By J. E. Spruiell, F. H. Patterson, B. F. Shuler

The microstructures and textures developed by the working of high-purzly thermochemically deposited tungstem sheet have been inuesligated. Greater than 60 pct reduction was required to deslroy the columnar grain structure which existed in the as-deposited sheet. With increasing reductions the texture gradu-ally charged from the initial as-deposited orientation with (100) parallel to the sheet normal to a (100}(011) ideal ovienlation with some spread about the rolling direction. This texture was retained after recrystalli-zation a1 2000°C. THE processes for depositing tungsten by hydrogen reduction of tungsten hexafluoride have been under development for the past several years.1,2 The nature of the deposition process is such that the as-deposited material contains a highly oriented columnar grain structure perpendicular to the deposition substrate. This well-defined columnar structure may be useful in certain applications293 but a wrought or equiaxed structure may be desired for some components such as tubing. Knowledge of the effects of working ther-mochemically deposited (TCD) tungsten is therefore necessary in order to establish the feasibility of obtaining worked and recrystallized microstructures and textures. The details of a recently developed technique for thermochemically depositing flat, uniformly thick tungsten sheet are presented with emphasis on the effects of deformation by rolling on the microstructure and texture. Although no work has been previously reported on the rolling and the annealing textures of TCD tungsten, there have been some determinations of textures for cold-rolled tungsten foil prepared from powder-metal -lurgy billets.4-8 The general description is that of a predominantly lurgy{100}(011) texture, with some spread about the rolling direction as an axis. pugh5 reports data both for cold-rolled and for annealed foil having about 96 pct initial cold work. He observed no change in texture, except for a decrease in the spread, for annealing treatments of 30 min at temperatures up to 1800°C. On annealing at 1900°C, both the low-temperature components plus new components which were described alternately as {001}(320) plus {001)(230) or as {100}(011) ± 12 deg about the sheet normal were observed. Above 1900°C, the new orientation existed alone, and it was stable up to 2500°C, the highest temperature that Pugh investigated. THERMOCHEMICAL DEPOSITION OF TUNGSTEN SHEET High-purity tungsten sheet was reproducibly deposited on the inner walls of a molybdenum mandrel by the thermochemical reaction WFs(g) + 3H2(g) - W(s) + 6HF(g). The mandrel was heated by a five-zone tube furnace which afforded a controllable fixed-temperature profile. Sheets measuring 1+ by 12 in. have been deposited with uniform thicknesses of up to 0.145 m. As shown schematically in Fig. 1, the purified reaction gases were metered into a mixing chamber at a Hz-to-WF6 ratio of 15 and preheated to 350°C. The flow rate of the WF6 was 300 cu cm per min at stp. These gases were directed through a conical injector into the deposition chamber. Inside this chamber hydrogen reduction of the WF6 to pure tungsten metal occurred on the hot walls of the molybdenum mandrel at a total pressure of 5 Torr. Typical temperatures for the five zones in the chamber were, respectively, 565", 540", 550°, 570°, and 590°C. The hydrogen fluorlde generated from the reaction, the excess hydrogen, and some un-reacted WF6 were pumped on through the scavenger

Jan 1, 1968

By R. P. Agarwala, M. S. Anand

Using residual activity technique, the diffusion of palladium, silver, cadmium, indium, and tin in alunzinum has been studied in the temperature range of 400" to 630°C. The diffusivities (in units of square centimeters per second) have been expressed as: IMPURITY diffusion in aluminum,1-9 silverand lead5 for cases of low solid solubility of the impurity in the host metal has yielded frequency factors in the range of l0-6 to l0-9 sq cm per sec whereas the activation energy is practically half the self-diffusion activation energy value. From the observed values of frequency factor, activation energy, and entropy of activation, it has been suggested' that these solutes are not diffusing by vacancy or interstitial mechanisms but by a mechanism which should be consistent with such low values of the diffusion parameters (Do and Q). However in spite of extensive work on these types of systems, the mechanism of diffusion is still not well understood. The present investigation on the diffusion of palladium, silver, cadmium, indium, and tin in aluminum has been carried out to throw further light on the diffusion mechanism in systems, where the solid solubility is very low (except for the case of silver). The results are discussed on the basis of solid solubility and the structural changes involved owing to the presence of the solutes in aluminum solid solution. An attempt has also been made to apply the existing theories of charge5-8 and size8 difference between the solute and the solvent. EXPERIMENTAL PROCEDURE Specimens (1/2 in. diam by 3/8 in. high) were machined out of pure aluminum (99.995 wt pct) rod obtained from Johnson Mattheys. They were sealed under vacuum in quartz tubes and annealed at 620° C for several hours; the grains thus developed were sufficiently large to eliminate the possibility of diffusion along the grain boundaries. The flat ends were prepared carefully after polishing as described previously,10 Radioactive nitrates of cadmium, indium, and tin and chloride of palladium containing, respectively, cd115, 1n114, sn113, and pd103 were dissolved in distilled water and mixed with 30 pct acetone. By means of a micropipet a drop of this solution was placed on a smoothly polished and lightly etched surface of the specimen. Due care was taken to see that the solution spread uniformly on the surface of specimen without trickling down its sides. Radioactive silver was elec-trodeposited using a AgCN-KCN bath. The amount of sample deposited in all the cases was not more than 0.1 µ thick. The samples were then sealed in quartz tubes in vacuum. The cadmium samples were sealed in a purified argon atmosphere to avoid evaporation. The samples were then diffusion-annealed. The temperature of annealing varied between 400° and 630°C and was controlled to ±5°C. On heating to -400°C,the deposits of cadmium, indium, and tin, which were of the order of 0.1 p in thickness, were converted to their respective oxides. The contribution of oxygen present in the lattice of aluminum due to these oxides has been calculated and found to be less than 10 ppm in all cases. Oxide method has already been used by other workers11'12 in diffusion studies without any controversy on the issue. However, in some of these investigations, metallic deposition was also tried. The diffusivities calculated from these measurements were found to agree very well with the diffusivities obtained by using the oxide method. Thus it is assumed that the measured diffusivities represent true diffusion coefficients. Since palladous chloride decomposes at about 500°C, the deposited samples which were to be diffusion-annealed below 500°C were heated in vacuum for a very short time at 500°C to allow the decomposition of palladous chloride to palladium metal. Time taken in decomposition of nitrates to oxides and chloride to metal was negligibly small as compared to the period of the diffusion anneals. The residual activity technique13 was used to study the diffusion profiles where thin layers from the specimen surface were removed by grinding it parallel to a flat surface on a 600-grade carborundum paper. The specimen was washed, dried, and weighed, the differ -ence of the weight being the measure of the thickness of the layer removed. After each such abrasion and weighing, the total residual activity on the surface of the specimens was measured by counting 0.656, 0.94,

Jan 1, 1968

By E. J. Fasiska, H. Wagenblast

The dilalion of a ivon by interslilial carbon was measured by two independent techniques —dilatometric mesurements at 719 c and X-ray measurments of the urlil cell parameters a1 room temperature after quenching. The relative expansion per increase in cavbon content by both methods is (2.9 + 0.3) x 10-3 pev at. pcl C nrzd is temperature- independent within experimental error. This corresponds to (6.3 5 0.6) cu cm per g-atom for the partial gram-atomic volume of carbon in a iron-only slightly smaller than the atomic volume for iron in the same temperature vange. THE only previous quantitative study of the dilational effect of carbon dissolved in a iron was performed in 1934 by Burns1 which, at the time, generated some discussion of possible sources of experimental error.2 For a system of such widespread importance, we felt that a new investigation was merited. Both X-ray diffraction and dilation measurements were used to determine the expansion of the a iron lattice by dissolved carbon, avoiding as much as possible any previous experimental problems and deficiencies. The dilation method at solution temperature offers not only measurements which are free of residual strain but also, in conjunction with the room-temperature X-ray measurements, a method to detect any large temperature dependence of the partial gram-atomic volume of carbon. To insure that quenching strains did not affect the room-temperature X-ray measurements, wire specimens of constant carbon content but different diameter were examined for such an effect. SPECIMEN PREPARATION The material used for both experimental techniques was "Ferrovac E" iron received in the form of 19-mm-diam rod and stated as having the following impurity contents: C, Cr, Cu, Mn, P, and V, each in the range of 10 to 50 ppm; Co, O, Mo, S, and Si, 60 to 100 ppm; W, 200 ppm; Ni, 230 ppm; N, 4 ppm. The stock material was cold-swaged to 0.71 mm diam for the Debye-Scherrer X-ray camera specimens and portions were cold-rolled from 6.3 mm diam to 0.79- and 0.25-mm sheet for X-ray diffractometer and dilation measurements. The wires were annealed in wet hydrogen for 6 hr at 840°C and 15 hr at 720°C, and then quenched into 0°C water. A chemical analysis for carbon after this treatment gave 0.0046 + 0.0014 at. pct C. Three portions of these wires were subsequently held at 719°C in three different hydrogen + methane mixtures and then quenched, resulting in carbon concentrations of 0.0283, 0.0598, and 0.1067 at. pct C by chemical analysis. After carburizing, the wires were swaged to 0.48 mm and electroplated with silver to prevent carbon loss during subsequent heat treatment. The final heat treatment consisted of holding the wires at 72 1°C for 5 min in a He-2 pct H mixture followed by quenching into 0°C brine. The wires were held at room temperature for a few minutes to remove the silver plating using a phosphoric acid-hydrogen peroxide solution, and then stored in liquid nitrogen until the measurements were made. EXPERIMENTAL TECHNIQUE A) Dilation Measurement. The dilatometer consisted of a gas-atmosphere vertical tube furnace modified so that length changes of a ribbon-shaped specimen could be measured externally. This was done by installing a gas-tight mercury seal at the top of the furnace as shown schematically in Fig. 1. The specimen (21.0 cm long, 1.27 cm wide, and 0.25 mm thick) was suspended in the center of the furnace by 3-mm-diam quartz rods with the upper one passing through the cap of the mercury seal. Above the cap, the upper quartz rod was coupled to a lever exerting a load of about 25 g (-12 lb per sq in.) on the specimen and having a 10 times mechanical magnification. The vertical position of a marker at the other end of the beam was read with a traveling microscope with a precision of 0.01 mm. The temperature gradient of the furnace was meas-

Jan 1, 1968

By Pradeep K. Rohatgi, Clyde M. Adams

Dendritic aggregate of ice formed on freezing of aqueous soluitions has been studied. Chlorides of sodium, potassiutn, lithiunz , and hydroget1 were used as solutes. The spacing between ice platelets or den-drites was experimenlally found proportzonal to the square root of freezing time when the freezing rate was constant from beginrting to end of solidification; the constant freezing rates were obtained during freezing of small droplets of aqueous soliitions surrounded by relatively large heat sinks. The transverse growth velocity of the ice platelets is proportional to the square root of the freezing rate. During unidirectional freezing from a constant temperuture chill, the solution at each location is subjected to a spectrum of freezirtg rates. The freezing rate is ini- FREEZING of solutions has been a subject of investigation in many disciplines. Aqueous solutions offer the advantage of transparenty; their study is of special significance due to the increasing interest in freezing processes for desalination. In addition dendritic solidification of aqueous solutions is in many ways analogous to freezing of metallic solutions. Aqueous solutions of most ionic salts freeze with tially low, passes through a maximum, and then decreases until solidificatimz is complete. The den-drite spacing increases linearly with the distance from the chill surface; it is inversely profiortional to the square root of the maximum freezing rate. The dendrite spacings in the two systems (the constanl freezing rate and the varying freezing rate) are equal, when the maximum freezing rate of the varying freezing rate system equals the average freezing vale of the constant freezing rate system. Mass transport in interdendritic liquid duriug solidificatiotz is analyzed; the experimental observations indicate that maximum concentration difference (AC) and supercooling (AT) in the interdendritic liquid are indepexdent of freezing rate. the separation of practically pure ice crystals from the liquid phase; with very few exceptions there is no solid solubility of ionic salts in ice. As an ice crystal grows there is rejection of solute from the moving interface into the liquid. Since the rejected solute moves primarily by diffusion, concentration gradients are established in the liquid. The highest solute concentrations are found in liquid immediately adjacent to liquid-solid interfaces and lowest concentrations farthest from the interface. Two-phase equilibrium obtains only at the solid-liquid interface; at other locations the liquid becomes supercooled because temperature gradients are negligible compared to concentration gradients. This is an immediate consequence of the fact that thermal diffusivities are considerably higher than mass diffusivities.

Jan 1, 1968

By G. S. Cole, G. F. Bolling

Fluid flow strongly influences ingl structure and the columnar -to-equaaxed transition. Artificial flow patterns siwzilar to the nuturul ones act to induce this transition, while dampening forces act to suppress this transition. It is shown here how simple mechanical forces can be applied to a systerrz in order to induce or slipPvess relative fluid flow and the change both the structure transition and the exact structures obtained. The example used is the effect of slow rotations and oscillations 012 a cooling- ingot (of laboratory scale). The details of rotution and oscillation for various cooling rates, lenlperal~ire gradients, and sizes of ingot are related to other solidzfication variables. THE grain structure of a casting can be changed by altering the fluid motion during solidification. Just how important these changes are depends directly upon the degree to which the fluid motion can be controlled. An early step in understanding the nature and influences of fluid motion was taken by studying natural thermal convection; when a static mechanical device was used to suppress natural flow the result was opposite to that obtained when an electromagnetic device was used to augnlent flow in a pattern similar to the natural one. ''2 Suppression allowed more columnar growth to occur, but "augmented natural convection" brought about an earlier columnar-to-equiaxed transition (CET). Since the solidification of a free ingot must have characteristics somewhere between those displayed during suppression and augmentation, we know that natural convection must influence the CET. Further, since heat transfer in the liquid is always some time-dependent combination of convection and conduction, it can easily be guessed that the temperature gradient in the liquid is the vital factor affecting the CET.1,2 It is obvious that the structure arising from the unadulterated solidification of an ingot, without external influence, is rarely if ever the best possible one. Although the pattern of the natural fluid flow may be considered efficient, the magnitude of the flow and the heat transfer decrease freely from the outset. For a

Jan 1, 1968

By Eugene A. Mizikar

A mathetnatical model of heal transfer in continuously cast steel slabs is described. The model, consisting of a unidimensional transient conduction equation and boundary condition equations, has been pvogrammed for computer solution. Temperatuve and solidification profiles calculated for a 6-in. slab, being cast under several conditions of secondary cooling, are presented and compared. Calculated solidification profiles are in agreement with reported expevinle~ztal values. For the mold zone, the predicted slab shell thickness can be described by: Resuilts of the study indicate that multibank spray cooling followed by radiant cooling should be employed when solidifying thick slabs with minimum surface temperature of 1600°F. Under these conditions, a 6-in. slab can be expected to solidify in about 8.3 min. Computer results also indicate that radiant cooling can replace spray cooling during solidification of the final 30 pct of slab with little increase in overall solidification time. CONTINUOUS casting has come to the forefront of the steel industry in recent years because of economic advantages resulting from increased yields and elimination of several processing steps. Considerable work, however, remains to be done regarding modifications to the process and operating procedures. Both a lack of operating plants in this country and the experimental difficulties associated with direct measurements on moving castings have made determination of solidification rates and temperature distributions difficult. An alternate approach is to mathematically simulate heat transfer in a continuously cast section, and then calculate the temperature distributions as a function of the controllable variables of the process. Simulation of heat transfer during solidification requires that a nonlinear mathematical problem be solved. As pointed out by Ruddle,' there are two mathematical approaches to the problem- the analytical approach and the numerical approach. While the analytical approach is certainly the more elegant of the two, it does require a number of inexact assumptions because of the complexity of the problem. For example, noteworthy analytical treatments of heat transfer in continuous casting have been developed by Savage Hills,3 and pehlke4 only by making one or more simplifying assumptions such as invariant thermophysical properties, constant heat-transfer coefficients in the mold, and linear temperature profiles in the shell. Simplifying assumptions such as these can introduce considerable uncertainty in the validity of results calculated with analytical solutions. Numerical solutions, which are considerably more versatile, appear to be better suited for solving solidification problems. Complex variations in the boundary conditions and variable thermophysical properties can be handled readily with this technique. Whereas numerical computations can be long and tedious when done by hand, results can now be obtained quite rapidly with the use of either the digital or analog computer. Several numerical models of heat transfer in continuous casting have been published. In 1963, Adenis, Coats, and Ragones published a numerical model used to calculate temperature distributions in direct-chill-cast magnesium billets. More recently, Donaldson and Hess 6 presented results obtained with a numerical computer model of heat transfer in continuously cast steel billets. In the present study, a model of unidimensional heat transfer in continuously cast slabs is presented. The method of solution on a digital computer is also included. Calculated temperature distributions and solidification profiles for various schemes of secondary cooling along with attempts to verify the model are also discussed. MATHEMATICAL MODEL The schematic representation of the slab continuous casting process in Fig. 1 illustrates that the slab passes through three distinct zones of cooling. Accordingly, the mathematical model consists of three parts: 1) solidification in the mold; 2) solidification in the spray cooling zone ; 3) solidification in the radiant cooling zone. Heat-Transfer Equations. The model was developed bymaking a heat balance on a horizontal slice of slab over the time period required for the slice to proceed from the liquid metal meniscus in the mold to the cutoff station. As shown in Fig. 2, the imaginary slice extends from the center line to the surface of the slab. As the slice moves downward, heat is conducted from the center line to the surface of the slab at a rate governed by the surface boundary condition and thermophysical properties of the metal in the slice. The following partial differential equation describes the conduction of heat in a medium moving at velocity U in direction Z:

Jan 1, 1968

By L. C. Michels, O. G. Ricketts

The disorientations between s?nall grains, whose growth has been arrested at an early stage of recrys-tallization, and the deformed matrix in cold-rolled aluminum single crystals were determined using transmission Kikuchi line and electron diffraction patterns. The orientations of the recrystallized grains were found to be random, and the disorientations of these grains with the matrix weve found to be intermediate to large. This leads to the conclusion that the observed vecrystallization began in small areas of large disorientation present in the cold-worked structure. heavily cold-worked thin sections of aluminunz single crystals and of polycrystalline aluminum and nickel were produced directly by a mechanical technique. The specinlens thus prepared were heated with the electron beam to bring about vecrystallization during observation in the electron microscope. Motion pictures taken du.ring heating and the electvon, microg.raphs taken both before and aftev heating allowed the recrystallization process to be traced to its ovigin. Re cvystallized grains originated in very s,mall regions of the cold-worked structure and developed through rapid migration of high-angle boundaries. The boundaries either were present as such in the matrix or were formed out of dense dislocation networks. SIGNIFICANT advances have been made in recent years in the study of nucleation of recrystallization using the technique of transmission electron microscopy of thin metal foils. Bollman1 in a study of heavily rolled polycrystalline nickel found support for the Cahn-Cottrell2,3 theory of nucleation. According to this theory nuclei form by the initially slow growth of subgrains formed through polygonization. During this initial period of slow growth (the incubation period) the migrating boundary of the subgrain increases its disorientation with the cold-worked matrix and thereby increases its mobility to become a rapidly migrating high-angle boundary. Bailey4,5 investigated the annealing behavior of several metals deformed both in tension and by rolling and concluded that recrystallization took place through the migration of high-angle boundaries. With low deformations these boundaries were present in the metal before deformation. With high deformation it was not possible to tell whether the boundaries were pieces of the original grain boundaries or were produced either during deformation or by polygonization during ameal- ing. Direct observation during heating of metal foils indicated that subgrains form by polygonization and grow at an uneven rate. The grain size obtained decreased with decreasing foil thickness indicating that the foil surface resists boundary motion. Votava,6 in heating stage experiments on rolled copper, observed nuclei to appear suddenly and grow in jumps of differing magnitude. However, he found no special dislocation configurations where the nuclei appeared. Fujita,7 as a result of a study of subgrain growth in heavily worked aluminum, concluded that the boundary of a recrystallized grain initially forms from the boundary of a group of subgrains. This occurred by a process of deposition of vacancies and dislocations in the group boundary as the boundaries within the group disappear. HU8,9 directly observed a similar process in heating stage experiments on 70 pct rolled Si-Fe single crystals. The growth of subgrains appeared to proceed by a coalescence mechanism. The observed fading away of the boundary between two subgrains was explained by the moving out of dislocations from the disappearing boundary into the connecting or intersecting boundaries around the subgrains. The subgrain size and degree of disorientation with the surrounding structure were thus increased. With the increase in disorientation occurred a corresponding increase in boundary mobility, which eventually allowed the boundary to migrate rapidly. This process was observed to occur within "microbands" consisting of parallel narrow segments disoriented by a few degrees present in the as-rolled structure. The conclusion of Rzepski and Montuelle10 that growth is preceded by the coalescence of blocks through disappearance of their common boundaries supports this view. In contrast to Hu's coalescence model for nucleation were the conclusions of Walter and ~och.""~ Working with the same material as Hu, of the same orientation and rolled to the same reduction, they concluded that nucleation occurred by the Cahn-Cottrell mechanism. They observed, in agreement with Hu, that recrystallization began in the "microband" regions which they referred to as "transition" bands. Bartuska13 studied subgrain growth in heavily rolled nickel using a beam heating method in the electron microscope. He concluded that nuclei for recrystallization form from the largest most perfect subgrains present in the cold-worked structure by rapid intermittent migration of parts of subboundaries. In rare instances he observed subgrain growth by coalescence. EXPERIMENTAL PROCEDURE The materials used in this study were 99.999 pct A1 supplied by A.I.A.G. Metals, Inc., and 99.999 pct Ni supplied by Johnson and Matthey and Co., Ltd. The Hitachi HU-11 electron microscope, with uniaxial

Jan 1, 1968

By A. F. Giamei, E. J. Freise

A discussion of the various factors affecting the accuracy of volume fraction determination by the direct comparison X-ray diffraction method is presented. To minimize errors introduced by nonrandomization effects such as preferred orientation and large grain size, as well as errors introduced by statistical effects, an iterative mathematical analysis is introduced. This analysis is applied to all observable diffractio~ spectra from a given specimen by means of computer techniques and is statistically superior to the standard direct comparison technique which utilizes only one or tm sets of intensity spectra. The computer program also presents a graphical interpretation of- the results which enables the investigator to visualize and readily assess the scatter in volume fraction estimates caused by deviations from randomness. Finally, the iterative analysis is applied to experimental data collected from a series of plain carbon steels in both the as-received and spheroidized conditions to determine the volume fraction of cemen-tite present in each case. The results show markedly good agreement with chemical analyses for all spheroidized specimens. In theory, quantitative X-ray diffraction is a power-ful analytical technique for precise determination of the volume fractions of various phases present in a multiphase poly crystalline aggregate. There are two generally used methods; both utilize the fact that the intensity of a diffraction line of a particular phase is a function of volume fraction of that phase present in the aggregate. The more common method is the so-called internal standard technique where a known amount of standard substance is mixed with the aggregate containing the unknown. The resulting ratio of the intensity of a particular diffraction line of the unknown to the intensity of a diffraction line from the standard is used to find the weight fraction of unknown material by reference to the intensity data obtained from a previously prepared set of standards containing the same amount of standard material. The details of this technique are outlined in standard works on X-ray diffraction.' The disadvantages of the technique are that it requires the use of powder specimens and that the powder mixture must be homogeneous near the surface to the maximum effective beam depth. The alternative technique is the direct comparison method in which the ratio of the intensity of a diffraction line of a phase in the aggregate to the intensity of a second-phase diffraction line yields the ratio of the volume fractions of each phase present. This method has been applied most extensively to the determination of the percentage of retained austenite in martensitic steels and to determining the amounts of hcp and fcc allotropic modifications in pure cobalt5 and the amounts of hexagonal and rhombohedra1 modifications in graphite.8 This method is applicable to bulk as well as powder aggregates and is the technique which will be considered in the following text. It is the purpose of the present communication to show that by combining the results of X-ray diffrac-tometry with the use of high-speed digital computers the results of the direct comparison quantitative X-ray analysis technique can be optimized by using all of the data available on a diffraction pattern. THEORETICAL DISCUSSION In optimizing any quantitative X-ray diffraction experiment, the problem of accuracy vs time to collect and analyze the experimental data arises. For any method to be practical, it is required that both experimental and analytical procedures are reasonably short. In most of the previous work performed by the direct comparison method, intensity data from only one or two sets of peaks were used to calculate the volume fraction of phases present in the aggregate. Consequently, rather long-time experimental measurements are required to assure that the intensity data are sufficiently accurate to justify the use of one or two sets of data. By using computer techniques to analyze the experimental data it becomes feasible to use all of the available data on a diffraction pattern. By so doing, the time spent in measuring any one diffraction maxima can be appreciably reduced. Although this results in poor counting statistics for any one maxima, the number of data points available for analysis is greatly increased. Based on the above discussion, it will be assumed that a continuous scanning counter-diffractometer technique will be used to collect intensity data from a two-phase mixture. The integrated intensity of the ith diffraction line from the a phase in the aggregate is given by:'" where is the volume fraction of the a phase, The various quantities in Eq. [la] are angular independent while those in [lb] depend on the hkl spectrum of a particular phase. The meaning of the individual quantities in Eqs. [la] and [lb] are given in Appendix 1. It is convenient at this point to outline briefly the factors which will affect the measured intensity of any one hkl spectrum. a) Extinction effects arise from two independent experimental conditions. Primary extinction arises from a high degree of crystal perfection and results in spectra having lower intensity than predicted by Eq. [I]. Any treatment, such as powdering, which reduces

Jan 1, 1968

By T. O. King, Y. P. Gupta

The self-diffusion of sodium in two sodium silicate liquids was measured in the temperature range 850" to 1500°C by the capillary-reservoir technique. Radioactive Na 22 was used as the tracer. The total count and autoradiographic methods were used for determination of the total Na 22 depletion and diffusion profiles of the dqy-used specimens. The diffusion coefficients obtained by the autoradiographic technique are slightly smaller than those obtained by a total count method. Error analysis of the two methods suggests that more confidence be placed in the results of the total count method. The experimental results were analyzed in terms of the existing activated rate process theory. The activation energy for diffusion was shown to decrease markedly as the temperature increased. This was attributed to a variation in the heat of activation with temperature, probably related to a change in the distribution of anions associated wilh the cation. In terms of a model, suggested for diffusion in liquid silicates, differences in the aclivation energies for diffusion and electrical conduction may arise from the effect of the electric field applied in conduction measurements. It is generally accepted that liquid silicates consist of cations and an equilibrium distribution of complex anions determined by temperature and composition. Transport properties in molten silicates are of interest, not merely because of their relevance to the kinetics of pyrometallurgical reactions and glassmak-ing processes, but also because they are useful to development of the theory of such ionic liquids. Self-diffusion is one such transport process that may, if studied for liquid silicates of widely varying compositions, indicate structural changes through changes in the activation energy for diffusion. The self-diffusion of calcium, silicon,' sulfur: aluminum, 4 and oxygenS in lime-alumina-silica melts and of iron6 in molten iron silicates have been measured. Unfortunately, the errors in some of the reported activation energies for diffusion are too large to allow firm conclusions concerning structure and the mechanism of the diffusion process to be drawn. The research reported here was a study of the self-diffusion of sodium in liquid sodium silicates. The soda-silica system was chosen since: i) a reasonable composition range can be covered in the binary system at moderate temperatures; ii) suitable isotopes of sodium (radioactive Na 22 and NaZ4) can be obtained; iii) data on the electrical conductivity and viscosity of sodium silicate liquids are available. However, the range of composition actually used in diffusion experiments was limited, to 20 to 35 wt pct soda, by the relatively high viscosity of silica-rich compositions and by evaporation of soda from basic melts. EXPERIMENTAL PROCEDURE The capillary-reservoir technique was used, wherein a radioactive tracer, Na 22, incorporated in the capillary melt, was allowed to diffuse out of the platinum capillary tube into a large reservoir of silicate liquid containing a chemically identical melt, but without radioactive tracer. After a specific diffusion time, both the total depletion in the tracer concentration and concentration-distance profiles of the diffused samples were measured by procedures to be described later. The diffusion cell assembly was similar to that used by Koros and King.' The temperature of the diffusion cell was measured with a calibrated Pt, Pt-10 pct Rh thermocouple located at the center of the liquid reservoir. The same thermocouple was used to obtain the temperature profile in the reservoir. The temperature at the top of the reservoir was slightly higher (2°C) than that at the bottom, to minimize convection in the capillary tubes, which were placed, open end up, in the reservoir. Convection was not expected to be a problem since the length-to-diameter ratio of the tubes was about 12:1 and the maximum capillary diameter was 1 mm. The diffusion cell was heated in a molybdenum-wire resistance furnace, previously used by Koros and King, but somewhat modified. A Pt, Pt-10 pct Rh thermocouple enclosed in an alumina tube and located near the furnace winding was used in conjunction with a preamplifier and Micromax proportional controller for temperature control, within 4°C, at temperatures near 1500°C. Before starting a diffusion run, the furnace was heated to the desired temperature and an alumina guide assembly for the capillaries was slowly lowered to within 2 cm of the liquid reservoir. The capillaries were thus heated to about the temperature of the bath. The run was started by lowering the assembly till the open ends of the capillaries were about 1 cm below the surface of the liquid. The run was ended by raising the assembly to about 15 cm above the liquid bath. Later, the sample assembly was slowly withdrawn from the furnace. Six diffusion samples were usually run at the same time. Three runs made with the open ends of the capillaries down were discarded because in the majority of these samples air bubbles trapped at the open end were observed. Some glass adhered to the outside of the capillary on withdrawal. This was carefully removed and used to check that the Na 22 activity in the sink remained at a low level. Materials. Nonradioactive sodium silicates were prepared by melting, in a platinum crucible, weighed quantities of sodium carbonate and powdered silica. To prepare radioactive sodium silicates, Na2 obtained in HC1 solution, was first checked for radioactive impurities by obtaining a y-ray energy spectrum, then the chloride ions were removed by anion-ex-

Jan 1, 1968

By A. D. Zunkel, A. H. Larson

Equilibrium arsenic contents of Pb-As alloys in contact with PbO-As2O3 slags containing less than 30 mol pct As2O3, were determined at 650°, 700: and 750 C in an inert at?rzosphere. In this temperature range, the arsenic content of the alloy increased with increasing temperature in the single-phase liquid slag region and decreased with increasing temperature in the two-phase slag region and the single-phase solid-solution slag region. The PbO-As2O3 phase diagram below 22 mol pct As2O3 was determined by thertrzal analysis and by application of a log ?As2O3/?PbO vS log XAs2o3 /x3pbO plot determined from the equilibrium actiuity data. The resulting phase diagram was not well-defined since the eutectic temperature was not detected in the thermal analysis experiments, although a region of terminal solid solubility of As2O3 was found. Results from the phase diagram determination are compared with an existing diagram in the literature. THIS experimental investigation is an extension of a study by the authors1 on the slag-metal equilibria in the systems concerned with commercial lead refining processes such as softening and dross fuming. The first part of this investigation was a study of the slag-metal equilibria in the Pb-PbO-Sb2O3 system. The only experimental work previously done on the Pb-PbO-As2O3 system was by Pelzel2,3 in which the phase diagram for the PbO-As2O3 system was determined below 50 wt pct As2O3 and the equilibrium constant for the reaction 3Pb + As2O3 + 3PbO + 2As was determined as a function of temperature. No slag-metal equilibrium data have been determined. It is due to the scarcity of information regarding the Pb-PbO-As203 system that this work was undertaken. This paper describes the determination of the slag-metal equilibria in the Pb-PbO-As203 system by equilibrating Pb-As alloys with PbO-As2O3 slags in an inert atmosphere, the effect of 1 wt pct additions of bismuth and copper on the slag-metal equilibria, and the PbO-As2O3 phase diagram both by thermal analysis and the use of the slag-metal equilibria data. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade and assayed as follows: 1) 99.8 pct PbO (0.014 pct insoluble in CHJCOOH, 0.02 pct not precipitated by H2S, 0.1 pct CaO, and 0.08 pct SiO2); 2) 99.95 pct As2O3; 3) 99.99 pct Pb; 4) 99.0 pct As; 5) 99.99 pct Cu; and 6) 99.97 pct Bi. Room-temperature X-ray patterns revealed no detectable impurities in any of these materials. Apparatus for Equilibrium and Thermal-Analysis Determinations. The resistance-heated crucible furnace used in this investigation employed nichrome elements and was mounted so that it could be raised to surround the reaction tube during each experiment and, subsequently, lowered. A schematic diagram of the apparatus is shown in Fig. 1. Each charge was heated in a 3+-in.-OD by 31/2-in.-high 416 stainless-steel crucible placed in a 41/4-in.-1D by 18-in.-long fused-silica reaction tube which was closed at one end. On a shoulder around the crucible was placed a 3: -in.-OD by 12-in.-long open-end fused-silica condenser tube. The open end of the reaction tube was covered by a water-cooled brass cap with ports for 1) admitting an inert atmosphere to the system through a stopcock, 2) introducing a stainless-steel, motor-driven, paddle stirrer into the crucible, 3) evacuating the system with a mechanical vacuum pump, and 4) sampling the melt with Vycor sampling tubes. The brass cap was fitted to the open end of the reaction tube with a silicone gasket and collar clamp. The furnace temperature was controlled by a Barber-Coleman Capacitrol controller and a chromel-alumel thermocouple. Due to the corrosiveness of the melt, the controlling thermocouple also served as the measuring thermocouple. The temperature of the melt was calibrated against the controller temperature and was checked periodically during each test with a Vycor-enclosed calibrated chromel-alumel thermocouple. The temperature measurement and control can be considered accurate to ±3°C. Procedure. The charge placed in the crucible for each experiment consisted of 1000 g of Pb-As alloy and 300 g of PbO-As2O3 slag. The crucible was then placed in the reaction tube, the condenser tube was placed on the shoulder of the crucible, the silicone gasket and brass cap were fitted on the open end of the reaction tube, and the entire system was evacuated and filled with argon ten times. After the last flushing, a positive argon pressure of 1 psig was impressed on the system. The furnace was then raised to sur-

Jan 1, 1968

By D. D. Pollock

Many constitution diagrams do not indicate the limits oJ solid solubility of the silver-rich solid solutions below 200°C. Thermoelectric measurements were employed to determine this limit in the nieighborhood of room temperature. The appearance of a second phase causes a discontinuity to occur in the tkevtrroelectric power as a function of cornposition at constant temperature and pressure. This discontinuity was employed to determine the limits of the silver-rich terzinal solid solutions of the Ag-A l, Ag-As, Ag- Bi, Ag--Ge, Ag-In, Ag-Pb, Ag-Sb, and Ag-Sn systenls at 30°C. CONSIDERABLE work has been done on the constitution of binary alloys of silver. The available data have been compiled by Hansen1 and Elliott.2 However, many of the binary diagrams do not show the limits of solid solubility of the silver-rich solutions below about 200° C. This work was undertaken in an attempt to extend these limits to the neighborhood of room temperature . PREPARATION OF ALLOYS All of the alloys were made with silver containing less than 0.014 pct (by weight) of impurities. The materials were weighed out into 225-g heats and melted in a high-frequency induction furnace. The indium, tin, and antimony alloys were melted in A1203 crucibles, under a boric anhydride cover, and were poured into split graphite finger molds. The aluminum, germanium, arsenic, lead, and bismuth alloys were melted in machined graphite crucibles; they were also covered with boric anhydride and poured into split graphite finger molds. The $-in.-diam ingots were heated to 750°C and were forged and hot-rolled down to 0.1 by 0.1 in. The wires were pickled in a 25 pct HNO3-75 pct H2O solution to remove any oxygen-rich surfaces. The wires were then annealed at 550°C for 2 hr in a dissociated ammonia atmosphere. They were then furnace-cooled for 20 hr to room temperature in this atmosphere. The wires were cold-drawn to 0.0808 in. diam. The finished wires were again annealed at 550°C in the same manner as in the first anneal. Thermoelectric Power. The thermoelectric power of a single specimen of each alloy was determined against pure silver which contained a maximum impurity content of 0.014 pct by weight. The wire specimens were straightened and then cleaned with ethyl alcohol. They were then reannealed in the same way as the finished wires to assure that any residual stress would be at a minimum level. Previous work has shown that the presence of small amounts of stress has the effect of decreasing the thermoelectric power. The alloy specimen was soldered to the pure silver wire to form the measuring junction. A standard set of copper leads was then soldered to the reference junctions of the thermocouple. These junctions were maintained in separate dewar flasks which contained finely shaved melting ice during the test. The thermal electromotive forces of the thermocouples were measured at four temperatures between 15° and 45°C. A known source of electromotive force was balanced against the output of the thermocouple until a null balance was reached. The data were then expressed in terms of the thermoelectric power at 30°C. The results were then converted to absolute thermoelectric power, s303.3 These data have an average error of less than ±0.2 pct. RESULTS AND DISCUSSION All of the experimental data are given in Table 11. Since the electromotive forces of the binary alloys of silver were determined against the pure silver from which they were made, the resultant thermoelectric powers are only a function of the intentionally added binary elements at the constant test temperatures. This provides a direct measure of the effects of the alloying elements. The absolute thermoelectric power of an alloy of silver is given4 by:

Jan 1, 1968

By C. Graeme-Barber, R. L. Bell, T. G. Langdon

An analysis is made of the formulas and ,methods used to estimate the contribution of grain boundary sliding to the overall strain of a polycrystal. The errors involved in the approximations and/or ,mistakes in earlier work are assessed quantitatively so as to make possible the critical use of previously published data. SINCE it has been found that, under conditions of very slow creep, the strain due to grain boundary sliding (?gb) may contribute as much as 80 pct of the total creep strain,1,2 it is obviously important to have reliable methods for estimating this grain boundary strain. In two recent papers Stevens3,4 has drawn attention to the pitfalls encountered in assessing ?gb. He criticizes 1) the assumptions made in the derivation of some of the formulas for ?gb, and 2) the indiscriminate averaging procedures used for obtaining the quantities substituted in these formulas. These and further criticisms of earlier work are mostly valid. Unfortunately the only formulas and procedures recommended are either impossible or very difficult to apply in practice. Furthermore no attempt is made to assess the errors involved by the earlier approximations or mistakes, and so it is not possible to make critical use of any of these early dab. The present article attempts to improve on these shortcomings by reference to empirical verification of easily applied formulas whose theoretical derivations involve some otherwise unjustifiable assumptions, and by a quantitative assessment of the errors in previous work. DEFINITIONS First it is necessary to define the terms and symbols to be used. The choice of symbols preferred here is a logical combination and extension of the v introduced by McLean5 and the u by Brunner and rant.' In Fig. 1 the two grains X and Y are displaced by the sliding vector AC. u is the component of sliding resolved along the stress axis, v is that measured perpendicular both to the stress axis and to the specimen surface, and w is that measured perpendicular to the stress axis but in the plane of the surface. Two angles define the orientation of the grain boundary: 8, between the stress axis and the surface trace of the boundary, and +, the internal angle on a longitudinal section cut perpendicular to the surface. In computing the strain resulting from the boundary displacement at all the in- dividual boundaries in a polycrystal the components u, v, or w are sometimes averaged along a longitudinal line (i.e., parallel to the stress axis), sometimes along a transverse line, and sometimes at randomly chosen boundaries. Averages obtained in these three ways are given subscripts 1, t, and r, respectively. Stevens rightly calls attention to the possibility of non-equiaxed grain shapes either at the start or at the end of deformation. In this article all values of numbers of grains per unit length will refer to measurements made before deformation. The subscripts 1 and t will be used for the number of grains per unit length obtained along longitudinal and transverse lines, r for that obtained by averaging along a number of randomly directed lines. FORMULAS FOR ?gb ?gt, as a Function of u. An obvious truth is that cgb can, in principle, be obtained by summation of all the v components at the boundaries intersected by a longitudinal line of known length I, viz.: where nl is the number of grains per unit length, parallel to the stress axis, in the unstrained specimen. There are assumptions in the analytic derivation of Eq. [I] due to Brunner and rant' but ~achinger' arrived at Eq. [la] by a rigorous method. Unfortunately the experimental procedure required by Eq. [ la] proves very difficult as boundary migration tends to obscure the points at which the longitudinal line meets the grain boundary and the errors on such measurements tend to be large, see Fig. 2. For example, on a specimen of Magnox AL 80 at a creep strain of 9.7 pct, 300 measurements of u obtained from the points of intersection of a longitudinal line with the grain boundaries gave ul = 8.95 ± 3.58 pm, or an error of ±40 pct, at the 95 pct confidence limit. These large errors due to migration may be avoided by measuring u from the separation of the segments

Jan 1, 1968

By G. E. Pellissier, P. H. Salmon Cox, B. G. Reisdorf

Banding that occurred in plates rolled from the early production heats of 18Ni(250) maraging steel is described and related to the segvegation of certain alloying elements (nickel, molybdenum, titanium), the extent of which was quantitatively evaluated by means of electron-microprobe analysis. The effect of banding on mechanical properties is discussed, with particular reference to observed directional differences in plane-strain fracture toughness of plates. It is shown that banding originates as interdendritic segvegation during ingot solidification and persists in some degree through normal soaking and hot reduction to plate. The results of the study showed that heating sections of small laboratory-cast ingots at 2200°F for 4 hr was sufficient to markedly reduce microsegregation and to considerably improve mechanical properties. Hot rolling of 7-in.-thick ingot sections to 1/2-in.-thick plate effected a similar reduction of microsegregation, but resulted in even greater increases in ductility and toughness than that obtained by homogenization treatment alone. DURING the past few years, considerable attention has been directed towards the low-carbon, high-alloy maraging steels and in particular towards the 18Ni-8Co-5Mo-0.4Ti alloy. The steels of this group, having an excellent combination of high strength and toughness, have a number of advantages over their more conventional medium-carbon low-alloy, quenched-and-tempered counterparts. In the annealed condition, the maraging steels are in the form of a ductile marten-site; aging at a relatively low temperature, typically 900°F for 3 hr, increases greatly the strength through the precipitation of intermetallic compounds. One problem in the early production heats of maraging steel was that the finished plate frequently displayed a banded structure. Previous work on other steels1-' had established that banding in wrought products is either a direct or an indirect consequence of chemical segregation, which occurs during solidification and persists to some extent through normal thermal and mechanical treatments. For example, Smith and others: in a study of low-alloy steel, were able to correlate the severity of banding in the wrought product with the degree of interdendritic segregation of nickel and chromium in the as-cast ingot. The effect of banding on the mechanical properties of steels is usually considered to be detrimental, although there is only limited evidence to suggest that a marked improvement in properties can be obtained with less heterogeneous structures. Comparison of the longitudinal and transverse tensile properties of banded and of homogenized 4340 steel showed that only the transverse ductility was improved by homogenization, but even then the improvement was not commercially significant.' Conversely, homogenization of through-the-thickness tension specimens of quenched-and-tempered steel plate, containing 1.47 pct Mn, increased the strength by as much as 10 pct and the tensile ductility by at least a factor of twos5 This improvement was related to the elimination of manganese-rich bands, which also are one of the factors responsible for cold cracking in the heat-affected zone of metal-arc welds.7 In the present study the nature and severity of banding in early commercial 18Ni(250) maraging steel plate and in laboratory-melted 18Ni(250) maraging steel plate was determined. The effects of banding on plane-strain fracture toughness and the effects of thermal homogenization treatments on the strength, tensile ductility, and toughness of 18Ni(250) maraging-steel as-cast ingots and rolled plate were evaluated. In addition, the effects of hot deformation by rolling on the mechanical properties of ingots were determined. 1) STUDIES OF BANDING IN EARLY PRODUCTION PLATE The chemical composition of the steel (A) used in this part of the investigation is shown in Table I. Banding was not clearly evident in either as-rolled or annealed* plate, but annealed and agedc** plate had a banded structure. The typical banded condition, Fig. 1, consists of layers of unetched austenite (white) and dark-etching martensite in a light-etching martensitic matrix. X-ray diffraction measurements showed that this steel contained more than 6 pct austenite. An electron-probe X-ray microanalyzer (using a focused beam of electrons) was used to determine the composition of the bands and of the material between the bands with respect to the main alloying elements— nickel, molybdenum, titanium, and cobalt. The recorded X-ray intensities were converted to concentration values with the use of a standard of similar composition. To facilitate probe positioning, all analyses were conducted on specimens that had been given a light etch. The influence of this etching on the analytical results was negligible; analyses made on the identical area before and after etching yielded essentially the same concentration values. The results of the electron-microprobe analyses at selected points revealed that the layers of austenite and adjacent dark-etching martensite contained greater amounts of nickel, molybdenum, and titanium than did the surrounding matrix, Table 11. The austenite layers

Jan 1, 1968

By Harold R. Larson, John F. Elliott

The standard free energies of formation of several nzetallic sulfides have been measured by a reversible electromotive-force cell employing stabilized zir-conia as the electrolyte. The oxygen potential at the cathode was fixed by the use of pure oxygen gas at 1 atm. It was established at the anode by bringing to equilibrium the reaction between the sulfide and oxide species present. Thus, Gf: for the sulfide could be obtained from the cell potential and the standard free energies of formation of the oxides participating in the reaction. The results in calories per cam rnole for the temperature range 850" to 1100°C are: Use of the reversible electromotive-force cell having an oxide-ion electrolyte to obtain the standard free energies of formation of some of the more stable metallic sulfides offers a convenient experimental method that is very productive. It also avoids some of the problems inherent in the experimental methods' for such studies which rely on precise determination of gas compositions, particularly if these compositions lie near the limits of our capabilities for accurate chemical analyses. The reaction equilibrium between the lowest sulfide of a metal, SO2 at a fixed pressure, and an oxide of the metal has a characteristic oxygen potential. For example: and for metals whose lowest sulfide is much more stable than the oxides of the metal, the equivalent reaction might be:

Jan 1, 1968

By Y. A. Chang

Heat content values of tantalum monocarbide and tungsten monocarbide have been determined from 325" to 985°K by means of a drop-type diphenyl ether calorinzeter. Based on the values obtained in the present study and those available in the literature, best values lected and computed from 298. 15°K to temperatures close to their respectiue melting points. At temperatures higher than 1700°Kfor TaC and 27000 K for WC, values of Cp and related thermodynamic quantities were extrapolated based on the two Debye parameters: one corresponds to the metal sublattice and the other to the carbon sublattice. The contrzbutzon In the total specific heat due to lattice dilation was evaluated using the Nernst-Lindemann relalionship. The calculated values of Cp were in good agreement with the In view of their refractoriness, tantalum monocar-bide (TaC) and tungsten monocarbide (WC) are of con- experimentally determined ualues. Furthermore, the calculated values of the absolute entropies at 298.15"K were 5.03 and 4.15 in comparison to the experimental values of 5.05 and 4.15, all expressed in the unit of cal per degg-atom. Using the same Debye parameters, values of the linear coefficients of ther mal expansion for TaC and WC were calculated from absolute zero to their respective melting points using the Grüneisen equation. The calculated values are in excellent agreement with the experimental values available in the literature. Finally, the values of the bulk modulus of TaC from room tenzperature to temperature near its melting Point were also calculated using the equation recently derived by Anderson. No cot~ipari-son between the calculated and experimental values can be made due to lack of experimental data. siderable practical interest. In order to completely define these materials, it is necessary to know their thermal properties as a function of temperature. Tantalum rnonocarbide having a NaCl structure (B-1 type) melts congruently at 4250PK,1 while tungsten monoearbide with a simple hexagonal structure (Bh type) melts per itectically at 3049°K into melt and graphite.2 In the present study, the heat content values (from which

Jan 1, 1968

By Colin M. Sargent

THE electron diffraction pattern as seen in the electron microscope represents an approximately plane section of the reciprocal lattice. Identifying the zone axis of a diffraction pattern is often laborious for a crystal of low symmetry, especially if several crystal orientations are present. A program has been written in FORTRAN II (Version 2) for the IBM 1620 which will assist in plotting out reciprocal lattice sections. The calculation is performed by choosing a zone axis [uvw] and determining the d spacings and angle between the planes (Ow - v) and (wO - u). (This procedure is varied slightly for zone axes with Miller indices equal to zero.) Cartesian coordinates for the reciprocal lattice points are then calculated for these planes and for (ww— [u + v]). Any reciprocal lattice points within the parallelogram formed by the origin and these three points are then computed. The input and output are best described by use of an example (Monoclinic ZrO2) used in the author's work. Input consists of two cards: 1) The crystal parameters: a, b, c, a, 8, y, e.g., 5.1477, 5.2030, 5.3156, 90.000, 99.380, 90.000. 2) Three numbers, D, E, F, e.g., 5, 3, 3.0710-the first is the limit of the sum (u + v + w) considered; the second limits the absolute value of u, v, and w to (E- 1), e.g., 2, so that zones (221) would be the highest order considered in this example; the third, F, is the required constant, yL. Output is in the format shown in Table I. The reciprocal lattice sections may then be plotted on standard graph paper and compared with the unknown diffraction pattern. (Note that no attempt has been made to deal with systematically absent reflections.) A card deck for the program is available from Colin M. Sargent, ARZ, W-PAFB, Dayton, Ohio, 45433.

Jan 1, 1969

By M. B. Bever, A. K. Jena

THE heats of formation ?H at 273°K of the compound AgMg as a function of composition have been measured by solution calorimetry.1 The value at the stoichiometric composition is -4.41 kcal per g-atom. From electromotive force measurements2'3 the heat of formation at 773°K of stoichiometric AgMg has been determined as -5.19 kcal per g-atom.4 The combination of these two values results in an unusually high negative temperature coefficient of the heat of formation d?H/dT = ?Cp = -1.6 cal per g-atom-OK. By contrast, published heat contents of the compound AgMg and the component elements above room temperature5 indicate that the temperature coefficient of the heat of formation of AgMg is nearly zero. In this communication calorimetrically measured heats of formation of A.K.JENA,Junior- MemberAIME,andM.B. BEVER,Member AIME, are Staff Member, Division of Sponsored Research, and Professor of Metallurgy, respectively, Massachusetts Institute of Technology, Cambridge, Mass. Manuscript submitted July 1, 1968. IMD AgMg below room temperature are reported and the temperature dependence of the heat of formation is discussed. The heat effects of additions of samples of the compound AgMg containing 50.1 at. pct Mg to liquid tin-rich solutions at 623°K were measured in a solution Calorimeter.6 The heat effects of additions plotted against the average of the atom fractions of solutes in the solution before and after each addition were a linear function of composition from which the heat effect at infinite dilution was obtained, Table I. The calorimeter was calibrated by additions of tin; the heat content (H623°K - H273°K) of tin was taken as 4.08 kcal per g-atom.4 The heat effect at infinite dilution of an addition of where heat of formation of AgMg at T°K, T = temperature from which samples are added (78°, 195°. and 273°K), Xi = atom fraction of i in AgMg, ?Hi = relative partial gram-atomic enthalpy of i in tin-rich solution.

Jan 1, 1969

By R. D. Pehlke, J. V. Gluck, R. L. Louvet

A study has been made of the effect of small additions of bismuth on the activity of zinc in dilute solution in molten tin. Free-energy interactions have previously been determined between zinc and various third elements where the solvents were molten bismuth or molten lead.'-4 In both of these solvents, the activity of zinc exhibits a strong positive deviation from ideal behavior (at 550°C y° for zinc in lead is 11.4 and for zinc in bismuth is 3.0). The present work, using tin as the solvent, is an extension to a case where the positive deviation is considerably diminished (y°Zn at 550°C is 1.63). Several previous investigators have studied the Zn-Sn binary system; however, little data is available in the range below 0.1 mole fraction zinc.5= Previous high-temperature galvanic cell studies in the Sn-Zn-Bi ternary system included the determination by Gluck and Pehlke of interactions in the bismuth-rich corner1 and separate investigations of the central region by Oleari and Fioriani6 and by Ptak and Moser.7 Yokokowa et al.8 conducted Knudsen effusion studies in the central region; however, their experiments at 625°K were conducted somewhat below the present experimental temperature range. Their results indicated an increase in zinc activity with the addition of bismuth. The present series of experiments was conducted in galvanic cells represented as follows: Zn Zn++ in LiCI-KC1 eutectic Zn + Bi in Sn (pure reference (fused salt electrolyte) (molten alloy) standard) The experimental apparatus. a multi-electrode system employing alumina crucibles and contained in a Vycor tube under a helium atmosphere, has been described previously, as have been the experimental procedures, precautions, and the methods of data reduction.1-4,- The experimental measurements were made over the range from 450° to 650°C. Between thirty and forty measurements were made in each run. The linearity of the electromotive force vs temperature relations was verified by linear regression techniques. The correlation coefficients exceeded 0.99. The experimental results summarized in Table I include the interpolated electromotive force at 550°C and the temperature dependence of electromotive force. Only results from stable and consistent cells containing more than 0.025 mole fraction zinc are reported. Attempts to run cells at 0.01 or 0.02 mole fraction zinc were not satisfactory. This is attributed to the closeness of the free energies of formation of the chlorides of tin and zinc. Calculations employing Wagner and Werner's criteria for displacement reactions10 indicated that reduction of the zinc content to 0.01 mole fraction places the cell near the borderline concentration for a 1 pct error in measured potential. The compositions shown in Table I are the actual weighed-in amounts. Previous experience has indicated that compositional changes during the running of a stable cell are negligible.' Over the range of compositions studied for the binary alloys, the activity coefficient of zinc was essentially constant indicating that Henry's law is followed to 0.05 mole fraction zinc. The temperature, OK, de-

Jan 1, 1969

By G. C. Rauch, T. H. Courtney, J. Wulff

The superconducting behavior of Nb-Ti alloys containing 40 and higher wt pct of Nb and variable oxygen content was studied as a function of thermomechanical processing. Critical current density (Jc) us applied transverse magnetic field (H) data were obtained for 0.010 in. diam wires at 4.2° Kin steady fields up to 120 kOe. The precipitate responsible for increase in Jc in each of the alloys studied was related to niobium and oxygen content. In alloys containing 40 to 60 wt pct Nb with less than about 1600 ppm of oxygen, w precipitation in the range 350° to 450°C appears to be responsible for the maximum value of Jc observed. In alloys of higher oxygen content (-2500 ppm), the oxygen-enriched a phase which precipitates in the temperature range 450° to 550°C is a more effective fluxoid pinner. Maximum Jc in low oxygen (350 ppm) 80 wt pct Nb alloys was achieved by 600°C aging heat treatments. Measurements of resistive critical field also reflect the changes in composition accompanying precipitation in these alloys. It is well known that the superconducting critical current density, Jc, of solid solution superconducting alloys can be increased by precipitation heat treatments.1-4 The precipitate, to serve as an effective superconzlucting fluxoid pinner and increase Jc, must be of proper size and spacing.' Its electronic properties must also be different from those of the matrix.6 As in age-hardenable systems, optimum temperature and time of aging are dictated by the composition and history of the particular solid-solution alloy under consideration. The alloy diagram of Ti-Nb7-9 shown in Fig. 1 is typical of ß-stabilized Ti alloys. Precipitation to achieve high Jc in Ti-Nb and Ti-Ta alloys is usually carried out in what is believed to be a two-phase a + ß region.1,2,4,10 Previous work on Ti-Nb4,11 and on other ß-stabilized systems such as Ti-V, Ti-Mo,12-14 has shown, however, that the first precipitate to appear is not necessarily (Y. Under specific conditions the meta-stable w phase is precipitated instead. A further complication arises in such alloys from the strong influence of contained oxygen on the phase stability and on the kinetics of precipitation.15,16 The superconducting critical current density of Nb-Ti alloy containing less than 36 wt pct Nb has been studied by Vetrano and Boom1 and Kramer and Rhodes.4 The most effective aging temperature was found to be about 425°C; fluxoid pinning was attributed to the precipita- tion of a by Vetrano and Boom and of w by Kramer and Rhodes. Although the latter workers used recrystal-lized material and the former cold-worked, studies carried out in our laboratory lead us to believe that the type of precipitate responsible for increased Jc is unaffected by prior cold-work.17 That other types of precipitates may also be effective, especially in higher oxygen-containing alloys, has been demonstrated by Reuter, et al.2 in this laboratory with the aid of electron microscopy. Reuter et al. found that at an aging temperature of 600°C, fee-TiO is precipitated, resulting in high values of Jc. Even higher values of Jc were observed after heat treatment at 500°C, but the precipitate could not be indexed as fee-TiO. Whether the precipitate was oxygen-rich w or a could not be clearly distinguished. The work nevertheless indicates that appreciable amounts of oxygen alter the nature of the phases precipitated at different temperatures, at least in alloys containing more than 36 wt pct Nb. Since such compositions are more readily worked into suitable wire than lesser niobium content alloys, it was decided to study the response to aging of the alloy compositions reported in the present paper with the hope of clarifying the effect of composition on the precipitation processes responsible for high values of Jc. I. EXPERIMENTAL Nb-Ti alloys containing 40, 50, 60, and 80 wt pct Nb were prepared by are-melting 35 g ingots of iodide crystal bar titanium and electron-beam melted niobium.

Jan 1, 1969

By Winston A. Wong, John J. Jonas

Commercial purity aluminum was deformed by extrusion over the temperature range 320° to 616°C and the strain rate range 0.1 to 10 per sec. Flow stresses and strain rates were calculated from the experimenLa1 ram pressures and speeds. The stress-strain rate-lemperature relationship in extrusion was found to be similar to that in creep. Extrusion, torsion, compression, and creep data extending over ten orders of magnitude of strain rate and over two orders of magnitude of stress were correlated by a single creep equation. It was concluded that hot-working is a thermally activated process, in which the rate-controlling mechanism is either the climb of edge dislocations or [he motion of jogged screw dislocations. The microstructural changes observed during extrusion were consistent with the proposed deformation mechanisms. ALTHOUGH great progress has been made in understanding the technology of extrusion, very little is known about the actual deformation mechanisms operating during flow. Previous accounts describing extrusion have indicated that the relationship between ram speed (V), pressure (P), and temperature (T) can be given as follows:1 V = apb and P = A' exp(-AT). In these equations, a and b are constants which depend on temperature, A' is a constant which depends on ram speed, and A is a "coefficient" with a different value for each metal. Although these equations have fairly wide application, they do not contribute much to a fundamental understanding of the deformation. Furthermore, extrusion has not hitherto been considered as a thermally activated rate process. This lacuna is surprising because hot-working is similar to high-temperature creep in several respects. There is, in fact, a fair body of experimental evidence suggesting that the material response under hot-working conditions is similar to that occurring under creep conditions, in spite of the many orders of magnitude difference in strain rate.2"4 Since creep has been extensively analyzed in terms of dislocation mechanisms, the comparison of hot-working to creep is useful, for it can suggest the possible deformation mechanisms operating during hot-working. In this paper, the hot extrusion of aluminum will be examined from the point of view of thermally activated deformation mechanisms, such as operate during creep. EXPERIMENTAL PROCEDURE The experimental procedure consisted of extruding commercial purity aluminum* over a range of ram velocities and temperatures at constant die reduction by the direct method. Details of the experimental equipment have been published elsewhere.5 Extrusion was carried out at each of the following billet temperatures: 320°, 376°, 445°, 490°, 555°, and 616°C at the following constant ram speeds: 0.002, 0.008, 0.02, 0.1, and 0.2 in. per sec.* All results were obtained using a square-shouldered die with an extrusion ratio of 40:1, giving a reduction in area of 97.5 pct. The ram force was the dependent variable, and was measured by means of strain gages on the ram and was plotted as a function of ram travel. The sequence of events before making an extrusion was duplicated before each run so as to minimize as much as possible variations in experimental conditions. For example, after the equipment had been assembled, the billet was allowed to heat up to temperature inside the insulated container. Once the container attained the desired temperature, a period of 1/2 hr was allowed to elapse before the extrusion was made. This time was found to be required to allow the billet to reach a steady-state temperature, as determined from previous tests. When all was ready, extrusion was carried out without interruption; that is, the billet was upset and extruded in one operation. EXPERIMENTAL RESULTS AND DISCUSSION The two usual experimental approaches for investigating high-temperature deformation exhibit an important common feature. In the first approach, which corresponds to creep, a constant stress (or load) is applied to the material at constant temperature and the resultant strain is recorded against time. After an initial transient stage, a state of constant strain rate exists (secondary creep), in which a steady-state condition is established which is sensitive to variation in either applied stress or temperature. In the second approach, a constant strain rate is applied and the resultant flow stress is recorded. This corresponds to the situation in hot torsion or hot compression, where it is observed that, for a constant test temperature, there is an initial rise in stress to a steady value which is maintained up to very high strains. In tests of this type, a steady-state region is also established in which the stress is sensitive to variation in either the strain rate or the temperature.3,4,6-16 In both types of tests, therefore, a steady-state region is established after an initial transient. In the case of hot-working this region may be called steady-state hot-working, and it is analogous to steady-state creep with which it has many common features. Stress Dependence of the strain Rate in Extrusion. In order to assess the stress dependence of the strain rate under extrusion conditions, and to compare it to that of creep, as well as of hot torsion and hot compression, the extrusion data were analyzed according to power, exponential and hyperbolic sine creep equations.

Jan 1, 1969