By Michel Dupuy, Daniel Calais

The study of self-diffusion of plutonium in E phase has been carried out by the welded couples method. The tracer used was puZ4O which is detected by its X-ray emission (conversion lines of uranium which are computed between 13 and 21 kev). Intensities were measured with a scintillation counter. Each layer was removed in a direction parallel to the original interface with a grinding machine and a thickness measured with a pneumatic comparator. The concentration-penetration curves obtained were corrected for the effect of heating time from room temperature to annealing temperature and for the expansion due to phase transformations of plutonium. They were analyzed by the generalized Gruzin method. Self-diffusion of plutonium in E Phase is very fast cm per sec between 500" and 620°C) and the diffusion zones are 2 to 3 mm wide for annealing times ranging from 30 min up to 10 hr. The Arrhenius law gives the temperature dependence in the form: From the point of view of self-dqfusion, PUE phase falls into the anomalous bcc metals category (Tip , Hfp, Zrp, Uy) with a low-frequency factor and an activation energy lower than those provided by standard correlations. No theory proposed hitherto to explain these anomalies (influence of dislocations, of extrinsic vacancies bonded to inlpurities, of bi-vacancies) can clearly explain the self-diffusion coeffzcients of plutonium. DIFFUSION in bcc metals is a present-day problem. A recent symposium (Gatlinburg, 1964), followed by a book,' has been devoted to it. A great many experiments seem to show that diffusion in certain bcc metals obeys unexpected laws. The activation energies measured are sometimes strangely low (B hafnium, y uranium). For certain metals (0 zirconium, p titanium) the curves of log D (D = diffusion coefficient) as a function of 1/T (T = absolute temperature) are not linear. The frequency factors Do, which are of the order of 1 sq cm sec-' in fcc metals, vary from 1 to 10~6 sq cm sec-'. Various theories have been put forward to explain these anomalies; none is yet satisfactory. We wished to introduce a new experimental result by studying the self-diffusion in c plutonium. This allotropic phase, stable from 475°C up to the melting point (640°C), is in fact bcc. Unfortunately, nothing is known of the characteristics of the point defects in this phase, which limits the scope of the hypothesis which can be made about the mechanism(s) of self-diffusion in plutonium. 1) EXPERIMENTAL METHODS 1) Principle. We used the welded couple method. The two pellets of the couple initially have different 240 isotope contents (X emitter). After diffusion, the concentration/penetration curves are drawn up by the generalized Gruzin method. 2) Gamma Spectrography. The metal used in our study is plutonium, either low in puZ4O (isotopic content 1 pct) or high in puZ4O (8 pct). The latter also contains plutonium 241 (-1 pct) and 300 ppm of ameri-cium produced by the reaction Pu2U-AmM1 + 8-. The emission spectra of these two plutoniums placed in leak-tight vinyl bags have been studied by y spectrograph~. The detector is a thin crystal of thallium-doped sodium iodide. The activity of the plutonium rich in 240 is about twice that of the plutonium low in 240 in the energy band of 17 kev (L conversion lines of uranium); this band was used in these measurements. 3) Preparation and Examination of the Diffusion Couples. Diffusion couples were made from plutonium with a high and low PU"' content. Pellets (6 6 mm. thickness 3 mm) mounted on a polishing disc with ground parallel faces were polished mechanically on both sides. In this way, pellets with two parallel faces were easily obtained. The polished pellets were joined by a 6 phase anneal (420°C, 1 hr) in a small screw press (pressure of 20 kg per sq mm cold); a centering ring enabled the two pellets to be pressed coaxially. The couples then were subjected to the diffusion treatment by annealing in the E phase in sealed silica ampules in argon at atmospheric pressure. The annealing temperatures and times are given in Table I. The couples were encased in a mild steel ring, the joint interface being thus parallel to the ground face of the ring. The diffusion couple/ring assembly underwent successive abrasions by means of a magnetic plate grinder. The thickness of the abraded layer was measured with a Solex pneumatic comparator when it was less than 0.1 mm (accuracy 0.2 p) or with a mechanical micrometer (accuracy 3 p) for passes of the order of 0.2 mm. All these operations were done in glove boxes, as plutonium is particularly toxic. After each abrasion we determined the emission spectrum of the ground face. The emissive surface is defined by means of a diaphragm 3 mm in diam. We noted more particularly the X activity in the 17-kev

Jan 1, 1969

By Richard B. Reese, George R. St. Pierre, Robert A. Rapp

The vapor pressures of pure iron and pure chromium have been measured using a Knudsen cell coupled with a mass spectrometer. The experimental results agree well with some previously reported data; heats of sublimation and vaporization have been calculated. From vapor pressure rr~easurernents, the activities of iron and chromium in their binary alloys have been determined for NcY = 0.10 to 0.65 over a 1400" to 1700~ temperature range. The activity of chromium in the liquid alloys was found to exhibit positive deviation from ideal behavior when referred to solid chromium as the standard state; however, for the activity of chromium referred to nonequilibrium undercooled liquid chromium as standard state, the activity behavior is almost ideal. ALTHOUGH the Fe-Cr system is important as the basic system of alloy steels, the thermodynamic properties of this system have not been thoroughly investigated at elevated temperatures. In view of the potential practical applications of such data as well as their contribution to alloy theory, further study of the Fe-Cr system was undertaken. In addition, further development of experimental techniques for equilibrium measurements at high temperature is required. The present research involved an application of the Knudsen effusion method in conjunction with a time-of-flight mass spectrometer. Belton and ~ruehan' have measured the activities in Fe-Ni and Fe-Co alloys by a similar method. Speiser, Johnston, and lackbburn' have determined the vapor pressure of pure solid chromium between 1283" and 1561°K by a Langmuir free evaporation technique. The vapor pressure of chromium was described by the expression: over the temperature range 1283" to 1561°K. McCabe, Hudson, and paxton3 have measured the vapor pressures of pure iron and pure chromium by the Knudsen cell technique around 1500°K. The vapor pressure and heat of sublimation at O°K, AH,", for pure chromium agreed within experimental error with the measurements of Speiser et al. at 1200°C. Kubaschewski and HeYmer~ determined the vapor pressure of pure solid chromium in the temperature range 1170" to 1400°C by the Knudsen effusion technique combined with a radioactive tracer analysis of crS1. Their results agreed with the work of previous investigators. Edwards, Johnston, and Ditmars5 have measured the vapor pressure of pure solid iron by the Langmuir technique between 1356" and 1519°K. The vapor pressure of solid iron in the temperature range studied was given by: The data of McCabe, Hudson, and paxton3 on the vapor pressure of pure iron around 1500°K by the Knudsen effusion technique were in good agreement with those obtained by Edwards et a~.~ Hultgren, Orr, Anderson, and Kelley give the selected values for the AH: of pure iron and pure chromium as 98,990 *200 and 94,340 * 500 cal per mole, respectively. These values are the average values determined in the several investigations by different methods. The Fe-Cr phase diagram7 is shown in Fig. 1. Previous determinations of activities in this system have been carried out by several investigators, but most of the work has been done on solid alloys. Using a Knudsen effusion method with cr5', Kubaschewski and Heymer4 reported that the Fe-Cr system exhibits positive deviation from the ideal behavior for compositions ranging from NCr = 0.0398 to 0.699 at 1170"

Jan 1, 1969

By R. M. Douthwaite, G. Birkbeck

The effect of grain size and specimen dimensions on the occurrence and magnitude of a yield point drop in pure iron has been examined. The tests were done at room temperature. The results indicate that gain size is the critical factor determining whether a yield drop occurs. The specimen diameter:gain size ratio does not influence the magnitude of the yield drop for the range of gain size and specimen diameters investigated. HUTCHINSON,' petchY2 and worthington3 have investigated the grain size dependence of the upper yield stress (uUYP) and the yield point drop, ouyp - aLYP, in Armco iron, mild steel, and Si-Fe, respectively. These authors used center-annealed wires to avoid stress concentration from specimen shoulders and to ensure uniformity of the applied stress. Coarsegrained specimens show no yield point drop; the yield point drop then increases as d-'I2 increases (where d is the grain diameter). These results can be understood in terms of Petch's analysis2 in which the magnitude of amp depends on the strain rate in the (limited) number of grains deforming plastically at the upper yield point. If N grains per unit volume are undergoing plastic deformation, the strain rate in the deforming grains is l/Nd3 times higher at the upper yield stress than when the whole specimen deforms homogeneously. If N is constant and independent of grain size at uUyp, then all the grains are deforming when ~d~ = 1, so there is no yield point drop. At finer grain sizes, the yield point drop is given by: where AU, is the friction stress increase corresponding to a tenfold strain rate increase. Christ, Smith, and Burton studied the upper yield point in 0.050-in.-diam wire specimens prepared from zone-refined iron. Each end of the 2; -in. specimens was soldered to a & -in. diam steel ball and the load applied through the two balls. There was a yield point drop in specimens with grain diameters less than 0.1 mm; no drop was observed in specimens of grain diameter greater than 0.1 mm that were free from veining substructure, but specimens of grain diameter 0.129 mm, annealed in the y range, showed an upper yield point. and this was associated with the presence of a veining substructure in these specimens. Christ et al. suggested the upper yield point occurs when more than a specific number of grains fill the specimen cross section so a multiplicity of slip is required to initiate plastic deformation. Table I summarizes the published data on the grain size at which the yield drop disappears. On the basis of this data the ratio of specimen diameter:grain diameter = 5 to 27 appears to be the critical value for the occurrence of a yield point drop. Thus, petch2 interprets the appearance and magnitude of the yield point drop in terms of the limited number of grains deforming plastically at uuyp, whereas Christ et a1. consider that the occurrence of the yield drop depends on the ratio specimen diame-ter:grain diameter. The published data cover a wide variety of materials so some variation between the results is to be expected, but the size range covered in the data of Table I is rather limited. In an attempt to discover whether the specimen diameter:grain size ratio or the grain diameter is critical in determining

Jan 1, 1969

By R. M. Brown, W. J. Murphy, B. M. Kapadia

An investigatiott was conducted to study the influence of nitrogen, titanium, and zirconium on the boron llardenabilzty effect in a low-carbon constructiona2 alloy steel. The experimental steels investigated exhibited a significant variation in hardenability, the variation being dependent on the interactions of boron, titanium, and zirconium with the nitrogen. Only the boron not combined with nitrogen was effective in increasing hardenability. Titanium, and with lesser effectiveness zirconium, combined with available nitrogen, thereby protecting the boron. The hardenabil-ity effect mas related to an empirical expression for the "effective" boron content, P, deduced from experimental evidence of these interactions. The hardenabzlity effect reached a maximum at about 0.001 wt pct 0, and decreased somewhat as P increased further. The physical understanding of this relationship is discussed. FOR many years boron has been added to steels to obtain high hardenability. Although a great deal of research has been conducted on boron-treated steels, certain aspects of the boron hardenability effect have not been fully understood. For instance, the magnitude of the hardenability effect has been observed to vary markedly, depending on the steelmaking technique, even when the amount of boron in the steel was essentially constant. Furthermore, the optimum amount of this element to be added has not been definitely established. A better understanding of the boron hardenability effect is essential because too small an addition of boron is likely to be ineffective, while an excessive amount can cause brittleness'' and hot shortness. The findings of earlier investigations have shown that the hardenability effect cannot be consistently related to the amount of boron added or retained in the steel. Grossmann observed that in a 0.60 pct C steel the hardenability increased to a maximum with mold additions up to about 0.0025 pct B and then decreased with larger additions. Other investigators5 likewise reported a maximum in the hardenability at about 0.003 pct B. Crafts and Lamont, however, found that in commercial open-hearth heats of medium-carbon steel the hardenability increased linearly with boron up to 0.001 pct and remained essentially unchanged with larger percentages up to 0.006 pct. Other investigators7,' also observed a rather constant hardenability effect in the range about 0.0005 to 0.0035 pct B. These observations and other evidence suggest that the effectiveness of boron in increasing hardenability probably depends, in addition to the amount, on the form of boron retained in the steel, this form being influenced by the presence of other elements. Both oxygen and nitrogen apparently exert the strongest influence on the hardenability behavior, since, at the temperature of liquid steel, boron readily combines with these elements, thereby losing its effectiveness as most experimental evidence seems to indicate. For consistent recovery of the boron effective in increasing hardenability, it is necessary that the oxygen and nitrogen in the steel be either reduced to extremely small amounts by the steelmaking practice or neutralized by combination with other elements before the addition of boron. The importance of achieving adequate deoxidation prior to the addition of boron in order to realize the full hardenability effect of boron has been sufficiently emphasized by earlier investigators. Digges and Reinhart' and others have investigated the role of nitrogen and have shown that nitrogen also interacts with boron and reduces or nullifies altogether its effect on hardenability. Moreover, their work also demonstrated that the addition of strong nitride formers such as titanium and zirconium reduce the deleterious effect of nitrogen on boron hardenability by combining with nitrogen to form stable nitrides. Another element which has a pronounced influence on the boron hardenability effect is carbon. It has been shown7'10 that the hardenability effect of boron diminishes with increasing carbon content, and becomes almost negligible at the eutectoid composition. This observation is useful in comparing the potential increase in hardenability from boron of steels with different carbon contents, but is not relevant to a study of the effects of normal steelmaking variables. The amounts of oxygen and nitrogen in steel vary with the steel composition and steelmaking practice employed. Most commercia1 low-alloy steels are fully deoxidized by the addition of silicon and aluminum, or other strong deoxidizers, which adequately protect the boron from oxidation. In addition, one or more of the elements such as titanium or zirconium are usually added, either separately or in combination with boron, in the form of complex ferroalloys, to protect boron from combination with nitrogen in the steel. However, the actual amount and type of addition employed for a given processing requirement are usually selected by trial and error, and have a rather limited range of applicability. As a result, substantial variations in the hardenability of boron-treated steels are often observed in practice, particularly when the nitrogen content of the steel is a significant processing variable. These variations might therefore be reasonably attributed to the interactions between boron, nitrogen, and titanium or zirconium present in the

Jan 1, 1969

By C. T. Liu, J. Gurland

The deformation behavior in tension of spheroidized carbon steels was studied at room temperature as a function of carbon content, 0.065 to 1.46 wt Pct, and carbide particle size, 0.88 to 2.77 p. It was found that the Hall-Petch strength-grain size relation is directly applicable to the yield and flow stresses of the two lower-carbon steels , 0.065 and 0.30 pct C. The strength data for the medium- and high-carbon steels, 0.55 to 1.46 pct C, also satisfied the Hall-Petch relation, provided that these data are based upon the particle spacing. Beyond 4 pct strain, the flow stress data of all the steels studied could be represented by the same Hall-Petch relation with dinerent spacings for grain boundary and particle strengthening. The behavior of the higher-carbon steels was consistent with the postulated formation of a dislocation cell network during processing and initial deformation (up to 4 pct strain). The cell size was assumed to be equal to the planar particle spacing. The true stress at the ultimate tensile strength was also found to be a function of the particle spacing. At a given temperature and strain rate, the yield and flow stresses of carbon steels depend on the type and dimensions of the microstructure. Starting with the work of Gensamer et al. in 1942,' experimental studies on pearlitic and spheroidized carbon steels revealed that the strength of steels is a function of two main parameters: the ferrite grain size2'3 and the carbide particle spacing;1'4'5 on this basis, two different strengthening mechanisms have been developed to apply to steels of low and high carbon contents, respectively. In polycrystalline iron and mild steels the grain boundaries are regarded as the major structural barriers to slip. The relation between strength and grain size is generally represented by the Hall-Petch equation which is based on a linear proportionality between strength and the inverse square root of the average grain size.2'3y677 However, Gensamer et al.' and Roberts et related the yield strength of medium -and high-carbon steels to the carbide particle spacing alone, and they found a linear relation between the logarithm of the mean free path in the ferrite and the yield strength in both spheroidized and pearlitic steels. By means of the electron microscope, Turkalo and LOW' extended the study to finer structures; they concluded that the logarithmic relation is not valid for the entire range of microstructures unless grain boundaries are also included in the measurement of the mean free path. For the specific case of spheroidized steels, Ansell and aenel' found that the yield strength data,4'5 when plotted as a function of mean free path, fit the Hall-Petch equation; however, T'ysong found that the same data fit the 0rowanl0 relation if a planar inter-particle spacing is used. Recently Kossowsky and ~rown" studied the strength of prestrained spheroidized steels, 0.48 and 0.95 pct C, and concluded that the strength due to the carbide dispersions varies linearly with the reciprocal of the square root of the mean free path between carbide particles and dislocation networks. Such networks were first observed by Turkalo." The conclusion common to all these studies is that the available slip distance in the ferrite is the most important variable in determining strendh. Previous work on carbon steels is restricted to limited composition and strain ranges. The mechanism which governs the flow properties is not clearly understood, and, in particular, little is known about the composition dependence of the transition between grain boundary strengthening and particle hardening. The purpose of the present work is to investigate the strengthening mechanism in spheroidized steels over a wide range of carbon content, 0.065 to 1.46 wt pct, and plastic strain, yielding to necking. The spheroidized structure was chosen because of its relative simplicity and the relative ease of control and measurement of the structural parameters. The experimental work is limited to tensile testing at room temperature at constant extension rate. The effects of the carbide particles on the fracture behavior of spheroidized steels are discussed elsewhere.13 EXPERIMENTAL PROCEDURE Eight different grades of vacuum-cast carbon steels were supplied in the form of forged and rolled plate by the Applied Research Laboratory of the U.S. Steel Corp. The compositions furnished with these steels are given in Table I; the carbon content ranges from 0.065 to 1.46 wt pct, or from 1.0 to 22.3 vol pct of carbide. The steel plates were cut transversely into rods a little larger than the test specimens, 1 in. gage length, i in. diam. The rods were austenitized in air (enriched with CO by a consumable carbon-rich muffle) at 50° C above theA, orA., temperature for 2 hr and then quenched in oil with vigorous stirring. The as-quenched rods were tempered in two stages in order to obtain the desired distributions and sizes of carbide particles. The rods were first tempered at 460° C for 10 hr and then at 700" C for periods ranging from 4 hr to 3 days, in vacuum. After final machining, all specimens were vacuum-annealed again at 650°C for 1 hr in order to relieve residual stresses. The tension tests were carried out in two steps. The initial part of the load-strain curve, up to about 2 pct strain, was determined on a Riehle testing machine with an extensometer of small strain range, 4 pct strain, in order to obtain the yield and initial flow piopertiesi As soon as the first part of the test was finished, the specimen was placed in an Instron testing machine equipped with a strain gage extensometer with a maximum strain range of 50 pct. The load-strain curve to fracture was

Jan 1, 1969

By W. F. Chiao

Ultrasonic attenuation, a, measurements in the frequency range of 5 to 55 mc per sec have been studied to determine their quantitative relationship with the following three variables of mixed microstructures in steels: 1) the volume percent, XF, of polygonal fer-rite in mixed structures of martensite and polygonal ferrite in Fe-Mo-B alloys: 2) volume percent, XA, of retained austenite plus martensite aggregates in high-carbon steel; and 3) substructural differences between 100 pct bainitic ferrite structures formed at various temperatures. The quantitative relationship obtained in the first two conditions by plotting a us the known structural parameters can be expressed, respectively, as: where al, a 2 and C1, Cz are constants. In the third condition the nature of the attenuation depends on the state of dislocations generated at the transformation temperatures and also on the alloy composition. From these measured results, the mechanism of ultrasonic attenuation caused by these mixed microstructures can also be studied. MUCH interest has recently been shown in the application of ultrasonic attenuation and wave velocity measurements to the study of the microstructural characteristics of steels. The general aims of most of the investigations in this field can be grouped into two categories: one is to study the mechanisms of ultrasonic losses caused by the characteristic phases in the microstructure of steel,''' and the other is to develop nondestructive test methods and applications for quality control.~' 4 Apparently no work has been done on the evaluation of ultrasonic attenuation meas -urements as a means of quantitative determination of a given phase in the microstructure of a steel. It is well-established that the decomposition of austenite results in four main microstructural constituents—polygonal ferrite, pearlite, bainite, and martensite—and that each phase has different mechanical properties. Thus, when a steel consists of mixed microstructures, the mechanical properties can often be related to a quantitative measure of the volume percent of each phase present. This study relates ultrasonic attenuation measurements to: 1) the volume percent of polygonal ferrite in mixtures of martensite and polygonal ferrite in Fe-Mo-B alloys; 2) the substructural differences between 100 pct bainitic ferrite structures formed at various temperatures; and 3) the vol- ume percent of austenite in austenite plus martensite aggregates in a high-carbon steel. The choice of the specimen materials was based on the laboratory stocks which were suitable to produce the required mixed microstructures for this study. EXPERIMENTAL PROCEDURES Materials and Heat Treatment. Polygonal Ferrite Plus Martensite Structures. This mixture of phases was produced in a vacuum-melted Fe-Mo-B alloy. The alloy was hammer-forged at 1900" ~ to a -f-in.-sq bar. By isothermally heat treating the alloy at 1300° F for various times and then water quenching, variations in the amount of polygonal (or proeutectoid) ferrite can be controlled in a microstructure in which the balance of the material is martensite. In the present work, four different times of isothermal transformation were adopted; after heat treatment, the four specimens were machined for ultrasonic measurements. The compositions, heat treatments, and dimensions of the four specimens are listed in Table I. 100 pct Bainite Structures Formed at Different Temperatures. It has been well-established by Irvine et al.= that the presence of molybdenum and boron in ferrous alloys can retard the formation of polygonal proeutectoid ferrite and expose the bainitic transformation bay, so that a more acicular or bainitic ferrite can be obtained over a wide range of cooling rates. Their investigation6 also showed that the mechanical properties of fully bainitic steels are usually closely dependent on the substructural characteristics of the steels. For studying the substructural characteristics in completely bainitic structures, six Fe-Ni-Mo alloys, of which five were free from carbon addition and one with 0.055 pct C addition, were selected so that a wide range of hardness values for 100 pct bainitic ferrite structures could be produced by normalizing at 1900" F followed by air cooling. The different bainitic transformation temperatures were recorded during air cooling. All of the alloys were vacuum-melted and then forged at 1900" F to square bars. Data on the six specimens of these structure series are summarized in Table 11. Austenite Plus Martensite Structures. The high-carbon steel used to study austenite plus martensite structures was vacuum-melted and then forged into Q-in.-sq bar. The series of mixed structures of austenite plus martensite was produced by quenching the specimens from the austenitizing temperature to room temperature and then refrigerating them at various temperatures within the range of martensite transformation to produce different amounts of retained austenite. Data on the four specimens of this series are listed in Table 111. Quantitative Analysis of the Microstructures. The microstructures containing martensite plus polygonal ferrite were analyzed by the point-counting technique.

Jan 1, 1969

By J. J. Frawley, W. J. Childs, W. R. Maurer

The object of this investigation was to determine the growth habit of bismuth and bisrrtuth alloy dendrites as a function of supercooling. To do this, techniques were developed to increase the amount of supercooling in bismuth and bismuth alloys. For pure bismuth, the growth habit was dependent on the amount of supercooling. At low amounts of supercooling, about 10" C, prismatic dendrites were obtained. With increased supercooling, about 20 C, a hopper growth habit was observed. In many cases where hopper growth had occurred, the hopper dendrites were twinned during the growth process. This twinned surface enable prismatic dendrites to nucleate and grow by a twin plane mechanism. When the amount of supercooling was increased to about 25 °C, the growth habit was a triplanar growth. With still greater supercooling, about 3s°C, a branched growth habit occurred. The exposed planes on the prismatic, hopper,, triplane, and branched dendrites have been determined. The growth habit of the dendrites which grew along the crucible wall was found to have the (111) as the exposed plane, with <211> growth direction. It is apparent that dendritic growth of a metal is dependent on its purity and the solidification variables present. One of the solidification variables is the degree of supercooling. Supercooling, although often observed, has not been studied extensively until recent years. For dendritic growth to occur in a pure metal, the metal must be thermally supercooled. After the dendrites grow into the supercooled melt, the heat of solidification raises the temperature of the specimen to the melting point of the material and the remaining liquid will solidify at this temperature. Decanting is the removal of this remaining liquid before complete solidification. This removal of the remaining liquid after recalescence had occurred is a great aid in the study of dendritic growth. In this investigation, decanting was accomplished by a vacuum-decanting technique . Other investigators1-5 have studied the growth characteristics of various low-melting-temperature pure metals and alloys as a function of supercooling. However, large degrees of supercooling were not included. For their study of dendritic growth of lead, Weinberg and chalmersl employed a decanting technique which was achieved by pouring off the remaining liquid, exposing the solid/liquid interface. This method was employed later by Weinberg and Chalmers2 for the investigation of tin and zinc dendrites. The method for obtaining a solid/liquid interface was improved by Chalmers and Elbaum. They employed a triggered spring which was attached to the solidifying section of the specimen. Upon activation, the spring jerked the solid interface away from the liquid melt. In the study of growth from the supercooled state, a metal of low melting point which exhibited a high degree of supercooling was desired. Bismuth gave very consistent supercooling when a stannous chloride flux was employed. The maximum supercooling obtained was 91°C, with an average supercooling of between 65" and 75°C. The consistency of supercooling greater than 50°C was very high. The use of vacuum to aid in the rapid decanting of molten metal has proven to be very successful in this investigation. The vacuum gives a rapid decantation, usually leaving the solidified metal structure sharply defined. The purpose of this investigation was to study the effects of supercooling and the effects of alloy additions on the growth habit of bismuth dendrites. The structure of bismuth has been variously defined as face-centered rhombohedral, primitive rhombohedral, and hexagonal. However, bismuth has only one plane with threefold symmetry, the (111) plane, and the crystal-lographic structure is considered a 3kn structure. MATERIALS The bismuth which was employed in this investigation was obtained from the American Smelting and Refining Co. of South Plainfield, N. J. The accompanying spectrographic analysis data indicated the bismuth to be 99.999+ pct pure. The tin was obtained from the Vulcan Materials Co., Vulcan Detinning Division, Sewaren, N. J. It was classified as "extra pure". Nominal analysis was 99.999+pct. In order to prevent contamination of the bismuth melt from the atmosphere, an anhydrous stannous chloride (Fisher certified reagent grade) was added to each melt. The fluxing action obtained from the use of the chloride provided a large amount of supercooling in the specimen. APPARATUS A 30-kw, 10,000-cps motor-generator set, connected to a 6+-in.-diam air induction coil, was employed to melt and superheat the specimens. The temperatures were recorded by means of a chromel-alumel thermocouple and a potentiometric recorder. The thermocouples were 0.003 in. in diam, and were encapsulated with Pyrex glass to prevent the thermocouple from acting as a nucleating agent and also from contaminating the melt. Fig. 1 illustrates the vacuum-decanting apparatus when a liquid flux was employed. A standard 30-ml Pyrex beaker was placed on top of an asbestos insulating block. A 5-mm-ID Pyrex tube with aA-in. spacer tip attached to its end was used for the decanting tube. The spacer tip contributed significantly to a successful decanting operation. The tip located the opening of the decanting tube about -^ in. from the bottom of the

Jan 1, 1969

By Minoru Sasabe, Mayurni Sorneno, Kazuhiro Goto

I) The Object of the Present Experiment. When the oxygen chemical potential in the gas phase is changed, the oxygen chemical potential in the liquid metal or in the liquid oxide phase will be subsequently changed. The object of the present experiment is to develop a method of measuring the change in the chemical potential of oxygen in liquid metals and in liquid oxides with respect to time, when the oxygen potential in the gas phase changes. II) The Experimental Method. The following types of the oxygen concentration cells with the solid electrolyte of Zr0z-CaO are used: KAZUHIRO GOTO, MemberAIME.MINORU SASABE,and MAYUMl SOMENO are Associate Professor, Research Associate, and Professor, respectively, Department of Metallurgical Engineering, Tokyo Institute of Technology, Meguro-ku, Tokyo, Japan. Manuscript submitted March 12, 1968, EMD. Igas phase liquid Ag or Pb ZrO2-CaO electrolyte!, The measured reversible electromotive force can be expressed by the next equation, provided that the transference number of the oxygen anion in the electrolyte is unity: E = RT/nF log (at electrode I)/P~ (at electrode 11) where is the electromotive force, R is the gas constant, T is absolute temperature, n is valence of oxygen anion, and Pq is the oxygen pressure at the electrodes. As shown in the previous work1 of the authors, the electromotive force is determined by the difference in the chemical potential of oxygen at the vicinity of the interfaces between the solid electrolyte and the electronic conductors used for the two electrodes. Fig. 1 shows the two kinds of the cell assembly used to measure the change of the chemical potential of oxygen in liquid metals and liquid oxides with respect to time. In both cases, the change of the oxygen pressure in the gas phase is measured by the independent oxygen concentration cell located above the

Jan 1, 1969

By J. W. Koger, R. E. Hurnrnel

QUENCHED, bcc p brass, P1, transforms to a mar-tensitic phase, when it is cooled below room temperature.&apos; This transformation can be followed using resistance measurements since the resistivity of the martensitic phase is considerably larger than that of the parent phase, Fig. 1.&apos; phillips3 first reported that, when Cu-Zn alloys containing between 37.0 and 39.0 wt pct Zn were quenched from the 0 region to room temperature, variable amounts of a phase could be observed depending on the mode of quenching. If the quench occurs very rapidly, the a phase forms by a "massive transformation". The resultant phase has the same composition as the high-temperature P phase from which it was formed. If the quench is less severe, the alloy is retained largely in the p form; however, some a is formed by precipitation. In this case, a contains more copper than the high-temperature 0 phase from which it has formed. The a phase most probably does not undergo a transformation in the temperature range where p transforms to low-temperature martensite. This can be deduced from the Eesistivity-temperature relation which is linear in this temperature range, Fig. 2. The stable a phase which is present along with R. E. HUMMEL is Assistant Professor, Department of Metallurgical and Materials Engineering, University of Florida, Gainesville, Fla. J. W. KOGER, Junior Member AIME, formerly with University of Florida, is now with Oak Ridge National Laboratory, Oak Ridge, Tenn. Manuscript submitted December 13, 1967. IMD.

Jan 1, 1969

By A. D. LeClaire

This paper claims to provide a description of diffusion processes in solids which is said to be a reformulation of Fick&apos;s Laws and therefore, presumably, is supposed to be as general as those laws. In fact, it appears to provide no more than an atomic model of a rather restricted type leading even to results in conflict with experiment. The restriction lies in the assumption, carried throughout the paper, that even in a chemical gradient the jump frequency i of an atom of species i is a function only of the composition on the plane from which it jumps, i.e., ?i = ?i(cl, c2 ...). This means that atom jumps in opposite directions from a site would occur with equal probability. There would then be no tendency for atoms to migrate preferentially in one direction along the gradient, so the model is incapable of accommodating the well established phenomenon of atom drift in a chemical gradient.10-" A more general model that does not suffer this difficulty was discussed in a paper13 I wrote in 1958, and the results therein already contain as a special case those given by Dr. DeHoff. The simplest sufficiently general assumption is to suppose that ?i is a function ?i(a1 a2,...; wl, w2, ..-) of the concentration aj and ? ?j at the site from which and to which, respectively, a jump is made. Any such function can always be expressed as a function of the sum and difference of its arguments. Thus d is the jump distance and g a geometrical constant. Obviously this is zero, i.e., no drift, if ??ri/??j = 0. X is written in this form, revealing two components of the total drift, because it can be shown that only the second component, depending on ??&apos;i/???(?j -aj), actually contributes to the net diffusion flux Ji. This component can be shown,13 by a straightforward ther-modynamic transcription, to be responsible for the so called "thermodynamic factor" in the Darken approximation for a chemical diffusion coefficient is the activity coefficient of i. Because the jump rate ?i in DeHoff&apos;s approximation has no dependence on the concentration gradient it does not seem possible to derive the Darken equation from his Eq. [6] without the further rather arbitrary assumption that ?i = const ri. It is to be noted too that the author&apos;s derivation of Eq. [12] is only valid when ?i is in fact a function only of the cj at the plane from which the atom jumps—for only then is ci?i a unique function of position and therefore of A. Author&apos;s Reply R. T. DeHoff I am indebted to Dr. LeClaire for his penetrating discussion of my paper, "A Reformulation of Fick&apos;s First Law". I concede that it does appear initially that the relationship presented in my paper could be derived from the detail atomic model of random walk and atom drift presented in Dr. LeClaire&apos;s approach. However, there are some important differences in concept and viewpoint which deserve further amplification. Dr. LeClaire&apos;s description is penetrating, detailed, and fundamental. His approach describes an extremely complex phenomenon, the displacement of atoms in a multicomponent gradient, at a sophisticated level. For precisely these reasons, his analysis has not proved to be useful for experimental studies that have practical objectives. For example, in order to obtain the information required to complete the analysis of the jump frequency distribution in a ternary system, the following series of experiments would, I believe, be required: 1) chemical (gradient) experiments, covering the composition range;

Jan 1, 1970

By H. Stuart, L. Zwell, N. Ridley

specimen that was subjected to 700°C for 250 hr is shown in Fig. 2(c). The precipitates in this foil appear round and exhibit only very faint strain contrast. From this evidence, along with that described above for the symmetry of the strain field, it may be concluded that this coherent precipitate is spherical, which is generally the favored shape for coherent precipitates when the lattice parameter mismatch is small.12 These observations are consistent with the assumption that this precipitate is the y&apos; (Ni3Al, Ti) phase. y&apos; is known to be spherical in the early stages of precipitation. It is fcc and is similar in composition to the matrix and thus would have contrast similar to that of the matrix as do these precipitates. Direct identification of the spherical precipitate did not prove possible because of its low volume fraction and small size. The results of this investigation suggest that the increases in yield strength and the decreases in elongation observed in 45-Fe 30-Ni 20-Cr alloys containing about 0.4 pct A1 and 0.4 pct Ti on prolonged aging at 550" to 700°C are very likely due to the presence of a coherent, spherical precipitate, thought to be y&apos;. Mi-crohardness measurements indicated that the precipitation of semicoherent M23C6 resulted in some matrix hardening. However, this precipitation process occurs much more rapidly than the changes in mechanical properties at these temperatures. 1C. L. Clark, J. J. B. Rutherford, A. B. Wilder, and M. A. Cordovi: J. Eng. Power, 1962, vol. 84, p. 258. 2 F. A. Comprelli and U. E. Wolff: USAEC Report GEAP-4745, General Electric Company November, 1964. 3C. N. Spalaris: A Monograph, USAEC Report GEAP-4633, General Electric Company, July, 1964. THERE have been many X-ray investigations of the room temperature lattice parameters of austenite which has been retained in quenched steels of various carbon contents. The results of these investigations have been collected by Wrazej,1 Wever et al.,2 and by Roberts3 and are included in Fig. 1 due to Pearson.4 The dashed line in Fig. 1 was considered by Roberts3 to most reliably describe the variation with carbon content of the lattice parameter of retained austenite. This line is given by the equation: a (Å) = 3.555 + 0.044 wt % C and recent unpublished measurements by one of the authors (LZ) support this relationship. The object of this communication is to draw attention to a relationship which describes the variation of the room temperature lattice parameter of &apos;equilibrium&apos; austenite with carbon content, and which is different from that for retained austenite. The relationship a(Å) = 3.573 + 0.033 wt % C has been obtained from lattice parameter measurements made on equilibrium Fe-C austenites at elevated temperatures, which have been extrapolated to room temperature. The room temperature lattice parameter of 3.555Å which the Roberts&apos; relationship gives for pure y-Fe is no: in agreement with the value of 3.573Å obtained when the high temperature lattice parameter data of Basinski et aL.5 and of Goldschmidt6 is extrapolated to room temperature. A linear extrapolation was

Jan 1, 1970

By Mary Louise Theodore, R. G. Aspden, D. A. Colling

T RACES of sulfur have a marked influence on the physical and mechanical properties of many iron-base alloys. The commonly used combustion method for the determination of sulfur content is not accurate enough at the 50 ppm level by weight and below to be useful in determining the influence of sulfur. Kriege and Wolfe&apos; have described a method for the determination of sulfur in iron alloys in which the sulfur is evolved as hydrogen sulfide followed by reaction with N, N-dimethyl-p-phenylenediamine, and iron (111) to form methylene blue which is measured spectrophoto-metrically. This method of determining sulfur has been used to study the activity of sulfur in Fe-Si-S alloys,&apos; but has not been previously applied to the determination of sulfur in Fe-Ni alloys because of the insolubility of nickel in dilute hydrochloric acid. Dissolution of nickel in dilute hydrochloric acid, however, can be greatly accelerated by the addition of a small amount of platinic chloride.3 By combining these two techniques in a procedure in which 0.005 pct platinic chloride in 1:l hydrochloric acid is used as the dissolving fect on the strength of the material. However, ductility is influenced by the presence of discontinuous precipitation. In Fig. 5, percent elongation data at room temperature and 1400°F is shown for two sets of specimens of Waspalloy which were solution heat treated at 1950°F and either quenched or slow cooled to the aging temperature and then aged for 100 hr at 1292" and 1598ºF, respectively. At room temperature the existence of a discontinuous precipitation cell at grain boundaries (see data point marked by arrow) has no apparent effect on ductility. However, at elevated temperatures a pronounced lowering of ductility occurs when discontinuous precipitation has occurred in the specimen. It would appear that the morphology of discontinuous precipitation "cells" at grain boundaries would be highly conducive to the initiation of cracks which in turn lead to premature "grain boundary" failure.

Jan 1, 1970

By Cuppam Dasarathy

THE object of this note is to report briefly certain results of investigations on the Fe-In phase diagram. BISRA-high purity H-iron and 99.9 pct pure indium were used to prepare the alloys. The experimental techniques consisted of thermal analysis, optical metallography, and X-ray diffraction. A phase diagram based on the present results as well as those reported earlier by the author&apos; is shown in Fig. 1. It is seen that the liquidus points fall on a smooth line which meets the monotectic isotherm at 1470°C. The liquidus extends up to 3.4 at. pct In. The phase boundary separating the two liquidus L1 and L2 is shown dotted. The experimental solidus meets the monotectic isotherm at -0.9 at. pct In. The 6/6 + L2 boundary drops steeply to the 6 + La/y + L2 boundary at -1350°C. In this region, it is impossible to detect satisfactory thermal arrests because of the steep phase boundary. The present diagram shows that indium lowers the temperature of the d/y transforma-tion and raises the temperature of the y/a transfor-mation. The y +d region is found to be very narrow. Indium gives rise to a restricted y field when alloyed with iron. The width of this field is between 0.4 and 0.5 at. pct In. Details of the alloys containing 40 and 50 at. pct In have already been reported by the author&apos; and the transformation temperatures of these alloys are included in Fig. 1. It appeared from optical metallography and X-ray diffraction that the room temperature solubility of indium in a iron is less than 0.28 at. pct since alloys of 0.28 at. pct In and above, slow cooled to room temperature, contained dark etching second phase particles situated both in the matrix and grain boundaries of the a-grains, see Figs. 2 and 3. These particles were identified to be unalloyed indium by X-ray diffraction. The lattice parameter of the a phase reached a maximum of 2.8672A at the indium level of -0.28 at. pct. The present diagram, Fig. 1, is in substantial agreement with that of Stadelmaier and Fiedler&apos; except for certain differences in detail. For example, they found the monotectic composition and temperature to be 7.0 at. pct In and 1443oC, respectively, while the present work indicates them to be 3.4 at. pct In and 1470°C. The 6 + L2/y + L2 transformation is indicated in the present work to occur at -1350°C, whereas Stadelmaier and Fiedler find this to occur at -1320°C. They also claim that the width of the y field is 0.2 at. pct In while the present work shows the width to be between 0.4 and 0.5 at. pct In. 1) Indium, when alloyed with iron, gives rise to a restricted y field, the width being >0.5 at. pct In.

Jan 1, 1970

By Michael Tenenbaum

Selected characteristics of nonmetallic phases were determined in low-carbon sheet steels which had been produced by various refining; deoxidizing, and casting procedures. The results showed little influence of the refining process on the quantity, distribution, size, and character of the nonmetallic phases. The quantity of inclusions was governed by the deoxidation procedures. While the mode of casting influenced the internal structure and the pattern of inclusion distribution, it had little effect on the quantity of nonmetallics. The vast majority of inclusions were under 30 µ in diam, and there was little change in size distribution during hot and cold rolling. The composition and structure of the inclusions were expained an the basis of known equilibrium phase diagrams for the appropriate systems. Additional work is needed to explain some of the observations of this paper. HENRY Marion Howe&apos;s contributions to the metallurgical profession include his many writings, the wisdom that he imparted to his students, and the inspiration that he gave to the many scholars, teachers, and industrialists who knew him personally. It was Professor Howe&apos;s intimate colleague, Albert Sauveur,1 who, in the first Howe Memorial Lecture, could have been speaking for the metallurgist of our generation as well as his own when he wrote, "...how many of us on the point of going astray were called back to the right path by Howe&apos;s guiding torch?" More than a quarter of a century later, Francis Foley,2 one of the last in the Howe Lecture series who worked directly with the great man, delivered the ultimate tribute, "...truth, in its time is so hard to identify." While Professor Howe strove to be right, "he was content if he provoked the reader to take the next step along the path to greater knowledge." Like so many of my predecessors, I sought guidance for this lecture by referring to Professor Howe&apos;s two classic texts, Metallurgy of steel,3 and Metallography of Steel and Cast Iron: the former book interpreting the facts as he saw them near the start of his career, and the latter—published 26 years later—pointing to many fertile fields for metallurgical investigation. Those of us who harvest the fruits of Henry Marion Howe&apos;s contributions to the metallurgical profession now look with wonder at the tremendous legacy he has provided. It is rewarding to study his writings and to recognize the anticipation of such aspects of modern ferrous metallurgy as: 1) Direct reduction 2) Steelmaking reactions 3) The approaches and benefits of degassing 4) Solidification mechanisms 5) Habits and behavior of nonmetallic inclusions 6) Recrystallization phenomena 7) Slip and slip propagation 8) Dislocations 9) Discontinuous deformation 10) Microscopic and macroscopic segregation

Jan 1, 1970

By G. R. St. Pierre, S. W. Gilby

The equilibrium vapors established over Fe-Cr-Ni alloys containing up to 50 pct Cr at 1600°C were determined by collecting the effusate from thoria Knud-sen cells. From these data, the activities of iron and nickel in the ternary alloys have been calculated. In a separate set of measurements, a mass spectrometer was used to determine the activities of the three components in a series of Fe-Cr-Ni alloys. In binary Ni-Cr melts, the activity coefficient of chromium referred to pure solid chromium as standard state is less than one at low chromium contents but is greater than one for melts containing more than 30 at. pct Cr. For Ni-Cr melts containing less than 10 at. pct Cr, In ?Cr = 0.15-0.92 N2. Ternary activity diagrams for Fe-Cr-Ni alloys are presented. In iron-rich alloys, the interactions between the three components are negligible; however, in nickel-rich alloys, the three principal interactions have significant positive values. THE activities of components in binary Fe-Ni alloys have been measured both in the solid solution1-3 and liquid solution4-6 temperature ranges. The determination for Fe-Ni melts have been made by three different methods: transpiration,4 Knudsen-cell effusion with analysis of an accumulated condensate,&apos; and Knudsen-cell effusion with direct measurements of relative component intensities by mass spectrometric methods.6 The results obtained by the three different methods in three different laboratories are in excellent agreement and considerable confidence is placed in the activity coefficients for Fe-Ni melts. At 1600°C, the activity coefficients in dilute solution are ?°Ni = 0.66 and ?oFe = 0.40 for the pure liquid components as standard states. Measurements made on solid solution Fe-Cr alloys7-10 indicate that the component activities are slightly greater than ideal. The measured activities in iron-rich Fe-Cr liquid alloy11-16 indicate almost ideal behavior for this system. The recommended activity coefficient of chromium in dilute solution in liquid iron at 1600o C, ?oCr, is 1.18 when referred to pure solid chromium as standard state and 1.04 when referred to pure undercooled liquid chromium as standard state." The conversion factor of 1.14 is based on a melting point of 1857°C and an enthalpy of melting of 4047 cal per g at. for chromium.21,37 The activity coefficient of iron in dilute solution in liquid chromium has not been measured. Activity measurements on solid Ni-Cr alloys have been made by several investigators.17-20 During the review of this manuscript, Fruehan12 published the results of a study on liquid Ni-Cr alloys at 1600°C. He used galvanic cells22 with ZrO2(CaO) as the electrolyte and Cr/Cr2O3 for the reference electrode. His results indicate that ?oCr in nickel at 1600°C is about 1.01 when referred to pure solid chromium and about 0.89 when referred to pure undercooled liquid chromium as standard state. The activity coefficient of nickel in liquid chromium is unknown. The compositions of vapors freely evaporating from some molten Fe-Cr-Ni alloys have been measured by Lyubimov, Granovskaya, and Berenstein.23 Their results, combined with known vapor pressures, indicate strong positive deviation for chromium in iron-rich alloys and strong negative deviation for chromium in nickel-rich alloys. EXPERIMENTAL PROCEDURES This research was undertaken to determine the activities of components in ternary Fe-Cr-Ni melts containing up to 50 at. pct Cr. At the initiation of the research, we decided to use a Knudsen-cell method wherein a portion of the effusing vapor is condensed on a cold plate.&apos; The composition of the equilibrium vapor for each alloy composition is determined in this method by holding the system under constant conditions for a period of time sufficient to collect enough condensate on the cold plate for chemical analysis. The activities of components in ternary alloys can be calculated from such vapor composition determinations by Eq. [1].24

Jan 1, 1970

By Frank E. Woolley, John F. Elliott

Mathematical models of the transient thermal behavior of a high-temperature solution calorimeter1-3 have been developed. The thermal behavior of the calorimeter is appoxirrzated by linear lumped-parameter models, and hence is described by sets of linear ordinary differential equations with constant coefficients The response of the models to various inputs is shown to agree with the response of the real system. Application of the modeling to experimental design and analysis of data illustrates the usefulness of simple models of complex systems. The early eperiments1,2 with the high-temperature solution calorimeter indicated that the change in the temperature of the bath resulting from the addition of a solute sample to the bath involved not only the direct effect due to the solution process but also possibly a secondary effect arising from the change in coupling between the bath and the induction heating coil. Consequently, an extensive analysis of the calorimeter was carried out, and models of the transient thermal processes of the instrument were developed to aid in improving the design and interpreting the behavior of the system. This paper describes the dynamic modeling; the use of it in treating experimental results has been reported earlier.3 The high-temperature solution calorimeter was constructed to measure directly the partial molar heats of solution of solute elements in a variety of liquid metal solvents.1-3 The calorimeter consists of an induction-heated liquid metal bath into which small samples of a solute element can be dropped. The bath temperature is recorded continuously, and the change in the measured bath temperature with time, dTm = f(t), resulting from the solute addition are the raw data from which the enthalpy change caused by the addition is determined. To extract the rmodynamic results from the data, the temperature change must be compared with that resulting from calibration additions of known enthalpy change. Accordingly, it is necessary to understand the transient thermal processes arising as a result of the addition to the bath. Neither modeling nor experimentation alone could provide the required insight into the working of the calorimeter. The alternate use of both methods in conjunction greatly assisted the design of the equipment and experiments, and the interpretation of the data. THE PHYSICAL CHARACTER OF THE SYSTEM The essential parts of the calorimeter, Fig. 1, for model studies are the thermocouple, the liquid metal bath and the surrounding refractories. The system is the solvent metal bath and those refractories around it which undergo a temperature change as a result of an addition to the bath, and which determine the way the temperature of the bath responds to an input. The inputs are the combined transient thermal effects arising when an addition is made to the bath. They include the thermal effects of the addition itself and the results of changed coupling between the bath and the induction coil. The response is the variation in the measured bath temperature, dTm(t) = Tm(t) - Tm(O), from an initial steady state resulting from the inputs. It was assumed in this study that the physical properties of the various elements of the system are independent of the inputs and time, although these properties may vary as the result of changes in the composition and size of the bath during a series of additions. This separation of inputs and the system is equivalent to assuming that the system is linear, i.e., that its behavior can be described by linear differential equations with constant coefficients. Linear behavior can be expected whenever the departure of each portion of the system from its steady-state condition is small enough to cause negligible changes in the thermal properties of the materials and in the various heat-transfer coefficients. Radiative heat transfer is important in this system, so the assumption of linearity should be valid only for small temperature deviations. Several conclusions were drawn from operation of the calorimeter in earlier experimental studies: 1) Radiative heat transport from the top of the bath is a significant portion of the total heat lost from the bath. However, for small changes in the bath temperature the change in transport by this path could be assumed to be proportional to the change in the bath temperature. 2) A very small portion of the heat input is lost through the thermocouple to its water-cooled holder. The thermal resistance and thermal capacity of the thermocouple protection tube are small, so the temperature of the thermocouple should follow closely that of the bath. 3) The remainder of the total heat lost from the bath will pass by conduction through the crucible to, and through, the other refractories, eventually being absorbed by the water-cooled induction coil or by the water-cooled sides and bottom of the enclosure. 4) The thermal resistance between the bath and crucible is very small. Thus the thermal capacity of the crucible will affect the temperature of the bath very soon after an addition of heat to the bath. 5) The thermal resistance between the crucible and the silica sleeve is large, especially if a radiation shield is placed in the gap. The effect of the thermal capacity of the sleeve thus will be significant only at longer times. The thermal resistance through the packing below the crucible also is large, so the packing and the silica sleeve will have similar effects on the behavior of the system. 6) A large temperature drop exists across the gap containing the water-cooled induction coil. Thus for relatively small changes in the thermal input to the bath, the refractories beyond the sleeve

Jan 1, 1970

By P. H. Lindon, J. C. Billington

Fe-O melts containing 0.045 pct 0 were deoxidized with Mn-Si-A1 alloys. Product compositions were reluted to the melt and alloy compositions and were found to be most sensitive to the aluminum content of the alloy. Low residual oxygen contents could be obtained when aluminum oxide was present in the Products because of the reduction of silica and manganese oxide activities. Flotation of the Products from a quiescent melt was followed both by analysis of the oxygen content and metallographic measurement of inclusion concentration. MnO-SiO2-A12O3 products were found to float most rapidly when their composition was such that their viscosity may be expected to be low. Changes in the particle size distribution indicates that particle coalescence occurred and differences in the degree of coalescence are thought to be responsible for the different flotation rates observed between products 0f differing composition. Measured flotation rates were slower than those Predicted from a model based on Stoke&apos;s Law, although alumina flotation might be reasonably accounted for by this model. Interfacial effects between oxide particles and the melt are believed to be responsible for the discrepancy. It has been recognized that deoxidation products constitute a large proportion of the nonmetallic inclusions present in killed steel. The amount of oxide inclusions which originate as deoxidation products depends largely upon three factors. These may be summarized, according to P16ckinger1 as: 1) Amount of primary products remaining in the steel prior to cooling. 2) Residual dissolved oxygen content of the steel after deoxidation. 3) Amount of secondary products, formed during cooling and solidification, which remain entrapped in the solid steel. In a well-deoxidized steel containing residual aluminum and/or silicon, the equilibrium dissolved oxygen content is usually very low and so the maximum amount of oxide which may be produced as secondary deoxidation products is small in comparison with the amount of primary products. It may be seen, therefore, that the amount of indigenous nonmetallic inclusions may be minimized if a low dissolved oxygen content is achieved by deoxidation and if the primary deoxidation products are efficiently removed. Oxides which originate by reaction of the metal stream with the atmosphere during teeming are not considered in the present study. It is known that two or more deoxidizers may result in a lower equilibrium oxygen content when used in conjunction with one another than when any of the individual deoxidizers are used alone. Equilibrium studies by Hilty and crafts2 and by Bell3 have shown that manganese increases the effectiveness of silicon as a deoxidizer, and Walsh and Ramachandran4 relate this to a reduction in the activity of silica in the products as the manganese :silicon ratio in the steel increases. It was also shown by Herty&apos;s work on deoxidation of steel by silico manganese alloys,5 that there existed an optimum ratio of manganese to silicon which gave a minimum inclusion content. This ratio was in the range 4:l to 7:l and the (FeO-MnO-SiO2) products formed by such deoxidation practice were found to lie in a composition range having very low liquidus temperatures (1170 to 1250°C approx). The optimum manganese:silicon ratio was then explained by postulating that these fluid products were able to coalesce and that the larger particles formed floated out of the steel very quickly as predicted by Stoke&apos;s Law. The present work examines the effectiveness of various Mn-Si-A1 alloys as deoxidizers and their effects on the composition and removal of primary deoxidation products from a quiescent melt. EXPERIMENTAL TECHNIQUE Approximately 250 g of prepared Fe-O alloy, containing 0.045 to 0.055 pct O, were melted in an alumina crucible and deoxidized at 1550°C by plunging a thin steel cartridge containing the deoxidizer below the melt surface. A high frequency induction furnace supplying current at 8.5 kHz was used to heat a graphite susceptor, the interior of which had been machined to give a wall thickness of 0.85 in. to form a receptacle for the alumina crucible. The iron melt was essentially quiescent as the induced current was concentrated at the external surface of the graphite susceptor by the skin effect. A nonoxidizing atmosphere was maintained over the melt by passing a continuous stream of argon through the lid of the susceptor. The melt temperature was measured before deoxidation, and again at the end of an experiment by means

Jan 1, 1970

By S. N. Singh, M. C. Flemings

Results are presented of a detailed study on the combined influences of ingot dendrite am spacing and thermomechanical treatments on the structure and solution kinetics of high --purity cast and worked 7075 alloy. Solution kinetics were found to depend sensitively on ingot dendrite am spacing and on details of therrnomechanical processing, including amount of reduction and extent of&apos; solution treatment before reduction. An approximate analysis is given for rate of solution of nonequilibrium second phase in the cast and worked structres; results of the analysis are compared with experiment. MICROSEGREGATION in high strength aluminum alloys manifests itself as "coring" (composition differences within the primary aluminum-rich phase), and as interdendritic second phase. The mechanism of formation of the microsegregation is understood, and approximate prediction of the amount of second phase is possible for simple binary systems.1,2 When alloy elements or impurities are present in amounts less than their solid solubility at solution temperature, any phases forming from these elements are termed "nonequilibrium" and can be dissolved by appropriate solution treatment. The rate at which the nonequilibrium phases are removed depends sensitively on their spacing (dendrite arm spacing in the cast material, or band spacing in wrought material). When alloy elements or impurities are present in amounts in excess of their solubility at the solution temperature, second phase particles form an "equilibrium" second phase that does not dissolve in heat treatment and may, in fact, coarsen in such treatment. Usual commercial, high strength, wrought aluminum alloys contain nonequilibrium second phases that were not fully dissolved during ingot processing. They also contain equilibrium second phases resulting from impurities present in amounts greater than their solubility. As has been shown by Antes, Lipson, and Rosenthal,3 and will be demonstrated further in a subsequent paper by the authors,4 significant improvements in mechanical properties of high strength alloys can be achieved by reduction or elimination of these second phases. Methods of elimination are 1) to employ high purity materials to minimize amounts of equilibrium second phase, and 2) to employ suitable thermomechanical processing techniques to fully eliminate nonequilibrium second phases. Work reported herein comprises a study of selected thermomechani- cal processing treatments, and of their influence on solution kinetics of wrought high purity 7075 alloy. EXPERIMENTAL PROCEDURE Melting and Casting. The bulk of the work reported was performed on a single ingot of high purity 7075 alloy. The ingot was 4 in. by 4 in. by 8 in. high, uni-directionally solidified following a procedure previously described.5 The mold was heated to 1350°F before pouring the melt. The bottom chill was carbon coated stainless steel. Water was circulated through the chill after the melt was poured. The 7075 alloy was prepared from high purity virgin material (aluminum, zinc, magnesium) and from master alloys (Al-50 pct Cu, A1-15 pct Cr, A1-5 pct Ti). Final measured melt composition (wt pct) was: Zn Mg Cu Cr Ti Fe Si Al 5.70 2.28 1.35 0.18 0.15 <0.002 <0.012 bal Melting was done in a silicon carbide crucible; all tools were coated with zircon wash to minimize iron contamination; degassing was by bubbling chlorine through the melt. che-rmomechanical Treatments. Detailed studies were made on material taken from a location approximately 13 in. from the chill and 51/2 in. from the chill (i.e., from 1 in. thick slices taken between 1 and 2 in. from the chill and between 5 and 6 in. from the chill). Solution treatment was done at 860°F in an air-circulating furnace with a "bottom drop" arrangement to achieve minimum delay time between solution treatment and quench. Samples solution treated in this way were 2 in. by 2 in. by 1 in. Temperature of the quench water was approximately 10°C. Mechanical reduction was by cold rolling. Samples 11/2 and 51/2 in. from the chill were treated for 12 and 24 hr, respectively, before cold rolling. Reduction by cold rolling was then 4/1, 16/1, and 35/1. In each case, several intermediate anneals (1/2 hr at 860°F) were used to permit reaching the final thickness without cracking; two such anneals were used for the 4/1 reduction, five for 16/1, and six for 35/1. After working, materials were again solution treated for various lengths of time from 0 to 48 hr and quenched in water. Structural Measurements. Secondary dendrite arm spacings were measured using procedures previously described.&apos; For each measurement reported, five photomicrographs were first made at X75. Measurements were made of dendrite arm spacings in at least 20 different grains (grain structure was equiaxed). Grain size measurements were made by running a number of random traverses across photomicrographs of the samples and obtaining the mean lineal intercept. Measurement of the volume percent of second phase and porosity was done by quantitative metallography. A two-dimensional systematic point count was used

Jan 1, 1970

By R. J. Fruehan, F. D. Richardson

Electrochemical measurements have been made of the activity of oxygen in copper and its alloys with silver and tin at 1100" and 1200°C. The galvanic cell used was Pt, Ni + NiO/solid ellectrolyte/[O] in metal, cermet, Pt The results do not support any of the equations so far designed for predicting the activities of dilute solutes in ternary solutions from activities in the corresponding binaries. If, however, a quasichemical equation is used with the coordination number set to unity, agreement between observed and calculated activities shows that this empirical relationship can be useful over a fair range of conditions. SEVERAL solution models have been proposed for predicting the activity coefficients of dilute solutes in ternary alloys from a knowledge of the three binary systems involved. Alcock and Richardson1 have shown that a regular model, and a quasichemical model,&apos; in which the dissolved oxygen is coordinated with eight or so metal atoms, can reasonably predict the behavior of both metal and nonmetal solutes when the heats of solution of the solute in the separate solvent metals are similar. But when this is not so, neither model gives useful predictions unless coordination numbers of one or two are assumed. Wada and Saito3 subsequently adopted a similar model to derive the interaction energies for two dilute solutes in a solvent metal. Belton and Tankins4 Rave proposed both regular and quasichemical type models in which the oxygen is bound into molecular species, such as NiO and CuO in mixtures of Cu + Ni + 0. However, their models have only been tested on systems in which the excess free energies of solution of the solute in the two separate metals differ by a few kilocalories. Ope of the reasons why more advanced models have not been proposed is because few complete sets of data exist for ternary systems in which the solute behaves very differently in the two separate metals. For this reason measurements have been made of the activities of oxygen dissolved in Cu + Ag and Cu + Sn. Measurements on both systems were made by means of the electrochemical cell, Pt, Ni + NiO/solid electrolyte/O(in alloy), cermet,Pt [1] The activity of oxygen was calculated from the electromotive force and the standard free energy of formation of NiO, which is accurately known.5 Before investigating the alloys, studies were made of oxygen in copper to test the reliability of the cell and to check the thermodynamics of the system. Of the previous studies those by Sano and Sakao,6 Tom-linson and Young,7 and Tankins et al.8,7 have been made with gas-metal equilibrium techniques; those by Diaz and Richardson,9 Osterwald,10 wilder," Plusch-kell and Engell,12 Rickert and wagner,13 and Fischer and Ackermann14 have been made by electrochemical methods. EXPERIMENTAL The apparatus employed was the same as described previously,9 apart from slight modification. The molten sample of approximately 40 g was held in a high grade alumina crucible 1.2 in. OD and 1.6 in. long. The solid electrolytes were ZrO2 + 7½ wt pct CaO and ZrO2 + 15 wt pct CaO; the tubes 4 in. OD and 6 in. long were supplied by the Zirconia Corp. of America. They were closed (flat) at one end. In one experiment with Cu + O, both electrolytes were used in the cell at the same time. The reference electrodes inside the electrolyte tubes consisted of a mixture of Ni + NiO. They were made by mixing the powdered materials and pressing them manually into the ends of the tubes, with a platinum lead embedded in them. The tubes were then sintered overnight in the electromotive force apparatus at 1100°C. By sintering the powders inside the tubes (instead of using a presintered pellet9) better contacts were obtained between the electrolyte, the powder, and the platinum lead. Troubles arising from polarization9 were thus much reduced. The electromotive force was measured by a Vibron Electrometer with an input impedence of 1017 ohm; the temperature was measured with a Pt:13 pct Rh + Pt thermocouple protected by an alumina sheath. The couple was calibrated against the melting point of copper. The cermet conducting lead of Cr + 28 pct Al2O3, previously found to be satisfactory9 for use with Cu + 0 was also found satisfactory with Cu + Ag + 0 and Cu + Sn + 0. Superficial oxidation was observed, but it did not interfere with the working of the cell. The reaction tube containing the cell was closed at each end with cooled brass heads and suspended in a platinum resistance furnace. The tube was electrically shielded by a Kanthal A-1 ribbon which was wound round it, and the ribbon was protected by a N2 atmosphere between the furnace and the reaction tube. The cell was protected by a stream of high purity argon which was dried and passed through copper gauze at 450°C and titanium chips at 900°C. All the metals used were of spectrographic standard. Procedure. In studies of the system Cu + 0, be-

Jan 1, 1970

By R. E. Cech, T. D. Tiemann

It has been shown that hydrogen may be made to serve as a rapid and eflicient reducing agent for Cu, Ni, Co, and Fe sulfides if a scavenging agent for hydrogen sulfide is intimately mixed with the sulfide particles being reduced. Accelerated reduction kinetics are demonstrated for nickel sulfide. Copper, nickel, and cobalt sulfides, when treated at certain temperatures in a combined reducing agent-scavenging agent system, are converted to voluminous masses of fibrous metal product. Studies have been carried out to determine the conditions which lead, on the one hand, to irregular poly crystalline fibers and, on the other, to long single crystal filaments a few microns in diameter. A mechanism is proposed to account for the formation of single crystal filuments. The sulfide minerals of Cu, Ni, Co, and Fe are an important source of these metals yet there has been comparatively little scientific effort devoted towards understanding reduction mechanisms of these minerals. This may be, in part, due to the fact that the most convenient reducing agents for carrying out such studies, viz., hydrogen and carbon, do not react appreciably with sulfides. We have found that the reaction of hydrogen with metal sulfides can be markedly accelerated by placing a scavenging agent for hydrogen sulfide in close proximity to the metal sulfide. A brief series of experiments demonstrating relative reduction rates is reported in this paper to illustrate the effect. With the reduction process thus accelerated we have observed an unusual type of reduction behavior on some of the sulfides investigated. Under certain conditions the metallic product of the reduction reaction takes the form of filaments growing outward from the sulfide particles. The present paper deals largely with efforts to classify the various types of growth forms observed. This study has shown that filamentary growths from sulfides take a much greater variety of forms than has heretofore been reported by Ercker,1 Hardy,2 and Nabarro and Jackson3 in their reviews of metallic growths from copper and silver sulfides. THERMODYNAMIC CONSIDERATIONS The thermodynamics for hydrogen reduction of metal sulfides is quite unfavorable. For the sulfides considered here equilibrium constants typically range from 10-3 to 10-5. These low equilibrium constants impose severe kinetic limitations on reduction since hydrogen sulfide must be transported out of the system at concentrations of only a few hundred ppm. Unless extremely high gas flow rates are employed the atmosphere surrounding any sulfide particle will always be essentially in equilibrium with the sulfide. If, however, one places an efficient scavenging agent for hydrogen sulfide in close proximity to the metal sulfide particles the concentration of H2S near the metal sulfide will be held to a very low value. This would permit the reduction reaction to proceed with little or no inhibition from a buildup of reaction product gas. It is well known that calcium oxide is capable of removing hydrogen sulfide from a hydrogen gas stream of low dew point.4 If a sufficient quantity of calcium oxide is mixed with the metal sulfide particles the reaction: CaO+H2S=CaS+ H2O [l] will substitute moisture in place of hydrogen sulfide in the gas stream and this will not affect, in a direct manner, the reaction: MeS +H2=Me + H2S [2] A convenient method of considering the thermodynamics of the combined reducing agent-scavenging agent system is to consider the atmosphere when the partial pressure of hydrogen sulfide is the same over both the metal sulfide and the scavenging agent, i.e., pH2S (1) =pH2S (2). As a consequence: pH2O (1) pH2(2) =K1K2 The chemical driving force for reduction will depend inversely upon the moisture content of the gas and will be 0 when, in the system, pH2O = pH2.K1K2. Table I lists values of the equilibrium constants for reduction and H2S scavenging reactions for a number of sulfides at several temperatures. Data are taken from Rosenqvist4,5 and Kelly.6 The equilibrium constant products calculated from this data show that the limiting level of gaseous reaction product has been increased by a factor of 10&apos; to l04 as a result of substituting a reducing agent-scavenging agent system for a simple reducing agent system. One possible side effect which must be considered is the possibility that the moisture evolved in the scavenging reaction might cause the atmosphere in the system to be sufficiently oxidizing to favor the formation of oxide rather than metal. This possibility was examined by comparing the equilibrium constant products listed in Table I with equilibrium constants for hydrogen reduction of the respective metal oxides. It was found that for copper, nickel, and cobalt the combined reduction-scavenging reactions could not develop a sufficiently high oxidizing potential in the

Jan 1, 1970