By Henry Howe

THIS paper is a discussion of the extremely valuable one of Mathewson and Phillips, The Recrystallization of Cold-Worked Alpha Brass on Annealing,1 which not only gives us a wealth of important data reached with great intelligence, but also shows both uncommon powers of imagination and a perfectly fair spirit. Let me try to analyze some of their results, and to enunciate some of the laws to which these results point. For brevity I refer to them as "The Authors." The page numbers in parentheses refer to their paper. 1. The Visible Aspects of Recrystallization.-Plastic deformation in a single direction, as in cold-rolling, draws the grains out in that direction, that is, inequiaxes them, without destroying their apparent individuality. Each grain seems to endure the drawing out without changing either its volume or its orientation materially, for the etching tint of each grain seems to be as uniform after as before the drawing out, save for the "etch bands,"2 shown in Figs. A to D of the Authors' Plate I. As the drawn-out metal is heated progressively, on reaching a certain "disintegration temperature" these old grains seem to break up, probably into submicroscopic fragments, and this apparent disintegration is followed by a coalescence of these fragments, so that their number decreases and their size increases, till they may become very much coarser than before the drawing out. Ruder3 coarsened the grains of silicon steel in this way till single grains reached an area of 50 cm. (7.75 sq. in.). The deformation itself probably breaks each grain up into many very small fragments, but the fact that each grain continues to have a uniform etching tint different from that of its neighbors indicates that these fragments retain the initial common orientation of the grain. The apparent disintegration which we observe, then, is rather an abandonment of community of orientation for individuality of orientation, by the fragments formed earlier during the deformation. Hence we

Jan 10, 1916

ZAY JEFFRIES (communication to the Secretary*).-Having seen Mr. Ruder's micrographs of electrolytic iron, I am of the opinion that the tentative explanation offered verbally is correct. Mr. Ruder has informed me that both of the samples were cooled in the furnace. The structures as shown in Figs. Band C resulted from the last cooling through the temperature range near 900° C. Assuming that the rate of cooling through this range was the same in both cases, the differences in struc-ture of the gamma iron in the two samples must have ]:)]-ought about, in some way, the variations in grain size and grain shape shown in Mr. Ruder's micrographs. Even though there is practically no temperature gradient in muffle-furnace treatment during the "soaking" period, during both heating and cooling, there is a temperature gradient. Fig. B should normally have been fine-grained prior to the last cooling, due to the comparatively low maximum temperature to which it was heated (1,000° C.). On cooling through the allotropic change point at 900°, these small gamma grains, iii conjunction with the temperature gradient, should form an ideal condition for germination. Germinant grains should form near the surface of the sample (the-colder portions) and the small gamma grains would be progressively absorbed as they changed into non-gamma iron. The elongated grains in Fig. B, converging toward the axis of the piece of iron, indicate that germinant grains first formed near tine surface and advanced their boundaries toward the interior of the sample. The gamma grains in Fig. C, however, should have been large, prior to the last cooling, due to time high temperature treatment (1,250 to 1,300° C.). In other words, to use one of Prof. Howe's expressions, the crystalline organization should be very complete and the change from gamma to non-gamma iron on cooling would take place reluctantly. This resistance to change from gamma to non-gamma iron would probably be greater in the interior of the large grains than at their boundaries. Non-gamma iron centers or nuclei would probably form at a great many places, at the grain boundaries, thus masking the influence, to a large

Jan 6, 1917

By Henry Howe

W. E. RUDER, Schenectady, N. Y.-In 1913 I presented a paper before this society on Grain Growth, and at that time it seemed to me that the only explanation for grain growth was that of critical strain. I do not think I published the photographs at the time, but I made some experiments on the effect of stretching sheets of metal. This allowed for fairly accurate determinations of the amount of cold deformation, At the time I worked-with silicon steel because one could see the change in grain growth with the naked eye. I stretched about 10-samples from 0.5 per cent. to 10 per cent., and, after heating to 1,050° C., I found that the maximum grain growth occurred at about 2 ½ per cent. cold deformation. This I designated "the critical strain" for maximum grain growth. About a year ago I talked with Prof. Jeffries, who explained to me his ideas of grain growth. It occurred to me that it would be a very easy thing to check the strain hypothesis against the strain and temperature hypothesis, if we took a certain number of these strips, strained exactly alike and heated to different temperatures; in that case the maximum grain growth ought to appear at a different percentage of deformation for each temperature. These experiments showed that there was, as Mr. Jeffries shows in his present paper, a decrease in germinative temperature with increased cold deformation. The samples were stretched from ½ to 8 per cent. and heated for 10 hr. in hydrogen. Samples were introduced into a furnace previously heated to temperature. A maximum grain growth was obtained at 5 per cent. deformation, when heated to 750° C.; at 2 ½ per cent. when heated to 800' C.; at 1 1/4 per cent., if heated at 950°C.; and at 5/8 per cent.. when heated at 1,100° C. This shows very clearly that the germinative temperature decreases with the increase in cold deformation. The growth was very much more marked, however, at the high temperature, i.e., the grain grew more rapidly and attained a much larger size than at lower temperature. In considering the photographs (Fig. A) those along the lateral edges should be ignored because.

Jan 4, 1917

By Arthur E. Bousu, C. T. Eddy, L. W. Eastwood

THE recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received considerable attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coalescence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by . Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presented in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are untenable. A paper on the theory of recrystallization with additional data will be completed in the near future by the writers.

Jan 1, 1935

By L. W. Eastwood

THE recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received consider-able attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coales-cence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presented in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are unten-able. A paper on the theory of recrystallization, with additional data, will be completed in the near future by the writers.

Jan 1, 1935

By J. E. Burke, C. W. Mason

IN attempting to study precipitation from a tetragonal lattice using solid solutions of bismuth in tin, it was found that although a Widnmanstatten pattern is observed 1 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process MICROSCOPICAL STUDIES Alloys were made from Chempur tin (Standard samples 42b and 42c, National Bureau of Standards), and bismuth (Kahlbaum C P ) by melting neighed quantities together under palm oil, stirring well, and casting in a heated graphite mold The polishing and etching techniques employed largely govern the visibility of the structural changes The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through BehrManning 3/o abrasive papers, lubricated by a solution of paraffin in kerosene A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution, repeated etching and polishing served to remove disturbed metal For high-power examination better preparation was necessary It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a Heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use A better procedure was as follows The metal lap was warmed slightly, and a 4-in circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C was poured over it, allowed to stand for 1 to 2 min and then washed off It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample The cloth was then charged with a paste of the relevigated alumina in water Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deteriorates after about 24 hr This is not serious, because a new lap can be prepared in about 5 min, and only small pieces of cloth are used Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer For the final etching, the most satisfactory reagent was that of Taffs,7 the formula for which is FeC13 6H20, 2 grams, HC1, 5 c c , H2O, 30 c c , C2H5OH (95 per cent), 60 c c This etchant reveals differences in com-

Jan 1, 1941

By George Langford

Introduction The manufacture of ductile beryllium is one of the most interesting problems confronting the metallurgist today, and one which becomes more acutely in need of resolution as the uses for beryllium increase. Beryllium belongs to the hexagonal group of metals along with zinc, magnesium, and cadmium. The melting point of the metal is about l,280°C. ± 5°C. Due to its brittleness, the metal's chief use is as an alloying agent in copper and iron. The very low absorption coefficient of beryllium for x-rays makes the metal ideal for x-ray windows, and, similarly, because of its low capture cross-section for neutrons, the metal holds a preferred position in the field of nuclear physics. Modern x-ray diffraction methods were responsible for explaining the mechanism whereby zinc metal, although brittle when cast, could be made ductile at room temperature. The diffraction patterns of zinc and magnesium indicated the importance of the parts played by recrystallization and preferred orientation in this mechanism. It was with this in mind that an Investigation into the recrystallization and preferred orientation of beryllium was undertaken. The investigation, after a series of experiments were conducted involving cold-working and annealing, yielded the recrystallization temperature curve for beryllium. Both the texture of preferred orientation and the effect of recrystallization on this texture when subjected to compressive stresses were also determined. W. A. Alexander, J. K. Swinton and L. M. Pidgeon, in their investigation on The Recrystallization Temperature of Beryllium (C.I.M., Trans., Vol. L, 1947, pp. 657-664), utilized the Brinell ball as a means of cold straining the metal. Sufficient strain was developed to estimate the recrystallization curve for the metal. However, in order to determine the lowest recrystallization curve, as well as to develop a preferred orientation structure, larger deformation than that possible with a Brinell ball was required. The plastic deformation of beryllium can be carried out at an elevated temperature above 700°C. Above 850°C., the metal is quite ductile and can be readily compressed or extruded.

Jan 1, 1948

By C. G. Dunn

MANY investigations have been made concerning the nature of plastic deformation and recrystallization of metals either in the form of polycrystalline materials or in the form of single crystals. However, similar work on strip materials composed of large grains as thick as the strip and having a high degree of preferred crystal orientation has not been carried out extensively. Such materials are ideal not only for studying changes in single crystals under conditions where neighboring grains exert their influences but also for obtaining the, complete change in orientation of a grain or group of grains during the course of plastic deformation and subsequent recrystallization. It is well known that first-order twins in the form of Neumann bands may be produced during the plastic deformation of ferrite crystals, particularly silicon ferrite crystals.1-3 Furthermore, it is believe that high-stress regions exist in the vicinity of these bands4a and it has been said that these banded regions would be active in recrystallization processes.5 Evidence to that effect in silicon ferrite had already been presented with photomicrographs showing recrystallization among Neumann bands during the early stages of recrystallization.5,6 Similar evidence has been published for nonferrous metals.5 Merging of fine parallel deformation bands during annealing to form twin bands of ordinary appearance in alpha brass has been offered not only as evidence of an active role being played by mechanical twins but also as evidence that such twins existed prior to recrystallization.5 Proof that such new structures are actually first-order twins, or even twins at all, must be considered inadequate except for those cases where X-ray or optical data have been obtained to confirm the necessary orientation relationship.7,8 A. B. Greninger has obtained excellent iliustrations of annealing twins in alpha irons Since his material was previously deformed by sharp hammering, a process that generally induces Neumann bands, the existence of twins following annealing might suggest that they grew from mechanical twins. In connection with transformation twins in alpha iron, Greninger reported that grains containing. three twin orientations occurred rarely and none occurred with three sets of well-developed bands.9 The work at the Pittsfield Works Laboratory on silicon ferrite in the form of large-grained strip steel deformed a small amount and annealed to partially recrystallize the grains indicates that the deformation and recrystallization processes that lead to annealing twins involve more complex processes than the formation of Neumann bands and the growth of such bands. Some groups of annealing twins are obtained which contain not only three well-developed twin structures, but also contain more than one order of twins. It is also shown, in one case, that an interrelated group of twins did not arise within one single parent grain and, furthermore, orientations of grains in the group

Jan 1, 1944

By Douglas Glenn Stalheim

The uniformity of the final cross sectional microstructure and subsequent final mechanical properties and shape of structural steels is dependent on the type or types of recrystallization behaviors that are created. There are three main recrystallization behaviors that are the foundation of the metallurgy created during production. Alloy design and subsequent processing design strategy drive how much of each recrystallization behavior is created through the cross section of the product. Carbon manganese steels create only one basic behavior while the addition of microalloys, in particular niobium, can add two additional behaviors. The behaviors are intertwined with each other and build upon each other. The three behaviors are Type I, static recrystallization, Type II, no-recrystallization, and Type III, metadynamic/dynamic recrystallization. How much of each behavior is generated through the cross section through the production influences the final transformed microstructure and corresponding mechanical properties and shape performance. This paper will discuss the three behaviors, how they are generated, how to identify which behavior is occurring through modeling or actual mill data. Actual examples from production will be discussed.

Aug 16, 2017

By W. A. Anderson, R. F. Mehl

RECRYSTALLIZATION of cold-worked metals has long been known to proceed by a process of nucleation and growth.1 When a cold-worked metal is heated to a temperature at which recrystallization will ensue, nuclei of new grains, essentially strain-free, appear and grow. As the process proceeds, nuclei continue to appear and to grow, until the cold-worked matrix has been entirely consumed and recrystallization has been completed (Fig. I). Conducted isothermally, a measurement of the fraction of the matrix recrystallized plotted against time, yields an isothermal recrystallization curve, showing the time course of the recrystallization process (Fig. 2).2 Evidently, then, the rate of recrystallization is determined by the rate at which nuclei form and the rate at which they grow. The rate of nucleation N is the number of nuclei that form in unit time in unit volume of the unrecrystallized matrix, and the rate of growth G is the increase in radius of the recrystallized grain per unit time. In recent years attempts have been made to determine N and G as these vary with the well-recognized variables affecting recrystallization: time, temperature, degree of deformation, etc.' Such studies yield information that is more fundamental than that conveyed by the conventional recrystallization diagram,' since the rate of recrystallization is thus analyzed into its two component rates.2 Methods are now available by which N and G can be measured, and analytical expressions have been developed for the interrelationships among N, G, the isothermal recrystallization curve, and the final grain size, which greatly facilitate analysis.2-4 The application of these methods has been demonstrated recently for the recrystallization of silicon ferrite.2 Data on N and G in dependence upon the recognized recrystallization variables are, however, very fragmentary;* values of N and G have been determined for some metals, but the effect of temperature, which would yield the fundamentally important activation energies, has been too little studied. Thus far there has been no detailed study of the recrystallization of any one metal in terms of N and G over appreciable ranges of the variables time, temperature, degree of deformation, and original grain size. It is the purpose of the present paper to provide such a study, employing aluminum.

Jan 1, 1945

By Abu Syed H. Kabir, Mehdi Sanjari, Steve Yue, Jing Su, In-ho Jung

AZ31 magnesium alloy sheets were produced by high speed rolling (HSR) at 1000 m/min at a low temperature of 100 ?. A high reduction of 72% can be achieved in single pass. At the reduction of 30%, the microstructure was covered by shear bands and twins. When the reduction was increased to 49%, dynamic recrystallization (DRX) was clearly observed in the vicinity of shear bands and twins and the full recrystallization was seen at a reduction of 72%. In order to study the static recrystallization (SRX) behavior on the heavily twinned structure, annealing was then carried out at 200 ? on the as-rolled specimens at the reduction of 30% for different times. Static recrystallized grains were also firstly observed on shear bands and twins after 45 s and the microstructure was mostly fully recrystallized after 1 h annealing with a few retained large elongated un-recrystallized grains. Texture weakening was found during annealing on the heavily twinned specimens by SRX, but not during high speed rolling by DRX. In the present study, effect of DRX and SRX on microstructure and texture evolutions during rolling and annealing were compared.

Jan 1, 2015

By C. H. Mathewson

Discussion of the paper of C. H. MATHEWSON and ARTHUR PHILLIPS, presented at the New York meeting, February, 1916, and printed in Bulletin No. 109, January, 1916, pp. 1 to 50. ZAY JEFFRIES, Cleveland, Ohio (communication to the Secretary*).¬The authors are to be congratulated for this interesting and valuable contribution. The paper as a whole shows very careful experimentation coupled with rare judgment in drawing conclusions. I have been working along similar lines for the last two years with other metals and alloys. In a short conversation with Dr. Mathewson about July 1, 1915, he mentioned the fact that different degrees of cold work greatly affect the temperature of recrystallization on annealing, Later I determined the recrystallization temperatures of iron, mild steel, and copper, with different degrees of cold work and found that the greater the degree of cold work, the lower the temperature of recrystallization on annealing. In the course of these experiments, I conceived practically the same ideas regarding the reasons for recrystallization as those advanced in the article under discussion. After a metal has been reduced by cold work to about one-fourth of its original area, the differences in orientation of different parts of a given grain can be seen plainly at a magnification of about 1,000 diameters. It is interesting to note that in Fig. A, Plate I, the lines of deformation are not parallel. For example,. in the large grain at the lower left corner of the micrograph, if the lines of deformation about 3g in. from the left edge are continued in a straight line, this line will intersect a straight line drawn as a continuation of the lines of deformation on the extreme right of the grain, at an angle of about 20°. Similarly, if the lines of deformation at the extremities of the large grain in the right central portion of the micrograph are extended, the lines intersect at an angle of about 35°. The individual lines of deformation are not straight. In some of these the parts of the broken lines intersect at angles as great as 15°.

Jan 5, 1916

By C. H. Mathewson

(New York Meeting, February, 1916) DURING the past year considerable work dealing with the mechanical properties and microstructure following the anneal under uniform conditions of certain types of commercial rolled brass has been done in this laboratory. Since these experiments were conducted with the active cooperation of the Bridgeport Brass Co., involving free use of its product, and have thus furnished information which is characteristic of some of its special mixtures, full publication of the numerical relationships and comparative results encountered does not seem justifiable. Some of the more general features of this work are, however, available and it is our present purpose to use the material in question, along with some results of special tests, in discussing the characteristics of recrystallization as related to the degree of hardening by strain and the ordinary annealing variables. We desire to make acknowledgment of the many courtesies extended by Mr. Charles Ferry, Metallurgist of the Bridgeport Brass Co., and the value of his cooperation, which has greatly stimulated the study of brass in this laboratory. A clear and systematic presentation of the principal relations between temperature and time of anneal, the changing physical properties and microstructure and the degree of previous reduction by cold-rolling, was first made, in the case of rolled brass and copper, by the French engineer, C. Grard,1 in 1909, although much fragmentary information of this general character had appeared earlier and the main facts involved were undoubtedly known to many brass specialists through their own private research. From this work, it appears that in the cartridge mixture (67 per cent. copper, 33 per cent. zinc) the properties imparted by cold-working within the limits, 13 to 75 per cent. reduction of area by rolling

Jan 1, 1916

By J. Schmidt

Cold drawing of copper wire rod is usually combined with an in-line annealing process to adjust the ductile microstructure of the wire again. One important key factor for successful annealing is the quality of the copper itself. Rod producers can check the recrystallization behaviour of the rod by different methods: chemical analysis, Spiral Elongation Test (SEN) as well as the Rapid Elongation Test (AR) are some examples of common testing methods. The comparison of the results of these methods does not always show sufficient correlations. The paper introduces firstly the SEN and AR-Tests and their different approaches to the mentioned task. The second step is to compare some results of the SEN-Test with the results of the AR-Test and identify causes of deviations. Thirdly, the effect of pre-annealing is discussed, which is especially common for wire rod with diameters of more than 8 mm.

Jan 1, 2007

By Julien Favre, Akihiko Chiba, Damien Fabregue, Yuichiro Koizumi, Eric Maire

"The mechanical behavior of Co-20Cr-15W-10Ni alloy is studied by compression tests at high temperature. Microstructures after deformation are evaluated using SEM-EBSD. Significant grain refinement occurs by dynamic recrystallization for high temperature and low strain rate (T>1100°C, <0.1s-1), and at high strain rate (~10s-1). Dynamic recrystallization is discontinuous and occurs by grain boundaries nucleation, leading to a necklace structure. The nucleation mechanism is most likely to be bulging of grain boundaries. However, recrystallization occurs also by rotation of annealing twins which can bulge as well. The modeling of mechanical behavior gives a fair quantification of flow softening due to dynamic recrystallization, indicating the progress of dynamic recrystallization with deformation.IntroductionCobalt-chromium alloys are used in biomedical applications for the elaboration of implants due to their outstanding mechanical properties and their high resistance to corrosion. For stent application a large ductile behavior is required in addition to the high mechanical strength. Indeed stents have to undergo a deformation until e˜40% during their expansion [1]. Conventional Co-Cr-Mo (CCM) alloys exhibit limited ductility (maximal deformation about e˜30%) [2]. Co-Cr-W-Ni (L-605) alloy is a better candidate for stent elaboration since its fracture strain can exceed 40% (comparable to nickel superalloys (Figure 1), while it keeps high mechanical strength. In spite of the presence of nickel element in this alloy, biocompatibility is sufficient for vascular implants, therefore L-605 alloy is extensively used for heart valves and stent elaboration [3]."

Jan 1, 2012

By Paul Beck

WHILE the recrystallization properties of most of the practically important metals are known in considerable detail, those of lead are still relatively little known in spite of some valuable contributions in recent years. This condition probably is due to the difficulties involved in applying the usual methods of investigation. The microscopic method of discriminating between the elongated deformed grains of the familiar lenticular shape and the equiaxed recrys-tallized grains is not successful with fully refined lead: lenticular grains cannot be seen under the microscope with any amount of deformation whatever. The probable cause of this phenomenon was recognized long ago. With large deformation the time of recrystallization at room tem-perature is shorter than the period of preparation of the specimen for microscopic examination; with small deformation the deformed grains are not noticeably elongated in the first place. However, with small deformation the migration of the grain boundaries can be observed. The only systematic investigations yet published on the recrystallization of lead, those by R. S. Russell,1-3 make use of the conditions just described. Russell considered recrystallization completed when no further migration of boundaries could be observed. A serious objection to this method arises from the fact that there is no evidence to support the view that grain-boundary migration results only from recrystallization. If such migration does result from other sources after recrystallization is com-pleted-after the deformed grains have been replaced by new unde-formed grains-the "time of recrystallization" as determined by Russell may be too long. Furthermore, the method is subject to the above-mentioned limitation because of the unavoidable period of preparation of the sample. According to Russell, even with the fastest technique 5 min. elapsed before the deformed samples were ready for examination, and consequently no recrystallization time shorter than 5 min. could be measured.

Jan 1, 1939

By C. K. Leith

AT the outset I would like to make it clear that I do not enter this discussion in a controversial spirit, but in an attempt to contribute something helpful to an understanding of a difficult problem. I have too high regard for the sterling quality of the work of the men who have studied this subject in detail to offer anything in the way of essential contradiction to their statements of fact. Difference of opinion arises from differing valuation of the possible alternative hypothesis which these facts suggest. Some degree of recrystallization in limestone contact zones has been recognized by many investigators. Earlier investigators, for the most part, assigned an important, if not the most important, role to recrystallization in development of these zones. With the growing recognition, of introduction of ores and gangue materials into the contact zone from igneous rocks through the medium of primary magmatic solutions, there has been a tendency to ascribe to this process most, if not all, of the chemical and mineralogical characteristics of the contact zone. This has involved a correspondingly diminished emphasis on recrystallization of substances already there as a factor in the process, and in some cases even the complete elimination of this hypothesis. From detailed study of a few contacts, casual observation of others, and a general familiarity with the literature, some of us have been led in recent years to raise the question whether the pendulum has not swung too far away from recrystallization toward direct introduction from igneous sources, and to argue for more recognition of the part played by recrystallization.1 The inevitable sequence has been that those of us who have taken this view have been charged, at least by inference, with emphasizing recrys-tallization to, the total exclusion of the alternative process. Scientists, like other men, like to classify and pigeon-hole views under simple and definite designations, leaving out qualifications which would tend to make the classification more difficult to state. This has made the problem seem more definite and simple, but has tended to obscure the fact that the disagreement is primarily not one relating to essential facts, but one of

Jan 6, 1914

By R. F. Mehl, J. K. Stanley

THE recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are employed.1 Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystallization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress .4,5† The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed .27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert measurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now

Jan 1, 1942

By R. F. Mehl, J. K. Stanley

THE recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are employed.1 Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystallization is not a heterogeneous reaction .within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress.4,5? The theory of recrystallization is not in advanced state; if recrystallization data were obtained, in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert measurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now

Jan 1, 1942

By Charles Barrett

RECRYSTALLIZATION textures-the orientations of grains after recrys-tallization-have been studied extensively not only because of their metallurgical importance but also because of the information they yield regarding the atomic movements during recrystallization. Recrystallized grains must possess the same orientations as the submicroscopic nuclei from which they have grown, and thus they offer a direct road by which experimenters can penetrate the submicroscopic realm. Many perplexing results have come of these studies, but one of the most striking has been the apparent difference in behavior between single crystals and polycrystalline grains. For example, Burgers and Louwerse have shown&apos; that when single crystals of aluminum are deformed by compression and are recrystallized (at 600° C.) the new grains appear with orientations that are different from the orientations of the deformed crystal in which they grew; but polycrystalline specimens, on the other hand, appear to have a [110] fiber texture both before and after recrystal-lization and thus to retain their texture during recrystallization. This apparent difference between the habits of single crystals and small grains is the subject of the first part of the present research and has been explained by findings reported herein. A similar situation appears to exist for aluminum when elongated or drawn into wires, for single crystals alter their orientation2,3 and polycrystalline wires retain their texture 4,1 6 upon recrystallization after elongation (at least with high-purity alumi-num), and it is possible that the explanation found in this paper for compression can be extended to cover elongation and other types of deformation as well. The second part of this paper deals with the theory of recrystallization textures. In the most successful theory for aluminum recrystallized after compression,1 much weight is given to the orientation of highly stressed nuclei in the deformed material. Taylor&apos;s "local distortions" are assumed to exist along the slip planes where displacement has occurred, consisting of fragments rotated in a specific way with reference to the slip plane and slip direction; namely, about an axis lying in the slip plane perpendicular to the slip direction. 1,7,8,9

Jan 1, 1940