Search Documents

By P. K. Koh

Chi phase (body-centered cubic, a = 8.89A) was found in as-cast 23 pct Cr-10 pct Mo-Fe alloy as well as in heat-treated 316, 316L, 317, and modified 446 stainless steels. Chi phase resembles sigma phase in its metastability, chemical composition, and brittleness. Microstructure and some of physical properties of chi phase were developed. MOLYBDENUM has been established as a desirable alloying element for the enhancement of corrosion resistance in Cr-Ni steels and creep and rupture strength in high temperature alloys. On the debit side, however, the molybdenum addition has been known to stimulate u formation. When the molybdenum-bearing steels were subjected to prolonged heating at elevated temperatures, losses of corrosion resistance and/or ductility have been observed. Andrews1,2 first found the existence of a new phase among the anodic FeC13 extracts from type 316 stainless steel solution treated and then reheated from 800" to 1100°C. This phase was designated x and was identified by diffraction patterns as of body-centered cubic structure with a value equal to 8.89? and similar to that of a manganese. He found that the x phase in this steel always coexisted with s phase, but failed to distinguish one from the other by metallographic technique. No definite conclusion was drawn regarding the equilibrium temperature ranges of these two phases. The appearance of Andrew's work recalled an un- explained structure observed several years ago at the Allegheny Ludlum Research Laboratories during the investigation of an experimental alloy containing 25 pct Cr, 10 pct Mo, and balance Fe. X-ray diffraction patterns on the as-cast material revealed the presence of a body-centered cubic phase having a lattice parameter of 8.89?. The structure was sufficiently similar to that of y chromium that for a time it was thought that the structure might be caused by the presence of some undissolved electrolytic chromium particles. The alloy as-cast was so brittle that it shattered after the slightest hot reduction by hammer cogging. This paper gives the results of some metallographic and X-ray diffraction studies on x phase as found in several experimental alloys as well as a few molybdenum-bearing commercial stainless steels. The analyses of materials studied were as shown in Table I. Experimental Procedure Metallography: Solid specimens were polished mechanically and etched in boiling 50 pct HC1 solution in order to best delineate x and s phases in the alloys studied. X-Ray Diffraction: The difficulty of satisfactorily developing diffraction lines for s phase in solid specimens has been previously reported by Bindari, Koh, and Zmeskal.V or this reason all specimens used in this investigation were subjected to anodic

Jan 1, 1954

By C. G. Dunn

According to a recently suggested effect of silicon on the re recrystallization textures of high-purity Fe-Si alloys with (111)[112] type rolling textures, the recrystallization texture for a rolled (110)[001] oriented iron crystal probably should be entirely different from that of a (110)[001] oriented 3 pct Si-Fe crystal. Comparative studies of iron and 3 pct Si-Fe crystals, however, show that both have (110)[Ool] recrystallization textures when the rolling textures are the (111)[112] type after reductions in thickness of about 70 pct. Qualitatively the results from the iron crystal are like those of polycrystalline high-purity 3 pct Si-Fe and not like polycrys-talline high-purity iron. The large effect previously noted probably involves unknown impurities or processing variables rather than silicon itself. Some problems on experimental and analytical procedure for a spherical X-ray specimen, which was machined from a laminated composite of sheet specimens, are treated in the Appendix. A possible strong effect of silicon on the textures produced in cold-rolled high-purity Fe-Si (HPFe-Si) alloys during primary recrystallization and normal grain growth was suggested in a recent paper.' All the textures were far from the random-orientation type, but that of iron, or of Fe-Si alloys of low silicon composition, was entirely different from the texture of 3 pct Si-Fe. The same effect was noted for the textures obtained prior to normal grain growth, i.e., for primary recrystallization.2 It is the main purpose of the present paper to provide some clarification of this silicon effect. All the HPFe-Si alloys from zero to 3 pct Si, which were rolled by two or more stages separated by anneals, developed (111)[112] type rolling textures.2 Thus, there was no effect of silicon on the rolling textures. Earlier, Gensamer and Mehl3 also found no effect of silicon on the rolling textures of Fe-Si alloys; they obtained the Kurdjum.ow and Sachs (K-S) rolling texture for iron,4 which is characterized as the three ideal components: (100)[011], (112)[li0], and (111)[112]. There is a difference between the HPFe-Si multiple-stage rolling texture and the K-S single-stage rolling texture, but this is a variable processing effect. Of interest here is the fact that the recrystallization textures from (111) [llZ] type rolling textures were different depending on the amount of silicon in the alloy. There was a relatively strong (110) [001] component in the recrystallization texture of HP 3 pct Si-Fe5,8,2 but no such component in HP 0.6 pct Si-Fe, for example; the recrystallization texture for the latter was two (111) [110] type components and a (111) fiber component 1,2 Several publications have shown that a strong (110) [001] recrystallization texture is derivable from a (111) [112] type rolling texture for 3 pct Si-Fe crystals reduced in thickness by about 70 pct.7-10 Furthermore it appears that the strongest of these (110) [001] recrystallization textures occurred when the orientation of the crystal prior to rolling was (110) [001].7 Barrett and evensoon11 found that the rolling texture of a (110)[001] oriented iron crystal was (111) [llj]. Accordingly, it seemed desirable to determine whether a (110) [001] oriented iron crystal, upon rolling and annealing, would behave like the 3 pct Si-Fe crystal (or the polycrystalline HP 3 pct Si-Fe) and thus produce a (110) [001] recrystallization texture contrary to the suggested silicon effect, or would behave like the polycry stalline HP iron or HP 0.6 pct Si-Fe and thus produce (lll) [110] type components in agreement with a silicon effect. Briefly, the idea here involves the use of more precisely defined textures to obtain if possible better control of important variables that affect the recrystallization process. PROCEDURE A (110) oriented crystal of Ferrovac "E" iron (99.9 pct pure) was prepared in sheet form 0.080 in. thick with the [001] direction parallel to the long dimension of the specimen.'' This crystal was etched to 0.073 in. thickness (to remove some small included grains) and then was cold rolled in a 6-in.-diam mill to a final thickness of 0.022 in. The rolling was unidirectional except for an inadvertent reversal at 0.061 in. thickness. At this thickness, and also at 0.040 in., the rolling was interrupted for transmission Laue photographs. Molybdenum Ka-radiation filtered with zirconium was used in a transmission method1' to obtain the cold-rolled (110) pole figure. The sample was a 0.002-in.-thick section taken from the central region of the 0.022-in.-thick cold-rolled crystal. For the primary recrystallization study, cold-rolled samples were etched from 0.022 to 0.021 in. thick and annealed in hydrogen at 850°C. Primary recrystallization to a fine-grained structure, Fig. 1, was obtained in a 5-min anneal. Eleven sheets after

Jan 1, 1963

By C. G. Dunn, J. L. Walter

COULOMB' and Coulomb and Lacombe2,3 have recently discussed secondary recrystallization in soft iron (99.5 pct Fe). They found that the appearance of this phenomenon was dependent on both the presence of impurities and the thickness of sheet specimens. They concluded that impurities such as carbon, sulfur, and oxygen in the soft iron stabilized the matrix structure and allowed growth of a few grains of specific orientations. They also found that secondary recrystallization ceased when the final thickness was small and attributed this complete inhibition of growth in thin sheet to the restraining action of thermal grooves. When purer iron (99.99 pct Fe) was used, normal grain growth but not secondary recrystallization was obtained. On the other hand it is known that the necessary stabilization of the matrix structure for secondary recrystallization in high-purity silicon iron probably does not depend on impurities but more likely results from the specimen thickness effect of Beck et al.,4 according to evidence and ideas advanced by Walter and Dunn,5,6 and Detert.7 Furthermore, Mullins8 has indicated that if a gas-metal surface energy difference exists across a grain boundary equal to or greater than about 3 pct of the grain boundary energy, then such a grain boundary should not become stuck. Similarly, Walter and Dunn have estimated that any increase in restraining force due to increased thermal grooving with decrease in

Jan 1, 1962

By W. R. Hibbard Jr., R. W. Guard, N. G. Ainslie

Evidence is presented that copper-base solid solutions of different solutes having equal grain sizes, no preferred crystal-lographic orientation, equal electron-atom ratios, and, within experimental scatter, identical initial yield strengths, need not have identical stress-strain curves at strains larger than about 0.04. The stress-strain behavior is rationalized in terms of the proposed Suzuki chemical interaction between solute atoms and extended dislocations using what is thought to be a somewhat different means of representing stress-strain data. ALTHOUGH the effect: of alloying element upon the strength characteristics of sold solutions is a subject which has received considerable attention in the past, the exact relationships between the common deformation parameters and certain common variables are not really known in some cases. As a result some of the experiments reported in the literature in which these variables are inadequately controlled lose some of their persuasion regarding underlying principles. Nonetheless, facts are known which bear pointing up: When the true stress, a, and true plastic strain, E, of tensile deformatic~n are plotted on a double logarithmic coordinate system, one may observe a straight-line relationship at strains greater than 0.02. The form of the curve in the linear region is given by a = Ken! where a represents true stress, E, true strain, and K and tn, constants. If the relationship holds, K and m define the flow characteristics of the material being tested. m and K, however, may vary with other parameters. Hollomon found that in a-brass, m is influenced by grain size. French and HibbardZ found in alloys of copper that inverse relationships existed between m and 1) the solute concentration for a given solute, 2) the 0.01 yield strength, and 3) the constantK. Lacy and Gensamer3 observed (du/d~) (= U/Em) to increase with increasing values of K in systems of alloyed ferrites (although with considerable scatter of data which may be attributed to uncontrolled grain size). Brick, Martin, and Angier* deduced in copper-base alloys a straight-line relationship (with some scatter) between the change in the Dph number due to solid-solution strengthening and the change in the Dph number due to work hardening which suggested that copper-base alloys having equal yield strengths might have identical stress-strain curves in the plastic flow regions. French and HibbardZ concluded that the yield strength of copper-base solid solutions is the proper basis for comparing the effects of solute elements. Also, Allen, Schofield, and ate' showed that, within their experimental variation, copper-base alloys of zinc, gallium, germanium, and arsenic having the same electron-atom ratios have the same true-stress true-plastic strain curves. Dorn, Pietrokowsky, and ~ietz' also found that with aluminum-base alloys the stress-strain curves in the flow regions are approximately the same if "equivalent" concentrations of alloying elements are used. Solute valence and lattice parameter distortion were the parameters used to determine equivalency. The present report describes an investigation in which an attempt was made to obtain copper-base solid-solution alloys of four solute elements having within close tolerances equal grain sizes and yield strengths, and to see if the level of yield strength does indeed define the flow curve regardless of solute type. During analysis of the data certain unexpected features of the stress-strain curves became apparent which gave rise to some speculation and are discussed at length in the paragraphs that follow. EXPERIMENTAL PROCEDURES Alloy Preparation—Using the data of French and HibbardZ as a first approximation, four different binary copper-base alioys were designed so as to have the same yield strength. In addition, other alloys were prepared in which the solute aoncentrations varied slightly from those calculated above so as to span a range of yield strengths, see Table L The yield strengths of all alloys prepared except the copper-tin alloys were subsequently found to Lie fairly close to one another. The copper used in the alloys was produced by the American Smelting and Refining Co. and was of very high purity (99.999 pct). The alloy additions and their initial purities are as follows:

Jan 1, 1960

By J. P. Neumann, L. Raymond

At temperatures near 1000°C, only the (112) (111) slip systems are operatire in tungsten. Therefore, the substructure introduced into the billet upon rleforming a single crystal by rolling at 1000 "C can be controlled by proper selection 01. processing ral'iubles. Using a reduction of 10 pct pel- pass, the (001)[110] and the (110)[001] crystals will deform by duplex slip rip to a 50 pet reduction in thickuess. These rolled single-crystal sheels are characlerized by anisotropic hardening, retention of ductility with warm working, lattice bending which is related to the conlacl (angle, and macroscopic dimensional changecs in the length bid not the width of the billet. When several slip systems become operative, a greater degree of work hardening is itztvoducetl into the crystal. This rolling- condition is characlerized by isotropic hardening, loss of ductilily with warm working, complex lattice distortions, and macro-scopic dimensional changes in both the length rind Width of the billel. IN tungsten, the {1 10}(111) slip systems are operative below room temperature,' while above 700°C only the {112{ (111) slip systems are observed.2,3 In the transition region, i.e., room temperature. both systems appear. It is the purpose of this investigation to show that tungsten single crystals deformed by rolling at a temperature where only one slip system is operative generate dislocation substructure which depends on the crystal orientation. For a specific crystal orientation. the resulting dislocation substructure can be further influenced by modifying the rolling procedure. Crystals oriented for multiple slip display less substructural sensi- tivity to modifications in processing techniques than do single crystals oriented for duplex slip. Under simple slip modes of deformation, very little work hardening is introduced into a rolled single-crystal sheet. Mechanical properties such as room-temperature strength. ductility, and hardness are used to confirm the existence of the different work-hardened conditions generated within the crystal by modified warm-rolling techniques. EXPERIMENTAL PROCEDURE Material. Single-crystal billets of four different crystal orientations. grown by the Arc-Verneuil technique. were ground to a size of 0.25 by 0.375 by 3 in. In terms of their rolling plane and rolling direction, the billets had the following orientations: (1101 [001 ] (110) [110] (001) [110] (001) [100] The actual orientation of all crystals was within 5 deg of the ideal orientations. The typical impurity content of the crystals is given in Table I. Polishing and Etching. Polishing was done elec-trolytically in a 20 g per liter aqueous solution of NaOH at approximately 10 v. It was established by the Laue back-reflection X-ray technique that the surface damage due to grinding and cutting operations with a diamond wheel did not exceed 0.001 in. Therefore after each cutting or grinding operation at least 0.002 in. was removed electrolytically from the surface in order to eliminate surface effects. By lowering the voltage to 3 v, subgrain boundaries and individual dislocations are identified in agreement with Berlec 4 where the etch-pit traces on a cubic plane form a square. The etching time was about 5 sec at room temperature. Rolling. Rolling was carried out on a Loma 2-high mill (Model 600). The peripheral velocity of the 6-in.-diameter rolls was 500 in. per min, with the surface temperature of the rolls about 400° to 450° C The billets were heated before each pass for 30 min in argon to 1000 C. Oxidation of the crystals during rolling in air resulted in a thin layer of greenish-yellow WO 3 This oxide was removed after each pass by immersing the crystals for a few minutes in a boiling NaOH solution. Prior to the initial rolling pass, a surface layer of 0.001 in. was removed by polishing. The crystals were then annealed in vacuum (10-4 torr) at 2400 C for 30 min. All crystals were rolled in the same direction; i.e., the same end was always introduced into the rolls. The rolling program was conducted in

Jan 1, 1965

By Roland de Wit

Conclusions reached in a paper by weertmanl are amplified in a mathematical and graphical way. It is shown that in a stressed crystal a straight dis-location may be in a position of unstable equilibrium with respect to helix development, and how a small perturbation may start the dislocation off on its helical path. Helix development occurs by diffision; bulk diffusion is necessary for development from a screw, but core diffision is sufficient for development from an edge dislocation. For a mixed dislocation helix development can take place by core diffusion if the helix also climbs; a diffusion reversal takes place when the slope of the helix equals the slope of the Burgers vector. The work done on a crystal by the external forces is graphically shown to be consistent with the direction of motion of the dislocation in helix development. Finally a detailed mechanism for tangle formation from helices is presented. In the course of helix development a glide situation may be reached where a segment of each helix loop lies in a slip plane in which it can expand by glide. Thus is it visualized how a helix can deteriorate into a tangle. A paper by weertmanl proposes dislocation-tangle formation by a helical dislocation mechanism. The present paper amplifies Weertman's arguments in a mathematical and graphical way and presents some further ramifications of the proposed model. The importance of dislocation tangles is discussed in Weertman's paper and the references cited therein. The mechanism of their formation is not yet understood. Weertman proposes that in cold-worked crystals conditions exist suitable for the conversion of straight dislocations into helices and subsequently into tangles. Helix formation occurs by a diffusion process and Weertman proposes that at low temperatures only core diffusion is important. The present paper necessarily repeats some of Weertman's work. Since the mathematical development and notation used are slightly different from his, this was thought necessary for clarity. GEOMETRY OF THE HELIX weertman2 has shown that the equilibrium form of any dislocation line is a helix if it is assumed that the energy per unit length (line tension) of the dis- location is constant. For the special case that no external forces act on the dislocation, the helix reduces to a straight line. We shall assume in this paper that the dislocation has a helical form even when it is not in equilibrium. The parametric equation of a helix is, see Fig. l: where a is the radius of the cylinder tangent to the helix, and 270 the pitch of the helix. The pitch is related to v, the number of turns per unit length (along the axis) by the relation: When a = 0 Eq. [I] gives a straight line in the z direction. The growth of a straight dislocation into a helix is now described mathematically by letting a vary from zero to its final value. The tangent to the helix is given by where is the path length along the helix. This gives the direction of t and since its magnitude is unity we must have So that dcp/ds = (a2 +p2)-"'. The curvature of the helix is given by where n = -(cos + sin) is a unit vector normal to the helix. Note that the vectors k and n always point toward the axis of the helix, Fig. 1. FORCE ON THE HELIX The external force which makes the straight dis-

Jan 1, 1963

By S. K. Mitra

A refinement of the Seeger model for intersection process is investigated which is in better agreement with experimental observations than the original. It is shown that, in single crystals, the strain hardening in Stage II is mainly due to the short-mnge interactions when intersection is the rate-controlling process. It is also demonstrated that the creep curves, as predicted by this theory, are in good agreement with the experimental observations. MOTT: Cottrell? and Seeger have developed an approximate theory for plastic deformation of single crystals over the range of variables where the strain rate is controlled by the rate of intersection of dislocations. Although it is now generally agreed that the low temperature deformation of many pure metals is controlled by the intersection mechanism, various dictates of the over-simplified Seeger model are not in good agreement with all the experimental facts. It is the purpose of this paper to reveal that by appropriate extensions of the Seeger model, particularly those suggested by Basinski: a much more reliable theory results. The refined model to be presented here will be shown to account, in a satisfactory way, for the effect of stress, temperature, and strain on the creep rate under constant stress and for the effect of temperature and strain on the flow stress in constant strain-rate tests. EXPERIMENTAL METHOD To Check the theoretical deductions, both creep and tension tests were conducted on single crystals of high-purity Al (99.994 pct Al) so oriented that both the active slip plane and the Burger's vector of the operative dislocations on that plane made angles of about 45 deg to the tension axis. Single crystals of aluminum (5/8 in. by 1/10 in. by 8 in.) were grown in a graphite mold under an inert atmosphere using the Bridgman method. The chemical composition of the aluminum is given in Table I. A common seed was used for all crystals and their orientation is shown in Fig 3. The extensometry consisted of two differential transformers with matched outputs mounted so as to measure the extension in a 2 in. gage length. The amplified difference in output of the two transformers was recorded by a potentiometer. The amplification was calibrated before each run so that one chart division of the recording potentiometer indicated a 105 shear strain on the specimen. Stresses were measured to the nearest 1 x l04 dynes per sq cm. ACTIVATION VOLUME The concept of Basinski that the activation volume is not constant but is a function of the force that aids thermal fluctuation in effecting the cutting of dislocations will be adopted in this section. The force acting due to an applied shear stress on the dislocation being intersected is where L is the mean spacing between the forest dislocations, is the Burger's vector and T is the back stress. A detailed discussion about the origin of back stress will be taken up later in this report. As shown by Basinski, the activation energy, U, that must be supplied by a thermal fluctuation in order to effect intersection, is equal to where x is the distance through which the dislocation must be translated for complete intersection, and Fm is the maximum force encountered in intersection. When the applied stress is decreased abrupt ly F also decreases and the activation energy increases correspondingly as documented in Eqs. [ 1 ] and [2]. The Seeger equation for the strain rate when the deformation is controlled by rate of intersection of where the shear strain rate (per sec) N = the number of points per unit vol at which intersection can take place

Jan 1, 1962

By M. Cohen, S. A. Kulin

AT a recent symposium on thermodynamics in physical metallurgy1 two opposing theories of the austenite-martensite transformation were presented. Both theories agreed that this type of reaction involves a nucleation process which requires activation and that the activated nuclei develop into the well-known martensite plates with tremendous speed. However, there were essential differences in the two points of view concerning the nature of the nucleus and the mechanism by which the nucleus propagates. According to Cohen, Machlin, and Paranjpe,' the nucleus is a strain center with sufficient elastic energy to initiate a cooperative displacement among the atoms of the parent phase when a sufficiently low temperature is reached. This displacement propagates as a wave in shear-like fashion to transform the austenite into martensite without benefit of diffusion. On the other hand, Fisher, Hollomon, and Turnbull3 regard the nucleus as a solute-poor region (in the austenite) of a size which becomes supercritical relative to coherent growth into martensite when an appropriately low temperature is reached. This growth process is taken to be an atom-by- atom transfer from the receding austenite lattice to the advancing martensite lattice through the coherent interface that exists between the two phases. The present paper is not conceded with the divergent views as to the nature of the nucleus but describes some critical experiments which differentiate between the two proposed mechanisms of propagation. Fisher' has summarized the latter issue in the following way: According to the cooperative displacement theory, the speed of formation of mar-tensite plates should not be decreased by lowering the temperature, and martensite should form with extreme rapidity at very low temperatures; whereas with the alternate growth process, the speed of the martensite transformation should be retarded at very low temperatures, decreasing to zero at the absolute zero. The atom-by-atom growth mechanism predicts a marked slowing down of the reaction rate with decreasing temperature because the rate of self-diffusion in the austenite is involved in this picture. For example, Fisher, Hollomon and Turn-bull5 estimate that the activation energy for this growth process in steel is (0.34)2(0.36)* times the activation energy for self-diffusion in y-iron. The two most recent determinations of the latter quantity are 67,900" and 74,2007 cal/mol, which may be averaged as 71,000 cal/mol. This, in turn, gives a value of 3000 cal/mol for the activation energy of the atom-by-atom process, and hence the rate of growth should vary as e 8,000/RT where R is the gas constant

Jan 1, 1951

By Sandip K. Mitra, John E. Dorn

The Basinki-modified Seeger equation for deformation of metals by means of thermally activated intersection of dislocations was used to ascertain the various factors responsible for the strain hardening of poly crystalline aluminum and a series of a solid solutions of magnesium in aluminum. The analyses were based principally on the rate of change of strain rate with stress and the Cottrell-Stokes ratio. From measurements of these quantities on a series of strain-hardened states, the force displacement diagram for intersection, the density of dislocations in the entanglements, and the contributions of the athermal local stress and long-range stress interactions were deduced. Poly crystalline aluminum was observed to have the same force-displacement diagram for intersection as single aluminum crystals, and the corresponding diagram for the magnesium alloys differed in a manner that suggested that small amounts of magnesium may decrease slightly the stacking fault energy of aluminum. Although poly crystalline aluminum had about the same initial density of dislocations as the single crystals, the density of dislocations increased much more rapidly with strain in the polycrystals. This factor and the higher back stresses generated in the poly crystalline aluminum were the major factors responsible for the higher strength of the poly crystalline aluminum, As the magnesium content of the alloys was increased, the initial density of the dislocations also increased. Most of the alloy strengthening arose from this factor; alloying effects due to short-range order strengthening, Suzuki locking, Cottrell pinning, and so forth, were estimated to be quite small. The gveater rate of strain hardening in the alloys was deduced to be due primarily to the greater increase in the density of the dislocations with strain as the magnesium content was increased. It is the purpose of the present investigation to shed additional light on the average plastic behavior of a grain in a polycrystalline aggregate, by analyses, based on dislocation theory, of appropriate experimental test results. These deductions when compared with those from single-crystal data will then serve to illustrate the major items of difference between the plastic behavior of single crystals and the average behavior of a grain in a

Jan 1, 1963

By M. E. Nicholson

IN order to understand how alloying elements influence hardenability through their effect on the rate of pearlite nucleation, it is advantageous to use a model to describe the mechanism of pearlite nucleation. The model which currently is most widely accepted has been described, among others, by Mehl et a1.1-3 and by Hultgren.4 Pearlite nucleation involves both the nucleation of ferrite and cementite.4,5 Cementite nucleates first, followed rapidly by the formation of ferrite at the cementite-austenite interface. The conclusion that cementite is the first phase to form during the process of pearlite nucleation is based, in part, on the observation that proeutectoid cementite is continuous with pearlitic cementite and that the orientation relationship between proeutectoid ferrite and austenite is not the same as that between pearlitic: ferrite and austenite.6,7 Recently, Smith" has suggested that the dissimilarity in orientation relations, instead of indicating the pearlite nucleation sequence, may be evidence that pearlite is nucleated in a grain adjacent to the one in which it is growing. Also, Modin9 as shown that ferrite in pearlite may be continuous with proeutectoid ferrite, and he has also shown that proeutectoid cementite is not always continuous with pearlitic cementite. Thus, it appears that the conclusion that cementite always initiates the pearlite nucleation process is open to serious question. The author believes that important evidence on the question of how pearlite is nucleated exists in the rates of pearlite nucleation of different steels. The following is a review and analysis of this evidence. If the nucleation of pearlite is considered as requiring the nucleation of both cementite and ferrite, then the time to nucleate pearlite consists of the time to nucleate the first phase to form, plus the time to nucleate the second phase at the advancing interface of the first. In the absence of a visible proeutectoid constituent, the second phase must be nucleated very soon after the first. If cementite is the first phase to form, the time to nucleate pearlite will be approximately equal to the time to nucleate cementite. Since the nucleation rate of a phase precipitating from solid solution increases with the degree of supersaturation, it would be expected that the rate of pearlite nucleation should increase with increasing carbon content. Digges10 has shown that the reverse is true. He determined the quenching velocity necessary to suppress pearlite formation in plain carbon steels as a function of carbon content. His results showed that pearlite formation could be suppressed with lower quenching velocities as the carbon content of the steel increased, at least up to 1.25 pct C, the highest carbon content he studied. Thus, it would appear that in plain carbon steels, in which pearlite is formed at the nose of the C-curve, the hypothesis that cementite nucleates first does not predict the observed change in nucleation rate. The validity of the current model of pearlite nucleation may be tested also by determining whether or not it predicts the relative influence of alloying elements on the nucleation of ferrite and pearlite. This can be done best by a consideration of the changes in a TTT diagram produced by a change in alloy content. Hultgren4 suggests that the general shape of a TTT diagram, as well as what constituents will form from austenite, can be predicted from the relative nucleation rates of ferrite and cementite. This is illustrated in the schematic diagram for a hypoeutectoid low alloy or plain carbon steel shown in Fig. 1. The C-curves for ferrite nucleation and for cementite nucleation are represented by AA' and CC', respectively, and the start of ferrite formation and pearlite formation are represented by AX and BC respectively. Adopting the current theory, Hultgren suggests that between X and C pearlite forms directly from austenite, since cementite nucleates more rapidly than ferrite in this temperature range. Conversely, at temperatures above Tx, ferrite is the first to nucleate and proeutectoid ferrite is formed. As proeutectoid ferrite grows, austenite becomes enriched in carbon, so that the cementite nucleation rate is increased. As a result, pearlite nucleation above temperature Tx is accelerated, beginning along BX and not along C'X. Temperature T, represents the temperature at which the nucleation rate of ferrite equals that of cementite. By extending this type of reasoning, using the principle that the nucleation rates of ferrite and cementite increase with increasing supersaturation of austenite with respect to these phases, it should be possible to predict the influence of carbon content on the shape of the isothermal transformation diagram. For a slightly higher carbon content than that of Fig. 1, the curve A A' representing the beginning of ferrite formation should be moved to the right, whereas the curve CC' representing the beginning of cementite formation should be moved to the left. For hypoeutectoid plain carbon and low alloy steels, this prediction does not agree with existing data. Instead, as the carbon content is increased, the pearlite curve moves to the right along with the ferrite curve and always appears to join it tangen-tially. This behavior is demonstrated by the TTT-curves of a series of manganese steels" shown in Fig. 2. In this figure, TTT-curves for four alloys containing 0.20, 0.40, 0.60, and 1.20 pct C are superimposed. The curves are identified in the figure legend. The letters F, P, and C are used to indicate the start of ferrite, pearlite, and cementite formation, respectively. In these steels, it appears that the nucleation of ferrite and of pearlite are related processes. As a result of the foregoing evidence, it is proposed that the formation of pearlite be considered as follows: Either ferrite or cementite may nucleate from austenite, then grow until the remaining phase is nucleated at the interface between the growing phase and austenite. (The growth of the first phase to form is assumed to be accompanied by a composition change in the adjoining austenite.) According to this model there are two modes of nucleating pearlite: 1—where cementite initiates the succession

Jan 1, 1955

By A. E. Dwight, A. F. Berndt

Binary and ternary alloys of uranium with transition metals were prepared with U2X stoichiometry. The compounds U2Tc, U2Rh, U2Os, and U2lr were formed by peritectic or peritectoid transformations, and were shown to be isostructural with U2Ru. The lattice constants are presented. Miscibility relationships obtained from the study of ternary alloys are graphically summarized in terms of an area-of-stability plot. The compound U2Re is not isostructural with either U2Ru or U2Mo. A series of compounds with stoichiometry U2X has been prepared in which X is technetium, rhodium, rhenium, osmium, or iridium. The only other U2X compounds, for which X is related to the above transition metals by proximity in the periodic table, are U2Mo and U2Ru. The structure of U2Mo is the tetragonal C11b type (MoSi2 type)1 and U2Ru is monoclinic, with a new structure type.' This investigation was undertaken to determine if any of the above compounds are isostructural with either U2Ru or U2Mo and to find the range of occurrence of these phases. EXPERIMENTAL Alloys were prepared from stoichiometric amounts of electrolytic uranium (99.99 pet pure) and transition metals of 99.5 pet purity (98+ pet pure Tc), by arc melting on a water-cooled copper hearth under an Ar-He atmosphere. Weight losses were negligible. The buttons were homogenized at temperatures between 700o and 800°C (900°C for U2Tc) in evacuated capsules and air-cooled. The X-ray powder specimens were annealed briefly at the temperature of homogenization. Except in the case of the technetium alloy, metallographic examination was used to determine the number of phases present. The radiation hazard involved in handling technetium precluded the use of metallography to examine U2Tc. The temperature and mode of formation of the U2X phases were determined by heating the metallographic specimens to successively higher temperatures, until examination indicated the presence of chilled liquid or a peritectoid transformation. RESULTS The U2X compounds investigated were found to be formed under the following conditions: UzTc unknown U2Ru peritectic 897o ± 3°C U2Rh peritectoid 755o ± 5°C U2Re peritectoid3 below 750°C Uas peritectic4 920°C U2Ir peritectoid 775o ± 5oC Debye-Scherrer patterns for the above U2X phases were made with CuKa radiation (nickel filter). The similarities in the positions and intensities of the strongest lines in the front-reflection region strongly suggested that U2Tc, U2Ru, U2Rh, U2Os, and U21r are isostructural with only minor differences in the unit-cell dimensions. The known lattice constants and intensities of the Debye-Scherrer rings for U2RU2 were used as a guide in order to index the low-angle X-ray reflections of the U2TC, U2Rh, U2Os, and U2Ir powder patterns. Approximate lattice constants for these compounds were thus obtained and were used along with the intensities observed for U2Ru to index the strongest lines in the back-reflection regions. A sin2 2? correction term was included and the lattice constants were refined and standard deviations estimated by least squares. Comparison of observed and calculated values of Q(= 4 sin2?/?2) used in these calculations are given in Table I. In each case when the positions of lines could not be resolved on the films they were not measured. The final lattice constants, with their standard deviations, are given in Table 11, along with the unit-cell volume and X-ray density. The values of the atomic volume5 of the transition ele-

Jan 1, 1965

By T. Federighi, S. Ceresara, C. Panseri

The results of an exploratory investigation by means of resistivity measurements at -195ºC, on the aging characteristics of a set of Al-Mg alloys with a maximum content of 7 pct Mg, are reported. Whereas for dilute alloys (Mg < 1.5 pct) only a decrease in resistivity is observed at about 100°C (due to the elimination of quenched-in vacancies), for more concentrated alloys such a decrease is preceded by an increase in resistivity in the range between -60ºand +40°C. Following some previous suggestions, this increase is considered as good evidence for clustering of solute atoms @reprecipi-tation process). From the analysis of the results it appears that, although the process is substantially similar to that observed in other Al-rich alloys, it is characterized by a strong interaction between vacancies and zones. THE process of formation of Guinier-Preston zones, i.e., preprecipitation,1&apos;2 which occurs during the aging at about room temperature in many supersaturated aluminum-rich alloys, has been extensively investigated in the past few years by several workers.2,3 owever, a very interesting question arises when the case of Al-Mg alloys is considered: although it is very easy to supersaturate Al-Mg alloys, just in the same way as for many other aluminum alloys showing preprecipitation, only very little experimental evidence was available until a short time ago in the literature supporting the existence of "natural" aging in supersaturated Al-Mg alloys (see, for example, Refs. 4 to 6). On the other hand, as is well known, the X-ray method is not useful in this case because the X-ray scattering factors of magnesium and aluminum atoms are about the same. Recently, however, Cordier and Detert7 have stressed that during the aging at about room temperature of a supersaturated Al-Mg 10 pct alloy it is possible to detect an increase in resistivity; since, as is well known, such an increase is observed also in most alloys showing preprecipitation, the above authors have interpreted their results as evidence for the formation of magnesium-rich clusters (or Guinier-Preston zones) during the aging. In the course of or ientative investigations on preprecipitation in several aluminum-rich alloys, we also could detect a similar phenomenon in more dilute Al-Mg alloys, see Instituto Sperimentale Metalli Leggeri, Annual Report, 1959, and also Ref. 8. Since the details of our observations, although of a preliminary nature, differ from those of Cordier and Detert and allow one to draw a more advanced picture of the preprecipitation process in Al-Mg alloys, we have thought it useful to report our results in this paper and to comment on them briefly.

Jan 1, 1963

By P. K. Foster, C. M. Payne, A. McNabb

Some measurements of the rate of loss of hydrogen from cylinders of iron and steel are analyzed in terrns of a trapping theory. The apeement is encozcraging and gives rise to estimates for the density of traps in the metal. Furthermore, the results appear to be consistent with the assumption that the diffusion constant D for the steady flux of hydrogen through iron lies on the extrapolation of the linear curve (log D us 1/T) obtained at higher temperatures. IT has been shown in a previous paper1 that the literature relating to hydrogen diffusion in steels contains sufficient evidence to invalidate the application of Fick&apos;s laws to hydrogen diffusion in steel at low temperatures. To account for the deviations from simple diffusion behavior a trapping theory was developed, and the fundamental laws modified accordingly. In the present paper, new data on the evolution of hydrogen from long cylinders are presented, and together with some published data are examined in terms of the requirements of the theory.&apos; Properties of solutions of the basic equations derived previously1 and appropriate to the present experimental conditions are outlined in the first section as they determine the form in which the experimental data must be presented for a comparison of theory and experiment. Two new solutions not previously reported have been derived as described in the Appendix. The experiments and treatment of data are then given in Sections 2 and 3 and the results are discussed in Section 4. 1) THEORETICAL CONSIDERATIONS The hydrogen-diffusion theory1 applied in this paper postulated that lattice-dissolved hydrogen at a concentration C diffuses randomly in accordance with Fick&apos;s first law, but that the lattice contains a uniform density N of traps which can capture and delay hydrogen atoms. kC atoms are trapped per second in a region containing unit concentration of vacant traps while p are released per second in a region containing unit concentration of occupied traps. On this basis it was shown (Eq. [30] of Ref. 1) that, when local changes in the lattice-dissolved concentration C are slow enough for equilibrium to be established with the traps, the system is represented in dimensionless form by the equation:

Jan 1, 1965

By Gerhard Bockstiegel

Kuczynski&apos;s formula has been derived for the case of nonspherical particles. TWO formulae of Kuczynski&apos;s type have been derived, one describing the increase in tensile strength, the other describing the progress of shrinkage of a powder compact. It has been strength,shown that the exponents of all three formulae each contain two magnitudes of different physical characters, viz, the geometrical factor a and the kinetic factor ß. The interrelationships between the three exponents are stated. SOME years ago Kuczynski1 experimentally showed that the radius, x, of the area of contact between very small spherical metal particles and a metallic block is related to the time of sintering, t, by the following equation x = constant tk [11 where k has the value 1/5 or 1/7. Assuming that the metal particles were perfect spheres and the metallic block was perfectly flat, he derived the foregoing equation from theoretical considerations of the process of material transport in metals, and he showed that exponent k is different for different mechanisms of transport, e.g., k = 1/2 for viscous flow (according to Frenkel2), k = 1/3 for evaporation and condensation, k = 1/5 for volume diffusion, and k = 1/7 for surface diffusion. From this Kuczynski concluded that the mechanism of transport was either volume diffusion or surface diffusion, depending on whether the value of k, as found in his experiments, was 1/5 or 1/7. Subsequently. Cabrera8 corrected Kuczynski&apos;s calculations with regard to surface diffusion, showing that the theoretical value of exponent k is 1/5 for both volume and surface diffusion. He supposed that the different experimental values of k were due to slight differences in the shape of the metal particles. An exponential relationship similar to the aforementioned was found by Okamura, Masuda, and Kikuta,4 Masuda and Kikuta, and Takasaki8 when studying the rate of shrinkage on powder compacts during sintering. The authors measured the shrinkage by means of the fraction w = Vp — V./Vp — V,,,, where V,, is the volume of the green compact, V, is the volume of the sintered compact, and V,,, is the volume of the compact in its densest state. This fraction, w, they found, is related to the time of sintering, t, by the equation w == constant tm. [21 Further, Bockstiegel, Masing, and Zapf7 observed that the tensile strength, s, of sintering iron powder compacts can also be related to the time of sintering, t, by an equation of the foregoing type, i.e., s = constant tn. [3] For exponent n the values 0.28 (S=2/7) and 0.35 ( 2/5) were obtained, and the authors pointed out that there might exist a simple interrelation between exponent n as found in their experiments and exponent k in Kuczynski&apos;s equation. The authors supposed that 2k = n, since the strength of adhesion between a metal sphere and a block (as in Kuczyn-ski&apos;s experiments) must approximately be proportional to their contact area, p. x2. Theoretical Considerations This paper is an attempt to correlate the fundamental experiments of Kuczynski&apos;s type with the results obtained with powder compacts as represented by Egs. 2 and 3. In particular, the paper is to show how the rate of sintering is influenced by the geometry of the sintering particles and by the type of material transport. As the geometry of particles conglomerating in a powder compact is very complex, some simplifying assumption has to be made, of course, in order to adapt the problem to mathematical treatment. In the following paragraph a suitable simplification is introduced, and Kuczynski&apos;s formula is derived for the case of nonsphcrical particles. Relation Between Area of Contact and Sintering Time—As the face of contact between two particles in a sintering powder compact is not necessarily a circle (as in the case of spheres sintering to a block), Kuczynski&apos;s formula is modified as follows: Let the perimeter of the face of contact be described by means of polar coordinates R, 4, as shown in Fig. la, so the area of contact, f, is determined by f= 1/2 . S112p[R(Æ) ]2 dÆ [4] Then, let the two particles be intersected by a plane perpendicular to area f. The intersection is shown in Fig. lb. According to the nomenclature in this figure, the distance, h, between the surfaces of the two particles is a function of T and Æ: h = h(r,Æ). For the particular case of spherical particles, as in Kuczynski&apos;s theory, this function becomes: h = constant r2. It shall be assumed here that in the close neighborhood of their

Jan 1, 1957

By Toshimi Yamane

The internal friction of cold-worked titanium iso-thermally annealed at temperature below the recrystallization temperature was measured. The internal friction was calculated from the half width of a resonance curve of the specimen which was vibrated transversally by the electromagnetic method. The experimental results were as follows: 1) The specimens annealed for a long time at temperature below the re crystallization temperature after cold working have the strain-amplitude dependent internal friction. 2) The internal friction increased by the cold working was decreased during the isothermal annealing. The reason of decrease of the internal friction is considered to be caused by the annihi-lation of lattice defects. 3) There is a linear relation between logQt-1/Q0-1 and (1/T)2/3 below the recrys-tallization temperature, where Q0-1 is the internal friction standing 24 hr at the room temperature after cold rolling, Qt-1 is the internal friction annealed at T°K for t min. 4) The hardness of the cold-worked titanium does not change by the annealing at 300°C for a long time but decreases by annealing at 400ºand 460°C. METALS, when cold worked, show sharp changes in physical and mechanical properties&apos; The internal friction of cold-worked metals increases sharply and has a maximum value1,2 connected with working de- grees. The increased internal friction of cold-worked metals is recovered by annealing. This phenomenon is the well known effect called Köster effect. The recovery of the internal friction occurs earlier than the changes in tensile properties, hardness, or X-ray diffraction, and is very sensitive to the structure of a metal. The mechanism of the recovery at a temperature lower than the recrystallization temperature is being considered variously by many investigators: there are such views as the annihilation of dislocations by smith,&apos; the rearrangement of dislocations mentioned by Nowick,4 and interaction of dislocation with point defects.5 Smith and Nowick also considered the interaction but it is so difficult for them to explain the rearrangement mechanism systematically, it being not considered a special model; therefore, we do not explain it quantitatively. Experiments measuring the recovery of the internal friction of cold-worked metals were performed by Gordon and Nowick6 on NaCl, and by Smith on copper. In addition, there are many studies, particularly those of measurements on copper by other investigators. There are comparatively many investigations on aluminum and iron which are the cubic system,&apos;-&apos; but only a few on metals of the hexagonal system.10 In view of this, I investigated cph titanium at room temperature and measured the internal friction after annealing isothermally at temperature lower than the recrystallization temperature. SAMPLES AND EXPERIMENTAL METHOD samples for the experiment were cut from a 6-mm titanium plate. The long direction of samples was

Jan 1, 1963

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,&apos; who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.&apos;" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.&apos; (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By N. S. Stoloff, R. G. Davies

A study has been made of the efject oj different dislocation-precipitate interactions upon the temperature dependence of the flow stress of aged Ni-14 at. pct A1 alloy. It is observed that when the dislocations bow between widely spaced (-20004 coherent Ni3Al particles the flow stress decreases with increasing temperature in the normal way. However, when the dislocations cut closely spaced (-5004 particles the flow stress is independent of temperature from -100 to 600°C, due to a balance between softening of the matrix and an increase in strength of the particles with increasing temperature. The retention of strength at high tempera-tures of commercial nickel-base alloys, which are strengthened by the precipitation of a phase based upon Ni3Al, is thought to be due to the unusual strength properties of Ni3Al. The flow stress of Ni3Al increases continuous1y from -196"C to a maximum at -600"C. It is concluded from a series of thermal-mechanical tests that the sevenfold increase in flow stress over this temperature interval is due to a lattice effect and is not diffusion-controlled. The flow stress of precipitation- or dispersion-hardened materials depends on the resistance to dislocation motion within the matrix and the extra energy required for dislocations to bow between or to cut particles. If the dislocations bow between the particles or if the strength of the cut particles is constant with temperature, then the flow stress of the precipitation-hardened alloy must decrease with increasing temperature due at least to the decrease in elastic modulus of the material. There will be softening also from thermally activated cross-slip or climb, offering an additional degree of freedom for dislocations to avoid particles. For example, in the case of nickel containing a dispersion of thoria,&apos; which most probably deforms by dislocations bowing between particles, the flow stress decreases by about 50 pct between 25" and 650°C. In A1-Cu alloys2 aged to produce the 8" precipitate, dislocations cut the particles, and the flow stress decreases by about 20 pct between -269" and 25°C. However, many commercial high-temperature nickel-base alloys, for example Inconel-X and Udimet-700, exhibit little or no decrease in flow stress with increasing temperature up to about 700°C. A characteristic feature of these alloys is that they are strengthened by the precipitation of a phase based upon Ni3A1. Guard and westbrook4 and flinn&apos; have shown that Ni3Al (and alloys in which a third element such as molybdenum or iron is substituted for part of the aluminum) is unusual in that the hardness and flow stress increase with temperature to a maximum at about 600°C. For the flow stress of a precipitation-hardened alloy to be independent of temperature we propose that the particles must be cut by dislocations moving through the matrix and that the strength of the particle must increase with increasing temperature. Theories of precipitation hardening do not take into account the flow stress of the dispersed particles that are cut during deformation; the only dissipative process usually considered7 is the creation of interface within the particle and between the precipitate and matrix. The purpose of the present investigation has been to study in detail the temperature dependence of the flow stress of a nickel-base alloy strengthened by the precipitation of Ni3Al in two structural conditions such that when deformation occurs it does so by dislocations a) bowing between the particles and b) cutting the particles, respectively. A simple binary Ni-14 at. pct A1 alloy was chosen because considerable information is already available for this system concerning phase equilibria and precipitation reactions and rates.&apos; Dislocation-precipitate interactions in the binary alloy should be similar to those in the more complex commercial alloys. In addition, the mechanical and physical properties of NisAl were studied in detail in the hope of elucidating the mechanism by which the strength increases with increasing temperature up to 600°C. EXPERIMENTAL PROCEDURE For the study of the effect of precipitation of Ni3A1 upon the temperature dependence of the flow stress, an alloy containing 14 at. pct A1 was utilized; a Ni-8 at. pct A1 solid-solution alloy was employed as a comparison material. Vacuum-cast ingots were hot-rolled at 1000°C and cylindrical compression samples, 0.20 in. diam by 0.40 in. high, were prepared from the 1/4-in.-diam rod. Specimens were recrystallized and solution-treated at 1000°C for 1/2 hr and then water-quenched. A preliminary study revealed that, when the Ni-14 at. pct A1 alloy was aged for 1 hr at 700°C, significant precipitation hardening was obtained, and that the structure was free from grain boundary discontinuous precipitation; an overaged condition was produced by annealing the aged specimens at 850°C for 1 hr. To circumvent the difficulties involved in the hot rolling and swaging of Ni3A1, compression samples,

Jan 1, 1965

By R. S. Craig, W. E. Wallace, G. S. Kamath

The destruction of long-range order in Mg-Cd, has previously been thought to occur as a second order process. In the present work a variety of X-ray diffraction techniques are employed to show that in this case and in Mg-Cd alloys containing frorn 20 to 33 1/3 at. pct Mg the process more nearly resembles an ordinary first order phase transformation. It is found that the ordered alloy, which occurs as a single phase at lgw temperatures, transforms with increasing temperature into a Cd-enriched disordered (P) phase and an Mg-enriched ordered (a) phase. The interval over which these two phases coexist under apparently equilibrium conditiovs extends from 25" to 87°C content. At 33 1/3 at. pct Mg the two-phase region has disappeared. Measurement of the long range order parameter, s, for the ordered phase in MgCd, (from superlattice line intensities) shows that it disorders only very slightly before it is transformed into the p form. Kinetic experiments reveal that when the a phase is formed frorn the p phase by suitably quenching so as to suppress phase segregation, the transformation is essentially complete and the a phase has acquired its equilibrium value of S in less than 1 min. In an earlier investigation carried out in this Laboratory1 the rate of disordering of the MgCd3 superlattice was determined over an extensive range of temperature. The process was found to be first order and the rate constant, k, was established. At the lowest temperatures studied k was found to increase exponentially with temperature. At higher temperatures, however, it passed through a maximum and for the 100 deg interval below the point at which the superlattice was destroyed k was observed to decrease with increasing temperature. The various theoretical treatments1-3 of order-disorder phenomena lead to a negative temperature coefficient for k near the superlattice critical temperature but this region for MgCdB seemed unusually wide. Detailed analysis of the point indicated&apos; that either the long-range order parameter, S, for MgCda varied with temperature in an anomalous way or the disordering in this instance is more complex than in the cases which have been treated theoretically. The original objective in the present work was simply to determine S vs temperature for MgCda to ascertain whether the disordering was in conformity with theoretical expectations.2° In an early stage of the work it was noted, however, that under equilibrium conditions ordered (a) and disordered (0) phases coexist in MgCd, over a considerable range of temperature. Since on thermo- dynamic grounds the coexisting phases must differ in composition, the investigation was enlarged to permit the compositions of the two phases in MgCd3 to be determined and to establish the extent of the two phase regions for alloys containing from 20 to 33 1/3 at. pct Cd.

Jan 1, 1963

By H. J. McQueen, G. C. Kuczynski

ThE useful properties of k6-Alfenol and the thermenol alloys (summarized by J. E. Nachman and W. J. Buehler&apos;) have encouraged research into those alloys which, having compositions near 25 at. pct Al, 75 at. pct Fe, undergo an ordering transformation between 500° and 550°C. The equilibrium diagram of the iron-rich iron-aluminum alloys was first determined by Bradley and Jay.2,3 They distinguished three structures: the disordered, which is bcc; FeAl, which is simple cubic with one Fe atom and one Al atom per lattice site; and Fe3Al, which is fcc with three Fe atoms and one Al atom per lattice site. This last structure may be conceived as eight body-centered cubes with Al atoms at the centers of alternate ones, so that Al atoms have only Fe as first and second nearest neighbors. Later, Osawa and Murata4 determined the boundaries of the different superlattice regions in the iron-rich Fe-Al solid solution by dilatometric and X-ray methods. Two of the six phases, which they found between 0 and 50 at. pct Al, were never identified by other workers. A. Taylor and R. M. ones,&apos; concurrently with and independently of this research, redetermined this diagram by measuring lattice parameters at temperature. Further reference will be made to their results. EQUILIBRIUM DIAGRAM A) Experimental Procedure—The alloys were prepared from NRC gas-free iron (99.9 pct Fe) and 99.99 pct Al. They were melted in alumina&apos; crucubles under vacuum in an induction furnace. If the ingots were unsound or showed more than a 3 pct weight loss, they were rejected. The ingots were homogenized at 1100°C for 24 hr before hot-rolling at 700" to 900°C from 1 in. to 0.25 in. thick. It is interesting to note that alloys containing more than 28 at. pct Al were able to take an 80 pct reduction of area in the ordered FeAl region. The dilatometer specimens and specimens for chemical analysis were cut from these plates. A Leitz dilatometer was used to measure the coefficient of linear expansion as a function of temperature. The specimens were slowly cooled from 900" to 300°C where they were annealed for 10 hr before slowly cooling to room temperature. The expansion was recorded photographically as the alloys were heated and cooled at 1.5oC per min between 100" and 1000°C. The magnetic measurements determining the Curie points were performed on the dilatometer specimens in the dilatometer, by using direct current in the furnace windings both to heat the specimen at 1.5°C per min and to serve as the primary coil. The regular specimen holder was replaced by a thin alundum tube on which was wound, as a secondary, a closely spaced coil of fine copper wire. A reversal of current in the furnace windings produced, in the secondary, an emf which was proportional to the induction in the specimen, and which could be detected on a galvanometer. In this way, it was possible to determine the Curie points of alloys to within * 5°C. B) Results and Discussion—The coefficients of linear expansion, as obtained from the dilatometer curves, are plotted as a function of temperature and composition in Fig. 1. Since in many cases the heating and cooling curves were superimposed, it was decided to measure slopes of heating curves only. Definite high peaks, due to the transformations, were observed on each curve between 400" and 520°C, and, for alloys containing more than 23 at. pct Al, a second set of smaller peaks at temperatures above 660°C. The sharpness of the peaks indicates that ordering to Fe3Al is a first-order reaction. The compositions and the temperatures of these peaks are listed in Table I. When these temperatures are plotted as a function of the composition, the result is the constitution diagram presented in

Jan 1, 1960

By J. B. Newkirk, D. L. Martin, A. H. Geisler, R. Smoluchowski

A FUNDAMENTAL investigation of the mecha-nism of the ordering reaction and of the accompanying changes in properties has been undertaken, since an extensive study of this process could well contribute to the knowledge of phase transitions in alloys. Cobalt-platinum alloys were chosen for the study since they exhibit interesting and unusual permanent magnet properties.1,2. In addition, the ordering reaction in cobalt-platinum alloys is a convenient one to study experimentally because of the high maximum ordering temperature, the large difference in the X-ray scattering power of cobalt and platinum atoms, and the relative ease with which the alloys can be plastically worked into wire and strip. In the early stages of this study, it became apparent that the published phase diagrams&apos;, &apos; of the cobalt-platinum system contained questionable features, in the region of 40 to 60 atomic pct Co, which were considered in another publication by the authors.4 That portion of the research reported elsewhere on the equilibrium states of cobalt-platinum alloys does not confirm the presence of a previously reported, high temperature disordered tetragonal phase and a low temperature body-centered cubic phase. On the other hand, the structure of the ordered phase is face-centered tetragonal with an atomic distribution analogous to that of CuAu.4 This lattice forms from the disordered face-centered cubic phase in such an orientation that the <100> directions are parallel to the <100> direc-tions of the disordered phase. At compositions other than the ideal 50 atomic pct the ordered phase can exist in equilibrium at high temperatures with the disordered phase. A Widmanstatten pattern of plate-like particles of the ordered phase parallel to (110) planes of the disordered matrix is observed when an initially disordered alloy is held at these temperatures. The temperature range of the two-phase region has been determined for three alloys by X-ray diffraction analyses, microscopic examination, and electrical resistivity measurements, and these results are incorporated with some of those of Gebhardt and Köster in the revised phase diagram of fig. 1. The purpose of the investigation reported here was to examine the mechanism of ordering in co-balt-platinum alloys by X-ray diffraction and metal-

Jan 1, 1951