Rates of oxidation were studied for levitation-melted samples of Fe-C, Fe-Si, Fe-C-Si, Fe-C-P, Fe-C-Mn, and Fe-C-S alloys oxidized by mixtures of either 5 or 10 pct O2, in helium at several temperatures in the range 1850o to 2050°C. The concentrations of the oxidized elements decreased linearly with time. Mass transport in the gas phase was found to be the rate-controlling step. Ilowever, a mulliple -film model was necessary to account for the flux of iron and manganese vapor counter to the oxygen flow. THE advent of the basic oxygen and spray-refining processes of steelmaking has generated considerable interest in the kinetics of reactions between oxygen-bearing gases and liquid iron alloys. The object of this research was the determination of the role of mass transport in the gas and metal phases and of surface chemical reactions in the overall oxidation process. Of the reactions for elimination of elements dissolved in liquid iron, the oxidation of carbon has been investigated most extensively. Studies by Fuji and Ura,1 Fuji,' and Gunji et a1.,3 done with pilot-scale basic oxygen furnaces, indicated that mass transport of gaseous oxygen was rate controlling when the metal carbon content was greater than 0.15 to 0.30 pct. When the carbon content was less than this critical amount, diffusion of carbon dissolved in the iron was thought to be rate limiting. L. A. Baker et a1.4,5 levitated samples of iron-carbon alloys and oxidized them in CO-CO2, CO-C02-He, and O2-He atmospheres at 1660°C. These investigators found that the metal carbon concentration decreased linearly with time and their samples exploded when the carbon content fell below about 0.8 pct. They concluded that the rate-limiting step was the transfer of oxidant to the gas-metal interface. A model based on this rate-limiting step predicted decarburization rates within a factor of two of those experimentally observed. The explosion of the samples was attributed to a shift in rate-controlling step from gas-phase mass transport to transport of carbon dissolved in the metal. L. A. Baker and R. G. ward6 and R. Baker7 used freely falling droplets to investigate oxidation kinetics. In both papers, the authors speculated that flame fronts may have been partially responsible for the lack of better agreement between experiment and theory. Swisher and Turkdogan8 oxidized liquid iron having an initial carbon content of 0.97 pct with CO-CO2 and CO-C02-Ar mixtures at 1580°C. They concluded that a surface reaction was the rate controlling step. Iron-silicon alloys have been oxidized by R. Baker7 and Filipov and Martynov.9 R. Baker 7 also studied iron-carbon-silicon alloys falling as liquid droplets through oxygen. He found that the rate of both carbon and silicon oxidation varied inversely with the drop radius. When the initial silicon concentration was greater than 6 pct, the samples cooled during their fall. Manganese oxidation has been studied by R. Baker,7 and by Filipov and Martynov.9 ward10 investigated the loss of manganese from liquid iron under vacuum. He found that mass transport of manganese vapor was rate limiting in argon atmospheres of 0.02 torr to 700 torr pressure. Iron-sulfur alloys were desulfurized with H2-He and H2-Ar mixtures by Peters et al.11 A model based on the transport of H2S from the gas-metal interface into the bulk gas gave fair agreement between the predictions of the model and the experimental results. EXPERIMENTAL TECHNIQUE Essentially, the technique consisted of using helium-oxygen gas mixtures to oxidize levitated samples of liquid binary and ternary iron-base alloys. The fused silica reaction tube is shown in Fig. 1. The coil design is similar to that of L. A. Baker et al.4'5 A Tef-lon-sheathed, ferritic stainless steel lifter (B) and an alumina pedestal (C) were used to support the sample in the coil prior to levitation and for the recovery of the sample. Samples were inserted into

Jan 1, 1970

By J. C. M. Li

A dislocation model is constructed for a cylindrical tilt boundary of which the axis of tilt is parallel to the axis of the cylinder. The strain energy per unit area calculated from this model agrees with thut of an infinite vertical wall of edge dislocations. Based on this model, a dislocation mechanism for the shrinking of such a cylindrical boundary is proposed. The power relation between the grain boundary velocity and the driving force is accounted fm by the stress dependence of dislocation velocity. The activation area for grain boundary motion is found to correlate with that .for Creep in aluminum. In the preceding paper' the velocity of a curved grain boundary is found to be a power function of the driving force, [1] where M is the velocity at unit driving force, y is the grain boundary energy, and p is the radius of curvature. This finding adds another nonlinear rate equation to metallurgical phenomena. While a macroscopic theory for the steady state as just presented2 can be used to understand the shape of the moving boundary, such theory usually does not provide any information about the atomistics of the process. It is attempted in this paper to discuss the nonlinear rate equation in terms of a dislocation mechanism. A DISLOCATION MODEL FOR A CYLINDRICAL TILT BOUNDARY Before a dislocation mechanism can be proposed for the motion of a cylindrical tilt boundary, it is necessary to construct a dislocation model for the boundary. For simplicity, a tilt boundary in a simple cubic lattice will be examined. Although this does not represent the situation in aluminum, it is expected that the general features will be similar. The details of the model in the fcc lattice can be constructed when a refinement of the simple model is called for. A cylindrical low angle tilt boundary in a simple cubic lattice is shown in Fig. 1. Two sets of edge dislocations are needed as shown. A schematic representation is shown in Fig. 2(a). In terms of a continuous distribution of dislocations, the density of dislocations n, of Burgers vector b, in the small segment ds of the grain boundary is Similarly the density of dislocations n, of Burgers vector bz in the same segment ds is where is the tilt angle of the grain boundary. Based on this continuous distribution of dislocations in the grain boundary, it can be shown that the interaction between a small segment of the boundary and the rest of it is zero. Furthermore, the stress produced at any point inside or outside the cylinder is also zero. This shows that the model is acceptable in the sense that the boundary has no long-range stresses. Since the model of continuous distribution of dislocations in the grain boundary does not reveal the interactions among individual dislocations, a discrete dislocation model has to be used for such purpose. For simplicity, an equivalent model is shown in Fig. 3. This arises because the total Burgers vector is, from

Jan 1, 1970

By Gordon H. Geiger, John M. Svoboda

One mechanism of metal penetration into mold aggregates by cast steels is vapor state mass transport. In order to further understand and quantify this mechanism, the steady-state diffusion of metallic vapors was studied at 1250" to 1600°C in controlled oxygen pressure atmospheres by measuring the weight loss from a metal bath whose vapors were allowed to diffuse through a porous aggregate compact held at constant temperature. Mass transport rates substantially greater than those predicted from the assumption that the vaporizing species was the elemental metal vapor were observed. Vaporization rates were found to increase with an increase in the oxygen partial pressure in the gas atmosphere with maximum vaporization occurring at oxygen partial pressures just below those in equilibrium with a liquid oxide layer at the given temperature. When the liquid oxide layer was present, no vaporization was observed. Metal carbonyls were ruled out as the vapor species involved because of their thermodynamic properties. The species with the enhanced volatility were deduced to be gaseous metal-oxygen molecules, probably the polynuclear oxides (FeO)2 and (Mn0)2. Diffusion followed the ordinary diffusion mode, and Knudsen diffusion is not important in normal foundry molds. The interdiffusivities of the metallic vapors and the mold atmosphere, through the porous aggregates, were measured. The effective interdif-fusivity of the vapor species and mold atmosphere through the aggregate may be expressed as follows: Deff,12 - — where E is the void fraction of the aggregate and 7 is the "tortuosity factor". Aggregate material had no effect on diffusion rates, and the only relevant parameter was the void fraction. Values for 7 ranged from 3 to 6 for normal foundry aggregates with 4 being considered a good representative value. An area of interest in high-temperature metallurgical processes which has received little attention in the past is the diffusion of metal vapor species in porous aggregates. Research into the metal penetration phenomenon' in foundry molds has shown that a major penetration mechanism is the vapor transport of metallic species into the porous foundry sand molds, followed by condensation of metallic films on the sand grains. Considerable study of the vaporization of metallic species has been reported in the literature, and the vapor transport properties of many metallic species have been determined.2'3 Many instances have been observed where the vaporization behavior could only be explained by the existence of a metallic species with a vapor pressure greater than the elemental metallic species. These species were identified or, in some cases, presumed to be carbonyls,4,5 hydroxides,6-9 or vaporous oxides.10-16 The diffusion of gases through porous aggregates has received considerable attention in the literature pertaining to catalysis, although primarily at low temperature, and more recently in the literature concerned with ore reduction.17-22 The following experiments were devised and carried out in order to determine the nature of the metallic species involved in the metal penetration phenomenon, and the effective diffusivities involved. EXPERIMENTAL APPROACH Steady-state diffusion was selected for experimental convenience. The experimental systems used, shown in Figs. 1 and 2, consisted of a porous aggregate specimen contained in an impermeable alumina tube held above, and just separate from a metal bath. The entire system was held at constant temperature and pressure in a furnace with a controlled oxygen partial pressure atmosphere. After a brief period of nonsteady state behavior, a steady flux of metal vapor through the porous aggregate will develop due to the concentration gradient of metallic vapor in the gas phase. The flux of metallic vapor from pressure may be neglected because there is no pressure gradient. There is no flux from convection because there is no net flow of gas within the metal-aggregate system, and thermal diffusion is negligible compared to the flux from ordinary diffusion. If the material being studied is allowed to vaporize until steady-state behavior is attained, the experimental results may be analyzed using Fick's First Law.

Jan 1, 1970

By John F. Abel

A good mining engineer is supposed to make a good mine. What then makes a good mining engineer? There certainly are a lot of answers to that question. The answers depend on whether you are one, work for one, or employ one. There are several cliches about mining engineers, and there is some truth in them-as there usually is in any stereotype. Hollywood chose Jeff Chandler to portray a mining engineer in Foxfire. The image here was of an almost one-man mining operation. When Chandler picked up a jackhammer, cradled it in his gut and started drilling out a tunnel round, it gave one the hives. I would have liked to see him finish just one round that way. There are limits to what even the most hairy-chested of us will try. We can assume that Hollywood feels it needs to over- draw any profession to add impact.

Jan 1, 1970

By E. J. Bonet, P. B. Crawford

It is fairly common practice to reinject water into the aquifer near the oil-water interface in water-drive reservoirs. There have been many studies of aquifer behavior without reinjection,l-5 but apparently no analytical studies have been made to indicate performance when injection wells are present in the aquifer. The diffusivity equation may be used to describe the pressure behavior in an aquifer. When sources are present it can be written as A general solution of Eq. 1 may be obtained as the sum of two solutions. One is a general solution of the homogeneous equation, obtained by dropping the source term in Eq. 1 and still satisfying the required boundary conditions. Another is a general solution of Eq. 1 satisfying homogeneous boundary conditions.1° The first solution, which corresponds to the aquifer without reinjection, has been given quantitative and qualitative treatment in the literature.l-5,8,9 The latter solution will be treated here. Solutions with variable injection rates are obtained by superimposing solutions with constant rates, so we have considered only the latter. Five cases have been treated here: 1. A linear aquifer of finite width and extent. Water is injected into the aquifer at point xo, yo at constant rate. The pressure along the line x = 0 is maintained at zero pressure. (See Fig. 1.) Equations showing the pressure distribution, rates, velocity and cumulative influx have been developed. Certain numerical results are shown. 2. A linear aquifer of finite width and extent. Water is injected into the aquifer at point xo, yo at constant rate. The rate of production along the oil-water water contact is maintained constant. Equations showing the pressure distribution inside the aquifer are presented. 3. A linear aquifer of finite width and extent. Constant pressures are maintained at opposite ends of the aquifer. Water is injected at constant rates at point xo, yo. Equations showing the pressure distribution are shown. 4. A linear aquifer of finite width and infinite extent. The pressure is maintained constant at the oil-water contact. Water is injected at a constant rate at point xo, YO. 5. A linear aquifer of finite width and finite extent. The pressure at the oil-water contact is maintained constant. Water is injected at constant rate per unit length along a line x,. The Linear Aquifer The linear closed aquifer, performing at constant terminal pressure was selected as the first case to be analyzed. The development of the equations is based on uniform injection per unit of thickness, and gravity effects are neglected. In practical application this condition is probably most closely achieved when the

Jan 1, 1970

By Neal P. Cochran

It is always a pleasure for me to address a group of mining engineers. I am doubly grateful when I am allotted sufficient time to describe the total Office of Coal Research program. My remarks are directed to our total program but I trust you will all understand my emphasis of the utilization aspect of our activities since that is my portion of the program. From its inception, the Office of Coal Research has sought out creative ideas for improving our national use of coal by developing new uses, improved mining procedures, lower costs, and appropriate studies with respect to the resource itself. Quite early in the game, our Economics and Marketing Division contracted for studies with respect to New England export market, Western coal, and similar items. Our Mining and Preparation Division has successfully developed a packaged coal-fired boiler and has partially developed a packaged fluid-bed type boiler as well. Our Mining and Preparation Division is working in such diverse fields as treatment of sewage with coal and the separation of coal into distinct-petrographic constituents so that all fractions of the coal can be put to the best possible use. We would like to be doing more work on improved mining methods, better preparation techniques, and any other mining improvement that will benefit the industry and our program. The synthetic fuel plants I will describe later will operate seven days per week, 24 hours per day. We would like the mine to operate on this same sort of cycle and are prepared to support research that will lead to this.

Jan 1, 1970

By L. T. Larson

The spectral reflectivity of zirconium in light of 441 to 668 nanometers (nm) wavelengths and air immersion has been determined. Bireflectance and apparent-angle -of-rotation measurements show zirconium to be optically isotropic when examined in light of approximately 484 nm wavelength. There is a direct relationship between bireflectance and the tilt of the basal pole of zirconium from the surface normal. This relationship allows the determination of the spatial orientation of the basal pole of an individual single crystal within a coarse-grained poly crystalline section to within± 2 to 3 deg for angles of basal pole tilt from 0 to 90 deg. In recent years considerable attention has been given to the quantitative determination of optical properties of opaque minerals by use of vertically incident, plane-polarized light. In particular, Cameron' and Cameron et a1.2 have developed criteria for the identification of a large number of anisotropic ore minerals based upon measurement of the apparent angle of rotation and the ellipticity or phase difference of the reflected light. It was shown by Larson and Pickle-simer3 that apparent-angle-of-rotation measurements may also be used to determine crystallographic orientations of grains of noncubic metals. In particular, it was shown that the basa.1 pole orientation in space of zirconium grains can be determined to ±3 deg for those grains with basal pole tilts of 10 to 90 deg from the plane of the section. Another, even more widely studied, optical property is reflectivity. cameron4 has commented upon measurement of the reflectance of plane-polarized, vertically incident light and Bowie and Taylor5 have made such measurements an integral part of their system of ore-mineral identification. Leow6 has reported on the spectral reflectivity of molybdenite and has used reflectivity values to calculate refractive indices and absorption coefficients. Cameron7 has made use of reflectivity values to ascertain aniso-tropic ore mineral symmetry and Piller and v. Gehlen8 have evaluated sources and importance of errors in reflectivity measurements as applied to calculation of optical constants. cambon9 has shown that reflectivity measurements using vertically incident, plane-polarized light are useful in the investigation of metals and in the identification of phases present in alloys. Bronson10 has made preliminary measurements on the optical anisotropy of beryIlium and Mott and Haines11 have published qualitative data on the intensity of light reflected from sections of bismuth, tin, and aluminum when these metals are microscopically examined under crossed polarizing plates. Koritnig12 has correlated the reflectivity of homogeneous solid solutions with their chemical compositions. From the above work and investigations in progress by this author, it is apparent that accurately determined values for the reflectance of vertically incident, plane-polarized monochromatic light from carefully polished surfaces of noncubic metals can prove useful in identification, composition determinations, and crystallographic orientation applications. Finally, reflectivity values, when measured in two media of differing refraction index and related to standards whose spectral reflectivities in these media are known, can be used to calculate optical constants such as refractive index and absorption coefficient. These constants may prove of use to those concerned with problems of electron band configuration. This paper reports the spectral reflectivity of zirconium measured in light of 441 to 668 nanometers (nm) wavelengths and air immersion. It also gives maximum bireflectance values for a prism section of zirconium in these wavelengths and shows how bire-flectance may be used to determine the crystallographic orientation of zirconium single crystals. Because of the lack of information on the reflectivities of the standards in oil immersion, no attempt is made to calculate the refractive indices or absorption coefficients although it is recognized that such values may be of fundamental importance. METHOD Single crystals of zirconium were cut by electro-discharge machining from a single-crystal rod grown from iodide bar by an electron-beam zone-melting process.13 The crystal sections were mounted in cold-setting epoxy resin and mechanically polished to a plane, uniform, bright surface. Each crystal was then chemically polished in a 26/26/43/5 mixture (by vol) of water, nitric, lactic, and hydrofluoric acids to remove the mechanically damaged and smeared surface layer. Final polish was obtained by electropolishing at 30 v in a bath of methyl alcohol and perchloric acid (98/2 by vol) at -70oc.14 Reflectivity measurements were made using a photometer system designed and developed at Oak Ridge National Laboratory and described in detail by Larson.15 Briefly, the reflectivity measuring system consists of a reflecting microscope; a double-beam, null-balancing photometer array; a mechanically driven microscope stage; and a direct X-Y readout of the reflectivity of the specimen relative to its orientation on the microscope stage. The measuring photometer receives its signal from the specimen through a slotted Wright occular placed on top of the photovisual head of the microscope. The reference photometer receives light through a flexible glass "light pipe" from a mirror in the reflecting system of the microscope. Monochromatic light is attained through use of interference filters (15-nm half-peak width pass bands) placed in front of a stabilized Vickers 12 v, 100 w, tungsten-filament, quartz-iodide lamp.

Jan 1, 1970

By J. Szekely

A rrlethod is presented for the estitnation of oxygen pickup by teettzed molten steel streams. Of the mechanisrt~s considered for oxygen absorption, physical entrainment appeared to be the most significant. The estent of this physical entrainment may be calculated by the application of boundary layer theory. It was found that the values of oxygen pickup thus predicted were in wry good agreement with data reported in the literature, in the case of short, well-defined metal streams. This entrainment model does not provide an adequate description of oxygen pickup by long streams, exoosed to external winds and where breakup of the streatn is likely. WheN molten steel is teemed into a mold or tundish it will absorb oxygen contained in its environment. Recently interest has been expressed in the measurement and possible prediction of the extent of this oxygen absorption: this interest owes its existence to two principal factors: a) the desirability of providing a quantitative assessment of the role played by the absorbed oxygen in impairing the quality of (vacuum degassed. stainless, or continuously cast) steel; b) the need for providing guidelines for stream protection methods. The purpose of this communication is to suggest a simple method for the prediction of oxygen absorption by continuous metal streams and to compare the predicted values with the data available in the literature. It is hoped that this method may provide at least an initial framework for the interpretation of additional data that might become available. FORMULATION Consider a continuous metal stream falling into a molten metal pool as depicted in Fig. 1. This system may absorb oxygen due to the following two mechanisms: 1) physical entrainment of gases (including oxygen) into the molten pool where reactions. thus absorption, will occur; 2) mass transfer (convec:tive diffusion) of oxygen to the metal stream. 1) Physical Entrainment. The physical entrainment may be calculated by using the concept of the diaplace-ttzent tlzickness of the laminar boundary layer, which will be stated briefly in the following.&apos; When a fluid flows past a solid surface, a portion of the fluid close to the surface is retarded due to fric-tional forces. This region in which the velocity of the fluid differs from that in the main stream is called the boundary layer. An illustration of this is given in Fig. 2 where it is seen that the thickness of the boundary layer increases as we move along in the x direction. In the laminar region, when Re, < 10&apos; the thickness of the boundary layer is given by the following relationship: f =4.64 Re;1" [1] where 61 is the boundary layer thickness, x is the length along the leading edge, Us is the velocity of the free stream, (i is the viscosity of the fluid (gas in this instance).

Jan 1, 1970

By G. S. Cole, G. F. Bolling

A series of Al-Cu alloys has been cast from constant superheat to solidify either with a hot top or with a free liquid/air interface. All the other variables which affect relative fluid motions were kept constant except the imposition of slow rotations m oscillations of the mold. Depending upon the exact circumstances, evi-dence could be found for the nucleation of equiaxed grains from dendrite bits detached from the columnar zone, or from the free surface, or from solid bits induced at pouring; a special experiment showed the solute buildup during ingot solidification and by inference the reality of constitutional supercooling. All methods of grain nucleation are thus supported. When solidification is arranged in a static mold the columnar- to-equiaxed transition occurs by one of these nucleation paths, subject to the natural decay of temperature gradients which promotes nucleation or the survival of nuclei. But when solidification is forced under special fluid flows it may display odd transitions. In one of these the equiaxed zone is synihesized from. dendrite bits detached from the solid/liquid interface. These survive under the concurrent lowering of temperature gradients and eventually cause transition by impeding columnar growth. GRAIN structure control is desired because real experience shows that specific properties are associated with specific cast grain structures. But since control is thus a matter of need and does not require understanding, much of casting remains art. For example, the manipulation of relative fluid motions in simple ingots provides a control of grain structure development,1-4 but theoretical insight is not required in order to broaden its potential applicability. Fortunately, however, once a variable like fluid flow is recognized it can also provide paths toward new insight. New observations using this variable have provided an insight which is curious. All the theories or descriptions of the columnar-to-equiaxed transition (CET) seem to be supported as long as the appropriate experiment is carried out. In order to develop this idea, let us ignore segregation, the chill zone (until a later section of this paper), and the origin and development of the columnar zone.= The details of questioning how equiaxed material forms in a casting may be divided in two. The first part is simply a questioning of the origin for equi-axed grains: are there fresh nuclei from heterogeneous nucleation, or dendrite bits broken off or melted from the columnar zone or elsewhere,6 or other solid bits surviving from the outset of freezing? The second is more complex, a questioning of the CET: does columnar growth slow down and allow the dominance of equiaxed grains, however they are formed, or do equi-axed grains take over and force columnar growth to stop? This "chicken-or-the-egg" second question can be quite useful, especially because it allows us to delineate the ordinary or NATURAL EQUIAXED ZONE and the induced or SYNTHETIC EQUIAXED ZONE. A natural equiaxed zone occurs if solidification proceeds in the absence of disturbances or extraneous forces such as ultrasonics, stirrings, and so forth. Both the CET theory proposed by Winegard and Chal-mers, 7requiring constitutional supercooling, and the CET theory suggested by Chalmers,8 requiring nuclea-tion only on pouring, pertain to the natural equiaxed zone. The best collating evidence to date for both these theories is contained in the work by Biloni and Chal-mers;9,10 the former theory7 is supported by special versions of the unidirectional growth experiment performed by Plaskett and winegardl1 and the latter theory&apos; is supported in detail for the solidification of small ingots. An equiaxed zone can be synthesized when disturbances caused by forced fluid flows2-4 or other artificial means9,10 break off or melt off dendrite tips from an advancing solid/liquid interface,* if (and only if) temperature gradients in the melt are (forcibly) reduced enough to ensure the survival of these bits of dendrites, 2&apos;3 Willful disturbances even so trivial as those produced by rapping a mold might be included here; as will be shown for example, this follows Southin&apos;s suggestion that the free liquid/air interface

Jan 1, 1970

By M. Earl Volin, M. Adnan Goksel

The hydro thermal agglomerating process described (U.S. Pat. No. 3,235,371, 1966)* is different from the cotzventional high-temperature processes. Green pellets or briquettes made with mixtures of moist iron-ore concen- trates and burned or hydrated lime fines are hardened in an azttoclave at 198°C and under steam pressure for 112 to 5 hr, with or without previous drying. Under the neutral conditiotzs, oxidation of magnetite does not occur as in the conventional processes. The resulting azzlomerates-- are hard and resistant to abrasion and weathering, and they do not disintegrate in the Under test. The equipment required for the process is not complicated, and favorable operating costs are projected because of the low temperamre and efficient heat recuperation. A low capital investment makes the process attractive even when the annual pellet production is below a million tons.

Jan 1, 1970

By P. E. Baker

An experimental study of heat flow in steam flooding was carried out with steam displacing water in a plane-radial fluid-flow model. Temperature distributions in the model reservoir, overburden, and substratum were measured at frequent intervals during flooding by means of a fixed array of thermocouples. Heat losses to overburden and substratum and the division of heat between the steam and hot-water zones in the reservoir were calculated from the temperature data by performing numerical integrations over the appropriate volumes. Temperature profiles and heat distribution results are presented. Some results were (1) the fraction of injected heat that is lost to overburden and substratum, when expressed as a function of time, did not depend on injection rate; (2) a significant portion of the injected heat was contained in the hot-water zone ahead of and underlying the steam front in the reservoir. The division of heat between the steam and hot-water zones did depend on injection rate; and (3) considerable gravity override was observed. The experimental results are compared with those of several published theoretical studies of heat transfer in hot-fluid injection; approximate agreement on heat losses is found with some of the most idealized theories. A valid comparison cannot be made in regard to steam us hot-water zone; basic interpretation of the hot-water zone, in terms of a vertical steam front, is clouded by gravity override in the experiments. INTRODUCTION The experimental study reported here primarily concerns two problems of heat transfer in steam flooding that have economic and engineering importance. These are (1) the fraction of injected heat lost to the overburden and substratum, and (2) the division of the remaining heat between a zone containing steam and a zone of hot water at lower-than-boiling temperature. The volume of the steamed region, which has a direct effect on oil recovery, can be calculated readily from these results. Several valuable theoretical studies have been published on this problem, but no experimental tests of the theories have previously appeared. Tests were needed because the effects of the necessary simplifications in the theories could not be determined otherwise. The basic, untested theoretical problem is the effect of "decoupling" heat and mass transfer, and the resulting inability to include the effects of heat transfer and condensation on fluid flow. The theoretical problem solved so far has been a heat transfer problem in which fluid is present as a heat carrier and flows in a stipulated manner, either linear or plane-radial. The simplifications that have sometimes been made in regard to thermal conductivity by, for example, Marx and Langenheim,l Lauwerier2 and Thomas3 apparently do not have an important effect on heat loss calculations, although the results of the different methods disagree to a certain extent, as shown by Spillette4 and by Ramey.5 A recent paper by the author6 compared the results of experiments in hot-water flooding with several theoretical results and showed a rather poor agreement. It will be seen that the experimental heat loss results for steam flooding, however, show acceptable agreement. These comparisons are discussed in a later section. EXPERIMENTAL APPARATUS AND PROCEDURE The system studied was one in which a sand pack, initially water saturated and at a uniform temperature, was flooded with steam at a constant rate and temperature. The temperature distribution in the "reservoir" and adjacent "strata" was measured with an array of thermocouples, and heat losses were determined from these measurements. The sand pack contained no oil because the only concern of the experiments was heat flow, and it was important to have the flow pattern as simple

Jan 1, 1970

By Larman J. Heath

Wellbore enlargement was tested using hydrazine hydrate in a gas-storage well in Ohio to increase the well productivity. The wellbore was to be enlarged by chemical disaggregation of the sandstone adjacent to the wellbore. Productivity immediately declined 49.1 percent and gradually declined to zero in 7 months. A down-hole camera survey showed a white-to-gray precipitate covering the entire wellbore surface. The precipitate was chemically analyzed and identified as mostly carbazic acid, a hydrazine derivative of carbonic acid. Formation of this precipitate was not anticipated; this viscous sub-stance caused the gradual loss in productivity of the well. The wellbore was not enlarged. Laboratory tests were run to determine what clay stabilization measures could be taken in sandstone cores to prevent clay swelling and particle migration caused by hydrazine hydrate. Normal clay stabilization methods did not prevent the virtually complete loss in permeability to hydrazine hydrate. Other laboratory tests using natural gas diluted with small amounts of carbon dioxide confirmed the ease with which carbazic acid could be formed in a hydrazine hydrate-saturated environment within and adjacent to the wellbore.

Jan 1, 1970

By Geoffrey Purcell

Although the extractive metallurgist has not yet tackled the problem of getting blood out of a stone, he must, when faced with the mini- metal values of today&apos;s ores, believe that this ultimate miracle will soon be expected of him. Even assuming that some plausible professor at one of the few remaining minerals industry schools could persuade the National Science Foundation to sponsor such a sanguine research project, the funds might have to go begging for want of a graduate metallurgist. Falling enrollment in fields devoted to nonrenewable mineral resources, long a matter of grave concern to educators, is now recognized as a problem of great national consequence urgently needing a solution. While the law of supply and demand might eventually be expected to right the imbalance of engineers, time is not on our side and action to correct the shortage is required now.

Jan 1, 1970

By Paul H. Johnson

Heap leaching is a simple means of recovering copper from oxide and oxide-sulfide ores. Although this method requires relatively low capital investment, it suffers from low copper recoveries and relatively high acid consumption. The objectives of this study were (1) to determine what factors influence these shortcomings, and (2) to establish a basis of correlation. between laboratory and field testing. The principal methods of leaching copper ores at the present time are heap, dump, in-place, and vat. A number of references are presented in the bibliography on the theoretical and practical aspects of these methods. In the heap-leaching method, crushed or uncrushed oxidized copper ore is placed on a prepared drainage pad. Acid leach solutions are dis¬tributed over the top of the heap, caused to percolate downward through the ore bed by gravity, and are drained from its base. The leach duration is generally a matter of a few months. Dump leaching is used to recover copper from very low-grade oxide-sulfide pit-waste materials. Here again, leach solutions are, percolated downward through a heap. However, in this method, little or no acid is added to the leach liquors, prepared drainage pads are not used and the leaching cycle is generally measured in terms of several years. Leaching agents are usually autogenously generated by the breakdown of sulfide minerals within the dump.

Jan 1, 1970

By Allison L. Hornbaker

Millions of years ago, in late Cretaceous time before man existed on Earth, tremendous orogenic forces began to change the face of the western part of the North American Continent. Catastrophic events marked by huge uplifts of thousands of square miles in the Cordilleran Belt, some of which are barely discernible in the geologic record, were accompanied by long periods of batholithic intrusions and volcanic eruptions. These events produced the great Rocky Mountain systems, which were at the time even higher and more rugged than they are today. Such activity continued into Tertiary time, and during the Pliocene and Pleistocene periods millions of tons of volcanic ash were hurled skyward by explosive volcanic activity and carried by the westerly winds to the east where it settled out of the atmosphere and deposited over thousands of square miles of the high plains. Unusually heavy rains, probably caused in part by the volcanic activity itself, together with high winds, reworked and redeposited the freshly fallen ash into lakes and depressions of varying sizes and shapes. Subsequent deposits of sand, gravel and loess covered the deposits of volcanic ash, preserving them in the condition in which they are found today. In many places erosion has cut through the sand, gravel, loess, and volcanic ash so that in favorable localities on hillsides and gullies, exposures of volcanic ash can be seen interbedded with sand and gravel.

Jan 1, 1970

By John A. Sievert

Sedimentary deposits contain an appreciable portion of the world&apos;s supply of uranium. Predictions of nuclear fuel usage in the United States indicate that these reserves will have to be tapped if the domestic industry is to be the major supplier of fuels for the nuclear reactors. Techniques developed within the petroleum industry are a base on which to build economically attractive fluid mining processes for the recovery of these uranium values. The problems central to the success of such mining processes are the containment, control, and recovery of a narrow band of pregnant leach solution as it progresses from the point of injection to the point of production Given sufficient incentive, suitable solutions to these problems can be found

Jan 1, 1970

By Lawson F

A rotating disc geometry has been used to provide a uniformly accessible surface for a kinetic study of the cementation of the metals cadmium, lead and silver from dilute aqueous solutions. This work is an extension of studies carried out on the Cu/Zn and Cu/Fe systems for which the rection rate was found to be completely solution-phase mass-transfer controlled. When the amount of material deposited was greater than 0.2 to 0.4 mg/cm2 there was an apparent enhancement in e which is attributed to the formation of a roughened deposit. This same phenomeon was obseived in the Cu/Zn Cu/Fe systems. Again, the rate of reaction of each system investigated was found to be solution-phase mass ,..~sfer controlled.

Jan 1, 1970

By J. B. Wagner, p. Hembree

The iron tracer diffusion coefficient of umstite has been measured at 110(fC across the phase field and at a single composition at 800°C. Assuming a simple cation vacancy model the tracer diffusion coefficient was found to be a linear function of the cation vacancy concentration at 1100°C. The equation is D = 3 x 20 29 where denotes the concentration of vacancies in numbers per cc. The tracer work at 800°C was carried out to investigate the reported "pinning" of tracer to the wustite surface at low temperatures. No evidence for the "pinning" of the tracer was found at 800°C in COz-CO gas mixtures. HIMMEL, Mehl, and Birchenall,&apos; Carter and Richardson,2 and Desmarescaux and La combe3 have measured the diffusion of iron tracer in wustite at several temperatures and compositions. The present work was undertaken to extend the measurements over a large composition range at 1100°C and to resolve certain apparent discrepancies in the data, expecially at lower temperatures. EXPERIMENTAL Wustite was prepared by oxidizing rectangular iron plates* in C02-CO mixtures. The samples were •The iron was supplied by the Battelle Memorial Institute courtesy of the American Iron and Steel Institute. The analysis is presented in Table I. quenched. Due to the inward flow of cation vacancies during oxidation, the center of the sample contained a thin void. The edges of the wustite slab were sanded until the sample could be split into two parts. Each part was then sanded on the front and back flat area until a smooth surface was obtained. The specimens were then replaced in the furnace and equilibrated at llOO°C in a predetermined COa-CO mixture by methods described elsewhere.4"6 The specimens were again quenched and the surfaces were lightly sanded to remove any roughness following the first equilibration. The specimens were then reequi lib rated in the same C02-CO mixture for thirty minutes in order to relieve any mechanical damage on the surface due to the polishing. The specimens were then quenched and the tracer was applied by an electroplating technique. The work of Carter and ~ichardson&apos; demonstrated that there was no systematic difference in the iron tracer diffusion coefficient in wustite if the tracer was plated, dried, or evaporated on the specimen. In the present study a piece of filter paper was saturated with an iron chloride solution of pH <* 3 that contained the tracer FeS5. The wustite was placed on the filter paper and made the cathode. A current density of 0.4 to 0.6 ma per sq cm was passed for about five to ten minutes. The thickness of the tracer layer was estimated to be about 7 x lom6 cm. This estimate was made by considering the area plated, the current flow, and time for plating and the activity of the iron in the plating solution. Different areas of the specimen were counted using a collimator to determine the uniformity of the tracer. Any specimen which exhibited a variation from the initial count rate (about 1500 cpm) by more than 15 pct was rejected. An estimate of the time necessary to convert the thin layer of iron tracer to wustite was made using the data of Pettit and wagner." he estimated time was 1 sec at 1100°C assuming linear oxidation kinetics. The shortest diffusion anneals were 1800 sec. The samples were suspended in the hot zone of a furnace by two platinum wires. Two separate specimens were run at the same time. Only the edges of each sample were in contact with the wires. The C02-CO gas of the same composition as that used in the pre-diffusion anneals flowed freely around the samples at a linear velocity of 0.9 cm per sec. To initiate a run, the specimens were lowered from the cold zone of a furnace to the hot zone by a magnetic lowering device." bout 60 sec were required for lowering. To terminate a run, the sample was withdrawn from the hot zone to the cold zone. Time zero for the beginning of the experiment was taken when the sample blended into the red glow of the furnace and conversely for the end of the experiment. The surface decrease method of measuring the tracer diffusion coefficient was used to collect the data. This method requires that counting geometry be reproducible because the specimen is counted before the diffusion anneal and after the anneal. A special jig was constructed for each specimen so the specimen could be removed from the jig and returned to the jig such that the well geometry was reproducible.

Jan 1, 1970

By R. B. Fermor

"The tyndalloscope is used in Europe for dust-hazard assessments in both coal and metal mines. Dust-hazard conditions can be directly evaluated by the tyndalloscope in many underground working situations, once the basic standard table or tables have been prepared from representative mine-rock samples.The tyndalloscope is excellent, in many cases, for diagnostic dust sampling during a working shift, because individual readings can be taken to within three-minute intervals. The limitations of the tyndalloscope are also discussed.The author suggests that a combination of both the tyndalloscope and gravimetric sampling methods would be an ideal match for most mine dust-hazard assessments."

Jan 1, 1970

By T. T. Gronfors

The excavation process and equipment used for excavation join firmly each other. By changing the process or method, the construction of equipment may be altered essentially. It has been possible to develop a wholy new type of hydraulic boom for tunnelling, when only parallel drilling instead of V-cut is used. The utilization of controlled blasting has made small holes more desirable. So the controlled blasting has had an influence on the selection of drill steel equipment and in this way also influenced the construction of the equipment.

Jan 1, 1970