By J. W. Spretnak, G. W. Powell, J. H. Bucher

Tlze room-temperature tensile fracture oj smooth, round specitnens of three ultrnhigh- strength steels tempered to a wide range of strength levels was studied by means by light and electron-microscopic examination of the fracture surfaces. The fracture of AISI 4340 and 300 M at all the strength levels studied, and H-11, except after tempering at 1200° and 1300°F, occurs in three stages. The initiation of fracture is internal (except in some lightly tcmpeved specimers in which fracture is initiated at surface flaws), and is nucleated largely by separation at metal-second phase intevjaces. TIze voids grow and, coalesce to form a crack. When the crack has reached a sufficienl size, rapid propngutio~z ensues. Failure in this stage of fracture usually occurs by dimpled rupture of inicroshear stefis. In the case of H-11 tempered in the 1125° to 1300°F range, fracture in the shear steps is predominantly by concentrated deformation without void formation. The termination of fracture is usually occomplished by the formation of a shear lib in which fracture occurs by shear dimpled rupture. In the case of H-11 tempered at 1200° and 1300°F, no shear lip was obserued, and the radial elelments extend to the surface—a true termination slage does not exist. ThE tensile fracture of several metals and alloys has been investigated.2-4 In the case of polycrystal-line materials, cup-cone fracture usually results. The mechanism of cup-cone fracture may be summarized as follows.5 Cavities are formed in the necked region of the specimen. They usually are initiated by inclusions or second-phase particles. The cavities extend outwards by means of internal necking, and a crack lying about perpendicular to the length of the specimen is formed in the necked region. Subsequent crack growth occurs by the spread of bands of concentrated plastic deformation inclined at an angle of 30 to 40 deg to the tensile axis. Cavities are formed in the bands of concentrated deformation. The deformation bands zigzag across the bar with the net result that mac-roscopically the crack extends about perpendicular to the specimen axis. The final separation, or cone formation, appears to occur by continued crack propagation along one of the deformation bands out to the surface of the specimen. The micromechanics of the tensile fracture of ultrahigh-strength steels have not been thoroughly investigated. Larson and carr6,7 studied the tensile-fracture surfaces of AISI 4340 with a low-power microscope and reported that three stages of fracture could be observed in general. A centrally located region characterized by circumferential ridges, an annular region characterized by radial surface striations, and a peripheral shear lip were found. It was first pointed out by 1rwin8 that the central region is very probably one of fracture initiation and slow growth, and that the annular, radially striated region is one of rapid crack growth. Presumably the crack grows slowly, assuming roughly a lenticular shape, until it is large enough for the initiation of rapid propagation. In this investigation, it was attempted to determine the fine-scale aspects of the room-temperature tensile fracture of some ultrahigh-strength steels, and to relate the variation in fracture mode with microstructure. The steels studied were AISI 4340, 300M, and H-11 tempered to a wide range of strength levels. I) EXPERIMENTAL PROCEDURE The compositions of the steels studied are given in Table I. The steel was received in the form of hot-rolled bar stock 5/8 to 1 in. in diameter from which oversized specimens were machined and heat-treated. The heat treatments employed are given in Table 11. Subsequent to heat treatment, the specimens were ground to the final dimensions and stress-relieved by heating for 1 hr at 350°F (with the exception of the as-quenched steel). Standard smooth round specimens of 0.252-in. diameter and 1-in. gage length were tested in a Tinius Olsen Universal Testing Machine using a cross-head speed of 0.025 in. per min. The relatively coarse aspects of the fracture topography were determined by light-microscopic examination of sections through the fracture surface of nickel-plated specimens. A direct carbon-replication technique9 was used in the electron-microscopic study of the fracture surfaces. The replicas were examined in the electron microscope, and stereo pairs of electron micrographs were taken. The stereo pairs were then examined using a Wild ST4 Mirror Stereoscope. Carbide and inclusion particles extracted in the replicas were analyzed by selected-area electron diffraction. II) EXPERIMENTAL RESULTS The mechanical testing data are summarized in Table 111. The values reported are the average of

Jan 1, 1965

By S. R. Goodman, Hsun Hu

The rolling texture transition in copper as a function of deformation temperature is found to be quite similar to that in high-purity silver. The ordinary copper type texture changes gradually to the brass type, accompanied by an increase in the stacking fault frequency, as the temperature of deformation decreases. The rolling textures obtained at low temperatures and the corresponding annealing textures compare remarkably well with the ordinary rolling and annealing textures of low-zinc brasses. Furthermore, it is also found that the observed stacking fault energies of copper specimens deformed at low temperatures correspond closely with those of low-zinc brasses, as deduced from measurements of the dislocation nodes. These results are consistent with the idea that texture transition may be significantly dependent on the stacking fault energy. It was shown in a series of previous publications1"3 that the rolling texture of high-purity silver changes gradually from the common silver type (or the brass type) to the copper type* with increasing temperature *The silver or brass type rolling textures are commonly described as (110)[112],4,5 whereas the copper type rolling textures are mainly (123) [a121 and (146)[211].5 Other ideal orientations have been used by various investigators for the copper type rolling textures, but the actual difference among these ideal orientations is rather small. of deformation, and that such texture transition can be correlated with the change in stacking fault frequency as a function of rolling temperature. Furthermore, it was shown that the formation of annealing textures in high-purity silver from the various rolling textures obtained during the course of texture transition depends entirely upon the deformation texture. From a common silver type or brass type rolling texture (such as produced by rolling at 0" or at 50° C) the recrystallization texture is mainly (120)[211], which is quite different from the recrystallization texture of brass.* However, for both ma- terials the orientation relationship between the rolling texture and the recrystallization texture can be expressed in terms of similar rotations around [Ill.] axes of approximately 30 or 35 deg. They differ in that the [Ill] rotational axes are different. In the case of high-purity silver, the axes of rotation are the two (111) poles near the plane normal of the deformed specimen with a (11l)[112] type rolling texture, whereas in brass, they are the (111) poles near the direction of rolling. For high-purity silver with a predominantly copper type rolling texture (such as produced by rolling at 150° or 200°C) the recrystallization texture is mainly (100)[001], or the cube texture, plus its twin orientations. It was shown previously6 that such reorientation observed in copper or aluminum can be described as [Ill] rotations of 30 to 40 deg. For intermediate cases, i.e., when the rolling textures are composed of a

Jan 1, 1963

By B. F. Decker, J. H. Keeler, W. R. Hibbard

Textures of hot-rolled, of cold-rolled, and of cold-rolled and annealed zirconium sheets were determined by use of an X-ray spectrogoniometer. All textures showed a tilt of the basal planes 240" from the rolling plane about the rolling direction. Deformation textures showed the [1010] direction to be approximately in the rolling direction. After recrystalliza-tion, the 111201 direction was approximately in the rolling direction. This texture was sharpened by annealing above the allotropic transformation. Textures of sheet produced by alternately cold rolling and then annealing were less strongly oriented than sheets that underwent severe deformation without intermediate anneals. THIS study of the deformation and annealing textures of high purity zirconium was carried out to supplement an investigation of zirconium and zirconium-base alloys. The spectrogoniometer method of pole figure determination was used and yielded more detailed and precise information than the photographic techniques used by previous investigators. Earlier investigations of the rolling textures of hexagonal metals titanium,1,2 beryllium," and zirconiumL having a c/a ratio slightly less than 1.6 disclosed a rotation of the basal planes from the rolling plane about the rolling direction so that the basal poles were inclined toward the transverse direction, and with one exception,& the [1010] direction was found parallel to the rolling direction. Similarly, hot rolling produced a spread of the basal poles in the transverse direction,2,3,5 With the [1010] direction parallel to the rolling direction. The textures of these metals after recrystallization differ somewhat from each other although still exhibiting the transverse rotation of the basal poles about the rolling direction. Zirconium" was found to have the [1120] direction in the rolling direction, beryllium" continued to have the [1010] direction in the rolling direction, and titanium' was shown to have the [1010] direction in the rolling direction (the cold-rolling texture) when annealed at 1000°F, changing to the [1120] direction in the rolling direction when annealed at 1500°F. It was suggested2 that the titanium retains the deformation texture after re-crystallization, and preferred grain growth at higher temperatures produces the second texture. Annealing above the allotropic transformation temperature did not appreciably change the high temperature recrystallization texture for titanium.' Coarsegrained zirconium showed more spread" in the transformation texture than in the recrystallization texture. The material used in this investigation was crystal-bar zirconium prepared by the iodide process. The major impurity was hafnium which was less than 0.3 pct. The composition obtained by spectro-graphic analysis is given in Table I. The hot-rolled specimen was prepared from a 50-g button of zirconium arc-melted in a water-cooled crucible under an argon atmosphere. This button was enclosed in a welded sheath of soft iron and the ensemble was rolled at 825°C. After each pass the sheath was put back into the furnace to allow it to return to the desired temperature. The zirconium ingot was reduced in this manner to a thickness of about 0.035 in., a reduction of approximately 90 pct. The sheet after removal from the sheath was alternately polished and etched to a thickness of 0.001 in. Cold-rolled specimens were prepared from crystal bar by a series of reductions of approximately 0.010 in. until the sheet reached a thickness of 0.010 in. after which it was cold-rolled to 0.001 in. thickness between sheets of alloy steel. The total cold reduction amounted to about 99.8 pct. Specimens were annealed in an evacuated Vycor or quartz tube. The transmission pole figures were obtained by the quantitative method of Decker, Asp, and Harker6 modified by Geisler7 using an X-ray spectrogoniometer with Cu Ka radiation. Unless otherwise specified all four quadrants were examined with 5" increments along the radius of the pole figure. Absorption corrections were made for changes in length of the X-ray path through the sample as inclination of the

Jan 1, 1954

By G. T. Murray

The aging behavior of a Cu-Ti (3.2 at. pct Ti) alloy has been followed by electrical resistivity, hardness, and metallographic changes. The resistivity data indicate two principal processes, the first causing a sharp decrease in resistivity, and the second, which occurs over a long period of time, a much smaller rate of decrease. Lamellar nodules, Widmanstätten platelets, and homogeneous continuous precipitation was observed. The Widmanstätten platelets grow at the expense of the latter. When this study was initiated, little information was available on the aging behavior of copper-base titanium alloys. Several articles'-3 that appeared in the early 1930's showed that these alloys could be strengthened by precipitation, but a detailed study was not made. Within the past year, however, two other more comprehensive studies4'5 have been reported in the literature, one consisting primarily of an investigation of mechanical properties, the other

Jan 1, 1961

By J. M. Dupouy, R. A. Rawe, M. B. Bever

The aging characteristics of a titanium alloy containing 13 pct V, I1 pct Cr, and 4 pct A1 have been investigated by hardness measurements, X-ray diffraction, and metallography. The P phase decomposes into 0 + a, and 0 + a, + TiCr, above about 1050°F; below this temperature a transition phase, believed to be w, precipitates first, followed by a, and TiCr,. The observed hardening is attributed to these reactions. Cold working of solution-treated specimens accelerates hardening and raises the hardness level attained. A TTT diagram is proposed. NEW titanium-base alloys, designated as "all-beta," have recently been developed. These alloys contain large amounts of P-stabilizing elements such as molybdenum, chromium, or vanadium. When cooled from the solution temperature, they consist only of P; in particular, the martensitic a,' phase does not form.

Jan 1, 1961

By H. C. Rogers

It has been shown previously'- 3 that when a mild steel or iron is charged with hydrogen, the normally observed yield point is eliminated or considerably

Jan 1, 1960

By A. E. Deruyttere, J. Van der Planken, M. Laurent, Van den Bergen

FahRENHORST and schmid1 observed that zinc single crystals work hardened less rapidly when strained in liquid air (- 185°C)than in a bath at -82°C, whereas at higher temperatures the rate of work hardening decreased with increasing temperature, as would be expected. Cadmium and magnesium showed no such decrease at -185°C. At that time the observed anomaly for zinc at liquid air temperature probably seemed insignificant. However it later was confirmed2 by experiments in liquid nitrogen (-196°C) and in the mixture solid carbon dioxide-acetone (-77"C) and therefore appeared to be real. seeger3 then suggested that the anomaly might be due to the different wetting of the zinc crystals by the cooling media. Recently a new confirmation was obtained,4 however the cooling media again were different: the rate of strain hardening was found to be lower in liquid nitrogen and liquid oxygen than in pentane cooled to various temperatures down to -126°C. Ekperiments will now be reported in which the medium surrounding the specimen at the different temperatures was the same, namely gaseous air. The single crystals were made from "Overcor 99.99" zinc. They were grown in a vertical traveling furnace on seeds of nearly the same orientations. The diameter of the crystals was 5 mm and the length between shoulders 140 mm. The brass shoulders were stuck to the crystals by means of araldite. A thin steel wire was fixed to each shoulder and served to fasten the specimen to a Houns-field tensile testing machine. The crystals with the shoulders and part of the wires were surrounded by two concentric cylindrical containers. The coolant. either liquid air or ground solid carbon dioxide, was poured into the outer container only. During cooling the containers rested on a support which was removed when the straining was started. In order to check the temperature which the crystals would attain inside the inner container, a hollow bar of zinc in which a thermocouple was fitted was first mounted in the apparatus as a substitute for a crystal. It appeared that a constant temperature, respectively - 183° and -72°C, was attained inside the bar, if a soaking time of the order of 1 hr was allowed and if the outer container was constantly kept filled. Accordingly, this procedure was adopted for every tensile test. To take account of the large scatter, fourteen tensile tests were performed with liquid air and seven with solid carbon dioxide. The orientation of the crystals and the results are presented in the table, in which the symbols have the following meaning: 1 : temperature x : initial angle between basal plane and specimen axis : initial angle between slip direction and specimen axis a : shear strain at fracture 0: average rate of strain hardening = —-——- 100 t0 and Te representing respectively the critical shear stress and the shear stress at fracture. Despite the scatter of the a- and 8— values which is of the same order of magnitude as in the work reported by Seeger and Trzuble,4 it is evident that the strain hardening rate is significantly lower at -183°C thanat-72°C. The table also contains the average values calculated from Seeger and Trauble's results at the corresponding temperatures: z.e., four results at -183oC and two at-70°, -71°C. These authors calculated 9 in a slightly different way, but this is unimportant. The agreement between the a-values shows that both sets of experiments are comparable despite the differences in experimental techniques. The rates of strain hardening also agree and it may therefore be concluded that the anomaly is not

Jan 1, 1962

By G. Koves

The behavior of case-hardened AISI C-1213 free -machining steel under complex impact-fatigue -wear load conditions was investigated. The inherently poor dynamic properties of the steel are mainly affected by the stress distribution in the case, component shape, and tempering. Cold-riveted components showed unexpectedly high dynamic strength compared to basic parts. A compromise beatment—which provides good dynamic properties, reasonable wear resistance, and fair riveting characteristics—zuas developed. A number of mechanical components in data-processing machines are made of free-machining carbon steel. Although, selected primarily due to manufacturing requirements, components made of these grades frequently undergo complex heat treatment and must sustain impact-fatigue loads. A typical free-machining steel is the AISI C-1213 grade, which is a resulfurized and rephosphorized open-hearth steel. While the undesirable effects of sulfur and phosphorus on the mechanical properties are well-known, data on dynamic properties are scarce.1"3 Rapid rotating or oscillating motion while carry- ing a high cyclic load requires a combination of wear resistance with high endurance limit and impact toughness. The inherently poor dynamic properties of the free-machining steel are further degraded by the machining, which introduces local stress-concentration areas. While the heat treatment (usually case hardening) improves some mechanical properties, it necessarily impairs others. Another problem arises when components, such as studs, must be fastened by riveting. The high crack-sensitivity of the free-machining steel, especially in the presence of a hardened case, makes this operation difficult. In view of the preceding considerations, it is of interest to investigate the behavior of a typical component under complex impact-fatigue-wear loading conditions in order to explore the effects of material, machining, and heat treatment, to obtain specific data on the dynamic characteristics of free-machining steel, and to arrive at a process which would adequately utilize the inherent qualities of this material. EXPERIMENTAL PROCEDURE To simulate actual service conditions, a typical component was selected, based on frequency of application, complexity of load, and processing difficulties. The dimensions and shape of the component—a stud used in many electromechanical document-handling machines—are shown in Fig. 1.

Jan 1, 1964

By W. A. Tiller, D. H. Lane

A simple zone melting technique for investigating the effect of ultrasonic irradiation upon ingot solidification is described. The effect of i) ultrasonic power level, ii) freezing velocity, iii) constant or variable frequency, iv) direction of irradiation, and v) transducer-cozlpling bar joint upon the grain size of type 316 stainless steel have been investigated. The results of this study support the postulate that the ultrasonic vibrations increase the nucleation probability in the layer of liquid adjacent to the freezing interface. In the first paper of this series,l the possible mechanisms whereby ingot structure may be altered by irradiating a solidifying melt with ultrasonic vibrations have been discussed. A new technique for efficiently introducing the ultrasonic energy into the solid-liquid interface region was presented and applied to ingot preparation by the consumable-electrode arc-melting technique. The experimental results support the postulate that the ultrasonic vibrations may refine the ingot structure by increasing the nucleation probability in the zone of liquid adjacent to the solid-liquid interface. The present paper describes the application of the same technique to a relatively simple laboratory-scale zone-melting apparatus. This apparatus is found to be well suited to the detailed study of ultrasonic technology in this area and allows one to determine, in particular, the minimum ultrasonic power level needed to produce a certain grain size in a particular material. The results of this study support the nucleation mechanism for grain refinement, but do not provide any deeper insight into the specific nucleation mechanism responsible for the effect. EXPERIMENT The apparatus used in these experiments is shown in Fig. 1 and illustrated schematically in Fig. 2. The material to be studied, type 316 stainless steel, was in the form of a 3/4-in. sq bar 30 in. long. This bar was placed in a square open-topped mold with open ends made from high-purity graphite coated with a flame-sprayed Al2O3, skin. Surrounding the crucible was a molybdenum susceptor with 3/8-in. diam holes spaced at 1-in. intervals along its length to serve as sight ports. A tapered transducer horn was brazed to one end of the specimen. The entire assemblage was enclosed in a quartz tube, the transducer itself projecting out one end and resting in a cooling tank. A vacuum seal between the coupling bar and the end plate enclosed one end. A similar plate and seal enclosed the other end. The system is gas tight and can be operated under vacuum or an inert atmosphere. For these experiments, flowing argon at 15 in. of Hg pressure was used. The heat source for melting the stainless steel specimen was a 2-in. long 3-kc induction coil placed around the quartz tube; this source heated the susceptor, inductively melting about a 3-in. zone of the sample by radiation. To move the molten zone at a specified rate, the induction coil was moved down the tube at this rate with the aid of a simple pulling device. Thus, the sample could be irradiated at varying ultrasonic frequencies and power levels and could be solidified at varying rates. The power input to the transducer was measured using a "John Fluke Model 120 VAW-Meter." 1 The power delivered to the interface region is probably only about 50 pct of that measured on the VAW-meter. In a typical run, when the ultrasonic power was turned on, the interface of the molten zone closest

Jan 1, 1961

By W. D. Robertson, D. A. Koss, A. J. Goldman

THE significance of the hcp (E) structure, which appears when Fe-Cr-Ni alloys (stainless steels) are transformed martensitically, has been the subject of considerable study and speculation.'-7 It has been proposed that the hcp structure is an intermediate phase in the transformation: fcc (austenite) — hcp (E) -bcc (0, martensite). However, recent studies by transmission electron microscopy6,7 have indicated that the hcp structure may be a consequence of the large shear strain (10 deg) associated with the fcc to bcc transformation. That is, the transformation to a bcc structure is accompanied by extensive dissociation of dislocations in the parent austenite, which has a low stacking-fault energy.'-'' X-ray diffraction analysis of the transformed alloy reveals a pattern of lines corresponding to an hcp structure, together with the parent austenite and the bcc product. The fact that the hcp structure is observed only in association with the bcc product in these alloys1'4'6'7 lends support to the conclusion that the hcp structure is a secondary product of the transformation. But, the evidence is circumstantial and more definite resolution of the two possibilities mains to be obtained. If the hcp structure is an intermediate product of the transformation, as in 1) above, then two distinct Ms temperatures should be observed, Ms and To evaluate this possibility, three different techniques that are particularly sensitive to the structural changes accompanying such transformations have been used in an attempt to detect two transformation temperatures in an Fe-15.1 Cr-11.7 Ni alloy: 1) high-sensitivity differential thermal analysis, 2) the temperature dependence of resonant frequency (elastic moduli), and 3) internal friction of cylindrical specimens vibrating in either longitudinal or torsional modes. To obtain the necessary sensitivity, a differential thermal analysis technique was developed for the purpose, Fig. 1. The differential temperature between a nickel standard and the specimen was amplified to produce a sensitivity of 0.02OC (0.7 v) in temperature difference. The specimen and the standard were surrounded by a copper block and the entire assembly was immersed in a solution of methyl and ethyl alcohol, freezing point, - 140OC, which provided the necessary thermal stability to reduce temperature fluctuations to negligible proportions. A cooling rate of about 1.5OC per min was obtained by bubbling liquid nitrogen through the liquid bath. In order to calibrate the experiment with respect to the evolution of heat in the transformation from fcc to hcp structures, differential cooling curves were obtained for an Fe-19.8 Mn alloy, which transforms martensitically to E.'"-' a Ms(e) temperature of 145°C was clearly defined by a temperature

Jan 1, 1964

By J. Tarwater

The torsional testing of cylindrical medium-carbon steel specimens, heat treated to a high strength level, revealed a stress-strain relationship that was dependent on the direction of torsional plastic pre-strain. This Bauschinger effect was observed in prestrained specimens both with and without subsequent elevated-temperature strain aging. Yield stresses in strain-aged specimens exceeded those of simply prestrained specimens and the difference in stress was greater when the prestrain direction opposed the test direction. This behavior is discussed in terms of the classical dislocation pile-up using Cottrell's equation, A plastically prestrained strain-hardenable member, loaded in a direction opposite to the direction of prestrain, produces a stress-strain relationship differing appreciably from the curve representing reloading in the prestrain direction. This phenomenon, referred to as the Bauschinger effect, will be discussed in terms of the stress differences ob- served at a specified strain. The effect, dating back to the 1880's, was first attributed to grain boundary stresses. When later work revealed that the effect was also present in single crystals, revised theories attributed the diminished applied reverse stress to assistance from internal long-range stresses. These stresses have been associated with dislocation pile-ups or with dislocation arrays having analogous stress patterns. The stress patterns are subject to alteration by interaction with interstitial solute atoms and acceleration of the interaction may be accomplished with elevated-temperature strain aging. As discussed herein, the interaction showed a directional effect with regard to the applied stresses necessary for small plastic strains. Aside from the rigorous Bauschinger stress-strai relationship, which compares prestrained members, it is interesting to compare the stress-strain curve of a member being prestrained with that of a prestrained member being reverse loaded. For small strains which are a fraction of the prestrain deformation, the applied stresses of the reverse reloaded member are smaller. However, as the reverse strain approaches the prestrain value, the stresses approach equivalence. It has been reported1 that the stress required to return a prestrained specimen to its initial "zero" position generally exceeds the prestrain stress because of the work hardening occurring on potential slip systems during prestrain.

Jan 1, 1963

By L. Ianniello

AMONG the more interesting peculiarities of plutonium is the brittleness of its room-temperature monoclinic phase, a, since the adjacent higher-temperature phase (transformation temperature, 112C), ß, is also monoclinic but very ductile. Other elements, e.g., tin and manganese, have phases which exhibit similar contrast in plasticity. However, it was considered unusual when the a phase which has less than 0.1 pet tensile elongation' was rolled to 90 pct reduction in thickness at room temperature.' Since brittle behavior often is a structure-sensitive property, but could also be the result of covalent-type bonding, further experiments reported here have been conducted in an attempt to illuminate the problem. Electrorefined plutonium was rolled under various conditions and examined to determine the strain-hardening characteristics and also to determine under what conditions rolling could be performed. The rolling mill had 6.0-in.-diam heatable rolls with a variable roll speed (6.25 to 445 in. per min). Microhardness measurements were taken using a square-base diamond indenter with loads from 50 to 1000 g. The method used for rolling plutonium at room temperature consisted of prior

Jan 1, 1964

By D. G. Westlake

Polycrystalline tensile specimens of various Zr-0-H alloys have been tested at 298°, 178°, and 77°K. Solute oxygen and hydride precipitates in quenched alloys made individual contributions to the yield strength at 0.2 pct strain which combined to produce a resultant strength increment, a,., Ductility changes which were ohserved can he interpreted in terms of the various oxygen and hydrogen concentrations, testing tem -peratures, and dispositions of the hydride. ADDITIONS of oxygen in solid solution were known to increase the yield and tensile strengths of polycrystalline zirconium as early as 1951.' More recently, the critical resolved shear stress (CRSS) for prism slip in zirconium single crystals was also shown to be affected by the solute oxygen impurity.' This latter work also demonstrated that large increments of strength could be contributed by the finely dispersed zirconium hydride precipitates that are present in quenched Zr-H alloys.3 It was concluded that the combined strengthening due to alloying could be expressed by where to is the increase in the CRSS due to solute oxygen alone and TH is the increase due to finely dispersed hydride precipitates. Eq. [I] is analogous to one used to express the combined strengthening effects of work hardening and neutron radiation damage.4 Eq. [1] was verified only indirectly and for only small amounts of the impurities—up to 0.14 at. pct 0 and 0.63 at. pct H. The present investigation was undertaken to obtain a more direct verification of the validity of the form of Eq. [1] for this system and also to determine the combined effects of oxygen and finely dispersed hydride precipitates on the tensile strength and ductility of polycrystalline zirconium. EXPERIMENTAL PROCEDURE Tensile specimens were machined from the same rolled billet of Kroll zirconium used in the earlier study.' These measured 38 by 4.7 by 0.5 mm and had 10-mm gage lengths which were 2.8 by 0.5 mm. Each specimen was ß-annealed in vacuo at 1173°K for 15.5 hr and a-annealed at 1073°K for 4 hr to D. G. WESTLAKE, Member AIME, is Associate Metal l ur-gist, Metallurgy Division, Argonne National Laboratory, Argonne, III. Manuscript submitted July 17, 1964. IMD______________ give an equiaxed structure with grain diameters averaging 0.06 mm. Oxygen was added by allowing the metal to react with a known quantity of oxygen during the 0 anneal and known quantities of hydrogen were added during the a anneal. Each alloy was encapsulated in Pyrex under vacuum, annealed at 873°K for 4 hr, quenched into ice water, and polished by immersion in a solution of 46.75 vol pct H2O, 46.75 vol pct concentrated HNO3, and 6.5 vol pct HF (49 pct) at 298°K. Special heat treatments given to a few specimens are described in the results below. Tensile tests were done on an Instron machine and were begun within 20 min after the quench, except where specified otherwise. Tests at 298°K were in air, at 178°K in acetone, and at 77°K in liquid nitrogen. All tests were at a strain rate of 8x sec-1. RESULTS AND DISCUSSION Yield Stress at 298°K. The compositions of alloys and the corresponding yield stresses (0.2 pct strain) are given in Table I. A plot of the yield stresses of the oxygen alloys, A, B, C, and D, indicates that varies linearly with CO1/2, where Co is the oxygen concentration, Fig. 1. This is in accord with Fleischer's6 theory for solution strengthening if the oxygen atoms do not cluster, or the cluster size remains constant with increasing oxygen concentration. In Fig. 1, it appears that if one could prepare some oxygen-free zirconium its yield stress would be very low. Therefore, we shall assume that for the oxygen alloys is equivalent to O0, the strength increment contributed by the presence of oxygen. The relationship between0.2and Co is expressed by 0.2 = 31.3 CO1/2, when the yield stress is in kg per sq mm and the concentration is in at. pct. Each of the hydrogen alloys, Al, A2, A3, and A4, contained 0.081 at. pct 0 as an impurity. In Fig. 1, it appears that this small amount of oxygen makes a significant contribution to the strength which cannot be ignored when we evaluate the contribution of the finely dispersed hydride. Let us assume the validity of the following equation: a0.2 = (a2o+a2R)1/2 [2] which is analogous to Eq. [I] for single crystals, and calculate values of UH for the hydrogen alloys by using the experimental values of 0.2 and o (0.081 at. pct) = 8.9 kg per sq mm. For 0.36 at. pct H, oH = 6.47; for 0.72 at. pct H, OH = 11.30; for 2.16 at. pct H, OH = 19.4; and for 3.60 at. pct H,

Jan 1, 1965

By Nicholas J. Grant, Rolf Nordheim, Bill C. Gissen

The system Cb-Re was examined in detail utilizing pure metals, careful melting techniques, and heat treatments. Metallographic and X-my methods were utilized for phase identification. In addition to soli-dus determinations, the composition limits and mode of formation of the intermetallic compounds 0 and X were determined. The binary constitution diagram Cb-Re has been the subject of a number of investigations.'-7 Two intermetallic phases have been described and tentative diagrams have been proposed. It was the aim of this investigation to obtain a complete and more accurate diagram through the use of purer alloys and improved techniques. The diagram worked out by Knapton7 was published after our experiments were concluded. EXPERIMENTAL METHODS The starting materials were Re powder of 99.95 pct purity, supplied by the Chase Brass and Copper Co., and Cb rondelles of 99.6 pct purity, supplied by the Electro Metallurgical Co. Typical analyses are given in Table I. The alloys were prepared from compacted Re powder and Cb rondelles; for critical compositions master alloys were used. The melts varied from 5 to 50 g and were melted nonconsumably in an Heraeus arc furnace, under ti-tanium-gettered laboratory grade argon. It was necessary to invert the buttons and remelt, followed by crushing and further remeltings, the number of which depended on the nature of the fracture of the alloy. The weight of each alloy was carefully checked after each melting operation. It was found that significant weight losses occurred only when loose Re powder was used. These losses amounted to a maximum of 3 wt pct in such instances, but did not occur after the charge was once molten, regardless of the composition. Typical loss of weight after 4 remelts, including crushing, amounted to 0.2 wt pct. Oxygen pickup during successive melting cycles did not appear to be significant, since the weight gain values never exceeded 0.01 wt pct. Control of the composition of the alloys was not too difficult; however, the problem of homogenization was a far greater one. Optimum alloying conditions were finally achieved by a combination of master alloy production and repeated crushing and remelting cycles. The compositions of the alloys utilized to determine the constitution diagram are listed in Table 11. The weight balance method was used ultimately as the sole analytical method, since repeated checks indicated that it was accurate to 0.2 pct, if the weight losses were small. The results were double-checked by a metallographic study of the homogeneity of the samples, since this was presumed to be the more serious factor. Heat treatments at 1200°C or lower were accomplished by sealing the specimens in Vycor tubes, heating in a Globar furnace, followed by air cooling. This was considered to be an adequate quench because of the very low temperatures involved. For temperatures of 1200" to 1900°, alloys were homogenized and heat treated in a tungsten-filament resistance vacuum furnace. From 1900" to 2750" a tantalum-tube resistance furnace was utilized, operating under a vacuum of 105 mm Hg. The temperature measurements up to 1200" were made by means of platinum-platinum 10 pct Rh thermocouples, with an accuracy of 5°C. For temperature measurements greater than 1200°C, optical pyrometers were used. They were calibrated against a standardized instru-

Jan 1, 1962

By W. C. Leslie

The textures of cold-rolled and of annealed iron are compared with those of an iron-0.8 pct copper alloy in which the amount of precipitation after cold rolling was controlled. Previously published pole figures -for cold-rolled and for annealed iron are confirmed. The effects of precipztatiotz after cold rolling are to retain the cold-rolled texture after annealing, to inhibit the formation of the usual allnealing texture, and to produce elongated recrys-tallized ferrite grains. It is suggested that the inhibition of new textures by precipitation after cold rolling is a general phenomenon. A great deal of attention has been paid to the development of texture during the secondary or tertiary recrystallization of ferritic alloys, but very little work seems to have been done on the control of texture during primary recrystallization. If such control were attained, it might be possible to simplify the processing of oriented materials or to change the characteristics of current cold-rolled and an-nealed products. From previous experience, it seemed likely that texture could be controlled by recrystallizing a supersaturated solid solution. Green, Liebmann, and Yoshidal found that the formation of preferred orientation in aluminum (40 deg rotation about <111> relative to the deformed matrix) was inhibited when iron was retained in supersaturated solid solution in the strained aluminum. The authors attributed this inhibition to iron atoms in solid solution. There is, however, an alternative explanation. Green et al, took a highly supersaturated solution of iron in strained aluminum and heated it to an unspecified temperature for recrystallization. It is probable that precipitation occurred prior to and during recrystallization, and it is proposed that the inhibiting agent is this precipitate, rather than the iron atoms in solid solution. It is important to note that precipitation before cold work is ineffective; the effective precipitate is that formed after cold working and either before or during recrystallization. The location and distribution of the precipitate are critical. Precipitation in such a manner has been found to have profound effects upon kinetics of recrystallization and the microstruc-ture of the recrystallized alloys.2-4 It would be surprising, indeed, if this were accomplished with no change in texture. Because of the relative simplicity of the system, and because of previous experience,4-7 it was decided to determine the effect of precipitation on texture in an alloy of iron and copper. Bush and Lindsay5 found an unspecified change in texture in cold-rolled and annealed low-carbon rimmed steel sheets when the copper content exceeded 0.1 pct. MATERIALS In earlier work, the rate of recrystallization of a low-carbon steel was greatly decreased by 0.80 pct copper, and, after the proper treatment, the recrystallized ferrite grains were greatly elongated.4 Accordingly, it was decided to investigate the effect of precipitation on texture at this level of copper content. The iron and the iron-copper alloy were made from high-quality electrolytic iron and OFHC copper, vacuum-melted in MgO crucibles, cast, hot-rolled to 0.2 in., then machined to 0.150 in. The compositions are given in Table I. The plates were heated to 925°C and brine quenched, twice. This produced a ferrite grain size of ASTM 0 in the iron and ASTM 1 in the Fe-Cu alloy. Disk specimens were cut from the heat-treated plates, repeatedly polished and etched, then used to determine (110) and (200) pole figures by reflection. Despite the complication of large grain size, these pole figures strongly indicated a random texture. PROCEDURES The copper content in solid solution in ferrite before cold rolling and recrystallization, and hence, the amount that could precipitate during the recrys-tallization anneal, was controlled at three levels by heat treatment. The specimens as quenched from 925° C were presumed to have all the copper, 0.80 pct, in solid solution. Other samples of the quenched alloy were aged 5 hr at 700°C to retain about 0.5 pct Cu in solid solution.6 A third set of quenched specimens was reheated to 700°C, then slowly cooled in steps, to reduce the amount of copper in solid solution to a very low level. All specimens were cold-rolled 90 pct, from 0.150 to 0.015 in. thick. The rolling was done in one direction only, i.e., the strip was not reversed between passes, with a jig on the table of the mill to keep the short specimens at 90 deg to the rolls. The rolls were 5 in. in diameter and speed was 35 ft. per min. Machine oil was used as a lubricant. In a supersaturated alloy, the maximum effect of the copper precipitate on microstructure and on recrystallization can be developed by a treatment at 500°C, after cold rolling and before recrystallization.&apos;

Jan 1, 1962

By R. M. Goldhoff, H. J. Beattie

The high-temperature properties of a 1 Cr-Mo-V forging steel are described. A series of controlled heat treatments was designed to delineate the effects of austenitizing and tempering treatments, temile strength, and grain size on such properties. Studies indicate that the mechanical properties and their varlations under creep can be described by the initial metallurgical structures and their changes droPirzg exposure, particulavly the carbide reactions. Such structures are described and correlated with the mechanical properties. FOR many years the large steam turbine industry has relied on the 1 Cr-Mo-V type forging steel for critical applications. Because of its adequate heat resistance and relative economy, it is currently in use in the temperature range up to about 1050" to 1075°F. Attempts to understand the large property variations attainable in this steel involve the structural modifications due to the wide latitude in its heat treatment. The heat treatment essentially involves a two-step process which includes solution-ing of carbides in the austenite range followed by a suitable tempering treatment below the critical to adjust the level of properties. The latter step is referred to as "secondary hardening" and is basically an ordinary aging reaction involving carbides. In the commercial heat treatment of large components of such steel, homogenizing and stress-relief anneals may be included and have some importance in determining subsequent properties. Several studies of the engineering properties of this steel as a function of transformation micro-structure have been reported.1 3 However, in this steel the carbide reactions, which are a function of composition and heat treatment, appear to be the property-controlling factor rather than the micro-structure defined as a transformation product. Thus, the tempering resistance of this type of alloy steel is mainly a function of the size and distribution of alloy carbides.4 However, it is also necessary to consider the stability of the microstructure and the effect of dynamic carbide reactions on subsequent properties. It is the purpose of this paper to show the interdependence of properties and corresponding structures, particularly carbide reactions, developed for a limited set of controlled heat-treatment conditions applied to 1 Cr-Mo-V steel. MATERIALS AND PROCEDURE The material for this work came from a large production forging whose chemical composition is shown in Table I. The property data accumulated on this steel as a function of heat treatment were room-temperature tensile and smooth- and notch-bar creep rupture at 1050°F (notch geometry: shank diameter = 0.357 in., depth = 50 pct, radius = 0.005 in.). To achieve controlled structural variations the temperature and time of both austenitizing and tempering were varied in a manner to produce a series of eight steels each at one of two grain sizes and one of two hardness levels in proper combination for valid comparisons. This will be clear upon examination of Table I. Structural studies involved the use of optical and electron microscopy as well as X-ray and selected-area electron diffraction. To reveal the nature of carbide precipitations, electrolytic extraction techniques were used with subsequent analysis of the residue by X-ray diffraction. Weight losses of the steel specimens during electrolysis were measured and successive chemical fractionations of the residues were applied and checked by X-ray examination. The details of fine structural distributions, morphologies, and crystallography of the precipitates as well as dislocation distributions were investigated by examining in the electron microscope three common types of preparation. a) Relief Replicas. Mechanically polished sections were etched in 2 pct nital, replicated with a nitrocellulose film, which was shadowed by chromium vapor deposited at a glancing angle of 20 deg. b) Extraction Replicas. A thin film of carbon was vapor-deposited on the polished and etched surface. The carbon films were then etched off and gathered on electron-microscope supporting grids. The carbides left imbedded in the carbon replica in their original distribution were then examined crystallo-graphically by selected-area electron diffraction. c) Thin Films. Specimens were mechanically ground and polished down to a thickness of 0.001 to 0.003 in. Final thinning was done electrolytically in a "chrome-acetic" electrolyte. When holes began to appear in the foil, the voltage was interrupted and applied in several 1-sec bursts. Sections of the foil between holes were thin enough to pass a 100-kv electron beam that carries an image.

Jan 1, 1965

By P. Greenfield, C. C. Smith, A. M. Taylor

J. E. Harris (Berkeley Nucclear Laboratories, England)—Greenfield et al.11 attribute abrupt changes in slope of their log o/log i curves for heat-treated Mg/0.5 pet Zr alloy (zA) to &apos;atmosphere&apos; locking. It is proposed here that a more reasonable explanation of the apparent strengthening at low rates of strain can be based on precipitation either during the preanneal or during the creep tests. All the tests were carried out above 0.5 Tm where solute atmospheres are likely to be largely evaporated2 and can migrate sufficiently rapidly so as not to impose any &apos;drag&apos; on the moving dislocations. McLean3 has derived an expression for determining the temperature Tc above which, due to the high-migration rate of the atmospheres, Cottrell or Suzuki locking can play no part in determining creep strength. This expression, which holds for an applied shear stress of not greater than 5 X 107 dynes per sq cm is: Tc/Tm= 7/6.8 - log10? where i = secondary creep rate The values for T, corresponding to the maximum and minimum reported creep rates at each temperature have been calculated from the data of Greenfield et al. These are given in Table VII. All the test temperatures were above T,, the margin being greater for the higher temperatures and for the lower strain rates where the breaks in the log s/log ? curves occurred. Dorn and his collaborators14, 17 have studied systematically the effect of solute hardening on the creep properties of an A1/3.2 at. pet Mg alloy. In the temperature range where strain aging occurred in tensile tests, abnormally high-activation energies for secondary creep were obtained but at temperatures above 0.43 Tm, solute alloying did not have any effect on the creep parameters. Moreover, there have been no reports of any strain aging phenomenon during elevated temperature tensile tests with ZA material.18 Instead of the observed strengthening being due to atmosphere locking, it is now proposed that precipitates play an important role in enhancing the creep strength of the material. There are two possibilities—precipitation of zirconium hydride during the high-temperature preanneal and/or precipitation of the hydride or a-zirconium during creep. On the basis of the former the results can be interpreted in terms of a critical stress being necessary to force the dislocations through or over preexisting precipitates. From the latter, if the strengthening is due to pre- cipitation during the test then hardening should be associated with a critical strain rate. At low rates of strain, time is available during the tests for precipitation to occur either directly onto dislocations (thus pinning them) or generally throughout the matrix (which would impede dislocation movements). Examination of the data of Greenfield et al. suggests that both mechanisms may be operative since they observed precipitation during creep and also found that their alloys exhibited high-creep strength in the early stages of the low-stress tests, i.e., before creep-induced precipitation had time to occur. It is not easy to understand why they considered that precipitation of zirconium hydride is unlikely to occur at 600°C while it can take place in tests in air at as low a temperature as 200°C. Precipitation of the hydride during the preanneal cannot be ruled out merely on the basis of metallographic examination. Hydride precipitates in ZA type alloys are very small and can only be accurately resolved in the electron microscope.9 For example, in this laboratory20 hydride platelets with major dimensions <(1/10) µ have been observed by electron transmission through thin film specimens of hy-drogenated ZA material. Complex interactions between dislocations and such particles are illustrated in Fig. 12. Additional evidence for precipitation during pre-annealing is provided by the data presented in Greenfield&apos;s Fig. 1 and Table IT. These show that the creep strength at 200o and 400°C increases with the time of preanneal at 600°C. Such increases cannot be explained on the basis of increases in grain size alone for further improvements in strength were observed when the material was annealed for longer times than that required to stabilize the grains. Although the main discussion is confined to ZA material, similar arguments can be used against the strain aging hypothesis proposed to explain the binary Mg/Mn alloy data. In this case no precipitation is possible during the preanneal, but precipitation-hardening during creep can occur.

Jan 1, 1962

By B. S. Tani, R. V. Schablaske, M. G. Chasanov

MEASUREMENTS of the solubility of scandium in liquid cadmium from 349" to 606°C by Chasanov, Hunt, Johnson, and eder&apos; led to the isolation and characterization of the intermetallic compound ScCQ. The solid phase found in equilibrium with a saturated solution of scandium in liquid cadmium above 422°C is ScCQ. The equilibrium solid phase below this temperature has not as yet been characterized. Hexagonal needles of ScCG were isolated from a 5 wt pct Sc alloy which had been ice-quenched from 500°C. Free cadmium was leached away from the intermetallic with saturated ammonium nitrate solution. The concentration of cadmium in successive leaches was followed polarographically and the leaching process was terminated when the rate of cadmium dissolution decreased markedly. Chemical analysis of the intermetallic thus isolated is as follows: 11.5 wt pct Sc and 88.3 wt pct Cd. The composition of ScCQ is 11.8 wt pct Sc and 88.2 wt pct Cd. X-ray diffraction powder photographs of ScCds taken in a 114.6-mm Debye-Scherrer camera with CuKa, radiation can be indexed on the basis of a hexagonal nit cell. Lattice coonstants are a. = 6.330 ± 0.001A to 6.324 i 0.001A and co = 4.853 i 0.001A. The a0 has a slight range with the lower value seemingly associated with the cadmium-rich terminus of the phase. With eight atoms in the unit cell the calculated intermetallic density is 7.54 g per cu cm; the density as determined by a liquid-displacement method is 7.7 g per cu cm. Powder-diffraction data for ScCQ are recorded in Table I. Stoichiometry, symmetry, unit-cell dimensions, and the number of atoms per unit cell indicate the MgsCd (D019) type structure for ScCQ; space group is D,&-P6,/mmc. Atomic coordinates are:

Jan 1, 1964

By J. B. Darby

In an investigation of various equiatomic alloys of transition elements, Dwightl did not find evidence for the CsC1-type ordered structure in VMn. More recently waterstrat2 has reported the occurrence of this structure in the alloy his sample had been homogenized at 1150°C and subsequently reannealed at 725°C after crushing to powder. The purpose of this note is to confirm the existence of the CsC1-type ordered structure in VMn and to report a lattice parameter. An equiatomic alloy was prepared by arc-melting under an argon atmosphere vanadium and electrolytic manganese having a purity of at least 99.9 pet. The composition was obtained by charging an excess of manganese and monitoring the weight loss until the stoichiometric composition was achieved; the assumption that the loss during melting was due to the vaporization of manganese appears to be a valid one.&apos; The calculated composition of the sample prepared was 49.85 at. pct V and 50.15 at. pct Mn. Specimens taken from the fractured as-cast buttons were wrapped in molybdenum foil and encapsulated in quartz capsules under vacuum; there was no evidence of a reaction between the alloy and foil. The X-ray patterns were obtained using filtered copper or chromium radiation with a Straumanis-type Debye-Scherrer camera having a diameter of 114.6 mm. The CrKa radiation is best suited for detecting the superlattice lines since it overcomes the slight difference in scattering powers of the components by making use of the anomalies in atomic scattering factor which occur when the frequency of the radiation is close to the characteristic absorption frequency of one of the elements.394 A specimen in the as-cast condition, as well as one which had been annealed for 1 week at 900°C and water-quenched, gave a diffraction pattern for the disordered bcc solid solution. However, when samples were homogenized at 900°C for 3 weeks followed by a subsequent anneal at 700°C for 6 to 7 weeks and then water-quenched or furnace-cooled, the (loo), (1111, and (210) Ka superlattice lines were observed in films taken with chromium radiation. An ao = 2.904 * 0.001 was determined by a Nelson-Riley extrapolation from a film taken with CuKa radiation. The author wishes to thank Mr. J. W. Downey and Mr. L. J. Norton for carrying out the experimental portion of this investigation. This work was performed at the Argonne National Laboratory under the auspices of the U.S. Atomic Energy Commission.

Jan 1, 1963

By P. Duwez, C. B. Jordan

A. J. SHALER*—I should like to congratulate the authors for having carried out such a precise set of experiments. It has been found useful, in sintering experimental compacts in vacuo, to make certain that the residual gas is not one which reacts with the metal. Since traces of oxygen can be kept away only with great difficulty, the technique is often adopted of using a "getter " of powder in the vicinity of the compacts, and, in addition, of permitting a small hydrogen leak to flow into the vacuum chamber. Did the authors use similar devices? This paper brings up a question concerning the definition of the word &apos; sintering.&apos; The authors restrict its use to the adhesion between particles. Kuczynski, in a paper presented at this meeting, applies the word to the growth of areas of contact between particles. I have used it to mean both these phenomena and also the dimensional changes which continue to take place after the first two have run their course. May I suggest that we should come to an agreement on the use of these words ? Fig 1 and 2 show an interesting feature: extrapolation of the curves to zero time does not give a densification parameter of zero. The higher the temperature, the higher is the intercept on that axis. These observations agree with the concept of a practically instantaneous densification taking place while the compact is being brought to heat. Such a change may be brought about by plastic deformation and primary creep. The stress pattern causing this first rapid flow is, to my mind, due to the force of attraction between the surfaces of opposite particles in the regions immediately flanking their common areas of contact. The stress is not temperature-sensitive, but at room temperature plastic deformation only proceeds until the metal in the area of contact can support it elastically. As the metal is heated, the elastic limit falls, and further plastic flow occurs. At the higher temperatures, this is followed by primary creep, and finally by the steady-state rate-reaction which the authors are seeking. If they were to recalculate their densification-parameter values, using, not the initial density of the cold compact, but the density after the compacts have been brought to temperature, the systematic deviations from linearity in Fig 3 and 4 might be eliminated. Such initial densities might be obtained by extrapolating the curves of Fig 1 and 2 to zero time. I am naturally pleased to see that such a very well done series of experiments leads to a heat of activation (for the densification process in hydrogen) that is much higher than that for self-diffusion, in confirmation of the less elaborate results reported by Wulff and myself (Ind. and Eng. Chem., (1948) 40, 838). J. T. KEMP*—I would like to comment on Dr. Shaler&apos;s remarks. There are apparently different interpretations of the word "sintering." It seems to me that an accurate definition of our word is essential in all metallurgy. May I point out, in this connection, that in practical metallurgy the word "sintering" has been applied to a bonding process in the preparation of ores and flue dust for fur-nacing. It would be unfortunate if in the area of powdered metallurgy we should establish a definition that is essentially different in meaning. F. N. RHINES*—I think that I can answer the question by saying that I see no essential difference between the use of the term "sintering" in extractive metallurgy and in powder metallurgy; physically the same things are going on. I admit sintering is used for different end purposes in the two cases. When we resort to the sintering of lead ore mixture we are doing so to obtain a chemically reactive, loose texture of some rigidity. This is only a difference in use. After all, in powder metallurgy we sometimes deliberately produce a very porous material which has just a little strength, just as in the case of sinter cake. P. DUWEZ (authors&apos; reply)—We agree that it would be helpful to have well-established definitions of such terms as "sintering." Since the question has now been raised, the time might be appropriate for its consideration by some suitable committee of one or more of the metallurgical societies. In answer to Dr. Shaler&apos;s first question, no getter nor hydrogen leak was used in our vacuum experiments, except insofar as the guard disks (used to reduce friction between specimens and trays) may have acted as getters. Dr. Shaler&apos;s statement that extrapolation of the curves of Fig 1 and 2 does not lead to zero densification at zero time apparently overlooks the logarithmic

Jan 1, 1950