By R. O. Williams

It is shown that Ni3Al precipitates homogeneously from nickel-rich alwminum alloys as plates on the (100) planes. Prior to actual precipitation a process occurs which is believed to be one of increasing short-range order. After precipitating the Ni3Al plates enlarge through competitive growth. Discontinuous precipitation can occur simultaneously with the above processes. Recent ideas of the origin of precipitation strengthening appear adequate to explain the hardness changes. REMARKABLY little appears to be known about the precipitation process in Ni-Al alloys in spite of their technical importance. This investigation originated to supply additional information about precipitation in general, this system in particular. Information on the structures and kinetics have been obtained through the use of hardness, X-rays, microscopy, calorimetry, and resistivity on high-purity alloys. PROCEDURES Six alloys, Table I, were prepared by melting carbonyl nickel and high-purity aluminum in alumina crucibles in vacuum and casting into 1-in. graphite molds. All rods were homogenized at least once at 1300°C for 24 hr prior to swaging and this was repeated on the first three alloys after 75 pct reduction. Alloy 4 could be reduced only 10 pct at 1000°C (probably in two-phase field) prior to fracture but 1/4-in. samples quenched from 1100°C were readily reduced cold. Alloy 5 was reduced 15 pct cold but failed on the next pass while alloy 6 of essentially the same aluminum content failed inter-granularly without apparent flow up to 1000°C. The alloys were heated in hydrogen at the elevated temperatures and formed thin, coherent aluminum oxide coatings which provided excellent oxidation resistance at lower temperatures. However, freshly prepared surfaces showed considerably less resistance at 500"to 700°C in air and apparently resulted in internal oxidation. As a consequence, low-temperature agings were carried out in evacuated tubes. RESULTS The isothermal hardening behavior of these alloys at 500"and 565C is given in Figs. 1 and 2. These results were obtained from samples cold worked 75 pct, recrystallized at 1000°C (1100°C for the 7.8 pct Al) and quenched in water. This recrystallization was used to give smaller grain sizes so as to obtain more uniform hardness values and the points represent an average of five readings. The electrical resistivity was measured on 1/16-in. wires quenched from 1000°C during aging at 495°C to give Fig. 3. The energy release and its rate are given in Fig. 4 for the 6.9 pct Al alloy during aging around 500°C. Inasmuch as this was a single run, its accuracy is not known but certainly the general shape and magnitudes are correct. The method used to obtain these results is described elsewhere.' Data for the aging at 600°, 700°, and 800°C of these alloys cold worked 50 pct are given in Fig. 5. Supplementary information from microscopy and X-ray diffraction have been included to indicate recrystallization, discontinuous precipitation and the appearance of superlattice lines from the Ni3Al. The hardness of these alloys as annealed, aged, cold worked, and cold worked and aged is given vs composition in Fig. 6. Those samples which were isothermally aged, Figs. 1 and 2, were reaged at 532°C and at successively higher temperatures for the indicated times to give the data of Fig. 7. These results as well as certain others, support the idea that the level of hardness reached for temperatures above 600°C are equilibrium values more or less independent of path. This being the case, the breaks in the curves would be the complete solution of the Ni,Al. The electrical resistivity versus temperatures for some of these alloys, both aged and unaged, is given in Fig. 8 along with those data from heating slowly (10 deg per day) to high temperatures. Interesting points include the lowering of the Curie temperature (the change in slope), the lack of any indications of a solubility limit and the large temperature coefficient for the Ni3Al. A slight break for Ni3Al around 100C shows up but this is not a Curie temperature as Ni3Al is not ferromagnetic down to -190°C. Metallographically both the nickel-rich solid solution and the Ni3Al appear very much like pure nickel. Profuse twin boundaries are present both

Jan 1, 1960

By C. E. Nelson, T. E. Leontis

THE properties and casting characteristics of sand-cast Mg-Al-Zn alloys, used commercially in this country and abroad, have been discussed in a number of articles during the past few years.'-" In addition, broad surveys of many compositions in the magnesium corner of the Mg-Al-Zn diagram between 0 and 12 pct A1 and 0 and 6 pct Zn have been presented by Busk and Marande7 and by Fox." The purpose of this paper is to furnish a comprehensive survey of the changes in tensile properties, micro-structure, and dimensional stability of two magnesium alloys, AZ92A and AZ63A,+ as a function of aging time and temperature after solution heat treatment. Rates of precipitation in Mg-Al-Zn alloys are slow enough so that a substantially homogeneous, supersaturated solid solution can be maintained even when these alloys are air-cooled from the heat-treating temperature. Consequently, even though it has been demonstrated9 10 that significantly higher strengths can be developed in some alloys in the aged condition by quenching rather than air cooling from the heat-treating temperature, general practice is to air-cool magnesium alloys. All the work discussed in this paper is based, therefore, on aging studies performed on material air-cooled from the heat-treating temperature. This investigation was intended to be a study of commercially practical aging cycles; the tensile properties were determined, therefore, up to aging times of 25-hr duration. The alloys, used in this investigation were prepared in the laboratory by remelting commercial ingots of the appropriate composition according to the procedures described in a previous paper" as the "crucible method." All melts were given the standard superheating treatment in order to insure the maintenance of a uniform grain size of 0.003 to 0.004 in. Standard test bars, 61/2 in. long with a 2½ in. long reduced section having a diameter of Y2 in., were cast from these melts in green-sand molds using a four-bar pattern. The alloys were heat treated according to the following schedules: AZ92A alloy: 500" to 780°F in 2 hr + 780°F (24 hr) AZ63Aalloy: 500" to740°Fin2 hr + 740°F (16hr) In commercial practice," AZ92A alloy is heat treated at 770°F for 18 hr and AZ63A alloy is heat treated at 730°F for 10 hr. The slightly higher temperatures and longer periods of heat treatment were used in order to obtain as homogeneous a solid solution as possible and thus to minimize inconsistencies in the

Jan 1, 1952

By D. H. Polonis, Gary A. Dreyer

This investigation involved a study of the reactions occurring during aging of supersaturated a phase in a CIL-Si alloy. The aging processes at temperatures below 552°C were studied by means of metallography, microhardness, and electrical resistivity measurements. During the initial stage of aging in the temperature range 275o to 525oC an anisotropic phase, which is visible in the form of striations in the micro-structure formed prior to the appearance of the -phase. This transition phase has been designated k' due to its structural similarity to the k phase. The rate of K' formation during aging increased with aging temperature. At 450o and 525°C the reaction appeared to reach completion before significant amounts of precipitation were observed. The overall precipitation reaction in this system involved four stages: formation of formation of at a grain boundaries, growth of particles in 7-egions, and coagulation of into large particles. The relative role of each of these processes is dependent on the temperature of aging. The formation of phase from supersaturated a during aging increases the electrical resistivity and slightly increases the hardness of a 4.9 pct silicon alloy. The formation of during aging decreases the electrical resistivity and increases the hardness until coalescence of particles begins during the final stages of aging. The coalescence of results in a decrease of both electvical resistivity and hardness. THE available literature does not record a detailed analysis of the aging processes in Cu-Si alloys. Such an analysis has been difficult due to both the limited data available and misleading microstructural observations which have been reported. Previous work suggests that a rather complicated series of processes may be involved in the aging of supersaturated a. The present investigation is concerned with an analysis of the sequence of these aging processes in a 4.9 pct Si alloy. The currently accepted version of the Cu-Si equilibrium diagram, Fig. 1, was published by C. S. Smith in 1940.' This diagram shows a eutectoid at 5.2 pct Si with the high temperature phase, having its composition range entirely to the right of this value. By quenching alloys in the composition range 4.6 to 5.2 pct Si from the region, Smith was able to retain the phase. However, this phase exhibited a striated microstructure which was anisotropic to polarized light. These striations were suggested by Smith to be duplex twins. Using an oscillating crystal X-ray method Barrett2 studied alloys containing 4.0 to 5.4 pct Si quenched from the and regions. The striations observed in quenched specimens were attributed by Barrett to quenching stresses. He found that striations could also be formed by deformation after quenching and identified them as stacking faults in alloys containing 4.0 to 5.0 pct Si. Barrett related the striations in alloys containing 5.0 to 5.4 pct Si both to stacking faults and to a metastable phase which he called The striated structure reported by smith' was also obtained by Hoffmann, et al. 3 By deeply etching their specimens the anisotropic phase on the surface was removed, leaving a structure which was microscopically similar to pure copper. By means of X-ray analysis before and after deformation at room temperature it was concluded that the anisotropic phase was metastable This conclusion has been questioned by Barrett who attributes the discrepancy to superposition of k and lines on the powder patterns of Hoffmann, et alm3 The decomposition of supersaturated according to smith' and Anderson,4 is very sluggish. However, Nony and Dreyer,5 and Hoffmann, et al.' found that deformation increases the rate of decomposition. X-ray studies by Hoffmann, et al on

Jan 1, 1962

By J. H. Westbrook, R. W. Guard

The influence of a number of alloying additions on the structure and hardness of Ni3Al (?') has been studied. Three general effects have been observed.. solid-solution hardening, strain aging, and defect hardening arising from deviations from stoichiometry. The solid-solution hardening phenomena are complicated relative to binary terminal solid solutions due to the possibility of virtually independent substitution for the component elements and to the concomitant effects of strain aging. In many superior nickel-base high-temperature alloys the elevated temperature strength is attributable to the presence of a dispersion of Ni3A1 (?') in a solid-solution matrix. Examples of such alloys are Inconel X-550, Inco 713, Waspalloy, and Nimonic 80. It is, therefore, appropriate to seek a further understanding of the properties and alloying behavior of this compound. Ni3Al, the compound most rich in nickel in the nickel-aluminum binary system, was first detected by litakal but not established with certainty until the much later studies of Bradley and Taylor' and Alexander and Vaughan.3 More recently the mechanism of formation was clarified by Floyd4 who showed that Ni3Al is the product of a peritectic reaction at 1395°C between the melt and the compound NiAl in agreement with the original suggestion of Alexander and Vaughan.3 Ni3Al has the ordered face-centered-cubic or Cu3Au structure in which the nickel atoms occupy the face centers and the aluminum atoms the cube corners, a0 = 3.570A. Despite earlier reports to the contrary. the compound apparently remains ordered at least to 1000oC.5 It exists over a narrow range of compositions (-3 pct wide) whose limits and temperature dependencies thereof have been reviewed recently by Taylor and Floyd.' Most previous workers have found Ni3Al to be both hard and brittle7,8 although Maxwell and Grala8 obtained 2.5 to 6 pct tensile elongation at room temperature and Alexander and vaughan3 described the material as "hard and tough" on the basis of observations made while preparing metallographic specimens. In a recent study one of the present authors found that although considerable intergranu-lar brittleness was evident: individual grains of a coarse-grained inert atmosphere arc-melted specimen were readily deformable.l0 The same study also showed Ni3Al to have an anomalous temperature dependence of hardness in that such a curve exhibits a number of peaks between room temperature and 800°C which could not be associated with any microscopically observable precipitation reactions or polymorphic transformations. It was, therefore, proposed in the present study to elucidate the anomalous high-temperature strength behavior and to examine the solid-solution alloying of this compound and the effects of such alloying on hardness. Sample Preparation and Experimental Procedure-Samples, both of pure Ni,Al and of various alloyed solid solutions based on Ni3Al, were prepared by arc melting 100-g buttons in an inert atmosphere arc furnace. All buttons were heat treated for 4 hr at 1275oC and examined metallographically for homogeneity. Microstructures were typically homogeneous and single phase with ASTM grain size about 1 and unusually clean grain boundaries. Chemical analyses showed good correspondence (within a few tenths of a percent) with intended compositions. Microindentation hardness data were obtained from room temperature to 800°C in vacuo using a balanced-beam type loading system in an instrument to be described in detail elsewhere." In general a 100-g load, a loading rate of 1 mm per min and an indentation time of 15 sec were used. Various indenter materials were used according to the materials bein tested because of specimen-indenter interaction. Fl Measurements of the Vickers-type indentations were made at room temperature. Hardness-temperature curves were run at least twice on each sample to ensure that surface work-hardening effects had been eliminated." Precision lattice-parameter measurements were made on powder samples using a back-reflection

Jan 1, 1960

By C. S. Smith, E. W. Palmer

IN 1934, when Gregg and Daniloffl wrote their excellent monograph on the alloys of iron and copper, the most recent literature on the constitution of the alloys indicated a narrow single-liquid area for 20" above the liquidus with a closed liquid mis-cibility gap above this. Since that time, however, a number of investigators have confirmed the much earlier studies of Mushet2 and Stead3 who, among others in the nineteenth century, had described the true state of affairs. Liquid copper and iron are completely miscible in the absence of carbon, but small amounts of carbon cause liquid segregation. In 1934, one of the writers' mentioned evidence for the absence of liquid separation in carbon-free alloys at temperatures up to 1700°C. Two years later, Mad-docks and Claussen5 unequivocally established the absence of liquid segregation and published a revised diagram, reproduced in fig. 1. They also studied the limits of the two-liquid area in ternary alloys of iron, copper, and carbon as a function of carbon and iron content. In the same year Simpson and Bannister" and Schumacher and Souden7 described in some detail the properties of alloys containing 50 to 75 pct Cu. More recently Hodges et al.16 have developed the copper-rich alloys for use as high-strength conductors. In 1937, Iwase, Okamoto, and Ameniya8 published data on the miscibility gap in ternary alloys of iron, copper, and carbon that supported the conclusions of Maddocks and Claussen, and definitely located the two-liquid area at temperatures of 1450" and 1540°C. They also reported that additions of 1 pct Al, Ni, Pb, Sn, or Zn caused no segregation in 50 pct Cu alloys at 1540°C. The use of copper in amounts approximating 1 pct has found industrial employment to an increasing degree in both wrought and cast steels, for such steels are capable of being precipitation-hardened following normalizing, and have high yield strengths. This is summarized by Gregg and Daniloff,1 Sallitt,9 and Lorig and Adams,10 while Alexander" gives additional information on the heat treatment of copper-steel castings. Lippert12 has described Digby's two-phase steels containing copper and chromium. The work described in the present paper was done in the years 1932 to 1934, at which time much of the information was new. The excellent work subsequently done in other laboratories but more promptly published makes the present paper in part only a confirmation of what is now well known. There has not, however, been published any unified study of

Jan 1, 1951

By C. S. Smith

The solubility of tantalum at 1100°C is 0.025 pct in pure copper, 1.2 pct with 20 pct Ni, and 2.7 pct with -30 pct Ni. The solubility decreases with temperature, and the alloys are precipitation hardenable. A 79/20/1 Cu-Ni-Ta alloy reaches maximum hardness after aging at about 750°C and, if cold worked, does not recrystal-lize below that temperature. The alloys have good tensile properties at moderately elevated temperatures and, since they can be hot and cold worked nearly as easily as cupronickel, they are suggested for service at temperatures above the usual limits for copper alloys. MASSIVE tantalum dissolves extremely slowly in copper-rich alloys, and tantalum powder forms refractory surface layers which prevent its solution unless special precautions are taken. After many trials, an 80 pit recovery was consistently obtained by using a mixture of a finely divided tantalum powder with two or three times its volume of potassium tantalum fluoride (K2TaF1,-melting point about 750°C) poured in a slow stream directly on to the surface of the molten copper alloy, so that each particle would remain coated with flux and be immediately and individually wetted by the molten metal. A 50-50 nickel-tantalum alloy has a melting point of about 1400°C and small lumps of it slowly but satisfactorily dissolve in molten copper-nickel alloys as does commerical "ferro-tantalum." The high affinity of tantalum for carbon makes it necessary to avoid carbonaceous crucibles. COPPER-TANTALUM ALLOYS Castings with good shrinkage resulted when 0.1 pct Ta or more was added to copper melted under charcoal and cast in air. Copper in two-pound melts to which 0.1, 0.15, and 0.2 pct Ta had been added retained residual amounts, by analysis, of 0.025, 0.023 and 0.026 pct, respectively. The solubility of tantalum in molten copper at about 1200 °C is therefore about 0.025 pct. The electrical conductivity of these three samples was 100.48, 100.00 and 100.20 pct IACS in the annealed condition, and 98.24, 97.98 and 98.08 in the cold-drawn condition. Wires 0.080 in. in diam withstood from thirteen to nineteen reversed bends after annealing for 30 min in hydrogen at 850°C and the metal was therefore completely deoxidized. The annealing temperature corresponding to 50 pct loss of work hardness in 1 hr in a strip cold rolled 77 pct reduction was 175C, compared to 230°C for equivalent undeoxidized material. It is unusual for a decrease of recrystallization temperature to result from an alloying addition, and the tantalum probably combines with and removes some minor impurity in the original copper that restrained its recrystalliza- tion. No difficulty whatever was encountered in hot or cold rolling or drawing these ingots, and were tantalum not so expensive it would make an excellent deoxidizer for copper. COPPER-NIcKEL-TANTALUM ALLOYS Studies were made of the solubility of tantalum in a large number of copper-rich alloys, but of these significant solubilities were found only in the case of an iron alloy (which, however, separated into two immiscible liquid layers) and alloys of copper and nickel, in which tantalum is freely soluble and which were found to have interesting properties. The latter alloys are the subject of U. S. Patent No. 2,430,306 (1947). They are not at present available commercially. The Ternary Constitution Diagram—The copper-rich corner of the constitution diagram was constructed on the basis of microscopic examination of samples of various composition and treatments. The alloys were hot rolled to 0.25 in. from castings 0.625 in. thick, then annealed for 1 hr at 1000°C, quenched, cold rolled to 0.10 in. and finally annealed for various periods of time at temperatures between 800" and 1100°C in a nonoxidizing atmosphere and quenched. When the solid-solubility limit had been transgressed, particles of a compound believed to be Ni2Ta*were

Jan 1, 1960

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth

IN THE past year, Jaffee and Campbell&apos; and Finlay and Snyder2 reported on the mechanical properties of titanium-base alloys, some of which were in the same ranges of composition as are covered in this paper. In this paper, evidence confirming that given by Finlay and Snyder on the effects of carbon, oxygen, and nitrogen on titanium will be presented; and, in addition, new data will be given on the effects of these elements on the flow properties and phase transformation of titanium. Materials and Preparation of Alloys The preparation and general properties of iodide titanium have been adequately described elsewhere.&apos; , As-deposited iodide titanium rod, prepared at Battelle, of Vickers hardness less than 90 was employed as the base metal in the present work. This was the same material as that used by Finlay and Snyder.2 The probable analysis reported by them for standard quality metal holds here also: N 0.005 pct, 0 0.01 pct, C 0.03 pct, Fe <0.04 pct, A1 <0.05 pct, Si <0.03 pct, and Ti 99.85 pct. Carbon was added in the form of flake graphite supplied by the Joseph Dixon Crucible Co. Oxygen was added in the form of c.p. grade TiO, powder, produced by J. T. Baker Chemical Co. Nitrogen was added in Ti3N4 powder, supplied by the Remington Arms Co. Individual ingots weighed 7 or 8 g. Carbon, oxygen, or nitrogen was added by placing the corresponding powder in a capsule made from as-deposited iodide titanium rods and melting the capsule with the balance of the charge. The charge was are-melted with a tungsten electrode on a water-cooled copper hearth under a partial vacuum of very pure argon (99.92 pct minimum). Melting was practically contamination free. Vick-ers hardness increases of less than 10 points were normal for unalloyed iodide titanium control melts. Nitrogen analyses of are-melted iodide titanium showed a nitrogen content of 0.005 pct, about the same as is present in the as-deposited rod. No tungsten pickup was found in a melt of iodide titanium analyzed for tungsten. Weight losses in melting nitrogen-free alloys were very small and varied consistently from nil to 0.015 g (0 to 0.2 pct). This permitted the use of nominal composition for these alloys. Chemical analyses made for carbon, which can be analyzed conveniently by combustion methods, justified this procedure. Where nitrogen was added, considerable splattering took place. Here it was necessary to analyze for nitrogen by the Kjeldahl method. The ingots were hot rolled at 850°C to about 0.045 in. thick. After hot rolling, the strips were descaled by mechanical grinding, and then given a cold reduction of 5 to 10 pct to insure a uniform thickness throughout the length of the specimen. The edge strips and the tensile strips were annealed in a vacuum of 1x10-4 mm Hg pressure for 3 1/2 hr at 850°C and furnace cooled. Methods of Investigation Hardness Measurements: At least five Vickers hardness measurements were taken using a 10-kg load on each sample in the following conditions: (1) top and bottom of each ingot, (2) top and bottom surface of as-rolled and annealed sheet, and (3) on cross-section of annealed sheet and all quenched specimens. Tensile Tests: Tensile tests were conducted on Baldwin-Southwark testing machines having load ranges of 600 or 2000 lb. Tests were made on 1-in. gauge-length specimens, 3 1/4-in. overall length, 1/2 in. wide, 0.040 in. thick, with a reduced section 1 1/4 in. long and 0.250 in. wide. Two SR-4, A-7 strain gauges, one mounted on each side of the specimen, were used to measure the strain over a limited range to determine the modulus of elasticity. After the modulus of elasticity readings had been taken, load vs. strain readings were taken, using only one strain gauge, at increments of 0.0001 in. until the yield points were passed and then at 0.001-in. increments to the limit of the strain-gauge indicator (0.02 in.). Strain readings above 0.02 in. per in. were taken every 0.01 in., using dividers to measure the strain between the 1-in. gauge marks until the maximum load had been reached. Crosshead speed, when using the SR-4 gauges, was 0.005 in. per min, and, when using dividers, 0.01 in. per min. Flow Curves: Flow curves were determined using the true stress-true strain data obtained during the tension test. The usefulness of this type of information has been dealt with very adequately elsewhere by L. R. Jackson,&apos; J. H. Hollomon,6 and many others. Flow curves of true stress vs. true strain could be converted to the more conventional cold-work curve of 0.2 pct offset yield strength vs. percentage of cold reduction by means of the transformation, 1/1 = 1/1-R, where R is the fraction reduction in cold working. Thus, the true strains corresponding to percentage reduction can be calculated, and the 0.2 pct offset yield strengths scaled off the — 6 curve by taking the true stresses corresponding to the values of 6 + 0.002 strain. Heat Treatment: For the transformation studies, the alloys were heat treated in a horizontal-tube furnace using a dried 99.92 pct argon atmosphere, and quenched into water. Essentially no contamination was found after several hours of heat treatment at temperatures up to 1050°C. Metallography: Specimens were prepared in the

Jan 1, 1951

By J. A. Rowland, C. W. Funk

THIS investigation is a part of the United States Bureau of Mines work in conserving the Nation&apos;s resources. The isothermal sections presented were developed as a guide to a comprehensive investigation of the properties and fabricating characteristics of copper-base alloys containing manganese and tin. These alloys are being investigated as possible replacements for the commercial bronzes containing substantial quantities of tin. Development of the isothermal sections has, therefore, been limited to the area between 0 to 20 pct Mn and 0 to 25 pct Sn. Since Heusler1 reported the ferromagnetic properties of the Cu-Mn-Sn alloys in 1903, the system has been the subject of several investigations. These studies were largely concerned with correlation of magnetic properties and crystal structure.2-6 Vero,&apos; however, established the solidus surface of the system, between 20 pct Mn and 40 pct Sn, by thermal and microscopic methods. The a, ß, and y solid solutions were also observed by Vero and reported to extend into the interior of the ternary system. For the present study, the annotated diagram of the Cu-Sn system prepared by Raynor&apos; and the Cu-Mn diagram by Dean and coworkers9 were used as the binary borders of the ternary system. Procedure The metals used in this investigation were electrolytic manganese, washed cathode copper, and three-star tin. The manganese, produced at the Boulder City pilot plant of the Bureau of Mines, had a purity of 99.9 pct; the copper contained less than 0.004 pct Bi and 0.001 pct S; the tin contained 0.070 pct Pb, 0.070 pct Sb, 0.050 pct Fe, and 0.065 pct Si. Heats of 1 lb were melted in alundum crucibles with a 3-kw induction furnace. The heats were chill-cast in iron or copper molds to form 6-in. ingots 3/4 in. in diameter. Molds were washed with graphite or zirconia, depending on the manganese content, and preheated to 150°C. The maximum impurity content of any alloy was 0.03 pct Fe, 0.02 pct Si, and 0.02 pct Al; in most cases, they contained less than half this quantity of any of these impurities. Composition of the alloys and their treatment prior to homogenizing are shown in Fig. 1. Designations adjacent to each composition refer to the heat numbers. With a few exceptions, ingots containing 20 pct Sn or less were hot-swaged. These ingots were swaged, after a 24-hr preheat at 650°C, to obtain a total reduction of 70 pct in cross section. Intermittent reheating was necessary, and reductions were limited to either 0.025 or 0.050 in. in diameter per pass. Selection of a 200-hr homogenizing treatment was based on extensive experiments which indicated that virtual equilibrium was reached after 150 hr. Structures were retained by quenching in water. Grain sizes in the specimens homogenized at 350" and 450°C were generally small. These homogenizing treatments were preceded by a 50-hr anneal at 650°C to facilitate phase identification by increasing the grain size in these specimens. The specimens were furnace-cooled from this temperature to the homogenizing temperature, and the heat treatment was continued for the standard 200-hr period. The homogenized samples were bisected to provide an internal section for metallographic examination. Optimum definition of the microstructure was obtained by successive polishing and etching. Quarter-strength ASTM copper reagent No. 13 gave the most satisfactory results.10 Filings from interior sections of the samples were used for diffraction studies. These filings were annealed in evacuated glass tubes at homogenizing temperatures for periods exceeding 50 hr and quenched in water. During this treatment the manganese content was reduced by significant amounts, probably by vaporization. This change in composition was considered in applying the diffraction data, which were used only as a means of identifying phases where the data were consistent with the metallographic evidence. Phase Identification The a solid solution is readily distinguished by the copper-colored, twinned, polyhedral grains, as shown in Fig. 2, and a face-centered cubic X-ray pattern. Tukon indentations, using a 25-g load, indicate a Knoop hardness of 155 for a quenched from 650°C. Using white light developed by a Wratten 78 A filter, the ß grains in etched specimens have a dark brown tint in contrast to the lighter copper-colored grains of the a phase. Knoop hardness values of 284 were obtained for the ß structure in specimens quenched from 650°C. The ß structure was also distinguished from the a phase by its body-centered cubic lattice. The acicular structure appearing in Fig. 3 was evident in several alloys of higher tin content after quenching from either 750&apos; or 650°C. Since a trans-

Jan 1, 1954

By Nicholas J. Grant, Michio Yamazaki

Cast copper alloys containing 10, 20, and 30 pct Ni and 0.75 to 0.80 pct Al were machine-milled into chips, then comminuted in a rod mill to fine flake powder utilizing a number of processing variables. The powders here internally oxidized, mostly at 800°C, in a low-pressure oxygen atmosphere. The consolidated powders were hot-extruded into bar stock. Room-tenmperature tension tests, stress-rupture tests mostly at 650°C, but also at 450° and 850°C, and hardness measurements after various annealing temperature treatments to study alloy stability were perfomted. Excellent room-temperature strength, high rupture strength at 650°C, and resistance to recrystallization at 1050°C were obtained. Problems in optimizing conditions for internal oxidation of Cu-Ni base alloys are discussed. THE interesting high-temperature properties of SAP&apos; have stimulated considerable effort in the study of more refractory alloy systems where the potential for high-strength alloys at high temperature is great.2-13 A number of methods have been utilized to produce the desired fine, hard particle dispersions, of which internal oxidation2,9,7 of dilute solid-solution systems offers considerable promise by virtue of the potential for producing ultrafine, well-dispersed oxides. While most of the published works are concerned with pure metal matrices, a number of investigators have studied the effects of solid-solution strengthening.10,19 Use of more complex alloy matrices (for example, aging systems) has been unsuccessful because overaging still occurs at high temperatures in the oxide-containing alloys.14.15 Solid-solution strengthening is, however, effective at very high temperatures9,10 and might be expected to contribute importantly to the strength of oxide-dispersion strengthened alloys. For this study, internal oxidation of solid-solution alloys of copper and nickel, containing small amounts of aluminum, was chosen as the method of alloy preparation. PREPARATION OF ALLOYS Three copper alloys containing about 10, 20, and 30 pct Ni and each containing 0.75 to 0.80 pct A1 (enough to yield about 3.5 vol pct alumina) were prepared as air-cast ingots measuring 2.5 in. diameter by 6 in. high (see Table I for the analyses). Processing steps for all the alloys were as follows (also see Table 11): 1) Homogenization of the ingot at 982°C (1800°F) for 45 hr in an argon atmosphere. 2) Machine milling of ingots into fine chips. Average thickness was about 0.1 to 0.2 mm. 3) Hydrogen reduction of chips at 593°C (1100° F) for 1 hr to reduce copper and nickel oxides. 4) Rod milling of chips to finer powders. 5) Hydrogen treatment of powders as in step 3. 6) Internal oxidation of the powders. 7) Hydrogen treatment of oxidized powders as in step 3. 8) Hydrostatic compression of evacuated powders. 9) Sintering of compacts in hydrogen. 10) Hot extrusion. Variations in processing among the alloys were made in steps 4, 5, and 10 (see Table 11). In the past, two methods were utilized to internally oxidize alloy powders. Preston and Grant3 surface-oxidized dilute Cu-Al powders to obtain the necessary amount of oxygen to oxidize the solute metal (aluminum and silicon), and then permitted the formed copper oxide to diffuse and react with the solute in an argon atmosphere. Bonis and Grant4 exposed Ni-A1 and other nickel alloys to an oxygen pressure derived from the decomposition of nickel oxide at a preselected temperature, in an argon atmosphere. Both methods are applicable and can be modified to generate a range of oxygen pressures for oxidation of the solute but not the solvent metals. Procedure I: Surface Oxidation of Alloy A3, Cu-10Ni-0.76A1. Powders of -20 to +28 mesh were surface-oxidized at 500°C (932°F) to obtain the desired amount of oxygen for oxidation of the aluminum to alumina; the powder was then sealed in Vycor and heated at 900°C (1652°F) for various times up to

Jan 1, 1965

By W. L. Phillips

Aluminum and copper single crystals were strained in shear, unloaded and rotated 60, 120, and 180 deg. The magnitude of the Bauschinger strain increased rapidly during the easy glide region and became constant as the easy glide limit was reached. An increment in stress was not required to continue slip in any close-packed plane or in the reverse direction during easy glide. A qualitative theory is proposed to explain the present results. FOLLOWING the initial work on tin by Bausch,&apos; there have been several investigatorsB7 who have employed the shear test to study the deformation of aluminum. In all cases the shear technique was employed in an attempt to obtain a more homogeneous shear than in the conventional tension test The direct shear technique has the obvious advantage, relative to the tension test, that a crystal may be stressed in any predetermined plane and direction, including the reversal of strain sense. In the present investigation the shear technique was employed with aluminum and copper single crystals and their behavior was studied with respect to deformation in all close-packed directions in the octahedral plane. In contrast to previous investigations, the shear technique was used in an attempt to obtain a stress-strain curve in shear which is identical with the corresponding tension curve and then to use the additional degree of freedom of the shear test to study the mechanical behavior of crystals in all close-packed directions in the octahedral plane. PREPARATION OF CRYSTALS Single crystals 1/2 in. in diam and 6 to 7 in. long, were prepared from aluminum containing 0.001 pct Si, 0.001 pct Fe, and 0.001 pct Zn, by spectro-graphic ana1ysis and from OFHC copper. Crystals were grown from the melt in graphite at a rate of 1 5 in. per hr. The copper crystals were grown under an argon atmosphere. No lineage structure was observed in Laue patterns, though small angle boundaries were present in the crystals. The aluminum and copper crystals were annealed at 640" and 900°C, respectively, for 24 hr and furnace-

Jan 1, 1962

By C. Elbaum

If a thin layer of liquid gallium is spread on a surface of solid aluminum, the gallium penetrates high-angle grain boundaries at a very rapid rate and separation along these boundaries follows. An experiment was carried out to investigate this phenomenon. A well-annealed specimen of aluminum 99.994 pct pure, consisting of several large grains was used, Fig. 1. The dimensions of the sample were 25 mm wide by 2.5 mm thick and all the grain boundaries extended through the entire thickness of the plate. This sample was prepared by strain-annealing and, as can be seen in Fig. 1, contained one long, straight boundary. An examination of the crystal orientations showed this boundary to be a coherent twin boundary. The angular misorientations between the grains forming the other boundaries were all in excess of 20 deg. A thin layer of liquid gallium was spread on one side of the specimen at about 30°C (the melting point of gallium is 29.7"C). After the application of the liquid the temperature was lowered to about 27°C. The gallium remained liquid at this temperature and it can be seen from the A1-Ga phase diagram1 that the liquid was probably saturated with aluminum.

Jan 1, 1960

By S. Weissmann, P. R. Swann, D. F. Wriedt

The sizes and density of precipitates in an intemally oxidized 0.19 wt pct Al-Ag single crystal have been determined by low-angle X-ray scattering and by transmission electron microscopy . The correlation in particle sizes measured by the two techniques is reasonably good. For an oxidizing temperature of 800°C the particles were found to INTERNAL oxidation of dilute alloys of aluminum in silver produces an oxide which has an excess of oxygen compared to Al2O3.&apos; It is believed that the excess oxygen is an indication of the small sizes of the oxide particles. Depending upon the particular model chosen for the oxide structure, the size of the o-A1 particles can be calculated as a function of the oxygen-to-aluminum ratio. These calculations pre- have diameters in the range 30 to 140A, with a mean size of about 50.4 as observed by electron microscopy. At lower oxidizing temperatures, less than 600°C, no clearly resolved particles are formed, and it is suspected that if A1-0 clusters exist they must be exceedingly small, i.e., 10A or less in diameter. dicto that the particles would vary in size from 15 to 100A. This range of sizes is amenable to detection by both small-angle X-ray scattering and transmission electron microscopy. This paper compares the cluster sizes in such internally oxidized A1-Ag alloys determined by transmission electron microscopy and small-angle X-ray scattering. SPECIMEN PREPARATION Single crystals were prepared from 99.9999 pct Ag, obtained from Cominco Products, and 99.99 pct Al, obtained from Aluminum Co. of America. All melting operations were carried out in graphite molds under flowing purified hydrogen in a horizontal zone refiner. The silver was first degassed,

Jan 1, 1964

By Herbert Herman, M. E. Fine

THE first decomposition product of a supersaturated aluminum-rich A1-Ag alloy at low tempera- tures is Guinier-Preston zones.&apos;-, The zones are ideal and each consists of a spherical shaped silver-rich cluster about 16 A in diam syrounded by a silver-poor shell approximately 72A in diam.&apos; The composition of the two regions is not known with certainty., After quenching from the solution anneal, these zones form rapidly on aging at temperatures as low as -30°C.5 The rate of zone formation increases with aging temperature; the activation

Jan 1, 1961

By Colman Goldberg

IT is customary to plot crystallographic planes or axes on a Wulff stereographic net which is ruled with parallels of latitude and meridians of longitude. If a single crystal is placed at the center of a sphere, the coordinates of a crystallographic plane or axis are the coordinates of the point where the axis intersects the sphere. The standard (HKL) projection is the projection for which the sphere is rotated so that the (HKL) pole is at the center of the projection. Schiebold and Sachs&apos; and many others have published standard projections for the more important planes of a cubic crystal. With Tables I and 11, it is possible to plot any plane (HKL) of a cubic crystal on a standard (001) projection if the absolute values of the individual H, K, and L are nine or less, which is almost always the case. Using the methods outlined by Barrett,&apos; the standard (001) projection can be rotated so that any arbitrary plane is at the center of the projection. The tables are believed to be important for two reasons: 1—The heretofore published standard projections usually are not of the proper size to fit the stereographic nets available. With these tables a standard projection can be made which will be of exactly the proper size for the available stereographic net. 2—With the tables, planes that do not appear on the previously published standard projections can be easily plotted. For these reasons, the tables are especially useful in the study of optical reflections from etched surfaces and can also be used to make a standard projection for the axis which is normal to the macroscopic surface. (This axis can be found by X-ray or optical methods.) Then if the crystal is etched, the effect of the etchant can readily be determined by comparing the latitude and longitude of the reflecting planes (as determined with an optical goniometer) with the standard projection that has been prepared. Use of the Tables Fig. 1 shows the meridians and parallel which have been designated as zero longitude and latitude. The tables themselves are self-explanatory. The

Jan 1, 1953

By R. W. Heckel

The conzpaction of metal powders is analyzed through density-pressure curves as a three-stage process — die filling, individual particle motion, gross compact deformatim. The densification occurring during each of these stages is evaluated quantitatively. The amount of densification in the first and second stages is primarily a function of particle geometry. The densification taking place in the third stage is dependent mainly upon the material. AT the present time the densification of powders during compaction is usually described by terms such as "compactibility," "compressibility," and "compression ratio." Schwarzkopfl has proposedthat compactibility be defined as the minimum pressure needed to produce a given green strength, while compressibility be used to indicate the extent towhichthe density of a powder is increased by a given pressure. Compression ratio is generally defined as the ratio of the compact density obtained at a given pressure to the apparent density of the loose powder. 13alshina found that the pressure imposed on a compact affects the relative volume of the compact according to the following relation: hP= - LV + C [ll where: P is the applied pressure, V is the relative volume of the compact, Ratio of the specific volume of the compact to that of the material without porosity. Lisa constant described as the modulus of pressing and is determined by the slope of a plot of h P vs V, and C is a constant which is determined by the intercept of a plot of InP vs V. Several drawbacks of the Balshin analysis may be noted from Fig. 1, which is a plot of pressure (loga-

Jan 1, 1962

By M. H. Richman, E. S. Meieran

An analytical method is presented which enables the electron diffraction patterns from a twinned region to be indexed. The method has only been applied to (112) twins in bcc lattices, but can easily be adapted to other types of twinned lattices. Calculations of all twin spots, including those superimposed on matrix spots, is made possible by this method. SINCE the advent of transmission electron microscopy, the analysis of selected-area electron diffraction patterns has become very important in the interpretation of electron micrographs. Frequently, as in the case of some martensites, twinned areas are observed and give rise to complex diffraction patterns, which so far can be analyzed only for the simplest orientations of the thin foil specimen with respect to the electron beam. In order to simplify the analysis of twin patterns of more complex orientations, an analytical method was devised which is capable of predicting the positions of all reflections from both matrix and twin regions for all possible foil orientations. Although the method has only been applied to the case of bcc metals twinned about a (112) plane, it is equally applicable to other Bravais lattices. This method has been successfully applied to selected-area electron diffraction patterns of Fe-Ni and Fe-Ni-C martensites and drawn tungsten wire. PROCEDURE Imagine the reciprocal lattice corresponding to a bcc material, with each point hkl representing the crystallographic plane (hkl). Since the extinction conditions require that for this lattice, only reflections where h + k + 1 = even integer are allowed, the three dimensional reciprocal lattice is actually fcc. Since in real space twinned regions and matrix regions are mirrored across a (112) plane, the twinned reciprocal lattice is derived from the matrix reciprocal lattice by a rotation of 180 deg about a (112) direction. While it is possible to calculate how a point hkl will shift under a twinning transformation to a new point htktlt using only the reciprocal lattice based on the orthonormal vectors [100], [010], and [001], the calculations are greatly simplified if a new orthonormal coordinate system containing the twin axis is introduced. The twinning operation then becomes a simple rotation of 180 deg about a principal coordinate axis (in this case the twinning axis), and a retransformation back to the original reciprocal space will give the position htktIt of the twinned reflection.

Jan 1, 1963

By W. L. Phillips

Single crystals of aluminum, brass, and copper oriented for (100) and (110) slip were extended at 25°, 400°, and 600°C in simple shear. Aluminum specimens oriented for nonoctahedral slip began to shear at a higher critical resolved shear stress than specimens oriented for octahedral slip. Parabolic stress-strain curves were obtained from zero strain. The initial rate of parabolic hardening was lower for specimens sheared on the (100) plane in a close-packed direction <110>, than for specimens sheared in a nonclose-packed direction <100>. metallographic evidence, however, showed that all slip traces could be explained in terms of (111) <100> slip. All attempts to cause nonoctahedral slip in copper and 70-30 a-brass single crystals were unsuccessful. Instead of shearing, the crystals bent, allowing {111} type planes to come into action. NONOCTAHEDRAL slip in aluminum has been reported under three different conditions: first, as the main mode of slip in tension experiments at elevated temperatures;&apos;-&apos; second, as the main mode of slip in direct shear experiments at room temperat~re; and third, as a minor mode of deformation, i.e., as cross-slip, in tension, shear, and bicrystal experiments at room and elevated temperatures."-l2 However, as far as the author knows, nonoctahedral slip has not been reported in either copper or 70-30 a-brass. The present study was undertaken to determine whether nonoctahedral slip could be obtained in aluminum, brass, or copper at room or elevated temperatures when the shear stress was approximately constant over the cross-section, a maximum at the center, or a maximum at the surface. EXPERIMENTAL PROCEDURE A detailed description of the crystal preparation and shearing apparatus has been given previo~sly. Cylindrical crystals 1/2 in. in diam and 8 in. long were grown from the melt in a temperature-gradient furnace. The aluminum contained 0.001 pct Zn, 0.001 pct S, and 0.001 pct Fe; the 70-30 brass contained 0.015 pct Pb, 0.001 pct Fe, 0.01 pct Ni, 0.02 pct Sn, and 0.005 pct Se; the copper was certified OFHC of 99.98 pct purity. All samples were electropolished prior to testing. The shear apparatus was a modified Bausch type. The strain sensitivity was 4 x lob4 Load was applied by clamping the rods attached to the shear plates in an Instron tensile machine. The rate of loading was 0.02 in. per min. In all cases a 1/8-in. gage length was used. For the tests performed at 400° and 600°C the shear plates, collars, and rods were made of stainless steel. These elevated-temperature tests were performed in an argon atmosphere. A) Aluminum at Room Temperature. Values of a and ß for the various slip planes and slip directions investigated are shown in Table I where a is the complement of the angle between the specimen axis and the slip direction, and ß is the angle between the specimen axis and the normal to the shear plane. The shear stress is a function of a (assuming ß - 0);10 when a is less than 27 deg, the shear stress on the slip plane for which the specimen is oriented has a maximum at the center of the crystal; at a = 27 deg the shear stress is constant across the slip plane; for a greater than 27 deg the shear stress is a minimum at the center. Fig. 1 shows the stress-strain curves for specimens cut from crystals 1, 2, and 5, which were sheared on the (010) plane in the [loll direction at room temperature. These three crystals have shear-stress distributions corresponding to the three dif-

Jan 1, 1962

By G. F. Bolling

HE high mobility of grain boundaries in zone-refined metals has been particularly demonstrated for lead above 150°C in grain growth studies1 and in the extensive work by Aust and Rutter.1 In these investigations, no elaborate precautions were taken to eliminate oxygen from the zone-refined lead; however the alteration of creep characteristics by oxygen concentrations of less than 5 x 10 -5 wt pet

Jan 1, 1962

By A. S. Keh, H. A. Wriedt

The Precipitation of nitrides in quenched Fe-N alloys, aged between 25° and 200°C, was studied by transmission electron microscopy. Different dislocation substructures were introduced into the materials by recrystallization, cold working, and by Phase transformation prior to the introduction of nitrogen. It was found that the precipitated nitrides, tentatively identified as Fe16N2, have (100) habit planes. Nucleation takes place Preferentially at dislocations and at subboundaries. It sometimes occurs in the matrix, probably on vacancy clusters, but rarely on high-angle boundaries. The process of nucleation on dislocations and subboundaries is very temperature dependent. At room temperature there is no particular orientation relationship between the dislocations involved and the (100) planes on which the nitride Particles formed. With increasing temperature, the nucleation sites tend to become restricted to those dislocation segments lying in (100) planes. The change of yield stress of the 0.022 and 0.043 pet N alloys during quench aging can be correlated semiquantitatively with the change in particle distribution. Strain aging in quenched alloys can be separated into two stages. The early stage is attributed to nitrogen segregation to dislocations and the later stage is associated with precipitation. When previously quench-aged specimens were strained and aged, no additional Precipitates could be seen, although a considerable amount of strain aging occurred. DURING the past two decades, the precipitation of nitrides from a iron has been extensively studied by various techniques. It has been established that two types of nitride exist. The stable nitride, Fe4N, forms at temperatures above 250oC and Fe16N2, the

Jan 1, 1962

By Hsun Hu

The microstructural changes during rolling and at various stages of recrystallization in (111)[112] oriented single crystals of Si-Fe have been studied by transmission electron microscopy. At very low deformation, the dislocation structure consists of jogged dislocation lines, edge dislocation dipoles, and numerous dislocation loops, which may be interpreted by the jog-formation mechanism in moving screw dislocations. Up to 70 pct rolling reduction, no sharply defined cells are formed. Subgrain forma- tion takes place somewhat earlier in the annealing process than in a similarly processed (110)[001] crystal. This may be partly responsible for the reported difference in the rate of recrystallization between (111)[112] and (110)[001] crystals. Evidence indicates that the formation of recrystallization nuclei occurs largely by the coalescence of sub -grains. This is consistent with previous observations on other Si-Fe crystals. AVAILABLE data in the literature indicate that the main features of rolling and annealing textures in (111)[112] and (110)[001] crystals are essentially similar. A (111)[112] or (111)[112] crystal can be rolled 70 pct without changing its initial orienta-

Jan 1, 1964