Search Documents

By H. B. Probst

Mechanical twins were produced in zone-refined tungsten single crystals by explosive working at room temperature. These twins are parallel to (112) planes and have irregular boundaries rather than the classical plane twin boundaries. These boundaries aye grooved surfaces in which the grooves themselves are parallel to a <111> direction and the sides of the grooves appear to be par-allel to (110) planes. TWINS were produced in tungsten single crystals by explosive working at room temperature. These twins differ in character from any previously reported for tungsten; however, they are similar to those found in molybdenum after compression at -196°C.1 Deformation twins "resembling Neumann bands in ingot iron" have been observed in tungsten by Bech-told and Shewmon.2 This observation was made with sintered polycrystalline tungsten pulled in tension to fracture at 100°C and using a strain rate of 2.8 x 10-4 sec-1. More recently Schadler3 found deformation twins in zone-refined tungsten single crystals pulled in tension at -196"&apos; and -253°C. These tests were conducted using a strain rate of 3.3 x l0-4 sec-1, and the twin bands were found to be parallel to a (112) plane. Deformation twins in tungsten&apos;s sister metal, molybdenum, were observed by Cahn.4 These twins were produced by compressing small (0.7 mm) vapor-deproducedposited molybdenum single crystals at -183°C. The compression was performed &apos;by impact." By the use of precession X-ray techniques, Cahn was able to identify the twin plane as {112} and the shear direction as <1ll>. Mueller and Parker1 produced deformation twins in polycrystalline electron-beam-melted molybdenum by compression at -196°C. Their "loading rate" was 5000 psi per min which, judging from their stress-strain curve, corresponds to a strain rate of approximately 0.3 x 10-4 sec-1. These twin bands were found to be parallel to (1 12) planes; however, they differed in appearance from previously observed twins. In place of straight and parallel twin boundaries they were found to be irregular, jagged, and sawtoothed. The sides of the saw teeth were identified as (110) planes and irrational planes of a (111) zone. The twins observed in the present work in tungsten single crystals are similar in appearance to those of Mueller and Parker in polycrystalline molybdenum. The starting material used in this investigation was 3/16-in. diam commercial tungsten rod produced by powder-metallurgy techniques. This material was converted to a single crystal by the electron-bombardment floating-zone technique.= The process was carried out in a vacuum of 10-5 mm of Hg using a traversing speed of 4 mm per min. Segments (=2 in. long and 3/16 in. in diam) of two crystals (A and B) produced in this manner were studied. Crystal A received one zoning pass, while crystal B received two passes. The two crystals were explosively worked at Bat-telle Memorial Institute in the following manner. A 1/2-in.-thick layer of plastic was applied to the crystals to serve as a buffer in an attempt to prevent cracking. The composite, crystal and buffer, was then wrapped with 1/8-in.-thick DuPont sheet explosive EL506A2 and detonated in water at room temperature. Metallographic samples of the worked crystals were prepared, and back-reflection Laue X-ray patterns were obtained using unfiltered molybdenum radiation. RESULTS AND DISCUSSION Blasting the crystals as described above failed to prevent cracking. The crystals fractured into several fragments about 3/16 to 1/2 in. long; however, the fragments were of sufficient size to be useful for the subsequent study. The diamond pyramid hardness of the crystals after blasting was in the range 430 to 450 as compared with 340 for the as-melted material, which shows a definite hardening resulting from plastic deformation. These hardness values were obtained using a 1000-g load and taking readings only in sound portions of the crystals free of cracks. The crystals exhibited profuse twinning as shown in Fig. 1. No such structure is present in the as-melted condition. Most of these twins have jagged twin boundaries and are similar in appearance to those found in molybdenum by Mueller and Parker. The twins in both crystals were found to be parallel to {112} planes. This identification was made by using the conventional two-trace method. Subsequent efforts to describe these twins more fully were carried out on crystal A. If the longitudinal axis of crystal A is placed in the (001)-(011)-(Il l) basic triangle of the standard cubic stereographic projection, as in Fig. 2, then the two sets of twins shown in Fig. 1 are parallel to the (112) and (121) planes. Fig. 3 shows a schematic representation of a twin with jagged boundaries. This type of twin with a <111>

Jan 1, 1962

By P. K. Koh

Chi phase (body-centered cubic, a = 8.89A) was found in as-cast 23 pct Cr-10 pct Mo-Fe alloy as well as in heat-treated 316, 316L, 317, and modified 446 stainless steels. Chi phase resembles sigma phase in its metastability, chemical composition, and brittleness. Microstructure and some of physical properties of chi phase were developed. MOLYBDENUM has been established as a desirable alloying element for the enhancement of corrosion resistance in Cr-Ni steels and creep and rupture strength in high temperature alloys. On the debit side, however, the molybdenum addition has been known to stimulate u formation. When the molybdenum-bearing steels were subjected to prolonged heating at elevated temperatures, losses of corrosion resistance and/or ductility have been observed. Andrews1,2 first found the existence of a new phase among the anodic FeC13 extracts from type 316 stainless steel solution treated and then reheated from 800" to 1100°C. This phase was designated x and was identified by diffraction patterns as of body-centered cubic structure with a value equal to 8.89? and similar to that of a manganese. He found that the x phase in this steel always coexisted with s phase, but failed to distinguish one from the other by metallographic technique. No definite conclusion was drawn regarding the equilibrium temperature ranges of these two phases. The appearance of Andrew&apos;s work recalled an un- explained structure observed several years ago at the Allegheny Ludlum Research Laboratories during the investigation of an experimental alloy containing 25 pct Cr, 10 pct Mo, and balance Fe. X-ray diffraction patterns on the as-cast material revealed the presence of a body-centered cubic phase having a lattice parameter of 8.89?. The structure was sufficiently similar to that of y chromium that for a time it was thought that the structure might be caused by the presence of some undissolved electrolytic chromium particles. The alloy as-cast was so brittle that it shattered after the slightest hot reduction by hammer cogging. This paper gives the results of some metallographic and X-ray diffraction studies on x phase as found in several experimental alloys as well as a few molybdenum-bearing commercial stainless steels. The analyses of materials studied were as shown in Table I. Experimental Procedure Metallography: Solid specimens were polished mechanically and etched in boiling 50 pct HC1 solution in order to best delineate x and s phases in the alloys studied. X-Ray Diffraction: The difficulty of satisfactorily developing diffraction lines for s phase in solid specimens has been previously reported by Bindari, Koh, and Zmeskal.V or this reason all specimens used in this investigation were subjected to anodic

Jan 1, 1954

By E. S. Machlin, C. W. Chen

THIS investigation is concerned with the origin of the intercrystalline voids and cracks formed in metals and alloys subjected to stress at elevated temperature. There have been many suggestions in the recent literature relating to this problem. Greenwood&apos; suggested that the voids may be produced by vacancy condensation. Zener has stated that shear-stress relaxation across grain boundaries could initiate high tensile stresses at the regions blocking grain boundary slip and thereby cause the formation of cracks. Chang and Grant3 have described the formation of cracks at grain boundary triple points and have experimentally verified Zener&apos;s mechanism for the grain boundary regions in the vicinity of a triple point. Subsequent to the completion of this investigation, Gifkins4 developed a model which made use of Stroh&apos;s5 mechanism of fracturing to produce sub-microscopic fractures that subsequently grow by grain boundary slip. Chen and Machlin,6 in answer to Gifkins, described a model deduced from the present investigation, in which grain boundary slip provides both the stress to fracture at grain boundary jogs and the deformation required to separate fractured jog surfaces. The possibility of gas condensation to form intercrystalline voids and cracks is eliminated as a basic mechanism because such voids and cracks are developed in vacuum melted material containing minute amounts, if any, of gaseous impurities. In a theoretical evaluation of this problem, Machlin7 concluded that void nucleation by vacancy condensation during creep-rupture is improbable but that vacancy condensation on supercritical sized voids to produce growth is probable. This investigation was begun to evaluate the suggested mechanisms for intercrystalline fracture. In particular, in order to correlate vacancy supersaturation ratios produced in creep with those determined by Bal-luffi and Seigle8 as critical for , the nucleation of voids, specimens were obtained from the same heat of brass as used by the latter authors, through the courtesy of Dr. Seigle. The experiments conducted in this investigation fall into the following categories: 1) Brass—observation of voids produced under a variety of conditions, including creep under compression, to evaluate the mechanisms of void nucleation and growth. 2) Bicrystal experiments to check the mechanism of void nucleation deduced in this investigation. 3) Morphology of intercrystalline voids produced in a variety of metals. Each set of experiments will be described and discussed separately. Experimental Techniques A special creep-rupture test rack was constructed which made it possible to apply the stress to the specimen in a controlled atmosphere of inert gas, reducing gas, or vacuum. All the creep-rupture tests on a-brass (30 pct Zn) were conducted in nitrogen under a pressure slightly above atmospheric. Either dead weight loading or constant elongation rate loading could be applied with the load measured by means of a strain gage dynamometer. In order to obtain a coarse-grained crystal structure stable at

Jan 1, 1958

By C. G. Dunn

According to a recently suggested effect of silicon on the re recrystallization textures of high-purity Fe-Si alloys with (111)[112] type rolling textures, the recrystallization texture for a rolled (110)[001] oriented iron crystal probably should be entirely different from that of a (110)[001] oriented 3 pct Si-Fe crystal. Comparative studies of iron and 3 pct Si-Fe crystals, however, show that both have (110)[Ool] recrystallization textures when the rolling textures are the (111)[112] type after reductions in thickness of about 70 pct. Qualitatively the results from the iron crystal are like those of polycrystalline high-purity 3 pct Si-Fe and not like polycrys-talline high-purity iron. The large effect previously noted probably involves unknown impurities or processing variables rather than silicon itself. Some problems on experimental and analytical procedure for a spherical X-ray specimen, which was machined from a laminated composite of sheet specimens, are treated in the Appendix. A possible strong effect of silicon on the textures produced in cold-rolled high-purity Fe-Si (HPFe-Si) alloys during primary recrystallization and normal grain growth was suggested in a recent paper.&apos; All the textures were far from the random-orientation type, but that of iron, or of Fe-Si alloys of low silicon composition, was entirely different from the texture of 3 pct Si-Fe. The same effect was noted for the textures obtained prior to normal grain growth, i.e., for primary recrystallization.2 It is the main purpose of the present paper to provide some clarification of this silicon effect. All the HPFe-Si alloys from zero to 3 pct Si, which were rolled by two or more stages separated by anneals, developed (111)[112] type rolling textures.2 Thus, there was no effect of silicon on the rolling textures. Earlier, Gensamer and Mehl3 also found no effect of silicon on the rolling textures of Fe-Si alloys; they obtained the Kurdjum.ow and Sachs (K-S) rolling texture for iron,4 which is characterized as the three ideal components: (100)[011], (112)[li0], and (111)[112]. There is a difference between the HPFe-Si multiple-stage rolling texture and the K-S single-stage rolling texture, but this is a variable processing effect. Of interest here is the fact that the recrystallization textures from (111) [llZ] type rolling textures were different depending on the amount of silicon in the alloy. There was a relatively strong (110) [001] component in the recrystallization texture of HP 3 pct Si-Fe5,8,2 but no such component in HP 0.6 pct Si-Fe, for example; the recrystallization texture for the latter was two (111) [110] type components and a (111) fiber component 1,2 Several publications have shown that a strong (110) [001] recrystallization texture is derivable from a (111) [112] type rolling texture for 3 pct Si-Fe crystals reduced in thickness by about 70 pct.7-10 Furthermore it appears that the strongest of these (110) [001] recrystallization textures occurred when the orientation of the crystal prior to rolling was (110) [001].7 Barrett and evensoon11 found that the rolling texture of a (110)[001] oriented iron crystal was (111) [llj]. Accordingly, it seemed desirable to determine whether a (110) [001] oriented iron crystal, upon rolling and annealing, would behave like the 3 pct Si-Fe crystal (or the polycrystalline HP 3 pct Si-Fe) and thus produce a (110) [001] recrystallization texture contrary to the suggested silicon effect, or would behave like the polycry stalline HP iron or HP 0.6 pct Si-Fe and thus produce (lll) [110] type components in agreement with a silicon effect. Briefly, the idea here involves the use of more precisely defined textures to obtain if possible better control of important variables that affect the recrystallization process. PROCEDURE A (110) oriented crystal of Ferrovac "E" iron (99.9 pct pure) was prepared in sheet form 0.080 in. thick with the [001] direction parallel to the long dimension of the specimen.&apos;&apos; This crystal was etched to 0.073 in. thickness (to remove some small included grains) and then was cold rolled in a 6-in.-diam mill to a final thickness of 0.022 in. The rolling was unidirectional except for an inadvertent reversal at 0.061 in. thickness. At this thickness, and also at 0.040 in., the rolling was interrupted for transmission Laue photographs. Molybdenum Ka-radiation filtered with zirconium was used in a transmission method1&apos; to obtain the cold-rolled (110) pole figure. The sample was a 0.002-in.-thick section taken from the central region of the 0.022-in.-thick cold-rolled crystal. For the primary recrystallization study, cold-rolled samples were etched from 0.022 to 0.021 in. thick and annealed in hydrogen at 850°C. Primary recrystallization to a fine-grained structure, Fig. 1, was obtained in a 5-min anneal. Eleven sheets after

Jan 1, 1963

By H. P. Stüwe

HE recent papers of Aust and Rutter112 have again brought to mind the importance of certain "special" orientation relationships between the lattices of two fcc crystals on the mobility of the grain boundary separating them. No theoretical treatment of this problem has been offered till now. The only principle published so far that has given an indication why certain orientation relationships should be "special" is the counting of "coincidence sites" according to the suggestions by Kronberg and Wilson.3 The "coincidence plots" published by these authors show, for instance, that two fcc lattices rotated by 38 deg around a common (111)-axis have 1/7 of their lattice sites in common. Such an orientation relationship is also characteristic for high boundary mobility. The accuracy of the orientation relationship needed for high mobility is not too rigid. Deviations up to 10 deg from the ideal orientation seem to be tolerable as can be gathered from the experimental data.&apos;j4 The auestion arises, then. how the density of coincidence sites will be affected by a deviatioi from mathematical accuracy. This can be checked by a simple model. Two sieves are prepared, the arrangement of the holes corresponding to lattice sites on a (111)-plane in a fcc crystal. They are placed upon each other, Fig. 1. One is kept fixed, the other is rotated around an axis pushed through one hole in common to both. The light falling through holes of both sieves is then a measure for the density of coincidence sites. If the diameter of the holes is very small, light intensity is contributed only by holes the centers of which coincide "exactly." If the diameter of the holes is rather large, some intensity will be contributed by

Jan 1, 1962

By D. Weinstein, F. C. Holtz

AS a possible method of improving the elevated temperature strength properties of zirconium, an investigation was initiated on the feasibility of producing a dispersion-strengthened material. Because of the high reactivity of zirconium, its high solubility for oxygen, and the stability of the Zr-0 solid solution, the major problem in such a development is choice of a suitable dispersant. Thus, in the present investigation we were concerned primarily with the stability of various dispersants in the zirconium matrix. The experimental procedure consisted of blending powders of zirconium and a dispersant, followed by cold compaction and extrusion. The best available source of -325 mesh zirconium powder contained between 1500 and 3500 ppm Oz; to this material, powders of zirconium carbide (5 p max), vanadium carbide (5 p max), alumina (0.03 p average), lan-thana (0.8 to 2 p), ceria (0.8 to 2 p), yttria (0.8 to 2 p), calcia (44 p rnax), or thoria (0.6 to 0.8 p) were added in amounts of 7 vol pct and compacted at 65 tsi. A cylindrical compact having a density between 70 and 80 pct of theoretical and dimensions of 1 in. diam by 1-114 in. high was thus produced. After canning in copper, these billets could be extruded (5: 1) on a 54-ton capacity, slow-traverse hydraulic press with the billet temperature at 1550°F and the extrusion die at 900°F. However, lack of densifica-tion of some of the extruded billets necessitated ratios of at least 23 :1. Ultimately, all billets were successfully extruded at 1500°F to 0.190 in. diam (32 :I), fully dense rods using a 200-ton capacity press and a ram speed of 90 ipm. The microstructures of as-extruded Zr-7 vol pct LazOS and Zr-7 vol pct Y2Os are shown in Fig. l(a) and (c), respectively. These structures are similar to all the as-extruded materials and consist of an elongated, single-phase zirconium matrix dispersed with oxide or carbide particles. Very little porosity is observed, and the interface between matrix and particles appears satisfactory. The size and distribution of particles, however, are not ideally of the type desired for dispersion strengthening. Since the primary study was of particle stability with respect to zirconium, no attempt was made to overcome agglomeration during powder blending and fabrication. Some areas exhibit fine, well-distributed particles; undoubtedly, a small proportion is submicroscopic and has the

Jan 1, 1963

By Hsun Hu

Based on Kurdjumoiv-Sachs orientation relationship for the fee bee transformation in metals, the jirzal crystal orientation resulting from successive transformations of bee-fee-bee has been analyzed mathematically. There are 528 different variants; many of ther are crystallograpyically equirvalent. Specific examples show that, for equal probability of all the variants, the principal crystallographic axes [100 ], [110], and [111] of the initial bcc crystal can be transformed into vairous axes in the fina1 crystal However, fur each of these principal crystallographic axes, a continuous range of orientation within certain regions of the unit triangle is completely avoided by the finctl Crystals. For uses of higher indices, the final orientations are more uniformly distributed throughout the unit triangle. Results from the PI-esent analysis are in good agreement with preferred Oientations Observed in a zone-meltecl iron bar. THE allotropic forms of iron are characterized by the unusual fact that at both high and low temperatures a bcc structure is stable, whereas at intermediate temperatures (1400" to 910°C) the metal is fcc. Hence, during cooling from its melting temperature, iron undergoes successive phase transformations ofd—? —a with corresponding changes in the crystal structure of bcc — fcc -bcc. while numerous studies have been made in the past of the 1 — a transformation in iron and in various iron-base alloys, no information is available in the literature as to the mechanism of 6 — l transformation and the lattice orientation relationship between these two phases. Experimental difficulties have apparently prevented researchers from undertaking these studies. The laltice orientation relationship between the parent and the new phases of iron resulting from

Jan 1, 1965

By C. G. Dunn, J. L. Walter

COULOMB&apos; and Coulomb and Lacombe2,3 have recently discussed secondary recrystallization in soft iron (99.5 pct Fe). They found that the appearance of this phenomenon was dependent on both the presence of impurities and the thickness of sheet specimens. They concluded that impurities such as carbon, sulfur, and oxygen in the soft iron stabilized the matrix structure and allowed growth of a few grains of specific orientations. They also found that secondary recrystallization ceased when the final thickness was small and attributed this complete inhibition of growth in thin sheet to the restraining action of thermal grooves. When purer iron (99.99 pct Fe) was used, normal grain growth but not secondary recrystallization was obtained. On the other hand it is known that the necessary stabilization of the matrix structure for secondary recrystallization in high-purity silicon iron probably does not depend on impurities but more likely results from the specimen thickness effect of Beck et al.,4 according to evidence and ideas advanced by Walter and Dunn,5,6 and Detert.7 Furthermore, Mullins8 has indicated that if a gas-metal surface energy difference exists across a grain boundary equal to or greater than about 3 pct of the grain boundary energy, then such a grain boundary should not become stuck. Similarly, Walter and Dunn have estimated that any increase in restraining force due to increased thermal grooving with decrease in

Jan 1, 1962

By Nicholas J. Grant, Robert H. Kane, Bill C. Geissen

The platinum-rich section of the Ta-Pt Phase diagram was worked out by metallographic and X-ray techniques, using twenty alloys; solidus temperatures and solid solubilities were determined. Besides s phase, four intermediate stoi-chiometric phases were found: TaPt (high-temperatzrre phase, structure unknown); TaPt2 (ortho-rhomhic, new type); a TaPt3 (orthorhombic, TiCu3 type); ß TaPf3 (monoclinic, new type). TaPt2 and TaPt3 melt congmentlv; two eutectic, two beritec-tic, and one eutectoid reactions occur in the inuestigated range. THE Ta-Pt system was examined as part of a study of the phase diagrams and the intermediate phases of niobium and tantalum with Group VIII transition metals. Since the main scope of this work was the relation among the ordered close-packed phases occurring in the concentration range from AB to AB3 (A = Nb, Ta; B = Pd, Pt, and so forth), only the platinum-rich side of the diagram was worked out thoroughly, while spot checks were made to determine the approximate outline of the tantalum-rich portion. The system has not been thoroughly treated in the literature; Greenfield and Beck1 in their survey of refractory metal intermediate phases found a o phase between -18 and 37 at. pct Pt which coexists at higher platinum concentrations with an unidentified intermediate phase. Browning2 worked on the range between 55 and 100 at. pct Pt; however, this preliminary study did not cover temperatures >1500°C, and included no conclusive crystallo-graphic data. More recently, a study of the platinum-rich section of the Ta-Pt system has been carried out by Ray,3 while Hartley, Parsons, and steedly4 have studied the tantalum-rich section. The crystal structures of TaPt2, a TaPt3, ß TaPt3, and others have been reported in abstracted form by Giessen and Grant.5 EXPERIMENTAL METHODS The methods of alloy preparation and processing and of the metallographic and X-ray procedures follow very closely those described by Ritter, Giessen, and rant&apos; for other refractory metal-noble metal systems, and will not be repeated except where significant differences exist. Starting materials were: tantalum rod of 99.95 pct purity, supplied by National Research Corp., and platinum sponge 99.9 pct, supplied by The International Nickel Co. An oxygen analysis of the tantalum rod showed 30 ppm O; other impurities were C, N, Si, Nb, Mo, none of these exceeding 50 ppm, and 100 ppm W. Homogeneous buttons were readily prepared as follows: ingots of 5 g were weighed and arc-melted under welding grade argon, followed by two remelts after inverting the button. Between 40 and 100 at. pct Pt, weight losses during the first melt rarely exceeded 0.1 pct, in which case the alloy was rejected, and were nil on subsequent remelts. Since the vapor pressure of platinum far exceeds that of tantalum, the small evaporation loss could be assumed to consist of platinum; therefore, a corresponding amount of platinum was added on the second melt. Since it was confirmed on pure tantalum samples that no weight gain through oxygen or impurity pickup occurs (see Ref. 71, it could be assumed that the uncertainty in the composition did not exceed ±0.1 at. pct for the range 40 to 100 at. pct Pt. For the four control melts from 0 to 40 at. pct Pt, an error of ±0.5 at. pct was calculated. Microscopic examination of the whole buttons after melting showed no inhomogeneity other than local coring. This was eliminated by a homogenization heat treatment. A total of twenty-three alloys were prepared. Heat treatments were carried out in a tantalum

Jan 1, 1965

By W. R. Hibbard Jr., R. W. Guard, N. G. Ainslie

Evidence is presented that copper-base solid solutions of different solutes having equal grain sizes, no preferred crystal-lographic orientation, equal electron-atom ratios, and, within experimental scatter, identical initial yield strengths, need not have identical stress-strain curves at strains larger than about 0.04. The stress-strain behavior is rationalized in terms of the proposed Suzuki chemical interaction between solute atoms and extended dislocations using what is thought to be a somewhat different means of representing stress-strain data. ALTHOUGH the effect: of alloying element upon the strength characteristics of sold solutions is a subject which has received considerable attention in the past, the exact relationships between the common deformation parameters and certain common variables are not really known in some cases. As a result some of the experiments reported in the literature in which these variables are inadequately controlled lose some of their persuasion regarding underlying principles. Nonetheless, facts are known which bear pointing up: When the true stress, a, and true plastic strain, E, of tensile deformatic~n are plotted on a double logarithmic coordinate system, one may observe a straight-line relationship at strains greater than 0.02. The form of the curve in the linear region is given by a = Ken! where a represents true stress, E, true strain, and K and tn, constants. If the relationship holds, K and m define the flow characteristics of the material being tested. m and K, however, may vary with other parameters. Hollomon found that in a-brass, m is influenced by grain size. French and HibbardZ found in alloys of copper that inverse relationships existed between m and 1) the solute concentration for a given solute, 2) the 0.01 yield strength, and 3) the constantK. Lacy and Gensamer3 observed (du/d~) (= U/Em) to increase with increasing values of K in systems of alloyed ferrites (although with considerable scatter of data which may be attributed to uncontrolled grain size). Brick, Martin, and Angier* deduced in copper-base alloys a straight-line relationship (with some scatter) between the change in the Dph number due to solid-solution strengthening and the change in the Dph number due to work hardening which suggested that copper-base alloys having equal yield strengths might have identical stress-strain curves in the plastic flow regions. French and HibbardZ concluded that the yield strength of copper-base solid solutions is the proper basis for comparing the effects of solute elements. Also, Allen, Schofield, and ate&apos; showed that, within their experimental variation, copper-base alloys of zinc, gallium, germanium, and arsenic having the same electron-atom ratios have the same true-stress true-plastic strain curves. Dorn, Pietrokowsky, and ~ietz&apos; also found that with aluminum-base alloys the stress-strain curves in the flow regions are approximately the same if "equivalent" concentrations of alloying elements are used. Solute valence and lattice parameter distortion were the parameters used to determine equivalency. The present report describes an investigation in which an attempt was made to obtain copper-base solid-solution alloys of four solute elements having within close tolerances equal grain sizes and yield strengths, and to see if the level of yield strength does indeed define the flow curve regardless of solute type. During analysis of the data certain unexpected features of the stress-strain curves became apparent which gave rise to some speculation and are discussed at length in the paragraphs that follow. EXPERIMENTAL PROCEDURES Alloy Preparation—Using the data of French and HibbardZ as a first approximation, four different binary copper-base alioys were designed so as to have the same yield strength. In addition, other alloys were prepared in which the solute aoncentrations varied slightly from those calculated above so as to span a range of yield strengths, see Table L The yield strengths of all alloys prepared except the copper-tin alloys were subsequently found to Lie fairly close to one another. The copper used in the alloys was produced by the American Smelting and Refining Co. and was of very high purity (99.999 pct). The alloy additions and their initial purities are as follows:

Jan 1, 1960

By J. P. Neumann, L. Raymond

At temperatures near 1000°C, only the (112) (111) slip systems are operatire in tungsten. Therefore, the substructure introduced into the billet upon rleforming a single crystal by rolling at 1000 "C can be controlled by proper selection 01. processing ral&apos;iubles. Using a reduction of 10 pct pel- pass, the (001)[110] and the (110)[001] crystals will deform by duplex slip rip to a 50 pet reduction in thickuess. These rolled single-crystal sheels are characlerized by anisotropic hardening, retention of ductility with warm working, lattice bending which is related to the conlacl (angle, and macroscopic dimensional changecs in the length bid not the width of the billet. When several slip systems become operative, a greater degree of work hardening is itztvoducetl into the crystal. This rolling- condition is characlerized by isotropic hardening, loss of ductilily with warm working, complex lattice distortions, and macro-scopic dimensional changes in both the length rind Width of the billel. IN tungsten, the {1 10}(111) slip systems are operative below room temperature,&apos; while above 700°C only the {112{ (111) slip systems are observed.2,3 In the transition region, i.e., room temperature. both systems appear. It is the purpose of this investigation to show that tungsten single crystals deformed by rolling at a temperature where only one slip system is operative generate dislocation substructure which depends on the crystal orientation. For a specific crystal orientation. the resulting dislocation substructure can be further influenced by modifying the rolling procedure. Crystals oriented for multiple slip display less substructural sensi- tivity to modifications in processing techniques than do single crystals oriented for duplex slip. Under simple slip modes of deformation, very little work hardening is introduced into a rolled single-crystal sheet. Mechanical properties such as room-temperature strength. ductility, and hardness are used to confirm the existence of the different work-hardened conditions generated within the crystal by modified warm-rolling techniques. EXPERIMENTAL PROCEDURE Material. Single-crystal billets of four different crystal orientations. grown by the Arc-Verneuil technique. were ground to a size of 0.25 by 0.375 by 3 in. In terms of their rolling plane and rolling direction, the billets had the following orientations: (1101 [001 ] (110) [110] (001) [110] (001) [100] The actual orientation of all crystals was within 5 deg of the ideal orientations. The typical impurity content of the crystals is given in Table I. Polishing and Etching. Polishing was done elec-trolytically in a 20 g per liter aqueous solution of NaOH at approximately 10 v. It was established by the Laue back-reflection X-ray technique that the surface damage due to grinding and cutting operations with a diamond wheel did not exceed 0.001 in. Therefore after each cutting or grinding operation at least 0.002 in. was removed electrolytically from the surface in order to eliminate surface effects. By lowering the voltage to 3 v, subgrain boundaries and individual dislocations are identified in agreement with Berlec 4 where the etch-pit traces on a cubic plane form a square. The etching time was about 5 sec at room temperature. Rolling. Rolling was carried out on a Loma 2-high mill (Model 600). The peripheral velocity of the 6-in.-diameter rolls was 500 in. per min, with the surface temperature of the rolls about 400° to 450° C The billets were heated before each pass for 30 min in argon to 1000 C. Oxidation of the crystals during rolling in air resulted in a thin layer of greenish-yellow WO 3 This oxide was removed after each pass by immersing the crystals for a few minutes in a boiling NaOH solution. Prior to the initial rolling pass, a surface layer of 0.001 in. was removed by polishing. The crystals were then annealed in vacuum (10-4 torr) at 2400 C for 30 min. All crystals were rolled in the same direction; i.e., the same end was always introduced into the rolls. The rolling program was conducted in

Jan 1, 1965

By R. J. Wasilewski

OBSERVATIONS have been made that the substitution of antimony for bismuth in Bi2Te3 leads to anomalies in some of the electrical and magnetic properties of the Bi2Te3-5S2TeS alloy system at the composition ratios 2 Bi2Te3 : 1 Sb2Tes and 1 Bi2Te3 : 2 Sb2Te3. Airapetiants and Efimova1 have reported the peaking of the nondegenerate hole mobilities, at these compositions for sintered materials and ascribe the peaking to the formation of ordered alloys. From a study of these materials produced by the Bridgeman

Jan 1, 1962

By Roland de Wit

Conclusions reached in a paper by weertmanl are amplified in a mathematical and graphical way. It is shown that in a stressed crystal a straight dis-location may be in a position of unstable equilibrium with respect to helix development, and how a small perturbation may start the dislocation off on its helical path. Helix development occurs by diffision; bulk diffusion is necessary for development from a screw, but core diffision is sufficient for development from an edge dislocation. For a mixed dislocation helix development can take place by core diffusion if the helix also climbs; a diffusion reversal takes place when the slope of the helix equals the slope of the Burgers vector. The work done on a crystal by the external forces is graphically shown to be consistent with the direction of motion of the dislocation in helix development. Finally a detailed mechanism for tangle formation from helices is presented. In the course of helix development a glide situation may be reached where a segment of each helix loop lies in a slip plane in which it can expand by glide. Thus is it visualized how a helix can deteriorate into a tangle. A paper by weertmanl proposes dislocation-tangle formation by a helical dislocation mechanism. The present paper amplifies Weertman&apos;s arguments in a mathematical and graphical way and presents some further ramifications of the proposed model. The importance of dislocation tangles is discussed in Weertman&apos;s paper and the references cited therein. The mechanism of their formation is not yet understood. Weertman proposes that in cold-worked crystals conditions exist suitable for the conversion of straight dislocations into helices and subsequently into tangles. Helix formation occurs by a diffusion process and Weertman proposes that at low temperatures only core diffusion is important. The present paper necessarily repeats some of Weertman&apos;s work. Since the mathematical development and notation used are slightly different from his, this was thought necessary for clarity. GEOMETRY OF THE HELIX weertman2 has shown that the equilibrium form of any dislocation line is a helix if it is assumed that the energy per unit length (line tension) of the dis- location is constant. For the special case that no external forces act on the dislocation, the helix reduces to a straight line. We shall assume in this paper that the dislocation has a helical form even when it is not in equilibrium. The parametric equation of a helix is, see Fig. l: where a is the radius of the cylinder tangent to the helix, and 270 the pitch of the helix. The pitch is related to v, the number of turns per unit length (along the axis) by the relation: When a = 0 Eq. [I] gives a straight line in the z direction. The growth of a straight dislocation into a helix is now described mathematically by letting a vary from zero to its final value. The tangent to the helix is given by where is the path length along the helix. This gives the direction of t and since its magnitude is unity we must have So that dcp/ds = (a2 +p2)-"&apos;. The curvature of the helix is given by where n = -(cos + sin) is a unit vector normal to the helix. Note that the vectors k and n always point toward the axis of the helix, Fig. 1. FORCE ON THE HELIX The external force which makes the straight dis-

Jan 1, 1963

By J. S. Ll. Leach, M. B. Bever

THE system copper-nickel exhibits complete solid and liquid miscibility1 The thermodynamic properties of such a system would not be expected to deviate greatly from ideality. Although the evidence is conflicting, anomalies in the composition dependence of various physical properties of solid copper-nickel alloys suggest that mixing may not be ideal.&apos; From measurements of the Hall coefficient it has been concluded that clustering occurs in these alloys. &apos; Considerations involving the phase diagram of the ternary system copper-nickel-chromium have led Mei-jering3 to predict a positive heat of formation for solid copper-nickel alloys. An electrochemical investigation of the activity of nickel in copper-nickel alloys showed unexpectedly large positive deviations from ideality.4 wagner5 has proposed that if the entropy can be considered ideal, these measurements would yield the following equation for the heat of mixing at 700°C H" = 3380 x,vl (l-xVi) cal per g atom [I1 The heat of formation at 722°C of solid copper-nickel alloys of the equiatomic composition has been measured in a reaction calorimeter as 540 cal per g atom. This note reports calorimetric measurements of the heat effects on dissolution of some copper-nickel ndon: in tin. These measurements were preliminary to a larger investigation, which was later discontinued. From them the heats of formation of the alloys can be calculated, if certain assumptions are

Jan 1, 1960

By S. K. Mitra

A refinement of the Seeger model for intersection process is investigated which is in better agreement with experimental observations than the original. It is shown that, in single crystals, the strain hardening in Stage II is mainly due to the short-mnge interactions when intersection is the rate-controlling process. It is also demonstrated that the creep curves, as predicted by this theory, are in good agreement with the experimental observations. MOTT: Cottrell? and Seeger have developed an approximate theory for plastic deformation of single crystals over the range of variables where the strain rate is controlled by the rate of intersection of dislocations. Although it is now generally agreed that the low temperature deformation of many pure metals is controlled by the intersection mechanism, various dictates of the over-simplified Seeger model are not in good agreement with all the experimental facts. It is the purpose of this paper to reveal that by appropriate extensions of the Seeger model, particularly those suggested by Basinski: a much more reliable theory results. The refined model to be presented here will be shown to account, in a satisfactory way, for the effect of stress, temperature, and strain on the creep rate under constant stress and for the effect of temperature and strain on the flow stress in constant strain-rate tests. EXPERIMENTAL METHOD To Check the theoretical deductions, both creep and tension tests were conducted on single crystals of high-purity Al (99.994 pct Al) so oriented that both the active slip plane and the Burger&apos;s vector of the operative dislocations on that plane made angles of about 45 deg to the tension axis. Single crystals of aluminum (5/8 in. by 1/10 in. by 8 in.) were grown in a graphite mold under an inert atmosphere using the Bridgman method. The chemical composition of the aluminum is given in Table I. A common seed was used for all crystals and their orientation is shown in Fig 3. The extensometry consisted of two differential transformers with matched outputs mounted so as to measure the extension in a 2 in. gage length. The amplified difference in output of the two transformers was recorded by a potentiometer. The amplification was calibrated before each run so that one chart division of the recording potentiometer indicated a 105 shear strain on the specimen. Stresses were measured to the nearest 1 x l04 dynes per sq cm. ACTIVATION VOLUME The concept of Basinski that the activation volume is not constant but is a function of the force that aids thermal fluctuation in effecting the cutting of dislocations will be adopted in this section. The force acting due to an applied shear stress on the dislocation being intersected is where L is the mean spacing between the forest dislocations, is the Burger&apos;s vector and T is the back stress. A detailed discussion about the origin of back stress will be taken up later in this report. As shown by Basinski, the activation energy, U, that must be supplied by a thermal fluctuation in order to effect intersection, is equal to where x is the distance through which the dislocation must be translated for complete intersection, and Fm is the maximum force encountered in intersection. When the applied stress is decreased abrupt ly F also decreases and the activation energy increases correspondingly as documented in Eqs. [ 1 ] and [2]. The Seeger equation for the strain rate when the deformation is controlled by rate of intersection of where the shear strain rate (per sec) N = the number of points per unit vol at which intersection can take place

Jan 1, 1962

By M. Cohen, S. A. Kulin

AT a recent symposium on thermodynamics in physical metallurgy1 two opposing theories of the austenite-martensite transformation were presented. Both theories agreed that this type of reaction involves a nucleation process which requires activation and that the activated nuclei develop into the well-known martensite plates with tremendous speed. However, there were essential differences in the two points of view concerning the nature of the nucleus and the mechanism by which the nucleus propagates. According to Cohen, Machlin, and Paranjpe,&apos; the nucleus is a strain center with sufficient elastic energy to initiate a cooperative displacement among the atoms of the parent phase when a sufficiently low temperature is reached. This displacement propagates as a wave in shear-like fashion to transform the austenite into martensite without benefit of diffusion. On the other hand, Fisher, Hollomon, and Turnbull3 regard the nucleus as a solute-poor region (in the austenite) of a size which becomes supercritical relative to coherent growth into martensite when an appropriately low temperature is reached. This growth process is taken to be an atom-by- atom transfer from the receding austenite lattice to the advancing martensite lattice through the coherent interface that exists between the two phases. The present paper is not conceded with the divergent views as to the nature of the nucleus but describes some critical experiments which differentiate between the two proposed mechanisms of propagation. Fisher&apos; has summarized the latter issue in the following way: According to the cooperative displacement theory, the speed of formation of mar-tensite plates should not be decreased by lowering the temperature, and martensite should form with extreme rapidity at very low temperatures; whereas with the alternate growth process, the speed of the martensite transformation should be retarded at very low temperatures, decreasing to zero at the absolute zero. The atom-by-atom growth mechanism predicts a marked slowing down of the reaction rate with decreasing temperature because the rate of self-diffusion in the austenite is involved in this picture. For example, Fisher, Hollomon and Turn-bull5 estimate that the activation energy for this growth process in steel is (0.34)2(0.36)* times the activation energy for self-diffusion in y-iron. The two most recent determinations of the latter quantity are 67,900" and 74,2007 cal/mol, which may be averaged as 71,000 cal/mol. This, in turn, gives a value of 3000 cal/mol for the activation energy of the atom-by-atom process, and hence the rate of growth should vary as e 8,000/RT where R is the gas constant

Jan 1, 1951

By R. H. Martinson, E. Teghtsoonian

The effects of magnesium-rich surface layers of varying thickness on the mechanical properties of LiF have been studied. The yield stress, critical tensile stress, and work-hardening slope increase linearly with layer thickness, while the strain to fracture decreases yapidly with increasing layev thickness. The results of tension tests, supplemente!d by metallogvaphic evidence, indicate that the yield stress and the critical tensile stress of LiF are not determined by surface-source operation. DESPITE many studies, which have recently been reviewed,&apos; certain fundamental aspects of the plasticity of LiF remain obscure. For instance, one question still awaiting a satisfactory resolution is: does the nucleation and/or multiplication of dislocations in LiF occur preferentially near the crystal surface? It is now well-known that mobile dislocation half-loops are readily introduced into LiF by surface damage and that the mechanical properties of LiF are affected by such surface damage. However, it is not known whether, in the absence of large numbers of artificially introduced surface sources, dislocations arise more easily near the crystal surface than in the crystal interior. It is also not known to what extent existing mobile dislocations multiply preferentially near the crystal surface. The present work is an experimental study of these matters. A short investigation of the effect of magnesium -alloyed surface layers on the deformation of LiF single crystals has been published by Westwood.~ Some relevant conclusions drawn from this research are restated here for purposes of comparison with the present work. 1) Tests on as-cleaved, chemically polished, coated and uncoated specimens show that a coating can restrict the operation of artificially introduced surface sources, thereby raising the yield stress. A coating also decreases the initial rate of work hardening of as-cleaved LiF crystals by reducing the number of active dislocation sources, so that mutual dislocation interference effects are lessened. 2) A catastrophic breakthrough of groups of edge dislocations piled up against the coating can cause stress drops in the stress-strain curve. 3) A surface coating can act as a stable barrier to the egress of dislocations, causing pile-up,

Jan 1, 1965

By M. T. Simnad, C. E. Birchenall, M. H. Davis

The transport mechanisms previously proposed in wustite and hematite have been confirmed by movement of inert markers during the growth of these phases. By similar measurements the mechanism for magnetite has been determined. The rates of growth of multilayer scales on iron, magnetite and hematite on wustite, and hematite on magnetite have been measured. All rates are found to be diffusion controlled under the conditions of the experiments. MANY studies have been made of the rate of oxidation of iron in both the low temperature, film-forming region and the high temperature scaling range. The interpretation of the results has been greatly complicated by the formation of multi-layered scales containing the various phases of iron oxides. In most cases no attempt has been made to determine the composition of the scale and its dependence on time of oxidation in a quantitative manner. However, several recent studies&apos;" have taken this variable into account. It is generally agreed that the growth of thick scales on iron follows a parabolic rate law for the increase of total thickness. In the thin film region agreement has been claimed with parabolic equations of various forms and with logarithmic equations. The discussion here will be concerned only with the formation of scales of considerable thickness, greater than several microns, although some of the conclusions may be applicable to thin films. A brief survey will be given of the solid phases of the iron-oxygen system, the stability of wiistite in bulk and in thin films, the relative densities of iron in the metal and oxides, and the kinetics of forma- tion of oxide scales on iron. New experimental results will be introduced at several points during the discussion, and an attempt will be made to formulate a mechanistic picture consistent with these observations. The experimental techniques are described in an appendix. Iron-Oxygen System Fig. la shows the iron-oxygen phase diagram. Wüstite ("FeO"): The lowest of the oxides has a NaCl type cubic lattice formed by close-packing of the relatively large oxide ions with the smaller iron ions arranged in the interstices. The ionic radius for 0&apos; is about 1.3 A, while Fe++ has a radius of about 0.8A and Fe"&apos; about 0.7A. Its range of existence on the phase diagram is very wide for an ionic material of this type and does not seem to include the stoi-chiometric composition FeO. These deviations appear to be well established as vacancies on iron lattice sites by the comparison of lattice parameters and densities for a series of compositions by Jette and Foote.4 The limits of the field are disputed, but the work which seems most reliable" indicates vacancies in from 5 pct to more than 12 pct of the iron sites. In order for the crystal to be electrically neutral, there must be electron holes which correspond to the formation of trivalent iron ions equal to twice the number of vacancies. Magnetite ("Fe³O4"): Considerable disagreement also exists in the literature about the stable range of the Fe³O4 field. Some diagrams show the Fe³O4 composition to be lower in oxygen than the formula indicates, but Schenck6 gives a diagram from the

Jan 1, 1952

By F. E. Streigert, J. H. Mallery, A. H. Geisler

The existing data on precipitation in Cu-Be alloys have been reconciled with some new data to present a more complete and rational analysis of the atomic rearrangements involved in the process. Two different coherent precipitates were proposed. Each is responsible for a type of diffuse X-ray diffraction effect. THE nature of the atomic rearrangement involved in the precipitation of the compound y-Cu-Be from supersaturated solid solutions of the copper-base alloys has been the subject of two extensive investigations.&apos;-" he precipitate in this alloy system has a rather simple structure; at equilibrium it has a body-centered cubic unit cell with copper atoms on the corner sites and beryllium atoms on the center site. While a simple mechanism would be expected to obtain for the precipitation process, those which have been proposed do not adequately explain all of the reported data. The purpose of the present report is to rationalize some of the previous observations and to contribute new data on the subject obtained by the usual techniques of structure analyses. The Cu-Be system of alloys represents one of the most extensively investigated precipitation systems, so a detailed review of the pertinent literature on structure is in order. Striations: Since one of the important features of the mechanism—the habit plane—is determined by microscopic examination, microstructural features that have been observed should be considered at this time in order to assess their role in the precipitation process in Cu-Be alloys. One of the most prominent features appears as regularly oriented markings or stripings (ripples or striations) across the crystals on a suitably polished and etched sample of the aged alloy. These have been observed and interpreted by many workers. Masing and Dah14 observed striations in both the a and /3 phases of a 2.5 pct Be alloy, and attributed them to the beginning of the precipitation of very fine y crystals along favored planes of the a matrix and to the local decomposition of the £ crystals into a plus y. These markings were apparent in both the a and /3 phases of the micrographs given by Smith5 for a 2.75 pct Be alloy, while Moore" detected them in the a matrix phase using polarized light. Desch7 attributed the markings to fine precipitate particles lined up on a family of matrix planes like Masing and Dahl had done, and he identified the planes as those of the (111) family, the slip planes of the matrix. The striations were presumably the structure which Northcott- eferred to as "martensitic." He found that this structure was present in samples that had been aged under widely different conditions with hardness values ranging from 160 to 400 VHN. Later Guinier and Jacquet&apos; also found striations in both the a matrix and secondary /3 phase. Their analyses showed that the striations were along (110) planes of the matrix phase, apparently in contradiction of the results of Desch. They found that the striations were developed during aging on the surface of a specimen that had been polished prior to aging.&apos; On this basis they concluded that the striations represented mechanical deformation by slip along (110) planes of the matrix resulting from precipitation stresses.&apos;" Similar but fainter striations were observed in the same manner on an A1-Cu alloy sample, in which the change in volume was much less than for Cu-Be alloys and

Jan 1, 1953

By W. L. Korbee, P. Hazebroek, M. Prats, E. E. Allen, C. A. 225-000-000-017 Verbraak, H. C. van Elst

In a recent paper,&apos; one of us has presented some experimental evidence on the relationship between twinning and brittle fracture in steel. From metallographic examinations of brittle fracture it could be derived that mechanical twins and microcracks are formed already in front of a running brittle fracture. A tentative explanation based on the evaluation of the statistical distribution of mechanical twins vs various angles to the fracture was given in the above mentioned paper. It was suggested that these twins are caused by stress waves emitted by a running brittle fracture. With the aid of high-speed photography and the use of photo-stress sheet we are now able to study in more detail the propagation of a brittle fracture and the emittance of stress waves connected with fracture. A typical example is given in Fig. 1. In this figure a running brittle fracture in an ordinary Thomas steel is shown. The experiment was performed on a Robertson apparatus and the stress waves caused by the fracture were made visible with photo-stress

Jan 1, 1962