By P. L. Rittenhouse, M. L. Picklesimer

A rapid and seniquantitative method of determining prefered orientation on large numbers of. Zircaloy-2 specimens was desired. knoop microhardness measurerrzetzls were irvestigated as a solldtion to this pro6lem. The variation of Knoop microhardness measurerlerzts on selected planes as a function of 'irzdenle axis relutilje lo cryslallograplzic or fabrication divectals were used to corzstrrcl a polar coordinate hardness contour map. With use of an empirical relationslip between the single-crystal hardnesses and those of the polycrystalline material conentional pole figures could be constructed which compare favorably also obtained. To determine preferred oriention qualitatively from hardness data requires a minimum of twelve measurements per plane on three, preferattention to grain size, specimen prepartion, and in-rreinetzt, and analjlsis is of the order of- 45 to 60 rrin. THE design of structures from Zr alloys requires consideration of preferred orientation and the resulting anisotropy of mechanical properties. Rapid and semi-quantitative methods of evaluating anisotropy and of determining preferred orientation are needed for quality control and for examining the large number of test specimens required in development programs. The variation of Knoop microhardness with indenter orientation has been studied in single crystals of several hcp metals including titanium.' beryllium,' magneium, and zinc.4 The maximum hardness observed on any crystallographic plane other than the basal plane invariably occurred when the long axis of the Knoop indenter was either parallel or perpendicular to the projection of the [ OOOI.] direction on the plane of examination. When the major slip mode was (0001)(i2i0j the maximum hardness occurred at the parallel positio! but when the operating slip system was {10i0) (i210) the hardness was a maximum perpendicular to the [0001] projection. A minimum hardness was always observed at a rotation of 90 deg from the maximum. It follows that the orientation of the projection of the [0001] can be determined on any non-basal plane by making hardness measurements at a number of indenter orientations. The determination of the orientation of the [0001] projection on two non-parallel, preferably orthogonal, surfaces of the specimen will allow location of the [0001] direction in the specimen. It seems possible that such measurements could be used to examine, at least qualitatively, the preferred orientation existing in polycrystalline hcp materials. An investigation of the microhardness anisotropy in Zircaloy-2 was undertaken to ascertain whether these measurements could be used for this task. EXPERIMENTAL PROCEDURE Single crystals of Zircaloy-2 were grown by an a-8-a annealing sequence using electron-beam heating.= The orientation of the crystals was determined by a conventional back-reflection Laue technique. The crystals were then mounted on a goniometer head and the desired crystallographic faces were milled and chemically polished. Polycrystalline Zircaloy-2 specimens were prepared from fabricated sheets or plates. Inverse pole figures for these materials were obtained using the X-ray diffraction techniaue described by Jetter, McHargue, and illiams.' A Wolpert-Greis Micro-Reflex hardness-testing machine was used to make the Knoop microhardness measurements. The single-crystal and polycrystalline specimens were loaded to 0.5 and 2.0 kg, respectively. Determination of the scatter of hardness numbers as a function of applied load for several indenter orientations on several specimen surfaces showed that the loads selected were the lightest consistent with minimum scatter. Heavier loads did not appreciably decrease the scatter and produced hardness impressions too large to be conveniently measured with the equipment used. Seven crystallographic planes of the single crystals were examined, while six planes of examination were used in studying Zircaloy-2 polycrystals. The specimens were rotated 10 to 15 deg after each measurement and from four to eight impressions were made at each angle of rotation. RESULTS The two angles which were used to relate crystallographic directions and planes in the hcp cell to the planes of examination of the single crystals are shown in Fig. 1. 8 is the angle between the c axis. [0001]. and the normal, N, to the plane of examination. a is the angle between the long diagonal of the Knoop indenter and the projection of the c axis on the plane of examination. For exampIe, if P = 90 deg and a = 0 deg, the plane of examination is of the family

Jan 1, 1967

By Robert E. Green, T. Hinton

The velocities of the three possible modes of elastic-wave Propagation have been calculated for single-crystal aluminum at 1-deg intervals throughout the standard steveographic triangle. The results are presented as isospeed contours. The deviations between the direction of maximum energy propagation and specirzen axes are presented as arrows drawn within the standard triangle. The orientation factors associated with dislocation nzotion on the primary slip system only and also on all twelve slip systenzs have been calculated for all three elastic waves. The orientation factors associated with a longitudinal standing--7aue resonant specivnen hazle also been calculated. The relevance of these results to ultrasonic attenuation measurements is discussed. DUE to the widespread use of ultrasonics in the investigation of the properties of solids a number of authors15 have discussed in detail the theory of elastic-wave propagation in solids. In this paper the modes of wave propagation are evaluated according to the procedure suggested by reeen' for the case of single-crystal aluminum at 1-deg intervals throughout the standard stereographic triangle. The wave speeds are presented in the form of contour diagrams within the standard triangle. The deviations between the direction of maximum energy propagation and the normals to the wave fronts are presented as arrows drawn within the standard triangle. The orientation-de pendent factors (orientation factors) associated with dislocation damping as derived in the preceding paper6 have been calculated for the case of aluminum at 1-deg intervals throughout the standard triangle. The orientation factors for dislocation motion on the primary slip system only and on all twelve slip systems are presented in the form of contour diagrams, for both the traveling- and the standing-wave conditions. The relevance of these results to ultrasonic attenuation measurements is discussed. ELASTIC-WAVE PROPAGATION Three waves can be propagated in a linear elastic homogeneous anisotropic medium. The velocity of propagation v of each of these waves in a medium of density p can be obtained from the determination of the eigenvalues and eigenvectors of the matrix equa- The A's are a series of moduli which are functions of the elastic constants cij and the direction cosines 1, m, and n of the specimen axis. In the case of cubic single crystals where there are only three nonzero elastic constants cll, c12, and C, the A's are, The solution of Eq. [I] will give the wave speeds (eigenvalues) and the direction cosines a, 0, and y of the particle displacements (eigenvectors). To obtain the direction of maximum energy flux requires the calculation of the energy-flux vector ET with com- w is the angular frequency, A, the amplitude, and v the velocity of the wave. The direction cosines a, b, and c of the energy flux vector are then given by

Jan 1, 1967

By R. J. Wasilewski

Elastic constants have been determined on single crystals of maximum-melting-temperature NiAl compound (50.6 at. pct Al) at 25°C. Temperature variations of Young&apos;s modulus in the three principal crystal directions between -150°C and +800°C exhibit no anomalies similar to those repovted for the isomor-phous compounds brass and AuCd. It is concluded that the ordered CsCl structure is stable throughout the temperuture range investigated NICKEL aluminide is a congruently melting inter-metallic compound of CsCl (B2) structure, stable over a rather wide composition range (40 to 54 pct Al). It exhibits a lattice-parameter maximum of a. = 2.883A at 50.6 pct 1,&apos; at which composition the excess aluminum atoms are randomly distributed on the vacant nickel sites;&apos; at higher nickel compositions the excess nickel atoms replace substitutionally in aluminum sites, while at higher aluminum compositions vacancies are present in the nickel sublattice.&apos; For compositions close to NiAl no significant variation in order has been observed at temperatures up to 900°C.3 At high nickel (65 pct) compositions the existence of a martensitic structural transformation has been reported.4 NiAl is isomorphous with the ordered B-brass structure and with the high-temperature structures of AuCd and TiNi alloys close to equiatomic composition. All of these exhibit anomalous elastic behavior as the temperature of their diffusionless transformation to lower-symmetry structures is approached.&apos;-&apos; This behavior has been explained as indicative of low stability of the CsCl structure in these compounds.8 The present paper reports the experimental determination of the elastic compliances of single-crystal NiA1. EXPERIMENTAL METHOD 1) Specimens. Polycrystalline NiAl was prepared by induction melting of carbonyl nickel and high-purity aluminum and casting into solid copper molds in gettered helium atmosphere. The castings thus produced were canned in mild steel and impact-extruded at 1100 to 1200°C to 38-in.diam rod. After the steel sheath was pickled off, the rods were converted to single crystals by repeated high-frequency satisfactorily produced the desired orientations in the form of crystals 38 in. diam by 8-12 in. long. These were subsequently center less-ground to 7 to 8 mm diam by 12 cm long, electropolished (in 80 pct methanol, 20 pct HzSO, at 25°C and 15 v), and their axial orientation determined to 1 deg by the Laue back-reflection technique. The rod dimensions were determined to 0.01 mm and the densities determined from geometrical dimensions and the weight of every specimen. The average density was 5.905 0.005 g per cu cm. 2) Elastic Data Measurements. Room-temperature elastic compliances Sii were obtained by determining to 0.1 cps the fundameGtal resonance frequencies in the longitudinal and torsional vibration modes. At these frequencies the following relations hold: E =p(2lfif =pvl= Sn- 2r[Sll- S12- -£„«] g -P(2iftf = pvf = (s<« - fr(sii - sw - ±s»y where vl and vt are the velocities, and f andft the resonance frequencies of the longitudinal and torsional waves, respectively; 1 is the length of the specimen, and r is the direction cosine factor—{cos2 a • cos2 0 + cos2 a . cos2 y + cos2 0 ¦ cos2 Y}. Given three crystals of orientations (loo), (110), and (111)) i.e., F = 0, 14, and 13, we can obtain six equations for the three unknown compliances, thus providing adequate internal check. Mode mixing can readily occur in the relatively long wavelength resonance utilized here. This could cause a significant error in the torsion wave velocities calculated from the apparent resonance frequenies. Therefore, throughout the present work, a method, described previosl,&apos; was used to ensure that no significant mode mixing took place at resonance. The apparatus used was originally designed for the Elastomat, Magnaflux Corp.. Chicago, 111. determination of flexural vibration resonance frequencies. At room temperature torsional vibration mode could be established by suitable positioning of the thin wires from the input and pick-up transducers, and longitudinal mode by cementing thin magnetic foils at the ends of the specimen, and inducing the vibration by means of electromagnetic transducers. Only flex-ural resonance frequencies could, however, be obtained reproducibly over the temperature range of -150 to 800°C. These data are considerably less accurate, the error in the modulus being estimated at -0.6 pct from the specimen dimensions and the room-temperature Poisson&apos;s ratio. The reproducibility of the resonance frequencies in repeat runs was, however, to better than l in 15,000, hence the relative elastic modulus error less than 0.02 pct. Therefore, the temperature variation of the principal Young&apos;s moduli obtained by flexural resonance, relative to room-temperature values, is believed to be satisfactorily accurate.

Jan 1, 1967

By R. P. Abendroth

The hydrogen-water vapor ratio at which Fe-Cr alloy, chromium oxide, andiron chromite coexist in equilibrium was determined between 900" and 1200°C. A thermogravimetric method was used to determine equilibrium conditions. The results fit a straight-line relationship in the temperature region studied, and are given by Reduction experiments were also performed to confirm the results of the equilibrium investigation. ThE oxygen pressures at which Fe-Cr alloy, chromium oxide, and iron chromite coexist in equilibrium have been previously determined by Boericke and angert,&apos; Morozov and Novokharski,&apos; and Katsura and uan. Only one determination (at 1300°C) was made by Katsura and Muan, but it agrees with the results of orozov and Novokharski. The results of Boericke and Bangert, however, differ appreciably from the results of these investigators. Previous studies have assumed that the equilibrium metallic phase is pure iron, but Dahl and Van vlack have shown that the iron contains from about 1 wt pct Cr at 1000°C to over 2 wt pct above 1300°C. The chromium oxide also contains a small amount of iron in solid solution. In the present study, hydrogen-water vapor mixtures were equilibrated with the condensed phases, using a therrnogravimetric method to determine equilibrium conditions. The reaction can be written EXPERIMENTAL General Procedure. The starting material was a sintered pellet of Fe2O3-Cr2O3 solid solution with a hole in the center, and was placed on a fused silica hook. This assembly was raised into the preheated hot zone of the furnace in a helium atmosphere, hooked onto a fused silica hangdown suspended from one arm of an Ainsworth Model RV-AU-1 recording balance, and the starting weight determined. A flowing hydrogen-water vapor atmosphere was then exchanged for the helium by evacuation, and the sample reduced until the weight loss indicated the sample composition to be in the alloy-Cr2O3-chromite field. The tem- perature was adjusted incrementally until constant sample weight was achieved for several hours, to within 0.02 mg. A hydrogen-water vapor atmosphere of different composition was then admitted, and the same procedure carried out. At the end of a series of determinations, the sample was examined by X-ray diffraction to verify the presence of the desired phases. Microscopic examination of the silica hook showed no interaction with the sample, nor did it lose any weight. Several criteria were used to insure equilibrium besides constancy of weight. For a given hydrogen-water vapor composition, equilibrium was approached from both oxidizing and reducing sides by varying the furnace temperature slightly. The resulting slow weight loss or gain was observed for several hours. Constant weight could be re-established by returning to the original furnace temperature. The last criterion used was varying the relative amounts of the phases by further reduction or oxidation, and observing any changes in temperature required for constant weight for a given hydrogen-water vapor atmosphere. None were observed. This procedure was essentially the same as approaching the equilibrium from oxidizing and reducing sides, but larger weight excursions were carried out. Sample Preparation. Reagent-grade Fe2O3 and Cr83 powders were mixed in the desired proportions and heated in air at 1250°C for 2 hr. The mixture was re-ground and heated in air overnight at 1250°C. X-ray diffraction showed complete solid-solution formation as a result of this procedure. The solid solution was then pressed into l/2-in.-diam pellets using Carbowax 4000 as a binder. The hole was drilled in the center, and the pellets were sintered 24 hr at 1250°C in air on a bed of Fe2O3-Cr2O3 of the same composition, contained in an alundum boat. After cooling, the pellet surfaces were abraded with 310 paper to remove any surface compositional differences, such as loss of Cr2O3. Chemical analysis of the sintered pellets was 67.16 wt pct CrP3 and 33.02 wt pct Fe203. Atmosphere Generation and Control. The hydrogen-water vapor atmospheres were generated by passing Matheson ultrahigh-purity hydrogen, with no further purification, through two water bubblers contained in a constant-temperature water bath. Since the water-vapor dew points required in this study were below room temperature, the bath was insulated, and was cooled by thermoelectric-immersion devices. The bath temperature was controlled to 0.0l0C. Since rather high flow rates of about 900 ml per min were used through the furnace tube, an independent check of the dew point was made to insure saturation of the hydrogen by the water vapor. Although the dew point could only be determined to within 1/2"C, the determined dew points agreed with the water-bath temper-

Jan 1, 1967

By G. G. Hancock, H. H. Johnson

Hydrogen gas at atmospheric pressure is shown to cause substantial embrittlement in a martettsitic high-stretzgth steel. Subcritical crack growth is observed at very lom stresses and with high growth rates. It is suggested that an adsorbed layer of hydrogen atoms at the crack-tip surface provides the damaging hydrogen. Oxygen in small quantity, as little as O.7 pct by volume, is shown to eliminate subcritical crack growth in gas environments caused by hydrogen or water vapor. However, dissolved oxygen in water has little or no influence upon crack-growth rates. Oxygen-stopped cracks may be restarted by water, or by hydvogen or water vapor if oxygen is removed from the environment. These observations are interpreted in terms of preferential adsorption of oxygen at the crack tip and the formation of an oxide barrier. RECENT investigations1-3 have demonstrated that environmental factors are frequently responsible for delayed failure in martensitic high-strength steels. The environment causes crack initiation from preexisting cracklike flaws at unexpectedly low stresses, often far below the uniaxial yield strength. The crack then propagates at a rate controlled by the environment and the crack-tip stress-field intensity; during this period crack propagation will cease if either the stress or the aggressive environment is removed, and this may be considered a definition of subcritical crack growth. Fracture occurs when the crack has grown to a critical length, such that the fracture toughness of the steel is exceeded. Several liquids are known to cause delayed failure, but water and water vapor are the most severely damaging of the environments investigated to date.&apos;-3 It has been suggested that hydrogen produced during corrosion reactions may be the actual embrittling agent2 The severe embrittlement caused by water vapor inevitably raises the question as to whether other gas environments are damaging. Previous work4&apos;5 has demonstrated that high-pressure hydrogen (2250 psi or greater) is an effective embrittling medium, as measured by such criteria as reduction in area, notch tensile strength, and time to failure. Moreover, the embrittlement was eliminated by the addition of small quantities of air or oxygen to the high-pressure hydrogen, but it was not influenced by additions of nitrogen or argon.4 In the present study attention is focused upon gas environments at atmospheric pressure, in particular hydrogen and oxygen. The influence of these constituents upon the initiation and growth of a crack from a pre-existing cracklike flaw in a high-strength steel was determined directly by the electric-potential method of monitoring crack growth. MATERIALS AND PROCEDURE The H-11 steel was supplied by the U.S. Naval Research Laboratory as 3 by 12 by 0.065 in. sheet specimens with 1-in. transverse center slots. The slot tips were finished by Elox machining to a radius of 0.001 in. or less. The yield strength was 230,000 psi; chemical composition and heat-treatment schedule are given in Table I. The experimental apparatus, precracking procedure, and incremental loading sequence have been described previously.3 In the only significant change, precracking was sometimes carried out by a hydrogen embrittlement and baking technique. All experiments were conducted at room temperature; the hydrogen gas environment was purified by a commercial palladium purifier. Crack initiation and propagation were followed by the electric-potential method,&apos;-3 using a calibration that has been recently dicussed. Stress-field intensities at the crack tip were computed by the conventional Irwin frmula; the plasticity correction was negligible and therefore not included. EXPERIMENTAL RESULTS A striking brittleness associated with molecular hydrogen at atmospheric pressure is demonstrated by the data in Table I1 and Fig. 1, which indicate that subcritical cracks in hydrogen initiate at lower stress-field intensities and propagate more rapidly than in fully humid argon. Ki and Kf are the crack-tip stress-field intensities at initiation and termination of subcritical crack growth, respectively. Termination, of course, corresponds to fracture. In both hydrogen and humid argon Ki is less than Kf

Jan 1, 1967

By J. C. Yannopoulos, N. J. Themelis

Ah electronic thermogravirnetric balance was used to measure the veductioiz rule o single cirpric oxide particles suspended in a stream of hydrogen. Very jzne thermocouples embedded in lie center and at the surface of the sphere recorded the variation of terw perature during reduction. In contrast to iron oxide reduction, where in most instances the rate of interface reactiokl is controlling, the heat- and mass-transfer phenotnena play a predolrinant role in the reduction of cupric oxide. The correlation of experitnental data or tnass lransfev lhrough the boundary layer at Reynolds nunlber 0-4 50 was as jollocs: ThE reduction of cupric oxide by hydrogen is represented by the equation: It is a highly exothermic reaction and the amount of heat released varies only slightly with temperature (-21,430 cal per g-mole at 400°C). Most of the published studies on this system have been conducted at temperatures in the range of 34 to 280c.l-&apos; The concensus of opinion has been that at temperatures below 200°C the reaction is preceded by an induction period during which there is very little or no reduction. The length of this period diminishes as the temperature of the reaction is increased1l5 and aseawa found that at 280°C reduction starts practically immediately when the oxide is exposed to hydrogen gas. The existence of an induction, or incubation, period has led experimenters to believe that the reduction of CuO by hydrogen is catalyzed by metallic copper.&apos; Boldurev and rmolaev found that mechanical additions of powdered copper to oxide did not affect its reduction, although metallic copper produced during the reduction seemed to have a catalytic effect. At least three other authors2&apos;5&apos;7 have reported that addition of copper had no effect on the rate of reduction. Pease and alor&apos; observed that water vapor had a strong inhibiting effect on the reduction at 1503C, but its effect was greatly diminished at 200 C. Pavlychenko and Rubinchik5 studied this reaction at 159 to 235 C and found that, once the reaction had been initiated, there was no inhibiting effect due to the introduction of water in the hydrogen stream; at temperatures above 183°C there was no inhibiting effect due to water vapor, either before or during reaction. The same authors noted that the rate of reduction was independent of pressure in the range of 200 to 700 mm Hg. aseawa investigated the kinetics of the CuO-Hz system at 160 to 280°C and estimated the apparent activation energy at 14,000 cal per g-mole. A similar value (13,500 1200 cal per g-mole) was reported by ond&apos; in the temperature range 148 to 216°C. Bond also reported that there was no incubation period and that water vapor had no inhibiting effect on reduction at temperatures above 190 C. The above studies have been conducted at temperatures below 280°C and the physical configuration of the system under investigation has not been defined adequately. However, it is well-known that the mechanism of gas-solid reactions depends on a number of in series physical and chemical rate prcesses.&apos;&apos; It is, therefore, essential to include among the experimental factors the geometry of the solid system and the mass-transport characteristics of the reducing gas. Scott studied the reduction of packed beds of cupric oxide cylinders by Hz-He streams of very low hydrogen concentrations at temperatures 400 to 600 C, pressure of 10 to 30 atm, and gas velocity from 0.18 to 5.8 ft per sec (3 < Rep < 30). The reduction rate was found to be mainly controlled by diffusion through the boundary layer and through the pores of the reduced copper phase. The following correlation was proposed: Scott in an earlier work studied the reduction of fixed beds of cupric oxide wire and found that the rate of flow of the gas stream through the bed had a controlling effect on the rate of reduction. The same mass-transfer phenomenon was observed by Bond and clark13 on a similar reduction system. The analogy between mass and heat transfer through the boundary layer which exists between a solid surface and the bulk stream stems from the similarity of the differential equations representing these phenomena

Jan 1, 1967

By Robert E. Green, T. Hinton

Expressions are derived for tke orientation factors appearing in the Grana to -Lucke theory of dislocation damping, for fcc crystals. The factors are given as functions of the elastic constants, the direction cosines of the specimen axis, atld the direction cosines of the particle displacemeizts, for darnping due to dislocation motion on each of the twelve possible slip systems as ixell as lor simultaneous dislocation rnotion on all twelve systems. RECENTLY Green&apos; has outlined the general procedure for calculation of the modes of wave propagation in a single crystal possessing a given crystallo-graphic orientation. In addition he has suggested how the results of such calculations along with calculations of the resolved shear-stress factors for slip enable the orientation-dependent factors (orientation factors) appearing in the Granato-Lucke theory of dislocation damping to be calculated. However, reen&apos; assumed that the maximum stress on dislocations was in the direction of the particle displacement of the elastic wave giving rise to the dislocation damping. The present cal&apos;culations show that this is an oversimplified approach appropriate only to special cases of high crystallographic symmetry. The exact calculation of stress on the dislocations can only be obtained by resolving the nine components of stress associated with the elastic wave into the appropriate slip direction and then summing. In this paper the general expressions for orientation factors are derived for fcc crystals in terms of the elastic constants, the direction cosines of the particle displacements, and the direction cosines of the specimen axis, bearing in mind the point mentioned above. Equations are presented which give the orientation factors for damping due to dislocation motion on each of the twelve possible slip systems as well as for simultaneous dislocation motion on all twelve systems arising from elastic-wave propagation. These orientation factors are appropriate to attenuation measurements made by the pulse-echo technique, where the elastic wave is a traveling wave. They will be compared with those for the case of a standing wave as derived by Granato and Lucke which are appropriate to measurements of internal friction by the resonance technique. The expressions for the orientation factors are compared with the five values given by insruch,&apos; based on unpublished work of Granato and Liicke, for positions of highest symmetry in the stereographic triangle. The various equations derived for modes of wave propagation and orientation factors have been evaluated for the case of aluminum crystals at 1-deg intervals throughout the stereographic triangle. These results will be presented in the form of contour diagrams in a subsequent paper3 and their relevance to ultrasonic measurements discussed. ORIENTATION FACTORS The coordinate system used for the calculations is shown in Fig. 1 and all specimen axes are taken to lie in the shaded standard triangle. The twelve slip systems are indexed according to Table I. Following the suggestion of lers, we may define the orientation factor Ok in the Granato-Liicke theory5 by the equation

Jan 1, 1967

By P. Chaudhari, Michael B. Bever

The heat of solution at infinite dilution of selenium in bismuth, the heat of mixing of selenium and bismuth, and the limit of solubility of selenium in bis~rzuth have been determined at 573, 623; and 663°K by metal solution calorimetry. The heat of forrrzation of the compound Bi2Se at these temperatures has been determined from the heat effects associated with the precipitation of the compound from a saturated solution oj selenium and bismuth. The published information on the thermodynamic properties of the system Bi-Se is limited. The heat of solution at infinite dilution of selenium in bismuth at 623°K has been measured.&apos; The heat of formation at 273 K1 and room temperature2 and the heat capacity at 80 K3 of the compound Bi2Se3 have been reported. An estimate of the heat of formation of the compound BiSe at room temperature has been published.2 Information on the phase relations in the system Bi-Se is available.&apos; In the investigation reported here the following quantities have been determined at 573", 623", and 663°K: 1) the heat of solution at infinite dilution of selenium in bismuth, 2) the heat of mixing of selenium and bismuth in bismuth-rich solutions, 3) the limit of solubility of selenium in bismuth, and 4) the heat of formation of the compound BizSe. These quantities were determined by the addition of selenium to bismuth-rich solutions in a metal solution calorimeter. The determination of the heat of formation at the tem- perature of the calorimeter bath involved the precipitation of the compound from a saturated solution in the calorimeter. 5,6 This method differs from that commonly used which requires the addition of the compound and of a mechanical mixture of its components and yields the heat of formation at the temperature from which the additions are made (273 K EXPERIMENTAL PROCEDURE AND CALCULATIONS The solution calorimeter has been described in detail.&apos; Pure bismuth (99.999+ pct) was used as the bath at the start of a run. The calorimeter was calibrated with small amounts of bismuth added from 273°K; the differences of the heat contents of bismuth at 273°K and the temperatures of the baths are listed in Table I. After the calibration, additions of hexagonal selenium (99.999+ pct) were made. Loss of selenium by evaporation was negligible. No unusual experimental difficulties were encountered.9 The differences in the heat contents10 of selenium at 273°K and the temperature of the bath, listed in Table I, were subtracted from the measured heat effects to give the "adjusted heat effects". The methods by which the heat of solution at infinite dilution, the

Jan 1, 1968

By Thomas L. Garrard, James A. Sprague, Rex B. McLellan, Samuel J. Horowitz

A simple rnodel for interstitial solid solutions has been devised in which each solute atom interacts with the solzlent lattice in such a way as to exclude an integral number of nearest-neighbor sites from being occupied by solute atoms. The vemaining interstitial sites ave not affected. In calculating the entropy of such a solution the increase in the number of interstitial sites available to solute atoms due to the ozlerlap of blocked sites is taken into account. The ther-modynamic functions and the solute activity fov the solution rnodel are calculated. It is shown that considevation of the overlap sues vise to a correction term of the order 8&apos; ( where 0 is the ratio of solute to solvent atoms) in the thevmodynamic functions of the solution and the solute activity. The theo,uetical equation for the solute activity was used to analyze the available data for the activity of carbon in austenite at three different temperatures. The use of a computer enabled many comparisons to be made between the experimental activity data and those predicted by both the complex blocking model and the simple, widely used blocking model in which the ozierlapping of blocked sites is not taken into consideration. Even though at the highest concentvations oj carbon the value of 0 is small it is shown that the best fit to the experimental data is found with the complex blocking model. RECENTLY it has been shown by analysis of gas-solid equilibriums that many interstitial solid solutions can be described by the quasi-regular solution model in which the partial energy of solution E, is independent of composition and, apart from a composition-independent term due to nonconfigurational factors, the partial entropy is that of an ideal solution. Dilute solutions of nitrogen in both bcc and fcc iron,&apos; dilute solutions of oxygen and silver,&apos; carbon in a Fe,&apos; and dilute solutions of carbon in ? Fe2 are all quasi-regular. In addition many hydrogen-metal solutions, both dilute and concentrated (with the notable exceptions of the H-Ni and H-Pd systems), can be described by this model.3 However, it has been shown that, at various temperatures, solutions of carbon in ? Fe begin to depart strongly from quasi-regular behavior at low concentrations. A plot of the activity of carbon in ? Fe relative to pure graphite vs atom fraction of carbon (Cc) calculated from Smith&apos;s data4 begins to depart from the (nonlinear) plot for a quasi-regular solution at about Cc = 0.02. Several statistical models have been proposed to account for the thermodynamic behavior of carbon in y Fe. Darken and smith4 set up a model in which a carbon atom in its octahedral site in the fcc lattice has either one or no neighboring carbon atoms in the twelve nearest-neighbor octahedral sites. It is assumed that the number of carbon atoms having more than one nearest neighbor is negligibly small and that a solute atom does not interact with another solute atom located at a greater distance than the first shell of interstitial sites. Thus this model contains two characteristic interaction energies. Darken and Smith showed that this model gives reasonable agreement with the measured variation of carbon activity ac with composition. It is noteworthy that Darken and Smith concluded from their analysis of the activity data using this model that there was a repulsive force between carbon atoms in austenite which reduces the concentration of C-C pairs below that corresponding to random mixing. Recently Aaronson, Domian, and pound5 have considered in detail the statistical model developed by Lachere and by Fowler and Guggenheim7 and have shown that it is compatible with the activity data for carbon in austenite. In Darken&apos;s model the energy of solution of carbon in austenite is dependent on temperature and concentration; the departure from Henry&apos;s law arises from the concentration dependence of the energy of solution. In Aaronson, Domian, and Pound&apos;s discussion of the Lacher, Fowler, Guggenheim model the interaction energy wy between adjacent carbon atoms in austenite is strongly temperature-dependent. Aaronson et al . suggested that this temperature dependence of wy and hence the energy of solution of carbon could be explained either by the formation of clusters of carbon atoms (despite the repulsive nature of wy) or by the dual occupancy of the octahedral and tetrahedral sites by the carbon atoms. However, a temperature-dependent heat of solution

Jan 1, 1968

By T. E. Scott, R. P. Zerwekh

The charactevistics of the deformatiotz of fcc thorium were examined between 78 and 473 K. Activation energy, actiuation volume, and the temperature dependence of the flow stress were determined and conlpared uith several theories for the rate-controlling mechnnistn of the tempemture-dependent component of the flou~ stress. It was established that the Cottrell-Stokes law does not hold, even approximately, for thorium. Through consideration of the above factors and other parameters, it was concluded that the vandom solute barrier theory proposed by Friedel demonstrates the best agreement with experimental observations of the deformation of thorium below ambient temperature. THORIUM, the first metal in the actinide series of rare-earth elements, is interesting and important from two points of view. In the more practical vein, it is a potential reactor fuel. As such, it is important to know its properties. Of specific interest here are the mechanical properties of thorium. Second, no detailed information concerning the deformation characteristics of the actinide elements has been gathered to date. In view of the interesting physical and chemical properties of these metals, their mechanical behavior might reveal characteristics which could improve our understanding of the mechanisms controlling deformation of the more common metals. For example, it has been shown1 that thorium exhibits a yield point which is greatly enhanced by interstitial solute elements such as carbon. This is not a normal occurrence in fcc metals. The goal of this investigation, therefore, was to characterize the deformation of polycrystalline thorium. MATERIAL AND PROCEDURES Thorium, made by the magnesium intermediate alloy process described by Peterson et al.,2 was rolled and swaged to 0.065-in.-diam wire. The metal analysis is given in Table I. After preparation, the oxygen and nitrogen contents had risen to 308 and 60 ppm, respectively. The 0.065-in.-diam wires were cut into 2-in. lengths and annealed in a vacuum of lo-&apos; Torr at 750°C for 1 hr, producing a grain size of 2735 grains per sq mm. The ends of the 2-in. sections were masked off so that a 1-in. gage length could be electropolished. Specimens were polished at 35 v in a solution of 6 pct perchloric acid in methanol which was maintained at 0°C . The gage diameters after polishing were about 0.0625 in. The tests were run on a screw-driven tensile machine at a constant crosshead speed corresponding to a strain rate of 0.005 min-&apos;. The strain rate was changed rapidly after each 0.01-in. extension between 0.005 min-&apos; and one of three higher strain rates which were selected in order to achieve strain-rate ratios of 5, 10, and 20. Tests were run at several temperatures from 78" to 473°K; most were tested at 423", 300°, 215", and 78°K. EXPERIMENTAL RESULTS Flow Stress vs Strain and Temperature. Typical true stress-true strain curves for thorium are shown in Fig. 1 for several temperatures over the range 473" to 78°K. The curves for 78", 215", 300") and 423°K were obtained from strain-rate change tests using the lower (0.005 min-&apos;) or base strain-rate values of stress. Additional tests, using the same base strain rate at different strain-rate ratios, gave curves which virtually superposed on those shown, indicating that strain-rate changes did not materially influence the work-hardening characteristics at the base strain rate. The curves for 273") 373") and 473°K were standard tensile tests at 0.005 min-&apos;. The behavior of the flow stress with temperature is

Jan 1, 1968

By Larry Kaufman, Joan B. Berkowitz-Mattuck, Edward V. Claugherty

The oxidation characteristics of hafnium and zirconiunr diboride were measured between 1200 and 2200&apos;K by a thermal- conductivity method which continuously ttzeasures the rate of reaction of oxygen with the diboride and by a metallographic air oridation method zuhich provides a measure of the total arr7ount of bovide conuerted to oxide for a given time interval. The oxidized specimens obtained from the tl~eritaal-coi~ductitrity method were also examined by quantitatire metal-lographic procedares. The significant results obtained in this investigation reveal that metal-rich compositions of lzafi~iutil diboride proride the most oxidation-resistatzt material up to 2000°K; hafnium diboride is tmre oxidation- resistant titan zirconium diboride at all tempevatures examined; the morphology of the oxide formed on H/B2 and Llie temperature coefficient qi. the oxidation rate constants change at the temperature of ttze monoclinic to tetragonal phase transition] in HfO2; the oxidation of neither HfB2 nor ZrB2, results iN catastrophic Jazlure at lorc. oxygen pressures; and pvefevetztial gvaLti boundary oxidation was not obsevued for either HfBi or ZYB, A comprehensive study of the high-temperature characteristics of refractory transition-metal di-borides is currently in progress. This program has included investigation of the physical, thermal, and thermodynamic properties of TiB2, ZrB2, HfB2, NbB2, and TaB2. In addition, aspects of the synthesis and fabrication of such materials have been studied. In view of the diverse nature of this research, a number of other laboratories have actively participated and contributed specific capabilities for analysis and characterization of these materials. As a consequence, an extensive description of the relevant properties of these compounds has emerged which is central in evaluating their high-temperature (1200" to 2500°K) performance. To date, information on thermodynamic stability, specific heat, and vaporization characteristics,1 hot hardness and electrical resistivity,1, 3 therma1 expansion:&apos;4 and thermal conductivity 1, 5 has been presented. This information has been generated on materials of the highest purity (98.5 to 99.9 wt pct Me + B) and density currently available. Samples fabricated by zone melting6 and high-pressure hot pressing"3&apos;7 techniques have been used to generate suitable specimens for all of the aforementioned studies. dation characteristics of the most oxidation-resistant of these materials, hafnium and zirconium diboride, is presented and a description of the synthesis and the experimental procedures used to prepare and characterize specimens is given. The high-temperature range under consideration (1200" to 2200°K) and the known dependence of oxidation characteristics on sample chemistry, density, and oxidation conditions required a close coupling of the synthesis, fabrication, and evaluation procedures.8 This was accomplished by continual surveillance of chemical composition of starting materials before and after specimen fabrication and by evaluation of density, phase constitution, and microstructural features prior to and after oxidation exposure. I) PROCUREMENT AND CHARACTERIZATION OF STARTING MATERIALS In view of the current state of the art in fabricating refractory boride materials, the methods used in preparing samples for the present study are given in detail as follows: starting materials were purchased in high-purity powder form and fabricated by high-pressure hot pressing into 0.40 by 1.00 in. bars from which oxidation specimens were obtained. The hafnium diboride used in this study was purchased from Wah Chang Corp.; the zirconium diboride from U.S. Borax and Chemical Co. These powders were routinely characterized by quantitative chemical analyses for metal, boron, carbon, oxygen, nitrogen, and iron, by qualitative emission-spectrographic analysis for trace impurities, by X-ray procedures for extraneous phase identification, and by powder densitometry for comparison with X-ray (theoretical) density. Hafnium and zirconium metal and elemental boron were also purchased as high-purity powders and characterized for impurities by emission-spectrographic analyses. The hafnium diboride was procured in three shipments which were designated as HfBl.g7(1), HfB1.88(2A), and HfB2.12(2). The indicated stoichiometry is based on the atomic ratio of total boron to total hafnium; the number in parentheses identifies the shipment number. Shipment 1 was 5 1b, shipment 2A, 1 1b, and shipment 2, 8 1b. The zirconium diboride was procured as a 20-1b shipment and designated as ZrB1.89(1). A small quantity of purified zirconium diboride was also supplied and designated ZrB1, 9(P). The averaged results for chemical analyses which were generally performed according to the procedures set forth in the compilation by KrieGe9 are presented in Table I. Qualitative spectrographic analyses indicated that Ca, Cr, Ti, Si, Zr (in H~B~), and A1 were present at levels between 0.01 and 0.10 wt pct. Other metallic elements were found to be less than 0.01 wt pct. Since it is virtually impossible to purchase these materials in the desired quantities (5 to 20 lb) as single-phase compounds it is necessary to obtain

Jan 1, 1968

By P. Chiotti, J. T. Mason

Ther?nal, X-ray, metallographic, and vapor pressure data were obtained to establish the phase diagram and standard free energy, enthalpy, and entropy of formation for the compounds in the Sw-Zn system. Four compounds, SmZn, SmZn2 , SmZn4.s, and SmZn8.5, melt congruently at 960°, 94Z°, 908°, and 940°C, respectively. The cornpounds SlnZns, Sm3Znll, and SnzZn7.3 undergo peritectic decomposition at 855", 870°, and 890C, respectively. Another compound of uncertain stoichiometry, SmZn11, undergoes peritectic decomposition at 760°C. Four entectics were observed with the following compositions in weight percent zinc and eutectic tenzperatures in degrees Centigrade: 12 pct, 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. An allotropic transformation and a composition range were observed for the SmZnz compound. The transfor)nation varies from 905" to 865°C as the zinc content increases from 16.0 to 48.5 wt pct, respectively. The free energy of formation of the compounds at 50PC varies between -15.9 kcal per mole for SmZn to -51.1 kcal per mole for SmZn,.,. Corresponding enthalpies vary between -19.2 to -78.3 kcal per mole. The ther-modynamic properties for the liquid alloys are described by the relations: A search of the literature revealed very little information on the Sm-Zn system. Chao et al.&apos; as well as Iandelli and palenzonai have reported the structure of SmZn to be cubic B2 type and Kuz&apos;ma et al3. have reported the structure of -sm2zn17 to be of the Th2Ni17 type. The purpose of this work was to establish the phase diagram of this system, to determine the zinc vapor pressure over the solid two-phase regions of the SYstem, and to calculate the thermodynamic properties of the compounds. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in this investigation were Bunker Hill slab zinc 99.99 wt pct pure and Ames Laboratory samarium. Analysis of the samarium by chemical, spectrographic, and vacuum-fusion methods gave the following average impurities in ppm: Nd, <200; Eu, <100; Gd, <100; Y, <50;Ca, 225; Ta, 400; Mg, 10; Cu, ~50; 0, 175; H, 20; and N, 15. The elements Fe, Si, Cr, Ni, Al, and W were not detected. The samarium was received as sponge metal and was kept under argon except when being cut with shears and when being weighed. Tantalum was found to be a suitable container for alloys with zinc contents up to the Sm2Znl, stoichio-metry. At higher zinc contents the grain boundaries of the tantalum containers were penetrated by the alloy and the containers failed during prolonged annealing. About 25 g of massive zinc and samarium sponge were sealed in tantalum crucibles equipped with thermocouple wells. These crucibles were in turn sealed in stainless-steel jackets. All closures were made by arc welding under an argon atmosphere. The samples were equilibrated in an oscillating furnace and in some cases were given various heat treatments in a soaking furnace. After appropriate heat treatment the steel jackets were removed and the alloy subjected to differential thermal analysis. The apparatus was calibrated against pure zinc and pure copper and found to reproduce the accepted melting points within 1°C. Alloys were subsequently subjected to metallographic examination and those of appropriate compositions were used for X-ray diffraction analysis and for zinc vapor pressure determinations. The vapor pressures were determined by the dewpoint method. Both the differential analysis and dewpoint measuring apparatuses have been described in earlier papers.4, 5 All alloy samples were etched with Nital (0.5 to 3 pct nitric acid in alcohol) except the samarium-rich alloys. These more reactive alloys were electro-polished in a 1 to 6 pct HClO4 in methanol solution at -700c at a potential of 50 v. EXPERIMENTAL RESULTS Phase Diagram. The results of thermal analysis are indicated by the points on the phase diagram, Fig. 1. Eight compounds and four eutectics were observed. The composition of the compounds and their melting or peritectic temperatures are given on the phase diagram. The four eutectic compositions in wt pct zinc and eutectic temperatures in % are: 12 pct,- 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. The stoichiometry of the most zinc-rich compound is still uncertain, but is very likely either SmZnll or SmZnlz. However, to simplify the presentation which follows it will be referred to as SmZnll. As shown on the phase diagram the phase regions for some of the samarium-rich alloys have not been unambiguously established. A sample of pure samarium was observed to transform at 924°C and to melt at 1074"C, in good agreement with corresponding val-

Jan 1, 1968

By Charles L. Thomas

A novel, highly sensitive, and reproducible nzetlzod for the determination of hydrogen in solid materials is presented. The procedure requires equilibration of the specimen with hydrogen gas, rapid quenching, and hot vacuum extraction of the dissolved gas with subse-quent quantitative analysis by mass spectroscopy. Good linearity is obtained for the Arrl~enius plots of the investigated metals. The advantages in the use of this method over that of Sieverts aye discussed. The solubility data for copper are in reasonable agveewzent with a considerable number of other inuestigations, wllile those fov silver are considerably lower than previously reported. The first known solubility data for gold are presented. Solubility equations and heats of MUCH of the data which are available on the solubility of hydrogen in various metals and alloys have been obtained by the classical Sieverts method.&apos; The method involves the measurement of a decrease in pressure of a gas in a calibrated system, and the calculated contraction in volume is attributed to the solubility of the gas in the metal sample. The procedure requires several corrections, such as the solubility of the gas in the container walls and the diffusion of the gas through these walls, as noted by Steacie and .Johnson2 and others. In addition, errors may be incurred due to reactions between metal surface impurities, such as oxides, and the saturating gas. The precise calibration of the measuring system where large thermal gradients exist can present additional difficulties. Also, accurate volumetric measurements of small quantities of gas are difficult. Many of the objections to the Sieverts method were overcome on solid materials by Ransley and ~eufeld,~ who first saturated the metal with hydrogen and performed a subsequent extraction and measurement of the gas by chemical means. Eichenauer and pebler4 and Eichenauer, Kiinzig, and pebler5 measured the diffusion coefficient and solubility by following the degasification of a sample as a function of a rate of increase in pressure in a previously evacuated system. Here again, however, the procedure involves many of the corrections of the Sie-verts method. The present investigation deals with the solubility of hydrogen in solid copper, silver, and gold by a technique which eliminates many of the aforementioned corrections and possible errors. This procedure requires equilibration of the specimen with gas, rapid quenching, and hot vacuum extraction of the dissolved gas with subsequent quantitative analysis by mass spectroscopy. EXPERIMENTAL Two completely separate systems were employed to accomplish first, the equilibrium saturation of the sample and second, the extraction of the dissolved gas. Saturation Apparatus. The saturation apparatus, illustrated in Fig. l, consisted of a vertically mounted quartz tube with a three-way valve for vacuum or hydrogen near the top and an outlet near the bottom leading to a butyl phthalate seal. The bottom end of the tube was terminated with a joint accommodating an O-ring sealed "Asco Stirring Gland" (The Emil Greiner Co.). This gland facilitated movement of the thermocouple without introduction of air into the system. The upper portion of the tube (above the furnace) was water-jacketed. A Welsh 1405-B mechanical pump provided the necessary system evacu-

Jan 1, 1968

By R. W. Smashey, B. J. Piearcey

The structure, composition, and morphology of the carbide phases present in the nickel-base superalloy, Mar-M200, hare been determined and three carbide phases observed. The MC carbide is a solidification product, and the M23 Co and M6C carbides are both prod~icts of solid-state precipitation. The identity of each phase usas determined by both X-ray and electron-diffraction techn~ques. Compositions of all three carbides were studied using the electron beam micro-probe analyzer and by unalyszs of electrolytically extracted residues. Optical and electron microscopy were employed in order that the time/temperature -dependent behavior of the carbides might be observed. Supplementary studies were completed on thin foils and oriented single crystals to determine the mor-phology and orientation relationship of each phase with that of the matrix. MAR-M~OO* is a high-temperature, creep-resistant superalloy designed for use in the as-cast condition. The "as-cast" microstructure consists of a solid-solution matrix, referred to as gamma (y), which contains a general, coherent precipitate of the inter-metallic Ni3(A1,Ti) referred to as gamma prime (?). As a result of dendritic segregation during solidification, a degenerate, spherulitic ? -?&apos; eutectic constituent is present at the grain boundaries and the in-terdendritic regions, which is nucleated by the y on the dendrite tips. A primary carbide phase, a solidification product, is also present at the grain boundaries and in the interdendritic areas, and an additional carbide appears at the grain boundaries as a fine discontinuous precipitate. The alloy is particularly susceptible to heat treatment. For example, the mechanical properties of the columnar grained mater- ial are substantially improved by solution heat treatment, followed by an intermediate temperature age. Metallographic examination of heat-treated material reveals, however, that exposure to elevated temperatures has a marked effect on the microstructure of the alloy; in particular, it is observed that precipitation of considerable amounts of various carbide phases occur. The following investigation was carried out to determine the morphology, composition, and behavior of the carbides in Mar-Ma00 as an aid to the determination of their effect on the mechanical properties and stability of the alloy. THE PRIMARY MC CARBIDE The MC carbide phase appears in the interdendritic interstices and the grain boundaries. In directionally solidified Mar-M200 the carbide appears as very small particles in the chilled region, Fig. l(a), whereas in material less affected by the chill, it becomes larger and develops a dendritic morphology, Fig. 1(b). Step polishing of metallographic specimens from this region shows that in directionally solidified material the individual carbide dendrites are connected in a dendritic network within the metallic interdendritic interstices, whereas in material from the chilled region and in conventional Mar-M200 they are discontinuous, isolated dendrites. No orientation relationship exists between the primary carbide and the matrix.

Jan 1, 1968

By J. F. Held

In a study of the influence of cold rolling on mechani cal properties of steel, it was found that the specific rolling procedure influenced crystallographic orientation. Properties developed by several rolling modes were determined and related to crystallographic orientation. Sanzples were cold-rolled various amounts on a laboratory mill. When palm oil was used as a lubricant, the crystallographic orientation was homogeneous throughout the thickness of the samples. Other samples were rolled without lubrication. Variations in intensity of the recrystallization texture components persisted throughout more than 50 pct of the volume of these samples. When the average plastic strain ratio, which is dependent upon crystallogvaphic orientation, was plotted as a function of percent reduction, a maximum was found at 40 pct in the samples which contained the observed texture variation. No maximum was found for the samples with the homogeneous texture distribution. Other mechanical properties, such as tensile strength and yield strength, were not influenced by the variation in crystallopaphic orientation. MECHANICAL properties of steel sheets depend, in general, upon the structural properties of the steel. For example, the Petch equation describes the relationship between yield strength and grain size. Other properties, such as hardness, vary with chemical composition. The plastic strain ratio, or R value, has been found to be dependent upon crystallographic orientation . In the course of investigating the effect of cold rolling on mechanical properties, it was found that a previously reported relationship between percent cold reduction and R value was not always observed. Published data had shown that the optimum cold reduction for best R values is 70 pct for aluminum killed steel.&apos; However, by altering the rolling conditions, the optimum reduction can be shifted to much lower values, or it can be moved to very high values. This paper describes the rolling conditions that lead to shifting of the optimum cold reduction. The effect of rolling conditions on the various structure parameters and the resulting mechanical properties are evaluated. EXPERIMENTAL PROCEDURE Samples of three low-carbon aluminum killed steels were cold-rolled various amounts on a 9-in.-diam 2-high laboratory mill. Hot-mill thermal practice and steel chemistries are listed in Table I. Steel A was rolled with palm oil lubrication and heavy reductions on each pass; i.e., a total reduction of 75 pct was ac- complished with a maximum of five passes. Steel B was rolled without lubrication, and light reductions were given on each pass. After approximately 75 pct reduction, it was necessary to use a small amount of light oil to achieve any additional reduction in thickness. Following cold reduction, the samples were box-annealed at 1300°F for 10 hr. The heating rate between 800" and 1300°F was 50°F per hr, and the cooling rate following the soak period was 50°F per hr. Tensile specimens were machined from the annealed material and these were used to measure yield strength, tensile strength, and the plastic strain ratio (R value). Recrystallization textures were determined by an inverse pole figure technique.*&apos;3 Integrated intensities of the (110), (002), (112), and (222) reflections were recorded for those planes lying parallel to the sheet surface. Examinations were made on both surfaces of each sample, and also at various levels beneath each surface to approximately 0.010 in. depth by etching techniques. RESULTS R Values. The R values obtained in steels A and B are shown as a function of percent cold reduction in Fig. 1. No optimum cold reduction was observed in steel A, rolled with palm oil lubrication. It is likely, however, that an optimum reduction would have occurred had higher reductions than 88 pct been employed. The optimum reduction in steel B occurred at 40 pct. The behavior in both of these steels is quite

Jan 1, 1968

By John F. Elliott, John P. Hager

The standard free energies of formation of the lowest stable sulfides of chromium, molybdenum, and tungsten in equilibrium with the corresponding metal hazle been determined by reacting the sulfide and metal with H2(g)/H2S(g) mixtures. The reaction is A method for estimating the standard ~nolav entropies and standard entropies of formation at 298°K of the sul-fides of refractory metals is presented. The standard free energies of formation of the lowest sulfides of the metals in group VIa of the periodic table are probably best determined with the reaction* is known with greater accuracy than is that property for any other sulfur-bearing compound or solution which might serve as a reference phase to establish the chemical potential of sulfur for the essential re- However, there still remain significant problems to the use of Reaction [I] in studying these sulfides. First, the equilibrium gas ratios (Ph2S/PH2) are very small, and with the most stable sulfides in the series the ratios tend to be at the limit of the range for precise chemical analysis (10-4); and second, the reaction rate for the formation or reduction of these sulfides appears to be relatively slow. A primary reason for the latter problem is that the gas phase near the equilibrium concentration has very little capacity for transport of sulfur. It is to be noted that the thermo-dynamic properties obtained from the experimental results by Eq. [I] apply for 1 g-atom of sulfur in the metal-saturated compound even though the exact composition of the compound has not been determined. The work reported here is a study of the standard free energies of formation of the lowest sulfides of chromium, molybdenum, and tungsten, and of copper, by Reaction [I]. In planning the experimental program, it was decided that the technique that has been used previously3"&apos; could be used with modification and that an improved analytical method was needed for determining H2S in the gas phase. THE EXPERIMENT The once-through flow of gas was selected in preference to recirculating the gas, a) because of the low sulfur capacity of the gas, b) because of the relatively slow rate of reaction and the danger of the

Jan 1, 1968

By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of- liquid Mg-Pb allojs have been determined by an isopiestic method from 18 to 42 at. pct Pb and by a thevmodynumic analysis of the phase diagram frofiz 0 to 100 at. pct Pb. In the overlapping composition range the magneszupn activity values derived by the two methods are in excellent agreement, thus mutually supporting the correctness of the Mg-Pb phase diagram previously determined by the authors and of the acticitzes deriz~ed isopiestically. SEVERAL studies have been made of the thermody-namic properties of liquid Mg-Pb alloys. Wagner and Engelhardt,1 Lantratov,2 Knappwost,3 Sryvalin et al.* and Wilson5 used the electromotive-force method, Scheil and Wolf8 and Schmahl and Sieben" applied the transpiration technique, and the present authors8 utilized the phase diagram to determine the activity of magnesium in the Mg-Pb system. The results of these studies are not in very good agreement and could not be incorporated into a general systematic analysis of the thermodynamic properties of the homologous series of the Mg-Group IV B systems Mg-Pb,8 Mg-Sn,° Mg-Ge,10and Mg-Si.11 The thermodynamic properties of the Mg-Pb system were therefore re investigated by an isopiestic technique which has been developed for similar studies in the Mg-SnB and Mg-Ge10 systems- Lead specimens, contained in iron or graphite crucibles, were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure to form alloys of compositions which depended on their temperatures, the temperature of the magnesium vapor source, and the thermodynamic properties of the system. EXPERIMENTAL PROCEDURE Magnesium (Dominion Magnesium Ltd., Toronto, Canada) of 99.99+ pct purity and lead (American Smelting and Refining Co.) of 99.999 pct purity were used. In the early experiments, Runs 2 and 3, the alloys were contained in uncovered high-purity iron crucibles. Alloys formed in the uncovered iron crucibles had to be chemically analyzed owing to the slight volatility of lead under the imposed experimental equilibration conditions. The compositions of these alloys were determined by a gravimetric analysis of lead as lead chromate. To avoid this problem, the remaining runs were made in covered graphite crucibles machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non- i reactivity of graphite with lead and magnesium has been previously established,&apos; and the experimental procedure has been described in full detail.&apos; In the runs using covered graphite crucibles it was found that the weight increases of the crucibles and their contents after equilibration equaled the magnesium contents of the alloys within the accuracy of the chemical analysis (i0.3 at. pct Pb). Clearly, the small lid openings of the graphite crucibles prevented significant lead losses during a run, and the weight increase was therefore taken as the magnesium content of the alloys. EXPERIMENTAL RESULTS At thermodynamic equilibrium the magnesium partial pressure of the specimens equaled that of the reservoir. Since the magnesium reservoir was always maintained at the temperature minimum of the system, the activity of magnesium of any specimen was given by the ratio of the magnesium reservoir pressure to the vapor pressure of pure magnesium at the specimen temperature. The standard state was chosen as liquid magnesium and the vapor pressure of liquid magnesium

Jan 1, 1968

By P. Chiotti, R. J. Hecht

Vapov pressure data of solid and liquid alloys along with phase diagram data WERE employed in calculating the thermodynamic properties for the Ca-Zn system. The relative excess partial molal free energy for zinc in the liquid alloys was fitted to the relation wnvre i is we tvmpvrutiirc in ucgrees neivtu ana in is the tr~ole fvaction. Relations for the standard free energy of fortnation for the eight cornpounds were developed. ThE phase diagram for the Ca-Zn system as determined by Messing et a1.&apos; is reproduced in Fig. 1. Earlier work on the phase diagram has been summarized by Hansen and Anderko2 and the very limited thermodynamic information for this system has been reviewed by Hultgren et a1.3 The heat of fusion for the compound CaZn2 has recently been determined to be 9260 cal per mole.4 Solubility data for calcium in zinc for the temperature range of 650" to 725°C were fitted by the relation and reported by Johnson and Dilloon5 In the present investigation zinc vapor pressure data were obtained by both the dewpoint and Knudsen methods in order to calculate the thermodynamic properties for liquid and solid alloys. The dewpoint method as employed in this work requires that only one of the components be significantly volatile, in this case zinc, and that the vapor pressure of pure zinc be known. For calculation purposes the vapor pressure data for pure zinc3 were fitted to the relations; for temperatures below 692.7K, the melting point of zinc. The corresponding free-energy relations for vaporization and sublimation of pure zinc are respectively. Some of the calculations also required knowledge of the free energy of fusion of zinc and calcium and the free energy for the 721°K allotropic transformation of calcium. The free energy of fusion of zinc was taken to be the difference between Eqs. [4] and [5], or The free energy of fusion and transition for calcium were based on the enthalpy values of 2040 and 222 cal per g-atom, respectively, as reported by Chiotti et al. 4 and the heat capacity data given by Hultgren et a1.3 and are represented by the relations, In the latter expression the difference in heat capacity between the a and 0 forms of calcium was neglected. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in preparing the alloys were Bunker Hill slab zinc, 99.99 pct pure, and Ames Laboratory calcium. The average impurities in the calcium in parts per million by weight, ppm, were N-17, H—77, Ba—216, Mg-15, Si—7, C—157, and Fe—9. The zinc was cleaned in dilute nitric acid and the calcium was used as received. The calcium was stored and handled in an argon-filled glove box and when removed from the dry box it was kept in an argon-filled desiccator. Tantalum was found to be a suitable alloy container. The alloy components were contained in a 1-in.-diam cylindri-

Jan 1, 1968

By L. R. Woodyatt, H. J. Beattie, C. T. Sims

Theories correlating the formation of u and related intermetallic compounds to the electron-per-atom density of binary and ternary alloys have appeared regularly in recent technical literature. These same principles can be modified and applied to complex precipitation-strengthened alloys such as the iron-, cobalt-, and nickel-base superalloys and the stainless steels. Since these complex alloys contain carbides and other phases that normally precipitate before the U-type phases, the nature and amount of the precipitated phases must be calculated first. The following general formula is then applied to the residual matrix composition of the alloy: element. The magnitude of the resulting number is indicative of whether the alloy will form a a -type phase. When these calculations (which are computerized) are systematically applied to alloys of knoun phase analysis, a breakoff in average electron-vacancy number is noted between U-free and U-prone alloys. Alloys with an average electron-vacancy number higher than the breakoff form a-type phases, while those with lower ones do not form these phases. This method could then be used to eliminate from consideration all experimental compositions that would precipitate undesirable phases. It also is useful in evaluating analyzed heats of alloys where minor heat-to-heat variations determine whether the alloy is o-free or o-prone. THE highly significant development of strong, ductile superalloys to provide reliable construction materials in the 1000" to 2500° F temperature range has been due principally to unremitting application of Edisonian techniques and logic by the dedicated physical metallurgists who have shouldered this responsibility. Tools such as the electron microscope, phase analysis, and computers to accomplish regression analyses have been used heavily, but the effort has been essentially practice of an art, rather than a science. The objective of this paper is to describe and illustrate application of some relatively fundamental principles to certain of these alloy systems in an attempt to remove some of the empiricism from the technology. Specifically, the work presented here deals with the use of periodic-group relationships to predict the formation of intermetallic phases which can occur in primarily austenitic (fcc) structures. Calculations that have been developed might be applied in the design of new alloys and the evaluation of known alloys, and thus have the potential of eliminating vast areas of unnecessary alloy preparation and evaluation. ALLOYING CONCEPTS AND STRUCTURAL FEATURES OF SUPERALLOYS Strength is produced in austenitic superalloys by three principle mechanisms: 1) precipitation of y&apos;; 2) formation of carbides; 3) solid-solution hardening by soluble refractory metals. The first mechanism requires the addition of aluminum and titanium, the second requires carbon and carbide-forming elements, while the third calls for the addition of molybdenum and/or tungsten. A considerable concentration of chromium is usually maintained to resist oxidation/corrosion, but it is also an important carbide-forming element. Fig. 1 shows a sketch and electron micrograph of the structure of a typical wrought nickel-base super-

Jan 1, 1967

By Jack L. Taylor

Single crystals of tungsten grown from powder -metallurgy swaged rod by high-temperative annealing were deformed in tetzsion at temperatures from 2500 to 5000 OF. Orientation of specittzen tensile axis, strained ratrix, and defortnation bands was determined optically by reflections from {110} etch pits. Slip traces meve analyzed and slip directiorz determined. Results indicate that {110}(111) , {112){111}. and {123}{111} type slip occur in tungsten over the terpe,atuve rutge investigated. Slip is orientation-dependent occuvring on tCuzt cowzbitzation oj slip plane and direction which has the highest critical resolved shear stvess. Overshooting appears to be a general occurrence between 2500&apos; and 5000°F. Dejornatiotz bands show rotation in a directiorz opposite to the yotation of tire tensile axis. DEFORMATION in bcc metals has been reviewed by Maddin and Chen,&apos; Keh and eissman,&apos; and most recently by Nabarro, Basinski, and olt. From these reviews it is apparent that some disagreement exists concerning the crystallography of plastic deformation in bcc metals. There is evidence of noncrystallo-graphic slip, the crystal slipping on or near a noncrys-tallographic plane in the (111) zone for which the resolved shear stress is greatest. There is also evidence to indicate that crystallographic slip occurs in the planes of the same zone. On the other hand, there is agreement that the close-packed direction ( 111) is the slip direction in bcc metals. Further, in pure bcc metals4 and alloys the operative crystallographic slip systems are strongly dependent on temperature. Both crystallographic and noncrystallographic slip have been reportede8 in tungsten, a group VIA bcc metal. The number of slip families which operate in the case of crystallographic slip, however, has been in question. The earliest study by oucher&apos; of single-crystal tungsten tested at temperatures of 1800 to 5000°F led to the conclusion that only {112)( 111) type slip operated. Raymond and eumann recently reached the same conclusion studying deformation by rolling of plasma-flame single crystals at 1800°F; however, only [loo] and [110] orientations were studied. Work at high temperatures by Leber and Pughs on tungsten and Chen and Maddin9 on molybdenum suggests that conjugate slip on nonparallel (110) planes may account for the slip on (112) and (123) planes found by others working with bcc metals. The present paper presents evidence of three families or modes of slip in tungsten in the temperature EXPERIMENTAL PROCEDURE Material. Standard microtensile specimens, 0.160 in. diam by 0.640 in. gage length, were ground from commercial powder-metallurgy swaged tungsten rod, type MK. Specimens were heated for 10 min at 5150°F or 6 hr at 5400°F in vacuum of 1 x 105 Torr or less to produce single crystals. At the lower temperature an average of two out of seven specimens heated in a group developed single crystals throughout the specimen length as shown in Fig. 1, the rest remaining wholly poly crystalline. At the higher temperature, three or four out of seven specimens became single crystal. Other than to note that Laue X-ray photographs generally showed sharp, well-defined spots, no attempt was made to assess crystal perfection or measure dislocation density. Two tungsten single crystals grown from the melt by the plasma-arc process were also used for this study.

Jan 1, 1967