By H. Nakano

The codeposition behavior of impurities such as Ag, Bi, Fe, Ni, Pb and Sb with Cu was investigated galvanostatically at 5-3000 A/m2 using a Pt cathode at 60 °C in acidic copper (I) chloride (cuprous chloride) solution at pH1-2 containing 1.0 mol/L of Cu+ and 4.9 mol/L of Cl-. The impurities were classified into two groups: Group I (Ag, Bi) which codeposits with Cu as a metal, and Group II (Fe, Ni, Pb, Sb) which is slightly involved in the deposited Cu in nonmetal form from the electrolyte. Silver and Bi in Group I behaved as more noble metals than Cu, and significantly codeposited with Cu, showing typical features of regular-type codeposition. When Cu was deposited dendritically, the Ag and Bi content in the deposit increased with increased duration of electrolysis as a result of decreased net current density caused by increased cathode area. The current efficiency for Cu deposition in impurity-free solution was 95-100% over 100-1000 A/m2, but it abruptly decreased at above 1000 A/m2 when the limiting current density of Cu was attained. Although Fe, Ni, Pb and Sb in Group II were involved to 0.01-0.02 mass% in the deposit, they had no influence on the current efficiency or morphology of Cu.

Jan 1, 2007

By Jae-Ho. Lee

Mercury is a toxic contaminant encountered in the extraction of gold from mercury-containing ores. It is found in the leach solution of CIP circuits and in the cathodes of the electrolyte cells used to electrodeposit the gold. The research conducted has examined the potential for selective removal of mercury from synthetic Au-Hg-CN electrolytes containing only gold, only mercury, and both gold and mercury. Cyclic voltammograms were obtained for mercury- coated copper electrodes with these cyanide electrolytes. Exchange current densities were determined from the voltammograms in the low overpotential region. Laboratory scale batch- electrolysis at constant current was also conducted for the electrolytes containing only mercury and both mercury and gold, at 20 and 50°C and from which the kinetic behavior associated with the process was analyzed. The surface of cathode before and after electrolysis was also characterized and a copper mercury intermetallic (CyHg,) was identified. Gold codeposited with mercury during the later stages of electrolysis. The results of this work corroborate that the mercury-amalgam copper electrode offers a viable electrochemical technique for the selective removal of mercury, however a high-surface-area cathode-cell would have to be utilized to provide for the desired selectivity.

Jan 1, 1994

By J. L. Bray

IT is well known that iron markedly improves the physical properties and casting characteristics of aluminum bronzes. The use of 1 to 4 per cent iron as the principal modifying addition has become common practice in many foundries melting aluminum bronzes. Although the beneficial effects of iron are unquestioned, there is some uncertainty regarding the structural changes caused by it in the basic copper-alumi-num system. It is agreed that a new constituent appears in abundance when the iron content reaches 2 to 4 per cent. This constituent, which frequently occurs in shapes resembling clover leaves, is sometimes assumed to be an aluminum-iron intermetallic compound. If this were correct we might expect a change in the structural relationships of the matrix in the direction of decreased aluminum content. On the other hand, it has been reported that iron has a negligible effect in altering the fundamental relationships of copper-aluminum alloys1. Others2,3 have reported an additive coefficient. Apparently it will be necessary to know the equilibrium relationships between the phases of the copper-aluminum-iron alloy system to establish any such theory as fact. When this has been done it may very well be that a further revision in the structural relationships may be necessary to describe the changes to be expected in commercial cast alloys. It was with this latter problem before them that the authors attempted to

Jan 1, 1936

By P. Ashayer, J. Curran

Introduction Rockfalls occur when rocks or boulders detach from mountains or hills and tumble down. They can pose significant hazards to infrastructure such as highways, buildings, and mine open pits, and they sometimes result in personal injury or death. Prediction of rockfalls is a difficult task. Slopes that are at risk of rockfall have highly variable geometries. The location, mass, and shape of the rocks that might dislodge and fall are uncertain. Moreover, the materials that make up a slope can vary considerably from one section to another. Furthermore, the relevant material properties are usually not well known. Performing probabilistic simulations of rockfalls, combined with proper statistical analyses, has proven to be an effective and acceptable method for dealing with these difficulties [1, 2, 3]. The movements of a falling rock can be classified as freefall, bouncing, sliding, toppling, or rolling. The falling trajectory is controlled mainly by the geometry of the slope, the block shape, and the energy dissipated at each contact of the block with the slope. A rockfall model is evaluated based on its ability to efficiently predict the velocity, frequency, height of bounce, and run-out distance of falling rocks. With this information, the engineer can design remedial measures such as restraining nets and ditches. Most of the existing rockfall simulators are based on particle models that consider the falling rock as an infinitesimal particle with a mass, called the lumped mass or stereomechanical models [1, 2, 3, 4]. Other models involve hybrid methods relying on simplified assumptions. The most common hybrid methods are based on contact searching for the movement of a dimensionless object and incorporate some aspects of rigid body impact for bouncing [5, 6, 7]. There are also some rigid body models in the literature that employ simplified versions of rigid body models [8, 9]. This study applies a more sophisticated rigid body theory based on rigid body impact mechanics (RBIM), which was developed by Stronge [10, 11, 12]. The new theory captures all modes of rigid body movement. Due to the importance of the rock geometry, single impacts of ellipsoidal and prismatic rocks with rectangular cross sections are investigated. The effect of rock slenderness on rebound velocities and energies is also investigated for ellipsoidal rocks. The correspondence between the model parameters and the data from the rockfall literature data will be discussed.

Jan 1, 2007

By J G. Shellnutt, Y Iizuka, T W-Y Hsia, T-C Liu

"An EXTENDED ABSTRACT is available for download. A full-length paper was not prepared for this presentation. The formation of magmatic oxide ore deposits hosted in chemically-evolved layered gabbroic intrusions is attributed to a variety of petrological processes, but there is little to no consensus on the general applicability of each model. Complicating the matter further is that many layered gabbroic intrusions are spatially and temporally associated with alkaline A-type granites, suggesting that there is a petrogenetic relationship between the two types of chemically different rocks. Our experimental results show that petrological modelling using a starting composition of high-Ti basalt from the Emeishan large igneous province can produce evolved silicic liquids that resemble the compositions of microgranular enclaves from the syenitic unit of the bimodal, oxide ore-bearing Baima igneous complex. The experimental results confirm that bimodal gabbro-granitoid complexes can form from a common parental magma and that early crystallisation of Ti-rich magnetite can explain the formation of the oxide ore deposits in the lower parts of the layered gabbroic intrusions. We conclude that crystallisation of a typical high-Ti basaltic parental magma can produce world-class giant magmatic oxide ore deposits and that the occurrence of some alkaline granites may be an indicator of their presence.CITATION:Shellnutt, J G, Hsia, T W-Y, Liu, T-C and Iizuka, Y, 2015. Cogenetic formation of the peralkaline syenite and oxide ore-bearing layered gabbroic intrusion of the Baima igneous complex, Emeishan large igneous province, south-west China , in Proceedings PACRIM 2015 Congress, pp 317–324 (The Australasian Institute of Mining and Metallurgy: Melbourne)."

Mar 18, 2015

By Pravin Mathur

"Praxair's CoJet® technology was introduced in 1997 to effectively inject chemical energy in electric arc furnaces. Coherent jets were invented as a revolutionary means of injecting oxygen and other gases into the EAF and into converters. Today, steel makers have widely accepted this concept in over 70 EAFs worldwide. Indeed, the whole industry has shifted to this new standard for chemical energy input in EAFs. CoJet® technology has also been implemented successfully in BOF converters.This paper will review the principles of coherent jets as applied to steelmaking. The key learnings garnered from several furnaces are also reviewed. In addition, while the CoJet® program has been widely accepted worldwide, based on steady feedback received from customers and the market place, several programs are underway in development and commercialization. These enhancements and new applications of CoJet® technology are also overviewed in the paper."

Jan 1, 2004

By Qiang Zhong, Bin Xu, Qian Li, Yong-bin Yang, Tao Jiang, Yan Zhang

The occurrence of different ringing behaviors in oxidized pellet kiln for two kinds of coal (A and B) with similar properties, is difficult to explain based on the relationship between kiln ringing and coal properties. In this paper, the interaction of coal ash with pellet scrap powder was considered by studying the cohering behavior of powders consisting of them. The results showed that the cohering briquette strength of pellet scrap powder increased considerably when mixed with a small amount of coal ash; a maximum could be reached when the mass percent ratio of coal ash was 1.5%; the strength of powder mixed with coal B ash was always higher in same firing system. This obviously illustrated that coal B caused a more serious ringing problem. The relevant mechanism was that the stronger reactivity of coal B ash made cohering briquette have a more perfect crystallization and a more compact structure.

Jan 1, 2015

By Bin Xu, Qian Li, Xiaoliang Liu, Yongbin Yang, Tao Jiang, Yan Zhang

The cohering behavior of iron ore pellet powder in kiln cannot be reflected entirely through the conventional briquetting method, so a novel natural stacking method was proposed in this paper. The results showed that in the two methods the cohering strength of powders from different iron ore pellets (numbered A, B and C) rose with the increase of roasting time and temperature andpresented the same result, i.e., C > B > A. Comparatively, the natural stacking powders obtained much lower cohering strengths under the same roasting condition. The structure analyses of ring from the kiln tail and cohering briquette by the natural stacking method indicated that the occurrence of crystallized particles of them were extremely similar. Therefore, the initial information of pellet powder’s cohering behavior could be provided by the natural stacking method, improving the methods to study the actual ringing process and mechanism of pellet powders in kiln.

Mar 1, 2017

By Diana Diaz, Rakshith Shetty, Vitaly Proschenko, Mike Mooney

Cohesive clay soil poses a significant risk to earth pressure balance tunnel boring machines (EPBM) due to unstable face pressure, clogging potential, high cutterhead torque, poor muck flow, low advance rate, etc. This paper details the performance measures desired when EPBM tunneling in clay soil, and the scientifically-supported conditioning methods to transform in-situ clay to a muck with such characteristics, giving particular attention to ground conditions. The paper then examines TBM data from multiple clay soil projects in the context of these performance measures to demonstrate the influence of cohesive soil conditioning on EPBM performance.

Jun 13, 2023

By John D. Price

In the constant search for ways and means of improving the quality of coke and thus making its use at the blast-fornace more satisfactory and economical, it has become increasingly evident that the present laboratory tests do not show the full picture of a coke's value as a blast-furnace fuel. This fact was recognized by Dr. A. C. Pieldner thirty-five years ago: (Ref. 1) here is perhaps no phase of fuel technicology which has aroused more discussion or regarding which there is more difference of opinion than the properties of coke which make it most suitable for blast-furnaces and other uses." Dr. Fieldner followed this assertion with a statement to the effect that men who write on this subject today (1923) have, because of conflicting experimental evidence brought forth in recent years, far less positive opinions on the matter than did writers of some years past. One is led to wonder if these statements are not just as true now as they were when first made.

Jan 1, 1959

By Huanyu Zhang, Quanqiang Ma, Huiqing Tang

Improvement of the coke quality for blast furnace (BF) iron making by hydrothermal oxidation treatment on coke quality was investigated. Results show that, under subcritical condition, sulfur removal rate is 15% and the weight loss is 3%; under supercritical condition, both sulfur removal rate and mass loss rate increase with the increase of H2O2 concentration. In the experimental conditions, sulfur removal rate and mass loss rates were 45% and 17%, respectively. Hydrothermal oxidation treatment could reduce the CO2 reactivity of the coke and the treatment under supercritical condition is more effective. Hydrothermal oxidation treatment could improve the graphitization of the coke and smoothness of pore boundary in the coke and the treatment under supercritical condition is more effective.

Jan 1, 2016

By Mariano de Córdova

In this paper, the coke oven life prolongation technology is reviewed from different points of view: blend design; battery heating; operational control; refractory maintenance. A summary of major inspections in critical areas, for the evaluation of the battery conservation situation is presented. A discussion on tools for the diagnostics of the degree of damage is carried out.

Aug 16, 2017

By Richard J. Wilson

The importance of coal as a major source of energy used by the steel industry has been increasing due to the gradual changeover from steel- making by the open hearth process to steelmaking by the basic oxygen process. Since the production of steel by the BOF process increases the demand for hot metal, there is a growing need to ensure the supply of coke required for the production of hot metal. Coal used for cokemaking has become, therefore, an increasingly important raw material for the steel industry in recent years. Our current projections indicate that coal will be the source of 71% of the total energy requirements of Inland Steel Company in 1985. As a result of the energy shortages of the last few years, various conservation programs have been initiated by the steel industry to reduce the consumption rate of fuel. The efforts to conserve energy have been successful to a great extent due to the rapid advances made in the technology of ironmaking that facilitated gradual reductions in the quantity of coke used per ton of hot metal produced in the blast furnaces. The decrease in the consumption rate of coke was made possible by the use of improved raw materials, such as iron ore pellets and fluxed agglomerates, the operation with high blast temperatures, the injection of auxiliary fuels, and the enrichment of the blast with oxygen. It is expected that additional reductions in the fuel consumption rate will be possible in the ironmaking operations of the large blast furnaces that are being equipped with facilities for proper burden distribution and for operation with higher blast temperatures at high top pressure. The purpose of this paper is to show the effects of coke quality on the production of BOF steel. The importance of coke quality will be pointed out by discussing the effects of the physical strength of coke on both the blast furnace productivity and the steelmaking operations of an integrated steel plant, such as Inland Stee1 Company.

Jan 1, 1980

By Silvio Pereira Diniz Maranha, Evandro Costa e Silva

The disposal of coal tailings in an economically and environmentally sustainable way can be considered one of the biggest challenges for coal producers due to their physical, chemical and mineralogical characteristics and the significant annual volumes generated. The processing and utilization of coal fines is recognized as one of the great technical challenges of this industry. These challenges become even greater when it comes to the use of tailings from coking coals. This is due to the potential changes in their various properties, variability of these characteristics along the deposits, the handling and dewatering aspects of the products and the granulometric restrictions imposed by the coking plants for the coals to be handling and coking. This work presents the current stage of project development for the use of a metallurgical coal fines dam, addressing the general concept of the project, the exploratory sampling program and the characterization of the tailings for process and product development purposes after processing. It aims at the characterization and the carbonization tests for product development, the mining method considered, product alternatives, suitable to the market, to be generated and the next steps.

Oct 3, 2019

By D. E. Wolfson, D. A. Reynolds, F. W. Smith

IN 1948 the U. S. Bureau of Mines began a three- phase program to evaluate the extent and quality of U. S. coking coal: 1) a factual appraisal of known recoverable reserves in beds of mineable thickness, 2) a study of preparation characteristics, and 3) a study of carbonization properties. A previous paper presented the methods used in assessing reserves.' Although this investigation is only partly completed, data on coking properties of the Pittsburgh district coals are now available. The results are presented in this article. When coals are selected for manufacture of metallurgical coke more factors must be considered than for any other major use, as no basic industry requires coal of such high quality and uniformity. This is particularly true in the Pittsburgh district, where blast furnace practice is based on use of cokes from high quality coals. Although it is true that inferior coals are carbonized in other industrial areas, both here and abroad, the Pittsburgh coals are the best economically obtainable in the required tonnages, even though they are not the most desirable for metallurgical use.

Jan 3, 1957

By John A. M. E. Church

AT the last meeting of the Institute, a discussion arose upon the question, " Is them pressure in coke ovens ?" and many of the members seemed to think that the superiority of the Belgian furnace might be due to the fact that it is a completely closed chamber, in which the gases given off by the coal are, or may be, at more than the atmospheric pressure. It seems to me that this position is untenable, and that an examination of one of these ovens in operation will show, not only that there is no excess of pressure in the coke chamber, but that the contrary is true, and a partial vacuum exists. The Belgian or François oven consists of a rectangular chamber closed at the ends by sliding doors, and furnished with flues in the side walls and floor. The new charge is introduced at a time when the furnace is so hot as to cause immediate and copious discharge of the volatile constituents of the coal. The gases pass downwards through the side flues giving out their heat to the walls and thus to the coal. Underneath the floor air is introduced and the gases burn, producing intense heat. Heat is also reflected from the arched roof upon the coal which is therefore heated from all sides. The especial advantage which this construction was designed to secure is that no air is admitted to the coke-chamber. All the heat is produced by the combustion of the uncokeable gases, and the yield ought to be a maximum. It is so in fact, allowing for the imperfections inseparable from furnace construction and management. Sometimes the yield is in excess of the percentage indicated by assay, showing that

Jan 1, 1873

By V. Pawlowsky-Glahn, E. Pardo-Igúzquiza, J. J. Egozcue, R. A. Olea

Compositional data constitutes a special class of quantitative measurements involving parts of a whole. The sample space has an algebraic-geometric structure different from that of real-valued data. A subcomposition is a subset of all possible parts. When compositional data values include geographical locations, they are also regionalized variables. In the Earth sciences, geochemical analyses are a common form of regionalized compositional data. Ordinarily, there are measurements only at data locations. Geostatistics has proven to be the standard for spatial estimation of regionalized variables but, in general, the compositional character of the geochemical data has been ignored. This paper presents in detail an application of cokriging for the modelling of compositional data using a method that is consistent with the compositional character of the data. The uncertainty is evaluated by a Monte Carlo procedure. The method is illustrated for the contents of arsenic and iron in groundwaters in Bangladesh, which have the peculiarity of being measured in milligrams per litre, units for which the sum of all parts does not add to a constant. Practical results include maps of estimates of the geochemical elements in the original concentration units, as well as measures of uncertainty, such as the probability that the concentration may exceed a given threshold. Results indicate that probabilities of exceedance in previous studies of the same data are too low.

Jan 1, 2015

By D. Swanson

Cold Detonation Physics (CDP) is a patented new field of explosives and the name for the explosive that is produced when non-toxic dry ice (frozen carbon dioxide) is combined with powdered metals such as magnesium and aluminum, which are non-toxic and nitrogen-free. The explosive is detonator-sensitive and detonates according to the rapid reduction of carbon dioxide back to carbon, which produces solids comprised mainly of metal oxides and about 5% carbon. CDP was determined to produce a maximum of 300 liters of carbon dioxide per kilogram (4.81 ft3 /lb) and about 1.5 liters of carbon monoxide per kilogram (0.024 ft3 /lb). Both these figures shift according to metal content where higher metal produces less gases. According to theoretical modelling, the relationship between static pressure and metal content was determined to be an inverse parabolic curve with optimum pressure at 25% to 31% metal, depending on the type/s of metal/s used. Velocity of Detonation (VOD) was determined by measuring light at the wavefront with fiber-optic cable inserted into a series of holes drilled into the side of a 3-inch diameter (76 mm) schedule 40 steel pipe containing the mixture. The highest VOD was observed at 25% magnesium and measured between 2,500 to 4,500 m/s (8202 to 14,764 ft/s) when initiated by a 454-gram (1-pound) booster and an electric detonator. A 25% 50:50 alloy of magnesium and aluminum sample shot at a higher velocity than magnesium, according to how the alloy generated smaller pieces of shrapnel when compared with shrapnel from a magnesium test. CDP, using 25% alloy, was tested for blasting limestone by drilling 3.5-inch holes (89 mm) and inserting a 3-inch x 4-foot cardboard tube (76 mm x 1.22 m) with the mixture, packed to a density of 0.62 g/cm3 . The blast was initiated with an electric detonator, behaved like ANFO with more energy and fractured rock sufficiently across the entire length of the borehole. Seismic analysis determined that CDP produces lower ground vibrations than traditional explosives.

Jan 1, 2024

By K. Yoshida

Recently, light magnesium alloy with superior heat radiating ability has been attracting attention in various fields. However cold plastic working of the alloy is very difficult and hot working necessary. Furthermore, the magnesium of products with complicated shapes is difficult, the processing cost is high, and the applicability of the alloy is limited. In this study, a technique for obtaining fine wires and tubes by cold drawing is examined to obtain wires and tubes with high strength, quality and surface morphology, while decreasing production cost. In addition, the shearing strain of magnesium alloy wires and tubes drawn under various drawing conditions was calculated by FEM analysis. It was clarified that cold drawing of magnesium alloy is possible. It was also demonstrated that greater reduction of the cross-sectional area could be realized during cold wire and tube drawing by optimizing the drawing conditions.

Jan 1, 2006

By Shabnam Sabah, Geoffrey Brooks

In oxygen steelmaking, splashing and droplet formation play a key role in the kinetics of the process. Though splashing has been studied by previous investigators, there is only limited understanding of how different cavity modes affect splashing. Therefore, a cold model study (at various lance heights and gas flow rates) has been carried out focusing on the issue of cavity modes and how it affects splashing phenomenon. Analysis using Fast Fourier Transform (FFT) was carried out on cavity oscillation that showed that frequency and amplitude of oscillation was highest in penetrating mode. Measurements of splashing over a range of conditions showed splashing greatly reduced when cavities went from splashing to penetrating mode. The results were validated and compared with plant data and previous model investigations.

Jan 1, 2014