By D. Kunstelj, M. Stubicar, A. Tonejc, A. Bonefacic

A. Bonefafcic, D. Kunsfeli, M. Stubicar, and A. Tonejc The present communication is concerned with the variation of the texture in aluminum wires with die angle and temperature, at constant speed of extrusion. Experiments were carried out concurrently on refined samples, with a stated purity of 99.997 pct pure A1 and commercial samples of 99.5 pct Al. Ingots of refined aluminum samples were machined to 30-mm-diam by 150-mm-long billets. These billets were transformed to 5-mm-diam wires by drawing. The final form, suitable for examination, was obtained by extrusion through conical-face dies with a 1-mm hole diam and extrusion ratio 5:l in diam. The initial form of the commercial aluminum samples was drawn wire 5 mm in diam. These samples showed a poorly defined texture with (111) as a major and (001) as a minor component. A similar defined texture appeared in the refined aluminum samples after drawing to 5 mm diam. Conical-face dies with different angles (defined by the axis and the generating line of the cone) were used in our experiments. The values of the angles were 27, 35, 45, 57, 63, and 90 deg. The extrusion container was fitted with a heating element and controller permitting temperatures up to 600°C to be maintained within i5"C. Extrusion was performed at 250°, 300°, 350°, 400°, and 500°C at constant speed (approximately 1 mm per sec) and constant die reduction. The extrusion product was a wire 1 mm in diam and approximately 20 cm long. In order to remove the surface layer with the "conical" texture and to reduce the absorption by the X-ray examination of the samples, the extruded wire was etched to 0.22 mm in diam. Experiments were performed in the middle sections of the 20-cm-long wires. In addition to the die of l-mm hole diam, dies with a 1.5-, 0.7-, 0.6-, 0.5-, and 0.4-mm hole diam and 63-deg die angle were constructed. In our experiments we did not find in these ranges any important difference concerning the texture of the extruded wires and we continued our work solely on the 1.0-mm die. The diffracted X-rays (Cu K radiation) were recorded photographically. Diffracted intensities were measured on the (111) reflection with a microphotometer. The relative amounts of texture components were determined from the areas under the diffracted maxima. We found the texture of extruded aluminum wires to be strongly influenced not only by the temperature of extrusion and the purity of the sample but also by the form of the die. It is generally admitted that cold-drawn aluminum wires have mainly a (111) texture with a small amount of (001) component, Table I of Ref. 1. In our experiments with wires extruded in conditions represented by Fig. 1, in some cases a single (001) texture was obtained. If these wires were drawn repeatedly at room temperature, X-ray measurements revealed a duplex (001)-(111) fiber texture. Further drawings increased the (111) and decreased the (001) texture component. In Fig. 1 the percentage of material oriented with (001) parallel to the extrusion direction is represented as a function of the temperature and the die angle (a), for commercial and refined aluminum samples, respectively. From these diagrams we may draw the following conclusions. The slope of the die (a) influenced more strongly the texture at the lower rather than the higher temperatures. Again, a stronger influence was found in the case of the commercial in comparison with refined aluminum samples. In the case of the commercial aluminum samples the amount of material with (001) texture increases with increasing wire temperature in an approximately linear manner. This effect is less pronounced in the pure aluminum samples, with the exception of the die with a = 45 deg. In this case the (001) texture decreases with increasing temperature, as shown in Fig. 1. Component (001) is more pronounced in higher-purity aluminum samples. Our experiments led to the conclusion that both (001) and (111) components are essentially stable in extruded aluminum wires. As we obtained a single (001) texture starting with a sample of drawn wire in which the (001) component was very weak, our experiments revealed that the (001) component is not a remnant of the initial texture; this is in disagreement with the findings of Vandermeer and McHargue.1 We gratefully acknowledge discussions with Professor M. Paic. 1 R. A. Vandermeer and C. J. McHargue: Trans. 7MS-AME, 1964, vol. 230, p. 667.

Jan 1, 1969

By Colin M. Sargent

THE electron diffraction pattern as seen in the electron microscope represents an approximately plane section of the reciprocal lattice. Identifying the zone axis of a diffraction pattern is often laborious for a crystal of low symmetry, especially if several crystal orientations are present. A program has been written in FORTRAN II (Version 2) for the IBM 1620 which will assist in plotting out reciprocal lattice sections. The calculation is performed by choosing a zone axis [uvw] and determining the d spacings and angle between the planes (Ow - v) and (wO - u). (This procedure is varied slightly for zone axes with Miller indices equal to zero.) Cartesian coordinates for the reciprocal lattice points are then calculated for these planes and for (ww— [u + v]). Any reciprocal lattice points within the parallelogram formed by the origin and these three points are then computed. The input and output are best described by use of an example (Monoclinic ZrO2) used in the author's work. Input consists of two cards: 1) The crystal parameters: a, b, c, a, 8, y, e.g., 5.1477, 5.2030, 5.3156, 90.000, 99.380, 90.000. 2) Three numbers, D, E, F, e.g., 5, 3, 3.0710-the first is the limit of the sum (u + v + w) considered; the second limits the absolute value of u, v, and w to (E- 1), e.g., 2, so that zones (221) would be the highest order considered in this example; the third, F, is the required constant, yL. Output is in the format shown in Table I. The reciprocal lattice sections may then be plotted on standard graph paper and compared with the unknown diffraction pattern. (Note that no attempt has been made to deal with systematically absent reflections.) A card deck for the program is available from Colin M. Sargent, ARZ, W-PAFB, Dayton, Ohio, 45433.

Jan 1, 1969

By M. J. Hordon, M. A. Wright

ReCENT work has indicated that the substantial decrease in the rate of fatigue crack propagation for aluminum observed below a critical vacuum level can be attributed to the depletion of oxygen or water vapor from the vicinity of the fatigue crack opening.' At reduced gas pressures, generally below 10-2 Torr with fatigue strain amplitudes in the range *1 to 2 x 10-3 and cyclic loading rates of 25 to 50 cps, estimated rates of oxide or hydroxide monolayer adsorption on newly formed crack surfaces can fall behind the actual rate of crack extension. Changes in the critical pressure required for the transition in fatigue behavior with changes in temperature, strain amplitude, and cyclic frequency can be interpreted from variations in the adsorption and crack growth rates.'" Although the adsorption model generally appears to explain the enhanced fatigue resistance of reactive metals in vacuum, the specific adsorbing gas species and nature of the adsorption mechanism are uncertain. In addition to the direct dissociation and adsorption of O2 on the metal surfaces,3 the dissociation of H20 and subsequent adsorption of H ions have been advanced for aluminum alloys.4 The present note describes some measurements of the fatigue behavior of 1100 aluminum in reduced partial pressures of specific gases including O2, H2O, and H2 in order to provide additional experimental data. Cantilever-type specimens of 1100-H14 aluminum were fatigued in cyclic reverse bending at constant strain amplitude using a multispecimen vacuum apparatus and procedure described previously.' After initial vacuum evacuation to 1 x 10-7 Torr, the appropriate gas species was bled into the system through a calibrated leak valve. The input rate was adjusted to maintain the desired pressure level under continuous evacuation, thus minimizing possible changes in gas composition during testing. High-purity input gases including 99.9 pct O2, 99.999 pct H 2, and water vapor from triply distilled H 2 O were used to provide residual pressures. Trace amounts of contaminant species were limited by passing the Oz and H 2 input gases through liquid-nitrogen-cooled copper coils prior to entry to the test chamber. Care was taken to repeatedly flush the gas lines and valves before testing to minimize the effect of adsorbed contaminants. Residual gas pressures in the range 10-6 to 5 x x3 Torr were monitored by an NRC ionization gage corrected for each gas species. In the higher-pressure range, 5 x 1CT3 to 5 x 10' Torr, an NRC alphatron gage was used. In operation, eight simultaneous fatigue tests were conducted at a constant strain amplitude of *1.2 x 10 at cyclic bending rates of 25 and 50 cps to give an average fatigue life of 6.5x 105 cycles-to-fracture at standard atmosphere and 3.3 x 106 cycles in 1 x 10"7 Torr vacuum. Representative results for the effect of residual O2, H2O, and H2 contents on the fatigue life are shown in Fig. 1 for tests performed at 50 cps. It is apparent that the presence of either O2 or H2O gas in the system at partial pressures greater than 10"3 Torr was noticeably detrimental to the fatigue life. In contrast, the enhanced fatigue resistance typical of high-vacuum environments was retained with pure H 2 through the pressure range up to 1 Torr. For partial pressures of H2 gas above 1 Torr, the fracture life noticeably decreased. The critical Hz

Jan 1, 1969

By J. A. Goebel, S. Rosen

IN the NiAl phase diagram the NiAl (CsC1-type) phase field extends over a large composition range. At elevated temperatures the nickel-rich phase boundary extends to a composition of about 70 at. pct Ni, a value which is within 5 at. pct of the Ni3A1 (Cu 3 Au-type) phase boundary.' At room temperature, however, the maximum nickel content is only about 60 at. pct. Experiments have shown that alloys containing greater than 63 at. pct Ni when quenched from temperatures below 1000°C contain the equilibrium phases NiAl and Ni3A1. On the other hand, when these same alloys are quenched from temperatures above 1000°C and examined microscopically, a typically martensitic decomposition product appears in the microstructure as shown in the micrograph of Fig. 1. The structure of the martensitic phase has been determined by employing powder X-ray diffraction techniques to be an "ordered" AuCu type (Strukturbericht Llo, space group P/4 mmm - DL). The diffraction pattern of this phase differs from that of AuCu in the appearance of superlattice lines. The structure is shown in Fig. 2. The open circles represent nickel atoms and the half-shaded circles represent nickel and aluminum atoms which are randomly distributed. The sites represented by half-shaded circles would be occupied solely by nickel atoms at a stoichiometry of Ni3A1. The alloys used in this investigation were prepared from 99.99 wt pct Al and 99.99 wt pct Ni by arc melting charges of varying compositions in a water-cooled copper hearth using a tungsten electrode in a gettered argon atmosphere. In all cases chemical analysis agreed within $ at. pct with the nominal compositions of the alloys. Annealing treatments were carried out in a vertical resistance furnace through which a stream of argon gas was flowing. Specimens, which were wrapped in tantalum foil, were quenched by allowing the specimens to drop into a bucket containing iced brine. X-ray diffraction patterns were obtained from -325 mesh powder specimens by using a 114.8-mm

Jan 1, 1969

By T. W. Watson, D. R. Flynn

,Measurements are reported for the thermal conductivity of four heat-resistant alloys which were measured at the National Bureau of Standards. Data are given for two samples of AISI Type 316 stainless steel covering a combined temperature range from -150° to + 800°C. The thermal conductivities of three samples of AISI Type 347 were measured over the temperature range from -150° to +150C. Thermal conductivity values are given for Carpenter 20 stainless steel from 100" to 800" C. Data are given for Inconel 702, in both the solution-annealed and the age-hardened condition, over the temperature range from -150" to +800C. SINCE 1958 the National Bureau of Standards, at the request of other government agencies or private laboratories, has carried out measurements of the thermal conductivity of a number of metals and alloys. This paper presents available thermal conductivity data obtained in this way on samples of four heat-resistant alloys. The data presented for Carpenter 20* stainless steel are, to the best of our knowledge, the only thermal conductivity values which have been reported for this alloy to date. Although thermal conductivity values for AISI stainless steels 316 and 347 have been reported by previous investigators, the present data are believed to be of particular interest because, for each alloy, the effect on thermal conductivity of small changes in chemical composition can be observed. The data on Inconel 702' are of interest, not only for

Jan 1, 1969

Filter aids are currently used in many industries to increase filtrate clarity and filtration rates. In other industries filtration could be improved if accept- able filter aids could be obtained cheaply. The present paper describes a simple thermal process for making filter aids from coal, outlines the effects of coal properties and major operating variables, and discusses the properties of satisfactory products. Several possible variations in reactor design have been used experimentally, involving fluidized beds of carbon or inert material, reaction of the particles while entrained in air, and a combination of entrainment and fluidization. The limits imposed on product yields by the composition of the parent coal are considered in relation to a range of Australian coals and one New Zealand coal; and the effects of temperature, residence time, and reactant flow rates have been studied in relation to product yields and characteristics.

Jan 1, 1969

By Ted C. Briggs

The Bureau of Mines is evaluating the thermodynamic properties of helium and helium-containing mixtures. Twenty-two compressibility runs were made with helium at 0° C and pressures to 800 atmospheres using a Burnett-type apparatus. Data from the 22 runs were treated simultaneously and as separate runs while different functional forms and weighting factors were used. A fourth-degree-polynomial equation in the pressure gives a statistically satisfactory representation of the compressibility factor when the data are treated simultaneously and a weighting factor of Pr-3/4 is used. The second virial coefficient of helium at 0° C from this investigation is 11.997±0.015 cm3 mole-1. The stated uncertainty is the random error standard deviation. Compressibility factors determined by this investigation are precise to better than 0.01 percent and are believed to be accurate to better than 0.02 percent.

Jan 1, 1969

By R. W. Smith, M. E. Brookes

The temperature at which th: quenched 0' (ordered bcc) phase transfo.rms to the ( (complex hexagonal) phase on heating has been examined for certain Ag-Zn and Ag-Au-Zn alloys using an electrical resistivity method. The transition temperature decreases by approxinzately 7°C as the zinc content is reduced by 1 at. pct. The critical temperature, Tc, for long-range order has also been measured for a number of Ag-Au-Zn alloys. Extrapolation to zero gold content suggests that Tc decreases by approximately 5°C per 1 at. pct reduction in zinc content. The 0 phase of the Ag-Zn system exists over a narrow range near the composition Ag zn,' Fig. 1, and has a bcc structure which is disordered above 272°C. Slow cooling to temperatures below the range 274"/258"C allows the complex hexagonal phase, r° to form.2 This is the stable structure at room temperature.3 Upon quenching 0 -phase alloys from high temperatures, it is found that the 0 — (' transformation is suppressed; but ordering takes place (i.e., 0 -0'). This ordered structure can also be obtained by the room-temperature aging of cold-worked (0.4 Deformation of the 0' phase gives rise to a fur- ther hexagonal phase ( (of nearly ideal axial ratio) which reverts to b' within a few hours.= In view of this, it has been suggested that the equilibrium struc-

Jan 1, 1969

By E. Zucker

In this paper, as in the 1960 CIM paper of the same name, s1gmf1cant new developments in electrical-mechanical mining equipment are briefly described. These include static thyristor-supplied D.C. drives for mine hoists, load-haul-dump systems, process controls with small and medium-size computers, and several other new items of equipment and Concepts. All the new hardware descriptions are given in the context of over-all process integration. This means the actual mechanical linking together of two or more processes and the preliminary step in the development of production-line mining.

Jan 1, 1969

By H. J. Heinen

Excellent gold recovery was demonstrated in a laboratory-scale leaching test on waste material from an open-pit mine in northeastern Nevada. An injection system of leaching was applied in which the sodium cyanide solution was introduced into the interior of the dump at selected points. Dissolution of gold from the waste material, which assayed 0.06 ounce gold per ton, was readily achieved because the gold occurred as submicroscopic particles in a porous host rock. Gold recovery of 80 percent was obtained in 11 days from material crushed to 1 inch in size, and recovery was 90 percent after 21 days.

Jan 1, 1969

By W. A. Weimer

Australia, the land of the kangaroo, koala, and the platypus, is often referred to as "down under" by people of the Northern Hemisphere. It is a tropical land and has very little freezing and thawing; consequently the in-place rocks are near the surface, exposing some of the unaltered mineralization. This type of geology induces the prospector and miner to search for minerals which lie at his feet (or not far under them), and it is adapted to open cut surface mining. Some of the rules and regulations applicable to exploration and mining in Australia will be interesting and helpful towards understanding acquisitions and control of minerals. They are common and basic to the United Kingdom. Throughout Australia practically all minerals are the property of the Crown (government), and their exploration and exploitation are administered by the state Department of Mines. Surface owners, or land lessees, do not control the minerals. Their mining codes protect the prospector. If a prospector obtains a permit, "miner's right," it entitles him to search for minerals any place within the state, only holding him responsible for damages he may incur in his exploration. If he finds something of interest, he may then apply for an authority to prospect, which gives greater latitude and protection in his work to develop the find. However, he will be obligated to spend a minimum specified amount to exclusively hold an area. He will be required to furnish maps, analyses, and geological data to the Mines Department. Presuming that he has located something economically valuable for mining, he may then apply for a mining lease or be granted a franchise to produce a specific material. It will contain a quantity clause so that the area cannot be held indiscriminately without production of the mineral. The states have Bureaus of Mineral Resources, Geology, and Geophysics that keep constantly abreast of the search for minerals and often do much of the drilling and deep boring to promote geological study for the states.

Jan 1, 1969

By M. J. Marcinkowski, K. S. Sree Harsha

A detailed numerical analysis has been made of the equilibrium configuration of partial dislocations in a blocked deformation twin under an externally applied stress. Twins made up of both pure screw and pure edge partials have been considered. The components of stress in the vicinity of the twin tip associated with each of these configurations have been plotted. It has been found that at some critical degree of oblateness the shear stress fields of the blocked screw or edge twin can both sPontaneously nucleate slip, whereas only the component of stress oxx about the edge twin can nucleate and propagate cracks. TWINNING becomes a predominant mode of plastic deformation at low temperatures and/or high strain rates. Fig. l(a) shows what must be the first step in the formation of a deformation twin, namely the formation of a loop of imperfect dislocation bounding a stacking fault. In an fcc crystal the partial dislocations have Burgers vectors of the type 1/6 a,(112) and the fault is of the intrinsic type while in the bcc crystal the partials have Burgers vectors of the type ao(lll). The stacking sequence of (111) planes in a perfect fcc crystal is given by ABC ABC, and so forth, and in one which contains a twin by ABCABACBA, and so forth. It is apparent that the stacking fault and twin give rise to no mistakes associated with adjacent close-packed planes; however, with respect to second-neighbor close-packed planes the faulted crystal has twice as many mistakes as the twin. The energy of the twin boundary may thus be taken to be one-half that of the intrinsic fault boundary. In the case of the bcc crystal the stacking sequence of (112) planes is given by ABCDEFABCD, and so forth, in a perfect crystal, by ABCDCDEFA, and so forth, in a crystal which contains a fault, and by ABCDCBAF, and so forth, in one which contains a twin. An analysis similar to that applied in the fcc crystal shows that both the fault as well as the twin involve no neighbor violations across adjacent planes. However, there are twice as many violations across second-neighbor (112) planes associated with the fault as compared to that of the twin. Thus once again the energy of the twin boundary may be taken as one-half that of the fault. It is important to note that, unlike the fcc, the faults in the bcc crystal involve first nearest-neighbor violations and are thus expected to be of much higher energy than those in fcc crystals. A more detailed analysis of the material discussed above can be found in Ref. 1. To a good approximation then, the lenticular twin shown in Fig. l(b) can be generated by adding partial dislocation loops on successive (111) planes for fcc crystals or (112) planes for bcc crystals in the manner shown, with no additional expenditure of chemical energy other than that required for the fault shown in Fig. l(a). In practice, deformation twins are much more extended than that shown in Fig. l(b) and more closely resemble one shown schematically in Fig. l(c). It is readily apparent that the free energy of the twin and matrix are identical. In those cases where the partials lead to a structural change, the free energy of the material contained within the dislocation array is lower than that of the matrix and we have the so-called martensite transformation. The present investigation is the first in a series of five major theoretical-experimental efforts which will deal with the static and dynamic behavior of twin nucleation and growth. There has been a recent surge in activity pertaining to the equilibrium shapes of twin lamellae2'3 and

Jan 1, 1969

By D. H. Chambers

The Bureau of Mines developed a process for producing high-purity zinc and tin by electrorefining from liquid amalgams. Commercial grade metals were dissolved in mercury to produce saturated amalgams at room temperature. Amalgams were also prepared by electrolytic transfer from soluble anodes of the metals to a mercury cathode. Amalgams formed by both methods were used as anodes in electrorefining cells to produce high-purity cathodes. Metal impurities, excluding mercury, were at levels of less than 5 ppm in zinc and 9 ppm in tin. Mercury content was about 2 to 10 ppm in zinc products, and this was effectively removed by heating the cathodes in a vacuum. Mercury was excluded from tin cathodes by pumping the tin electrolyte through tin turnings and controlling the cell temperature.

Jan 1, 1969

By P. S. Kotva

Dislocation substructures in superalloy matrices of varyzng co)npositions have been studied. In general, it has been found that the alloys can be classified into ''high", ''medium", and "low" stacking fault energy classes based on the type of dislocation substructure observed in the matrix and that the substructure can be correlated to the stacking fault energy. The effect of different types of dislocation substructure and dislocation reactions on the intragranulur precipitation of carbide phases has been studied. In a Ni-Cv-Mo-Fe matrix, precipitation of MC carbides in association with stacking faults has been observed. In most superalloys, solid-solution strengthening and precipitation hardening are the chief mechanisms employed to achieve strength. The latter contribution to strength is usually achieved by the precipitation of / in certain wrought alloys. Insufficient attention has been given to the problem of obtaining strength in su-peralloys by controlling precipitation of carbides on imperfections within the matrix. The present work was undertaken to investigate the dislocation substructure in various superalloy matrices, to study the effect of such substructure on subsequent precipitation of carbides in the matrix, and to investigate whether certain modes of precipitation of carbide phases found in austenitic stainless steels2"4'6 would occur in nickel-base alloy matrices with dislocation substructures of the same type as those found in austenitic steels. 1) EXPERIMENTAL TECHNIQUES Five-pound heats of the various alloy compositions reported here were vacuum-cast. The ingots were given light deformation by rolling to break up the as-cast structure and then homogenized for 24 hr. HASTELLOY alloy X (nominal composition: Ni-2OCr-17Fe-8Mo-0.05C) was homogenized at 2150°F and In-cone1 625 (nominal composition: Ni-20Cr-5Fe-8Mo-3.5Cb-0.05C) was homogenized at 2280°F. Fabrication of 0.004-in. sheet was achieved by cold rolling with intermediate annealing treatments being carried out at the same temperature as those used for homogeniza-tion. Each solution anneal was followed by quenching. The aim of this procedure was to redissolve as much of the primary carbide phase as possible. Samples of the 0.004-in. sheet were cut and encapsulated in quartz capsules and then heat-treated in the tube furnaces. Thin foils were prepared using an ethanol-10 pct perchloric acid bath at 32°F and at a voltage of 22 v. A "window" technique was employed. Observations were made on a JEM-7 electron microscope operating at 100 kv. 2) EXPERIMENTAL RESULTS a) Types of Dislocation Substructure. Fig. 1 shows a schematic correlation between stacking fault energy, SFE, and the type of dislocation substructure observed in various matrices of nickel- and cobalt-base alloys. A precise quantitative determination of stacking fault energy is not implied in the figure but the correlation between stacking fault energy and the type of dislocation substructure obtained allows alloys to be divided into three classes in analogy with the classification employed by Swann and ~uttin~' for binary alloys of copper. Class I alloys are associated with a "high" SFE and show a cellular substructure of dislocations as typified by the micrograph of a thin foil of pure nickel deformed 4 pct at room temperature in Fig. 2. With decreasing SFE the tendency toward cell formation is lessened and dislocations tend to be arranged in coplanar groupings. Examples of this class of alloys with "medium" SFE are provided by the mi-crostructure of solution-heat-treated, quenched, and deformed thin foils of HASTELLOY alloy X, "Waspaloy" (prior to any aging), and Inconel 625. Fig. 3 shows a thin-foil micrograph of an alloy of Inconel 625 composition, solution-heat-treated, quenched, and deformed 5 pct at room temperatures. No evidence of any cell structure can be obtained in materials of "medium" stacking fault energy, Fig. 3, even after severe deformation. The stacking fault energy of the alloy shown in Fig. 3 is, however, not low enough to make the dissociation of dislocations visually obvious. As stacking fault energy decreases further, with successive addition of solute in the matrix, there is an increased tendency toward dissociation of dislocations and cross slip becomes progressively more difficult. Eventually, when the stacking fault energy is "low" enough, complete dissociation of dislocations is seen to occur as shown in Figs.

Jan 1, 1969

By David R. Poirier

Activity data of carbon as a function of both temperature and composition throughout the stable austenite range is correlated by mearts of an equation derived from a quasi-chemical model. The carbon activity data of austmite for temperatures between 800° and 1200°C are utilized in conjunction with the activity of carbon calculated for the y solidus using the activity of carbon in liquid iron and published austenite-liquid equilibria. The results agree very well with Chip-man's correlation; however, a small difference in the activity of carbon in the high-temperature range of the austenite field is evident. Excellent agreement is found for the heat of solution of graphite in infinitely dilute austenite; from this study the value is 10,550 cal as compared with Chipman's value of 10,680 cal. AS part of a program to study microsegregation in dendritic solidification of ternary Fe-C-Cr alloys, it was desirable to be able to describe the equilibria between austenite and liquid iron in Fe-C-Cr alloys. In this regard, it was necessary to correlate existing data on the activity of carbon in Fe-C austenite as a function of both temperature and composition. At that time, Chipman's analysis1 of the thermodynamics of binary Fe-C austenite was not available. It will be shown that this study and Chipman's study agree rather well throughout the stable austenite range of temperature and composition; however, some small differences appear at temperatures greater than the eutectic temperature. Benz and Elliott 2 presented isoactivity lines for austenite superimposed on their revised Fe-C phase diagram. Using an expression from Darken and Gury 3 representing Smith's4 activity data between 800" and 1000°C, they found that the activities extrapolated above 1000°C to the solidus did not agree with the activities determined from the corresponding liquidus compositions. It is the purpose of the following argument to reconcile carbon activity data of austenite with the activity in liquid Fe-C alloys as determined by Rist and Chipman. 5 In addition, a simple analytical expression is sought for computational convenience. ACTIVITY DATA OF CARBON IN ZRON Fig. 1 shows the activity of carbon in Fe-C austenite as determined by Smith, 4 Schenck and Kaiser, 6 Scheil et a1.,7 and Bungardt et al.' The lines are merely drawn to separate the data into the respective isotherms. These data are inadequate to determine the activity of carbon at temperatures greater than 1200°C. The activity coefficient in Fe-C liquid alloys was assumed by Rist and chipmans to obey the following

Jan 1, 1969

By d&apos, L. Berenbaum, F. Heurle, R. Rosenberg

The structure of aluminum films obtained by evaporation was studied by electron microscopy, mostly by replica techniques and X-ray diffraction. The resistivities and stress conditions of the films were also determined. Film properties were studied as a function of source selection, substrate type, residual pressures of oxygen and water vapor, substrate temperature, and rate of growth. The formation of abnormal localized growths and whiskers resulting from annealing treatment subsequent to deposition was investigated. Films deposited onto single-crystal substrates were found to be epitaxially 0riented; for such films, relative orientations between films and substrates were determined. ALTHOUGH wide use has been made of evaporated aluminum films for the formation of conducting lines on semiconductor devices, relatively little has been reported concerning the structural characteristics of such films.1"9 The purpose of this study was to obtain an overall view of the dependence of these characteristics on film deposition and subsequent annealing conditions, which were similar to those used in silicon planar technology. Accordingly, most of this study was carried out using oxidized and bare silicon wafers as substrates, although some work was also done using alkali halide, magnesium oxide, and mica substrates. However, the main concern remained pragmatic. Emphasis was given to the study of the effects of deposition and annealing conditions on film characteristics such as structure, resistivity, and stress. I) EXPERIMENTAL PROCEDURES The films which were investigated in this study were deposited in 18-in.-diam glass chambers which were connected to the usual type of trapped diffusion pumps filled with silicon oil. Through the use of liquid-nitrogen-cooled Meisner traps and titanium sublimation pumps placed inside the deposition chambers, the pressure could be lowered to the lower portion of the 10- I Torr range and little increase in pressure would occur during the deposition cycle. Unless described otherwise, the substrates were 1-in.-diam p-type silicon wafers having a resistivity of 10 ohm-cm. The wafers were oxidized in wet oxygen at 975°C followed by a short dry-oxygen exposure at the same tempertture to a total oxide thickness of approximately 6000A. The wafers, backed by a layer of gallium, were mounted onto molybdenum discs brazed to a copper block.10 The latter was heated by imbedded commercial cartridge heaters. The substrate temperature could be maintained to within +10°C of a prescribed temperature during film deposition. The search for a satisfactory source for the controlled evaporation of aluminum has led to the use of 1-in.-diam crucibles" machined from rods of a commercially available, refractory composite* of Bn and

Jan 1, 1969

By Charles T. Holland

The tonnage produced on mechanized automated retreating longwall faces in the United States is growing rapidly. This time last year some 14 faces were operating, and in addition to that, three were known to be down looking towards revision or repairs before being placed back in service. These, it is believed, are now in service. It is estimated at the present time, therefore, that somewhere between 20 and 25 faces are being operated in the country. A survey made last year by the School of Mines, West Virginia University, indicated that longwall mining in general has been beset with a great many problems, some more serious than others. The problems that we propose to discuss here are those pertaining to roof and floor trouble in the tailgates. Longwalls are operating in this country at the present time under an overburden ranging from 200 feet to nearly 3000 feet. Main and tailgate entries are operating in panels of up to five each, with the width of the pillars between these entries varying from 20 to 50 feet. Face lengths are running from 270 feet to 670; actually a face 800 feet long should be possible. The most economical face is often spoken of as being around 450 feet.

Jan 1, 1969

By E. J. Rapperport, J. P. Pemsler

We have made calculations to evaluate the sensitivity of atomic absorption as a technique to measure vapor pressure changes with temperature. Our conclusion, supported by the experimental findings presented in this work, is that the ultimate sensitivity of the technique is well below lo-' Torr. This magnitude of vapor pressure sensitivity makes the method extremely attractive for thermodynamic studies. Atomic absorption techniques have been used previously in this connection by Scatchard and Boyd' and by vidale2 with a much lower sensitivity reported. Scatchard and Boyd's work measured cadmium pressure over Ag-Cd alloys in the range 0.02 to 0.3 Torr, and Vidale estimated that sensitivities of only 10"5 to 10"6 Torr are to be expected. Atomic absorption appears to be particularly well-suited to thermodynamic studies for several reasons: A) It is extremely sensitive; our experiments indicate an ability to measure vapor pressure changes of 10"9 Torr. B) It is highly selective; there is seldom interference among the resonant wavelengths of the various species. C) It may be performed in an absorption cell under static conditions. This alleviates such problems as surface impoverishment of alloys, attainment of equilibrium, and temperature measurement and control. D) Simultaneous, or near-simultaneous, vapor pressure measurements may be made for several elements in a given system. Experimental. The physical basis of the technique is the highly selective absorption of particular wavelengths by specific atomic species. In most atomic absorption work the element of interest is incorporated into a hollow cathode lamp to provide a characteristic spectral source of high intensity. The spectra lines characteristic of the element in the cathode are attenuated by atoms of that element in the radiation path. Radiation from silver or cadmium hollow cathode lamps was directed along a path containing a 10-cm evacuated silica cell. The cell was positioned within a silica windowed furnace and contained silver, cadmium, or an Ag-Cd alloy. As the furnace temperature was elevated, the number of atoms of the absorbing element in the vapor phase within the cell rose, and the resonant radiation was increasingly absorbed. Intensities were measured by passing the radiation through a Techtron Model AA-4 one-half meter grating atomic absorption spectrometer equipped with a photo-multiplier detector. In order to minimize instabilities in the source, the hollow cathodes were allowed to warm up for several hours and were run at only 2 5 to 30 pct of their maximum rated amperage. In addition the attenuated beam was monitored before and after each reading. The attenuation of resonant wavelengths may be related to vapor pressure by the following relationships.

Jan 1, 1969

By F. Weinberg

Lead single crystals have been deformed in tension over the temperature range of 4.2°K to the melting point. Changes in flow stress resulting from temperature cycling and strain rate cycling have been measured as a function of temperature for crystals of different orientations and purity. It was found that the flow stress ratio, after correcting for the temperature dependence of the shear modulus, decreased progressively with temperature above approximately 0.5Tm. The activation energy calculated from the high-temperature portion of the curve was found to be markedly higher than that of self-diffusion. For single glide crystals, the corrected flow stress showed an increase above 0.5 Tm before decreasitzg with temperature. This increase is attributed to static recovery occurrittg during temperature cycling. THE temperature dependence of the flow stress, based on temperature cycling and strain rate cycling, has been extensively investigated,' and on the basis of these results dislocation models of the work-hardening process have been proposed. In general, the flow stress is divided into two parts, ts, the short-range interaction term, which is only effective at low temperatures and which decreases with increasing temperature, and TG, the long-range stress term, which is independent of temperature after allowing for the temperature dependence of the shear modulus. The observations demonstrating that tG/µ is independent of temperature were generally carried out at low temperatures to minimize recovery effects. Several investigations have been reported on flow stress measurements at high temperatures2"5 which demonstrate that TG/µ does not remain constant at temperatures above 0.5Tm (where Tm is the melting temperature of the material in OK). Specifically, Hirsch and warrington3 carried out temperature cycling tests at two strain rates on single and polycrystalline aluminum up to 0.8 Tm and on polycrystalline copper. For aluminum they found that the flow stress ratio (the flow stress at temperature T2, divided by the flow stress at the reference temperature T1 in one temperature cycle) dropped progressively with increasing temperature above 0.5Tm. From the slopes of the high-temperature portions of the curves, they determined an activation energy for the deformation process of 1.6 ev (at best) which they considered was in agreement with the activation energy of self-diffusion, 1.35 ev. Calculations of the activation volume demonstrated that the deformation was not controlled by dislocation climb. They proposed a mechanism in which the rate-controlling process at high temperatures was due to the rate of move- ment of vacancies away from jogs, i.e., that of self-diffusion. Results of Lucke and Buhler4 on single crystals of aluminum confirmed this conclusion. They measured the critical resolved shear stress of aluminum over a wide range of temperature and strain rates. They found that the temperature dependence of the critical resolved shear stress was similar to that of the flow stress ratio, as determined by Hirsch and Warrington, and from their data calculated an activation energy for high-temperature deformation of 1.35 ev identical to that of self-diffusion. More recently Gallagher5 has carried out a detailed investigation of the temperature dependence of the flow stress ratio of copper, silver, and gold. In all cases, he found that the flow stress ratio, after adjusting for the shear modulus temperature change, drops at high temperatures. The activation energies he determined were found to be appreciably higher than the activation energy of self-diffusion of the material being considered. The flow stress ratio was found to be dependent on the orientation of the material, and, in addition, an anomalous increase in the flow stress ratio for copper, oriented for single glide, was observed above 0.5Tm. The purpose of the present investigation was to measure the critical resolved shear stress, the flow stress ratio, and the strain rate sensitivity of lead, primarily as a function of temperature. The results should indicate whether, following Lucke and Buhler, the critical resolved shear stress of lead has the same temperature dependence as the flow stress, and, following Hirsch and Warrington, whether the activation energy for high-temperature deformation in lead is the same as that of self-diffusion. Lead deforms as a normal fee material,6'7 is available in high-purity form, can readily be grown as single crystals, and, for this investigation, has the very considerable advantage of having a low melting point, 327°C. The observations of the critical resolved shear stress of lead have been published elsewhere.' EXPERIMENTAL PROCEDURE The experimental procedure was essentially the same as that used in the critical resolved shear stress measurements.' Single crystals of 99.999 pct (59) and 99.9999 pct (69) lead were deformed in tension with a table-model Instron in a silicone oil bath above room temperatures and in a cooled methyl alcohol or liquid-nitrogen bath below room temperatures. The test specimens were rectangular in section, 0.65 by 0.33 cm, and had a 5-cm gage length. The specimens were grown as single crystals with tapered ends, which fitted into matched tapered grips for testing. To obtain the flow stress between two temperatures, specimens were first deformed approximately 1.0 pct at the higher temperature. The test was then stopped, the load relaxed, the oil bath removed without disturbing the specimen, the grips and specimen cooled with a fan and then immersed in liquid nitro-

Jan 1, 1969

By d&apos, I. J. Agati

The stockpiling and reclaiming of bulk materials can be a challenging task for engineers seeking the optimum solution for plant needs, reliability, and at lowest unit cost. The objective of this paper will be to expose advantages, disadvantages and limitations of many storage and reclaiming systems to the responsible engineer and management. The paper will emphasize the practical aspect of stockpiling and reclaiming methods. Many valuable and interesting papers are available dealing with the theoretical viewpoint and application of a particular manufacturer's machine. Several of these are mentioned in the bibliography. As many practical parameters as possible will be given. After twenty years in the field of designing and selling bulk materials handling systems, the needs of the user and the plant are recognized and reasonably understood. This paper cannot give solutions to all problems In this vast field but will stress practical applications and examples of various installations. The evolution of advancements in materials handling is based upon not only technological innovations, but learning from many experiences of others and utilizing them as stepping stones to improved installations.

Jan 1, 1969