By J. Gordon Scott

The Iron Ore Company of Canada has now been operating a computer for the grading or blending of direct shipping ores for two years. This paper deals with the computer application pertaining to the grading of direct shipping ore. It consists of five sections. The first part deals briefly with a description of the operation of the Iron Ore Company of Canada; the second with the source and flow of the various data required to grade or blend ore; the third briefly outlines the computer programs used in this application; the fourth illustrates the mathematical approach used to properly blend ore. The final section briefly describes other technical computer programs.

Jan 1, 1964

By Robert M. Dreyer

In an industrialized nation, as the process of industrialization continues, the ratio of the value of production of non-metallic to metallic minerals normally increases gradually over a period of years. For example, in the United States, the ratio of the value of production of non-metals to metals now is approximately two-to-one. Those of us who come from California like to think that we inherit the mantle of the old hard-rock miner, but the truth of the matter is that, in California, of the total value of mineral production exclusive of fuels, 97% comes from non-metallic - industrial - minerals. Since the industrial minerals furnish a principal source of raw materials for the construction and chemical processing industries and since these two industries, in industrialized nations, generally increase directly with increasing population, the future of industrial mineral production both in the United States and throughout the world is indeed bright. Because of the importance of industrial mineral production, it often surprises those of us in the industrial mineral industry to find that industrial minerals are poorly understood by many of our colleagues in the mining industry. I think that one reason for this comprehension of the industrial mineral industry is that the education of both geologists and mining engineers still markedly emphasizes exploitation of the metals.

Jan 1, 1964

By Y. C. Liu

An analysis is presented to show that the formation of rolling textures in fcc metals can be rationalized in terms of flow mechanisms operative during the rolling process. First, a general approach used by Calnan is followed, where the rolling process is approximated on the basis of two axes, p and Q. In this treatement there are two separate sets of slip systems, one for each axis, and it is shown that a homogeneous rotation can he achieved by restricting the slip systems for the two axes to share common slip directions Then, two criteria are used to select the active slip systems for the axis P: they must have relatively high resoloed shear stresses, and dislocations on these slip systems must interact attractively in order to lower total energy content Finally, a method of analysis is introduced to locate the end position of an axis by knowing its acti7.e slip systems. The result of the analysis indi- cates that two main flow mechanisms operate in fcc metals. The ideal orientation derived from one oj-them is (8 13 21) (21 8 13) which is very close to the (358) (523) orientation observed experimentally on the rolling texture of copper. This flow mechanism should only he operative in metals containing dislocations extended into partials separated by less than five times their lattice parameter. The ideal orientations derived from the other flow mechanism are a combination of (1 10} (112) and a spread of orientations with (110) parallel to the rolling plane. This type of ideal orientations corresponds to those observed in the rolling texture of silver 30:70 brass, and binary alloys with high alloying content. This flow mechanism should be operative in any fcc metal regardless of its stacking-fauIt energy. When a polycrystalline metal is subjected to a large amount of plastic deformation, it is generally observed that grain orientations alter and align themselves towards certain positions, eventually reach-

Jan 1, 1964

By J. J. Sense

The Mission Unit of American Smelting and 'Refining Company is located in Pima County, Arizona, approximately twenty miles southwest of the City of Tucson. The Unit consists of an open pit copper mine and concentrator. The concentrate is shipped by rail to Company Smelters at Hayden, Arizona, or El Paso, Texas Mine stripping began at Mission in the fall of 1959, and construction of the 15,000 tons per day concentrator gas started in the spring of 1960, The first ore was treated in mid summer of 1961 and full ore production was reached in August of 1961. At that time over 46,000,000 tons of material had been moved from the pit. Current production (ore and waste) averages over 100,000 tons per day. Total production to date (ore and waste) over 120,000,000 tons.

Jan 1, 1964

By D. Weston

During recent years there has been a great deal of confusion in the North American mining industry with the introduction of new comminution terminology and claims (without substantiative evidence), for various types of equipment in this field. The authors will attempt to clarify the terminology used, and where possible, give illustrations of plant practice with actual operational and pilot plant data. This is considered necessary in order to obtain a clear picture of the comparison of such equipment to the revolutionary change that the Aerofall Mill has brought to the mining industry.

Jan 1, 1964

By K. C. Mills, E. T. Turkdogan

The results on the rates of vaporization of Fe-Ni alloys, levitated by an electromagnetic field in a stagnant atmosphere of helium, are shown to be in close agreement with those predicted theoretically. AS shown in Part I of this series of papers, the rates of vaporization of metals enhanced by convection currents are increased further by the process of condensation of metal vapor when there is a steep temperature gradient in the boundary layer. At the time this theoretical work was completed one of the authors (K. C. Mills) had already carried out some experimental work on the rates of vaporization of molten Fe-Ni alloys. The experimental work was done under conditions which make it possible to compare the experimental rate data with those predicted on theoretical grounds. EXPERIMENTAL The object of the experiments was to evaluate the activities in a number of binary metal systems. The details of the experimental technique are given in another paper by Mills, Kinoshita, and Grieveson,2 and, for the present purpose, a brief mention of the relevant features of the experimental method will be adequate. Using an induction coil, the metal weighing about 1 to 1.5 g was levitated by the electromagnetic field in a stagnant atmosphere of pure helium. The helium was freed from oxygen and water vapor in the usual manner, and its pressure in the vaporization chamber was maintained at 1 atm through a bleeder device. The vaporization chamber consisted of a pyrex tube, 2.8 cm diam, with a side arm connected to the helium bleeder. The bottom of the tube, shaped conical, was surrounded by the induction coil, and the top was sealed with an optical flat for the purpose of measuring the melt temperature with a two-color optical pyrometer. By suitable adjustment of the high-frequency power input, the metal was brought to the desired temperature in about 30 sec of levitation. After a specified vaporization time, e.g., 3 to 4 min, the alloy was quenched by switching off the power. The amount of metal vaporized was determined from the difference between the initial and final weights of the sample. During the vaporization time, temperature fluctuations of about ±10°C were observed. COMPARISON OF EXPERIMENTAL DATA WITH THEORETICAL VALUES The experimental results are given in Table I. As already mentioned, the attainment of the vaporization temperature took about 30 sec from the moment of levitation. Therefore, the times recorded in Table I are 30 sec less than the total time; this is considered to be a reasonable estimate of actual vaporization times.

Jan 1, 1964

By Henry N. McCarl

The New England States form the most northeastern portion of the continental United States and include Connecticut, Rhode island, Massachusetts, Vermont, New Hampshire, and Maine. These states have an aggregate population of over 10.5 million people, and an average annual population rate increase of about 1.3%. A great deal of new construction is required each year to meet the increasing demand for new homes, roads, offices, factories, and warehouses. Yet, prices of construction materials such as blocks and concrete are generally higher in New England than in other well populated areas of the United States. This is an indication of local demand being somewhat greater than supply, an atmosphere conducive to new developments in the production of construction materials. One such field of development is the rapidly growing Lightweight Aggregate Industry. Recent construction in Boston has used a great deal of lightweight aggregate. New structures using lightweight aggregate in lightweight concrete include the following: M.I.T.'s 20-story Earth Science Center and 17-story Married Students Housing Project Prudential Life Insurance Center, West End Redevelopment Project at Charles River Park, Hotel Americana, and the British-owned 33-story office building at 50 Pearl Street.

Jan 1, 1964

By A. Steiner, E. Miller, K. L. Komarek

Equations have been derived to calculate the chemical potentials of the components of liquid binary alloys from liquidus and enthalpy data. The equations are applicable to systems with intermetal-lic compounds of limited solid solubility. The liquidus curve of the Mg-Sn system was accurately redetermined, and the melting point of the compound Mg2Sn was found to be 770.5° * 0.3°C. The thermo-dynamic properties of the liquid alloys were calcu -lated from the liquidus data. The activity of tin shows both positive and negative deviations from Raoult&apos;s law and the relative integral entropy is positive. THE phase boundaries in an equilibrium phase diagram are functions of the thermodynamic properties of the coexisting phases. Specifically, the shape of the liquidus curve near an intermediate compound is determined by the properties of the compound and the liquid phase. Hauffe and wagnerl have derived an equation for the chemical potential differences (ui) of the liquid alloys near the congruent melting point when the heat of fusion of the compound and the liquidus curve are known. In their derivation the temperature dependence of the ui value was neglected, and liquid of stoichio-metric composition was chosen as the reference state. To obtain chemical potentials over the ntire composition range of the phase diagram with the pure components as the reference state, equations have been derived which incorporate the temperature dependence of the chemical potentials. Such a thermodynamic analysis can be carried out when the liquidus curve and the enthalpy values are known. The equations have been applied to the redetermined liquidus curve of the Mg-Sn system to obtain the thermodynamic properties of liquid Mg-Sn alloys. The Mg-Sn phase diagram has been studied by various investigators and the results have been compiled and critically assessed by Hansen.2 Preliminary thermal analyses showed that the basic features of the diagram were correct. The system has one congruent melting compound, Mg2Sn, two eutectics, and some solid solubility of tin in magnesium. However, the published liquidus temperatures show considerable scatter. In order to perform an accurate thermodynamic analysis, the liquidus curve between the magnesium-rich and tin-rich eutectic compositions was therefore redetermined by careful thermal analysis using highest-purity starting materials. EXPERIMENTAL PROCEDURE The magnesium metal (Dominion Magnesium Ltd, Toronto, Canada) had a purity of 99.99+ pct with the following impurities (in ppm): 20 Al, 30 Zn, 10 Si, <1 Ni, <1 Cu, <10 Fe; tin (Cominco Products, Spokane, Wash.) contained 99.999+ pct Sn. The graphite crucibles were machined from graphite rods (United Carbon Products Corp., Bay City, Mich.) which had an average total ash content of less than 30 ppm. All the graphite parts were baked out in vacuum at 950" to 1000°C for a minimum of 24 hr to remove volatile organic materials. The graphite crucibles (3 in. long, 1-5/8 in. OD, 1-3/8 in. ID) were tightly closed with a threaded cover (1/2 in. thick) which had a central thermocouple well (2-1/4 in. long, 5/16 in. OD, 3/16 in. ID). Cover and thermocouple well were machined from one piece of graphite. A thin sheath of quartz was inserted in the well to protect the thermocouple

Jan 1, 1964

By K. J. Brondyke, P. D. Hess

Lack of correlation between densities of aluminum alloy samples solidified under reduced pressure (vacuum gas test) and hydrogen content of the metal is explained on the basis of inclusions serving as nuclei for hydrogen bubble formation. As a result of these findings, the vacuum gas test is suggested as a practical tool to indicate metal cleanliness and the potential effects of hydrogen. Visual obseroation of the sample during solidification under vacuum provides more useful information than that obtained either from density meas -urements or sectioning of the solidified sample. A rapid, practical method of detecting and measuring gas in molten-aluminum alloys has been sought for many years. The development of the vacuum gas test appeared to solve this problem. However, the vacuum gas test is subject to certain limitations, and the results must be interpreted mindful of these limitations, as described herein. Since the only gas which is appreciably soluble in aluminum is hydrogen, the terms gas and hydrogen will be used interchangeably in this paper. In the early days of the aluminum industry, when techniques were not as refined as they are today, it was customary to pour small "pancakes" of alumi- num on a metal plate. These were allowed to solidify under atmospheric pressure. Excessive gas in the metal was evidenced by the appearance of small bubbles on the surface of the "pancake".&apos; It is obvious that such a method would only show very high gas levels far above any which could be tolerated by today&apos;s standards of quality required for most applications. Various attempts were made to develop methods which would be more sensitive. Among these were measurements of density of aluminum alloys solidified under controlled conditions, radiography of cast slabs, and examination of fractures. The method which showed the greatest promise and appeared most practical was the solidification of a sample of the molten aluminum alloy under vacuum. The samples so solidified are evaluated either by observation for bubble emission during solidification, by sectioning the solidified sample and examining for porosity, or by determining the density of the solidified sample. This test is known internationally as the Straube-Pfeiffer test or the reduced-pressure solidification test, but in America it is commonly referred to as the vacuum gas test2-&apos; and will be so designated in this paper. The determination of density appeared an attractive and convenient means of providing a numerical rating for the samples. Attempts were made in some instances to correlate densities to hydrogen contents. Unfortunately, the visible loss of gas during solidification of samples with high gas contents precluded a correlation of vacuum gas test densities with the observed gas evolution. This led to Alcoa&apos;s use of two different pressures; 50 mm of

Jan 1, 1964

By Alvin W. Schillinger

Drilling was not entirely satisfactory in the search for native copper in the Osceola amygdaloid footwall as mining showed oreshoots to be more continuous than drilling indicated. The Geophysics Department of Michigan Technological University developed a portable induced polarization drill hole probe with a 3 electrode configuration and a sampling radius of 5&apos;± A 20 ma current of alternately reversed polarity is pulsed at 3.5 sec. intervals and readings are taken every two feet. Potential is read during the "on" cycle for resistivity determinations. During the "off" cycle, after 10 ms delay, the I.P. potential is sampled for 10 ms and recorded. Resistivity (ohm-feet) and "S" values (mv/v) are plotted on semi-log paper. A lithologic log is plotted based on resistivity and anomalous "S" values noted. The low resistivity amygdaloid contains sills of high resistivity basaltic trap. Verified by core logs, amygdaloid-trap contacts could be picked to ±.5&apos; from resistivity alone. Lithologic logs of long steel holes, based&apos; on resistivity, now replaced sludge logging. An "S" value of 30 mv/v was established as the lower limit of diagnostic I.P. effects in mineralized amygdaloid and 50 mv/v as a threshold value for ore. Of 914 footwall zones drilled, 315 were probed yielding 203 anomalies. Success increased from 34% for drilling to 72% for drilling and probing. As checked by mining, 46 probe results were 78% correct. Failures were due to the instrument not detecting copper or to the misinterpretation of an anomaly. No false anomalies were found.

Jan 1, 1964

By R. P. Abendroth

This study is concerned with the kinetics of selective oxidation of chromium in a commercial Fe-Cr-Ni alloy. Selective oxidation of chromium in this alloy, by use of a low oxygen-potential atmosphere, leads to the formation of a compact, protective layer of Cr2O3. This layer serves to protect this alloy from gross scaling when it is subsequently exposed to severe oxidizing conditions at high temperature. The interaction of low oxygen-potential atmospheres close to equilibrium with Fe-Cr and Ni-Cr alloys has been studied by others."&apos; These studies werk concerned with the surface-structure variations under slightly oxidizing conditions. NO detailed study was made of the oxide scale formation kinetics, however. The alloy samples were cut from 0.012-in.-thick sheet, with an apparent surface area of 7.1 sq cm. These sheet samples were abraded through 4/0 metallographic paper, and washed in alcohol and acetone. The analysis of the sheet alloy is (in weight percent): 42 pct Ni, 5.5 pct Cr, 0.09 pct C, 0.18 pct Al, 0.36 pct Si, 0.26 pct Mn, balance Fe. The weight gain vs time data were obtained with a 2-g capacity fused-silica spring—cathetometer system. The spring deflection was optically magnified ten times before being read by the cathetometer. A sensitivity of about 0.01 mg was attainable. The spring was enclosed in a water jacket maintained at 60°C to minimize the effect of temperature changes. The sample was suspended from the spring with a fused-silica hangdown and was positioned in the thermal center of a mullite furnace tube. Sample temperature was read with the aid of a thermocouple placed outside the mullite tube and an inside vs outside temperature calibration. Temperature change during the course of a run was ±0.25°C, with a temperature gradient of less than l.O°C over the length of the sample. Total temperature uncertainty was no more than ±3.0°C. Alignment difficulties between the hangdown and radiation shields in the furnace tube required that the sample be positioned in the furnace when cold, and heated with the furnace until the temperature stabilized at the desired point. This required 5 to 6 hr, and was carried out in Matheson ultrahigh-purity hydrogen. Oxidation was started, after evacuation, by introducing a hydrogen-water vapor mixture, obtained by saturating hydrogen with water vapor at 31.00o ± 0.02oC. Oxidation was continued for 90 min. Gas flow was 300 ml per min during heat up and oxidation. Since only several milligrams of oxide are formed on each sample, chemical analysis of the oxide is difficult. A representative analysis is: 80 pct Cr2O3, 5 pct Fe2O3, 3 pct Al2O3, 4 pct MnO, 7 pct SiO2, 1 pct or less NiO. X-ray diffraction analysis of the oxide as formed on the alloy gives rhombohedra1 Cr2O3, and barely distinguishable amounts of a cubic spinel phase, and possibly AlZOs and SO2. The identification of these latter two compounds is by no means certain. The spinel phase could be based on iron or manganese as these elements are present in significant amounts in the oxide. The results of the kinetic studies using 31°C dew-point hydrogen-water vapor mixtures were found to conform to a parabolic rate law. In many cases the parabolic plot consisted of two intersecting straight lines, defining an early and a late rate for a particular run, and in the other cases the parabolic plot consisted of one straight line for the entire run. The slopes of the various straight lines were determined by the method of least squares. Reproducibility of the data was good enough for multiple runs at the same temperature such that the value given for the rate constant is the average for two or more closely similar values, rather than widely varying values of the rate, where more than one determination is indicated in Table I. The exhibition of only one or of two rate constants during a run can happen at the same temperature. Thus, Table I shows that at 11&apos;74°C a single rate constant was obtained from one sample, while other samples oxidized at the same temperature gave an early and a late rate constant. It should be noted that the single rate constant corresponds very closely with the early rate constant. This is also true at 1153°C. The time at which the late rate started to appear was variable, usually occurring 20 to 40 min after oxidation had started.

Jan 1, 1964

By Paul L. Cloke, S. R. Titley

Paul L. Cloke (Assistant Professor, Dept. of Geology and Mineralogy, The University of Michigan, Ann Arbor, Mich.) - On examination of the paper by S. R. Titley it appears that several errors have been made, many of them of a fundamental nature. It is the intent of this discussion to point out these mistakes, and, insofar as possible with the data at hand, to correct them. EXPERIMENTAL WORK Ferrimolybdite-Limonite-Water: The results of the experiments described are very difficult to interpret; nevertheless, a correct interpretation is essential as is pointed out subsequently. The difficulties become apparent when reasons are sought for the continuing change of pH after conversion of ferrimolybdite to ferric hydroxide and for the change of pH when -stirring is stopped after a steady value has been reached. In seeking an explanation of this experiment it seemed to this writer that the (temporarily) steady pH values might be due to kinetic rather than equilibrium effects. In this view the steady pH on stirring might be explained as a balance of several reactions proceeding simultaneously. The first of these would be the slow solution of ferrimolybdite,

Jan 1, 1964

Safety rules for installing and using electrical equipment in and about coal mines covered in this information circular supersede those previously included in Bureau of Mines Bulletin 514, issued in 1952. This revision brings these rules up to data and more nearly in line with present operating and safety practices in the industry. The, rules are intended to supplement existing existing Federal and State regulations, and no provision shall be construed to oppose or supersede any provisions of the Federal Mine Safety Codes, the Federal Coal Mine Safety Act, or the mining laws of any State. The rules were designed to permit progress, such as application of new or improved materials and equipment or use of new practices where these materials, equipment or practices retain or improve the level of safety established by these requirements. It is hoped that they will fill the need for a concise edition for mine electricians and electrical engineers, especially those who do not have ready access to more detailed rules or codes.

Jan 1, 1964

By E. G. Loesche

Grinding mills in which the comminution takes place between rollers and the surface of a disc, table or ring are generally known as roller type mills. The Loesche Mill, also known as the Disc Roll Mill, is a special type of roller mill in which the grinding surfaces consist of two rollers assembled over a horizontal disc or table which rotates at a relatively low speed. This design is particularly applicable to industry&apos;s present day demand for large capacity grinding mills.

Jan 1, 1964

By A. F. Witt, A. M. Gaudin, A. K. Biswas

Finite contact angles in the rutile-water-organic liquid system are traceable to contamination or are due to addition of a surface-active agent. Finite contact angles are invariably accompanied by hysteresis.1-7 Besides surfactant concentration and pH, the nature of the organic liquid is found to be a factor influencing the magnitude of contact angle hysteresis. In a recent paper the authors have reviewed principles and applications of measurement methods for contact angles and their hysteresis.22 In this paper, these methods are applied to a system consisting of rutile, an organic liquid (benzene, decane, or dode-cane) and water. Surfactant (dodecylamine hydro-chloride) was used at various concentrations and various pH values. MATERIALS A synthetic rutile crystal supplied by the Linde Co. was used. It is a cylinder 1/2 in. diam, with faces cut perpendicular to the c-axis. The crystal is stated to be alumina-free and to be 99.9% pure. Rutile is a high surface energy solid, its calculated average field strength being 2.7 x 105 e.s.u.,9 its dielectric constant10 is 114. The zero point of charge of rutile was measured11 and found to be at pH 6.0. The atomic distances and bond angles of the tetragonal crystal of rutile have been precisely determined.l2 The organic liquids were specially purified. Reagent grade benzene was repeatedly shaken with concentrated sulfuric acid to remove thiophene, then neutralized with sodium hydroxide solution, rinsed with distilled water, dried overnight over anhydrous calcium chloride and filtered. The refractive index of this chemically purified benzene was 1.4977 (at 25°C) - very close to that of pure benzene (n25 1.4979).13 Both n-decane and n-dodecane were washed with aqueous sodium hydroxide, concentrated sulfuric acid (repeatedly, until the acid layer was colorless) and again with alkali, to free the organic hydrocarbon from fatty acids and unsaturated hydrocarbons. The organic phases were subsequently washed with distilled water and dried over anhydrous sodium sulfate. The filtered hydrocarbons were then distilled under vacuum (9-10 mm pressure). Decane, thus purified, showed traces of unsaturated and of carboxylic compounds. On gas chromatographic analysis the purified n-dodecane showed the presence of two impurities. However, the relative retention times of these components did not change substantially when measured on a polar or a nonpolar column. This indicates that the compounds were probably in the same polarity class, i.e. the components were nonpolar like dodecane. Conductivity water has always been one of the liquids. Conductivity of the water used was 10-6 ohm-&apos; cm". Dodecyl ammonium chloride was prepared from pure amine (supplied by Armour and Co., Chicago), by Li in the MIT Mineral Engineering Laboratory.14 The critical micelle concentration at 25°C is known, 0.0138 mol per liter15 or 3.06 gpl. All our experiments have been done at concentrations lower than the critical micelle concentration. The glass vessels, glass drop holder and the rutile crystal were all cleaned with hot chromic acid followed by distilled water, concentrated hydrochloric acid, and again distilled water, and conductivity water. During the experiments, a nitrogen atmosphere was maintained. For this purpose, commercially purified nitrogen was further purified by passing it over hot copper wire at 450°C, then through columns of acidic chromous chloride solution, concentrated alkali solution and distilled water. APPARATUS AND METHODS Hysteresis was produced by the "captive drop" or constant volume drop method as well as by the "expanding-contracting drop" or variable volume drop method. The image of the drop while it is expanding, contracting or moving is projected on a screen and photographed. The developed film is projected through an enlarger and the contact angles measured with a protractor.

Jan 1, 1964

By W. A. Backofen, G. Y. Chin, W. F. Hosford

The effect of machine stiffness on discontinuous flow and fracture of the 2024 aluminum alloy was studied in tension at 4.2OK. An increase of machine stiffness was found to decrease the amount of elongation and drop in load during discontinuous flow, thereby postponing fracture to larger strains and higher stresses. The possibility of utilizing stiffened tools in deformation processing to suppress shear fracture originating from unstable flow was indicated. The problem of nucleating discontinuous flow and the role of the effective mass of the system in discontinuous flow were also considered. AT low temperatures the plastic flow of metals is often discontinuous, with sudden load drops and elongations.1,3 Basinski1,4 has presented strong evidence that discontinuous flow, at least in aluminum alloys, occurs under nearly adiabatic conditions. During testing the load may drop suddenly and flow become localized when the thermal softening, due to heat generated in plastic straining, is greater than the strain and strain-rate hardening. This instability criterion is more easily satisfied at low temperatures because 1) the volume specific heat is reduced so that relatively large temperature increases are possible in straining, and 2) the flow stress is relatively temperature-dependent. The important role of adiabatic shear in ductile fracture processes has been emphasized,5-1 and consideration has already been given to the influences of thermal and mechanical properties on the tendency of a material to undergo adiabatic shear.17677 By focusing attention on how the mechanical loading system influences low-temperature discontinuous flow, additional insight into adiabatic shear and its effect on fracture may be gained. EXPERIMENTAL PROCEDURE Because of its low thermal conductivity, the 2024 aluminum alloy exhibits a highly consistent discon- tinuous-flow behavior at 4.2°K and was therefore chosen as the material for study. Machined specimens of 0.113 in. diam and 1.125 in. gage length were solution heat-treated at 490°C for 3 hr, quenched into cold water, and immediately immersed in liquid nitrogen until just before testing. Testing was done at 4.2°K by immersion in liquid helium at a crosshead drive rate of 0.03 in. per min. As normally used (hard-machine basis), the spring constant of the testing machine was k = 25,000 lb per in. By inserting beam springs in series with the specimen, this value could be lowered by a factor of about 100. Details can be found elsewhere.? As a result of variable machine stiffness, the actual strain rate ranged from about 3 x 10 5 to 3 x 10-4 per sec from one test to another, as well as within any one test. However, preliminary tests had established that the tensile curves were not altered significantly by this strain-rate variation. Fig. 1 shows a typical load vs plastic-elongation curve for a solution heat-treated 2024 aluminum alloy specimen pulled in the standard hard machine (k = 25,000 lb per in.) at 4.2"K. The elastic extension has been subtracted. Plastic flow proceeded smoothly from yielding at approximately 22,000 psi (load = 220 lb) to a strain of about 4 pct at which point the flow became discontinuous. The magnitude of the load drops as well as the plastic elongation per drop increased with increasing strain until the specimen finally broke abruptly. The load-elongation behavior of a sample tested with a relatively soft machine under otherwise identical conditions is given in Fig. 2. In general, there

Jan 1, 1964

By Burton H. Boyum

The paper generally reviews the iron ore occurrences and regional geology of Western Australia, but features in particular the mesa deposits of PJasic Materials - Cliffs International. Initial production is planned from a aeries of mesa deposits of Eocene-Oligocene age. The ore is oölitic to pisolitic goethite and hematite. Source of the iron in the mesa deposits is thought to be from the Precambrian iron-formations. The geology and occurrences of the mesa iron ore deposits are summarized and illustrated.

Jan 1, 1964

The Sixtieth Regular Meeting of the Rocky Mountain Coal Mining Institute convening at the Stanley Hotel in Estes Park, Colorado, was declared in session at 10:10 a.m. by Past President Mike Zakotnik, Jr., General Superintendent, The Kemmerer Coal Company, Frontier, Wyoming. Mike introduced Claude P. Heiner, President, Minerals and Development Corporation, Salt Lake City, Utah; and President of the Rocky Mountain Coal Mining Institute. President&apos;s Address Members of the Rocky Mountain Coal Min- ing Institute, guests, visitors and friends: I feel this is a distinct honor to talk to you on the occasion of this 60th regular meeting of the Institute. I once assumed this would be the Institute&apos;s 60th birthday, but later found that the first meeting was held in the State Capitol at Denver on November 12, 1912, at which time a comparatively small group of operators duly organized the Institute; a Mr. Weitzel of Colorado Fuel & Iron Company was then elected president and our late and dearly remembered Fred W. Whiteside, whose wife Gussie now carries Fred&apos;s work forward, was elected secretary. From Fred&apos;s records, early meetings were held semi-annually at rather irregular intervals, so that this 60th meeting is approximately the 52nd birthday of the organization and I am number 44 to serve as president. This latter development, I am sure, was conjured up last year by certain members at Glenwood Springs when I was absent. Anyway, I am honored and trust &apos;that these sessions will be both interesting and instructive in helping us on our way in the coal business.

Jan 1, 1964

By Irving B. Cadoff, Ernest Levine

The crack formation and propagation in the single -phase Cu-4 pct Ag alloys were studied. The alloys were loaded in mercury to various stress levels, the mercury was removed, and the specimen examined for cracks. Cracks were found to develop below the fracture stress; the frequency of such cracks increased with increasing stress level. Some cracks were nmpropagative. Fracture in mercury was found to occur by the link-up of cracks formed at various stress levels rather than by the growth and propagation of a single crack. If the mercury environment is removed prior to a critical amount of crack formation, then continued loading results in ductile fracture. The appearance of the cracks at selected grain boundaries is related to the relative orientation of the boundaries, as are the propaga-tive characteristics of the crack. The mercury interaction appears to be one of lowering the strength of the metal-metal bonds in the high-stress area of the grain boundary. GRIFFITH&apos;S microcrack theory1 proposed a critical crack size above which a crack in an elastic material grows with decreasing energy at a stress of From his theory it was proposed that the presence of a liquid tends to lower the surface energy of the microcrack faces2 leading to a decrease in the critical crack size necessary for spontaneous fracture propagation. stroh3 proposed that the stress concentration at a grain boundary due to pile-up may initiate a microcrack at the grain boundary. petch4 and Stroh5 evaluated the stress distribution at the head of a pile-up in a polycrystal-line material and deduced that the critical crack size and hence of is dependent on the grain size. Experimental verification of this dependence was found by petch6 for hydrogen embrittlement of steel. Studies in stress-corrosion cracking7 have provided a picture of fracture which shows that initial separations occur in a scattered, independent fashion in regions of high tensile stress. A minimum or threshold stress is necessary to produce a sufficient stress concentration to initiate frac- ture. These separations join up to form a crack. The extension of fracture is largely discontinuous and consists of a joining up of cracks. In recent worka evidence of this scattered crack network was found in a Cu-Ag alloy embrittled by mercury. For the Cu alloy-Hg couple, the crack path has also been found to be dependent on the orientation of adjacent grains, and with the addition of zinc to mercury a reduction in embrittlement along with a change in fracture morphology was found.9 In this present study, a mercury-dewetting method was used to observe crack initiation and fracture morphology when a Cu-4 pct Ag alloy is deformed in mercury and Hg-Zn solutions. PROCEDURE Specimens of Cu-4 pct Ag were prepared as in previous crack-path studies.&apos; The specimens were heated at 770°C for 24 hr and water-quenched Tension tests using a table-model Instron were carried out in mercury and in various concentrations of Hg-Zn. Loading was in steps up to the fracture stress, with the load being removed and the specimen examined for surface cracks at each step. The specimens were dewetted after each load to permit examination of the surface structure and rewetted prior to continued loading. The specimens were wetted by electro polish ing in phosphoric acid, rinsing in alcohol, and then immersing in a pool of mercury. Dewetting was accomplished by flame heating the specimen for 30 sec in a vacuum. Some surface contamination was found, but not enough to obscure crack configurations and grain boundaries. RESULTS Fracture Characteristics in Mercury. Fig. 1 is a stress-strain curve showing the progressive step-wise loading of the specimen. As may be seen from the graph, the first position stopped at a is at a stress 5000 psi below the expected fracture stress of 25,000 psi. Examination of the specimen after removal of mercury showed only one crack. The appearance of this crack at a stress far below the fracture stress of this alloy in mercury did not affect the stress-strain curve in any manner. The specimen was then recoated with mercury and deformation was continued (curve b, Fig. 1) raising the stress by 4000 psi, and the same procedure re~eated. The initial crack was located and appeared as in Fig. 2 (crack lb). In this figure the crack is

Jan 1, 1964

By N. S. Stoloff, R. G. Davis

It is concluded from an X-ray stztdy that the formation of the hcp Mg3Cd superlattice is a nuclea-tion and growth reaction. A two-phase, ordered-plus-disordered, region is observed between 153" nnd 141"C. A maximum in the flow stress is observed both at temperature and in quenched specimens within the two-phase region. The peak arises fro112 the extra energy required to create antiphase boundary upon cutting the ordered regions. Hardening during isothermal annealing in Mg3Cd has been shown to be similar to the domain hardening in Cu3Au-type alloys in that up to the maximum the structure is ordered domains growing into a short range ordered matrix. The hardening is due to a combination of short range order strengthening and the strengthening produced when antiphase boundary has to be created. In a recent study1 of the effect of long-range order upon the mechanical properties and deformation modes of hcp Mg3Cd a comparison was made be- tween quenched (disordered) and slow-cooled (fully ordered) specimens. The most striking observations were that the disordered alloy yields at a much higher stress than the ordered alloy, and that there is a change in slip mode from primarily (_0001) ba_sal slip in the disordered state to (0001), {1010}, {1122}, and {l011} slip in the ordered state. The main purpose of the present work is to extend these observations to determine whether MgsCd exhibits a peak in flow stress at an intermediate degree of order, or at a critical domain size, as do other orderedstems. However, disagreement exists about the Mg3Cd order transformation with respect to: 1) the location of the critical temperature for order, 165°C or 153"~,&apos; and 2) how the degree of order varies with temperature. Welber et a1.5 concluded from specific heat measurements that the formation of Mg3Cd is a second-order reaction with the degree of order a continuous function of temperature, while Moore and Raynor concluded that it is neither a first-order reaction, with the degree of order a discontinuous function of temperature, nor a second-order reaction. Consequently it was considered necessary to undertake an X-ray investigation into the change in degree of order and structure in the

Jan 1, 1964