By C. G. Dunn, J. L. Walter

Either (100) (001] or (110) (0011 oriented secondaries, or both, depending on annealing atmosphere and material composition, grew in a matrix of 2-dimensional grains. The growth dependence of secondaries of(hkl) orientation in the iron and 0.6 pct Si-Fe is explained in terms of surface energy driving forces and the dependence of these driving forces on both (hkl) orientation and amount of oxygen at the surace. (100) [001] grains grow when suflicient oxygen is present at the gas-metal interface to make y100 the lowest (hkl) surface energy. When little or no oxygen is present at the gas -metal interface, making Y110 the lowest surface energy, (110) (001 1 grains grow. When Y100 and y110 are approximately equal but lowest among (hkl) surface energies, both (100) (0011 and (110) (0011 grains grow simultaneously. An excess of surface oxygen produces complete grain growth inhibition in high-purity iron; i.e., a 3-dimensional grain structure is retained over long annealing periods. However, a small amount of silicon in the iron reduces the growth inhibiting tendency of oxygen without altering the (hkl) surface energy relationships. Some information on annealing twins is presented. SECONDARY recrystallization in high-purity a iron, cold rolled to strip a few mils thick, was reported recently.' The present paper provides additional information on this subject, also furnishes similar information on both zone-refined iron and a high-purity 0.6 pct Si-Fe alloy, and treats the more important surface phenomena that determine to a large extent whether one or more secondary recrystallization textures will appear during annealing. Previous studies on high-purity 3 pct Si-Fe2,3 have shown the importance of (hkl) and impurity-atom dependent gas-metal surface energies on the formation of secondary recrystallization textures in high-purity material. For example, either (100) or (110) oriented grains may have the lowest surface energy depending on the amount of oxygen at the gas-metal interface, and hence the highest driving force for growth if other growth factors are the same. Another important phenomenon in high-purity material is stabilization of the matrix structure; neither impurities nor a strong matrix texture seem to be necessary when recrystallization and normal grain growth occur, developing a stable two-dimensional type grain structure. The average grain size in such a structure is usually between one and two times the specimen thickness. Consequently, most of the grains have grain boundaries terminating at exposed surfaces, and this results in gas-metal interfaces (or hkl surfaces) as well as

Jan 1, 1962

By W. L. Phillips

Single crystals of aluminum, brass, and copper oriented for (100) and (110) slip were extended at 25°, 400°, and 600°C in simple shear. Aluminum specimens oriented for nonoctahedral slip began to shear at a higher critical resolved shear stress than specimens oriented for octahedral slip. Parabolic stress-strain curves were obtained from zero strain. The initial rate of parabolic hardening was lower for specimens sheared on the (100) plane in a close-packed direction <110>, than for specimens sheared in a nonclose-packed direction <100>. metallographic evidence, however, showed that all slip traces could be explained in terms of (111) <100> slip. All attempts to cause nonoctahedral slip in copper and 70-30 a-brass single crystals were unsuccessful. Instead of shearing, the crystals bent, allowing {111} type planes to come into action. NONOCTAHEDRAL slip in aluminum has been reported under three different conditions: first, as the main mode of slip in tension experiments at elevated temperatures;&apos;-&apos; second, as the main mode of slip in direct shear experiments at room temperat~re; and third, as a minor mode of deformation, i.e., as cross-slip, in tension, shear, and bicrystal experiments at room and elevated temperatures."-l2 However, as far as the author knows, nonoctahedral slip has not been reported in either copper or 70-30 a-brass. The present study was undertaken to determine whether nonoctahedral slip could be obtained in aluminum, brass, or copper at room or elevated temperatures when the shear stress was approximately constant over the cross-section, a maximum at the center, or a maximum at the surface. EXPERIMENTAL PROCEDURE A detailed description of the crystal preparation and shearing apparatus has been given previo~sly. Cylindrical crystals 1/2 in. in diam and 8 in. long were grown from the melt in a temperature-gradient furnace. The aluminum contained 0.001 pct Zn, 0.001 pct S, and 0.001 pct Fe; the 70-30 brass contained 0.015 pct Pb, 0.001 pct Fe, 0.01 pct Ni, 0.02 pct Sn, and 0.005 pct Se; the copper was certified OFHC of 99.98 pct purity. All samples were electropolished prior to testing. The shear apparatus was a modified Bausch type. The strain sensitivity was 4 x lob4 Load was applied by clamping the rods attached to the shear plates in an Instron tensile machine. The rate of loading was 0.02 in. per min. In all cases a 1/8-in. gage length was used. For the tests performed at 400° and 600°C the shear plates, collars, and rods were made of stainless steel. These elevated-temperature tests were performed in an argon atmosphere. A) Aluminum at Room Temperature. Values of a and ß for the various slip planes and slip directions investigated are shown in Table I where a is the complement of the angle between the specimen axis and the slip direction, and ß is the angle between the specimen axis and the normal to the shear plane. The shear stress is a function of a (assuming ß - 0);10 when a is less than 27 deg, the shear stress on the slip plane for which the specimen is oriented has a maximum at the center of the crystal; at a = 27 deg the shear stress is constant across the slip plane; for a greater than 27 deg the shear stress is a minimum at the center. Fig. 1 shows the stress-strain curves for specimens cut from crystals 1, 2, and 5, which were sheared on the (010) plane in the [loll direction at room temperature. These three crystals have shear-stress distributions corresponding to the three dif-

Jan 1, 1962

By G E. Craig, W. M. Williams

A simple, easily constructed apparatus suitable for the zone refining of iron and other reactive materials is described. After eight passes at one inch per hour, the iron produced showed a marked drop in hardness to 49 Brinell. In addition, an arbitrarily -defined recrystallization temperature was lowered by about 35°C and the rate of grain growth greatly increased. CERTAIN materials, of which iron is one, are so reactive that they cannot be zone refined in any known container without becoming contaminated. For such substances, the floating zone method ( 1) may be used. In this method, the specimen is supported vertically in an inert atmosphere and the molten zone supports itself by its own sur-face tension. The method was first applied to silicon (2) and has since been used for other reactive metals such as zirconium and titanium. Smith and Rutherford (3) have previously reported on the floating zone refining of iron; the efficiency of the method for reducing the car-bon content was demonstrated on

Jan 1, 1962

By C. K. Jankousky

The midwestern area referred to is the Illinois basin. The coals presently worked are mainly the No. 5 and No. 6 coal seams which vary in thickness from five to eleven feet. Present average of the more important No. 6 id about nine feet. The coal can vary considerably in toughness within the same mine with some coal perhaps rashing very easily and other coal being extremely difficult to cut. Top is generally well laminated shales with some fortunate areas having limestone roof. There are local areas with troublesome top of poorly laminated shales, shale with slickensides and shale intermingled with small partings and traces of coal. The bottoms are generally one to three feet of clay which softens readily on exposure to moisture. The mines are dry although some water is released and collects from rapid penetration of the seam by continuous miners. However, there are locally wet areas. Most of this material refers to mines of the Freeman Coal Mining Corporation. The mining operations written about are underground mines in southern and central Illinois.

Jan 1, 1962

By Floyd G. Anderson

This report reviews and summarizes information on prevention and suppression of dust in mining, tunneling, and quarrying published in the United States during the years 1958 through 1960. Unpublished pertinent data developed or assembled by the Bureau of Mines during this period also are included. Silicosis statistics reported by the U.S. Public Health Service indicate a sizable silicotic population in the United States and suggest a need for greater dust-control effort. A joint medical-environmental survey was begun by the U.S. Public Health Service and the Bureau of Mines to evaluate the magnitude of the silicosis problem in the metal mining industry in the United States.

Jan 1, 1962

By T. G. Edgeworth

Some of the historical background of the industry is reviewed, with reference to the different types of reduction cells in use for aluminum smelting. Factors to be considered in cell des1gn involve capital, power, and operating costs. The trend is apparently toward larger cells. The industry is studying new construction materials for cell linings, as well as alternate electrolyte compositions and other design changes which will improve productivity and energy efficiency. The aluminum smelting activity in other countries is briefly reviewed. TODA Y'S industrial production of aluminum is still based on the simultaneous discoveries made in 1886 by Charles Martin Hall in Ohio, and Paul Heroult in France. Up to that date, only about 50 tons of aluminum had been produced in the world, and the price at that time was about $5 per pound. Sucl1 figures must be contrasted with the present world aluminum smelting capacity of over five mil-lion tons per year, and a price of about 25 cents per pound.

Jan 1, 1962

By John Ward Smith

The potential economic value of oil shale depends on the products from thermal degradation of the rock, because no other practical method for producing valuable material from oil shale has been found. Detailed study of thermal degradation behavior can aid in characterizing oil shales and their deposits and in evaluating oil-shale processing methods, Numerous publications describe various pyrolysis properties of oil shales (see surveys 3, 9, 11 and articles 1, 2, 4-8, 10, 12),4 but they do not describe a generally applicable analytical procedure for detailed evaluation of thermal degradation products. The analytical method presented here for such evaluations is designed to provide for: 1. Control of retorting conditions--temperature, heating, rate, reaction atmosphere--plus some control over retort pressure and carrier-gas flow, 2. Precise direct gravimetric measurement of the thermal degradation products--oil, water, gas, and spent charge (residue after thermal treatment of the charge). 3. Samples of all products. 4. Determination of the identities and amounts of gaseous compounds produced. 5. Elemental analysis and gross heating value of all products. 6. Determination of the distribution in the retorting products of the elements present in the original samples.

Jan 1, 1962

By Donald W. Mitchell

Research shows that water neutralizes the explosion hazard of coal dust when present in sufficient quantity and when intimately mixed with the dust. The quantity of water required to neutralize coal dust and coal-rock dust mixtures is about equal to the limiting moisture adsorptive capacity of the dust; the adsorptive capacity increases with increase in the fineness and volatile content of the coal. Pools of water or high atmospheric humidity do not reduce the explosion hazard. Although wetted dust is less dispersible than dry dust, poor dispersibility cannot be relied on as the sole safeguard against explosion. Dust mixtures that contain water in excess of their limiting adsorptive capacity are dispersed and ignited by severe initiation sources. Pure coal dust adsorbs water with difficulty and retains water poorly; adsorption and retention is increased by the addition of rock dust the coal; the rock dust agglutinates wetted coal and assures that incombustible is present should drying occur. Therefore, it is advantageous to rock-dust wet areas in bituminous coal and lignite mines. When coal-rock dust mixtures are wetted and subsequently dried, the explosion hazard is about the same as for dust which was not wetted.

Jan 1, 1962

By F. L. Wideman

This report describes a computer program that is used for the calculation of the coordinates and elevations of subsidence survey pins located by intersection. This program was developed for the Federal Bureau of Mines by the Numerical Analysis Laboratory, University of Arizona. These calculations, although relatively simple, are both tedious and time-consuming when computed with a desk calculator and trigonometric tables. In this survey, a large number of pins were surveyed repeatedly, and it was evident that both time and money could be saved by using a digital computer.

Jan 1, 1962

By Milton E. Wadsworth, R. Ted Wimber

Cobalt sulfate solutions containing ammonium acetate and chloroplatinic acid were reduced by hydrogen in a pyrex-glass lined autoclave in the temperature range of 170o to 232°C and hydrogen partial pressure range of 115 to 830 psia. The reduction rate was directly proportional to the hydrogen partial pressure and surface area of the pyrex glass and was independent of the quantity of chloroplatinic acid added initially. Experiments involving the variation of the relative concentration of ammonium acetate indicated that the reducible cobalt complex was probably the diacetate complex of cobalt, Co(AC)4H20, or a new mononcetate complex Co Ac, which was in solubility equilibrium with a pink precipitate of CO(AC)-4HzO. THE reaction in which a metal is dissolved by an acid to produce gaseous hydrogen and a salt solution was discovered early in the history of chemistry. In 1859 Beketoff found experimentally that this reaction could be reversed; i.e., a salt solution could be reduced by gaseous hydrogen to produce a metal and an acid. A review of work done on this phenomenon since that time may be found elsewhere., The hydrogen reduction of a cobalt salt solution is facilitated by complexing the cobalt ion. An ammonia complex of cobalt has been reduced commercially in the recovery of cobalt metal. A new reducible complex of cobalt was discovered5 when it was found that a co-baltous sulfate solution containing ammonium acetate could be reduced by hydrogen at temperatures in the region of 200°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature below its normal boiling point, a violet color became apparent, indicating complex formation. The nature of this complex was investigated5 by the addition of NH4Ac to a CoSO4 solution maintained at 85o. During the first additions of NH, Ac, the pH of the solution remained fairly constant at about 5.85. However, as the ratio of NH,Ac to CoSO, approached two, the pH rose and then leveled off at about 6.05. The absorption spectra of a Co(Ac), solution and a CoSO,, NH Ac solution were obtained at 85°C and were compared and found to be the same. These findings suggested that the diacetate complex of cobalt, Co(Ac),.4H20, was formed at 85°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature above about 165o, a finely divided pink precipitate appeared. The X-ray diffraction pattern of this precipitate indicated that it was Co(Ac), - 4H,O. In addition, it was discovered that when chloroplatinic acid, H,PtCl;, was added initially to the cobalt sulfate-ammonium acetate solution, a faster reduction was obtained. The roles of the solution complex, pink precipitate and chloroplatinic acid in the reduction process were then investigated. APPARATUS The experimental work was carried out in a two-liter stainless-steel autoclave. Adetailed description of the autoclave and the auxiliary equipment used in maintaining constant temperature and pressure may be found elsewhere.= Because the stainless steel was corroded, and also because it acted as a hydrogena-tion catalyst, an all-glass liner was fabricated such that the solution came only into contact with flame-polished pyrex glass. EXPERIMENTAL PROCEDURE The solutions used in the experimental work were prepared by dissolving reagent grade chemicals in distilled water. Although variation of the brand of ammonium acetate appeared to have no effect on the experimental results, CoSO, 7H O from the J. T. Baker Chemical Co. of Phillipsburg, N. J.,was found to give faster reductions than that prepared by Allied Chemical and Dye Corp., N. Y. The former was used throughout the course of the experimental work and was weighed up at the outset of each experiment. The ammonium acetate was dissolved to form a 6M stock solution, which was stored under refrigeration. A 10 pct solution of chloroplatinic acid (J. T. Baker Chemical Co.) was diluted to a 1.15 x 1Q2 M stock solution, which was standardized by precipitation of K,PtCl, as outlined by Scott. The appropriate volume of the chloroplatinic acid, H,PtCl,, solution was pipetted into the clean, dry glass liner. The cobalt sulfate-ammonium acetate solution, which had previously been saturated with

Jan 1, 1962

By Larry Kaufman

A useful method for estimating the entropy of NaCl type compounds has been developed by combining the Debye theory of specific heat with the Lindemann formula. This method pemnits calculation of the entropy from a knowledge of the atomic weight, atomic volume, and melting point of the compound. Comparison of the calculated and observed entropies of 35 NaCl type compounds over a wide temperature range yields good agreement thus establishing the usefulness of the method. Application of the method to other crystal types is also discussed. KUBASCHEWSKI~ has suggested a useful method of estimating the enthalpy of formation of inter-metallic compounds from a knowledge of the crystal structure, lattice parameter, and heats of sublimation of the component elements. This method is quite valuable in predicting the tendency for compound formation in a given system and is of particular value in considering systems for which no experimental data are available. In order to supplement the enthalpy calculation afforded by Kubschewski&apos;s method, it would be of value to be able to estimate the entropy of compounds so that the entropy and free energy of formation could be evaluated. Although a considerable body of such data determined by calorimetric and equilibration techniques exists at present, the difficulty of making such measurements (particularly at high temperatures) and the ever increasing number of new compounds which are of interest make the desirability of such a computational method clear. This paper deals with a method for calculating the entropy of a compound from a knowledge of the atomic weight, atomic volume, and melting point. Since these data are generally easier to determine and therefore more readily available than thermo-dynamic data, they should provide an additional tool in estimating the stability and reactivity of compounds at high temperatures. I) THE ENTROPY OF PURE METALS As a first approximation, the specific heat of a pure metal can be represented by a sum of terms where C,($/tI is the vibrational specific heat calculated on the basis of the Debye theory, lo4 TC, (0/T) is an approximation to the Cp - C, correction. T is the electronic specific heat, and Cp (p) is the magnetic specific heat. Although the Debye theory does not provide a complete description of the vibrational specific heat, i.e., the Debye temperature 0 is not a constant, it does provide a good approximation when used properly. Blackman6&apos;7 has written several reviews on this subject discussing the different values of 0 determined by various methods (specific heat, X-rays, elastic constants, electrical resistivity, and so forth), as well as the observed temperature dependence of 0 with T. In the present case the 0 in Eq. [I] naturally refers to the specific heat 0. The variation of Debye 0 (as determined from specific heat measurements) with temperature is observed to exhibit its most radical behavior at very low temperatures. At higher temperatures the 8 values are observed to become more nearly constant. Blackman6&apos;7 has presented the variation of 0 with temperature for several metals. His tabulation is reproduced in Table I. Reference to Table I shows that above a certain temperature level, 0 remains fairly constant. The value of 0 which is most useful in computing the specific heat, and hence the entropy, is the value of 0 in the range 0/6 « T « 0. In 1910, Lindemann&apos; suggested a relation for estimating Debye 0 values. According to this formula, where V is the atomic volume, T is the melting point in &apos;K, M is the atomic weight, and CL is a constant. Mott and Jones9 present this formula and state that there is at present no satisfactory theoretical explanation, but that it does have an empirical basis. By using the valuesof 0 in Table I along with known1&apos; values of M, T, and the molar volume VM, where the Lindemann constant can be evaluated. This

Jan 1, 1962

By Gerald W. Elger

This report compares the quality of zirconium metal prepared by batch reduction of zirconium tetrachloride by (1) sodium, (2) magnesium, and (3) mixtures of sodium and magnesium. Criteria for quality are based on chemical analyses and hardness testing of zirconium arc-melted from sponge. The best quality zirconium with respect to low oxygen content and hardness numbers was prepared by reaction of zirconium tetrachloride with a mixture of sodium and magnesium. It was found that this reaction could be successfully carried out by two methods: (1) addition of sodium and magnesium before the initial reaction and (2) periodic injection of sodium during reaction of zirconium tetrachloride with magnesium. The largest quantity of metal was found to be recovered from experiments in which a mixture of sodium and magnesium was used. Magnesium appeared to be a better reductant than sodium because magnesium-reduced zirconium contained less oxygen and exhibited lower hardness numbers than sodium-reduced metal.

Jan 1, 1962

By A. T. Aldred

HIS note reports the existence of several new scandium intermetallic compounds of the A2B and AB stoichiometries where the A element is scandium and the B element is from group VIII or IB of the periodic table. Alloys were arc melted from high-purity materials using 2-g charges. Typical lot analyses for the materials used are given in Table I. Chemical analyses were not made on the alloys as there was little or no weight loss on melting. After annealing the specimens for 14 days at 600°C and water quenching, metallographic and X-ray techniques were used to determine the occurrence of the various phases. Table II lists the relevant data for the A2B phases. The Ti2Ni structure,2 has ninety-six atoms in a face-centered cubic cell, whilst the Al2Cu structure is body-centered tetragonal.3 The occurrence and stability of the various A2B type phases in transition metal alloy systems has recently been considered by Nevitt.4 The Ti2 Ni-type phases occur over a relatively narrow range of radius ratios from 1.14-1.26 with A partners mainly from the titanium group and B partners predominantly from the cobalt group. This suggests that both a favorable relative size of the atoms and a favorable electron concentration are necessary conditions for the existence of this structure type. A12Cu-type phases involving Ti group elements as A partners are formed with B partners from the cobalt and nickel groups, predominantly the latter, and have a higher radius ratio (1.27-1.29) than the Ti2Ni-type phases. The occurrence of both Sc2Pd and Sc2Co can be rationalized in terms of these considerations but SczNi is anomalous because of its high radius ratio. The radius ratios are calculated from the Goldschmidt CN12 radii and it might be postulated that the scandium atom is reduced in size in the compound. Unfortunately the apparent atomic size of scandium in the compound cannot be calculated from a knowledge of the structure and lattice dimensions. The crystal structure of the Sc2Au compound could not be identified from the powder diffraction pattern, but it is interesting to note that it is isostructural with a series of A2Au phases where A is a rare earth element.5 Pertinent information concerning the AB phases found in this investigation is given in Table 111. All the phases have the ordered bcc CsCl structure. The occurrence and stability of CsC1-type phases have recently been discussed by Dwight,7 who concludes that the relative sizes of the atoms do not appear to be a controlling factor (the radius ratios of all the known phases vary between 0.985 and 1.439) but that the occurrence of the phase is predominantly dependent on the relative positions of the A and B partners in the periodic table. As a measure of the stability of a given CsCl phase it has been customary to define a lattice contraction on alloying, DAB — dAB, where DAB is the AB interatomic spacing as calculated from the Goldschmidt CN8 radii and dAB is the AB interatomic distance in the compound (= v3/2 ao). Values of the parameter DscB -dScB for the compounds found in this investigation are given in column 5 of Table III and are plotted in Fig. 1. If the lattice contraction does in fact reflect the stability of a phase then Fig. 1 shows two very interesting trends when the position of the B partner in the periodic table is considered. Firstly, within any given group the stability increases in order on going from the first to third long period. Secondly, within any given period the stability increases in order as the B partner is taken from the copper, nickel, and cobalt groups. In the case of the second long period, the lattice contraction reaches a maximum at ScRh and then decreases to ScRu. The same trend could

Jan 1, 1962

By C. S. Boland

The Copper Range Company&apos;s mining properties are located in the Upper Penisula of Michigan. (Fig.). Early work indicated the presence of copper ore in a bedded deposit, confined to the base of the Upper Keweenawan Nonesuch shale, and exploitation of this deposit on a portion of the Company&apos;s property was undertaken by White Pine Copper Company. Diamond drilling of the White Pine orebody indicated that a major fault pattern terminated the values to the South-west. Further drilling Southwest of the fault zone proved a downward displacement of the ore bearing horizon some 1,500 feet and a lateral displacement of approximately 4,000 feet; and in this area an ore deposit was outlined in a large asymmetrical syncline locally plunging to the South-west. (Figs. 2 and 3)

Jan 1, 1962

By John C. Sawyer

A brief review is given to show that catastrophic oxidation of stainless steel in the presence of lead oxide is similar in many respects to catastrophic oxidation as caused by MoO3 and V2O5, Experimental data are presented to show that lead oxide accelerates the normal oxidation process of stainless steel by chemically altering the normally protective oxide film formed on the base metal. Data are given to show that similar reactions occur during oxidation of stainless steel in the presence of MOO3,and V2O5. THE mechanism by which pure metals oxidize at high temperatures has been the subject of intensive research for many years and much has been accomplished towards understanding the processes involved. The mechanisms by which alloys oxidize have also been investigated, but due partly to the fewer number of investigations and partly to the complexity of the oxide systems present, available knowledge is not as extensive as with pure metals. When oxidation processes are further complicated by atmospheres contaminated with sulfide, halide, or oxide vapors, the knowledge of fundamentals becomes meager or altogether lacking. Thus, it is not surprising to find that the catastrophic oxidation of stainless steels in metal oxide vapors of MOO, and V2O5 is not a well understood phenomenon despite the fact that a number of investigations have been undertaken. The literature in dealing with the subject of catastrophic oxidation is primarily concerned with the effects of MOO3 and V2O5, but does mention that other metal oxide vapors, one of which is lead oxide, appear to promote a similar type of accelerated oxidation. While this latter effect is virtually unknown, the deleterious effect of lead oxide is of considerable commercial importance, as it is believed to be one of the fundamental reasons for exhaust-valve failure in gasoline engines. For this reason studies have been in progress for many years attempting to better understand the mechanism involved. Modern exhaust-valve alloys"2containing 20 to 25 pct Cr plus nickel and/or manganese are in effect high-grade austenitic stainless steels exhibiting ex- cellent oxidation resistance in air at exhaust valve operating temperatures of 1100° to 1700°F; yet these same alloys are prone to corrode during engine service because of the conditions attending their operation. These conditions are such that the valves become coated with deposits of complex lead compounds mainly derived from gasoline additives of tetraethyllead, ethylene dibromide, and ethylene dichloride. Literature searches3-7 and discussions with various investigators show that considerable difference of opinion exists as to the nature of the lead-bearing deposits found on the surface of exhaust valves and the atmospheres to which they are subjected; yet, all seem to generally agree that corrosion, a gradual transformation of alloy to nonmetallic products of corrosion, is a consequence of the presence of lead compounds. This majority opinion seems to be substantiated by laboratory engine tests which show that corrosion does not occur to any appreciable extent when lead-free fuels are used. The first observations of catastrophic oxidation reported in the literature were probably made by pfeil,8 but it was Leslie and Fontana9 who undertook the first detailed study of the phenomenon. Their work was chiefly centered on the acceleration of oxidation which took place when stainless steels containing more than 3 pct Mo were heated in air with restricted circulation. These investigators reported that the presence of other oxides near the surface would further accelerate the rapid oxidation which occurred. While they recognized that the effect was attributable to the presence of molybdenum, it was Rathenau and Meijering" who emphasized the fact that the presence of molybdenum in the alloy was incidental to the presence of MOO3 vapor in the atmosphere surrounding the specimens. Evans,11 as well as Cunningham and Brasunas 12 studied similar

Jan 1, 1962

By William J. Campbell

Evaluation by the Bureau of Mines of published expansion values for magnesium oxide shows significant variation in values, which may be attributed to sample variables, experimental errors, or systematic differences between measuring techniques. To eliminate the sample variable in measuring expansion, thermal expansion characteristics of a high-purity polycrystalline magnesium oxide were determined by 21 cooperating laboratories using one or more of the following techniques; X-ray camera, X-ray diffractometer, dilatometer, interferometer, and telemicroscope. All expansion values were corrected by the author to a single reference temperature of 25° C. Linear expansion was expressed as a power series in the form of the following equation. Expansion (percent) = [[ A + B (?t) + C (?t)2] ?t 104] The constants, A, B, and C, were determined by least square techniques for X-ray camera, X-ray diffractometer, and dilatometer data separately, and for combined data of all five techniques. Expansion values are tabulated from 26° C. to 1,400° C. in 2° C. intervals using constants derived from X-ray camera data. Below approximately 500° C., expansion values obtained by dilatometric and interferometric methods are significantly lower than those by X-ray methods; above 500° C., this bias decreases rapidly. Comparison of results within methods showed the least variance for X-ray camera results; dilatometer and X-ray diffractometer results have about the same variance. The average deviations, in percent, between observed and calculated expansion values among methods were approximately 10 percent from 100°C. to 300°C., 5 percent from 300°C. to 500°C., and 2 percent from 500°C. to 1,400°C. Maximum deviations were approximately twice as large in most instances.

Jan 1, 1962

By E. J. Yoder, N. B. Aughenbaugh, R. B. Johnson

Mineral aggregates experience degradation during field and laboratory compaction. Reduction in the aggregate size is accomplished by abrasion of the particle edges and fracturing of individual pieces which have become overstressed. Little is known of the factors that govern the amount of breakdown experienced for a given situation. A field study was made of the factors affecting aggregate breakdown under compaction using three carbonate aggregates of different physical properties. The preliminary results indicate that rock type, compactive effort, gradation, and thickness of compactive layer are factors which exert the greatest influence. Mineral aggregates experience a mechanical breakdown of some of the aggregate pieces into smaller fragments during any compaction process, whether in the field or laboratory. This phenomenon occurs as abrasion of the sharp edges during movement and reorientation of the particles in densifying and/or as granulation and fracturing of those pieces which have become overstressed. Two types of aggregate breakdown occur in the field. These may be classed in a general category of aggregate degradation.* One occurs during the con- * Aggregate degradation has been defined in many different ways. For this paper it is considered as any breakdown of larger particles into smaller ones, whether mechanical or chemical. struction period and is related to the densification of the aggregate body from a loose state to a relatively dense mass by heavy compaction equipment. This type is almost entirely a mechanical action. The other occurs after the construction period when the roadway has been put into use. This in-service breakdown is; a different phenomenon from the breakdown during construction in the sense that it combines mechanical with chemical changes. Time becomes an important consideration that may cause subordinate factors in construction degradation to develop into principal ones for in-service breakdown. Breakdown of aggregates in service has been extensively studied by investigators from the northwestern

Jan 1, 1962

By A. M. Gaudin

In the first place, let me thank you for inviting me to appear before you today to speak to you on "Mineral Industry Problems - Present and Future". It is a distinguished honor for me to have this opportunity, and I am highly appreciative of this distinction. The beautiful surroundings of Gatlinburg and the pleasantness of a summer occasion are a wonderful tonic for all of us, yet they should not blind us to the seriousness of our Industry&apos;s problems No doubt, because of my past appearances before members of the Society of Mining Engineers, at which I discussed wholly scientific topics, or research in the Applied Sciences, you may be expecting me to revert to these subjects. But I intend to venture in a field that is new to me, yet old to all of us, the field of Economics.

Jan 1, 1962

By Robert D. Pehlke, Arden L. Bement

A mass transfer coefficient for the removal of hydrogen from liquid aluminum by inert flush degassing has been determined experimentally at 700°C. A mathematical model has been derived, assuming transport control, which adequately describes the experimental data. The removal of hydrogen is shown to increase with decreasing bubble size, and with increasing flow of flushing gas. The presence of hydrogen in liquid metals in amounts which exceed the solid solubility at one atmosphere hydrogen pressure is highly undesirable, causing unsound ingots or castings, or resulting in difficulties during further fabrication. The removal of hydrogen from liquid metals can be accomplished by several methods, the principal two being vacuum treating and inert flush degassing. The design of a process involving either of these techniques is based on the mass transfer coefficient for hydrogen between the liquid metal and a hydrogen-dilute gas phase. In an effort to extend our knowledge in this area, an investigation of the rate of removal of hydrogen from liquid metals by inert gas flushing was undertaken. In view of the difficulties encountered with gas porosity in the casting of aluminum and aluminum alloys, and because of certain experimental advantages, liquid aluminum was selected for the study. PREVIOUS INVESTIGATIONS The removal of gases from liquid metals, particularly steel, has received considerable attention in recent years, The first definitive work of a theoretical nature was presented by Geller1 who considered the case where equilibrium exists between purging gases and metal bath during flushing, and also deviations from this ideal case. Hulme2 has surveyed a number of experimental studies and discussed some of the practical limitations of removing dissolved gases from molten metals. More recently a number of studies have been reported on degassing of steel melts by flushing with an inert gas.3&apos;4 Considerable work has also been reported on aqueous and organic liquid-gas systems, and an excellent summary prepared by Hovis.5 The treatment of liquid aluminum by a flushing gas to remove dissolved hydrogen has been known for several decades.6 A number of gases have been used for this purpose, including nitrogen, argon, and chlorine, or mixtures of these gases. Tikkanen and Erkko7 have studied the relative density changes of aluminum castings poured from melts degassed with chlorine, nitrogen, and mixtures of the two gases. Their

Jan 1, 1962

By F. M. Yans, A. D. Donaldson, A. R. Kaufmann

Beryllium was mixed by powder. metallurgical techniques with copper, nickel, iron, and chromium, respectively, to form beryllium -rich binary alloys which Mere then extyuded and rolled transtverse to the extrusion direction. The effect of each alloying element was determined by tensile testing. In solid solution, small amounts of iron and nickel had an embrittling effect, while copper in solution increased the strength but had no effect on ductility. The effect of chromium was complicated and not readily explainable. Observations concerning the planes and modes of fracture were made. BERYLLIUM possesses some very attractive properties for general design applications, especially its strength to weight ratio which is approximately twice that of aluminum and three times that of stainless steel. Equally significant, however, is its combination of high moduli , high strength (approximately 70,000 psi tension and 40,000 psi shear), and low density (0.0658 Ib per in.3), which has made it a potentially important structural material for use in high-speed aircraft and missiles. The main attractions of beryllium are most marked when compared to other constructional alloys now in use. For example, while its density is approximateiy that of magnesium, its modulus of elasticity is approximately seven times that of magnesium, three times that of titanium, four times that of aluminum, and 1 1/3 times that of steel. Furthermore, its relatively high strength and high melting temperature permit design for service temperatures to about 1100°F. It is felt by the aircraft industry in general,&apos; that the high cost of beryllium can easily be amortized by the savings in fuel costs, and increases in aircraft payload and range. The only factor which has prevented the use of the metal in structural applications is its lack of sufficient ductility. It is this property that has retarded the development and utilization of beryllium. Beryllium&apos;s modes of deformation, Fig. 1 indicate that the main fracture planes at room temperature in a randomly oriented sample are the (0001) basal planes; the (1150) prism planes are the planes of secondary fracture.&apos; Klein, Macres, Woodard, and Greenspan3 obtained elongations of up to 40 pct in beryllium sheet rolled above 700°C when the (0001) basal planes were oriented parallel to the plane of the sheet (see Fig. 2).

Jan 1, 1962