By S. G. Shabestari, S. Saeidinia, P. Mokarian

"The experiments were conducted to investigate the influence of various process parameters in rotary degassing of aluminum alloy AS5U3G. Degassing was carried out by use of argon inert gas. The flow rate of the gas was investigated in the range of 12 to 21 L/min., 350 to 500 rpm rotor speed, 6 to 12 minutes degassing time, and 755°C to 780°C melt temperature. Degassing efficiency was evaluated through measuring the density of RPT samples. By optimizing the process parameters, RPT sample density was increased up to 2.73 g/cm3, which guaranties the production of high-quality aluminum castings. Tensile strength and elongation were increased considerably by degassing process. Scanning electron microscopy (SEM) shows small size and well-distributed microporosity. IntroductionOne of the major problems associated with the casting of aluminum alloys is the formation of gas porosity. Aluminum and its alloys are very susceptible to hydrogen absorption. Because solubility is much lower in solid state than liquid state, hydrogen atoms leave their position during solidification and combine together to form hydrogen molecules. These micrometer- scale cavities, called microporosity, cause the reduction of mechanical properties, particularly strength, ductility, fracture toughness, fatigue resistance, pressure tightness, and corrosion resistance (Laslaz, 1991; Jorstad and Rasmussen, 1993; Sigworth and Wang, 1994; Korasani, 1996; Anson and Gruzleski, 1999; Zhang et al., 2000). To avoid these problems and produce good quality castings, it is necessary to remove hydrogen from the melt. Several methods are available for degassing aluminum melt. One of them is a rotary degassing system using inert gas, e.g. Ar or N2. Various thermodynamic and kinetic factors govern the removal of hydrogen from molten aluminum (Anderson, 1987; Sigworth, 1987; Pignault, 1993; King and Reynolds, 1995). These are some parameters that affect degassing efficiency. Some of them are discussed here and some are examined in this project."

Jan 1, 2004

By Subhas G. Malghan

The response of feldspar flotation to tallow diamine dioleate collector in the presence of sulfuric acid is studied using batch flotation experiments. Application of this non-hydrofluoric acid (non-HF) reagent system in the flotation of mineralogically and chemically different feldspar ores is compared with that of the conventional hydrofluoric acid system. The dependence of flotation recovery and concentrate grade on feed particle size distribution, conditioning time, pulp density, and pH, combined variation of collector and acid addition rates, sodium hydroxide concentration in the collector solution, and initial pulp pH prior to conditioning is studied. The results have been discussed in relation to applicability of the non-HF system to plant trials, and the nature of the collector adsorption in the selective flotation of feldspar.

Jan 1, 1978

By Hani Henein

"Heat transfer between droplets/particles and a gas phase plays an important role in the transport of numerous materials processing operations. These include rapid solidification operations such as gas atomization and spray forming, as well as chemical systems such flash furnaces. Chemical reaction rates and solidification are dependent on the rate of gas-particle or gasdroplet heat transport. Using a heat transport model validated using single fluid atomization of molten droplets; the effect of process variables on heat losses from droplets was examined. In this work, the effect of type of gas, droplet size, gas temperature, gas-droplet relative velocity on the heat transport from AA606 l droplets was examined. The most critical of these process variables to heat transfer is identified and will be presented.IntroductionIn materials processing, droplets are often encountered and used in processing a wide range of liquids and slurries. The small size of the droplet enables high reaction rates or high solidification rates in many systems. In order to capitalize on these high rates of transport processes, sprays are· also developed to maximize throughput. The design of these sprays, however, does not account for the transport steps and rate limiting mechanisms at the droplet surface. Rather, spray design focuses on maximizing the break-up of a stream or slurry into small size droplets or controlling the spread of the spray. Spray systems in industrial use typically generate droplets of wide size distribution leading to a wide range of reaction times for each of the droplets. Often the generation of a spray involves a number of coupled phenomena such as stream break-up, droplet-gas transport, droplet size distribution and spray geometry. Using gas generated sprays, it is not possible to identify how individual process variables contribute and control each of these coupled phenomena. While many mathematical models have been developed of sprays and they attempt to simulate coupled droplet transport, they do not provide insight into the contributions of different mechanisms in heat transfer. This is primarily because the basic fundamental heat transport between droplet and gas cannot be isolated from other gas spray phenomena experimentally such as two-way thermal coupling [l]. Thus, experimental validation of heart transfer of large and complex industrial spray models is not carried out. Hence, the validity of spray models remains in question and the approach required to optimize spray processes cannot be clearly identified"

Jan 1, 2004

By M. Laframboise, M. Buarzaiga

High-pressure acid leaching (HPAL) of nickel laterites has received considerable attention in recent years. High paymetals extraction, good selectivity, and advances in pressure hydrometallurgical technology are some of the reasons for this interest. Falconbridge Limited (Sudbury. Ontario) investigated the HPAL process using both fresh water and seawater for ore processing. The use of seawater resulted in a chloride concentration of 7.8 g/L in the autoclave feed. A test program was developed to study the effect of process water and leach temperature on the leaching behaviour of different ore compositions from the Koniambo deposit in New Caledonia. The work showed that salinity has a major effect on autoclave chemistry. This paper explores the results.

Jan 1, 2004

By X. Cao, M. Xiao, M. Jahazi

Magnesium alloys have low hardness, wear, erosion and corrosion resistance. The repair of service-damaged aerospace components made of magnesium alloys is an attractive solution in terms of time and cost saving. The feasibility of applying laser beam technology to repair ZE41A-T5 magnesium alloy sand castings in the machined surface conditions was studied using a continuous wave 4 kW Nd:YAG laser system. The influence of process parameters such as laser power, cladding speed, wire feed rate and defocusing distance on the shape, size and area of single cladding beads is discussed using a process optimization software. Sound single clad beads with good geometric characteristics were obtained using strictly controlled laser process parameters. The overall results indicate that laser surface cladding using filler wire has the potential for repairing aerospace components made of cast magnesium alloys.

Jan 1, 2006

By M. Suzuki, T. Shiomi, M. Nakada, K. Tsutsumi

Mold powder plays an important role in the continuous casting process for high quality steel production. It is well known that mold powder entrapment causes surface defects in steel sheet and the high viscosity of mold powder prevents the entrapment of mold powder in molten steel in ultra low carbon steel. This paper deals with the entrapment of mold powder caused by suction by Karman?s vortex in a laboratory experiment. At first the effect of the viscosity of oil and interfacial tension between water and oil was investigated in a water model experiment. Then hot model experiments were carried out by mold powder and molten steel. The amount of mold powder entrapment was affected by the viscosity and the interfacial tension between molten steel and mold powder. As a result, the following equation of the mold powder entrapment was obtained. m=1.06*107?-0.255?m-s-2.18 The amount of mold powder entrapment decreased when the viscosity and interfacial tension increased. But the effect of viscosity was larger than that of interfacial tension in the case of the industrial mold powder when the viscosity was under 0.5 Pa.s, interfacial tension was from 1200to 1300 mN/m.

Jan 1, 2004

By S. R. Mitchell, M. C. Fuerstenau, A. M. Gaudin

The two principal attributes of a thickener pulp are its settling rate and the ultimate pulp density of the thickened mud. Testing for evaluation of thickening attributes of a pulp has usually been done batch-wise by placing the pulp in a one-liter glass graduated cylinder and noting the position of the boundary between clear liquor and mud as a function of time. Refinements in testing have included repulping a thickened mud to various dilutions and evaluating the settling rate on these various repulped muds. This is considered to make possible an estimate of the settling rate as a function of pulp density and therefore to pinpoint the slowest settling pulp which ought to be critical from the standpoint of thickener plant design. Finally, tests are sometimes made with model-size continuous thickeners of arbitrary size. In batch tests it is generally accepted that the behavior of a pulp is described by a curve such as the one shown in Fig. 1, in which the position of the boundary between clear liquor and mud (the mudline) is plotted against time. It has also been assumed that the initial settling rate (the slope of the line segment AB) is descriptive of the pulp and independent of the size and shape of the container. Where the settling rate is slower and clearly a function of time (portion CD of the settling curve), it has been assumed that the data are not of much use because of the intrusion of compacting phenomena. The next important datum is the height, PE, which is a measure of the so-called ultimate pulp density. This quantity is assumed to be characteristic of the pulp and independent of the container.

Jan 6, 1959

By Karl Hoover, Cassandra Spence, Brent Bachewich, Jaakko Levanaho

"Since year 2000 the gold recovery into copper concentrate at Hudson Bay Mining and Smelting has reduced considerably during the summer months. This initiated a testwork program in the fall 2003 to find reasons and solutions for such change. During the testwork mineralogical factors, water quality effects and different reagents were evaluated. The reason for the lower recovery appeared to be the sensitivity of some collectors to pulp temperature. As a result of the work different collectors are being used in the mill in the summer than in the winter. A modification to the water system was also made to provide cooler water to the mill in the summer months.INTRODUCTIONHudson Bay Mining and Smelting (HBMS) is located in Northern Manitoba, just on the border of Manitoba and Saskatchewan. The complex consist of four different mines, Callinan, Trout Lake, Konuto Lake and 777 mine including copper smelter and zinc hydrometallurgical plants producing metallic copper and zinc. Gold is a very important byproduct providing about 30% of the mine revenue. In early 1990s when the company was facing declining ore reserves and was starting to gradually close down the operations, the 777’th exploration drill hole discovered a new orebody, which initiated a $0.5 billion expansion program. The main projects were a new 777 hoist with underground development and a new zinc cell house. About $30 million was used to increase the mill throughput to the present 2.27 million tonnes or 2.5 million short tons per year. The expansion programs were finished by the end of the year 2003.Historically the gold recovery at HBMS has varied between 60 and 70%. The recovery has been somewhat lower during the summer months. Gold recovery improvement projects were conducted throughout the 1990s, but were not focused on the seasonal gold recovery variance. However, since 2000, when the water system modifications to meet the increased water demand were completed, the gold recovery during the summer has been much lower than in the past. In August 2003 gold recovery fell below 30%, which initiated a metallurgical research program to discover the reasons behind the low gold recovery in the summer."

Jan 1, 2005

By Jian Deng, Hehua Zhu, Lianyang Zhang

Rockburst is defined as a sudden and violent explosion of rock on the surface of a rock excavation. Rockburst has been regarded as the least understood and most feared hazard problem for underground rock excavations. Traditionally, rockbursts were classified into the strain, pillar, and fault-slip categories. However, rockbursts are also known to occur at stress levels well below the rock yield strength, in mines where the rock is far from brittle, or without the presence of geological discontinuities. A plausible explanation of rockbursts is buckling, which has been identified as one of the main mechanisms for rockbursts. It is observed that rockbursts are often induced by dynamic loadings (pulses) from adjacent blasting. Therefore, the present paper studies the effect of pulse shape and amplitude on pillar rockbursts induced by dynamic loadings from blasting using the method of numerical analysis. The governing equation of a pillar’s motion is set up and the mechanism of pillar rockbursts is investigated through a practical example. The results show that it is not the shape of a pulse but the impact energy to decide the occurrence of pillar rockbursts. If all other parameters remain the same, pillar rockbursts are more likely to occur when the pulse duration is longer. The parametric resonance and the perturbation of dynamic loadings are also found to play an important role in the occurrence of rockbursts. These insights would provide invaluable clues about the mechanism and for better control of pillar rockbursts.

Apr 26, 2022

By R. L. Pozzo, I. Iwasaki

A previous investigation showed that corrosion currents estimated from polarization curves for the pyrrhotite-grinding media system under abrasion correlated well with corrosion currents estimated from marked ball wear test data by applying Faraday's law. Freshly abraded metal debris were magnetically attracted to pyrrhotite and lowered the rest potentials of the mineral particles, thereby affecting the corrosive wear. The investigation was extended to explore the interactions between a non- magnetic sulfide mineral, pyrite, and abraded metal debris and their effects on the corrosive wear mechanism. The electrochemical behavior of a three-

Jan 1, 1988

By R. L. Pozzo

A previous investigation showed that corrosion currents estimated from polarization curves for the pyrrhotite-grinding media system under abrasion correlated well with corrosion currents estimated from marked ball wear test data by applying the Faraday's Law. Freshly abraded metal debris were magnetically attracted to pyrrhotite and lowered the rest potentials of the mineral particles, thereby affecting the corrosive wear. The investigation was extended to explore the interactions between a nonmagnetic sulfide mineral, pyrite, and abraded metal debris and their effects on the corrosive wear mechanism. The electrochemical behavior of a three-electrode system involving pyrrhotite, pyrite and grinding media was also investigated as a first step towards elucidating the nature of interactions that occur in the grinding of complex sulfide ores.

Jan 1, 1987

By J. C. C. C. Menezes, R. A. S. Silva, A. V. Colling, I. A. H. Scheneider

"Coagulants rich in ferric sulfate can be obtained from pyrite-containing coal tailings using a biohydrometallurgical process. The aim of this study is to evaluate the relationship between quantity of pyrite and rate of oxidation, with regard to the consequent production of ferric sulfate for potential use as a coagulant for water and wastewater treatment. Leaching experiments were carried out on the laboratory scale on four coal tailings with different concentrations of pyrite. Characterization of the coal tailings was conducted for the following parameters: total sulfur, pyritic sulfur, sulfate sulfur, organic sulfur, and elemental analysis of CHN (carbon, hydrogen, nitrogen). The samples were also subjected to X-ray diffraction analysis to assess their mineral compositions. The leaching experiments were accomplished using a laboratory column constructed as a packed bed reactor with a sprinkling system in a closed circuit. After four weeks of leaching, the liquor was filtered and evaporated to an iron concentration of about 12 percent w/w, which is typical of the ferric sulfate coagulants commercialized in Brazil. IntroductionCoagulants used for the treatment of water and wastewater are predominantly inorganic salts of ferric iron and aluminum. Aluminum salts, including aluminum sulfate and aluminum chloride, and prehydrolyzed metal-ion reagents, such as polyaluminum sulfate (PAS) and polyaluminum chloride (PAC), are the coagulants most widely used for water treatment (Bratby, 1980; Tchobanoglous et al., 2003; Buzin et al., 2014).However, the presence of residual amounts of aluminum in drinking water has been controversially implicated in neurological diseases (Association of California Water Agencies, 2000; Becaria et al., 2006; Campbell, Hamai and Bondy, 2001; Rondeau et al., 2000; Walton, 2006). A possible alternative is to use iron-based coagulants, such as ferric chloride, ferric sulfate or polyferric sulfate, instead of the aluminum salts (Jiang, Graham and Harward, 1996; Jiang and Graham, 1998). Iron-based coagulants are commonly produced by the acid dissolution of iron scraps or iron ore (Tchobanoglous et al., 2003).Recent studies have shown that it is possible to produce ferric sulfate coagulants from the pyrite present in coal tailings through a biohydrometallurgical process (Colling et al., 2011). The main advantage of this process is that it does not require acid addition, which can be favorable in terms of production costs. Acidophilic bacteria, such as Acidithiobacillus ferrooxidans, can increase the rate of pyrite oxidation and dissolution by several times (Kontopoulos, 1998; Brett and Jillian, 2003; Johnson and Hallberg 2003). They can be highly significant in the bioprocessing of coal tailings for the production of ferric coagulants, as their action favors the acidification of the medium and iron leach (Colling et al., 2011)"

Jan 1, 2016

By H. Nakazawa, I. Iwasaki

Galvanic contact, occurring between electrically conducting minerals in flotation pulps, may affect the nature of mineral surfaces and influence their floatabilities. Rest potential and galvanic current measurements were made on an electrode combination of pyrite and pyrrhotite under nitrogen, air and oxygen aeration conditions. The results were correlated with their oxygen-consuming characteris- tics and flotation behaviors. The galvanic contact improved the floatability of pyrrhotite, but adversely affected that of pyrite. Auger electron spectroscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy indicated that the formation of hydroxide or oxide and sulfate species of iron on pyrrhotite decreased, whereas that on pyrite increased when these minerals were held in contact. An electro- chemical mechanism was proposed for the observed behaviors.

Jan 1, 1986

By Xiaolu Ye

"Comprehensive utilization of Bi and Sn from the tin-associated polymetallic tailings by “gravity separation – flotation combination process” has been studied, which was verified that the novel process is an effective method to deal with the high content pyrrhotite tin-associated polymetallic tailings. In this investigation, ore property analysis and magnetism analysis of pyrrhotite were conducted to research and develop reasonable beneficiation flowsheet. The results of ore property analysis present that pyrrhotite was not closely related to bismuth and tin minerals. Particle size analysis results indicated that pyrrhotite was mainly in the form of fine particles. The magnetic analysis results show that pyrrhotite was distribution in all the three types of pyrrhotite in a single mining area, which indicated that variable magnetism of with different crystal structure pyrrhotite. The process of “low intensity magnetic separation - high intensity magnetic separation” shown an excellent adaption for the high content pyrrhotite tin-associated polymetallic ore compared with the single flotation process based on the magnetism variable of pyrrhotite. The results of whole process test indicated that a bismuth coarse concentrate assaying 5.63% of Bi at 81.77% recovery was obtained, which treat the conditions for the Bi-S separation flotation. In addition, the content of sulfur in the tin concentrate decreased from 2.5% to 1.5%, which provided a new reference for other tin-associated polymetallic tailings. INTRODUCTION Tin has been applied extensively in catalytic chemistry, gas sensors, tin plating, and plumbing. Tin-bearing polymetallic ores have been the important deposit types to recycle tin with the rapid depletion of mineral resources. The comprehensive utilization of the associated elements has been a preoccupation for the mineral processing researchers."

Jan 1, 2018

By H. W. McQuaid

IT IS usually assumed that chemical specifications are sufficient for steel to be used for case carburizing, and if the steel analyzes within the ordinary limits specified for steel for this purpose, no difficulty traceable to the steel used should be encountered in obtaining satisfactory results in the case carburizing and hardening. Much work has been done to determine the effect of various alloying elements on the rate of carbon penetration, etc. but, to our knowledge, little if anything has been published in regard to the effect of the quality of the steel on the final results in the hardening of case-carburized steel parts. The writers believe that the structure of the case both before and after quenching is greatly affected by the actual condition of the steel itself as made, and that for good results in the case-carburizing and hardening departments, the steel should be of the best possible quality as regards non-metallic impurities. It is the purpose of this paper to prove that the presence of excess dissolved oxides in the steel, as made in the melting furnace, affects permanently the results obtained in carburizing and hardening and that it is possible that the presence of dissolved oxide can result in total unfitness of low-carbon steel for, case hardening purposes. When races and rolls for roller bearings are made from a low-carbon steel, case carburized and hardened, it is of primary importance that the results of this treatment be of the highest quality. It is necessary, therefore, that in the case-carburizing work each detail be rigorously checked to avoid any defects which would cause the loss of much time and material. The case carburizing with which this paper deals was done in under-fired oil furnaces. The temperature of each furnace is controlled by means of a platinum platinum-rhodium thermocouple, in connection with a potentiometer indicator and potentiometer recorder. The temperature of each furnace is registered every 15 min. by an operator, who is continually checked by the automatic recorders.

Jan 2, 1922

By J. J. Jonas

The categories of interpass time encountered in hot rolling are characterized. These are shown to fall into three broad categories: short (in rod rolling); intermediate (in strip processing); and long (in plate schedules). The effects of interpass time on recrystallization and carbonitride precipitation are described, and particularly on the interaction between these two mechanisms. The interactions, in turn, determine the final microstructure produced as well as the mechanical properties.

Jan 1, 2005

By Hidenori Hatta, Takero Watanabe, Hideo Yoshida

"The effect of the quenching rate on age hardening in an Al-6.0mass%Zn-0.75mass%Mg alloy sheet was investigated. The quenching rates and aging conditions were as follows: water quenching (WQ) or furnace cooling (FC) followed by pre-aging at 20°C,then artificial aging at 120, 160 or 200°Cwere performed. The peak strength of the FC and the WQ are very similarat120°C aging. It is important high strength was obtained even at the extremely slow quenching rate. On the other hand, the strength of the WQ significantly decreased compared to the FCat200°C aging. GP(I) zones were formed during the pre-aging at 20°C even if the cooling rate was very slow like the FC, and were transformed into the GP(II) ones at 70°C or higher and then into the ?’ phase. However, these zones were dissolved by reversion during heating to 200°C. Thus the strength of the WQ decreased. On the other hand, it is considered that an unknown cluster or GP zone with a thermal stability formed during the FC was not dissolved up to 200°C and was transformed into the ?’ phase. Therefore, a higher strength was obtained in the FC for the200°Caging.INTRODUCTIONAl-Zn-Mg alloys are widely available in commercial production because these alloy have lower quench sensitivity and can be produced by air cooling (AC). Heat treatable aluminum alloys are usually produced by water quenching (WQ) to increase their strength because a high cooling rate inhibits the precipitation of the stable phase during cooling and increases supersaturated solute atoms. However, Baba(1967)reported the strength of an Al-6%Zn-1.8%Mg(mass%) alloy without additional elements quenched by very slow cooling (15°C/min) was 96% of that quenched by WQ. Furthermore,the age hardening at room temperature (RT) occurs after annealing at 410°C followed by furnace cooling (FC, 0.5ºC/min or less)in these alloys. Therefore, the process of annealing at 410 to 430°C for 120 min followed by AC, and reheating at 230°C for 240 min, then cooling is recommended in the specifications (Japan Aluminum Association, 2011). Matsuda and Yoshida(1996)also recommended annealing at 300°C for Al-Zn-Mg alloy extruded products to inhibit age hardening at RT by precipitating the solute atoms and decreasing them in the matrix. It has been considered that the higher the content of excess quenched-in vacancy becomes by WQ, the higher aging rate at RT is obtained. Therefore,it is theoretically and commercially important to clarify the reason why the age hardening occurs relatively quickly in almost no excess quenched-in vacancies such as the FC, and why the same strength as the WQ can be obtained in the FC"

Jan 1, 2018

By Arthur Phillips

THE progress made in recent years in the art of dispersion-hardening has naturally led to an intensive study of alloy systems capable of yield-ing supersaturated solid solutions at ordinary temperatures. In general, the investigations have been confined to rather precise determinations of solubility limits and to experimental approaches designed to furnish more complete information regarding the rate and nature of precipitation under appropriate thermal conditions. Efforts are being made to focus more sharply on the atomic changes that are a direct consequence of the instability of the supersaturated solution. Here precision X-ray methods have come to be of considerable importance because lattice parameter measurements indicate very precisely the concentration of solute atoms in the solvent lattice. In spite of the general acceptance of parameter values as a criterion for the placing of solubility limits, it may be suggested that no thorough appraisal has been made of the several factors that conceivably may affect such measurements. More specifically, little attention has been devoted to the significance of surface energy conditions, specimen size and method of preparation, with par-ticular regard to the genesis of the grains and the surface concentration changes as a consequence of heat treatment and etching. Stenzel and Weerts1 recently published the results of a detailed study of precipitation reactions in aluminum-rich copper alloys. They found that, although copper lowers the lattice constant of aluminum, a 5 per cent copper alloy quenched from 150° and 225° C. had parameter values unquestionably higher than that of pure aluminum. Their results seem to substantiate, at least qualitatively, the earlier work of von Göler

Jan 1, 1934

By K. S. Raja, B. McNall, B. Pesic

"High-level radioactive wastes are stored in large underground storage tanks made of low-carbon steel. The wastes consist of concentrated solutions of sodium nitrate (NaNO3) and sodium hydroxide (NaOH), and the radionuclides 137Cs, 99Tc, and 90Sr. The corroding steel microenvironment may produce localized reducing or oxidizing conditions that affect the solubilities of the species such as Tc(VII) and Tc(IV), which in turn modifies the kinetics of corrosion of the storage tank. To understand the influence of technetate ions on the corrosion of steel, electrochemical polarization studies of A 537 steel samples were carried out in 1 M NaNO3 + 0 .05 M S r(NO3)2 + 0.1 M NaOH with and without addition of HReO4 at different temperatures (24 – 85 °C). The concentration of HReO4 was varied from 0.014 – 0.04 M.INTRODUCTIONAqueous processing of spent nuclear materials generates a large amount of high-level radioactive wastes. The wastes are primarily salt solutions of sodium hydroxide and sodium nitrate which also contain fission products such as 137Cs, 99Tc, and 90Sr. Among the high level radioactive fission products, Tc-99 is of great importance because of its high concentration, long half-life (2.1 x 105 years), high solubility in geologic waters as technetate, and rapid diffusivity through the geologic systems. The solubility of technetate ions varies depending on the oxidizing conditions prevailing in the storage containers. High level radioactive wastes are stored in single shell or double shell tanks made of low carbon steels such as ASTM type A15, A516-70 and A537. Most of the available literature on corrosion of steel in simulated radio active waste environments pertains to nitrate induced stress corrosion cracking (Subramanian & Mickalonis, 2005). The corroding steel microenvironment may produce localized reducing or oxidizing conditions that affect the solubilities of the species such as Tc(VII) and Tc(IV). Corrosion of steel and formation of Fe(II) and Fe(III) will affect adsorption and reduction of Tc species. The radioactive species can irreversibly be sorbed on the steel surface by oxidation of Fe(II) to more stable Fe(III) and fixed as less soluble Tc(IV)/Fe(III). The solubility of Tc species is also affected by other factors such as dissolved oxygen, local pH, temperature etc. How the corrosion behavior of steel will be affected in the presence of Tc species is not clearly understood.Cartledge (Cartledge, 1960) demonstrated that passivation of iron can be achieved in the presence of oxygen along with suitable inhibitor ions/molecules of the general formula XO4 n-, such as pertechnetate (TcO4 -). The pertechnetate ion is univalent. Since it is derived from a strong acid, no buffering action can be expected from this ion. The redox potential of the reaction (1) is 0.738 VSHE (Pourbaix, 1974)."

Jan 1, 2012

By Thomas A. Lang, Kanwarjit S. Chawla, Francis S. Kendorski

Unlined water tunnels have often been used as pressure conduits for hydroelectric projects. However, fallouts of rock in such tunnels are not uncommon and in many cases have been attributed to erosion of shears and seams. A case history of such a fallout is described. An appraisal of the conditions pertaining to the fallout led to the conclusion that rapid changes in the water pressure in the tunnel resulting from operating conditions were significant factors in initiating the fallout. Other factors that contributed to the fallout are also described.

Jan 1, 1976