By S. C. Das. Gupta, B. S. Lement

isothermal formation of martensite occurs in the range of —65o to —197oC and is always preceded by some athermal transformation. By rapid cooling the isothermal, but not the athermal, component of transformation can be suppressed. Stabilization against isothermal transformation can be induced by cycling from below M. to room temperature. A LTHOUGH the transformation of austenite to XV martensite is generally believed to occur only on cooling, recent evidence indicates that this reaction can also occur at constant temperature. Isothermal formation of martensite was observed in tool steel by Fletcher, Averbach, and Cohen.'. They found that the hardening reaction that occurs during the quenching of a plain carbon or low carbon alloy tool steel does not stop immediately when room temperature is reached; instead austenite continues S. C. DAS GUPTA is Research Fellow, Department of Metallurgy, University of Notre Dame, Notre Dame, Ind. B. S. LEMENT, Associate Member AIME, is on the Research Staff, Department of Metallurgy, Massachusetts Institute of Technology, Cambridge, Mass. Discussion on this paper, TP 3123E, may be sent, 2 copies, to AIME by Dec. 1, 1951. Manuscript, April 16, 1951. Detroit Meeting, October 1951. This paper represents part of a thesis by S. C. Das Gupta submitted in partial fulfillment of requirements for the degree of Doctor of Philosophy in Metallurgy to the University of Notre Dame. to transform at room temperature although at a decreasing rate. Since only a small amount of austenite transforms in this fashion, isothermal formation of martensite was considered to be merely a "tailing off" effect of the main hardening reaction. Another point of view was advanced by Kurd-jumov and Maksimova"' * who reported that the austenite-martensite reaction could be suppressed by rapid cooling of a 6 pct Mn-0.6 pct C steel in liquid nitrogen and that as much as 25 pct martensite could be formed by reheating to and holding at subzero temperatures above that of liquid nitrogen. These investigators came to the conclusion that martensite is thermally nucleated at certain special regions in the austenite and subsequently grows to observable dimensions. Isothermal transformation of austenite to martensite was cited by Fisher, Hollomon, and Turnbull" as evidence supporting another nucleation and growth theory of martensite formation. According

Jan 1, 1952

By G. R. Speich, S. A. Kulin

R. C. Shnay (Dept. of Mines and Technical Surveys, Ottawa, Ont., Canada)-—The authors are to be congratulated on an interesting and informative paper. However, several questions arise when the isothermal formation of martensite .is considered in relation to the formation of bainite at temperatures near the M, point. The reactions in an alloy and in a plain carbon steel would appear to be comparable; and in the course of a recent investigation of the austenite-bainite transformation in a plain carbon steel,Ia the writer has obtained data at temperatures above and below the M, point. These data are in some respects similar to those of the authors and a comparison would seem justified. The steel used in this investigation had the nominal composition: C, 0.80 pct; Mn, 0.20; and Si, 0.20. The course of the transformation was followed by the use of a magnetic balance. The magnetic moment of the specimen as determined by this instrument is directly proportional to the percentage of the total volume of the specimen which has transformed to bainite. ~lf specimens were austenitized at 1850°F for 4 hr, quenched to the transformation temperature, and quickly transferred to the magnetic balance. Readings were taken at regular intervals until the transformation had stopped. A typical transformation curve is shown in Fig. 9. The preliminary curve preceding the S-shaped curve was found at all temperatures above the M, to around 600°F. Both the extent of this preliminary curve and the time interval between it and the S-shaped curve were found to decrease with increasing temperature as was suggested by Davenport and Bain.14 Therefore,

Jan 1, 1953

By R. B. G. Yeo

Pronounced isothermal martensite formation at room temperature was measured dilatometrically in a steel containing 0.01 pct C, 24.9 pct Ni, 0.26 pctAl, 2.58 pct Ti and 0.25 pct Cb. It is shown that martensite will form isothermally if stabilization of the austenite-martensite transformation is eliminated by removal of carbon. The decarburization of two iron-nickel alloys allows isothermal transformation to martensite to occur at temperatures above their athermal Ms temperatures. In an Fe-22.4 pct Ni alloy, at the 0.008 pct C level, the Ms temperature during air cooling is 85°F higher than that during- water quenching-. At the 0.15 pct C level this difference is reduced to only 5°F. The introduction of carbon causes stabilization during air cooling which lowers the Ms temperature virtually to the same level as determined during mate?. quenching. Thus in the 0.15 pct C alloy, the Ms temperature is almost independent of cooling rate. It is suggested that rival theories of martensite formation should be reexamined in alloys of sufficiently low carbon and nitrogen content to eliminate the complication of stabilization. The Ms temperature of a steel containing 0.01 pct C, 24.9 pct Ni, 0.26 pct Al, 1.58 pct Ti and 0.15 pct Cb, solution treated at 1500°F and air cooled as 1/8-in. diam specimens, was found to be 57 °F. 1 However, when held for several hours at room temperature the steel hardened slightly and became appreciably ferromagnetic. Isothermal transformation to martensite was first revealed by Kurdjumov and Maksimova2 in an iron-base alloy containing 0.6 pct C, 6.0 pct Mn and 2 pct Cu. Most of the other studies of isothermal martensite have also been confined to highly alloyed steels which transform at subzero temperatures; for instance, DasGupta and Lement, 3 Cech and Hollomon, 4 Machlin and Cohen,5 Shih, Averbach, and Cohen.6 Averbach and cohen7 noted a rapidly decaying volume increase at room temperature in a steel containing 1 pct C, 1.5 pct Cr and 0.2 pct V. cina8 and Marshall, Perry, and Harpster9 have described the isothermal transformation to martensite at room and subzero temperature in stainless steels. Kurdjumov10 has recently reviewed the subject, noting that the isothermal formation of martensite can be observed only in the temperature range somewhat below Ms or below -50°C. The isothermal formation of martensite may be characterized as follows: 1) It occurs in steels of widely different compositions, the main prerequisite being a low transformation temperature. 2) The transformation occurs by the formation of new plates and not by the growth of old ones. 3) The isothermal transformation is suppresed by stabilization during slow cooling or holding at temperatures near room temperature. However, the factors governing this mode of transformation are still not fully understood. The formation of martensite isothermally suggests an activated process. The early theories of martensite formation did, in fact, utilize classical nucleation concepts. Kurdjumov 11 first proposed the presence of thermally activated nuclei of different sizes and compositions which would grow if they reached critical size during cooling. This treatment was enlarged and developed quantitatively by Fisher, Holloman, and Turnbull12,13 and was later reviewed by the latter two authors.14 Fisher15 associates Ms with a nucleation rate of one per cc per sec. At slightly higher temperatures the nucleation rate is so low that isothermal formation of martensite is not observed in reasonable times. At slightly lower temperatures the nucleation rate is so high that it could not be suppressed by rapid cooling. By judicious use of parameters Fisher 16 was able to obtain good agreement between classical nucleation theory and the incubation times of martensite formation.4 However the application of these principles to martensite formation in iron-nickel alloys15 predicts that an alloy containing about 30 pct (31 at. pet) Ni would not transform. The presence of an Ms temperature at -223° C in an alloy containing 34.1 pct (33 at. pct) Ni led Kaufman and cohen17 to reject the hypothesis of homogeneous nucleation in favor of the reaction path theory originally proposed by Cohen, Machlin and Paranjpe.18 This theory conveniently explains the formation of martensite athermally but becomes labored when dealing with isothermal formation. Kaufman and cohen19 did explain the isothermal activation of embryos by assuming it to be a result of the expansion of their boundary dislocation loops but this treatment predicts an upper temperature limit of isothermal martensite formation.

Jan 1, 1962

By E. S. Machlin, Morris Cohen

The isothermal formation of martensite in a 71 pct Fe, 29 pct Ni alloy is found to take place mainly by the nucleation of new plates rather than by the growth of existing ones, and is dependent on the temperature and time of the isothermal hold, the amount of atherrnal martensite present, the state of internal strain, and the application of tensile stress. The conclusion is reached that the isothermal nucleation is activated by thermal fluctuations superimposed on localized regions of very high strain. The reaction-path concept, involving martensite nucleation at strain embryos by athermal activation on cooling, or by thermal fluctuations on holding, reconciles the athermal and isothermal modes of transformation, and offers a unified picture of the kinetics of martensite formation. THE phenomenon of isothermal martensite formation has been the subject of considerable study lately,'-' and its reality has been thoroughly established. The existence of such isothermal transformation has been claimed to confirm the nucleation and growth hypothesis as applied to the martensitic reaction.1 " However, the isothermal formation of a martensitic phase is also compatible with the reaction-pathw escription of the transformation. The purpose of this investigation is to examine the isothermal mode of the martensitic reaction, both theoretically and experimentally, in order to test the likelihood of the above two mechanisms. Material and Methods The alloy used in this study contained about 71 pct Fe and 29 pct Ni. The complete analysis was 29.5 ± 0.2 pct Ni, 0.036 pct C, 0.02 pct N, 0.19 pct Mn, 0.09 pct Si, 0.008 pct P, and 0.006 pct S. The amount of isothermal transformation was determined by electrical resistance measurements using a Kelvin double bridge. The specimens were in the form of rods 1/16 in. diam x 4 in. long. Aus-tenitizing was performed at 1095°C for % hr either in a pre-purified nitrogen atmosphere or in an evacuated Vycor tube, followed by oil quenching to room temperature. After this treatment, the samples were completely austenitic, and the transformation studies were conducted at subatmospheric tempera- tures. Lineal analysis and X-ray determinations of retained austenite were used to calibrate the electrical resistance changes in terms of the percentage of martensite. The martensite range curve for this alloy is given in Fig. 9 of ref. 6. The M, temperature occurs at about -18°C (255°K). Reaction-Path Theory The nucleation and growth description of the martensitic transformation that occurs isothermally has already been given by Kurdjumow.','2 However, no comparable treatment exists using the reaction-path concept." Consequently this section presents the reaction-path description of the isothermal mode of the martensitic transformation. According to the latter theory, there is a reaction path (a strain) which describes the relative motion of the atoms during their transference from the austenitic to the martensitic state. The possibility exists, therefore, that the nucleation of a martensitic plate is accomplished by an embryo that comprises a state intermediate between that of austenite and martensite. This state may be attained within a finite volume by means of a homogeneous strain of the austenitic matrix. There is a free-energy barrier (F.) along the reaction path, corresponding to a critical strain in a critical volume. When activation is achieved, a spontaneous increase in strain and volume of the embryo takes place to generate the full-size martensitic plate. This mode of nucleation is to be distinguished from the more conventional mode involving embryos of the martensitic phase that merely grow in size by an interface motion. There are two ways whereby embryos in the austenitic phase can achieve the critical state of strain for isothermal nucleation: 1—through the formation of internal strains by plastic deformation or by stress; and 2—through thermal fluctuations, preferably superimposed upon existing internal strains. The activation free energy F,, must be supplied either mechanically by internal strains or thermally by energy fluctuations, or by a combination of both.

Jan 1, 1953

By Gareth Thomas

The analysis of Kikuchi pattersns of exct ovientalions from single cryslals and paired Kikuchi lines from single and overlapping crystals is shown to be useful and quanlitalve and is applied to Phase transfovnzcitions including ordering, spinodals, mavten-silic, and nuclealion and growth pyocesses. 112 pinciple, the analysis of exacl orientations enables the crystal system and the Bravais lattice of a crystal to he determined. The advantages of the davk-field imaging technigure for detecting vevy small precipitates are also described. ALTHOUGH Kikuchi electron-diffraction patterns were first observed nearly 40 years ago,' little systematic application seems to have been made of them, until fairly recently during electron microscopy, when their usefulness in contrast experimen and for determining exact orientations8'9 has been pointed out. With the availability of gonio-metric specimen tilting stages it has now become possible to make much wider use of diffraction patterns, particularly the Kikuchi pattern, which is the main subject of this paper. The treatment presented here is not exhaustive but it is hoped that it will stimulate more use of Kikuchi patterns during electron-microscopy investigations. The Kikuchi pattern is formed as a result of Bragg diffraction of the inelastically scattered electrons produced during the interaction of the beam and thick specimens, The important feature of these patterns is that they give an accurate representation of the symmetry of the crystal being investigated, so that it is possible to identify crystal systems and even the Bravais lattice. This means that new structures, e.g., formed in phase transformations, may be identified during normal electron microscopy, so that Kikuchi-pattern analyses considerably extend the uses of the electron microscope. Recent work has also shown that dark-field images are more informative than bright-field images, particularly, for observing small precipitates. The second part of this paper discusses some applications and advantages of dark-field imaging in studies of two-phase systems. 1) DIFFRACTION PATTERNS 1.1) Spot Patterns. Electron-diffraction spot patterns have their limitations because of the importance of the form factor on the intensities and shape of the reciprocal lattice points. Because of the extension of these points into relrods, reflections are possible over a large angular range (+5 deg) and the patterns from thin regions can be complicated because second-layer relrods intersect the reflecting sphere. Spot patterns can thus give only an approximate idea of the crystallography unless the foil is tilted into exact orientation. In this case the spot pattern is symmetrical, with equal numbers of spots on the positive and negative zone directions about the origin. Such cases are necessary for structural analyses and have been used recently to determine the crystal structure of the ordered Ta64C phase." Exact orientation means that the plane of the reciprocal lattice lies exactly normal to the incident beam as shown in Fig. 1(b). It should be noted that in exact orientations the angle of reflection is less than the exact Bragg angle 9 so that the reciprocal lattice points lie to the outside of the sphere, Fig. 1(b). This deviation is denoted by the parameter s and in the usual convention4 s is negative for exact orientations and, of course, zero at the exact reflecting position shown in Fig. l(a). In order to avoid secondary reflections from thickness relrods it is advantageous to work in thicker regions of foils. Diffraction from thick regions may also produce Kikuchi patterns and as dis-

Jan 1, 1965

By A. Spilners, M. Simnad

The rates of formation of the different oxides on molybdenum in pure oxygen at 1 atm pressure have been determined in the temperature range 500° to 770°C. The rate of vaporization of MOO, is linear with time, and the energy of activation for its vaporization is 53,000 cal per mol below 650°C and 89,600 cal per mol at temperatures above 650°C. The ratio Mo03(vapor.lzing)/MoOS3(suriace) increases in a complicated manner with time and temperature. There is a maximum in the total rate of oxidation at 6W°C. At temperatures below 600°C, an activation energy of 48,900 cal per mol for the formation of total MOO, on molybdenum has been evaluated. The suboxide Moo2 does not increase beyond a very small critical thickness. At temperatures above 725°C, catastrophic oxidation of an autocatalytic nature was encountered. Pronounced pitting of the metal was found to occur in the temperature range 550° to 650°C. Marker movement experiments indicate that the oxides on molybdenum grow almost entirely by diffusion of oxygen anions. USEFUL life of molybdenum in air at elevated temperatures is limited by the unprotective nature of its oxide which begins to volatilize at moderate temperatures. Although the oxide/metal volume ratio is greater than one, the protective nature of the oxide film is very limited. Gulbransen and Hickman' have shown, by means of electron diffraction studies, that the oxides formed during the oxidation of molybdenum are MOO, and MOO,. The dioxide is the one present next to the metal surface and the trioxide is formed by the oxidation of the dioxide. Molybdenum dioxide is a brownish-black oxide which can be reduced by hydrogen at about 500°C. Molybdenum trioxide has a colorless transparent rhombic crystal structure when sublimed, but on the metal surface it has a yellowish-white fibrous structure. It is reported to be volatile at temperatures above 500" and melts at 795°C. It is soluble in ammonia, which does not affect the dioxide or the metal. In his extensive and classic investigations of the oxidation of metals, Gulbransen2 has studied the formation of thin oxide films on molybdenum in the temperature range 250" to 523°C. These experiments were carried out in a vacuum microbalance, and the effect of pressure (in the range 10-6 yo 76 mm Hg), surface preparation, concentration of inert gas in the lattice, cycling procedures in temperature, and vacuum effect were studied. The oxidation was found to follow the parabolic law from 250" to 450°C and deviations started to occur at 450 °C. The rates of evaporation of a thick oxide film were also studied at temperatures of 474" to 523°C. In vacua of the order of 10- km Hg and at elevated temperatures, an oxidation process was observed, since the oxide that formed at these low pressures consisted of MOO, which has a protective action to further reaction in vacua at temperatures up to 1000°C. Electron diffraction studies showed that, as the film thickened in the low temperature range, MOO8 became predominant on the surface. Above 400°C MOO, was no longer observed, MOO, being the only oxide detected. The failure to detect MOO, on the surface of the film formed at the higher temperatures does not militate against the formation of this oxide, since according to free energy data MOO3, is stable up to much higher temperatures. At the low pressures employed, this oxide would volatilize off as soon as it was formed. Its vapor pressure is relatively high and is given by the equations" log p(mm iig) = -16,140 T-1 -5.53 log T + 30.69 (25°C—melting point) log p(mm He) = -14,560 T-1 -7.04 log T+1 + 34.07 (melting-boiling point). Lustman4 has reported some results on the scaling of molybdenum in air which indicate a discontinuity at the melting point of MOO, (795°C). Above the melting point of MOO,, oxidation is accompanied by loss of weight, since the oxide formed flows off the surface as soon as it is formed.5,6 Qathenau and Meijering7 point out that the eutectic MOO2-MOO3 melts at 778C, and they ascribe the catastrophic oxidation of alloys of high molybdenum content to the formation of low melting point eutectics of MOO3 with the oxides of the melts present. Fontana and Leslie -explain the same phenomenon in terms of the volatility of MOO,, which leads to the formation of a porous scale. Recent unpublished work by Speiser9 n the oxidation of molybdenum in air at temperatures between 480" and 960°C shows that the rate of weight change of molybdenum is controlled by the relationship between the rates of formation and evaporation of MOO,. They have measured the rates of evaporation of Moo3 in air at different temperatures and estimated an activation energy of 46,900 cal. This compares with the value of 50,800 cal per mol obtained by Gulbransen for the rate of sublimation of MOO, into a vacuum.

Jan 1, 1956

By F. D. Rosi, C. A. Dube, B. H. Alexander

WHEN a deformed polpcrystalline metal is heated to a sufficiently high temperature, a recrystallized structure develops which consists of small, essentially stress-free grains. This transformation is referred to as primary recrystallization. Under certain conditions, on prolonged annealing of the specimens, a type of grain coarsening occurs in which a small number of grains commence to grow at various points by devouring the neighboring finegrained primary structure, which, in itself, exhibits a marked stability toward normal grain growth. This grain coarsening process has been referred to by Burgers' as "secondary recrystallization" or "exaggerated grain growth." Although much work has been done on recrystallization and growth processes, present knowledge of the factors which determine the occurrence and growth of secondary grains is inadequate for the advancement of a theory which accounts for the observed characteristics of this recrystallization phenomenon. In this respect, it would be important to make measurements of the velocity of growth of these large secondary grains. The early work of Feitnecht2 on aluminum showed that the size of secondary grains increased with temperature and time, suggesting that such measurements would be possible. More recently, Burgers1 found that the growth velocity of these grains in aluminum was constant over a large time interval, as is generally found for the growth velocity of primary grains in a uniformly deformed test piece.3-5 It is reasonable to expect that the determination of the activation energy of the secondary growth process might lead to a better understanding of the underlying atomic mechanism. This investigation, therefore, is one of a series primarily designed to measure the growth velocity of secondary grains at various temperatures for silver, copper, and aluminum. It is hoped that these studies along with those of orientation relationships, will establish a sound basis for theorizing as to the origin and nature of the secondary transformation. Experimental Procedure The metal used in the present investigation was high-purity silver (999.9 fine), which was supplied in the form of cold-rolled plates 0.250 in. thick. These plates were annealed at 500°C for 1 hr and then straight-rolled to a thickness of 0.04 in. in three reductions of approximately 45 pct, followed in each case by an anneal at 450°C for 1/2 hr. The 0.04 in. sheets were given a final reduction of approximately 50 pct, which resulted in a thickness of 0.02 in., thereby insuring two-dimensional crystal growth. Individual specimens of this material about 1x3 cm were used for all heat treatments, unless otherwise noted. The annealing was carried out under an atmosphere of argon in an Inconel tube furnace whose temperature was controlled to within -+2°C. Metallographic examination of the secondary transformation was accomplished by mechanically polishing the specimens on one side to approximately one half their thickness through 2/0 metallographic emery paper, and then electrolytically polishing in a solution of potassium ferrocyanide and sodium cyanide. With a current density of approximately 20 amp per sq dm, the time required to obtain a satisfactory surface varied from 3 to 5 min. Standard potassium bichromate was used to etch the electrolytically polished surfaces. A heavy etch with this solution produced a sharp contrast between the secondary grains and the fine-grained primary structure, darkening the latter while leaving the large secondary grains bright. All area measurements of the secondary crystals were made with a planimeter on enlarged tracings of the grains.

Jan 1, 1953

By J. W. Rutter, K. T. Aust

The migration of individual, large-angle grain boundaries has been studied as a function of tempereature and solute concentration in specimens of zone i.e filled lead containig very small additions of silver and of gold. Tile results are compared with various the-ories of grain boundary migration and with observations made prev.iorlsly of grain boundary migration in similar specimens of zone-refined lead containing tin additions. A previous investigation by the authors dealt with [he temperature dependence of grain boundary migration in bicrystals of zone-refined lead containing small additions of tin.' It was shown that tin additions as low as a few parts per million cause a large decrease in the grain boundary migration rate at any given temperature, as well as a marked increase in the temperature dependence of the migration rate. It was found that existing theories of grain boundary migration. based on the motion of dislocations. or upon the concept of atom transfer in groups across the boundary (group process theory). or upon the control of grain boundary motion by volume diffusion of impurity atonls along with the boundary. are incapable of accounting for the observations. The single process theory of grain boundary migration. which is an absolute reaction rate calculation based on the transfer ui atoms singly across the moving boundary, was found to predict the migration rate reasonably well for a number of boundaries whose motion was shown to be very little influenced by impurities, but not for boundaries whose illation was influenced markedly by impurities. It was concluded that the elementary process of grain boundary migration involves the activation of single atoms during transfer across the boundary. and that inadequate knowledge is available to permit the influence of impurities to be properly taken into account. The present study was initiated to check the validity of the above conclusions with other alloy systems, namely high-purity lead with small additions of silver and of gold. Both silver and gold diffuse faster. and with a lower activation energy of volume diffusion. than does tin in lead;' consequently, a study of the effects of silver and gold on grain boundary migration in high-purity lead offered a means of testing theories of boundary migration based on bulk diffusion of the solute (eg. ref. 3). In addition. it was hoped that the present work, in comparison with the results for tin in lead, would provide information concerning which factors are important in determin- ing the interaction between solute atoms and a grain boundary. EXPERIMENTAL PROCEDURE The preparation of bicrystals of zone-refined lead, with various silver or gold additions, was identical to that previously described for the lead-tin alloys.''4 Each bicrystal consisted of a striated crystal which was grown from the melt. and an adjacent striation-free crystal which was introduced by artificial nucleation and growth.''4 The striation or lineage substructure in the melt-grown crystal provided the driving force for grain boundary migration. During the preparation of striated single crystals by growth from the melt, it was found that silver or gold concentrations as low as 2 or 3 ppm by atoms were sufficient to cause formation of the hexagonal cell structure. which is due to the presence of impurity, during freezing. This structure is revealed on the solid-liquid interface by decanting the liquid during freezing. The hexagonal cell structure was observed previously4 in zone-refined lead crystals with tin contents above approximately 200 ppm by atoms. These concentrations of silver, gold, or tin are in agreement with the predicted amounts required for cell formation in lead,5'6 under the present conditions of freezing.4 The absence of cell structure at decanted interfaces, therefore, served as a useful indication that the silver or gold contents were less than 2 or 3 ppm by atoms in the specimens as grown. It was found that grain boundary migration occurred only very slowly when the solute content approached that necessary for cell formation. As a result, the present experiments were conducted with silver or gold additions less than 1 ppm by atoms. This impurity level is well within the solid solubility limits for silver and gold in lead.7 The annealing treatments, measurements of grain boundary velocities, and orientation determinations were carried out as described previously.' However. each bicrystal was also chemically polished in a solution consisting of 8 parts glacial acetic acid and 2

Jan 1, 1961

By R. G. Davies

Isothermal annealing of quenched Fe3Al reveals that the superlattice forms by the nucleation and growth of ordered domains. The activation energy for isothermal ordering and initial domain growth is -29 keal per mole, which is thought to he the activation energy for vacancy migration. Domain growth, in the absence of excess vacancies, has an activation energy of -100 keal per mole. A maximum in the hardness is observed when the structure consists Of ordered domains, -35-4 in size, growing into a short-range ordered matrix and, also as a function of degree of order, S, with an infinite domain size at S = 0.4 to 0.5. It is proposed that both maxima are due to a transition from deformation by unit dislocations to deformation by superdislocntions. FE-AL alloys containing more than -23 at. pet Al, when quenched from above the critical temperature for the Fe3A1 type of order, always contain the maximum possible amount of FeAl (B2) type of order' (see Fig. 1). Thus when the Fe3A1 superlattice forms, in a 25 at, pet A1 alloy, it does so from an imperfect FeAl structure. The formation of the Fe3Al superlattice has been the subject of several recent X-ray,1, 2 electrical-resistivity,3"6 and dilatometric3 investigations. McQueen and Kuczynski3 concluded that the isotherma1 ordering of Fe3Al, after quenching from 800°C (T,, the critical temperature for order, is 55O°C), takes place by the nucleation and growth of ordered domains. However, Feder and Cahn4 found that the isothermal ordering was complex but more like a homogeneous nucleation process than a nucleation and growth process. Lawley and Cahn2 reported that the degree of order is a continuous function of temperature which is a characteristic of a homogeneous nucleation process. Thus, the evidence is conflicting as to the nature of the Fe3Al ordering reaction. Lipson7 was the first to suggest that ordered domains should exist in the Fe3A1 structure since, as

Jan 1, 1964

By G. Borelius

ABOUT the turn of the century, Gibbs' thermo-dynamic theory of heterogeneous equilibrium, on the one hand, and the experimental methods of thermal and microscopic analysis, on the other, gave to the physical metallurgist his first scientific tool, the equilibrium diagram. The classical equilibrium diagram of a binary alloy system shows the boundaries between ranges of homogeneous and heterogeneous equilibrium in their dependence of concentration and temperature. A homogeneous solid sohtion which on cooling passes such a boundary is assumed to precipitate, forming a mixture of two phases with different concentrations. The equilibriunl diagram and the equilibrium theory, however, give no information about the time scheme of the process or the intermediate states passed during precipitation. For this reason it satisfies neither the practical need of the metallurgist nor the curiosity of the physicist. As a matter of fact, in the heat treatment of alloys for technical use the objective very seldom is the equilibrium state. Thus good mechanical properties of construction material are connected, for the most part, with some intermediate state. As these intermediate states are thermodynamically unstable, there is, from a theoretical point of view, always to be expected a decay of the good properties with time; and it is a matter also of practical interest to know whether this natural life time of a material is of the order of, say, ten or thousands of years. Thus, for many reasons, there is a current demand to complete our knowledge of equilibrium through knowledge of the kinetics of the precipitation phenomena. From the point of view of the physicist, the most interesting question in this case is whether there are any general laws governing the kinetics. According to a generally accepted view, precipitation is ruled by two more or less independent phenomena, the formation of nuclei of a new phase and the growth of these nuclei. It is also commonly accepted that there is a tendency for the velocity of growth to increase with increasing temperature because of the increasing mobility of the atoms. There is also a tendency for the velocity of growth to decrease in the neighborhood of the two-phase boundaries. So far, however, very little is known quantitatively about this fundamental phenomenon in the case of solid metallic systems. In our laboratory attention has been directed especially toward the nucleation phenomena, and a series of measurements have been carried out with the guidance of a work- ing hypothesis (based on experiences from previous work on order-disorder transformations in alloys) about the influence on the nucleation of thermo-dynamic potential barriers. However, before discussing the experiments, the theoretical ideas will be considered. In a binary solid solution the arrangement of atoms on the lattice points approaches with increasing temperature a state of full randomness, as illustrated by the ball model of Fig. 1, that might represent a [111] plane of a face-centered alloy with 30 pct "black" and 70 pct "white" atoms. In reality the atoms are changing places continually with their neighbors so that the picture should rightly have been a moving one. On account of this thermal motion the concentration of black atoms within a certain group of, say, a hundred or a thousand lattice points fluctuates with time around the bulk concentration of 30 pct in a manner governed by statistical laws. With decreasing temperature two independent changes in this state grow more and more important. First, the mobility of the atoms decreases, and second, the forces between the atoms will have an increased influence on the fluctuations. In alloys with a tendency for precipitation, which are the concern of this lecture, the distribution function of concentration fluctuations will broaden, so that the relative probability of great local variations from the bulk concentration increases. Fig. 2 gives an example of such a fluctuation. When the alloy is supercooled below the solubility limit into the range of two-phase equilibrium, the fluctuations will now and then at some point give rise to a state that resembles the equilibrium state and thus will form a stable nucleus that is capable of growing by diffusion processes. In discussions with colleagues and in the literature, I have often encountered the idea that three or four atoms of the dissolved metal could form a nucleus of the new phase. A look at the ball model might be enough to indicate that this cannot be true. If it were true, there should be nothing but nuclei, whereas we know from experiment that nucleation must be a rather rare occurrence. In fact we have, as will be mentioned later, certain reasons to believe that the nuclei are formed by fluctuations containing some hundreds of atoms, which should be the order of the number of black balls in the fluctuating group of the figure, if it were extended into three dimensions. As a working hypothesis we have assumed that the fluctuations producing nuclei, though large and rare, still are ruled by the distribution laws of fluctuations of the supercooled solid solution in its initial state. Thus the probability of nucleation will be connected to the thermodynamic properties of the solid

Jan 1, 1952

By E. T. Turkdogan, P. Grieveson

Experimental results are presented for the rate of solution of nitrogen in a iron in the temperature range 750° to 873°C and in 6 iron in the temperature range 1410° to 1470°C. It is shown that the rate controlling process is diffusion of nitrogen into the iron. The diffusiting of nitrogen in a and 6 iron is derived from the results, and the temperature dependence of the diffusivity is represented by the equation D = 7.8 x e- 18,900/RT sq cm per sec. The solubility of nitrogen in a and 6 iron, in equilibrium with 1 atm pressure of nitrogen, has been measured. Using these results and other available data, it is found that the variation of the logarithm of nitrogen solubility with the reciprocal of absolute temperature is nonlinear. In an Appendix, some results of Darken and Smith are presented for the rate of solution of nitrogen in iron using ammonia + hyidrogen mixtures. These data also support the view that diffudsion of nitrogen in iron is the rate-controlling process when ammonia + hydrogen mixtures are used. A considerable effort has been made to obtain data on the solubility1-5 and diffusivity of nitrogen in a iron6-l2 because an understanding of the effect of nitrogen on the properties of steel must be based on an accurate knowledge of the properties of nitrogen in pure iron. However, no information is available concerning the kinetics of solution of nitrogen in a and 6 iron. Recently the authors13 have investigated the rate-controlling mechanism operating in the kinetics of solution of nitrogen in y iron. This study was directed to determine the rate-controlling processes for similar reactions with a and 6 iron as well as to establish values for the solubility of nitrogen in equilibrium with nitrogen gas in a and a iron. EXPERIMENTAL The procedure used in experiments to determine the rate of solution in cylindrical iron rods was the same as that described in a previous communication.13 Ferrovac E grade iron used in all experiments contained the following impurities in weight percent: C, 0.005; Mn, 0.001; P, 0.002; S, 0.006; Si, 0.006; Ni, 0.025; Cr, 0.002; V, 0.004; W, 0.02; Mo, 0.01; Cu, 0.001; Co, 0.01; 0, 0.007. After cleaning the surface, the iron rods were treated in an atmosphere of purified hydrogen for 17 hr before the reacting gas was introduced for known experimental times. After quenching, the samples were sectioned radially and analyzed for nitrogen. In addition to experiments using rods, iron foils were used in the measurements of solution rates of nitrogen in a iron. The foils of two different thicknesses were prepared by cold rolling Ferrovac E grade iron cylindrical rod to 0.051 and 0.152 cm. Foil samples were used in a rectangular form 5 cm long and 1.25 cm wide. The specimens were thoroughly cleaned of surface oxide with fine emery cloth and degreased with carbon tetrachloride immediately before entry into the furnace. The experimental procedure was the same as that used in the study with rods. At the completion of an experiment, the foil samples of the nitrogenized iron were analyzed for nitrogen after discarding 0.3 cm from the perimeter of the specimen. Iron foils were nitrogenized and denitrogenized in the a and 6 range with a gas mixture of 95 pct N and 5 pct H for times varying from 5 min to 2 hr. Results obtained for the average composition of nitrogen in iron for these experiments are presented in Fig. 1. Prior to the denitrogenization experiments, the samples were saturated with nitrogen at 1000°C and 0.67 atm N, giving a uniform nitrogen concentration of 0.0204 pct. According to the known a-y phase boundary in the Fe-N system,14 this composition lies within the ferrite region at temperatures 750" to 850°C. Use of this initial nitrogen content insured that reaction occurred between the gas and a single solid phase, a iron. Examples of the results for the mean concentrations of nitrogen in cylindrical iron rods, 0.356 cm radius for both the a and 6 ranges are given in Fig. 2. Typical examples of the results obtained for the radial distributions of nitrogen in rods are presented in Fig. 3. It appears that the results for radial distributions can be extrapolated to constant surface compositions which agree with the equi-

Jan 1, 1964

By D. Turnbull, J. H. Hollomon, J. C. Fisher

Application of the concepts of nu-cleation and growth to the analysis of experimental transformation data has led to valuable descriptions of phase transformations, an outstanding example being the transformation austenite —* pearlite which has been examined with particular care by Mehl and co-workers.&apos;-5 In addition to the pearlite transformation, the proeutectoid fer-rite and proeutectoid carbide transformations are known to proceed by nucleation and growth. Martensite, on the contrary, until recently was thought to form by a mechanism involving neither nucleation nor growth; however, extension of standard nucleation theory6 suggests that martensite, bain-ite, and the other products of austenite decomposition all grow from nuclei in the parent phase. The theory that martensite forms by nucleation and growth is strongly supported by recent experimental work of Kurdjumov and Maksimova.7 The concepts of nucleatioli and growth have been fruitful also in providing a sound basis for quantitative theoretical treatments of the kinetics of phase transformations. For example, Volmer and Weber8 and Becker and Döring9 developed the theory of nucleation from fundamental considerations to a point where excellent agreement was obtained with the results of experiments on the condensation of supercooled vapors. As a result of their analysis, the kinetics of vapor-liquid transformations now can be predicted. It seems probable that application of the theories of nucleation and growth to a quantitative study of austenite decomposition similarly will clarify the nature of the individual transfor: mations involved, and will enable the calculation of austenite transformation kinetics. In the present paper, the theories of nucleation and growth are applied to the austenite ? martensite transformation in steels. The analysis begins with a discussion of nucleation in single component systems. Martensite appears to be coherent with the parent austenite, hence the nucleation theory is modified to include the effects of elastic distortion. Nucleation in the two component iron-carbon system then is discussed, for most steels are primarily alloys of these two elements. Finally, M. temperatures and martensite transformation curves are calculated for each of several alloy steels of varying carbon and chromium content, and are compared with those determined experimentally by Lyman and Troiano10 and Harris and Cohen.11 Nucleation Theory NUCLEATION IN SINGLE COMPONENT SYSTEMS6,12-14 The work required for reversible formation of a region of phase within the parent a phase is expressed conveniently as the sum of two terms: W1 = Aa, the product of the area of the interface and the interfacial free energy, and W2 = VAf, the product of the volume of the region and the free energy increase per unit volume associated with the transformation. The total work is therefore W = Aa + VAf. When a is more stable than ß, Af is positive and W increases without limit as the volume increases. The transformation a ?ß does not occur. It is nevertheless true that small regions of phase ß enjoy temporary existence here and there in the a. The equilibrium number of ß regions of given size is proportional to exp(— W/kT) per unit volume of a, assuring that larger (ß regions occur with diminishing probability. When a is less stable than ß, Af is negative and W passes through a maximum as V increases. Assuming for simplicity that regions of ß are spherical, as is true when the interfacial tension is isotropic and there are no elastic strains, W = 4r2a + (4/3)*r3Af The maximum value of W is W* = 16iro3/3Af2 [1] for regions with radius r* = -2o/Af. [2] For single component condensed systems it has been shown14 that the steady rate of nucleation of 0 per unit volume of untransformed a is nearly proportional to exp[- (W* + Q)/kT] where Q is the activation energy for the unit processes of adding or removing one atom from an embryo or nucleus. If To is the temperature at which a and ß are in equilibrium, the rate of nucleation is a maximum at a temperature 0 < T < To where (W* + Q)/kT is a minimum. P regions smaller than critical size are called embryos; they tend to grow smaller and disappear, only exceptionally growing larger. Regions equal to or larger than critical size are called nuclei. A critical size nucleus may grow indefinitely large or may shrink back to a, either process decreasing the free energy of the region.

Jan 1, 1950

By E. A. Gulbransen, K. F. Andrew

THIS paper. will present the results of our studies on the kinetics of the gas phase reactions of co-lumbium and tantalum with O2, N2 and H2. Studies on zirconium and titanium have been previously reported.9,11 Due to their high melting points and their many excellent physical and chemical properties, colurn-bium and tantalum have been finding their places as useful metals in science and industry. Chemically the metals are very inert to gas and liquid phase corrosion at room temperature. However, at moderate temperatures of 250°C and higher the metals react readily with oxygen and hydrogen. It is of interest to study the gas phase reactions of these metals for the following reasons: (1) to compare the rates of the several reactions with those of other metals and to correlate the rate data with theory and structure predictions, (2) to add basic information on the practical difficulties of the reduction, refining and working of columbium and tantalum, (3) to anticipate new uses for the metals and (4) to understand the role that the metals play as components in high temperature alloys. Literature Survey A number of papers exist in the literature on the gas phase reactions of columbium and tantalum with O2, N2 and H2; however, only fragmentary data have been reported on the kinetics of these reactions. Although the free energy of formation of the oxide Ta2O520at 25°C has been determined and some thermodynamic work has been reported on columbium and its oxides, the data are not sufficient to make equilibria calculations at elevated temperatures. Oxidation: 1. Kinetics: The rate of oxidation of columbium and tantalum has been studied by McAdam and Geil23 using the interference color method. Tantalum is reported to oxidize more slowly than columbium, zirconium and iron. The amounts of oxidation of columbium after 20 hr in air for several temperatures are reported by the Fansteel Metallurgical Corporation.36 Columbium starts to oxidize in air at about 200°C. The oxide is said to be adherent and prevents further oxidation until the temperature is raised. Columbium is reported not to become brittle on heating in air for short periods like tantalum because the oxide film prevents further reaction. The columbium oxides dissolve into the metal when heated in a vacuum at temperatures between red heat and 1200°C. Above 1200°C the oxides are reported to evaporate. Columbium, in the oxide free state, is an active getter in vacuum tubes. 2. Preparation and Structure: G. Grube, O. Kuba-schewski and K. Zwiauer15 have studied the decomposition of Cb2O5 in argon. They find that CbO2 is formed slowly at 1150° and rapidly at 1300°C. Cb2O5 can be reduced to CbO2 by moist H2. The reduction of this dioxide to the lower oxides is rapid. By varying conditions CbO2, Cb2O3, CbO and Cb2O can be formed. CbO2, CbO and Cb2O have independent lattices while Cb2O3 is a stoichiometric mixture of CbO and CbO2. In a later paper O. Kuba-schewski" has shown that CbO is cubic and that CbO2 has a rutile type of lattice. The most exhaustive work on the oxides of columbium is that of G. Brauer.8 The number and constitution of the solid phases in the binary system Cb-O were investigated by the preparative, analytical and X ray methods. He indicates that only the oxides Cb2O5, CbO2 and CbO exist with limited regions of homogeneity. The solid oxide Cb,O, exists

Jan 1, 1951

By R. K. McGeary, B. Lustman

Orientation relationships and rates of annealing of 97 pct cold rolled zirconium have been studied by X-ray techniques, metallography, and by hardness measurements. The process of annealing occurring by the formation of domains, and their subsequent growth without recrystallization, is demonstrated. NUMEROUS investigators1-&apos; have revealed sub-grain formation after annealing cold worked metal single crystals and have generally described the results in terms of a dislocation mechanism of polygonization.5,6 in heavily cold rolled polycrystal-line aluminum the first stages of heating cause an apparently spontaneous subdivision of regions of the deformed matrix into a great number of slightly disoriented domains followed or accompanied by rapid growth of certain domains to form a recrystallization texture.7,8 In the present investigation the isothermal rate of annealing of cold worked polycrystalline zirconium has been studied by X-ray techniques, metallography, and by hardness measurement. It will be shown that, rather than by the usual nucleation and growth mechanism,"12 the process of annealing can best be explained by the formation of domains early in the annealing treatment and the subsequent growth of these domains without recrystallization. Experimental Procedure All the experimental work was performed on an arc-melted ingot of high purity zirconium crystal bar made by Westinghouse in a production scale deBoer unit. The weight percentage of impurities in the zirconium were as follows: C, 0.04; Fe, 0.05; Hf, 0.014; W, 0.01; Ti, Ni, and Al, 0.003; Si and N, 0.002; Cr and Cu, 0.001. Metallographically the zirconium showed only a single phase. The 4 in. diarn ingot was forged at 760°C to a 1 1/2x3 in. plate and was then rolled at 760°C to 0.150 in. thickness and annealed at this temperature for 20 min to produce an equiaxed grain structure of about 0.1 mm average grain diameter. The hot rolled plate was roller-leveled, surface ground to 0.135 in., cold rolled 83 pct reduction in thickness on a two-high mill, and then to a total reduction of 97 pct on a Sendzimir mill. The 0.004 in. strip material so produced received no subsequent mechanical treatment. Specimens % in. square were sheared from the rolled strip and isothermally annealed at 104 mm Hg in an all glass vacuum system equipped with a Vycor furnace tube. The temperature data presented are the average temperatures during the runs and did not vary more than about k3"C. X-ray Diffraction Methods: When zirconium is drastically cold rolled, a high degree of preferred orientation results in which prism poles, {1010}, are perpendicular to the rolling direction. After fully annealing this material an entirely new texture develops which corresponds to a 20" or 40" rotation of the deformation texture about hexagonal axes of

Jan 1, 1954

By K. A. Jackson, G. A. Chadwick, A. Klugert

The diffusion field ahead of a lamellar interfnce is analyzed using an electrical analog. A self-consistent solution is obtained for the shape of the interfnce and the diffusion field by an iterative process. The solutions presented here are for a 50-50 eutectoid or eutectic, The shape of the interface is found to he independent of growth velocity and lamellar spacing, and to depend on the relative values of interfacial free energies at the phase houndaries . The mode of growth of lamellar eutectics and eutectoids has been a subject of much interest for many years.1-4 Mehl and Hagel 1 have shown photomicrographs taken by Tardif when he attempted to determine experimentally the shape of an advancing pearlite interface; the results are completely ambiguous. Brandt&apos; and schei13 have made approximate calculations of the composition ahead of a lamellar growth front. The shape of the advancing front and the composition distribution ahead of the front are difficult to calculate because one depends on the other. It is the purpose of the present paper to describe a method by which this calculation has been done. Lamellar-eutectic growth usually occurs under conditions where the growth is fairly rapid, and the interface temperature is close to the eutectic temperature. The growth rate is usually determined by heat flow. Eutectoid growth, on the other hand, can best be studied by quenching to some temperature, and allowing growth to proceed isother-mally. In both cases the growth is believed to be controlled by diffusion* rather than by the atomic kinetics of the transformation. This being the case, a single treatment of the diffusion equation will apply to both cases, provided the region of the interface in a eutectic may be considered to be isothermal. If a part of the interface could appreciably change its thermodynamic driving force by advancing ahead of or lagging behind the mean interface, then the two cases would not be similar. Eutectics normally grow in temperature gradients of the or-der of a few degrees per centimeter. The normal eutectic spacing is the order of a few microns. Part of the interface would have to extend many lamellar spacings ahead of the mean interface before it experienced sensibly different conditions. The interface temperature is usually a few tenths of a degree below the eutectic temperature so that temperature differences of the order of one-thousandths of a degree (a displacement of one lamellar spacing) would be unimportant. Protrusions large compared to the mean spacing do occur when one phase only grows into a eutectic liquid. This is usually a dendritic type of growth, and easily distinguishable from the lamellar mode of growth. A single treatment of lamellar growth will apply equally well to both eutectic and eutectoid decomposition. At the interface, which as shown above is essentially isothermal, the difference between the equilibrium eutectic temperature Teu and the actual interface temperature Ti, can be divided into two parts: 1) the composition varies across the interface, so that the local equilibrium temperature is not Teu; and 2) the interface is curved, so that the local equilibrium temperature is depressed according to the Gibbs-Thompson relationship. This undercooling can be written as Teu-Ti =?T = mAC(x) + a/r(x) [1] where ?C(X) is the departure of the composition at a point x on the interface from the eutectic composition, see Fig. 1, r(x) is the local radius of curvature at a point x on the interface, m is the slope of the liquidus line on the phase diagram, and a is a constant given by where s is the interfacial free energy, TE is the equilibrium temperature, and L is the latent heat of fusion. The calculations in this paper will be made only for the case where the phase diagram is symmetric, that is, the eutectic occurs at 50 pct, the liquidi have the same magnitude slope m at the eutectic temperature, and C,, the amount of B rejected when unit volume of a freezes, see Fig. 2(a), is the same for both phases. As shown in Fig. 2(b), the composition ahead of the a phase will be rich in B, the composition ahead of the ß phase will be rich in A. The composition at the phase boundary is the eutectic composition. The difference between the local liquidus temperature and the actual tempera-

Jan 1, 1964

By T. H. Alden

A correlation has been found in rock-salt structure single crystals between the latent hardening, measured by the direct stress activation of oblique slip systems, and the stress-strain behavior in simple compression. Materials with high latent hardening, like LiF, strain-harden at a low rate (Stage I) even when severely constrained. KCl, in contrast, shows low latent hardening and a tendency to strain-harden at a high rate (Stage 11). This correlation suggests that oblique slip is essential for Stage II hardening of these materials. THE role of secondary slip in the strain hardening of metal single crystals is a topic of lively controversy. On the one hand are theories in which secondary dislocations participate directly in Stage II hardening in the fcc metals, for example through the production of sessile dislocations,1 forest intersections, or jog formation. Much of the experimental evidence on which these theories are based has been reviewed by Clarebrough and Hargreaves.~ On the other hand, a recent theory5 denies that secondary slip has an essential role in Stage II hardening or in the transition from Stage I to Stage 11. In the latter view, Stage I is not terminated by an increase in the activity of secondary systems but by the exhaustion of undeformed material.6 The experiments reported in this paper will not resolve this controversy since the materials being studied are cubic ionic crystals rather than metals. However, the results do show in an unusual way a direct connection between "secondary" (nonortho-gonal or oblique) slip and strain hardening in these materials. Specifically, a correlation has been found between two independently measured properties, first the latent hardening of oblique (110)(1i0) slip systems as measured by direct stress activation of these systems, and second the stress-strain behavior at small strains. From prior work, it was known that in most cubi-cally oriented rock-salt structure crystals, two orthogonal slip systems operate and exclude the other equally stressed pair, oblique to the first pair.7&apos;8 This observation apparently indicates that a significant interference exists between slip on oblique (110) planes and a relatively small interference between orthogonal (110) planes. The present experiments were begun with the intent of obtaining a quantitative measure of this difference by means of a study of latent hardening in these crystals. I) EXPERIMENTAL METHODS The experiments were basically of two types, first the determination of stress-strain curves by compression along a single (100) axis, and second the measurement of latent hardening by compressive prestrain along one cube axis followed by the determination of the yield stress in a second (latent) cube direction. All tests were done at room temperature in an Instron machine by compression between lapped, parallel steel faces. Three specimen shapes were used. For long crystals (nominal dimensions, 1/8 in. square by 1/2 in. long) the ends were lubricated with an oil-graphite mixture. Superior results with short crystals (about 1/8 in. cube) were obtained using 0.003-in. teflon film.&apos; Thin crystals (1/4 in. square by 3/32 in.) were used for latent-hardening measurements and similar results were obtained with either lubricant. Test specimens were cleaved from Harshaw single crystals which had been irradiated to a dose of lo8 roentgen using a cobalt-60 source. The irradiation raises the yield stress and tends to prevent plastic deformation during sample preparation.10 Prior to testing, the irradiation hardening was removed by an anneal at 400°C. Ideal compression specimens have flat, parallel faces. In short specimens particularly, satisfactory results demand a close approximation to this ideal. In the present work, cleaved surfaces were often used directly as compression faces. The degree of success using this method depends on two factors: 1) the smoothness of cleavage faces, and 2) the extent to which the crystal is deformed or crushed by the chisel during the cutting of a long crystal into short pieces. Unfortunately, only one material of those studied, LiF, was completely satisfactory. NaF, NaC1, KC1, and KBr behaved less well so that

Jan 1, 1964

By L. Zwell, H. A. Wriedt

X-ray Lattice parameter and bulk density measurements were made at room temperature on solid solutions of nitrogen in purified a, iron, containing from 0 to 0.053 wt pct N. When nitrogen is dissolved in a, iron, the fractional increase in unit cell volume (X-ray diffraction) and the fractional increase in volume per gram of iron (bulk density measurement) are the same within experimental error. The two sets of results when averaged show that the unit cell edge of a, iron increases linearly by 3.2 X 10-2 A per wt pct N dissolved and that the partial gram-atomic volume of nitrogen at infinite dilution in a, iron is the same as it is in nitrogen-martensite, that is, 5.90 cm3. RECENT reviews17&apos; of literature dealing with the lattice parameter of ferritic iron-nitrogen alloys indicate that the dilating effect of dissolved nitrogen on the bcc unit cell of a iron is not known with confidence. Five investigations3-7 either revealed no effect of nitrogen or were inconclusive. Among other investigations, where quantitative data were obtained, the results of Osawa and Iwaizumi8 indicate too large an effect, and those of Eisenhut and Kaupp9 show the lattice parameter of ferrite varying with the nitrogen content at concentrations far beyond the known solubility limit. It is not clear in Burns&apos;10 data what value should be used for the lattice parameter of nitrogen-free ferrite in calculating the dilation. Burdese11 shares with Burns the shortcoming that the iron-nitrogen alloys were solution-treated and quenched with undissolved nitride present. The consequence is that the un- certainties in the solubility limit1 are added to those in the lattice parameter measurements when the variation of lattice parameter with nitrogen content is computed. For a system of such widespread interest, we felt that a new investigation was merited. Both X-ray diffraction and bulk density measurements were used to determine the dilation of the , a iron lattice by dissolved nitrogen. EXPERIMENTAL PROCEDURE Material. The bulk density and X-ray diffraction experiments were both made with specimens of a purified iron (denoted as "B iron")- from Battelle Memorial Institute. The impurity contents were as follows: As, C, Cu and Pb—50 ppm; Ag, Al, Co, Ga, 0, Ti-11 to 50 ppm; B, Be, Ca, Cd, Cr, Mg, Mn, Mo, N, Ni, S, Sb, Si, Sn, V, W-10 ppm or less. The vacuum-cast ingot was hot-forged and annealed. Pieces of the forged stock were machined and cold-rolled to give strip stock 0.08 and 0.002 in. thick for density and for X-ray measurements, respectively. Preparation of Specimens. Starting with a piece of the cold-rolled iron stock, the general sequence of operations, after an initial recrystallizing anneal, was to measure the density or lattice parameter, nitrogenize, remeasure the property, age or denitrogenize, and again measure the property. Duplicate analyses for nitrogen were made by a modified Kjeldahl method on portions of the actual density specimens and on pieces nitrogenized to equilibrium alongside the X-ray specimens. Annealing of the density specimens was performed by sealing the pieces with the as-rolled surfaces removed by filing into evacuated "Vycor" capsules and treating for 1 hr at 750°C followed by furnace cooling. (TO check the effect, if any, of annealing procedure, a specimen also was

Jan 1, 1962

By M. H. Pilkuhn, H. Rupprecht

The junction luminescence of GaAsxP1-x diodes containing up to 47 pct Gap was studied. Diodes were prepared by diffusing zinc into n-type material which was eithw boat- or vapor-gvown. Observations concerning the energy and the line shape of the spontaneous emission are presented and discussed; in particular the influence of inhomogeneous phosphorus distribution is considered. The role of reabsorption of the junction radiation is pointed out. With increasing current, the peak emission shifts to higher enwgy. This is alm true in cases where slow line narrowing occurs simultaneously. The length dependence of the threshold current density for lasing at 77 °K was examined for lasers made from the same material. It was found that longer lasers have lower threshold curvent densities, Estimates of the characteristic laser losses are given. Data concwning the range of Gap concentration in which stimulated emission was observed are presented. FORWARD-BIASED p-n junctions in mixed alloys of GaAsxPl-, emit light whose wave length depenfs on the composition of the alloy ranging from 8400A (x = 1) to 5350A (x = 0) at 77°K. Laser action in vapor-grown material was first reported by Holonyak and evacqua,&apos; and in boat-grown material by Ainslie, Pilkuhn, and Rupprecht.&apos; In both cases this was observed for low Gap concentration where GaAs,Pl-, is still a "direct" semiconductor with the lowest conductance-band minimum at k = 0 and a subsidiary minimum in the [loo] direction. As the Gap concentration is increased, the subsidiary [loo] minimum in the conduction band is lowered and finally becomes the lowest minimum for Gap concentrations above 50 pt,3 making the alloy an &apos;&apos;indirect" semiconductor. It is of interest to determine up to which Gap concentration stimulated emission can be observed. EXPERIMENTAL Boat-grown material was prepared by N. Ainslie of IBM by horizontal Bridgman technique. The material was n type and silicon-doped up to a concentration of 10&apos;&apos; cm-&apos;. Vapor-grown material was made by E. Hull of IBM or received from Merck & Co. Diodes were fabricated in a similar manner as in the case of GaAs by zinc diffusion. Details about the diffusion can be found in a later paper.4 All diodes were of Fabry-Perot structure with two parallel sides cleaved and the other two sides sawed. Their width ranged from 50 to 150 p and their length from 50 to 700 p. RESULTS AND DISCUSSION Spectral Distributions. A typical display of the junction luminescence of a GaAsxPl-, diode is shown in Fig. 1. The liquid-nitrogen and room-temperature curves which were taken at a very low current (25 ma dc) show a relatively sharp high-energy emission which is band-edge radiation. They also show a broad low-energy emission which is due to transitions to deep impurity levels. This latter emission line may have different shapes and positions depending on the nature of the material. It can sometimes be quite near the band gap giving rise to "bumps" in the high-energy line. The results presented in this paper will be concerned only with the high-energy emission which becomes more intense relative to the low-energy emission when the current is increased and the temperature is lowered.

Jan 1, 1964

By G. F. Sager, B. J. Nelson

Magnesium alloy forgings offer higher and more uniform mechanical properties than heat treated magnesium alloy castings and are used principally for light weight parts that may be stressed in fatigue or subject to impact loads, or where space limitations do not permit the use of the necessarily bulkier magnesium alloy castings. Compositions and Properties of Magnesium Forging Alloys The nominal compositions and properties of the principal commercial magnesium forging alloys are given in Table 1. The two that are most commonly used are AMC58S and AM65S. The former has the highest strength and is, therefore, employed for heavy duty applications. However, the forging of this alloy and of AMC57S ordinarily requires the use of slow speed hydraulic presses. The forging alloy AM65S combines good, although somewhat lower, mechanical properties with excellent forging characteristics. This alloy can be forged on hammers, upsetters, rolls, and mechanical presses, as well as on hydraulic presses. These characteristics make it particularly useful for many applications. Manganese Segregation in AM65S The alloy AM65S contains 5 pct tin, 3 1/2 pct aluminum, and a small amount of manganese, the manganese being added to insure satisfactory resistance to corrosion. Some manganese segregation was occasionally encountered in this alloy. In many applications, such segregation is of no particular consequence, but when forgings are acid dipped prior to the application of various chemical coatings, the segregated particles of manganese constituent may stand in relief. The resultant surface roughening may impair appearance and is undesirable in forgings employed in the textile industry, where very smooth surfaces are essential to avoid the catching and breaking of fine threads. An effort was therefore made to determine the cause of manganese segregation in this alloy and find a method for its elimination. Radiographic examination of a series of cast ingot sections and extruded samples of the AM65S type having manganese contents ranging from zero to about 0.7 pct revealed no appreciable manganese segregation when the manganese was less than about 0.4 pct. A small amount was observed with a manganese content of 0.46 pct and considerable with manganese contents of 0.6 pct or higher. Attempts to eliminate the manganese segregation by variations in the melting and casting conditions were unsuccessful and it soon became apparent that the trouble was attributable to the fact that the manganese contents that caused segregation were in excess of the amounts that would remain in solution at temperatures encountered in the melting and/or casting operations prior to the complete solidification of the ingots. A knowledge of the amounts of manganese that would be soluble in molten alloys of the AM65S type at various temperatures was obviously desirable. The liquid solubilities of manganese in binary Mg-Mn alloys and in Mg-Al-Mn and Mg-Zn-Mn alloys have been determined by Tiner and others,* but no data on the solubility of manganese in molten magnesium alloys containing tin and aluminum are given in the literature. For this reason, an investigation to determine the solubility of manganese in a magnesium alloy containing 5 pct tin and 3.5 pct aluminum (AM65S type) was undertaken.

Jan 1, 1950

By M. Kaufman, D. Rosenthal

IT would be of great importance to our understanding of the phenomena of fracture in metals if a unique relationship could be established between stress and some easily measurable parameter of deformation up to the fracture. It is known that no such relationshir, has been found when the parameter was the mechanically measured strain,&apos; the major part of which is plastic. The present investigation was initiated to determine, among other things, if the X-ray or lattice strain" might be a • For the definition of lattice strain see ref. 2. more suitable parameter. To this end, annealed stress free*&apos; specimens of 61s aluminum alloy were ** Freedom of stress in this particular case means absence of those stresses which can be checked by the technique employed. tested at room temperature and liquid nitrogen temperature (—195OC), by first maintaining the same temperature from the beginning until the end of the test, and then with crossovers from one temperature to the other. Three major factors had to be taken into consideration in designing the specimens and testing equipment. The test setup must allow X-ray pictures to be taken while the specimen is under load (for as much as 2 hr at a given load). Provision must be made for maintaining the test specimen at the temperature of liquid nitrogen as well as at room temperature. In addition, the specimen must be able to rotate to allow the X,ray beam to take in as large a sample of grains as possible, to maintain centering, and to correct for effects of large grains. The final design of the specimen and equipment is shown in Figs. 1 and 2. The specimen and grips are hollow, enabling liquid nitrogen to be poured in through a funnel-container arrangement while the specimen is rotating. The diameter of the specimens at the 2 in. gage section is 5/16 in. with a 3/16 in. diameter hole through the center. A small pilot valve in the lower grip allows a very small stream of liquid nitrogen to escape, thus assuring circulation of the liquid at all times. A low temperature silicone grease-tissue paper packing is used to seal all joints. The specimen is held in the grips by a pin. Spherical socket joints at top and bottom are used to allow for proper alignment. The grips are connected to the thrust bearings by means of plastic couplings to decrease the heat flow. Rotation is accomplished by means of a motor which drives a plastic gear (integral with the lower coupling) through a semiuniversal joint to allow for deforma- tion of the specimen. The torque applied to the specimen is very small. The maximum stress caused by this torque at the highest loads reached was found to be less than 200 psi, The whole unit was mounted in a 10,000 Ib testing machine. An insulation cage was placed around the specimen to cut down air circulation, and consequent frosting of the specimen, and also to reduce radiation and convection heat losses. A narrow window, covered on both sides with a thin plastic materiai allows the X-ray beam to reach the specimen. Thermocouples placed just outside the pilot hole at the lower grip, in the bottom of the funnel container and near the top of the funnel container permitted checks of the

Jan 1, 1955