By Hai-Peng Guo, Lu Jiang, Xiao-Man Yan, Bing Xie, Hong-Yi Li

Traditional, calcium compounds cannot be used in vanadium extraction processing due to the limitation of sodium roasting technology, which results in unsatisfied dephosphorization for vanadium-containing hot metal in converter and thus increasing the dephosphorization burden for subsequent steelmaking. The calcium roasting technology is an alternative for vanadium extraction and allows adding lime into vanadium slag in converter. In the present study, vanadium was leached by soda from roasted vanadium slag with high calcium content. Effects of roasting temperature and time, leaching temperature, Na2CO3 concentration andliquid to solid ratio on vanadium leaching rate were studied. The results show that 94% of vanadium was extracted by roasting the vanadium slag at 950℃ for 2.5h and then leaching in 160g/L Na2CO3 liquid at 95℃ for 1h with liquid to solid ratio of 10:1 ml/g. Impurities of Si and P reacted with calcium and formed insoluble Ca2SiO4 and Ca3(PO4)2 respectively.

Jan 1, 2015

By T. Gunawansa, T. L. Alford, Zhao Zhao, A. R. Lanz, N. David Theodore

Many sustainability issues arise during the manufacturing processes that are currently used for solar cells. Solar energy is a renewable energy source that is independent of the earth’s resources, and it is therefore important for the development of more sustainable technologies. Microwave annealing (MW) has been proposed as a technically feasible fabrication scheme for large area silicon solar cells. Apart from that, microwave annealing has been demonstrated to be a promising alternative for repairing damage and electrically activating dopants in ion-implanted semiconductors for integrated circuit manufacturing. A microwave oven is cheaper than conventional furnace systems. In addition, microwave heating is much more efficient than conventional furnace heating, as heating is directly produced inside the material. This minimizes the loss of energy due to heating of the ambient. There is a need for more efficient processing techniques. In this study, microwave annealing is used as an alternative to the current postimplantation processing. Arsenic-doped silicon was microwave annealed (with an aluminacoated silicon carbide susceptor) to activate dopant atoms and to repair damage that was caused by ion implantation. Sheet resistance and Hall effect measurements were used to assess the extent of dopant activation. Rutherford backscattering spectrometry (RBS) with ion channeling was conducted to determine the extent of recrystallization. The dopant activation and recrystallization resulting from microwave annealing is compared with that resulting from conventional rapid thermal annealing (RTA) with the same heating profile. The results show that when compared to RTA, susceptor-assisted microwave annealing results in better dopant activation for shorter anneal times under the same heating conditions.

Jan 1, 2015

By Xiao-hui Fan, Xu-ling Chen, Zhi-yuan Yu1, Guanghui Li, Min Gan, Yun-song Huang, Tao Jiang

Compared with the traditional de-NOx processes by cleaning the waste gas, a new approach for reducing the formation of NOx during sintering process is proposed. Since more than 90vol% of NOx comes from the fuel combustion, the influence of sintering coke breeze pretreated by CO(NH2)2 additive on the NOx emission is researched. As adding CO(NH2)2, the reduction agents (NHi) are generated during the pyrolysis of CO(NH2)2, which reinforce the NOx reduction, And the appropriate content of CO(NH2)2 is 1.0 mass% of coke breeze.

Jan 1, 2015

By Cui Wang, Bing Dai, Haibin Zuo, Jianliang Zhang

The damage mechanism of ductile cast iron cooling stave applied to No.4 blast furnace of Guofeng steel was analyzed through damage investigation in details, the damage causes: hightemperature gas flow erosion, wear of burden, high-temperature ablation, carburizing damage, improper operation on blast furnace, etc. were given out both in macroscopic and microscopic views. It can be obtained from metallographic diagrams that the diameter of graphite nodules increases, the number per unit area reduces, and roundness declines, successively, from cold to hot surface, which are not conducive to stave longevity. In summary, the material for staves manufacture should be better in comprehensive mechanical properties to prolong the service life, thus making blast furnace long campaign.

Jan 1, 2015

By Enrui Dai, Weibing Chen, Bin Yang, Wenhui Ma, Haisheng Fang, Hui Wang

LiMn0.8Fe0.2PO4/C composite was prepared by an improved solid-state method and the effect of calcination temperature on properties of the obtained materials was investigated. The results showed that increasing calcination temperature from 600 to 700 oC improved the performance of the LiMn0.8Fe0.2PO4/C due to enhanced crystallinity and increased conductivity, but further increase in calcination temperature to 800 oC led to degraded performance due to particle growth and decrease in porosity. Therefore, the LiMn0.8Fe0.2PO4/C composite prepared at 700 oC exhibited the best electrochemical performance, and could deliver a high capacity of 152 mAh g−1 at 0.1 C, 147 mAh g−1 at 1 C and 114 mAh g−1 at 10 C. In addition, the performance of the LiMn0.8Fe0.2PO4/C and LiMn0.8Fe0.19Mg0.01PO4/C was compared when they were obtained at the optimum calcination temperature.

Jan 1, 2015

By E. B. Zanelato

The process of casting metals and alloys occurs through the fusion of this metal and its subsequent casting into a mold with the dimensions and geometry close to the final piece. Most foundries use sand casting molds for making you. This work aims to characterize and evaluate the foundry sand to allow its use in segments of Civil Engineering, creating a viable destination for a residue is that discarded. The following characterization tests were performer: particle size, chemical analysis, X-ray Diffraction and Density Real grain. For the execution of the test specimens was used to 1:3 cement and sand, and the incorporation of 10% and 20% of the total mass replacing the sand, and the trace reference. The results show that best results in compression and bending tests were obtained by replacing 10 % of common sand for sand casting.

Jan 1, 2015

By Buket Tunçer, Mehmet Buğdaycı, Onuralp Yücel

ZrB2 and TiB2 are one of the most significant metal borides. They are being used in various industrial areas from space technology to nuclear industry owing to their physical properties such as high melting point, high thermal/electrical conductivity and low density. Present study was conducted in two main stages: Self-propagating high-temperature synthesis (SHS) reactions and leaching. ZrO2, TiO2, B2O3 were used as starting material and Mg used as a reductant to produce ZrB2-TiB2 powders via SHS. Therefore, it was aimed to determine production parameters, leaching conditions and comprehensive examination of final product features. The samples were characterized by using chemical analysis (AAS), XRD, XRF and SEM/EDS techniques

Jan 1, 2015

By Yong Xian, Zhaohui Sun, Honggang Zhong, Qijie Zhai, Jie Sun

Vacuum refining is admitted as an effective means to remove impurities in the process of alloy smelting. In this paper, Orthogonal and single factor experiments were carried out to investigate effects of multiple factors, such as superheat degree of the melt, degassing time and vacuum degree, on the vacuum refining process. The results showed that the best removal rate of oxygen and nitrogen is up to 82.71% and 61.3%, respectively, due to high vacuum degassing efficiency. It is found that the superheat degree is minimal impact on the deoxidization rate, in addition, nitrogen removal is controlled by the degassing time. The inclusions exist in the AlV55 alloy are mainly composed of oxides and vanadium-nitrogen compounds.

Jan 1, 2015

By Dany Racine, Daniel Marceau, Denis Laroche, Dmitry Lukovnikov

Carbon base materials play a critical role in the performance of Hall-Héroult cell. The determination of their thermo-physical properties is of primary importance for modeling and designing complete cell systems. However, overcoming the associated experimental hurdles is complex and often underestimated. Of them are the Poisson’s ratio measurements and the continuous oxidation/burning of the materials at temperatures above 200°C. The novel procedure developed in this research is based on the Gleeble® 3800 system. Its vacuum chamber allows test with a chosen atmosphere at temperature of more than 1000°C. Young’s modulus, Poisson’s ratio and the coefficient of thermal expansion values can all be adequately measured using a single test. Cylindrical carbon samples (: 50mm, L: 100mm) were tested in the modified system at temperatures ranging from room to 950°C without any trace of oxidation. The resulting values were also in good agreement with literature data for a specific graphite material.

Jan 1, 2015

By Marcos Aurélio S. Costa, Nilton F. Nagem, Andreia B. Henriques, Herman S. Mansur, Alexandra A. P. Mansur, Antonio E. C. Peres, Valeria G. Silva

The superfine material generated in the Bayer process was used in one innovatively way as a precursor to geopolymerization techniques because of the presence of Gibbsite. Gibbsite can play a role in system adjustment because of the SiO2/Al2O3 ratio. Furthermore in the geopolymeric system it was studied the influenceof the additives such as kaolin, metakaolin and sodium trisilicate in an alkaline media. Others conditions to form the geopolymer were also evaluated such as solid/liquid ratio, SiO2/Al2O3 ratio and total alkaline. The raw materials and geopolymeric products were characterized by several techniques e.g. XRD, DSC, FTIR and SEM. Through the FTIR technique it was observed an increase in intensity and bandwidth in the region centered at 1010 cm-1, which is related to the asymmetric vibration Si(Al)-O, this is an indicating of the possible geopolymer formation This broadening of the band promotes a relative disappearance (overlapping) peaks at 965 and 935 cm-1 associated with raw material (ESPDust).

Jan 1, 2015

By Shengli Wu, Jinming Zhu, Wei Huang, Xinliang Liu

The sinter of high basicity would interact with lump ores or acid pellets in the cohesive zone of blast furnace due to the difference of chemical composition and micro structures. The results of this work showed that the softening-melting properties of lump ores and acid pellet would be obviously improved by the high temperature interaction. However, the high temperature interaction index (INI) would be influenced by many factors, such as chemical composition, porosity, interaction interface and so on. The INI between sinter and porous limonite lump ore (L-2) was much higher than that of dense hematite lump ore (L-1) and acid pellet (P-1). In addition, though the softening and melting properties of L-2 were poorest in respective iron ores, the softening and melting properties of integrated burden B (consist of sinter and L-2) were not worse than other integrated burdens due to the strong high temperature interaction.

Jan 1, 2015

By Run-sheng xu, Hai-yang WANG, Di ZHAO, Teng-fei SONG, Jian-Liang Zhang

This paper was mainly focused on the different semi-cokes and charcoal which could be new fuels for blast furnace injection. Through the comparative study with bituminous coal and anthracite coal, the properties of semi-cokes and charcoal were presented in this research. 10 indexes of different fuels were obtained by different standard experiment, including proximate analysis, ultimate analysis, igniting point, explosivity, transportation characteristic, ash properties, grindability, calorific value, combustibility and reactivity with CO2. According to the data analysis, it provided a theoretical basis for rational utilization of various blast furnace fuels, and helped to broaden the scope of the blast furnace injection fuels. This research could contribute to energy conservation, emissions reduction, and sustainable development of iron and steel enterprises.

Jan 1, 2015

By Ma Lijuan, Zhang Yubing, Wang Bo, Sun Huilan

The effect of lime ratio on phase composition and alumina leaching property of MgO-contained calcium aluminate clinker were investigated by analytical reagent, the XRD analysis of its mechanism was discussed. The results showed that: when the sintering temperature was 1350 ℃, C/A was 1.4, A/S was 1.3 and the content of MgO was 4%, the increase of the C/A promoted the formation of C12A7 and restrained the formation of Q-phase. The alumina-leaching ratio of the clinker (A/S was 1.3) was increased from 74.33% to 91.34% when the content of CaO was 5.21%.

Jan 1, 2015

By Qian Li, Haiyan Leng, Kuo-Chih Chou, Haoyuan Xiao, Zhigang Yu

Magnesium borohydride and Magnesium alanate were synthesized by mechanochemical metathesis reaction. The thermal decomposition behaviors of Mg(BH4)2-nMg(AlH4)2(n=0.5,1) systems were investigated as potential hydrogen storage materials. The results showed that the systems started to desorb H2 at 120 ℃ and desorbed 3.9 wt. and 4.9 wt.% H2 below 300 ℃ when n equals 0.5 and 1, respectively, while individual Mg(BH4)2 started to desorb H2 at 250 ℃ and desorbed only 0.82 wt.% H2. Because of the exist of the Mg(AlH4)2, the isothermal desorption kinetics of Mg(BH4)2 in the Mg(BH4)2-0.5Mg(AlH4)2 systems was 50% faster than that of pristine Mg(BH4)2. In addition, the re-hydrogenation rates also increased 49.4% and 37.9%.

Jan 1, 2015

By Jin-yan TIE, Ke-xin JIAO, Qian Li, Hai-bin ZUO, Jian-Liang Zhang, Meng SHEN

This paper designs three factors such as temperature, pH, conductivity and three levels of orthogonal test. Temperature is a significant factor. However PH and conductivity are not significant through poor analysis. Further research is conducted on the temperature. Temperature stability is 50 . Suitable water velocity is 2.3m/s, which is calculated based on the largest part of the heat flux intensity and the corresponding water temperature should be controlled with 1.5. Meanwhile, water velocity increased has little effect on the heat transfer capabilities.

Jan 1, 2015

By Gaifeng Xue, Xiaohong Xu, Meng Liu, Yijie Song, Guotao Xu, Jixiong Liu

BN (Boron Nitride) based composites were prepared with hot-pressing by using h-BN as main material in ceramic preparation process. The relative density, bending strength, vickers’ hardness, thermal shock resistance, thermal expansion coefficient, thermal conductivity, phase composition and microstructure were tested and analyzed by using modern testing technology. The results indicate that the best formula is B, the relative density is 97%, the bending strength is 260 MPa, the hardness is HV5 343kg/mm2, the thermal expansion coefficient is 2.8×10-6℃-1, the thermal conductivity is 22 W/(m.K) and have no crack after thermal shock for 20 times by water cool. XRD analysis indicates that the main phase compositions are h-BN, β-Si3N4 and sialon. SEM studies show that the grains wrapped up by solid solution.

Jan 1, 2015

By C. B. Piazzarollo

Red Ceramic materials are widely used in Civil Construction in Tropical Countries. However, these materials have high porosity and low mechanical strength. Thus, in order to improve these properties, recycle mineral wastes was incorporated into clay from Campos - RJ, ornamental rock waste, from the gneisses cutting of Cachoeiro - ES, 150 km from Campos. After the addition of up 10% of waste in clay mass, ceramic pieces were produced and subjected to the tests of porosity (P) and flexural strength (FS). The test material contains 53.3% clay and 67% waste slit. The X-ray diffraction identified the presence of kaolinite, quartz and feldspar for the clay and, for the waste, quartz and orthoclase. The results of FS and P showed that the residue influenced, positively, the ceramic piece, with strength gains especially from 920º up to 960°C.

Jan 1, 2015

By Guo Chen, Jin Chen, Jinhui Peng

In this study, the influences of the green evaluation variables on the characterization of microwave shaft furnaces were systematically investigated. These variables include: resource consumption, environment impact, production cost, processing time and quality of microwave shaft furnaces. A greenness evaluation index, evaluation system and evaluation model of microwave shaft furnaces were established. The analytic hierarchy process and fuzzy comprehensive evaluation were applied to the evaluation process. Resource consumption and environment impact had a statistically significant effect on the green evaluation of microwave shaft furnaces. The results indicated that green evaluation techniques can be applied effectively and efficiently to the process manufacturing of microwave shaft furnaces.

Jan 1, 2015

By Vinicius Alves Gomes, Jean Igor Margem, Thallis Cordeiro, Frederico Muylaert Margem, Roberto Faria Jr., Sergio Neves Monteiro, Marina Rangel Margem

Natural fibers are attracting the interest of engineering sectors owing to specific advantages such as lightweight and lower cost as well as for their inherent condition of being renewable, biodegradable, recyclable and neutral with respect to CO2 emission. In particular, the fiber extracted from the malva plant stem is nowadays recognized as one of the strongest lignocellulosic fibers. However, the thermal properties of the malva fibers have yet not been fully investigated. The present work had as its objective to investigate, by photoacoustic spectroscopy and photothermal techniques the thermal properties of diffusivity, specific heat capacity and conductivity of a pressed malva fibers sample. The results revealed that these fibers showed a superior thermal insulation capacity.

Jan 1, 2015

By Qingwei Qin, Ping Xue, Guangqiang Li

Ausmelt furnace slag contains about 0.9% Cu (mass %). With increasing the amount of Ausmelt furnace slag, the recovery of copper from it will produce an enormous economic yield. The recovery of copper by floatation from slow cooled Ausmelt furnace slag was studied in this paper. The phases and composition of the slow cooled slag were analyzed. The factors which affected the copper recovery efficiency such as grinding fineness, pH value of flotation medium, different collectors and floating process were investigated. It was shown that the size distribution of the primary grinding and secondary grinding of middling were 75% for particles less than 0.074mm and 82% for particles less than 0.043mm respectively. The closedcircuit experimental results with butyl xanthate as collector in laboratory showed that the copper grade reached 16.11% and the recovery rate of copper reached 69.90% and the copper grade of tailings was only 0.2%.

Jan 1, 2015