By Scott Samson, Weidong Wang, Shekhar Bhansali, Vandana Upadhyay

"We present an improved design for the two-arm polysilicon thermal actuator. The classic thermal actuator design produces a localized hot spot at approximately the center of the thin actuator arm. This phenomenon limits the actuator efficiency, lifetime, and reliability. Since the actuator deflection is based on thermal expansion of the material, advantage may be gained by making the temperature profile more uniform along the hot-arm length. In our design, the geometry of the thin arm is modified by forming a nonlinear structure near the approximate location of the original hot spot. Electromechanical simulations of this design show an increase in deflection, due to a flattening of the temperature profile along the hot arm. The solid model generation, finite element analysis and simulations are carried out using PEA software. Experimental devices are in the process of being fabricated by using a polysilicon rnicromachining process.1. IntroductionMost active MEMS devices employ some kind of actuating mechanism to increase functionality. Various actuating mechanisms like magnetic, electrostatic, thermal, magnetostatic and piezoelectric have been investigated and incorporated for actuating microstructures. The primary features required from many on-chip actuating mechanisms are large deflection (>10 µm), low actuation voltage, low power.consumption, reliability, fast response, ease of design and fabrication, and small size. Thermal actuation is an attractive mechanism for rnicromechanical devices requiring high actuation forces, large deflections, good linearity and low actuation voltage. Thermal actuators, also known as ""electrothermal actuators"", ""heatuators"" or ""U-shaped thermal actuators"", have been largely used in MEMS based devices to provide both in-plane and out-of-plane actuation [l] .Thermal actuators are also easily compatible with standard CMOS circuitry due to their low driving voltage. However, high power consumption remains a major drawback of the thermal actuation mechanism."

Jan 1, 2004

This paper describes developments in ferro-nickel furnace technology, specifically improvements to cooling methods, furnace controls, and high voltage furnace operating regime. The evolution of these technologies is briefly presented, as context for describing the current state of the art that has enabled ferro-nickel furnace operation at over 75 MW and specific energy consumption of less than 400 kWh/t dry ore. Examples from existing operations are used to illustrate present best practices, and potential future trends are discussed: The paper begins with an overview of the fundamental aspects of pyrometallurgical treatment of lateritic ores that drive ferro-nickel furnace design. Furnace wall cooling methods are related to the requirements resulting from specific furnace process conditions, including slag and metal compositions, as well as arc and bath power. The benefits of high productivity and low specific energy consumption resulting from high voltage (shielded-arc) operating practice are discussed, along with the furnace controls and electrical power train that enable such operation even with captive power generation. This paper is an update of that which the authors prepared for the Infacon X ferro-alloys conference.

Jan 1, 2004

By Yves Fouquet

Recent exploration demonstrates that hydrothermal systems related to upper mantle ultramafic outcrops are common in the modern ocean. Most sites are located on slow spreading ridges with a low magmatic budget. Volcanogenic Massive Sulfide (VMS) deposits, associated with basalt, along the Mid Atlantic Ridge (MAR) are volcanically controlled near the topographic highs at the center of the segments. Three preferential settings are identified for ultramafic sulfide mineralization: 1) Off axis, on rift valley walls, near the amagmatic ends of the segments; 2) Non-transform offsets and 3) Ultramafic dome structures at the ridge transform fault intersection. The upper surface of these domes is often interpreted as a detachment fault. Three processes are considered for driving hydrothermal cells in ultramafic rocks: 1) regional heat flow at the ridge axis 2) Cooling of a deep gabbroic intrusion and 3) exothermic heat produced during serpentinisation. Along the Mid Atlantic Ridge, four types of ultramafic hydrothermal mineralization are observed: 1) High temperature (>350°C) sulfide mineralization related to low pH fluids, (ex. The Logachev field at 14°45? N and the Rainbow field at 36°14 N); 2) Medium temperature carbonate chimneys (<100°C) related to high pH fluids (ex. The Lost City site at 30°N); 3) Low temperature diffuse venting associated with extremely high methane discharge and pervasive alteration and silicification of both volcanic and ultramafic rocks (ex : The Saldanha field at 36°34 N); 4) Stockwork mineralization and quartz veins with sulfides related to gabbroic intrusions within ultramafic rocks (15°N). When compared to mineralization in a basaltic environment, sulfide deposits are enriched in copper, zinc and specific elements related to an ultramafic rock source such as Ni and Co. They are also significantly enriched in gold which, unlike in basaltic environments, has a bimodal occurrence both in low temperature Zn-rich assemblages and in high temperature Cu-rich mineral assemblages. The Cu-Zn-Co-Au deposits along the Mid Atlantic Ridge seem to be more common than on land where few similar VMS deposits are known. We consider that ultramafic VMS deposits on slow spreading ridges constitute a specific marine type of mineralization that is less easily than back arc deposits, incorporated into the continent during obduction processes.

Jan 1, 2004

By Bill Loviza, Jimmy Sanders

This report is not everything we would like it to be. Access to information concerning unresolved legal actions is a sensitive matter. Obtaining the information presented in this report was a challenge alone. The Tennessee Department of Commerce and Insurance, Division of Fire Prevention, the firms and individuals that elected to share information did so with various assurances of nondisclosure, confidentiality or anonymity. All those providing information did so with the expectation that the industry and ultimately the public would benefit from this effort. We offer special thanks to Assistant Commissioner, Fire Prevention, Emmett Turner, recently retired Director, Bomb and Arson, Dick Gardner and Director, Codes Enforcement, Randy Safer for support that made this endeavor possible. We make no claim with regard to being a scientific study. We did the best we could with available information. Our task was one of assembly, sorting and reporting. Where collateral information was available we used it.

Jan 1, 2004

By K. Madi, E. Yeugo Fogaing, S. Forest, M. Boussuge, L. Massard, M. Huger, Gaultm C.

This study has been carried out owing to the French research program PROMETHEREF, which aims to improve the knowledge of thermal and mechanical properties of industrial refractories at high temperature. In this frame, this paper relates a collaborative study between Saint-Gobain CREE, R&D Centre for Saint-Gobain Ceramics & Plastics in Europe (Cavaillon), the Materials Center P.M. Fourt of Ecole des Mines de Paris (Evry) and the Research Group on Heterogeneous Materials (GEMH) of ENSCI (Limoges). Data collected at high temperatures by using different means (bending tests, ultrasonic measurements,...) allows the identification of the high temperature behavior of two fused cast materials, produced by Saint-Gobain group for the glass manufacturing industry. The results emphasize the importance of the transformation of zirconia and of the viscosity of the glassy intergranular phase on the mechanical behavior. Damage under the form of microcracking caused by thermal expansion mismatch between the phases is also observed during cooling down at low temperature, when the material is elastic.

Jan 1, 2004

By S. Sun

The equilibrium distribution of Cu, Fe and Ni between Cu-Ni-Fe mattes and Pt alloy was measured as functions of the sulphur partial pressure (pS2), oxygen partial pressure (pO2),temperature and Fe content of the matte. The distribution ratios of Cu, Fe and Ni between matte and alloy were independent of oxygen pressure when the pS2was fixed at 2.5x10-5atm and pO2was varied between 10-15and 10-12atm. The distribution ratio of Cu, Fe and Ni increased as the sulphur partial pressure increased. The Cu and Ni distribution ratios decreased with increasing temperature and the Fe distribution ratio increased slightly over the temperature range of1350?1500°C. For mattes where the proportions of Cu and Ni were kept constant, the distribution ratio of Cu increased as the Fe content in the matte increased. The Fe and Ni distribution appeared to be independent of the iron content in the matte and had a value of 1.2 and 1.6 respectively. The activity of Cu, Fe, Ni in the matte was calculated using a regular solution model for solid Pt-Fe-Ni-Cu alloy. The activity coefficient of Cu, Fe and Ni decreased as pO2and pS2increased.The activity coefficients also appeared to be independent of the Fe content and temperature over the range of 36 to 54 wt% iron and 1350 to 1500°C respectively. Keywords: activity, alloy, matte, thermodynamics

Jan 1, 2004

By W. W. Rudolph, L. N. Trevani, P. R. Tremaine

UV-visible spectroscopy, Raman spectroscopy, and vibrating tube densimetry have been used in our laboratory to determine equilibrium constants of aqueous species at temperatures as high as 325 °C. The UV-visible and Raman spectra of solutions containing metal complexes and ionized acids or bases can be used to yield formation constants by applying curve fitting methods to resolve the contribution of each species. Colorimetric pH indicators identified by Johnston and coworkers at the University of Texas (Austin) provide an alternative means of determining ionization constants and the pH of complex mixtures. High precision density measurements over the same range yield standard partial molar volumes, which are key parameters for "equations of state" for aqueous species. Examples are given for the copper-ammonia system, simple carboxylic acids, and the iron-sulphate system.

Jan 1, 2004

By Li. Jiarong, Zuojian Liang, Qingyan Xu, Baicheng Liu, Shizhong Liu, Hailong Yuan

Single crystal solidification of turbine blades is a key technology for the production of reliable and high efficiency gas turbines. The solidification process of single crystal investment castings causes a number of problems that have to be solved such as the increase of casting defects and complexity of production process. Computer modeling and simulation is helpful to predict the defects and improve the process design. In the paper, a mathematical model for three dimensional simulation of solidification and single crystal growth of investment castings was developed based on CA, mechanism of crystal growth and basic transfer equations such as heat, mass transfer equations. Many factors including constitutional undercooling, curvature undercooling and anisotropy, which had vital influences on microstructure evolution, were considered in the model. Temperature, crystal growth interface and structure defects of investment castings of single crystal superalloy were investigated at withdrawal rates of 4.5mm/min and 7mm/min. Simulated results showed that microstructure evolution and structure defects were predicted reasonably and calculated results were coincident with experimental ones. The study indicated that three dimensional solidification simulation technique is a powerful tool for understanding the fundamental of solidification and the formation of structure defects in single crystal investment castings and finally for optimizing process design.

Jan 1, 2004

By A. K. K. Rompel, G. K. Chunnett

Introduction Structure appears to be of secondary importance to the Bushveld Complex when viewed from a distance. However, a closer look already reveals that large fault zones bound the Bushveld Complex. These fault zones are deep-seated crustal lineaments of continental magnitude such as the Thabazimbi-Murchison Lineament, the Johannesburg-Barberton Lineament, the Palala Fault zone and the Rustenburg fault. Furthermore, the Bushveld Complex is transected by large faults such as the Vlakfontein Fault, visible in the Pilanesberg, the Steelport Fault and the Laersdfrift Fault in the Eastern Bushveld, the Brits Graben, and a multitude of dyke generations (Figure 1). When pursuing structures on a project scale, the lack of outcrop, particularly in the western part of the Bushveld, is of no help for the exploration geologist. Consequently, the first dataset that needs to be considered is the Landsatimagery. Older Landsat TM 5 or newer Landsat ETM 7 will immediately reveal areas of outcrop for field visits, and, after further processing, indicate the geological units, in particular the platiniferous Critical and the Main Zone of the Rustenburg Layered Suite (Figure 2). Airborne magnetic surveys are the subsequent dataset necessary for any decent interpretation of the geology under the ?Black Turf? cover. Currently Anglo Platinum acquires aeromagnetic surveys with a flight height of 20 m and a line spacing of 50 m. These result in high-resolution imagery absolutely crucial for dyke delineation and dip modelling, stratigraphic layer detection, IRUP detection and possibly pothole discovery and fault delineation (Figures 3 and 4). However, the aeromagnetic surveys and the Landsat imagery reveal structures very much confined to the surface and may be hundreds of metres above the platiniferous reef horizons. This may lead to inaccuracies. When determining the underground structures for shaft sinking and mine planning, a 3D seismic survey is advisable. Too many shafts have been sunk in the Witwatersrand Basin for gold and in the Bushveld for platinum without sufficient information of the structure beneath. Recent 3D seismic surveys in the Bushveld have proven the technology and visualized the reef horizons and led to an interpretation of the underground structure (Figures 5 and 6). [ ]

Jan 1, 2004

By P. Mpofu

In this work, the modification of interfacial chemistry of colloidally stable kaolinite clay dispersion has been carried out to improve its flocculation performance and dewatering behaviour. Synergistic action between dispersion pH, hydrolyzable metal ion and high molecular weight polymeric flocculant structure type (anionic polyacrylamide-acrylate copolymer (PAM) and non-ionic polyethylene oxide (PEO)) was found to play a pivotal role in inter-particle bridging, the enhancement of the settling rate and extent of consolidation of the pulps. Flocculation with PEO led to higher settlings rates in acidic than alkaline pH, whilst for PAM, the maximum dewatering rate was achieved in the neutral pH range 6 - 7.5. Upon shear, the PEO flocculated pulps showed dramatic improvement in consolidation to 40 wt%, the extent of which was greater at lower than high pH values. For PAM-based pulps were however, not shear-responsive, lower sediment solid contents of 15 - 23 wt% was observed between pH 3 and 11. Hydrolysable metal ions, Mn(II) and Ca(II), used respectively at pH 7.5 and 10.5 in conjunction with PAM and PEO, significantly enhanced the settling rates and consolidation of the pulps. The findings exemplify the strong links existing between pH-mediated particle surface chemistry. polymer structure-conformation, inter-particle bridging and dewaterability of kaolinite dispersions.

Jan 1, 2004

By B. D. Pandey, D. Bagchi, Premchand

During the separation and recovery of metals from the ammoniacal leach liquor of Indian Ocean nodules by solvent extraction-electrowinning (SX-EW) in close-loop operation, the copper electrolyte containing ~40g/L Cu, 20 g/L Ni and 180 g/L sulphuric acid is bled-off to control the impurities. The recovery of copper and nickel as powders has been examined from the copper bleed solution following partial decopperisation, crystallization of mixed sulphate of the two metals and aqueous hydrogen reduction. From the dissolved sulphate solution containing 17.68 g/L Cu, 18.83 g/L Ni and 0.03 g/L Fe, the copper powder was precipitated at initial hydrogen pressure of 26 bar in an autoclave in 90 min at 140 °C. The residual copper from the spent solution was removed as sulphide and nickel powder was then recovered (99%) in two stages from a solution of pH 4.5 at 40 bar pressure and 190 °C. However, 98% nickel recovery in one stage was achieved when hydrogen reduction was carried out from an ammoniacal solution in the pH range 9-11. Copper and nickel powders were produced from the bleed solution with acceptable purity and specifications suitable for P/M applications.

Jan 1, 2004

By S. A. Shuey, P. Taylor

The recycling of electronic waste (e-waste) tends to be a rather complex undertaking when considering the intimate bonding of materials in the average printed circuit board. The development of a recycling process is further complicated when considering the wide variety of products being generated under the heading of “electronics” as well as the constant change in materials of construction coupled with the speed at which electronics are changing. CSM researchers have undertaken a survey of the current state of pyrometallurgical processing of e-waste. This base-line will set the stage for the development of new recycling technology at CSM.

Jan 1, 2004

By H. Arima, Y. Kudo

In general, the iron content of zinc leach residue produced by sulphuric acid leaching from calcine is disposed as jarosite or goethite into a tailing dam. More recently, these iron residues have been treated pyrometallurgically to avoid waste disposal. The Iijima refinery selected a different zinc leach residue treatment process for iron control when it was established in 1971. The Iijima refinery is the only plant in the world that has processed a zinc leach residue by the combination of SO2 pressure leaching and O2 pressure hematite precipitation. The process enhances zinc recovery and recovers gold, silver, copper, lead and rare metals in saleable by-products. This paper focuses on the two stages of autoclave application in the zinc leach residue treatment process. The detailed flowsheet and recent advancements to improve the quality of by-products are discussed.

Jan 1, 2004

Viscosity measurements were carried out on slags in the CaO-Cu2O-CuO-MgO-SiO2systemcontaining ~ 63 wt% SiO2in air. The experimental work was carried out over a range of temperatures where the slags were completely liquid. Initial measurements were on a binary CaO-SiO2slag to which incremental additions of CuxO-MgO-SiO2slag with the same silica mole fraction were made. The viscosity-temperature relationship was measured for slags with‘Cu2O’contents of 0.02, 0.19, 0.38, 0.79, 1.69, 2.47, 3.01, 5.31 and 10.0 wt%. The proportions of Cu+and Cu2+in the slags were determined. The oxidation state of Cushifted from predominantly Cu+to Cu2+, with the Cu+/Cu2+ratio of approximately 0.3 for slag with a Cu content above 2 wt%. This is equivalent to Cu1.13O. The trends observed for changes of Cu2+/Cu+redox ratio with slag chemistry were consistent with the literature. Decreasing the CaO content by substituting copper oxide resulted in a decrease in the Cu+/Cu2+redox ratio. The change in ratio corresponded to a shift of the value of x in CuxO from an initial value of 1.8 to 1.1,when the slags contained 10% ‘Cu2O’. In this study, the SiO2content of the slags varied between 64 and 60 wt% as the Cu content increased. The viscosity of the slag containing 10 wt% CuxO was nearly 4.5 times lower than the binary CaO-SiO2slag. As the silica mole fraction (xSiO2) actually stayed constant (0.61±0.009),the results show that CuxO acted as a network breaker. Comparison with other ternary slags with similar silica mole fractions suggest that that addition of CuxO to silicate slags has a stronger effect on lowering the viscosity than FeO or MnO has on a molar basis. Keywords: viscosity, copper, silicate, slags

Jan 1, 2004

By Ozdemir. O.

Magnesium additions to aluminum enhance strength and hardness, lowering density, and improving corrosion resistance. However, during melting and casting processes, significant amounts of magnesium are lost due to selective oxidation. Preventing these losses would reduce the production cost and improve the quality of the final product. The effects of strontium addition on the oxidation behaviour of aluminum-0.5% and 1% magnesium alloys were investigated by monitoring sample weight gains with time with a thermogravimetric balance at 750°C. Sample cross sections have been examined using Field Emission Gun Scanning Electron Microscope.

Jan 1, 2004

By Frederick C. Rhyner

Drilled shafts have become an economical foundation choice for bridges in the northeast United States, especially when they can be constructed over water without the use of cofferdams. For the Boscawen-Canterbury Bridge over the Merrimack River in New Hampshire, an unusual design was used to avoid the use of cofferdams and avoid the need for pier caps at the waterline. This design used a pair of integral drilled shaft ? columns to form a bent type of substructure for support. Drilled shafts were 8-foot diameter, about 90 feet deep, with 16-foot long rock sockets. These are integrally constructed with 6-foot diameter reinforced concrete columns extending 37 feet from the waterline to the superstructure. Design load cases focused on lateral loads from ice flows, stream flows, wind and seismic events. Alternative analyses using different methods were made to check the design results. This paper discusses the subsurface conditions, design of the drilled shafts and columns, rebar and joint detailing issues, and construction of the drilled shafts.

Jan 1, 2004

By J. Robison, H. Pieterse, C. C. Smith, M. Luque, S. Chipman

Phase change during pressure let down releases significant amounts of energy that must be controlled to avoid undo wear and tear on equipment. Hydrometallurgical slurries require flow control equipment (valves and tanks) made of expensive materials to withstand the abrasive, and often corrosive nature of the slurry. Presented is a model of the nozzle of a let-down choke which is designed to control the flow pattern that exits the choke (valve) as it enters the receiving tank. This model can be used to design chokes which allow for the dissipation of the energy released during pressure let down by spreading the stream over a significant portion of the slurry pool in the receiving tank to minimize wear on equipment near the nozzle exit and the bottom of the slurry tank. An example uses the model to choose the nozzle expansion (area) ratio to select the outlet slurry velocity and slurry expansion angle.

Jan 1, 2004

By R. Todd Swinderman

Variations in designs between belt cleaner systems are so wide that it is impractical to establish a dimensional stan- dard. The number of variables that affect the efficiency of belt cleaners is too great to assume a required number or style of cleaners for broad classifications of bulk solids or typical applications. The amount of carryback remaining on the belt is more dependent upon the characteristics of the bulk solid and the physical parameters of the conveyor system than it is on tonnage of material conveyed. Therefore, a performance-based standard is proposed. Three levels of cleaning performance are proposed: • Level I cleaning is general specified when concerns about carryback are not critical. Cleaning systems normally associated with achieving a Level I performance are single or double cleaner systems with one-piece blades undergoing poor to average maintenance. Frequent cleaning of the carryback that falls from the return run will likely be required. • Level II cleaning is generally specified when carry- back is of concern but does not create a safety or environmental problem. Cleaning systems normally associated with Level I1 performance are multiple cleaner systems with segmented blades undergoing the manufacturer&apos;s specified maintenance. Regular but infrequent cleaning of the carryback that falls from the return run will likely be required. • Level III cleaning is generally specified when con- cerns about carryback are critical. Concerns range from safety to environmental to product contamination. Cleaning systems normally associated with achieving a Level 111 performance are multiple cleaner systems in conjunction with at least one low- volume water spray. Scheduled inspection and the manufacturer&apos;s specified maintenance would have to be performed to maintain a high level of cleaning performance. Difficult-to-clean bulk materials may require the use of a washbox system with multiple cleaners using a combination of low-volume eater sprays to lubricate the cleaners and high-volume sprays to keep the washbox and discharge piping freely flowing. Further addition of a water and sludge recycling system reduces the amount of water that ends up in the product to a negligible amount. Very infrequent cleaning of the carryback that falls from the return run will be required. PURPOSE The purpose of this proposal is to propose a standard method for specifying belt cleaner systems based on user expectations and equipment performance over time. DEFINITION In bulk solids handling by conveyor belt, carryback is the material that adheres to the belt after the belt discharges its cargo. PROPOSED STANDARD Required Basic Good Practices There are a number of basic design and operating principles that are good practice for the selection, installation, and maintenance of belt cleaning systems on conveyors in order to achieve "standard belt cleaning performance over time. 1. The Belt Cleaning System shall be designed to meet the performance requirements based on the worst operating conditions and worst bulk solids proper- ties that are expected. 2. Each conveyor discharge point shall be designed to readily accept the manufacturer&apos;s recommended minimum number of belt cleaners. In addition, the discharge chute shall be designed to accept, with minor modifications, at least one additional cleaner if it is required.

Jan 1, 2004

By J. Alexis, G. Ye, E. Burström

Over the past twenty years the 3 MW DC arc furnace at MEFOS has been frequently used for development of new processes. These processes include recovery of valuable metals from slag, sludge and dust from steel and other metallurgical industry, treatment of ashes from power plant and incinerators, smelting reduction of minerals and zinc recovery from EAF dust. The process characteristics of the DC arc furnace operation in terms of: ? selective reduction, ? total reduction, ? process stability and flexibility, ? dust carry-over, ? thermodynamic conditions provided in the hot spot area, ? precision in composing slag products These are analysed and described in this paper based on technical results from selected test campaigns over the years and thermodynamic considerations. The electromagnetic properties of DC arcs beneath the electrode have been studied by CFD simulation. The calculated result enables us to understand some interesting technical phenomena observed. The heat balance has also been considered based on data obtained from test campaigns and heat balance calculation.

Jan 1, 2004

By Robert Hopler

DESCENT INTO A COAL MINE From “The Playbook of Metals, including Personal Narratives of Visits to Coal, Lead, Copper, and Tin Mines,” by John Henry Pepper. Published by Routledge, Wa rne, and Routledge, London, 1862 ENGINEERING NEWS New Yor k January 22, 1903 THE BEGINNING OF THE END OF DYNAMITE. In another part of this issue we have reported the results of some test results made upon one of the safety powders. It will pay every c o n t r a c t o r, miner, or user of explosives in any form to carefully re a d the article re f e r red to. Dynamite has done a gre a t work in the service of man, as did black powder before it; but its i n h e rent dangers are admitted by all and are proved by the long list of deaths and injuries, and destruction to property which annually occur through its use. Why should we continue to use an explosive that annually kills and maims hund reds of men, when others are available which are equally powerful, no more expensive and far less liable to accidental discharg e ? Dynamite when first manufacture d is pure and comparatively safe; but most unfortunately it does not always stay pure; it “rots,” and then it is exceedingly dangerous. More than this, the explosive part of dynamite is a liquid, nitro - g l y c e rine, which is absorbed or soaked up by sawdust, wood pulp or the like. So long as this liquid nitro - glycerine remains pure and remains “soaked up,” or absorbed t h e re is little danger. It has been found, however, that the nitro - g l y cerine leaks under certain conditions. During thawing it fre q u e n t l y leaks out of the stick, or if it becomes wet the water causes the n i t ro-glycerine to leak out. In either case free liquid nitro - g l y c e r i n e escapes, and in that free state it may be exploded by any very slight shock. Nor is this all, if a stick of frozen dynamite be bro k e n a c ross it has been found by tests that the frozen nitro - g l y c e r i n e w h e re thus broken is very sensitive to shocks afterward .