Search Documents

By N. A. D. Parlee, I. D. Shah, W. C. Phelps

THIS note reports on a continuation of a program on the thermodynamics of Fe-S-X systems in the "steel-burning" temperature range begun by Bock, Barloga, and parlee.' Small coils of 0.039-in.-diameter pure iron (Ferrovac-E) wire were equilibrated with Fe-S-0 melts in ingot iron crucibles under argon at 1324°C in the assembly shown in Fig. 1, the lower part of which was heated in a large Globar furnace. Fig. 1 shows (R) the coiled iron wire sample, (M) the Fe-S-0 melt prepared from desired proportions of ferrous sulfide and ferric oxide, (K) the iron crucible, (I) a mullite guide tube, (J) an alumina crucible, (L) alundum sand, (N) crushed mullite, (Q) hollow cylinders of K30 brick, (C) a steel rod, (B), (El, (F), (G), (P), and (O), details of brass water-cooled head, and (H) a mullite tube 2-3/4 in. ID and 26 in. long. The rod (C) bearing the sample could be removed at will and be replaced by a tube for sampling the melt, or by a thermocouple for comparing the melt temperature with a control thermocouple not far from the 2-3/4-in. mullite tube. After equilibration the iron coils were treated with acid to remove the outer layer of metal and then they were analyzed for sulfur by a standard combustion method. The melt samples were analyzed for oxygen by a variation of Lander's2 hydrogen-reduction method for mattes, and for sulfur by the ASTM combustion-iodometric method NO. E 30-47. When the results of some forty-two runs were examined it was found that the sulfur and oxygen contents of the equilibrated melts showed good consistency, in that the plotted compositions fell along the smooth curve shown in Fig. 2. The points on this curve represent the experimental compositions of melts in equilibrium with ?-iron (Fe-S-0) solid solutions. These solid solutions are saturated with sulfur and oxygen with respect to the melt and therefore have the same sulfur and oxygen activities as the melt. The curve drawn through the points therefore delineates the ? liquidus. It falls in such a position as to roughly confirm the liquidus curves of Hilty and crafts3 at 1200" and 1300°C which are

Jan 1, 1965

By B. Hyatt, E. Klokholm

The reesistivity of Cu-Pd alloys of 9.6 to 29 pct Pd alloys was measured after plastic deformzation in tension. For all compositions a continzting decrease in resistivity with increasing plastic strain was observed. By comparison with the results of Damask on a brass ad Cu3Au, it was deduced that these anonzalous decreases in resistivity are due to the decrease in short-vunge order caused by cold work. An anomalous decrease in the resistivity of cold-worked CU-Pd alloys was first reported by Jaumot and Sawatzky.' They observed decreases in the electrical resistivity when disordered Cu-Pd alloys drawing at room temperature. Recently, a similar anomaly was reported by Aarts and Houston-Mac-Mi1lan2 in Ag-Pd alloys containing 10 to 45 pct Pd. The plastic deformation in this case was produced by tensile strain at liquid-nitrogen temperatures. For AE-Pd alloys the relative resistivity change becomes positive for tensile strains of about 20 pct.

Jan 1, 1960

By Irving B. Cadoff, Ernest Levine

The fracture path in a Cu-4 pct Ag alloy wet with mercury was found to he dependent on the heat treatment used prior to tensile testing. Both quenched and slow-cooled alloys were embrittled by the mercury.. For quenched alloys, which were single -phase, the crack path was intergranular. Slowly cooled alloys, which contained precipitate platelets, exhibited transgranular fracture. By comparing stress-strain data for these alloys with similar data on mercury -embyittled solid-solution alloys, it was found that the role of the precipitate and that of the grain boundary in the fracture process were equivalent . THE fracture path which results when metals are strained in a liquid environment appears to be dependent upon the nature of the specific system. Mixed transgranular and intergranular cracking has been observed in the 2024 T4 aluminum alloy when wet with a Hg-Zn amalgam.' Transgranular fracture was induced in an A1-4 pct Cu alloy by masking off the grain boundaries from the liquid Hg-Zn amalgam.' The embrittlement of solid-solution alloys of copper in mercury results in intergranular fracture.' The effect of a precipitated phase on the fracture path in copper alloys is the subject of the present investigation. Cu-4 pct Ag was chosen so that its behavior could be compared with previous work on embrittlement of copper alloys. PROCEDURE High-purity copper (99.999 pct) was used as a base metal, along with 99.999 pct purity silver. Melting was carried out in graphite crucibles with manual agitation to get adequate mixing. The ingots were homogenized by means of vacuum annealing, chemically cleaned, and cold-rolled with intermediate vacuum anneals, to the desired thickness of 0.025 in. The rolled sheets were sheared to the final specimen size of 1 by 0.025 by 0.1 in. The specimens were then electropolished in phosphoric acid (concentrated) and heat-treated in an evacuated capsule at the solution temperature of 770°C. One batch was slow-cooled and the other quenched in water. The thermal etching which occurred during heat treatment was sufficient to permit grain boundary and precipitate delineation. Tensile tests were carried out in air and in mercury on a Table-Model Instron at a pulling speed of 0.2 in. per min. Wetting was accomplished by electro-polishing in phosphoric acid, rinsing in alcohol, and immersing in a pool of mercury. Once wet the coating was stable throughout the mechanical tests. In our studies it was found that wetting the surface or total immersion in mercury produced identical results. For convenience, the wetting technique was used for the experiments described. The crack pattern was observed directly on the surface by removing the mercury after testing. De-wetting was accomplished by flame heating the samples in a vacuum after testing and before observation of the surface. No etchant or polishing was used so as not to obscure the crack pattern on the surface. The mercury removal, however, resulted in a pitted surface but otherwise left the pertinent features visible. Photomicrographs were taken in this condition so as not to disturb the structure associated with the crack pattern. The average precipitate spacing was measured previous to coating the sample with mercury by use of an optical eyepiece micrometer. RESULTS The microstructure of the quenched specimens was single-phase while that of the slow-cooled specimens contained thin platelets of a second

Jan 1, 1964

By N. S. Kenny, A. A. Burr

THE purpose of this note is to present evidence that vacancies, which have been produced by quenching from a high temperature, alter the rate of strain-hardening of an hep single crystal. The majority of investigations of the effects of quenched-in vacancies on the yield stress of metals have been made using fee samples in the form of thin wires. However, there is an inherent disadvantage in using such wires to study the effects of vacancies on the rate of strain-hardening of metals because fee wires begin stage II slip either immediately upon yielding or very shortly thereafter. When stage II slip occurs, very rapid strain hardening also occurs, masking the effects of vacancies on the rate of hardening. In this investigation single crystals of magnesium hep were studied since magnesium has only one slip plane at low temperatures and has, therefore, an extensive easy glide region. In addition, the effect of both static and dynamic recovery on the rate of hardening were eliminated by testing in liquid nitrogen. Both forms of recovery occur in hep metals by dislocation climb, which is a diffusion controlled mechanism and is negligible at liquid nitrogen temperatures. Finally, the dependence of the strain-hardening rate on the crystal orientation was eliminated by using the equations of Schmid and Boas.' Variations in the strain-hardening rate could, therefore, be attributed to the presence of vacancies. Single crystals in the form of rods approximately 5 mm in diam and 6 cm long were grown by a modified Bridgman technique from commercial high-purity magnesium (99.97 pet) supplied by the Dow Chemical

Jan 1, 1962

By R. E. Ogilvie, N. L. Peterson

DURING the past few years there has been considerable effort devoted to the understanding of radiation effects on materials. The concept of the Frenkel defect and other lattice defects suggests that radiation may alter the rate of many metallurgical phenomena, especially those which are diffusion controlled. In 1953 R. R. Coltman and T. H. ~lewitt' found an appreciable effect on the ordering rate of Cu,Au due to fast neutron bombardment. Since then several rather comprehensive theories have been proposed on radiation enhanced diffusion in solids.2"4 If the energy of the radiation is above the threshold energy for the removal of atoms from their lattice sites, Frenkel defects will be produced. These defects can be produced uniformly throughout a relatively thick specimen by high-energy X-rays permitting bulk property studies without the limitation of sample dimensions. In this work high-purity arsenic containing 30 ppm of impurities was allowed to diffuse from the gase- ous phase at 700°C into single crystals of p-type germanium containing 0.1 ppm of indium. As the arsenic diffuses into the P-type germanium, an n-type layer will form in the diffusion zone. At the p-n junction the concentration ratio of the arsenic to the indium is constant. Experimental Procedures—The germanium specimens, 10 mm by 10 mm by 5 mm, were polished and etched to a mirror finish. The specimens were then sealed off in a vycor glass capsule at 3 x 10"5 mm Hg pressure with a sufficient amount of arsenic powder to produce a one-half atm pressure of arsenic at 700°C. Specimens were annealed at 700°C without radiation. The diffusion coefficient determined from these samples agrees within 8 pct of previous work done by Fuller.' Three specimens were given diffusion anneals at 700°C in a small tube furnace centered beneath the target of a 2-mev Van de Graaff generator. The specimens when in the furnace were 10 cm directly below the target of the generator. These specimens were irradiated continuously during the diffusion run with the Van de Graaff operating at 2 mev with a tube current of 225 to 250 pamp. The intensity of the x-radiation at the surface of the specimen inside the furnace was approximately 4.5 x l05 roentgens per hr. The temperature was controlled within m2°C by a chromel-alumel thermocouple throughout this work with no observed temperature change due to the radiation. By careful lapping, the samples were polished at an angle of 5 deg to the diffusion zone, giving a XI0 increase in the visible diffusion zone. The location

Jan 1, 1960

By E. F. Koch, J. L. Walter

oriented crystals of iron and iron with 3, 5, and 6.25 pct Si were rolled to reductions of 10 and 70 to 97 pct at room temperature. Similarly oriented crystals were deformed in tension. Dislocation substructures of the deformed crystals were observed by transmission electron microscopy to determine the effect of silicon on the formation of substructures. Pole figures were obtained to relate orientation changes to substructure. When rolled 10 pct, the iron crystals and the 3 pct Si-Fe crystals formed cells, 1 and 0.2 u in diameter, respecliuely. Cells were absent in the higher-silicon crystals. Extended dislocations and possible stacking faults were observed in the 6.25 pct Si-Fe crystal rolled 10 pct and annealed at 650°C. The stacking-fault energy was estimated to be 20 ergs per sq cm. Rolling to 70 pct resulted in the formation of sub-bands (0.9 µ wide) ill the iron crystals and transition bands (containing 0.2-µ-wide subbands) in the 3 pct Si crystals. No subbands formed in the 5 pct Si-Fe crystal until it was ankzealed. SliP occurred on (112) planes ill tension. The slip traces on the 3 pct Si crystal were wary while those on the 5 pct Si crystal wvere straight. The strain-hardening coefficient for the 5 pct Si crystal was nearly zero. Cells did not form, at least at elongations up to 10 pet. The results suggest that cross slip of iron is restricted by additions of silicon beyond about 3 pct possibly by formation of immobile extended dislocations. IN a previous paper' the authors described the substructures developed in (100)[001]-oriented crystals of 3 pct Si-Fe which were rolled to reductions of 10 to 90 pct at room temperature. At low reductions (10 to 20 pct) cells, approximately 0.2 to 0.3 ja in diameter, were formed. The cell walls consisted mainly of edge dislocations. With increasing reduction (up to 50 pct) the cells were seen to elongate in the rolling direction. In certain regions of the crystal there were significant reorientations which were characterized as rotations about an axis normal to the (100) or rolling plane. These regions were called "transition bands". The regions in which there were no reorientations were called ('deformation bands". At reductions of 60 to 70 pct the elongated cells in the transition bands became sub-bands separated by low-angle tilt boundaries with angles of disorientation of about 2 deg. The elongated cell structure in the deformation band was replaced by a general distribution of dislocations. It was noted that the width of the subbands in the transition bands remained 0.2 to 0.3 µ; i .e., the width of the subbands was the same as the initial cell diameter for reductions up to at least 70 pct. From this, and from considerations of the mechanism of formation of the transition bands,' it was concluded that the subbands evolved directly from the initial cells. In order to check this conclusion, it was decided to examine the relationship between initial cell diameter and width of subbands produced by large rolling reductions. Cell size is known to be dependent upon the temperature of deformation.2,3 However, preliminary experiments with 3 pct Si-Fe crystals indicated that the change in cell size with increasing temperature of deform,ation was not sufficient for the present purpose. On the other hand, cell diameters generally reported for iron deformed at room temperature2'3 range from 1 to 2 p, a factor of 3 to 10 larger than the cells in 3 pct Si-Fe rolled to 10 pct reduction,' indicating the possibility of a marked dependence of substructure (at least in terms of cell size) on the amount of silicon in iron. Thus, the investigation was enlarged to include the study of the effects of varying silicon content on substructure in lightly rolled as well as in heavily rolled crystals of iron and iron with 3, 5, and 6.25 pct Si. The crystals used in this study all had the same orientation, (100)[001], with respect to rolling plane and rolling direction. These were rolled to reductions of from 10 to 97 pct and the substructures determined by electron transmission microscopy in both the rolled state and after annealing. In addition, stress-strain curves were obtained from (100)[001]-oriented crystals of iron and 3 and 5 pct Si-Fe to determine the effect of silicon on tensile properties. The dislocation substructure of the tensile specimens was also determined for Samples pulled to 2 and 10 pct elongation at room temperature for comparison with the substructures produced by rolling. 1) EXPERIMENTAL PROCEDURE Crystals with 3, 5, and 6.25 pct Si were prepared by annealing 0.012-in.-thick sheets of high-purity Si-Fe in purified argon at 1200°C to effect growth

Jan 1, 1965

By J. H. Jackson, P. D. Frost, C. H. Lorig, A. C. Loonam

THIS paper describes (1) the effect of sodium on the tensile ductility of magnesium-lithium base alloys, and (2) the precautions necessary to avoid sodium contamination. Effect of Sodium on Properties The harmful effect of sodium in magnesium-lithium base alloys has been recognized by other investigators.1,2 However, quantitative data on its effect have not hitherto been published. The effect of sodium on the ductility of an 87 pct Mg-9 pct Li-4 pct Zn alloy is shown in fig. 1. The sodium was introduced by adding sodium chloride to the flux, which consisted of 50 pct LiC1-50 pct KC1. Moderately high ductility was obtained at an indicated sodium content of about 0.05 pct. Actually, the value probably was less than 0.05 pct, be-cause analyses of the lithium, which were more accurate than those of the alloy, indicated that the highest ductility was obtained when its sodium content was 0.02 pct or less. In fact, in alloys having somewhat greater strength than this particular composition, the sodium content of the lithium must be under 0.01 pct to avoid embrittlement. The effect of sodium on the ductility of several alloys having fairly low strength levels is shown in fig. 2. These alloys were melted with a flux containing 75 pct LiC1-25 pct LiF, to which various quantities of sodium chloride had been added. Sodium had no significant effect in pure magnesium but markedly decreased the ductility of the magnesium-lithium-zinc alloy, even though the alloy contained only 3 pct Li. As the lithium content of the binary alloys was increased, the ductility of the sodium-free alloys also increased. However, the effect of sodium on ductility became progressively more pronounced. Sodium raised the minimum hot-rolling temperatures, particularly those of the high-strength alloys, but its effect, in this respect, was less critical than its effect on tensile ductility. For optimum cold roll-ability, a low-sodium content was required. No deleterious effect of sodium on the stability of properties at slightly elevated temperatures was found. Control of Sodium in the Alloys Optimum ductility is obtained in the magnesium-lithium base alloys when sodium-free materials are used. Commercial lithium was formerly the chief source of contamination. Now purified lithium is usually available. When lithium of ordinary purity is used, the effects of sodium can be minimized by using a flux consisting of 75 pct LiC1-25 pct LiF. Bubbling nitrogen through the melt also helps remove sodium. The damaging influence of sodium on the ductility of the magnesium-lithium base alloys was observed very early in the alloy development program. The discovery came about as a result of chemical analyses made on the lithium used in the alloys. Ductile alloys had been made from lithium containing about 0.2 pct Na, whereas the lithium used in the brittle alloys contained about 0.9 pct Na. The first magnesium-lithium alloys were melted under commercial fluxes ordinarily used in melting magnesium alloys. These fluxes were unsuited for scavenging the contaminating sodium, and the resulting alloys were not ductile. Next, a flux containing 50 pct KC1-50 pct LiCl was tried. This was somewhat more effective but still was not satisfactory. After a number of different experimental fluxes had been investigated, one containing 75 pct LiC1-25 pct LiF was adopted. This flux made it possible to obtain good ductility in the alloys. The

Jan 1, 1951

By W. C. Winegard, A. Galibois, C. J. Beingessner

The effects of solutes on the distribution of two-dimensional configurations of grains in zone-refined tin have been studied. When solutes with partition coefficients (ko) greater than unity are added, three-sided pains become more prevalent and the growth law changes. It is shown by electron-Probe micro-analysis that a solute buildup occurs ahead of a moving grain boundary when ko > 1. It has been found recently1, 2 that solutes with partition coefficients greater than unity have a larger retarding effect on grain growth than solutes with k, less than unity. ko is defined as the ratio of the concentration of solute in the solid to the concentration of solute in the liquid with which the solid is in equilibrium. Niessen and winegard2 have suggested that this effect is probably due to the complex shape changes which occur during the process of grain growth and that no theory based on single boundary motion3-5 can explain the results. They suggested that the dissociation of the unstable fourfold junction was delayed in alloys where ko was greater than 1 because the boundaries at the junction had to move into a region of high solute concentration. If indeed this mechanism were correct, it was felt that not only would the dissociation of fourfold junctions be affected by the solute buildup ahead of the boundaries, but the collapse of three-sided grains would be impaired. These combined effects would naturally lead to a modification in the distribution of the number of sides per grain seen on a two-dimensional section. The present investigation was undertaken to test these hypotheses by examining the grain-growth process in detail. EXPERIMENTS The Distribution of Grain Configurations in Zone-Refined Tin as Seen on a Two-Dimensional Section. Following the method of Bolling and Winegard,6 zone-refined tin was cast into button-shaped specimens and, subsequently, plastically deformed under a drop hammer at room temperature. The resulting flat coin-shaped samples were annealed at 200°C, some for 50 sec and others for 100 sec. The specimens were then examined to determine the distribution of the number of sides per grain, i.e., the num- ber of crystals adjacent to any particular grain in the section. For simplicity, the grains were classified as three-sided, four-sided, and so forth; this concept is schematically illustrated in Fig. 1. As indicated by smith,' it was necessary to examine every grain within an enclosed area to obtain a proper distribution of the relative frequency of each type. The distributions for the two annealing times are illustrated in Fig. 2. The total number of grains examined is also indicated on the figure. It is evi-

Jan 1, 1965

By G. Sachs, E. J. Riping

All ferrous alloys can be made brittle by straining at sufficiently low temperatures. However, the changes in mechanical properties for different ferrous materials with decreasing testing temperature do not appear to follow any universal law. In particular, complex effects of testing temperature have been observed if cold worked steels were subjected to tensile tests at low temperatures. EFFECTS OF PRESTRAINING AT A TEMPERATURE ABOVE THE TESTING TEMPERATURE ON THE FRACTURE CHARACTERISTICS‡ A considerable amount of data has been presented by a number of investigators on the fracture characteristics of various cold worked steels.' These data usually relate to a two-step procedure first used by Davidenkov,² consisting of stretching by tension to a certain strain or " prestraining" at room temperature and then completing the tensile test, or "testing" at the temperature of liquid air. On the basis of data of this type made available to date, ferrous alloys can be classified into two groups with respect to their fracture characteristics observed on testing at a low temperature after prestraining at room temperature. Very complex phenomena have been observed for all annealed steels. On the other hand, some observations indicate that steels in certain other conditions represent a fundamentally simpler relation. In considering the effect of prestraining at one temperature on the properties obtained at some lower temperature, it should be expected that any cold work reduces the ductility retained in proportion to the magnitude of the cold work. However, the test data presented to date indicate that only heat treated (quenched and tempered) steels appear to conform to this expectation, according to the very limited test data in Fig 1, presented by McAdam, Geil and Mebs. This series of tests, Fig 1, shows that the retained ductility became smaller the larger the prestrain. However, this decrease is less than the amount of prestrain or, in other words, less than the decrease in ductility at the prestraining temperature. These effects of prestraining are fundamentally identical with those observed by Bridgman3 when a steel was prestrained (in tension) under hydrostatic pressure and then subjected to a regular tension test. It appears, therefore, that the basic effect of prestraining under conditions which yield a higher ductility than the (subsequent) testing procedure, consists of gradually increasing the total ductility of the metal from the initial low value of testing to the higher value of prestraining. On the other hand, all annealed steels, if cold worked by tension at room temperature and then tested at a lower temperature, provided that some ductility is retained, showed a far more complex behavior than that discussed above. This relationship is exemplified by Fig 2, for three pearlitic steels.4,5 These particular steels were selected because of the various shapes of their ductility-prestrain curves. All three steels, and any other investigated so far, suffered a rapid decrease in retained (and consequently also in total) ductility when subjected to small pre-strains. Then, after exceeding a certain prestrain it was generally observed that the ductility recovered.* This rather complex behavior of annealed steels may be tentatively correlated with the presence of stretcher strains at small restrains. Heat treated steels do not exhibit stretcher strains. This fact might possibly explain their simpler prestrain-retained ductility relationship. The destructive effect of these stretcher strains may possibly be associated with the presence of triaxiality, which may occur in any highly non-uniform stress and strain state (and which is retained as residual stress after unloading). Even a small degree of triaxiality may then cause a reduction in ductility, or even embrittlement at a sufficiently low testing temperature. The discussion presented above deals with the effects of cold working at a high temperature on the fracturing

Jan 1, 1950

By R. I. Garrod, R. A. Coyle

The shapes and positions of X-ray reflections from specimens of copper, steel, and aluminum alloy haue been examined in the elastic and plastic ranges both while the specimen was under stress and in the unloaded condition. For the aluminum alloy the shape was unaltered by the application of stress either within the elastic limit or in the plastic range provided that no additional plastic strain was induced. In copper the broadening accompanying plastic deformation was very slightly reduced when the specimen was unloaded. A similay but more marked elastic component of broadening was also found for steel, but in this case below the yield stress. Line profiles corrected for instrumental and particle-size broadening indicate very large internal stresses in local regions of the plastically deformed metals. The results are discussed in terms of a recent suggestion that the heterogeneous dislocation distribution between the cells and their boundary walls plays a major role in the peak shifts and broadening of the X-ray reflections. STUDIES of the X-ray line profiles from strained polycrystalline aggregates concentrate usually on one or the other of two main parameters: a) the displacement of the peak of the intensity contour from its position for a strain-free aggregate, or b) the shape of the profile. From peak shifts data can be obtained either on the relation in both the elastic and plastic ranges between applied external stress and average lattice strains in a given (hkl) direction, or, alternatively, on the residual lattice strains which are present after a plastically deformed specimen is unloaded.' On the other hand, the shapes of the broadened profiles from cold-worked metals can be analyzed to separate the broadening produced by small particle size and by heterogeneous lattice strains.' In this paper the terms "size broadening" and "strain broadening'' are used in the general sense adopted by warren.' In the past, apart from two early qualitative observation, it has been customary to examine only the movements of the peaks of the profiles while the specimen is actually under load, since the line broadening induced by plastic strain remains after removal of the external stress. Consideration of the implications of existing data of this type suggests, however, that fruitful additional information on a number of fundamental aspects might be gained by careful examination of whether the X-ray line profile is in fact different in the loaded and unloaded states of the specimen. By taking advantage of the sensitivity and convenience of modern diffractometer techniques it is possible to explore with relative ease the magnitude and importance of any elastic effects which may be superimposed upon the well-known permanent changes in profile. The main aim of the work to be described was thus to investigate this point for typical metals and alloys. For this purpose annealed specimens were extended first elastically and then plastically and the positions and shapes of X-ray reflections were recorded. Initially it was anticipated that prime interest would center on observations within the plastic range; it has been found, however, that small changes in profile sometimes occur both before and after the nominal elastic limit of the material is reached. It is shown that the results obtained have important implications in relation to the structural changes and processes associated with deformation. I) EXPERIMENTAL To enable the diffraction lines to be recorded while the specimen was under uniaxial-tensile stress, a small hydraulic testing machine was designed and constructed for direct attachment to the goniometer of a Philips diffractometer. The specimens, which were machined from 1/2-in.-diam rod and had a central rectangular section 3/8 by 1/16 in. over a gage length of 1 in., were held in the machine by split collets mounted in grooves in the cylindrical ends of each specimen. No special precautions were taken to ensure precise axiality of loading. Constant oil pressure was maintained by a lever and weights system and transmitted to the loading rig by flexible pipe. The actual load on the specimen was measured by a load cell in the machine to an accuracy of * 1 pct. To enable smooth X-ray profiles to be obtained the specimen and machine were oscillated continuously during recording through *7-1/2 deg about the normal half-angle position of the goniometer. The three materials chosen for the investigations were high-purity copper as representative of a ductile fcc metal, a low-carbon steel for a bcc metal, and an aluminum alloy as a material in which the proof stress/ultimate strength ratio is high. Details are as follows. a) Copper. 99.999 pct purity. After machining the specimen surface was polished mechanically and

Jan 1, 1964

By J. T. McGrath, G. B. Craig

Tensile tests on aluminum single crystals, grown from the melt, revealed that the yield stress of these crystals was raised as the amount of striation substructure was increased. The number of striation-type boundaries was varied by changing the rate of growth of the crystals. The results are interpreted in terns of a blockage of dislocation movement by striation boundaries. IMPERFECTIONS are known to have a large effect on the mechanical properties of metals. Teghtsoonian and Chalmers 1 studied a block or striation-type substructure in tin and found that the formation of the striations depended upon rate of crystal growth and orientation. They found that the angular misorienta-tion between neighboring striations varied between 15 min and 5 deg. Atwater and chalmers2 investigated striations in tin and lead, and found that purity was another factor which influenced their formation. There was a limiting purity above which the striations were straight and regular. There is little information in the literature concerning how substructures in melt-grown crystals affect strength. washburn3 introduced small-angle boundaries into zinc by a shear process and found a subsequent increase in yield stress which he attributed to the presence of these boundaries. Lauriente and pond4 found the critical resolved shear stress in aluminium crystals grown from the melt, to increase with etch pit density. The etch pits were used as an indication of growth imperfections. In Hibbard's5 work on lineage structure in copper crystals grown from the melt, he tested one crystal containing interlineage boundaries, and found a 50 pct increase in the critical resolved shear stress. Fleischer and Chalmers6, in a recent paper, mention briefly that, in the production of aluminium crystals from the melt when the growth rate was raised from 1.2 to 18 cm per hr, the yield stress increased 50 pct. They felt that the increase in yield stress with rate of growth might be attributed to a higher concentration of impurities in the gage length and also might be affected by the increased number of small-angle boundaries (striations). The present investigation was undertaken to determine the effect of the striation substructure on the strength of aluminum single crystals. EXPERIMENTAL PROCEDURE Aluminum single crystals of 99.9992 purity were grown from the melt using a technique described by Chalmers.7 The growth rate was varied from 0.6 to 20 mm per min, thus producing crystals with varying numbers of striation boundaries. To avoid prior deformation, the crystals were chemically cut to the desired length with a saturated solution of cupric chloride. They were then annealed at 580°C for 24 hr and allowed to cool slowly in the furnace. Finally, the specimens were electropolished using an electrolyte of 5 parts ethyl alcohol and 1 part perchloric acid. Each specimen was approximately 5 in. in length and 0.125 sq in. in cross section. The average orientations of the 5 series of crystals studied are shown on the stereographic projection of Fig. 1. The crystals were strained approximately 2 pct in a soft tensile machine. The strain sensitivity was 3.6 x 10-4 cm over a 5-cm gage length.

Jan 1, 1960

By I. R. Kramer, L. J. Demer

Aluminum single crystals were pulled in an electrolytic cell allowing surface removal during the deformation. The extent of Stages I and 11 of the stress-st-aitz curve was increased and the slope decreased as the rate of metal removed from the surface was increased. An increase of the strain rate caused a decrease in the effectiveness of the metal removal. The data indicate that the work-hardening coefficient in Stage I is determined primarily by the conditions which exist on the surface of the crystal. In Stages 11 and 111, both surface effects and internal barriers are important. ALTHOUGH numerous investigations have been conducted on the plastic flow characteristics of metals in an attempt to explain the mechanism of work-hardening, relatively few studies have taken into account the influence of the surface. In all current theories of work-hardening it is assumed that the impediments to the movement of dislocations are within the crystal. The barriers due to the surface and the existence of solid and liquid films have been neglected even though it has been demonstrated that the surface exerts a large effect. A number of investigators1-l8 have shown that solid films on the surface of single crystals markedly affect their mechanical behavior. In general, the presence of a solid film tends to increase the yield stress and increase the work-hardening rate. Often, on single crystals, Stage I and, at times, Stage II regions are completely suppressed. Various mechanisms have been offered for the effects of oxide and metal films as well as the influence of electrolytes. Of these, concepts concerned with the locking of surface dislocation sources and the blocking of dislocations at the surface resulting in pileups appear to be actively considered at present. Barrett,11 Takamura,6 Gilman,19 Lipsett and King,20 Shapiro and Read,10 and Weiner and Gensamer21 are among those who have interpreted their results in terms of piled-up dislocations at the surface, while Adams.22 and Chalmers and Davis23 have explained their experimental observations in terms of locking of surface dislocation sources. In general, the change in plastic flow properties due to electrolytes has been explained in terms of the unblocking or unlocking of dislocations by the removal of the oxide films. In considering the two proposed mechanisms, it appears that the locking of sources of surface dislocations by a solid film should exert a primary influence only on the critical resolved shear stress for flow and not on the slopes of Stages I and 11. However, the blocking at the surface of dislocations from internal sources may also affect the critical resolved stress and furthermore exert an influence throughout the whole plastic range. In certain cases it does not seem feasible to explain the results of experimental observations in terms of locking of surface dislocation sources. The abnormal aftereffects found by Barrettll,12 by removing the oxide by an acid treatment are excellent evidence of the blocking of dislocations at the surface. Additional evidence in favor of a blocking due to a pileup of dislocations at the surface may be found from the observations that the critical resolved shear strength continues to increase with the thickness of the oxide layer until very heavy oxide layers are formed. If the locking of surface dislocations sources were the dominant factor, the critical resolved shear stress would not be expected to increase after all of the surface sources were locked by the formation of the oxide. This may be expected to happen after a few atomic layers of the oxide are formed. In spite of the above evidence on the strong influence of the surface on the plastic flow characteristic, this has been ignored in current theories of work-hardening. Seeger24,25 suggested that most of the dislocations may slip out of the crystal only when the specimen axis is within certain areas of the orientation triangle. In other areas the resolved shear stress in other glide systems is large enough to generate dislocations which can form Lomer-Cottrell locks, thereby decreasing the average slip distance in some directions and causing a larger hardening rate. Friede126 assumed that at the beginning of Stage 11, a large number of Lomer-Cottrell dislocations are formed by a catastrophic process which used up all the Frank-Read sources on the secondary slip-planes. In this manner a fixed number of Lomer-Cottrell locks is formed which act as barriers against which the dislocations can pile up. In Stage 111, Seeger24 and Diehl, Mader, and Seeger25 proposed that Lomer-Cottrell barriers are circumvented by the cross slip of extended screw dislocations. Cottrell and Stokes,27 Friedel,26 Cottrell,26 and stroh29 suggest that the Lomer-Cottrell dislocations collapse under the stress field of the dislocation pileup. It is the purpose of this paper to report the changes in Stages I, II,and III of the deformation process in

Jan 1, 1962

By I. R. Kramer, L. J. Demer

T. H. Alden and R. L. Fleischer (General Electric Research Laboratory)— The authors' results indicate clearly and, we believe, significantly that during tensile deformation the surface layers of an aluminum crystal are hardened more severely than the interior of the crystal. A probable explanation of this effect, as the authors indicate, is that dislocations in the primary slip system may be obstructed at the surface or, it should be added, near the surface. The intent of this discussion is to show that the oxide film on aluminum is not likely to be responsible for this effect, but that the results can be understood if it is assumed the secondary slip is more active in the surface layers than in the interior. Prior study has shown that the principal mechanical effect of an oxide film on a single crystal is to raise the yield stress while leaving the rate of strain hardening during the initial deformation relatively unaffected.33 Since the yield stress is unchanged during polishing in the present case, we conclude that continual removal of the oxide film exerts a small effect on the plastic hardening.* It appears that the hardening interactions are occurring not only at the immediate surface, but to an appreciable depth below it, although with decreasing severity. For example, Kramer and Demer found that with removal of 0.004 in. from a specimen, the easy glide region was extended somewhat; but the yield stress did not decrease. The initial yield stress was recovered only after 0.041 in. was removed. Since a very brief polish would permit dislocations trapped behind a surface film to run out,34 extra dislocations must, instead, be trapped to a considerable depth below the surface. The same conclusion is drawn from the observation of decreasing hardening slope with increasing surface removal rates. If the hardening interactions were only at the immediate surface, a full softening effect would be observed at some small removal rate. The view is taken here that strain hardening is principally caused by small amounts of secondary slip.35 The secondary dislocations will interact in various ways with the primaries, interfering with their motion and causing them to accumulate in the crystal. Prior studies of easy glide have shown Diehl's model of hardening to be qualitatively consistent with the effects of impurities,36 of temperature,36 and of crystal size.37 On this basis the enhanced hardening of the surface layers in aluminum arises from increased secondary slip at and to some depth below the surface. Selective removal of this hardened layer is expected to decrease the measurable "bulk" hardening, the effect increasing with the removal rate and decreasing with the applied strain rate. We suggest that the stress on secondary systems is raised by the bending moments arising from interactions with the grips during the deformation. This stress from the grips has been shown to be a maximum37 near the surface, and hence, increased secondary slip should result. Prior investigations of grip effect:; indicate that as the grip stresses are raised by changing the crystal shape, the easy glide slope increases while the extent of easy glide decreases.38-40 It has been shown also that bending moments superimposed during tensile testing may either decrease easy glide, when supporting the moments caused by gripping, or increase it, when cancelling the gripping moments.38 This interpretation of the authors' results, emphasizing the special importance of secondary slip near the surface, is also consistent with the earlier results of Rosi.41 Copper crystals alloyed with silver in the surface layer show greatly increased easy glide compared with pure copper. In addition, the easy glide slope is reduced. The effect of bulk alloying in extending easy glide has been well established and has been interpreted as indicating the relative difficulty of secondary slip in alloy crystals. Since non-basal glide is difficult in zinc crystals, the effects of surface removal during deformation may be less important. Experiments to test this idea are in progress. I. R. Kramer and L. J. Demer (authors' reply)—The authors wish to thank Dr. Alden and Dr. Fleischer for their discussion. Our interpretation of the data in the paper is that dislocation motion is obstructed by "debris" which starts to form at the surface and extends towards the interior of the crystal with further plastic deformation. The fact that we did not find a reversion from Stage II to Stage I by surface removal shows that in Stage II the "debris" fills the entire cross-section of the specimen. Drs. Alden and Fleischer take the view that bending stresses due to the grips are responsible for the

Jan 1, 1962

By I. R. Kramer

Studies of the effect of size of the specimen on the change of slopes of Stages I and 11 by surface removal showed that the change of Stage I was independent of size with respect to the polishing rate; however, the change in the slope of Stage 11 with polishing rate increased directly in proportion to the surface area. The removal of the surface during the test affected the plastic deformation characteristics of gold, aluminum, and zinc single crystals and polycrystalline aluminum. The apparent activation energy of aluminum was found to be decreased markedly by removing the surface during the deformation process. In previous papers1-3 it was shown that the surface played an important role in the plastic deformation of metals. By removing the surface layers of a crystal of aluminum by electrolytic polishing during tensile deformation, it was found that the slopes of Stages I, II, and III were decreased and the extents of Stages I and II were increased when the rate of metal removal was increased. By removing a sufficient amount of the surface layer after a specimen had been deformed into the Stage I region, upon reloading, the flow stress was the same as the original critical resolved shear stress and the extent of Stage I was the same as if the specimen had not been deformed previously. The slope of Stage I was decreased 50 pct and that of Stage 11 decreased 25 pct when the rate of metal removal was 50 X 10"5 ipm. These data show that in Stage I the work hardening is controlled almost entirely by the surface conditions, while in Stages 11 and III both surface conditions and internal obstacles to dislocation motion are important. It appears that during the egress of dislocations from the crystal, a fraction of them becomes stuck or trapped in the surface regions and a layer of a high dislocation concentration is formed. This layer would not only impede the motion of dislocations, but would provide a barrier against which dislocations may pile up. In this case, there will be a stress, opposite to that of the applied stress, imposed on the dislocation source and dislocations moving in the region beyond this layer. It has been found convenient to refer to this layer as a "debris" layer. The "debris" layer may be similar to the dislocation tangle observed by thin-film electron microscope techniques.4 Reported in this paper are the results of studies on the effects of removing the surface during plastic deformation on aluminum crystals of various sizes. The effects of the surface on the yield point behavior of gold and high-purity aluminum crystals as well as the creep behavior were also determined. The effects of surface removal on polycrystalline aluminum (1100-0 and 7075-T6) are also reported. EXPERIMENTAL PROCEDURE For those portions of the investigation involving creep and tensile specimens, single crystals, having a 3-in. gage length and a nominal 1/8-in. sq cross section, were prepared by a modified Bridgman technique using a multiple-cavity graphite mold. The single crystals were prepared from materials which had initial purities of 99.997, 99.999, 99.999, and 99.999 pct for Al, Cu, Zn, and Au, respectively. The aluminum specimens for the size effect studies were prepared through the use of a three-tier mold in which crystals having a cross section of 1/8, 1/4, and 1/2 in. were grown from a common seed. The mold design was arranged so that one 1/2-in. crystal, two 1/4-in. crystals, and four 1/8-in, crystals of the same orientation could be cast. With this technique, it was possible to obtain only one set of crystals with the same orientation. Because of this limitation, it was not possible to determine both the changes of extent and slope of the various stages since a large number of crystals of the same orientation would have been required. Instead, only the change of slope as a function of the rate of metal removal was studied by abruptly altering the current density of the electrolytic polishing bath at various strains within the regions of Stages I and 11. The experimental techniques used for the tensile studies were essentially the same as those used previously.1,3 The specimens were deformed in a 200-lb Instron tensile machine, usually at a rate of 10-5 sec-5. A methyl alcohol-nitric acid solution was used as the polishing bath for aluminum. The temperature was maintained constant within ±0.l°C by means of a water bath. The tensile machine was

Jan 1, 1963

By C. Feng, I. R. Kramer

A study was conducted to determine the influence of the surface on the yield point of fcc metals and high-purity iron. For the high-purity fcc metals, the yield Point produced by restraining a specimen may be eliminated by removing a sufficient amount of the layer. A yield point similar to that in fcc metals was found when iron specimens were pre-strained after a prior deformation. This yield point is not due to an aging effect but is associated with the surface layer. The yield points in age-hardenable aluminum alloy and those connected with "work softening" are not affected by a surface-removal treatment and are, therefore, caused by bulk-type dislocation reactions. The yield point which appears in previously strained fcc metals has been the subject of numerous studies. Several theories have been advanced to explain this "unloading-reloading" yield point. Cottrell and stokes,' from their study on the effect of temperature on plastic properties of high-purity aluminum, considered that it was the result of an avalanche "breakdown" of Lomer-Cottrell sessile dislocations. Haasen and Kelly2 extended this concept of dislocation-dislocation interaction to account for the yield point when unloading and reloading was carried out at the same temperature. On the other hand, strain aging was found to be responsible for the yield point in A1-Mg alloy by Westwood and Broom,3 and in aluminum alloys containing various amounts of alloying elements by Smallman, Williamson, and Ardley.4 In these cases, the yield point is considered to be associated with the locking of dislocations by impurity atoms. Birn-baum and filer5,6 and Takamura and muira7 reported that, when a high-purity copper specimen was prestrained, then held at a lower stress, and finally reloaded at the prestrain temperature, a larger yield point was observed. Such an increase was attributed to the locking of dislocations by point defects. In addition, Bolling8 suggested that both mechanisms, i.e., dislocation-dislocation interaction and strain aging, are responsible for the yield phenomenon, at least in a brass. Thus, there appears to be experimental evidence for both the strain aging and dislocation-dislocation interaction theories to explain the yield point in the fcc metals and alloys. In a previous article,9 one of the authors observed that, if sufficient amounts of metal were electrolti-cally removed after deformation of a high-purity aluminum single crystal, the yield point did not appear upon reloading. Continued pursuit in this area revealed that the effect of the surface on the yield-point phenomenon is not limited to one metal but affects a variety of metals of different lattice structures. Nor is the effect limited to the yield points produced by simple unloading-reloading at constant temperature; the surface exerts an important role on the yield point even when the temperature is changed at some stage during the test. It is the intent of the present article to give additional information regarding the effect of the surface on the yield-point phenomenon and to show the association between the yield point in both fcc and bcc metals and the existence of a heavy concentration of dislocation in the region near the surface of a deformed specimen.10 EXPERIMENTAL Materials. The single crystals used in this study had a nominal cross section of 0.125 by 0.125 in. and a 3-in. gage length and were prepared by a modified Bridgman technique. The initial purity for the metals was 99.997, 99.999, and 99.999 pct for aluminum, copper, and gold, respectively. Bar stock of these same materials was used in the preparation of the polycrystalline specimens of aluminum and copper. The iron specimens were machined from rods of "ferrovac", reported to have a purity of 99.98 pct. In addition, a precipitation-hardening aluminum alloy, containing 1.5 pct Cu, 2.5 pct Mg, and 5.5 pct Zn, was used. The polycrystalline specimens of iron, copper, and the aluminum alloy had a diameter of 0.17 in. and a gage length of 2 in. while the high-purity aluminum specimen had a nominal rec-

Jan 1, 1965

By I. R. Kramer

Single crystals of aluminum were pulled in tension in a solution of paraffin oil and stearic acid. The critical resolved shear stress did not change with the concentration of the stearic acid solution; however, the extents and slopes of Stages I and II were affected greatly. The observations lend evidence that the weakening effect of surface-active agents is controlled by the rate of desorption of the metal soap formed by the reaction of the surface-active agent and the metal surface. IT has been shown by various investigators1-" that surface-active agents markedly affect the mechanical properties of single crystals. (A surface-active agent, for the purpose of this report, is defined as a long-chain organic molecule which contains one or more polar groups. Usually, however, investigations have considered only molecules having one polar group.) In general, when single crystals are deformed in some solutions containing surface-active agents, the creep rate, Fig. 1, is increased and the yield strength is decreased. The fatigue strength has been reported to be affected also.ll Rehbinder and his asociatesl' explained the "weakening" effect of surface-active agents in terms of physical adsorption. They assumed that a large pressure was created in microcracks which existed on the surface of the crystal." Harper and Cottrell,' from their study of the effects of surface conditions, found that the deformation characteristics of zinc single crystals were not altered by a solution containing a surface-active agent unless the surface of the specimen had an oxidized surface. They concluded that the role of the polar molecule was to remove the strengthening effect of the oxide coating. Later, And-radeetBpresented additional evidence which appeared to agree with this conclusion. In contrast, Klinken-berg et al.7 reported data which confirmed the results of Rehbinder. Using zinc and cadmium crystals which had been cleaned by electrolytic polishing, a large increase in the creep rate was observed when Lle specimens were tested in a 1 pct oleic acid-paraffin oil solution. They also reported that the creep rate

Jan 1, 1962

By I. R. Kramer

A study was made of the effect of surface-active agents an copper, gold, and zinc single crystals as well as polycrystalline aluminum. The study on coppw showed that the maximum effect of the surface -active agent occurred at the same concentration of the solution as that at which the rate of solution of the copper soap was the greatest. Surface -active agents did not affect the creep behavior of gold or freshly polished zinc specimens. The creel-, rate of zinc specimens in a solution containing a surface-active agent zoas always lower than that of freshly polished specimens. In previous papers1'2 it was reported that the surface played an important role in the plastic deformation of metals. By removing the surface layers of a crystal of aluminum by electrolytic polishing dur- ing tensile deformation, it was found that the slopes of Stages I, 11, and In were decreased and the extent of Stages I and I1 were increased when the rate of metal removal was increased. The results of the investigation of surface-active agents showed that changes in the slopes and extents of Stages I and II occurred when single crystals of aluminum were deformed in tension in a bath containing solutions of paraffin oil and stearic acid. The amount of change was a function of the concentration of stearic acid and the maximum effect occurred at a concentration of 0.002 mole per liter. These results were interpreted2 in terms of the rate of solution of metal soaps which form as a result of the chemical reaction between the surface-active agent and the metal. According to this interpretation, the "weakening" effect is controlled by the rate of solution of the soaps which depends upon the concentration of surface-active agents. At low concentrations, the number of metal soap molecules formed is low; at high concentrations, the rate of solubility is low, because of the high degree of saturation.

Jan 1, 1963

By J. G. Y. Chow, S. B. McRickard

The tensi1e properties of Ferrovac iron have been studied from 4° to 300°K. The stress required for macroscopic yielding was found to he constant below approximately 50°K. The effect of mechanical twinning on this low -temperature stress plateau was investigated. The onset of twinning occurs in this iron between 130° and 150°K and depending on its previous thermal history the twinning-stress curue may drop below or remain above the vield-stress curves as the temperature is lowered. Twinning has been shown to initiate slip in quenclzed iron at low temperatures. In no instances, however, did the onset of twinning alter the continuity of the yield stress -tempwature curve. Our data shows that carbon inhibits twinning and slip at low tem-peratures. This observation nay be used to explain the ductile-to-brittle transition in iron. The effect of fast neutron irradiation on yielding and embrittlement in iron and Fe-C alloys is offered as supporting evidence for this viewpoint. THE mode of yielding in iron at low temperatures was studied in an attempt to find an expression based on a single mechanism to describe the thermal dependence of the yield stress of iron. There are two types of inflections observed in the variation of the yield stress with temperature in iron and Fe-C alloys. The first is associated with ductile behavior and consists of a region extending 50" to 100°K above absolute zero in which the yield stress is independent of temperature. The second is observed in more brittle materials such as Fe-C alloys and irradiated iron and consists of an abrupt discontinuity in the yield curve as the temperature is lowered through a ductile-to-brittle transition point. The temperature dependence of the yield stress for iron with four grain diameters as found in this study is shown in Fig. 1. To varying degrees all the curves appear to flatten or approach an asymptotic value as the temperature is lowered below 50°K. Several other investigators1,2 have observed a plateau in the yield stress of iron and steel at low temperatures and in 1956 Louat3 presented a theory which contained an explanation for this behavior. In a subsequent exchange with Erickson and Low4'5 who attributed the plateau to the onset of mechanical twinning Louat8 showed that twinning first occurs in iron and steel tested in tension at temperatures as high as 140°K which is well above the observed plateau in yield stress. Furthermore he pointed out that both twinning and slip are basically dislocation processes and that with modified parameters his original theory still applied when deformation is initiated by twinning. Variables which affect the ductile-to-brittle transition in iron are test temperature, strain rate, composition and grain size.7 LOW,8 Hahn et al.,9 and Hull10 have provided evidence which links brittle fracture at a given temperature with the specimen grain size and the onset of twinning. In fact, Hull equates the brittle fracture stress to the twinning stress. On the other hand brittle fracture has been observed in the absence of twinning and priestnerl1 has given a fracture criterion which is valid whether or not fracture is preceded by extensive twinning. The data presented here clarify the role of twinning in the low-temperature deformation of iron. Strong evidence is given that the amount and distribution of interstitial impurities such as carbon are of

Jan 1, 1965

By D. I. Bardos, A. M. Bardos, Paul A. Beck

The approximate effective silicon radii in ternary Laves phase alloys with transition elements and silicon were found to range between 1.16 and 1.21A, i.e., considerably smaller than the atomic radius calculated for elemental silicon. The atomic radii were found to increase with the size of the transition element atoms in the structure. It has been noted by Aronsson1 that silicon in solid solution in iron, cobalt, and nickel has an effective CN 12 atomic radius of approximately 1.20Å, a value very much smaller than the CN 12 radius of 1.34Å derived from the interatomic distances in elemental silicon.7 The unusually short metal-silicon interatomic distances in transition element monosilicides and disilicides have been also pointed out by various investigators.1 A similar tendency was observed by Nevitt in Cr3O type silicides.2 Recent work on Laves phases in ternary systems of silicon with transition elements4"8 suggested that extensive Laves phase fields may occur in such systems.8 It has been pointed out by Laves7 that the MgCu2 and MgZn2 type structures lend themselves particularly well for the determination of the effective radii of the component atoms. In these AB2 phases the B atoms are arranged in close packed straight lines, and their distances are related in a simple manner to the lattice parameters.8 The present work was undertaken in order to find out whether or not the B transition element in such AB2 Laves phases can be replaced to an appreciable extent by silicon. In cases where extensive substitution proves to be possible, the "average atomic radius for the B site" at various silicon contents was to be determined, and the effective atomic radius of silicon calculated by extrapolation to complete replacement of the B component by silicon. The following ternary systems were studied: Ti-Mn-Si, Ti-Fe-Si, V-Co-Si, V-Ni-Si, Nb-Fe-Si, Nb-Co-Si, Ta-Fe-Si, Ta-Co-Si, and Mo-Fe-Si. In all of these alloy systems, the Laves phase solid solutions were found to extend over a considerable range of silicon content. As previously reported,4"8 in the V-Co-Si, V-Ni-Si, and Mo-Fe-Si ternary systems Laves phases do occur, even though there are no corresponding binary Laves phases. In stabilizing the Laves phase, silicon acts as if it were decreasing the effective electron concentration of the alloy.8 A more detailed study of the boundaries of the Laves phases in the V-Co-Si and V-Ni-Si systems has been made and will be published elsewhere. In both cases, the elongated Laves phase fields extend parallel to the B-Si side of the composition triangle, clearly showing that silicon is substituting for cobalt, respectively, nickel over a wide range of compositions. The binary Laves phases NbCo2 and TaCo2 have the cubic MgCu2-type structure. It was found that, in both ternary systems with silicon, again the MgZn2-type hexagonal Laves phase is stabilized and that this phase extends to high-silicon contents. In each ternary system at least three Laves phase alloys of the composition A(B1_xSix)2 were used, x here denoting the fractional substitution of the B-transition element atoms by silicon. The alloys, listed in Table I, were prepared by arc melting in argon. Each specimen was water quenched after a homogenizing anneal of 3 days at 110(FC, except for the Mo-Fe-Si alloys, which were annealed at 1200°C. Metallographic examination showed that most of the homogenized alloys consisted of a single phase, although some had minor amounts of a second phase, as shown in Table I. X-ray diffraction patterns were prepared using an asymmetrical focusing camera of large resolution and Fe Ka radiation. The patterns were indexed, and the lattice parameters of the hexagonal Laves phases were determined from the available diffraction lines of highest indices: (213), (205), and (313). The lat-

Jan 1, 1963

By Harry A. Lipsitt, Douglas Y. Wang

A fatigue study in completely reversed axial tension-compression has been perforried on high-purity titanium and on three high-purity alloys of titanium. The alloys each contain approxi7nately 0.75 at. pct of a single interstitial element; carbon, nitrogen, and oxygen, respectivley. The results corroborate a previously published theory which proposed that strain aging under alternating stress was responsible for the fatigue limit behavior of certain alloys. The present data indicate that in these alloys an increasing strain-talline aging effect under alternating stress is provided by oxygen, carbon, and nitrogen, respectively. CURRENT research on the nature of the fatigue limit in metals suggests that the presence of a fatigue limit in metallic materials is a manifestation of strain aging that occurs under alternating stress.lm5 A comprehensive theoretical model based on the above hypothesis has been developed to explain the existence of a fatigue limit.' This model also provides increased insight into several other fatigue phenomena as under stressing, overstressing, and coaxing effects. The theory, as well, provides equal understanding for those cases where no real fatigue limit is observed. Briefly, this theory assumes that the S-N curve for a pure metal is a smooth function of the applied stress, and the effect of adding an element that is soluble (or forms a precipitate) in the pure metal is simply to shift the S-N curve to the right. If the added element confers the power to strain age, the result is a further shift of the S-N curve, this time upward and to the right. Since strain aging is not expected to be a strong function of stress, and since damage per cycle is known to be quite stress dependent, it is to be expected that there will be some limiting lower stress at which the strengthening due to strain aging will balance the damage due to crack propagation. This stress is the fatigue limit. The position of the fatigue-limit knee was thought to be a function of the magnitude of the strain-aging effect on both the finite and infinite life portions of the S-N curve. Although the strain aging hypothesis seems to be reasonably valid for bcc materials,2'6 it needed to be tested for both fcc and cph metals. This report is the first of a series concerning the fatigue-limit behavior of titanium with varying amounts of the interstitial solutes (C, N,, and 4) that are known to cause static strain aging in titanium. Yield-point effects have been reported for polycrys-talline high-purity titanium alloys containing either carbon, nitrogen, or oxygen.7'9 These effects were observed at testing temperatures in the range 100 to 300'. In addition yield-point and strain-aging effects have been reported for single crystals of titanium containing 0.1 wt pct C plus N.' These yield points were observed over a wide temperature range, but no room-temperature aging occurred. Aging at 180' was required to cause the return of the yield point. The magnitude of the yield phenomena in titanium containing interstitials is not expected to be as large as is observed in bcc metals because of several factors. Titanium has a very high chemical affinity for oxygen and nitrogen. The thermodynamic stability of solutions of oxygen or nitrogen in titanium is recognized. Lattice parameter measurements of titanium containing arbon, oxygen,1° or nitrogen" show that the "c" parameter is expanded more than the "a" parameter, but that up to about 2 wt pct this results in an insignificant change of the axial ratio 'c/a." Ehrlich" has shown that the sites occupied by interstitial atoms in titanium are spherically symmetrical and therefore a lattice expansion, at a constant c/a ratio, results in a simple dilation of the interstitial site. Such a dilation involving no shear has been shown to react only with edge components of dislocations.13 This causes only a weak pinning action. Shear stresses would be anticipated locally when only one of the two interstitial positions was occupied. The carbon atom will cause a symmetrical distortion of the lattice whereas the oxygen and nitrogen atoms have, in addition, the previously mentioned chemical affinity of titanium for these elements. These factors will result in a considerably smaller reduction of free energy upon the association of interstitial atoms with dislocations, and therefore a much weaker pinning than has been observed for the bcc metals. These considerations would lead to the hypothesis that of the interstitial elements considered here carbon would cause the strongest pinning effect in titanium where the amount of interstitial in solution is constant. This hypothesis will be borne out in the analysis of the present results.

Jan 1, 1962