By W. E. Bron, E. S. Machlin

GRAIN boundary migration in V-shaped thin specimens of high purity silver was studied. Each specimen contained two crystals having the relative orientation: (111)A/(111)B; (ll0)A/(101)B. The boundary between these two crystals varied between a continuous curved and an alternating two plane interface. The plane interfaces were oriented parallel to (101)A/(011B) and (121)A/(211)B. Traces of these planes are shown in Fig. 1. Evidently the two plane interface, although of higher area, comprises lower total interface energy than the average curved boundary it replaced. The plane boundaries were found to move at 650 °C to consume the broad segment of the V opposite to the direction of interface area and energy decrease. On investigation, using the thermal etching technique of Hendrickson and Machlin,1 it was found that the outer grain contained 8.3x108 more dislocations per cm" than the grain at the apex of the V. Consequently, the boundary moved to decrease the strain energy associated with the difference in dislocation density across the boundary. The rates of motion of specific {110} and {112} boundaries were measured during interrupted anneals at 650°C by referring the position of the boundaries to each other and a fiducial line on the specimen surface. The measured rates of motion are 0.075 and 0.025 mm per hr for the {110} and {112} boundaries, respectively. Plots of grain boundary motion vs time of annealing show straight lines with little deviation of data points from these lines.

Jan 1, 1957

By P. R. Sperry, P. A. Beck, J. Towers

Dahl and Pawlek1 found that electrolytic copper develops extremely coarse grains at 1000°C after about 90 pct reduction by rolling. This coarsening occurs only under conditions of penultimate grain size, deformation, and alloying which lead to the "cube" recrystallization texture.l,2,3,5 The peculiar angular shapes and straight grain boundaries of the coarse grains were noted by several investigator.1,4,5 On the other hand, coarsening in Fe-containing aluminum or in AI-Mn alloys8 does not depend on a "cube" (or any well developed) recrystallization texture. It is true that increasing deformation by rolling, and, therefore, an increasingly well developed re-crystallization texture, are associated with decreasing incubation periods of coarsening.6-7-8 Nevertheless, coarsening readily develops in aluminum even after only 30 pct reduction by rolling, where the recrystallization texture is very weak.6,8 Also, coarsening was observed by Jeffries9 many years ago in sintered thoriated tungsten, which presumably has no preferred orientation. In all these cases coarsening is associated with grain growth inhibition by a dispersed second phase.8,9 The annealing temperature has to be suficiently high to overcome the inhibition at a few locations. But if it is too high, growth starts at many points, and the resulting grain size becomes much smaller.9 Normally, the coarse grains are more or less equiaxed, and the boundaries have a typical ragged appearance.6.8 Cook and Macquarie4 demonstrated that, in addition to the texture-dependent coarsening previously found at 1000°C,l electrolytic tough pitch copper may also coarsen at 800°C after 50 pct reduction by cross rolling. The coarse grains formed under such conditions have rounded shapes and ragged boundaries, like those in aluminum. When the annealing temperature is higher, the tendency for their formation decreases. All these observations suggest that the coarsening at 800°C is associated with inhibition by a second phase. Actually, coarsening at 800°C after 50 pct reduction by cross rolling was observed only in tough pitch copper,4 which contains Cu2O particles. On the other hand, the texture-dependent 1000°C coarsening occurs in both tough pitch and oxygen-free copper;4 it does not appear to depend on the presence of a dispersed second phase. However, the interpretation of the 800°C coarsening in Cu after 50 pct rolling as an inhibition-dependent process, similar to the coarsening in A1-Mn alloys, is somewhat weakened by the fact that this coarsening was reported4 to occur only after cross rolling, and not after straight rolling. It was, therefore, decided to re-examine this question. A 1 in. diam electrolytic tough pitch copper rod, No. 2 hard drawn, was annealed for 20 min at 700°C, rolled to 0.5 in., annealed 10 min at 700°C, and straight rolled to 0.064 in. It was then given a penultimate anneal of 20 min at 500°C and it was cut into four sections, which were given final reductions by straight rolling as follows: A 30 pct reduction of area B 50 pct reduction of area C 70 pct reduction of area D 90 pct reduction of area Specimens cut from the four sections were finally annealed at 800°C in an oxidizing atmosphere. Strip A remained fine grained up to 10 hr, but the specimen annealed 12 hr consisted of only 2 large grains. Strip B had a few scattered large (1/2 to 3/4 mm) grains after 1 min, although the balance of the specimen consisted of fine grains of about 0.02 mm. After 5 min there were several 10 to 15 mm grains present, and after 1 hr strip B was completely coarsened. The coarse grains had the same characteristics (see Fig 1) as those obtained by Cook and Macquarie at 800°C after cross rolling. Strip C had several grains of 0.05 to 1 mm after 1 min, but it was still largely fine grained after 12 hr. After 48 hr it consisted entirely of grains of about 0.5 to 4 mm, with an extraordinarily large number of twin bands. Strip D remained com- pletely fine grained after 4 hr at 800°C. These results indicate that, in the deformation range of 30 to 70 pct reduction, the incubation period for coarsening as well as the rate of growth and the final size of the coarse grains decreases with increasing deformation. Similar

Jan 1, 1950

By A. E. Nehrenberg

IN an earlier publication' it was shown that the.. shape assumed by a volume of growing austenite is inherited from the prior structure. The matrix grains of pearlitic microstructures are equiaxed, and austenite grows in an equiaxed manner in these prior structures. Martensite and bainite, on the other hand, have an acicular grain structure, and the austenite produced in such structures grows in an acicular manner. In the discussion of this paper' it was pointed out that in cold-rolled tempered martensite, austenite grows in an equiaxed, rather than an acicular manner. The results of an experiment carried out to arrive at an understanding of this behavior are illustrated by the micrographs. Fig. 1 shows the acicular microstructure produced by heating tempered martensite to a temperature within the Ac1-Ac3 range, 1350°F. When tempered martensite is cold rolled, then heated to the same temperature, the equiaxed structure shown in Fig. 2 is produced. A sample of cold-rolled tempered martensite heated at 1350°F just long enough for the formation of a small amount of austenite is shown by Fig. 3 to have an equiaxed (recrystallized) ferrite grain structure. The small particles of. austenite which formed at 1350°F in the equiaxed ferrite matrix are likewise equiaxed. Thus, the equiaxed growth of austenite in cold-worked tempered martensite is not a contradiction of the principles described in the previous paper, for the growth pattern reflects the matrix grain structure existing at the time of austenite formation. References A. E. Nehrenberg: The Growth of Austenite as Related to Prior structure. Trans. AIME (1950) 188, pp. 162-174; Journal of Metals (January 1950). 2 J. R. Vilella and R. A. Grange: Discussion of ref. 1. Trans. AIME (1950) 188, pp. 1378-1381; Journal of Metals (November 1950).

Jan 1, 1953

By Howard Martens, Pol Duwez

XPERIMENTS were performed on a Cr-Fc alloy Econtaining 44.7 pet Cr in order to determine the heat evolved during the transformation of the a solid solution into the s phase, and the change in volume accompanying the transformation. Since previous measurements on the rate of formation of a from s indicated that the reaction was quite fast as soon as the equilibrium temperature of 820°C was exceeded by some 50°, standard thermal analysis experiments were performed on heating specimens of s at the rate of approximately 40°C per sec. A definite thermal arrest was observed at 870"C, Fig. 1. This result indicates that the reverse seaction of into a is exothermic. From the heating curve of Fig. 1, taking 15°C per sec as the heating rate in the neighborhood of the transformation, 2.4 sec as the time for transformation, and assuming that the specific heat of the alloy at 850°C is an average between iron and chromium, namely 9.5 cal per mol per "C, the latent heat of transformation is approximately 342 cal per mol. The order of magnitude of this latent heat was also obtained by comparing the heating curve of Fig. 1 with a similar curve obtained with pure iron under identical experimental conditions. It was found that the length of the thermal arrest for s was about 1.8 times as long as that for iron. Since the latent heat of the a to 7 iron transformation is 203 cal per mol1, 2 the latent heat of it to a would be 365 cal per mol, which is in relatively good agreement with the value determined from the heating curve. For the determination of volume change, thermal expansion curves were recorded using a specimen containing 44.7 pet Cr and completely transformed to cr by previous treatment. The curves were recorded at a rate of heating of about 4°C per min and at approximately 840°C a sharr, increase in length of about 0.08 pet took place. Fig. 2. It is therefore established that the specific volume of a near the transformation temperature is about 0.24 pet smaller than that of a, and consequently, when the s phase forms in an a matrix, it would tend to shrink away from the matrix. Since the s phase is known to be extremely brittle, these results offer an explanation for the microscopic cracks often observed in the a phase under the microscope. The results of this study are in qualitative agreement with previously published data on stainless steel 19-9DLa and on a Cr-Fe alloy containing 45 pet Cr.' The increase in density due to the transformation from n to s given in ref. 4 is 0.90 pet. These measurements, however, were made at room temperature. whereas the presently reported 0.24 pet is the change at the temperature at which the transformation takes place during heating. In the graph of Fig. 2, the percentage change in length that would be observed at room temperature is given by the length X, which is about 0.27 pet. This would correspond to 0.81 pet in volume change. Acknowledgment This work was done at the Jet Propulsion Laboratory, California Institute of Technology, under Contract No. DA-04-495-ORD-18 with the Army Ordnance Corps, Washington, D. C. The authors wish to thank this agency for permission to publish the results of this investigation. References I H. Klinkhardt: Measurements of True Specific Heats at High Temperatures. Annalen der Physik (1927) 84, pp. 167-200. - H. Esser and W. Runghardt: Influence of the Method, of Dctcrmination on the Measured Heat Content of Iron. Archtvo ffur Dct Eisenhiittenwesen 11934) 8, pp. 37-38. J. J. Gilman, P. K. Koh, and 0. Zmeskal. Delta Ferrite Formation and its influence on the Formation of Sigma in a Wrought Heat Resisting Steel. Trans. ASM 1 1949) 11, pp. 1371-1388. 1 J. M. Thomas: Discussion of ref. 3. Trans. ASM (1949) 41, pp. 3 390-1392.

Jan 1, 1957

By L. D. Jaffe

THE data recently published1-" on heat treatment of titanium alloys have not been readily systematized into an overall picture. When the ß titanium phase transforms isothermally at low temperatures, the hardness follows a typical age-hardening pattern, going through a peak as schematized by the "hardness" vs "time of isothermal transformation" coordinates of Fig. 1. As the temperature is raised, the peak will decrease in height and occur at shorter times; slowing must however take place as the /3 transus is approached. The brittle microconstituent in the region of peak hardness has been termed /3'. Its structure is still undetermined but it is clearly a transition stage from soft /3 to the £ + a that is found at the right of the peak. On continuous cooling, high cooling rates correspond to short times on Fig. 1; abscissa labeling has been added accordingly. Extremely rapid cooling will retain soft /3; very slow cooling will precipitate soft a; intermediate rates give hard 8'. Increasing distance from the water-quenched end of a Jominy hardenability bar corresponds to slower cooling (right on Fig. I), but the range of cooling rates covered by a Jominy bar is only a small portion of that shown in the figure. The p-stabilizing alloying elements retard the transformation process, moving the material to the left on Fig. 1. A lean alloy is harder water-quenched (P') than air-cooled (/3 +a); a rich alloy is harder air-cooled (/3') than water-quenched (/3). Examples of the position of various compositions with respect to the curve, based on limited data in the literature, are given at the top of the figure. Oxygen and carbon accelerate the transformation process, moving the material to the right on Fig. 1. If an alloy quenched quickly enough to retain soft /3 is reheated below the £ transus (tempered), it ages, going through a hardness maximum as time increases (moving right on Fig. 1). Material which after cooling from the /3 range lies on or right of the hardness peak, will move still further right on tempering, and so soften. Since the rate of the tempering (aging) reaction increases with temperature, the figure also may be used to represent the variation in properties with tempering temperature, at short tempering times. The simple picture given here neglects martensite transformation, as well as differences between decomposition products of /3 formed by direct isothermal transformation and those formed by quenching and tempering. It may nevertheless be of use as a guide for practical heat treatment and for further research.

Jan 1, 1955

By H. J. Oberson, J. H. Brown

Comminution devices such as rod or ball mills are characteristically nonselective in their operation in that all material fed to a mill is ground to some extent. This is unfortunate when the object of comminution is liberation, for not only is energy expended in breaking pure gangue particles wasted, but, since gangue is frequently the predominant phase, the opportunity for such loss is great. Ideally, in this application a comminuting device should develop fracture only in locked particles. In the present investigation an attempt was made to use the large density difference which may exist between minerals to prevent comminution of one while grinding the other. EXPERIMENTAL MATERIALS AND EQUIPMENT The two minerals used in this work were -8-mesh galena and -8+ 20-mesh quartz. All tests were made on 2000-g charges containing 50 pct by weight of each mineral. Heavy media suspensions consisted of -100-mesh ferrosilicon in water. For grinding, a laboratory mill 10 in. diam by 12 in. long was filled to about 30 pct of its volume with either a ball or a rod charge. The balls ranged in size from 3/8 to 1 1/8 in. in diam; the rods ranged from 5/8 to 1 1/4 in. diam by 11 in. long. EXPERIMENTAL PROCEDURE In all tests employing heavy media, the ground pulps were treated as follows: 1) After recovering the ground charge from the mill but before drying, the pulp was wet screened on 200 mesh. 2) After drying the + 200-mesh product from step 1, the ferrosilicon was removed magnetically. 3) The nonmagnetic quartz and galena product from step 2 was sized on 10-mesh through 200-mesh screens. 4) The mineralogical composition of each screen fraction was determined by measuring its specific gravity. The specific gravity was related to the weight of galena in the fraction through the relationship

Jan 1, 1961

By J. R. Spencer

When supplies of high pressure mercury or other liquids are required in analytical work, it is convenient to have the source of supply at a relatively constant pressure and available in sufficient volume to satisfy the requirements of the apparatus in use. It is also desirable that the pressuring device be as simple and as inexpensive as possible and convenient to operate. This pump combined with a small storage reservoir containing gas under pressure has the attributes of (1) positive control of the maximum output pressure through the use of a regulator in the low pressure air supply; (2) an increasing capacity as the rate of withdrawal of mercury from the pressured system is increased; and (3) simplicity, requiring only the use of a lathe, drill press, and welding unit in its construction. DESCRIPTION Essential parts of the pump are shown in Fig. 1. In appearance the unlt is similar to the usual steam pump in common use in industrial applications although considerably smaller in size. The main differences lie in the area ratio of the air and mercury pistons and in the design of the air valve mechanism. Approximate diameters of these pistons are 4.25 in. to 0.375 in. respectively, giving an area ratio of about 130 to 1. The air piston (2) is attached to the end of shaft (4), with the mercury piston being merely a reduced extension of the shaft. Mercury intake and discharge to the pump are controlled by high pressure check valves that screw into the ports indicated at (6). Air supply is controlled by the valve assembly mounted on top of the

Jan 1, 1950

By L. Thomassen, N. Spooner, J. M. Thomas

NI-CR and some Ni-Cr-Fc alloys, when used as electrical resistance heating elements in reducing atmospheres, at times suffer rapid breakdowns due to so-called "green rot." These reducing atmospheres are most frequently used in bright annealing and heat-treating furnaces which are kept for long periods of time at 1500' to 1800°F. The green rot is a preferential oxidation of the chromium in the alloy to such an extent that the remaining metal frequently becomes ferromagnetic. The Curie point (magnetic transition point) at room temperature for a pure Ni-Cr alloy is known to be at about 7 pct Cr.¹ This represents a severe loss in chromium for one popular grade of resistance alloy, which is nominally 80 pct Ni-20 pct Cr. The formation of oxides along the grain boundaries makes the ribbon brittle and gives the fracture a green, earthy appearance—hence the name. The authors have studied this phenomenon, simulating the industrial conditions by heating resistance ribbons in various reducing atmospheres, such as moist hydrogen or the atmosphere specified in the ASTM test.² This atmosphere contains 16 pct H2, 10 pct CO, 4 pct C02, 1 pct CH1, 1.5 to 2.5 pct H2O, balance N2. Little success was had in producing severe corrosion with the commercial 80 pct Ni-20 pct Cr alloys. It had been noticed, however, that 90 pct Ni-10 pct Cr alloy wires deteriorated very rapidly when placed in the bottom of narrow thermocouple protection tubes. The bottoms of the tubes with the wires were heated in air. This took place both in porcelain tubes and in Inconel* tubes either with the cold end open or loosely stoppered with asbestos. On examination the wires showed microstructures which would be classified as green-rot corrosion. Subsequent investigations with various alloy wires confirmed the observation that corrosion occurred in some wires, including 80 pct Ni-20 pct Cr alloys, much more rapidly in such tubes than had occurred previously in test atmospheres mentioned above. When 90 pct Ni-10 pct Cr alloys are oxidized with an abundant air supply, the oxide coat consists of both nickel and chromium oxides. In this case thermodynamic equilibrium between the oxides is not established. However, when oxidized 90 pct Ni-10 pct Cr alloy specimens were heated to 1500" to 1800°F inside small diameter tubes, the oxide coat transformed to a bright metallic outer layer of nickel or nickel-rich alloy, beneath which appeared a green oxide, followed by intergranularly attacked metal. The obvious explanation is that in the narrow tubes, thermodynamic equilibrium is being established according to the equation NiO + Cr (in alloy) ? Ni + Cr2O3 This reaction is favored due to the fact that the oxygen pressure over nickel oxide is more than 10"' times the oxygen pressure over the green chromium oxide. The initial oxygen in the tubes is depleted very rapidly by oxidation of the wire and of the tube, if it is metallic. A confirmation of the occurrence of the reaction, reduction of NiO by the chromium in the alloy, was obtained by putting oxidized nickel foil into an evacuated quartz tube along with a piece of bright 90 pct Ni-10 pct Cr alloy ribbon, and heating the tube at 1820°F for a number of hours. The nickel oxide on the foil was completely reduced to pure nickel, leaving a bright foil. The 90 pct Ni-10 pct Cr alloy became strongly magnetic and showed the typical green-rot structure. Weights of the samples before and after testing showed the weight loss of the foil to approximately equal the weight gain of the ribbon. Evidently the bottom of long, narrow protection tubes, stoppered or not, may under certain conditions act just as the sealed quartz tubes in respect to being a confined space in which oxygen is not freely replenished. This condition of oxygen depletion can be prevented by introducing a small amount of air into the bottom of the tube. Many conditions becloud the green-rot phenomenon, such as carburization, sulphidization, and the presence of other corrosive agents. However, these experiments have shown that the basic reaction is a case of internal oxidation which can occur simply by adjusting the oxygen pressure to a low enough level so that the atmosphere will leave the nickel intact and oxidize the chromium. The action of the other agents in commercial atmospheres can then be taken up as individual cases. From these and numerous other tests completed to date or still in progress, it is believed that a more critical evaluation of electrical resistance alloys for their resistance to green-rot corrosion can be made. A much better understanding of the mechanism for this type of corrosion should also result. A more complete report on these experiments will be published later. In the May 1953 issue: TP 35213 Discussion: Solubility of Carbon and Oxygen in Molybdenum by W. E. Few and G. K. Manning, discussion by N. A. Gokcen: p. 747, first column, the fifth, sixth, and seventh lines should be the first, second, and third lines, followed by the present first, second, third, fourth, eighth, ninth, and tenth lines.

Jan 1, 1954

By W. M. Baldwin, C. R. Johns

Cobalt is reported1,2 to scale in accordance with the Pilling and Bed-worth3 parabolic law: where w = weight increase per unit surface area K = constant l = time The reported values of the parabolic oxidation constant, K, in the temperature range 600 to 1100°C follow an Arrhenius type of equation as inspection of Fig 1 shows. According to Valensi's theory5 on the scaling of metals where multiple-layered scales (for example, MeX, MeX2, and others) are possible, this fact could be construed as indicating that a single oxide only is formed on cobalt in this temperature range. Since the single straight line extends above 920°C where only CoO is stable in air (see Fig 2) it might be inferred that this is the only oxide formed on scaling. Arkharov and Voroshilova10 have studied the scales formed when cobalt is heated in air in the temperature range 385 to 800°C and report that CoO is indeed found in the scale but that CoO4 is also found as an overlay and in increasing amounts in the lower temperature ranges. No quantitative data regarding the relative proportions of the two oxides were reported. Again in the light of Valensi's theory this would indicate that the straight line in Fig 1 would be expected to undergo an inflection at some point in the temperature range 385 to 800°C. Chauvenet2 has studied the oxidation rates of CoO to Co3O4 and has found this reaction to proceed parabolically with time but reports parabolic scaling rates which are considerably (about ten times) larger than the scaling rates of cobalt metal itself. This is difficult to explain in terms of Valensi's theory although a full discussion of the possible discrepancy cannot be made in view of the lack of sufficient data. These points made an investigation of the scaling behavior of cobalt in air an attractive study. Discussion of Results Relatively large (approximately 95 sq cm of surface area) samples of 0.020 in. thick electrolytic cobalt strip,* sanded with 2/0 paper, were heated in air in a cyclone type furnace. The samples were weighed before and after the scaling treatment. The weight increases so observed obeyed the Pilling and Bedworth parabolic law at all temperatures studied. The parabolic scaling constants when plotted on a logarithmic scale as a function of absolute temperature are reproduced

Jan 1, 1950

By C. E. Sims

IN an earlier paper by Sims, Moore, and Williams: data were given to show that hydrogen contents of 0.3 relative volume (0.00033 wt pct), existing at the center of 4-in.-square cast-steel coupons, could be removed by aging at 400°F for 125 hr. At the end of that time, complete restoration of normal ductility for the steel was obtained. Replicate specimens of the same steel were aged at room temperature up to 555 days or .18 1/2 months. At the end of that time, the hydrogen content at the center had fallen to 0.13 relative volume or 0.00015 wt pet, but there was no perceptible change in the ductility. On the basis of experience with accelerated aging of 1-in. and 4-in. coupons and room temperature aging of 1-in. coupons, it was predicted that, some time after two years and when the hydrogen content has been reduced to about 0.10 relative volume, there would be some recovery of ductility. One set of three bars remained, and these were held for 1310 days, or more than three years. Then tensile test bars were cut from the center, and these bars were sampled for hydrogen analysis at the time they were broken. The sample specimens were cylinders % in. in diam x 1 1/4 in. in length. The data showed that in this time the average hydrogen content had fallen to 0.096 relative volume or 0.00011 wt pct, and the ductility had increased sharply. Elongation had risen from 10 to 17.3 pct, while reduction of area increased from about 16 to 27.5 pct. On the basis of these data, fig. 1 was drawn to replace fig. 15 of the earlier paper. Extrapolation of the curves of fig. 1 indicates that it would require a period of about 2200 days or approximately six years at room tem- perature to reduce the hydrogen to the minimum value and to recover full ductility in the center of the coupons. The aging process apparently involves the movement of hydrogen from the interior to the surface of the bar and evaporation at the surface. This flux of gas presumably follows some diffusion mechanism, and an effort was made to use the aging data, obtained at room temperature and at 400°F, to calcu-late coefficients of diffusion, in the hope that they might indicate the nature of the diffusion. The conclusion was reached. however. that the data were inadequate for such a purpose.

Jan 1, 1951

By J. B. Gayle

PRESENT flotation processes depend almost entirely on the buoyant properties of air bubbles to effect separations of mineral and gangue, but there is no convenient method for measuring aeration in flotation cells. Consequently the relation between aeration and cell performance has not been definitely established. In connection with a comparative study of kerosene and froth flotation processes, a modification of the displacement method' was developed in which air escaping from the cell surface is measured with a wet-test meter. The arrangement shown in Fig. 1 is satisfactory for use with a number of cells and is not critical, except that care must be taken to use connections and tubing large enough to avoid excessive back pressures. Attempts to use smaller tubing resulted in back pressures that caused displacement of the liquid level in the receiver, so that some air was lost around the sides, an occurrence readily visible when measurements were taken with only water passing through the cell. With the arrangement shown, the manometer indicated an average reading of about 1/2-in. water pressure. No loss of air was evident. Fig. 2 presents typical data for a standard Denver sub-A 24x24-in. unit cell operated at impeller speeds from 0 to 710 rpm. Each plotted point represents the average for five readings distributed over the entire cell surface. Readings were taken with only water passing through the cell. Results of this type have been used in a study of the influence of operating variables on cell performance and in detecting inherent differences in the operating characteristics of cells of various kinds. Although the information presented in Fig. 2 resulted only with water passing through the cell, the apparatus is suitable for use during flotation of coal when various reagents are present. Possible modi- fications that might prove convenient under special circumstances include varying the size and shape of the receiver and substituting a calibrated, inverted, water-filled carboy or other gas-measuring device for the wet-test meter. If such modifications result in excessive back pressures, some form of draft should be applied at the discharge end of the measuring system.

Jan 1, 1959

By H. E. Stauss, G. Sandoz

AN increase in the value of magnetostriction1 * is known to result from the annealing of some ferromagnetic alloys in a magnetic field. Similar increases may be anticipated in the value of the magnetostriction of alloys that are of interest because of their normal high values. Two were selected for trial, 87 pct Fe-13 pct Al(Fe,Al) and 69 pct Co-31 pct Fe, the latter being used as a representative of the Co-Fe alloy series. The influence of a magnetic field present during annealing is explained by the domain theory of magnetism." The field orients the domain vectors in its own direction when the alloy is at or below the Curie temperature, and holds them there until the metal is cold. During cooling the interaction stresses between neighboring grains are largely relaxed. Interaction stresses will reappear, however, if the state of magnetization of the specimen is changed in any way, and will be larger the more the new state of magnetization differs from the one existing during the magnetic anneal. In this connection the 180" reversal of a magnetization vector is not considered a change because a simple reversal does not tend to produce a change in shape of a magnetized region. When the field existing during the anneal is removed after the metal is cold, the domain vectors can turn back only to the nearest crystallographic directions of easy magnetization because return to random

Jan 1, 1953

By T. lkeda, R. S. Montgomery. A. Hara

Actual test specimens used in the previous laboratory wear investigation,' were fully characterized and the data is given in Table 1. Most of the carbides tested could be placed into groups of similar mean grain size. When the wear rates of the members of these groups were plotted as functions of their hardnesses, a family of curves resulted; curves for groups containing data from larger grained composites were at lower wear rates at the same hardnesses. Most specimens tested showed only A-1 porosity (ASTM Standard designa-

Jan 1, 1971

By Roscoe C. Clark

A study of the effect of various corrosive waters on five different types of cements indicated that those cements containing less than 5 per cent tricalcium aluminate were the most resistant to corrosion. INTRODUCTION Oil field experience indicates that some formation waters are excessively corrosive to some cements. A study has been made to determine the most corrosive waters and the relative resistance of various types of cement to these corrosive waters. PROCEDURE This study of the corrosion of cement was limited to an evaluation of the effect of various corrosive waters on five different types of cements. A determination was made of the types of cements which offer the greatest resistance to corrosion and of the chemical contents of waters found to be the most destructive to cements. The laboratory tests were conducted by immersing small cylinders of 20 samples of set cement in various corrosive waters. The initial mixing of most of the cement slurries was done using Tulsa tap water as the mixing water; however, a few of the slurries were mixed using a sulfate water as the mixing water. When the 20 samples had been immersed for a period of nine months, they were removed from their corrosive baths, inspected and photographed. The field tests were conducted by placing ten cement specimens, each contained in a screen wire thimble, in the gas anchors of insert pumps in wells in six different fields. The specimens were observed whenever it was necessary to pull the pumps and were returned to the 1aboratory when deterioration had reached a serious state. EXPERIMENTAL RESULTS In both the field and laboratory tests the resistance of the different cements to corrosion was determined by the condition of the samples and the number of samples of each that were in good condition at the end of the immersion period. Table I lists the various cements tested in the order of their resistance to corrosion with the most resistant at the top and the least resistance at the bottom. An analysis of Table I reveals that the upper half of the table predominates in slow set and sulphate resisting cement.: (low 3CAO.A12O3 content) while in the lower half the port-land and high early strength cements are in the majority. Of the last two the high early strength cements appear to offer less resistance to sulfate water corrosion. An investigation of the composition of the cements listed in Table I indicated that as a general rule the cements containing less than five per cent tricalcium aluminate will exhibit the greatest resistance to corrosion. The destructive action of various corrosive waters was compared by listing the waters in the order of those containing the largest number of samples that failed completely. These ratings are presented in Table II with the most corrosive waters listed first and the least corrosive last. Figs. 1 and 2 show the end views of cement samples which had been immersed in the baths of five per cent MgSO, water and the five per cent Na2SO4 water respectively in the laboratory. These .pictures are representative of the results obtained and present a pictorial evaluation of the corrosive resistance of various types of cements.

Jan 1, 1950

By P. K. Foh, C. G. Dunn

IN an investigation of the rolling and recrystalliz-ing textures obtained from single crystals of Si-Fe, Koh and Dunn included specimens in the (111) [lie] orientation.1,2 This note reports some additional results obtained on samples of this orientation set aside for further study. After, primary recrystallization longer annealing treatments at 980°C produced only normal grain growth; after 16 hr at 980°C the largest grains were approximately 0.010 to 0.020 in. in diam. The orientations of 13 of the larger grains were found by the transmission Laue method. The unidentified (110) poles of these grains have been added to the (110) pole figure obtained after primary recrystallization2 to give the plot shown in Fig. 1. When grain identifications are also included, such a plot reveals the following. Two orientations agree almost exactly with the peak pole ,density positions of component B of the primary recrystallization texture, one with component A, and one with component C. All the remaining orientations except one have (110) poles near weaker and unidentified pole density peaks. In fact, the correlation is good enough for an identification of eight components. Previously only components A, B, and C were certain. The results are perhaps even more informative when combined with the (110) pole figure of the cold-rolled crystal to give the plot shown in Fig. 2. Each of the 13 orientations is identified and uniquely determined by selecting two (110) poles per crystal, which are 90" apart. The plot shows that every grain of the 13, except grain 6, has a (110) pole in common with a (110) pole concentration of the cold-rolled crystal. The orientation relationship with the cold-rolled orientation may be expressed as approximately 25" rotations about <110> axes, which is in agreement with the results found for coarse-grained primary recrystallization.2 If primary recrystallization had occurred according to the <110> rule without preference, there would have been 12 components. Actually our limited data reveals nine of the possible 12. The integrated pole figure also shows preferences among them, since three are considerably stronger than the rest. In addition to the above direct information, the following conclusions may be drawn. Primary recrystallization of the (111) [110] cold-rolled crystal produces a limited number of weak and strong components with the larger than average primary grains from these components related to the cold-rolled crystal by 25° <110> relationships. In arriving at this conclusion of limited orientations the (111) [110] orientation has to be ruled out as a source of large primaries for two reasons. First, growth in this orientation was not observed, despite an expected high grain boundary mobility (due to its 25" <110> relationship with every component of the texture). Secondly, primary recrystallization usually produces grains in new orientations, particularly in a single orientation matrix; but (111) [110] is not new. Other orientations besides those of the <110> type may be considered unlikely, of course, because the <110> relationship holds quite well for primary recrystallization2 and should produce the large primaries. There are exceptions to this rule, but probably not enough to provide large

Jan 1, 1958

By J. B. Darby, P. A. Beck

IN a previous publication,&apos; the 1200°C isothermal section of the Cr-Mo-CO system was surveyed. It was found that starting from the binary (Cr,Co)a, the u phase extends deep into the ternary system in the form of a narrow band, which, when extrapo-

Jan 1, 1956

By Roscoe C. Clark

In a previous technical note&apos; by Walter Rose, evidence is offered in support of the contention that "the possibility of describing oil recovery features in terms of capillary pressure phenomena has not been established entirely." It is not the purpose of this note to present further discussion of this possibility but rather to point out that the argument presented there does not appear to be generally valid. In the cited note&apos; reference is made to the experiments of Welge2 wherein it was shown that when water was displaced by oil from a core the pressure in the water phase was less than in the oil phase but that when this oil was then produced by water drive the pressure in the water phase was greater than in the oil phase. Rose has concluded from these observations that conditions of static equilibrium did not obtain since the fluid saturations were such that phase discontinuities seemed unlikely. The argument from which this conclusion was drawn is based on the contention that "the pressure is always greatest in the non-wetting phase at each static interstitial interface of contact with the wetting phase." This premise appears to have been reached from a consideration of capillary phenomena in cylindrical tubes, although it may a1so hold for other types of pore geometry, hut as will be shown below it does not hold for all pore shapes and hence is not generally applicable. Since the pore structure of porous media such as reservoir rocks i- in general so complex as to defy exact description. it is undoubtedly of great value to establish a model in terms of pore shapes of known geometry, provided of course that the limitations of the model are recognized. That the limitations of the capillary. or cylindrical, tube model have not always been fully recognized will be evident from the following discussion of a pore of different shape hut one which may a. logically he considered a.; the capillary tube. The pore space to be considered is that shown in Fig. 1, which may be thought of as the "hole in a doughnut."* Consider the interface, A-B-A&apos;, between two immiscible fluids, P, and P2, which interface meets the solid alone a line, A-C.A&apos;-C&apos;. The interface A-B-A&apos; is the surface of a spherical segmen† while the line of mutual contact be-

Jan 1, 1950

By Emma Smith, R. W. Guard

INVESTIGATION of the nickel-rich end of the Ni-Zr system has been prompted by an interest in the effect of small amounts of zirconium in high temperature alloys. Hansenl presents a hypothetical diagram based on the work of Allibone and Sykes,2 who investigated the system up to 44 atomic pct (55 wt pct) Zr by metallographic means. Since the alloys they used were melted in Alundum crucibles they were probably contaminated with appreciable amounts of aluminum. They found two compounds which they called Ni3Zr and Ni4Zr. Hayes, Roberson, and Paasche3 identified a compound NiZr (50 atomic pct Zr) with a melting point of 1470°C. Such a high melting compound is not compatible with the observation of Allibone and Sykes2 hat a eutectic is formed near 50 atomic pct. The alloys containing up to 60 atomic pct Zr were melted in an inert atmosphere in a noncon-sumable electrode arc furnace. Analysis of most of the alloys indicated negligible loss of zirconium. The alloys were examined in the as-cast condition and also after annealing for 6 hr at 1175°C (or 1000°C for the alloys between 25 atomic pct and 45 atomic pct). Metallographic specimens were etched using mixtures of HF-HNO3-H2O or acetic acid- HN0,-H,O. The specimens for the solidus determinations were wrapped in molybdenum foil and sealed in evacuated quartz tubes. Specimens to be heated above 1300°C were enclosed in zirconia tubes inside the quartz to prevent reaction with molybdenum. The solidus determinations were carried out by heating the specimens at various temperatures for a few minutes and then examining the interior structure metallographically to determine at what temperature melting began. The 150 mesh powders for X-ray analysis were annealed in an evacuated quartz tube for 2 hr at 540 °C to remove cold work. Alloys with 22.5 atomic pct Zr and 44.4 atomic pct Zr required annealing at 700 °C for complete recovery. The grains of both of these alloys were soft and rather ductile. Both Debye-Scherrer film patterns and spectrometer traces were made for each alloy using filtered copper radiation. Results and Discussion The presence of a substantial amount of second phase in an alloy with 1.1 atomic pct Zr indicated that the solid solubility of zirconium in nickel is somewhat less than 1 atomic pct. The a0 value for the face-centered-cubic matrix in the same alloy was equal to that of pure nickel, so that the solubility must be very small. This observation is as expected from the large atom size difference. Annealed specimens of alloys with 15.0, 16.7, 22.5, 28.6, 44.4, and 59.4 atomic pct Zr showed. micro-structures that were essentially single phase. When

Jan 1, 1958

By R. B. Rosene, G. L. Foster, A. R. Hendrickson

he properties of some of the common fracturing oils, such as sand-falling rate, fluid loss and viscasity, are a function of the three major constituents of the oil. These are: asphaltic material, parafin waxes and a base oil. The base oil can be either high or low viscosity. Asphaltic material increases viscosity by thickening the oil, decreasing the rate of fall of sand through the oil. at temperatures up to 200" F. When large arnorrnts of parafin wax are present, much of the wax i.s not dissolved, but is present in the form of rnicroscopic crystals. 7&apos;his, of course is limited to temperatures below the melting points of waxe.s. As a result, parafin waxes clo not function primarily as thickener.7, but rother as bullting materials. The functiori of wax, without asphaltic material, in a low viscosity base oil is uniquely unlike that of wax with asphalt coexistent in the oil. The resulting difierence in wax crystal size governs the sand-falling rate to a large extent. An ideal type of fracturing oil is one containing neither asphalt nor waxes. In such cases, the viscosity and resulting low sand-falling rate are apparently due to soluble resin- ous hydrocarbons, which are compatible with formation oils. INTRODUCTION Since the introduction of hydraulic fracturing as a method of stimulating production from oil and gas wells, a variety of fluids have been employed to open the fractures and carry the propping agent. Such fluids include gels, emulsions, and oils. In the latter category, the use of refined oils has increased tremendously, and it is probably safe to assume that such oils represent more than one-half of the total fluid used in fracturing. The general acceptance of refined oils for fracturing can be accounted for on the basis of their relatively low cost and general applicability. To minimize transportation costs, such refined oils are generally obtained within the local areas of operation. As a result there are several kinds of oil used in different areas, with a wide variation in the basic composition. These types may vary from a fair grade of lubricating stock to a highly viscous cut-back asphalt. or road oil. Originally, little attention was paid to the composition of the oils used for fracturing, and any oil which would carry sand was considered satisfactory. Recently, however, service companies and well operators have become more concerned with the type of oils used for fracturing. With this in mind, the present work was undertaken to evaluate and compare many widely used fracturing oils to determine which constituents were most desirable for fracturing purposes. Some of the important properties of fracturing fluids are sand-falling rate, viscosity, and fluid loss. Other properties, that are actually of no less importance, include flash point, pour point, emulsifying tendencies with formation brines, and compatability with the formation oils. This discussion has been limited, however, to the first mentioned properties in order to give some idea of the general composition of the refined oils, how they function, and why. PROPERTIES OF FRACTURING OILS The properties of fracturing oils are a function of the three major constituents of the oil. These may be designated as: (1) asphaltic material, (2) paraffin waxes and (3) a base oil, which may be of either high or low viscosity. The asphaltic material clas-

Jan 1, 1956

By D. J. Blickwede

WHEN iron is dipped in molten zinc at temperatures in the range 840" to 930°F, the two metals react to form layers of Fe-Zn compounds which adhere to the iron. At the galvanizing tem- perature, the successive layers are:&apos; y (Fe5Zn21), 61 (FeZn;), and 5 (FeZn13), in conformity with the Fe-Zn constitution diagram. There is no quantitative information in the literature on the rates of growth of the individual alloy layers over the temperature range 840° to 930°F. Rather all the past experiments have studied the loss in weight of iron as a function of galvanizing

Jan 1, 1954