By W. H. Young

The thickness of the coal seam is one of the more important items influencing the productivity and general overall efficiency of operation of a coal mine. The average thickness of coal seams mined in the United States has changed very little in the past 40 years. The first measurement of thickness of bituminous coal and lignite seams was made for 1920, when the average thickness was 5.3 feet.2 The average thickness for later years was as follows: 1945, 5.4 feet; 1950, 5.3 feet; 1955, 5.2 feet; 1960, 5.3 feet; and 1965, 5.2 feet.3 Table 1 includes data on number and production of bituminous coal and lignite mines classified by 1-foot intervals of seam thickness mined in 1920, 1945, 1950, 1955, 1960, and 1965. Though bituminous coal and lignite are mined today from seams of exceedingly variable thickness--less than 2 feet to more than 50 feet--a large majority of the production, 62 percent in 1965, came from seams 3 to 6 feet thick. This is not surprising since the coal seam of moderate thickness presents the least mining difficulties.

Jan 1, 1967

By E. A. von Hahn, T. R. lngraham

The rates of cementation of pd11 on electropolislzed copper cylinders were studied in aqueous perchloric acid solutions at pdII concentrations from 0.02 to 0.1 mM. The cylinders were rotated at various high speeds to reduce the diffusion layer to a minimum thickness. In 0.1 M HClO4 solutions, the cemented palladium is dense, adherent, and shiny. The rate data indicate that there are two stages in the deposition. In the initial stage, the rate of cementation is first order with respect to the pd11 concentration. The second stage is much slower. The first stage is consistent with rate control by the diffusion of pd11 ions to the copper surface, and/or chemical reaction at the surface, and the second stage is consistent with rate control by the diffusion of copper ions from the cop-per surface through the deposit of cemented palladium, out to the main body of solution. In 0.001 M HClO4 solution, only the first stage is evident and the rate is more rapid than at higher acidities. This rate enhancement is attributed to PdOH+ ions that predominate at low acidity and aye more reactive than unhydrolyzed pdII. The deposit is porous and loose. All of the cemented deposits are Pd-Cu alloys rather than pure palladium. Activation energies are 9.5 kcal per mole in 0.1 M HClO4 and 7.4 kcal per mole in 0.001 M HClO4. CEMENTATION or displacement reactions occur between aqueous solutions of metal salts and immersed metals according to the general equation: where M1 is electrochemically the more noble metal. Although these reactions find considerable application in metals recovery processes (e.g., the cementation of copper192 or gold3), in electrorefining processes (e.g., solution purification before electrolysis4,5), and in plating and metal finishing processes,6 few studies have been made of the kinetics of such reactions.7-9 The rates of cementation reactions will depend on one or more of the following factors: a) chemical reactions at the metal-solution interface; b) ionic transport to or away from the interface;'-' and c) the character and adherence of the cemented deposit on the substrate metal,6a,10 because the deposit will inhibit the rate of transport of dissolving ions (M2m+) into the solution. In this investigation, the kinetics of the early stages of cementation were studied to obtain an understanding of the reaction mechanism under conditions in which the deposit was sufficiently thin that its inhibiting effect could be disregarded. To achieve this, very dilute solutions in Mn+ were used. Cementation rates are often fast in the initial stages and transport-contr01led.9 To find conditions under which transport control would shift to chemical control, very high stirring velocities were used to minimize the diffusion-layer thickness. Of the many possible cementation reaction systems, the palladous perchlorate-copper system was chosen for this investigation because it was believed to involve simple ion-for-ion exchange. In addition, there are no interfering side reactions, such as the reduction of hydrogen ions, and anion effects are usually absent in perchlorate solutions. EXPERIMENTAL Materials. Reagent-grade chemicals and redistilled water were used in all experiments. Palladous perchlorate stock solutions (0.02 M) were prepared by dissolving 99.5 pct Pd sponge (Johnson Matthey and Mallory Ltd.) in concentrated nitric acid, adding concentrated perchloric acid, evaporating twice slowly (to prevent PdO precipitation) to a small volume, and diluting in a volumetric flask. To prevent gradual hydrolysis of PdII, the stock solutions were made 0.4 M in HC104. Tests for pdIV (Ref. 11) and C1- were negative. Copper strips were cut accurately from 0.025-in. electrolytic tough pitch sheet, Sample 1 (Mines Branch stock or Canadian Copper Refineries Ltd., Montreal), or from oxygen-free, high-conductivity sheet, Sample 2 (American Metal Climax O.F.H.C. brand, sold by Utility Brass and Copper Corp., Brooklyn). The strips were annealed for 1 hr at 335°C in a stream of purified nitrogen (Union Carbide, Linde Division) which had

Jan 1, 1967

By W. O. Philbrook, R. H. Spitzer, F. S. Manning

A generalized mathematical model has been developed to describe the kinetics of the gaseous, topo-chemical reduction of porous hematite spheres. Gas-solid reduction is permitted at each of three advancing interfaces and is controlled by a complex series-parallel sequence of chemical and transport steps. Despite the fact that transport resistances are significant to the advance of each interface, little deviation from linear advance is predicted for the first 98 pct of reduction. Calculations to predict the movement of magnetite /wustite interface by a solid-state diffusion mechanism have been incorporated into the earlier dense-pellet model.' The porous-pellet model is found to give a better description than the dense-pellet one for McKewan's measurements2 of interface movements in dense polycrystalline hematite reduced in hydrogen-water vapor mixtures. THIS paper reports a continuation of work"3" directed toward the better understanding of gas-solid reactions and the development of mathematical models that may be helpful in the design or control of ore-reduction processes. Laboratory studies of the reduction of single oxide samples in tube furnaces normally employ an abundant excess of pure reducing gas. Reduction may appear to be adequately described by a model assuming gas-solid reaction solely at the iron/wustite interface.''' However, when iron ore is reduced in either a fixed bed or an efficiently operated counter-current column, there are portions of the bed where the partially spent gas is no longer capable of reducing wustite to iron. Nevertheless, the formation of the intermediate reaction products, wustite or magnetite, can and does continue. In order to account for this aspect of the reduction of beds of particles, three semiempirical mathematical models were devised.' One of these was for the limiting case of completely dense particles, and two alternatives were provided for porous particles. For purposes of the analysis, a dense pellet was defined as one in which the wustite and magnetite layers were impervious to the reducing gas when the atmosphere was capable of forming iron. In a porous pellet, the intermediate product layers were assumed to be sufficiently permeable to allow reducing gas to penetrate beyond the iron/wustite interface to form wustite and magnetite by removal of oxygen as a gaseous product rather than by a solid-state redfiction mechanism. Further progress required a better understanding of the reaction of the individual particles with the gas stream. A comprehensive mathematical treatment was developed' to describe the continually changing interplay of transport and reaction steps

Jan 1, 1967

By G. Bonnivard

"A complete laboratory process for the treatment of lateritic ores containing a high proportion of iron, as well as chrome and alumina, has been established. The ores treated originate from the tropical zones and result from superficial climatic alteration. According to recent estimates, the known reserves of such ores reach many billions of tons, thus representing huge potential reserves for the elements they contain.The process used is based on the alkaline roasting of pelletized ore in the presence of sodium carbonate. This treatment results in the separate recovery of pellets of upgraded iron ore, pure chrome oxide and hydrated alumina. The research described in the paper aims at determining the best experimental conditions for obtaining the highest extraction of the required oxide from this type of ore."

Jan 1, 1967

By John Sasadi

The mining industry depends upon inexpensive water transportation. Today, large quantities of mined products are transported by ships over oceans, from continents to continents, over lakes and waterways to the ultimate users. Sometimes, the routes these Bulk Carriers travel cover only a few hundred miles, sometimes thousands of miles halfway around the world. Most of the products of the mining industries are relatively inexpensive. A significant portion of their cost to the ultimate users are in the cost of transportation and not in loading and unloading these commodities at the ports of origination or destination. So far, the industry has produced very efficient loading and un- loading installations, but has very little influence over marine transportation or the design of the vessels themselves. Very little was ever published dealing with integrated transportation systems properly correlating all phases of the operation; namely, loading, marine transportation and unloading bulk materials.

Jan 1, 1967

By J. J. Demeter

A tube-wall reactor with a Raney nickel catalyst deposited on the outer wall of the tube by flame spraying is effective in the practically complete conversion of 3H2+1CO synthesis gas to a high-Btu gas (methane) at an hourly space velocity of 7,000 volumes of gas (NTP) per hour per volume of annular volume. Partially reacted synthesis gas containing an appreciable amount of methane can also be treated in this reactor to increase the heating value to over 900 Btu per cubic foot. Excellent heat removal through the metal wall to a coolant and temperature control were obtained. The heat transfer co-efficient from the catalyst to the coolant was about 275 Btu per hour per square foot per ° F. Synthesis tests were conducted with tubes 1.2 inches in ad by 6 inches long, and 1.3 inches in od by 36 inches long. When operating at a synthesis gas rate of 100 to 120 scfh per square foot of catalyst-coated tube, catalyst life was long enough to realize a catalyst cost for the raw Raney nickel alloy of about 0.3 cent per 1,000 cubic feet of pipeline gas (900 to 950 Btu per scf). Gas recycling at ratios of 1:1 to 3:1 was effective in increasing conversion and in extending the life of the catalyst to about 16 weeks. In cost and in operating characteristics the tube-wall reactor compares favorably with the fluidized-bed and hot-gas-recycle reactor systems for the synthesis of high-Btu gas from H2+CO.

Jan 1, 1967

By Robert M. Asimow, Bisuddhi Riddhagni

THE use of back-reflection Laue photographs for crystal orientation is standard in many research projects. The time required for the orientation of any given crystal depends largely on luck and the skill of the investigator. In any case, where large numbers of crystals are used, this time can be quite considerable when the standard methods involving a Greninger chart and Wulff net are employed. For this reason the technique described below was developed. This new procedure applicable for cubic crystals (without preparation of new charts) largely eliminates the skill and luck factors and makes possible the determination of orientation in minutes. The procedure works in the following way: the Laue photograph is examined and arbitrarily an important hyperbola is picked out. An important hyperbola is defined as one which contains some spots through which several hyperbolas pass. Such a hyperbola inevitably corresponds to a low-index zone axis. The angles between the reflection planes causing all the spots on this hyperbola can be read directly from a Greninger chart in the usual manner. If the hyperbola contains more than five spots, these interplanar angles will positively identify the zone axis and the indices of each of the reflecting planes. However, initially since neither the zone axis nor the Miller indices of a diffraction spot are known, there are a very large number of possibilities that must be considered. Using tables of interplanar angles to check out every possibility would be quite tedious, so that this approach is not generally used. Instead, various poles are plotted on a stereographic projection. In the cubic system, however, it is possible to plot out once and for all the angles between all planes of a particular zone axis up to some upper limit of Miller indices. This has been done for all low-index zone axes in Fig. 1. Given these charts, it is quite a simple matter to identify the spots of the unknown hyperbola. All that is necessary is to plot the angles read off the Greninger chart to the same scale as Fig. l(b) on a strip of paper. Then this strip can be slid along each zone axis of Fig. l(a) until a good fit is obtained. Once this is accomplished, the Miller indices of each spot are given and thus the orientation problem is solved. To check, it is possible to pick a second hyperbola and see whether a compatible solution is obtained. This is most conveniently done by picking for the second hyperbola one that contains a spot common with the first. If the specimen axis is chosen parallel to the incident X-ray beam, then usually the [ loo] hyperbola will appear on the film as one of the more important hyperbolas and consequently will be either chosen initially or as a check. Using the [100] hyperbola, after the (001) or (011) spots have been identified, the latitude and longitude of the specimen axis can be read directly from the Greninger chart so that it is unnecessary to use a Wulff net for the entire orientation procedure. This makes the operation not only quicker but more accurate. Of course, if neither the first nor second hyperbolas correspond to [loo] then a third hyperbola can be chosen.

Jan 1, 1967

By D. J. Crawford

The Lucerne Valley Operations of the Minerals, Pigments and Metals Division of Chas. Pfizer & Co., Inca, are located about 5 miles south of the town of Lucerne Valley, California. These operations consist of several limestone quarries, a whiting plant which produces finely pulverized limestone products, a-kiln which produces granular quicklime and lime products, and maintenance shops, warehousing, shipping, and office facilities. Construction of the Lucerne Valley plant began in 1961 as the result of a decision to utilize large undeveloped reserves of limestone in that area. Quarry development was started in the following year; and by 1965, Lucerne Valley had become the principle limestone and lime facility of the Western Operations of the Minerals, Pigments and Metals Division.

Jan 1, 1967

By R. Simon

Maurer's review1 summarizes quite thoroughly the various theoretical developments and experimental findings that contribute to the knowledge of rock mechanics in drilling. This discussion supplements Maurer's paper by including generalities that either have been incompletely treated in his review, or formulated from new considerations by the discussant and from hitherto unpublished experimental data. These generalities are associated with the observation that all mechanical methods of rock drilling essentially comprise a sequence of indexed, concentrated loadings on the bottom of the hole being drilled. A concentrated loading is defined as a mechanical loading by a tool that contacts at any one time only a small fraction of the surface of the body being worked and penetrates only a small fraction of the body thickness. The surface in this application is the bottom of the hole. The deformation of ductile material by concentrated loading has received considerable attention because of the importance of indentation tests for measuring hardness of metals. Some of the generalities involved in concentrated loadings on ductile materials apply also to concentrated loadings on more brittle materials such as rock. Among these generalities is the applicability of similitude considerations to scaling laws and to force-displacement and energy-volume characteristics for tools of various shapes, as summarized by Tabor.2 Vork on the flow and fracture behaviors of glass loaded with pyramidal and spherical indenters is reviewed by Douglas.3 Maurer refers to the work of Evans and Murrell on wedge loadings on coal and on mixtures of pitch and sand. It is evident from Maurer's paper that a considerable portion of the studies of rock mechanics in drilling, such as crater formation experiments, has involved concentrated loadings on rock.

Jan 1, 1967

Wrenching between basement blocks is considered to be the mechanism whereby a well developed set of en echelon folds and an associated fracture system are developed in the Fitzroy Depression, Western Australia. The regular geometry of these structures accords with a right lateral regional coupling between high-standing, basement blocks bounding a trough filled with a thick pile of stratified Phanerozoic sediments. The structures developed during or after the Mesozoic Era, but the couple is inferred to have been applied to blocks outlined by old lineaments, which may reflect strains or ruptures in basement that developed during the Precambrian, and which were regenerated during Palaeozoic and Mesozoic time.

Jan 1, 1967

By S. G. Cupschalk, F. A. Dahlman, J. J. Wert

Studies have been undertaken to determine the indicidual effects of particle size, degree of long-range ovder, antiphase domain size, and root mean square stran on the microhardness and yield strength of ordered alloys. Dnta have been analyzed for Cu3Pt initzally ordered to a value of 0.82 and after deformations of 1 and 6 pct. It was observed that deformation fleatly reduced the degree of long-range order. Furtherrnore, wztkin this range of relatively small deforntntlons, the average particle size changed very little while the antiphase domain size was greatly reduced. Smultaneosly, the mcrohardness changed by a factor of two durzng the deforrtation process. PREVIOUS studies have reported some of the effects of cold work on the broadening of X-ray diffraction peaks. These investigations were performed on powder and wire samples representing both ordered and disordered states; i.e., the specimens were initially studied in a severly cold-worked condition. By comparing the difference in line shape between the annealed and cold-worked peaks, fundamental information was obtained concerning particle size, strain distribution in different crystallographic directions, degree of long-range order, and change in antiphase domain size. Considerable theoretical work has been done concerning the analysis of diffraction data obtained from cold-worked metals. Stokes' expressed the change in diffraction profiles in terms of Fourier coefficients. Much of the work in this area has been summarized by warren2 in an extensive review article concerning the analysis of plastic deformation by X-ray diffraction. Cohen and Bever3 applied these techniques in studying the effects of cold work on alloy systems exhibiting long-range order. They utilized the Fourier coefficients of fundamental peaks in conjunction with those of the superlattice peaks to determine the change in antiphase domain size. Little work of this nature has been reported for ordered systems that have undergone small degrees of plastic deformation. The purpose of this investiga-tion was to determine the effects of small deformations in such a material with respect to particle size, strain distribution in various crystallographic directions, antiphase domain size, degree of long-range order, and hardness. EXPERIMENTAL PROCEDURE CusPt was used for the initial investigation since the order-disorder transformation takes place with- out a change in crystal structure. The transformation is readily detectable via X-ray diffraction techniques due to the large difference in the scattering factors of copper and platinum. Additionally, the alloy is relatively low melting (approximately 1300°C) and is easily deformable in both the ordered and disordered states. 1) Specimen Preparation and Cold Working. A 100-g, 12-in. diam., cylindrical specimen of Cu3Pt was prepared by melting and casting 99.99 pct pure Cu and Pt i.n vacuo. Prior to any mechanical working, the material was homogenized in a vacuum for 60 hr at 100O0C, and surface defects were removed by machining to a depth of approximately 116 of an in. The material was then cold-rolled, with an intermediate anneal, into a strip approximately 12 in. wide by 14 in. thick. Straightening and flattening removed another 0.025 in. from the thickness. After a recrystallization treatment at 750°C for 30 min, the specimen was slow-cooled from 55OoC, at the rate of 6°C per hr, down to 150°C to induce superlattice formation. This treatment yielded an ASTM grain size of 7 and a degree of long-range order equal to 0.83 0.06. After obtaining X-ray and Knoop hardness data, the sample was cold-rolled approximately 0.75 pct in one pass through a hand-operated jewelers' mill. X-ray and hardness data were again obtained and the specimen was reduced an additional 5.41 pct in a single pass through the mill. 2) X-Ray Measurements. The specimen was examined in the ordered condition and after the two degrees of cold working previously mentioned using a General Electric XRD-5 unit equipped with a spectrometer and scintillation counter. Using Mo-Ka radiation with a zirconium filter, six orders of the 100 reflection were obtained. It was anticipated that point counting would be necessary for an accurate determination of the low-intensity peaks and tails: however, it was demonstrated that, by using a scanning speed of 0.2 deg per min and the appropriate time constant, the recorded data were sufficiently accurate. Thus, for ease of experimental procedure, all peaks were recorded on chart paper. Specimen position in the holder was considered to be insignificant after making a series of measurements of the same peak area in different positions with respect to the beam. Since peak overlapping did occur at high values of 20, it was necessary to separate the peaks graphically prior to analyzing the data in order to minimize this source of error. The peak tails were also carefully drawn to obtain the best possible data. Fourier coefficients of the line profiles were calculated on an IBM 7072 computer, and graphical meth-ods2j3 were employed in analyzing the results. For this type of calculation, in which the line profile is represented by intensities taken at set intervals, the intervals selected must be sufficiently small to give an accurate representation of the line profile. It was decided that for 20 = 0.02 deg the line profiles were

Jan 1, 1967

By Charles R. Simcoe

It was pointed out in a recent paper'g that the initial flow stress of as-quenched martensite is very low even in an alloy steel with an M, well above room temperature. It was also shown that the high ultimate tensile strength resulted from a very high rate of work

Jan 1, 1967

By E. L. Day

"In the early 1930s during the course of test work with a simple gold ore, it was evident that the time required to dissolve the gold by cyanidation was very much longer than should have been needed theoretically for the maximum size gold particles in the ore, A similar conclusion appeared to be valid for other gold ores. In a cyanidation system there are many factors which can influence the dissolution rate of gold, and a decision was made to investigate the more obvious variables, because a literature survey at the time showed that with the exception of the work of Yamazarki on the dissolution of silver in cyanide solution, virtually no attention had been given to this subject, Our work was not reported because the intention was to do this on completion of the Study, but owing to the demands on the Section's personnel for other work the investigation was never completed. Although other investigators have since studied the problem, the methods which we adopted and some of the conclusions may be of interest to metallurgists concerned with gold ore treatment.Form of GoldExperiments with gold ores were not possible because of the number of uncontrollable variables present in a gold ore-cyanidation system, therefore pure metal and reagents were used. Initially some experiments were carried out with gold leaf, but it was soon apparent that metal in this form was unsuitable because the uneven thickness of the leaf caused it to break up into pieces and. there was difficulty in determining precisely when complete dissolution had taken place, Numerous factors both expected and unexpected were found to influence considerably the results and much experimental work was necessary to establish the procedures which were finally adopted, Experiments were carried out with gold in the form of foil, wire, rings and sols. Finally, gold foil in the form of cylinders was adopted for most of the experiments although some work with gold in the sol form was included in the programme. Also some experin1ents were carried out with a gold ore to see if effects which were obtained with sodium chloride on gold sols were applicable to gold ores."

Jan 1, 1967

By George W. Healy, Ko Yamaguchi

In typical calorimetry the energy given off by a material under study is transferred to a water bath, whose temperature is sensed by a thermometer; for correct measurement the water bath must attain a uniform temperature to which the thermometer must respond. This introduces two sources of error, non-uniformity of the heat sink and a time lag until its temperature is registered. These errors may become important where a rapid process such as solidification of metals and alloys is being studied by means of Oelsen'sl quantitative thermal analysis. To overcome this difficulty, a calorimeter sink was conceived in which the water bath is replaced by a copper coil, which serves simultaneously as heat

Jan 1, 1967

By P. L. Hendricks, J. W. Spretnak

The interstitial atom principally responsible for the yield point and strain aging in electron-beam-melted tantalum is identified by analysis of the kinetics of the return of the yield point after an increment of plastic deformation. Two sets of specimens contained two levels of oxygen with very low hydrogen contents and the third set had comparable oxygen and hydrogen contents. The activation energy for the return of the yield point agrees well with that for diffusion of oxygen for the first two sets of specimens. For the third set of specimens, the activation-energy value lies between those for diffusion of hydrogen and for diffusion of oxygen. The advent of the dislocation model of plastic deformation in metals has revitalized interest in the yield point and strain aging in bcc metals containing a certain minimum content of interstitial solute elements. Much theoretical and experimental work has been performed in recent years to elucidate the detailed mechanism of these phenomena. The purpose of this investigation is to attempt to identify the principal interstitial element responsible for the yield-point phenomenon in electron-beam-melted tantalum by analysis of the kinetics of the return of the yield point after an increment of plastic deformation. Some of the earlier theories of the yield-point phenomenon proposed a grain boundary film of iron carbide. Such models could not satisfactorily explain all features of strain aging and the yield-point phenomena. The most widely accepted explanation is that of Cottrell,1 later extended by Cottrell and Bilby.2 Strain aging is ascribed to "locking" of dislocations by interstitial solute "atmospheres". The yield-point phenomenon results when the dislocations are torn away from their atmospheres. The strain-aged condition is re-established after sufficient time to allow the interstitial atoms to diffuse to the dislocation lines and re-establish the locking atmospheres. Clearly, the Cottrell-Bilby model is concerned with the bulk of the grain and does not specifically involve the grain boundary. The recent modification of the Cottrell-Bilby model is a redirection of attention to the role of the grain boundary and the possibility of multiplication of a limited number of free dislocations rather than unlocking all of the dislocations. Theories have been advanced by Hahn3 and conrad4 which are modifications of the Cottrell-Bilby theory. The model proposed by Hahn indicates that, although the possibility of un- locking anchored dislocations is not excluded, it implies that unlocking is not necessarily required to explain yield drop. Locking of dislocations during the aging treatment is a necessary part of the theory; however, it assumes that dislocations once locked remain locked. It is suggested that the yield drop observed is a result of the following factors: 1) the presence of a small number of mobile dislocations initially, 2) rapid dislocation multiplication, 3) the stress dependence of dislocation velocity. In the case of bcc metals, locking is considered to be the means by which dislocations are immobilized. Cold working of the metal results in the generation of larger numbers of new dislocations and the stress dependence of the dislocation velocity accounts for yield drop observed. Conrad' has proposed a model similar to the one just described which applies to strain aging of iron and steel and which logically could be extended to other bcc metals. This model also does not require large-scale unlocking of dislocations. It is proposed that, during initial loading of a specimen below the upper yield stress, a few dislocations are torn free of their Cottrell atmospheres at regions of stress concentrations. With an increasing stress, some multiplication of dislocations occurs by a double cross slip mechanism, thus giving a preyield microstrain. At some critical stress represented by the upper yield stress, sudden profuse multiplication of dislocations occurs, enabling plastic flow to proceed at a lower stress. In this model, microstrain, preyielding, and flow represent the movement of free dislocations. It should be noted that this model also requires the locking of dislocations by interstitial solute atoms for the occurrence of a yield point; however, unlocking of large numbers of dislocations is not required. If it is assumed that the yield point will return when some fraction of free dislocations produced during pre-straining are pinned, the number of solute atoms required to pin unit length of a dislocation line can be calculated when prestrain and reloading are done at the same temperature and strain rate. Since the migration of solute atoms back to the stress fields of dislocation lines is controlled by the diffusion rate of interstitial solute atoms, it is to be expected that the activation energy for strain aging would be identical to the activation energy for diffusion. It would also be expected that the strain aging observed will be controlled by the fastest diffusing species capable of producing locking over the temperature range investigated. The rate of yield-point return has been found to be adequately expressed by an empirical rate equation of the form: rate=Ae-Q/RT [1] where A = constant, Q = activation energy, R = gas constant, and T = absolute temperature. Cottrell and Bilby2 have expressed the number of atoms per unit length of dislocation line which arrive

Jan 1, 1967

By K. L. Komarek, P. F. J. Landler

Synthetic polycrystals of wustite were reduced ilz H2-H2O mixtures over limited roncentration ranges wiltun the wustite. field and the weight changes were continuously followed with a McBain quartz spiral balance. The reduction was. found to be controlled by a combined surface plus solid-state diffusion reaction. The solid-state diffusion had an activation energy of 38 kcal. Self--diflusioities of iron decreased with itzcreasing vacancy concentration. The activation energy of. the surface reaction runs different tor- different samples. The surface reaction-rate constan increased with increasirzg vacancy concentration. THE reduction of the oxides of iron has been studied for many years. Edstroem' has summarized the early work and has provided much information on the reduction of magnetite and hematite by hydrogen and carbon monoxide. More recent summaries are those by smeltzer2 and Themelis and Gauvin.3 Most investigators have reported that the iron metal which forms the outer layer during gaseous reduction is rather porous. According to Kohl and Engel14 the formation of such a porous iron layer depends on the properties of the underlying wiistite layer, on the reaction of the gas with the wustite surface, and on the transport of matter through the wustite layer. McKewan, Quets, Wadsworth, and Lewis, and Knacke 10 have found that, if a porous iron layer is formed, a surface reaction between gas and wustite at the bottom of the pores controls the rate of reaction. Seth and ROSS 11 and Warner 12 have pointed out that the influence of the gaseous pore diffusion through the porous iron layer cannot be neglected. It has further been shown that the wiistite layer formed during reduction is dense and that transport of matter across the layer occurs only by solid-state diffusion of iron ions.13,14 The solid-state diffusion rates observed by Edstroem and Bitsianis 14 and the surface reaction rates observed by Quets eta1.' show that an interaction of the two steps in controlling the reaction rate has to be considered. In this investigation the reduction of wustite was studied with respect to the interaction of the two steps, isolated from any other effects, by reducing wustite within the wustite field from higher to lower oxygen concentrations with H2-H2O gas mixtures. A similar study with CO-CO2 mixtures has been performed by Levin and wagner.15 Fused synthetic wustite polycrystals were reduced in steps of 0.4 wt pct from 24.4 to 23.2 wt pct 0 and over a temperature range from 700" to 1050°C. A few tests were also conducted with reduction steps from 24.4 to 23.6 wt pct 0 and 24.5 to 23.2 wtpct0. The Fe-O phase diagram is shown in Fig. 1 where the composition of the gas phase in equilibrium with the condensed phases is plotted as pct H2 vs the temperature. A careful study of the literature led to the conclusion that the fully drawn equicomposition curves (in wt pct O) in the wustite field used by Edstroem 1,16 and other authors needed some correction. Based on results by Darken and Gurry17 (shown as open circles) and on some of our own data, four corrected curves for 23.2, 23.6, 24.0, and 24.4 wt pct O were calculated (drawn as dashed lines in Fig. 1) which should replace the fully drawn equicomposition curves. MATERIALS AND APPARATUS Materials and Specimen Preparation. Wustite was prepared from iron sulfate (Fisher Scientific Co., New York) which had a purity of over 99.92 pct, with small amounts of manganese, copper, and zinc adding up to 0.03 pct. From the aqueous solution iron oxalate was precipitated and decomposed to magnetite according to Economos. 18 The magnetite powder was pressed into cylinders and sintered in vacuum at 900°C for several hours. The sintered compacts were placed in a platinum crucible of 2.5 cm diam which was fitted into a high-purity alumina crucible and then inserted into the center of the graphite heating element of an electric resistance furnace.lg The furnace was evacuated to below 1 p Hg and the magnetite sample was slowly heated. The evolution of gases during heating deter-

Jan 1, 1967

By Thornton L. Neathery

Geologic investigation of a mineralized zone in eastern Alabama indicates that large quantities of talc and soapstone are scattered over a wide area close to the surface. Laboratory experiments show that this material may be upgraded to a high-quality talc. A market survey indicates that the talc deposits may be of current and long-range interest. The anthophyllite asbestos which is associated with the talc does not appear to occur in sufficient quantities to be considered as a primary commercial source.

Jan 1, 1967

By Edwin M. Thomasson

Helium shipments for 1965 exceeded the volume shipped during the previous year for the 16th successive time. Shipments from Bureau of Mines helium plants were 698.6 million cubic feet, 2 about 4.7 percent more than in 1964. Production at Bureau of Mines plants totaled 757.4 million cubic feet, and an additional 3,549.6 million cubic feet was produced by private companies participating in the helium conservation program and purchased by the Bureau of Mines and stored underground for future use. The Bureau of Mines continued to sell helium at $35 per thousand cubic feet, the price established in 1961. Production and sales of helium increased from the one private plant operating entirely outside the Government's helium program. A second private plant was virtually complete at yearend, although actual production had not commenced.

Jan 1, 1967

By P. T. Allsman

INTRODUCTION The honor of being the recipient of the Mining Society's Daniel C. Jackling Award for 1966 imposes on me the responsibility to search for the subject that I would be best qualified to discuss. It seems that my experience in the mineral industry — nearly 15 years in private and 30 years in public employment — should uniquely qualify me to comment upon the relationships between the mining industry, mineral engineering as a profession, and government, and the changing economic, technologic, political and social changes that dictate their relationships. Such conditions, the increasing knowledge of the world mineral resource base, the greater demands of an expanding population with a rising standard of living, shall be evaluated with respect to our profession — mineral engineering. In all of these forty or so years, I have been in close touch with many phases of the mineral and energy resource industries, especially those of the United States. Particularly during the past 10 years, I have had a ringside seat at the "goings on" in Washington. During all of this period I have observed and analyzed many of the problems of the industry and its relations with the government. During the past few years, I have had increased opportunity for doing research and have found a need to learn something about the mathematical techniques that are undergoing such a revival since electronic computers were developed. One of these techniques is multivariate analysis, which is a system for correlating a large number of complex variables. By applying this technique to the seemingly chaotic present-day situation, there emerges a course of steady improvement in the minerals resource industries that wars, depressions, and political strife have failed to obstruct for long. In short, I advocate a need for new concepts in mineral engineering to cope with the changes, pos- sibly adding many more specialized areas on one end of the spectrum, and broad engineer-generalist approaches at the other. The meeting place shall be where the intricate mineral resource problems at the frontier of knowledge merge into the socio-techno-logical problems of the world. HISTORICAL INVOLVEMENT OF GOVERNMENT IN MINERAL RESOURCE PROBLEMS Involvement of government in mineral resource problems undoubtedly is as old as government itself. But passage of the Mining Act of 1866, superseded by the Act of 1872, was the first major entry of our Federal Government into the problems of mining. Passage of the law was necessary to resolve many conflicting claims and disputes in mining. The General Mining Law of 1872 and the Mineral Leasing Laws of 1920 apply to millions of acres of public lands and to certain privately owned land on which the mineral rights have been reserved to the Federal Government. The extensive involvement of government in the mineral industry business today often comes as a shock to the mineral engineer who has begun to climb the ladder to the top in his company. He is often poorly prepared to cope with the situation and becomes frustrated and even hostile. Better knowledge of the role of government perhaps would ease his situation. In our political system, private industry is responsible for producing minerals. To make certain that the production is adequate for a peace-time economy, and to guarantee the Nation's security in an emergency, the Federal Government finds it expedient to develop policy and engage in regulatory, educational, and research activities. A few examples will illustrate the varied role of government in relation to mineral problems. In varying degrees many agencies of the Executive Branch of Government have responsibilities that influence the functioning of the mineral and energy industries. In addition, of course, Congress, the Judiciary, and State and local governments exercise great influence. The Department of the Interior is primarily responsible for activities to promote the development and conservation of mineral and fuel resources, and the

Jan 1, 1967

By Robert C. Bates

Variations in water percolation rates through saturated cohesionless hydraulic backfill (mill tailings) have been studied in relation to the many physical aspects of the system to determine the most important factors in causing these variations. A multivariable least-squares regression analysis of 135 separate tests shows that a reliable estimate of the water percolation rate through typical hydraulic backfill can be made if the bulk density (unit weight), specific gravity, and grain-size distribution are known or can be estimated. Equations for predicting percolation rate, coefficient of permeability, and seepage velocity are developed both for the range of data analyzed and for extrapolation. The prediction equations for use within the range of data studied are quite accurate, while the ones developed for extrapolation are less accurate but still give reasonable approximations of flow rates. The equations given are valid for cohesionless materials that are free of clays and micas, exemplified by classified mill tailings. The equation developed for predicting percolation rates is as follows: 1nP20 = 11.39147 + 2.853422 1n(VR X D10) + 0.1747436 VR X Cu -178.8039 D10 X D50 + 311.7034 (DSO )3, (1) where P20 = percolation rate, inches per hour at 20° C; correction factors for other temperatures are given in the text, VR = void ratio, dimensionless, D10 = effective size (diameter in millimeters of the 10-percent-finer grain size), Cu = coefficient of uniformity (ratio of the diameter of the 60-percent-finer grain size over D10), D50 = average size (diameter in millimeters of the 50-percent-finer grain size), and In = natural logarithm (log to the base e). The prediction equation for percolation rate is rather complicated, so for practical use a nomograph that simplifies the solution of the prediction equation was developed.

Jan 1, 1967