By M. J. Ferrante

The preparation and subsequent reduction of vanadium trichloride was investigated as a process for the production of high-purity vanadium metal. Chlorine was reacted with vanadium oxide in the presence of carbon to vanadium tetrachloride. The contaminant vanadium oxytrichloride was also formed and later converted to tetrachloride by reaction with chlorine in the presence of activated charcoal. Vanadium tetrachloride was stirred continuously during thermal dissociation to vanadium trichloride powder from which volatile contaminants were removed by distillation. The vanadium trichloride powder was reduced to vanadium sponge by controlled feeding of the trichloride into molten magnesium. Excess reductant and byproduct salt were removed from the vanadium sponge by high-vacuum distillation. Batches as large as 6.5 kilograms of sponge metal were prepared at an average reaction efficiency of 98 percent. Vanadium sponge after consolidation by arc-melting contained 820 to 11330 ppm of interstitial impurities and had a hardness between Rockwell B 40 and 70, This metal exhibited excellent workability at room temperature. The purification of impure vanadium metal by electron-beam melting resulted in lowering interstitial impurities from 1,890 to 504 ppm and hardness from Rockwell B 87 to 28.

Jan 1, 1968

By J. M. Steininger

The mechanism of flotation of sphalerite with sulthydryl compounds of different acidities has been interpreted in terms of chemisorption of unionized collector molecules on hydroxylated zinc surface sites. At a constant collector concentration of 1.5 x 10 -4 M, the upper pH limit of flotation has been found to be directly and closely related to the negative logarithm of the collector acidity constant, pKa The experimental results indicate that flotation is prevented when about 95% of the collector is ionized. At low pH, collector adsorption decreases because of the reduction in number of hydroxylated zinc surface sites. These two effects explain why sphalerite does not float with the more acidic sulfhydryl compounds. Typical anionic collectors for sulfide minerals are short chain xanthates or dithiophosphates which are nearly completely ionized in the generally alka- line flotation circuits.1,2 Flotation mechanisms have therefore been usually interpreted in terms of ionic collector adsorption and competition with ionic depressants of the same sign as the collector. A few attempts have been made, however, to consider adsorption of neutral collector molecules. Contact angle measurements obtained by Wark and cox3 have been interpreted by Cook and Nixon4 as representing adsorption of the free acid molecules on sulfide minerals such as pyrite, galena, chalcopyrite, and sphalerite. Cook and Nixon tried to show that the free acid concentration of the collector was substantially constant along the curves relating collector addition and minimum pH for bubble adherence. However, in a review of the subject,5 Sutherland presented new data on the flotation of pyrite with mercaptobenzothiazole which did not support the hypothesis of constant concentration of either collector ions or collector free molecules. He further showed that, with the assumption of constant occupation of surface sites, both theories lead to relations between pH and collector addition having similar mathematical expressions. In fact, with the more likely assumption of variable occupation of surface sites which results in more complex relationships, it appears impossible to

Jan 1, 1968

By R. K. Koch

The vapor pressures of liquid molybdenum and liquid zirconium were determined by the Langmuir free-evaporation method. An electron-beam furnace with a water-cooled copper crucible was used for melting. Temperature was measured with a two-color ratio pyrometer. The vapor-pressure data led to the following equations: [log p (atm) = 5.429 - 28,380 T for liquid molybdenum in the range 2,890° to 2,990° K, and log p (atm) = 6.521 - 30,940 T for liquid zirconium in the range 2,229° to 2,795° K.] Third-law evaluations of each data set gave mean heats of sublimation (298.15° K) of 157.6 ± 1.8 kcal/mole and 148.4 ± 2.4 kcal/mole for molybdenum and zirconium, respectively, where the uncertainties are two standard devia¬tions. Second-law standard heats of sublimation determined from sigma plots and tabulated enthalpies were 143.5 ± 2.7 kcal/mole and 149.2 ± 3.8 kcal/mole for molybdenum and zirconium, respectively. The better agreement in heats of sublimation for zirconium is attributed to the 566° K temperature range studied which permitted a more accurate definition of the vapor pressure curve than could be obtained from the 100° K span for molybdenum. This supposition was verified by making a sigma-prime plot which utilized solid vapor pressure data for molybdenum to extend the evaluation range by 800° K. This gave a standard heat of sublimation of 155.2 ± 1.6 kcal/mole which is in good agree¬ment with the third-law value. The plot also gave a standard entropy of sublimation (298.15° K) of 35.73 ± 0.48 eu.

Jan 1, 1968

By P. L. Weston, S. E. Khalafalla

A systematic study was made by the Bureau of Mines on the effect of so me hypothesized accelerators for the process of wustite reduction in carbon monoxide. When small concentrations of promoter materials in the order of 0.69 at. pct were added to the reducible charge, the rate of reduction to iron was increased. Promotion phenomenon prediction was made in light of a suyface reduction mechanism with the aid of Vol'kenshtein's effect regarding the propagation of crystal lattice disturbances by small amounts of relatively larger interstitial ions. The acceleration produced by a typical promotor, such as potassiunl, increases with protnoter concentration up to a maximum, beyond which the reduction rate decreases. Concentration for maximum promotion depends on the nature and physicochemical properties of the promoter. The extent of reduction rate enhancement is found to be directly proportional to the atomic volume and electronic charge of the additive. DESPITE the enormous volume of literature on iron oxide reduction, very little is reported concerning additive or impurity effects on this important metallurgical process. The beneficial effect bf calcium compound additions on the reducibility of iron oxide sinters has been reported by Tigerschiold,1 vor dem Esche,2 and Edstrom. Doi and Kasai~ found that the addition of lime or limestone to iron ores helps to break up any unreducible compounds, such as fayalite or ilmen-ite. and thus free the combined iron for reduction. Schenck et al. 5 suggested that the increased reduction rate obtained when adding lime could be accounted for by the instability of wustite in the presence of lime. Acid-base slagging reactions resulted in wustite disproportionation according to The dicalcium ferrite formed will yield iron and calcium oxide during reduction. Regenerated calcium oxide dissociates more wustite. This mechanism has been used by Seths and white7 to explain their experimental results. Recently, Strangway and ROSS' attributed the calcium carbonate acceleration of iron oxide agglomerate reduction to increased porosity, both initial as well as that developed during reduction. Aside from calcium carbonate, or oxide, no other promoter was noted in the literature, except for a brief mention by Barrett and woodg on the effect of sodium carbonate and aluminate as activators for the hydrogen reduction of magnetite at 600°C. The present investigation systematically studied a host of other promoters, including calcium and sodium, in an attempt to elucidate the mechanism by which promotion takes place and to fit the results into a simple chemical model. To attain this goal, the effect of promoter physical properties, such as atomic volume, electronic charge, and concentration are related to wustite reduction kinetics in this paper. Wustite reduction to iron, rather than the overall hematite reduction, was chosen since this reaction is known to be the slowest, and hence the rate-deter mining step for the overall iron oxide reduction process. EXPERIMENTAL PROCEDURE Raw Materials and Their Preparation. The pure or impregnated wustite pellets were prepared from minus 400-mesh chemically pure hematite powders. A known weight of hematite was thoroughly and uniformly mixed with a calculated weight of the additive. The mixed paste containing 35 wt pct water was gradually heated from 400" to 1200° C and fired at 1200°C for approximately 4 hr in an air atmosphere. After cooling, the sinter was pulverized to minus 100 mesh and pelletized into minus 4- plus 5-mesh spheres. Pellets were fired, similarly to the paste mix, air-cooled, sized, and stored. An appropriate weight of the charge (20 g) was placed in a zirconia reduction tube maintaining a uniform oxide bed height of 1 cm and a cross section of 7.1 sq cm for all of the test runs. The samples were supported in the vertical reaction tube by a bed of fragmented insulating firebrick plus 3- to 6-mesh alumina beads. The hematite was then transformed to wustite by reduction with a 30 pct CO2-70 pct CO gas mixture at 1000°C in a globar furnace. Complete conversion to wustite was ascertained by a continuous infrared gas analyzer recording the CO-CO2 content of the effluent gas until no carbon monoxide was absorbed from the inlet gas, and inlet-outlet gas analysis remained constant for 30 min. The wustite sample was then reduced with 100 pct CO at 100WC. From the recorded data, an initial rate of reduction was determined by the initial slope of the graph percent reduction vs time. In order to estimate the accuracy of the data, five separate determinations of the reduction curve of pure wustite, under otherwise identical conditions, were performed. The maximum deviation from the average reduction at 14 min amounted to 2 2 pct reduction. This deviation corresponds to 3.8 pct variation based on the percent reduction of the sample. Aiiy impurity effect below the limits of this maximum deviation was considered a spurious result. If the effect exceeded + 4 pct, then it was considered as a positive one. Considerable care was exercised in determining the initial rate from the slope of the initial segments of the curve. Each reduction curve was examined separately on large graph paper and the best tangent to the curve at zero time was drawn. The slope of this tangent was taken as a measure of the initial fractional reduction per minute. Although the time required to reach 50 pct reduction may be of special practical significance, initial rate measurements are invaluable in fundamental studies. These rates provide a measure of the process kinetics on the initial

Jan 1, 1968

By E. L. Litchfield

The electrification of ammonium nitrate-fuel oil (AN-FO) blasting agents by pneumatic loaders is described and discussed. The consequences of the electrification are considered in light of the initiation requirements of electric blasting caps. It is recommended (1) that semiconductive loading tubing be utilized and (2) that the resistivity of the AN-FO be controlled; it is further recommended that the operator (3) test to assure continuity of the electric detonator legwire-bridgewire-legwire circuit prior to insertion of the cap into charge or borehole, (4) keep the legwires shunted but not otherwise connected to ground during loading of the blasting agent into the borehole, (5) assure that the borehole is discharged prior to hooking up the detonator leads, (6) assure that he is himself discharged prior to handling the detonator leads, and (7) assure that the blasting cap leads are never carried to the AN-FO loader. The basis and significance of these recommendations are explained.

Jan 1, 1968

By Wilson Blake

A mathematical model based on the finite element method of stress analysis has been used to describe the behavior of the western wall of the Kimbley Pit as its slope was steepened from 45 degrees to 57 degrees. Theoretical stress changes because of slope modification are slight except at the toe of the modified slope. Magnitudes of stress created are small when compared with the strength of a competent rock. Resulting displacement patterns point out the need for determining the in situ state of stress at a site prior to excavation or modification. A comparison of model results with field measurements shows that, in general, the model has described the measured behavior of the west wall of the Kimbley Pit remarkably well.

Jan 1, 1968

By Frank C. Di Luzio

REMARKS BY FRANK C. DI LUZIO, ASSISTANT SECRETARY OF THE INTERIOR FOR WATER POLLUTION CONTROL, BEFORE THE ANNUAL MEETING OF THE AMERICAN INSTITUTE OF MINING ENGINEERS, NEW YORK CITY, FEBRUARY 25-29, 1968 POLLUTION PROBLEMS AFTER MUNICIPAL-INDUSTRIAL WASTE CONTROL I am happy to have this opportunity to discuss pollution problems related to the mining industry and the role of mining engineers in protecting our environment. Technological Power and Pollution of the Environment The increasing power of technology to destroy and disrupt the natural environment and the ecological systems upon which life depends has reduced man's margin for error in the use of this power. We must act, therefore, to deter and prevent the occurrence of future ecological disasters such as that caused on the British and French coasts by the sunken oil tanker, the TORREY CANYON, the Clinch River fish kill which occurred when a dam broke and released coal ash from a power plant operation, or that which threatened on the Clark Fork River in Montana when a strike at the Anaconda Copper Company threatened to shut down pollution control activities, thereby endangering fish and plant life on the Clark Fork River with copper waste. In the past, pollution of the environment has tended to be slow. But now, the increased power of technology to damage nature, the loss of in¬sulating space and the compression of time--all reduce our margin for error and the cushion which space and time once provided for our mistakes.

Jan 1, 1968

By P. Nyul, S. Caplan, M. F. Lamorte, T. Gonda

Therrnal resistance is measured on GaAs laser diodes in the temperature range 77" to 300°K. These data show that typically the thermal resistance increases fifteen times from 77 to 300°K. The increase is attributed to the decrease in thermal conductivity of Gds. Nornzalized thermal-resistance experimental and calculated from published thermal-conductivity data) values are compared and good agreement shown. In many practical applications, it is desirable to obtain high average power output from laser diodes. Average power output is determined in large measure by the external efficiency and thermal resistance of the diode.'-3 The average input power with which a laser diode may be pumped is dependent on the thermal resistance. Thermal resistance has been studied over the temperature range from 77" to 300°K which is usually of interest in practical applications. This correspondence presents data on thermal resistance for GaAs laser diodes and compares them to values calculated from thermal-conductivity data. Junction heating arises from three distinct components: 1) joule heating, 2) nonradiative recombinations, and 3) reabsorption of radiation. In high-threshold lasers, joule heating predominates.4 Typically, the nonradiative recombination is not negligible and contributes significantly to junction heating. The loss caused by reabsorption may be of the order of the joule-heating loss.' The fabrication and the geometry of laser diodes have been described in other publications.5 The data presented were obtained from diodes which were fabricated from the same region of a wafer to minimize differences. Fig. 1 shows four types of heat sinks employed in this study. In types 1 and 2, the laser cavities are alloyed; pressure contacts are employed in types 3 and 4, and indium is plated on the inside faces to improve the intimacy of contact between the diode and the heat sink. The thermal resistance R is defined by the following relationship: where AT is the junction-temperature rise above the heat-sink temperature for the diode power dissipation Pd. For measurement of thermal resistance, a direct current is passed through the junction, in the range from 1 to 50 pct of threshold. The diode is placed in the laser mode by superimposing a current pulse of low-duty cycle on the direct current.3 Junction-temperature rise is obtained from the time-resolved laser spectrum at the leading edge of the current pulse.' Typically, the laser line shift is 2.5A per OK. The resolution employed in these experiments is 0.5A; therefore, the accuracy in the temperature measurement is 0.2K. Typically, the temperature rise is 2" to 20°K. The power dissipation is the difference between the dc power input, and the radiation power exiting the diode. The measurement accuracy is less than 1

Jan 1, 1968

By N. Arbiter

Fracture under low velocity free-fall and double impact, and under slow compression have been-investigated. The pattern of breakage and the size distribution of resulting fragments for sand-cement and glass spheres have been determined. Photoelasticity methods were used to simulate the stress distributions in free-fall impact in order to explain the observed patterns of breakage. Oblique fracture planes, occurring only in free-fall impact, develop along lines which coincide with the trajectories of principal compression as determined by mathematical analysis Breakage efficiencies for different modes of fracture were compared for both types of spheres. For the same specimen and loading system, static loading and low velocity dynamic loading induce geometrically similar stress fields resulting in reasonably similar fracture patterns and shapes of fragments.

Jan 1, 1968

By Arthur R. Still, Paul Gilmour

The ore deposit of the Iron King mine occurs in a group of steeply-dipping metamorphosed eugeosynclinal volcanic and sedimentary rocks of Precambrian age. Within this sequence, the ore deposit lies at the contact of a unit made up of rhyolitic tuff and interbedded andesite and a structurally underlying series consisting of andesitic tuffs, minor rhyolitic tuffs, and argillaceous sediments. Field evidence suggests that these rocks have been overturned. The ore deposit is made up of a series of overlapping, conformable or bodies consisting of massive pyrite and associated lenses of massive quartz. These contain recoverable amounts of gold, silver, lead, zinc, and copper. A parallel zone of copper mineralization occurs within the hanging-wall rocks. The deposit is considered to belong to a large and important group characterized by mineralogical composition and the lithology and structural type of the host rocks. Evidence regarding the origin of the deposit is reviewed, and it is concluded that the ore bodies were formed through the agency of volcanic hot springs on, or near, a submarine surface of deposition

Jan 1, 1968

By L. A. Neumeier

Sound experimental ingots of zinc alloys for use as rolling slabs were cast with a specially constructed, semicontinuous casting machine. Nominal alloy compositions of Zn-1.0 percent Cu, Zn-0.12 and 0.36 percent Ti, and Zn-1.0 percent Cu-0.03 to 0.36 percent Ti were cast. This Bureau of Mines study was conducted to evaluate the suitability of the casting procedure for providing stock for rolling into sheet. Microscopic examination of ingot sections revealed structures in which grain size varied from the outer to center ingot zones. Columnar grains present in the center zone of the Zn-1.0 percent Cu ingot were absent in the titanium-containing ingots. The ingots with titanium displayed a finer grain size and eutectic structure in the center ingot zone than in the outer zone; the transition in grain size between the two zones was quite abrupt in some ingots. The overall grain size of the titanium-containing ingots was finer than that of alloys cast by more conventional methods. Chemical analysis revealed that compositional segregation is not a significant factor in the formation of the ingot structure. Microstructural studies of small ingots of similar alloys solidified at slow, fast, and intermediate rates confirmed that the ingot structure in the semicontinuous-cast ingots is related to cooling rate, which is, in turn, related to the particular casting machine design and the influx of cooling water on the withdrawing ingots. Microstructures of thin sheet hot-rolled from slabs of the semicontinuous-cast ingots demonstrated that the ingot structure does not preclude the rolling of sheet having a uniform microstructure. Results of hardness surveys of the semicontinuous-cast ingots demonstrated that copper and titanium exert essentially additive hardening effects in these cast alloys.

Jan 1, 1968

By R. J. Wagner, G. H. Gronhovd, A. J. Wittmier

The paper describes the results of a series of full-scale boiler tests run to determine the ash fouling characteristics of a North Dakota lignite as a function of sodium content of the coal. Four levels of sodium were investigated and rate of fouling was determined both by boiler performance and by specially constructed probe equipment. Discussed is information on chemical and physical properties of the ash deposits. The vast lignite deposits in North Dakota are becoming increasingly important as a source of low-cost fuel for power generation. A new 200-megawatt lignite-burning plant located near Stanton, N.D., was placed in operation early in 1966. Another 172-mega-watt unit in the same area is scheduled for operation late in 1966, and plans have recently been announced for a 212-megawatt unit to be in operation by 1970. If these plants show good performance, western North Dakota could become a major power production center for a large geographic area in the upper midwest. One of the problems associated with the use of lignite in power boilers is its tendency to form troublesome ash deposits on boiler tube surfaces. This problem varies considerably from one lignite-fired boiler to another and is dependent upon such factors as source of lignite, boiler design, load factor, tube metal temperatures, and soot-blowing practices. This report presents data on sodium content* variation in a North Dakota mine, describes the results of a series of tests performed to determine the relationship between ash fouling tendencies and the sodium content, and tells how the mining company and electric utility have coordinated their operations to reduce the ash fouling problem. GENERAL BACKGROUND Until recent years it was generally assumed that North Dakota lignite from a given mine had qualities peculiar to that mine, but that within the mine, the lignite was quite uniform. In 1959, the Otter Tail Power Co. installed a 53.5-megawatt lignite-burning unit at its Hoot Lake plant, Fergus Falls, Minn. Shortly after the unit was put into operation, it was noted that at certain times under high load conditions, ash fouling problems were quite severe, but not consistent or predictable. Each time fouling occurred in the unit the position of the loading shovel at the mine was noted. Within two years it became apparent that there were certain areas in the Knife River Coal Mining Co. mine at Beulah, N.D., where the lignite apparently had a high fouling tendency for the Hoot Lake unit. Results from analyses of the coal did not show large differences in moisture percentage, ash percentage, heating value, or ash fusion temperature between the highly troublesome and less troublesome coals. After three years of operation, the troublesome areas had been quite well defined and the mining company started a procedure of bypassing these areas when load conditions at the plant were high and then returning to the troublesome areas to load the lignite during the summer months when peak loads were lower. It was noted that the lignite from the areas which caused severe fouling under high load conditions produced much less fouling at the lower summer loads. However, bypassing certain areas in the strip pit caused the mining company to disrupt their continuous loading schedule, which in turn upset their continuous stripping schedule and made for less efficient mining operation. Meanwhile, at the Hoot Lake plant, the number of soot blowers on No. 2 boiler had been increased from 30 to 55, and a very rigorous blowing schedule had been adopted resulting in soot blowers operating at least some part of 21 hrs per day. Fouling problems continued, with a resulting reduction in plant economy and reliability. During this period the Federal Bureau of Mines Coal Research Laboratory at Grand Forks, N.D., had initiated various research programs relating to the study of lignite ash and ash fouling problems. One project was a survey in which full seam samples were obtained from various locations in all the major

Jan 1, 1968

By H. Pew, J. H. Field

To alleviate pollution more restrictive legislation is being enacted, either limiting emission of pollutants or the type of fuel that can be utilized. The nature and magnitude of air pollution problems affecting the mining, preparation, coking and combustion of coal are described. Methods for combatting particulate emissions by use of mechanical separators and electrostatic pre-cipitors are discussed. Proposed methods to meet the problem of gaseous emissions currently receiving considerable attention are described, with special emphasis on methods to decrease pollution by sulfur oxides. Concern about air pollution goes back several centuries, but until very recently most effort has been aimed at coal smoke and other visible pollutants. The classic example of a 'successful' campaign for smoke abatement and control is the fruitful combined effort of the city of Pittsburgh and its surrounding Allegheny County, which eventually led to the reconstruction of downtown Pittsburgh at an estimated cost of one billion dollars. Historically, the city's downtown Golden Triangle district had been afflicted by pollutants evolving from steel mills, from a variety of other industries, and from railroad locomotives. Efforts to alleviate the situation prior to 1943 were virtually ineffective. In 1945, however, a comprehensive redevelopment plan was prepared and backed by state authority. Within a few years a clean, modern metropolis has evolved where once stood America's famous 'smoky city.' But the victory in Pittsburgh, as in various other American cities, has not solved the national problem. Current estimates indicate that 133 million tons annually of air pollutants from all sources still are emitted annually into the atmosphere above the United States. About 10% of this annual effluent is particulate matter so that most of the remaining pollution problems will be solved only when other effluents are reduced. Essentially, these are sulfur oxides, nitro- gen oxides, hydrocarbons, and carbon monoxide. Over the years, both states and local communities have tended to increase the restrictions on smoke and fly ash — problems mostly of concern in the combustion of coal. Prior to the middle 1950's, ordinances sometimes permitted emissions of smoke equivalent to as much as No. 3 on the Ringlemann scale. Since 1956, no ordinance has been passed which allows smoke of greater than No. 2. Under today's conditions of improved fuels, equipment and practice, a few communities have passed laws prohibiting emission of smoke of any density darker than Ringlemann No. 1. The majority of existing laws on fly ash emission in the U.S. limit emissions equivalent to 0.85 lb of fly ash per 1000 Ib of flue gas. In recent years, however, regulations which have been adopted give cognizance to the higher level of performance now obtainable with improved equipment. A comparison of the restrictions of five codes adopted since 1960 is given in Table I. The most stringent of these is the one for New York City which provides for a maximum emission of 0.6 lb fly ash per million Btu heat release (equivalent to roughly 0.51 lb/1000 lb of flue gas). The first comprehensive effort to restrict the emission of SO2 resulted from the passage of a 1937 law in St. Louis. This regulation stipulated that coal containing in excess of 23% volatile matter and 2% sulfur must be washed, thereby presumably producing some effective reduction in the input sulfur content. This was followed in 1949 by a Los Angeles County law which prohibited the emission of SO2 in concentrations greater than 0.2%. Most SO2-restrictive legislation passed since that date has been based on this limiting 0.2% SO2 by volume, although modifications are occasionally permitted under selected conditions, sometimes based on the fact that certain limiting ground concentrations are not exceeded — such as in the rules adopted by the San Francisco Bay area. To date, no legislation has been passed in the U.S. to limit the generation of nitrogen oxides from the combustion of fossil fuels. However, such oxides are considered to be of potential importance in air pollution control because of their possible detrimental effects on health and their reported role in the formation of photochemical smog. Interest in reducing oxides of nitrogen from powerplant and auto exhausts is increasing and regulations limiting their quantity can be expected in the future.

Jan 1, 1968

By R. A. L. Black

13.8-1. Introduction. Table 13.8-1 shows that production from the African continent is an important part of total world mineral production. In three of the major particular resources listed, diamonds, gold, and cobalt, African production accounts for considerably more than half the world output. Overall, South Africa including South West Africa plays a dominant role in the mineral economy of Africa, other than in petroleum production. Table 13.81 also shows that much of the production is won by surface mining methods. In addition to the minerals listed in Table 13.8-1, Africa is a main world source for the following minerals: [Beryl 33% of total world production Columbium-tantalum 50%" " 1' Platinum group metals 20% l' " 11 Corundum 55%" " " 11 Vermiculite 30% (' " (6 Uranium oxide 15 0/, of free world production] South Africa and Rhodesia together account for nearly all of this production, except for columbium (niobium) of which Nigeria is the main producer. Thus the importance of southern Africa as a major mineral province can readily be appreciated. The consequences of serious political or military conflict between white-dominated southern Africa and the rest of the continent would be grave indeed, particularly for the West whose financial and economic interest in Africa as a whole is very large. The development of mineral resources in Africa involves the same basic elements as are involved anywhere else in the world: exploration, drilling and sampling, metallurgical assessment, and economic evaluation before, if it is justified, a prospect is brought to the productive stage. The same range of factors controls the economic viability of a project in Africa as elsewhere, of which the most important are:

Jan 1, 1968

By G. B. Gibbs

Various semiempirical equations which relate defect-formation energies and entropies with elastic and thermal properties of a metal crystal are shown to be related by a simple model for lattice energy. An illustrative comparison of theory with experiment is made using self-diffilsion data for fee metals. SEVERAL workers have related the free energy of defect formation with elastic and thermal properties of a crystal lattice, particularly elastic bulk modulus and Debye temperature. The present note shows how the various approaches are related by a simple model for lattice energy. A comparison of theory with experiment is given using the self-diffusion parameters of fee metals. 1) A MODEL OF THE CRYSTAL LATTICE The internal energy per atom in a metallic lattice may be written U=Ui-Ue [1] where Ui and Ue refer to ion-ion interaction and valence electron energies, respectively. The volume per atom V has an equilibrium value 52 for which

Jan 1, 1968

By R. E. Reed-Hill, W. H. Hartt

The "(3034) " twin lamellae in magnesium have been reexamined using electron microscope replicas. The double twinning sequence (1011)- (1012) for these lamellae has been reconfirmed. Evidence is presented showing that the irrational habit of these twins is probably the direct result of a need to accommodate the second-order twinning shear. This accommodation vesults in both an external shear in the matrix and an internal shear in the lamella. A model is presented which accounts for the experimental obseruations. HCP metals are generally characterized by strong textures in which the basal planes of the grains tend to be aligned parallel to the rolling direction in sheet or plate and to the axis of wires and rods. Since these directions are normally those in which finished products may be subjected to uniaxial tensile stress, these textures effectively place the crystals of magnesium objects in orientations unfavorable to both basal slip and {1012) twinning, the easily activated deformation systems of this metal. However, when magnesium crystals are deformed near room temperature by a tensile stress nearly parallel to the basal plane, another mode of deformation can occur.',2 This is _a double twin which forms first by twinning on {loll), followed by retwinning on (1012). The resulting twin lamellae are of considerable interest. First, they can be responsible for "brittle fracture''; when a tensile stress axis lies in the basal plane, because the reoriented crystal structure of a lamella is well-aligned for slip while the parent crystal is not. Extensive internal deformation may thus occur while the matrix is still almost undeformed. This deformation can produce a ductile rupture running the length of the twin.3 Complete failure of the specimen may then oc-cure by the spreading of cracks from one twin lamella to another, or by the movement of a crack into a grain boundary and then along grain boundaries. Since the the volume fraction of these doubly twinned elements is normally very small, the fracture may be classed as brittle, although the fracture mechanism is, of itself, essentially ductile. It is quite probable that the ductility transition, normally observed4 in magnesium at or slightly Obove room temperature, is closely associated with these second-order twins. The detailed relationship of these twins to fracture in single crystals will be the topic of another paper. The present paper is concerned with a second important aspect: the irrational habit of these double twins that falls close to {3034), or approximately 7 deg away from the primary (10il) twin habit. There is good reason to believe that this habit results directly

Jan 1, 1968

By T. D. Tiemann

The extraction of iron oxide from several types of siliceous iron ore by digestion in sulfuric acid solutions was investigated in the temperature range from 80 to 258°F at concentrations from 10-60% H2SO4. Degree and rate of extraction were found to be critical with respect to both temperature and acid concentration, requiring temperatures in excess of 250° F and acid concentrations of 50% to effect 80-90% extraction of iron oxide in 60 min. Rate of extraction is directly related to surface area and apparently controlled by the rate of chemical reaction. The activation energy was found to be approximately 25,000 cal per g mol. Extraction characteristics of the several ores were found to be similar. The Department of Minerals and Metals Engineering at the University of Wisconsin conducts a continuing research program to develop processes for the utilization of low-grade iron ore deposits such as the nonmagnetic taconites of the Wisconsin Gogebic range. Methods under study include high-intensity magnetic and high-tension electrical concentration, flotation, direct reduction and chemical extraction. Concentration of a number of low-grade siliceous iron ores by the extraction of silica in sodium hydroxide solutions has been reported by the writer and others in the literature.1,2,3,4 Residual concentrates containing as much as 65% iron have been obtained from taconites containing less than 30%. Currently an alternative approach is under study, namely the dissolution of iron oxides from siliceous gangue by extraction in acid, with subsequent recovery of the iron from solution. Such a process for extracting iron oxide from the low-grade oclitic deposits of Alberta with hydrochloric acid was investigated and described by Gravenor, Govett and Rigg.5 The current investigation, which is entirely devoted to extraction with sulfuric acid, is the subject of this paper. In part, the objective of this research was to determine the possibility of leaching iron ores in situ with sulfuric acid. The investigation of a recovery method is left to later research. The ores investigated contained hematite (Fe2O3) as the principal iron-bearing mineral and minor amounts of goethite (Fe2O3 .H2O), magnetite (Fe3O4), and iron-bearing silicates. The gangue was essentially quartz occurring as single crystals and microcrystalline aggregates. Detailed description of the ores may be found in the literature.1,2,4,6 A comparison of the specific ores used in this investigation is shown in the partial analyses of Table I. EXPERIMENTAL METHODS All extractions were made at atmospheric pressure using beakers with a mechanical stirrer for those tests run below the boiling point, and Erlenmeyer flasks for those at the boiling point. A thermostatically controlled hot plate was used for heating, and this maintained the mean temperature within the solution to within ±3°F during extraction. The sample of ore for extraction was weighed to + 0.02 g. For tests below the boiling point, the sample was added to the beaker containing the sulfuric acid solution at the desired temperature. For the boiling-point tests, the sample was added to the Erlenmeyer flask followed by distilled water and the

Jan 1, 1968

By John Chipman

Published data on the equilibria of carbon in binary Fe-C austenite with H2-CH4 and CO2-CO gas mixtures are used to obtain the constants of an equation repre -senting the activity coefficient of carbon throughout the stable austenite range of temperatutre mid compositiotl. Calculated values for the solubility of graphite are found to be in agreement with the best-published direct observations. Its heat of solution is 10,680 calper g-atom. The free energy of formation of cementite is culculated from the equilibrium compositions of austenite and of gas. Its entropy and heat of formation are also obtained. BASIC knowledge of the high-temperature properties and treatment of steels is contained in the Fe-C diagram and its extensions for the effects of alloying elements. The application of thermodynamics to the Fe-C system, with addition of alloying elements, can serve to simplify and systematize this knowledge. The points of beginning are the binary fee solution, austenite, concerning which our information is reasonably complete, and the binary carbide, cementite. Further studies must include the other phases of the binary system, a and liquid, and for these an accurate knowledge of the ? phase boundaries is essential. These studies should provide a firm base for systematic study of the effects of alloying elements on all phases of the system, their transformations, and precipitation phenomena. With the aid of the simplifying thermodynamic concepts of activity coefficients and interaction parameters it is to be hoped that the results of these studies will be amenable to computer solution thus making the information on multicomponent systems more readily available than would be possible in multidimensional diagrams. Studies of the thermodynamic properties of austenite have utilized equilibrium measurements on the reactions:

Jan 1, 1968

By G. B. Craig, B. Ramaswami

The temperature and strain rate dependence of the flow stress ratio and the stvain rate dependence qi the flow stress of annealed polycrystalline a zirconiur were determined over the temperature range 30 0" to 1000°K. Some evidence was found for strain aging and discontinuous flow in the temperature ranges 520" to 650°Kand650" to 760°K, respectively. The Cottvell-Stokes relationship was obtained when deformation occurred by twinning as well as slip. The flow stress ratio showed a strong dependence on temperature and strain rate above 800°K. The expevirnental evidence indicated that the rate-controllitzg mechanism for the deformation of a zirconium above 800°K was dislocation climb, and that the deformation was not thermally activated in the range 520" to 800°K. The stacking-fault energy of a zirconium was estimated to be about 250 ergs per sq cm. A knowledge of the temperature and strain rate dependence of the applied stress necessary to deform a crystalline solid is essential for understanding the thermally activated processes occurring during deformation.' Several experimental techniques have been developed for studying these processes.273 One of the techniques is the deter mi nation of the strain rate dependence of the flow stress at constant temperature. In close-packed crystals, it has often been observed that the change in stress due to a change in the strain rate varies linearly with the flow stress, (~1,' This relationship, known as the Cottre ll-Stokes law, is obeyed when deformation occurs by glide alone. However, when deformation occurs by twinning as well as glide, there is disagreement among different investigators on whether the Cottrell-Stokes law is observed. Whereas Thornton et ~1.~find departures from Cottrell-Stokes law when twinning occurs in copper, ~avis~ and sasinski? find that Cottrell-Stokes law is obeyed when deformation occurs by twinning as well as slip in cadmium and magnesium, respectively. One of the main objectives of this study is to determine whether the Cottrell-Stokes law is obeyed when deformation occurs by twinning as well as slip. The second technique that has been used extensively to study the thermally activated deformation of crystals is the determination of the ratio of the flow stresses, at identical dislocation structures and con-

Jan 1, 1968

By W. W. Anderson, S. Razi

Electroluminescetrce of single crystals of terbium-(loped ZnS prepared by vapor-transport technique shows the sharp line specirum characteristic of the 4f— 4ft,ansitiotzs of the trivalent Tb3 rotz. V-I tt~easuverr~ents give evidence of space-ellarge-lirrlited curvent but the thrveshold for trap-filled law behavior is not iu agreement with Lampert&apos;s theory for. Single injection. Variations of &apos;brightness with applied voltage, the observation of double peaks its brightness because joms, and the spatial distribution oi electroLur?zir~escerrce indicate that the accelet~atiotz-collision mechanism involving the bst lattice and/ov shallow traps is most likely to be responsible fov excitation of&apos; electrolnminescence. Efficiency rtreusuver)~etits show the quantwn efficiency to be about 10 pct and powev efficiency about 0.05 pct. Effect of anr~eallng the crystal in sulfur vapor is to enluztzce llle rare-earth emission. It rs pvoposed tlzat sulfitv anr~ealing crreates acceptorr-lvpe defects with which the donor-type vare-eavtll ion can associate more readily vesulting in enhanced rare-earth emission. A&apos;o such e~zlznr~cerr~etrt is obserued when the crystal is atztrealetl in zinc vapor. Photolianinescence of ZnS doped nith a variety of rare earths also shows tile slurvp l~rze rwve-eavtlz erriission which in sorrretirr~es accompanied by broad band, stvuctureless lattice emission. Photo-atrd electrolutr~itzesce?~ce of ZIIS:Tb slw~rj do!rlit~unt rare-earth emission in the ~ticirzity of 54(3OA corre-sporrdit~g to the transition D* — Fj. Hoz~!el)er, the detailed line structuve of the luo spectvtr is cliffevet~t, irzdicutit~g that different sites are active in the two processes. Decay of rave-eartlr fluorescence in ZnS doped with any of sei!evul vuve eurtlzs car1 be described by a single exporleritial e.scepl joy ZrlS:lIo. Tl~is exceptiotr can be explaitred it~ tevrr~s of tlre closely spaced er~evgy 1e1:els Jov the HO~&apos; iorr. Decay lime measurertzekzts jov ZnS:Tb, using pulsed elect,-ical ar~d pulsed opticcll excitutiorzs, (11-e itz goor1 agrcetrier~t. LUMINESCENCE of rare-earth-doped materials has been a subject of interest for the past 20 years. Within the past few years there has been a considerable increase in rare-earth research motivated in search of new and more efficient laser materials and also due to the use of certain-rare-earth compounds in the preparation of color television screens. The purpose of this study has been to seek an understanding of some of the basic processes involved in exciting the rare-earth luminescence which is associated with transitions within the 4f shell of the trivalent rare-earth ion. Single crystals of ZnS doped with a variety of rare-earth ions have been prepared by vapor-transport technique described elsewhere.&apos; Photoluminescence was excited by a high-pressure short-arc mercury lamp together with suitable glass and chemical filters. For electroluminescence, sinusoidal and pulse excitations were used. 1) ELECTRICAL CHARACTERISTICS 1.1) V-I Measurements. Electroluminescence experiments were performed on crystals of terbium-doped ZnS. The samples were cleaned and etched and indium or In-Ga alloy contacts were alloyed on by heating in H2 atmosphere to 600°C for times ranging up to 10 min. Static voltage-current measurements were made on several samples. Fig. 1 shows the results for a typical sample. For voltage V < 20 v, the V-I relationship is linear giving a resistivity of 2.5 x 109 ohm-cm for this particular sample at room temperature. In the range of 20 to 250 v, I varies as V "3 and at still higher voltages (when electroluminescence is visible to the scotopic eye) current varies as Vs up to 600 v, all at room temperature. At 77"K, for V > 200 v, / I vge5 up to 1000 v. The V-I characteristics at room temperature follow reasonably well the behavior predicted by Lampert&apos; for one carrier space-charge-limited current in an insulator with traps although, as shown later, the expression derived by Lampert2 for the threshold for trap-filled law behavior Vtfl yields an unrealistically low value for trap density if we use the experimental value of 300 v for VtfL. Assuming the case for shallow trapping, the transition from Ohm&apos;s law behavior to space-charge-limited behavior occurs at voltage Vtr given by where no = thermally generated free carrier density, L = length of the sample, e = static dielectric constant, 6 = ratio of free to trapped electron densities, e = electron charge. For the ZnS:Tb crystal, L = 0.5 mm, E = 8.3 €0, Vtr - 20 v, and no = 5 x 10&apos; per cu cm, calculated from the ohmic behavior assuming electron mobility of 100 sq cm per v-sec. This results in 9 = 0= As more and more electrons are injected the Fermi level moves up in the forbidden gap toward the conduction band. If we assume a single-energy level for traps (which is not strictly correct, as we will show later), the current voltage characteristic is profoundly affected when the Fermi level crosses the trap level. The traps are now filled and injected carriers can no longer be immobilized in traps. Hence, current rises sharply with voltage. The transition from space-charge-limited behavior to the trap-filled behavior occurs at voltage VTFL given by

Jan 1, 1968