By H. C. Fiedler

Heats of high purity iron containing 3.1 pct Si and be -tween 0.0003 and 0.0295 pct N were prepared by vacuum melting ad then pouring while in a nitrogen atmosphere with the pressure between 0 and 90 psi. Strip from a heat with 0.0184 pct N underwent complete secondary recrystallization during the final anneal. Heats with less nitrogen had too few Si3N4 particles to restrain normal grain growth, and the heat with higher nitrogen had too many particles to allow complete secondary recrystallization. In the hot-rolled structure, Si3N4 precipitates only at the grain boundaries, with the consequence that annealing after hot-rolling diminishes the ability to subsequently undergo secondary recrystallization. In contrast to this behavior, ALNprecipitates uniformly in the hot-rolled structure. Under 1 atm of nitrogen, Si3N, in 3.1 pct Si-Fe dissociates between 900" and 950°C; the solubility of nitrogen increases from 0.0010 pct at 900" to 0.0030 pct at 1200°C. The solubility of nitrogen in Si-Fe has been the subject of many investigations. Corney and Turkdogan1 heated a 2.83 pct Si alloy in nitrogen and found the solubility, under 1 atrn of nitrogen, to be 0.0019 pct at 900°C. They claimed that Si3N4 did not form in the alloy above 705°C in 1 atrn of nitrogen. Fryxell et al.2 heated samples of 3.25 pct Si-Fe containing 0.0025 pct N over a range of temperatures and then analyzed for total nitrogen by vacuum fusion and for nitrogen in solution by a modified Kjeldahl technique. At 900°C, they reported the solubility of nitrogen in equilibrium with Si3N4 to be 0.0011 pct. pearce9 found the solubility of nitrogen at 900°C under 0.95 atrn of nitrogen to be 0.0017 pct in a 3.06 pct Si alloy. He reported that Si3N4 does not form above 770°C in 1 atrn of nitrogen. Although internal friction measurements have given somewhat higher values for the solubility,4-6 if the solubility of nitrogen is as low as has been reported by most investigators, and if Si3N4 is stable up to at least 945°C at 1 atrn pressure of nitrogen as reported by Seybolt,7 a small amount of nitrogen in properly processed Si-Fe should be effective in promoting secondary recrystallization. The requirement is that in the final heat treatment there be enough small, well-dispersed particles of Si3N4 to restrain normal grain growth. Fast8 has obtained secondary recrystallization by nitriding high-purity 3 pct Si-Fe after hot-rolling to a thickness of 0.118 in., followed by processing to 0.012 in., and annealing. A large amount of nitrogen, 0.076 pct. was introduced during the nitriding heat treatment, but he has since reported9 that "a few hundredths of a percent" is sufficient. Small amounts of aluminum10 or vanadium" nitride are capable of promoting secondary recrystallization. Heats containing as little as 0.010 pct A1 or 0.042 pct V and from 0.006 to 0.009 pct N underwent complete secondary recrystallization at final gage, whereas heats with lesser amounts of aluminum or vanadium did not.l2 To be reported is the behavior of nitrogen in high-purity 3.1 pct Si-Fe, and the relation of this behavior to the ability to undergo secondary recrystallization. PROCEDURE Ingots weighing 1 lb were made by vacuum melting high-purity electrolytic iron (A104, Glidden Co.) and high-purity silicon (Monsanto Co.). The latter was used in preference to ferrosilicon to insure a low aluminum content. The design of the melting furnace permitted pouring with the furnace atmosphere either below or above atmospheric pressure. Accordingly, at the completion of melting, nitrogen was admitted to the desired pressure and the heat then immediately poured. The ingots were sound, with no indication of porosity. In Table I are listed the heats investigated, the nitrogen pressure at pour, and the nitrogen and oxygen contents as determined by vacuum fusion with a platinum bath at 1850°C, a procedure which insures measurement of the total nitrogen.13 In addition, all heats contained 3.1 pct Si and not more than 0.002 pct C, 0.003 pct S or 0.005 pct Al. It was subsequently found that the quantity of nitrogen contained in the heats in Table I does not necessarily represent that obtained under equilibrium conditions. For example, the ingot poured immediately after 1 atrn of nitrogen was admitted to the chamber contained 0.0093 pct N, whereas an ingot poured 3 min after the nitrogen was admitted contained 0.021 pct N and another poured after a 6-min delay contained 0.029 pct N. While some bleeding of the hot top occurred in the latter instance, the ingot when examined in cross section appeared sound. The ingots were heated to 1325°C in hydrogen and rapidly rolled to 0.080 in. in 3 passes. The roll speed of the final pass was reduced so as to increase the quenching effect of the rolls. The hot-rolled pieces were processed both as-hot-rolled and after heating for 3 min at 900°C in hydrogen. After cold-rolling to 0.026 in., the strips were heated for 2 min at 900°C in hydrogen, then cold-rolled to the final gage of 0.012 in. The loss of nitrogen in going from the ingot to cold-rolled strip was no more than 10 pct. The final heat treatment, which was for the purpose of develop-

Jan 1, 1970

By R. L. Stephenson

The effect of fabrication variables on the creep-rupture properties of TZM (Mo-0.5 pct Ti-0.08 pct Zr-0.03 pct C), Cb-TZM [columbium-modified TZM (7140-1.5 pct Nb-0.5 pct Ti-0.8 pct Zr-0.05 pct C)], and TZC (Mo-1.2 pct Ti-0.25 pct Zr-0.15 pct C) has been studied at 982º. 1093º, 1204º, and 1315°C for rupture times up to 1000 hr. The creep tests were performed in vacuum creep furnaces, employing cold-trapped oil-diffusion pumps, operating at pressures 2 X 10-7 tory. After-test chemical analyses showed no significant changes in interstitial content. The creep-rupture properties of TZM, fabricated according to current mill practice, were determined in the stress-relieved and in the re crystallized conditions to provide control data. Specimens of TZM, Cb-TZM, and TZC fabricated according to each of two experimental fabrication schedules were then tested. The schedules differed in terms of in-process annealing temperatures and warm -working temperatures. The data make several conclusions evident. Fabrication variables do indeed have a profound effect on the long-time creep-rupture properties of molybdenum alloys. Strengths of these alloys compare very favorably with those of other refractory metal alloys in the temperature range studied. FOR several years we have been engaged in the evaluation of the creep-rupture properties of promising refractory metal alloys. We consider the determination of these properties to 1000 hr at several temperatures necessary for a valid comparison. Such an evaluation indicated that the creep strengths of Mo-0.5 pct Ti and TZM (Mo-0.5 pct Ti-0.08 pct Zr-0.03 pct C) compare favorably with those of other refractory metal alloys. Tensile and recrystallization data of other investigators1,2 show an effect of fabrication variables. More specifically, those fabrication schedules which produce high strength through work hardening exhibit the least thermal stability. A similar conclusion was reported by perkins3 for Cb-TZM. This would lead one to expect that, in terms of creep, those materials showing higher strength at short times and low temperatures would exhibit lower strength at long times and high temperatures. If these expectations were fact, a substantial improvement could be made in these alloys by optimizing their fabrication schedule in terms of their anticipated service temperature. We therefore undertook a study of the effect of fabrication variables on the long-time creep properties of TZM, Cb-TZM (Mo-1.5 pct Cb-0.5 pct Ti-0.08 pct Zr-0.05pct C) and TZC (Mo-1.2 pct Ti-0.25 pct Zr-0.15 pct C). MATERIALS All materials used were supplied by the Climax Molybdenum Co. of Mich. Our original intention was to test the same heat of each alloy in different conditions. Fabrication difficulties prevented this; however, heats with nearly identical analysis were selected. The compositions of the materials used are listed in Table I. All materials were supplied in the

Jan 1, 1970

By L. Leibowitz, M. G. Chasanov, L. W. Mishler

A drop calorimeter system is described for use in measuring enthalpies to 3600°K. Data are presented for tungsten between 2800" and 3600°K. The enthalpy of tungsten in cal per mole between 2000° and 3600°K can be represented by the equation HºT- Hº298 = - 1.7622 X 103 + 5.7772T + 8.9861 where T is in degrees Kelvin. A tabulation of com -puted values is presented for heat capacity, entropy, and free energy function. A drop calorimeter has been constructed to carry out enthalpy measurements at temperatures to 3600°K. Samples are heated by induction1 and dropped into a commercial adiabatic calorimeter, modified for this purpose. The experimental temperature is limited by the melting point of container materials and compatibility of the container and its contents. Several high-temperature drop calorimeters have been described in the literature1-5 but none has been used at temperatures as high as those in the present work; our measurements of the enthalpy of tungsten range from 2800" to 3600°K. DESCRIPTION OF EQUIPMENT An overall schematic view of the equipment is shown in Fig. 1. Power for the induction coil is supplied by a 25-kw 250 kHz Ther-Monic generator coupled to an iron core RF transformer. The Sample capsule is suspended in the work coil by 10-mil diam tungsten wires which are wrapped around a horizontal 5-mil diam tungsten wire. The horizontal suspension wire is clamped between two massive copper electrodes which are fixed in an x-y motion device that allows adjustment of the position of the heated capsule from outside the vacuum chamber. The copper electrodes are connected by flexible copper straps to a 1250-joule (5 kv, 100 pfarad) condenser bank. When it is desired to release the capsule, the condensers are discharged through the horizontal suspension wire causing it to vaporize rapidly. Very reliable and precise release of the capsule is achieved in this manner. Experiments have shown that no heat correction is required for this discharge energy. As part of the temperature measuring system, two prism holders have been incorporated in the apparatus. The upper prism holder is in the main vacuum chamber itself, whereas the lower one is in a side arm attached to the drop tube below the gate valve. The upper prism is mounted on a rotary vacuum feed-through, and may be moved under a protective shield when not in use. This prevents deposition of vapors on the prism surfaces when temperature measurements are not being made. Similarly, the lower prism is mounted on a push-pull vacuum feed-through, and when not in use may be pulled into its side tube. The prism mountings are fitted with guides and stops so that they may be moved precisely into the desired position. The aim throughout is to minimize the time the prisms are exposed to vapors from the hot samples. At the high temperatures reported in this paper, only the lower prism was used. The upper prism holder in these cases was fitted with an additional radiation shield. By using a prism and viewport, the lower surface of the samples can be observed by an optical pyrometer. The measurements discussed in this paper were obtained with a Leeds and Northrup 8622-C-S series manual pyrometer which is estimated to be accurate to 0.5 pct. Pyrometer calibrations and prism and window corrections were carried out in the conventional manner6 using tungsten strip lamps calibrated by the National Physical Laboratory, Teddington, England. Prism corrections were rechecked after each use. All work to date has been done in vacuum, and no measurable change has been observed in the prism correction below -2300°K for the upper prism and below -2800°K for the lower one. The total time of exposure of the prisms is about 50 sec per run. At high temperature, the final temperature reading is corrected by using the final A value for the prism; see Ref. 6 for details of this procedure. The calorimeter is a modified Parr Instrument Co. (Moline, lll.), Series 1230 adiabatic calorimeter with automatic jacket control. Other authors5 have used a similar calorimeter with good results. The calorimeter jacket cover and calorimeter cover are attached to the drop tube which contains a radiation shield. This shield is a gold-plated copper disc which can be operated manually from outside the calorimeter. The receiver is attached below the radiation shield and is lined with tungsten. In a typical experiment, the calorimeter and its jacket water temperatures were adjusted to 0.000°K temperature difference. The sample was allowed to equilibrate in the furnace at the desired temperature for about 20 min. The initial calorimeter temperature was then recorded, the sample dropped, and appropriate shutters closed. After about 3 min, the drop tube and receiver were filled with helium to 60 torr. The final calorimeter temperature was recorded after it had remained constant over a 5-min period. The equilibration time in the calorimeter was about 25 min. Thermistor probes are used to operate a hot and cold water supply system to maintain the jacket temperature equal to the calorimeter temperature. For actual measurements of the calorimeter temperatures, a quartz thermometer was used (Hewlett Packard Dymec Thermometer, Model #2801A). This thermome-

Jan 1, 1970

By J. Waldman, M. B. Bever, A. K. Jena

The heats of formation at 273°K of 6 silver-rich Ag-Cd solid solutions and the heat of formation at 78°K of one solid solution have been measured by tin solution calorimetry. The heats of formation are analyzed in terms of the quasichemical theory. If the enthalpy diffel-ence between a hypothetical fcc form and the hcp form of cadmium is taken into account, this analysis does not lead to the conclusion put forth in the literature that electronic effects make significant contributions to the heats of formation of silver-rich Ag-Cd solid solutions. The temperature dependence of the heats of formation is appreciable and negative near 78ºK, but decreases gradually to nearly zero abore 400°K. The relative partial enthalpies per grarn -atom of silver at 541°K and cadmium at 532" and 541°K in tin have also been determined. THE composition range of the silver-rich Ag-Cd solid solutions stable at room temperature extends to about 40 at. pct Cd. Heats of formation of these solid solutions at 308" and 723°K have been measured by solution calorimetry.1,2 Heats of formation for an average temperature of 800°K have also been calculated from vapor pressures.2,3 The heats of formation deviate from the values predicted by the quasichemical theory above about 30 at. pct Cd. This deviation has been attributed to electronic effects at the Brillouin zone boundaries.2 The heats of formation of Ag-Cd alloys are essentially the same at 308", 723", and 800°K; consequently the temperature dependence of the heat of formation d?H/dT = ?Cp is vanishingly small, although from the exothermic heats of formation a negative value would have been expected. In the investigation reported here the heats of formation at 273°K of 6 silver-rich Ag-Cd solid solutions and the heat of formation at 78°K of 1 solid solution have been measured by tin solution calorimetry. The results are analyzed in terms of the quasichemical theory and the dependence of the heats of formation on temperature is discussed. The relative partial enthalpies per gram-atom of silver in tin at 541" and cadmium in tin at 532" and 541°K were obtained in the course of this investigation. The values of the temperature dependence of the relative partial enthalpies per gram-atom of silver in tin derived from the data reported by various investigators2,4-9 are contradictory. The literature contains only a value for 517°K of the relative partial enthalpy per gram-atom of solid cadmium in tin.2 EXPERIMENTAL PROCEDURES Samples of Ag-Cd solid solutions were prepared by melting weighed amounts of silver (99.99 pct pure) and cadmium (99.95 pct pure) in graphite crucibles under a flux of molten potassium chloride.10 The solidified ingots were sealed in evacuated Vycor tubes and annealed at 775°K for 10 days. The ingots were swaged and drawn into wires. The wires, sealed in evacuated Pyrex tubes, were held at 725°K for 5 hr and cooled to 365°K at an average rate of 2.5ºK per hr, followed by furnace cooling to room temperature. Chemical analysis of samples taken from different parts of each ingot gave no indication of segregation. Metallographic examination showed the samples to be homogeneous. Samples of the solid solutions or of the component elements were added to tin-rich baths in a calorimeter." At the start of a run the bath consisted of pure tin. Silver was used in the form of wire of 0.01-in. diam as supplied and cadmium in the form of lumps. Gold (99.999 pct pure) was added with the samples in order to reduce the endothermic heat effect of additions of Ag-Cd solid solutions. Samples of only one composition were added in a run and the ratio of the weight of alloy to that of gold was the same in all additions of a given run. In each run several calibrating additions of tin were made from 273°K. The heat contents of tin were calculated from the following equation, which is based on published data:12 (HTºK- H279º) = 6.70 T - 72,300/T + 20 cal/gram-atom; 505°K < T < 650°K The heat effect of each addition was plotted against the average of the sum of the atom fractions of solutes in the solution before and after that addition. The total concentration of solutes at the end of a run was less than 2 at. pct. In this range the heat effect was a linear function of the atom fraction of the solutes. The heat effect at infinite dilution and the composition dependence of the heat effect were obtained from the plots. RESULTS AND DISCUSSION Evaluation of Data. The linear dependence on composition of the heat effects of additions suggests that in the dilute range the enthalpy interaction coefficients other than the first-order coefficients of silver, cadmium, and gold are negligible, as shown in a concurrent publication.13 The heat effects at infinite dilution and the values of the composition dependence of the heat effects are listed in Table I.

Jan 1, 1970

By J. E. Dutrizac, R. J. C. MacDonald, T. R. lngraham

When sintered disks of synthetic chalcopyrite (CuFeS2) were leached in acidified aqueous solutions of ferric sulfate, the following reaction stoichiometry was obtained: CuFeS2 + 2Fe2(SO4)3 = CuSO4 + 5FeSO4 + 2S Over the temperature range from 50º to 94ºC, the reaction displayed parabolic kinetics. The parabolic rate constant for the dissolution of copper is given by the equation: log.k(mg2/cm4-hr)= 11.850 - 3780/T The activation energy for the dissolution process is 17 ± 3 kcal per mole. The parabolic kinetics have been attributed to the progressive thickening of a sulfur film on the surface of the chalcopyrite. When the leaching solutions contain less than 0.01 molar Fe+3 , the Fe concentration influences the rate of leaching, probably through a mechanism involving the diffusion of ferric sulfate through the sulfur layer. At higher Fe+3 concentrations, the rate control in the leaching. reaction has been attributed to the diffusion of ferrous sulfate through the sulfur. The rate of reaction is insensitive to changes in acid concentration and in disk rotation speed. ThE reaction of acidic ferric sulfate solutions with various sulfide minerals is of practical interest for both bacterial and heap leaching. This leaching medium is generally used with low-grade ores that cannot be treated profitably by conventional means. In both bacterial leaching1-3 and heap leaching, the active agent for sulfide dissolution is ferric sulfate. Although the reactions of ferric sulfate with chalcocite, covellite, and bornite have been investigated,4*7 the kinetics of leaching chalcopyrite with ferric sulfate have not been thoroughly studied. This paper reports a study of that reaction. EXPERIMENTAL Reagent-grade sulfur was purified by the method of Bacon and FanelliB and then it was vacuum-distilled to remove any soluble magnesium salts that had been introduced during the purification procedure.9 From stoichiometric quantities of the purified sulfur and hydrogen-reduced electrolytic copper sheet (99.90 pct Cu), CuS was synthesized at 450°C in a vacuum-sealed, pyrex vessel. About 24 hr was required for the completion of the reaction. A similar procedure involving hydrogen-reduced iron wire (99.90 pct Fe) was used to synthesize FeS1.002. A 2-furnace arrangement was required. The iron was heated to 800°C while the sulfur was maintained at about 400°C. Although the reaction to consume the sulfur was rapid, the material required additional heating (1 week) in a sealed silica ampoule at 800°C before it was homogenized. X-ray powder diffraction analysis confirmed that the copper sulfide was covellite and that the iron sulfide was troilite. The composition of the iron mineral was confirmed by wet chemical analysis. The two sulfides were ground to minus 100 mesh, weighed in equimolar amounts, mixed thoroughly, and pressed into pellets at 80,000 psi. The pellets were vacuum-sealed in pyrex ampoules and then sintered for 3 days at 550°C after an initial heating at 450°C for a few hours. The pellets were then cooled, polished with 3/0 emery paper, rinsed in acetone, and stored. The material had the characteristic brassy color of chalcopyrite and was shown by X-ray diffraction to be CuFeS2. Microscopic examination of the polished surfaces revealed small inclusions of pyrite (approximately 0.5 vol pct) as the only impurity. The presence of small amounts of a second iron compound will not alter the amount of dissolved copper but might increase the amount of ferrous ion slightly. It was calculated that dissolution of all of the pyrite and 100 mg of Cu (a typical value) would change the expected ferrous concentration by only 4 pct. Microscopic examination of a pellet after leaching revealed that the pyrite was not preferentially solubilized; only those pyrite grains at the surface were attacked. Hence, the pyrite is unlikely to alter the rate of copper dissolution. The chalcopyrite disks were about 1.7 mm thick and 27 mm in diam. They were about 80 pct of theoretical density, and for this reason their true reaction area was somewhat larger than the 5.8 sq cm area presented by the polished face. The disks were cemented to lucite cylinders in such a way that only the polished face was exposed. The disks were then leached by methods previously described.6,7 RESULTS AND DISCUSSION Stoichiometry and Kinetics. The initial experiments were directed to the problem of resolving the stoichiometry of the leaching reaction. Disks of CuFeS2 were leached at 80°C for various periods of time in acidified ferric sulfate solutions that were protected from oxidation by a cover of flowing nitrogen. When the disks had been partly leached, they were removed, their soluble salts were washed out, and then they were treated with CS2 in a Soxhlet extraction apparatus. The ratio of elemental sulfur to dissolved copper thus obtained was approximately 2 to 1. After the extraction of elemental sulfur from the pellet, the residue consisted of unreacted chalcopyrite only. For runs in which an appreciable amount of copper was dissolved, the ratio of ferrous ion to cupric ion in the solution was

Jan 1, 1970

By T. Toda, R. Maddin

A study has been made of the microstructure and mechanical properties of splat-cooled aluminum-base gold alloys with gold concentration from 0.25 to 5.0 wt pct. These alloys have been quenched from the liquid state by a torsion-catapult technique, which has made it possible to pepare specimens suitable for mechanical property measwements. From the electron micrographs it has been shown that the solid solubility of gold in aluminum can be extended to 2.5 wt pct (0.35 at. pct) by splat-cooling, while the maximum equilibrium solubility is known to be less than 0.3 wt pct (0.04 at. pct). The very fine grain size (several tenths of a micron), the extended solid solubility, and the fine dispersion of a second phase (AuAl2) contribute concurrently to a substantial strengthening effect. In Al-5 wt pct Au splat-cooled specimens of less than 50 thickness, the yield strength is 17 kg per sq mm or 6 times as large as the strength of bulk specimens. For the Al-1.0 to 2.5 wt pct Au solid solution obtained by splat-cooling, the yield strength reaches 7.5 kg per sq mm after an aging treatment (for 10 hr at 200°C), while it is 3.7 kg per sq mm for the corresponding bulk specimens. A great deal of research has been done in recent years on the structure and the properties of metals and alloys rapidly quenched from the liquid state.&apos; The term "splat-cool" has been used with the meaning of a rapid quenching from the liquid state., The splat-cooling techniques have produced large numbers of new structures, which are expressed in terms of metastable phases,3 concentrated solid solutions,4 amorphous phases,5&apos;6 new phases,7 and so forth. Nearly all previous studies have concentrated on the physical properties; i.e., crystallography, structure, electrical resistivity, magnetism, and so forth, of the splat-cooled metals and alloys. The mechanical strength of splat-cooled metals and alloys has hardly been investigated except for some recent work by MOSS&apos; on A1-V alloys. The principle common to all experimental techniques developed to obtain very rapid quenching rates is based on the heat transfer by conduction. Liquid must be in good thermal contact with a substrate of high heat conductivity. Both of the published devices known as the "gun" and the "piston and anvil" techniques suffer from certain shortcomings. For example, the specimen obtained by the gun technique is very small and flaky, and hence inadequate for mechanical properties measurements. On the other hand if the material is forced to yield a continuous speci- men by the piston and anvil technique, it is probable that some plastic deformation occurs during the quench. A novel method for rapid quenching of a liquid metal or alloy, the "torsion-catapult", has been devised by Roberge and Herman9 at the University of Pennsylvania. In the apparatus the melt is thrown out of a curved furnace by a catapult and impinges on a copper substrate. The apparatus has the advantage of producing a continuous foil which is relatively large in size and of a quality suitable for the measurements of mechanical properties. The quenching rate is estimated to be of the order of l05 to l06 ºC per sec, (comparable to rates achieved by the piston and anvil technique). In selecting an alloy to be studied we were made aware of the fact that gold was believed to be "insoluble" in in and consequently age hardening in the A1-Au system appeared to be interesting. Quite recently Heirnendahl13-15 revealed that the solid solubility, as determined by transmission electron microscopy, was 0.3 wt pct Au at 640°C and 0.25 wt pct Au at 600°C, decreasing with decreasing temperature. In an A1-0.2 pct Au alloy after quenching from a solution treating temperature of 600°C the yield stress was 2 kg per sq mm, and it increased up to 6 kg per sq mm after aging for 1 to 10 hr at 200°C. The precipitation occurred in the form of platelike particles mainly on (100) matrix planes. The intermediate phase n&apos;, the equilibrium phase n (AuAl2), and lattice relationships between both precipitates and the matrix were also investigated by electron microscopy. One of the purposes of the present research is to determine whether or not the solid solubility in this system, in which gold has a very small solubility in

Jan 1, 1970

By J. C. Swartz

New measurements of graphite and cementite solubilities in ferrite have been obtained to resolve disagreements among previous data. To measure graphite solubility, specimens of iron were equilibrated with rarious carburizing atmospheres at temperatures be-twee~z 480" and 1435°C. The carbon activity of each atmosphere relative to graphite was taken from published data. After quenching from each equilibration treatment the concentration of carbon (typically 10 pprn by wt) was determined from the height of the Snoek peak in the internal friction spectrum. A few inclividual analyses by combustion support the reszdts of Smith on the solubility of graphite near the eutectoid temperature. Combination of these combustion and internal friction analyses determines In a, (at 0.01 wt pct) = 24,000/RT - 12.72, where a, is the activtity relative to graphite in ferrite at fixed cornposition. The same specimens were used to determine the solubility of self-stressed cementite precipitates. The results indicate solubilities of 6.3, 23.2, and 68 pprn carbon by wt at respectively 400°, 500". and 600°C. The once large discrepancy between the cementite solubility determined by internal frictiori and that calculated from flee energy data has been almost completely resolved. A recent study1 (hereafter designated I) on the solubility of cementite in a iron did not fully resolve the disagreement among previous data. The remaining disagreement is illustrated by the phase diagram in Fig. L The data of I are represented by the line labeled "stress-free" cementite. They determine a heat of solution of cementite of (14.8 * 0.2) kcal per mole which contrasts with the (20 * 1) kcal per mole derived from Smith&apos;s graphite solubility2 and the formation energy of cementite.3 Toward resolving this disagreement we have obtained new data on the solubilities of graphite and cementite. METHODS As in I the Snoek peak in the internal friction spectrum was used to measure the concentration of carbon dissolved in ferrite. This method relies on the relation C=kQ-1 [1] in which C is the concentration of dissolved carbon, Q-I is the Snoek peak height, and k is a proportionality factor which is a function of the peak temperature, polycrystalline texture, and other parameters characteristic of the ferrite lattice. To determine true heats of solution via Eq. [1], it is necessary to establish that k is independent of the temperature from which the specimen is quenched. Some evidence on this point is contained in a separate report.* Additional evidence is shown by the data points in Fig. 1. These represent the Snoek peaks of two specimens carburized to about 10 ppm C, copper plated, and quenched first from 888º then from 588°C. The copper plate was removed before each Snoek peak measurement. These data show that there is no detectable dependence of k on quenching temperature. The solubility of graphite was determined by repeatedly carburizing various specimens of iron wire with gas mixtures of known carbon activity relative to graphite. To cover a wide temperature range within the a phase boundaries it is desirable to use as low a carbon concentration as is compatible with reasonable precision. With the present internal friction apparatus the best compromise of these desires is a concentration near 10 wt ppm. The dashed line in Fig. 1 was used to approximate the activity of carbon* for

Jan 1, 1970

By Peter Soo

Pvestrained Ferrovac E iron has been neutron-irradiated at approximately 90°C to an integrated flux of 1020 nut (E > 0.82 mev]. The irradiation was found to produce an incveased temperature dependence of the flow stress in addition to a greatly increased athemal stress. Measurements of the flow stress and stress relaxation, from which the activation volume and activation energy for slip were deduced, show that neutron irradiation changes the rate -controlling slip process to one based on dislocation interactions with tetragonal distortions which are Produced around submicroscopic interstitial loops in the lattice. The study indicates that without prestraining prior to irradiation the chances of detecting a change in the rate -controlling slip process are greatly reduced because in the initial stages of slip a substantial fraction of the radiation defects are swept out of the slip plane by gliding dislocations. Thus, activation parameters which are subsequently measured are representative of a greatly reduced defect density and would not differ appreciably from those for unirradi-ated material. The large increase in the athermal component of the flow stress is probably connected with the presence of depleted zones in the lattice which are introduced by irradiation. ALTHOUGH fast neutron-irradiation has not been observed to markedly alter the activation parameters for slip in bcc metals,&apos; small but significant changes do occur. Most experimenters agree that irradiation predominantly increases the athermal component of the yield stress.&apos;-= In addition to this, Laidler and smidt7 have shown that in iron irradiated to 5 X 10" nvt and molybdenum irradiated to 10" nvt, changes occur in the activation volumes for slip. A similar conclusion has been reached by Milasin and Malkin8 for irradiated iron. Work by Ohr et a1.5 shows that for Ferrovac E iron, irradiated to 1.2 X 1016 nvt, small increases in the activation energy for slip also occur. So far these changes in the activation parameters have not been explained on a firm theoretical basis. One important factor which would minimize the chances of detecting a change in the slip mechanism upon irradiation is the presence of "channeling" which has been observed in molybdenum,9 niobium,10 and iron.11These channels are formed by gliding dislocations which sweep irradiation defects out of the active slip planes and thereby create zones in which continued dislocation motion is encouraged. The activation parameters for the dislocations gliding in the defect-free channels would, therefore, be similar to those for unirradiated iron and a change in the rate-controlling slip process would be difficult to detect. In the present work, an attempt has been made to reduce the effect of uneven deformation on the measured activation parameters for slip in neutron-irradiated Ferrovac E iron polycrystals, so that a more realistic assessment of the effects of neutron-irradiation could be made. Primarily, the experiments involve the irradiation of specimens which had been prestrained to 9 pct elongation at room temperature prior to insertion into the reactor. It was hoped that the introduction of a large number of evenly distributed dislocations would substantially decrease any channeling effect which might otherwise occur. MATERIAL AND EXPERIMENTAL PROCEDURE The starting material was vacuum-melted Ferrovac E iron, an analysis of which is given in Table I. The standard tensile specimen had a gage length of 1.125 in., a cross-sectional diameter of 0.120 in., and a re-crystallized grain size of 1.2 x 10-3 in. All tensile tests were conducted on a floor model "Instron" tensile machine at a strain rate of 3 x 10-4 per sec. The irradiation of the prestrained specimens was performed in the Brookhaven High Flux Beam Reactor to an integrated flux of 1020 nvt (E > 0.82 mev) at a temperature of about 90°C. All specimens were excap-sulated in high-purity aluminum sheaths which were lightly swaged around the samples to ensure good thermal contact. Subsequent measurements on the irradiated specimens showed that within experimental accuracy the swaging had not deformed them. EXPERIMENTAL RESULTS Fig. 1 shows the flow stresses for a series of unirradiated control samples. In order to produce a comparable dislocation substructure throughout the test sm range, all specimens were prestrained

Jan 1, 1970

By Barry D. Lichter, Pierre Sommelet

High-temperature heat contents of InAs and GaAs were measured over the temperature range 400°K to temperatures above the melting points using a di-phenyl ether drop calorimeter. Smoothed values of the thermal properties have been derived and tabulated at even temperature interuals . The heats of fusion of InAs and GaAs were determined as, respectively, 8790 ± 200 and 12,590 ± 300 cal per g-atom at the respective melting points of 1210º ± and 1513º ± 1°K, yielding entropies of fusion of 7.26 * 0.16 and 8.32 ± 0.20 cal perºK per g-atom, respectively. A general discussion of the thermal properties of III-V com-pounds is given. THE low-temperature heat capacities of InAs and GaAs have been determined by Piesbergen.1Using a dynamic temperature modulation technique, Miller2 has determined the heat capacities of the compounds as well as GaSb and Ge between room temperature and 650°K; however, it has been observed that values determined by drop calorimetry for GaSb3 and for germanium4 are consistently about 5 pct lower than Miller&apos;s results. Cox and Pool10 report values for the heat content of InAs and GaAs and the heat of fusion of InAs. No value for the heat of fusion of GaAs appears to have been previously reported. This paper reports results of high-temperature heat content investigations of InAs and GaAs measured in the range 400" to above 1500°K employing a diphenyl ether drop calorimeter. These results, together with our previous results on III-Sb compounds3 as well as heat-content measurements5 of solid InP and Gap, are used in a general discussion of these compounds. EXPERIMENTAL PROCEDURES High-purity samples of the compounds, stoichio-metric to ±0.1 at. pct, were supplied in the form of crushed crystal fragments by Dr. Carl Thurmond of the Bell Telephone Laboratories. The sample preparation, description of the calorimeter, and details of the heat content measurement have been previously described.3 Samples were sealed in evacuated silica capsules and suspended by a Pt-Rh wire in a Pt-wound vertical tube furnace, heated to temperature

Jan 1, 1970

By S. S. Shen, M. J. Pool, P. J. Spencer

Heats of solution of gold and copper in dilute Au-Cu-Sn alloys have been determined using a liquid metal solution calorimeter. The self-interaction coefficient, Au - has been calculated at constant copper concentrations and n cu has likewise been determined at constant gold contents. Good experimental agreement is obtained between the interaction coefficients and nAu Cc thus demonsbating the reliability of the measured heat values. The measured data are compared with the Predictions of certain solution models. In previous publications,1,2 the results of calori-metric investigations of dilute Ag-Au-Sn and Ag-Cu-Sn alloys have been presented. The present work on the Au-Cu-Sn system concludes a program of studies of enthalpy interaction coefficients in dilute alloys of the Group IB metals with tin. Since the definition and derivation of an enthalpy interaction coefficient has been discussed previously,1,2 no restatement of this theory will be presented here. From the determination of the partial heat of solution of gold and copper in ternary alloys of various copper and gold contents, values of the interaction coefficients can be calculated. These coefficients give an insight into the various solute interactions that occur in the liquid solutions since changes in their magnitude and sign reflect bonding changes that are taking place in alloys of varying solute contents. EXPERIMENTAL Details of the design and operation of the liquid metal solution calorimeter used in this work may be found in a paper by Poo1.3 For the present studies copper of 99.999 pct purity was supplied by American Smelting and Refining Co., gold of 99.999 pct purity by A. D. Mackay, Inc., and tin of 99.99 pct purity by Baker Chemical Co. At the commencement of each series of experimental drops, a tin solvent bath consisting of between 70 and 90 g of the pure metal was inserted in the calorimeter. The weight of the bath was accurately determined and to it were added appropriate amounts of gold or copper to give alloys of the desired composition. For determinations of approximately 0.0015 g-atom samples of Cu were used and for measurements of ?HAu approximately 0.0025 g-atom additions of Au. The heat capacity of the bath was determined at regular intervals during a series of drops using tin calibration samples. Measurements were made of the heat of solution of copper in alloys containing a constant 0.01, 0.02, 0.03, and 0.04 mole fraction of Au, respectively, in order to determine ?HCu in each alloy, and the same mole fractions of copper were used to determine equivalent values for nAu at constant copper concentrations. The composition of the bath was maintained at the desired constant gold or copper content by making calculated additions of the appropriate solute throughout the experiments. The limiting values ?HAu in alloys of constant copper content and of %c, in alloys of constant gold content were studied as a function of the mole fraction of copper or gold respectively in order to determine and nCu. Heat content and heat capacity data used in calculating values of ?ºHAu and ?HCu at the experimental temperature of 720°K were obtained from Hultgren et a1.4 &apos; RESULTS AND DISCUSSION Determinations of ?HAu. The partial heat of solution of gold in pure tin as a function of gold concentration was determined in the previous study of dilute Ag-Au-Sn alloys1 and can be represented by the least-squares expression: ?HAu(l) =-8075 + 2413xAu [l] which is valid between XAu= 0.00 and xAu = 0.05. The standard error in the constant term, which represents the partial heat of solution of gold at infinite dilution in tin,?HºAu(l)is 35 cal per g-atom, while the standard deviation of the slope, which represents n Au is ± 619 cal per- agtom. Corresponding expressions for ?HAu(l) in alloys containing constant mole fractions of 0.01, 0.02, 0.03, and 0.04 copper were obtained from the data listed in Table I and are themselves given in Table II. Fig. 1 illustrates the partial heat of solution of gold as a function of its concentration in each of the alloys. For the four alloys of constant copper concentration, the values obtained for ?HºAU(l) (in order of increasing copper content) are -8141 i 36 cal per g-atom, -8210 ± 42 cal per g-atom, -8202 ± 46 cal per g-atom and -8268 ± 51 cal per g-atom. The corresponding values of the self-interaction coefficient, n Au, for these alloys are 3103 * 644 cal per g-atom, 2425 ± 676 cal per g-atom, 2574 * 717 cal per g-atom and 2523 ± 899 cal per g-atom. In Fig. 2 these values of n Au are plotted as a function of the copper content of the alloys and are seen to remain approximately constant within the experimental limits. The addition of increasing, small amounts of copper to dilute binary Au-Sn alloys thus has no apparent effect on Au-Au interactions in these dilute liquid solutions, although more exothermic values of ?HºAu(l) do result from an increase in the copper content of the alloys. Analogous behavior was observed with additions of silver to dilute Au-Sn alloys.&apos; By

Jan 1, 1970

By E. T. Turkdogan, L. S. Darken, R. J. Fruehan

Further consideration is given to the application of the quadratic formalism to evaluate the thermodynamics of binary metallic solutions from experimental data. The use of the thermodynamic relation, in(r1/r2) dN2= 0, in the evaluation of activity data is discussed. The empirical correlations derived previously for enthalpies and entropies of solutions in Part II are shown to be predicted theoretically for a special case. The applicability of the quadratic formalism to the activity coefficients for binary organic solutions is demonstrated. DARKEN&apos; introduced a quadratic formalism describing the composition dependence of the activity coefficient in the terminal regions of binary metallic solutions. In a subsequent paper (Part II) Turkdogan and Darkeen2 extended this formalism to the enthalpy and excess entropy of binary metallic solutions, and showed that the available data for the activity coefficients and heats of mixing of many solid and liquid binary metallic solutions confirm reasonable applicability of the quadratic formalism. Much variation was noted, however, in the extent of the terminal regions from one system to another, commonly from about 10 to 70 at. pct. For the present purpose, equations derived previously need be given only for one of the terminal regions, e.g. region (I), 0 < N2 < N&apos;2: where subscripts 1 and 2 indicate quantities for components 1 and 2 and superscript ° the values at infinite dilution; other terms are: N = atom fraction, y = activity coefficient, = partial molar enthalpy of solution, ?HM = molar heat of solution, ?Sx = excess partial molar entropy, ?Sx = excess molar entropy. The heat and entropy like terms (constants) el, and S12 are defined in the following expression for the temperature dependence of a12, thus a12 £12 — s12 rnl 2.303RT 2.303 R l J Using this formalism, the thermodynamics of binary systems in the terminal regions may be described over a temperature range of experisental interest in terms of eight quantities: Lº1—Lº2, ?Sx1,?Sxº2 , £12 ,£21,fiai, S12, and S21. In the previous paper, these quantities were evaluated for many solid and liquid binary solutions, and two significant correlations were observed between these thermodynamic quantities pertaining to the terminal regions, thus [10] and [11] Combining Eqs. [9], [l0], and [ll] and rearranging gives a12 -a21 = 1.382R log rº2- 0.08(?S2xº- ?S1xº) [12] Since the second term involving entropies is small and Eqs. 1101 and [ll] are empirical relations, the above equation may be simplified to a12 = 2.74 log rº2 [13] Using the values of a&apos;s and y°&apos;s compiled in Parts I and 11, a12 - a21 is plotted against log(rº2/rº1) in Fig. 1; the line drawn has a slope of 2.74. For Hg-K at 300°C, log(yº2 /yº1)= —5.10, not shown in Fig. 1, and from correlation [13], a12 - a21 = -13.97; this is to be compared with -10.76 derived from the activity data (Part II).

Jan 1, 1970

By R. A. Pasternak, B. Evans

A dynamic technique for the determination of solubilities of gases in metals has been explored, using the N-Nb system as a test case. An initially clean sample, maintained at constant high temperature, is exposed to the gas at low pressure: the rate of sorp-tion and the corresponding change in sample resistance are measured continuously. A pronounced decrease in the slope of the resistance concentration curve is observed at the terminal solubility. The rate of gas uptake by the sample was determined in an ultrahigh-vacuum flow system equipped with a servo-control which maintains constant pressure in the sample chamber; the system and the technique have been described in detail elsewhere. 1,2 The sample was held at constant temperature during sorption by maintaining approximately constant power input into it; this results in constant temperature, since the emissivity of a metal is independent of moderate concentrations of dissolved gas. The simple electrical circuit used both for heating and for resistance measurement is shown in Fig. 1. The power input into the filament is where R is the filament resistance, RL is an adjustable resistance in series with the filament, and VT is the constant dc potential of the power source. If RL is set equal to R at the beginning of an absorption run, the power input becomes insensitive to subsequent resistance changes; for example, an increase of 20 pct in sample resistance is accompanied by a decrease in power input of less than 0.8 pct; i.e., the

Jan 1, 1967

By A. J. Opinsky

ThE superior performance of nonsag tungsten wire in lamps has been ascribed to the large-grained micro-structure that can be developed in it. The orientations of these large grains have been studied several times; most published data1-&apos; appear to be similar to those plotted in Fig. 1. These new data were obtained by X-ray back-reflection Laue technique from all of the large grains occurring in thirteen different wires that had been heated at the lowest possible temperature for the formation of large grains. Here the wire axis is plotted in terms of the principal directions of the cube. Rosi decided that the preferred orientation of the large crystals could be described by a single ideal orientation, (531), being parallel to the wire axis.&apos; Rieck2,3 and Mannerkoski&apos; have essentially confirmed this finding. Opinsky, Orehotsky, and Seigle argued that the data suggest that (211) is parallel to the wire axis instead of a single ideal orientation.5 This {211} contains the (531) ideal orientation and would appear to be a more general case. Ahlborn and Wassermann report that their orientation data stretch from ( 110) through (531) to (311) 8 This is part of the locus of (211). All these investigators have determined the orientations of the large grains by back-reflection Laue techniques. They have all obtained essentially similar results. On the other hand, Swalin and Geisler, who obtained their data by neutron diffraction, indicated that the preferred orientation of the large grains in doped wire is (110) .7 These findings cannot presently be reconciled with the pole density data described in the previous paragraph. Rosi1 and Rieck2 have advanced arguments about how their orientations could occur. Nevertheless, the crystallographic link between the (110) (cold-worked) fiber texture and the preferred orientation of the large grains has remained missing. This link can be provided through the concept of coincidence-type boundaries. Such boundaries separate two grains that have a certain number of common lattice sites. Coincidence relationships that result from rotations about low index directions are given by Brandon et a1 .&apos; What is desired is a calculation of those orientations that bear a coincidence relationship with the (110) fibers of the cold-worked matrix. This situation arises in the following fashion. Heating the tungsten wire for a combination of time and temperature falling short of the formation of the nonsag structure yields a structure that is still fibrous in nature and the preferred orientation remains (110). During grain growth, the growing grain is in contact with these fibers. It is hence possible that the entire process may begin by the passage of a coincidence boundary into a (110) fiber. The calculations were carried out analytically and checked graphically. Following Brandon et a1.,8 coincidence relationships from 1 in 5 to 1 in 19 have been considered. The results of the calculations are given in Fig. 2. Of the coincidences examined, some of those occurring upon rotation about ( 110) come closest to the experimental points in Fig. 1. Nineteen of the twenty-three data points in Fig. 1 can be attributed to the ideal orientations A, B, C, and D in Fig. 2. As determined analytically, three crystals lie within 4 deg of point A, four lie within 21/2 deg of point B, eleven lie within 5 deg of point C, and one lies within 1 deg of point D-a total of nineteen. The off-lying points are near the |110| point of the triangle.

Jan 1, 1968

By J. C. Scully

In June, 1965, Sanderson and scully5 reported at the Conference on Environment Sensitive Mechanical Properties of Materials at the Research Institute for Advanced Studies at Baltimore that thin foils of titanium could be prepared by chemical polishing in a mixture of 44 pct HF and 73 pct HNO3 in the volumetric ratio 2:3. The technique is simpler than that since reported by Rice and Orava. As-received annealed titanium (containing 0.8 pct Fe and 30 ppm H) in the form of sheet 0.05 cm thick is placed in the solution and moved up and down. The reaction is violent but suitable foils are obtained very easily and consistently. A typical micrograph is shown in Fig. 3. The small precipitates were not identified. Yamane and ueda6 observed many spotlike features which they referred to as small dislocation loops. While their spots may be due to the reaction of the warm foil with the air as suggested by Rice and Orava, the precipitates in Fig. 3 are also found when foils of titanium are prepared by electro-polishing at low temperatures and subsequently examined in the electron microscope without any inter- mediate warming. Furthermore, they are not a surface effect. It is necessary to add that alloys of titanium cannot be so easily thinned by the chemical polishing solution described above since it contaminates the a, phase with hydrogen and produces y hydride. These matters are described at length in a paper7 and their relevance to stress corrosion is considered elsewhere.&apos;-* Author&apos;s Reply The authors are grateful to Dr. Scully for bringing to our attention his hitherto unpublished technique for thinning unalloyed titanium, and deeply regret the unintended apparent duplication. The chemical thinning solution (7 parts HNO3 and 3 parts HF, by volume) reported by us is the same as that with which, for some period in the past, we had experienced success in the preparation of foils from single and polycrystalline niobium. Its subsequent effective application to titanium was a logical step, which, clearly independently of Scully, was conceived by Mr. Rice, to whom full credit is due. A few comments are warranted concerning some of the details of the preceding Discussion. It is evident to the discerning reader that the two thinning techniques under consideration are chemically almost identical, and in that sense are equally "simple". The chemical aspect is, of course, the one of primary importance in both communications. Thereafter, the relative simplicity is dictated by the mechanics of the actual thinning operation selected by the individual investigator. Our standard dimpling, or dishing, procedure was chosen with a view toward providing, for the electron transparent areas of the sample, the maximum protection from extraneous deformation during handling. That the long, straight dislocations visible in Scully&apos;s electron micrograph of a seemingly recovered structure closely resemble handling dislocations would tend to indicate the merit of our adopted technique. Features similar to those which Scully has attributed to precipitates, without any apparent diffraction contrast confirmation, were not observed in any of our clean foils taken from annealed or deformed specimens. This was admittedly somewhat surprising since the 3700 ppm (nominal) Fe in the A-70 commercial-grade titanium examined should have given rise to TiFe precipitates. Presumably these existed but were un-resolvable. Curiously, Scully&apos;s "precipitate1&apos; density is fairly high although the iron content quoted was less than one-fourth of that in our material. One is forced to conclude from the evidence that prior thermal and mechanical treatments are responsible for the two different types of structure observed.

Jan 1, 1968

By W. C. Winegard, C. J. Beinjessner

PREVIOUS investigations 1,2 of Fe3P described by pearson3 and schubert4 show that Fe3P has a bct unit cell having four Fe3P tetrahedra centered around each lattice point. The space group is 14, No. 82, and all atoms occupy general positions 8(g). The cell dimensions3 are: a = 9.090, c = 4.446 kX, with an axial ratio of c/o = 0.4891. We have measured the lattice parameters of Fe3P, using a Fe as an internal temperature standard, at 23°, 414°, and 678°C and computed the thermal expansion over this temperature range. The Fe,P was prepared by melting under vacuum (after flushing with argon) a commercially pure iron and "ferrophosphor" in a high-frequency induction furnace. Part of the ingot was crushed for X-ray examination and for chemical analysis. X-ray diffraction and light microscopy indicated iron phosphide (Fe3P) present as the major constituent and a small amount (about 5 pct) of a Fe. Chemical analysis showed 0.05 wt pct Si, 0.008 wt pct N, 0.018 wt pet C, and less than 0.02 wt pct each of other metallic elements. X-ray diffraction powder patterns were obtained from a mixture of iron and Fe3P sealed in an evacuated quartz capsule using a Unicam high-temperature

Jan 1, 1968

By R. Kossowsky

USING etch-pit techniques, Johnston and Gilman&apos; have shown that the stress dependence of dislocation velocity can be represented by the expression where r, is the dislocation velocity, a is the applied stress, and oa, is the stress to produce a unit velocity. Noble and Hul12 showed that the exponent m is strain-dependent and increases rapidly in the work-hardening region. This was explained by arguing that in the work-hardened material the applied stress required for any given velocity will be greater than in the annealed material by an amount equal to a back stress due to work hardening. schadler3 has stressed the importance of substructure as a possible source of error in dislocation velocity measurements, and took care to make velocity measurements in which dislocations moved such short distances that interactions with boundaries were avoided. schadler3 also pointed out that, if standard testing equipment is used, measurements of m from flow stress data could be seriously in error in materials with a high initial work-hardening rate. Noble and Hu112 have further argued that, due to the strain dependence of m , the extrapolation to zero strain4 to obtain the true value of m can be justified only in the preyield region. Microstrain experiments in high-purity iron5,6 have led to the conclusion that aiA (Ref. 5) (defined as the stress to first produce a permanent set of 10-6 in. per in.) and oflow are not controlled by the same deformation mechanism. It has been proposed5,6 that aA is governed by the lattice resistance to the motion of screw dislocations in a given slip plane and that oflow is controlled by the lattice resistance to a full-scale cross slip. The purpose of this note is to extend Noble and Hull&apos;s argument further and to show that measurements of m from flow stress data can be in error due to the rapid increase in stress in the microstrain region6 when stress is increased beyond aA. Double z-one-refined single crystals of molybdenum (with the (101)[ 111] slip system operating and a Schmidt factor of 0.475) were used in an experimen-

Jan 1, 1968

By David P. Shoemaker, Clara Brink Shoemaker

The I phase was discovered by Bardos, Malik, Spiegel, and Beck1 in the V-Ni-Si system at 1100°C and in the Mn-Co-Si and Mn-Ni-Si systems at 1000°C. Kuzma and Hladyshevskii2 and Kuzma, Hladyshevskii, and cherkashin3 have reported a new phase, which they named the S phase, in the Mn-Co-Si and the Mn-Ni-Si systems at 800°C at approximately the I phase compositions. The powder diffraction diagrams of the I and S phases, compared by Bardos el al.,1 are related but show distinct differences in relative intensities. Professor Paul A. Beck kindly sent us a specimen of the (v-Ni-Si) I phase for single-crystal study. Precession and Weissenberg diagrams taken with a tiny single-crystal fragment showed that the structure is monoclinic with a large unit cell. The cell dimensions were refined from a powder diffraction diagram taken with CrKa radiation in a 57.3-mm camera with our computer program LSCELP4 using only the indices of those reflections that were observed on Weissenberg diagrams (hnl, with n = 0 through 9 and n = 12) and precession diagrams (Okl, lkl, Izk0, hkl, hk2). Table I shows the agreement obtained between the l/d values calculated with the final values for the cell dimensions and the l/d values observed by Bardos et al .1 for I(V42Ni33Si25), by US for I(V41Ni36Si23), and by Kuzma and Hladyshevskii2 for S(MnpCoSi). The powder patterns contain many broad and diffuse lines. In fact practically all powder lines observed are near-superpositions of several reflections. The refinement program is not set up to handle several reflections contributing to one observed line: the position of each line is refined with the aid of one set of indices only. The final values for the cell dimensions were obtained from the lines of strong or medium intensity with the indices indicated by asterisks in Table I: a0 = 13.403(6), bo = 23.336(15), co = 9.129(6)A ß = 99.11(6) deg The standard deviations (given in parentheses) are those calculated by the refinement program from least-squares theory and do not take into account that the lines included in the refinement may not have been correctly indexed in every case or that the position of a line may also be partly determined by the overlapping reflections. The agreement between the calculated and observed I phase patterns is fairly good, although some discrepancies occur. Not all observed lines could be indexed with the incomplete set of sin-

Jan 1, 1968

By O. D. Gonzalez

ThIS communication presents the results of a determination of the permeabilities of hydrogen and deuterium in a iron from 360° to 560°C. Recently Heu-mann and primas&apos; have given values of the diffusivity and solubility in a iron of the two isotopes from which the permeability can be calculated. The work reported in the present communication, however, is a direct measurement of the rate of permeation of the isotopes through an identical iron specimen under the same conditions, so that systematic errors can be minimized in the calculation of the ratio of the permeabilities—the value which is usually of main importance in establishing limits for isotopic differences in diffusive processes. Experimentally the procedure used was the usual one: a steady-state flow of gas produced by a pressure difference across an iron membrane was observed as the pressure rise with time in a previously evacuated, calibrated volume connected to the outlet side of the membrane, while a constant pressure of gas was maintained on the opposite inlet side. The membrane was a cylindrical tube 9.38 cm long, 0.730 cm inside diam, 0.187 cm wall thickness, fabricated of 99.95 pct vacuum-melted National Research Corp. iron (less than 0.003 pct C). One end was sealed by a heliarc-welded iron (99.95 pctj lid of 0.147 cm thickness; the other end of the tube was welded to a 304 stainless-steel tube (0.318 cm ID and 0.318 cm wall) which connects to a vacuum system and to the calibrated volume including a dibutylphthalate manometer. The temperature of the iron membrane was maintained constant to ±0.l°C and was measured with an iron-constantan thermocouple which was calibrated against a standard Pt/Pt-Rh thermocouple: the temperature variation along the length of the membrane did not exceed ±0.5°C. Hydrogen was allowed to pass through the membrane assembly for 72 hr at 615°C before permeability measurements were begun. The system was tested at temperature before and after the experiments by a substitution of helium for hydrogen in the inlet side; under these conditions the pressure rise observed in the outlet side was negligible at all times. The gases used for the permeability measurements were 99.95 pct Matheson prepurified H2 and 99.7 pct D2 (0.3 pct HD) from the Isomet Corp. The gases were dried with liquid N2 before use. In Fig. 1 the logarithms of observed flows, jt, for a pressure difference of 73.4 cm Hg are plotted against T-1 Each point in Fig. 1 represents the slope determined by a least-square evaluation of a plot of the pressure in the outlet side of the membrane against time, including at least two separate sets of observations. Each point in the figure has an uncertainty of ±0.6 pct arising from the experimental uncertainty in the pressure and time measurements. The standard deviation of the observed pressures from the straight lines in all cases is less than the experimental precision of the measurements. The observed flow, jt, includes a small but not negligible flow through the stainless-steel connection.

Jan 1, 1968

By L. H. Cadoff, L. M. Adelsberg

The layer growth method has been used to investigate the reaction kinetics of liquid titanium and hafnium with carbon and the [liq] - [liq + TiC] and [liq] - [liq + HfC] phase boundaries at temperatures above 1800°C. The equipment and experimental procedures used in this investigation are basically identical to those described in an earlier paper&apos; on the Zr-C reaction. Temperature control, however, was improved significantly by connecting a Latronics Colo-Ratio automatic pyrometer and a controller to the power source. The subsequent temperature variations were ±10°C; previously ±20°C was obtained using manual controls. The absolute accuracy of the pyrometer, however, must be considered to be only ±40°C.* The spectrographic analyses of the materials used in this study are listed in Table I. The isothermal reactions of titanium (1800° to 2700°C) and hafnium (2300" to 3000°C) with carbon (graphite crucibles) resulted in the formation of carbon-saturated liquid metal and layers of Tic and HfC, respectively. The thicknesses of the carbide layers, determined from metallographic measurements at 100 times, as a function of carburization time and temperature are given in Figs. 1 and 2. At each temperature, parabolic growth behavior for these reactions was observed and could be expressed as x2 =Kpt, where X is scale thickness (corrected for heating and coolingL), Kp the parabolic growth constant, and t the isothermal carburization time. Values of Kp as a function of temperature for the carbides are shown in Fig. 3 and listed in Table 11. The growth constants are expressible as: kpTiC = 0.2 exp(-61,800/RT) sq cm per sec for Tic and Kp HfC = 2.62 exp(-95,300/RT) sq cm per sec for HfC. The liquidus phase boundaries were determined from metal samples treated in graphite crucibles for different times ranging from 4 to 100 min at each of the temperatures indicated in Table 11. Metallographic examination revealed that the carbide precipitates were distributed uniformly throughout the frozen metal matrices. This is attributed to the rapid cooling rates (800°C per min) and the small difference in density between the precipitated carbide and the liquid metal.

Jan 1, 1968

By H. A. Davies

DURING a current program of research on the structure and properties of liquid sodium alloys, the need arose for information on the solubilities as a function of temperature of several B subgroup metals in liquid sodium. In the absence of reliable information in the literature for several of these systems, par- ticularly at temperatures in the range 100° to 300°C, an apparatus was constructed to determine solubilities by a direct melt-sampling technique, followed by wet-chemical analysis for both sodium and the solute metal. The details of the technique have been described previously.&apos; The solubility of indium in liquid sodium was determined at eight temperatures in the range 100° to 270°C. The solubility as a function of temperature is shown on Fig. 1; this represents the liquidus line over this composition range. A cooling curve was plotted after the completion of the sampling and an arrest was observed at 94.9°C which must be interpreted as being the result of a eutectic reaction. By extrapolation of the liquidus to this temperature, the eutectic composition was estimated to be about 0.25 at. pct In. The present estimate of the eutectic temperature and composition are in good agreement with the values of 96.0° to 96.2°C and between 0.28 and 0.45 at. pct In, respectively, which were reported by Heycock and Neville.2 However, no further information on the liquidus of this system at the sodium-rich end could be found in the literature for comparison. One compound: NaIn, has been reported in this sys-

Jan 1, 1968