Search Documents

By B. F. Oliver, C. W. Haworth

Pure tin and Sn-0.5pct Pb ingots have been frozen unidirectionally from the base. For quiescent melts that were initially undercooled, a transition from lower eqlciaxed structure to an upper columnar structure is found in the alloy ingots. Columnar to equi-axed back to columnar transitions are observed in superheated alloy ingots, but no such equiaxed band is observed impure tin. The reproducible equiaxed band is associated with a thermal undercooling followed by a recalescence. This undercooling is <5"C, whereas the critical (maximum obtainable) under-cooling for both the pure tin and the alloys used is -20°C. A similar undercooling is observed at the same position in the pure tin ingots, although in this case no clear transition in structure can be seen. The structure of the pure tin ingots is either entirely columnar or mixed columnar-equiaxed. A consideration of the detailed thermal history of the ingots indicates that the ingot macrostructures are determined by the occurrence of a local therlnal undercooling in conjunction with nuclei multiplication and transport mechanisrris. GENERALLY it is found that a pure metal ingot solidifies so as to produce an entirely columnar structure. Frequently an alloy ingot is found to have a columnar outer zone and an equiaxed central portion. Early systematic work to examine the factors controlling the formation of the equiaxed structure was reported by Northcott&apos; who showed that, for copper alloys frozen unidirectionally with a given ingot practice, the alloying element influenced the length of columnar crystals and the extent of the equiaxed structure. Northcott showed that alloys with a wider freezing range more readily produced the equiaxed structure. The nucleation process can be important in producing equiaxed structures; frequently an alloy which readily solidifies with an entirely columnar structure will produce an entirely equiaxed structure when a nucleating agent is added to the melt.&apos; The formation of the equiaxed structure was attributed by Winegard and chalmers3 to the presence of constitutional supercooling; that is, a region of liquid in front of the growing solid could have a temperature below its equilibrium liquidus temperature. Thus, with a small enough temperature gradient in the liquid, it was suggested that the presence of constitutional supercooling may be sufficient to bring about the nuclea-tion necessary for the formation of an equiaxed structure. Although this explanation is plausible, and may be relevant in many ingots, Walker has described an experiment&apos; for which constitutional supercooling seems to be an unlikely cause of nucleation. A Ni-20 pct Cu alloy, repeatedly undercooled more than 50"C, was crystallized and found to show the typical colum-nar-equiaxed structure. The separation between the liquidus and the solidus for the alloy is 40°C. Thus, in this experiment the nucleation required for the formation of the equiaxed structure must have come about in some other way than by the nucleation catalysis constitutional supercooling hypothesis. Chalmers has suggested more recently5 that nuclei (in a typical ingot) are present immediately after pouring and are prevented from redissolving by the constitutional supercooling effect. More recently Uhlman, Seward, Jackson, and ~unt&apos; have shown direct evidence using ice and organic materials that freeze dendritically that the "remelt mechanism" may be an extremely effective crystal multiplication process during the freezing of ingots under conditions involving dendritic growth. JSlia" experimentally demonstrated the detachment of dendrite arms. chernov14 has analyzed the dendrite arm detachment process as a coarsening phenomena driven by the minimization of interphase area. Katta-mis and ~lemings" working with undercooled steel melts give evidence supporting this mechanism. Mechanisms of dendrite arm detachment such as those assisted by convection are believed to be the origin of the macrostructures obtained in this study. This study makes no attempt to distinguish the relative contributions of these mechanisms. The object of the present work was to obtain accurate temperature measurements during the solidification of an ingot and to correlate these measurements with the formation of equiaxed grains in the resulting ingot structures. Similar previous work is very limited. The measurements carried out by Northcott are neither sufficiently extensive nor sufficiently accurate for any interpretation. Plaskett and winegard7 carried out experiments on A1-Mg alloys in which they observed values of the temperature gradient, G, in the liquid and rate of freezing, R (for a given alloy solute content Co), at the transition from a columnar to an equiaxed structure. They reported that equiaxed crystals were produced at values of G/G approximately proportional to the solidus composition. Similar experiments using Pb-Sn alloys carried out by £111011" showed a linear relation between G/R and the solidus composition. However, the thermocouples were in the mold wall rather than in the melt and, in one case, ingot surfaces were examined. There is ambiguity in the meaning of the values of G and R measured in all these experiments. APPARATUS AND EXPERIMENTAL PROCEDURE Alloys were prepared by induction melting 99.999 pct Sn and 99.999 pct Pb to form a Sn-0.5 wt pct Pb alloy in air in a graphite crucible and casting into a cylindrical graphite mold 6 in. long, 1 in. in diarn , and with a & in. wall thickness. This mold was mounted on a copper base through which cooling water could be

Jan 1, 1968

By B. E. Terkelsen, B. J. Piearcey

A study has been made of the effect of unidirectional solidification on the creep behavior, stress-rupture properties, and thermal shock resistance of four nickel-base superalloys. The alloys Mar-MZOO, B-1900, IN 100, and TRW 1900 show improved rupture ductility and thermal shock resistance when tested with the columnar grains parallel to the major stress axis during test. The relative improvement in creep-rupture properties depends on the intrinsic strength of the alloy, a property which depends on composition, heat-treatnient, and crystallographic orientation. The data clarifies some of the factors affecting the properlies of the cast nickel-base superalloy. COMPONENTS designed for high-temperature use have, in recent years, been fabricated by precision casting techniques using nickel-base alloys developed specifically for use in the conventionally cast condition. This development was a result of both the increasing complexity of the component and the recognition that high-temperature strength was incompatible with workability. The use of castings can be economically favorable, but, more important, the recent complex designs of air-cooled gas turbine blades and vanes in alloys which possess the necessary high-temperature strength cannot be forged. Common modes of failure of high-temperature components are excessive creep, creep rupture, and thermal fatigue. If rupture occurs then the mechanism is usually by inter crystalline cracking along those grain boundaries oriented transverse to the major stress axis. In the stronger alloys, rapid propagation of intercrystalline cracks result in apparent premature failure demonstrated by the absence of third stage creep in a creep-rupture test and low rupture ductility. Tensile ductility shows a similar trend, that is, decreasing ductility with increase in strength. It is not surprising, therefore, that increases in creep strength have only been obtained with a loss in resistance to thermal shock, a property which shows a dependence on tensile ductility. VerSnyder and ~uard&apos; showed that the application of unidirectional solidification to a brittle Ni-Cr-A1 alloy both improved the rupture life of the alloy and increased rupture ductility. Since this casting method results in columnar grains, it appeared that the solution to the lack of ductility in nickel-base alloy components was the elimination of the source of failure, namely the transverse grain boundaries. This concept was recently developed2 to produce cast-to-size gas-turbine blades and vanes consisting entirely of columnar grains oriented parallel to the major stress axis of the component. Not only did the process impart increased rupture life and ductility to the components, but it also increased their resistance to thermal shock. During this development, the effect of unidirectional solidification on the properties of several alloys was investigated. The resulting data allows certain conclusions to be drawn regarding the factors affecting the creep and stress-rupture properties of the cast nickel-base superalloy and also its resistance to thermal shock. Detailed information was obtained on the alloys Mar-MZOO, B-1900, In 100, and TRW 1900. The composition of the alloys studied are shown in Table I. MATERIAL PREPARATION AND TESTING The conventionally cast alloys are cast as +-in.-diam bars in innoculated shell molds under conditions designed to maintain control of grain size. Unidirec-tionally solidified casting were produced in the form of 3-in.-diam ingots. Specimens from the latter were machined such that the axes of the columnar grains were parallel with the axis of the test bar, except in certain cases where the transverse properties of the material were being evaluated. The specimens were tested in an axial loading creep machine.&apos; Temperatures were measured with thermocouples, attached just outside each end of the gage length, to assure uniform temperature along the entire specimen. Chromel/alumel thermocouples were used up to 1800"F and Pt/Pt-10 pct Rh thermocouples above 1800"F. The specimen temperature was recorded and maintained within i2"F throughout the test. Creep extensions were measured automatically with extenso-meters attached to ridges on the specimen and recorded continuously using linear variable differential transformers and multipoint recording equipment. MICROSTRUCTURE The microstructures of transverse sections of the four alloys studied are shown in Figs. 1 and 2. Fig. 1 shows optical micrographs of the alloys, both in the conventionally cast and unidirectionally solidified conditions. Each alloy displays a cored dendritic structure, a distribution of MC carbide, and the presence of the y — y&apos; eutectic constituent.~ In the case of IN 100 and B-1900, Fig. 1 indicates that in these specimens the eutectic is degenerate. That is, it consists only of y&apos; pools indicating that the y constituent has been solutioned during the cooling period after solidification. The major effect of unidirectional solidification on the microstructures of the alloys is a tendency to promote a more dendritic form of MC carbide and an increase in dendrite arm spacing, both effects being a result of the slower solidification rate in the unidirectional solidification technique. V, lec tron micrographs of transverse sections of the four alloys in the two cast conditions are shown in

Jan 1, 1968

By G. B. Craig, B. Ramaswami

The temperature and strain rate dependence of the flow stress ratio and the stvain rate dependence qi the flow stress of annealed polycrystalline a zirconiur were determined over the temperature range 30 0" to 1000°K. Some evidence was found for strain aging and discontinuous flow in the temperature ranges 520" to 650°Kand650" to 760°K, respectively. The Cottvell-Stokes relationship was obtained when deformation occurred by twinning as well as slip. The flow stress ratio showed a strong dependence on temperature and strain rate above 800°K. The expevirnental evidence indicated that the rate-controllitzg mechanism for the deformation of a zirconium above 800°K was dislocation climb, and that the deformation was not thermally activated in the range 520" to 800°K. The stacking-fault energy of a zirconium was estimated to be about 250 ergs per sq cm. A knowledge of the temperature and strain rate dependence of the applied stress necessary to deform a crystalline solid is essential for understanding the thermally activated processes occurring during deformation.&apos; Several experimental techniques have been developed for studying these processes.273 One of the techniques is the deter mi nation of the strain rate dependence of the flow stress at constant temperature. In close-packed crystals, it has often been observed that the change in stress due to a change in the strain rate varies linearly with the flow stress, (~1,&apos; This relationship, known as the Cottre ll-Stokes law, is obeyed when deformation occurs by glide alone. However, when deformation occurs by twinning as well as glide, there is disagreement among different investigators on whether the Cottrell-Stokes law is observed. Whereas Thornton et ~1.~find departures from Cottrell-Stokes law when twinning occurs in copper, ~avis~ and sasinski? find that Cottrell-Stokes law is obeyed when deformation occurs by twinning as well as slip in cadmium and magnesium, respectively. One of the main objectives of this study is to determine whether the Cottrell-Stokes law is obeyed when deformation occurs by twinning as well as slip. The second technique that has been used extensively to study the thermally activated deformation of crystals is the determination of the ratio of the flow stresses, at identical dislocation structures and con-

Jan 1, 1968

By E. Miller, R. Geffken, K. L. Komarek

The thermodynamzc properties oJ liquid Cd-Sb alloys were investigated using the cell arrangement measurments were obtained every 2°C at a heating and cooling rate of 12°C per hr and at equilibrium every 2O0C frorn 500°C down through the stable liquidus. The S-shaped asCd US composition curve was used in the cotnposition regzon near Cd,Sb, to calculate a tempeerture-dependent inleraction coefficient from quasichemical theory. Rapid changes in a scd were observed at a transition temperature varying from 400" to 465°C depending on con/kosition. It could not be determined if the changes in aScd were discontinuous, but tlze composition dependeke of the magnitude of the change is indicative of a second-order phase transformation in the liquid. The values of the experimental changes in ASCd are in agreement with calculations from the slope of the transition temperature, using the concept that a second-ovdev phase transition occurs in liquid Cd-Sb alloys. II is suggested that the transformalion is associated with the formation of Cd4Sb3 molecules in the liquid. ThE structure of liquid alloys is the subject of many investigations. X-ray, resistivity, and thermody-namic data have been interpreted as indicating varying degrees of short-range order in the liquid in alloy systems forming inter metallic compounds. In general, the melting process is not a transition from an ordered to a completely disordered state, but some degree of order is retained in the liquid. Maximum ordering in the liquid state occurs close to the melting temperature of the compound and the arrangement of atoms becomes more random at higher temperatures. Of special interest in this respect is the Cd-Sb system. It is one of the few metallic systems which form both stable and metastable compounds when liquid alloys are cooled at normal rates. The stable system exhibits an intermetallic compound, CdSb, melting at 459"c.l A second compound, CdrSbs, has also been reported,&apos; melting close to this temperature. The metastable system has one compound, CdsSbz, melting at 420"c.I Resistivity measurements on liquid Cd-Sb alloys close to the liquidus temperatures have been interpreted in terms of a complex ordering behavior which changes rapidly with increasing temperature.3 The resistivity-composition curve is characterized by two maxima corresponding in composition to CdSb and CdsSbz. The resistivity-temperature plots show sharp breaks for alloys in the composition range of 45 to 70 at. pct Cd on cooling through a transition temperature close to the stable liquidus. Fisher and phillips4 investigated the influence of temperature and composition on the viscosity of liquid CdSb alloys. The viscosity of some alloys increases sharply on supercooling below the stable liquidus. A maximum in the viscosity-composition curve occurs at the composition CdSb. The thermodynamic properties of liquid Cd-Sb alloys have been investigated by Seltz and ~e~itt&apos; and Elliott and chipmane by the electromotive-force method and their results are in good agreement. However, these investigations were carried out at temperatures well above the liquidus temperatures of the alloys, and the temperature coefficients of the electromotive force, dE/dT, were obtained from experimental points for each alloy at a few temperatures considerably above the liquidus temperature. Scheil and ~aach&apos; investigated the thermodynamic properties of this system by the dew point method in the temperature range from about 100°C above the stable liquidus down into the supercooled liquid region. They reported several anomalies, i.e., the activity of a melt on heating differed from that on cooling, and the activity increased sharply in the limited temperature interval immediately above the liquidus temperature of the stable alloy, followed by a sudden decrease below the liquidus. Values obtained on heating and cooling were not in agreement. A reinvesti-gation of a few alloys by Scheil and Kalkuhl&apos; by the electromotive-force method failed to confirm these observations. The authors concluded that the anomalies were due to inhomogeneities in the starting alloys and they discarded their previous results. The present investigation was undertaken in order to obtain thermodynamic data close to the liquidus temperature and in the supercooled region where the anomalies were originally reported, employing the electro motive-force method. This method is quite precise and will most easily permit observations of small changes in activity and partial molar entropy with temperature. Measurements were taken every few degrees so that the dE/dT values could be calculated over the entire temperature range and small changes in the thermodynamic properties close to the liquidus temperature could be observed. I) EXPERIMENTAL PROCEDURE Specimens were prepared from 99.999+ pct Cd and Sb (Cominco). Surface oxide was removed by scraping and then melting the metals under vacuum and filtering through Pyrex wool. Appropriate amounts of the metals were weighed on an analytical balance to k0.1 mg, sealed in double Pyrex capsules under vacuum,

Jan 1, 1968

By S. J. Burns, W. W. Webb

The dislocation arrangements formed during unsteady propagation of cleavage fractures on (010) planes in LiF have been investigated by high-resolution etch-pit techniques and by X-ray diffraction topogvaphy. In impurity-hardened crystals, cracks propagating in any direction on (010) planes at velocities of about 103 cm per sec are usually accompanied by light plastic deformation which is enhanced wherever the crack is allowed to hesitate. Dislocations with [011] type Burger&apos;s vectors are often formed looped around the crack tip. They are dragged along with the crack tips leaving edge dislocations lying nearly parallel with the clearage surface about 5µ from it. These dislocations are easily overlooked since they may initially intersect with the cleavage surface infrequently and later may disappear from the crystals due to image forces during aging at room temperature. Although the plastic work associated with these dislocations is only comparable with the reversible (010) surface energy, an instability in crack propagation appears due to a limit of the velocity with which dislocations can be dragged along with the crack. Transition to a fully brittle nonplastic fracture mode occurs when the crack velocity exceeds the velocity with which dislocations can be moved by the stress field of the crack. TRANSITIONS between brittle and ductile modes of fracture appear to be common processes in the behavior of materials in which the flow stress is close to the stress at which brittle cracks can propagate. High-strength engineering alloys fit into this category and the transition from ductile to brittle modes of crack propagation may be associated with catastrophic failures in these important materials. The methods of theoretical mechanics indicate the geometrical conditions in which these processes may occur but the detailed mechanisms controlling the generation of dislocations in the initiation of the plastic mode and the process by which the loss of plasticity occurs on transition to the brittle mode are not yet clear. Since these mechanisms are not amenable to direct observation in engineering alloys we have chosen a semi-ductile alkali halide LiF as a model system in which to observe transition mechanisms between plastic and brittle modes of crack propagation. Cleavage cracks in this system are known to undergo a plastic-elastic transition at velocities between 103 to 104 cm per secl and dislocation configurations in LiF are amenable to study by optical-microscopic observation of dislocation etch pits2 and by X-ray diffraction topography.3 We have been able to identify a dislocation mechanism responsible for the transition from brittle to slightly plastic modes of crack propagation in LiF. A model based on this mechanism permits calculation of the critical crack-propagation velocity for this transition and indicates the importance of the stress dependence of dislocation velocity in determining the critical crack velocity. Of course, this model cannot be carried directly over to more complex materials but it is quite possible that its qualitative features are generally applicable. Dislocations intersecting fresh cleavage surfaces in LiF were reported by Gilman,4 by Forty,5 and by Wash-burn et a1.6 Such dislocations were construed to have been nucleated where the cleavage crack hesitated or stopped, near stress concentrators, such as cleavage steps, on the crystal face. The loci of such dislocations deposited On the cleavage plane in bands were called "stop lines" or "deformation zones". Gilman, Knudsen, and walshl measured the velocity of cleavage cracks in lithium fluoride by evaporating thin resistive strips on the crystal side and recording

Jan 1, 1967

By B. E. Sundquist

The various methods based on solution models for obtaining free energies of mixing from miscibility-gap data have been applied to a number of binary-alloy systems. For nine of these systems there exist experimental thermodynamic data that permit a comparison of the results to experiment. It was found that the method of van der Toorn and Tiedema almost invariably leads to results that are physically unacceptable and that vary drastically with small changes in the miscibility-gap parameters. The subregular solution model is found in all cases, except the Al-Zn, Fe-Cr, and Cu-Pb systems, to exaggerate the free energy of mixing by 30 pct or more. The model developed by Lumsden is found to give results that are often in excellent agreement with experiment and which exaggerate the free energy of mixing by no more than 30 pct. These results and others give evidence that the Lumsden treatment of the effect of unequal atomic sizes and of imperfect configurational randomness due to deviations of AB bond energies from the mean of AA and BB bond energies is adequate for most systems. ANALYTIC expressions are frequently proposed for the dependence on composition of the activities of the components of a solution. Because the development of solution theory is incomplete, these expressions contain parameters which must be determined by experiment. The measurement of activities is often difficult and consequently such measurements are less readily available than are measurements of phase equilibria which, under certain conditions, can also be used to evaluate these parameters. For example, suppose it is known that two structurally dissimilar phases, each of known composition, in an n-com-ponent system are at equilibrium at a given temperature and pressure. n equations can be set up in terms of these parameters expressing the equality of the chemical potential of each component in the two phases. In addition, one can write the Gibbs-Duhem equation for each phase that also contains these parameters. Thus, if these n + 2 equations contain n + 2 parameters, these parameters can be determined (at the temperature in question) from the phase diagram alone. If the average number of parameters in each expression for the activity of a given component in a given phase is V then there will be 2nV parameters involved. Equating 2nV to n + 2 shows that, for n + 2, V = 1. If the temperature dependence of each parameter were to be expressed in some explicit form one could use equilibrium conditions at a number of temperatures to increase V. The situation is much improved when the two phases in equilibrium are structurally similar. It can then be assumed that, stably or metastably, two phases will become one at higher temperatures. Thus the number of parameters involved becomes nV instead of 2nV. Hence, V = 2 for n = 2 using only one temperature. (It is implied here that the activity expressions used are valid over the entire composition range.) In this investigation only the equilibrium of two structurally similar, two-component phases (miscibility-gap systems) will be considered. The various proposed solution models will be applied to a number of these systems and the results compared with available experimental results. All of the analytic expressions that have been proposed for the free energy of mixing of a two-component system are of the form where ?Gmix is the free energy of mixing per mole of solution, N1 and N2 are the mole fractions of components 1 and 2, respectively, and f(Ni, T) is some function of composition and temperature. In the "ideal" solution model f = 0. In the "regular" solution model f = a constant. Since these two models permit only a symmetric equilibrium diagram they will not be considered further here. The simplest model that permits a nonsymmetric miscibility envelope is the so-called "subregular" solution model proposed by Hardy.1 This model gives where the Ci(T) are functions of temperature only. The same expression for f is obtained from the "linear a function" model proposed by Darken and Gurry2 and applied to miscibility-gap systems by Wriedt.3 This model requires that the a function defined by be a linear function of composition (yi is the activity coefficient of component i). This model is not purely hypothetical for it has been found2 to hold true for a number of systems. It is readily shown3 that the f(Nl, T) obtained from this model is of the form given in Eq. [2]. It will be noted that the subregular solution model contains only two parameters and hence both of them can be determined at any desired temperature below the critical temperature, Tc, for a miscibility-gap systems in the manner described previously. At T, the two constants can be determined by equating the second and third derivatives of ?Cmix with composition to zero. Another two-parameter model was proposed by Lumsden4 who set

Jan 1, 1967

By Rodney P. Smith

The diffusivity of carbon (0.1 wt pct C) in Fe-Nz alloys (0 to 100 pct Ni) has been determined for the temperature range 860° to 1100°C. As a function of nickel content, the diffusivity has a maximum near 60 pct Ni (the maximum diffusivity being about 1.3 times that in the absence of nickel); the activation energy has a maximum between 40 and 50 pct Ni and a maximum between 80 and 90 pct Ni. The difference between the minimum activation energy and that in iron is about 3000 cal pev g-atom; Do has a minimum between 40 and 50 pct Ni and a maximum between 80 and 90 pct Ni. The results cannot be rationalized by an approximate thermodynamic treatment. THE diffusivity of carbon has been determined in a number of iron alloys over a limited concentration range. It seemed desirable to investigate a system which allows an extended range of alloy composition within a single-phase region. The Fe-Ni system is ideal in this respect, in that all alloys from 100 pct Fe to 100 pct Ni are fee in a convenient temperature range.&apos; The carbon diffusivity was determined by a decar-burization method. The experimental procedure was identical with that used to determine the diffusivity of carbon in y Fe-Co alloys.2 The experimental data are given in Table I. A small correction (order of a few percent) has been made to the measured carbon loss to correct for the carbon lost from the ends of the cylinders.&apos; Since the diffusivity of carbon varies with carbon content the measured diffusivity is an average value for a carbon content between zero (surface) and that at the center of the sample at the end of the decarburization periods. In making the correction in D to 0.1 wt pct C it is assumed that the measured D corresponds to the arithmetical mean of the carbon content at the surface and at the center of the sample at the end of the decarburization period.3 Since this correction is small (<4 pct in D) and since for our decarburization times the changes in carbon content at the center of the sample was small the mean carbon content could have been taken as half the initial value. It is further assumed that the change in D with carbon content for the alloys is the same as that for the diffusion of carbon in iron. From the data of Wells, Batz, and Mehl4 and of smith5 the correction of D from the mean carbon content to 0.1 wt pct C is 0.3 (0.1 - mean wt pct C). The results for iron are given in Ref. 2. Within the experimental error log Do.l%C for each alloy is a linear function of 1/T; the constants for the equation determined by the method of least squares are given in Table I. The deviations of the experimental points from the least-squares line are of the order of 2 pct in D. A comparison of our results for the diffusivity of carbon in nickel with those of other investigations is shown in Fig. 1. The lower curve in Fig. 1 is a linear extrapolation of values calculated* from the equation of Diamond6 for the relaxation time (temperature range 100° to 500°C). The results indicate a small increase in the activation energy over the temperature range 100° to 1400°C; however, it is difficult to say whether the change in Q is real or experimental error. Certainly the change in Q is less than the variation of 5 kcal per g-atom in the diffusivity of carbon in a iron.6 The experimental data for all the alloys are plotted in Fig. 2. As a function of nickel content the diffusivity has a maximum near 60 wt pct Ni at all temperatures investigated and possibly a minimum between 80 and 90 wt pct Ni for temperatures below 1000°C. The activation energy, Q, and log Do are plotted as a function of the nickel content in Fig. 3. Due to the limited temperature range of our experiments neither Q nor Do can be determined precisely; the activation energies appear to be consistent to ±0.3 kcal per g-atom; however the deviation from the absolute values may be considerably larger, see Table II. The Do values probably have little significance. The solid line for Do in Fig. 3 represents the values required to reproduce the experimental values for D when Q has values represented by the upper solid line The diffusivity of carbon may be expressed in terms of the mobility B22, the activity coefficient r2,

Jan 1, 1967

By Klaus Schwerdtfeger

The rate of formation of silicon monoxide from silica spheres has been measured at 1500°C in H2, H2-H2O, H2-He, H2-Ar, and CO-CO2 gas mixtures. Indications are that in the hydrogen-containing gases the reaction rate is mainly determined by convective diffz~sion. In the CO-CO2 mixtures the rate approches a constant value which is independent of sphere diometer (and gas velocity). This suggests that a surface reaction becomes rate controlling in CO-CO2 gas. WHENEVER silica is exposed at elevated temperature to a strongly reducing atmosphere there occurs, inevitably, a volatilization of silica by the formation of gaseous silicon monoxide. Because of the importance of this reaction in metallurgical processes and laboratory experiments, its kinetics were studied in the present work. EXPERIMENTAL The spheres made of vitreous silica were suspended by a molybdenum wire in the hot zone of a gas-tight high-purity recrystallized alumina furnace tube of 3.1 cm internal diam and 100 cm length. Molybdenum wire resistance heating was used. A purified H2, H2-H2O, H2-He, H2-Ar, or CO-CO2 gas mixture was passed through the tube, from top to bottom. The amount of silicon monoxide formed was determined by weighing the silica balls before and after the experiments. The silica balls were made from commercially available translucent fused quartz glass. In experiments with hydrogen-containing gases the silica stayed vitreous during the experiment, whereas in experiments with CO-CO2 mixtures, which were performed over longer times, the balls were always crystallized to cristobalite (as determined by X-ray examination) at the surface. Constant-pressure head capillary flowmeters were used to control the composition of H2-He, H2-Ar, and CO-CO2 gas mixtures. The oxygen and water vapor were removed from the gases containing hydrogen by passage through columns containing platinized asbestos (450°C) and an-hydrone. The CO was purified from O2 and CO2 by passing it through activated copper (200°C) and through ascarite. The H2-H2O gas mixtures were prepared by passing purified Hz through a mixture of oxalic acid dihydrate and anhydrous oxalic acid held at a constant temperature in a water bath. The equilibrium water vapor pressures of oxalic acid dihydrate-anhydrous oxalic acid mixtures were taken from the available data.1 The furnace system was checked for sufficient gas tightness at regular intervals. As an additional check, the H2O and CO2 contents were measured in the exit gas and were found to agree closely with the metered contents when H2-H2O or CO-CO2 mixtures were used. When purified H2 was used, H2O pressures found in the exit gas were always below 0.1 mm Hg. These contents originate either from an incomplete reoxidation of silicon monoxide in the cold part of the furnace or from small leaks which cannot be avoided. If the latter is the case, such small uncontrolled H2O contents decrease the partial pressure of SiO in equilibrium with SiO2 by less than about 7 pct, which is considered small in comparison to other experimental uncertainties. The temperature of the furnace was controlled automatically in the usual manner. The reported temperature was measured with a Pl-Pt/l0pct Rh thermocouple and was accurate to ± 5°C. TRANSPORT-CONTROL LED RATE OF REDUCTION The gaseous convective diffusion from the surface of a sphere can be predicted from the semiempirical relationship obtained by Ranz and Marshall2 in a study of the evaporation of water and benzene drops in air. The following equation applies:

Jan 1, 1967

By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of liquid Mg-Ge alloys have been determined between 1000°and 1500°K by an isopiestic method. Germanium specimens, heated in a temperature gradient and contained in covered graphite crucibles of special geometry, were equilibrated with magrtesium vapor in closed titanium tubes. The crucible design allowed free access of magnesium vapor to the samples during the equilibration to form alloys of magnesium and germanium, but prevented magnesium losses from the crucibles on quenching the titaniuin tubes to terminate the experimental runs, thus preserving the equilibrium alloy compositions. The activities and partial molar enthalpies of magnesium and the integral thermodynamic properties of the system were calculated from the experimental data. THE Mg-Ge phase diagram&apos; shows one congruent melting compound, Mg2Ge, of essentially stoichio-metric composition, two eutectics, and very limited terminal solid solubilities. Very little information is available on the thermodynamic properties of the Mg-Ge system. The free energy of formation of Mg,Ge was recently deter-mined2 by a Knudsen cell technique in the temperature range 610° to 760°C. The standard enthalpy of formation of Mg,Ge was measured calorimetrically by Bever and coworkers.3 The present study was undertaken as part of a general investigation of the thermodynamic properties of the homologous series of Mg-Group IVB systems, i.e., Mg-Pb,4 Mg-Sn,5 Mg-Ge, and Mg-Si. An isopiestic technique was used which was developed by the authors5 for investigating the thermodynamic properties of liquid Mg-Sn alloys. Specimens of the nonvolatile component, contained in covered graphite crucibles, are heated in a temperature gradient in an evacuated and sealed titanium reaction tube, and equilibrated with magnesium vapor of known pressure. The method employs crucibles of special geometry which preserve the high-temperature equilibrium composition of liquid alloys having a highly volatile component such as magnesium on termination of the experimental runs by quenching the crucibles to room temperature. EXPERIMENTAL PROCEDURE First reduction germanium of 99.999+ pct purity (Eagle-Pitcher Co., Cincinnati, Ohio) and 99.99+ pct magnesium metal (Dominion Magnesium Ltd., Toronto, Canada) were used. The graphite crucibles were machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non-reactivity of graphite with germanium at the temperatures used in this study had been previously established by Scace and Sleck.6 The experimental procedure has been previously described in detail.5 The selection of a particular crucible geometry for a run was determined by a combination of imposed experimental conditions, the principle being that more tightly covered crucibles were required to preserve alloy compositions during quenching when higher magnesium pressures and higher specimen temperatures were used. Depending upon the composition range of the equilibrated alloys the source of the magnesium vapor was either pure magnesium or a two-phase mixture of Mg2Ge + Ge-rich liquid of known magnesium pressure. The experimental runs can be divided into the following three groups on the basis of crucible geometry and magnesium source material. Crucibles with Small Holes and Pure Magnesium Reservoirs. The crucible dimensions were identical to those of the Mg-Sn investigation5 except that the hole diameters were reduced to 0.010 in. because of the higher temperatures and higher magnesium pressures involved in the Mg-Ge system. During an equilibration run, magnesium vapor diffused from the reservoir to each specimen through the small holes, one drilled through the crucible lid and two others drilled through graphite baffles positioned vertically inside the crucible between the lid hole and the specimen. Since the magnesium pressure was high, i.e., in the range 117 to 277 Torr, during the equilibration time of approximately 24 hr, equilibration was not impeded by these holes. A specimen composition at equilibrium was fixed by the relative temperatures of the specimen and the reservoir, and by the thermodynamic properties of the system. Upon brine quenching the titanium reaction tube to end a run the vapor pressure of magnesium above the liquid alloys decreased exponentially with decreasing temperature, and the small cross-sectional areas of the holes (4.9 x 10"* sq cm) drastically reduced magnesium losses from the crucibles. Because of its low vapor pressure, germanium losses from crucibles during a run were at most 0.2 mg for pure germanium and correspondingly less for the alloys. This crucible geometry satisfactorily retained the equilibrium alloy compositions on quenching for magnesium-rich (from 3 to 33 at. pct Ge) alloys provided their temperatures were below the melting

Jan 1, 1967

By F. A. Crossley

The titanium-rich end of the Ti-A1 system has been investigated up to 35 at. pct A1 (23 wt pet). One conzpound Ti3Al was found to occur between primary a and TiAl. It is ordered hcp with DO19 structure, it has virtually no solid-solubility range, and it has a closed maximum at about 875°C. OIL either side of the compound are a +Ti3Al two-phase fields. The limiting a1uminum solubility in primary a at the titanium-rich end is indicated to be 7.5 at. pct A1 (4.4 wt pet) at 550°C and about 6.8 at. pct Al fl wt pct) at 500°C. Quenching alloys from above the a + Ti3Al two-phase field produces the following structures with respect to alloy composition: Up to 13 at. pct A1 (7.8 wt pet), a solid solution; from 15 to 18 at. pct A1 (9 to 11 wt pct), shear transformation product or martensite; from 19 to approximately 30 at. pct (11 to 19 wt pet), submicro-scopic coherent Ti3Al in an a malvix. The twin hcp phase fields reported in the literature are the result of nonequilibrium corzdztions. Ti-A1 alloys, once partitioned by dwelling- in the a + ß phase field during either hot working or heat treatment, are extremely difjicult to homogenize at temperatures below 1000°C. Such partitioned alloys exhibit the characteristics or symptoms of two-phase materials, and may be said to suffer the "twin-phase syndrome". THE earliest investigations of the Ti-A1 system by Ogden et al.1 and Bumps et al.2 reported wide solubility of the primary solid solutions. Aluminum was reported soluble in the low-temperature allomorph to the extent of 37 at. pct (25 wt pct), and the first intermediate phase was reportedly TiA1. Somewhat later Kornilov et al.3 reported a similar diagram with phase boundaries displaced towards lower aluminum contents and higher temperatures. Beginning about this time (1956) reports in the literature made it very clear that one or more intermediate phases occurred at lower aluminum contents than TiAl.4-17 These reports included five major investigations of the titanium-rich end of the Ti-A1 diagram.4,12,14,16,17 Three of these diagrams show two two-phase fields below 37 at. pct Al, while two of them show a single two-phase field. The existence of the phase Ti3A1 is firmly established and is included in each of the diagrams, except one—that of Sato and Huang.12 The new phases are reportedly hcp and differ from primary a only slightly when disordered, and when ordered the "a" parameter is approximately one,4,12,15 two, 6-10,13,14 or four14 times that for primary a. Beyond this, however, the diagrams are remarkable for their lack of agreement. Two tacit assumptions are usually made in phase-diagram determinations of metal systems. These are: 1) equilibrium anneals bring the alloy to equilibrium or to indistinguishable closeness to it, and 2) equilibrium conditions established at elevated temperatures are either "frozen" by rapid quenching for evaluation at room temperature, or quench-transformation products are recognized as such. In the current investigation evidence was obtained that over substantial composition ranges neither of these two conditions was met in any of the more recent major investigations. I) MATERIALS, METHODS, AND TECHNIQUES The alloys of this investigation were prepared by nonc on sum able electrode arc melting. Materials used in the preparation of the alloys are summarized in Table I. The investigative tools employed were: optical and electron microscopy, differential thermal analysis (DTA), disatometry, X-ray diffraction, electron diffraction, and resistometry. Alloys for microscopic and X-ray investigations were prepared as 15-g melts. Alloys containing from 7 through 11 at. pct A1 were hot-rolled out of a furnace at 900°C, from 12 through 15 at. pct out of a furnace at 1000°C, and from 16 through 18 at. pct out of a furnace at 1125°C. Alloys containing more than 18 at. pct A1 could not be hot-rolled. The ingots were covered with Markal coating prior to hot rolling to minimize atmospheric contamination. After hot rolling, alloys containing up to 15 at. pct A1 were ground and pickled to remove 7 mils from each surface; alloys containing 16 and 18 at. pct A1 were skinned to a

Jan 1, 1967

By R. S. Rickard, M. C. Fuerstenau

Anodic polarization curves for iron dissolution and cathodic polarization curves for copper deposition and ferric and hydrogen ion reduction were studied. These results were used to predict the relative rates of the reactions: The rates of the first two reactions were found to be first order with respect to the reacting ion, and the rale-controlling step was diffusion of the ions to the callzode surface. The rate of hydrogen ion reduction in an oxygen-free solution is dependent on the reciprocal of the square root of the hydrogen ion activity. In solutions containing oxygen, the rate of hydrogen reduction becomes dependent on the square root of the partial pressure of oxygen. At equal concentrations copper precipitation occurs about twice as fast as ferric ion reduction. In an air-saturated solution containing 0.01 M cupric ion at pH 2, the rate of hydrogen ion reduction zs about 10 times slower than that of copper precipitation. At pH values below 3, the rate of hydrogen reduction in oxygen-free solutions is very slozu. COPPER cementation has been utilized industrially for many years as a means of recovering copper from aqueous solutions. There are many different types of cementation plants, but all simply provide a means of contacting iron with relatively dilute copper solutions. In the past little or no attention has been paid to rates or mechanisms of the reactions involved. As a result, this and other studies&apos;-3 have been undertaken recently to establish the important parameters in this system. The reactions involved in copper cementation by iron are: Since transfer of charge is involved in every case, these reactions should be considered from an electrochemical point of view. In any electrochemical system involving electrolytic conduction, passage of electrons necessitates ion transfer to the respective electrodes according to Faraday&apos;s law. The current in the system will be proportional to the rate of ion transfer, and, therefore, when the current in the galvanic cell is known, the rates of the reactions involved can be determined. Galvanostatic electrode measurements5" are applicable for these electrochemical studies, in that with this technique polarization curves (current density vs electrode potential) are established by impressing a constant current through an electrode and measuring the electrode potential. Once the current density, electrode potential, and reacting area are known for each reaction in this cementation system, the rates of the iron-consuming reactions can be determined. EXPERIMENTAL MATERIALS Several metal electrodes were used in this investigation; they are shown in Table I. Solutions were made with reagent-grade salts and conductivity water. Air, nitrogen, and oxygen were employed. All of these gases were saturated with water and degreased prior to use. EXPERIMENTAL PROCEDURE The experimental work was divided into two general areas. The first area involved galvanostatic measurements, which were used to determine the rates of reactions as a function of various parameters. The second area comprised actual cementation experiments to check the rates predicted from the electrode measurements. Galvanostatic Electrode Experiments. Polarization curves were obtained using a standard galvanostatic technique5&apos;= with the apparatus shown in Fig. 1. The various electrode polarization experiments were run the same way except for changes in solution composition, polarity, and type of measured electrode. The general procedure involved the following steps: 1) a solution was made 0.5 M in sulfate ion and to the desired cation concentrations; this solution was placed in a constant-temperature bath and saturated with the desired gas; 2) the electrodes were cleaned and placed in the electrode holder; 3) the previously cleaned apparatus was assembled and immersed in a constant-temperature water bath (temperature controlled to ± 0.05"C); 4) the electrode was then positioned; the solutions were introduced, and the polarization meas-

Jan 1, 1969

By P. S. Kotva

Dislocation substructures in superalloy matrices of varyzng co)npositions have been studied. In general, it has been found that the alloys can be classified into &apos;&apos;high", &apos;&apos;medium", and "low" stacking fault energy classes based on the type of dislocation substructure observed in the matrix and that the substructure can be correlated to the stacking fault energy. The effect of different types of dislocation substructure and dislocation reactions on the intragranulur precipitation of carbide phases has been studied. In a Ni-Cv-Mo-Fe matrix, precipitation of MC carbides in association with stacking faults has been observed. In most superalloys, solid-solution strengthening and precipitation hardening are the chief mechanisms employed to achieve strength. The latter contribution to strength is usually achieved by the precipitation of / in certain wrought alloys. Insufficient attention has been given to the problem of obtaining strength in su-peralloys by controlling precipitation of carbides on imperfections within the matrix. The present work was undertaken to investigate the dislocation substructure in various superalloy matrices, to study the effect of such substructure on subsequent precipitation of carbides in the matrix, and to investigate whether certain modes of precipitation of carbide phases found in austenitic stainless steels2"4&apos;6 would occur in nickel-base alloy matrices with dislocation substructures of the same type as those found in austenitic steels. 1) EXPERIMENTAL TECHNIQUES Five-pound heats of the various alloy compositions reported here were vacuum-cast. The ingots were given light deformation by rolling to break up the as-cast structure and then homogenized for 24 hr. HASTELLOY alloy X (nominal composition: Ni-2OCr-17Fe-8Mo-0.05C) was homogenized at 2150°F and In-cone1 625 (nominal composition: Ni-20Cr-5Fe-8Mo-3.5Cb-0.05C) was homogenized at 2280°F. Fabrication of 0.004-in. sheet was achieved by cold rolling with intermediate annealing treatments being carried out at the same temperature as those used for homogeniza-tion. Each solution anneal was followed by quenching. The aim of this procedure was to redissolve as much of the primary carbide phase as possible. Samples of the 0.004-in. sheet were cut and encapsulated in quartz capsules and then heat-treated in the tube furnaces. Thin foils were prepared using an ethanol-10 pct perchloric acid bath at 32°F and at a voltage of 22 v. A "window" technique was employed. Observations were made on a JEM-7 electron microscope operating at 100 kv. 2) EXPERIMENTAL RESULTS a) Types of Dislocation Substructure. Fig. 1 shows a schematic correlation between stacking fault energy, SFE, and the type of dislocation substructure observed in various matrices of nickel- and cobalt-base alloys. A precise quantitative determination of stacking fault energy is not implied in the figure but the correlation between stacking fault energy and the type of dislocation substructure obtained allows alloys to be divided into three classes in analogy with the classification employed by Swann and ~uttin~&apos; for binary alloys of copper. Class I alloys are associated with a "high" SFE and show a cellular substructure of dislocations as typified by the micrograph of a thin foil of pure nickel deformed 4 pct at room temperature in Fig. 2. With decreasing SFE the tendency toward cell formation is lessened and dislocations tend to be arranged in coplanar groupings. Examples of this class of alloys with "medium" SFE are provided by the mi-crostructure of solution-heat-treated, quenched, and deformed thin foils of HASTELLOY alloy X, "Waspaloy" (prior to any aging), and Inconel 625. Fig. 3 shows a thin-foil micrograph of an alloy of Inconel 625 composition, solution-heat-treated, quenched, and deformed 5 pct at room temperatures. No evidence of any cell structure can be obtained in materials of "medium" stacking fault energy, Fig. 3, even after severe deformation. The stacking fault energy of the alloy shown in Fig. 3 is, however, not low enough to make the dissociation of dislocations visually obvious. As stacking fault energy decreases further, with successive addition of solute in the matrix, there is an increased tendency toward dissociation of dislocations and cross slip becomes progressively more difficult. Eventually, when the stacking fault energy is "low" enough, complete dissociation of dislocations is seen to occur as shown in Figs.

Jan 1, 1969

By J. M. Oblak, W. A. Owczarski

A cellular appearing recrystallization product formed by annealing a cold-worked nickel-base super-alloy at 1800°F has been studied by electron nzicroscopy. Prior to deformation, an equilibrium micro-structure of fcc matrix y and cuboidal ,,&apos;, Ni (Al, Ti), precipitates of CuzAu structure had been established by an age at 1825°F. The strain-free recrystallization cells consist of very large rodular y&apos; particles in a y matrix. They precipitate is oriented and coherent both before and after recrystallization. The results showed that y&apos; coarsening accompanies recrystallization at 1800°F. However, it does so as a secondary effect and does not necessarily take place at lower temperatures. The structural similarity of this reaction to cellular precipitation in other systems indicates that lattice strain may also play a significant role during some cellular precipitation reactions. THERE have been numerous microstructural investigations of recrystallization in single-phase materials but two-phase systems have received much less attention. The second phase can either remain inert or be altered along with the matrix during recrystallization. If the second phase is an oxidelm3 or a relatively inert pre~ipitate,~, recrystallization is retarded when the interparticle spacing is less than 1 p. Prior to the onset of recrystallization, these materials show a well-polygonized substructure with the subgrain size limited by the interparticle spacing. Since recrystallization by the motion of preexisting grain boundaries6 is not observed, retardation has been related to particle pinning of the subboundaries. This pinning prevents coalescence&apos; or growth8 of subgrains to a critical size (formation of a high-angle boundary) necessary to initiate recrystallization. In a material such as a nickel-base superalloy both y matrix and y&apos; precipitate are altered by the recrystallization reaction. Haessner et al.&apos; studied the recrystallization of a cold-rolled Ni-Cr-A1 alloy by electron microscopy. The material was initially cold-rolled in the supersaturated condition. upon annealing at 750°C, immediate precipitation of 7&apos;occurred. Presence of this 7&apos; greatly retarded the onset of recrystallization which eventually took place by the development of randomly oriented, strain-free grains. The original •/ was dissolved at the recrystallization interface and reprecipitated as oriented, coherent par-tiles in the new grain. Recrystallization caused a refinement of .)&apos; particle size. Recently ~hillips&apos;&apos; investigated recrystallization of Ni-12.7 at. pct Al. Reduction by cold rolling presumably elongated the p&apos; precipitate into lamellae that remained coherent with the matrix. After recrystallization at 600" to 750°C, there was no unusual change in y&apos; particle size al- though there was a tendency toward clustering along the prior rolling direction at 750°C. Above 750°C, the recrystallized grains were generally free of precipitate. Studies in the somewhat analogous Cu-3.23 wt pct CO" and Cu-2 wt pct&apos;2 systems demonstrated that the coherent cobalt-rich fcc precipitate in these alloys obstructed softening, initiation, and completion of recrystallization. The precipitates were deformed into lam~llae during rolling and those of diameter less than 250A remained coherent. Recrystallization took place by the growth of new grains into the recovered or poly-gonized material. In the first study," both matrix and precipitate reoriented in the same manner upon passage of the recrystallization interface. There was no change in particle size or morphology. Tanner and ~ervi,~ on the other hand, observed that motion of the recrystallization fronts was strongly hindered by the pinning action of coherent precipitates in the deformed material. Particles in contact with a pinned boundary coarsened and coalesced leaving a denuded zone in the unrecrystallized region. When the number of pinning points was sufficiently reduced by coalescence, the boundary swept past these particles and through the denuded zone. The authors1&apos; considered this as a variation of discontinuous precipitation with both chemical driving force and deformation strain energy contributing to recrystallization. Preliminary observations by the present authors had revealed that recrystallization in Udimet 700, a nickel-base superalloy, occurred in an entirely different manner. Optical metallography showed that the recrystallized product formed as cellular colonies containing coarse y&apos; particles elongated in the direction of cell growth. In this investigation the structural features of this reaction were investigated by transmission electron microscopy. EXPERIMENTAL PROCEDURE As-received I$-in. rounds of Udimet 700* were (wtpct) 18.4 15.2 4.95 4.42 3.43 0.06 0.031 0.14 Bal. solution-annealed for 4 hr at 2150" and then fast air-cooled. An initial y-~&apos; structure was established by a 4-hr age at 1825°F followed by a fast air,cool. Essentially the equilibrium volume fraction of ?&apos; at 1825°F is precipitated within 4 hr. Microstructural examination showed no measurable increase in the amount of precipitate after longer aging times. Deformation consisted of swaging to 52 pct RA with 6 pct reduction per pass at room temperature. To reduce the precipitation potential to a negligible amount, recrystallization anneals were conducted at 1800"~ (982"~). Microstructures were investigated by optical and transmission electron microscopy. To prepare foils for electron microscopy, the material was first sliced into 30-mil slabs parallel to the swaging direction. Discs were dimpled and electrolytically cut from

Jan 1, 1969

By George V. Smith, Daniel E. Sonon

Various mechanical properties of the Ni-Co-C alloy system were investigated to delineate the strengthening effect of carbon. Carbon concentration, cobalt concentration, vain size, temperature, and strain rate were varied so that thermal activation analysis and the Hall-Petch analysis could be used to evaluate the strengthening effect of carbon. Increasing carbon increased the strength of nickel and a Ni-60 pct Co alloy , with the effect becoming more pronounced at lower temperatures. Yield stress depended linearly on carbon concentration in nickel, but it depended on the square root of carbon concentration in the Ni-60 pct Co alloy. The Hall-Petch slope of nickel increased with carbon concentration; however, that of the Ni-60 pct Co alloy did not. The yielding behavior of these alloys was sensitive to composition, grain size, and temperature. Cobalt eliminated serrations in the flow curve of carbon-containing nickel at 300&apos; and weakened them severely at higher temperatures. Pairs, or clusters, of carbon atoms appear to be responsible for the observed strengthening behavior. FLINN&apos; conducted several experiments with carbon in nickel in an effort to provide information on the strengthening effect of interstitial impurities in solid solution in fcc metals and alloys. Strengthening which increased with decreasing temperature led him to conclude that carbon causes Cottrell locking in nickel. Fleischer2 analyzed Flinn&apos;s data and calculated that the strengthening effect of carbon in nickel was smaller by a factor of fifty than the strengthening effect of carbon in a! iron. Fleischer2 termed the magnitude of strengthening of carbon in nickel "gradual" and that of carbon in a! iron "rapid". He attributed "gradual" hardening to hydrostatic strains and localized changes in modulus of elasticity around solute atoms, whereas he attributed "rapid" hardening to tetragonal strains around solute atoms. Sukhovarov et a1.3-7 reported strain aging and serrated plastic flow in nickel, both of which they attributed to the presence of carbon. Serrated plastic flow has been rationalized by a process involving a series of dislocation pinning and multiplication steps.8, This process is more probable when screw dislocations are strongly pinned. Screw dislocations cannot be pinned by pure hydrostatic forces from the symmetrical strains of an interstitial impurity in an fcc lattice, except for small, second-order effects. However, they might be pinned by localized changes in modulus of elasticity around solute atoms,&apos; by the pinning of the edge components of the partial dislocations of an extended screw dislo~ation,&apos;~ or by clustered groups of solute atoms whose net elastic stress field is unsymmetric. The purpose of the present work was to investigate various mechanical properties of the Ni-Co-C a1loy system which are sensitive to pinning effects in order to delineate the specific pinning mechanism of carbon. Carbon concentration, grain size, temperature, and strain rate were varied so that thermal-activation analysis and the Hall-Petch analysis could be used to evaluate the pinning mechanism. Cobalt was added to lower stacking fault energy so that the number and extension of split, screw dislocations would be increased in order to test the possibility of pinning by carbon at extended screw dislocations. EXPERIMENTAL PROCEDURE Nickel and cobalt (both 99.98 pct-. pure) were melted with graphite in stabilized zirconia crucibles and cast at lo-&apos; Torr to form Ni-C and Ni-60 pctCo-C alloys. Two ingots were heated to 1250°C and were forged to 1-in.-sq bars. These bars were machined to 4-in.-round bars, and then swaged cold to 0.144-in. -diam rods. Reductions in area of approximately 75pct were used with intermediate anneals at 900°C for 1 hr. The carbon content of batches of 0.144-in.-diam rods from each ingot was reduced to two levels by annealing 5-in. lengths in palladium-purified, dry hydrogen at 1100°C for 25 and 100 hr. The remaining material from each ingot was annealed at 10"5 Torr for 1 hr at 1100"~. These treatments gave a total of three carbon levels for both the nickel and the Ni-60 pct Co alloy. The 0.144-in.-diam rods were swaged to 70-mil wire, cut into test specimens, and then re crystallized at lom5 Torr in capsules for 1 hr at temperatures ranging from 760" to 1050" ~. The capsules were broken and the specimens were immediately quenched into water. Average grain size was measured using Hilliard&apos;s method of circular intercepts." Annealing twin boundary intercepts were counted in addition to grain boundary intercepts to establish an average grain size. Average grain sizes ranged from 5 to 140 p depending on the cobalt concentration and re-crystallization temperature. Tension tests were made in duplicate at various temperatures at a crosshead speed of 8.34 x 10"4 in. per sec with an Instron Universal Testing Machine. Specimens of 1-in. gage length with soldered ball ends were used at atmospheric and cryogenic temperatures. Pinch grips were used on specimens at elevated tem-

Jan 1, 1969

By N. J. Grant, Per Knudsen, J. T. Blucher

The fatigue behavior of three SAP alloys was studied in ternzs of strain rate and temperature, at high strains. The k values in the modified Manson-Coffin equation, Nk4 = C, were less than 0.5 under all test conditions, and change with strain amplitude for the lower-oxide alloys at about 2 pct strain. Lowest k values were near 0.25. Strain rate had no effect on life at 80 F, but had an increasingly greater effect with increasing temperature above 500". Life decreased with decreasing strain rate, above 500"F, and with increasing temperature. Ductility at fracture in a tension test was indicated to be an important factor in determining 1ife in these big+-strain tests with the SAP alloys. INEVITABLY, in the course of mechanical tests at elevated temperatures, particularly if significant time at temperature is involved, there are large changes in structure; these changes make it difficult to relate behavior patterns over ranges of temperature or strain rates at high temperatures. Such changes are to be expetted in low cycle fatigue at low strain rates and high temperatures. Accordingly, it was of great interest to examine the low cycle fatigue behavior of SAP / an aluminum oxide dispersion-strengthened aluminum, a type of alloy which had shown unusual structure stability to temperatures as high as 1000" to 1150°F and resisted recrys-tallization essentially to the melting temperature.&apos;j3 Since the matrix is pure aluminum, there are no complications of averaging, agglomeration, or phase solution. It was also desirable to check the Manson-Coffin equation4?&apos; for the SAP alloys, namely N~E~ = , where ep is the total plastic strain amplitude, k and C are constants, and N is the number of cycles to failure. Here, too, was an opportunity to check the roles of temperature and strain rate with a very stable material. Tavernelli and coffin6 had concluded that k had a value of about 0.5 for many alloys and C was equal to ~/2, where E is the fracture ductility determined from a static tension test. The results were obtained from low-temperature tests where creep and diffusion processes are unimportant. Manson7 found k = 0.6 fitted his data reasonably well; however, in later analyses of a large amount of low cycle fatigue data generated at room temperat~re@"~ he found k to vary from 0.6 for short lives to 0.21 for long-life fatigue tests. In the latter studies,89g Manson separated the total strain range into elastic and plastic components when he found that k was influenced by the nature of the strain. The use of EL (total strain) instead of EP (total plastic strain)4&apos;5 makes a difference in the resultant k value. The ratio of changes with temperature, strain rate, and strain; further, there are the problems in the determination of the elastic strain. Based on these considerations, and the improved fit of points in a plot of by Wells and Sullivan,&apos; is also utilized in these studies. Anderson and wahl,14 using commercial 1100 aluminum, and Blucher and Grant,15 using 99.99 pct pure aluminum, found an increase in life with increasing test temperature. Anderson and Wahl were the first to report low cycle fatigue results from SAP materials. With increasing temperature, the role of strain rate becomes more important. In this regard, care must be exercised to differentiate between frequency (wherein strain rate may vary from zero to a maximum in each cycle, sinusoidally, for example), and constant strain rate, as used in the present study, in a saw-tooth type cycle; in the latter case, the frequency is not specified but can easily be calculated from the strain and strain rate data. It has generally been found that life in low cycle fatigue tests decreases with decreasing frequency16 or with decreasing strain rate at elevated temperatures.15 Coffin,17 reviewing Eckel&apos;s work,16 also reported that k increased with decreasing frequency for acid lead, yielding values from 4.0 at a frequency fo 6.6 cycles Per day to 1-46 at a frequency of 7440 cycles per day; the value of k decreased to 0.58 at a frequency of 2.38 x lo6 cycles per day. EXPERIMENTAL PROCEDURE Three SAP alloys, of two nominal compositions, were tested. Alcoa supplied XAP 005 as 2-in.-diam extruded bar, of nominal composition A1-7 wt pct A1203. The Danish Atomic Energy Commission supplied SAP 930 (A1-7 wt ~ct Ala3) and SAP 865 (A1-13 wt pct Al&) manufactured by Swiss Aluminium Ltd., in the form Of $-in.-diam extruded rod. Metallographic comparison of the structures of XAP 005 and SAP 930 showed the former to have a more uniform oxide distribution. Button-head specimens were machined in the longitudinal direction of the bar with 0.4 in. gage length by 0.2 in. diameter, with a fillet radius of j-B in. After machining, the specimens were electropolished in a 1 to 4 mixture of perchloric acid to methanol to remove all machining marks. All test bars were in the as-extruded condition. The fatigue tests were performed on a hydraulically activated, axial strain machine, with complete reversal of strain.15 Test conditions were:

Jan 1, 1969

By E. S. Fisher, L. C. R. Alfred

The elastic anisotropy factors, c4,/c6,, c3,/cll, and c12/cl,, for hcp metal crystals vary significantly among the dgferent unalloyed metals. Significant variations with temperature are also found. The effects of elastic anisotropy on the dislocation in an elastic continuum with hexagonal symmetry have been investigated by computing the elasticity factors for the self-energies of dislocations in fourteen different metals at various temperatures where the elastic moduli have been reported. For most of the metals the effects of the orientation of the Burgers vector, dislocation line, and glide plane are small and isotropic conditions can be assumed without significant error. Significant effects of anisotropy are, however, found in Cd, Zn, Co, Tl, Ti, and Zr. The elasticity factors have been applied in the calculations of dislocation line tensions, the repulsive forces between partial dislocations, and the Peierls-Nabarro dislocation widths. It is predicted that the increase in elastic anisotropy with temperature in titanium and zirconium makes edge dislocations with (a), (a + c), and (c) Burgers vectors unstable in basal, pyramidal, and prism planes, respectively. The probability of stacking faults forming by dissociation of Shockley partials in basal planes also decreases with increasing c4,/c6, ratio, when the stacking fault energy is greater than 50 ergs per sq cm. The widths of screw dislocations with b = (a) in titanium and zirconium increase very significantly in prism planes and decrease in basal planes as c4,/c6, increases. The effects of elastic anisotropy on various dislocation properties in cubic crystals have received considerable attention during the past few years. In the case of cubic symmetry the departure from isotropic elasticity depends entirely on the shear modulus ratio, A = 2c4,/(cl, —c12); i.e., the medium is elastically isotropic when A = 1. Foreman1 showed that an increase in the ratio A produces a systematic lowering of the dislocation self-energy for a given orientation and Poisson&apos;s ratio. ~eutonico~, has shown that large anisotropy can have a marked effect on the formation of stacking faults by the splitting of glissile dislocations in (111) planes of fcc and (112) planes of bcc crystals. ~iteK&apos; made similar calculations for (110) planes of bcc metals. Both studies of bcc metals showed that the large A values encountered in the alkali metals tend to reduce the repulsive forces between Shockley partial dislocations. In fcc metals, however, A does not vary over the large range encountered in bcc metals; consequently, the effect of A on the forces between Shockley partials is masked somewhat by the differences in Poisson&apos;s ratio between metals. The effect of A on the line tension of a bowed out pinned dislocation has also been investigated for cubic crystals, first by dewit and Koehler5 and more recent- ly by Head.6 In both cases the line energy model is applied and the core energy is not taken into account, thus making the conclusions somewhat tenuous with regard to the physical interpretation. Nevertheless, the fact that a large A decreases the effective line tension is clearly evident and the tendency for large A to produce conditions that make a straight dislocation unstable (negative line tensions) also seem evident. Head, in fact, shows visual microscopic evidence that stable V-shaped dislocations occur in 0 brasse6 For hcp metals the definition of elastic anisotropy is more complex and, furthermore, significant deviations from an isotropic continuum are found among a number of real hcp metals, especially at higher temperatures. The present work was carried out to survey the effects of elastic anisotropy on the elasticity factors, K, that enter into the calculations of the stress fields around a dislocation core. Some isolated analytical calculations have previously been carried out for several hcp metals but they are restricted in the dislocation orientations and temperature.8&apos;9 The present computations are based on single-crystal elastic moduli that have appeared in the literature and consider various orientations requiring numerical computations. The results are then applied to survey the effects of temperature on the dislocation line tension and dislocation splitting in hcp metals. PROCEDURE Anisotropy Factors. The degree of elastic anisotropy in hcp crystals cannot be described by a single parameter, such as the A ratio in cubic crystals. The following three ratios must be simultaneously equal to unity in order to have an elastically isotropic hexagonal crystal: The magnitudes of these ratios at several temperatures, as computed from the existing data for the elastic moduli of unalloyed hcp metals, are given in Table I. There are no cases of complete elastic isotropy, but the large anisotropy ratios encountered in the cubic alkali metals are also missing. There are, however, several significant differences among the hcp metals, the most notable being the relatively small A and B ratios in zinc and cadmium and the differences in the magnitudes and temperature dependences of A. It has been noted that the temperature dependence of A has a consistent relationship to the occurrence of the hcp — bcc tran~formation. For cadmium, zinc, magnesium, rhenium, and ruthenium, A is less than unity at 4&apos;~ and, with exception for rhenium, decreases with increasing temperature. In the case of rhenium, A has essentially no temperature dependence between 923&apos; and 1123"~, so that it is clear that A does not approach unity at higher temperatures. Cobalt is similar to the above-mentioned group of metals in that it also does

Jan 1, 1969

By E. T. Turkdogan, W. L. Worrell

The rate of reaction of hydrogen sulfide with ferrous sulfide was studied by measuring the initial rates of sulfidation of iron strips in hydrogen sulfide-hydrogen-argon mixtures at 670°, 800°, and 900" C. The time-dependent surface sulfur activity is derived from the instantaneous rate of sulfidation with the assumption that diffusion in the sulfide layer is in a pseudo-steady state with the gas-sulfide chemical reaction. The rate of sulfur transfer from hydrogen sulfide to the surface of iron sulfide is proportional to the partial pressure of hydrogen sulfide and inversely proportional to the activity of sulfur at the surface of the sulfide layer. The derived rate equation is based on the assumption that most of the surface sites on the chemisorbed layer of iron sulfide are occupied by sulfur atoms and that the slow rate-controlling reaction is the dissociation of hydrogen sulfide on the chemisorbed layer. The experimental results are in reasonable accord with this reaction model. 1 HE slow approach to parabolic growth rate in the sulfidation of iron in hydrogen sulfide-hydrogen mixtures is a manifestation of slow approach to surface equilibrium between the gas and the surface of the sulfide layer. For example, at 800°C and Fig. 7 in Part I, the parabolic growth rate begins after approximately 1 day of sulfidation time. With decreasing temperature and decreasing partial pressure of hydrogen sulfide, the time necessary to reach gas-sulfide surface equilibrium is much longer. These observations are similar to those reported previously by Turkdogan et al.&apos; on the oxidation of iron to wustite in hydrogen-water vapor mixtures. The slow approach to gas-sulfide equilibrium is well-demonstrated by the results in Fig. 1 where the square of the weight gain per unit area, ( g S per sq cmI2, is plotted against time for gas mixtures having PH g//>H = 1.0 with 0, 25, 50, and 67 pct Ar at 800°C. The value of 1.5 X lo-&apos; (g S per sq cm)&apos; corresponds to almost complete sulfidation of the iron strip (- 0.05 cm thick) to iron sulfide. The points fall on S-shaped curves. If the inflection parts of the curves are considered to be linear, thus indicating parabolic growth rate and the establishment of gas-sulfide equilibrium, their slopes would have to be the same for a fixed ratio in the gas mixture. Such is not the case, and the slopes for the "linear" parts of the S-shaped curves are lower than the value when gas-sulfide surface equilibrium is established. The subject matter of this paper is the kinetics of the surface reaction of hydrogen sulfide with iron sulfide during the early stages of sulfidation of an iron strip. EXPERIMENTAL RESULTS The apparatus and materials used were the same as those discussed in Part I. In the present experiments of relatively short duration, a purified iron strip, 5 by 2 by 0.05 cm, which was suspended in the uniform hot zone of a vertical zircon tube, reacted with a flowing gas mixture of hydrogen sulfide-hydrogen-argon. The sample was suspended from a gold chain attached to a calibrated silica spring. The amount of sulfur picked up by the iron, which formed a layer of iron sulfide, was determined by measuring the displacement of a reference point on the silica spring, using a cathetom-eter. In all cases, the degreased sample was first annealed in a stream of oxygen-free dry hydrogen for several hours to remove any impurities such as oxygen, nitrogen, or carbon which might have been present on the surface of the sample.&apos; The rate measurements were carried out at 670°, 800°, and 900° C in hydrogen sulfide-hydrogen-argon mixtures with pH2 s/Ph2 ratios from 4 to 0.1. In a few experiments of short duration no sulfur deposition was observed in gas mixtures with (comments concerning sulfur deposition at high pH s/ph ratios were made in Part I.) Typical examples of the results obtained are shown in Fig. 2 for two temperatures and two gas compositions. With the present experimental technique, reproducible rate data could be obtained only after a uniform

Jan 1, 1969

By R. H. Hopkins, R. W. Kraft

X-ray and metallographic analysis reveal that the preferred cryslallograPhic relationships in direc-tionally solid~fied Pb-Sn eutectic specimens can be stated: interface growth direction, Experiments in which tin single-crystal seeds were used to nucleate the eutectic demonstrate that the normal lamellar structure observed at steady state can be forced to break down initially to a semide-generate structure when the crystallograPhic direction of the tin seed does not lie within the preferred eutectic interface plane. A normal structure eventually develops by preferred grain growth. X-ray topo-graphs and rocking curves substantiate that the perfection of eutectic samples increases as growth proceeds until steady-state conditions prevail. RECENT years have seen substantial progress made in the understanding of eutectic solidification through both intensive theoretical1&apos;&apos; and experimental investigations (see Ref. 7 for a review and extensive bibliography of both aspects). Several important observations concerning the nucleation and growth aspects of binary eutectic solidification have been brought to light. Briefly some of these include the nonrecipro-cal nucleation of one phase upon another,&apos;j9 the tendency for a specific low-index direction of one or both phases of the eutectic to be aligned in the growth direction during unidirectional solidification,&apos;0711 and the production of lamellar microstructures having a preferred interface plane between "11-13 phases. Questions quite naturally arise as to the mechanism by which preferred grain growth evolves during eutectic solidification and what relationships (if any) connect the initial nucleation of one phase upon another with the preferred growth directions and interface planes observed after a few centimeters of growth in many systems. This study was initiated in an attempt to answer these questions. An experiment was devised in which both the nucleation and growth steps in the crystallization of a binary eutectic, Pb-Sn, could be correlated with subsequently developed eutectic morphology and crystallography. This was accomplished by nucleating the eutectic upon a tin single crystal seed and then causing the eutectic to grow from the seed by directional freezing. The morphology of the structures produced in this manner was then monitored metallographically and the orientation relationships and substructural perfection determined by X-ray analysis. The information thus ob- tained was correlated to the growth history of the samples. EXPERIMENTAL DETAILS The eutectic of composition 38.1 wt pct Pb and 61.9 wt pct sn14 was prepared by accurately weighing lead and tin of 99.999+ (from ASARCO and Lytess Metals and Chemicals, respectively), melting in a clean Pyrex beaker under an argon blanket, and casting into the proper crucible for resolidification as described below. Tin seeds were grown by the method of ~halmers," saw-cut, oriented by the Laue method, and soldered to the pull rod of the Czochralski puller. All seeds were given a final electropolishing (to assure the removal of any deformed material from the cutting operation) and acetone degreasing immediately prior to the nucleation experiment in which they were to be used. Eutectic samples were unidirectionally solidified in a horizontal graphite boat1&apos; or by pulling from the melt16 with tin (or graphite) seeds. A flowing argon atmosphere was employed in all experiments and growth rates and temperature gradients, constant for a given run, varied from 2 to 4 cm per hr and 8" to 15°C per cm over the course of all the experi-

Jan 1, 1969

By H. E. Cook

The Ising model for the internal energy of a binary alloy has been used to obtain a general equation for the critical resolved shear stress of partially ordered crystals. The equation expresses the stress in terms of the Warren "alphas " and can be used to estimate the variation in strength with order without the assumption, present in the original formulation of this problem in terms of domain size, that order is complete within each domain and that the domains are of ungorm size and shape. In addition, it is the general equation, according to the Ising model, for strengthening by short-range order. Two applications of the equation are considered: One is an estimate of the variation in strength of CkAu with long-range order. The other is an estimate of the variation in strength of FeCo with quench temperature. Reasonable agreement is found with the variations reported in the literature. When the internal energy of an alloy crystal depends upon the distribution of solute, the strength of the crystal will also depend upon it because a portion of the applied stress for plastic deformation will be: where V is the volume of the crystal and E(E) is the energy change associated with the solute redistribution caused by the plastic strain, E. We expect T to equal zero for a crystal having a random arrangement of solute because the arrangement would remain random after plastic deformation. Likewise, we expect it to equal zero when the crystal is perfectly ordered because the motion of paired dislocations found in such crystals does not disrupt order. However, when short-range order exists or when long-range order is incomplete, plastic deformation will decrease the amount of order and additional work, proportional to the ordering energy, will be expended. Fisher&apos; estimated T for crystals having short-range order by assuming an interaction energy between neighboring atoms and estimating the change in the number of unlike neighbors as a dislocation moved through the crystal. (His analysis was limited and several workers2"6 have since given more complete ones.) Fisher minimized the importance of a strengthening mechanism of this type for paired dislocations in a structure having long-range order. ~ottrell,&apos; however, pointed out that T could be appreciable for ordered crystals having antiphase domains. He attributed the strengthening to the increase in surface energy of the domains as they were cut by paired dislocations. Ardley,&apos; in his test of Cottrell&apos;s theory, found that r for Cu3Au crystals obeyed the equation: for 1 > t where 1 is the domain size, t is the domain wall thickness, and y is the surface energy of an antiphase boundary. His experiments represent the classic confirmation of the strengthening mechanism proposed by Cottrell. However, the assumptions involved in using Cottrell&apos;s theory are valid only for large domain size in CU~AU,~"~ i.e., when Eq. [2] reduces to: For small domains, ~linn~ has questioned Ardley&apos;s assumption that order was complete, and, indeed, Stoloff and ~avies" fpnd it incomplete until a size of approximately lOOA was reached. Even when the order within a domain is complete, it is not obvious how one determines the appropriate value for I in a structure where domains vary in size and are irregularly shaped. The purpose of this paper is to estimate T without restrictions upon the degree of order and domain shape. Our major assumption will be the use of a generalization of the model proposed by Bethe" (the Ising model) for the internal energy. This will in fact allow us to combine the theories for strengthening by short-range order and by antiphase domains into a single, general formalism. We will use the results to estimate the variation in strength of Cu3Au crystals with long-range order8 and the variation in flow stress of FeCo crystals with quench temperature.12&apos;13 INTERNAL ENERGY For simplicity, we restrict our considerations to those binary solid solutions which can be described as an arrangement of atoms on a Bravais lattice. An atom site will be indexed by three numbers (PI, pz, p3) determined by the vector: from the origin fixed at atom (0, 0, 0) to the atom site where a&apos;, an, and a, are the lattice translation vectors. We write: For the energy of the crystal where pi(p) is the probability (either zero or one) of finding an atom of type i (i = 1, 2) at site (p), which is shorthand for (pl, pz, p3) and pj(p + r) is that for an atom of type j (j = 1, 2) at the site (p + r), which is shorthand for (pl + rl, The coupling parameter, resents the energy associated with the pair Pi(p), Pj(p + r). The crystal is assumed large enough so that surface effects can be neglected; therefore, trans-lational and inversion symmetry require the coupling parameters to obey the relations

Jan 1, 1969

By S. K. Asunmaa, W. D. English, N. A. Tiner, W. A. Cannon

This paper discusses the reaction of metal surfaces with fluorine. Fluorination reactions result in the formation of metal fluoride films which are "passive" toward further reaction of the metal with fluorine. These films are very adherent, and do not easily detach from the substrate metal by mechanical flexing or thermal shock. Exposure of passive films to a humid atmosphere produces hydrated metal fluorides which cause secondary fluorination reactions upon reexpo-sure of the metal surface to fluorine. The surface films formed range from 10 to 30A in thickness and they pow at the expense of surface oxide films. The apparent film formation is completed rapidly in 15 to 30 min on stainless steel and nickel surfaces. On copper and on Monel surfaces, the film at first grows rapidly, then increases slowly over an extended period of time. Passive films are formed at all fluorine pressures in the range from 0.1 to 1.4 atm at room temperature. ALL metals react when exposed to fluorine. These reactions generally produce surface films which consist of metal fluorides. The rate of reaction is largely determined by the extent to which these films are protective. Although there is an extensive literature concerning reactions of oxygen with metals, there are very few investigations reported concerning fluorine-metal reactions. Brown, Crabtree, and ~uncan&apos; investigated the kinetics of the reaction of gaseous fluorine with copper metal which had been freshly reduced in hydrogen. The reaction rate was independent of pressure over the range from 6 to 60 torr. A logarithmic rate law was obeyed in the temperature range from 25" to 300" ~. There was some deviation at higher temperatures which could have been the onset of a parabolic law. The calculated film thicknesses ranged from about two molecular layers, 10A, for 5 hr exposure at room temperature to thirty-five molecular layers for 5 hr exposure at 200" . The authors concluded that no single mechanism could explain all the observations. O7Donnell and spatkowski2 studied the reaction of fluorine with copper at 450°C at pressures from lo to 133 torr. The reaction was found to be pressure -dependent and followed a logarithmic rate law. It was not entirely diffusion-controlled, and fluorine was thought to be the migrating species in the reaction. Miscellaneous metal-fluorine reactions were investigated by Haendler et ~1.~ Reaction products were identified but no rate data were determined. Air Prod- ucts and Chemicals, Inc., have conducted an investigation of reactions between fluorine and various metal powders at room temperature and 85° C. Fluoride film thickness as a function of time of exposure was reported on the assumption that the reaction takes place between fluorine and metal to form the normal metal fluoride. Surface areas of the powders were only estimated so the relative film thicknesses may not be exact. The data showed reaction rates which were generally logarithmic in character, the rate of film growth virtually ceasing after a few hours exposure time for some alloy powders. The effect of moisture on fluoride films was also investigated by measuring additional reaction with fluorine after exposure of passivated powders to atmosperic moisture. The fluorination of iron was studied by 0&apos;~onnell~ at temperatures from 225" to 525" ~ and at pressures ranging from 20 to 200 torr. In all ranges, the reaction followed a logarithmic rate law and was dependent on the square root of the gas pressure. The author concluded that fluorine gas passes through pores in the film. As the film grows, the blocking of pores leads to a rapid decrease in reaction rate; hence a logarithmic rate law is observed. Jarry, Fischer, and Gunther&apos; investigated the mechanism of the reaction of fluorine with nickel at about 600" to 700°C. On the basis of the metallographic examination of fluoride scales growing on the nickel and from separate radioautographic data, it was claimed that fluorine is the migrating species in the reaction. This is in sharp contrast to the growth of oxide films on nickel where it has been shown that nickel ions migrate through the scale to the gas-solid interface to react with oxygen. Few investigations have been reported of the reaction of fluorine with metal oxides. Such investigations should be of great significance for a better understanding of passivation in view of the ubiquitous oxide films on technical alloys. Haendler et al.3 studied the reaction of fluorine with oxides of copper, tin, titanium, zirconium, and vanadium. Copper (I) oxide reacted as follows in the temperature range 150" to 300"~: temperature above 300" ~ was required for the CuO to react to form additional copper fluoride. Ritter and smith7 also investigated the reaction of fluorine with copper (11) oxide. An oxide powder comprised of spherical particles with a fairly high surface area was reacted with fluorine, starting at room temperature and increasing to 100° C over a period of 3 or 4 hr. The initial reaction was slow until the fluoride film thickness reached about to or 15R at which time the reaction rate accelerated, then decreased again. Most of the kinetic data was obtained during this final phase of reaction. The authors conclude that the film grows slowly at first until the stresses developed in the distorted lattice are sufficient to rupture the initial

Jan 1, 1969