By Bernard Porter

The solubility of UO2 was determined at 1,250° C. in ternary melts of UF4 and BaF2 with CaF2, LiF, and SrF2. The solubility of Ce02 was measured at 800° and 850° C. in a solution of CeF3, BaF2, and LiF. The amount of La203 which dissolves at 950° C. in a binary mixture of LiF and LaF3 and a ternary of LiF, LaF3, and BaF2 was also measured. In each case, the amount of soluble oxide was mound to be less than 5 weight-percent. A procedure was developed for filtering fused, oxide-saturated fluoride melts in order to obtain a representative sample for chemical analysis. The oxide content of the samples was determined by an inert-gas fusion procedure.

Jan 1, 1961

By Alton B. Cook

The practice of using partly depleted oil reservoirs for gas-storage operations is proving successful. Moreover, this practice provides a method of secondary oil recovery when gas is cycled at full-storage reservoir pressure. Because of the relative newness of this operation, a study was undertaken to assist engineers in developing improved gas-injection and production procedures and in calculating the amount of gas needed for completely repressuring reservoirs. This paper is the third in a series reporting the progress of a study by the Federal Bureau of Mines of reservoir performance during complete gas repressuring and gas cycling. A procedure for estimating secondary oil recovery by this method is also under study. One report (7)3/ describes the laboratory equipment. The other report (8) gives (1) data on the New York City field, Clay County, Tex., which has been converted to gas-storage operations; (2) laboratory data from research with a model oil reservoir, in which primary production, complete gas repressuring, and gas cycling for the New York City field were simulated; and (3) theory to explain reservoir performance during gas repressuring.

Jan 1, 1961

By C. E. Baltzer

This paper highlights the position of coal supply in regard to the requirements for electric-utility operations. The text and the appended tables outline the trend of thermal power development and fuel use in the electric-utility industry. Mention is made of several argumentative factors influencing the use of coal in relation to competitive oil and gas, and of the importance attached to developing a realistic understanding of the respective problems faced by the supplier and consumer of coal. * * * TREND OF" THERMAL POWER DEVELOPMENT T HE RATE OF ADVANCE in thermal power has been significant during recent years, particularly in the Atlantic Provinces, the Prairie Provinces, Ontario, and British Columbia. While dependence on thermal power in Quebec and the Northern Territories is less than in the remainder of Canada, these regions also eventually will have need for increased amounts of such power.

Jan 1, 1961

By M. A. Hammer

In this study by the Federal Bureau of Mines Pennsylvania anthracite from the Eastern Middle field was oxidized by concentrated nitric acid at steam-bath temperature for 24 to 1,000 hours. The quantitative data obtained include yields of nitric-acid soluble and insoluble products and the distribution of carbon and ash in each. The acid-insoluble residues were examined for solubility in aqueous sodium hydroxide. With a sodium hydroxide concentration of at least 1 normal, a portion of the residue could be extracted in the form of a true solution. With lower alkali concentrations, peptization occurred. Alkali solubility of the residue increased with length of oxidation. However, when expressed in percentages of original coal weight, the alkali solubility remained essentially constant after 192 hours of oxidation. This suggests that the alkali-soluble products are converted to acid-soluble products at the same rate as the original coal substance is converted to alkali-soluble material. Microscopic observations of the peptization of the acid-insoluble residues revealed a gross micellar physical structure. The action of nitric acid is apparently not restricted to the surface of a coal particle. The acid penetrates the particle through the pore structure, dissolving some of the ash and altering the bonds between the coal micelles. The bond alteration, as indicated by ultimate analyses, involves the physical and chemical adsorption of the components of nitric acid. Some of the altered bonds are not thermally stable; this instability is shown by the complete loss of peptizing ability when the acid-insoluble products are heated above 200° C. This loss is accompanied by the evolution of water, oxides of nitrogen, and hydrocyanic acid.

Jan 1, 1961

By H. Margolin, A. Coucoulas

Fused alumina or silica crucibles were used as the containing vessel. X-ray powder photographs were taken with CrKcll radiation and the use of Straumanis type Norelco cameras of 114.6 mm diam. Crystallographic data for these compounds are shown in Table I. These results are in agreement with others of this series reported previousiy by Wernick and Geller.l The abnormally large atomic volume of Eu and Yb metal3 is manifested in EuAl2, and YbAl2, when one compares them with the compounds reported in Ref. 1. However, the behavior of Yb in the Ni compound is the same as that observed in Ni5Yb having the Cu5Ca structure.4 Thus, it appears that Yb has a valence closer to 3 only in the Ni compounds; i.e.. the 2s and Id electrons are lost to the conduction band.1,4 Europium in EuAl2 appears to have a valence closer to 2. In previous work.' X-ray patterns of ingots of NdCo2 indicated a multiphase material with faint indication of the presence of a phase having the MgCu2 structure. It was thought that NdCo2 formed peri-tectically from the melt, resulting in a multiphase system when cooled under nonequilibrium conditions. An X-ray pattern of a sample from a melt cooled more slowly than in past work showed that the major phase was NdCo2. The lattice constant, Table 1, is in excellent agreement with the value one can predict from the data of Ref. 1. One of the other phases was identified as Co5Nd. The author wishes to thank J. H. Wernick for his guidance in this work, and D. Dorsi for the preparation of these compounds. 'J. H. Wernick and S. Geller: AIME Trans., in press. 'J. H. Wernick and S. E. Haszko: to be published. 'F. H. Spedding and A. II. Daane: Progress in Nuclear Energy, Series 5, Eds.: H. M. Finniston and J. P. Howe, McGraw-Hill Book Co., 1956. 'S. E. Haszko: to be published. 'J. H. Wernick and S. Geller: unpublished work. 6J. 11. Wernick and S. Geller: Acia Cryst., 1959, vol. 12, p. '162. A reinvestigation of the lattice parameters of Ti-Sn alloys by the present authors has revealed consistently hiher c and a values than those obtained by Worrier. The difference is most pronounced in the c-parameters which are, therefore, used as a basis of comparison. This discrepancy was not due to air contamination, since precautions were taken to exclude this possibility. Specimens for Debye-Scherrer photograms were prepared by arc-melting 15-g buttons of Bureau of Mines titanium and 99.99 pct Sn, with compositions of 6, 8, 10, and 12 at. pct Sn. These buttons were forged under an oxygen-acetylene torch to 1/8-in. sq rods to produce relatively fine grained material. Scale and some surface were ground off, and the rods, after wrapping in molybdenum and titanium sheet, were vacuum annealed 15 min at 800 °C to remove hydrogen. Heat treatment of one of the samples at 875°C to produce ß and reveal a at the surface showed no surface contamination. Following the vacuum treatment, the specimens were wrapped in molybdenum and annealed for 1 week at 800°C under two atmospheres of argon. After water-quenching, the rods were ground so that the thickness tapered to 0.1 mm at the tips. The ground specimens were then recapsuled as previously and reannealed 1 hr at 800°C to remove cold work. The

Jan 1, 1961

By E. Morrice

This report of the Federal Bureau of Mines presents a laboratory procedure, with the requisite equipment, for electrowinning ingot (liquid) cerium metal from a fused-fluoride bath, the metal purity being about 99.9 percent. Physicochemical studies, including bath properties and electrochemistry, are included, with a speculative model of the mechanisms involved. An historical review of the methods used for electrowinning misch metals and yttrim-group metals, as well as individual rare-earth metals, is presented. The electrolytic preparation of metal from fused salt and nonaqueous media is summarized, along with the unsuccessful attempts at depositing the metals from aqueous solutions.

Jan 1, 1961

By Gordon Jackson

"There are two accomplishments of air and gas drilling: a new series of economic and mechanical challenges; and, acceptance as a standard drilling and completion tool.The new challenges are related to the concept of using a gaseous circulating medium in drilling for oil or gas. For purposes of discussion, a two part division has been made: the challenge of fluid invasion control and that of equipment and tools. Great strides have been made in the development of materials and techniques to combat formation fluid invasion. Chemicals and the ""mist drilling"" technique, now in use, have the versatility to cope with a wide range of downhole fluid entry conditions.Equipment and tools have been developed to meet the challenges of better, more economic drilling and completion possible with a gaseous circulating fluid. Economic and operational challenges remain.Acceptance of air and gas drilling as a normal operating tool was reached with difficulty. It is now established as a means of reducing costs in exploratory and develop-mental well drilling, exemplified in a recent study of 226 wells covering 419,407 feet of hole in the United States. Air reached the projected depth in 85 per cent of the operations, although formation water was encountered in 48.7 per cent of the holes. Slim hole bit performance and cost all compared for overall bit averages as part of analysis."

Jan 1, 1961

By Harvard Eng

An industrial survey was made for the Missouri Basin Field Committee of the Department of the Interior to determine the type and quantity of water-borne mineral wastes and the water requirements of metal-processing industries in the basin in Kansas and western Missouri. Data are presented on metal-processing plants visited through June 30, 1959. Most of the plants were in the greater Kansas City area. This report is to be supplemented with a similar publication on other industries, including those producing sand and gravel, coal, petroleum, and chemicals. In 1958, 19 million pounds of waste materials was discharged from metal processing industries. Approximately 14 million pounds of this waste was in the form of ferrous sulfate, and 2 million pounds was ferric phosphate. Galvanizing, other hot dipping, and automotive industries contributed the greater part of iron compounds wasted; some of this waste occurred as sludge that was not discharged to water courses but was hauled to refuse dumps, podium was present in nearly all industrial wastes, and the total of more than 900,000 pounds constituted one of the larger material losses. Although small in quantity, electroplating and allied coating wastes contained metals that were expensive when originally purchased.

Jan 1, 1961

By L. A. Panek

During the past three years, USBM has developed an apparatus and technique for direct measurement of existing pressure and change of pressure in mine rock. This relatively simple and inexpensive monitor is reliable for months after being installed. It is used to determine shift of ground pressure created by different sequences of mining, to ascertain the cause of rock failures, and to evaluate the need for artificial support. The technique has been employed to measure pressures in limestone, greywacke, concrete, diabase, and soft iron ore. When rock is subjected to a load it is deformed. Ordinarily this is observed in a mine as the displacement of one point with respect to another—the deflection of the roof, which may be observed as a convergence between roof and floor; or the extrusion of material from the rib, which may be observed as a decrease of the distance between the rib and the post of a timber set. The effect of excessive pressure may be a rockburst if the rock is strong, or it may be squeezing ground if the rock is soft. Some desirable effects of high stress (high in relation to strength) are the caving of roof in a longwall mining operation, the caving of ore in block caving, and the decrease in mechanical energy required to break down the mineral seam in a retreating pillar-robbing operation. In any case, whether the observable effect of rock load is desirable or undesirable, it is a displacement, and depends on the following four factors: 1) The structure—the size and shape of openings, pillars, and linings, the geologic bedding and jointing. 2) The mechanical properties of the rock—prin-cipally the strength, modulus of elasticity, and flow characteristics. 3) The load or applied stress—primary sources are the weight of superincumbent rock, which increases with depth, and unrelieved tectonic stresses; secondary sources are redistributed pressures caused by other nearby openings, especially large mined out zones (rock pressure depends partly on the rock structure created by mining). 4) Duration of load, related to the length of time the opening is exposed. CONTROL OF ROCK DISPLACEMENT Rock displacement can be controlled by control of these four factors. Consider now the means of exercising such control over these factors. Control of the structural features is obviously possible to a great extent, as such control is exercised largely by choosing the method of mining and the methods of natural and artificial support. Rock properties vary, even within a particular mine, but they are controllable only in the limited sense that control may be exercised by choosing the beds or zones to be mined so that rocks with undesirable properties will not occupy critical positions within the rock structure created by mining. Rock pressure is the most complex of the four factors through which ground control can be achieved because it is invisible, difficult to measure, and poorly understood. Rock pressure is controllable only to the extent that control is exercised on the rock structure created by mining. Considering openings within a particular mine, time of exposure varies, and is readily controllable because it is easily measured and easily understood — the longer an opening stands, the greater the likelihood of failure or excessive convergence. Control is exercised by choice of an appropriate sequence of driving openings of different classes, such as haul-ageways and rooms, which are required to remain well supported for different lengths of time under different conditions. Again, control is exercised through the method of mining. All controllable factors can be controlled by proper design of the mining method. The orientation and relative positions of the mine workings and the sequence of their excavation are likely to be much more important to ground control than is the design of artificial support. This implies that the major decisions in regard to ground control are made, knowingly or not, at the time the mining method is chosen. WHY MEASURE ROCK PRESSURE In addition to restrictions on the several factors, control implies the measurement of these factors in some sense, whether only qualitatively by visual observation, or by actual quantitative determination with a measuring instrument. Rock pressure is the most difficult of these factors to measure, largely because of the interaction between the measuring device and the rock. Nevertheless, the quantitative

Jan 1, 1961

By A. E. J. Gallagher

This report summarizes the results of flotation studies conducted by the Federal Bureau of Mines on samples of extremely fine-grained lead-zinc sulfide ores. Samples from five ore deposits in the Pine Creek area, Coeur d'Alene district, Idaho, and one deposit in the Metaline district, Washington, were studied at the Albany Metallurgy Research Center to determine the recovery of sulfide lead and zinc by flotation. During the investigation it was found that flotation could be effectively applied to the selective recovery of exceedingly fine-grained lead and zinc sulfide minerals. Separation of galena and sphalerite was obtained on pulps ground through 1,600-mesh, in which most of the particles were smaller than 5 microns. Selectivity and recovery of minerals in this fine size range were enhanced by use of a chemical dye, diphenylthiocarbazone, as a galena promoter. Although unsuccessful on one ore, application of the dye in treatment of two other very fine-grained ores yielded lead concentrates containing over 62 percent Pb at recoveries in excess of 85 percent. More than 55 percent of the lead in these concentrates occurred as particles smaller than 2 microns.

Jan 1, 1961

By Nathaniel Wollman

About nine years ago the President's Materials Policy Co commission under the chairmanship of William Paley released its report entitled "Resources for Freedom." Not long ago the Senate Select Committee on National Water Resources under the chairmanship of Senator Kerr released a study entitled Water Supply and Demand. Both reports contained projections of future water user the report for 1975, and the Select Committee print for 1980 and 2000, It is my task to compare the two reports. In the initial letter from Mr. Kazmann arranging for thus session he suggested that I present "a critical evaluation of the Paley Report's section on water ?ten years later,? which might include a comparison of predicted and actual water-use rates and would spotlight the assumptions which lead to errors in the predictions , . ." It is possible to compare the results of both studies, and it possible to explain art of the differences that can be found between them. The remainder must remain shrouded in doubt, since the Paley Report did not give all details of the methods used in estimating the com¬ponents of water use.

Jan 1, 1961

By D. E. Parson, W. A. Morgan

This paper offers a brief review of current literature pertaining to vacuum degassing or vacuum casting of steel as practiced in the U.S.A., Germany and the U.S.S.R. The advantages of vacuum degassing of large forging ingots, heavy section casting, for the conversion of rimming bessemer steels to killed steel and for the production of transformer steels are discussed. Operating pressures, reduction in gas contents and improvements in hydrogen segregation, steel cleanliness and mechanical properties, obtained with the various techniques, are described. The paper includes a description of an experimental vacuum stream-droplet degassing unit and some preliminary results obtained at the Physical Metallurgy Division Research Laboratories Department of Mines and Technical Surveys, Ottawa on laboratory steel melts. Experimental 500 lb direct arc, basic melts have been spray cast into either ingot moulds or dry sand moulds, held inside a vacuum tank. Also 500 lb melts have been

Jan 1, 1961

By A. R. Turner

AERIAL survey methods have made enormous technical advances and gained new recognition since World War II. Before enlarging on this statement and reviewing some of the uses of aerial survey in industrial development it is important to de-fine what is meant by "aerial survey". The subject will be discussed in the broadest sense and references will be made to the four sections that compose the overall field of surveying operations from the air. These are: 1. Aerial photography and photo-graphic mapping. 2. The use of airborne electronic instruments for geodetic distance measurement and the determination of ground elevations. 3. Airborne geophysical surveying. 4. The extraction of qualitative and quantitative information from aerial photographs through the processes of "reading", analysis and interpretation. Many sciences and techniques are combined in aerial survey operations. The tools of the business include aircraft, finely engineered cameras, elaborate film processing and printing equipment, ground survey instruments, precision stereo-plotting instruments, map -

Jan 1, 1961

By M. Schussler, J. S. Brunhouse

Arc-melted and electron-beam melted tantalum in the cold-worked and the recrystallized conditions showed high strength, good tensile ductility, and excellent notch toughness down to 321°F. Arc-melted material, containing moderate amounts of interstitials, possessed better short-time strength than higher purity electron-beam melted material up to 2000°F. Cold-working substantially strengthened arc-melted tantalum, whereas electron-beam melted material exhibited a low work-hardening rate and possessed better formability characteristics. With identical compositions and microstructures, the mechanical properties of melted tantalum and uacuum-sintered tantalum should be similar. TANTALUM metal usage is increasing rapidly in a number of applications. The outstanding chemical corrosion resistance of tantalum accounts for its applications in chemical processing equipment for severe service conditions and for surgical uses in the medical field. The largest present requirements for tantalum are in the electronics industry, where its special properties are useful in capacitors. The high melting point (5425°F) and inherent ductility of tantalum also suggest that tantalum and tantalum-base alloys might offer an excellent combination of high strength at very high temperatures and good fabri-cability. Pure tantalum has been used in significant amounts in parts requiring high-temperature strength, such as heating elements, reflectors, and heat shields in high-vacuum high-temperature furnaces and in electronic tubes. A few very promising tantalum-base alloys have been developed and are being investigated extensively. The possibilities for tantalum as a high-temperature structural material, either unalloyed or alloyed, will become better defined when more extensive mechanical property data are known. pughl measured the tensile properties of vacuum-sintered tantalum in sheet form for the temperature range of 78" to 1500°K (-321' to 2240°F), and Bechtold reported data obtained at low temperatures.' Drennen3 determined creep and stress-rupture properties of both vacuum-sintered and arc-melted tantalum sheet at 1200 °F. Some additional data on the mechanical properties of tantalum at temperatures up to 5000 °F have been summarized elsewhere.4'5 It is probable that large structural shapes of tantalum, either unalloyed or alloyed, can most readily be produced from ingots prepared by melting. Consequently, the present investigation was undertaken to determine more extensive short-time mechanical properties of tantalum metal consolidated by melting. EXPERIMENTAL PROCEDURE Melting and Fabrication—Two tantalum ingots were utilized in this study to obtain information on the effect of interstitial elements on mechanical properties. Both ingots were melted from Union Carbide Metals Co. tantalum dendrites.

Jan 1, 1961

By M. D. Carver

The purpose of this investigation was to determine the effects of variations in content (near the residual level) of the impurities aluminum, nitrogen, manganese, and copper on the corrosion rate in pressurized hot water and in pressurized steam of zircaloy-3, a zirconium-base alloy of 0.25 percent tin and 0.25 percent iron. Thirty-five 10-pound ingots were cast with the appropriate additions of impurity elements, and these were converted to wrought sheets. These specimens were then tested both in water and in steam. The analysis of the resulting data showed that in environments of either pressurized hot water or superheated steam, corrosion rates increased with increasing content of aluminum, nitrogen, or manganese, but were not affected by variations of copper. The effects of aluminum and nitrogen were found to be greater than the effect of manganese. INTRODUCTION At the request of the Atomic Energy Commission (AEC) in August 1956, the Federal Bureau of Mines, in cooperation with Bettis Plant of Westinghouse Electric Corp., began investigating the effects of certain impurity elements on the corrosion rates of zircaloy-3 in pressurized hot water and in pressurized steam. It was necessary to know these effects in order to set control limits on residual impurity levels in zirnaloy-3, intended for heat transfer service in the nuclear reactor of the pressurized water type. A factorial expert it was designed by Westinghouse statisticians. The Atomic Energy Commission provided raw zirconium sponge purchased from Wah Chang Corp. The Bureau's laboratory at Albany, Oreg., made material of different combinations of impurity levels and subjected the material to corrosion tests. This report will describe the work done at the Bureau laboratory and will show, quantitatively the effects of different residual levels of aluminum or nitrogen, or manganese or copper on corrosion rates.

Jan 1, 1961

By F. E. Armstrong

This report describes development and application by the Bureau of Mines of techniques and instruments for using radioactive inert-gas tracers to determine flow paths through petroleum reservoirs that have natural fracture systems and for which water injection has been selected as the stimulative production method. A field test was made to prove the techniques and evaluate instrumentation. The feasibility of applying the techniques and instruments to the solution of reservoir problems in other stimulative methods of production also is discussed. Oil commonly is displaced from sandstone host rocks by the action of a driving force that causes the oil to move through interstices of the rock and into production wells. In addition to the requirements of oil being trapped within the sand pores and the presence of an effective displacement mechanism, the rock itself must have adequate permeability to permit flow of oil and other fluids.

Jan 1, 1961

By Wilbur I. Duvall

Surface vibrations of ground, rock, and structures resulting from blasting or other sources are often measured with portable seismographs. These instruments are usually supported by a three-point mount or tripod which is simply placed on a horizontal surface on which vibration levels are to be measured. The rigid-body motion of a tripod-supported seismograph is considered from the point of view that there should be no slippage of the feet with respect to the surface and none of the feet should leave the surface as a result of imparted motion. From these studies the following design criteria are deduced which assure that the seismograph will respond accurately to vibration levels as large as 1/2 g.:3/ First, the coefficient of friction between the feet and the surface on which the instrument rests should be as large as possible, preferably approaching unity; second, the center of gravity of the instrument should be vertically above the centroid of the three-point mount; and third, the vertical distance between the center of gravity of the instrument and the centroid of the three points of contact with the surface should be less than the perpendicular distance between the centroid point and anyone of the three sides of the triangle formed by the three points of contact. Portable seismographs that do not satisfy these conditions should be clamped to the surface if vibration levels above 0.1 g. are to be recorded.

Jan 1, 1961

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

Dispersion-containing titanium-copper alloys were prepared having mean free paths varying from 1.0 to 9.7 P. Tensile studies at room temperature and at 1000°F showed that little or no strengthening occurred when the mean free path exceeded 3 p. However, at lower values of mean free path appreczable strengthening was observed. A considerable amount of strengthening also resulted from copper in solid solution. DURING the past several years, an increasing amount of study has been devoted to dispersion hardening, an alloying process in which increased strength is obtained through the addition of a ran-

Jan 1, 1961

By D. H. Trollope

In engineering in general, close agreement between theoretical predictions and structural performance is rare—this is particularly true in rock slopes. Since the complexity of natural arrangements makes exact theoretical solutions of associated structural problems almost impossible, the role of theory should be that of developing guides or markers to which observations and experience can be related. The author in this paper has outlined the results of a theoretical study of highly idealized models which represent both granular materials and jointed rock. Some important practical considerations result—especially in regard to horizontal stresses—when theory is compared with full-scale experience. In the field of engineering activity, specific examples of close agreement between theoretical prediction and structural performance are rare. Particularly is this so for the case of rock slopes, where, owing to the complexity of the natural arrangements, it is quixotic to expect exact theoretical solutions to the associated structural problems. The role of theory is rather that of developing signposts or guide rails to which observations and experience can be related. It is with this in mind that the present paper has been prepared; the author's aim has been to set out briefly the results of a theoretical study of highly idealized models which represent both granular materials and jointed rock. Despite the idealization of the problem, it will be seen that the theoretical conclusions are in accord with full-scale experience, particularly as far as horizontal stresses are concerned, and they point to some important practical considerations. CLASSIFICATION OF ROCK SLOPES At the risk of over-simplification, an attempt has been made to classify the problem of rock slopes into three broad categories with respect to internal stress systems. These are illustrated in Fig. 1. It is tacitly assumed in this classification that the strength of individual particles is very much greater than the interparticle strength whether the particles are the crystals of an igneous rock (Case I) or the blocks of Cases 2 and 3. The Homogeneous Monolith: This case is representative of uniform unjointed rock. Under relatively low stress conditions the internal stress system may approximate to that of an elastic body as given by Terzaghi.' It is more usual, however, for overall stability, to consider the material as a rigid plastic which yields in shear when S =C + c tan 4> where S is the shear yield stress, o is the normal stress on the surface of failure, and C and d are empirical constants according to the Mohr-Coulomb criterion of failure. Sokolovsky has recently developed, for the first time, a series of mathematical solutions to problems involvinga C, mass subject to self-weight. He demonstrates that for such a case a semi-arch (Fig. 2) is stable. A corollary of this argument is that for a true C, d material a curved overhanging slope is possible and such an observation may well aid field identification of these materials. The shape of the curved slope face is however directly dependent on the C-value, and from the long-term point of view this is a most difficult value to establish with any degree of confidence. It is customary to measure C and 0 in some form of shear test—usually a triaxial compression test—on core specimens sampled from the rock, and as far as the author is aware the present case is the only one in which, as far as overall stability is concerned, such tests are

Jan 1, 1961

By R. H. Jamison

A relatively new haulage system is described. Employed by the Delmant Fuel Co.. the "Full Dimension" system provides an uninterrupted flow of coal from a loader or continuous miner at the face to the main line transportation system. This system is said to provide a higher percentage of recovery as well as additional safety and production. Delmont Fuel Co. is employing a comparatively new system of transportation known as a Full Dimension system. Cne of these systems has been in operation for a year at the company's 10-B Mine as a part of a conventional section. A second was installed at the No. 10 mine in late 1960 to handle the production of a Colmol in a pillar section. SYSTEM COMPONENTS A Full Dimension system is a haulage system that provides an uninterrupted flow of coal from a loader or continuous miner at the face to the main line transportation system. The equipment required for this system consists of a series of interconnected chain conveyors that are mobile and articulated. They will retract or extend a sufficient distance for the development of a five-entry system; or, in the Colmol pillar section, it provides reach of 210 ft in all directions from the section belt. The components of this system are: l)One 160-ft chain line placed in tandem with the belt conveyor. It has a self-propelled drive, is 20 in. wide and 9 in. deep. Moving this conveyor requires the assistance of a loading machine or cutting machine. 2) One 40-ft piggyback that discharges along the entire length of the 160 ft chain conveyor. 3) A mobile bridge carrier, which is a self-propelled conveyor with four wheel steer and four wheel drive, twenty-eight feet long, it delivers coal to the receiving end of the piggyback. Axles steer individually making possible almost lateral movement. 4) Another 40-ft piggyback, duplicate of item 2 that delivers coal along the entire length of item 3 (mobile bridge carrier). 5) A second mobile bridge carrier, similar to the first, which deliver coal to the piggyback (item 4). 6) A third 40-ft piggyback, duplicate of items 2 and 4. This pig is attached to the loading machine and delivers its coal along the length of the second mobile bridge conveyor. Since the original preparation of this paper, the Delmot Fuel Co. has been able to eliminate the 160-ft chain conveyor. This was accomplished by connecting the outby piggyback directly to a loading machine with an extended boom. The loading machine loads directly onto the belt. This change has resulted in a substantial reduction in moving time and greatly increased flexability. A single trailing cable powers the entire string of equipment. It is attached to the side of the equipment in such a way as to keep it off the ground and afford maximum protection. The tramming rate of this equipment is 90 fpm. The conveyor capacity in a conventional section at Delmont's mines is 7.5 tpm and in the Colmol section is 5.5 tpm. This regulation is a simple function of conveyor speed. To visualize operation of this equipment, it would be well for me to touch briefly on local conditions in the Upper Freeport seam in which we mine. (Also, see the photographs of some of the equipment in use.) DELMONT'S TOPOGRAPHY The Delmont Fuel Co. operates two mines in this seam in Westmoreland County, Pa. The No. 10 mine, which was opened in about 1912, is now almost worked out. Depending on economics in the industry, it has a life of two to four years on a declining production basis. A year ago a new drift mine was opened which is called No. 10-B. It is about two miles from the cleaning plant and is connected thereto by an overland belt conveyor. The new mine is being developed at a rate calculated to take up the slack as the old mine plays out. The Upper Freeport seam averages 4.2 ft in thickness in the area of the Delmont mines. It carries 4 in. of boney coal at the top of the seam and a middle man of from 2 to 4 in. We mine just above a 1-in. slate parting which has 4 to 6 in. of highly laminated coal beneath it. This material normally makes a very firm bottom. The roof varies from dark shale to sand rock and 36-in. bolts are placed on 4-ft centers for roof support. All working places are driven 20 ft wide on development and 25 ft wide on retreat. Selection of mobile chain conveyor equipment when it became available, was a very natural move for Delmont Fuel to make, because chain conveyors and piggybacks had been in use at the company's mines for about 12 years. Grades in the new mine

Jan 1, 1961