By Gary A. Kingston

Rolled steel, steel forgings, and steel castings in the Pacific Northwest (Washington and Oregon) are produced principally in the Seattle, Wash., and Portland, Oreg., metropolitan areas. Steel-mill products are rolled from carbon and some alloy &eels by three companies into shapes such as reinforcing bar, rods, rounds, squares, flats, and hot-rolled strips; structural shapes, - such as angles, channels, and I-beams, also are rolled. Carbon and alloy steel ingots are poured and forged at a Seattle plant into ship shafting, drive shafts, billets, slabs, bars, rings, hooks, and other items. Static, shell, investment, and centrifugal castings are produced at 19 steel foundries in a wide range of steel specifications. All Pacific Northwest steel output is based on remelting steel scrap. Local iron ore might be used in the future to supplement steel scrap as a metal source. Ore reduction would probably be achieved by methods other than the blast furnace. Current melt-shop practice and problems are basically the same in Pacific Northwest steel plants as in cold-melt shops in other parts of the country. Quality steel production is receiving more emphasis in this region with the installation of modern analytical equipment and vacuum pouring and melting facilities.

Jan 1, 1962

By J. H. Gwynne

[ ]

Jan 1, 1962

By R. M. Waterstrat

The phases occurring in the V-Mn system were studied by means of X-yay diffraction and metallo-paphic techniques, using are-melted alloy specimens annealed in the temperature range 800° to 1150°C and quenched. The bcc solid solution extends at 1250°C all the way from vanadium to 6-manganese. Below 1050°C the a-phase is formed, and the terminal a-manganese phase is stabilized up to about 900°C by vanadium in solid solution. IN the only previous general survey of the V-Mn system Cornelius, Bungardt and Schiedtl reported the existence of three intermediate phases corresponding to the approximate compositions VMn,, VMn, and V5Mn. The phase VMn8 has recently been identified as a o phase2 but the alloy VMn was found to have a bcc structure2 corresponding apparently to the vanadium solid solution rather than to the large cubic unit cell reported by Cornelius et al. 1 Subsequent work by Rostoker and Yamamoto3 has shown that the vanadium-base bcc solid solution extends to at least 15 pct Mn at 900°C. An alloy corresponding to the composition VMn, was examined by Elliott,4 who reported that the as-cast sample as well as samples annealed at 1200o and 1300°C had bcc structures, but that annealing at 1000°, 800") and 600°C produced two phases. One of these phases was apparently the bcc solid solution and the other resembled the o phase structure. Hellawell and Hume-Rothery5 established the phase relationships in manganese-rich alloys above 1000°C, and showed that the o phase in this system is replaced by the 6 Mn (bcc) solid solution at temperatures above 1050°C. These results suggest that a continuous bcc solid solution may exist above 1050°C between vanadium and 6 Mn. The present investigation was undertaken in order to develop more complete information in regard to this system. EXPERIMENTAL METHODS The alloys used in the present work were prepared by arc-melting electrolytic manganese having a minimum purity of 99.9 pct and vanadium lumps with a purity of 99.7 pct. The major impurities present in these metals were carbon, nitrogen, and oxygen and this would account for the small percentage of nonmetallic inclusions observed metal-lographically. The arc-melting was at first performed under a helium atmosphere and it was necessary to keep the melting times as short as possible in order to minimize the loss of manganese by vaporization. It was later found that the evaporation of manganese was considerably reduced when the melting was done under argon atmosphere. The final composition of each alloy was calculated by assuming that the total weight loss during melting was due to evaporation of manganese. Compositions which were calculated in this manner agreed reasonably well with the results of chemical analysis, as shown in Table I. Spectrographic analysis revealed the presence of contamination by tungsten, but in no case was the percentage of tungsten greater then 0.4 at. pct. The specimens were in each case broken in half and the fractured section was examined visually and microscopically for evidence of inhomogeneity. Each specimen was homogenized at temperatures near l100°C, as shown in Table I. After this treatment most specimens consisted of large columnar grains of the bcc vanadium solid solution. The etchant used in most of the metallographic work consisted of 20 pct nitric acid, 20 pct hydro-flouric acid, and 60 pct glycerine. It was found that this etchant would clearly delineate the phases present in these alloys although it does not produce any striking contrast between the phases. For certain manganese-rich alloys, a 1 pct aqueous solution of nitric acid was used. This etchant gave a brown color to the a-manganese phase, whereas the o phase was virtually unattacked and appeared very light as shown in Fig. 1. The etchants used by Cornelius et a1.l were found to produce spurious effects in some of these alloys. In particular, the vanadium-rich alloys etched in hot sulfuric acid often appeared to consist of two phases when both X-ray diffraction and etching with the glycerine-acid mixture indicated the presence of single phase bcc solid solution. A few percent of what appears to be an oxide or nitride phase was found at the grain boundaries and in the interior of the grains, especially in the vanadium-rich alloys. All alloys were annealed in sealed silica tubes containing 1 atm of pure argon and these tubes were then quenched in cold water. Although some manganese loss occurred during annealing, the loss seemed to be confined to the surface of the speci-

Jan 1, 1962

By Wilbur I. Duvall

In a review of so 40 papers on damage to residential structures resulting from blasting, only 3 were found that present data on the observed amplitude and frequency of the vibration levels produced by blasting together with an observed degree of damage to a residential structure. The data from these three reports have been analyzed statistically to determine if one of the quantities, displacement, velocity, or acceleration, is more reliable than the others for estimating the degree of damage to a residential structure. From this analysis the conclusion is drawn that a given degree of damage to a structure is most closely related to the magnitude of the particle velocity of the wave motion passing thru the earth at the structure location. On the average, only minor damage it observed for peak particle velocities of 5.4 inches per second, and major damage is observed for peak particle velocities of 7.6 inches per second. When the spread of the data is taken into consideration, the following statement can be made: Wave motions that have a peak particle velocity in excess of 2 inches per second have a fair probability of producing some damage to structures, whereas wave motions that have a peak velocity less than 2 inches per second have a very low probability of causing any damage. Therefore, the recommendation is made that vibration levels in the vicinity of residential structures should be maintained below a peat particle velocity of 2 inches per second. The above criterion for safe blasting is considered to hold over a wide variety of soil and rock conditions because the original data were obtained for a wide range of soil and rock conditions and on various types of residential structures. INTRODUCTION Ever since explosives were discovered and developed for mining purposes, there has existed the problem of what effects the air and ground vibrations resulting from blasting have on structures of various types. This problem is

Jan 1, 1962

By R. D. Fisher, A. G. Metcalfe, F. A. Crossley

AN investigation of the application of magnetic stirring to the consumable arc melting of aluminum and nickel demonstrated that grain refinement could be obtained when there was sufficient stirring force. Also, it was found that grain refinement could be obtained in aluminum by alternately reversing the polarity of the current through the magnetic stirring coil. The effect of the latter was to periodically reverse the direction of rotation of the molten metal.' Because of their promise, these findings were applied to conventionally cast aluminum. Shortly after this work was begun, Kondic2 reported experiments in which aluminum cast with 40° C (72° F) of superheat exhibited a grain size of 10 to 20 grains per cm2. When interrupted rotation was applied during solidification by mechanical means, a grain size of 800 to 1000 grains per cm2 was obtained. Magnetic Stirring Applied to Conventional Casting— The applicability of magnetic stirring to producing grain refinement in conventionally cast metal was evaluated in the following way. Three pounds of aluminum were cast into a clay-bonded graphite mold. The mold was surrounded by a magnetic stirring coil of 1000 turns. A direct current of 200 amp was passed through the casting by means of a graphite electrode which was immersed from the top. A current of 5 amp was passed through the stirring coil. The aluminum (1100 or 25) was superheated to 1600° F (871° C) and fluxed by passing chlorine gas through the melt for 2 min prior to casting. Two additional castings were made for comparison: 1) a conventional casting of metal superheated to 1600° F and 2) a similar casting through which 200-amp current was passed during solidification, but without current in the magnetic coil. Macrosections of these three ingots are shown in Fig. 1. Very remarkable grain refinement resulted in the magnetically stirred casting. It may be noted that the casting through which 200-amp current was passed has a coarser structure than the conventional casting. It would appear that this is due to the additional heat input generated by the current to the former casting. Mechanical Rotation Applied to Conventional Casting—A casting temperature of 1600° F was used throughout. Some 1 1/2 -lb castings rotated at 150 rpm were predominantly columnar with small areas of coarse, equiaxed grains close to the lower mold wall. Following these, a series of 3-lb castings was made. Macrosections of these ingots are shown in Fig. 2. The imposed rotational speed was 250 rpm. Turbulence or acceleration in the solidifying liquid was the significant factor. Fine grain size resulted in the material solidified during the period of acceleration of the liquid to the imposed rotational speed. When uniform rotational motion was achieved, the grain structure reverted to columnar. The final casting shown in the lower right-

Jan 1, 1962

By Carl G. Hogberg

To the casual observer there is probably no simpler appearing operation in the mineral industry than a limestone quarry. It might seem that the entire operation - from the drilling, blasting, and loading of the stone, its transport to a mill for crushing, washing and sizing, to loading into boats, railroad cars, or trucks for delivery to customers - can be comprehended at a glance. But no first impression could be more misleading. It is one of the purposes of this presentation to sketch the broad outlines of the extensive limestone industry in the United States which, measured in terms of volume of production since the end of World War II, has grown almost 300 per cent to a national level in 1957 of 384 million net tons.1 Another objective will be to discuss in more detail this industry in the State of Michigan. For this latter purpose, the Michigan Limestone Division plants at Calcite and at Cedarville will be used as examples. These descriptions will, we believe, show that the limestone business has complexities to match its size.

Jan 1, 1962

By Erhard Hornbogen

Twins were propagated into large, well-annealed crystals of a, iron-phosphorous and a, iron-molybdenum solid solutions. Strain fields caused by interaction of these twins were made visible by precipitation. These strain fields can be explained by assuming that transmitted and reflected plastic waves are created when a twin strikes an obstacle with high velocity. The twin front itself can be regarded as a shear wave that may be able to develop a one-dimensional shock front. The occurrence of {WO} fracture by the reflected stress is also discussed. The described effects were not found when twins propagated at lout velocity into disturbed crystals, for example, into crystals previously deformed by slip. DEFORMATION twinning leads to shearing of a crystal lattice under external load. The shear appears to be homogeneous over a large number of crystal layers. In a iron, shear occurs on the (112) planes and in the <1ll> directions. The formation of a twin proceeds by the movement of partial dislocations that change the stacking at the twinning plane.l, In the bcc lattice, this partial dislocation can be created by dissociation of a sessile a/2[111] dislocation that lies in the (112) plane: Cottrell and Bilby&apos;s spiral mechanism can explain the homogeneous shear, but has not been proven experimentally. Nevertheless, this mechanism can explain the possible high velocity of formation of a twin. In Cottrell and Bilby&apos;s model, as in other models of twinning or phase transformation, a much higher energy is required to spread the first stacking fault than to add new layers by further movement of the partial dislocations. The dislocations will therefore become accelerated proportional to the difference between the stress, tN, to nucleate and tp to propagate the twin. It has been assumed3,4 that tn is the stress required to make two partial dislocations of apposite sign pass for the first time. After the first layer of new stacking has been formed, the maximum stress is TN=Gb/4pd where G is the shear modulus, b is the Burgers vector of the partial dislocation, and d is their perpendicular spacing so that the amount of shear is S = b/d. From this formula, a value of 25 kg per mm2 has been estimated for twinning in Zn3. The measured values are smaller, but local internal stresses may help to provide the necessary stress. For a iron, a higher value can be expected, mainly due to the higher value of G. That agrees with the observation that "burst" twinning occurs if the yield strength is in-

Jan 1, 1962

By Paul F. Sikora, John W. Weeton, Philip A. Clarkin

Effects of variations in carbon content and micro-structure on the stress-rupture properties of a liquid-phase-sirztered, Izeut-resistunt alloy were studied. Using the powder rnetallurgy technique, specimens could be produced having stress-rupture profierties equivalent to or better than those of the alloy in wrought form. In addition, sintered specimens were easily hot worked even when carbon contents were as high as I pct. Correlations between stress-rupture properties and micro structure were obtained in some cases. IT is well known that many alloys used in high-temperature service are quite complex both from the standpoint of chemical composition and microstruc-ture. During the development of these alloys their complexity has in some cases led to treatment schedules which, while practical, often do not fully utilize available alloying elements. For example, in some alloys, massive carbides that form during ingot practice may never be dissolved by reasonable solution treatments and therefore are unavailable for subsequent precipitation hardening, Ref. 1. This investigation was undertaken to determine whether the powder metallurgy method of consolidation might provide distinct advantages over the conventional melting method. First, segregation of alloying elements might be eliminated or reduced and thus a more efficient use of these elements obtained. Second, the structures produced in powder specimens might differ considerably from those normally seen in castings, which would perhaps result in better response to subsequent mechanical or thermal treatments. If these results could be achieved, it was felt that both forgeability and stress-rupture properties might be improved. The alloy used in this investigation was S-816 produced by powder metallurgy methods. The influence of carbon content over the range of 0.1 to 1.0 wt pct was studied for the alloy in the as-sintered condition and after three additional treatments involving heat treatment, hot swaging, and combinations thereof. EXPERIMENTAL Standard S-816 has the composition shown in Table I. It is a cobalt-base alloy having a nominal carbon content of 0.4 pct and is classified as a precipitation-hardening alloy. This alloy was chosen because it is representative of a class of heat-resistant alloys and because adequate information was available concerning its response to various treatments and its subsequent properties. For this study, -100 mesh alloy powder having essentially the same composition as shown in Table I but without the 0.4 pct C was used. Desired carbon variations, achieved by wet mixing the alloy powder with graphite, ranged from 0.1 to 1.0 wt pct. Specimens were hydrostatically pressed and then sintered in vacuum by slowly heating until incipient melting was observed. Sintering this way gave a liquid phase in the interstices of the powder particles and achieved reasonably high densities. The average density of as-sintered specimens was about 95 pct of wrought alloy density. In order to obtain various microstructures, some specimens were heat treated (solution treated for 24 hr at 2150°F, water quenched; aged 16 hr at 1400°F, air cooled); others were hot swaged at 2150 o F (50 pct reduction in area), while still others were hot swaged (50 pct reduction in area) and then given the above heat treatment. During hot swaging it was observed that forgeability was quite good even when specimens contained as much as 1.0 pct C. Specimens were evaluated by stress-rupture test-

Jan 1, 1962

By Carl F. Lutz, Robert F. Mehl

A layer of brass was formed on 0 brass using a vapor-solid reaction technique. The variation in composition with distance within the phase layer and across the a -ß interface was determined by an electron probe. The diffusivities were calculated as a function of concentration; the diffusion coefficient in brass was found to change by a factor of twenty-five over a compositional range of 8 at. pct. An explanation is proposed to account for the large change in the diffusivity, based on possible stresses in the diffusion zone; it is suggested that the concentration dependence of the thermodynamic factor might decrease the activation energy with increasing zinc content. ALTHOUGH the body of data on diffusion coefficients (D- values) in terminal solid solutions and in isomorphous systems is quite large, there is but little quantitative information for intermediate alloy phases. This paper recounts measurements of D-values for the ? phase in the Cu-Zn system. The experimental method employed consists in the forming of alloy layers and determining and analyzing the concentration-distance (c-x) curve. The experimental method employed could have been applied to several systems; the Cu-Zn system was chosen because the D-values in the a and ß phases are well known, and can thus be used for purposes of comparison. The rates of growth, of intermediate alloy layers are known for a number of systems. In nearly all cases the thickness varies parabolically with time, as to be expected if the rate of growth is controlled by the D-values. In a few cases, nonparabolic behavior has been noted.1 Nonparabolic growth may be the result of a) a variation of the composition at the phase interface with time, b) interface-controlled kinetics, c) short diffusion times coupled with long vacancy lifetimes (in vacancy diffusion),2 and d) crystal reorientation during diffusion in anisotropic systems.3 In the Al-Ni system4 and in the Al-u5 system parabolic growth kinetics are slowly approached after an initial transient period. In general those phases stable at a given temperature in a system A-B appear as separate phase layers when A and B are put in contact and given a diffusion he at-treatment. In most cases the compositions at the interface of adjacent phase layers are those read from the phase diagrams for the termini of the respective phases. This discontinuity in concentration is taken as independent of time, and the growth of one phase at the expense of another is assumed to be independent of interface kinetics, i.e., the rate of interface movement is controlled by volume diffusion in the phases concerned. wagner6 has given many solutions for multi-phase diffusion processes, assuming that the chemical diffusion coefficient, D, is independent of concentration, as have others. Jost7 has pointed out that the familiar Boltzmann-Matano solution is as valid for a (c-x) curve exhibiting concentration discontinuities at phase boundaries as for the usual single-phase case. Heumann and associates8,9 have applied this solution to the multi-phase case, but lacking concentration data within the several layers were forced to assume linear concentration gradients, thus calculating only average D-values. The purposes of the present study were: 1) to determine the dependence of D on concentration, 2) to calculate the intrinsic diffusion coefficients D?Cu and D?Zn, 3) to establish the time-law for the movement of the interface, 4) to determine the concentration limits at the ß-? interface, and, 5) to attempt to clarify the mechanism of diffusion. EXPERIMENTAL PROCEDURE The ? phase is exceedingly brittle; conventional solid couples and conventional sectioning methods were thus inapplicable. Vapor-solid couples were accordingly employed. Unfortunately the equilibrium vapor pressures of Zn for the ? phase are unknown; to escape this awkwardness, samples were enclosed in a capsule containing powder of an alloy of known composition, sufficiently large in quantity as to be effectively an infinite source, maintaining the concentration of Zn at the sample surface constant with time. The sources of Zn-vapor which can be employed in reaction with Cu, or a brass, or ß brass, to form a layer of ? brass satisfactorily wide in concentration range, are alloys of the phases ?, or ? + E or ? + d (depending on the temperature).

Jan 1, 1962

By F. B. Petermann

The Bureau of Mines conducted electric furnace smelting tests on sintered flotation concentrate and siliceous log-washed are. The flotation concentrate was derived from the Maggie Canyon deposit of the Artillery Mountains area, Mohave County, Ariz., and contained, before sintering, 35.6 percent Mil and 19.4 percent Si02 + A1203. The log-washed ore was from the McGregor deposit of the Artillery Mountains area, Mohave County, Ariz., and contained 31.2 to 33.6 percent Mil, 19.5 to 27.6 percent Si02 + A1203, and 2.5 percent Pb. This work was undertaken to determine the most effective smelting technique for producing standard products from such nonspecification ore and concentrates. The objective was to collect data, using a small furnace, which would be reasonably accurate and permit extrapolation to large-scale practice for comparing with results on specification-grade are.

Jan 1, 1962

By J. B. Cohen, B. W. Howlett, M. B. Bever

The partial molar heats of solution at infinite dilution in tin of aluminum at 300° and 350°C and of gallium, indium, and thallium at 240°, 300°, and 350°C have been measured by tin solution calori-metry. Aluminum, gallium, and thallium are endo-thermic on solution; indium is exothermic. Any temperature dependence of the heats of solution lies within the experimental scatter. Over the dilute ranges investigated, only aluminum has a measurable change in its heat of solution with composition. HEATS of solution of one element in another reflect the interaction between them. The investigation of partial molar heats of solution in dilute alloys is of particular interest as the properties of the solvent are altered to only a limited extent by the presence of the solute and also as the interaction between solute atoms is small. When the heats of solution of a related series of elements in a solvent are known, a systematic comparison may be made. In the investigation reported here, the partial molar heats of solution of the Group III elements aluminum, gallium, indium, and thallium in dilute solution in tin were measured. This work follows an investigation of the heats of solution in tin of the Group IB elements.&apos; EXPERIMENTAL PROCEDURES Materials. Samples of gallium, indium, and thallium were obtained from Johnson, Mathey and Co., Ltd. Indium and thallium were supplied as wire, 1.6 mm in diam; gallium was in the form of irregular pieces. The supplier reported the following minimum purities: gallium—99.95 pct; indium—99.99 pct; thallium—99.99 pct. The aluminum, obtained from Alcoa Research Laboratories, was reported to be 99.995 pct pure. The tin was supplied by Baker and Co., Inc.; the reported analysis indicated a tin content of at least 99.96 pct with lead as principal impurity. Calorimeter. this description will cover only the essential features of the calorimeter with special attention to modifications made since an earlier description was published.&apos; A Dewar flask containing the tin bath was held in a constant-temperature bath of a near-eutectic mixture of lithium, sodium, and potassium nitrates. This bath, which was stirred vigorously, was heated by a primary resistance winding in the container wall and by a secondary winding immersed in the salt. The voltage supplied to both windings was stabilized. The temperature of the salt bath was controlled by means of a platinum resistance thermometer in one arm of a Wheatstone bridge. The light from a mirror galvanometer in the bridge circuit fell on a photocell which controlled the current in a saturable reactor in series with the secondary winding. In this manner, the temperature of the salt bath was controlled to ±0.003°C and that of the tin bath to at least ±0.002°C. Each of these temperatures was measured by two iron-constantan thermocouples in series, coiled in a helix to minimize heat loss and immersed in the salt and tin baths in protective sheaths. The temperature of the laboratory was kept constant to ± 1°C during a run. Specimens were dropped into the tin bath from an addition arm held at O°C which was part of the cal-orimetric system. The system was evacuated to about 0.02 1 to minimize oxidation and to reduce transfer of heat. The bath was stirred by a glass stirrer introduced through a double Wilson seal. The samples were scraped clean before weighing, which was carried out as rapidly as possible. Each sample was immediately placed in the evacuated addition arm to minimize contamination. These precautions were especially necessary with aluminum. After the runs with gallium and thallium at all temperatures and with indium at 240° and 350°C (Series I) were completed and before the runs with indium at 300°C and aluminum at 300° and 350°C (Series 11) were begun the following changes were made. The shape of the Dewar flask was changed so as to result in a lower surface to volume ratio of the bath and at the same time the amount of tin was reduced from 500 to 400 g. The paddle type stirrer was replaced by a helical screw and the rate of stirring was increased to about 150 to 200 rpm.

Jan 1, 1962

By Charles Zahn

Direct mass spectrometric determination of alcohols in the presence of hydrocarbons has not been possible because of the similarity of hydrocarbon and alcohol mass spectra. Experiments have demonstrated that by converting the alcohols to their trimethylsilyl derivatives, characteristic mass spectra are obtained free of interference from hydrocarbon ion fragmentation. Hexa- methyldisilazane is the reagent selected for the conversion, An improved method of preparing the reagent is given, Mass spectrometric determination of alcohols as trimethylsilyl ethers now is not only possible without prior separation from other materials, but the range of the room-temperature mass spectrometer is also extended to include the C10 alcohol region. Water does not interfere because it is converted to hexamethyldisiloxane, which has its own distinctive mass spectral peak, Experience indicates that other compounds such as glycols, amines, and phenols probably could also be determined by mass spectrometry of their trimethylsilyl ethers. Studies on the similar detemination of phenols in coal oils have been started, When mass spectrometry is not available, gas-liquid chromatography of alcohols before and after their conversion to the trimethylsilyl derivatives probably could be performed. The preparation and properties of the trimethylsilyl derivatives of 23 alcohols, 2 glycols, 3 amines, and 1 mercaptan are detailed. INRODUCTION During investigations by the Bureau of Mines at the Pittsburgh Coal Research Center relative to the development of Fischer-Tropsch processes, complications were encountered in the mass spectrometric analysis of alcohols in hydrocarbon oils. The fragmentation peaks of the alcohols and the hydrocarbons were so similar that an accurate analysis was not possible, Since involved separation techniques are necessary to isolate alcohols from hydro-carbons for separate determinations, efforts were turned to the search for a

Jan 1, 1962

By E. T. Turkdogan, L. S. Darken

Calcium ferrite melts were equilibrated with sulfur and oxygen-bearing gases at temperatures within the range 1290°C to 1620°C. The results show that at oxygen partial pressures below 10-4 atm the sulfide-reaction occurs and at higher oxygen pressures the sulfur dissolves in the melt principally as sulfate ion. It is also observed that when the product increases, sulfate ions are converted to pyrosulfate ions and the results permit the evaluation of the pyrosulfate/sulfate ratio. It is shown that the ratio y CaSO,/rCaO increases with decreasing concentration of calcium oxide in calcium ferrite, silicate and aluminate melts. Indications are that oxy-acids, e.g. silica, alumina and ferric oxide, increase yCaS0,. A few experiments were carried out within the sul-tide range and the results are in accord with those obtained by other investigators on aluminate and silicate melts. BECAUSE of the industrial importance and theoretical interest, many investigators have studied the reactions between molten oxides, silicates or alumi-nates, and gases containing oxygen and sulfur. The early work reviewed by Schenckl and studies made by Bardenheuer and Geller2 indicates that solution of gaseous sulfur in an oxide melt resulted in the replacement of the oxide ions by the sulfide ions. Measurements made by Grant and Chipman3 on the equilibrium partition of sulfur between molten iron and complex silicate melts also demonstrated that, for a given temperature and silicate composition, the distribution of sulfur between slag and metal increased with decreasing oxygen content of the metal. Fincham and Richardson4 studied the effects of temperature and partial pressures of sulfur and oxygen on the solubility of sulfur in simple silicate and alumino-silicate melts. They observed that at oxygen partial pressures below about 10-5 atm sulfur in the gas dissolved in the melt as sulfide ions, replacing an equal number of oxide ions of the melt. At oxygen partial pressures higher than 10-3 atm, sulfur entered the melt as sulfate ions. Similar studies were made by St. Pierre and Chipman5 using calcium ferrite and calcium silico-ferrite melts. The experimental data presented in this paper were obtained in this Laboratory about 10 years ago; this is the first formal presentation although a preliminary report was given previously.6 In each of these experiments, a pure synthetic CaO-Fe2O3 melt in a platinum crucible was equilibrated with a gas mixture (SO2-O2, SO,-air, SO2-CO, or SO2-CO2-CO) at a temperature ranging from 1296°to 1620°C. The experimental technique was essentially the same as that reported by Darken and Gurry,7 the main difference being that the atmosphere in the reaction chamber contained sulfur dioxide together with oxygen, or carbon dioxide-carbon monoxide

Jan 1, 1962

By O. N. Carlson, S. A. Bradford

Discontinuous yielding in tensile tests was observed in V-O alloys in the temperature ranges of 150° to 175°C and also 350° to 400°C. The magnitude and intensity of the serrations were found to vary considerably with oxygen content. Maxima were observed in tensile and yield strengths and in the strain-hardening coefficient at the higher temperature only. The strain rate sensitivity was observed to be negative between 150° and 400°C. THIS investigation was undertaken to study the effect of oxygen on the tensile properties of iodide vanadium in the temperature range of 25o to 450°C. Brown1 observed an increase in strength between room temperature and 400°C in vanadium metal, and found that oxygen and nitrogen had a rather pronounced effect on the strength and ductility. A maximum in the tensile strength was observed by Rostoker et al.2 near 300oC and by Pugh3 around 450°C for calcium-reduced vanadium. Pugh also found a maximum in the yield strength and in the strain-hardening exponent, and minima in the elongation and strain rate sensitivity at the same temperature. Eustice and Carlson4 reported the appearance of serrations in the stress-strain curves between 140° and 180°C in iodide vanadium containing 600 ppm O. These anomalies in the mechanical properties indicate that strain aging occurs in vanadium, but the impurity or impurities responsible for the above-mentioned effects have not been identified. The phenomenon of strain aging is usually characterized by the return of the yield point after interruption of a strength test. In the temperature range where strain aging occurs, the yield and tensile strengths attain maximum values, elongation and strain rate sensitivity exhibit minima, and discontinuous yielding is generally observed in the stress-strain curve. Cottrell5, 6 has postulated that strain aging is due to the migration of solute atoms to dislocation sites to produce locking after the dislocations have broken free from their impurity atmospheres during the initial yielding. At the strain-aging temperature the process is a dynamic one in which the solute impurity atoms diffuse to the vicinity of the moving disloca- tion producing "locking" which gives rise to maxima in the tensile strength and serrations in the elongation curves. Cottrel17 has noted that discontinuous yielding in iron occurs when the diffusion coefficient of nitrogen, D, and the strain rate, i, are related by D = 10-9 €. EXPERTMENTAL PROCEDURE The vanadium metal employed in this study was prepared by the iodide refining process as described by Carlson and owen.8 A representative analysis of the vanadium used in this investigation was: 150 ppm O, <5 ppm N, <1 ppm H, 150 ppm C, 150 ppm Fe, 70 ppm Cr, <50 ppm Si, 30ppm Cu, 20 ppm Ni, <20 ppm Ca, <20 ppm Mg and <20 ppm Ti. Alloys containing from 200 to 1800 ppm O, all of which lie in the solid solution range of the V-O system, were prepared by arc melting vanadium together with portions of a high-oxygen master alloy. The master alloy was prepared by tamping pure V2O5 into holes drilled in a vanadium ingot and arc melting this five or six times in an inert gas atmosphere, inverting the button between each melting step. The oxygen content of the master alloy was then determined by vacuum fusion analysis. Vanadium containing less than 150 ppm O was prepared in the following manner. A bar of iodide vanadium was deoxidized by sealing it in a tantalum crucible with a few grams of high-purity calcium. This was held at 1100°C for 4 days to allow time for the oxygen to diffuse to the surface and to react with the calcium vapors. The calcium oxide product was later dissolved from the surface of the bar with dilute acetic acid. In this way vanadium containing from 20 to 50 ppm O was prepared. Sample Preparation. The are-melted ingots were cold swaged into 3/16-in. diam rods and these were machined into cylindrical tensile specimens with a reduced section of 1.00-in. length and 0.120-in. diam. The test specimens were annealed for 4 hr at 900°C in a dynamic vacuum of mm of Hg to remove hydrogen from the metal. This recrystal-lization treatment produced a uniformly fine-grained structure with a mean grain size of approximately 0.06-mm diam. The oxygen contents reported in this paper were determined by a vacuum fusion analysis of the tensile specimens after testing. Analyses for other interstitial or metallic impurities showed no significant changes from that of the original material. Tension Tests. Tension tests were performed on a screw-driven tensile machine at a constant cross-head speed of 0.01 in. per min. Tests at elevated temperatures were carried out by heating the

Jan 1, 1962

By Harold L. Riley

This Bureau of Mines paper describes the methods and practices used at the Peck quarry of the Crab Orchard Stone Co., Inc., one of the leading producers of dimension stone in the Crossville, Tenn., area. The product is marketed under the registered trademark "Crab Orchard Stone". Another large producer of stone from the Crossville district sells its product under the registered trademark of "Tenn-Quartz". Both companies, and a number of other companies and individuals who quarry and process dimension stone from the same general geological formation, are members of the Quartzite Producers Association of Tennessee. The salable product is shipped throughout the country for use as architectural building stone. In 1959, 653,008 cubic feet of stone was produced in the Crossville area and was sold for $1,414,405. Terms and descriptions used in this report are those of the quarry and building trades. The offices, pitching sheds, wire saws, railroad siding, and storage areas of the Crab Orchard Stone Co., Inc., are on a side road 0.3 mile north from a point 2.2 miles east of Crossville, Tenn., on U.S. Highway 70. The quarry is on this same side road 2.0 miles south of Highway 70. Crossville is 62 miles west of Knoxville and 65 miles northeast of Chattanooga, Tenn.

Jan 1, 1962

By D. G. Oss, S. E. Erickson

An automatic control method for the ferrosilicon heavy media process maintains media density within 0.01 specific gravity points. Continued demands for higher grade, competitive products from the Mesabi Range have resulted in experimental work such as that detailed for one concentrator. Various methods, step by step procedures and instruments used at an iron ore beneficiation plant in the development of an automatic control system are described. Work continues and it is hoped that further applications of control instrumentation can be made in the next operating season. The need for instrumentation and automatic control of the various parameters in the heavy media process of iron ore beneficiation has been apparent for some time. Continued demands for higher grade, competitive products from the Mesabi Range have made it necessary to increase the efficiency of the process in every possible way. In a typical heavy media flow scheme for iron ore beneficiation (Fig. 1) a sized, prepared feed (generally about —1% in. to +% in.) is fed to a heavy media separatory vessel, along with a ferrosilicon slurry. A separation of the feed is made on the basis of specific gravity. Low density particles overflow a tailings discharge weir, while high density ore particles sink to the bottom of the high density pool and are moved away to the concentrate discharge chute. Both products are passed over drainage screens and then are cleaned thoroughly of attached ferrosilicon on wash screens. Float material is generally stockpiled, while the sink product is shipped as a final concentrate. Undersize from the drain screens is returned directly to the circulating media sump. Wash screen undersize is cleaned of contaminating ore particles and slimes by passing through magnetic separators. Provision is also made for splitting a portion of the tailings drain undersize into the cleaning circuit if necessary for control of depth of tailings overflow, or for additional cleaning as required. Cleaned ferrosilicon is stored in a densifier and returned to the Circulating media sump as make-up material. Dilution water is also added to this sump to maintain a desired specific gravity of the circulating media. As in any process, operational intelligence is secured only by keeping records of the process variables. Generally apeaking, plant operators have neither the inclination nor the time to keep complete and detailed records of these variables over the course of their shift. Before instrumentation was added to aid the operator, specific gravity was measured by weighing a given volume of pulp at intervals of from 30 to 60 min. Scale readings were made at the beginning and end of each shift. No records were kept of operating conditions, such as rpm of the separatory ves-sel, media level in the machine, tons per hour of the products, and so forth. These items were recorded only when spot checks were made by the metallurgical staff. CONTlNlJOUS DENSITY RECORDING The first process instrument used, other than the usual ammeter on the drive motor of the separatory vessel, was a nuclear density gauge and its associated circular chart recorder. These instruments were used to indicate and record specific gravity of the circulating media. This was a tremendous aid to the operator in that tie was able to observe and correct the specific gravity at any time. There was also added incentive to make frequent corrections because of the permanent record made by the recorder of the densities. The addition of the nuclear density gauge was influential in securing optimum quality and recovery of the heavy media product. Manual control was improved, and it became possible for a good operator to main control within f.05 specific gravity units. This compares with an unknown quantity, estimated at f0.15 gravity units, when manual measurement and control was used. An example of the improvement in manual control over the course of one season&apos;s operations is shown in Fig. 2. Chart A is typical of the records made shortly after the gauge was installed. Needless to say, it was difficult for operators and foremen alike

Jan 1, 1962

By H. D. Kline

This paper is one of a series being prepared by the Bureau of Mines on methods, practices, and costs in various mining districts in the United States. The paper describes mining and ore recovery methods common to the Batesville manganese district, Independence County, Ark., and gives the costs of producing merchantable ore by three operators whose methods were more or less typical of those of many other local manganese producers. The operating costs reported were those of Leonard Baxter at mines on Brooks Hill for the calendar year 1958 and Arkansas Mining and Exploration Corp. at Section 16 mine and the Searcy group of mines and Miller-McGee Corp. at the Diener mine during the first 6 months of 1959. Manganese are was mined in the district as early as 1849 and almost continuously thereafter until August 1959, when termination of the Government&apos;s domestic manganese purchase program resulted in complete cessation of mining activity. During those years, production came from more than 189 mines and properties, of which only a few produced as much as 30,000 tons of merchantable ore.

Jan 1, 1962

By L. F. Mondolfo

An investigation of the relationship between properties of the elements and type of binary diagram formed was conducted. It was found that, for each type of equilibrium diagram, the factors for the size, valence, electronegativity, period, melting point, entropies of fusion, and sublimation calculated for each pair of elements cover a range of values. However, these factors show sufficient relationship to the equilibrium diagram so that the correlation of several of them can be used to predict the type of diagram formed, or at least limit the choice to only a few types. ThE goal of the metallurgist concerned with alloy development has always been to find a method that predicts the properties that can be obtained when a certain metal is added to another one. In most cases a qualitative predictiton of properties can be made if the equilibrium diagram is known. However, this means that for new metals the alloy development has to start with the experimental determination of the equilibrium diagrams. Because this determination is at least as complicated and time-consuming as the determination of the properties themselves, most alloy development has taken place by trial and error, and the study of the equilibrium diagrams has followed rather than preceded the creation of new alloys. Alloy structures and properties depend on the interaction between electrons and a complete knowledge of these interactions would permit prediction of structure and properties of alloys. Unfortunately direct measurement of these interactions is extremely difficult and somewhat doubtful and only properties that depend on them can be measured easily and with certainty. Study of the relationship between properties of the elements and equilibrium diagrams is not new. Besides the well known Hume-Rothery rule of the necessity of an atomic diameter fit within 15 pct for extensive miscibility in the solid, and the wide knowledge of the effect of such factors as size, electronegativity, electron-atom ratio on solid state features,"&apos; work relating to liquid state and liquid-solid reactions can be found in the literature. Of particular interest is the work by Axon,3 who investigated the effect of size and melting point on a selected number of eutectic and monotectic dia-

Jan 1, 1962

By H. I. Aaronson

Isothermally formed plates of proeutectoid a, lengthen at approximately the rates predicted by the Zener-Hillert equation, indicating that their lengthening kinetics are controlled by the volume diffusion of chromium in the ß matrix. Solution annealing treatments in the vicinity of the transus introduce a second mode of transformation, in which the lengthening rate is at least 1.8 x 104 faster than predicted by this equation. Little or no volume diffusion appears to accompany the latter transformation. The Presence of oxygen is evidently a Prerequisite for the occurrence of this reaction. X HE effects of thermal history prior to the initiation of transformations which proceed by nucleation and diffusional growth are currently evoking considerable interest. The rate of nucleation (but not the rates of growth) of pearlitel and of bainite,2 and the over-all rates of aging reactions in Al-cu3 and Al-si4 alloys have been shown to be appreciably dependent upon thermal history in the solid-solution region"&apos; or in the two-phase region prior to the onset of pre~ipitation.3,4 In none of these reactions, however, was the transformation mechanism changed by variations in the temperature-time path used to reach the reaction temperature. Preliminary experiments reported by M. K. McQuillan5,8 and a systematic investigation by Farrar and Margolin7 have disclosed that the transformation behavior of hypoeutectoid Ti-Cr alloys is considerably more sensitive to thermal history. Qualitative evidence strongly suggests that not only the rate of nucleation but also the rate of growth and even the mechanism of the ß — a reaction can undergo remarkable changes when a solution annealing treatment in the vicinity of the ß/a +ß, or transus temperature, is interposed between a high-temperature solution anneal (conventionallq at 1000°C) and the isothermal reaction treatment. The present investigation was undertaken in an attempt to ascertain the nature and origin of these effects. Study of the changes in the kinetics and morphology of the ß - a, reaction produced by varialtions in thermal history was the primary means employed for this purpose. EXPERIMENTAL PROCEDURE The compositions of the alloys used in this in~esti~ation are given in Table I. These alloys were homogenized for 5 days at 1050° C in evacuated (2 x 10 -5 mm of Hg), zirconium-gettered fused quartz capsules. The capsules themselves were enclosed in a porcelain chamber evacuated with a mechanical pump during the homogenization anneals. Upon completion of homogenization, the alloys were cooled to room temperature and then reheated to 550°C for 3 1/2 days in order to transform the alloys to a finely divided mixture of a and TiCr2, and thus provide an approximately constant initial mi-crostructure. Individual specimens were sealed in evacuated and internally gettered Vycor capsules and heat treated as previously described.8,9 EXPERIMENTAL RESULTS Ti-10.64 Pet Cr. This investigation was largely performed on the 0.64 pet Cr alloy. The "base"

Jan 1, 1962

By W. C. Smith, P. J. Hickey

After a short historical background of the process evolution, this article descvibes present-day plant facilities and operating techniques utilized for high-purity bismuth production. The plant is one of the world&apos;s largest, with an annual output of some one million pounds of refined bismutlz. PREVIOUS papers1 written by staff members of Cerro de Pasco Corp. have referred briefly to the production of refined bismuth. Since the Corporation is one of the world&apos;s foremost producers of high-purity bismuth, a detailed description of the process for extracting the metal may be of general interest. Following a short historical background of the development of the actual process, this presentation will trace the progress of bismuth from its entry into the primary smelting circuits to its concentration in electrolytic lead cell slimes. Our facilities for the treatment of anode muds will be described and the extractive methods given in some detail, with particular emphasis on the techniques which result in the production of refined metal. HISTORICAL BACKGROUND Shortly after Cerro de Pasco began smelting operations at Oroya, Peru in 1922, it became apparent that the dust carried by copper converter gas contained appreciable amounts of bismuth. Although dust collection efficiency was poor prior to building of the 550-ft stack and installation of the central cottrells in 1938, a large stock of dust was accumulated during the intervening years, having the following approximate composition: Oz. per ton Ag - 11.0 Pct Sn — 0.5 Pct Pb - 49.0 Pct Zn - 6.5 Pct Bi - 2.0 Pct Insol. - 1.5 Pct Cu - 0.7 Pct Fe - 2.3 Pct Sb - 3.0 Pct S - 10.0 Pct As - 7.5 In the mid-1920&apos;s, experimental crucible melts of this dust with carbon indicated that most of the bismuth and silver, and some of the lead, could be reduced to a fairly clean bullion. Other products were a small amount of leady copper matte and a slag high in zinc, arsenic, antimony, and lead; this slag contained some tin but only small quantities of silver, bismuth, and copper. After the laboratory results had been confirmed by operation of a small reverberatory, a dust reduction furnace was constructed. The ±10 pct Bi-Pb bullion produced from this operation was stocked until 1930, when an Oroya-designed converter type furnace3 was installed for the elimination of arsenic, antimony, and some lead from the bullion. This process concentrated the bismuth from 10 to about 60 pct. By means of the bismuth process developed4 by W. C. Smith at East Chicago (1909-1914) and the discovery of a method5 for separation of lead from bismuth with chlorine gas in 1929, it became possible to begin production of refined bismuth. Unfortunately, bismuth deleaded with chlorine always contained residual chlorides, and the removal of the chlorides by caustic soda left a lead content of 0.02 to 0.04 pct. This final problem was solved6 by substitution of air-blowing for the caustic treatment, which effectively removed all excess chlorine and gave bismuth which was practically lead-free. In 1934, a pilot electrolytic lead refinery began operations at Oroya. Lead smelting was resumed in 1935 and two years later a 100-ton-per-day lead refinery was put into service. In conjunction with the latter, the present-day Anode Residue Plant was constructed. Until 1940, the plant treated both lead anode slimes and dust reduction bullion. The dust reduction furnace was shut down in that year, and all cottrell dusts (with the exception of the product from the arsenic cottrell) were mixed with pyrite and treated in a Wedge roaster to eliminate all possible arsenic. Calcine from this operation joined the sinter plant feed; hence the bismuth from the copper and lead circuits was collected in the lead bullion and subsequently in lead anode slimes from the electrolytic lead refinery. The latter source has been the only bismuth-bearing material of any consequence entering the Anode Residue Plant from late 1940 to the present. A copper refinery began operating in 1948, and the cell mud from this plant is mixed with lead slimes and processed through the same circuit, though only a small quantity of bismuth is present in electrolytic copper cell residues. BISMUTH INTAKE Present-day routes which are followed by the new bismuth feed from its entry into the primary smelting circuits to its arrival at the Anode Residue Plant are traced schematically in Fig. 1. As illus-

Jan 1, 1962