By H. M. Davis, T. S. Jones

A methodfor accelerating the reduction of a metal oxide by carbon monoxide is to incorporate in the reduction system a nonreducible oxide which has a strong affinity for carbon dioxide and will remove it from the product gases. The effectiveness of this method was investigated by veduction experiments on specially prepared powder mixtures of SrO-ZnO ("active'.) and SrCO3-ZnO (reference). Measurements at 750o and 677°C showed that the rate of reduction of ZnO by CO was as much as an order of magnitude greater in the presence of SrO. Under the experimental conditions at least as much CO2 as generated by veduction was absorbed when SrO was present. Enlzancernent of the veduction rate by SvO resulted from modification of' gaseous djfitsion processes. THE specific question posed in this investigation was whether the reduction reaction CO + ZnO - Zn(g) + COa [1] could be accelerated by incorporating strontium oxide into the oxide charge undergoing reduction. Provided the strontium oxide was active enough, it could remove carbon dioxide from the product gases of ( 11 and form strontium carbonate, thus modifying Reaction [ 1] to CO + ZnO + SrO = Zn(g) + SrCO3 [ 2] This study of the comparative rates of Reactions [ I] and [2] can be considered as a particular case of a general scheme for increasing the rates of reduction of metal oxides by carbon monoxide. The limits of applicability of this scheme are indicated in the simple thermodynamic analysis presented in the appendix. This analysis primarily dictated the choice of the system, CO-ZnO-SrO, employed in this investigation. In addition, it was thought that a study of this scheme by use of the CO-ZnO-SrO reaction system would be of special interest in view of indications in the literature1-3 that the gaseous reduction of zinc oxide is prone to rate control by diffusion in the gas phase. The distinction should be pointed out between this and other efforts to increase the rates of reduction reactions through the use of addition agents. Additions of a wide range of chemicals have been tried with de- grees of apparent success varying from slightly negative to highly positive. The reasons for making additions have included the use of salts to produce effects akin to catalysis,4, 5 the alteration of the microstruc-tural details of the reduction process (including solid-state diffusion),6-8 and the conversion of an en-dothermic reaction into one that is exothermic or autogenous.9-12 The means used to attempt alteration of the enthalpy change has commonly been to incorporate lime into the charge, so that heat is generated by reaction with either of the reaction products, carbon dioxide or water. The use of lime in this way makes endeavors such as that of Edstrom and Wiberg similar to the present one. Furthermore, the basic principle behind the present work has previously been set forth.13 However, a detailed investigation of the type of reaction described in this work does not appear to have been conducted. EXPERIMENTAL PROCEDURE From both conceptual and physical standpoints, Reaction [2] is to be considered as the sum of two reactions:

Jan 1, 1968

By I. R. Kramer

The effect of the specimen diameter, d, on the flow stress, cra of polycrystalline aluminunz (99.997) was studied. The increase in the flow stress could be accountedfor by the increase in the surface layer stress, with decreasing specimen diameter. Both , and a, were found to be proportional to For the smaller-dianzeter specimen (< 0.033 in.) at strains less than aboul 0.1, the work hardening of the surface layer was greater than that associated with the bulk of the specimen. At higher strains the work hardening due to the bulk appears to be independent of the specimen diameter. THE increase in the strength of metals with decreasing diameter is well-known; however, an adequate explanation for the cause of the size effect is still lacking. The earliest systematic investigation of size effect appears to be that of Onol who reported that for aluminum monocrystals the resistance to slip at low strains increased as the specimen diameter decreased. A change in the stress-strain curve beyond 0.001 strain was not found. However, Suzuki et a1 .&apos; reported for monocrystals of a brass and copper having diameters in the range of 2 to 0.12 mm that the entire stress-strain curve was raised as the specimen diameter was decreased. The effect of size was most apparent when the diameter of the specimen was less than 0.5 mm. In the discussion of this paper Honey-combe reported a size effect in copper crystals as large as % in. diam. These results are in agreement with those of paterson3 and Garstone et al.4 While the majority of the investigations on size effects was conducted in terms of the variation in the diameter of the specimen, several investigators studied the influence of the specimen geometry. For example, Wu and smoluchowski 5 reported that in aluminum monocrystals the slip system was a function of the specimen dimension in the slip direction. King-man and Green 6 studied the influence of size on the compressive stress-strain relationship of aluminum monocrystals when the ratio of length to diameter was constant. Their specimen diameters ranged from to & in. For specimens oriented for single slip the critical resolved shear stress for the smaller-size specimens increased with decreasing diameter. No effect was observed in the large-size specimens. Specimens having an orientation near the corners of the stereographic triangle did not exhibit a size effect. Apparently, the increase in strength with decrease in the diameter of the specimen is a general phenomenon and has been observed in a brass |T and cadmium as well as in aluminum and copper.&apos; In a series of investigations (for example Ref. lo), it was shown that during deformation a surface layer was formed which imposes a back stress, a,, on the moving dislocations. It is reasonable to predict that this surface layer stress, as, should be a function of the specimen diameter and could possibly account for the flow stress size effect. In fact, experimental evidence will be presented to show that this is the case; i.e., the increase in flow stress with decreasing size is equal to the increase in the surface layer stress, as, with size. In addition, data will be presented on the variation with size of and a* where is the back stress associated with the generation of dislocation obstacles in the bulk of the specimen and a* is the net effective stress acting on the mobile dislocations. A limited investigation was carried out on gold specimens to determine the influence of an oxide film. EXPERIMENTAL PROCEDURE The aluminum specimens were prepared from -in. bar stock (99.997 pct purity). The 0.350- and 0.150-in.-diam specimens were machined directly from the bars while the specimens having a diameter of 0.033, 0.020, and 0.015 in. were prepared by swaging and drawing to 0.04 in. and electropolishing almost to final size. The specimens were prepared with a 2-in. gage length. The specimens were annealed in vacuum (-10-4 Torr) at 350°C for 8 hr. The grain diameter of the specimens in the various specimen diameter groups was 0.08 ± 0.02 mm. Gold specimens of two diameters, 0.14 and 0.03 in., were prepared in a similar way and annealed at 650°C for 8 hr. The grain diameter of the gold specimens was 0.2 mm. After annealing the specimens were electrochemically polished to the final size and tested in an Instron tensile machine at a strain rate, E&apos;, of 10- 3 per min. While it was possible to determine the surface layer stress, a,, in the larger-size specimens by measuring the difference, Aa, between the stress before unloading the specimens and the initial flow stress after removal of the surface layer as outlined in detail in Ref. 10, this method is not applicable for small wires because of the difficulty in obtaining a sufficiently accurate measure of the diameter. The values at the various strains were therefore determined by measuring after the specimen had been annealed at 35°C for 4 hr. It has previously been shown" that the two methods give the same results for a provided that the annealing temperature is low enough to affect only the surface layer and not the dislocation barriers in the bulk of the specimen. For the gold specimens a treatment at 150°C for 16 hr was found to be satisfactory for the determination of by the low-temperature annealing method. EXPERIMENTAL RESULTS Determination of a,, and a,. The stress-strain curves for the various diameter aluminum specimens, plotted in terms of the logarithms of the true stress, and true strain, are given in Fig. 1. These curves represent the average data taken from at least ten specimens at each size. Over the range of strains investigated the curves follow the empirical equation

Jan 1, 1968

By J. E. Zeilinger

This Bureau of Mines report describes the preparation characteristics of the significant coalbeds of Clarion County, Pa. Of the 15 samples collected, 1 was of metallurgical quality as received, 4 could be sufficiently upgraded to provide acceptable products, and the remaining 10 samples could not be upgraded to metallurgical quality because their sulfur contents could not be lowered to meet the standard. For steam or power generation, 1 sample was of low sulfur content as received, 1 sample could be upgraded to low sulfur content, and 10 samples could be upgraded to medium sulfur content. The original sulfur content of the remaining three samples can be appreciably reduced by removal of the sink 1.58 specific gravity material; however, these coals would be classified as medium sulfur coals both before and after removal of the sink material.

Jan 1, 1968

By P. Chiotti, J. T. Mason

Ther?nal, X-ray, metallographic, and vapor pressure data were obtained to establish the phase diagram and standard free energy, enthalpy, and entropy of formation for the compounds in the Sw-Zn system. Four compounds, SmZn, SmZn2 , SmZn4.s, and SmZn8.5, melt congruently at 960°, 94Z°, 908°, and 940°C, respectively. The cornpounds SlnZns, Sm3Znll, and SnzZn7.3 undergo peritectic decomposition at 855", 870°, and 890C, respectively. Another compound of uncertain stoichiometry, SmZn11, undergoes peritectic decomposition at 760°C. Four entectics were observed with the following compositions in weight percent zinc and eutectic tenzperatures in degrees Centigrade: 12 pct, 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. An allotropic transformation and a composition range were observed for the SmZnz compound. The transfor)nation varies from 905" to 865°C as the zinc content increases from 16.0 to 48.5 wt pct, respectively. The free energy of formation of the compounds at 50PC varies between -15.9 kcal per mole for SmZn to -51.1 kcal per mole for SmZn,.,. Corresponding enthalpies vary between -19.2 to -78.3 kcal per mole. The ther-modynamic properties for the liquid alloys are described by the relations: A search of the literature revealed very little information on the Sm-Zn system. Chao et al.&apos; as well as Iandelli and palenzonai have reported the structure of SmZn to be cubic B2 type and Kuz&apos;ma et al3. have reported the structure of -sm2zn17 to be of the Th2Ni17 type. The purpose of this work was to establish the phase diagram of this system, to determine the zinc vapor pressure over the solid two-phase regions of the SYstem, and to calculate the thermodynamic properties of the compounds. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in this investigation were Bunker Hill slab zinc 99.99 wt pct pure and Ames Laboratory samarium. Analysis of the samarium by chemical, spectrographic, and vacuum-fusion methods gave the following average impurities in ppm: Nd, <200; Eu, <100; Gd, <100; Y, <50;Ca, 225; Ta, 400; Mg, 10; Cu, ~50; 0, 175; H, 20; and N, 15. The elements Fe, Si, Cr, Ni, Al, and W were not detected. The samarium was received as sponge metal and was kept under argon except when being cut with shears and when being weighed. Tantalum was found to be a suitable container for alloys with zinc contents up to the Sm2Znl, stoichio-metry. At higher zinc contents the grain boundaries of the tantalum containers were penetrated by the alloy and the containers failed during prolonged annealing. About 25 g of massive zinc and samarium sponge were sealed in tantalum crucibles equipped with thermocouple wells. These crucibles were in turn sealed in stainless-steel jackets. All closures were made by arc welding under an argon atmosphere. The samples were equilibrated in an oscillating furnace and in some cases were given various heat treatments in a soaking furnace. After appropriate heat treatment the steel jackets were removed and the alloy subjected to differential thermal analysis. The apparatus was calibrated against pure zinc and pure copper and found to reproduce the accepted melting points within 1°C. Alloys were subsequently subjected to metallographic examination and those of appropriate compositions were used for X-ray diffraction analysis and for zinc vapor pressure determinations. The vapor pressures were determined by the dewpoint method. Both the differential analysis and dewpoint measuring apparatuses have been described in earlier papers.4, 5 All alloy samples were etched with Nital (0.5 to 3 pct nitric acid in alcohol) except the samarium-rich alloys. These more reactive alloys were electro-polished in a 1 to 6 pct HClO4 in methanol solution at -700c at a potential of 50 v. EXPERIMENTAL RESULTS Phase Diagram. The results of thermal analysis are indicated by the points on the phase diagram, Fig. 1. Eight compounds and four eutectics were observed. The composition of the compounds and their melting or peritectic temperatures are given on the phase diagram. The four eutectic compositions in wt pct zinc and eutectic temperatures in % are: 12 pct,- 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. The stoichiometry of the most zinc-rich compound is still uncertain, but is very likely either SmZnll or SmZnlz. However, to simplify the presentation which follows it will be referred to as SmZnll. As shown on the phase diagram the phase regions for some of the samarium-rich alloys have not been unambiguously established. A sample of pure samarium was observed to transform at 924°C and to melt at 1074"C, in good agreement with corresponding val-

Jan 1, 1968

By Pablo Hadzeriga

Great Salt Lake brine was subjected, in laboratory scale, to conditions simulating solar evaporation. Solid phases and the variation in composition of the liquid phase throughout the potassium salts crystallization zone are presented. These experimental results are discussed and compare with stable equilibrium data of the quinary system Cl-, SO4, Na+, K+, Mg + + and H2O. The Great Salt Lake brine in Utah is a vast reserve of several potential chemicals which has attracted much attention in the recent past. From the standpoint of an ore reserve, it may be said that the lake contains a low grade ore which has to be concentrated by evaporation of water. Because of the fairly favorable weather conditions in the Great Salt Lake area, it seems reasonable to consider solar evaporation as an economical means of concentration. From the view of phase chemistry, the main constituents of Great Salt Lake brine make it belong to the five component system: C1-, SO4=, Na+, K+, Mg++ and H2O. Because of their low concentration, the presence of other elements may be regarded as having little effect on the equilibrium of the five main components. Equilibrium data for the quinary system of our interest has been available for many years. Using these data, it is possible to calculate how the brine of the lake will concentrate when subjected to solar evaporation. In practicing solar evaporation, the weather factor and supersaturation conditions cannot be ignored, but their introduction into calculations using equilibrium diagrams is almost an impossible task. With the experimental work presented in this paper, an attempt is made to compare the stable equilibrium data of the quinary system as applied to the case of the Great Salt Lake brine and the dynamic equilibrium when that brine is subjected to continuous solar evaporation. Sea water brine belongs to this quinary system when only the major constituents are considered. The study of this system has been carried on since the last decades of the nineteenth century. The reason for these intensive studies was to give a geological explanation to the underground potash deposits. AS a result, many theories were presented trying to relate the equilibrium data with the geological formation, paragenesis and metamorphism of these deposits. Two main approaches were followed for the equilibrium studies of this quinary system. One of them, and the best known to us, was the school started in Germany in the last century by J. H. Van&apos;t Hoff. The other one, which started about the same time, was the school of N. S. Kurnakov in Russia. Both approaches were different and as a consequence generated opposite theories about the geological formation of potash deposits. The Van&apos;t Hoff school studied the quinary system of sea water under careful laboratory control, resulting in stable phase diagrams. During these studies, Van&apos;t Hoff recognized the difficulties in crystallizing some double salts.&apos; ". . . . we unexpectedly found that some compounds whose formation in the solutions under investigation was possible at 25°C, nevertheless totally failed to put in an appearance. These, not to mention the calcium salts, were leonite, MgSO4 . K2SO4 4 H2O; kainite, KC1-MgSO4 . 3 H2O; and kieserite, MgSO4 .H2O. Even exceedingly slow crystallization with the addition of the compounds themselves did not remove the condition of supersaturation in the case of these bodies." However, those salts (leonite, kainite, and kieserite) were included in the stable phase diagram at 25°C as shown in Fig. 1 using D&apos;Ans data.3 The figure also shows the sequence of crystallization of the Great Salt Lake brine according to the stable diagram. In later studies by the Van&apos;t Hoff school, especially by D&apos;Ans,3 Karsten,4 Autenrieth,5,6 attention

Jan 1, 1968

By James H. Aase

Selected glacial lake clay deposits in Minnesota were sampled, tested, and evaluated to determine their suitability for use as a bonding agent in iron ore pellet manufacturing. Preliminary tests conducted on clay samples obtained from five ancient glacial lake basins identified the clays in the Lake Agassiz glacial lake basin near Cook, Minn., as having the greatest bonding potential. An auger drilling program was conducted to obtain substantial quantities of representative material for detailed testing. The drilling indicated the presence of large clay reserves in excess of 500 million tons within the 12-square-mile area investigated. Bench scale tests indicated that the bonding properties of Cook area clays, when activated with relatively small quantities of sodium carbonate monohydrate (Na2C03?H2O), imparted excellent strength characteristics to iron ore pellets. Larger scale continuous pelletizing tests were made to confirm the bench scale results. These tests indicated that use of 1 percent activated clay alone as binder gave the iron ore pellets an overall strength slightly lower than with 0.75 percent bentonite, considered the industry standard. Use of 0.5 percent activated clay plus 0.5 percent bentonite produced better pellet strength qualities than use of 0.75 percent bentonite alone, without increasing the silica plus alumina content. The data from both bench scale and larger scale continuous tests suggest that the Cook, Minn., clays can be utilized after activation either alone or in combination with bentonite at an economic advantage over present pelletizing practice with bentonite.

Jan 1, 1968

By Richard S. Culver

In spite of the widespread interest in rock bolt research, relatively little is known about the critical region surrounding the bolt anchor. In analyzing the stress distribution around an opening resulting from rock bolt support, it is commonly assumed that the bolt is fixed at a point far enough from the surface so that the anchor does not influence the performance of the bolt. Furthermore, a bolt anchor is assumed to per- form satisfactorily if it will hold the design load with a minimum amount of load relaxation, commonly called bleedoff. From the standpoint of the design engineer both of these assumptions are reasonable, but they ignore the fact that the extremely high stresses in the region of the anchor are capable of generating fractures in the rock. Lang1 estimated the bearing stresses for a slot and wedge anchor on a one-inch-diameter bolt to be as high as 125,000 psi. This paper describes a more thorough analysis of the magnitude of the stresses around the anchor and the nature of the potential fractures that might result. It should be emphasized that there are two types of anchor-associated fracturing which may occur. The more common form, particularly in soft rock, is severe localized crushing of the rock in the immediate vicinity of the anchor, which makes securing the anchor difficult and causes bleed- off. It is also possible to develop larger single fractures which propagate out from the anchor, affecting the strength of the entire rock mass. The formation of these larger fractures is of primary concern in this paper. In addition to estimating the contact stresses and pullout load for slot and wedge bolt anchors, Lang carried out an important study of rock bolt interaction which served as a basis for the experimental phase of this investigation. In the first phase of his tests, a plate of photoelastic plastic was compressed by a row of piano wire bolts, simulating the interaction of bolt stress fields to form a zone of uniform compression (Fig 1). To show the supporting effect of this beam, hr carried out another test series

Jan 1, 1968

By Walter S. White

The Michigan native-copper district has produced about 5,400,000 tons of copper since mining began in 1845. The copper occurs primarily as open-space fillings and replacements in amygdaloidal flow tops and conglomerate beds of the Portage Lake Lava Series, of middle Keweenawan age. Secondary minerals with which the copper is associated include microcline, chlorite, epidote, pumpellyite, prehnite, quartz, and calcite; zeolites, other than laumontite, are not abundant. A zonal pattern of the secondary minerals transects bedding and suggests regional metamorphism mainly to the grade of the prehnite-pumpellyite graywacke facies of Coombs. Most of the major copper deposits are near the upper limit of abundant quartz in this zonal pattern. The distribution of copper in both amygdaloid and conglomerate deposits is controlled partly by primary permeability of the rocks and partly by later tectonic fracturing that was concentrated in the mechanically weak flow tops and sedimentary beds. Ore shoots and deposits are therefore controlled partly by primary structural features, such as areas of thick and thin fragmental amygdaloid or the boundaries of conglomerate lenses, and partly by regional structure: a number of ore deposits are in synclinal downwarps. The copper-bearing solutions that formed the deposits were ascending. They may have come from a large concealed intrusive, or may have been driven out of the porous tops of lava flows when the rocks were compacted and metamorphosed at great depth in the central part of the Lake Superior syncline. The second hypothesis seems more consistent with the widespread distribution of the copper, its relation to mineral zoning that represents truly regional metamorphism, its native state, and the likelihood that copper deposition was later than most or all of Keweenawan volcanism.

Jan 1, 1968

By A. D. Zunkel, A. H. Larson

Equilibrium arsenic contents of Pb-As alloys in contact with PbO-As2O3 slags containing less than 30 mol pct As2O3, were determined at 650°, 700: and 750 C in an inert at?rzosphere. In this temperature range, the arsenic content of the alloy increased with increasing temperature in the single-phase liquid slag region and decreased with increasing temperature in the two-phase slag region and the single-phase solid-solution slag region. The PbO-As2O3 phase diagram below 22 mol pct As2O3 was determined by thertrzal analysis and by application of a log ?As2O3/?PbO vS log XAs2o3 /x3pbO plot determined from the equilibrium actiuity data. The resulting phase diagram was not well-defined since the eutectic temperature was not detected in the thermal analysis experiments, although a region of terminal solid solubility of As2O3 was found. Results from the phase diagram determination are compared with an existing diagram in the literature. THIS experimental investigation is an extension of a study by the authors1 on the slag-metal equilibria in the systems concerned with commercial lead refining processes such as softening and dross fuming. The first part of this investigation was a study of the slag-metal equilibria in the Pb-PbO-Sb2O3 system. The only experimental work previously done on the Pb-PbO-As2O3 system was by Pelzel2,3 in which the phase diagram for the PbO-As2O3 system was determined below 50 wt pct As2O3 and the equilibrium constant for the reaction 3Pb + As2O3 + 3PbO + 2As was determined as a function of temperature. No slag-metal equilibrium data have been determined. It is due to the scarcity of information regarding the Pb-PbO-As203 system that this work was undertaken. This paper describes the determination of the slag-metal equilibria in the Pb-PbO-As203 system by equilibrating Pb-As alloys with PbO-As2O3 slags in an inert atmosphere, the effect of 1 wt pct additions of bismuth and copper on the slag-metal equilibria, and the PbO-As2O3 phase diagram both by thermal analysis and the use of the slag-metal equilibria data. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade and assayed as follows: 1) 99.8 pct PbO (0.014 pct insoluble in CHJCOOH, 0.02 pct not precipitated by H2S, 0.1 pct CaO, and 0.08 pct SiO2); 2) 99.95 pct As2O3; 3) 99.99 pct Pb; 4) 99.0 pct As; 5) 99.99 pct Cu; and 6) 99.97 pct Bi. Room-temperature X-ray patterns revealed no detectable impurities in any of these materials. Apparatus for Equilibrium and Thermal-Analysis Determinations. The resistance-heated crucible furnace used in this investigation employed nichrome elements and was mounted so that it could be raised to surround the reaction tube during each experiment and, subsequently, lowered. A schematic diagram of the apparatus is shown in Fig. 1. Each charge was heated in a 3+-in.-OD by 31/2-in.-high 416 stainless-steel crucible placed in a 41/4-in.-1D by 18-in.-long fused-silica reaction tube which was closed at one end. On a shoulder around the crucible was placed a 3: -in.-OD by 12-in.-long open-end fused-silica condenser tube. The open end of the reaction tube was covered by a water-cooled brass cap with ports for 1) admitting an inert atmosphere to the system through a stopcock, 2) introducing a stainless-steel, motor-driven, paddle stirrer into the crucible, 3) evacuating the system with a mechanical vacuum pump, and 4) sampling the melt with Vycor sampling tubes. The brass cap was fitted to the open end of the reaction tube with a silicone gasket and collar clamp. The furnace temperature was controlled by a Barber-Coleman Capacitrol controller and a chromel-alumel thermocouple. Due to the corrosiveness of the melt, the controlling thermocouple also served as the measuring thermocouple. The temperature of the melt was calibrated against the controller temperature and was checked periodically during each test with a Vycor-enclosed calibrated chromel-alumel thermocouple. The temperature measurement and control can be considered accurate to ±3°C. Procedure. The charge placed in the crucible for each experiment consisted of 1000 g of Pb-As alloy and 300 g of PbO-As2O3 slag. The crucible was then placed in the reaction tube, the condenser tube was placed on the shoulder of the crucible, the silicone gasket and brass cap were fitted on the open end of the reaction tube, and the entire system was evacuated and filled with argon ten times. After the last flushing, a positive argon pressure of 1 psig was impressed on the system. The furnace was then raised to sur-

Jan 1, 1968

By A. L. Muler

Since 1956, when Broadbent and Callcott 1 proposed to analyze breakage processes by matrix methods, several authors and their co-workers have proposed various models of grinding that, in principle, could lead to fully automated grinding circuits. In particular, Meloy and Gaudin2, Gardner and Austin3, Kelsall and Reid4, Neloy and Bergstrom5, Callcott and Lynch 6, and Draper and Lynch have, by either computer simulation or by experimental data, or by a combination of the two, verified that comminution is reasonably well described by at least two functions: a selection function and a breakage function. The stage concept proposed by Callcott and Lynch6 requires that a classification matrix be included to completely describe breakage in an open circuit rod mill. The purpose of this work, portions of which are herein described, is to accumulate sufficient information on the breakage characteristics of quartz and magnetite in an open circuit rod mill, so that several of the theoretical and experimental approaches proposed in the literature can be compared with each other. Data is being gathered to compare the experimental method used by Kelsall and paid against the stage approach of Callcott and Lynch.

Jan 1, 1968

By R. E. Reed-Hill

Recently Levine applied the Conrad-Wiedersich17 equation where H is the activation enthalpy, v the activation volume, T* the effective shear flow stress, T the absolute temperature, and ? the strain rate, to an analysis of titanium single-crystal data. The activation energy as a function of testing temperaturs obtained from specimens oriented for single (1010) prismatic slip is shown in Fig. 12. This diagram indicates a different linear dependence of H on T in the temperature interval from 220° to 300°K than from 0° to 220°K. Levine interpreted the break in this curve as indicating a change in the thermally activated mechanism controlling the flow stress. The purpose of this communication is to point out that the data in Fig. 1 is not consistent with the concept of a flow stress controlled by a simple thermally activated mechanism between 220° and 300°K. The Conrad-Wiedersich relation assumed that the strain rate can be expressed by:

Jan 1, 1968

By Y. H. Liu, G. W. Powell

Thin foils made from the gold-rich region of- short (0.15 mm)Au-Ag diffusion couples annealed at 880°C for 1 hr were examined in ax electron microscope and the structures were compared with that of pure gold subjected to identical heat treatments. The couples underwent Plastic deformation (bending) during the diffusional anneal. The foils prepared from the diffusion zone have a higher dislocation density and incidence of subboundaries than pure gold. The plastic bending of the couple can be interpreted in terms of the climb of edge dislocations, which are pavallel to the bend axis, along the direction of diffusion. THE interaction of lattice defects during interdiffu-sion between two metals has been considered by several investigators. In particular, da Silva and Mehl,1 Barnes,&apos; and Bardeen and Herring3 have proposed models based on interactions between point and line defects to account for the Kirkendall effect (marker movement). Each of these models is based on dislocation climb, which can either add or remove lattice planes, induced by an under- or supersaturation of vacancies. A theoretical treatment of the nucleation and growth of voids by the condensation of vacancies has been presented by Seitz.4 Stresses can arise in a binary diffusion couple as a result of the vacancy flux and the gradient in the lattice parameter. rinkmman&apos; has investigated the effects of diffusion-induced stresses on void formation; the results of his analysis suggest that voids can form and grow under the influence of these stresses in the absence of an excess vacancy concentration. The relationships between vacancy supersaturation and diffusion-induced stresses and void formation have been elucidated also by Balluffi and seigle6 who concluded that the stress generated by a vacancy supersaturation aids the growth of voids. Experimental evidence which indirectly shows that stresses are produced by chemical diffusion has been obtained by several researchers.2,7-9 This evidence consists in part of the observation by light microscopy of the formation of subgrains, a process characteristic of the high-temperature deformation of some metals during creep.&apos;0 More striking, however, is the plastic bending of short (0.2 mm) Cu-Ni couples observed by Barnes2 and of boron-doped silicon crystals reported by Queisser.9 Diffusion-induced dislocations in iron and silicon have been investigated by Ainslie et a1.11and Schwutte and Queisser,12 respectively, the former using transmission electron microscopy and the latter an X-ray transmission technique. Matthews and Crawford13 observed the formation of boundaries by the climb of interfacial misfit dislocations in thin, vapor-deposited Au-Pd couples diffused in situ in an electron microscope. In order to obtain additional information on the phenomena associated with defect interaction and diffusion-induced stresses in binary couples, an electron transmission study of foils prepared from the diffusion zone of short Au-Ag couples was undertaken. The initial objective was to investigate the processes occurring at various points of the diffusion zone. Subsequent research demonstrated that foils could be prepared only from the gold-rich region of the diffusion zone using the technique described herein. EXPERIMENTAL PROCEDURE Preparation and Annealing of the Diffusion Couples. The couples were made from annealed, high-purity (99.999 pct). polycrvstalline gold and silver sheets (0.075 mm thick). Shall (0.075 by 5 by 17 mm) elec-tropolished coupons of gold and silver were pressure-bonded by heating the two metals in a graphite device to 770°C and holding at this temperature for approximately 30 min. The quality of the bond was ascertained by metallographic examination at 150 times. Each couple subsequently was annealed at 880°C for 1hr; under these conditions, the extreme portions of the

Jan 1, 1968

By David K. Fountain

"The growth of the mining industry in British Columbia in the last ten years has been largely the result of the development of large low-grade copper and molybdenum deposits. There are two problems which must be solved in the search for mineral deposits of this type. It is necessary to detect large volumes of rock containing a low percentage of total sulphide mineralization1 and, secondly, to get some idea of the economic significance of this mineralization. The standard geophysical exploration techniques available have a varying degree of application in the search for disseminated sulphide de-posits. The electrical methods, and the induced polarization method in particular, are the most successful direct methods, and magnetic methods have indirect application in most situations. This is illustrated by geo-physical survey results from several properties in British Columbia."

Jan 1, 1968

By A. G. Starliper

Laboratory studies were made to produce whiskers of tungsten over a wide range of operating temperatures. Hydrogen reduction of tungsten hexachloride in a vacuum furnace at temperatures from 2,7000 to 3,3000 C yielded a small quantity of tungsten whiskers, provided a low degree of supersaturation was maintained. Direct measurements of 3,000,000 to 4,000,000 psi were obtained for the ultimate tensile strengths of individual whiskers averaging 3 to 4 microns in diameter with average aspect ratios of 1,000. This compares with strengths of 300,000 to 400,000 psi for 13-micron-diameter commercial filaments.

Jan 1, 1968

By J. C. Coughlin, M. C. Flemings, T. Z. Kattamis

Experiments on Al-4.5 pct Cu alloy shou the dendrite arnz spacing increases with time during isothermal holding in the liquid-solid region. This coarsening of the dendrite structure is then shown to occur at roughly the same rate during solidification as during isothermal holding. Final dendrite arm spacing in both types of experiments depends primarily on coarsening kinetics. It is concluded that driving force for the coarsening is reduction of liquid-solid sur/ace area. Calculations based on two simple models show qualitative apreement with experinzent. 1 HERE has been considerable interest in recent years in determining effects of solidification variables on dendrite arm spacing in cast alloys. The interest has resulted primarily from the clear evidence that 1) the degree of homogeneity which can be obtained in a cast alloy with commercially practical homogeni- zation treatments depends on dendrite arm spacing, and 2) mechanical properties of the heat-treated casting depend on the homogeneity obtained.&apos;-&apos; In wrought alloys, microsegregation from the original ingot is carried to some extent into the final wrought product, and affects mechanical properties in similar fashion Experimental evidence available indicates that dendrite arm spacing in cast aluminum alloys is influenced only by cooling rate (or "local solidification timev*) and alloy content.Fig. 1, for example,

Jan 1, 1968

By E. P. Whelan

A recent investigation1 into the origin of "ghost boundaries" in dilute Cd-Mg alloys has indicated the persistence of a segregated solidification substructure in spite of a homogenizing treatment designed to remove such segregation. Although no grain growth experiments have been reported on these segregated alloys, the homogenizing treatment used in grain growth studies on other dilute alloys2-7 is similar in

Jan 1, 1968

By Robert M. Becker

A thick-wall cylinder solution applicable to the evaluation of anisotropic elastic parameters is derived for the interpretation of stress relief data. For a restricted class of problems, a special relationship among certain orthotropic moduli yields stress distributions for the plane orthotropic problem that are identical to the corresponding isotropic case. A ring or hollow cylinder with these specialized anisotropic properties subjected to uniform radial loads is one of the problems in this class. Consequently, known stress solutions are used to develop the strains and displacements for a specialized orthotropic thick-wall cylinder under uniform pressures. The results are consistent with anisotropic equations used in the evaluation of in situ rock stresses.

Jan 1, 1968

By J. C. Scully

In June, 1965, Sanderson and scully5 reported at the Conference on Environment Sensitive Mechanical Properties of Materials at the Research Institute for Advanced Studies at Baltimore that thin foils of titanium could be prepared by chemical polishing in a mixture of 44 pct HF and 73 pct HNO3 in the volumetric ratio 2:3. The technique is simpler than that since reported by Rice and Orava. As-received annealed titanium (containing 0.8 pct Fe and 30 ppm H) in the form of sheet 0.05 cm thick is placed in the solution and moved up and down. The reaction is violent but suitable foils are obtained very easily and consistently. A typical micrograph is shown in Fig. 3. The small precipitates were not identified. Yamane and ueda6 observed many spotlike features which they referred to as small dislocation loops. While their spots may be due to the reaction of the warm foil with the air as suggested by Rice and Orava, the precipitates in Fig. 3 are also found when foils of titanium are prepared by electro-polishing at low temperatures and subsequently examined in the electron microscope without any inter- mediate warming. Furthermore, they are not a surface effect. It is necessary to add that alloys of titanium cannot be so easily thinned by the chemical polishing solution described above since it contaminates the a, phase with hydrogen and produces y hydride. These matters are described at length in a paper7 and their relevance to stress corrosion is considered elsewhere.&apos;-* Author&apos;s Reply The authors are grateful to Dr. Scully for bringing to our attention his hitherto unpublished technique for thinning unalloyed titanium, and deeply regret the unintended apparent duplication. The chemical thinning solution (7 parts HNO3 and 3 parts HF, by volume) reported by us is the same as that with which, for some period in the past, we had experienced success in the preparation of foils from single and polycrystalline niobium. Its subsequent effective application to titanium was a logical step, which, clearly independently of Scully, was conceived by Mr. Rice, to whom full credit is due. A few comments are warranted concerning some of the details of the preceding Discussion. It is evident to the discerning reader that the two thinning techniques under consideration are chemically almost identical, and in that sense are equally "simple". The chemical aspect is, of course, the one of primary importance in both communications. Thereafter, the relative simplicity is dictated by the mechanics of the actual thinning operation selected by the individual investigator. Our standard dimpling, or dishing, procedure was chosen with a view toward providing, for the electron transparent areas of the sample, the maximum protection from extraneous deformation during handling. That the long, straight dislocations visible in Scully&apos;s electron micrograph of a seemingly recovered structure closely resemble handling dislocations would tend to indicate the merit of our adopted technique. Features similar to those which Scully has attributed to precipitates, without any apparent diffraction contrast confirmation, were not observed in any of our clean foils taken from annealed or deformed specimens. This was admittedly somewhat surprising since the 3700 ppm (nominal) Fe in the A-70 commercial-grade titanium examined should have given rise to TiFe precipitates. Presumably these existed but were un-resolvable. Curiously, Scully&apos;s "precipitate1&apos; density is fairly high although the iron content quoted was less than one-fourth of that in our material. One is forced to conclude from the evidence that prior thermal and mechanical treatments are responsible for the two different types of structure observed.

Jan 1, 1968

By Neil J. Sullivan, Goode. George E.

"The Adams mine, operated by Jones & Laughlin Mining Company, Ltd. and located near Kirkland Lake, Ontario, produces one million tons of iron ore pellets per year. This paper briefly describes the mining and concentrating operation and deals mainly with the operation of the pellet plant. The orebody consists of fine-grained magnetite and some hematite, with alternating layers of chert, and is mined by conventional open-pit methods. After crushing and grinding, the ore is concentrated by magnetic separation and flotation. Agglomeration is accomplished by the grate-kiln pelletizing process. The plant layout and general operation will be discussed in detail."

Jan 1, 1968

By J. H. Swisher

ALUMINUM deoxidation equilibrium in liquid iron has been the subject of many investigations. Sawamura and Sano1 have written a critical survey of the literature on this subject and consider the data of Gokcen and chipman2 and of d&apos;Entremont, Guernsey, and Chip-man3 to be most reliable. The present study was undertaken to check these data and extend the range of the experiments to lower temperature. The experiments consisted of equilibrating 5-lb Fe-Al melts with recrystallized alumina crucibles at 1580o + 10oC, and analyzing the solidified ingots for aluminum and oxygen. The electrolytic iron stock contained 100 ppm C, 20 ppm 0, and trace amounts of other elements.* The stock was induction-melted in an atmosphere of 5 pet H2 in argon to attain equilibrium between the melt and the crucible. The temperature was measured with a W, 3 pet Re/W, 26 pet Re thermocouple, and the equilibration time was about 4 hr. The results are plotted in Fig. 1 along with curves obtained from the data of d&apos;Entremont et al.,3 for temperatures of 1740o and 1910°C. The present results can be seen to be consistent with the previously reported high-temperature data. The reaction under study is AI2O3 (s) = 2 Al (l) +3O [1] for which the deoxidation product is Kl =[% Al]2 [%O]3 [2] (Under the experimental conditions, Fe A12O4 is not expected to form.4) In Fig. 2, values of log Ki evaluated at 0.01 pet A1 are plotted against 1/T, using data obtained from all the investigations under consideration. The deoxidation product is plotted in Fig. 2 in lieu of the equilibrium constant (normally obtained by evaluating Ki as pet A1 — 0) because of the uncertainty involved in extrapolating to zero concentration. The difficulty in extrapolating the present data for 1580°C is apparent curvature in the log Ki vs pet Al plot. This curvature is perhaps due to the uncertainty in oxygen analysis for concentrations of 5 ppm and below. For the data of Gokeen and chipman,&apos; the extrapolation is also difficult because of experimental scatter. The line drawn through the points plotted in Fig. 2 may be represented by the equation:

Jan 1, 1968