By Denis Tepavac, Mark Trim

Structural performance of fiber reinforced concrete (FRC) depends on its ability to carry tensile forces after cracking. Australian Standards AS5100-2017 and AS3600-2018 are the only available design standards that establish a test procedure to determine strength and toughness of an FRC in direct tension. Direct tensile testing of fiber reinforced shotcrete samples was performed to determine if the model and guidelines in AS5100/3600 were applicable to shotcrete; all previous testing was from cast samples. In addition to direct testing, micro CT-scanning was also performed. The paper presents tests performed, results, and how the tests could be used on future projects. In addition, a brief summary is provided of the guiding structural mechanics used for estimating residual tensile strength and test methods utilized to verify those estimates.

Jun 13, 2023

By J. D. Miller, C. L. Lin

Liberation of valuable minerals during size reduction is an important aspect of mineral processing technology. In practice, most quantitative information on liberation is based on the application of stereological theorems for the analysis of image data from two-dimensional polished sections. On this basis an estimate of the volumetric grade distribution is made. Recently, a new method based on cone-beam xray microtomography has been used for direct determination of the three-dimensional liberation spectrum of multiphase particles 100 microns in size or less. Preliminary results for a packed bed of particles indicate that high spatial resolution (approximately 15 microns) and the direct processing of raw volumetric data are two important benefits offered by this new method. Three dimensional liberation analysis by microtomography provides an excellent opportunity to overcome many of the limitations of currently used polished section techniques. For example, detailed textural information is provided. Of course microtomography provides an independent method to verify current procedures used for analysis and transformation of polished section data into an estimate of the volumetric grade distribution. More important, however, is the possibility that this method could be developed as a routine procedure for liberation analysis in the 21st century.

Jan 1, 1997

By F. Qi, T. Frišcic, C. Mottillo

"One of the principal goals of modern industry is to minimize the environmental impact and increase the materials- and energy-efficiency of transforming raw materials into valuable products. This paper will highlight our latest laboratory-scale research in low-energy, low-solvent reactivity of metal oxides and their conversion into popular metal-organic frameworks (MOFs), zeolitic imidazolate frameworks (e.g. Basolite® Z1200 component ZIF-8), and metallodrugs (e.g. bismuth subsalicylate, active component of Pepto-Bismol®). Mechanochemical ion- and liquid-assisted grinding (ILAG) and ""accelerated aging"" techniques will be presented, along with novel low-energy and solvent-free approaches, inspired by geological weathering processes, for converting metal oxides into metal-organic materials. INTRODUCTIONThe development of environmentally-friendly processes, which would in the same time be more materials- and energy-efficient than the existing ones, is one of the central concerns of modern chemical research. In that sense, the focus of the chemist has been mainly on the preparation of carbon-based organic molecules and adaptation of traditional organic synthesis to the recently delineated ideals of Green Chemistry. However, there is a growing realization within the chemistry community that significant energy, materials, and ecology-related benefits can be achieved and, indeed, targeted in the transformations of materials that are typically associated with inorganic chemistry and minerals processing. The principal aim of this highlight contribution is to illustrate how, through the use of approaches associated with solventfree chemistry and mechanochemistry (James et al., 2012), one can develop a clean and efficient system of chemical and materials transformations involving oxide precursors that normally belong to the realm of inorganic chemistry and mineral processing. In particular, this contribution will provide an overview of the recently developed mechanochemical and solvent-free reactivity of metal oxides towards small organic molecules. These mechanochemical reactions, including the methods of liquid-assisted grinding (LAG, Frišcic & Jones, 2009) and ion- and liquid-assisted grinding (ILAG, Frišcic, 2010), have so far provided a radically different means to construct advanced metal-organic materials (e.g. porous metal-organic frameworks, [MOFs] or metallodrugs) by rehabilitating metal oxides as precursors, eliminating the use of bulk organic solvents, and avoiding the use of high temperatures."

Jan 1, 2012

By O. Babak, O. Leuangthong, M. A. Cuba

Integration of data from multiple sources and/or multiple scales is a common, yet challenging aspect of geostatistical resource modeling. Common approaches to data integration are based on a cokriging framework that assumes a consistency of scale in the information that leads to a requirement to composite the data prior to model construction. It is well known that the geostatistical model parameters are scale dependent. In particular, the volume variance of integrating these various scales has a direct impact on the semivariogram that should be used in model construction and/or the assessment of volume-variance relations as it affects resource estimation. This paper reviews and compares two different approaches for semivariogram upscaling. The first approach is the scaling laws. It is an empirically derived approach, involving several simplifying assumptions, one of which is a strict assumption of invariance of the semivariogram shape. The second approach is a theoretically derived direct upscaling of the semivariogram. This approach has been around for a number of years, but is seldom implemented due to software limitations. In this paper, we present a numerical integration approach to facilitate direct semivariogram upscaling. The advantage of direct upscaling over the scaling laws approach is shown by considering a synthetic example and a case study. Further, in the case of multiple codependent random variables, the extension of the direct semivariogram upscaling to the cross semivariograms is derived and an upscaled consistent linear model of coregionalization is presented.

Jan 1, 2013

By J. G. Peacey, P. Hancock, R. -Q. Li

A pyrometallurgical process for the direct recovery of zinc from zinc concentrates and zinc/iron residues has been proposed and tested extensively by Noranda. The process consists of smelting bone-dry zinc containing materials (sulfide concentrates and secondary zinc/iron materials) in a molten iron oxysulfide bath to volatilize metallic zinc into a SC^-free offgas. Sulfur contained in the feed materials is fixed as an iron oxysulfide matte for disposal. Thus, this process not only is capable of treating zinc sulfide concentrates and secondary zinc materials simultaneously, but also eliminates the need of sulfuric acid production. Detailed thermodynamic analysis and experimental test work are described in this paper.

Jan 1, 2000

By W. G. Davenport

Smelting oxidizes Cu-Fe-S concentrate to matte. Converting oxidizes this matte to metallic copper. Smelting and converting are, therefore, part of the same oxidation process. It would seem natural, then, that smelting and converting should be combined to produce metallic copper in one step. This would: (a) maximize S02 capture by restricting S02 emission to a single, continuous source (b) minimize industrial oxygen and fuel requirements (c) minimize cost. This chapter discusses one step, direct-to-copper flash smelting as it is practiced in 2000. It then uses. the matrices of this book to determine: (a) the industrial oxygen and oil requirements of direct-to copper flash smelting (b) the distribution of Cu between metal and slag during direct-to-copper flash smelting. It concludes that direct-to-copper flash smelting: (a) captures?S02 efficiently from its single continuous stream of SO2 off gas (b) minimizes oxygen/oil consumption but: (c) sends -114 of its Cu-in-feed to slag.

Jan 1, 2001

By C. H. Mathewson

COPPER and the copper-base solid solutions readily form twin crystals when plastically deformed at a suitably elevated temperature or annealed after cold deformation. In fact, no feature of the microstructure of these materials is more prominent or characteristic than these straight-sided bands or simple lines of division which sometimes come from groups of thin polysynthetic lamellae, penetrating part way or wholly through the parent grain substance, but often divide the grain into a few or perhaps only two crystallographically related parts. Nearly always the bands as seen in the usual microscopic examination of a specimen come into vivid contrast with the adjacent crystalline material owing to the inherent difference in orientation. Bands which under special conditions of orientation cannot be seen with vertically incident light are often visible under oblique illumination and, when this fails, contrasting effects usually may be obtained by using polarized light. There is no longer any doubt that these synthetic banded structures obtained in the ordinary course of working and annealing are due to twinning of the spinel type which was observed long ago in a number of metals crystallizing in the isometric system.1 It has been customary in metallurgical literature to designate these synthetic twins, which grow into prominence during an annealing process, as "annealing twins" without regard to the actual mode of their formation, which is, indeed, obscure and with scant recognition of the fact that prior deformation is essential, no twins having been observed in metal of known unstrained history. This is questionable; especially in view of. the fact that in a number of metals and minerals, reorientation into the twin configuration is known to occur as a result of a simple shearing mechanism along the recognized twinning planes and the

Jan 1, 1930

By J. E. Urosek

Decisions made during a response to a mine fire or an explosion greatly affect the final outcome. The safety of miners should be the primary concern with accounting for all of the miners the first issue for resolution. If miners have not safely evacuated from the mine, the last known location of the miners at the time of the event and anticipated travel routes are primary exploration areas. After the mine is evacuated, there are many very important decisions that must be made quickly and often under great stress. It is critical that the mine operator establish an orderly method to direct the mine emergency response. Designation of a Command Center, staffed with personnel charged with developing plans, is a common method of establishing control. Scheduling of key mine managers will be critical, since decisions must be made 24 hours a day and people working for extended periods with little or no sleep do not always make clear or cognizant decisions. Internal communications, passing information on to subsequent shifts, and external communications with families and media must be accurate and timely. Assembling resources for responding to the mine emergency is critical for an effective response, and pre-planning can pave the way to a successful recovery. Sampling mine gasses and accurately determining the composition of gas mixtures is a common tool used to develop response plans in all fires and explosions. It is essential that preparations for emergency situations are made well in advance of a disaster. Effective communications are essential for mine management to successfully respond to a mine emergency. This paper discusses some considerations which need to be addressed in directing a response to a mine fire or explosion.

Jan 1, 2009

By Zoltan Susanszky

Technical development in blasting requires improvement of industrial explosion techniques in two fields. One is to apply increasingly exact and economical solutions with more effective explosives, the other is to restrict as much as possible the environmental effect of explosions.

Jan 1, 1978

By W Z. Liu, Q Q. Shi, H T. Yang, X L. Zhang

In order to improve the cutting blasting effect of dimension stone mining, the water coupling directional cutting blasting technology was put forward. Based on the test apparatus and special charge configuration, the mechanism of directional cutting blasting was analysed. Directional device changes the initial equilibrium of the total energy of shock wave effect on blasthole wall. The initial directional crack first appears in the blasthole wall that makes contact with the directional device. Then, two cracks are connected along the direction of the blasthole centre line under the action of detonation pressure and water wedge. The plexiglass tests showed that water coupling directional cutting blasting technology produced cracks along with the predetermined direction completely. The cutting surface was smooth and only a few short cracks appeared around the blastholes. It proved the validity of this technology.CITATION:Liu, W Z, Zhang, X L, Yang, H T and Shi, Q Q, 2015. Directional blasting rock cutting technology, in Proceedings 11th International Symposium on Rock Fragmentation by Blasting, pp 815–818 (The Australasian Institute of Mining and Metallurgy: Melbourne).

Aug 24, 2015

By NARAYAN K. BHAGAT, ARVIND K. MISHRA, Aditya Rana, M. M. Singh

The paper presents an innovative directional controlled blasting (DCB) technique for excavating unstable slopes along the Konkan railway in India without disturbing the traffic. New empirical formulae for small geometry blasting to estimate burden and throw were developed. A unique sequence of firing and excavation with powder factor varying between 0.04 and 0.39 kg/m3, irrespective of the actual free face, was used for rock blasting. The process controlled the throw of blasted material over the track and resulted in a smooth and stable wall. The slope angle was changed from 80–82 to 45–47 degrees, and possible wedge, planar and toppling failures were eliminated. No incident of rockfall and slope failure along these slopes has been observed after the stabilization.

By Viktor Tokle, C. W. Dawson

The Devico directional core drilling system and its capabilities are described, with reference to other directional drilling technologies and the advantages and disadvantages of these systems. The advantages and disadvantages of a number of borehole navigation systems are also presented. A discussion of the applications of the technology follows, illustrated by case histories. Finally, the environmental impacts and benefits of the technology, in comparison to more conventional systems, are presented.

Jan 1, 1999

In recent years the use of directional drilling has become increasingly popular in several applications. These include shaft pilot holes, exploration drilling, mine service holes and drilling beneath surface structures and obstacles. The prime objectives are to increase accuracy and reduce time, cost and environmental disturbance.

Jan 1, 1992

By Calvin J. Konya

Many controversies and differences of opinion exist in blasting technology. The primer location in small diameter dynamite columns is an example of one of these controversial areas. It is generally agreed that in rotation firing of small diameter blastholes, primer placement near the bottom of the borehole is beneficial since it reduces the likelihood of cutoffs. The controversy results in the actual location of the primer in the bottom of the blasthole. Some references indicate that the primer cartridge should be the first cartridge in the bottom of the hole, with the cap pointed toward the collar of the hole. Others indicate that performance is improved with no sacrifice in safety by placing a tamped cartridge first in the hole, and the second cartridge being the primer. The following investigation provides some factual data for consideration.

Jan 1, 1980

By Yi Tan, Kazuki Morita, Yaqiong Li

Molten Si-Al alloy, with the addition of Sn, was used for metallurgical grade Si purification by a low-temperature solidification method, with the aim of improving the recovery rate of Si. In this ternary melt, bulk Si was grown with a planar front by a directional solidification process under a well-controlled thermal gradient and growth rate conditions, thereby reducing the contamination of solvent metals. Effects of cooling rate, amount of Sn addition, and temperature gradient on the quality of bulk Si were determined. The criterion for constitutional supercooling for single-phase growth from multicomponent melts was employed to evaluate the growth process.

Jan 1, 2015

By Arthur Phillips

THE study of anisotropy in metals has been greatly stimulated in recent years by the rapid development of X-ray methods for determining the crystallographic relationships of wrought and annealed materials. Prior to this time the knowledge regarding the directional properties of commercial alloys consisted almost exclusively of observations of a practical nature made during the fabrication of metal objects, supplemented by a limited number of mechanical tests on specimens cut at various angles to the direction of working. Such observations clearly indicate that the common methods of cold-working metals cause both a crystallographic and a mechanical fibering varying in character and degree according to the nature and extent of the deforming process. Even after annealing, following certain not too well known combinations of reductions and anneals, a preferred orientation may exist, thereby constituting a residual fiber effect sufficiently pronounced to manifest directional properties. With the application of the X-ray the experimental horizon was extended chiefly because the study of anisotropic metals promised to offer direct and quantitative evidence regarding the involved mechanism of fragmentation and plastic flow. As a natural consequence the intensive studies in this direction have yielded a vast accumulation of data of ultimate potential value. Unfortunately, however, as is commonly the case in entering a virgin field of experimentation, many of the data cannot be molded into complete and coherent form because of the many unrelated conditions of the experimental projects. Again, the results of the study of single crystals have been rather naturally but at times indiscriminately applied to polycrystalline metals. Furthermore, sweeping statements have been made regarding the behavior during working and annealing of metals and alloys, entirely on the basis of similarity in lattice arrangement. There is abundant reason for believing that relatively small concentration variables, differences, in magnitude and distribution of applied stresses, and the character of associated annealing treatments may in some cases greatly influence the mechanics of flow and consequently largely determine the final structural characteristics of the metal.

Jan 1, 1932

By Arthur Phillips

DURING the past few years considerable interest has been shown in the study of fiber, and its effect, in wrought metals. Fiber has recently been defined as a "condition of parallelism of important lines or details in the structure. "1 Briefly stated, two distinct types of fiber are commonly encountered. One results from the alignment in the direction of working of constituents, more or less segregated, such as slag, oxides, carbides and dendritic formations. The second, and least understood, type is produced by working the metal below the recrystallization temperature in such a way as to develop a parallelism of the grains. This condition is readily recognized by the pronounced elongation of the grains in the direction of working. Under certain deformational treatments the grain fragments produced by cold working tend to orient in certain definite directions with respect to the axis of extension. Furthermore, even in metals that have been annealed after cold working preferred orientations may be present. It is perhaps logical to assume that such marked parallelism of structural elements would be manifested by directional properties in the metal. As a matter of fact, tests on many kinds of materials have shown differences in varying degrees. In recognition of this condition, propel design, for many purposes, places the fiber axis in such a way as to present the direction of maximum strength to the greatest applied stress.

Jan 1, 1931

By E. C. Bohlen, H. l. Burghoff

THE work reported in this paper was carried out to supplement the existing information concerning directional properties and recrystallization textures of annealed brass sheet and strip. These characteristics are of direct interest when the forming and drawing properties of such material are being considered. Among those who have made contributions in this field are Bass and Glocker;1 Bauer, Göler and Sachs;2 Phillips and Samans;3 Pratt;4 Price;5 Cook;6 Richards;7 Brick;8 and Brick and Williamson.9 These investigators have found, in general, that in brass strip that shows directional variations in properties, tensile strength has a minimum value and elongation has a maximum value at 45° to the rolling direction. The most pronounced directional properties have been found in material given the greatest reductions in rolling followed by high annealing temperatures. Recrystallization texture of brass has been variously reported as (113)[112], (001)[100], and a combination of (110)[115] and traces of the primary rolling texture, (110)[112]. The directional studies have been very informative, but actual tests appear to have been confined to material in its final condition. Tests at intermediate stages have received little attention although previous history of some materials has been partly considered. Perhaps the most comprehensive investigation was made by Cook,6 who studied the directional properties of 70-30 brass strip for which the final and penultimate, or next to the last, anneals and the final reductions were varied. He found that, for any given combination of penultimate anneal and final reduction, the tendency toward the development of directional properties was reduced as the temperature of the final anneal was decreased. In addition to drawing cups and making tensile tests of the finished material at various angles to the rolling direction, he measured the frequency and the angles of twins in grains for several specimens. Plots of his twin counts showed directionality for the materials that produced eared cups. TEST MATERIALS AND EQUIPMENT For this investigation, one commercial heat of 68-32 brass was cast in the form of bars for cold-rolling, 13 ½ in. wide and 1 ½ in. thick. The analysis was as follows: 68.83 per cent copper, 0.04 per cent lead, 0.01 per cent iron, 31.12 per cent zinc (by difference). The bars were so processed to the final thickness, 0.020 in., as to obtain on this thickness all possible combinations of the variables listed below except those involving the sequence of 84 per cent penultimate reduction and 84 per cent final reduction: I. Penultimate reductions of 37 per cent, 50 per cent and 84 per cent; 2. Penultimate anneals at 800°, 900°, 1050° and 1200°F.; 3. Final reductions of 37 per cent, 50 per cent, 69 per cent and 84 per cent;

Jan 1, 1942

By C. A. Komar

Renewed interest in the underground gasification of coal evolves from comprehensive studies of earth fracture systems that indicate that the movement of fluids can be controlled in the coalbed. In particular, directional property studies of natural microfissure occurrence, permeability, ultrasonic velocity, tensile strength, and orientation of intervals of inherent rock weakness, together with geologic structure setting and fracture trace analysis, can predict the gaseous flow paths in the coalbed. Having this information, the dominant direction in which gases generated and/or liberated by heat would move can be determined so that appropriate well patterns can be developed. Together with advances made in drilling technology that permit long horizontal holes to be drilled through the coal seams, tests can be conducted to determine whether directional control will permit devolatilization of the coalbed and gasification of the remaining hot coke in a systematic manner to produce a low-Btu gas suited for the generation of electricity.

Jan 1, 1973

By Michael Alber

Pullout tests on resin grouted rock bolts have been executed in coal mines and surface test sites. The goal of this study was to provide some qualitative information about the rock mass quality from mandatory tests with a bit little more effort. Movements of rock bolt head and steel plate at different load levels were analyzed and were found to yield information about the rock mass deformability. The tests were interpreted similar to plate bearing tests and a rock mass compressibility index C was assigned. This index reflects the complex interactions between the rock mass, resin grout and bolt under load. Although further research is necessary it may be concluded that those tests may aid in recognizing geological conditions.

Jan 1, 2003