By A. G. Doll

The Bond low energy impact (crushing) work index test is specified to be performed on rock specimens between 50 mm and 75 mm in effective diameter. NQ-diameter drill core, frequently used in mineral exploration programs does not meet that specification, it being 45 mm diameter or less. This paper reports the effect of performing the impact test on contiguous sections of HQ diameter and NQ diameter core, exploring the hypothesis that the contiguous intervals give equivalent results in spite of the core diameter difference.

Jan 1, 2012

By R. Phillips, A. G. Doll, D. J. Barratt

"The Bond low energy impact (crushing) work index test is specified to be performed on rock specimens between 50 mm and 75 mm in effective diameter. NQ-diameter drill core, frequently used in mineral exploration programs does not meet that specification, it being 45 mm diameter or less.This paper reports the effect of performing the impact test on contiguous sections of HQ diameter and NQ diameter core, exploring the hypothesis that the contiguous intervals give equivalent results in spite of the core diameter difference."

Jan 1, 2012

By HASSAN E. EL-SHALL, AYMAN A. EL-MIDANY, KERRI-ANN A. HUE

Modifying the hydrophobicity of clay is necessary to accommodate large mycotoxin molecules such as zearalenone (ZEN). In this study, tricaprylmethylammonium (TCMA) chloride and common corn oil were used to modify clay. The results indicate that more than 90 percent of ZEN could be removed using clays modified by TCMA and corn oil at acidic and neutral pH due to the expansion of intergallery spacing as a result of TCMA surfactant intercalation within the clay-forming layers. The removal percentage depends on the pH and amount of clay used. Complete removal can be achieved at acidic pH and small clay amount.

By Ayman A. El‑Midany, Hassan E. El‑Shall, Kerri‑Ann A. Hue

Modification of clays is necessary for the zearalenone (ZEN), as long-chain mycotoxins, removal. The organic-cations were usually used to modify the clay hydrophobicity to accommodate the large mycotoxin molecules. In this study, tri capryl methylammonium (TCMA) chloride and common corn oil were used in clay modification. Several characterization techniques such as XRD, FTIR, and TGA were used to identify the d-spacing changes after modification either by TCMA or corn oil. The results of applying the TCMA-corn oil-modified clays in ZEN removal indicated a noticeable improvement where more than 90% of ZEN could be removed in vitro at acidic and neutral pH values. The success of eliminating a high percentage of ZEN molecules is due to the expansion of intergallery spacing as a result of TCMA surfactant intercalation within the clayforming layers. The removal percentage does not depend only on pH but also on the amount of clay used. In addition, the ZEN removal in the presence of corn oil is better at acidic pH and small clay amount where the ZEN can be fully removed.

Sep 27, 2021

By Satyajeet Ghosh, Edward F. Glynn

Many of the proposed techniques for calculating the reliability of rock slopes utilize Monte Carlo simulation. Monte Carlo approaches are attractive because they provide means of solving probabilistic problems with deterministic algorithms. One disadvantage shared by all simulation-based stability analyses is that they assume all the random variables are independently distributed. The paper focuses on the independence assumption and examines the effect of correlation on the probability of failure. In particular it considers the influence of possible (albeit hypothetical) correlation between joint attitudes [(8)] and joint friction angles [($)]. The study indicates that neglecting correlation can introduce significant errors into the reliability computations. With a modest positive correlation between [8] and [$] the error can lead to a 100% overestimate of the probability of failure.

Jan 1, 1982

By Zhan Zhang, Hiromi Nagaumi, Zhen Li

"Recently, the remarkable strengthening effect of ??-Al(Mn, Fe) Si dispersoids at both ambient temperature and elevated temperature were found by several researches. A large amount of dispersoids can be formed by applying special heat treatments and within a suitable range of chemical composition of AA3xxx alloys. In the present work, the influences of Cr addition on the mechanical properties and microstructures of the Al-Mn-Mg-Si alloys were investigated. The mechanical properties at ambient and elevated temperatures were evaluated by micro-hardness and yield strength. Moreover, the microstructures in as-cast and heat-treated conditions were quantitatively analyzed by optical and electron microscopes. Results revealed that Cr also had effect on the number density and volume fraction of dispersoids. Micro-hardness and yield strength at ambient temperature increased with the increasing content of Cr, and the Cr addition increased the yield strength at elevated temperature as well. Moreover, the creep resistance at 300°C improved dramatically with the increasing content of Cr.INTRODUCTION Traditionally, AA3xxx aluminum alloys were widely used in packaging, automobile and architecture industries, because of its good formability, excellent corrosion resistance and weldability. And AA3xxx alloys were considered as non-heat-treatable alloys. However, the strengthening effect of dispersoids in AA3xxx alloys was discovered recently (Li & Arnberg, 2003;Li, Muggerud, Olsen, & Furu, 2012; Li, Zhang, & Chen, 2016; Liu & Chen, 2015).Alarge amount of dispersoids could precipitate by a proper heat treatment.In order to further improve AA3xxxalloys, the composition of the alloys should be optimized. A few previous studies were reported to investigate the influence of compositions on AA3xxx alloys. Adding Mn element could enhance the precipitation of ??-Al(Mn, Fe)Si dispersoids and improve the yield strength(Muggerud, Mørtsell, Li, & Holmestad, 2013), as long as the concentration of Mn was under the solid solution limit. Fe decreased the solubility of Mn and accelerated the precipitation rate of ??-Al(Mn, Fe)Sidispersoids(Li & Arnberg, 2003), the yield strength and creep resistance at elevated temperature could increase with an optimized content of Fe(Liu & Chen, 2016). Mg element would affect the nucleation process of ??-Al(Mn, Fe)Sidispersoids by forming metastable Mg2Si(Hirasawa, 1975; Li, Zhang, & Chen, 2017a; Lodgaard & Ryum, 2000), metastable Mg2Si precipitated during heating process and promoted the precipitation of ??-Al(Mn, Fe)Sidispersoids, moreover, Mg provided solid solution strength for AA3004 alloys(Li et al., 2016). Si increased the volume fractionof ??-Al(Mn, Fe)Sidispersoids(Muggerud et al., 2013)and decreased the size of ??-Al(Mn, Fe)Sidispersoids(Li, Zhang, & Chen, 2017b). With the addition of Mo, the size of dispersoids became finer with a higher volume fraction, the volume percentage of dispersoid free zones was reduced. Elevated temperature yield strength and creep resistance improved due to Mo addition (Liu, Ma, & Chen, 2017).However, the effect of Crelements on microstructure and mechanical properties of AA3xxx alloys were rarely reported."

Jan 1, 2018

By Jian Li, J. Miles, P. Liu, W. Cook, W. Zheng, Alvin Qian

"High temperature corrosion resistance is one of the key challenges in water-cooled nuclear reactor material development. Iron based materials with low Cr content exhibits superior high temperature mechanical properties. However, due to the relatively low Cr content, their corrosion resistances under supercritical water (SCW) conditions are generally poor. High-Cr alloys, despite their much improved corrosion resistance, often suffer from embitterment due to the precipitation of sigma phase in the microstructure. In this study, corrosion resistance of an in-house produced high Cr steel (25%Cr) showed much better corrosion resistance compared to that of low Cr alloy (14%Cr). This high-Cr steel can potentially be used as a corrosion-resistant coating for structural materials in sew applications.INTRODUCTIONThe supercritical water-cooled reactor (SCWR) concept is one of the promising designs for the next generation nuclear reactor, in which the water coolant is designed to be at about 625°C and 25 MPa at the outlet of the reactor core. Under these relatively high-temperature and high-pressure conditions, the cooling water is at supercritical state. High-temperature mechanical properties, corrosion resistance and radiation damage are some of the key challenges. At present, no single commercial material can meet all the requirements of the severe SCWR in-core conditions. Canada supports research in several key areas of SCWR development, including materials selection. A major focus is on materials development, selection and evaluation for both in-core and out-of-core components.Allen et. al. [1] carried out a comprehensive study on the SCW corrosion resistance up to 600 °C on commercially available high temperature materials including Ni-based super alloys, various types of stainless steels and ferritic/matensitic steels. They concluded that ferritic steels develop a relatively thick but mechanically stable oxide layer, while austenitic alloys develop a thinner oxide layer that has been found to spall in some cases. Of the three types of alloys examined, the Ni-based alloys exhibited the lowest oxide thickness, however pitting was observed in the vicinity of intermetallic precipitates."

Jan 1, 2011

By Lifeng Yang, Xiang Zhang, Liang Yuan, Yonghui Wang, Bing Hou, Mian Chen, Rixing Zhang

Large-scale hydraulic fracturing technique has been widely applied to the development of shale gas reservoirs, where the interaction between natural fractures and critical fracture zones has substantial impact on the propagation of hydraulic fractures. Therefore, it is of significant importance to understand and experimentally verify such mechanism. To reach this end, tri-axial fracturing tests were implemented on 400mm×400mm×400mm block samples collected from Longmaxi shale outcrops. The interplay between hydraulic and natural fractures was investigated during the tests, factoring in the role of pump rate in affecting the created fracture network. Based on the experimental results, the critical fracture zone, defined as the weak formation zone nearby the wellbore created by staged pressure implementation that is observed rapid fracture propagation upon next stage of pressure increase, was thoroughly investigated. The analysis illustrates that given the high brittleness of the shale formation, abundant critical fracture zones are generated around natural fractures with pressure building up at a relatively low pump rate. As the pump rate increases, hydraulic fractures initiate and come into play with critical fracture zones, implying emergence of a large number of micro-cracks. A changing pump rate modifies the way of interaction between hydraulic and natural fractures and the subsequent formation of fracture network. Long term fracturing fluid injection with relatively low pump rate below the activation of critical zones is suggested. Also proposed is appropriate timing when applying a specific pump rate that will contribute to the improvement of hydraulic fracture propagation.

Jan 1, 2015

By P. N. Anyalebechi

The effects of a cross-hatched grooved mold surface topography, casting speed, and superheat on the morphology of solidifying shells of aluminum alloy 3003 have been characterized by a series of immersion tests. The cross-hatched grooves were 0.232 mm deep with wavelength or spacing between 1 mm and 15 mm. The shells solidified at casting speed of less than 10 mm/s on the 1 mm spaced cross-hatched grooved mold surface were fairly uniform with little or no localized variations in thickness. However, the propensity for non-uniform shell growth morphology was exacerbated by an increase in casting speed, melt superheat, and the wavelength of the cross-hatched grooves. This is provisionally attributed to their effects on interfacial heat transfer and wetting of the mold surface by the molten metal.

Jan 1, 2008

By S. Banisi, S. Zare, M. Mahmoudi, M. Maleki-Moghaddam, M. Yahyaei

As the orebodies become more complex and lower grade, there is an increasing demand from crushing circuits for a finer product. When the product from a crushing circuit does not satisfy the requirements of the downstream processes, the cost of production increases. Thus, enhancing the performance of cone crushers through optimisation of their operating factors becomes important. One of the key factors affecting performance of cone crushers is the filling of the crushing chamber during the operation. The effect of varying the filling of the crushing chamber of a cone crusher was investigated. To assess the crusher performance, parameters such as crusher capacity, power utilisation, and reduction ratio were used. Extensive plant trials were conducted to obtain samples and operational data when the crusher chamber was 50% full (half-full) and 100% full, which is 300 mm above the top of the crusher chamber (super-choked condition). The results indicated a 62% difference in the crushing capacity when the crusher was operated in a super-choked condition compared to the half-full chamber level. In the super-choked condition, the size-specific energy at 12.7 mm was 20 % lower than that of the half-full condition. The Bond ball mill work index (BBWI) of crusher product indicated that the BBWI of the product of the super choked condition is 5.6% less than that of the product of half-full condition. This can be attributed to the generation of micro cracks in particles due to increase in the interparticle breakage when the crusher was operated in the super-choked mode. Keywords: Cone crushers, crushing efficiency, crushing chamber filling

Jan 1, 2020

By S. Mohanta, I. D. Behera, B. Sahoo

"Run-of-mine coal contains particles of different sizes with different specific gravities, and when this coal is crushed, the amount of material present in a particular density class changes. This alters the washability characteristics of the coal, which affects the quantity, quality, and separation efficiency of the gravity-based coal washing process. The degree of difficulty in washing a typical coal at a particular specific gravity depends mostly on the amount of material occurring within ±0.1 specific gravity range, which is known as ‘near-gravity material’ at that particular specific gravity of separation. In this paper, two numerical indices, namely ‘near-gravity material index’ and ‘index of washability’, are used to quantify the distribution of near-gravity material in different density classes and to evaluate the degree of difficulty involved in the washing process. The results of this preliminary investigation indicate the uniform distribution of near-gravity material in all density classes for finer size fractions, whereas for coarser size fractions more near-gravity material is present in the lower density classes, making the washing process more difficult at a lower specific gravity of separation. IntroductionThe prime objective of coal beneficiation is to remove physical impurities as effectively and economically as possible. The beneficiation process includes various operations on the asmined coal to make it more suitable for enduse application without destroying the physical identity of the coal. There are several coal beneficiation processes, but gravity-based separators remain the most efficient unit operation for removing the undesirable gangue material from run-of-mine coal. These separators exploit the difference in density between coal particles and gangue particles to effect a separation. The feed is introduced into an aqueous suspension of ultrafine magnetite with a particular density. The feed particles with a relative density less than that of the suspension (clean coal) float to the top surface of the suspension, whereas particles denser than the suspension density (gangue material) sink to the bottom. When the difference in density between the particle and the aqueous suspension is large, the separation is easy, but when this difference is less the separation becomes much more difficult since the settling velocity of the particles is very low. This lower settling velocity increases the probability that particles that should report to floats report to sinks, and vice versa, hence increasing the amount of misplaced material. Therefore, the degree of difficulty in beneficiating a typical coal at a particular specific gravity depends on the amount of material occurring within ±0.1 specific gravity range. This is known as ‘neargravity’ material, also termed ‘near-dense’ material, at that particular specific gravity of separation."

Jan 1, 2016

By Takanori Kokubo, Kenta Suzuki, Tomohiro Sasaki, Toshiya Anami

"Previous work has shown that the strengthening Al-Mn alloys with copper leads to the formation of an undesirable reduction in recrystallized grain size. In this study the mechanisms of strengthening and recrystallization behavior in a continuously cast automotive heat exchanger fin stockof Al-1.1wt%Mn-0.5wt%Fe-0.3wt%Si with a0.3wt%Cu addition were investigated. Metallurgical analysis revealed that the Cu strengthening was dominated by the formation of dispersoid particles, while solid solution strengthening decreased with the Cu additions. This result is attributed to the decrease in the amount of Mn solid solution. The post brazing recrystallized grain size was reduced compared to that not containing Cu. It is postulated that the Cu addition leads to a decrease in the amount of Mn in solid solution which leads to a finer grain size. This effect is attributed to Mn in the aluminum matrix inhibiting boundary migration but allowing other grains to grow during heat treatment. The results are rationalized based on particle stimulated nucleation (PSN), wherein dispersoid particles are more likely to become active recrystallization nuclei during the heat treatment. The increase in the number of active dispersoid particles with Cu addition is correlated to the recrystallized grain structure.INTRODUCTIONImprovements in properties such as strength, braze ability and corrosion resistance in thermal fin stock alloys are all means to gain improved efficiency in heat exchangers particularly in automotive applications. While Al-Mn alloys dominate automotive heat exchanger fin stock alloy, even small chemical compositional changes can profoundly influence these properties (Kawaharaet al., 2004; Yoshino et al., 2009). The microstructure (particularly the grain size and shape) also plays a key role in determining the product performance and hence the thermo-mechanical processing (TMP) must also be considered. The casting method (typically conventional direct chill, DC, or continuous casting) significantly influences the properties in no small part due to the very different TMP routes that are used. Continuous casting is generally favored for fin stock applications as its higher cooling rate (which can be 2 to 3 orders of magnitude higher than DC casting) leads to finer as-solidified intermetallic particles and an increase in super-saturated solid solution elements (such as Mn)that are known to improve fin stock performance such as strength, braze ability(Okiet al., 2008)."

Jan 1, 2018

By M. Tadayonsaidi

The effect of alloying elements on the mechanical properties and thermal expansion of 336 casting alloy usually used as piston alloy which has low thermal expansion and very good high-temperature mechanical properties and good wear resistance was investigated. The mechanical properties and thermal expansion characteristic of samples with different combination of alloying elements, which enhance to reduce the cost of products, have been studies, The results show remarkable increase in the mechanical properties with increasing the amount of Cu and Mg, while are reduced with increasing amount of Ni, On the other hand, the use of eutectic aluminum alloy as 336 alloy with higher percent of Cu and Mg and lower percent of Ni are recommended for industry, due to economical viewpoint and satisfactory properties.

Jan 1, 2005

By Sevinc Yildirim, Cigdem Oruclus

"Metal-Porous Silicon (PS) based structures dipped in water show the direct hydrogen fuel cell behavior. The effect of the thickness of the cupper (Cu) film on the electrical properties of direct hydrogen fuel cell is studied by fabricating Cu/Porous Silicon/n-Silicon/Indium structures. PS samples were produced electrochemical etching of n-type single crystalline silicon with a resistivity of 1,25 Ocm and (111) orientation. The thin films of Cu with different thickness between 200 and 600 nm were deposited on PS surface by electron-beam technique. Investigation of the effect of Cu layer on the performance of the structure indicates that the performance parameters such as open circuit voltage (Voc) and short circuit current (Isc) strongly depend on the Cu layer thickness. It was observed that the divice with an 350 nm Cu layer exhibits the highest open circuit voltage (0,5 V), short circuit current (0,01 mA) and power density (10 W.m-2).IntroductionHydrogen is the most attractive and ultimate candidate for a future fuel and an energy carrier. Hydrogen is recognized as the environmentally desirable clean fuel of the future since it can be used directly in different types of hydrogen fuel cells [1]. In the past years, the rise in portable electronics requires the development of miniature fuel cells compatible with standard silicon micro fabrication technology. Most silicon micro-fuel cells have used the polyperfluo-rosulfonic acid membranes (Nafion R) as a proton exchange membranes (PEM) that is not really integrated with standard micro fabrication techniques [2-5]. The composite materials such as inorganicorganic hybrid materials (Nafion-silica, Nafion-borosiloxane etc) are next generation of proton conducting membrane [4-8]. But, fuel cells run on pure hydrogen gas, which can be produced with other energy resources. Hydrogen smallest atom and thus the H2 gas can leak easiliy. The application of hydrogen for power sources has been greatly restrained due to the lack of safe and convenient generation and storage methods.A kind of hydrogen fuel cells Metal-PS-Si structures used as an energy water directly. There is no need pure hydrogen. Cu-PS-Si Schottky-type fuel cells with as proton-conducting membrane and the thin-film cupper catalist and water as fuel, which are interesting for fabrication of lowcost miniature fuel cells. Generation of the open-circuit voltage and short-circuit current has been observed by Cu-PS-Si structure dipping in different hydrogen-containing solution."

Jan 1, 2014

By Pizhi Zhao, Jingwei Zhao, Zhenshan Liu, Yiheng Cao

"A new Al-Mg-Si-Zn alloy designed for automotive outer panel was trial-produced with industrial procedure. The final product shows a strong planar anisotropy. X ray diffraction analysis shows such strong anisotropy is caused by the dominating cube texture component in the final product. The reason for such high cube texture component was investigated by tracing texture evolution starting from the hot roll slab. It is found that certain cube texture components already exists in the hot rolled slab. The density of cube texture component shows as a wavy change through the following1st cold rolling, inter-annealing, 2ndcold rolling and solution treatment. This study shows that the cold rolling in the laboratory can well represent the texture evolution during the industrial production. The results obtained by lab rolling hints that change of second cold rolling reduction has weak effect on the planar anisotropy, when the gauge of hot rolled slab and final sheet are fixed.INTRODUCTIONWith the rapid progress of light-weighting in the automotive industry, aluminum sheets get more and more application as closure panel and structure parts. Recently the dominating alloy for outer panel is 6xxx series, containing the main alloy elements Mg and Si. The popular gradesareAA6016,AA6111, AA6022, and AA6014. These alloys still cannot satisfy the various requirements from automotive manufacturers. Most suppliers of automotive aluminum sheets are developing their own specific grades according to the customer’s demand. To increase the baking response, anew Al-Mg-Si-Zn alloy was designed, concerning the high combination energy between Zn solutes and vacancies formed during the quenching stage of automotive sheet manufacture. This combination is helpful to the precipitation of ß”phase during the paint baking (Wang, 2015,2016; Yan, 2014).The plastic strain ratio (r value)is a key index of the formability of automotive body sheet. A high r value means a good formability. The r values in different directions can be used to evaluate the planar anisotropy of the metal sheets. The trial produced Al-Mg-Si-Zn sheet shows a strong planar anisotropy with respect to r values. Since the r value is tightly related with texture, the texture evolution from hot roll slab (HRS) to final T4P temper was analyzed with X ray diffraction (XRD) to find the reason for the high anisotropy. Besides, the cold rolling reduction (CRR) was varied in the laboratory to modify the texture distribution, i.e., the planar anisotropy."

Jan 1, 2018

By Shinnosuke U, Zhang HE

In this paper, it is shown that the higher the pre-activation concentration of copper ions in pulp, the larger the adsorption amounts of copper ions and xanthate on arsenopyrite surface, and the better the arsenopyrite flotability in strong alkaline medium. On arsenopyrite pre-activated with cupric ions, the xanthate adsorption density in strong alkaline medium is approximately equivalent to that of cupric ions. It is therefore concluded that an amount of copper ions adsorb on arsenopyrite surface first, and then an amount of xanthate can (and only can) adsorb dependently on the surface active sites produced by these adsorbed copper ions on the mineral, so that arsenopyrite is kept rather flotable and is hardly separated from pyrite even in very strong alkaline medium. Selectively wiping out the surface copper active sites on arsenopyrite is the key point of successful separation of pyrite from arsenopyrite. According to this theory, a new 'SZLI' (know-how) method was recommended to satisfactorily deal with the difficult separation.

Jan 1, 1993

By George Onorato, Giovanni Bonita

Deep soil mixing (DSM) has now become a ubiquitous ground improvement technique across the globe for producing soil-cementous materials for many types of complex civil and environmental applications. In the field, the cementation bonds of the soil-cement materials are formed under a confining stress conditions; however, these conditions are generally not considered as most wet grab specimens are cured and tested under ambient atmospheric conditions. This has led to an underestimation of the engineering and mechanical properties of the soil-cement mixed material. This paper presents the preliminary findings of the effect of confining stresses on the mechanical properties of soil-cement mixed samples. This paper discusses the specialized field techniques used for modeling confining stresses during curing and presents the preliminary findings from different soil types. The findings indicate a strength increase within samples cured under a confining stress relative to nonconsolidated samples. The magnitude of the strength increase also appears to be different for different soil types. Finer-grained soils appear to exhibit a larger relative strength increase with confining stress relative to predominately granular soils.

By A. Roca, V. A. Quezada, O. A. Benavente, M. Cruells

The leaching pretreatment of copper ores is widely used in the Chilean mining industry. Agglomeration and acid curing have been identified as the most useful pretreatments. Of these, acid curing was recognized as beneficial in the dissolution of copper minerals, even in sulphides such as chalcopyrite. Extensive acid curing times have an impact on copper extraction, generate a homogeneous acid distribution in the mineral bed and benefit the inhibition of aluminum-silicate minerals (acid consumers). This document describes some of the theoretical background and results regarding the effect of acid curing in a chalcopyrite sample with 74% purity according to Qemscan analysis and a 28.5% of total copper. Leaching tests are carried out at 25, 50 and 70°C, evaluating the effect of a pretreatment on the chalcopyrite dissolution. The original sample and products generated were characterized by X-ray diffraction analysis and Scanning Electron Microscopy (SEM). The performed experiments indicate a direct relation between the effect of curing time and temperature in copper extraction. 92% of copper can be extracted in a leaching at 70°C and with 15 days of curing. Elemental sulfur, jarosite and copper polysulfide (CuS2) have been detected in leaching products. INTRODUCTION The copper extraction from minerals is a technique that has been developed for hundreds of years in the world. In 2017, the largest copper producer was Chile, exported 5.5 million tons (COCHILCO, 2018). However, in order to preserve this production level means overcoming multiple challenges. In the case of the Chilean copper deposits, the average copper grade in 2016 was 0.65%, lower than the 1% declared in 2004 (Consejo Minero, 2018). This is mainly due to the deeper of the deposits reaching sulfide mineral zones, mainly chalcopyrite. Traditionally, these sulfurized zones ore are treated through concentration by flotation and subsequent pyrometallurgical treatments. However, for some copper companies it is complex to process by this alternative, due to the high costs and high rates of water consumption. The mineral resources of these companies are known as "low-grade sulfides" and do not allow, economically, the treatment of these minerals through concentration by flotation. This is how hydrometallurgy becomes an alternative for the treatment of this type of deposits. In addition, several companies have hydrometallurgical plants, which would allow the operational continuity of these plants.

Jan 1, 2019

By M. Howe

This is a study of the impact of cyanide from mining waste on riparian communities, primarily vegetation, near Whitewood Creek, down-stream from Homestake Gold Mine in Lead, South Dakota. Cyanide is used in gold processing and the effluent, until fairly recently, was discharged directly into Gold Run Creek which empties into Whitewood Creek. Vegetation, soil, and water were collected from four different sites over a six month period, and samples tested for cyanide concentration. Data indicate a relationship between cyanide in soil and its uptake by certain plants, also, that the Homestake cleanup effort has made the stream viable again.

Jan 1, 1983

By E. L. Tucker

IN THE metallurgy of precious metals, it has been standard practice for years to use cyanogen compounds, so it was but natural that early investigators in the field of flotation should consider these compounds as possible flotation reagents. In Australian Patent 9508, of 1913, alkali cyanides were described as suitable reagents for the separation of heavy sulfide minerals, the reagents being employed either in an alka-line or neutral circuit. In U. S. Patent 1236501, of 1917, to John M. Tibbet, the use of cyanide in conjunction with soda ash or lime is described. One of the claims of this patent reads, "An improvement in the cyanide process for the treatment of ores comprising, mixing the ore with cyanide solution and oil and alkali: emulsifying the oil in the presence of the ore, the alkali and the cyanide solution, floating a portion of the values in the pulp by producing gas bubbles in the mixture-and removing the values floated." More recently, Sheridan and Griswold, in U. S. Patents 1421585 and 1427235, describe a somewhat similar process and have, successfully introduced it in. the mill of the Timber Butte Milling Co. U. S. Patent 1429544, of 1922, to Stevens, describes the use of double cyanides of copper, zinc, and lead. The success of cyanide as a reagent in the differential flotation of lead and zinc sulfides in highly complex ores is proof that these patents have a solid foundation.. Although the technique of their application to particular ores has been worked out in many cases, no one, so far as is known, has attempted to describe the nature of the action of the cyanide or to determine the ideal conditions for its, application. It was the purpose of the present investigation to gather information on these points. Naturally this would have been an exceedingly ambitious.

Jan 8, 1925