By Ralph Hultgren

IN solid solutions atoms of differing sizes occupy the same crystalline lattice, requiring that some of them be compressed and others expanded. The energy involved has been called misfit strain energy and is an important concept of crystal chemistry. If the atomic sizes and elastic constants of interatomic bonds are known, the misfit energy may be calculated,' provided certain simplifying assumptions are allowable. Usually, isotropic crystals are assumed and interatomic distances are taken to be the statistical average determined from X-ray diffraction. Such calculations yield values of the misfit energy of the order of 1 or 2 kcal per atom in alloys such as Au-Cu at compositions of 50 atomic pct. However, evidence has accumulated in recent times that atoms change their sizes with composition of alloys, implying electronic rearrangement of the bonds. The size changes have been found particularly by application of the X-ray method developed by Warren, Averbach, and Roberts.' Thus, Averbach, Flinn, and Cohen3 determined radii in Au-Cu alloys. Oriani4 showed that these new radii led to a calculated misfit energy in disordered AuCu, which was decreased from the values calculated by the usual theory more than twenty-fold, to only 80 cal per g atom. Thermodynamic calculations from the phase diagram5 also show misfit energy to be no more than a few hundred calories per g atom in this alloy. The question of what electronic rearrangements are possible therefore becomes compelling in estimating misfit energy. In the following pages the results of certain calculations on the AuCu tetragonal superlattice are submitted. Conclusions drawn from these should be applicable in large degree to disordered solid solutions. As in all ordered states, bonding distances in the superlattice are individually known, rather than being merely average distances as found from lattice constants of disordered states. Moreover, only the Au-Au and Cu-Cu distances are strained; the elastic constants of these are known in the elementary state. In the usual calculation it is necessary to assume elastic constants for Au-Cu bonds. Misfit energy has thus been calculable without the need of many simplifying assumptions usually made. It is still assumed that equilibrium bond lengths and elastic properties of the bonds are the same in the alloy as in the pure metals. As previously discussed, this is probably not correct. Also assumed is that the bonds are not affected by strain of neighboring bonds. A calculation of Young's modulus from compressibility data shows this to be far from true; extensive electronic rearrangements take place. It would seem that misfit energy cannot be calculated from elasticity data for the elements. The usual methods may, however, give an upper limit which is often much higher than the true value. The question of electronic rearrangement is, of course, a complex one. Pauling's theory gives a simple, approximate treatment of the relation between type of bond and bond distance. This has been applied with some success to the Au-Cu system, as will be shown in a later section. Misfit Energy in Au-Cu Alloys Hume-Rothery and Raynor6 discuss the Au-CU system as a type example of strain energy. The gold atom is 12.8 pct larger in diameter than the copper atom, near the size factor limit beyond which solid solubility is severely restricted. They therefore consider the misfit energy to be large, a conclusion for which they believe they find evidence in the phase diagram. Gold and copper are completely miscible in the solid state, but the alloy has a minimum melting point at an intermediate composition. From this Hume-Rothery and Raynor conclude that the strain energy is nearly large enough to prevent miscibility; the phase diagram tends toward a eutec-tic type. In Ag-Cu, which has almost identical size relationships, solid miscibility is quite limited; whereas in Au-Ag, where atomic sizes are nearly the same, there is complete miscibility without a minimum in the melting point. From their arguments the heat of formation of Au-Cu would be expected to be endothermic or only slightly exothermic, that of Ag-Cu to be endothermic, and that of Au-Ag to be exothermic. Deviations, from Ve-gard's law of additivity of atomic radii support these conclusions, since Au-Cu and Ag-Cu both have pronounced positive deviations, and Au-Ag has a negative deviation. Nevertheless, Au-Cu alloys form exothermically; indeed, considerably more exothermically than Au-Ag, Table I. Hence, strain energy must be much less important in this case than Hume-Rothery and Raynor have supposed.

Jan 1, 1958

By Stanley Rajnak, John E. Dorn

The saddle-point activation energy for the nu-cleation of a pair of kinks is estimated as a function of the applied stress, the lattice constants, and the height and shape of the Peierls' hill by employing the line-energy model of a dislocation. The kinetics of disloration motion by the Peierls' mechanism are discussed and the microscopic dislocation velocities and macroscopic strain rates are formulated by the Arrkenius type of approach in terms of the activation energy for the formation of pairs of PEIERLS was the first to illustrate that a straight-dislocation line has its lowest energy when it lies in a potential valley parallel to lines of closest packing kinks. The log of the dislocation velocity is found to be approximately proportional to the log of the local applied stress. It is also shown that the low-temperature mechmical properties of several bcc metals might be explained in terms of the Peierls mechanism, good agreement being obtained between theory and experiment for the flow stress us ternperature, activation energy vs stress, and activation volume us stress curves for these metals. of atoms on the slip plane. When such a straight dislocation is moved rigidly from one valley toward the next, the atoms in the vicinity of the core of the dislocation change their positions and bond angles, causing the energy of the dislocation to increase. Midway between two adjacent valleys, the disloca-tion energy reaches a maximum value and any additional small displacement will cause the dislocation to fall down the hill into the next valley. The maximum shear stress necessary to promote such

Jan 1, 1964

By L. Segle, R. Resnick

NUMEROUS experiments in the past few years have proven that void formation occurs quite generally in the diffusion zone of bimetal specimens1-4 The phenomenon has been explained in terms of the accumulation of lattice vacancies resulting from unequal diffusion of the constituents and their eventual precipitation as holes.= Attention has recently been directed to the fact that voids also form within homogeneous metals during high-temperature creep.' The idea has been put forward that these voids form by the condensation of excess lattice vacancies generated by intersecting dislocations.".' If the precipitation of lattice vacancies from solution is treated as a nucleation and growth process, the predicted vacancy concentration for homogeneous nucleation of voids at an observable rate is 100 to 1000 times the normal thermal equilibrium concentration. It appears that voids actually form during diffusion at vacancy supersaturations which are much lower than this8 According to the calculations of Machlin,' the same must be true for voids formed in homogeneous metals during creep, if these are considered to arise from the precipitation of lattice vacancies. Therefore, if the vacancy mechanism is valid, it seems that the holes which form in diffusion and creep specimens are heterogeneously nucleated by imperfections or impurities in the metal. Irregularities in the frequency and distribution of voids in diffusion couples bear out this explanation.' , It is not known at the present time what the nuclei are on which vacancies condense. Various investigators have speculated that they could be certain dislocation configurations, already existing voids produced during solidification or working, gas pockets, or inclusions in the metal. Relatedly, the precise value of the degree of vacancy supersatura-tion for void nucleation is still uncertain. An initial attempt to estimate this value from diffusion data, made by Balluffi, indicated that voids form in diffusion couples at vacancy concentrations which may

Jan 1, 1958

By J. Gurland

THE microstructure of sintered carbides consists of particles of metal carbides, such as WC and TiC, embedded in a metallic binder which is usually a cobalt—or nickel-rich solid solution. One of the important factors influencing the strength of the alloys is the degree of dispersion of the carbide particles in the binder matrix. While it is generally accepted

Jan 1, 1960

By W. R. Hibbard Jr., R. W. Guard, N. G. Ainslie

Evidence is presented that copper-base solid solutions of different solutes having equal grain sizes, no preferred crystal-lographic orientation, equal electron-atom ratios, and, within experimental scatter, identical initial yield strengths, need not have identical stress-strain curves at strains larger than about 0.04. The stress-strain behavior is rationalized in terms of the proposed Suzuki chemical interaction between solute atoms and extended dislocations using what is thought to be a somewhat different means of representing stress-strain data. ALTHOUGH the effect: of alloying element upon the strength characteristics of sold solutions is a subject which has received considerable attention in the past, the exact relationships between the common deformation parameters and certain common variables are not really known in some cases. As a result some of the experiments reported in the literature in which these variables are inadequately controlled lose some of their persuasion regarding underlying principles. Nonetheless, facts are known which bear pointing up: When the true stress, a, and true plastic strain, E, of tensile deformatic~n are plotted on a double logarithmic coordinate system, one may observe a straight-line relationship at strains greater than 0.02. The form of the curve in the linear region is given by a = Ken! where a represents true stress, E, true strain, and K and tn, constants. If the relationship holds, K and m define the flow characteristics of the material being tested. m and K, however, may vary with other parameters. Hollomon found that in a-brass, m is influenced by grain size. French and HibbardZ found in alloys of copper that inverse relationships existed between m and 1) the solute concentration for a given solute, 2) the 0.01 yield strength, and 3) the constantK. Lacy and Gensamer3 observed (du/d~) (= U/Em) to increase with increasing values of K in systems of alloyed ferrites (although with considerable scatter of data which may be attributed to uncontrolled grain size). Brick, Martin, and Angier* deduced in copper-base alloys a straight-line relationship (with some scatter) between the change in the Dph number due to solid-solution strengthening and the change in the Dph number due to work hardening which suggested that copper-base alloys having equal yield strengths might have identical stress-strain curves in the plastic flow regions. French and HibbardZ concluded that the yield strength of copper-base solid solutions is the proper basis for comparing the effects of solute elements. Also, Allen, Schofield, and ate' showed that, within their experimental variation, copper-base alloys of zinc, gallium, germanium, and arsenic having the same electron-atom ratios have the same true-stress true-plastic strain curves. Dorn, Pietrokowsky, and ~ietz' also found that with aluminum-base alloys the stress-strain curves in the flow regions are approximately the same if "equivalent" concentrations of alloying elements are used. Solute valence and lattice parameter distortion were the parameters used to determine equivalency. The present report describes an investigation in which an attempt was made to obtain copper-base solid-solution alloys of four solute elements having within close tolerances equal grain sizes and yield strengths, and to see if the level of yield strength does indeed define the flow curve regardless of solute type. During analysis of the data certain unexpected features of the stress-strain curves became apparent which gave rise to some speculation and are discussed at length in the paragraphs that follow. EXPERIMENTAL PROCEDURES Alloy Preparation—Using the data of French and HibbardZ as a first approximation, four different binary copper-base alioys were designed so as to have the same yield strength. In addition, other alloys were prepared in which the solute aoncentrations varied slightly from those calculated above so as to span a range of yield strengths, see Table L The yield strengths of all alloys prepared except the copper-tin alloys were subsequently found to Lie fairly close to one another. The copper used in the alloys was produced by the American Smelting and Refining Co. and was of very high purity (99.999 pct). The alloy additions and their initial purities are as follows:

Jan 1, 1960

By R. H. Martinson, E. Teghtsoonian

The effects of magnesium-rich surface layers of varying thickness on the mechanical properties of LiF have been studied. The yield stress, critical tensile stress, and work-hardening slope increase linearly with layer thickness, while the strain to fracture decreases yapidly with increasing layev thickness. The results of tension tests, supplemente!d by metallogvaphic evidence, indicate that the yield stress and the critical tensile stress of LiF are not determined by surface-source operation. DESPITE many studies, which have recently been reviewed,' certain fundamental aspects of the plasticity of LiF remain obscure. For instance, one question still awaiting a satisfactory resolution is: does the nucleation and/or multiplication of dislocations in LiF occur preferentially near the crystal surface? It is now well-known that mobile dislocation half-loops are readily introduced into LiF by surface damage and that the mechanical properties of LiF are affected by such surface damage. However, it is not known whether, in the absence of large numbers of artificially introduced surface sources, dislocations arise more easily near the crystal surface than in the crystal interior. It is also not known to what extent existing mobile dislocations multiply preferentially near the crystal surface. The present work is an experimental study of these matters. A short investigation of the effect of magnesium -alloyed surface layers on the deformation of LiF single crystals has been published by Westwood.~ Some relevant conclusions drawn from this research are restated here for purposes of comparison with the present work. 1) Tests on as-cleaved, chemically polished, coated and uncoated specimens show that a coating can restrict the operation of artificially introduced surface sources, thereby raising the yield stress. A coating also decreases the initial rate of work hardening of as-cleaved LiF crystals by reducing the number of active dislocation sources, so that mutual dislocation interference effects are lessened. 2) A catastrophic breakthrough of groups of edge dislocations piled up against the coating can cause stress drops in the stress-strain curve. 3) A surface coating can act as a stable barrier to the egress of dislocations, causing pile-up,

Jan 1, 1965

By M. E. Nicholson

IN order to understand how alloying elements influence hardenability through their effect on the rate of pearlite nucleation, it is advantageous to use a model to describe the mechanism of pearlite nucleation. The model which currently is most widely accepted has been described, among others, by Mehl et a1.1-3 and by Hultgren.4 Pearlite nucleation involves both the nucleation of ferrite and cementite.4,5 Cementite nucleates first, followed rapidly by the formation of ferrite at the cementite-austenite interface. The conclusion that cementite is the first phase to form during the process of pearlite nucleation is based, in part, on the observation that proeutectoid cementite is continuous with pearlitic cementite and that the orientation relationship between proeutectoid ferrite and austenite is not the same as that between pearlitic: ferrite and austenite.6,7 Recently, Smith" has suggested that the dissimilarity in orientation relations, instead of indicating the pearlite nucleation sequence, may be evidence that pearlite is nucleated in a grain adjacent to the one in which it is growing. Also, Modin9 as shown that ferrite in pearlite may be continuous with proeutectoid ferrite, and he has also shown that proeutectoid cementite is not always continuous with pearlitic cementite. Thus, it appears that the conclusion that cementite always initiates the pearlite nucleation process is open to serious question. The author believes that important evidence on the question of how pearlite is nucleated exists in the rates of pearlite nucleation of different steels. The following is a review and analysis of this evidence. If the nucleation of pearlite is considered as requiring the nucleation of both cementite and ferrite, then the time to nucleate pearlite consists of the time to nucleate the first phase to form, plus the time to nucleate the second phase at the advancing interface of the first. In the absence of a visible proeutectoid constituent, the second phase must be nucleated very soon after the first. If cementite is the first phase to form, the time to nucleate pearlite will be approximately equal to the time to nucleate cementite. Since the nucleation rate of a phase precipitating from solid solution increases with the degree of supersaturation, it would be expected that the rate of pearlite nucleation should increase with increasing carbon content. Digges10 has shown that the reverse is true. He determined the quenching velocity necessary to suppress pearlite formation in plain carbon steels as a function of carbon content. His results showed that pearlite formation could be suppressed with lower quenching velocities as the carbon content of the steel increased, at least up to 1.25 pct C, the highest carbon content he studied. Thus, it would appear that in plain carbon steels, in which pearlite is formed at the nose of the C-curve, the hypothesis that cementite nucleates first does not predict the observed change in nucleation rate. The validity of the current model of pearlite nucleation may be tested also by determining whether or not it predicts the relative influence of alloying elements on the nucleation of ferrite and pearlite. This can be done best by a consideration of the changes in a TTT diagram produced by a change in alloy content. Hultgren4 suggests that the general shape of a TTT diagram, as well as what constituents will form from austenite, can be predicted from the relative nucleation rates of ferrite and cementite. This is illustrated in the schematic diagram for a hypoeutectoid low alloy or plain carbon steel shown in Fig. 1. The C-curves for ferrite nucleation and for cementite nucleation are represented by AA' and CC', respectively, and the start of ferrite formation and pearlite formation are represented by AX and BC respectively. Adopting the current theory, Hultgren suggests that between X and C pearlite forms directly from austenite, since cementite nucleates more rapidly than ferrite in this temperature range. Conversely, at temperatures above Tx, ferrite is the first to nucleate and proeutectoid ferrite is formed. As proeutectoid ferrite grows, austenite becomes enriched in carbon, so that the cementite nucleation rate is increased. As a result, pearlite nucleation above temperature Tx is accelerated, beginning along BX and not along C'X. Temperature T, represents the temperature at which the nucleation rate of ferrite equals that of cementite. By extending this type of reasoning, using the principle that the nucleation rates of ferrite and cementite increase with increasing supersaturation of austenite with respect to these phases, it should be possible to predict the influence of carbon content on the shape of the isothermal transformation diagram. For a slightly higher carbon content than that of Fig. 1, the curve A A' representing the beginning of ferrite formation should be moved to the right, whereas the curve CC' representing the beginning of cementite formation should be moved to the left. For hypoeutectoid plain carbon and low alloy steels, this prediction does not agree with existing data. Instead, as the carbon content is increased, the pearlite curve moves to the right along with the ferrite curve and always appears to join it tangen-tially. This behavior is demonstrated by the TTT-curves of a series of manganese steels" shown in Fig. 2. In this figure, TTT-curves for four alloys containing 0.20, 0.40, 0.60, and 1.20 pct C are superimposed. The curves are identified in the figure legend. The letters F, P, and C are used to indicate the start of ferrite, pearlite, and cementite formation, respectively. In these steels, it appears that the nucleation of ferrite and of pearlite are related processes. As a result of the foregoing evidence, it is proposed that the formation of pearlite be considered as follows: Either ferrite or cementite may nucleate from austenite, then grow until the remaining phase is nucleated at the interface between the growing phase and austenite. (The growth of the first phase to form is assumed to be accompanied by a composition change in the adjoining austenite.) According to this model there are two modes of nucleating pearlite: 1—where cementite initiates the succession

Jan 1, 1955

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,' who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.'" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.' (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By E. J. Whittenberger, F. N. Rhines

The formation of casting porosity is viewed as a nucleation and growth process with solidification shrinkage and gas precipitation as cooperative driving forces. Experimental evidence evaluating the individual contribution of each force confirms the major premise that microporosity is nucleated by gas precipitation. Additional data disclose the effects of the identity and quantity of gas, the temperature range of freezing, and the freezing rate upon the amount and distribution of porosity in light metal castings. POROSITY, as it commonly occurs in metal castings, has been ascribed to the contraction that accompanies the freezing of the metal, to the evolution of dissolved gases from the liquid during cooling and freezing, and, most frequently, to a combination of the two.'" "Pipe" formation is universally associated with solidification shrinkage; spherical "gas holes" are understood to be retained bubbles of gas; but the origin of microporosity, which usually exhibits an irregular or scalloped outline when viewed in cross-section, remains a subject of continuing debate.", ' The present research constitutes an endeavor to show what parts are played respectively by shrinkage and gas evolution in the initiation and growth of micropores and what factors determine their number, size, shape, and distribution. A preliminary outline of the mechanism of cavity formation in castings will serve to coordinate the experimental findings that will be reported and will at the same time provide a general theory of the origin of casting porosity. Basic to the mechanism of cavity formation that will be proposed are the following established facts: 1—that liquid metals and alloys contract gradually during cooling down to the freezing range, where a relatively large contraction, known as the "solidification shrinkage," takes place (exceptions in bismuth and gallium being noted);' 2—that the capacity of liquid metals and alloys for dissolving gases diminishes with cooling until, in the freezing interval, a large decrease takes place (various exceptions being noted and excluded from present consideration) ;.: and 3—that freezing proceeds counter to the direction of heat flow, the freezing front most commonly being composed of a system of tapering dendrite stalks and side arms which are coarser the lower the freezing rate and which protrude into the liquid for a distance that is greater the longer the freezing temperature interval of the alloy and the smaller the thermal gradient.' The mechanism by which voids are generated

Jan 1, 1953

By J. H. Scaff, H. C. Theurer, E. E. Schumacher

The microwave region of the radio spectrum was effectively utilized in radar designs during the recent war and it has become of increasing interest in the field of communications. Work in this field has led to an important use for silicon—that of the point contact rectifiers†1 in the frequency converter of microwave (radar or radio) receivers—and has stimulated considerable interest in the electrical properties and preparation of silicon and its alloys. Silicon is an electronic semiconductor. Its conductivity at room temperature results principally from the presence of certain impurities. While for metals an increase in impurity content increases the resistivity, for semiconductors such as silicon the opposite occurs and, in general, the addition of impurities lowers the resistivity. Silicon materials may be classified into one of two groups depending upon the manner in which the impurities contribute to electrical properties. These have been termed for convenience p-type or n-type. P-type silicon develops a very large positive thermal emf against metals, has a Hall coefficient of positive sign and a low resistance direction in point contact rectification with the silicon positive with respect to the point. N-type silicon, on the other hand, develops a negative thermal emf against metals, has a Hall coefficient of negative sign and a low resistance direction in rectification with the silicon negative with respect to the point. Impurities which produce n-type silicon are called donors inasmuch as these elements contribute to electrical conductivity by donating electrons to an unfilled energy band in the silicon. On the other hand, elements which produce p-type silicon are known as acceptors as these impurities contribute to the electrical conductivity by accepting electrons from a filled energy band permitting what is known as conductivity by "holes" in which the sign of the carriers appears to be positive. A general treatment of the mechanism of conduction in semiconductors from the viewpoint of modern band theory has been given recently by Pearson,2 by Becker, Green and Pearson,3 and by Torrey and Whitmer.4 In this investigation boron and aluminum have been found to be acceptors, and phosphorus, arsenic, and antimony to be donors in silicon. Data on the effect of boron and phosphorus on the electrical properties, when present singly and in combination, have been acquired. These data are discussed in the present paper. Raw Materials Used and Methods for Adding Seeond Constituents Silicon from two sources was used in this work and these will be referred to as A and B respectively. Silicon A is a material of high purity supplied by the Electro Metallurgical Co. It is prepared by chemical purification of "commercial" silicon obtained from the arc furnace reduction of SiO2. It contains 99.8 pct silicon, minimum, with small amounts of calcium, iron, aluminum, boron, and phosphorus as the principal impurities. This material was extensively employed in these studies as well as in the commercial preparation of rectifier materials. Silicon B is a material of high purity from the du-Pont Co. It is prepared by a pyrolytic reduction of Sicl4 and is free of analytically detectable amounts of boron and phosphorus. Its use permitted study of the effect of boron and phosphorus individually on the properties. This material contains, however, spec-troscopic traees of a number of metals, some of which affect electrical and rectification properties. Typical analyses for the two grades of silicon are given in Table 1. To make controlled additions of boron to the charge it was necessary to employ a low boron content master alloy since the quantity of boron to be added was usually only a few thousandths of one percent. The alloy containing nominally one percent boron was prepared by melting chemically pure boron with silicon A using the melting techniques for 320 g silicon

Jan 1, 1950

By J. J. Gilman

The data presented indicate that the critical shear stress and strain-hardening Thedatapresentedrate of a zinc monocrystal depend on the orientation of its slip direction with respect to its external boundaries. The tendency of a crystal to form deformation bands also depends on its shape. THE plastic behavior of pairs of zinc monocrystals in which both members of the respective pairs had the same orientation with respect to the longitudinal axis, but each had different orientations with respect to their rectangular external shapes, were compared in this investigation. The purpose of the investigation was to see what influence the shape or surface of a zinc crystal has on its mechanical properties. In a previous investigation of triangular zinc monocrystals,1 anomalous axial twisting was observed which seemed to be related to the triangular shape of the crystals. Wolff,' in 400°C tensile tests of rectangular rock-salt crystals bounded by cubic cleavage planes, found that, of the four equivalent slip systems, the two with the "shorter" slip directions yielded and produced slip lines at lower stresses than the other two. This observation and the work of Dommerich³ as formulated by Smekal4 as a "new slip condition" for rock-salt: "among two or more slip systems permitted by the shear stress law, with reference to the formation of visible slip lines by large individual glides, that slip system is preferred which has the shortest effective slip direction." More recently, Wu and Smoluchowski5 reported essentially the same effect for ribbon-like (20x2x0.2 mm) aluminum crystals at room temperature. Experimental Chemically pure zinc (99.999 pct Zn), purchased from the New Jersey Zinc Co., was the raw material. Glass envelopes, containing graphite molds and zinc, were evacuated while hot enough to outgas the graphite but not melt the zinc. At a vacuum of about 0.2 micron the envelopes were sealed off and then lowered through a furnace at 1 in. per hr so as to melt and resolidify the zinc and produce mono-crystals. One-half of one of the molds is shown in Fig. la. Each mold consisted of four pieces from a cylindrical graphite rod that was split longitudinally and transversely at its midpoints. Rectangular milled grooves 0.050 in. deep and % in. wide formed the mold cavity when the split halves were assembled with twisted wires. Fig. lb shows the specimen shape obtained when the top and bottom mold-halves were rotated 90" with respect to each other. Good fits prevented leakage and excess zinc was necessary to provide enough liquid head to fill the mold completely. In removing soft crystals from the molds it was impossible to avoid small amounts of bending. However, manipulations were carried out whenever possible with the crystals protected by grooved brass blocks. All specimens were annealed prior to testing. From the top and bottom sections of each crystal, X-ray specimens and tensile specimens 7 to 8 cm long were sawed. The tensile specimens were annealed inside evacuated tubes for 1 hr at 375°C. Next the crystals were cleaned and polished by 2-min dips in a solution of 22 pct chromic acid, 74 pct water, 2.5 pct sulphuric acid, and 1.5 pct glacial acetic acid.' Cleaning was followed by a 10-sec dip in a 10 pct caustic solution, then washed in water and alcohol, and dried. This treatment results in a bright surface covered by an invisible oxide film. The testing grips were a slotted type with set screws and were supported in a V-block during the mounting operations in order to avoid bending the crystals. A schematic diagram of the recording tensile-testing machine is shown in Fig. 2. The machine has been described elsewhere.' The head speed was 0.3 mm per sec for all tests. The crystal orientations were determined by the Greninger X-ray back-reflection method with an estimated accuracy of 1. Description of Crystal Geometry A schematic picture of a rectangular zinc mono-crystal is shown in Fig. 3. ABD designates the front edge of a basal plane (0001) of the crystal, the only active slip plane for zinc at room temperature. Of the three possible (2110) slip directions, the active one is indicated by an arrow. Cartesian coordinates are taken parallel to the specimen edges. The normal, n, to the basal plane (n is parallel to the hexagonal axis) has the direction cosines a, ß and ?. X0 = 90 — y is the angle between the longitudinal axis and

Jan 1, 1954

By S. L. Lopata, E. B. Kula

A variation of yield and tensile strength with direction has been noted in heat-treated 4340 steel which had been warn-worked by rolling in the austenitic condition prior to quenching. Measurements by X-rays showed a preferred orientation of martensite crystals. Various ideal preferred orientations of martensite were calculated by assuming a preferred orientation for austenite and transforming this to martensite by the Kurdjumov -Sachs and Nishiyama relationships. Comparison with the measured preferred orientation showed that the ideal rolling texture for austenite in 4340 steel could be expressed as a (112) [111] texture with a component of (110) [112]. No evidence was found for any fiber axis in the rolling direction, or fop- a (123) [412] texture. The observed martensite pole figures can be adequately accounted for by these ideal austenite textures and by the Kurdjumou-Sachs or Nishiyama transformation relationships between austenite and martensite. ALTHOUGH preferred orientations are found in cold-rolled steel sheet and in many nonferrous metals, they are not generally encountered in wrought, heat-treated high-strength steels, since such steels are generally not cold worked sufficiently to develop a strong texture, and any texture that is present is removed during heat treatment by the phase transformations taking place. This report gives details on a preferred orientation found in warm-rolled and hardened 4340 steel. In a recent study, a special combination heat-treating and working technique was used in which 4340 steel was deformed in the austenitic condition, and before re crystallization of the austenite could occur, quenched to form martensite.' Since the austenite was unrecrystallized, it was cold worked and hence could have contained a preferred orientation which could be transmitted to the martensite on quenching, and this in turn could be manifested as a directionality of mechanical properties. Such a directionality of properties was found as a result of working, and this prompted an X-ray study of the preferred orientation. Literature Survey— Rolling Texture in Face-Cen-tered-Cubic Austenite—M a preferred orientation is found in a rolled and hardened steel, it is first appropriate to consider what texture existed in the austenite as a result of the rolling but prior to the transformation to martensite. The changes taking place as a result of the austenite-martensite transformation are then considered. In view of the instability of austenite in 4340 steel at low temperatures, no direct determination of the austenite texture was made. However, an estimate of the texture for austenite in 4340 steel may be made by considering the textures found for other face-centered-cubic metals. Barrett' has reviewed the rolling textures for many materials. The most common orientation in face-centered-cubic metals has the (110) planes parallel to the rolling plane and the [112] directions parallel to the rolling direction, or (110) [112]. Other orientations found are (112) [111], as well as (100) [001], (110) [001], and others. Beck and his co-workers, using quantitative pole figures, report that (123) [121],3 later corrected to (123) [412],4 better describes the ideal orientation. smallman5 reported that the ideal preferred orientation for high-purity face-centered-cubic metals is (123) [121], but that there is a transition to (110) [112] as solid solution elements are added. The latter texture tends to occur more readily at lower temperatures. This transition between the two textures was explained by differences in the slip characteristics with concentration or temperature. More recently, Jones and Fell6 concluded that the (123) [412] texture for face-centered-cubic metals could equally well be represented by a mixture of (110) [112] and (112) [111] textures, and hence it had no physical reality. From the above results it can be seen that there is no agreement on the "ideal" texture for fcc metals and, hence, no firm basis for assuming a texture for austenite in 4340 steel. Therefore, the orientations (110) [112], (123) [412], and (112) [111] have been considered in the following.* *The (123) [4121 is identical to the (123) [121] rotated 90 deg. Orientation Relationship between Austenite and Martensite—When martensite forms from austenite, certain crystallographic planes of the martensite are parallel to planes in the austenite. This orientation relationship was first determined by Kurdjumov and

Jan 1, 1960

By C. G. Dunn, P. K. Koh

The primary recrystallization textures of 11 single crystals cold rolled 70 pct were determined. The effect of crystal orientation on recrystallization behavior was investigated also and found to be large. An exception was found to the relationship that strong components of the recrystolliza-tion texture are rotated from the cold rolled texture by 30° about <110> axes, but generally this relationship was found to hold quite well. Evidence supporting oriented nucleotion was found and discussed in terms of probable active slip systems and <110> edge dislocations. THE present paper is one of a series&apos;.&apos; on recrys-tallization phenomena in cold rolled 31/4 Si-Fe single crystals and is mainly concerned with the textures produced on recrystallizing from stable end orientations. Data for the cold rolled textures of the crystals used have been reported by Koh and Dunn." Their results showed that the sharpness of the cold rolled textures varied throughout the range of stable end orientations and that the tendency to re-crystallize was related to the sharpness of the cold rolled texture, wherein the rate of recrystallization increased and the size of recrystallization grains decreased with decreasing sharpness of the cold rolled texture. In the project under consideration the cold rolled crystals involved a range of initial orientations that, together with those studied earlier,&apos; provide information on several points. The first point is whether the recrystallization texture from a (111) [112] cold rolled texture, a stable end orientation that can be approached from different directions, correlates in any way with the initial orientation before cold rolling, or whether the recrystallization texture is entirely determined by the observable features of the cold rolled texture. The second point involves a preliminary study to see if the main components of the recrystallization textures correlate with the most probable active slip systems. The third point is to determine what effect departure from slip on one slip system has on the tendency to recrystallize. Experimental Procedure Nine specimens from a previous investigation and two additional ones from thicker stock (lot D) but of similar composition to the others were used in the present work. The latter two crystals, like the nine, were cold rolled to a reduction in thickness of 70 pct and the amount of widening was determined. Depending on their primary recrystallization behavior, the cold rolled crystals were given short or long anneals at temperatures of 980°C or higher. Table I summarizes the data on initial orientations, the textures obtained by cold rolling, and the anneals given to provide samples for the present work. Fine grained specimens were thinned to 0.002 in. thickness and placed in an integrating specimen holder. Chart recordings using a transmission X-ray method and MoKa radiation were obtained for diffraction from (110) planes. This method,&apos;,3 which gives data for all of the pole figure except a central region of 30" radius, proved sufficient to give generally five, and sometimes six, of the six possible pole concentration areas of any one component of the texture. These data, therefore, were generally adequate for a positive identification of each component present. The first texture obtained for specimen B-2 was poorly defined because of too coarse a grain structure and therefore too few crystals in each component for satisfactory X-ray reflections. The same

Jan 1, 1957

By Irving B. Cadoff, Stojan M. Zalar

AgInTe2, CuInTe2, and all Proportions of CuxAg1-xInTe, forMed homogeneous single phase alloys after direct solidification from the nielt. X-ray analysis indicated a zinc-blel~de strzccture typical of the chalcopyrite compounds, and the electrical resistivity and Sccbeck coefficient values were in the semiconducting range. AuInTe, and AuxA4g,-, InTe, formed by what appeared to be a peritectic reaction (the thermal analysis curves showing more than one arrest) and were conseyue~ztly polyphase. Substitution of copper into AgIrzTe, resulted in a continuous transition in the room tenzperature Seebeck coefficient from the negative AgIzTe, to the positive CuInTe,. A zero coefficient was obtained at about Cuo.55 Ago.45 InTe, . The temperatzire variation was similar to that observed for the stoichiometric compounds, that zs, tendency towards "p" concEuction at elevated temperatures. The thernzoelectric figure of merit for the compo~uzds, as determined by the Putley -Harmnn method were in the range 10- to 10-7 "K-l; the thermal conductivities in the order of 0.15 cal per sec-cm-oK. INCREASED interest in semiconducting intermetallic substances is expanding much of recent research from simple binary compounds into polyatomic systems and solid solutions. Ternary compounds A&apos; represent a covalent extension of the binary semiconductors Within the a tin isoelec-tronic series, Ag-Cd-In-Sn-Sb-Te-I, divalent cadmium atoms in CdTe are being substituted for by monovalent silver and trivalent indium atoms to form the compound AgInTe, . By cross-substitution with elements of other isoelectronic series, a great number of ternary compounds A &apos;B"&apos;c? is possible. In all of them, however, a necessary though not sufficient condition for the covalent, semiconducting bond—that there be four sharing orbital electrons per atom—must be fulfilled. In AgInTe,, each silver or indium atom is tetrahedrally surrounded by four tellurium atoms, while each tellurium atom is co-valently bound to two silver and two indium atoms. Synthetic chalcopyrites A&apos;B"&apos;c~ were first recognized as potential semiconduct&rs by Goodman and Douglas.&apos; Austin, Goodman, and Pengelly discuss preparation difficulties and some electronic measurements on AgInS, , AgInSe, CuInSe, , AgInTe, , and CuInTe,. Chalcopyrites A B c2v are mentioned in papers attempting to classify and predict semiconducting behavior of intermetallic compounds; on the basis of saturated tetrahedral sp3 bonds,3 by specific selection criteria,&apos; and by crystallographic considerations."

Jan 1, 1962

By R. W. Heckel, H. W. Paxton

The growth of grain boundary films and Widmanstiitten plates of proeutectoid cementite in hypereutectoid steels ulas considered quantitatively in three plain carbon steels and one "pure" iron-carbon alloy. Growth was found to take place at a slower rate than would be predicted on the basis of a model invoking rate control by long range diffusion of carbon. The films in the pure alloy grew faster than those in the plain carbon steels. A possible explanation is suggested. In 1904, Nernsst&apos; and Brunner2 postulated that ionic crystals growing in supersaturated aqueous solutions grew at rates determined by diffusion through the solution to the growing crystal interface. The gradient down which the diffusion took place was assumed to be fixed by the supersaturated bulk solution concentration, the concentration dt the crystal surface and some arbitrary distance. The flux of material to the crystal was described as Flux where D is the diffusion coefficient, A the crystal surface area, Ci the bulk solution concentration, Co the saturated solution concentration, and 6 the thickness of the diffusion zone. It is obvious that the expression is an adaptation of F+ick&apos;s3 first law of diffusion (steady state). This was the initial formulation of what will be defined here as "diffusion controlled growth," i.e., growth limited by the long range diffusion of a component either to or from the advancing interface assuming both phases at the interface to be in equilibrium. This idea of equilibrium interface concentration implies an infinite reaction rate at the interface. Volmer, Zener,&apos; and 11schner6 have derived expressions for the diffusion controlled growth of spherical precipitates in metallic systems. These analyses agree that the growth in a given direction should be parabolic with time. Brown and Hawkes7 observed that graphite, formed both from the decomposition of cementite and from the decomposition of eutectoid austenite in cast irons, grew according to a parabolic relationship and, therefore, concluded that the laws of diffusion controlled growth, as defined above, were obeyed. They, among others, failed to consider, however, that parabolic growth is a necessary, but not sufficient, condition for diffusion controlled growth. Mehl and Dube"&apos; have pointed out that equilibrium may not be realized because the concentration at the interface cannot change instantaneously from that of the bulk to the saturation value. Furthermore, they propose that an equilibrium solute concentration in the parent phase adjacent to the precipitate would remove the thermodynamic activity gradient across the interface and, thus, stop the growth process. Frisch" has also emphasized the importance of interface concentrations that vary throughout the growth of a new phase. The variation in activity across an interface, as discussed by Onol&apos; and Cahn and Hilliard,12 is of fundamental importance to this question. Ham13 considered the data of Turnbull14 on the growth of barium sulfate in aqueous solutions. He concluded that the data could be analyzed in terms of a radiation-type boundary condition. Flux across interface = K (c, - C,) [21 where C, is the concentration in the solution at the interface, Co the saturated solution concentration, and K the proportionality constant. The edgewise growth of Widmanstlitten plates, frequently referred to as the rate of lengthening, was first considered by Zener.&apos;&apos; Basing a mathematical analysis on steady-state (constant velocity) growth he concluded that where G is the growth rate, D the solute diffusivity, Ci the concentration in the bulk, Co the equilibrium interface concentration, C, the concentration in the precipitate, a a constant, Y the radius of curvature of the edge of the plate, and rC the critical radius, i.e., the radius which would increase the activity of solute at the interface at equilibrium under the influence of capillarity to that of the bulk. Zener1&apos;

Jan 1, 1961

By K. R. Van Horn

RESIDUAL stresses in metals operate under a cloak of mystery, as they have neither been seen in the laboratory nor detected by means of the microscope. In spite of their phantom-like nature, they frequently exert metallurgical effects that cannot be ignored. In some cases the results have been detrimental, causing rejections or premature failures, but frequently the effects have been highly beneficial to the producer or consumer of metal products. First, however, what is a residual stress? When a metal is plastically deformed by bending, rolling, pressing, or by a phase transformation or precipitation from solid solution, or by a sharp temperature gradient resulting from nonuniform cooling, quenching, or welding, it remains in a state of strain. The strains or strain gradients produced by such operations and retained after all external forces are released are known as residual strains, and the accompanying stresses as internal or residual stresses. Many defects or failures in metal products have been ascribed to residual stresses, sometimes erroneously, because there was no other apparent explanation after the usual metallurgical tools of diagnosis had been applied. For example, during World War 11, the forged aluminum alloy aircraft cylinder head in the reciprocating engine began to replace the cast head with the familiar cooling fins. The fins were machined in the solid forged head by an ingenious milling operation. One plant reported an epidemic of excessive distortion during the delicate high-speed milling. A thorough examination revealed that the composition, heat treatment, mechanical properties, and metallurgical quality of these heads were comparable to those of forgings that machined satisfactorily. It was then claimed that the cause of the machining difficulties was connected with residual stresses resulting from the quenching during the solution heat treatment. An elaborate stress analysis actually demonstrated, however, that the magnitude of residual cooling stresses was lower in the cylinder heads which machined poorly than in those which were satisfactory in this respect. Subsequent tests proved that the machining problems in this case originated from variations in the tools and tool design. Sources of Residual Stresses in Metals Residual stresses are of two origins—mechanical and thermal. Thus, stresses may be produced in a metal by any cold-working process. The distribution and magnitude of these mechanically produced stresses can be calculated in a satisfactory, although approximate, manner for such simple cases as bending, torsion, and expanding of tubes. However, most manufacturing processes are too complex, and the original stress-strain relations in the products are not sufficiently known to permit calculation of the resulting residual stresses. Also, a specific process, such as wire drawing, may vary in complexity or uniformity of working, and large or small residual stresses may result, depending on the conformation of the dies and other features of the working process. Neither substantially unidirectional deformation, such as can be imparted by stretching a metal product having essentially the same mechanical properties throughout the cross section, nor deformation

Jan 1, 1954

By B. H. Kear

All the possible ways of forming simple two-dislocation boundaries in multiple slip orientations are deduced. It is shown that the principal differences in work hardening behavior of crystals plastically deformed in these orientations can he accounted for in terms of the likelihood of formation of diffuse boundaries, or deformation bands, consisting of the products of dislocation reactions of the Lomer type. Also, it is pointed out that the break-up of boundaries under the applied stress is more likely to yield interstitial jogs than vacancy jogs, whereas glide dislocations cutting throuqh dislocations trapped in particularly stable boundam&apos;es can acquire both types of jogs. USING Frank&apos;s&apos; grain boundary formula, Ball and Hirsch2 determined the parameters of all the possible boundaries that can be built from two sets of glide dislocations in the fee structure. This paper deduces the geometrical possibilities for the formation of these two-dislocation boundaries in the different multiple slip orientations, and discusses the role of boundaries in work hardening and in jog formation. Formation of Two-Dislocation Boundaries in Mutiple Slip Orientations. The parameters of the possible two-dislocation boundaries for any crystal orientation can be deduced most conveniently using the boundary formulae due to Amelinckx,3 in conjunction with the stereographic projection shown in Fig. 1. Suppose that slip occurs in a-BC and ß-CA. According to Amelinckx, when the two systems of glide dislocations are parallel, the rotation axis, u, of the boundary is parallel to (a x ß) and the unit normal, u, defining the boundary plane is parallel to (a x ß) x (BC x CA). On the other hand, when the glide dislocations form a crossed grid, u is parallel to (BC x CA) and u is parallel to (a x CA) x (ß x BC). In Fig. 1, (a x ß) is the pole of the great circle passing through a and ß, so that u is parallel to DC, i.e., parallel to [110]. Furthermore, (a x ß) x (BC x CA) is the pole of the great circle passing through DC and 6, so that u is parallel to [110]. Hence, when all the glide dislocations are parallel, the boundary is pure tilt with parameters u = [110], v = [ 110]. Similarly, it may be shown that the corresponding crossed grid of dislocations is a mixed boundary with u = [111], u = [111]. Consider the case of a crystal compressed in the [001] orientation. In this orientation, according to Fig. 1, there are eight available slip systems. In what follows, the different types of two-dislocation boundaries that are possible in this orientation will be examined by taking different combinations of two slip systems out of the available eight, with a-BC always one of the systems. Case (i)—Slip Systems a-BC and d-CB. The formation of a tilt boundary in (101), which consists of a crossed grid of edge dislocations with vectors BC andCB, is illustrated in Fig. 2(a). As the figure shows, slip is required in the system a-BC in one part of the crystal and in d-CB in the other part, with both sets of dislocations entering the boundary from opposite sides. The rotation axis of the boundary lies in (101), depending on the relative densities of the two sets of edge dislocations in the boundary. Case (ii)-Slip Systems a-BC and ß-CA. The two possible boundaries are shown in Figs. 2(b) and (c); boundary (b) is tilt with u = [110], u = [110], and

Jan 1, 1962

By Hsun Hu, R. S. Cline

A detailed studj) of texture formation in 2 pet Al-Fe single crystals with initial orientations of approximately (111) [112], (112) [111], and (112) [111] was made by examining the textures developed on the surface and at various interior sections of the crystal after rolling to various amounts. Depending&apos; upon the initial orientation of the crystal, the surface and interior textures may differ only in sharpness, or may differ essentially in orientation. The orientation of the (111) [112] crystal does not change upon rolling up to 70 pet, but after rolling more than 90 pet a distinct component of (001) (110] orientation is developed. The texture formed in the two (112) (1111 type crystals consists of (111) (1121 and (001) (1101 components. The latter, however, is largely confined to the surface layers. The textures formed on both sides of the crystal are identical, and the texture composition profile is approximately symmetrical with respect to the central section of the strip thickness. The formation of these texture components is analyzed. DURING the past seven or eight years, deformation and recrystallization textures in rolled Si-Fe single crystals have been extensively studied by various investigators.1-7 From these studies, much knowledge on texture formation in bee crystals of various initial orientations was obtained. However, these results also raised many questions, regarding particularly the correlation between deformation and recrystallization textures, as well as the deformation texture itself of some particular crystals. To take a (111) [112] type crystal as an example, it was shown by Dunn and Koh2, 3 that this orientation does not change during deformation by rolling. This finding is consistent with the conclusion reached by Barrett and Leven-son8 with respect to iron crystals that (111) [112] is one of the stable end orientations. However, different recrystallization textures were observed by Dunn and Koh3 in (111) [112] type crystals of different initial thickness, which widened differently during rolling even though their deformation textures were identical. Another interesting example, also from the results of Dunn and Koh2&apos;3 is that of texture formation in a (112) [111] crystal. This crystal developed a two-component deformation texture of (111) [112] plus (001) [110]. Its recrystallization texture, however, was found to be predominantly (110) [001], which is related to the (111) [112] component by a simple [110] rotation. This crystal, therefore, behaved as if the other deformation texture component, (001) [110], were not present. There are also discrepancies among the results of different investigators, as well as numerous unexplained fine features of the deformation texture of crystals of various initial orientations. In order to have a better understanding of all of these points, a detailed study of deformation textures is greatly needed. One of the obvious things that has been completely overlooked in previous texture studies is the possible effect of surface texture. All past work on the texture of Si-Fe single crystals was conducted in a rather simple manner, i.e., the rolled crystals were etched to a very thin sheet; then their textures were examined by transmission X-ray techniques. For recrystallization texture studies, unless precautions are taken by etching off a sufficient amount of the surface layer before annealing, the texture developed in the interior may be affected by the surface layer, which may well have a different initial texture and which may have undergone recrystallization earlier than the interior of the specimen. Because of this effect, it is now planned to reexamine the texture of various rolled and annealed single crystals at the surface, and at various sections below the surface by using reflection techniques. In some cases, both surfaces of the rolled crystal will be examined. In one of Dunn&apos;s early papers,9 he noted that at an early stage of rolling the crystal seems to divide roughly through the middle to become a sample which in effect consists of two layers having some what different orientations. This effect has never been further explored. The investigation described in the present paper constitutes the beginning of a series of thorough investigations of texture formation in deformed bee single crystals designed to clear up some of the uncertainties which have been discussed. We have chosen a high-purity 2 pet Al-Fe alloy for this investigation. It is known that the allotropic transformation of iron is eliminated by alloying with approximately 1petAl. Such an alloy, being very similar to silicon ferrite, can be heated to the solidus temperature without phase transformation. One reason for choosing A1-Fe instead of Si-Fe for the present investigation is that we have been able to make single crystals of a vacuum-melted high-purity A1-Fe alloy by the strain-anneal method without much difficulty, but were not successful in doing so with a vacuum-melted high-purity Si-Fe alloy. For many research purposes,

Jan 1, 1962

By P. R. Sperry, P. A. Beck, Hsun Hu

As described by means of quantitative pole figures, the inside texture of highly rolled aluminum and copper strips may be approximately described by four equivalent ideal orientations near (123) [121]. If rolled in reversed passes, the surface texture of copper is also near (123) [121], that of aluminum is (100) [011]. The inside texture of highly rolled brass is (110) [112]. The surface texture is the same, if rolled in reversed passes. The surface texture of all three metals is related to the inside texture, but asymmetrical, if rolled without reversal between passes. MANY previous investigations dealing with the subject of the present work were reviewed by Wassermann.1 Barrett,2 Brick,3 and Richards.&apos; The recent introduction of quantitative methods for pole figure determination by Decker, Asp, and Harker,5 Schulz5 and others made it possible to reinvestigate some of the finer points which the earlier more qualitative photographic methods left undecided. The rolling textures of silver and of 70-30 cartridge brass have been quite consistently characterized by the ideal orientation of (110) parallel to the plane of rolling and [112] parallel to the rolling direction. On the other hand, it has been recognized by several investigators that certain other face-centered cubic metals, such as copper and aluminum, developed rolling textures rather different from that of brass. These textures have been variously described by the following ideal orientations, singly or in combinations with each other: (110 [112]: (112) [111]; (135) [335]; (135) [211], etc. The discrepancies usually have been attributed to the lack of sharpness in the textures and to the attendant difficulty of associating "ideal orientations" with pole figures showing great scatter of orientations. It seemed desirable to investigate by the new quantitative methods to what extent the apparent lack of sharpness may have been brought about by the qualitative methods used previously, rather than by the textures themselves, and to decide, if possible. between the various ideal orientations which have been proposed. Another problem, not satisfactorily settled by earlier investigations. concerns surface textures in rolled metals. For instance, in rolled aluminum the surface texture in some cases appeared to be similar to the texture inside the sheet, whereas in other cases it was reported to be entirely different.&apos; The conditions under which such differences may have arisen, and the possibility of the occurrence of different surface textures in other face-centered cubic metals do not appear to have been examined in detail. The present work was undertaken to investigate the above questions. Some of the results obtained have been described- riefly. Experimental Procedure Specimen Preparation: In the present investigation 2s aluminum, electrolytic tough-pitch copper, and commercial 70-30 brass were used. These materials were available in the form of cold-drawn rods. 1 in. diam for tough-pitch copper and commercial 70-30 brass and 11/2 in. diam for 2s aluminum. The cold-drawn bars were alternately annealed and rolled 30 pct lengthwise in several cycles until a penultimate thickness of 0.500 in. was reached. The intermediate and the penultimate anneals were carried out for 30 min at 380°C with 2s aluminum, and for 30 min at 550°C with 70-30 brass. For tough-pitch copper, the intermediate anneals were 30 min

Jan 1, 1953

By W. A. Wood, W. H. Reimann

A study is made of the creep that can be induced in armco iron at room temperature by superposing small amplitudes of alternating torsion on a tensile creep load. It is shown that the creep differs from that in comparable tests on copper in being trmsient only. At the same time, though transient, the creep can produce extensions of some 10 pct under creep loads less than the tensile yield stress of the material. The creep can be largely suppressed b$ applying cyclic strain of suitable amplitude before applying the creep load and the metal thereby stabilized. At room temperature, plastic flow in a metal under steady load is normally limited by strain-hardening processes. However, if a small cyclic stress is superposed on the steady load these processes may be more or less neutralized and, as shown in recent investigations,&apos;-4 plastic flow may continue. In this way annealed copper, for example, can be induced to creep continuously to fracture under loads as small as 1 tsi. Dislocation mechanisms possibly responsible for this room-temperature creep have been usefully reviewed by Feltner.But discussion so far has been based mainly on creep as it is found in close-packed metals initially in the annealed state, and their behavior may not be general. In fact, recent work shows that the form of creep in annealed copper is different from that even in cold-worked copper;7 the creep thus depends on the dislocation pattern already in a metal as well as on the metal itself. This paper describes the creep in annealed armco iron, tested in the same way as the above-mentioned copper. One object was to see how creep in a typical bcc metal compared with that in the annealed close-packed metals. Another object was to utilize the fact that a bcc metal like iron has a more pronounced elastic range than close-packed metals like copper and to find to what extent the creep load or superposed cyclic stress had to exceed their re-

Jan 1, 1964