By A. A. Bauer, H. A. Saller, F. A. Rough, J. R. Doig

among uranium alloy systems are the U-Zr, U-Ti,and U-Mo binary systems, in that an intermediate phase, of limited solubility range, exists in each system. These intermediate phase alloys offer a promising field of investigation, both as binary alloys and as ternary alloy combinations. While a limited amount of work has been done on the binary alloys, none has been done on ternary combinations of these alloys. As a possible prelude to more intensive investigation of these systems, a study of the phase relationships between the 6 phases of the U-Zr and U-Ti systems was undertaken. The solid-state portions of the binary constitutional diagrams for the U-Ti,1 Zr-Ti,2 and U-Zr3 systems are shown in Fig. 1. The solid to liquid transformations are not shown, as these transformations were not studied in the ternary system. The phase designations employed are based upon those shown in the uranium constitutional diagrams. The crystal structures of the various phases are given in Table I. Experimental Materials and Methods The ternary section presented is based upon the results of thermal, metallographic, and X-ray analyses of a series of alloys ranging in composition between the phases of the U-Zr and U-Ti systems (U-74 atomic pct Zr to U-35 atomic pct Ti). After preparation of the alloys, thermal data were obtained. On the basis of these data, specimens were heat treated and examined metallographically. Specimens were then selected from those heat treated for X-ray determination of the phases present in what were considered critical phase regions. Alloy and Specimen Preparation—Alloys for this investigation were prepared from selected as-reduced uranium and crystal-bar zirconium and titanium. For nominal compositions, see Table 11. Charges were arc melted from five to seven times under a helium atmosphere, finally being cast into wire-bar form for fabrication. A zirconium getter button was used to clean the furnace atmosphere prior to melting. The alloys were homogenized 20 hr at 900 °C and furnace cooled. A portion of each bar was then removed for thermal analysis; the remainder was saved for fabrication. Alloys 8 through 14 were placed in steel tubes along with zirconium getter chips and, after flushing with argon, the tubes were welded shut and rolled at 1500 °F to a 50 pct reduction in diam. The remaining alloys were annealed 24 hr at ll00°F to insure transformation of the ? phase to the 8-U2Ti phase and were then hot rolled from a salt bath. Attempts to roll alloys 6 and 7 at 1100 °F were unsuccessful. Following this, attempts were made to roll pieces of alloys 1 through 5, which had cracked rather severely during casting, at 1200 °F, but these efforts were also unsuccessful. These alloys were, therefore, further treated in their cast and homogenized condition. All alloys were pickled to remove oxide formed during rolling. Thermal data were obtained on these alloys by conventional differential thermal analysis at a heating rate of 30C per min, and by a high-speed heating method at rates of approximately 10°C per sec. For the latter method of analysis, a 36-gage Chromel-Alumel thermocouple is spot welded between two slivers of alloy, the sandwich being en-

Jan 1, 1958

By W. Chubb

By measuring the hardness of metals at temperatures just above and just below their allotropic change point, it has been established that crystal structure has a real effect upon the strength of metals. The DPH of cobalt, iron, titanium, uranium, and zirconium have been measured at temperatures up to 1000°C. It was found that the body-centered-cubic crystal structure is always the softer structure when it is involved in an allotropic transformation. The close-packed and more complex structures are inherently harder, and may be expected, therefore, to be better base materials for high strength alloys. IT has been observed that for metals with nearly the same melting point (i.e., tin and lead, magnesium and aluminum) the metal with the more complex crystal structure has a higher tensile strength and hardness. It might be asked whether this effect is really caused by the difference in crystal structure; and, if so, just what is the contribution of crystal structure to the strength of these metals. A qualitative answer to these questions can be obtained by measuring the change in hardness produced by the change in structure in metals exhibiting allotropic forms. The evidence for changes in mechanical properties during allotropic transformations is rather meager. In 1909, Rosenhain and Humfrey' observed that "ß" iron showed much less deformation at the transformation temperature than a iron. By means of a torsion test, Lee found that iron bars were "critically plastic" at the a-7 transformation temperature. Sauerwald and Knehans have shown that the dynamic hardness of iron increases between 900" and 1000°C. In 1930, Albert Sauveur' presented data on the hardness, tensile strength, and torsional strength of pui-e iron up to 1000°C. He concluded, "At 900°C, the a iron transforms into y iron, and this is accompanied by increased strength and stiffness and decreased ductility." The same year, Schischokin" obtained data on the hardness of thallium at temperatures above and below its transformation temperature. His data are replotted on semilogarithmic coordinates as Fig. 1. The fact that his data fall on straight lines in this type of plot is believed to attest to the purity of his metal and the accuracy of his results. In 1941, Nadai and Manjoine" obtained tensile data on pure iron with an indicated increase in strength at about 900°C. These experiments make it quite evident that changes in mechanical properties occur when a metal transforms from one crystal structure to another; but, except for Schischokin's data on thallium, none of the measurements seem accurate enough to determine the relative magnitude of the mechanical property change. Materials The metals that have been examined for changes in hardness during transformation include l—as- deposited commercial electrolytic cobalt about 99.7 pct pure, 2—Armco ingot iron, 3—are-melted iodide titanium of a purity in excess of 99.8 pct, 4—uranium of a purity in excess of 99.5 pct, 5—are-melted iodide zirconium of a purity in excess of 99.8 pct, 6—annealed, 0.08 pct C, rimmed steel, and 7—commercially pure RC55 titanium. While the purity of the first five of these materials leaves something to be desired, it will be noted that the observed hardness discontinuities occurred at the accepted transformation temperatures. (These temperatures are indicated by vertical arrows in Figs. 1 and 3 through 7.) The last two materials are commercial alloys introduced to show the effect of minor alloying elements upon the hot hardness curve. Apparatus Hardnesses at elevated temperatures were determined by means of a vacuum hot hardness machine. A diagram showing the basic features of this machine appears as Fig. 2. This machine is essentially a deadweight hardness .machine in a furnace within a vacuum chamber. The sapphire-tipped indentor

Jan 1, 1956

By R. W. Kraft

A comprehensive analysis of the crystallographic and metallographic structure of several Al-CuAl, lamellar eutectic grains solidified under equilibrium conditions has been performed. A consistent pattern was discovered which was interpreted in terms of a detailed atomistic model of an interface describable as: Interface II {111} AL 11 {211} <101>Al <120> ? Several arguments are presented to substantiate the theory. It is compared in detail with another interface model characteristic of the Wid-manstatten precipitate of CuAl2 in A1 at low Cu levels. In addition, a concept is proposed to help explain the structure of the compound CuAl2. It has been shown that the eutectic alloy between A1 and CuA1, can be forced to solidify as substantially parallel lamellae throughout a relatively large volume&apos; by appropriately controlling the solidification parameters of growth rate, thermal gradients, and impurity level and by causing solidification to proceed in a unidirectional fashion from one end of an ingot to the other. A typical ingot solidified in this manner shows three distinct zones along the length of the ingot, Fig. 1. At the head end is a region consisting of many different grains, some of which are elongated slightly in the direction of solidification. After a few centimeters of growth, this polygrained region gradually merges into the second zone which consists of a very few elongated coarse grains. The third zone at the tail end is a region of eutectic colonies caused by segregation of impurities. Microscopic examination of transverse and longitudinal sections of the ingots reveals that during the initial stages of growth (zone I) the lamellar structure is frequently highly distorted and twisted but that it straightens out in zone 11. This characteristic pattern suggests that nucleation of a eutectic grain begins randomly at the head end of the ingot, and that some particular orientation relationship between the phases is more favorable from an energy consideration than others for one reason or another, so that some grains grow and others which are less favorably oriented do not. The favorably oriented or "low energy" grains continue to grow until excess solute rejected at the advancing liquid-solid interface destroys the parallel lamellar structure by forming a cellular rather than a substantially planar interface. When this occurs, the parallel lamellae fan out and eutectic colonies are formed because the lamellae grow perpendicular to the local interface. Questions naturally arise as to the crystallographic nature of the "low energy" grains. What do the grains which persist into zone II have in common? Can this explain the stability of such grains during growth? To answer the first question it is necessary to determine the crystallographic orientation of the lamellae of each phase relative to one another. This has been done for Al-CuAl2 eutectic alloys by two different techniques on specimens prepared in different ways.2&apos;3 The results were different from each other and from a third orientation relationship between A1 and CuA1, reported for overaged A1-Cu alloys.4 The three orientation relationships are summarized below to illustrate their similarities and their differences. (001) ? 11 (001) A1; [l00] ? 11 [l00] Al Eutectic, Ref. 2 (001) 8 1) (001) A1; [1001 ?11 [1101 A1 Eutectic, Ref. 3 (001) ? 11 (001) A1; [l00] ? 11 [310] Al; Widmanstfitten, Ref. 4 It is not surprising that different orientation relationships were found by Ellwood and Bagley,&apos; and Takahashi3 since the solidification conditions were quite different. Nor is it surprising that Mehl, Barrett, and Rhines 4 found still another value since they were studying another type of alloy. Nevertheless, it would be expected that some logical and systematic pattern could be found if all the alloys were at equilibrium since the same two phases are

Jan 1, 1962

By S. Floreen

Measurements have been mode of the effects of tempering and austenitizing heat treatments, the work-hardening characteristics, and the effects of test temperature and strain rate on the properties of a low-carbon Fe-18 pet Ni martensitic alloy. In many respects the alloy behaved quite similarly to cold-worked iron. One notable quality was the excellent ductility at temperatures as low as 20°K. Many of the qualities of the maraging steels could he related to the properties of the Fe-Ni matrix. THE 18 pet Ni maraging steels have demonstrated that unusual combinations of strength and toughness may be obtained by age hardening a low-carbon Fe-Ni martensite matrix.&apos; These properties must, to some extent, reflect the properties of this Fe-Ni matrix, and therefore an understanding of the properties of this matrix is a prerequisite to a complete understanding of the steels. There have been several recent studies of Fe-Ni-C martensites, but not much attention has been paid to alloys with very low carbon contents. At low carbon levels the crystal structure of these alloys is essentially bee.2 Electron transmission microscopic examination of a 20 pet Ni binary alloy showed martensite platelets separated by low angle boundaries.3 Plastic deformation of the low-carbon alloys has been shown to proceed by wavy glide.4 The hardness of these martensites is typically RC 28, and their yield strengths are 70 to 80 kg per sq mm.2, 5 Their ductility is excellent. Room-temperature tensile elongations of 18 pet and reductions of area of 70 pet have been observed in an Fe-18 pet Ni binary alloy.5 These observations have provided a qualitative understanding of the flow characteristics of these alloys. To date, however, no thorough study of their properties has been made. In particular, it is not known to what extent the deformation characteristics of low-carbon martensites are similar or dissimilar to those of pure iron or other bee metals. The present work was undertaken to provide more detailed information on the flow characteristics of a low-carbon Fe-18 pet Ni martensite. PROCEDURES, RESULTS, AND DISCUSSION Materials. A 40-lb heat of the Fe-18 pet Ni alloy used in this study was made by vacuum-induction melting. The charge materials were electrolytic iron and electrolytic nickel. A carbon boil was used to achieve deoxidation. After the boil the heat was refined by additions of 0.1 wt pet Ti and Al. These additions are commonly used in the maraging steels to keep the carbon and nitrogen contents in solid solution at a minimum. After casting, the heat was

Jan 1, 1964

By Frances H. Clark

IN wartime, the fabrication and use of metals assumes increased importance, for a modern war of sizable proportions cannot be undertaken with- out a vast supply of this material. Light alloys of aluminum and magnesium, which were comparatively unknown in the last war, will play an important role in this one. Due to research on a vast scale in the interim of years, industry is today well equipped to fabricate metals on an enormous scale. Research for the past year has been most productive and a comprehensive survey in the space of this article would be impossible. It is hoped that the stressing of a few items here and there out of a great quantity of able work will indicate in a small way the advances made within recent times. Specific references to the literature will be omitted at the Editor&apos;s re- quest but some authors of papers that I have found of special interest are mentioned.

Jan 1, 1940

By E. P. Abrahamson

The effect of transition element binary solid solution additions upon the re crystallization temperature of nickel has been investigated. All additions raised the re crystallization temperature. Both the rate of change of re crystallization temperature with at. pet solute and the limit of initial linearity are found to correlate with the free atom ground state outer electron configuration of the solute element. A comparison of all of the correlations for the transition elements studied has yielded a set of empirical relations, which allows the prediction of the effect of dilute binary transition elements on the recrystallization temperature of other transition elements. The work of Abrahamson, et al.1-7 on dilute binary solution alloys indicated a correlation between the free atom ground state electron configuration of the solute and both the brittle-ductile transition and re-crystallization temperature. Further, it has been shown3,4 that the limit of initial linearity may also be correlated with the solute electron configuration. Since previous studies have dealt with bee and hexagonal base elements, this study is made to note what effect, if any, the fee base structure might have. Nickel also serves to give a solvent configuration which will allow the comparison of all of the transition element solvents. Olsen8 has studied the effect of some trace elements upon the recrystallization of nickel. He included only Ti, Zr, W, Mn, and Co of the transition elements. The differences in change of recrystallization temperature were attributed to the solute atom size and to the solubility of the solute in nickel. PROCEDURE All alloys were made using 99.9 + pet Ni with 0.003 C, 0.015 Fe, 0.007 0, and 0.0007 H. The solute elements were 99.9 + pet pure. According to the published binary phase diagrams9 and metallo-graphic examinations at X750, all solute elements were in solid solution. The alloys were arc melted and remelted four times in the form of cubic 200-g buttons under an argon atmosphere. They were then hot forged at 800oC to 0.750 in. diam, machined to 0.60 in., vacuum annealed for 1 hr at 700°c, swaged to 0.40 in. and annealed at 700oC for 1 hr in vacuum. The grain size was checked and found to be 77 * 20 grains per sq mm. The specimens were then swaged to 0.187 in., yielding 76 ± 1 pet cold work. All alloys were then chemically analyzed for the solute addition. The interstitial contents remained at the values of the starting material when checked on random alloy specimens. The swaged rod was cut into 8.25 in. lengths and heat treated in a gradient furnace for 1 hr. The gradient was maintained at 250" to 850°C over an eight inch length, recorded by twelve thermocouples. Control was ± 3oC, accomplished at the hot end. The recrystallization was determined metallo-graphically over the entire specimen. The criterion chosen was that point on the specimen showing the first recrystallized grain at a constant magnification, X200. Specimens were repeated, and the agreement was found to be generally ± 3oC.

Jan 1, 1962

By R. C. Gifkins, A. Gittins

A. Gittins and R. C. Gifkins (University of Mel-houvne)— Evidence from somewhat similar experiments to those described in this paper has led us to the conclusion that possibility 2) of the four listed on p. 319 is a description of what happens in grain boundary sliding. That is, sliding is limited by accommodation deformation, it being necessary to the Continuance of sliding that this accommodation should take place. An example of such accommodation, though probably not the most important, is fold formation at triple points. The evidence and arguments for this point of view are set out in Refs. 14 to 16. In particular, an experiment with a lead bicrys-tall5 seems to support point 2) rather than 3). In creep of this specimen it was found that at least 90 pct of the extension of a zone 0.3 mm wide at the boundary was supplied by sliding at the boundary. The sliding was localized in a region at the boundary very much smaller than 0.3 mm, in fact, in a region too narrow to resolve optically. In poly crystalline Specimens&apos; there appears to be a surface effect, as found by Rachinger," but it appears that this may not manifest itself at low strains. "Low strains" means <10 pct for a Pb-TI alloy, <2.5 pct for magnesium or "Magnox" A12 alloy, or <40 pct for a 0 brass. Up to this extension the sliding, measured by the mean vertical step at boundaries, is proportional to extension. We are able to say this with some confidence, since the error bars on our points are statistically derived. Our results would lead us to think that the error bars on other work, including that of Mullendore and Grant, are much too large at low strains to show this

Jan 1, 1963

E. R. JETTE*—The way this ternary was developed there are two directly determined points on each of the iso-thermals except the 700° isothermal, where I believe there is only one. How were the end points determined, and what was the basis for it? Whose work formed the basis for the silver copper line ? M. B. BEVER †—At most temperatures the authors determined three points of the isothermal line. For example it can be seen from Fig 3 and 4 how three points for the 600°C contour line were obtained. The authors took two additional points for each temperature from the copper-silver binary diagram contained in Hansen&apos;s volume on constitution diagrams. It is correct that the 700°C contour line is based only on one point in the ternary field which was found by a slight extrapolation of Fig 4. R. I. JAFFEE*—Are the tie lines representing phases in equilibrium parallel to the silver-copper boundary ? M. B. BEVER—Are you asking that as a matter of principle ? R. I. JAFFEE—I assumed that would follow from principle. I wonder if that is in accordance with the authors&apos; ideas too. M. B. BEVER—I do not believe the authors obtained any information on the tie lines in the two-phase field. Of course, in the limiting case of very low gold contents the tie-lines approach to the silver-copper boundary, but generally in the two-phase field I do not think that the tie-lines have to be parallel to the boundary. E. R. JETTE—1 am quite sure they do not have to be parallel. You cannot tell from this work in which direction they go. E. A. GULBRANSEN*—Were any pycnometric measurements made to check the lattice parameters of the alloys ? M. B. BEVER—I did not hear any-

Jan 1, 1950

By R. I. Jaffee, R. W. Wood, H. R. Ogden, D. N. Williams

D. W. Morgan, D. H. Polonis,and R Taggart (Uuivevsity of Washington)—Dispersion hardening in titanium-copper alloys is of particular interest to us in view of our current research activities in phase transformations in this system. We should like to raise questions concerning several points in the paper. The flow sheet for fabrication and heat treatment (Authors&apos; Fig. 2) indicates that 0.045 in sheet is treated in air for a period of 30 min at 1625&apos; F. Were any surface coatings used to reduce oxygen contamination at this stage? One might ask the same question about the 8-hr annealing at 1400F. Contamination during fabrication and heat treatment of such thin sections could be considerable without some protection. Although the authors state that no analyses were made, they note that contamination masks the distinction between base strengths of the different alloys. In this connection, what fabrication and heat-treatment procedures were used in obtaining the comparison specimens of unalloyed titanium? It would seem that oxygen contamination must cast doubt on the reliability of the proposed strength-mean free path relationship deduced from the data (Authors&apos; Fig. 5). It is usual to evaluate dispersion hardening on the basis of yield strength rather than ultimate tensile strength, and accordingly we have replotted the authors&apos; Fig. 1 to include yield strength. The yield strength data do not justify a discontinuity of 3 p at either 70" or 1000 OF. Can the authors substantiate their conclusion 1) with additional evidence? Otherwise it seems that they have succeeded only in pointing out the possibility of a linear relationship between yield strength (or Uts) and the logarithm of the nleall free path, comparable with that demonstrated for iron-carbon alloys (Authors&apos; Ref. 2). Work in our own laboratories has shown that the hardness of the phase Ti,Cu is 235 Vpn, and that of a 1.5 pct (at.) (2 pct wt) supersaturated solid solution of copper in titanium is 190 Vpn. This small difference in hardness would suggest that Ti2Cu should not be a very effective dispersion-hardening phase. D. N. Williams, R. W. Wood, H. R Ogden, RI. L Jaffee (authors&apos; reply)— This discussion brings out some interesting points with respect to the interpretation of our results, and also raises some questions regarding the experimental technique. We shall consider the latter questions first. Contamination during heat treatment was prevented by performing all heat treatments in argon-filled Vycor capsules. Fabrication was done in air, with the usually observed scaling. Scale was removed

Jan 1, 1962

By Robin O. Williams

Robin 0. Williams (Oak Ridge National Laboratory)— The authors have questioned the degree to which the coherency strains between the iron-rich and chromium-rich phases are isotropic as proposed in Ref. 5 on the basis of the difference between the elastic properties of the two phases. The relative magnitude of the stresses is determined by the moduli as shown by Eqs. [2], [3], and [4] of Ref. 34. However, the moduli of the two phases have no direct bearing on the uniformity of either the stress or strain within either phase. The idea that the strains are isotropic within each phase (but normally of different magnitude and always of different sign) is based entirely upon the experimental observation that X-ray line broadening has not been detected even when the particles become rather large. It has not proven possible to grow the particles sufficiently large that they lose coherency. Based upon this lack of line broadening one can estimate an upper limit for the nonuniformity of the strains within each phase as follows. It is considered possible to detect line broadening if it is as great as 10 pct of the separation of the K, doublet for the (211) line using chromium radiation. The doublet separation would correspond to a total strain of 0.0017 such that the total variation of lattice parameter relative to the average lattice is now k0.05x0.0017 or something less than ± * For the present case the strain in each phase is roughly 0.002 such that the variation of strain within a phase will not exceed 5 pct. It is stated that the expression derived for strengthening for the hydrostatic straining as observed in this system would substantially overestimate the magnitude due to dislocation flexure. This is contrary to the conclusion reached in the original paper34 for the present range of particle sizes. What is the lowest temperature at which a has been observed to form in this alloy? M. J. Marcinkowski, R. M. Fisher, and A. Szirmae (nutlzors&apos; reply)— -Williams&apos; arguments based on X-ray findings for a chromium-rich precipitate and an iron-rich matrix strained to a common lattice parameter are certainly convincing. This being the case, there are no shear components of strain associated with the precipitate-matrix aggregate to interact with the shear components of the dislocation stress fields, contrary to the opinion expressed by the present authors. On the other hand, the present authors, in spite of this error, did not expect the shear interactions to be significant. The chief objection to Williams&apos; model in the present case is that the various segments of the dislocation line are assumed to pass from one potential valley to the next independently of neighboring segments. This is only true for a highly flexible dislocation line, i.e., one whose radius of curvature is something less than the center to center distance between precipitate particles which amounts to about 90A in the present alloy. In order to maintain this curvature, an externally applied shear stress of at least 230,000 lb per sq in. would be required or about four times the observed stress. It is therefore concluded that the dislocation lines move rather rigidly through the lattice. This being the case, the forces on the dislocation resulting from the hydrostatic interaction between the stress fields of the edge-dislocation components and the precipitate particles should average out to zero; that is particles above the below the slip plane produce forces on the dislocation of opposite sign and therefore will cancel when averaged over the entire length of the dislocation. On the other hand, since the dislocation is not perfectly rigid, Williams&apos; model may lead to some strengthening, but far less than that predicted. A second and equally serious objective to using Williams&apos; strengthening model for the present alloys is that profuse wavy slip due to the motion of screw dislocations played a predominant role not only in the unaged alloys but in the fully aged ones as well. Since the screw dislocation has associated with it only shear components of stress the hydrostatic strengthening model no longer applies. In view of these arguments the present authors must reject Williams&apos; model of strengthening as being pertinent to the present alloy system. The present authors have made no detailed study of the lowest temperature at which a forms in the quenched ferritic alloys. None was ever observed n the alloys aged at 500°C so that forma-tion must occur at temperatures higher than this and was therefore not a factor in the present study.

Jan 1, 1965

By H. J. Beattie

R. L. Stegman and M. R. Achter (U.S. Naval Research Laboratory)—In a study of the surface structures developed in the fatigue of nickel at low strains as a function of temperature, we have obtained similar results.3 As our apparatus permits fatigue tests to be conducted in vacuo, there was no masking of the surface at high temperatures by oxidation so that the structures there could be observed directly. The relatively few broad slip bands observed at room temperature gave way at 300°C to a large number of uniformly distributed and narrower slip bands. At 550°C deformation began to concentrate around the grain boundaries and progressively increased up to 800°C. In addition fatigue strength was observed initially to increase with increasing temperature up to about 600°C due to the effectively increased ductility caused by the dispersal of fatigue damage. The fatigue strength then decreased at higher temperatures as grain boundary cracking dominates. Maria Ronay, W. H. Reimann, and W. A. Wood (authors&apos; reply)— The authors are pleased to note that R. L. Stegman and M. R. Achter reach similar conclusions from their study of surface slip on nickel. However, they would emphasize that their own conclusions are based on what is shown by study of specimens that have been sectioned and that this study also shows that surface slip is not necessarily representative of what happens below the surface.

Jan 1, 1965

By R. L. Stegman, M. R. Achter

R. L. Stegman and M. R. Achter (U.S. Naval Research Laboratory)—In a study of the surface structures developed in the fatigue of nickel at low strains as a function of temperature, we have obtained similar results.3 As our apparatus permits fatigue tests to be conducted in vacuo, there was no masking of the surface at high temperatures by oxidation so that the structures there could be observed directly. The relatively few broad slip bands observed at room temperature gave way at 300°C to a large number of uniformly distributed and narrower slip bands. At 550°C deformation began to concentrate around the grain boundaries and progressively increased up to 800°C. In addition fatigue strength was observed initially to increase with increasing temperature up to about 600°C due to the effectively increased ductility caused by the dispersal of fatigue damage. The fatigue strength then decreased at higher temperatures as grain boundary cracking dominates. Maria Ronay, W. H. Reimann, and W. A. Wood (authors&apos; reply)— The authors are pleased to note that R. L. Stegman and M. R. Achter reach similar conclusions from their study of surface slip on nickel. However, they would emphasize that their own conclusions are based on what is shown by study of specimens that have been sectioned and that this study also shows that surface slip is not necessarily representative of what happens below the surface.

Jan 1, 1965

By A. N. Holden

A DISLOCATION mechanism has been described by Cottrell&apos; by which metals can yield locally, I. form Liiders bands, giving rise to a characteristic stress-strain curve with a sharp yield point and appreciable strain at constant or decreasing stress. It is undoubtedly the best mechanism that has been suggested to date." In its present development, however, the dislocation mechanism provides a more satisfying explanation for the sharp yield point than for the extensive localized flow occurring at the lower yield stress. The primary objective in this paper is to extend the dislocation mechanism to account for localized cataclysmic flow by a dislocation collision process and to give experimental evidence to support such a process. Only the yielding of iron containing carbon -will be discussed, although other metal-solute systems are known to behave similarly. Cottrell Mechanism In brief, Cottrell explains the yield point in the following way: The dislocations in iron which must propagate to produce slip usually lie at the center of local concentrations of carbon atoms, since segregation about these dislocatlons relieves some of the local stress resulting from them. A dislocation surrounded by a "cloud" of carbon atoms is thus anchored, and a higher stress is required to set it in motion than to move a free dislocation. Considering all available dislocatlons to be anchored in this fashion, the iron exhibits a yield point when the first dialocations break free and move through the lattice causing slip. This first breaking away of a dislocation enables other dislocations to break loose by "interaction" and the process becomes a cataclysm producing local deformation or Luders bands. The yield point in the stress-strain diagram for iron is absent in freshly deformed material, but returns gradually with time; the phenomenon is one aspect of what is called strain aging. The rate at which the yield point returns following straining depends on the temperature of aging. According to Cottrell the rate of return of the yield point in strained iron is limited by the rate of diffusion of carbon at the aging temperature, the mechanism is onr: of reforming the solute atmospheres around carbon-free dislocations that had stopped moving coincident with the removal of stress. If the specimen is retested immediately after straining and unloading, carbon will not have had time to diffuse to, and re-anchor, dislocations and the yield point will not occur. The carbon diffusion limitation for the rate of strain aging apparently applies if the criterion for strain aging is either the change in hardness" or the change in electrical resistance" of the strained speci- men with aging time. The possibility exists, however, that the yield point actually returns to strained iron at some rate other than that deduced from hardness or electrical resistance data. Therefore, as a preliminary experiment, the rate of yield point return in a rimmed sheet steel strained 6 pct in tension was measured at 27°, 77°, and 100°C. A plot of yield-point elongation for each of these temperatures against aging time appears in Fig. 1. The aging process is described by curves which rise to a plateau value of elongation that seems independent of temperature, but at a rate that depends on temperature. Very long times lead to a further rise in the yield-point elongation above the plateau value. However, if the later increase in yield-point elongation is ignored and the log of the time to reach half the plateau value of elongation is plotted against 1/T, a straight line results for which an activation energy of about 25 kcal pel- mol may be assigned. Within the accuracy of this sort of experiment this is approximately the activation energy for the diffusion of carbon in iron (20 kcal per mol), and the carbon diffusion limitation suggested for the yield-point return on strain aging is valid. The Cottrell mechanism thus explains in a qualitative manner the occurrence of a yield point in iron and its return with strain aging. It fails, however, to explain some of the other experimental observations that have been made of the yielding behavior of iron. For example, it is known that the yield point in iron becomes less pronounced with increasing grain size. Annealed single crystals of iron have very small yield-point elongations .if indeed they have any,&apos; compared to a polycrystalline steel. If the only requirement for a yield point is that the dislocations in the lattice of the annealed. material be anchored by carbon atoms, the difference in the behavior of single crystals and polycrystals is not explained. That a dislocation mechanism may be entirely consistent with little or no yield point in an annealed single crystal will become apparent later when dislocation interaction is discussed. Strain aging produces a definite yield point even in single crystals. This accentuation of the yield-point phenomenon in single crystals after strain

Jan 1, 1953

By V. R. Thompson, R. C. Westgren

In a recent paper,1 the solid-solution strengthening of tungsten and tantalum in a portion of the W-T;-MO-C~ alloy system was described. Additions of tantalum and columbium to tungsten led to significant strengthening, and the introduction of dispersions into these alloys was suggested as a means of further increasing strength. Dispersion strengthening of columbium and molybdenum alloys has been studied extensively.2-4 The approach used to dispersion-strengthen molybdenum alloys appeared equally suitable for tungsten alloys, and, therefore, a brief study was undertaken to determine to what extent the introduction of carbide dispersions would strengthen a solid-solution tungsten-base alloy. A base composition of tungsten and 10 to 12 pet Cb was selected; previous work1 had shown that the tensile strength of this solid-solution alloy was 50,000 psi at 3000°F. For the study of the effects of small additions of

Jan 1, 1964

By R. L. Fleischer, W. F. Hosford

Tensile data for coarse grained aluminum Polycrystals suggest that the "grain size" effect is not due to dislocations piled up at grain boundaries but rather is primarily a relative size effect due to surface crystals being weaker and less confined. STUDIES directed at interpreting hardening of poly-crystalline metals normally identify their strain hardening properties with those in some particular type of single crystal.1"4 The recent recognition in face centered-cubic metals of a nearly linear stage with rapid hardening occuring at comparable rates for both polycrystals and single crystals, suggested that the same process or processes determine both cases and hence that there exists some justification for the use of single crystals to understand polycrystals. Further evidence for the above view may be found by an approach initiated by Chalmers:5 By using bicrystals of controlled orientation it is possible to begin to assemble a polycrystal and also to study grain boundary effects in detail. In this way it has been found that a single grain boundary affects easy glide but not the subsequent stage II hardening.6 This result suggests that a sensitive way to observe grain boundary effects in polycrystals would be to vary grain size and measure easy glide. As will be seen, easy glide is only possible for coarse-grained samples, and hence the results will serve to fill in the gap in measurements between single crystals and bicrystals on one hand and fine-grained polycrystals on the other. One problem inherent in comparing single crystals with polycrystals is the uncertainty as to what slip systems are acting in a polycrystal. To compare the two types of samples, rates of shear hardeninn---L. on the acting -planes are needed. and these may be computed only if it is known what particular systems are active. The acting systems were examined for a coarse-grained polycrystal and it will be shown that the systems supplying the preponderance of slip can be determined with little ambiguity. EXPERIMENTAL PROCEDURE Twelve samples of aluminum were prepared by chill casting into a heated graphite mold, followed by annealing at 635° ± 5°C for 24 hr with an 8-hr fur- nace cool, and finally either etching7 or electropol-ishing.&apos; The samples, with a 7 to 10 cm length between grips and 4.4 by 6.6 mm in cross section, were deformed at a strain rate of about 3 10 -3 . per min in a tensile device which has been described elsewhere.5 The composition was reported by Alcoa as 99.992 pct Al, 0.004 pct Zn, 0.002 pct Cu, 0.001 pct Fe, and 0.001 pct Si; nine samples were deformed while immersed in liquid helium and three in air at room temperature. The stress-strain curve for one of the samples (P-1) deformed at 4.2 "K has been reported previ~usl~.~ This sample was selected for determination of active slip systems. Eighteen of the crystals were examined by optical microscopy to determine the angles of slip line traces and by X-ray back reflection to determine orientation. By this means the slip planes were determined and the resolved shear stress factors for possible slip systems could be computed. Finally each sample was sectioned so that after etching, the number of crystals could be counted for each of ten newly exposed surfaces. The average of these ten values will be termed n, the number of crystals per cross section. Values of 11, varied from 1.9 (nearly bamboo structure) to 12.7. Sketches of typical cross sections appear in Fig. 1. RESULTS AND DISCUSSION: SLIP SYSTEMS 1) Determination of Acting Slip Planes—The stress axis orientation and operative slip planes in eighteen crystals of sample P-1, as determined by slip line traces and crystal orientation, are summarized in Fig. 2. For one of the crystals two planes had a common trace. so that the traces alone did not distinguish which plane or planes were slipping. However it was found that the stress resolving factor for the primary system was 0.386, .while that for the most stressed system in the other plane (indicated bv the dotted arrow) is 0.138. It will be assumed tgerefore that only the primary plane acted. Since the orientations were determined after extending the samples 4 pct, the stress axes may be rotated from their original value by as much as 2 deg in some cases. It is interesting to note that in five crystals only one slip plane acted, in eight two acted, and in five three planes were observed—an average of two slip

Jan 1, 1962

By H. Conrad

The strain hardening associated with the creep of magnesium single crystals at room temperatu.Je was investigated by shear tests in which the direction of stressing was reversed a number of times after creep in a <100> direction. The strain hardening was strongly anisotropic; the largest amount occurring in the direction of flow and the least 180 deg to this. The time law for creep changed from a parabolic type to logarithmic for the first and subsequent reversals of stress. For a given stress the creep strain decreased significantly for the first and second reversals and then only slightly for subsequent reversals. The logarithmic creep constant a changed in a similar manner. A linear relationship was observed between the creep strain for a given reversal and the stress. The slope for the third reversal yielded a strain hardening coefficient 12 to 16 times greater than that observed for unidirectional flow. Al-though no recovery was observed upon resting at room temperature, the hardening resulting from stress reversals could be completely removed by heating to 450" C. PREVIOUS work1.&apos; indicated that the creep rate of magnesium single crystals tested in the temperature range of 78" to 364°K decreased with time. This was attributed to an increase in internal stress resulting from an accumulation of dislocations at internal obstacles. The object of the present investigation was to further evaluate the nature of this hardening by conducting tests in which the direction of stressing is changed after previous creep in shear in a given slip direction. Previous to 1950 three investigations indicated that a Bauschinger effect3 occurred for single crystals as well as polycrystals brass in tension compression,

Jan 1, 1960

By C. H. Li, R. D. Carnahan, R. J. Stokes, T. L. Johnston

When silver chloride deforms by pencil glide at temperatures of 26ºand 72°C, grain size has no effect upon the proportional limit and the material necks down to a knife edge under tension. At -196ºC, deformation takes place on fewer slip systems to produce straight slip traces, the flow stress becomes sensitive to grain size and fracture occurs by cleavage from an intergranular source without any reduction in area. THERE are significant differences between the appearance of the slip bands formed in silver chloride and in the alkali halides at room temperature. The bands in sodium chloride, e.g., are fine and geometrically straight, whereas in silver chloride they are coarse and wavy.&apos; Such differences in the slip behavior prompted us to inquire what the effects of grain boundaries might be on the mechanical properties of these solids. As an introduction to a general study of ionic poly-crystal behavior, we have investigated the effect of grain size on the stress-strain relationships in silver chloride at different temperatures. We have chosen silver chloride chiefly because polycrystals can be easily prepared free from cracks and macroscopic voids by conventional techniques. Moreover, as we shall see, the slip behavior can be readily modified by changing the temperature. It will be shown that the effect of grain size on the yield stress of silver chloride is strikingly dependent upon the temperature of deformation and that this temperature effect comes about through a change in the number of slip systems which operate at the onset of plastic flow. EXPERIMENTAL PROCEDURES Polycrystalline tensile specimens were made by recrystallizing cold-rolled AgCl sheet. Thirty-gram quantities of AR grade silver chloride powder were melted in a low heat capacity furnace, cast into cylindrical forms 3/4 in. in dim and approximately 1 in. in length and then extruded with a 16:l reduction ratio into rods 3/16 in. in dim. Extrusion temperatures were varied from room temperature to 350°C. In order to impart various degrees of cold&apos;work to the extruded rod. All extrusions were then cross rolled to sheet 0.040 in. in thickness at room temperature and machined to form tensile specimens having a gage length of 0.750 in. with a width of either 0.250 or 0.145 in.* Annealing was carried out in an air oven at 200°C for periods up to 20 hr. specimens having average grain diameters ranging from 0.024 to 0.40 mm were prepared by varying the extrusion temperature and annealing time in the conventional manner. To obtain specimens with grain sizes larger than 0.40mm, lightly deformed thin prisims of silver chloride single crystals (supplied by Harshaw Chemical Co.) were recrystallized. Grain size determinations were made by an intercept method and revealed that the grains were equi-axed. Laue back-reflection X-ray patterns showed little tendency to form a preferred orientation texture. Specimens which were to be used for the slip band studies were polished by immersion in fresh boiling concentrated NH,OH for 60 sec. They were then etch polished for 10 sec on each side by hand lapping on a stationary velveteen lap wetted with a dilute Hypo solution (5 g of Kodak Acid Fixer in 100 cc H20). Finally the specimens were rinsed in warm water and alcohol, blown dry and carefully mounted in the tensile machine for testing. Tensile tests were performed at three temperatures, namely, 26º, -72º, and -196°C. A screw-driven hard tensile machine was used at a constant strain rate of 0.006 in. per in. per min. Loads were determined with a light- proof ring fitted with A-18 strain gages and extensions were measured with a 0.0001 in. dial gage. Constant level baths of alcohol with dry ice and liquid nitrogen were used to maintain the two lower test temperatures. EXPERIMENTAL RESULTS Reproducibility—In view of the light sensitivity and reactive nature of silver chloride, it was necessary to determine whether reproducibility depended upon either exposure to light or to the condition of the surface. However, during the course of the work it became clear that variation of laboratory lighting

Jan 1, 1962

By D. F. Kaufman, E. D. Levine, L. R. Aronin

The deformation of&apos; impure beryllium crystals by basal glide at room temperature invariably tevminates by basal cleavage after a few percent strain. It is generally accepted that .fracture of this type is caused by the splitting of low) -angle boundaries, or bend planes, by obstacles that restrict the motion of the bed planes in the deforming crystal. The details of such a process have been developed by Stroh, who showed that the high tensile stress norrnal to the basal plane in the region where the bend plane is split results in the propagation of a basal cleavage crack, provided there is no available dejorvrlatzon mode having a shear component normal to the basal plane It has been postulated that puvification of beryllium might lead to increased basal ductility by the vemoval of barviers to bend plane motion and possibly by the activation of nonbasal defor~rlation systems. Large increases in the amount of basal glide that can he sustained prior to fracture have been observed in crystals purified by zone refining. In each case, eventudal fracture was by sharp basal cleavage, suggesting that the split bend plane model still applies to tile fracture of beryllium of rensonably high purity. In the present work, calculations are made to show to what extent basal duetilits can be increased by purification while the split bend plane .fracture process remains applicable. Experimentally observed ductilities are generally somewhat lower than those predicted by calculation because of premature failure due to defects introd~cced during specimen preparation and testing. SEVERAL investigators1-4 have studied the deformation characteristics of beryllium single crystals of commercial purity, and have related the strong anisotropy of plastic deformation in single crystals to the problem of brittleness in polycrystalline beryllium. For most orientations, the principal deformation mode is basal slip, which, at temperatures between 300" and 900°K, begins at a critical resolved shear stress of approximately 1500 g per sq mm and terminates after 3 to 6 pet glide strain by cleavage on the basal plane in the neighborhood of (1120) bend planes that are formed during the deformation. This type of fracture, which is also observed in zinc at low temperatures, has been interpreted by stroh5 to be caused by the splitting of bend planes by obstacles to their motion. In the Stroh model, a (11.20) dislocation wall, or bend plane, moving along the slip direction under the action of the applied stress, encounters obstacles which cause part of the bend plane to be held up, the other part continuing to move. Stress concentrations are built up in the region where the bend plane is split, with a high tensile component normal to the basal plane, resulting in a microcrack at the end of the split wall. Because no deformation mode having a shear component at an angle to the basal plane is available to relieve the stress at the crack tip, the crack can propagate under a sufficiently high applied stress. The Stroh criterion for crack propagation is given by

Jan 1, 1964

By T. E. Leontis

The specific effect of various rare-earth metals on the room- and elevated-temperature properties of magnesium has been evaluated. Alloys containing didymium exhibit the highest tensile and compressive strengths at room and elevated temperatures. All the rare-earth metals increase the creep resistance of extruded magnesium at temperatures in the range of 400° to 600°F, but the degree of enhancement depends on the temperature and on the concentration of the added metal. THE effects of rare-earth metals on the properties of sand-cast magnesium were discussed in some detail in earlier paper by the author.&apos; The present paper deals with the effect of the same alloying elements on the properties of extruded magnesium. This investigation also had as its aim the development of a wrought alloy having a better combination of room-temperature strength and ductility and elevated-temperature strength and creep resistance than is found in magnesium-Mischmetal-manganese alloys, which have been reported earlier.2-5 The only known attempt to study wrought magnesium alloys containing pure cerium instead of Mischmetal was made by Mellor and Ridley.6 They found that in the form of rolled bars there is a definite, optimum cerium content for creep resistance at 200 °C and that the creep resistance of these alloys at 200 °C is significantly Improved by heat treatment at 550" to 580"C. In the present investigation the compositional variation in mechanical properties of the following alloy systems is presented: I—magnesium-Misch-metal. 2—magnesium-cerium-free Mischmetal. 3— magnesium-didymium. 4—magnesium-cerium. 5— magnesium-lanthanum. Alloys containing predominately praseodymium are not included in this series because of the lack of this material. Experimental Procedures The alloying ingredients used in preparing the alloys described herein are the same as those reported in the earlier paper.&apos; Cerium-free Mischmetal is the rare-earth mixture remaining when the cerium is removed from Mischmetal, which contains all the rare-earth metals as they occur naturally in mon-azite sand, the ore from which Mischmetal is produced. Removal of both cerium and lanthanum from Mischmetal leaves what is commonly called "didym-ium," consisting predominantly of neodymium and praseodymium. Although the composition of the particular batch of each metal used may differ somewhat from the analysis presented previously, these differences are not great enough to warrant repeat- ing the specific composition of each material. The electrolytic magnesium used as the starting material in these alloys has the same typical analysis as that given in the earlier paper.&apos; The alloys were prepared in small laboratory melts applying all the necessary precautions for alloying rare-earth metals with magnesium described by Marande.&apos; Most melts were large enough to cast one 3 in. diam billet 10 in. long. In a few cases, particularly the didymium-containing alloys, the lack of sufficient amounts of the rare-earth metal limited the size of the billet to 6 to 8 in. All billets were scalped to a diameter of 2 15/16 in. and faced to a length of 9 ¼ in. as limited by the size of the extrusion container. The alloys were extruded into ½ in. diam rod on a 500-ton direct-extrusion press using a 3 in. container. The details of the extrusion step are: billet preheat, 925°F (2 hr); container temperature, 900°F; die temperature, 900°F; extrusion speed, 10 ft per min; reduction ratio, 36:1; and percent reduction, 97.3. The lower melting point of alloys containing didymium&apos; necessitated reduction of the extrusion speed to 5 ft per min in order to prevent hot shorting during extrusion. Adequate lengths were cropped from both ends of each extruded rod to assure that all the material used for tests was extruded under uniform conditions. Tensile and compressive properties at room temperature are reported in the several conditions of heat treatment. The ASTM designations are used to distinguish these conditions as follows: T5—Direct age at 400°F (16 hr) T4—Heat treat at 950°F (4 hr) for alloys containing didymium T4—Heat treat at 1050°F (4 hr) for all other alloys T6—T4 + age at 400 °F (16 hr) The lower heat-treating temperature for alloys containing didymium is necessitated by the lower melting point of these alloys. All heat treatments were conducted in electrically heated, circulating-air furnaces. A protective atmosphere containing 0.5 to 1.0 pct sulphur dioxide was used for the high temperature heat treatments. Tension and creep specimens 6 Yz in. long and compression specimens 1½ in. long were cut from the extruded rod. A reduced section of ? in. diam was machined on the tension specimens, whereas on the creep specimens a reduced section of 0.450 in. diam

Jan 1, 1952

By N. Jaffe, J. E. Dorn

This investigation is concerned with the possibility that the creep resistance of metals might be reduced as a result of recovery at the creep temperature when the applied stress is reduced. For this purpose the effect of stress on the recovery of the creep behavior of pure polycrys talline aluminum was investigated in the cross-slip temperature range where the activation energy for creep is 28.000 cal per mole. Before recovery all specimens were given the same substructure by creeping them under a stress of 7800psi to a strain of 0.218. Recovery was then accomplished by holding the specimens at the creep temperatures of 327" and 337°K under a series of reduced stresses for various periods of time. When the original stress was reapplied the specimens crept more rapidly than when the original stress was first removed, illustrating that recovery did take place. The extent of recovery could be indexed in terms of the UNDER certain conditions of test, the creep rate decreases over the primary stage of creep often by as much as a factor of 10~B. Since the external variables of stress and temperature are held constant, such pronounced and significant changes in the creep rate must be attributed to various substructural modifications that are introduced as a result of creep itself. At the secondary stage of creep, over which the creep rate remains constant and the substructure no longer changes, a balance must be achieved between the rate of increase in creep resistance due to creep straining and the rate of recovery of the substructural modifications. The general validity of these concepts on substructural changes has already been shown,&apos; including the corollary that a more creep-resistant substructure is introduced under a more rapid creep rate arising from a higher applied stress.&apos; In spite of these well-documented facts, very little progress has been additional strain undertaken by the recovered specimen to achieve the same strain rate as the unrecovered specimen. It is significant that the higher recovery stresses gave the most rapid rates of recovery. Over the high range of reduced stresses, where some creq took place during recovery, the activation energy for recovery equaled that for creep, namely 28,000 cal per mole. But for stresses during recovery below 0.80 of the original creep stress, no creep was detected during recovery and an activation energy for recovery of about 72,000 cal per mole was obtained. Whereas the activation energy of 28,000 cal per mole suggests that cross-slip of dislocations is responsible for this recovery, the mechanism for the 72,000 cal per mole process is not known. This activation energy, however, is about twice that for self-difhsion. made in determining, in satisfactory detail, precisely what substructural changes so effectively modify the creep rate.&apos; Up to the present, electron microscopy has failed to uncover, in a satisfactory quantitative manner, the mechanistic processes involved. Since, however, creep, at least at moderate and high temperatures, arises from one or more types of dynamic recovery processes, it should be possible to shed additional light on the total problem by investigating the recovery of creep resistance. The importance of such an investigation becomes apparent when the fact is recognized that there has yet been no direct experimental proof that the rate of softening due to substructural changes as a result of recovery equals the rate of hardening due to creep-induced substructural strengthening over the secondary stages of creep. Furthermore the problem of what happens to the creep-strain induced strengthening when the material recovers either at zero or some reduced operating stress has significant engineering consequences. It was for these reasons that the present investigation on the recovery of creep behavior was initiated. Inasmuch as a substantial background has now developed on the creep of high-purity aluminum, this material was again selected for the current investigation. Furthermore extensive evidence is now

Jan 1, 1963