking-fault energy, the constriction energy is negligibly small and therefore the activation energy decreases practically linearly with the stress according to as will be recomfirmed later, where Uo is jog energy at the absolute zero, G and Go are the shear moduli at the test temperature T and O°K, respectively, L is the spacing of the forest dislocations, t is the applied shear stress for slip, and tGo is the stress field that must be surmounted athermally.

Jan 1, 1965

By T. B. Massalski, C. S. Barett

THAT metals and alloys of the body-centered-cubic structure tend to become unstable at low temperatures is so nearly universal that any exceptions are worthy of special attention. Studies of the exceptions may disclose unrecognized examples of metastability or may shed light on the nature of some of the factors that stabilize the body-centered-cubic phase. Among the structurally analogous body-centered-cubic 3/2 electron compounds, the ß-phase in the Cu-Zn system deserves further attention for, although this phase is known to undergo partial mar-tensitic transformation on cooling below room temperature to the temperature of liquid nitrogen when the composition is less than about 42 wt pct Zn, it does not transform on cooling .when there is more than this amount of zinc present.1-4 The present authors recently found that an alloy containing 48.35 wt pct Zn could be transformed, however, if deformed severely at room temperature or lower temperatures.V his discovery led to the suggestion that the jerky flow of ß-brass single crystals6 and some of the unusual temperature variations of the yield strength and hardness are due to strain-induced transformation during the tensile tests. The present investigation is an extension of that work to cover the entire available range of compositions of Cu-Zn ß-phase alloys and certain interesting compositions of the ß-phase in the Cu-Zn-Ga system. Particular attention is given to the structure of the transformation product resulting from cold work, which is found to vary with alloy composition, and to the temperature range in which transformation can be induced in the various alloys. The composition limits of the body-centered-cubic phase in the Cu-Zn system, based on a recent review by Raynor7 and the precision determinations of Beck and Smith: are shown in Fig. la; in the ß region the alloys are disordered and in the ß region they are ordered. The rate of ordering is so rapid that a high degree of order is found in any of these alloys immediately after quenching. Experimental The nine binary and four ternary alloys of this investigation were prepared from cathode copper (99.99 pct purity), electrolytic zinc (99.99+ pct), and gallium (99.98+ pct). All alloys were cast in transparent Vycor tubing, homogenized at temperatures between 800° and 890°C, and quenched in water. Ternary alloys were cast in small amounts (-5 g) to predetermined compositions to fall along a line of constant electron concentration in the ternary system. Changes of weight during the casting operation of the ternary alloys were not greater than 1 part in 2500 from the intended nominal weights and therefore their compositions were accepted without chemical analyses. All binary alloys were cast in larger amounts (100 to 150 g), homogenized, and hot rolled after preheating to 800°C. The central portion of the rolled strip of each alloy was annealed for eight days and quenched in brine. All binary alloys were analyzed chemically. The compositions, heat treatments, and metallographic appearances of all alloys are tabulated in Table I. Various samples were subjected to heat treatment or cold work at several temperatures and were then examined metallographically or by means of X-rays. Specimens about 6x6x3 mm in size were examined metallographic ally to confirm the presence of the ß-phase after quenching. Cold work was introduced by fastening each sample between two pieces of steel, cooling the assembly to the desired temperature, and transfering it rapidly to a vise where moderate or severe compression was immediately applied. Cold working at liquid helium temperature was done by a chisel-shaped tool mounted on an X-ray spectrometer, described elsewhere.% A!! metal-

Jan 1, 1958

By T. Price, H. A. Holl, A. P. Greenough, A

UdIN, Shaler, and ulff&apos; first used wires for the determination of the surface energy of a solid metal. A gage length was marked by tying knots in the wires, which were then suspended in a cylinder of the same metal, heated in an inert atmosphere for the appropriate time, cooled to room temperature, and finally removed from the furnace so that the lengths of the wires could be measured. With iron wires, difficulties associated with deformation during the phase changeszp3 made it necessary to measure the gage lengths at the tem-

Jan 1, 1964

By E. S. Bumps

A series of macrographs are presented for the purpose of graphically recording the strain phenomenon that accompanies the energy transition in the Charpy impact testing of a mild steel that is susceptible to strain aging. STRAIN patterns in mild steel Charpy impact specimens were obtained in order to determine whether, on the first appearance of plastic strain during deformation, the initial fracture cracks appear in the region of plastic strain or in the elasti-cally deformed regions between. Although this attempt to locate the initiation of cleavage was not successful, the observed strain patterns illustrating various stress conditions in partially deformed Charpy specimens are presented along with a discussion of the possible dependence of transition energy on the yield phenomenon. Earlier work on the development of strain patterns in mild steel have been reported by Fry1 and later by Jevon.2 Harris, Rinebolt, and Raring3 observed characteristic strain markings on the surface of Charpy V-notch impact specimens fractured above and below the transition temperature which they presented schematically. It is intended that the strain figures presented here will add to the literature a graphic correlation of strain with transition energy in impact specimens. Samples of % in. round hot rolled, 0.20 pct C steel were machined to standard 0.394 in. sq, V-notch Charpy impact specimens. Preliminary testing involved determination of transition temperature, Fig. 1, using a Sontagg impact tester. These data were subsequently used to select temperatures above, within, and below the transition range at which specimens were partially deformed. Partial deformation was obtained by either varying the energy or the testing temperature, see Table I. Macroscopic strain figures shown in Figs. 2 to 19 were produced by several metallographic repolish-ing and etching steps. The macroetchant used was as follows:4 120 g HCl, concentrated; 100 ml water; and 90 g cupric chloride. Strain figures were obtained on the outer surface and on sections through the central portion of the impact specimens in order to determine an approximation of the volumetric strain pattern. In the tensile strain figures reported by Jevon, it was found that strain etching would not work immediately following strain unless the material was heated to 200°C. The impact strain patterns presented here were obtained without this heating, but the specimens were not etched until ten months after straining. This confirms a discussion of Jevon&apos;s paper, in which it was pointed out that strain figures can also be developed after aging for long periods of time at room temperature. Hardness of the strained and unstrained portions, revealed by the etched pattern, was explored using R, impressions converted to R, hardness values. Discussion of Results In the impact test, as in the tensile test, some parts of the specimen yield and deform plastically, while other regions are deformed only elastically. The plastic deformation bears a relation to the imposed stress pattern. In the strain figures presented here, the plastically deformed regions are the dark etching ones. The strain figures are always symmetrical because the stress state in the Charpy-type specimen under impact loading is symmetrical. The difficulties encountered to produce initial cracks are intimated in Figs. 2 and 4. At a temperature of —75ºF, the stress was not sufficient to pro-

Jan 1, 1953

By D. Weinstein

Yieldilzg in annealed arc-cast molybdenunz in torsion was studied as a function of strain rate and tem-perature. The temperature dependence of the yield point for different strain rates was used to calculate a heat of activation for the yield point. The heat of activation was not a constant but was approximately a linear function of the stress at yield. It is proposed that the rate effect in yielding is determined in part by a site place-change of C (or other interstitial atom) in the metal. THE low-temperature embrittlement phenomenon in metals and alloys has been known to exist for a long time. Although a transition from ductile to brit-tle behavior has been observed in some close-packed hexagonal metals1 and a face-centered cubic alloy, the most common class of metals exhibiting this be-havior has a body-centered cubic lattice structure. For example, a ductile to brittle transition has been observed in iron,3 molybdenum,4 chromium,5 colum-bium,6 and tungsten.7 In the present investigation, molybdenum specimens were tested in torsion over a wide range of temperatures at three widely separated strain rates, and the temperature for onset of embrittlement was determined. Characteristic of body-centered cubic metals and closely associated with plastic deformation is the appearance of a sharp upper and lower yield point. Theoretical explanation of the yield point in iron and low-carbon steel is due to Cottrell,8 who attributes the phenomenon to the pinning of dislocations by the formation of impurity atmospheres around the dislocations. These atmospheres tend to lock the dislocations and make them more difficult to move. The stress required to move a dislocation and thereby cause plastic deformation is greatly increased, and thus an upper yield point is observed. In addition, theoretical analysis,9 as well as experimental observations, show that the upper yield point is strongly a function of temperature. The upper yield point is observed to decrease with an increase in testing temperature, and above a certain temperature (-700° K in iron) it no longer appears. This is consistent with the concept that thermal vibrations will help free a dislocation from its atmosphere, so that the external stress required to free a dislocation from its pinning atmosphere decreases with increasing temperature. Furthermore, with increasing temperature the equilibrium concentration of impurity atoms around a dislocation decreases exponentially with the result that the dislocation is less firmly pinned. In Cottrell&apos;s theory of yield point a static model is visualized in which the pinning atmospheres, particularly interstitial atoms, are immobile, and the dislocations are anchored to stationary positions in the lattice. However, experiments1,7 show the upper yield point to be time-dependent or a function of the rate of straining, a high strain rate causing a high upper yield point. Present theory does not adequately account for the rate dependence of the yield point, and the exact function of the interstitial atom is not under stood. Nevertheless, observation of the temperature dependence and rate dependence strongly suggests that the upper yield point phenomenon is due to the interaction between dislocations and pinning atoms, and that a diffusion mechanism is important in determining the yield point.

Jan 1, 1962

By James H. Bechtold

The yield strength of annealed tungsten was found to have a strain rate exponent 12 times as great as that of low carbon steel. The effects of temperature and strain rate could be correlated through the Zener-Hollomon parameter with a heat of activation associated with yielding of 32,000 cal per g-atom. This heat of activation is independent of strain although both the temperature and strain rate dependence of the yield strength vary with strain. MOST metals have mechanical properties that are relatively insensitive to strain rate, especially at temperatures below that at which creep is important. In iron and molybdenum," however, relatively large strain rate effects are observed in the temperature range where the rapid increase in yield strength occurs which leads to the ductile to brittle transition. In this temperature range Zener and Hollomon&apos; have suggested that the effects of strain rate and temperature T on the yield strength could be correlated through a single parameter, P, in the following manner where Q is a heat of activation characteristic of the metal and associated with some unspecified relaxation process. They also observed that if the temperature is restricted to a relatively narrow range— below room temperature for steel—that the logarithm of the yield strength could be expressed as a linear function of the logarithm of P. From this relation the logarithm of stress should be a linear function of the logarithm of the strain rate at constant temperature: where r will be referred to herein as the strain rate exponent. At a constant strain rate the logarithm of stress should be a linear function of l/T, ay(e = C) ~ eT [4] where q = Qr [5] and is referred to herein as the temperature exponent. These equations have been found to relate the effects of temperature and strain rate on the yield strength of molybdenum in the temperature range wherein the ductile to brittle transition occurs, —75° to +150°C.2 Bechtold and Shewmon3 have shown recently that the ductile to brittle transition in annealed tungsten occurs in the temperature range +150° to +350°C. In this temperature range the yield strength in-

Jan 1, 1957

By F. Forscher

Pronounced porosity, decreasing with distance from the fracture surface, is found in the necked region of tensile specimens tested at room temperature or liquid nitrogen temperature. A hydrogen solution treatment followed by a quench prevents pore formation in tests at —196°C, but has little effect on tests made at room temperature. Reduction of area values at —196°C are strikingly improved by the same treatment, but show no improvement in room temperature tests. The experimental results support the hypothesis that strain-induced porosity results with hydride initially present or, in material containing less than 50 ppm H, with hydride precipitated by strain aging. ZIRCONIUM&apos;S advent as an engineering material in nuclear reactor construction has brought forth many investigations concerned with the properties of this metal and its alloys. Some attention has been given to the ductility of the metal.1, 2 Particularly, the effect of hydrogen on the impact strength was noted," indicating a pronounced dependence of ductility on the hydrogen content and its distribution in the metal. Micro graphic:&apos; and X-ray diffraction studies&apos; have shown that a precipitated hydride phase causes embrittlement in zirconium,&apos; which implies a distinctly different mechanism from that causing hydrogen embrittlement in steels."-&apos; In the latter case, it is assumed that atomic hydrogen diffuses to rifts, where it forms molecular hydrogen under such internal pressures that it causes the rifts to enlarge, leading to fracture. Thermo-dynamic studies of the Zr-H system8, 9 also indicate that the internal pressure of molecular hydrogen would be too low to cause any damage to the zirconium at room temperature, and the formation of a zirconium hydride (d phase) is favored." It is noteworthy that this phase has a face-centered-cubic structure and nearly 18 pet larger molar volume than close-packed-hexagonal a-zlrconlum&apos; Other features of the ductility of zirconium are the absence of a typical cup-cone failure upon tensile testing, a pronounced strain-induced porosity in the necked region of a tensile bar, Fig 1, and the associated spongy appearance of the fracture surface A tremendous improvement in ductility at liquid nitrogen temperature can be observed following a heat treatment that retains the commonly present quan- tities (10 to 50 ppm) of hydrogen in solution. Such tests show a typical cup-cone failure and the absence of strain-induced porosity, Fig. 2. The present paper reports results of an investigation into the causes of strain-induced porosity in zirconium. Room temperature tensile fractures of mild steel, aluminum, and titanium have also been examined for strain-induced porosity. In each case porosity could be detected, but the amount was orders of magnitude less than was found in zirconium. Of the three metals, titanium showed the strongest effect. Material, Specimens, and Preparation The greater part of this investigation was done on Westinghouse crystal bar zirconium, are-melted, forged, and hot-rolled. Chemical analyses of the hot-rolled plates are given in Table I, along with those of the Foote crystal bar zirconium used in this work. The specimens were machined from the hot-rolled plate (1550°F) of 1/2 in. thickness and subsequently heat-treated according to one of the treatments shown in Table IS. All specimens were machined round, the longitudinal axis in the rolling direction, with a gage

Jan 1, 1957

By George Krauss, M. Cohen

The reverse martensitic transfomzation (i.e., the conversion of martensite to austenite on heating) was investigated in Fe-Ni alloys containing 30.5 to 33.5 wt pct Ni. The reversed austenite was found to be sufficiently distorted to exhibit marked differences in mechanical properties and to undergo recovery and re crystallization on further heating. In particular, the yield strength of the reversed austenite was as much as 2.5 times higher than that of the virgin austenite: with five cycles of the direct and reverse martensitic transformation, the yield strength was 2.6 times higher. There was an accompanying decrease in strain-hardening capacity and in stable ductility or uniform elongation. The recrystallization was observed to follow sigmoidal kinetics, but was characterized by an abnormal1y large temperature dependence which was evidently due to carbon segregation at the migrating grain boundaries. Upon recrystallization, the strength Properties reverted to those of the virgin austenite, but the ductility did not fully recover until the annealing temperature was further raised to dissipate the carbon segregation at the grain boundaries. The transformation of reversed austenite to produce second-generation martensite resulted in an unusually imperfect structure, thereby leaditg to additional strengthening. Horlleuer, the martensitic phase was much less responsive in this respect than was the austenite. MOST martensitic transformations are capable of undergoing a reverse transformation back to the austenitic phase on heating.&apos; This reaction, like the direct transformation to martensite on cooling, is usually athermal. In analogy with the Ms andMf temperatures for the martensitic transformation (where M, > Mf), the reverse transformation is characterized by the As andAf temperatures (where As<Af). It is well-known that the finish (Af) of the martensite-to-austenite reaction on heating may occur at a temperature where austenite is not stable relative to other phases in the equilibrium diagram.&apos; Reverse martensitic transformations have been found to influence the properties of the parent austenitic phase in a number of ferrous alloys. The austenite thus produced after one or more reversals is significantly altered in strength, microstruc-ture, diffusivity, and annealing characteristics compared to well-annealed, virgin austenite. The first detailed observations of such phenomena were made by Wasserman3 on an Fe-30 wt pct alloy. He found that the reversed austenite (i.e., austenite formed by the reverse martensitic transformation) was much stronger than the original austenite, and the second-generation martensite (i.e., martensite produced from the reversed austenite) was somewhat stronger than the first-generation martensite. On heating the reversed austenite, recrystallization occurred in a manner similar to that of a cold-worked metal; the Laue spots sharpened and the strength decreased.4 In recent years, Russian workers have shown considerable interest in these reverse martensitic transformations. Most of such investigations5-10 have been concerned with the stabilization of reversed austenite relative to subsequent martensitic transformation, and because of its unusual nature, this phenomenon will be discussed in detail elsewhere." On the other hand, the annealing behavior of reversed austenite and the attendant variation in properties have received little attention beyond the experiments of Wasserman.3,4 Gridnev eta1.,8 in one of the few such studies. followed the hardness change of reversed austenite as a function of time at three annealing temperatures. The marked strengthening of austenite achieved by the reverse martensitic transformation has been referred to as "transformation strengthening" by Wasserman3,4 and as "phase hardening" by Malyshev et a1.7,9,10 to differentiate it from hardening produced by cold working. Both groups of investigators noted that further strengthening of the austenite could be attained by repeated or cyclic transformations, but the first cycle resulted in the most pronounced effect. Evidence of the altered microstructure of reversed austenite has been reported by Maximova and Nikonorova6 and by Edmonson and KO.12 The former found that reversed austenite was much more sensitive to etching than the original austenite, and the latter authors observed a (&apos;ghost" structure resembling martensite in certain areas of the reversed austenite. Enhancement of the self-diffusion rate in reversed

Jan 1, 1962