By G. K. Manning, E. R. Stein, E. E. Underwood

Columbium, carbon. and nickel additions were made to iron-base alloys with 20 pct CY. The effects on microstructure, precipitation-hardening characteristics, and High-temperature properties were investigated by means of metallographic, hot-hardness, and magnetic measurements. An austenitic alloy consistilzg of Fe-20Cr-14Ni-0.8C-2.5Cb had higher hot-lzaciness at 1700°F than the other alloys investigated. Its favorable standing is attributed to an enhanced interaction of Cb and Cr4C particles dispersed within a stable austenitic matrix. FOR the past 20 years, cobalt- and nickel-base alloys have been used for the more stringent high-temperature applications because of their excellent creep resistance. Although their performance is quite satisfactory, other base materials must be considered for large tonnage, low-cost applications such as for the automotive gas turbine. Iron-base alloys are also used extensively, but at somewhat lower temperatures, primarily because of the instability of particles or because precipitation occurs at relatively low temperatures. Since unusual stability has been reported for Fe-Cb and Cb-C compounds.1-3 it was hoped that effective amounts of these compounds could be taken into solution at temperatures just below the melting range, then precipitated upon reheating. Actually, strengthening was found to occur by both precipitation hardening in some alloys and by phase transformations in others. Among the alloys investigated, that with the best high-temperature properties owes its strengthening to a combination of carbide particle interaction and a relatively stable austenitic matrix. EXPERIMENTAL PROCEDURES Small preliminary melts of about 100 g were made in a vertical Glotube furnace, using alundum crucibles and an argon atmosphere. Alloys weighing 35 lb were melted in a basic-lined induction furnace, also under argon. The compositions of the alloys are given in Table I. The nickel-free alloys were usually ferritic, while those containing nickel were generally austenitic. Depending upon the particular heat treatments, or the combination of alloying elements, two-phase alloys of ferrite and austenite could be obtained. In the following text, however, the nickel-free or nickel-bearing alloys are referred to simply as either ferritic or austenitic alloys respectively. The small ingots were swaged at 2000°F, in steps, to rods of approximately 3/16-in. diam. The large ingots were forged at 2100°F to 1-in. sq bars. No difficulties were encountered in swaging or forging any of the alloys to as much as 90 pct reduction in area. For heat treating at temperatures above 2000°F, specimens were sealed in quartz tubes under a partial pressure of helium. No special precautions were found to be necessary at lower temperatures. Intermetallic compounds in the preliminary alloys were identified by means of X-ray diffraction measurements. Correlation of these results with micro-structural characteristics (such as color, shape, size, and location) of the compounds aided in their identification. Magnetic susceptibilities were also obtained at room temperature with a Magne Gage instrument after the various heat treatments. To

Jan 1, 1962

By I. B. Cadoff, J. C. Bilello, R. Rosenberg

Diffiusion of magnesium into the surface of LiF crystals to controlled depths and subsequent heat treatments provided a wide range of surface zone harahesses and structure, The bend strength of the LiF crystals was increased by as much as an or-dev of magnitude. Ductility was achieved when dislocation generation occurred in the diffusion zone or when dislocations penetrated to the surface from the intevior. A critical surface hardness of 130 to 140 kg per sq mm was found helozu which generation could take place in the diffusion zone and ahoue which the zone was impenetrable, This hardness was obtainable by several methods, among them the aging of quenched MgF2 -LiF solutions to produce MgF, precipitation. Maximum hardness was ohtained in quenched specimens with no visihle evidence of MgF,. Diffusion-zone formation followed a parabolic rate law and an activation energy of 20.9 kcal per mole was obtained for the process. RECENTLY, the properties of ionic crystals as related to surface condition have been receiving much attention, specifically the transitions between ductile and brittle behavior. Originally Joffe 1 showed that NaCl crystals could be made ductile by immersion in water and related this to the elimination of surface microcracks. Aerts and DeKeyser 2 and Gorur 3' have subsequently shown that ionic crystals are inherently ductile and are embrittled through contact with air. Machlin and Murray4 hypothesized that a layer of NaCIO3 produced by contact of ozone with NaCl induced embrittlement by acting as a barrier to outward dislocation flow. westwood,' Rosenberg and Cadoff,9 and Bilello and cadoff' have reported surface strengthening of LiF crystals by coating with a magnesium compound and then heat treating for adherence. The major effect of the coat was to inhibit dislocation-slip lines from reaching the specimen surface. westwoods showed microcrack formation and fracture to be caused by slip-band interactions at the surface. The material presented in this paper is an extension of the work reported earlier by Bilello, Rosenberg, and cadoff'6,7 and illustrates the wide range of surface properties and bulk behavior obtainable by use of heat-treated magnesium-diffused surface regions in LiF crystals. EXPERIMENTAL PROCEDURE The LiF single crystals were obtained from the Harshaw Chemical Co. Some batch to batch variation was observed; therefore all specimens for a given test series were cleaved from the same crystal. The typical dimension used was 1 by 0.1 by 0.40 in. Surface damage resulting from cleavage was removed by chemically polishing in a 2 pct NH4OH solution. Each group of specimens was given a vacuum anneal at 700°C for 4 hr to provide a base standard for measuring comparative effects of various surface treatments. To produce the reacted surface zone, the annealed specimens were immersed in a boiling suspension of MgF, in doubly distilled HzO, agitated slbwly for 30 sec, removed, and dried at room temperature. Uniform coatings of MgF, were deposited with a thickness of approximately 5 mils. It should be noted that this technique can be modified for use with crystals which are soluble in water by using boiling absolute alcohol as the dissolving medium. This was found effective for the coating of NaCl with MgF2. The diffused surface zone was obtained by annealing the coated samples at elevated temperatures in a vacuum of lob4 mm Hg. Penetration depth was controlled by varying the annealing time from 1/2 to 28 hr. After heat treatment, the samples were tested for bend strength and hardness. Load was applied by four-point bending in a hard-beam testing jig. Four-point rather than three-point bending was used to provide a wide area of constant stress and to minimize the effect of localized inhomogenities in the specimen. The deflection rate was 8 x min-' and the distance between knife edges was 1/4 in. Load-time curves were obtained from a chart recorder coupled to the machine and converted to resolved shear stress on the shear plane vs deflection, as plotted in the figures. The unstressed portions of the sample outside of the two outer knife edges were used for the microhardness studies. Microhardness measurements were made with a Bergsman tester attached to a Reichert metallograph. All hardness impres-

Jan 1, 1964

By T. A. Read, H. K. Birnbaum

Deformation of AuCd alloys having the 8 (orthorhombic) and (3" (tetragonal) structures occurs by the stress induced motion of twin boutdaries. A restoring force acts on displaced twin boutdaries as a result of internal energy increases in the volume through which the boundaries are displaced. The phenomonology of the twin boundary motion is described and a mechanism for twin boundary motion and the restoring force is proposed. A time-dependent stabilization behavior of the twin boundaries, which is observed after the twins are formed by the diffusionless phase transformations, is described. THE AuCd 8 phase (ordered bcc structure) exhibits a transformation to a phase having an orthorhombic structure, 8' (space group D'), for compositions in the vicinity of 47.5 at. pct Cd and to a phase having a tetragonal structure, 8" (point group 4/m, m,m), for compositions in the vicinity 50.0 at. pct Cd. Both transformations are diffusionless, occur on cooling at 60" and 30OC, respectively, and are crystallo-graphically reversible.' They are accompanied by an inhomogeneous deformation which was observed to be twinning in the low-temperature phase. 3'4 The transformations may occur by a "single interface" or by "multiple interfaces."5'6 In the "single interface" transformation, the twinned product phase consisted of two twin orientations as shown in Fig. 1. In the multiple interface transformation the product phase contained "domains" each of which contained two twin orientations, Fig. 2. Deformation of specimens containing transformation twins was achieved by motion of the twin boundaries. Releasing the applied stress resulted in the displaced twin boundaries returning towards their initial positions. This "pseudo-elastic" behavior of the boundaries varied with time after the formation of the twin boundaries by the transformation.

Jan 1, 1961

By R. H. Hiltz

Three titanium alloys, known to provide a mechanically unstable p structure after quenching, were selected as material for a study of the Origin and nature of stress-induced transformation. Data from hardness and tensile tests were used to study the initiation of marten site and the effect of the transfornation and transformation products on the mechanical properties of B titanium, particularly the stress-strain relationships. With the exception that the materials investigated showed a natural aging reaction in the P condition, their behavior is analogous to that of' stress-transforming stainless steels. The transformation starts after initial yielding and is essentially complete just prior to .maximum loading. Once initiated, the martensite itself is capable of propagating the transformation. The deforn-ing materials show low strength, high ductility, and a high strain-hardening exponent. In metallic systems which undergo a diffusionless transformation on cooling, it is possible to produce a similar transformatiorl by plastic deformation under special conditions. Dewez' in delineating Ms temperatures for the titanium-rich end of most titanium binary systems:, established the point of intersection of Ms with room temperature for those particular alloys. Alloy compositions which would quench to mechanically unstable p were established from these data. The first investigation into the possibility of stress-induced transformation occurring in titanium met with little success. It was concluded that such a transformation in titanium was possible only under very special conditions. Continued effort in this direction, however, showed certain Ti-Mo binaries to be highly susceptible to this phenomenon. This fact was utilized by Liu to study the habit planes of martensite and by Machlin and wenig5 to study the effects of stress and plastic deformation on the P to a prime transformation in titanium alloys. The first investigation of the mechanical properties of these alloys was conducted by Holden and his coworkers at Battelle Memorial Institute.' The potentiality of the alloys i3s sheet-forming material was recognized, and the data reappeared in a survey of this type of titanium material.? The initial optimism was tempered by the difficulties in obtaining homogeneous 2i-Mo alloys in commercial-size ingots. The increasing need for good sheet-forming material kept investigation in this direction active, resulting in the development of a commercial alloy of this type.' This study was undertaken to obtain a clearer picture of the mechanism of stress-induced transformation in titanium. MATERIALS AND TEST PROCEDURE Three alloys were selected for this investigation: one a Ti-Mo alloy; another a Ti-Cr-Mo alloy, known to deform martensitically; and the third, a Ti-V alloy with an Ms below room temperature and an Md above room temperature, but known to contain w phase in the quenched condition. The compositions of these alloys are given in Table I. These alloys were cast as 5-lb experimental ingots, employing skull melting. The ingots were hot-forged into 1-in.-round bars. Two 72-in.-thick slices were cut from each bar for hardness testing; the remainder was cut into 0.252-in. tensile blanks. The tensile blanks and one hardness disc from each bar were heated in salt to a temperature 100°F above the 0 transus, held 2/2 hr, and brine quenched. X-ray analysis showed the pieces to be 100 pct 8.* *Omega cannot be distinguished from p by the technique employed. Tensile blanks were machined to size after this treatment. TO prevent transformation due to machining stresses, the shoulders and gage length were ground. True stress-true strain curves were

Jan 1, 1960

By D. W. Levinson, L. F. Mondolfo, N. A. Gjostein

MANY investigations are reported in the literature on the age hardening of Al-Mg-Zn alloys but most of them are concerned mainly with mechanical property changes. The present investigation was started to determine the structural changes in an AlMgZn alloy. The alloy composition was chosen in the existing phase diagram" so as to lie on the quasi-binary section Al-(AlZn)Mg Actually, it was found that the diagram as published was inexact at the lower temperatures and that the phase in equilibrium with aluminum at the lower temperatures is not the ternary compound. Technique The alloy used for the investigation was prepared from high purity materials and the resulting composition as determined by chemical and spectro-graphic analysis was: Zn, 6.17 pct; Mg, 2.13 pct; CU, 0.03 pct; Si, 0.009 pct; Fe, 0.005 pct; and the remainder, aluminum. An ingot -in. thick was cast, homogenized, hot and cold-rolled to strip 0.064-in. thick for dilato-metric and powder work, and to foil 0.005-in. thick for single crystal work. Solution treatment temperature for all specimens was 475°±5°C for periods of at least 1 hr, either in air furnaces or lead baths. Aging was done in oil or Pb-Bi baths controlled to within ±3°C. The aging was investigated at the following temperatures: room (30°), 130°, ZOO0, 260°, and 300°C. For the dilatometric study, the length changes were measured continuously, at temperature, using strips of alloy 10 in. long, shaped as channels to eliminate undesirable deflection due to bending. To compensate for thermal expansion and contraction due to the variations in the temperature of the aging baths, the dilatometers were built of the same alloy as the one being tested, with the same shape and size, but with material fully annealed. Gages on which 0.0005 in. could be read and 0.0001 in. estimated were used to measure the dilation. Length changes were also measured at room temperature. Strips approximately 10 in. long were solution-treated, quenched, and measured in a supermicrome-ter in which 0.0001 in. could be read and 0.00001 in. estimated. The specimens were immediately aged for a given time, remeasured, and then the cycle was repeated, including the solution treatment. The error of measurement with this technique was somewhat larger, but the results confirmed those obtained by continuous measurements. The sheet used for the dilatometric work was checked to determine grain orientation. Both X-rays and etching methods revealed a rather coarse grain size but only a negligible amount of preferred orientation. Thus, volume changes calculated from length changes are not invalidated by preferential orientation effects. Pieces of the sheet used for the dilatometric work were also used for the metal -lographic work. Filings for the powder X-ray study were produced from a homogenized piece of sheet. These filings were magnetically purged of iron, screened to 200 mesh, sealed in a Pyrex tube containing an argon atmosphere, and solution-treated. When quenching, the glass tube was broken, so that the powder dropped directly into cold water. After drying with alcohol, the powder was sealed into capillary tubes containing an argon atmosphere and then aged for the required times. In spite of all these precautions the three strongest lines of a( Al2o) appeared in all patterns, and were used as internal standards. By the use of these standards, accurate corrections for film shrinkage were obtained. For the back reflection patterns, annealed nickel powder was mixed with the specimen to act as internal standard. A preliminary investigation was made in small (57.3 mm diam) powder cameras. From these patterns the changes which took place in the solid-

Jan 1, 1957

By R. W. Fountain, W. D. Forgeng, G. M. Faulring

Precipitation of the phase Co3Ti (Cu3Au type) from a Co-5 pct Ti a11oy has been investigated using single-crystal X-ray diffraction techniques. Oscillation and transmission Laue patterns of specimens aged for short-time periods at 600" C indicate the formation of titanium-rich and titanium-poor zones coherent with the {100} matrix planes. Longer aging times at 600° C establish that the equilibrium phase also forms on the {100} matrix planes as platelets. These observations are corroborated by electron metallography; electron diffraction studies show the phase Co3Ti to be ordered. A probable sequence of the precipitation reaction is discussed. A previous publication by two of the present authors reported on the phase relations and precipitation in Co-Ti alloys containing up to 30 pct Ti.1 The results of this investigation established the existence of a new face-centered cubic inter metallic phase, ranging in composition from about 17.0 to 21.7 pct Ti at temperatures below 1000° C The decomposition of the fcc supersaturated solid solution was studied employing hardness and electrical resistivity measurements. The changes in hardness upon precipitation in alloys containing 3, 6, and 9 pct* Ti were found to be associated with an initial increase in hardness followed by a plateau and then a second, more pronounced hardness increase. Investigation of this behavior by electrical resistivity measurements suggested that two different kinetic processes were involved, which, when interpreted in terms of the kinetic relation,2-4 indicated that initial precipitation was in the form of thin plates. On continued aging, the plates impinged during the growth process. The general features of these findings have been confirmed by Bibring and Manenc,5 while, in addition, they report the phase to be ordered. The present investigation was undertaken to provide more definite information on the structural relationships between the precipitate and the matrix. EXPERIMENTAL PROCEDURE Single crystals of a (20-5 pct Ti alloy were prepared from the melt employing the Bridgman technique. Poly crystalline rod, 1/2 in. in diam, prepared from vacuum-melted material, was machined to 3/8- in. diam to remove any surface contamination that may have resulted from hot-working. The crystals were grown under a purified hydrogen atmosphere in high-purity alumina crucibles heated by induction. Considerable difficulty was encountered in attempting to grow monocrystals because of the high melting point of the alloy and the high solute concentration. However, one crystal about 6 in. long was obtained which was essentially a single crystal except for one or two very small grains around the periphery. The as-grown crystal was solution heat-treated for 24 hr at 1200°Cin a purified argon atmosphere and water-quenched. One-quarter-in. slices were taken from each end of the solution heat-treated crystal for chemical analyses, and the remainder of the crystal was mounted and oriented by the back reflection Laue Method. The chemical analysis of the crystal was as follows: Pct Ti Pct 0 Pct C Pct N Pct H Pet CO 5.29 0.08 0.004 0.002 0.0003 Balance By proper tilting of the crystal, it was possible to obtain slices 1/32 in. thick of [loo] and [110] orientation. The solution heat-treated crystal slices were sealed in silica capsules for the aging treatments, with titanium sponge placed at one end of the capsule to act as a getter. All slices were water-quenched from the aging temperatures, the capsules being broken under the water to ensure a rapid quench. Thinning of the slices for transmission X-ray studies was accomplished by a combination of mechanical and electrolytic techniques, the final thickness being about 0.1 mm. Laue patterns of the solution heat-treated crystal indicated that no strain was introduced by the thinning technique. ELECTRON METALLOGRAPHY After X-ray examination, the structural changes attending the precipitation were followed by examination of direct carbon replicas of polished and etched surfaces of the single-crystal slices and extracted phases. The earliest indication of significant structural change was observed after aging at 600°C The structure of a heavily etched, solution-treated crystal is shown in Fig. l(a). Aside from the etch pit pattern, no regularity of background structure is observed. On the other hand, in the background of the specimen heated for 500 hr at 600°C, the etching pattern shows a directionality indicating the influence of minute precipitate particles, Fig. l(b). On electrolytic dissolution of this specimen in 10 pct HC1 in alcohol, a large volume of very small, flattened cubes

Jan 1, 1962

By T. B. Massalski, H. W. King

An hcp phase may be induced by cold working the ß&apos; phase of the Ag-Zn system. This phase reverts to ß&apos; on subsequent aging. No phase change occurs on cold working the o phase, but ß&apos; is formed when the deformed alloy is subsequently aged at room temperature. It is concluded that for alloys near 50 at pct Zn the ordered bcc ß&apos; phase is the equilibrium structure at room temperature. WhEN the disordered bcc ß phase of the Ag-Zn system is cooled to temperatures below 258o to 274oC, it transforms to a complex hexagonal phase <o.1,2 The nature of the o ß=o transformation has been the subject of some discussion,2&apos;3 and the structure of o has been described in detail.&apos; The latter phase appears to be stable on aging at room temperature but decomposes following cold work. When alloys containing approximately 50 at. pct Zn are rapidly quenched from the 0 phase field, the ß ? o transformation may be suppressed; but the ß phase undergoes an ordering reaction (ß ? ß&apos;). The ß&apos; structure may also be obtained as a result of cold working and aging at room temperature.4 Kitchingman, Hall, and Buckley4 have suggested that the decomposition of (o following cold work proceeds in two stages, (o ? ß followed by ß ? ß&apos;, but did not confirm this by experiment. When the ordered &apos; phases in the systems Cu-Zn5 and Ag-Cd6 are cold worked, they become unstable and transform to a close-packed hexagonal phase (( ) indicating that when order is destroyed in a ß&apos; structure the close-packed hexagonal phase may in many cases be more stable. It thus became of interest to study more closely the effect of cold work and annealing on the stability of both the ß&apos; and o phases in a Ag-50 at. pct Zn alloy. Predetermined weights of spectroscopically-pure Ag and Zn, supplied by Johnson and Matthey, were melted and cast under 1/2 atm of He in transparent vycor tubing. The ingot was homogenized for 1 week at 630°C and quenched into iced brine. Since mechanical polishing was found to induce a phase change, sections were first polished at room temperature, sealed in tubes under 1/2 atm of He, reannealed for several days at 630o or 200°C and then quenched into iced brine. Sections of the alloy thus prepared were found to be homogeneous when examined under the microscope. The sample quenched from 630°C (ß -phase region) was pink in color, whereas the sample quenched from 200°C (o-phase region) was silver. The latter sample showed the characteristic hexagonal anisotropy when examined under polarized light. Filings of the alloy were examined at room temperature, after various heat treatments, using an RCA-Siemens Crystalloflex IV diffractometer with filtered CuKa radiation. The X-ray reflections from flat powder specimens quenched from 630o and 200°C and sieved through 230 mesh were recorded graphically at a scanning speed of 1/2 deg per min. The resultant patterns are shown in Figs. 1(a) and 1(b) and may be identified as those of the 8&apos; and <02 structures respectively. The lattice parameter of the ß&apos; phase was determined as 3.1566Å.* This value compares very well withthatto be expected for a 50 at. pct Zn alloy from the data of Owen and Edmunds? and indicates that no loss of Zn occurred during casting. In order to study the effect of cold work upon the ß&apos; and o phases, filings made at room temperature and sieved through 230 mesh were mounted immediately in the diffractometer-i.e., without a strain-relief anneal. Changes in structure on subsequent aging were followed by scanning repeatedly over the regions of the low index reflections of the ß&apos; and o structures-i.e. , 28 from 35 to 44 deg. Immediately after filing the 8&apos; specimen, additional diffraction peaks were observed in the low-index region of the pattern, as shown in Fig. 1(c). These additional peaks do not coincide with those of the o structure, Fig. l(b), but may be indexed as the (10.0), (00.2), and (10.1) reflections of an hcp phase (<) with nearly ideal axial ratio. However, this hexagonal phase appears to be very unstable since within a very short time at room temperature it reverts back to the ordered ß&apos; phase, the reversion being complete within seven hours. The 5 ? ß&apos; reversion reaction is, therefore, very similar to those already reported in Cu-Zn5 and Ag-Cd6 7&apos;alloys. The action of filing caused the deformed surface of the originally pink ingot to become silver in color, indi-cating that the ( phase possesses similar reflecting properties to the o phase. Hence, the subsequent

Jan 1, 1962

By R. I. Jaffee, F. C. Holden, H. R. Ogden

The mechanical properties of Ti-C and Ti-C-0 alloys can be altered by heat treatments to dissolve or reject carbon from solid solutions. The maximum strength is obtained by annealing just below the peritectoid temperature. Quenching from the ß-carbide field results in softening. Impact behavior is influenced by the extent of solution of interstitials CARBON is not as important in titanium alloys as it was in earlier years when graphite induction melting was more prevalent. With induction melting, carbon pickup is about 0.5 to 0.8 pct. Cold-mold arc melting with graphite electrodes, which is among the more current methods, results in carbon pickup of 0.1 to 0.2 pct. The titanium-sponge melting stock itself contains about 0.02 to 0.07 pct C, picked up from the magnesium used in the reduction process. Thus, carbon is still one of the more important contaminants in titanium and needs careful study and evaluation in order to understand titanium and titanium alloys. Moreover, it is equally proper to consider carbon as an alloying addition because, in controlled amounts in titanium alloys, it may serve a most useful function. This is particularly the case where the ultimate in toughness is not required. The addition of carbon to titanium results in a peritectoid-type system as illustrated in Fig. 1. The solubility of carbon is seen to be higher in the a phase than in the ß phase in the temperature range of interest. Below the peritectoid temperature, the solubility of carbon in a titanium decreases with decreasing temperature. This type of system permits many microstructural and heat-treatment variations which may influence the properties of the alloys. The study of how the microstructure variations affect mechanical properties is described in this paper. Experimental Procedures The experimental techniques and testing methods used in this work were the same as those described in detail in a previous paper.&apos; No further descriptions will be given except where changes have been made. High purity iodide titanium, produced by the New Jersey Zinc Co., was used in all of the alloys. Carbon additions were made using high purity spectro-graphic carbon electrodes in order to obtain the highest purity carbon available. The alloys were prepared by double arc melting to reduce the possibility of segregation. The alloys were forged at 875°C to ¾ in. round, descaled, vacuum annealed for 5 hr at 900°C to remove the residual hydrogen, and swaged to ¼ in. round at 750°C. All heat treatments were made on material in this initial condition. Two of the early Ti-C ingots were found to have been contaminated in melting. Vacuum-fusion analyses showed that the two contaminated alloys had picked up oxygen, so the test results on these two alloys permitted an evaluation of ternary Ti-C-0 alloys. A list of the alloys and their compositions are given in Table I. Properties of Ti-C Alloys In a peritectoid-type system, such as the Ti-C system, the chief microstructural variable which influences the properties is solid-solution strengthening. For a given composition, it is possible to control the disposition of carbon, either in solid solution or as the compound Tic, by suitable heat treatments. When in solid solution, the carbon present in the alloy makes a definite contribution to the strength of the alloy. However, when present as Tic, it has very little effect on the strength. Other microstructural variables considered in this investigation were transformation structures and grain size. As discussed in subsequent sections, these variables have only a minor effect on properties as compared to the solid-solution effect. Solid-Solution Strengthening: The principal strengthening mechanism for Ti-C alloys has been found to be solid-solution strengthening. Carbon in interstitial solid solution strengthens titanium, but has very little strengthening effect if present as the compound. Since carbon has a higher solubility in

Jan 1, 1956

By R. Taggart, J. W. Barton, G. R. Purdy, J. G. Parr

The constitution and mechanical properties of heat-treated alloys containing up to 10 pct* Ni in Ti have been investigated. The effects of quenching and of various isothermal treatments ale described, and C-curves are presented. The production of the precipitated and the martensitic hexagonal phases on quenching is discussed. MARGOLIN, Ence, and Nielsenl have determined the titanium-nickel phase diagram. A study of the transformations in gas-quenched and tempered powder specimens was made by Polonis and Parr.&apos; Some isothermal transformation work was carried out by Margolin and ~unshah, who determined transformation curves for 4 and 6 wt pct alloys, while Robinson et al.investigated the formation of the w phase in a quenched and tempered alloy, Margolin and Bunshah showed that while a martensitic transformation could be obtained on quench- ing thin sections of a 4 wt pct alloy, a 6 wt pct alloy precipitated a nonmartensitic phase. The present investigation was undertaken to obtain more information on the transformations in quenched, quenched and tempered, and isothermally transformed lump specimens of alloys containing up to 10 pct Ni. Isothermal transformation curves have been determined for 7 and 10 pct alloys and cooling curves have been obtained for quenched alloys containing up to 7 pct Ni. The mechanical properties of 2, 5, and 10 pct alloys were studied, with the object of relating properties to microstructures. EXPERIMENTAL METHODS Alloys containing up to 10 pct Ni were prepared from sponge titanium and spectrographic standard nickel by levitation-melting and chill-casting in a split copper mold. The 5 and 10 pet alloys were prepared from sponge Ti having an as-melted hardness of 115 Vpn. The other alloys were made from a sec-

Jan 1, 1961

By Robert Bakish, William D. Robertson

AFTER more than fifty years of investigation and continuing failure in service, a satisfactory mechanism to explain stress corrosion cracking in homogeneous alloys is still lacking. The relative chemical activity of grain boundaries and adjacent grains, inferred from the boundary structure, has been used to explain intergranular cracking in a brass.&apos; This concept is probably correct as a general hypothesis, but it requires much more extensive development in order to explain satisfactorily the observed phenomena. For example, the specific function of the solute in an alloy must be considered, because intergranular failure does not occur in pure metals,&apos; which are structurally similar to homogeneous alloys. Also, in this connection, an inter crystalline fracture path in binary copper alloys can be changed to a transcrystalline path by relatively small ternary additions.&apos; The fracture path in ß brass is predominantly transcrystalline,&apos; in contrast with an inter crystalline path in a brass. Whether the two different fracture paths are the result of a difference in composition, crystal structure, or the state of long range order is unknown and cannot be determined with ß brass, because only the ordered state can be obtained at room temperature. The study of chemical activity at structural sites in the Cu-Zn system is restricted by the formation of opaque films in an ammonia environment in which stress corrosion cracking is generally observed. Furthermore, both components of the alloy are chemically active and the interpretation of observations is therefore relatively complicated. The Cu-Au system is a better choice for the purpose of studying structural factors. In particular, CuAu is very susceptible to cracking in ferric chloride and opaque films are not formed in this solution; it may be obtained in different states of long and short range order; and, finally, only copper is oxidized in dilute ferric chloride, which considerably simplifies the chemical problem. To provide information necessary for a more general explanation of stress corrosion cracking in homogeneous solid solutions, the following structural factors have been investigated in a Cu-Au alloy having a composition corresponding to Cu,Au: 1) the effect of long and short range order; 2) the structural sites from which copper is removed from the annealed and cold worked polycrystalline alloy; and 3) the effect of annealing time and temperature on structural reactions in the cold worked alloy. Experimental Procedure A Cu-Au alloy of nominal Cu3Au composition was cast from cathode copper and high purity gold and fabricated into sheet and wire. Chemical analysis for copper and gold indicated 48.92 wt pct Cu and 51.01 pct Au. Quantitative spectrographic analysis indicated 0.01 pct Ag, 0.002 pct Pd, 0.001 pct Pb, and 0.002 pct Fe, with traces of magnesium, silicon, and zinc. Presumably most of the remaining 0.055 pct corresponds to the limits of analytical precision. Heat treatments of wire and sheet were conducted in argon or vacuum. Wire specimens, 0.064 in. diam, were heated for 1 hr at 850 °C to establish a definite

Jan 1, 1957

By J. T. Norton, H. Blumenthal, S. J. Sindeband

The interstitial phases formed by the transition elements with carbon, nitrogen and boron constitute a unique class of substances which are of considerable technical interest because of their well developed metallic properties and their high hardness and melting points. They are also of interest from the point of view of structure. It was pointed out by Hagg1 some years ago that the principal factor determining these structures was the relative sizes of metal and metalloid atoms. He predicted that if the ratio of the radii of metalloid to metal atoms was less than 0.59, the metal atoms would be arranged in a close-packed fashion of relatively simple type. This prediction has been amply confirmed. It appears, however, that this specification applies most generally to those structures in which the metalloid atoms occupy isolated positions in the lattice and there is no tendency for strong binding between the metalloid atoms themselves. The series of borides of the type MeB2 formed from the transition elements of the fourth (Ti, Zr) and fifth (V, Cb, Ta) groups of the periodic table provide an opportunity to investigate this situation further. If one takes as a basis the radius of 0.87 A for the boron radius and the Goldschmidt values for the metal atoms in 12 coordination, then the radius ratio varies from 0.54 for zirconium to 0.64 for vanadium, which latter is considerably greater than Hagg&apos;s limit of 0.59. It was of interest, therefore, to see if these five elements would form borides of the MeB2 type and have simple isomorphous structures. When this investigation was initiated, relatively little information had been published on the structure of this group of borides. McKenna2 reported the preparation of ZrB2 by a carbon reduction process. Its structure was hexagonal and the approximate lattice constants were given as a = 3.15 A, c = 3.53 A. Ehrlich3 reported the structure of TiB2 as being of the C 32 type with a = 3.02, c = 3.21 and c/a = 1.06 A. Recently, Kiessling4 published the results on ZrB2, showing it to be one in which the metal atoms are arranged in a simple hexagonal lattice with the boron atoms in flat sheets, midway between the layers of metal atoms. The structure is C 32 type with a = 3.169, c = 3.530 and an axial ratio =1.11 A. He also states that CbB2 and TaB2 are isomorphous with ZrB2. Preparation of Borides The borides of titanium, zirconium, columbium and tantalum were made by the electrolysis of fused salt baths after the method described by Andrieux.5 The bath, totalling about 6500 g in each case had the following general composition: Metal Oxide + B2O3 + CaO + CaF2. The actual proportions of the ingredients were determined for each individual case. Although Andrieux reports the preparation of vanadium boride by the same electrolytic method, several attempts proved unsuccessful. However, it was possible to prepare VB2 by the carbon reduction method used by McKenna to produce ZrB2. The mixture consisted of V2O5 + 6B2O3 + 11C and the reduction was carried out in an induction heated graphite crucible. This method proved satisfactory for ZrB2 and TiB2 and undoubtedly the others could be made in the same way. The borides, which were all in the form of fine gray metallic crystals from the electrolytic bath or gray powders from the reduction process, were carefully separated from other constituents and analyzed chemically for metal and boron content. The densities of the boride powders were measured using a standard 10 cc pyenometer at 18°C and ethyl benzene proved to be the most satisfactory liquid for this purpose. X Ray Technique The boride crystals, as prepared, were too small for single crystal examination so that powder techniques were employed. Patterns of the finely ground borides were prepared, using the Norelco recording X ray spectrometer. The lines on these patterns were indexed with the aid of Hull-Davy charts and the approximate dimensions

Jan 1, 1950

By C. S. Smith, K. K. Ikeuye

In an earlier paper1 one of the authors called attention to the significance of the relative free energies of grain boundaries and interphase boundaries in alloys in determining the shape and distribution of micro-constituents. The ratio of the interphase and inter-crystalline boundary energies (that is, —?12, where ?12 is the energy of the interface between a crystal of phase 1 and a crystal of phase 2, and ?11 is the energy of the boundary between two crystals of phase 1) will be denoted by F. It is this ratio that determines, by the simple triangle of forces relation, the dihedral angle, ?, of phase 2 where it adjoins a boundary between two grains of phase 1. On a metallographic sample various angles are actually obtained because of the random orientation of the plane of observation, but the statistically most frequent angle is the true one. These basic principles were discussed in detail in the earlier paper. The experiments described below show the effect of both composition and temperature on ? and T for some alloys containing a liquid phase, and provide data on the rate of approach to the equilibrium angles in both solid and liquid phases. All the alloys were melted in a graphite crucible and cast into ingots 3/4 by 11/8 in. cross-section. Some of the aluminum alloys consisted of two immiscible liquids from which uniform castings could not be obtained. The amount of liquid phase varied locally to a considerable extent and the analyses were meaningless. Nevertheless, the composition of the liquid would not differ from that in an alloy of the intended gross composition, and the synthetic composition of the alloys was therefore used in considering the surface energy results. The ingots were given initial deformation by cold-rolling to 50 pct reduction, annealed, and given a second 50 pct reduction prior to cutting into small samples for heat treatment at the times and temperatures subsequently reported. The resulting micro-samples were carefully prepared metallographically and examined at magnifications of 650, 1280, or 2500. The objectives used were 21X, 0.40 NA (dry); 41X, 0.65 NA (dry); and 80X, 1.40 NA (oil emulsion). The appropriate angles were measured by rotation of the stage of a Bausch and Lomb metallograph to align the appropriate boundaries successively with a cross-hair in a micrometer eyepiece. About 250 angles were measured on each phase. Though the angles were read to 1°, the accuracy is probably not above 3°, because of uncertainty in setting the cross-hair tangent to the sometimes curved boundary. The corners of very small particles, particularly in early stages of adjustment after cold-rolling, were difficult to measure and the results were slightly dependent on the magnification used (compare Fig 1-C and 1-D). With particles of larger size and more nearly equilibrium shape, magnification made no difference (vide Fig 1-F and 1-G). The measured angles were grouped in 10° intervals (5° if ? was less than 20°) and plotted in bar

Jan 1, 1950

By G. K. Manning, A. R. Elsea, C. R. Simcoe

Boron increases the hardenability of hypoeutectoid steels by decreasing the nucleation rate of ferrite and bainite. It is postulated that concentrations of lattice imperfections, such as exist at the grain boundaries, furnish the necessary energy for nucleus formation. Boron, because of its atomic diameter, will concentrate at lattice imperfections where sites of suitable size are present. Boron will decrease the energy of these local areas by occupying these sites. This mechanism accounts for the large increase in hardenability observed with small amounts of boron. The loss of the boron hardenability effect and the boron precipitate formation are explained on the basis of increased concentration of boron at the grain boundaries either with increasing boron content of the material or with increasing temperature. COMMON alloying elements affect both the nucleation and growth rates of the austenite decomposition reactions.&apos; This effect is largely a result of the slow diffusion rates of these elements. Although a small addition of boron markedly increases the hardenability of steel, the diffusion rate of boron, which is of the same order of magnitude as that of carbon, can hardly account for this effect. An addition of boron in the range of 0.001 to 0.003 pct is about as effective as an addition of 0.30 pct Mo, 0.40 pct Cr, or 1.25 pct Ni in increasing the hardenability of a 0.40 pct C steel;&apos; however, increasing the carbon content of the steel decreases the effectiveness of the boron addition."&apos; The difficulty in understanding why so small an addition of boron can replace much larger quantities of the more strategic alloys, together with the erratic behavior sometimes encountered in boron-treated steels, has interfered with their general acceptance by industry. In the belief that an understanding of the mechanism by which boron increases the hardenability of steel should lead to a more general acceptance of boron-treated steels, a research investigation to determine this mechanism was undertaken at Battelle Memorial Institute under sponsorship of Wright Air Development Center. Experimental Work In order to study the effect of boron on the transformation of austenite to ferrite and bainite, a group of steels was made with a basic composition similar to that of the SAE 8600 series. This base composition was chosen because it has sufficient hardenability to permit accurate measurement of the times required for transformation to start at various temperatures. The chemical analyses of the steels used in the first part of this investigation are listed in Table I. These steels were made as 200 lb heats in an induction furnace. The furnace charge was Armco ingot iron with the alloying elements added as ferroalloys. After the alloy additions were made, the heat was deoxidized with 0.125 pct Al. A 100 lb ingot was cast and an addition of 0.003 pct B, as ferroboron, was made to the metal remaining in the furnace. This metal was cast into a second 100 lb ingot. The ingots were forged to 11/4 in. diam bar stock from which end-quench hardenability specimens were obtained. Part of this material was further reduced by hot rolling to lx¼ in. bar stock from which specimens were obtained for isothermal transformation studies. Studies of Nucleation and Growth: End-quench hardenability tests were performed on these steels, using an austenitizing temperature of 1600°F. The hardenability curves, shown in Fig. 1, indicate that boron treatment resulted in considerable increase in hardenability of the steels. Any such change in hardenability must result from a change in the transformation rate of the austenite, and these rate changes can be established readily by isothermal transformation studies. Isothermal transformation studies were conducted on these steels as follows: specimens were austeni-tized at 1600°F for 15 min, transferred to a lead bath operating at a constant subcritical or intercritical temperature, held for various lengths of time, and water quenched. The specimens were sectioned for metallographic examination to determine the amount and the type of transformation products present. In order to determine the effect of boron on the formation rate of ferrite, isothermal transformation tests were made on the 0.20 pct C steel in both the boron-treated and boron-free condition at an intercritical temperature of 1375°F where ferrite is the only decomposition product of this low carbon austenite. The results of these tests are shown in Fig. 2, where the percentage of ferrite formed is plotted as a function of time at temperature. It is apparent that boron markedly decreased the transformation rate of austenite to ferrite at this temperature.

Jan 1, 1956

By W. Ivanick, Frank W. Glaser

ORDERING reactions of Fe-Si compositions in the a region have been mentioned in a number of review articles.7-8 However, little is known in regard to the critical temperature, T at which this transformation takes place. Greiner and Stoughton,&apos; in a study of the constitution of iron-rich Fe-Si alloys below 800°C, placed the onset of order at a composition of about 4 to 5 wt pct (7.5 to 9.5 atomic pct) Si. They observed that at this composition the ductility and strength begin to decrease sharply and brittleness develops. During X-ray studies they observed only the appearance of superlattice lines for compositions containing 12.5 atomic pct Si. More recent X-ray diffraction studies- etected the appearance of superstructure lines (corresponding to the calculated positions of [Ill] and [ZOO] reflections) for alloys containing 9.5 atomic pct. This fact confirms Greiner and Stoughton&apos;s original hypothesis in regard to the onset of order at compositions containing about 7.5 to 9.5 atomic pct Si. The physical properties.of Fe-Si alloys containing more than 10 atomic pct Si have been studied only to a limited extent. Their extreme brittleness and difficulties of sample preparation render them of little industrial use in comparison with alloys in the 0 to 10 atomic pct Si range. The properties of Fe-Si alloys reported to date are mostly properties measured at room temperature on ordered compositions It appears that because of experimental difficulties fully disordered alloys could not be produced in the critical composition ranges and their properties could therefore not be reported. In Figs. la, lb, and lc, a summary of physical properties of Fe-Si alloys, measured during recent investigations of the influence of silicon additions to iron, is presented. No mention of determination of the critical temperature, T for disorder could be found in the literature. The following is an account of work done in an attempt to: 1) produce the disordered state of various Fe-Si alloys and establish the critical temperature, T for disordering, and 2) compare the electrical and thermal conductivity characteristics of the ordered and disordered phases as functions of composition. Materials, Preparation of Test Samples, and Testing Methods Fe-Si alloys with high silicon contents (about 10 atomic pct) are usually prepared using powder metallurgy techniques. This method insures accurate compositions and high purity through the use of protective atmospheres during solid state diffusion alloying of the mixed powders."" Iron and silicon powders were mixed in the desired proportions, cold or hot pressed, and then homogenized at 1150°C for periods ranging from 6 to 12 hr under a protective getter and in a hydrogen atmosphere. Fully homogenized samples were quenched in water from various and successively higher temperatures to establish the critical temperature for disorder. Temperatures were determined using Pt—Pt-Rh thermocouples in contact with the test samples. Test bars were approximately 0.6x1.25x7.5 cm. Electrical measurements were made at room temperature by determining the potential drop over a 1.5 cm span for a current of 10 amp. Densities of the samples were determined by immersion. High temperature electrical resistivities were measured using previously described techniques.&apos;" Specific heat conductivity up to 200°C was measured by heating one end of the test bar and water-cooling the other; heat conductivity was then obtained by subtracting the rate at which heat entered the water from the

Jan 1, 1957

By S. L. Craig, C. Orr, H. G. Blocker

WITHIN recent years gas adsorption methods have been developed for measuring the surface area of finely divided materials and have become extremely valuable in research on the corrosion and the catalytic activity of metals. Rather elaborate apparatus is required, and a single determination is so time-consuming that these methods have not been utilized to the fullest extent; the methods are un-suited for most routine control work such as that encountered in powder metallurgical operations and in processes employing metal catalysts. These difficulties are largely eliminated, and surface area is reduced to a routine determination if the liquid-phase adsorption of a surface-active agent such as a fatty acid can be used. When the affinity of the fatty acid carboxyl group for the solid surface is greater than its affinity for the solvent, a unimolec-ular layer of orientated fatty acid molecules will be formed at the solid-liquid interface in a manner similar to that of a compressed fatty acid film on a water surface. The measurement of surface area is then reduced to a measurement of fatty acid adsorption. This propitious circumstance, first investigated by Harkins and Gans,¹ has been employed with somewhat inconclusive results by a number of investigators in evaluating the surface properties of metals, metal catalysts, and metal oxides. The specific surface area values for nickel and platinum catalysts, determined from the adsorption of a number of fatty acids from various solvents, were found by Smith and Fuzek² to agree with values calculated by the gas adsorption technique of Brunauer, Emmett, and Teller," he so-called BET technique. And recently Orr and Bankston4 have also reported good agreement between nitrogen gas and stearic acid adsorption results in the measurement of the surface areas of clay materials. On the other hand, Ries, Johnson, and Melik5 found only order-of-magnitude agreement between these two methods in studying supported, cobalt catalysts having specific surface areas as great as 420 sq m per g; the reason is partially attributable to the very porous nature of the materials. Greenhill,6 investigating the adsorption of long-chain, polar compounds in organic solvents on a number of metal powders, concluded that a uni-molecular layer of stearic acid was formed on exposure of the solid to the acid solution and that the presence of an oxide or another film did not alter this result. Furthermore, the adsorption process appeared to be the same whether or not the sample was degassed prior to exposure to the solution. Greenhill estimated the surface area of one of the powders he investigated from microscopic diameter measurements, and obtained a rough check with surface area evaluation. Russell and Cochran7 found moderate agreement for alumina surface area results by fatty acid and gas adsorption methods. In addition, they also found that the prolonged heating and evacuating pretreatments previously used by investigators were unnecessary. The present work, however, considerably extends these previous investigations, shows that fatty acid adsorption can be used to determine the surface area of a variety of metals and metal compounds, offers further confirmation of the correctness of gas adsorption methods, and presents a simplified technique for the determination of the metal surface area which is suitable for routine work. Experimental Technique Basically, the fatty acid adsorption method is quite simple. It consists of exposing a sample of the material of which the surface area is desired to a fatty acid solution of known concentration. By analysis of an aliquot of the solution, the concentration after adsorption has occurred may be determined. The difference between the initial quantity of acid in solution and the final quantity is that quantity of acid adsorbed by the sample. The specific surface area of the adsorbent material may be calculated from the quantity adsorbed and the weight of the sample. In agreement with the findings of others as outlined above, it was found entirely unnecessary to degas or pretreat the nonporous materials employed other than by drying them thoroughly. However, precaution was necessary so that the dried sample entered the fatty acid solution with little exposure to moisture. The effect of moisture on the interaction of stearic acid with finely divided materials has been thoroughly investigated by Hirst and Lancaster." They found the presence of water merely reduced the amount of acid adsorbed by powders such as TiO2, SiO2, Tic, and Sic. With reactive materials such as Cu, Cu2O, CuO, Zn, and ZnO, however, water was found to initiate chemical reaction. Only with ZnO was reaction observed when the solid and the solu-

Jan 1, 1953

By G. R. Speich

RECENT studies by Smith and Olney,1,2 Olney,3 Greifer and Salli,4 Rys etal., and Olney and smith 6 have established that graphite is the first decomposition product to format the surface of hypereutectoid plain-carbon steels when they are austenitized in a vacuum or inert atmosphere and slowly cooled. This graphite evidently forms directly from the austenite and only at the surface of the specimen. The interior of the specimen is found to be free of graphite. The graphite layer can almost completely cover the specimen surface and the rate of its formation is markedly sensitive to the orientation of the austenite. The present work was undertaken to study this phenomenon further, especially with regard to the effect of temperature and austenite orientation. The material studied in this work was a high-purity iron-carbon alloy containing 0.88 pct C, 0.005 pct Mn, 0.016 pct Si, 0.005 pct S, and 0.002 pct P. Specimens were heat-treated in a commercial hot stage modified for rapid quenching.7 This permitted direct observation of the formation of the surface graphite. A vacuum of 10"" to 10-5 mm of Hg prevented oxidation or decarburization of the specimens. Specimens were austenitized for 30 min at 1100°C and quenched to a series of lower temperatures where they were isothermally transformed. Surface graphite was observed to form at 700°, 750°, and 780°C but not at 825°, 900° or 1000°C. Since the maximum solubility of austenite for graphite is 0.88 pct C at 800°C,8 surface graphite only forms at tem-

Jan 1, 1962

By F. H. Buttner, H. Udin, J. Wulff

Using a modified Udin, Shaler, and Wulff technique, the surface tension of gold Udin, purified helium was found to be 1400 ± 65 dynes per cm for the temperature range 1017° to 1042°C. IN the original Udin, Shaler, and Wulff technique for measuring the surface tension of copper: variously weighted wires were allowed to extend or contract in a copper cell held at elevated temperatures in vacuum. By plotting stress vs. strain for a wire array in one test, the stress at zero strain is obtained. This is the point where the contractile forces resulting from surface tension are balanced by the applied load, according to the expression: y = e=o r [1] where y is the surface tension in dynes per cm; a,,,, the stress at zero strain in dynes per cm; and T, the radius of the wire in cm. The assumption that the wires deform viscously permits the drawing of a straight line through the points on the stress-strain plot. Justification of the assumption has received further experimental support recently.&apos;-&apos; The presence of grain boundaries in the wires requires a correction to the original expression used." Thus: y = d4=T [l- (dl) (ar)Y1 [2] where, n/l is the number of grain boundaries per unit length, and a, the ratio of grain boundary tension to free surface tension. Alexander, Kuczynski, and Dawson in studying the creep of gold wire in vacuum were unable to obtain reproducible values of the surface tension of gold. In plotting stress vs. strain for progressively longer times, they found that the stress at zero strain drifted with time from positive stress values to negative values. Similarly, for the surface tension of silver, reproducible values were obtained only when a purified helium atmosphere was substituted.&apos; Evidently the evaporation rate of silver in vacuum is too high at the temperatures employed to obtain solid-gas equilibrium even in a similar metal enclosure. Thus reproducibility of results is lost. Experimental Procedure The experimental procedure was much the same as that originally developed by Udin, Shaler, and Wulff with a few modifications and improvements. For greater accuracy in strain measurements, knots gave way to cut gage marks as shown in Fig. 1. These were made with a hand-driven lathe in which razor blades serv&apos;ed as cutting tools. Also a more precise cathetometer with a screw accurate to 0.00015 cm was used. The tests were conducted in an atmosphere of purified .helium rather than in vacuum in order to avoid possible evaporation difficulties. Five mil wire of high purity gold (99.98 pct) was used. After cutting in the gage marks, each wire of a series of about 12 was differently loaded by welding a gold ball to one end. This was done by dipping the end of the wire in a cooling gold droplet, previously melted on a charcoal block with a No. 2 acetylene torch. The other end of the wire was strung through a hole in a gold lid and twisted over the edge to hold the wires fixed and in suspension from the lid. The lid and mounted wires were then dipped in pure ethyl alcohol to dissolve any skin oils and dirt on the surface of the wires due to handling. Finally the lid was put in place on an alundum crucible lined with gold so that the wires hung freely within the gold-lined chamber. This whole assembly was next heated in a quartz nichrome wound tube furnace and heated for a few minutes at 600°C to soften the wires. After this anneal the wires were easily straightened with tweezers. The wire assembly was finally annealed 10" to 25°C above the subsequent test temperature for 2 hr. This treatment allowed the grains to grow to equilibrium size and shape. After the anneal, the lid was mounted in front of the cathetometer. The gage length was measured by sighting the 40 power microscope on the upper lip of the lower gage mark for the first reading, then traveling up to the lower lip of the upper gage mark for the final reading. This procedure was repeated four times to give an average gage length value. In this manner the annealed gage length and the final gage length could be measured to determine the strains. During all measurements, grain counts were made.

Jan 1, 1952

By J. J. Pye, J. B. Drew

The surface-diffusion coefficients of Ni63 diffusing on low-index planes of nickel single crystals have been measured over the temperature range from 400° to 1000°C using a precision autoradio-gvaphic technique. The activation energy for sur -face diffusion appears to he the same on the {111}, {110), and (100) planes and amounts to -0.60 ev. This is in good agreement with the value (-0.62 ev) reported for (111) planes obtained by mass-transport techniques. In an earlier paper, the authors have reported self surface-diffusion coefficients on silver.&apos; In that work, a deviation of the diffusion coefficients from linearity in the Arrhenius plot was observed at high temperatures. This effect was attributed to a loss of tracer atoms into the bulk by volume diffusion. The purpose of the present work was to extend the technique developed to the nickel surface-diffusion system up to the point where volume diffusion would come into play. The nickel system especially lends itself to this technique due to the high efficiency of the isotope in darkening the film and the large absorption of the weak radiation (0.063 mev /3- particle of the trapped tracer atoms. The diffusion coefficients and ictivation energy for different orientations on nickel can also be compared with a report published by Blakely and Mykura 2 where a mass-transfer technique was used. This paper reports the self surface diffusion of nickel on the low-index planes over a wide temperature range using a precision autoradiographic technique. EXPERIMENTAL PROCEDURE The experiment is similar to that described in the earlier publication consisting of a radioactive needle as a source resting on a flat, smooth, chemically polished surface annealed in a dynamic dry-hydrogen atmosphere. The needle is held snugly on the surface by a holder fabricated from commercially pure nickel. The point source is made by grinding down a small-diameter nickel rod until a tip of approximately 0.1 mm radius is formed. It is then etched and the needle tip plated with the radioactive isotope Ni63. Nickel single crystals were used whose main impurities were spectrographically determined as Co 0.05, Fe 0.007, C 0.005, and S 0.003 pct. The surfaces, oriented to within 1/2 deg of the low-index planes, were carefully mechanically polished and etched in a 50-30-10-10 hot solution of acetic, nitric, sulfuric, and phosphoric acids giving a smooth polished surface. The crystals were then washed in distilled water and alcohol. Annealing temperatures ranged from 400° to 1000°C with a furnace arrangement in which the crystals could be brought up to temperature in times short compared to diffusing times. The temperature was maintained constant to ±10°C. In the temperature range investigated, the ratio of the surface-diffusion coefficient to the volume-diffusion coefficient (Ds/Du) was 105 or more and the mean bulk-penetration values, calculated from literature values of volume-diffusion coefficients,3 were on the order of 10-5 cm. After the diffusion anneal, the sintered needle is removed, and both the radius of the needle point and spot left on the crystal face are measured. The crystal is then placed on photographic film. Diffusion profiles are obtained by scanning the film with a recording microdensitometer which has a slit width of 10µ. DISCUSSION AND RESULTS The experimental conditions are such that the source strength and needle radius are essentially constant and the time is adjusted such that the mean bulk penetration is small. An exactly analogous heat-flow problem has been considered by Carslaw and Jaeger4 and the solution can be written in integral form as:

Jan 1, 1964

By H. I. Aaronson, C. Wells

Configurations of ferrite crystals have been found in a plain carbon steel which appear to have resulted from the nucleation of new ferrite crystals at the interphase boundaries of previously formed crystals despite the high carbon concentrations which necessarily develop at these boundaries. This phenomenon has been termed sympathetic nucleation. An attempt has been made to reconcile the occurrence of sympathetic nu-cleation with current nucleation theory. THIS investigation is one of a series on the formation of proeutectoid ferrite from austenite. From the viewpoint of chemical composition, this reaction consists of the nucleation and diffusional growth of crystals of carbon-poor ferrite within a matrix of carbon-rich austenite. The austenite adjacent to the austenite-ferrite boundaries will be greatly enriched in carbon, approximately to the value of the y/(a + y) equilibrium curve or its metastable extrapolation at the temperature of transformation. Those areas of austenite appreciably farther removed from the growing ferrite, on the other hand, will be relatively unaltered in composition, especially at the earlier stages of transformation. Since rates of nucleation are considered to decrease exponentially with decreasing supersaturation,&apos; the frequency with which ferrite nuclei appear at austenite-ferrite boundaries should be negligible in relation to that at which they form in other regions of the austenite. During this investigation, however, many groupings of ferrite crystals have been found which appear to have resulted from the nucleation of ferrite at austenite-ferrite boundaries. This phenomenon has been given the name of sympathetic 71.1tcleation. A number of micrographs of morphological configurations caused by sympathetic nucleation will be presented, after which an explanation for this reaction will be proposed in terms of current nucleation theory. Some of the structures to be considered are composed of bainite, an aggregate of ferrite and carbide, rather than of ferrite. Since ferrite and bainite differ only in that bainite forms under conditions which result in the nucleation of carbides behind the advancing austenite-ferrite boundaries,&apos; it will usually be unnecessary, for the purpose of this paper, to distinguish between the two reaction products. All studies were performed on an electric furnace steel (obtained from the Vanadium Alloy Steel Co.) containing 0.29 pct C, 0.76 pct Mn, 0.25 pct Si, 0.005 pct P, and 0.007 pct S. The alloy was cast as a 150 Ib, 7x7 in. cross section ingot and forged into bars 2x2 in. in cross section. These bars were homogenized for 48 hr at 1250°C in an Endo-Gas atmosphere. The depth to which decarburization penetrated during this heat treatment was determined by chemical and microscopic analyses and the affected metal was removed by machining. Specimens for isothermal transformation studies were cut from the remaining material; most of these specimens were 1/2x1/4X1/16 in., though some with a thickness of 1/32 in. were prepared for use at the shorter reaction times and lower reaction temperatures. Specimens were austenitized for 30 min at 1300°C, isothermally reacted for various times at temperatures ranging from 775" to 475 "C, and then quenched in iced water. The austenite grain sizes within individual specimens ranged from ASTM Nos. 1 through —4. A commercial heat-treating salt which was continuously deoxidized by an immersed graphite crucible served to minimize the loss of carbon during austenitizing; thick covers of powdered graphite and immersed graphite rods effectively prevented decarburization in the lead pots employed for the isothermal reaction treatments. The heat-treated specimens were sectioned and mounted in Bakelite. Following the completion of standard grinding and mechanical polishing procedures, the specimens were electrolytically polished with a Buehler-Waisman apparatus and etched in 2 pct nital. Experimental Results Rules of Evidence for Sympathetic Nucleation—On the basis of observations made on a single plane of polish, one precipitate crystal may be considered to have been sympathetically nucleated at the inter-phase boundary of another precipitate crystal when the following conditions are fulfilled: 1) The sympathetically nucleated crystal is not in contact with a grain boundary or a subboundary in the matrix phase. 2) The shape, size, and location of the crystal at whose boundary sympathetic nucleation occurred (hereafter termed the base crystal) and the crystal formed by sympathetic nucleation substantially pre-clude the possibility that the plane of polish em-ployed may have concealed the fact that both crys-tals actually nucleated at a grain boundary or a sub-boundary in the matrix phase.

Jan 1, 1957

By David Moskowitz, Ira Binder, Robert Steinitz

THE hard refractory borides of the transition elements of the 4th, 5th, and 6th groups of the Periodic System have been the subject of a number of recent investigations.&apos;-&apos; It is well known now that most of these elements form several different borides, and Kiessling8 has summarized the rules which govern to some extent the arrangements of the boron atoms in the various structures. Melting points of a few borides have been published." The systems Fe-B, Ni-B, and Co-B have been reported," but, as these borides are rather low melting, they are outside of the groups of boron compounds considered here. Brewer&apos; has tested the stability of various borides and estimated a number of eutectic temperatures between different borides, but in no case was the complete system of a transition metal and boron investigated. The phase diagram becomes of special importance if the preparation of the borides from the elements in powdered form is considered; the lowest eutectic temperature will determine the first appearance of a liquid phase. Also, the knowledge of high temperature phases, if they exist, is important for the preparation of bodies from these borides by hot pressing or sintering. During the investigation of various metal borides,7 it was found that there were more boride phases existing in the Mo-B system than reported by Kiessling." They occur, however, only at temperatures above 1500°C and were, therefore, not found by him. This led to a study of the equilibrium diagram of the Mo-B system. ranging from 0 to 25 pct B and from room temperature to the liquidus. Part of this investigation was reported during the "Research in Progress" session at the 1952 Annual Meeting of the AIME.11 Raw Materials and Preparation of the Borides The raw materials used were commercial molybdenum and boron powder, both supplied by the Molybdenum Corp. of America. The molybdenum powder was 99+ pct pure? while the boron powder contained about 83 to 85 pct B. A large percentage of the impurities in this powder was oxygen, with the rest formed by iron, calcium, and unknown substances. The low purity of the boron used was, however, not considered detrimental to the final product, as most of the impurities evaporated at the high temperatures at which the borides were formed. The final product always had a minimum purity of 96 to 98 pct (figured as molybdenum and boron), with carbon, iron, and probably oxygen being the remaining products. Carbon is usually present as graphite. The chemical analyses always confirmed the compositions which corresponded to the crystallographic structures as determined by X-ray diffraction, and the boron content of the finished product agreed closely with that of the starting mixture; no boron was lost during the boride preparation. The chemical analysis methods employed for molybdenum and boron were previously described by Blumenthal.12,13 The powders were mixed by hand in the desired proportions, compressed at room temperature under low pressure, and then heated under hydrogen to about 1500" to 1700°C in a graphite crucible to form the borides. Usually, the three well-known borides Mo,B, MOB, and Mo,B,, which are stable at room temperatures, were prepared in this way, and all other compositions were made by mixing these borides in various ratios or by the addition of molybdenum or boron powders for the very low or very high boron contents. Preparation of two-phase compositions directly from the elemental powders was tried only occasionally to check whether equilibrium could be reached in this way. Experimental Procedures The stable borides were mixed in the desired ratios and heated under hydrogen in graphite crucibles to various temperatures. The well insulated crucibles were heated in a high frequency induction furnace. Special care was taken to obtain exact temperature measurement, which proved much more difficult than originally anticipated. It is believed that individual temperature measurements have an error of less than ±25ºC, while melting or transformation temperatures are accurate within ±50°C. The temperatures were measured with an optical pyrometer which was aimed at the closed end of a graphite tube extending down into the crucible. close to the samples. Attempts to measure directly through the hydrogen exit stack failed. The crucible arrangement is shown in Fig. 1. Heating was done at a slow rate to be sure that the temperature inside the crucible was uniform. The specimens were kept at the final temperature for about 30 min. For the investigation of high temperature phases, some samples were quenched. They were heated, without atmosphere protection, in a very small graphite crucible which could be rapidly removed from the high frequency coil, and dropped into water. These quenched samples were afterwards annealed to establish the equilibrium at lower temperatures. The melting points or the positions of the solidus and liquidus lines were determined by heating the specimens to various temperatures and examining them at room temperature for evidence of a liquid phase. These results were checked later on by thermal arrest curves, especially to determine the exact position of the eutectic temperature line. For this purpose about 200 g of the boride were melted in a graphite crucible, in an arrangement similar to Fig. 1. Slow cooling was assured by very good

Jan 1, 1953