By S. Y. Ezz, K. El•Guindi

A vertical tube, 8 m long and 2.5 cm in diameter, electrically heated to 650°C throughout the majority of its height, was used to study the-effect of ore feed rate and hydrogen flow rate on the reduction of fine iron ore particles. A correlation could be obtained between the combined effect of the amount of reducing gas and reduction time and the per-cent reduction. The results suggest that a method based on the reduction of fine iron ores while falling through up-streaming hydrogen cannot be recommended for industrial application.

Jan 1, 1969

By D. McLean

For many pu@oses uniform strength is desired over a long temperature range, coupled to a band of softness at the hot end for easy shaping. Various types of material fulfill such a requirement to different degrees, depending on the regularity of their atomic structure. In long-chain polymers and vitreous glasses the irregular structure leads to a steep temperature dependence of deformation resistance and the temperature band between the hard and brittle condition and the soft condition is only about 100 C. In crystals and especially metals the atomically regular structure leads to a much smaller sensitivity over a wide temperature band, thus approaching the ideal behavim. The reason for this insensitivity is that the regular crystalline structure deforms by the movement of dislocations and the elastic interactions of dislocations in- PLASTICS, GLASSES, AND CRYSTALS The ease or otherwise of deformation varies with temperature much more in some substances than in others. This is an important matter when service over a wide temperature range is needed, especially volve energies of several hundred electron volts compared with which the energy of thermal agitation is insignificant. However, temperature affects a metal's defmmation resistance through its influence on the annealing, m coarsening, of the three-dimensional dislocation network. This coarsening is a phenomenon very similar to grain growth and ideas about grain growth can be applied to it. Taking into account also the temperature dependence of the glide resistance from alloying additions, a reasonable account can be given of the overall effect of temperature on deformation strength and of stress and grain size on deformation rake. Special structures me described. some arising from these ideas and as yet untried, which may benefit metals and polymers but not ni-treous glasses. when in addition a degree of softness suitable for shaping is required at some stage. It would be nice if one could write on this subject in as much detail about plastics, glasses, and so forth, as about metals, but there has been far more study of this matter in metals than in other substances, which is one reason why most of this paper concerns metals. However, in Fig. 1 there are shown the deformation strengths of several nonmetallic substances as a function of temperature. In many tests the attempt at deformation caused breakage and the graph lines are then drawn dashed. Long-chain plastics, a glass, and a crystalline substance are included in Fig. 1. The notable feature of all of them is the sensitivity of the

Jan 1, 1969

By H. M. Manasevit, R. L. Nolder, L. A. Moudy

The observation that silicon-on-sapphire crystallo-graphic relationships exist which are unrelated to one another implies that there are regions of sapphire orientations containing these relationships which are separated by boundaries. The presence of these boundaries is demonstrated, initially on rounded cylindrical surfaces md more definitively on flat sapphire substrates with orientations along primary crystallograPhic zones. By means of reflection electron and X-ray diffraction techniques the crystallographic relationships have been studied. Two new relationships have been found, viz., (111) Si (1014) sapphire and (001)Si (1012) sapphire. Also found were multicrystalline relationships. The approximated boundaries between the crystallographic regions for each relationship are shown by means of a stereo-graphic projection. These studies also clarify discrepancies in the literature concerning the silicon-sapphire relationships on the (1120) sapphire substrate. SINCE the first report of the deposition of single-crystal silicon on sapphire in 1963' this epitaxial system has been the object of study by many semiconductor laboratories. In particular, there has been strong interest in the crystallographic relationships between the two materials. In 19652,3 we demonstrated that at least four distinct modes of orientation relationships can occur, namely, (100)Si (0112) sapphire, (111)Si 11 (1124) sapphire, (111)Si (1120) sapphire, and (111)Si (0001) sapphire. Each relationship could be obtained when the substrate plane was at the particular orientation indicated. Other workers as well as our laboratory concurred in general with the initial results. However, two discrepancies were observed. First it was observed by Joyce et a1.4 that on a (1120) substrate a (110) silicon deposit could be obtained. This was actually consistent with the (111)Si (1124) sapphire mode. Second, two other laboratories,5,6 as well as our own,7 have found a deposition on the basal plane which is different than our initial findings. Even though a (111)Si deposit was obtained, the crystallographic relationships were not identical to those previously found. Subsequent work in our laboratories has confirmed that the form found in these later investigations of the basal plane is by far the more predominant, and the original finding was an anomaly. The relationships which have been previously estab1.ished are summarized in Table I. It is seen that at present a rather small number of possible substrate orientations has been investigated. Therefore, it seemed appropriate that a systematic investigation of silicon epitaxy on various sapphire substrate orientations would be of value. It was expected that the answers to three questions could be obtained from such an investigation. These are as follows: 1) Since we know of at least four distinct modes of orientation relationships, over what range of substrate orientation do these modes occur and what is the form of the boundary expected between the different regions in which each mode occurs? 2) Are there other modes which occur on substrate orientations not previously investigated? 3) What is the explanation for the discrepancy between our laboratory's findings and those results reported by Joyce et al.4 concerning the relationships occurring on (1120) substrates? APPROACHES AND EXPERIMENTAL METHODS Two different approaches were used. Initially, depositions were carried out on rounded cylindrical surfaces which lay perpendicular to the (0112) plane.* By this means the presence of boundaries and their approximate positions could be determined. Finally and more definitively, depositions on flat sapphire substrates with a variety of orientations, mostly along primary crystallographic zones and about the (1120) plane, were studied by means of reflection electron diffraction and X-ray diffraction (using back-reflection Laue patterns and full circle goniometer techniques) in order to determine crystallographic relationships. The sapphire orientations investigated by these means

Jan 1, 1969

By R. R. Beebe

Marcona Corporation produces about 3.5 million long tons of iron ore pellets annually on its two travelling grate pelletizing machines at San Nicolas, Peru. During 1969, these pellets will be shipped to customers in four marketing areas--Japan, the United States, Europe, and South America. All of these sales are on the open market, and product quality is a major concern. Typical chemical, structural, and quality test results for Marcona pellets are given in Table 1. [ ]

Jan 1, 1969

By H. E. Cook

The Ising model for the internal energy of a binary alloy has been used to obtain a general equation for the critical resolved shear stress of partially ordered crystals. The equation expresses the stress in terms of the Warren "alphas " and can be used to estimate the variation in strength with order without the assumption, present in the original formulation of this problem in terms of domain size, that order is complete within each domain and that the domains are of ungorm size and shape. In addition, it is the general equation, according to the Ising model, for strengthening by short-range order. Two applications of the equation are considered: One is an estimate of the variation in strength of CkAu with long-range order. The other is an estimate of the variation in strength of FeCo with quench temperature. Reasonable agreement is found with the variations reported in the literature. When the internal energy of an alloy crystal depends upon the distribution of solute, the strength of the crystal will also depend upon it because a portion of the applied stress for plastic deformation will be: where V is the volume of the crystal and E(E) is the energy change associated with the solute redistribution caused by the plastic strain, E. We expect T to equal zero for a crystal having a random arrangement of solute because the arrangement would remain random after plastic deformation. Likewise, we expect it to equal zero when the crystal is perfectly ordered because the motion of paired dislocations found in such crystals does not disrupt order. However, when short-range order exists or when long-range order is incomplete, plastic deformation will decrease the amount of order and additional work, proportional to the ordering energy, will be expended. Fisher' estimated T for crystals having short-range order by assuming an interaction energy between neighboring atoms and estimating the change in the number of unlike neighbors as a dislocation moved through the crystal. (His analysis was limited and several workers2"6 have since given more complete ones.) Fisher minimized the importance of a strengthening mechanism of this type for paired dislocations in a structure having long-range order. ~ottrell,' however, pointed out that T could be appreciable for ordered crystals having antiphase domains. He attributed the strengthening to the increase in surface energy of the domains as they were cut by paired dislocations. Ardley,' in his test of Cottrell's theory, found that r for Cu3Au crystals obeyed the equation: for 1 > t where 1 is the domain size, t is the domain wall thickness, and y is the surface energy of an antiphase boundary. His experiments represent the classic confirmation of the strengthening mechanism proposed by Cottrell. However, the assumptions involved in using Cottrell's theory are valid only for large domain size in CU~AU,~"~ i.e., when Eq. [2] reduces to: For small domains, ~linn~ has questioned Ardley's assumption that order was complete, and, indeed, Stoloff and ~avies" fpnd it incomplete until a size of approximately lOOA was reached. Even when the order within a domain is complete, it is not obvious how one determines the appropriate value for I in a structure where domains vary in size and are irregularly shaped. The purpose of this paper is to estimate T without restrictions upon the degree of order and domain shape. Our major assumption will be the use of a generalization of the model proposed by Bethe" (the Ising model) for the internal energy. This will in fact allow us to combine the theories for strengthening by short-range order and by antiphase domains into a single, general formalism. We will use the results to estimate the variation in strength of Cu3Au crystals with long-range order8 and the variation in flow stress of FeCo crystals with quench temperature.12'13 INTERNAL ENERGY For simplicity, we restrict our considerations to those binary solid solutions which can be described as an arrangement of atoms on a Bravais lattice. An atom site will be indexed by three numbers (PI, pz, p3) determined by the vector: from the origin fixed at atom (0, 0, 0) to the atom site where a', an, and a, are the lattice translation vectors. We write: For the energy of the crystal where pi(p) is the probability (either zero or one) of finding an atom of type i (i = 1, 2) at site (p), which is shorthand for (pl, pz, p3) and pj(p + r) is that for an atom of type j (j = 1, 2) at the site (p + r), which is shorthand for (pl + rl, The coupling parameter, resents the energy associated with the pair Pi(p), Pj(p + r). The crystal is assumed large enough so that surface effects can be neglected; therefore, trans-lational and inversion symmetry require the coupling parameters to obey the relations

Jan 1, 1969

By Nestor Torres-Acuña, Fathi Habashi

Metallic copper of purity equal to commercial electrolytic copper is deposited during the anodic dissolution of technically available white metal, Cu2S, in m acidic solution of' copper(II) sulfate as electrolyte and copper sheets as cathodes. The process may be applied on commercial scale since it has the advantage of by passing the converting and poling steps, decreasing pollution problems due to SO, and recovering the sulfur of the white metal in the elemental form. The anodic dissolution is believed to take place in three steps: The working conditions that lead to 98 pct cathodic current efficiency are: 30 gpl Cu2+ and 100 gpl H2SO4 in electrolyte, current density 1.0 amp per sq dm, and tetnperature of bath 40°C'. DURING the smelting of copper, nickel, lead, and zinc sulfide ores, large amounts of sulfur dioxide are produced. Because the release of this gas in the atmosphere causes pollution problems, many attempts were made in the past for its recovery either in liquified form or processed to sulfuric acid. Although these two forms of sulfur are the usual forms that are consumed by the chemical and metallurgical industries, their storage and transport usually raise economic problems. It was realized, long ago, that a process by which sulfur can be recovered directly in the elemental form would be most attractive. Elemental sulfur is easily stored and transported, and is readily converted to SO2, H2S, or H2SO4 when needed. Processes aimed to recover the metals from their sulfide ores, and at the same time by-product sulfur in the elemental form, were recently reviewed.' As early as 1882, Marchese2 patented a process in which a matte having the composition: Cu 15, Pb 14, Fe 41, and S 25 pct was electrolyzed. According to cohen3 the process was applied on a pilot scale by the Aktiengesellschaft fur Bergbau-, Blei-, und Zinkhiitten-betriebe at Stolberg, Rheinland, Germany. The process was unsuccessful, however, owing to the contamination of the electrolyte during electrolysis. Studies in this field were reported by Bernfeld4 and Egli.5 Borchers et a1.6-8 developed the process further by using white metal (Cu 78.2 pct, S 19.6 pct) instead of the matte, and a pilot plant was operated by the Mansfeldschen Kupferschiefer Co. at Eisleben, German~.~ It appears, however, that the process never went into commercial operation. Further studies in this direction were carried out by Russian workers.10-23 The International Nickel Co. of Canada erected a pilot plant at Port Colborne in 1951 to apply the process to nickel matte which is essentially pure nickel sulfide."'- 26 Full-scale plant went into operation at the Thompson Refinery in Manitoba in 1964.27 In this method nickel sulfide matte is melted and cast into anodes analyzing 76 pct Ni and 20 pct S with small amounts of copper, cobalt, and iron. These anodes are then electrolyzed in an aqueous solution of NiS04 at pH 4. Further work on this method was reported in the literature.28-31 In this paper, experiments on the anodic dissolution of white metal in aqueous copper sulfate solution are reported. EXPERIMENTAL White metal, Table I, obtained from The Anaconda Co., was cast in form of anodes 10 by 7.5 by 1 cm, Fig. 1. The anodes are mechanically strong and do not break easily; when polished they gave a shiny gray metallic appearance. From the chemical composition shown in Table I, it can be seen that the atomic ratio Cu:S corresponds approximately to the formula CU2.06S. The copper in excess to the formula Cu2S is most probably present as a separate phase since metallic copper could be seen under the microscope, Fig. 2. Fig. 3 shows the X-ray diffraction pattern of white metal which matches fairly well with that of reagent-grade Cu2S.

Jan 1, 1969

By M. Yokoi, K. Yoshida, T. Ishihara

The solubility of aluminum in cryolite melts has been determined by measuring the weight loss of aluminum submerged in melts contained in closed silicon nitride crucibles. The solubility in pure cryolite has also been checked with radioactive isotopes. The solubility decreases with increasing A1203 concentration, decreasing temperature, and decreasing cryolite ratio. The change of aluminum solubility in pure cryolite with the activity controlled by using Al-Ag and A2-Cu alloys supported the assumption that aluminum would dissolve in the form of monovalent ions according to the reaction 2AI + A1' —3 A1'. DURING the electrolytic production of aluminum, the electrodeposited metal redissolves in the bath in some form and is subsequently oxidized back to the former ionic state. This dissolution is believed to cause a decrease in current efficiency. Reported data on the solubility of aluminum in cryolite melts are scattered. The mechanism of the dissolution has not yet been determined, although certain tentative interpretations have been proposed. Many previous studies were performed under different test conditions. Studies were performed in open Systems and closed systems,'o and some were apparently not given sufficient time to Saturate." The solubility can be determined either analytically or gravimetrically. The analytical determination involves measurement of hydrogen gas evolved when frozen cryolite bath saturated with aluminum is treated with sodium hydroxide or hydrochloric acid. The gravimetric determination, adopted by many investigators,'-37'3>14 involves measurement of weight loss of the metal after equilibration with a known amount of salt. It appears that the former technique yields much smaller values of solubility than the latter technique. This large difference in results strongly suggests that the dissolved metal in the cryolite melt is no longer in the metallic state. In the present study, the solubility was determined by the gravimetric technique at various activities of aluminum using A1-Ag and Al-Cu alloys. An attempt was also made to determine the ionic (or atomic) state of the dissolved metal from the solubility data. 1) EXPERIMENTAL Apparatus. Preliminary tests demonstrated that silicon nitride was suitable as a container material since it is compatible to both the fluoride melts and molten aluminum. Crucibles were made from silicon powder nitrided with Nz gas at 1600°C. The good compatibility between crucible and melts is due to the near perfect nitrogenation of silicon. Only small amounts of silicon were found in the aluminum metal after the experiments. The crucible dimensions were 90 mm inside height, 38 mm ID, 105 mm outside height, and 50 mm OD. Close-fitting lids made of silicon nitride were also prepared. The crucible was placed in a close-fitting graphite crucible heated by a vertical Kanthal furnace, Fig. l. The lid and crucible are fastened tightly together by the condensation of vaporized bath in the narrow gap between them. The temperature was measured in the wall of the graphite crucible and controlled within * 5°C. The temperature difference between the measuring point and the interior of the melts was initially determined. Materials. The materials used were: Greenland cryolite (impurities CaF,, 0.5 pct; AlzO3, 0.2 pct; high-purity aluminum metal (purity 99.99 pct); A1203 and AlF, (provided by Nippon Light Metal Co., Ltd); reagent-grade NaF and CaF2; and 99.9+ pct Ag and Cu. Powdered reagents were carefully dried before use. A1-Ag and A1-Cu alloys were prepared before the experiments; their composition was checked by analysis

Jan 1, 1969

By P. Marier, T. R. lngraham

The kinetics of the sulfation of MnO,, MnzO3, and Mn3O4 in SO,, SO3, and O, mixtures was examined and the descending order of sulfation rates at temperatures near 400°C was found to be Mn,O3 > MnO, > Mn3O4. The respective activation energies for the thermal decomposition of MnO, and Mn,O, are 39 and 47 kcal. At 900°C, the thernzal decomposition of MnSO, to MnzO3 is slower than that to Mn3O4. The respective activation energies are 62 and 51 kcal, respectitely. MANGANESE is used to improve the hot workability of steel in the proportions of approximately 13.5 Ib of ferromanganese per ton of steel produced. This requirement accounts for about 95 pct of its large industrial market in North America. The remaining 5 pct is used in the battery and chemical industries. In most North American ores, the percentage of manganese and the manganese-to-iron ratio are not suitable for the direct production of ferromanganese. Hence, most of the North American requirements for manganese are satisfied by importing ore. Typically, many of the studies done on native low-grade manganese resources have been directed toward the production of ore substittes" and the recovery of manganese from open-hearth slags.3 Of the wide variety of processes which have been proposed, the most popular involve compounds in the Mn-S-O system. The thermodynamic properties of manganese and its compounds were reviewed by ah' in 1960 and, more recently, lngrahams discussed the thermodynamics of some of the reactions involved in the Mn-S-O system at normal roasting temperatures. The conditions for producing manganese sulfide during the reduction roasting of manganese sulfate are discussed by Fuller and Edlund.9 A novel scheme was proposed recently by zimmerley7 for utilizing waste sulfur dioxide from stack gases to recover the manganese from ocean-mined manganese nodules. Very little of the work published on manganese compounds has been related to reaction rates. Singleton et 1.' studied the rates of reaction on the MnO-C and Mn7C3-3MnO systems and observed linear and parabolic kinetics respectively in the systems. Tatievskaya et a1.' studied the low-temperature reduction of Mn&, MnO,, and Mn& in HZ and CO, and reported activation energies in the range 1628 kcal. In this paper, the rates of some of the decomposition and formation reactions involving MnSO4, MnOz, MnzO3, and Mn3O4 will be examined after the conditions for the thermodynamic stability of the individual compounds have been designated. CONDITIONS FOR STABILITY OF MnSO4, MnOz, MnZO3, AND Mn3O4 The areas of stability for h'hSO4, MnOz, MnzO3, and h3O4 were established from the data of Mah4 and Ingrahams and are shown in the predominance area diagram,10 logpq- logpsq, in Fig. 1. The diagram is drawn for two temperatures, 700°K, solid lines, and 1100°K, dotted lines. The sketch for the lower temperature includes the conditions likely to prevail in the Zimmerley patent7 when manganese nodules react with sulfur dioxide and that for the higher temperature indicates the conditions for recovering MnzO3 or Mn3O4 from MnSO4 during a roasting reaction. From the fact that the boundary between the areas of stability of MnOz and hSO4 at 700°K is parallel to the abscissa, it is evident that MnOz and SO2 should react together to produce MnSO4, irrespective of the oxygen pressure in the system. If the source of sulfur for sulfation were from waste flue gases, it is likely that the oxygen content of the gas stream would be more than sufficient to oxidize any MnsO4 to MnzO3, 107 atm of O2 required, or even to convert any Mnz03 to MnOz, 0.02 atm OZ required, prior to sulfation. At 1100°K, the diagram indicates that MnSO4 may be converted directly to either MnzO3 of Mn3O4, depending upon the prevailing partial pressure of oxygen. When the gas stream contains more than 1 pct Oz, logpq = -2, only MnzO3 would be recovered from an experiment done under equilibrium conditions. At oxygen partial pressures of less than 1 pct, one would expect to bring about a reversible exchange between MnSO4 and Mn3O4 by appropriate adjustment of the partial pressure of SOZ. These various reactions will be described in the subsequent kinetic experiments.

Jan 1, 1969

By T. E. Hill

The Bureau of Mines investigated the possibility of physically separating Missouri and Minnesota granites into commercially usable fractions of feldspar, quartz, and mica by mineral dressing techniques. The probability of r covering a feldspar fraction from raw granite suitable for commercial uses was developed through correlation of the iron oxide content by extensive petrographic studies. This probability evaluation also included Wisconsin granites and a high-feldspar iron ore concentration tailing from Missouri. Laboratory recoveries of feldspar and quartz were on the order of 80 percent. Mineral content of each fraction was generally over 95 percent, indicating excellent response to separatory techniques, Acid leaching of feldspar and quartz concentrates to remove iron oxide improved the grades chemically; however, occluded iron oxide particles in the leached products prevented attaining top grades of feldspar. Mica was removed as scrap grade at low recoveries. Each concentrate conformed to some category of commercial feldspar, quartz, or mica.

Jan 1, 1969

By J. F. Smith, J. E. Davison

A value for the enthalpy of formation of z2 of -3.14 i 0.21 kcal per g-atom has been measured by the technique of acid solution calorimetry. This result is in quite good agreement with two earlier determinations by tin solution calorimetry and by direct reaction caloriinetry, and averaging of values determined from the three independent calorimetric techniques gives enhanced precision and accuracy with AHh8 (CaMgZ) = - 3.15 i 0.05 kcal per g-atom. For comparison with experimental data, values for the enthalpies of formation of CaMgz, SrMgz, and BaMgz of -9.8, -7.9, and -2.8 kcal per g-atom were estimated from a calculation based on the LVigizer-Seitz approximation as modified by Raimes for polyvalent elements. While complete quantitative accord between these calculated talues and available experimental data is lacking, nonetheless numerical accord is better than might be expected and, more importantly, parallel numerical trends are observed between experimental and calculated vnlues. WITHIN the past decade the enthalpy of formation of CaMg, has been determined a) from measurement of magnesium vapor pressures over binary Ca-Mg alloys,' b) by solution calorimetry with liquid tin as the solvent,' c) from measurement of hydrogen vapor pressures over ternary alloys of calcium, magnesium, and hydrogen,3 and d) by direct reaction alorimetr. The value from tin solution calorimetry is the most precise and is probably the most reliable, and this value is within the quoted uncertainties of the other three experimental results. The overall agreement among the four independent investigations is quite good, particularly so when the diversity of techniques is noted. On the basis of this agreement, CaMgz was chosen as a test material to evaluate the operation of a newly constructed apparatus for the determination of enthalpies of formation of intermetallic phases by acid solution calorimetry. This was believed to be a severe test because of the high chemical reactivity of both calcium and magnesium which reactivity presumably accounts for the fact that an early determination5 of the enthalpies of formation of Ca-Mg alloys by acid solution calorimetry yielded values significantly more negative than the four recent determinations. EXPERIMENTAL APPARATUS AND MATERIALS Experimental Apparatus. The enthalpy of formation of CaMg, was determined by measuring the difference between the heat evolved when dissolving the metallic compound and the heat evolved when dissolving equivalent amounts of unreacted metallic elements in hydro- chloric acid. This was done differentially with an apparatus consisting of twin calorimeters which were constructed to be as nearly identical as possible. The advantage of differential calorimetry is that systematic errors arising from the individual calorimeter design tend to cancel. A schematic representation of the apparatus is shown in Fig. 1. A dead air space around both calorimeters was provided by a large, thermally insulated jacket. Each calorimeter consisted of a 2-liter Dewar flask which was completely enclosed in a copper container. Each Dewar contained 1600 g of 2.5hr HCl to act as the solvent, and thermal effects resulting from solvent evaporation were minimized by covering the acid with 50 g of mineral oil. There was no detectable reaction between the acid and the mineral oil. Equivalent amounts of mechanical energy were added to the calorimeters through twin stirring rods which were driven at the same rpm by a single motor with the intent of the stirring being to maintain thermal equilibrium throughout the solvent. To calibrate the heat capacities of the calorimeters, known amounts of electrical energy could be added by passing measured voltages and currents for known times through submerged heaters, approximately 20 ohms, which were wound noninductively from Manganin wire. A 6-v storage battery was used as a power source, and a dummy heater was used as an exercise circuit to allow the battery to stabilize at a constant electromotive force before energizing one or the other of the calorimetric heaters. A type K-2 potentiometer was used to measure the potential drop across an energized heater while the current was determined from the potential drop across an external standard resistor. Times of energization were measured with an electric timer, and the electrical energy supplied to a heater

Jan 1, 1969

By Fred Perea

The practical example of the effectiveness and necessity of establishing and maintaining close communications between the design engineering section and operating section of a large plant concerned with the building of an underground crusher will be presented.

Jan 1, 1969

By A. Roy MacLean

This paper outlines the changes in modern-day coal mining that have been brought about by the increased cost of labour and the use of new and highly efficient equipment. In the latter category are mentioned the ramp-plate, the Bretby cable carrier, armoured face conveyors and the shearer-loader. Greater productivity and increased safety are emphasized.

Jan 1, 1969

By B. Wilshire, W. J. Evans

W. J. Evans and 8. Wilshire SEVERAL recent investigations1-6 have shown that the strain, c, during transient and steady-state creep is well-represented by the expression: € = e0 + et(l - e-mt) + Esl [l] where Eo is the instantaneous strain on loading, ET the total transient strain, C, the steady creep rate! and m a constant relating to the rate of exhaustion of transient creep. However, it has been noted6 that deviations from this equation occur over the first 10 to 15 pct of the transient stage, when the creep rate, (. decreases more rapidly than is predicted by this equation. This rapid decrease has been attributed to a large change in work-hardening coefficient. It 1s widely accepted that steady-state creep results from a balance between the rate of strain hardcning h and the rate of recovery r (=-s(st) as: dE/dt = Es = r/h [2] Comparison of values obtained for h at the end of the initial extension and during steady creep suggests that h increases several fold during the transient stage. which has the effect of reducing the creep rate proportionally.7 To examine the dependence, on r and h, of the deformation behavior during transient and steady-state creep. a series of constant-stress creep tests was carried out at 413°C at 6000 psi using 70-30 a brass. Prelinlinary investigation showed that. with this material. the transient stage constituted a significant portion of the total creep life (-0.4tf. where tf is the time to fracture). The alloy. obtained from Metals Research Limited. was made from high-purity copper, 99.999 pct. and zinc. 99.99 pct. Heat treatment at 675°C for 4 1/2 gave a uniform grain size of 5 mm-1. Details of specimen preparation and creep testing procedures have been given previously.6 Values of h (?s/?E) were determined by measuring the instantaneous strain. ?E. which occurred on increasing the stress during creep by a small amount. ?s. Similarly. v (= -?s/ ?t) was derived from the incubation period. At, after a small decrease in stress.' Several values of v and h were obtained throughout duplicate creep tests. using different stress increments in the range 300 to 800 psi. The accuracy with which Eq. [I] represents the present creep curves was established by determining the best value of the constants Es, Et, m , and 6, using a digital computer program based essentially on the graphical solution for this equation devised by Conway and Mullikan.9 About 40 strain/time readings were taken during transient and steady-state creep. Over most of the creep curve, the average difference between the measured reading and the calculated strain at the appropriate time was less than 0.0001. However.

Jan 1, 1969

By Paul H. Johnson

Chemical mining may be defined as the in-place extraction of metal values from ores located within the confines of a mine (that is, broken or fractured ore, stope fill, caved material, or ores in permeable zones) or ores located in dumps, prepared ore heaps, or tailing ponds. The term solution mining has, in general, been used to mean the in-place dissolution of water-soluble mineral salts with leach solutions. Chemical mining is presently in its embryonic stage. Basic research needs to be done to understand the influence of physical and chemical factors in chemical mining, and applied research needs to be done on both a small and a large scale to develop practical techniques of field practice. The areas of research include the following: (1) Leaching chemistry, the influence of physical, chemical, and biological factors in in-place leaching (2) Hydrodynamics of chemical mining systems (3) The development of new, as well as old, leaching agents for use under chemical mining leach conditions (4) The development of new means of contacting fine and coarse materials (with solutions) under static leach conditions (5) The development of new processes for generating and regenerating chemical mining leach solutions (6) The development of metal recovery processes

Jan 1, 1969

By J. D. Hunt, D. T. J. Hurle

A uariety of eutectic structures are formed in faceted/nonfaceted eutectics. The various structures are explained in terms of the absence or presence of small facets in the liquid groove. Regular structures are produced when, for purely geometric reasons facels cannot form. The presence of a facet in the liquid groove leads to the formation of an irregular or a cell-like complex regular structure, due to the relative immobility of the groove. A classification of eutectics was proposed by Hunt and jackson, based on the presence or absence of facets on the primary phases (the absence of facets may be predicted from the dimensionless entropy of melting2). Eutectics were divided into three groups: 1) eutectics in which both phases grow in a nonfaceted manner; 2) eutectics in which one phase grows faceted, the other nonfaceted; 3) eutectics in which both phases grow faceted. It was suggested that regular1 rodlike or lamellar structures1 should be formed in the first group, that irregular or complex regular structures1 should be formed in the' second, and that irregular structures1 should be formed in the third. Recently it has been shown that the structural classification is incomplete. Regular rodlike structures (InSb-NiSb eutectic3), or broken lamellar structure (Bi-Zn eutectic, Fig. 8), are formed in alloys of the second group when the faceted phase has a large volume fraction. Hunt and jackson' argued that regular structures could form in faceted/nonfaceted systems, but that such structures would be unstable in the presence of microfacets on the lamella of the faceting phase, because the growth rate at a point on such a facet would depend on the kinetic undercooling at the point of nu-cleation on the facet, and not on the local kinetic undercooling. In these circumstances it would not be possible to consistently balance the compositional and kinetic undercooling over a lamellar structure and thus obtain a stable isothermal interface. In this paper we discuss in detail the origin of the various structures formed in faceted/nonfaceted systems, pointing out that the most important factor promoting the formation of a regular structure is the absence of a facet in the liquid groove. 1) FACET FORMATION IN SINGLE-PHASE MATERIALS Facets form when there is an energy barrier for the addition of a new solid layer on an existing solid. When a barrier is present,2 growth proceeds by the lateral movement of steps across a crystallographic plane. The rate-controlling stage of the process occurs when the step is first formed. Hulme and Mullin6 have shown that faceting in single-phase materials can only occur when both interface curvatures are convex with respect to the solid and when the surface is tangential to the facet plane. When even one of the curvatures is concave a facet does not form because new layers of solid from adjacent regions can always feed the facet plane, Fig. 1. Growth under these conditions is then as easy as elsewhere. Similar considerations will apply to eutectic growth; consequently the shape of the faceted phase is extremely important. 2) LAMELLAR SPACING CHANGES IN EUTECTICS Jackson and Hunt7 have shown that the interface undercooling AT of a growing lamellar interface (neglecting kinetic undercooling) is related to the lamellar spacing, A, and growth velocity, v, by an expression of the form: where m, Ql, and nL are constants of the system given in Ref. 7. Eq. [I] is plotted for fixed v in Fig. 2. Jackson and Hunt postulate that a regular eutectic grows near, but to the right of the minimum in the AT vs A curve. They argue that the spacing cannot be to the left of the minimum because the interface is then unstable to fluctuations in A. It cannot grow too far to the right, because when the spacing becomes too wide an isothermal interface can no longer be maintained over the large-volume-fraction phase.7 It is argued that during any change in growth rate the lamellar spacing remains in the permitted range by the movement of lamellar faults. When the spacing is too wide, the fault, shown in Fig. 3, moves to the left; when the spacing is too narrow it moves to the right. The faults, however, have to be formed. heir formation has been shown to occur when local regions deviate considerably from the spacing defined by the lamellar When the spacing is locally too narrow (it passes to the left of the minimum, Fig. 2), pinching off of the narrow phase occurs. When the spacing is locally too wide, the interface on the large volume-fraction phase can no longer be maintained as an iso-

Jan 1, 1969

By G. L. F. Powell, L. M. Hogan

Large degrees of undercooling have been produced in bulk samples, 400 g, of copper and Cu-O alloys by melting in a slag of commercial soda-lime glass. The maximum degrees of undercooling obtained for copper, hypoeutectic and hypereutectic Cu-O alloy samples were 208°, 218°, and 97°C, respectively. No grain refinement as a function of undercooling was observed for the pure copper samples although in Cu-O alloys there was a marked decrease in grain size at degrees of undercooling greater than 150°C. The grain size change is the result of recrystallization during or immediately following the freezing process. THE first report of a large degree of undercooling in a bulk sample of metal was that by Bardenheuer and Bleckmann1 who produced 258°C undercooling in a 150-g sample of iron by melting in a glass slag. Garbeck2 extended this technique to nickel, cobalt, and copper and reported maximum undercoolings of 220°, 230°, and 60°C, respectively, while Fehling and schei13 undercooled a large number of metals as 2 to 20-g samples slagged in glass. Subsequently, one of the authors4 applied the glass slag technique to bulk samples, -500 g, of silver and obtained a maximum undercooling of 250°C. It was concluded that impurities which normally catalyze nucleation at small degrees of undercooling could be removed by oxidation and solution in a glass slag. Large undercooling of bulk samples of iron, nickel, cobalt, and their alloys has also been reported by other authors.8'10'11 Of the five metals mentioned above, copper was the only one which had not been undercooled by at least 200°C in the form of a large bulk sample. Since copper exhibits high liquid solubility for oxygen, as do iron, nickel, cobalt, and silver, it was considered that a much larger degree of undercooling than that observed by Garbeck for copper should be possible. This was obtained by modification of the technique applied previously to silver and the results of undercooling experiments with 400-g samples of copper form part of this paper. The undercooling behavior of Cu-O alloys was also studied, and the influence of a small oxygen content on the grain structure of undercooled copper was observed metallographically. 1) EXPERIMENTAL The copper was obtained as oxygen-free high-conductivity copper, the major impurities of which were Fe 0.01 pct, Zn 0.015 pct, and Si 0.02 pct. Melting was carried out in an open-ended vertical cylindrical fur- nace wound with Kanthal wire. A schematic diagram of the experimental setup is shown in Fig. 1. The undercooling technique previously used for silver4 involved preoxidation of the samples by melting the silver in contact with the atmosphere. The oxygen content was subsequently reduced by freezing the samples under a glass slag, whereby the oxygen was evolved as gas and the continuous glass cover over the surface prevented re-solution of oxygen when the sample was remelted. Since oxygen is not released as gas when a Cu-O alloy is frozen. the technique had to be modified for use with copper. Also, copper is oxidized during fire refining so that an in situ preoxidation treatment of the samples was not considered to be a prerequisite to large undercooling. Experimentation proved that this supposition was correct. Instead, it was found that care was necessary during melting of the copper under glass to minimize oxygen pickup. Samples of copper weighing 400 g were prepared by adding 50-g pieces of copper to a vitreous silica crucible partly filled with soda lime glass at a temperature of approximately 1000°C. Each piece was quickly immersed in the glass slag and held at this temperature until the oxide coating on the surface decomposed. This change was easily observed and coincided with the formation of gas bubbles in the glass

Jan 1, 1969

A number of suggestions have been made to improve the design of cells used for electro winning and electro refining of metals. Most of these designs have been aimed at increasing the current density used in order to improve cell capacity, although the purpose of some has been to produce electro deposited metals in a continuous manner. Improvements in the electrolyte flow pattern in conventional cells have resulted in an increase in the rate of mass transport of metal ions to the electrode surface; giving rise to lower concentrat- ion polarization and an improvement in the nature of the product obtained, Other cell designs are based on a moving electrode, usually a rotating disk, and these may include provision for removal of the product in a continuous manner, The maximum current density which can be used in an electro- lytic deposition process is determined by the limiting diffusion current, the physical nature of the, product, the purity of the product required and by the increase in power costs which result from the higher cell voltages, This paper examines the properties of an agitated bed of particles as an electrode system when used for a metal deposition Process,

Jan 1, 1969

By C. T. Holland

Coal mining has been an important industry in the Appalachian area for many years. This is particularly true in the northern part of the area, namely, in Pennsylvania, West Virginia, and Ohio. Also, in the south a great deal of mining activity has been carried on in Alabama, Kentucky, and southwest Virginia. Some of the by-products of this activity has been the production of mineralized water from the mines in copious quantitites. The southern Appalachians have been somewhat more fortunate in that the water there has had a considerable amount of alkalinity in it, which has to a large extent eliminated some of the more undesirable aspects of mine drainage. Northern Appalachia, including central and western Pennsylvania, the Monongahela basin in West Virginia, and the Appalachian area in eastern Ohio have not been so fortunate in that coals in those areas and the top and bottom rock have, in many cases, shown considerable quantities of pyrite, and the water does not carry the carbonates found farther south.

Jan 1, 1969

By J. O. Wheeler

"DEFINITION OF THE REGION, ITS BOUNDARIES, AND PHYSICAL AND GE'OLOGICAL CHARACTERISTICSTHIS PAPER concerns the Western Cordilleran region, embracing most of British Columbia, the southern half of Yukon Territory and the southwestern most part of the District of MacKenzie. It excludes Vancouver Island and the Queen Charlotte Islands, which are discussed in a background paper on the Pacific Continental Shelf. The region is bounded on the south by the northwestern United States, on the west by the continental shelf and Alaska, on the north by the front of the Ogilvie Mountains, on the northeast by the axis of the MacKenzie Mountains and on the east by the Rocky Mountain Trench.The region is dominated by two mountain chains that con tain icefields and glaciers: the St. Elias, Coast and Cascade Mountains in the west; the Selwyn, Pelly, Cassiar, Omineca and Columbia Mountains in the east. The Intermontane region between these mountain chains consists of lower mountains and plateaus. In the mountains, the region above the timberline and many of the steep valley-walls provide good exposures of rock, but these areas are subject to rockslides and landslides and in winter to snow avalanches. Much of the Western Cordillera was covered by ice-sheets at various times during the Pleistocene epoch. Consequently, the larger valleys in the mountains and much of the Intermontane region contain much glacial drift and alluvium and only limited exposures of rock. This same terrain in the Southern Cordillera, however, is the most favourable for agriculture. Parts of the region, particularly in the two mountain chains, are heavily forested. Elsewhere, the forest cover is less, with grassland prevailing in the south and tundra in the north."

Jan 1, 1969

By A. F. Crawley

The density and viscosity of 1iquid thallium have been measured by absolute methods to temperatures of about 200° and 150°C, respectively, above the melting point. These new data reported, especially density data, do not closely confirm previous work. Density p, in g per cu Cm, is shown to vary linearly with temperaluve t, in °C, according to the equation p = 11.658 - 1.439 X l0-3t. The viscosity data obey the well-known Andrade equation nv1/3 = A exp C/vT , the constants A and C for thallium having values of 2.19 x A and 79.648, respectively. This paper reports some new data for the density and viscosity .of liquid thallium. Measurements of these fundamental physical properties were undertaken as part of a continuing research program at the Mines Branch, Department of Energy, Mines and Resources, Ottawa. Canada. A literature search has revealed that data are so scarce that there could not be a consensus on the true values of the density and viscosity of liquid thallium. To be more specific, there exists only one set of viscosity data' and only two acceptable sets of density data,273 one of which is limited in scope.3 In Liquid Metals Handbook,3 another density study is reported but indications of impurities in the thallium render the results suspect. In this situation, further careful experimentation was required to realize the true density and viscosity of thallium. EXPERIMENTAL METHODS Density. Densities were determined using a graphite pycnometer. The technique and its accuracy have been discussed in earlier papers.4'5 It is considered that experimental data can be obtained which are accurate within +0.05 pct, all sources of random and systematic errors having been evaluated. Density results for thallium were identical whether measured under an atmosphere of argon or a vacuum of 5 x 10-6 torr and, for the most part, the argon atmosphere was used. Viscosity. Viscosity measurements were made in an oscillational viscosimeter by an absolute method—the liquid metal being held in a closed graphite cylinder. Design and operation of the apparatus, constructed in this laboratory, have previously been discussed.6 For thallium, runs were made under a vacuum of about 2 x 10-6 torr. To evaluate viscosity coefficients from the various experimental parameters, the mathematical analysis of Roscoe7 was used. Measurements of the necessary parameters and the accuracy of these measurements have also been discussed.6 The cylinder dimensions were corrected for the anisotropic expansion of graphite, as discussed for density measurements.4,5 It is well-known that thallium oxidizes rapidly and hence a newly machined surface quickly tarnishes in air. The oxide film, however. is nonadherent and is easily removed by rubbing or by solution in water. Hence, immediately before use, both density and viscosity charges were immersed in water, wiped dry, and quickly transferred to the apparatus which was then rapidly evacuated. Specimens removed after determinations were only slightly tarnished and there was no other evidence that tarnishing affected the results. For example, the sharpness of the specimen edges from the containing vessels indicated complete filling by the liquid metal. Thallium of 99.999 pct purity was used in this investigation. Because of its high toxicity care was exercised in handling this material. For example, the melting procedure to prepare machinable ingots was carried out in an open, well-ventilated area, while protective gloves were always worn when handling the solid metal. RESULTS AND DISCUSSION Density. Measurements were made over a tempera-ture range of about 200°C above the melting point. The results are listed in Table I and plotted in Fig. 1. From the graph it is evident that the relation between density and temperature is linear. Such a relation has been observed before in this program for other metals and alloys475 and elsewhere by other workers. A least-squares analysis of experimental data gives the equation: pT1 = 11.658 - 1.439 x 10-3t where p = density in g per cu cm and t = temperature in "C. In Fig. 1, together with the present results, the data of Schneider and Heymer2 in the corresponding temperature range have also been plotted. Evidently, the two sets of data do not agree well, the results of Schneider and Heymer being about 0.6 pct higher. Viscosity. Viscosity data were obtained from the melting point, 303.5°C, up to 457.5"C. The data are listed in Table I and in Fig. 2 the plot of these results demonstrates a smooth curvilinear relation between

Jan 1, 1969