By W. C. Leslie

The textures of cold-rolled and of annealed iron are compared with those of an iron-0.8 pct copper alloy in which the amount of precipitation after cold rolling was controlled. Previously published pole figures -for cold-rolled and for annealed iron are confirmed. The effects of precipztatiotz after cold rolling are to retain the cold-rolled texture after annealing, to inhibit the formation of the usual allnealing texture, and to produce elongated recrys-tallized ferrite grains. It is suggested that the inhibition of new textures by precipitation after cold rolling is a general phenomenon. A great deal of attention has been paid to the development of texture during the secondary or tertiary recrystallization of ferritic alloys, but very little work seems to have been done on the control of texture during primary recrystallization. If such control were attained, it might be possible to simplify the processing of oriented materials or to change the characteristics of current cold-rolled and an-nealed products. From previous experience, it seemed likely that texture could be controlled by recrystallizing a supersaturated solid solution. Green, Liebmann, and Yoshidal found that the formation of preferred orientation in aluminum (40 deg rotation about <111> relative to the deformed matrix) was inhibited when iron was retained in supersaturated solid solution in the strained aluminum. The authors attributed this inhibition to iron atoms in solid solution. There is, however, an alternative explanation. Green et al, took a highly supersaturated solution of iron in strained aluminum and heated it to an unspecified temperature for recrystallization. It is probable that precipitation occurred prior to and during recrystallization, and it is proposed that the inhibiting agent is this precipitate, rather than the iron atoms in solid solution. It is important to note that precipitation before cold work is ineffective; the effective precipitate is that formed after cold working and either before or during recrystallization. The location and distribution of the precipitate are critical. Precipitation in such a manner has been found to have profound effects upon kinetics of recrystallization and the microstruc-ture of the recrystallized alloys.2-4 It would be surprising, indeed, if this were accomplished with no change in texture. Because of the relative simplicity of the system, and because of previous experience,4-7 it was decided to determine the effect of precipitation on texture in an alloy of iron and copper. Bush and Lindsay5 found an unspecified change in texture in cold-rolled and annealed low-carbon rimmed steel sheets when the copper content exceeded 0.1 pct. MATERIALS In earlier work, the rate of recrystallization of a low-carbon steel was greatly decreased by 0.80 pct copper, and, after the proper treatment, the recrystallized ferrite grains were greatly elongated.4 Accordingly, it was decided to investigate the effect of precipitation on texture at this level of copper content. The iron and the iron-copper alloy were made from high-quality electrolytic iron and OFHC copper, vacuum-melted in MgO crucibles, cast, hot-rolled to 0.2 in., then machined to 0.150 in. The compositions are given in Table I. The plates were heated to 925°C and brine quenched, twice. This produced a ferrite grain size of ASTM 0 in the iron and ASTM 1 in the Fe-Cu alloy. Disk specimens were cut from the heat-treated plates, repeatedly polished and etched, then used to determine (110) and (200) pole figures by reflection. Despite the complication of large grain size, these pole figures strongly indicated a random texture. PROCEDURES The copper content in solid solution in ferrite before cold rolling and recrystallization, and hence, the amount that could precipitate during the recrys-tallization anneal, was controlled at three levels by heat treatment. The specimens as quenched from 925° C were presumed to have all the copper, 0.80 pct, in solid solution. Other samples of the quenched alloy were aged 5 hr at 700°C to retain about 0.5 pct Cu in solid solution.6 A third set of quenched specimens was reheated to 700°C, then slowly cooled in steps, to reduce the amount of copper in solid solution to a very low level. All specimens were cold-rolled 90 pct, from 0.150 to 0.015 in. thick. The rolling was done in one direction only, i.e., the strip was not reversed between passes, with a jig on the table of the mill to keep the short specimens at 90 deg to the rolls. The rolls were 5 in. in diameter and speed was 35 ft. per min. Machine oil was used as a lubricant. In a supersaturated alloy, the maximum effect of the copper precipitate on microstructure and on recrystallization can be developed by a treatment at 500°C, after cold rolling and before recrystallization.&apos;

Jan 1, 1962

By E. P. Klier, Jane Jellison

The course of the transformations on cooling in a series of Cu-A1 alloys has been followed by means of thermal analysis, X-ray diffraction, and optical metallogrAphy. Specimen size was found to have a pronounced effect on the time of completion of the pearlite transformation due to modification in the unmber of nuclei. The ordeving transformation zvas observed for all cooling rates for all alloys studied, and is considered insuppvessible. At intermediate cooling&apos; rates, a transitional struchire for 011 alloy compositions and based ox the bainite reaction was observed. The alloys of aluminum and copper possess a eu-tectoidal region at from about 9.4 to 16 pct Al. Above the critical temperature, the disordered bcc phase, 0, is stable. At subcritical temperatures, the 0 phase decomposes under equilibrium conditions into the stable phases, a and y,. At the eutectoid composition, these phases develop a lamellar pearlite structure, in appearance much like that found in steels. During rapid quenching from supercritical temperatures, the diffusion processes required for the formation of the equilibrium phases are suppressed, and the 0 transforms to an acicular martensitic phase, designated B or y&apos; depending on the aluminum content, or to a mixture of the two. Early investigators of this system concentrated on determining the equilibrium phase diagram, &apos;&apos;&apos; the structure of the equilibrium phases,3 and later the isothermal decomposition of the 0 phase at subcritical temperatures, or the decomposition of the martensite on tempering. Other work which treated the nonequilibrium transformations concentrated largely on the martensite transformations and the structure of the b and y&apos; phases.15"17 Since the pearlite and martensite transformations in this system resemble those in steels, the one being formed by nucleation and growth of adjacent lamellae of the equilibrium phases, and the other by a diffusionless, shear-type transformation, the present study has been undertaken to investigate the structures formed on continuous cooling, with the objective of constructing cooling transformation diagrams analogous to those derived for alloy steel systems. In particular it was desired to determine whether parallels between the A1-Cu and iron-iron carbide systems on continuous cooling extended to encompass the intermediate phase, namely the bainite structures, which form by a combined martensitic-diffusion mechanism,&apos;&apos; but which are supersaturated with respect to the equilibrium phase upon which their crystal structure is based. To this end the transformations in representative alloys of the Cu-A1 B eutectoid system have been followed, using the methods of thermal analysis, X-ray diffraction, and optical microscopy. EXPERIMENTAL PROCEDURE Materials. The materials tested were those used by Klier and Grmko 5 in their study of the isothermal decomposition of these alloys. The alloys were melted in graphite crucibles and chill-cast into 5 by 2 by 1/4 in. ingots. The ingots were then hot-rolled to sheets 1/8, 1/16, and 1/32 in. thick. The compositions are given in Table I. Specimen Preparation. Specimens for thermal analysis were in the form of small squares approximately 1/4 in. on a side. For the 11.9 and 13.5 Al-Cu alloys, the sheet thickness was 1/16 in. and for the 10.5 A1-Cu alloy the 1/32-in. sheet was used. One lead of a chromel-alumel thermocouple was spot-welded to either face of the square with the specimen itself thus forming the hot junction of the thermocouple. Specimens for X-ray analysis were prepared as filings from martensitic sheet stock and were sealed in glass ampoules under 1/2 atm of argon. Metallographic examination of the powder specimens was carried out on a portion of the heat-treated filings mounted in lucite. All specimens were examined metallographic ally after etching

Jan 1, 1965

By R. M. Goldhoff, H. J. Beattie

The high-temperature properties of a 1 Cr-Mo-V forging steel are described. A series of controlled heat treatments was designed to delineate the effects of austenitizing and tempering treatments, temile strength, and grain size on such properties. Studies indicate that the mechanical properties and their varlations under creep can be described by the initial metallurgical structures and their changes droPirzg exposure, particulavly the carbide reactions. Such structures are described and correlated with the mechanical properties. FOR many years the large steam turbine industry has relied on the 1 Cr-Mo-V type forging steel for critical applications. Because of its adequate heat resistance and relative economy, it is currently in use in the temperature range up to about 1050" to 1075°F. Attempts to understand the large property variations attainable in this steel involve the structural modifications due to the wide latitude in its heat treatment. The heat treatment essentially involves a two-step process which includes solution-ing of carbides in the austenite range followed by a suitable tempering treatment below the critical to adjust the level of properties. The latter step is referred to as "secondary hardening" and is basically an ordinary aging reaction involving carbides. In the commercial heat treatment of large components of such steel, homogenizing and stress-relief anneals may be included and have some importance in determining subsequent properties. Several studies of the engineering properties of this steel as a function of transformation micro-structure have been reported.1 3 However, in this steel the carbide reactions, which are a function of composition and heat treatment, appear to be the property-controlling factor rather than the micro-structure defined as a transformation product. Thus, the tempering resistance of this type of alloy steel is mainly a function of the size and distribution of alloy carbides.4 However, it is also necessary to consider the stability of the microstructure and the effect of dynamic carbide reactions on subsequent properties. It is the purpose of this paper to show the interdependence of properties and corresponding structures, particularly carbide reactions, developed for a limited set of controlled heat-treatment conditions applied to 1 Cr-Mo-V steel. MATERIALS AND PROCEDURE The material for this work came from a large production forging whose chemical composition is shown in Table I. The property data accumulated on this steel as a function of heat treatment were room-temperature tensile and smooth- and notch-bar creep rupture at 1050°F (notch geometry: shank diameter = 0.357 in., depth = 50 pct, radius = 0.005 in.). To achieve controlled structural variations the temperature and time of both austenitizing and tempering were varied in a manner to produce a series of eight steels each at one of two grain sizes and one of two hardness levels in proper combination for valid comparisons. This will be clear upon examination of Table I. Structural studies involved the use of optical and electron microscopy as well as X-ray and selected-area electron diffraction. To reveal the nature of carbide precipitations, electrolytic extraction techniques were used with subsequent analysis of the residue by X-ray diffraction. Weight losses of the steel specimens during electrolysis were measured and successive chemical fractionations of the residues were applied and checked by X-ray examination. The details of fine structural distributions, morphologies, and crystallography of the precipitates as well as dislocation distributions were investigated by examining in the electron microscope three common types of preparation. a) Relief Replicas. Mechanically polished sections were etched in 2 pct nital, replicated with a nitrocellulose film, which was shadowed by chromium vapor deposited at a glancing angle of 20 deg. b) Extraction Replicas. A thin film of carbon was vapor-deposited on the polished and etched surface. The carbon films were then etched off and gathered on electron-microscope supporting grids. The carbides left imbedded in the carbon replica in their original distribution were then examined crystallo-graphically by selected-area electron diffraction. c) Thin Films. Specimens were mechanically ground and polished down to a thickness of 0.001 to 0.003 in. Final thinning was done electrolytically in a "chrome-acetic" electrolyte. When holes began to appear in the foil, the voltage was interrupted and applied in several 1-sec bursts. Sections of the foil between holes were thin enough to pass a 100-kv electron beam that carries an image.

Jan 1, 1965

By P. Greenfield, C. C. Smith, A. M. Taylor

The Mg-Zr alloy ZA and Mg-Mn alloy AM503(S) are shown to have a markedly improved resistance to creep deformation after suitable heat treatments. This improvement makes them suitable for certain stress-bearing fuel element components in nuclear reactors. The extent of strengthening is described and an explanation of the behavior of both materials is given, based on a combination of strain-aging and grain growth. The increase in operating temperatures of fuel element components in Calder Hall type nuclear reactors has necessitated the development of magnesium base alloys with a very high resistance to creep at temperatures up to 500°C. Such alloys are not required for fuel element cans, which require high-creep ductility rather than strength, but for can supporting and stabilizing components, which are needed to support the imposed loads without deforming more than about 1 pct in times of up to 40,000 hr. The amount and type of alloying addition made to magnesium for these parts is limited by the necessity of keeping the cross-section to thermal neutrons as low as possible. The alloys must also possess a high resistance to oxidation in CO2. Alloys which have been developed for this application include ZA, an alloy of magnesium with 0.5 to 0.7 pct Zr and AM503(S), an alloy of magnesium with 0.5 to 0.75 pct Mn. In the as-extruded condition these alloys are very weak and ductile in creep but it has been found that they can be strengthened to a significant extent by heat treatment. This paper describes the method of developing a high-creep resistance in ZA and AM503(S), the extent of the strengthening produced and discusses the probable mechanisms of strengthening. TEST MATERIALS Specimens were taken from typical casts of ZA and AM503(S) alloys extruded into 2 1/4-in.-diam bars, supplied by Magnesium Elektron Ltd. Typical analyses of the bars were as follows: The as-extruded mean grain diameter was 0.001 to 0.002 in. for the ZA alloy and 0.003 in. for the AM503(S) alloy. EXPERIMENTAL METHODS Extruded bars of ZA alloy, 2 1/4 in. in diameter and 9 in. long, were heat treated in electrical resistance furnaces in an atmosphere of flowing CO2 containing 50 to 300 ppm water, thereby reducing the extent of oxidation compared with that which would have occurred in air. Heat treatments were carried out at 600oc for times of 8, 24, 48, 72, and 96 hr and material was subsequently both furnace cooled and water quenched. In order to measure the effect of time of heat treatment, specimens were creep tested at 400°C and 336 psi for about 1000 hr. Subsequently, the behavior of material heat treated for 96 hr at 600°C and furnace cooled was tested at a variety of stresses from 200° to 500°C. Tests were also conducted at 200o and 400°C on material in the as-extruded condition for comparative purposes. With the AM503(S) alloy, only the effect of heat treatment at 565°C for 4 hr was examined. It has been shown1 that such a heat treatment produces marked strengthening in this alloy. Tests on this material were conducted at a variety of stresses at 200°, 300°, and 400oc with comparative tests on as-extruded material at 200o and 400°C. The creep tests were carried out on machines using dead-weight loading and direct micrometer strain measurements on specimens 5 in. long and 0.357 in. diameter. At temperatures of 400° C and below, the creep tests were conducted in air, but at higher temperatures an atmosphere of CO2 was used. Grain size measurements were made on ZA in the extruded and heat treated states and on each specimen after creep testing. This was done by a line count of a minimum of 20 grains in two or three random fields in the longitudinal and transverse directions. The same method was used for measuring the grain size of as-extruded AM503(S), but the grain size of the heat treated material was so large that this method could not be employed. For heat-treated AM503(S) the large grained characteristics (between 0.1 and 1 in.) were confirmed by the measurement of individual grains. In the case of the ZA alloy, specimens taken from various stages in the program were analysed for hydrogen by a combustion method. Material in various states was also analysed for the soluble and insoluble zirconium content by dissolving in dilute hydrochloric acid. This technique has been useda for the determination of amounts of zirconium present

Jan 1, 1962

By P. Greenfield, C. C. Smith, A. M. Taylor

J. E. Harris (Berkeley Nucclear Laboratories, England)—Greenfield et al.11 attribute abrupt changes in slope of their log o/log i curves for heat-treated Mg/0.5 pet Zr alloy (zA) to &apos;atmosphere&apos; locking. It is proposed here that a more reasonable explanation of the apparent strengthening at low rates of strain can be based on precipitation either during the preanneal or during the creep tests. All the tests were carried out above 0.5 Tm where solute atmospheres are likely to be largely evaporated2 and can migrate sufficiently rapidly so as not to impose any &apos;drag&apos; on the moving dislocations. McLean3 has derived an expression for determining the temperature Tc above which, due to the high-migration rate of the atmospheres, Cottrell or Suzuki locking can play no part in determining creep strength. This expression, which holds for an applied shear stress of not greater than 5 X 107 dynes per sq cm is: Tc/Tm= 7/6.8 - log10? where i = secondary creep rate The values for T, corresponding to the maximum and minimum reported creep rates at each temperature have been calculated from the data of Greenfield et al. These are given in Table VII. All the test temperatures were above T,, the margin being greater for the higher temperatures and for the lower strain rates where the breaks in the log s/log ? curves occurred. Dorn and his collaborators14, 17 have studied systematically the effect of solute hardening on the creep properties of an A1/3.2 at. pet Mg alloy. In the temperature range where strain aging occurred in tensile tests, abnormally high-activation energies for secondary creep were obtained but at temperatures above 0.43 Tm, solute alloying did not have any effect on the creep parameters. Moreover, there have been no reports of any strain aging phenomenon during elevated temperature tensile tests with ZA material.18 Instead of the observed strengthening being due to atmosphere locking, it is now proposed that precipitates play an important role in enhancing the creep strength of the material. There are two possibilities—precipitation of zirconium hydride during the high-temperature preanneal and/or precipitation of the hydride or a-zirconium during creep. On the basis of the former the results can be interpreted in terms of a critical stress being necessary to force the dislocations through or over preexisting precipitates. From the latter, if the strengthening is due to pre- cipitation during the test then hardening should be associated with a critical strain rate. At low rates of strain, time is available during the tests for precipitation to occur either directly onto dislocations (thus pinning them) or generally throughout the matrix (which would impede dislocation movements). Examination of the data of Greenfield et al. suggests that both mechanisms may be operative since they observed precipitation during creep and also found that their alloys exhibited high-creep strength in the early stages of the low-stress tests, i.e., before creep-induced precipitation had time to occur. It is not easy to understand why they considered that precipitation of zirconium hydride is unlikely to occur at 600°C while it can take place in tests in air at as low a temperature as 200°C. Precipitation of the hydride during the preanneal cannot be ruled out merely on the basis of metallographic examination. Hydride precipitates in ZA type alloys are very small and can only be accurately resolved in the electron microscope.9 For example, in this laboratory20 hydride platelets with major dimensions <(1/10) µ have been observed by electron transmission through thin film specimens of hy-drogenated ZA material. Complex interactions between dislocations and such particles are illustrated in Fig. 12. Additional evidence for precipitation during pre-annealing is provided by the data presented in Greenfield&apos;s Fig. 1 and Table IT. These show that the creep strength at 200o and 400°C increases with the time of preanneal at 600°C. Such increases cannot be explained on the basis of increases in grain size alone for further improvements in strength were observed when the material was annealed for longer times than that required to stabilize the grains. Although the main discussion is confined to ZA material, similar arguments can be used against the strain aging hypothesis proposed to explain the binary Mg/Mn alloy data. In this case no precipitation is possible during the preanneal, but precipitation-hardening during creep can occur.

Jan 1, 1962

By S. Saito, P. A. Beck

The crystal structure of MoNi3 was determined by means of X-ray diffraction. This structure is isotype with that of ovgered TiCu3. The lattice parameters are: a. = 5.064A, bo = 4.224A, co = 4.448A, and zf 0.157. If the orthorhombic distortion (slight relative to the corresponding orthohexagonal unit cell) is disregarded, the structure may be described in terms of a close-packed ordered atomic layer, stacked in the sequence: abab. The structztres of ordered TiCu3 and TiAl3 are homotectic. The three types of ordered hexagonal phases, iso-structural with TiNi3, MgCd3, and VCo3, are known to occur in AB3 alloys of transition elements of the first, second, ad third long periods. It was noted1 that phases with the TiNi3 structure occur selectively in alloys of Ti-group elements with Ni-group elements. In AB3 alloys of Ti-group and V-group elements with Co-group elements the AuCu3-type structure predominates.&apos; The vCO3 structure, which was determined very recently,&apos; has hexagonal symmetry, but the actual atomic arrangement here, too, is rather closely related to the ordered cubic structure of AuCu3-type. However, an ordered hexagonal close-packed structure of the MgCd3-type occurs in MOCO33 and WCO3.4 Consequently, the question arises as to whether or not the crystal structure of MoNi3 is also of the MgCd3-type. Grube and winkler5 found that MoNi3 has a hexagonal close-packed structure with a = 2.54A and c/a = 1.65. They pointed out that some additional weak diffraction lines could be observed in the powder pattern, which may have been due to an ordered atomic arrangement in this phase. However, no detailed information was obtained by them and the structure was apparently not further investigated by others. The present work was, therefore, undertaken in an attempt to determine in detail the structure of MoNi3, and to investigate the possibility of ordering. EXPERIMENTAL METHODS Alloys used in the present work were arc-melted in a water-cooled copper crucible under helium atmosphere. Electrolytic nickel and molybdenum, both 99.9 pct pure, were used. Chemical analyses were not made, but the melting loss was not higher than 2 pct for any alloy. Ingots were first homogenized at 1200°C for 48hr, quenched, heavily cold worked, and then annealed at 820" or 860°C for 1 week, followed by quenching in cold water. Powder specimens for X-ray work were prepared by crushing the heat-treated solid specimens. In order to remove strains, the powders were reannealed in evacuated scaled fused silica capsules for 6 hr at the same temperature at which the corresponding solid specimens were annealed. X-ray photographs were taken with an asymmetric focussing camera, using unfiltered CrK or CuK radiation. EXPERIMENTAL RESULTS The X-ray diffraction patterns of alloys containing 20.8, 25, and 26.4 at. pct Mo, homogenized at 1200°C, showed the face-centered-cubic structure of the Ni-base a-solid solution. It was revealed, however, by micrographic examination that the 26.4 at. pct Mo alloy contained in addition very small amounts of a second phase, in accordance with the phase diagram.6 On the other hand, the 20.8 at. pct Mo alloy after annealing at 820°C gave the X-ray diffraction pattern of the ordered face-centered-tetragonal MONi4.7 In this pattern several additional weak diffraction lines were also observed, corresponding to the strongest diffraction lines of MoNi3. The alloys containing 25 and 26.4 at. pct Mo after annealing at 820" or 860°C gave X-ray diffraction patterns, as shown in Tables I and 11, corresponding to MoNi3. Each one of the reflections which could be tentatively indexed on the hexagonal close-packed cell of Grube and Winkler,5 with the exception of the basal plane reflections, was split into a doublet, as seen in Table I. Since microscopically the alloy consisted of a single phase, it seemed probable that the lattice of MoNi3 is actually slightly deformed, as compared with the tentative hexagonal unit cell. In addition to these diffraction lines, several weak lines were also present, as shown in Table 11, which could not be indexed at all on the hexagonal close-packed cell considered. Satisfactory indexing of all diffraction lines observed was found to be possible by using an orthorhombic unit cell with ao = 5.064A, ft = 4.224A, and c = 4.448A. These values, whose accuracy is estimated to approximately ± 0.008A, correspond to 95.14A3 for the volume of the unit cell, and to an X-ray density of 9.50 g per cm3. If no attention were paid to the weak reflections listed in Table II, a reduced -unit cell of half the volume (a = 2.532A, b = 4.448A, and c = 4.224A), closely related to the orthohexagonal cell, might be used. The dimensions of the orthohexagonal cell of the same volume as the reduced cell are: a = 2.562A, b = 4.437 A, and c = 4.183A. It may be seen that in the reduced cell the a axis is slightly shorter, while the b and c axes are slightly longer than those corresponding to the orthohexagonal cell of the same volume. This slight orthorhombic distortion is re-

Jan 1, 1960

By D. Harker, E. Epremian

The constitution of the nickel-tungsten system has been studied by a number of investigators, the most recent of which are Ellinger and Sykes.1 On the basis of metallography, electrical resistivity and hardness measurements and some X ray diffraction work, they constructed a consitution diagram (Fig 1). Ellinger and Sykes report a0 for the alpha face-centered cubic phase (nickel saturated with tungsten) as 3.66?.‡ The gamma phase (tungsten saturated with nickel) is given as body-centered cubic, but no value of a. is recorded. At 43 pct tungsten by weight (approximately 20 at. pct) a beta phase is reported, but structure and lattice parameter are not known. Primarily on the basis of metallographic evidence, they conclude that beta is a new phase and rule out the possibility of formation of a superlattice since they- observe a new phase in the microstructure. Grube and Schlecht2 report an ordering reaction in a system similar to the Ni-W (Ni-Mo) and Harker3 has shown that NirMo forms a superlattice upon the pre-existing face-centered cubic lattice of the alpha phase. Elliniger arid Sykes observed a change in the diffraction pattern of a 4.3 pct W alloy upon aging and attributed it to the formation of a new phase. Thus, there appears to be some question as to the character of the beta phase reported by Ellinger and Sykes. The purpose of the present work is to determine precisely the structure and nature of the beta phase in the Ni-w system of X ray diffraction methods. Experimental Procedure One inch diameter ingots of 43.66 pct, 40.15 pct and 34.06 pct .tungsten by weight (19.8, 17.6 and 14.1 at. pct respectively) were melted and cast under vacuum from electrolytic nickel and pure wire filament grade tungsten. The ingots were soaked for 16 hr at 1300°C in a hydrogen atmosphere furnace, then swaged at this temperature and finally drawn to 0.020 in. diam wire. Some of the bar stock was retained in 1/2 in. diam rod for hardness and metallographic studies. Wire samples for diffraction work were sealed in evacuated quartz tubes and subjected to the various solution and aging heat treatments in a hydrogen furnace. X ray photograms were taken in a Debeye-Slierrer camera using copper K radiation filtered by nickel foil. Results X RAY DIFFRACTION The lattice parameters of the alpha and gamma phases at saturation were determined by an X ray photogram of the 19.8 at. pct W alloy after solution heat treatment at a temperature well within the alpha-gamma range above the peritectoid temperature (17 hr at 1150°C—oil quenched). The alpha phase was found to be face-centeted cubic with a. of 3.594 ± 0.001?, while the gamma phase was determined as body-centered cubic with a. of 3.158 ± 0.001?. Exactly the same phases and parameters were ohtained with the 17.6 at. pct W alloy for the same solution heat treatment. Thorough analysis was made of an X ray photogram of a 19.8 at. pct alloy sample in the quenched and aged condition (solution treated 1T hr at

Jan 1, 1950

By Nicholas J. Grant, Bill C. Giessen

The phase diagram Ta-Ni has been treated repeatedly; investigations up to 1958 are summed up in Ref. 1. Since then, an equilibrium diagram has been presented by Kornilov and Pylaeva.2 They found the following intermediate phases: Ta2N; (CuA12 type),3 "TaNi" (p phase, Mo8Co7 type), TaNiz, and TaNi3 (Ticus type).5 Of these, the crystal structure of TaNin remained unknown, and no further literature reference was found. According to Kornilov and pylaeva,&apos; TaNil melts peri-tectically at 1420°C. A 5-g alloy of Ta + 66.7 at. pct Ni was prepared by inert-gas arc melting using 99.95 pct Ta rod (NRC-MG) and 99.9 pct Ni shot (Fisher). The weight loss after three melts was <2 mg; a microscopically homogeneous ingot resulted. As shown in Ref. 6, no oxygen or impurity pickup needed to be considered under these conditions. Specimens were annealed for 15 hr at 1350°C, 15 hr at 1205oC, and 15 hr at 875°C with subsequent powdering and stress relief for 10 min at 1350°C, 15 min at 1205oC, and 1 hr at 875oC, respectively. Micrographs and X-ray analysis (114.6 mm Norelco camera, filtered CuK, radiation) showed homogeneous one-phase alloys in the as-cast state and at all three temperatures, all having the same powder pattern except for broad lines in the as-cast state. From this it is concluded that either TaNi, melts congruently or its melting behavior is a transition between the eutectic and peritectic cases. Since it was found that very slight surface contamination on stress relieving can considerably alter the structure of similar phases (e.g.,TaPt3),7 patterns before and after stress relief were also compared; they were identical except for line broadening in the non-stressrelieved condition, and two faint impurity lines in the stress-relieved samples. The powder pattern is presented in Table I. All lines were accounted for by indexing with a tetragonal lattice, 0Yh- I4/mmm , with a, = 3.154 ± 0.001A, co = 7.905 * 0.002i and c/a = 2.506. The atomic positions are: 1000; 1/2, 1/2, 1/2] + 2Ta(a): 000; + 4Ni(e): *(002); z = 0.333 * 0.002 This proves TaNi2 to be a representative of the MoSiz (Cllb) type. The variable parameter was determined by grouping the visually estimated intensi- ties according to their 2 indices, plotting their F values, and varying z for best fit, which was obtained at z = 0.333= 1/3. Since absorption was not considered, only the relative intensities with similar 28 can be expected to agree. The interatomic distances are presented in Table 11; the standard error is *o.o2A, resulting chiefly from the uncertainty in z. These distances indicate a coordination number 10 for both kinds of atoms and show that the pseudohexagonal layers along (110) are rather un-distorted. The mean atomic volume of 13.1A3 is close to the Vegard&apos;s law value of 13.3A3, showing

Jan 1, 1964

By B. S. Tani, R. V. Schablaske, M. G. Chasanov

In the Ti-Cd system two intermediate phases, TiCd and Ti Cd, have been found and characterized by X-ray diffraction powder techniques. An earlier reference&apos; had reported the existence of the compound Tisd. No structural details, however, were given nor was there any indication of the possible existence of other binary compounds. Studies of the solubility of titanium in liquid cadmium2 led to the discovery of both TiCd and Tisd. The solid phase in equilibrium with saturated solutions of titanium in liquid cadmium at temperatures below 620°C is TiCd, whereas TizCd is the equilibrium solid phase above 620°C. Both thermal analysis and X-ray studies show that a peritectic reaction between the y phase (~isd) and cadmium to form the 6 phase (Ti Cd) occurs at 620°C. X-ray diffraction powder photographs of material isolated from the ingots used in the solubility measurements as well as material prepared by a direct heat of the appropriate stoichiometric amounts of titanium and cadmium can be indexed on the basis of a tetragonal unit cell with a = 2.904 ± 0.002A, co = 8.954 * 0.004A, c/a = 3.083. No variation of lattice parameters indicative of a range of composition is evident. With four atoms in the unit cell the calculated density of the intermetallic is 7.05 g per cm3; the observed value is 7.07 g per cm3. The TiCd lattice is primitive as indicated by the fact that there are no systematic absences among hkl reflections. The absence of all hko reflections for which h + k = 2n + 1 is also evident. This systematic absence indicates the following two space groups, C\h — P4/n and D&~4/nmm; both groups, however, have the same two- and four-fold positions. Stoichiometry, symmetry and space group indicate two likely structure types. They are the PbO-litharge3 (B10) type and the Ti CU (B11) type. Spatial considerations favor the B11 structure with atoms placed in the following positions: 2Ti (c) 0, 1/2, Z; l/2, 0, Z 2Cd(c) 0, 1/2, Z; 1/2, 0, Z The TiCd structure may be summarily described as a layered structure in which double cadmium layers alternate with double titanium layers along the c-axis. The best agreement between calculated and observed intensities is obtained for the values ZTi = 0.608 and ZCd = 0.130. Calculated and observed powder intensities as well as other pertinent powder data are recorded in Table I. Interatomic distances for the proposed structure are recorded in Table II and are to be compared with the distances of closest approach for titanium and cad-

Jan 1, 1962

By W. L. Phillips

Stress-strain curves were obtained for single crystals of 70 pct Ag-30 pct Zn tested in tension and shear. Samples tested in tension and shear had comparable resolved shear stresses and stress-strain curves. The {111} <110> slip system was observed. It zoas found that the9.e is a barrier to slip in both latent close -packed directions and that the magnitude of these barriers is proportional to prior strain during easy glide. It was observed that cross-slip in tension and shear was most frequent in crystals with an initial orientation near <100> "Oershoot" zoas observed in tension. The amount of this "overshoot" was independent of initial orientation. AN idealized concept of plastic deformation indicates that a single crystal should yield at some stress that is dependent on crystal perfection and it should then continue to deform plastically by the process of easy glide which is characterized by a linear stress-strain curve and a low coefficient, d/dy, of work hardening. Hexagonal metal crystals generally conform to this ideal concept of laminar flow. In fcc metals the range of easy glide is always restricted in magnitude and it is strongly dependent on orientation, composition, crystal size, shape, surface preparation, and temperature. Since one of the principal differences between the two crystal systems, both of which deform by slip on close packed planes, is the existence of latent slip planes in the fcc crystals, it has been proposed that the transition from easy glide to turbulent flow, characterized by rapid linear hardening, is due to slip on secondary planes intersecting the primary plane.ls Several theories have been proposed to explain the linear hardening and parabolic stages of the stress -strain curve.6"10 The easy-glide region is the least understood of the three stages. The stress-strain characteristics of Cu-Zn, which shows a long easy-glide region, have been extensively investigated."-" In light of recent ideas on dislocations, cross-slip, effect of solute atoms, and stacking fault energy, it was felt that the certain features of this earlier work might be compared with another alloy, Ag-30 pct Zn, which also exhibits a long easy-glide region. Tension and shear stress at room temperatures were employed. The results obtained, together with some interpretation of the observations, are described below. EXPERIMENTAL PROCEDURE The silver and zinc used for mixing the alloys were 99.99 pct pure. The two components were weighed to within 0.1 pct of the weights required fo the alloy composition. They were then placed in a closed graphite mold and the mold and contents were heated in 100°C stages from 500&apos; to 900°C with sufficient time and vigorous agitation at each stage provided to dissolve the silver. The crucible was then heated to 1150°C and agitated violently before being quenched in oil. The resulting alloy rod was machined free of sur face defects and then placed in a graphite mold designed for growing single crystals. The graphite mold was closed with a graphite plug and was encased in a pyrex glass tube which was connected to a vacuum system. The tube and mold assembly were placed in a furnace; the tube was evacuated and the furnace was rapidly heated to a temperature sufficient for fusing and sealing the glass. The glass-encased evacuated mold and contents were then lowered through a vertical furnace. The top section of the furnace was held at 100 °C above the melting point of the alloy. The lowering rate was 1.5 in. per hr. The tension specimens were 1/4 in. diam; the shear specimens were 1/2 in. diam. These specimens were then removed from the mold, etched, and chemically polished with hot (60°C) Chase etch reagent (Crz03-4.0 g, NH4C1-7.5 g, NHOs-150 cc, HzS04-52 cc, and Hz0 to make 1 liter). In preparation for tensile testing, the specimens were carefully machined to a diameter of about 0.200 in. to permit a gage length of 6 in., annealed for 16 hr at 800&apos; to reduce coring, and then cleaned and polished. A modified Bausch-type shear apparatus which has been described previously18 were employed. The gage length was 1/8 in. This shear apparatus was placed in an Instron tensile testing machine. EXPERIMENTAL RESULTS A) Tension. Several specimens were extended at room temperature to determine the effect of initial orientation on the stress-strain curves of Ag-30 pct Zn. The initial orientation and the resolved shear stress supported by the active slip system at various total strains are plotted in Fig. 1. The critical resolved shear stress, t,, initial rate of work hardening, d/dy, and length of the easy-glide region are independent of orientation. The arrival at the symmetry line is shown by an arrow in Fig. 1. During the easy-glide region of the stress-strain

Jan 1, 1963

By P. Duwez, C. B. Jordan

The phenomenon of the change of volume of pressed powder compacts upon sintering is well known in the field of powder metallurgy. Depending upon the metal or metals involved and the pressure used in forming, a compact may, in the course of time of sintering at a given temperature, expand mono-tonically, contract monotonically, or first show a volume change of one sign followed by a change of the opposite sign. It is clearly desirable to have accurate knowledge of the magnitude and sign of the change in dimensions to be expected in any given case, both from the point of view of direct usefulness in the fabrication of parts by powder metallurgy, and from the longer range viewpoint of elucidating the fundamental mechanism of metallic sintering. The present study was therefore undertaken as a first step in acquiring systematic and reasonably quantitative knowledge of the change in density of metal powder compacts during sintering. For practical reasons, copper was selected as the material to be studied first, and its densification followed as a function of temperature and time of sintering in hydrogen and in vacuum. Experimental Procedure The copper powder used was that designated by the manufacturer (Metals Disintegrating Co., Elizabeth, N. J.) as MD-151. This powder was sifted through Tyler standard screens to separate the fraction having particle size range between 200 mesh and 325 mesh, and this fraction was used in all the subsequent work. Compacts weighing about 10 g were then pressed in a 1 in. diam round die, using a pressure of 20,000 psi throughout. Sintering was carried out in commercially built electric furnaces in which the resistance windings are so disposed as to produce a nearly uniform temperature along the axis of the furnace for a length of about 18 in. centrally located. In order to be able to sinter in a controlled atmosphere, a 2 in. stainless steel tubing was inserted in the furnace. Each end of the tube was cooled by a water jacket about 7 in. long, and closed with a rubber stopper. The hydrogen used for one series of specimens was purified as described in Ref. 1. For the other set, a pressure of about 0.5 mm Hg was maintained during sintering by a Welch Duo-Seal Pump. The specimens were heated on square trays made of stainless steel. In placing specimens in the trays, a thin even layer of powdered aluminum oxide was first sprinkled on the bottom of the tray. A copper guard disk about half the thickness of the specimen was then placed in the tray and covered with a second layer of alumina. The actual specimen was then set on the guard disk, and a final coat of alumina sprinkled over the specimen. This technique was evolved for sintering the specimens in such a way as to reduce the influence of unknown extraneous factors to a minimum. If the specimen is placed directly on the tray and sintered, it is found that the resulting shape is that of a frustum of a cone, rather than a section of a right circular cylinder, since friction with the tray prevents the bottom of the specimen from contracting at the same rate as the top. In the arrangement used in these experiments, the guard disk provided a support which shrank at the same rate as the specimen, and the alumina powder reduced to a minimum friction between guard disk and tray, and between specimen and guard disk. The procedure followed in sintering consisted of bringing the furnace to the required temperature, and then inserting the specimen into the central heated portion of the furnace tube in one of the two atmospheres used. At the end of the heating period, the specimen was cooled by bringing it into a portion of the furnace surrounded by a water jacket. These manipulations were carried out without opening the furnace, by means of rods which were attached to the trays and operated through a sliding seal in the rubber stopper. The progress of densification of the copper compacts was studied at 1300, 1400, 1500, 1600, 1700, and 1800°F. At each of these temperatures, a specimen was allowed to sinter for each of the following time intervals: M, 1, 2, 4, 8, 16, 32, and 64 hr. The thickness and diameter of each specimen were measured with micrometers before and after sintering, and each was weighed on an analytical balance after sintering. Results The techniques described in the preceding section were found to give satisfactory results. The specimens were not detectibly warped after sintering, and were usually of uniform diameter (that is, truly round) to within 0.001 in., a very few showing a variation in diameter of ±0.002 in. All specimens were found to have the same diameter

Jan 1, 1950

By P. Duwez, C. B. Jordan

A. J. SHALER*—I should like to congratulate the authors for having carried out such a precise set of experiments. It has been found useful, in sintering experimental compacts in vacuo, to make certain that the residual gas is not one which reacts with the metal. Since traces of oxygen can be kept away only with great difficulty, the technique is often adopted of using a "getter " of powder in the vicinity of the compacts, and, in addition, of permitting a small hydrogen leak to flow into the vacuum chamber. Did the authors use similar devices? This paper brings up a question concerning the definition of the word &apos; sintering.&apos; The authors restrict its use to the adhesion between particles. Kuczynski, in a paper presented at this meeting, applies the word to the growth of areas of contact between particles. I have used it to mean both these phenomena and also the dimensional changes which continue to take place after the first two have run their course. May I suggest that we should come to an agreement on the use of these words ? Fig 1 and 2 show an interesting feature: extrapolation of the curves to zero time does not give a densification parameter of zero. The higher the temperature, the higher is the intercept on that axis. These observations agree with the concept of a practically instantaneous densification taking place while the compact is being brought to heat. Such a change may be brought about by plastic deformation and primary creep. The stress pattern causing this first rapid flow is, to my mind, due to the force of attraction between the surfaces of opposite particles in the regions immediately flanking their common areas of contact. The stress is not temperature-sensitive, but at room temperature plastic deformation only proceeds until the metal in the area of contact can support it elastically. As the metal is heated, the elastic limit falls, and further plastic flow occurs. At the higher temperatures, this is followed by primary creep, and finally by the steady-state rate-reaction which the authors are seeking. If they were to recalculate their densification-parameter values, using, not the initial density of the cold compact, but the density after the compacts have been brought to temperature, the systematic deviations from linearity in Fig 3 and 4 might be eliminated. Such initial densities might be obtained by extrapolating the curves of Fig 1 and 2 to zero time. I am naturally pleased to see that such a very well done series of experiments leads to a heat of activation (for the densification process in hydrogen) that is much higher than that for self-diffusion, in confirmation of the less elaborate results reported by Wulff and myself (Ind. and Eng. Chem., (1948) 40, 838). J. T. KEMP*—I would like to comment on Dr. Shaler&apos;s remarks. There are apparently different interpretations of the word "sintering." It seems to me that an accurate definition of our word is essential in all metallurgy. May I point out, in this connection, that in practical metallurgy the word "sintering" has been applied to a bonding process in the preparation of ores and flue dust for fur-nacing. It would be unfortunate if in the area of powdered metallurgy we should establish a definition that is essentially different in meaning. F. N. RHINES*—I think that I can answer the question by saying that I see no essential difference between the use of the term "sintering" in extractive metallurgy and in powder metallurgy; physically the same things are going on. I admit sintering is used for different end purposes in the two cases. When we resort to the sintering of lead ore mixture we are doing so to obtain a chemically reactive, loose texture of some rigidity. This is only a difference in use. After all, in powder metallurgy we sometimes deliberately produce a very porous material which has just a little strength, just as in the case of sinter cake. P. DUWEZ (authors&apos; reply)—We agree that it would be helpful to have well-established definitions of such terms as "sintering." Since the question has now been raised, the time might be appropriate for its consideration by some suitable committee of one or more of the metallurgical societies. In answer to Dr. Shaler&apos;s first question, no getter nor hydrogen leak was used in our vacuum experiments, except insofar as the guard disks (used to reduce friction between specimens and trays) may have acted as getters. Dr. Shaler&apos;s statement that extrapolation of the curves of Fig 1 and 2 does not lead to zero densification at zero time apparently overlooks the logarithmic

Jan 1, 1950

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

The tensile properties, creep resistance. and thermal stability of highly alloyed Ti-Al-Zr alloys were examined. On the basis of these studies, the Ti-7Al-1ZZr composition was selected for more complete evaluation. The alloy was found to be weldable and free from excessive directionality. In addition, it developed maximum properties without requiring heat treatment other than an annealing operation in the alpha field. The alloy was recommended for scale up and is presently being investigated on a production-level basis. One of the more attractive properties of titanium alloys is their ability to withstand stress at moderately high temperatures, and a considerable amount of effort has been devoted to increasing the maximum service temperature of titanium alloys. This work has suggested that the optimum alloys for high-temperature service will be single-phase a (close-packed hexagonal) alloys containing significant amounts of aluminum. However, the maximum amount of aluminum which can be alloyed with titanium is between 6 and 8 pct,l since at high-aluminum contents an embrittlement reaction occurs in the anticipated service temperature range, 800" to 1100°F. It has been shown that the embrittlement reaction involves decomposition of the high-aluminum a phase to one or more new phases.&apos; Since this reaction does not occur at intermediate or low-aluminum contents, it was felt that intermediate Ti-A1 alloys might be strengthened by a-soluble ternary additions without inducing the embrittlement reaction. The first alloying addition considered was tin, which shows extensive solubility in a titanium and has moderate strengthening tendencies. Unfortunately, it was soon apparent that tin also promoted the embrittlement reaction, and that to obtain a stable alloy, the aluminum content had to be reduced as the tin content was increased. The second alloying addition considered was zirconium, which is similar to tin in its effects on titanium. This element did not contribute to the embrittlement reaction and, in fact, appeared to increase the maximum amount of aluminum which could be alloyed with titanium without inducing instability. This paper describes an investigation of the Ti-A1-Zr a alloy region. Alloys containing from 4 to 12 pct A1 and from 6 to 15 pct Zr were examined. The properties of these alloys are described and the bases for selecting an optimum composition is outlined. This composition, Ti-7A1-12Zr, is presently being scaled up in tonnage quantities, and is being evaluated extensively throughout the industry. In addition to presenting the basis for its selection, this paper presents a description of the properties developed in laboratory material as determined during the alloy investigation. These properties suggest that this alloy can fill an important position in applications requiring light weight, fabrica-bility, weldability, and strength to 1000oF or higher. EXPERIMENTAL PROCEDURES Titanium alloy ingots were prepared by inert electrode arc melting under an argon atmosphere. Alloying elements used were 110 Bhn titanium sponge, high-purity aluminum, and reactor-grade zirconium. Pancake-shaped ingots were prepared weighing approximately 300 g. The composition of the ingots was checked by weight measurements before and after melting. The pancake ingots were forged at 2000°F to approximately half their original thickness to give a flat plate roughly 1/2 in. thick. This plate was then rolled at 1800&apos; to 1600°F to 0.250 in. thick. All of the alloys examined fabricated well. However, alloys containing 15 pct Zr tended to overheat due to exothermic oxidation, and scaling was excessive. As might be anticipated from its effect in decreasing the ß transus, increased zirconium appeared to improve fabricability somewhat, especially during rolling at lower temperatures. Except for a limited study of heat-treatment response, all alloys were examined in the a-annealed condition. Prior to heat treatment the a and ß tran-sus temperatures were determined by metallo-graphic examination of samples quenched after annealing at 50-deg intervals in the transformation region. These data are shown in Fig. 1. Recrystal-lization appeared to occur in about 1 hr in the range 1300º to 1500ºF. Therefore, alloys were annealed for 1 hr at 1550ºF (4 and 5 pct Al), 1600ºF (6 through 7-1/2 pct Al), or 1650°F (8 or more pct Al). This produced an equiaxed a grain structure. In most alloys, a "ghost" structure was visible after the a-annealing treatment, as shown in Fig. 2. This structure apparently resulted from the acicular

Jan 1, 1963

By P. W. Barton, A. A. Johnson, E. J. Hughes

THE only systematic work on the effect of carbon on the recovery and recrystallization kinetics of iron so far reported in the literature is that of Venturello et al.1 These workers found that doping high-purity iron so that it contained up to 86 ppm C caused a marked retardation of recovery but had little or no effect on the recrystallization kinetics. Such evidence for an effect as was obtained was inconclusive. In the course of a study of electron-beam zone-refined iron the authors have recently examined the effect of added carbon on the recrystallization kinetics of this material. The amount of carbon added was about 50 pct more than was used by Venturello et 01. and definite evidence was obtained that carbon at this level retards recrystallization. The starting material was taken from a batch of 0.2-in.-diameter Johnson-Matthey spectroscopically pure iron rods which had been further purified by being given three passes at 4 in. hr-1 in a standard MRC electron-beam zone-refining unit. The purity of this material. which was used in two other investigations of the properties of high-purity iron,2,3 was established by an extensive series of analyses. Four laboratories, the National Research Corp., Newton, Mass., the Naval Research Laboratory, Washington, D.C.. the Battelle Memorial Institute, Columbus, Ohio, and the National Physical Laboratory. Teddington. Middlesex, England. carried out analyses for carbon. oxygen. and nitrogen. and in addition a complete mass-spectrograph analysis was carried out at Battelle. In all, twelve analyses were carried out for carbon, seventeen for oxygen and twelve for nitrogen. The amounts of these elements found to be present were 10 * 7, 8 i 5, and 0.9 i 0.1 ppm, respectively. The limits given are rms deviations. Two results, one of 46 ppm of oxygen and another of 31 ppm of nitrogen, were rejected as anomalous. The mass-spectrograph analysis revealed the major impurity to be 25 ppm of tungsten. All of the other elements detected were present in amounts less than 0.5 ppm. Some of the rods were doped with carbon by being immersed in a suspension of carbon in oil, heated in a vacuum at 400°C, and then zone-leveled to make the distribution of carbon uniform. Carbon analyses carried out on three of the doped rods gave a mean value of 130 ± 45 ppm. Some of the doped and undoped rods were deformed 58 pct by swaging and cut into specimens 1/2 in. in length. Isothermal recrystallization experiments were then carried out on them at 575", 600°, 615", 630°, and 650°C, the volume fraction of each specimen recrystallized being measured by a point-counting method described by Hilliard and Cahn.4 The results for the two types of specimens are shown separately in Figs. 1 and 2. In Fig. 3 the pairs of recrystallization curves for each temper-

Jan 1, 1965

By E. G. Schempp, W. A. Morgan

The influence of modifications in the molybdenum, vanadium and, to a limited degree, carbon and boron content to a basic composition of 5 pct Cr, 0.75 pct Mo, 1 pct V hot-work tool steel composition, was studied in respect to hardenability, grpain- coarsening temperature, and tempering charactevistics. Tensile, impact, and fatigue pvoperties were studied for the most promising compositions. An alloy with a typical composition of 0.43 pct C, 4.97 pct CI-, 0.33 pct Si, 2.25 pct Mo, and 1.00 pct V uas found to offer the most favorable combination of properties in respect to high-strength applicntions when tempered at 1100°F. MANY 5 pct Cr high-strength steels are at present being manufactured in North America which fit well into the classification of the AISI-SAE system. Much interest has been shown in these materials as ultra-high-strength steels for use at elevated temperatures. The limiting temperature of use lies at the point where the steels begin to soften rapidly. Although a great deal of information has been made available in the past two years on the properties of selected alloys in this series, little information exists on the effect of systematically varying the ccntent of one or more elements in the 5 pct Cr-base alloy. This paper presents the results of an investigation of the effect of variations of the carbon, molybdenum, vanadium, and, to a limited extent, the silicon, manganese, boron, and niobium content of a 5 pct Cr steel to the AISI H-13 base analysis. EXPERIMENTAL PROCEDURE All experimental heats were melted in a 50-lb. induction furnace. The melting stock consisted of

Jan 1, 1962

By N. Nakanishi, C. M. Wayman

The effect of small copper additions on the mar-tensitic transformation behavior in Au-47.5 at. pct Cd was studied by measuring electrical resistivity as a function of temperature. The transformation behavior was found to change and transformation start (M,) temperatures for both the ß to ß&apos; and ß to ß&apos; transformations were depressed substantially by the addition of small amounts of copper. Both M, temperatures were lowered approximately 70°C per at. pct Cu. Copper also had the effect of narrowing the transformation hysteresis region (resistivity us temperature), and for the alloy Au-47.5 Cd-1.5 Cu there was little or no hysteresis; in this alloy, the reverse transfmmation upon heating apparently occurs below the thermodynamic equilibrium temperature, To. THE ß phase in the Au-Cd system occurs at the electron/atom ratio 3/2, and is similar to other ß phases in alloys based on copper, silver, or gold. It is of the CsCl type, in which a considerable degree of long-range order persists to the melting temperature.&apos; The phase boundaries of the ß phase are not known precisely below 300° C, but at room tem- perature the phase exists from approximately 46 to 52* at. pct Cd.2 At low temperatures, the ß phase transforms in a diffusionless (martensitic) manner. Alloys having a composition near 47.5 pct Cd transform upon slow cooling to an orthorhombic3 phase, ß&apos;, at - 60°C. Alloys having a composition near 49.0 pct Cd, transform at - 30°C into a phase, ß", which has been recently identified as trigonal.4 Alloys having compositions near 48.5 pct Cd will transform into both the 0&apos; and 0" phases over a range of temperatures. The progress of transformations can be observed

Jan 1, 1963

By J. T. McGrath, R. C. A. Thurston

Poly crystalline specimens of copper, and copper with various additions of zinc, were tested in plane-bending fatigue. In tests performed at a constant stress, the fatigue life of copper increased slightly with the addition of up to fifteen per cent zinc. There was a sharp increase in fatigue life as further additions of zinc of up to 35 pct were made. Surface observations showed that the coarse slip bands that are characteristic of fatigue became narrower as the concentration of zinc increased. The rate of crack propagation also decreased with increasing zinc content. It is suggested that the fatigue behavior is controlled by cross slip processes. CROSS slip occurs when dislocations move from one primary slip plane to another along a connecting or cross slip plane. The primary and cross slip planes have a common slip direction. Wide stacking faults, having low energy, tend to make cross slip more difficult. According to recent theories, the ability of a material to cross slip is important to the formation and propagation of fatigue cracks. McEvily and Machlin2 have examined this concept experimentally by fatiguing single crys tals of lithium fluoride, sodium chloride, silver chloride, and KRS-5.* The latter two materials ex- hibit easy cross slip, while the former two do not. Normal rapid fatigue failure was obtained in the silver chloride and KRS-5 specimens, whereas it was much more difficult to achieve in sodium chloride and lithium fluoride crystals. Furthermore, numerous slip band extrusions and intrusions were found in silver chloride and KRS-5 crystals, whereas only one isolated extrusion was found in lithium fluoride and none was found in sodium chloride. McEvily and Machlin also consider that there is no clear-cut demarcation between crack initiation and propagation. The intrusion-extrusion process, which initiates crack formation, continues ahead of the cracks to allow propagation of these cracks along slip bands. The process of cross slip is therefore important not only to crack initiation, but also to crack propagation. Holden4 postulates that fatigue crack growth is dependent upon cross slip and thus upon stacking-fault energy. Using an X-ray microbeam technique, he found a cyclic subgrain structure in fatigued aluminum and a-iron. Holden suggests that micro-cracks develop in the densely-packed sub-boundaries ahead of the main crack front, and when sufficiently numerous join up to promote crack growth. The ease with which a subgrain structure could form would depend upon the ability of the dislocations to cross slip, and thus upon the stacking-fault energy. Hence in aluminum, which has a high stack-ing-fault energy and in which cross slip is easy, Holden found that the relative rate of fatigue crack propagation was considerably greater than in stainless steel, a low stacking-fault energy material. It has been shown by a number of investigators that the probability of forming deformation stacking faults in copper increases as zinc is added.5-7 Cross slip should, therefore, become more difficult as the zinc concentration is increased. In order to check the validity of the foregoing theories, it was decided to test copper and copper with various additions of zinc in plane bending fatigue, and determine to what extent their fatigue properties are dependent upon their ability to cross slip. EXPERIMENTAL PROCEDURE Fatigue tests were carried out on polycrystalline OFHC copper and various copper-zinc alloys with 5, 15, 20, 30, and 35 wt pct Zn. The Cu-Zn alloys were obtained commercially in sheet form. Test specimens, as shown in Fig. 1, were machined from sheet that had been reduced to an approximate grain size of 0.040 mm, the heat-treatment procedure being similar to that of Feltham anc copley.8

Jan 1, 1963

By C. R. Simcoe, T. J. Koppenaal

The effect of direct and alternating currents on the quench aging behavior in an Al-4 pct Cu alloy has been investigated by use of resistivity measurements. The reaction rate increases with direct current density in the investigated range of 1000 to 3000 amps per sq cm. Alternating current of a specific frequency is observed to decrease the reaction rate by a factor of about two. ErDMANN-JESNITZER et al.,1,2 investigated the effect of direct and alternating current on the quench and strain aging behavior of low-carbon iron. In both cases they observed that direct current accelerates the aging reaction and that an alternating current can completely inhibit the aging process. The purpose of the present research was to investigate these phenomena in the quench aging behavior of an Al-4 pct Cu alloy and to determine the correlation, if any, between the increase in the observed reaction rate and possible heating effects accompanying the aging with direct current. EXPERIMENTAL PROCEDURE The aluminum-base alloy used in this investigation contained 3.98 wt pct Cu (1.72 at. pct) with impurities of 0.003 pct Si, 0.002 pct Fe, and 0.001 pct Mg. The alloy was rolled into a ribbon about 0.36 mm thick and 3.7 mm wide. The ribbon was split end from end with the ends being used as electrical contacts and the central unsplit section, about 5.3 cm in length, serving as the specimen. Solution treatment was accomplished by quenching from a salt bath at 520° ± 2°C into water at 25° ±0.5°C; the specimen was immediately transferred to a liquid nitrogen bath. All aging was done at 75° ± 0.2°C in a rapidly stirred ethylene glycol bath. Resistivity measurements were made by the double potentio-metric method employing a standard resistor; for purposes of convenience, the resistance measurements were made at 77°K. The transfer of the specimen from the aging bath to a liquid nitrogen dewar was accomplished in less than 1 sec. The aging kinteics were studied with the specimen being aged under the influence of direct current, alternating current, and without any type of current. The amount of heating caused by direct currents was investigated by soldering a thermocouple on the specimen surface and measuring the temperature change after applying various current densities. The temperature was observed to increase (from 75°C, the aging temperature) about 0.8°, 3.0°, and 8.5°C with direct currents of 1000, 2000, and 3000 amp per sq cm, respectively. When employing alternating current, the circuit was monitored with an oscilloscope and adjustments made to produce a normal sine-wave pattern. RESULTS Prior investigations3&apos;4 in the aging characteristics of A1-4 wt pct Cu have shown that the resistivity initially increases, reaches a maximum, and then decreases to values significantly lower than the as-quenched resistivity. This type of behavior is seen in Fig. 1 which shows the resistivity at 77°K as a function of aging time at 75°C observed in this investigation. At this aging temperature, the resistivity maximum is seen to occur in about 1 to 1-1/2 min and it further decreases to the as-quenched value in about 24 min. The behavior observed with the application of direct currents of 1000, 2000, and 3000 amp per sq cm during aging is shown in Fig. 2. With increasing current densities, (+) ?pmax decreases and the rate of the aging process increases. The time necessary to reach the as-quenched resistivity value decreases from 24 min for aging without current to about 16, 10, and 7 min for aging with 1000, 2000, and 3000 amp per sq cm direct current, respectively. Fig. 3 shows the results obtained when two changes were made during the aging with 2000 amp per sq cm

Jan 1, 1963

By J. M. Hodge, H. M. Reichhold, R. D. Manning

The work reported in this paper represents the first of a series of investigations of the factors governing notch toughness in ferritic materials. This paper is concerned with two of these factors, namely, the effect of ferrite grain size, and the effect of an alloy content of 3.64 pct nickel. Every effort has been made to hold other variables constant in order to isolate the effects of these two. The compositions chosen for study were 0.02 pct carbon in order to eliminate the variable of carbide distribution, one steel being a plain carbon steel and the other alloyed with 3.64 pct nickel. Both steels were fully killed with silicon, without an aluminum addition, so that the variable of deoxidation practice was held constant. Finally, all samples were water quenched from 1200°F and tempered 24 hr at 300°F in order to hold the quench aging variable constant and to decrease the tendency for grain boundary carbide precipitation. The ferrite grain size was varied by heat treatment over the range of A.S.T.M. grain size numbers of about 2 to 6 in each steel so that the effect could be evaluated individually and the notch toughness of each steel could be compared at comparable ferrite grain sizes. Materials and Experimental Procedure MATERIALS The materials for this investigation were obtained from Battelle Memorial Institute as 250 Ib induction melts which were forged into 134 in. square bars and then rolled into 0.6 in. square bars. Both steels were deoxidized with silicon, the aluminum content being held to a minimum. Check analyses of these materials are shown in Table 1. HEAT TREATMENT FOR GRAIN SIZE The grain size was varied by varying both the cooling rate and the austeni- tizing temperatures. The heat treatments used and the corresponding grain size values are tabulated in Table 2. A semicontinuous network of grain boundary carbide was observed in the microstructure of both the plain carbon and nickel steels in the as rolled condition and an additional heat treatment was necessary to eliminate this variable. Therefore, all samples were water quenched from 1200°F and tempered 24 hr at 300°F as a final treatment before testing. This heat treatment served to eliminate to a great extent the grain boundary carbide network and to hold the quench aging effect constant. IMPACT TESTING Standard keyhole Charpy impact tests were machmed after heat treatment. A bath of acetone and dry ice was used for refrigeration of the samples down to temperatures of —94°F (—70°C) and a bath of either methyl-cyclohexane or isopentane, cooled by

Jan 1, 1950

By Vito J. Colangelo

The primary object of this study was to determine the effect of ferrite and its orientation upon the mechanical properties of a precipitation -hardening stainless steel with particular attention to the short-transverse properties. The investigation consisted of Jour major parts : the preliminary investigation of billet properties, the effect of forging reduction and ferrite content upon mechanical properties, the effect of notch orientation upon impact strength, and the relationship of heat composition to ferrite content. Low ductility and impact strength in the short transverse direction were found to he associated with the orientation and shape of- the ferrite plates. It was also determined that impact strength varied with notch orientation. The test values obtained with the notch perpendicular to the plane of the ferrite plate were lower than those obtained in the notch-parallel condition. The over-all investigation showed that high ferrite contents in general had a deleterious effect upon mechanical properties and that the ferrite content could he minimized by exercising rigorous control of the heat composition. A careful balance of elements, nitrogen in particular, must he maintained in order to reduce the formation of ferrite. THE precipitation-hardening stainless steels were developed to fulfill a need for high-strength corrosion-resistant alloys. In the annealed condition they are soft and ductile and possess many of the desirable characteristics of the austenitic stainless steels. In the hardened condition, the alloys exhibit the high strength and hardness of the martensitic stainless steels. The alloy under consideration in this investigation has a nominal composition as follows: C Mn Si Cr Ni Mo N 0.13 0.95 0.25 15.50 4.30 2.75 0.10 The hardening mechanism is identical to that of other hardenable steels in that it depends upon the transformation of austenite to martensite. This alloy because of its annealed structure and its ability to be hardened combines the desirable forming and corrosion properties of the austenitic grades with the high hardness and strength levels attainable with the hardenable grades. The reason for this apparent duplicity of proper- ties can be explained by considering a basic metallurgical difference between the hardenable stainless steels and those of the austenitic group. Both types are austenitic at 1800°F but, while the martensitic grades transform to martensite upon rapid cooling to room temperature, the austenitic grades remain austenitic even when cooled to temperatures below room temperature. The major difference then is in the degree of austenite stability. This stability can quantitatively be described by the Ms temperature. The Ms is defined as that temperature at which austenite begins to transform to martensite. The austenitic grades for example may be cooled to -300°F without producing significant quantities of martensite. The hardenable stainless steels on the other hand have an Ms temperature in the vicinity of 400" to 700°F. In cooling to room temperature, these alloys traverse the entire Ms-Mf range and show almost complete transformation to martensite. The semiaustenitic stainless steel, however, occupies an intermediate position with respect to its austenite stability. The analysis is so balanced that the Ills temperature lies at or slightly above room temperature. The resulting alloy retains much of its austenite at room temperature and yet responds to hardening heat treatments. Achieving this delicate balance of elements is therefore of great importance. Slight imbalances of the equivalent Cr-Ni ratios frequently result in the presence of 6 ferrite. It is the effects of this ferrit with which we are concerned, more specifically the effect of the quantity and ferrite orientation upon mechanical properties, particularly ductility. PROCEDURE A) Preliminary Investigation of Billet and Forging Properties. In order to determine the effect of ferrite on billet properties, billet stock from three heats with various ferrite contents was utilized. Tensile specimens were obtained in the transverse and longitudinal directions from this material and heat-treated as shown in Tables I and 11. Forgings were made from these same heats, the purpose being to determine what effect, if any, the ferrite might have upon the mechanical properties. These forgings were made in such a manner as to elongate the ferrite in the longitudinal and transverse directions. The method of forging was as follows. A section was cut from a 6-in.-sq billet of Heat A and flat-forged to 1-1/2 in. thick. Working was done from one direction only with no edging passes as shown

Jan 1, 1965